Organic electroluminescent materials and devices
By designing organic photoelectric materials with metal coordination complex structures with specific aspect ratios and rotational dipole moment alignment, the problem of insufficient photon extraction efficiency and color purity in OLED devices is solved, and more efficient photon extraction and longer equipment life are achieved.
Patent Information
- Application Number
- JP2017119911
- Authority / Receiving Office
- JP · JP
- Patent Type
- Patents
- Current Assignee / Owner
- Priority Date
- 2017-06-09
- Filing Date
- 2017-06-19
- Publication Date
- 2025-01-28
- Estimated Expiration
- 2037-06-19
AI Technical Summary
Existing OLED devices have limitations in photon extraction efficiency and color saturation, especially when achieving efficient full-color display and white light emission, it is difficult to take into account both photon extraction efficiency and color purity.
By designing an organic photoelectric material with a metal coordination complex structure, it increases its aspect ratio in one direction and optimizes the rotational dipole moment (TDM) alignment within the molecule to improve the photon extraction efficiency.
The photon extraction efficiency and color purity of OLED devices are significantly improved, and the full-color display effect is enhanced, especially under white light emission and high brightness conditions, achieving higher external quantum efficiency and longer device life.
Smart Images

Figure 0007622316000112 
Figure 0007622316000113 
Figure 0007622316000114
Abstract
Description
[Technical field]
[0001] This application claims priority under 35 U.S.C. §119(e)(1) to U.S. Provisional Application No. 62 / 352,119, filed June 20, 2016, U.S. Provisional Application No. 62 / 516,329, filed June 7, 2017, U.S. Provisional Application No. 62 / 352,139, filed June 20, 2016, U.S. Provisional Application No. 62 / 450,848, filed January 26, 2017, U.S. Provisional Application No. 62 / 479,795, filed March 31, 2017, and U.S. Provisional Application No. 62 / 480,746, filed April 3, 2017, the disclosures of which are incorporated by reference in their entireties.
[0002] The present disclosure relates to compounds for use as phosphorescent emitters and devices, such as organic light emitting diodes, that include said compounds. More specifically, the present disclosure relates to organometallic complexes that have a larger aspect ratio in one direction to increase efficiency and their use in OLEDs. [Background technology]
[0003] Optoelectronic devices that utilize organic materials are becoming increasingly desirable for a number of reasons. Many of the materials used to make such devices are relatively inexpensive, so organic optoelectronic devices have the potential for cost advantages over inorganic devices. In addition, the inherent properties of organic materials, such as flexibility, may make them well suited for certain applications, such as fabrication on flexible substrates. Examples of organic optoelectronic devices include organic light-emitting diodes / devices (OLEDs), organic phototransistors, organic photovoltaic cells, and organic photodetectors. For OLEDs, organic materials may have performance advantages over traditional materials. For example, the wavelength at which an organic light-emitting layer emits light can generally be easily tuned with appropriate dopants.
[0004] OLEDs utilize thin organic films that emit light when a voltage is applied across the device. OLEDs are becoming an increasingly interesting technology for use in applications such as flat panel displays, lighting and backlighting. Several OLED materials and configurations are described in U.S. Patent Nos. 5,393, 6,433, 6,511, 6,671, 6,781, and 7,933, 7,825, which are incorporated herein by reference in their entireties.
[0005] One application of phosphorescent emissive molecules is full color displays. Industry standards for such displays require pixels adapted to emit specific colors, referred to as "saturated" colors. In particular, these standards require saturated red, green, and blue pixels. Alternatively, OLEDs can be designed to emit white light. Conventional liquid crystal display emission from a white backlight is filtered with absorbing filters to produce red, green, and blue emission. Similar techniques can be used with OLEDs. White OLEDs can be either single EML devices or stacked structures. Color can be measured using CIE coordinates, which are well known in the art.
[0006] An example of a green emitting molecule has the following structure: [ka] The compound is tris(2-phenyl)iridium, denoted as Ir(ppy)3.
