Microgel particles and related compositions, systems, and methods for use in 3D printing and 3D cell culture media

Abstract

Microgel particles for use in three-dimensional cell culture media are described. The microgel particles may be swellable and may have properties conducive to improved function and health of cells dispersed within the three-dimensional cell culture media. Related compositions, systems, and methods are also described. Also provided are a plurality of microgel particles and a liquid cell culture medium, in which the microgel particles swell to form a granular gel. Also provided are methods for preparing a three-dimensional culture medium. The method may include mixing a plurality of microgel particles (e.g., those described above) in the liquid cell culture medium. Also provided are methods for disposing cells in the three-dimensional cell culture medium. Also provided are methods for synthesizing proteins.

Description

[Technical field]

[0001] This application claims the benefit of U.S. Provisional Patent Application No. 62 / 469,939, filed March 10, 2017, and U.S. Publication No. 62 / 616,107, filed January 11, 2018, which are incorporated by reference in their entireties.

[0002] This invention was made with Government support under Grant No. DMR1352043 awarded by the National Institutes of Health. The Government has certain rights in this invention.

[0003] The disclosed embodiments relate to compounds, methods, and systems relating to three-dimensional cell culture. [Background technology]

[0004] Conventional cell culture techniques include culturing cells on two-dimensional (2D) substrates, such as microwell plates or petri dishes. Such 2D cell cultures often include a culture medium disposed on the substrate to promote the culturing of cells. However, the 2D environment of conventional cell cultures is often a poor substitute for the three-dimensional (3D) environment established by cells in vivo. For example, cell behavior often strongly depends on the microenvironment around the cells, i.e., in 2D cell cultures, the microenvironment around the cells may be different from the one that the cells would establish in the 3D microenvironment.

[0005] Thus, there is a need for improved compositions and methods for 3D cell culture media. Summary of the Invention

[0006] Microparticles for use in three-dimensional cell culture media (and related methods, uses, and compositions) are described. In some embodiments, the composition for use in the three-dimensional cell culture media comprises a plurality of microgel particles. The microgel particles may comprise a crosslinked polymer network. The crosslinked polymer network may in turn comprise a low charge density polymer molecule and a crosslinker. The low charge density polymer molecule may comprise a plurality of charged groups, and the average spacing between the charged groups is greater than ¼, ½, 1×, 1.5×, or 2× the Bjerrum length for the charged groups.

[0007] In one embodiment, a method of forming a microgel particle is provided. The method may include forming a solution including a crosslinker, a first monomer, a second monomer (wherein the second monomer is an acidic monomer, a basic monomer, a permanent cationic monomer, or a zwitterionic monomer), an initiator, and a solvent. The method may further include initiating the formation of a polymer in the solution, and precipitating the polymer from the solution where the polymer forms a microparticle.

[0008] In one embodiment, a three-dimensional cell culture medium is provided, which may include a plurality of microgel particles, such as those described above, and a liquid cell culture medium, in which the microgel particles swell to form a granular gel.

[0009] In one embodiment, a method for preparing a three-dimensional cell culture medium is disclosed, the method comprising mixing a plurality of microgel particles, such as those described above, in a liquid cell culture medium.

[0010] In one embodiment, a method for disposing cells in a three-dimensional cell culture medium is disclosed, which may include depositing cells in a granular gel comprising a plurality of microgel particles, such as those described above, swollen with a liquid cell culture medium.

[0011] In one embodiment, a method for synthesizing a protein is disclosed, which may include culturing cells in a vessel containing a granular gel comprising a plurality of microgel particles swollen with a liquid cell culture medium, and extracting from the vessel a protein synthesized by the cultured cells.

[0012] Other advantages and features of the present invention will become apparent from the following detailed description of various non-limiting embodiments of the present invention, when considered in conjunction with the accompanying figures. Unless otherwise noted, references cited herein are incorporated by reference in their entirety. In cases where the present specification and a document incorporated by reference include conflicting and / or inconsistent disclosure, the present specification shall control.

[0013] The details of one or more of the invention are set forth in the accompanying drawings and the description that follows. Other features, objects, and advantages of the invention will be apparent from the description and drawings, and from the claims. [Brief description of the drawings]

[0014] The accompanying drawings are not intended to be to scale. In the drawings, each identical or nearly identical element shown in various figures may be represented by a similar reference number. For clarity, not every element has been referenced in every figure. In the drawings: [Figure 1A] 1A-1C are schematics and formulas for low charge density particles. [Figure 1B] 1A-1C are schematics and formulas for low charge density particles. [Figure 1C] 1A-1C are schematics and formulas for low charge density particles. [Diagram 2] 2A-2B show examples of devices for culturing and interacting with 3D cell cultures. [Diagram 3] FIG. 3 is a schematic representation of the synthesis of anionic acrylamide hydrogels via precipitation polymerization, according to one set of embodiments. [Figure 4]FIG. 4 is a schematic representation of the synthesis of pH-responsive anionic acrylamide hydrogels via precipitation polymerization, according to one set of embodiments. [Diagram 5] FIG. 5 is a schematic representation of the synthesis of pH-responsive cationic acrylamide hydrogels via precipitation polymerization, according to one set of embodiments. [Figure 6] FIG. 6 is a schematic representation of the synthesis of permanent cationic acrylamide hydrogels via precipitation polymerization, according to one set of embodiments. [Figure 7] FIG. 7 is a schematic representation of the synthesis of zwitterionic acrylamide hydrogels via precipitation polymerization, according to one set of embodiments. [Figure 8] Figure 8 shows a method for preparing polyelectrolyte microgels with various charge densities through precipitation reactions: MAA-methacrylic acid, CBMA-carboxybetaine methacrylate, qDMAEMA-quadranized dimethylaminoethyl methacrylate. [Figure 9A] 9A to 9D are graphs showing the rheological changes of cationic microgels to which calcium was added. [Figure 9B] 9A to 9D are graphs showing the rheological changes of cationic microgels to which calcium was added. [Figure 9C] 9A to 9D are graphs showing the rheological changes of cationic microgels to which calcium was added. [Figure 9D] 9A to 9D are graphs showing the rheological changes of cationic microgels to which calcium was added. [Figure 10] FIG. 10 is a graph showing the yield stress (σy / σy0) as a function of C salt / C charge (mM / mM) in anionic and cationic microgels. [Figure 11] FIG. 11 is a graph showing the yield stress (σy / σy0) as a function of C2 charge / C salt (mM2 / mM) in anionic and cationic microgels. [Figure 12]FIG. 12 is a graph showing the yield stress (σy / σy0) as a function of C salt / C charge (mM / mM) in zwitterionic microgels. [Figure 13] FIG. 13 is a graph showing the yield stress (σy / σy0) as a function of C salt / C charge (mM / mM) in anionic (MAA), zwitterionic (CBMA), and cationic (qDMAEMA) microgels. [Figure 14] FIG. 14 is a bar graph showing % cell viability in anionic (MAA), zwitterionic (CBMA), and cationic (qDMAEMA) microgels. [Figure 15] FIG. 15 is a graph showing free calcium (%) as a function of C salt / C charge (mM / mM) for anionic (MAA) and zwitterionic (CBMA) microgels. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0015] Disclosed herein are compositions and methods for increasing the functionality of cells cultured in 3D cell culture media. The materials described herein can be used to create 3D cell culture media, allowing for faster cell culture, cell migration, and / or more robust fluorescent material and / or protein expression by cells cultured in the media. For example, the 3D cell culture media described herein can be constructed to provide improved functionality and health of cells dispersed within the 3D cell culture media.