[0007] In this figure and later figures herein, we depict the coordinate bond from nitrogen to the metal (here Ir) as a straight line.
[0008] As used herein, the term "organic" includes polymeric and small molecule organic materials that can be used to fabricate organic optoelectronic devices. "Small molecule" refers to any organic material that is not a polymer, and "small molecules" can actually be quite large. Small molecules can include repeat units in some circumstances. For example, the use of long chain alkyl groups as a substituent does not remove a molecule from the "small molecule" class. Small molecules can be incorporated into polymers, for example, as pendant groups on a polymer backbone or as part of the backbone. Small molecules can also serve as the core moiety of a dendrimer, which consists of a series of chemical shells built on the core moiety. The core moiety of the dendrimer can be a fluorescent or phosphorescent small molecule emitter. Dendrimers can be "small molecules," and it is believed that all dendrimers currently used in the field of OLEDs are small molecules.
[0009] As used herein, "top" means furthest from the substrate, while "bottom" means closest to the substrate. When a first layer is described as "disposed over" a second layer, the first layer is disposed further from the substrate. There may be other layers between the first and second layers, unless it is specified that the first layer is "in contact with" the second layer. For example, a cathode may be described as "disposed over" an anode, even though there are various organic layers in between.
[0010] As used herein, "solution processable" means capable of being dissolved, dispersed or transported in and / or deposited from a liquid medium, either in the form of a solution or suspension.
[0011] A ligand may be referred to as "photoactive" if it is believed that the ligand directly contributes to the photoactive properties of the emissive material. A ligand may be referred to as "ancillary" if it is believed that the ligand does not contribute to the photoactive properties of the emissive material, although the ancillary ligand may modify the properties of the photoactive ligand.
[0012] As used herein, and as would be generally understood by one of ordinary skill in the art, a first "highest occupied molecular orbital" (HOMO) or "lowest unoccupied molecular orbital" (LUMO) energy level is "greater than" or "higher than" a second HOMO or LUMO energy level if the first energy level is closer to the vacuum energy level. Since ionization potentials (IPs) are measured as negative energies relative to the vacuum level, a higher HOMO energy level corresponds to an IP having a smaller absolute value (a less negative IP). Similarly, a higher LUMO energy level corresponds to an electron affinity (EA) having a smaller absolute value (a less negative EA). In a conventional energy level diagram with the vacuum level at the top, the LUMO energy level of a material is higher than the HOMO energy level of the same material. A "higher" HOMO or LUMO energy level appears closer to the top of such a diagram than a "lower" HOMO or LUMO energy level.
[0013] As used herein, as would be generally understood by one of ordinary skill in the art, a first work function is "greater than" or "higher than" a second work function if the first work function has a higher absolute value. Since work functions are generally measured as negative numbers relative to the vacuum level, this means that a "higher" work function is more negative. In a conventional energy level diagram with the vacuum level at the top, a "higher" work function is illustrated as being further away from the vacuum level in a downward direction. Thus, the definition of the HOMO and LUMO energy levels follows a different convention than work functions.
[0014] Further details regarding OLEDs and the above definitions can be found in US Pat. No. 6,399,633, which is incorporated herein by reference in its entirety. Summary of the Invention
[0015] According to an aspect of the present disclosure, a compound is disclosed having a metal coordination complex structure with at least two ligands coordinated to a metal. The compound has a first substituent R 1a first distance between the metal and R 1 is defined as the distance between one of the atoms in the R 1 the first distance being longer than any other atom-metal distance between the metal and any other atom in the compound; a sphere having a radius r having its center at the metal, the radius r being greater than the radius of the sphere between the metal and any other atom in the compound; 1 When the first distance is defined as the smallest radius that allows for enclosing all atoms that are not part of the radius r, the first distance is at least 2.9 Å longer than the radius r.