[0016] For example, 3D cell culture medium has been proposed using commercially available carbomer swollen with liquid cell culture medium.However, commercially available carbomer (used to form 3D cell culture medium) tends to sequester nutrients from liquid cell culture medium.According to an embodiment, the 3D cell culture medium is prepared using microgel particles prepared with polymer that has reduced affinity for nutrients, such as minerals (e.g., calcium), from the liquid cell culture medium used to swell the microgel particles.

[0017] The use of microgel particles with low charge density disclosed herein, in some embodiments, results in a 3D cell culture medium that performs much better than 3D cell culture medium prepared with materials with high charge density. As used herein, the term "low charge density" refers to a property of microgel particles in which the average spacing of charged groups on the polymer backbone is close to or greater than the Bjerrum length of the system at standard ambient temperature (25°C). In some embodiments of low charge density microgel particles, the average spacing of charged groups on the microgel particles is greater than ¼, ½, or ¾ of the Bjerrum length of the system. In some embodiments, the average spacing of charged groups on the microgel particles is greater than the Bjerrum length of the system. In some embodiments, the average spacing of charged groups on the microgel particles is 1.5 times, 2.0 times, 2.5 times, or 3.0 times greater than the Bjerrum length of the system.

[0018] Bjerrum length characterizes the cross-over length at which charged groups on a polymer backbone begin to electrostatically interact. Returning to the figures, Figures 1A-C help to further clarify the concepts of low charge density and Bjerrum length. Figure 1A provides a schematic diagram of a copolymer chain containing neutral and charged groups. As one possible example of such a copolymer chain, Figure 1B shows a copolymer containing neutral acrylamide groups or monomer units and charged methacrylic acid groups or monomer units. Figure 1C provides a formula for determining the average distance between the charged groups of Figure 1A and for determining the Bjerrum length of the charged groups. As further shown in Figure 1C, a polymer with low charge density is defined as one in which the average distance between the charged groups is greater than the Bjerrum length of the system.

[0019] The average distance between the charged groups is defined in Equation 1:

number

[0020] The Bjerrum length for a system, such as a 3D cell culture medium, is defined by Equation 2:

number

[0021] Such polymers may be used to form microgel particles that can be swollen with liquid cell culture medium, resulting in 3D cell culture medium that forms a "yield stress" material onto which cells can be deposited in defined patterns, sometimes yielding to allow the culture of cell clusters.

[0022] According to some embodiments, when the 3D cell culture medium includes low charge density microgel particles, the 3D cell culture medium does not sequester nutrients from the liquid cell culture medium. Such nutrients may be minerals in some embodiments. Such nutrients may be multivalent ions (e.g., calcium ions) in some embodiments. However, when the average spacing between charged groups on the polymer backbone of the microgel particles is smaller or much smaller than the Bjerrum length (i.e., the particles have a high charge density), the multivalent ions often become sequestered. Sequestration of multivalent ions, e.g., calcium ions, can significantly adversely affect the function and health of cells in the 3D cell culture medium. Therefore, the use of low charge density microgel particles disclosed herein can provide improved function and health of cells in the 3D cell culture medium. The low charge density particles disclosed herein provide the desired swelling capacity while avoiding the disadvantages in cell health and viability caused by high charge density particles.

[0023] The 3D cell culture medium described herein allows for the culture of a variety of cellular structures, including, but not limited to, spheroids, embryoid bodies, tumors, cysts, and microtissues, and may also be used to preserve the structure of tissue engineered tissue constructs. In certain embodiments, the 3D cell culture medium may comprise a hydrogel comprising microgel particles dispersed in a liquid cell culture medium.

[0024] According to one embodiment, the microgel particles may comprise a biocompatible polymer and a crosslinker. The polymer acts as a polymer backbone to which the crosslinker is attached forming a polymer network. The polymer may be a copolymer comprising first and second monomeric units. The first or initial monomeric unit may be neutral while the second monomeric unit, or comonomer unit, may be charged. The components of the polymer network may be selected to promote the formation of low charge density microgel particles.

[0025] Monomers comprising a major percentage of the microgel particles may include acrylamide, N-alkylacrylamide, N,N-dialkylacrylamide, and acrylates. Non-limiting examples include acrylamide (AAm), N,N-dimethylacrylamide, N-isopropylacrylamide, poly(ethylene glycol) acrylate, poly(ethylene glycol) methacrylate, N-vinylcaprolactam, vinyl acetate, 2-hydroxyethyl acrylate, and N-vinylpyrrolidone.

[0026] The charged comonomer may include an ionic (i.e., having an acidic or basic functional group) comonomer. In some cases, the comonomer may have an acidic functional group and may be an acidic comonomer. Non-limiting examples of acidic comonomers include methacrylic acid, acrylic acid, sodium 4-styrenesulfonate, 2-acrylamido-2-methylpropanesulfonic acid, 2-carboxyethyl acrylate, and vinyl benzoic acid (all isomers). In some embodiments, the incorporation of the acidic comonomer in the microgel particles is less than 20 mol%. In some embodiments, the incorporation of the acidic comonomer may be from about 0 mol% to about 30 mol%, from about 0 mol% to about 20 mol%, from about 0 mol% to about 15 mol%, from about 0 mol% to about 10 mol%, or from about 0 mol% to about 5 mol%.

[0027] The charged comonomer may include an ionic (i.e., having an acidic or basic functional group) comonomer. In some cases, the comonomer may have a basic functional group and may be a basic comonomer. Non-limiting examples of basic comonomers include 2-(dimethylamino)ethyl methacrylate, 2-(dimethylamino)ethyl methacrylate, 2-(dimethylamino)ethyl acrylate, 2-aminoethyl methacrylamide, N-(3-aminopropyl) methacrylamide, and N-(3-dimethylaminopropyl) methacrylamide. In some embodiments, the incorporation of the basic comonomer in the microgel particles is less than 30 mol%, for example, less than 20 mol%. In some embodiments, the incorporation of the acidic comonomer may be from about 0 mol% to about 30 mol%, from about 0 mol% to about 20 mol%, from about 0 mol% to about 15 mol%, from about 0 mol% to about 10 mol%, or from about 0 mol% to about 5 mol%.

[0028] The charged comonomer may include a permanently ionized (i.e., having a permanent positive or negative charge, or both) comonomer. In some cases, the comonomer may have a permanent cationic functional group and may be a permanent cationic comonomer. Non-limiting examples of permanent cationic comonomers include (3-acrylamidopropyl)trimethylammonium chloride, [2-(acryloyloxy)ethyl]trimethylammonium chloride, and (2-dimethylamino)ethyl methacrylate)methyl chloride. In some embodiments, the incorporation of the acidic comonomer in the microgel particles is less than 20 mol%. In some embodiments, the incorporation of the permanent cationic comonomer may be from about 0 mol% to about 30 mol%, from about 0 mol% to about 20 mol%, from about 0 mol% to about 15 mol%, from about 0 mol% to about 10 mol%, or from about 0 mol% to about 5 mol%.

[0029] The charged comonomer may include a permanently ionized (i.e., having a permanent positive or negative charge, or both) comonomer. In some cases, the comonomer may have a zwitterionic (i.e., having both a positive and negative charge) functional group and may be a zwitterionic comonomer. Common zwitterionic groups include carboxybetaine, sulfobetaine, and phosphobetaine. Non-limiting examples of zwitterionic comonomers include 3-[[2-(methacryloyloxy)ethyl]dimethylammonio]propionate, [2-(methacryloyloxy)ethyl]dimethyl-(3-sulfopropyl)ammonium hydroxide, [3-(methacryloylamino)propyl]dimethyl(3-sulfopropyl)ammonium hydroxide, and (2-methacryloyloxyethyl phosphorylcholine). In some embodiments, the incorporation of zwitterionic comonomers in the microgel particles is less than 20 mol%. In certain embodiments, the incorporation of acidic comonomer may be from about 0 mol% to about 30 mol%, from about 0 mol% to about 20 mol%, from about 0 mol% to about 15 mol%, from about 0 mol% to about 10 mol%, or from about 0 mol% to about 5 mol%.

[0030] In some embodiments, the molar ratio of the first monomer and the second monomer can be controlled to provide the desired low charge density microgel particles. For example, in some embodiments, less than 60% of the sum of the first and second monomers is a second monomer (e.g., an acidic, basic, permanent cationic, or zwitterionic comonomer). In some embodiments, less than 50%, less than 40%, less than 30%, or less than 20% of the sum of the first and second monomers is a second monomer (e.g., an acidic comonomer).

[0031] A crosslinker is typically a compound capable of reacting with two or more polymer chains. In some embodiments, for example, the crosslinker is a compound that contains at least two vinyl groups. In some cases, the crosslinker is a low molecular weight compound. Non-limiting examples of suitable crosslinkers include N,N-methylenebis(acrylamide) (MBA), diethylene glycol diacrylate, pentaerythritol triallyl ether, and N,N-ethylenebis(methacrylamide).

[0032] In some embodiments, the crosslinker is a polymer. In some embodiments, the polymer may be a polyether. A non-limiting example of a suitable crosslinker is poly(ethylene glycol) diacrylate ("PEGda"). The crosslinker may be selected to have a number average molecular weight suitable for promoting the formation of microgel particles with desired swelling properties. In some cases, the crosslinker has a number average molecular weight between 250 g / mol and 10,000 g / mol. In some cases, the crosslinker has a number average molecular weight of at least about 500 g / mol, at least about 1000 g / mol, at least about 2000 g / mol, at least about 5000 g / mol, at least about 10,000 g / mol, at least about 20,000 g / mol, or at least about 50,000 g / mol. In certain embodiments, the crosslinker may be from about 500 g / mol to about 1000 g / mol, from about 500 g / mol to about 2000 g / mol, from about 500 g / mol to about 5000 g / mol, from about 500 g / mol to about 10,000 g / mol, from about 500 g / mol to about 20,000 g / mol, from about 500 g / mol to about 50,000 g / mol, from about 1000 g / mol to about 5000 g / mol, from about 1000 g / mol to about 10,000 g / mol, from about 1000 g / mol to about 20,000 g / mol, from about 1000 g / mol to about 50,00 0 g / mol, about 2000 g / mol to about 5000 g / mol, about 2000 g / mol to about 10,000 g / mol, about 2000 g / mol to about 20,000 g / mol, about 2000 g / mol to about 50,000 g / mol, about 5000 g / mol to about 10,000 g / mol, about 5000 g / mol to about 20,000 g / mol, about 5000 g / mol to about 50,000 g / mol, about 10,000 g / ml to about 20,000 g / mol, or about 10,000 g / mol to about 50,000 g / mol.

[0033] Initiators generally refer to substances capable of generating radical species under certain conditions (e.g., exposure to light and / or heat, or redox conditions). Initiators may include thermal initiators, including azo and peroxide compounds. Examples include azobisisobutyronitrile, 1,1'-azobis(cyclohexane-1-carbonitrile), 2,2'-azobis(4-methoxy-2,4-dimethylvaleronitrile), 2,2'-azobis(2,4-dimethylvaleronitrile), dimethyl 2,2'-azobis(2-methylpropionate), 2,2'-azobis(2-methylbutyronitrile), 2,2'-azobis(N-butyl-2-methylpropionamide), 2,2'-azobis[2-(2-imidazolin-2-yl)propane]dihydrochloride, 2,2'-azobis(2-methylpropionamide). Examples of initiators include, but are not limited to, 2,2'-azobis[N-(2-carboxyethyl)-2-methylpropionamidine] dihydrochloride, 2,2'-azobis[2-(2-imidazolin-2-yl)propane], 4,4'-azobis(4-cyanovaleric acid), 2,2'-azobis[2-methyl-N-(2-hydroxyethyl)propionamide], benzoyl peroxide, dicumyl peroxide, tert-butyl peroxide, tert-butyl peroxybenzoate, tert-butyl 2-ethylhexylcarboxylate peroxide, lauroyl peroxide, and 2-butanone peroxide. Initiators may also include photoinitiators. Examples include, but are not limited to, 2,2-dimethoxy-2-phenylacetophenone, Irgacure initiator (e.g., Ciba® IRGACURE® 2959), or 2-hydroxy-4′-(2-hydroxyethoxy)-2-methylpropiophenone.

[0034] The polymerization can be initiated with a redox initiator system, typically including ammonium persulfate (APS) or potassium persulfate (KPS) as a cocatalyst and a diamine compound. Examples of diamines include TEMED and dimethylaminopropionitrile (DMPN).

[0035] The concentration of monomer in the reaction mixture (e.g., the solution from which the microgel particles are precipitated) can affect the properties of the resulting microgel particles. Monomer concentrations that can be used include, but are not limited to, about 0.01M to about 0.1M, about 0.1M to about 1M, about 1M to about 2M, about 0.1M to about 0.8M, about 0.1M to about 0.6M, about 0.1M to about 0.4M, and about 0.1M to about 0.2M.

[0036] The crosslink density of the microgel particles can be governed by the ratio of monomer to crosslinker in the reaction mixture. The molar ratio of monomer to crosslinker includes, but is not limited to, about 10:1, about 20:1, about 50:1, about 100:1, about 150:1, or about 200:1. Ranges may also be formed from these ratios (e.g., about 10:1 to about 20:1).

[0037] According to an embodiment, a method may be performed to form microgel particles. The method includes forming a solution including a crosslinker; a first monomer; a second monomer (wherein the second monomer is an acidic monomer, a basic monomer, a permanent cationic monomer, or a zwitterionic monomer); an initiator; and a solvent. The method may further include initiating the formation of a polymer in the solution; and precipitating the polymer from the solution (wherein the polymer forms the microgel particles).

[0038] According to some embodiments, the microgel particles are prepared using a precipitation polymerization method, in which the monomers dissolve in the reaction medium, but the polymer formed does not. As the polymer is formed, it becomes insoluble and precipitates out of solution. In the presence of a crosslinker, discrete microparticles can be formed under certain conditions.

[0039] A free radical polymerization system generally includes an initiator capable of acting as a radical source (e.g., a photoinitiator, a thermal initiator, a redox initiator), one or more monomers (e.g., a vinyl monomer), and, optionally, a solvent. The mechanism of free radical polymerization is as follows: First, an initiator forms a free radical (e.g., through homolytic bond cleavage). In some cases, at least one of the free radicals may subsequently react with a monomer to form a monomer radical. The monomer radical may then react with one or more additional monomers to form an active polymer chain (i.e., a polymer radical). In some cases, an active polymer chain may terminate through biradical termination (e.g., recombination or disproportionation) to form an inactive polymer chain that is unable to react further (e.g., an active polymer chain P n and active polymer chain P m reacts to form an inactive polymer chain D n+m or inactive polymer chain D n and D. m (Forming a).