[0016] According to another aspect, an OLED is disclosed that includes an anode, a cathode, and an organic layer disposed between the anode and the cathode, the organic layer including a compound having a metal coordination complex structure, the compound being capable of functioning as an emitter in an organic light emitting device at room temperature, the compound having at least two ligands coordinated to the metal, and the compound having a first substituent R at one site around the ligand. 1 a first distance between the metal and a distance R furthest from the metal; 1 said first distance being greater than any distance between said metal and any other atom in said compound; a sphere having a radius r at its center, said radius r being greater than any distance between said metal and any other atom in said compound; 1 When r is defined as the smallest radius that allows for enclosing all atoms that are not part of the molecule, the first distance is at least 2.9 Å longer than the radius r.
[0017] According to another aspect, an OLED is disclosed that includes an anode; a cathode; and an emissive layer disposed between the anode and the cathode, the emissive layer including a phosphorescent emissive compound. The phosphorescent emissive compound has a characteristic emission spectrum with a full width at half maximum (FWHM) value of 40 nm or less. The OLED has a typical emission spectrum of 0.1 mA / cm at room temperature when a voltage is applied across the device. 2 has an EQE of at least 25% as measured by
[0018] According to another aspect, a consumer product is disclosed that includes an OLED. The OLED includes an anode; a cathode; and an organic layer disposed between the anode and the cathode, the organic layer including a compound having a metal coordination complex structure. The compound can function as an emitter in an organic light emitting device at room temperature; the compound has at least two ligands coordinated to the metal; and the compound has a first substituent R at one site around the ligand. 1 a first distance between the metal and a distance R furthest from the metal; 1 said first distance being greater than any distance between said metal and any other atom in said compound; a sphere having a radius r at its center, said radius r being greater than any distance between said metal and any other atom in said compound; 1 When r is defined as the smallest radius that allows for enclosing all atoms that are not part of the molecule, the first distance is at least 2.9 Å longer than the radius r.
[0019] According to another aspect, a consumer product is disclosed that includes an OLED, the OLED including: an anode; a cathode; and an emissive layer disposed between the anode and the cathode, the emissive layer including a phosphorescent emissive compound; the phosphorescent emissive compound has a characteristic emission spectrum with a FWHM value of 40 nm or less, and has a specific emission spectrum of 0.1 mA / cm at room temperature when a voltage is applied across the device. 2 has an EQE of at least 25% as measured by [Brief description of the drawings]
[0020] [Figure 1] FIG. 1 shows an organic light emitting device.
[0021] [Diagram 2] FIG. 2 shows an inverted organic light emitting device that does not have a separate electron transport layer.
[0022] [Diagram 3] FIG. 3 shows an example of a 2-phenylpyridine based iridium phosphorus light emitter.
[0023] [Figure 4] FIG. 4 shows an example of a 4-substituted pyridine structure in which the transition dipole moment vector (dashed line) is aligned along the long axis of the molecule.
[0024] [Diagram 5] FIG. 5 shows an example of a phenylpyridine-based ligand in which substitutions at R1, R2, R3, and R4 allow for longitudinal axis alignment with the TDM vector represented by the dashed line.
[0025] [Figure 6] FIG. 6 shows a structure in which a trans nitrogen-bound CN ligand is attached to a diketone introducing C2 rotational symmetry.
[0026] [Figure 7] FIG. 7 is a schematic diagram of the trans nitrogen axis and the preferred alignment of the TDM vector and major axis with this axis.
[0027] [Figure 8] FIG. 8 shows a schematic diagram of the C3 or pseudo-C3 symmetric structure and the R1, R2, and R3 molecular long axes, as well as the preferred alignment of the TDM vector with this C3 rotation plane.
[0028] [Figure 9] FIG. 9 shows one possible ligand substitution pattern that allows for molecular long axis and TDM alignment with the C3 plane of rotation of the fac-tris-bidentate organometallic emitters.
[0029] [Figure 10] FIG. 10 shows an example of a bottom-emitting OLED device stack for determining EQE without optical enhancement.
[0030] [Figure 11]FIG. 11 shows the experimental setup for the angle-dependent photoluminescence experiments used to measure emitter alignment.