[0040] In precipitation polymerization, a solvent is needed to solvate the monomers and desolvate the formed polymer. Non-limiting examples of suitable solvents include ethanol, benzene, toluene, xylene, tetrahydrofuran (THF), 1,4-dioxolane, anisole, N,N-dimethylformamide (DMF), N,N-dimethylacetamide (DMAC), dimethylsulfoxide (DMSO), water, methanol, hexane, heptane, and acetonitrile.

[0041] The polymerization temperature may range from about 0° C. to about 120° C. In some cases, the temperature at which the polymerization is carried out is about 120° C. or less, about 110° C. or less, about 100° C. or less, about 90° C. or less, about 80° C. or less, about 70° C. or less, about 60° C. or less, about 50° C. or less, about 40° C. or less, about 30° C. or less, about 20° C. or less, about 10° C. or less, about 0° C. or less, or about −10° C. or less. In certain embodiments, the temperature at which the polymerization is carried out is from about -10°C to about 20°C, -10°C to about 50°C, -10°C to about 100°C, from about 0°C to about 20°C, from about 0°C to about 30°C, from about 0°C to about 40°C, from about 0°C to about 50°C, from about 0°C to about 100°C, from about 10°C to about 20°C, from about 10°C to about 30°C, from about 10°C to about 40°C, from about 10°C to about 50°C, from about 10°C to about 100°C, from about 20°C to about 30°C, from about 20°C to about 40°C. C, about 20°C to about 50°C, about 20°C to about 60°C, about 20°C to about 70°C, about 20°C to about 80°C, about 20°C to about 90°C, about 20°C to about 100°C, about 30°C to about 50°C, about 30°C to about 100°C, about 50°C to about 60°C, about 50°C to about 70°C, about 50°C to about 80°C, about 50°C to about 90°C, about 50°C to about 100°C, about 50°C to about 110°C, or about 50°C to about 120°C.

[0042] The size of the resulting individual microgel particles is measured using a phase contrast optical microscope. The size of the microgel particles is preferably less than 10 μm. In some cases, the size of the microgel particles is less than 5 μm. In some cases, the size of the microgel particles is between 3 μm and 5 μm.

[0043] The resulting polymer may comprise a crosslinked copolymer of a monomer and an ionic comonomer. In certain embodiments, the resulting polymer has a number average molecular weight of at least about 500 g / mol, at least about 1000 g / mol, at least about 2000 g / mol, at least about 5000 g / mol, at least about 10,000 g / mol, at least about 20,000 g / mol, at least about 30,000 g / mol, at least about 40,000 g / mol, at least about 45,000 g / mol, at least about 50,000 g / mol, at least about 60,000 g / mol, at least about 70,000 g / mol, at least about 80,000 g / mol, at least about 90,000 g / mol, at least about 100,000 g / mol, at least about 200,000 g / mol, at least about 300,000 g / mol, at least about 400,000 g / mol, or at least about 500,000 g / mol. In certain embodiments, the polymer comprising one or more dormant functional groups has a molecular weight of from about 500 g / mol to about 5000 g / mol, from about 500 g / mol to about 10,000 g / mol, from about 500 g / mol to about 20,000 g / mol, from about 500 g / mol to about 30,000 g / mol, from about 500 g / mol to about 40,000 g / mol, from about 500 g / mol to about 45,000 g / mol, from about 500 g / mol to about 50,000 g / mol, from about 500 g / mol to about 60,000 g / mol, from about 500 g / mol to about 70,000 g / mol, Approximately 500g / mol to approximately 80,000g / mol, approximately 500g / mol to approximately 90,000g / mol, approximately 500g / mol to approximately 100,000g / mol, approximately 500g / mol to approximately 200,000g / mol, approximately 500g / mol to approximately 300,000g / mol, approximately 500g / mol to approximately 400,000g / mol, approximately 500g / mol to approximately 500,000g / mol, approximately 10,000g / mol to approximately 20,000g / mol, approximately 10,000g / mol to approximately 30,000g / mol, approximately 10,000g / mol to approximately 40,000g / mol, approximately 10,000g / mol to approximately 45,000g / mol, approximately 10,000g / mol to approximately 50,000g / mol, approximately 10,000g / mol to approximately 60,000g / mol, approximately 10,000g / mol to approximately 70,000g / mol, approximately 10,000g / mol to approximately 80,000g / mol, approximately 10,000g / mol to approximately 90,000g / mol, approximately 10,000g / mol to approximately 100,000g / mol, approximately 10,000g / mol to approximately 200,000g / mol, approximately 10,000g / mol to approximately 300,000g / mol, approximately 10,000g / mol to approximately 400,000g / mol, approximately 10,000g / mol to approximately 500,000g / mol, approximately 40,000g / mol to approximately 50,000g / mol, approximately 40,000g / mol to approximately 60,000g / mol, approximately 40,000g / mol to approximately 70,000g / mol, approximately 40,000g / mol to approximately 8 ...90,000g / mol, approximately 40,000g / mol to approximately 100,000g / mol, approximately 40,000g / mol to approximately 120,000g / mol, approximately 40,000g / mol to approximately 130,000g / mol, approximately 40,000g / mol to approximately 140,000g / mol, approximately 40,000g / mol to approximately 150,000g / mol, approximately 40,000g / mol to approximately 160,000g / mol, approximately 40,000g / mol to approximately 170,000g / mol, approximately 40,000g / mol to approximately 180,000g / mol, approximately 40,000g / mol to approximately 200,000g / mol, approximately 40,000g / mol to approximately 250,000g / mol, approximately 40,0 / mol ~ approximately 90,000g / mol, approximately 40,000g / mol ~ approximately 100,000g / mol, approximately 40,000g / mol ~ approximately 200,000g / mol, approximately 40,000g / mol ~ approximately 300,000g / mol, approximately 40,000g / mol ~ approximately 400,000g / mol, approximately 40,000g / mol ~ approximately 500,000g / mol, approximately 80,000g / mol ~ approximately 100,000g / mol, approximately 80,000g / mol ~ approximately 200,000g / mol, The number average molecular weight ranges from about 80,000 g / mol to about 300,000 g / mol, about 80,000 g / mol to about 400,000 g / mol, about 80,000 g / mol to about 500,000 g / mol, about 100,000 g / mol to about 200,000 g / mol, about 100,000 g / mol to about 300,000 g / mol, about 100,000 g / mol to about 400,000 g / mol, or about 100,000 g / mol to about 500,000 g / mol.

[0044] Number average molecular weight Mn can be obtained by taking the number average of the molecular weights of the individual polymer chains according to Equation 3:

number

[0045] According to an embodiment, the 3D cell culture medium may be prepared by dispersing microgel particles in a liquid cell culture medium. The microgel particles may be mixed with the liquid cell culture medium using a centrifugal mixer, shaker, or any other suitable mixing device. During mixing, the microgel particles may swell in the liquid cell culture medium to form a material that is substantially solid when the applied shear stress falls below the yield stress, as described above. After mixing, entrained air or bubbles that were entrapped during the mixing process may be removed via centrifugation, stirring, or any other suitable method of removing bubbles from the 3D cell culture medium.

[0046] Hydrogels, for example 3D cell culture medium, may be prepared by adding microgel particles to aqueous solutions at various concentrations. In some embodiments, the aqueous solutions may comprise liquid cell culture medium. For example, polymer concentrations of less than 10wt% (based on the aqueous solution) may be used. Preferably, polymer concentrations of less than 5% are used. Highly preferably, polymer concentrations of less than 2% are used.

[0047] In some embodiments, the preparation of the 3D cell culture medium includes a buffering step to adjust the pH of the microgel particles and liquid cell culture medium mixture to a desired value. For example, some microgel particles may be made of a polymer with a predominantly negative charge, which may make the 3D cell culture medium too acidic (having a pH below the desired value). The pH of the 3D cell culture medium may be adjusted by adding a strong base to neutralize the acid and raise the pH closer to the desired pH. Alternatively, the mixture may have a pH higher than the desired value, and the pH of such a mixture may be lowered by adding an acid. According to some embodiments, the desired pH may be in the range between 5.5 and 6, or between 4.5 and 8.

[0048] As one non-limiting example, the 3D cell culture medium comprises approximately 0.2% to approximately 0.7% microgel particles by weight, which may be mixed with any suitable cell culture medium and swollen to form a 3D cell culture medium comprising approximately 99.3% to approximately 99.8% liquid cell culture medium by weight, as described above.

[0049] When mixed with liquid cell culture medium, the microgel particles can swell with the liquid cell culture medium to form a granular hydrogel material that functions as a 3D cell culture medium. Depending on the specific embodiment, the swollen microgel particles can have a characteristic size on the micron or submicron scale. For example, in some embodiments, the swollen microgel particles can have a size between about 0.1 μm and 100 μm, between about 1 μm and 100 μm, between about 1 μm and 50 μm, or between about 0.1 μm and 50 μm. Other values ​​are also possible.

[0050] As used herein, the term "microgel particles" refers to particles suitable for use in hydrogels and applies to particles both as they are incorporated into a hydrogel, as well as before and after incorporation into the gel.

[0051] Any suitable liquid culture medium may be used. The particular liquid cell culture medium may be selected depending on the type of cells to be placed in the 3D cell culture medium. The suitable liquid cell culture medium may be human cell culture medium, murine cell culture medium, bovine cell culture medium, or any other suitable cell culture medium. Depending on the particular embodiment, the microgel particles and the liquid cell culture medium may be combined in any suitable combination. For example, in one embodiment, the 3D cell culture medium comprises approximately 0.5% to 1% by weight of microgel particles.

[0052] Additionally, the 3D cell culture medium may have any suitable mechanical properties, and in certain embodiments, the mechanical properties may be adjusted via the relative concentrations of the microgel particles and the liquid cell culture medium, for example, a high concentration of microgel particles results in a 3D cell culture medium with a high elastic modulus and / or high yield stress.

[0053] The disclosed adjustability is advantageous for controlling the environment around the cells placed in the 3D cell culture medium.For example, the 3D cell culture medium may have mechanical properties adjusted to be similar to those found in vivo, so that the 3D cell culture medium may mimic the natural environment of the cells.However, it should be understood that the mechanical properties of the 3D cell culture medium may not be similar to those found in vivo, or may be adjusted to any suitable value, so that the present disclosure is not so limited.

[0054] The shear modulus of the hydrogel is measured by performing an oscillator frequency sweep at 1% strain over a wide range of frequencies. The shear modulus of the hydrogel preferably exceeds the shear viscous modulus by a relatively constant value less than 100 Pa. In some cases, the shear modulus of the hydrogel is less than 50 Pa. In some cases, the shear modulus of the hydrogel is from about 10 Pa to about 100 Pa, from about 10 Pa to about 80 Pa, from about 10 Pa to about 60 Pa, from about 10 Pa to about 40 Pa, or from about 10 Pa to about 20 Pa.

[0055] The yield stress of a hydrogel system (e.g., 3D cell culture medium) corresponds to a shear rate independent stress value. The yield stress of a hydrogel is measured by applying a unidirectional shear rate to a hydrogel sample, recording the resulting shear stress, and fitting the Herschel-Bulkley model to the resulting stress versus strain rate curve. The yield stress of the 3D cell culture medium can be less than 10 Pa. In some cases, the yield stress of the 3D cell culture medium is less than 5 Pa. In some cases, the yield stress of the 3D cell culture medium is approximately 5 Pa. In some cases, the yield stress of the 3D cell culture medium is approximately 1 Pa to approximately 10 Pa, approximately 1 Pa to approximately 8 Pa, approximately 1 Pa to approximately 6 Pa, approximately 1 Pa to approximately 4 Pa, or approximately 1 Pa to approximately 2 Pa.

[0056] According to an embodiment, the 3D cell culture medium may be made of materials such that the granular gel material undergoes a temporary phase change due to an applied stress (e.g., thixotropic or "yield stress" materials). Such materials may be solid or some other phase that retains its shape under an applied stress below the yield stress. Upon application of a stress above the yield stress, these materials may become a fluid or some other more malleable phase that may change shape. When the applied stress is removed, the yield stress material may become a solid again. Stress may be applied to such materials in any suitable manner. For example, energy may be applied to such materials to create a phase change. Energy may be in any suitable form, including mechanical, electrical, radiation, or light, etc.

[0057] The terms "yield stress" and "yield stress material" have been used and characterized in various ways in the art. For ease of explanation, the terms "yield stress" and "yield stress material" will be used herein, unless otherwise indicated, in accordance with the Herschel-Bulkley equations:

number

[0058] Furthermore, "yield stress" (i.e., Herschel-Bulkley yield stress) has been measured in the art in a variety of ways. Unless otherwise indicated herein, the yield stress of a sample is determined via the following method, by shearing the sample in a rheometer using a plate-plate configuration and via the Herschel-Bulkley equation: Prior to shearing, the rheometer tool surface may be roughened to prevent or reduce slippage at the sample-tool interface. Using the rheometer, the sample is subjected to high shear rates (e.g., 1000 s -1 ) and low shear rate (0.001s -1 ) at various shear rates between 100 and 200 mm. For each shear rate, the sample is sheared for 30 seconds, after which the shear stress data is collected and averaged. A series of shear stress measurements are collected consecutively for each shear rate. These shear rates are used to determine, via the Herschel-Bulkley equation, (1) whether the material has a yield stress (i.e., Herschel-Bulkley yield stress), and (2) the yield stress for the material. Those skilled in the art will recognize that for materials that have a yield stress, a plot of shear stress versus shear rate will show a plateau region at low shear rates, with data points that asymptotically approach the yield stress of the material at low shear rates. The yield stress is the shear stress at these small, near-zero shear rates, or at low or near-zero shear rates, e.g., 10 -3 s -1 0 strain rate, shear rate of 0. As used herein (unless otherwise indicated), a "yield stress material" is a material having a yield stress that can be determined via this method. Those skilled in the art will appreciate that for a yield stress material at low shear (e.g., near zero shear rate) (i.e., a Herschel-Bulkley yield stress material), the shear stress is independent of shear rate, and instead indicates a shear stress that depends only on the elastic component of the material.

[0059] The 3D cell culture medium made from the yield stress material may allow easy placement and / or retrieval of group cells at any desired location within the 3D cell culture medium, as described above. For example, cell placement may be achieved by causing a phase change from solid to liquid at a desired location within the yield stress material, such that the yield stress material flows and displaces when the cells are injected or otherwise placed at the desired location. After injection, the yield stress material may solidify around the placed cells, thus trapping the cells at the desired location.

[0060] However, it is understood that any suitable method may be used to deposit cells or other biomaterials in the 3D cell culture medium. For example, a syringe, a pipette, or other suitable tool may be used to inject cells into one or more locations of the 3D cell culture medium. In some embodiments, the injected cells may be formed into a pellet, for example, by centrifugation. However, it is understood that the 3D cell culture medium described herein allows cells to be suspended in liquid, thereby avoiding a centrifugation step when performing the test.