[0031] [Figure 12] FIG. 12 shows experimental data comparing horizontally oriented emitter Compound 152 with randomly (isotropically) oriented emitter tris(2-phenylpyridine)iridium. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
[0032] In general, an OLED comprises at least one organic layer disposed between and electrically connected to an anode and a cathode. When a current is applied, the anode injects holes and the cathode injects electrons into the organic layer(s). The injected holes and electrons migrate to the oppositely charged electrode, respectively. When an electron and hole localize on the same molecule, an "exciton" is formed, which is a localized electron-hole pair having an excited energy state. Light is emitted via a photoemissive mechanism when the exciton relaxes. In some cases, the exciton may be localized on an excimer or exciplex. Non-radiative mechanisms such as thermal relaxation may also occur, but are generally considered undesirable.
[0033] Early OLEDs used emissive molecules that emitted light from their singlet state ("fluorescence"), as disclosed, for example, in U.S. Patent No. 4,769,292, which is incorporated by reference in its entirety. Fluorescence emission typically occurs on a time frame of less than 10 nanoseconds.
[0034] More recently, OLEDs have been demonstrated that have emissive materials that emit light from triplet states ("phosphorescence"). Baldo et al., "Highly Efficient Phosphorescent Emission from Organic Electroluminescent Devices," Vol. 395, pp. 151-154, 1998; ("Baldo-I") and Baldo et al., "Very high-efficiency green organic light emitting devices based on electrophosphorescence," Appl. Phys. Lett., Vol. 75, No. 3, pp. 4-6 (1999) ("Baldo-II"), which are incorporated by reference in their entireties. Phosphorescence is described in further detail in U.S. Pat. No. 7,279,704, columns 5-6, which are incorporated by reference.
[0035] FIG. 1 shows an organic light-emitting device 100. The figures are not necessarily drawn to scale. The device 100 may include a substrate 110, an anode 115, a hole-injection layer 120, a hole-transport layer 125, an electron-blocking layer 130, an emissive layer 135, a hole-blocking layer 140, an electron-transport layer 145, an electron-injection layer 150, a protective layer 155, a cathode 160, and a barrier layer 170. The cathode 160 is a compound cathode having a first conductive layer 162 and a second conductive layer 164. The device 100 may be fabricated by depositing the layers described, in order. The properties and functions of these various layers, as well as example materials, are described in more detail in US Pat. No. 7,279,704, columns 6-10, which are incorporated by reference.
[0036] Further examples are available for each of these layers. For example, a flexible and transparent substrate-anode combination is disclosed in U.S. Patent No. 5,844,363, which is incorporated by reference in its entirety. An example of a p-doped hole transport layer is m-MTDATA doped with F4-TCNQ in a molar ratio of 50:1, as disclosed in U.S. Patent Application Publication No. 2003 / 0230980, which is incorporated by reference in its entirety. Examples of emissive and host materials are disclosed in U.S. Patent No. 6,303,238 to Thompson et al., which is incorporated by reference in its entirety. An example of an n-doped electron transport layer is BPhen doped with Li in a molar ratio of 1:1, as disclosed in U.S. Patent Application Publication No. 2003 / 0230980, which is incorporated by reference in its entirety. U.S. Patent Nos. 5,703,436 and 5,707,745, which are incorporated by reference in their entirety, disclose examples of cathodes including composite cathodes having a thin layer of metal such as Mg:Ag with an overlying transparent, conductive, sputter-deposited ITO layer. The theory and use of blocking layers are described in more detail in U.S. Patent No. 6,097,147 and U.S. Patent Application Publication No. 2003 / 0230980, which are incorporated by reference in their entirety. Examples of injection layers are provided in U.S. Patent Application Publication No. 2004 / 0174116, which is incorporated by reference in its entirety. A description of protective layers can be found in U.S. Patent Application Publication No. 2004 / 0174116, which is incorporated by reference in its entirety.