[0061] Regardless of how the cells are positioned in the medium, the yield stress of the yield stress material may be large enough to prevent yielding due to gravity and / or diffusion forces exerted by the cells, such that the position of the cells in the 3D cell culture medium may be substantially constant over time. Because the cells are fixed in place, they may be later retrieved from the same location for assay or testing by causing a phase change in the yield stress material to remove the cells. As described in more detail below, the placement and / or retrieval of the cell population may be performed manually or automatically.

[0062] The stress-relieving material described herein may have any suitable mechanical properties. For example, in some embodiments, the stress-relieving material may have an elastic modulus between approximately 1 Pa and 1000 Pa when the material is in a solid or other phase where the material retains its shape at an applied stress below the yield stress. In some embodiments, the yield stress required to transform the stress-relieving material into a fluid-like phase may be between approximately 1 Pa and 1000 Pa. When transformed into a fluid-like phase, the stress-relieving material may have a viscosity between approximately 1 Pa s and 10,000 Pa s. However, it should be understood that other values ​​for the elastic modulus, the yield stress, and / or the viscosity of the stress-relieving material are also possible, as the present disclosure is not so limited.

[0063] In some embodiments, the yield stress may be adjusted to match the compressive stress felt by the cell population in vivo, as described above. Without wishing to be bound by any particular theory, a yield stress material that yields at a particular stress value allows for the culture or expansion of an unlimited and / or unlimited cell population. Specifically, as the cell population grows, it may exert hydrostatic pressure on the surrounding yield stress material; this hydrostatic stress may be sufficient to cause the yield material to yield, thereby allowing the expansion of the cell population. In such embodiments, the yielding of the yield material during the culture of the cell population may provide the cell population with a yield stress material that maintains a constant pressure during the culture. Furthermore, since the yield stress material will yield when the applied stress exceeds the yield stress, a 3D cell culture medium made from the yield stress material may not be able to apply a stress to the cell population that exceeds the yield stress. The inventors recognize and appreciate that such an upper limit on the stress applied to a cell population can help ensure that the cells are not unnaturally constrained, damaged, or otherwise altered due to the application of large compressive stresses.

[0064] According to certain embodiments, the 3D cell culture medium made from a yield stress material may yield to accommodate waste, for example, fluid or other extracellular material from the cells disposed within the 3D cell culture medium. Without wishing to be bound by any particular theory, the pressure in the extracellular space may increase due to the expulsion of fluid or other material from the cells; if the yield stress of the 3D cell culture medium is exceeded, the 3D cell culture medium will yield to accommodate the waste, and the cells may expel fluid or other material without restriction. Such a 3D cell culture medium's ability to accommodate cell waste may enable the 3D cell culture medium to more closely mimic the in vivo environment. Furthermore, the inventors have recognized and understood that the 3D cell culture medium made from a yield stress material may allow for easy removal of cell waste for assays, testing, or any other suitable purpose, as described in more detail below.

[0065] The cell population may be placed in the 3D cell culture medium made from the yield stress material via any suitable method. For example, in some embodiments, the cells may be injected or otherwise placed in a specific location in the 3D cell culture medium with a syringe, pipette, or other suitable placement or injection device. In some embodiments, an array of automated cell dispensers may be used to inject multiple cell samples into a container of 3D culture medium. The tip of the placement device may be moved through the 3D cell culture medium to impart a sufficient amount of energy to cause yielding in the area around the tip so that the placement tool can be easily moved to any location in the 3D cell culture medium. In some examples, the pressure applied by the placement tool to deposit the cell population in the 3D cell culture medium may also be sufficient to cause yielding so that the 3D cell culture medium flows to accommodate the cell population. The movement of the placement tool may be performed manually (e.g., "by hand") or by machine or any other suitable mechanism.

[0066] In some embodiments, multiple independent cell populations may be placed in a single volume of 3D cell culture medium. For example, the volume of 3D cell culture medium may be large enough to accommodate at least 2, at least 5, at least 10, at least 20, at least 50, at least 100, at least 1000, or any other suitable number of independent cell populations. Alternatively, the volume of 3D cell culture medium may have only one cell population. Furthermore, it should be understood that a cell population may include any suitable number of cells, and the cells may be of one or more different types.

[0067] Depending on the specific embodiment, the cell groups may be arranged in the 3D cell culture medium according to any suitable shape, structure, and / or pattern. For example, the individual cell groups may be deposited as spheroids, and the spheroids may be arranged on a 3D grid, or any other suitable 3D pattern. The individual spheroids may all contain approximately the same number of cells and may be approximately the same size, or alternatively, different spheroids may have different numbers of cells and different sizes. In some embodiments, the cells may be arranged in shapes, such as embryoid or organoid bodies, tubes, cylinders, toroids, hierarchically branched duct networks, high aspect ratio objects, thin closed shells, or other complex shapes that may correspond to the structures of tissues, ducts, or other biological tissues.

[0068] According to an embodiment, a 3D cell culture medium made from a yield stress material may enable 3D printing of cells to form a desired pattern in three dimensions. For example, a computer-controlled injector tip may trace a spatial path within the 3D cell culture medium and inject cells at multiple locations along the path to form a desired 3D pattern or shape. The movement of the injector tip through the 3D cell culture medium may impart sufficient mechanical energy to cause the area around the injector tip to yield, allowing the injector tip to easily move through the 3D cell culture medium and also accommodate the injection of cells. After injection, the 3D cell culture medium may return to a solid-like phase to support the printed cells and maintain the printed structure. However, it should be understood that 3D printing technology is not required to use the 3D cell culture medium described herein.

[0069] 3D cell culture media made from yield stress materials may facilitate the recovery of cells from the cell culture media via a reverse process to that used to deposit the cells. For example, cells may be removed by simply moving a removal device, such as a syringe or pipette, to the location where the cells are located and aspirating the cells out of the cell culture media. As described above, moving the tip of the removal device through the 3D cell culture media may provide sufficient energy to cause the material to yield and accommodate the removal of cells from the 3D cell culture media. Such an approach may be used, for example, as part of a testing process in which multiple cell samples are deposited in the 3D cell culture media. The deposited cells may be cultured under the same conditions, but different samples may be exposed to different drugs or other treatment conditions. One or more samples may be collected multiple times to investigate the effect of the treatment conditions on the cells.

[0070] In some embodiments, the 3D cell culture medium may be used to support and / or preserve a cell-engineered tissue construct. For example, a tissue construct including a scaffold or other suitable structure on which a plurality of cells are placed may be placed in the 3D cell culture medium. The 3D cell culture medium may provide support that preserves the complex structure of the tissue construct while also providing a 3D environment for cell culture that may mimic that found in vivo.

[0071] It is understood that one or more compounds may be deposited with and / or adjacent to the cells. For example, soluble, non-cytoplasmic components may be deposited with the cells. These may include structural proteins (e.g., collagen, laminin), signaling molecules (growth factors, cytokines, chemokines, peptides), chemical compounds (pharmaceuticals), nucleic acids (e.g., DNA, RNAs), and others (nanoparticles, viruses, gene transfer vectors).

[0072] According to one embodiment, a method of synthesizing a protein is provided. Cells may be cultured in a vessel containing a granular gel comprising a plurality of microgel particles swollen with a liquid cell culture medium. Proteins synthesized by the cultured cells may then be extracted from the vessel. For example, in one embodiment, the cultured cells are pancreatic islet cells and the protein is insulin.

[0073] 2A-2B show examples of cell culture and interaction devices, including examples of interaction devices of such devices.

[0074] FIG. 2A shows a device 200 in which a biological cell 202 is suspended at a specific position in a 3D cell culture medium 204. The device includes interaction devices 210A and 210B that provide materials to the 3D cell culture medium 204. The device 210A provides a liquid cell culture medium that, when mixed with the microgel particles, forms the 3D cell culture medium 204. The device 210A may provide a liquid culture medium that provides nutrients as the cell 202 absorbs and uses the liquid cell culture medium from the 3D cell culture medium 204. The device 210B may also provide a substance, for example, by providing a controlled release substance 206 loaded with a drug to the 3D cell culture medium 204. The controlled release substance 206 may diffuse through the 3D cell culture medium 204 and be absorbed by the cell 202.

[0075] The device 200 may further include an interaction device that removes fluid from the 3D cell culture medium 204. As shown in Figure 2A, the device 200 may include a pump (e.g., a vacuum pump) 212, which may remove fluid from the 3D cell culture medium 204 via an outlet 214. In an embodiment, as shown in Figure 2A, the device 200 may include a filter-like membrane 216, which may allow some material to flow to the outlet 214, but may block hydrogels or other materials of the 3D cell culture medium 204 from passing through.

[0076] FIG. 2B shows another example of device 250, including various interaction devices. Devices and materials in the example of FIG. 2B that are identical to devices / materials in FIG. 2A share the same reference numerals. The example of FIG. 2B shows perfusion tubes 260 that allow one or more substances to be provided to the 3D cell culture medium 204. Three perfusion tubes are shown. The same substance may be provided from each tube 260, or different substances may be provided. Substances that may be provided include liquid cell culture medium, medicines, or other substances.

[0077] 3A and 3B may, in some embodiments, be operable to provide a substance to specific locations within the 3D cell culture medium 204, and in some embodiments, may be operable to provide a substance to form a concentration gradient of the substance along the 3D cell culture medium 204. By forming a gradient, different cells 202 may be exposed to different concentrations of the substance. Following exposure, the cells 202 may be interrogated (in and out of the 3D cell culture medium 204) to determine the effect of the different concentrations on the cells 202.

[0078] In one embodiment, as described above, the devices 210B and 260 of Figures 2A and 2B may be inserted or removed directly into the 3D cell culture medium 204 while the cells 202 are cultured in the 3D cell culture medium 204.

[0079] In the example of Figures 2A and 2B, pump 212 may be used to remove material from 3D cell culture medium 204 for any suitable purpose. For example, pump 212 may operate to remove by-products of cellular activity, including waste products or proteins produced by the cells, or by-products of cellular activity to be collected. As another example, pump 212 may impose a force on 3D cell culture medium 204 to remove material (e.g., material provided by device 210A, 210B, 260) through 3D cell culture medium 204. Pump 212 applying such a force is shown in the example of Figures 2A and 2B, but in other embodiments, the force source may be centrifugally rotating device 200, 250, or gravity, or any other suitable force source.

[0080] These and other aspects of the present invention will be further understood upon consideration of the following examples, which are intended to illustrate certain specific embodiments of the invention and are not intended to limit its scope to that defined in the claims. EXAMPLES

[0081] The following examples describe non-limiting embodiments of various aspects of the invention. Tables 1 and 2 provide a summary of key characteristics of the process parameters and hydrogels described in the examples below. Table 1 provides a summary of the precipitation polymerization conditions. Table 2 provides a summary of the properties of the packed hydrogels.

[0082] [Table 1]

[0083] [Table 2] EXAMPLES

[0084] This example describes a non-limiting method for forming microgel particles and the resulting particles. This example describes a composition that includes a monomer, an acidic comonomer, a crosslinker, a thermal initiator, and a solvent.

[0085] Acrylamide, methacrylic acid, and poly(ethylene glycol) diacrylate were dissolved in ethanol along with a thermal initiator (AIBN) and heated. n = 700 g / mol) and AIBN in a ratio of 45:4:1:0.5:0.05 (by weight). The mixture was purged with argon for 30 minutes to remove oxygen from the reaction. The flask was placed in a preheated oil bath at 60 °C for 4 hours. As the polymer formed, it precipitated out of the solution as discrete microgel particles. Figure 3 shows the reaction for the synthesis of anionic microgel particles. The molar ratios of the monomers are x = 0.82, y = 0.17, and z = 0.01, as shown in Figure 3.

[0086] The microgel particles were filtered, resuspended in ethanol, filtered again, and dried overnight in a vacuum oven. The microgel particles had a diameter of approximately 1-3 μm. The shear modulus at 1 Hz of a hydrogel (3 wt % polymer) made of these particles was approximately 20 Pa. The yield stress of a hydrogel (3 wt % polymer) made of these particles was approximately 2 Pa. EXAMPLES

[0087] This example describes a composition including a monomer, an acidic comonomer, a crosslinker, a thermal initiator, and a solvent. The molar ratios of the monomers were x=0.82, y=0.17, and z=0.01, as shown in FIG. 3. Ethanol, acrylamide, methacrylic acid, PEGda (M n = 700 g / mol) and AIBN in a ratio of 95:4:1:0.5:0.05 (by weight). The mixture was purged with argon for 30 min to remove oxygen from the reaction. The flask was placed in a preheated oil bath at 60 °C for 4 h. The microgel particles were filtered, resuspended in ethanol, filtered again, and dried in a vacuum oven overnight. EXAMPLES

[0088] This example describes a composition including a monomer, an acidic comonomer, a crosslinker, a thermal initiator, and a solvent. The molar ratios of the monomers were x=0.90, y=0.09, and z=0.01, as shown in FIG. 3. Ethanol, acrylamide, methacrylic acid, PEGda (M n= 700 g / mol) and AIBN in a ratio of 45:4:0.5:0.5:0.05 (by weight). The mixture was purged with argon for 30 min to remove oxygen from the reaction. The flask was placed in a preheated oil bath at 60 °C for 4 h. The microgel particles were filtered, resuspended in ethanol, filtered again, and dried in a vacuum oven overnight. The microgel particles had a diameter of 1-3 μm. The shear modulus at 1 Hz of a hydrogel (10 wt % polymer) made of these particles was approximately 40 Pa. The yield stress of a hydrogel (10 wt % polymer) made of these particles was approximately 4 Pa. EXAMPLES

[0089] This example describes a composition including a monomer, an acidic comonomer, a crosslinker, a thermal initiator, and a solvent. The molar ratios of the monomers were x=0.83, y=0.17, and z=0.002, as shown in FIG. 3. Ethanol, acrylamide, methacrylic acid, PEGda (M n = 700 g / mol) and AIBN in a ratio of 45:4:1:0.1:0.05 (by weight). The mixture was purged with argon for 30 min to remove oxygen from the reaction. The flask was placed in a preheated oil bath at 60 °C for 4 h. The microgel particles were filtered, resuspended in ethanol, filtered again, and dried in a vacuum oven overnight. EXAMPLES

[0090] This example describes a composition that includes a monomer, an acidic comonomer, a crosslinker, a thermal initiator, and a solvent.

[0091] Acrylamide, methacrylic acid, and N,N-methylenebis(acrylamide) were dissolved in ethanol along with a thermal initiator and heated. Ethanol, acrylamide, methacrylic acid, N,N-methylenebis(acrylamide), and AIBN were mixed in a ratio (by weight) of 45:4:0.5:0.1:0.05. The mixture was purged with argon for 30 minutes to remove oxygen from the reaction. The flask was placed in a preheated oil bath at 60 °C for 4 hours. Figure 4 shows the synthesis reaction for the synthesized microgel particles. The molar ratios of the monomers were x = 0.90, y = 0.09, and z = 0.01, as shown in Figure 4.

[0092] The microgel particles were filtered, resuspended in ethanol, filtered again, and dried in a vacuum oven overnight. EXAMPLES

[0093] This example describes a composition including a monomer, an acidic comonomer, a crosslinker, a thermal initiator, and a solvent. The molar ratio of the monomers was x=0.81, y=0.17, and z=0.02, as shown in FIG. 4. Ethanol, acrylamide, methacrylic acid, N,N-methylenebis(acrylamide), and AIBN were mixed in a ratio (by weight) of 45:4:1:0.2:0.05. The mixture was purged with argon for 30 minutes to remove oxygen from the reaction. The flask was placed in a preheated oil bath at 60°C for 4 hours. The microgel particles were filtered, resuspended in ethanol, filtered again, and dried in a vacuum oven overnight. The microgel particles had a diameter of approximately 2-4 μm. The shear modulus at 1 Hz of a hydrogel (2 wt% polymer) made of these particles was approximately 20 Pa. The yield stress of a hydrogel (2 wt% polymer) made of these particles was approximately 2 Pa. EXAMPLES

[0094] This example describes a composition including monomer, acidic comonomer, crosslinker, thermal initiator, and solvent. The molar ratio of monomer was x=0.82, y=0.17, and z=0.01, as shown in FIG. 4. Ethanol, acrylamide, methacrylic acid, N,N-methylenebis(acrylamide), and AIBN were mixed in a ratio of 45:4:1:0.1:0.05 (by weight). The mixture was purged with argon for 30 minutes to remove oxygen from the reaction. The flask was placed in a preheated oil bath at 60° C. for 4 hours. The microgel particles were filtered, resuspended in ethanol, filtered again, and dried in a vacuum oven overnight. EXAMPLES

[0095] This example describes a composition including monomer, acidic comonomer, crosslinker, thermal initiator, and solvent. The molar ratio of monomer was x=0.82, y=0.17, and z=0.01, as shown in FIG. 4. Ethanol, acrylamide, methacrylic acid, N,N-methylenebis(acrylamide), and AIBN were mixed in a ratio of 95:4:1:0.1:0.05 (by weight). The mixture was purged with argon for 30 minutes to remove oxygen from the reaction. The flask was placed in a preheated oil bath at 60° C. for 4 hours. The microgel particles were filtered, resuspended in ethanol, filtered again, and dried in a vacuum oven overnight. EXAMPLES

[0096] This example describes a composition including a monomer, a basic comonomer, a crosslinker, a thermal initiator, and a solvent. The molar ratios of the monomers were x=0.82, y=0.17, and z=0.01, as shown in FIG. 5. The ethanol, acrylamide, 2-(dimethylaminoethyl) methacrylate, PEGda (M n = 700 g / mol) and AIBN were mixed. The mixture was purged with argon for 30 min to remove oxygen from the reaction. The flask was placed in a preheated oil bath at 60 °C for 4 h. The microgel particles were filtered, resuspended in ethanol, filtered again, and dried in a vacuum oven overnight. EXAMPLES

[0097] This example describes a composition including monomer, permanent cationic comonomer, crosslinker, thermal initiator, and solvent. The molar ratio of monomer was x=0.82, y=0.17, and z=0.01, as shown in FIG. 6. Ethanol, acrylamide, [2-(acryloyloxy)ethyl]trimethylammonium iodide, PEGda (Mn=700 g / mol), and AIBN were mixed. The mixture was purged with argon for 30 minutes to remove oxygen from the reaction. The flask was placed in a preheated oil bath at 60° C. for 4 hours. The microgel particles were filtered, resuspended in ethanol, filtered again, and dried in a vacuum oven overnight. EXAMPLES

[0098] This example describes a composition including monomer, zwitterionic comonomer, crosslinker, thermal initiator, and solvent. The molar ratio of monomers was x=0.82, y=0.17, and z=0.01, as shown in FIG. 7. Ethanol, acrylamide, 3-[[2-(methacryloyloxy)ethyl]dimethylammonio]propionate, PEGda (Mn=700 g / mol), and AIBN were mixed. The mixture was purged with argon for 30 minutes to remove oxygen from the reaction. The flask was placed in a preheated oil bath at 60°C for 4 hours. The microgel particles were filtered, resuspended in ethanol, filtered again, and dried in a vacuum oven overnight. EXAMPLES

[0099] Figure 8 shows a method for preparing polyelectrolyte microgels with various charge densities through precipitation reactions: MAA-methacrylic acid; CBMA-carboxybetaine methacrylate; qDMAEMA-quaternary dimethylaminoethyl methacrylate.

[0100] 9A-9D are graphs showing the rheological changes in cationic microgels with added calcium.

[0101] FIG. 10 shows the effect of c 塩 / c 帯電 Yield stress (σ) as a function of (mM / mM) y / σ y0 ) is a graph showing

[0102] FIG. 11 shows the effect of c 2 帯電 / c 塩 (mM 2 Yield stress (σ) as a function of y / σ y0 ) is a graph showing

[0103] FIG. 12 shows the effect of c 塩 / c 帯電 Yield stress (σ) as a function of (mM / mM) y / σ y0 ) is a graph showing

[0104] FIG. 13 shows the c in anionic (MAA), zwitterionic (CBMA), and cationic (qDMAEMA) microgels. 塩 / c 帯電 Yield stress (σ) as a function of (mM / mM) y / σ y0 ) is a graph showing

[0105] FIG. 14 is a bar graph showing % cell viability in anionic (MAA), zwitterionic (CBMA), and cationic (qDMAEMA) microgels.

[0106] FIG. 15 shows the c 塩 / c 帯電 Graph showing free calcium (%) as a function of (mM / mM).

[0107] Unless otherwise defined, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which the disclosed invention belongs. Publications cited herein and the material for which they are cited are specifically incorporated by reference.

[0108] Those skilled in the art will recognize, or be able to ascertain using no more than routine experimentation, many equivalents to the specific embodiments of the invention described herein which equivalents are intended to be encompassed by the following claims.

Claims

1. 1. A composition for use in a three-dimensional cell culture medium, comprising: The composition comprises: A plurality of microgel particles, each of the plurality of microgel particles comprises a crosslinked polymer network; the crosslinked polymer network being low charge density polymer molecules, each of the low charge density polymer molecules comprises a plurality of charged groups, and the average spacing between the charged groups is greater than ¼, ½, 1×, 1.5×, or 2× the Bjerrum length of the three-dimensional cell culture medium at standard ambient temperature (25° C.); and Crosslinking Agent Including, wherein each of the low charge density polymers is a random copolymer comprising primary and secondary monomer units, the primary monomer units being derived from acrylamide and the secondary monomer units being derived from methacrylic acid, and less than 20% of the sum of the primary and secondary monomer units being secondary monomer units. A composition comprising:

2. The composition of claim 1 , wherein the crosslinker has an average molecular weight between 250 g / mol and 10,000 g / mol.

3. The composition of claim 1 , wherein the crosslinker comprises PEGDA or MBA.

4. The composition of claim 1 , wherein the crosslinker is hydrophilic.

5. A composition according to any one of claims 1 to 4, and The composition swells in a liquid cell culture medium to form a granular gel. A three-dimensional cell culture medium comprising:

6. 6. The three-dimensional cell culture medium of claim 5, wherein the three-dimensional cell culture medium has a pH between 5.5 and 6.

7. 6. The three-dimensional cell culture medium of claim 5, wherein the three-dimensional cell culture medium has a yield stress of 1 Pa to 10 Pa.