[0037] FIG. 2 shows an inverted OLED 200. The device includes a substrate 210, a cathode 215, an emissive layer 220, a hole transport layer 225, and an anode 230. Device 200 may be fabricated by depositing the layers described, in order. Because the most common OLED configuration has the cathode disposed above the anode, and device 200 has the cathode 215 disposed below the anode 230, device 200 may be referred to as an "inverted" OLED. Materials similar to those described with respect to device 100 may be used in the corresponding layers of device 200. FIG. 2 provides an example of how some layers may be omitted from the structure of device 100.
[0038] The simple layer structures illustrated in Figures 1 and 2 are provided as non-limiting examples, and it is understood that embodiments of the present invention may be used in conjunction with a wide variety of other structures. The specific materials and structures described are exemplary in nature, and other materials and structures may be used. A functional OLED may be achieved by combining the various layers described in various ways, or layers may be omitted entirely, based on design, performance, and cost factors. Other layers not specifically described may also be included. Materials other than those specifically described may be used. While many of the examples provided herein describe the various layers as including a single material, it is understood that combinations of materials, such as mixtures of hosts and dopants, or more generally mixtures, may be used. Layers may also have various sublayers. The names given to the various layers herein are not intended to be strictly limiting. For example, in device 200, hole transport layer 225 transports holes and injects holes into emissive layer 220, and may be described as a hole transport layer or a hole injection layer. In one embodiment, an OLED may be described as having an "organic layer" disposed between a cathode and an anode. The organic layer may comprise a single layer, or may further comprise multiple layers of different organic materials, for example, as described with respect to Figures 1 and 2.
[0039] Structures and materials not specifically described may be used, such as OLEDs (PLEDs) composed of polymeric materials such as those disclosed in U.S. Patent No. 5,247,190 to Friend et al., which is incorporated by reference in its entirety. As a further example, OLEDs having a single organic layer may be used. OLEDs may be stacked, for example, as described in U.S. Patent No. 5,707,745 to Forrest et al., which is incorporated by reference in its entirety. OLED structures may deviate from the simple layered structures illustrated in Figures 1 and 2. For example, the substrate may include angled reflective surfaces to improve outcoupling, such as mesa structures as described in U.S. Patent No. 6,091,195 to Forrest et al. and / or dimple structures as described in U.S. Patent No. 5,834,893 to Bulovic et al., which are incorporated by reference in their entirety.
[0040] Unless otherwise specified, any of the layers of the various embodiments may be deposited by any suitable method. For organic layers, preferred methods include deposition by thermal evaporation, such as those described in U.S. Pat. Nos. 6,013,982 and 6,087,196, which are incorporated by reference in their entirety, inkjet, organic vapor phase deposition (OVPD), such as those described in U.S. Pat. No. 6,337,102 to Forrest et al., which is incorporated by reference in its entirety, and organic vapor jet printing (OVJP), such as those described in U.S. Pat. No. 7,431,968, which is incorporated by reference in its entirety. Other suitable deposition methods include spin-coating and other solution-based processes. Solution-based processes are preferably carried out in a nitrogen or inert atmosphere. For other layers, preferred methods include thermal evaporation. Preferred patterning methods include deposition via mask, cold welding, such as those described in U.S. Patent Nos. 6,294,398 and 6,468,819, which are incorporated by reference in their entirety, and patterning associated with some of the deposition methods, such as inkjet and OVJD. Other methods may be used. The material to be deposited may be modified to be compatible with the particular deposition method. For example, substituents such as alkyl and aryl groups, branched or unbranched, and preferably containing at least 3 carbons, may be used in small molecules to enhance their ability to undergo solution processing. Substituents with 20 or more carbons may be used, with 3-20 carbons being a preferred range. Materials with asymmetric structures may have better solution processability than those with symmetric structures, as asymmetric materials may be less prone to recrystallization. Dendrimer substituents may be used to enhance the ability of small molecules to undergo solution processing.
[0041] Devices fabricated according to embodiments of the invention may further include a barrier layer. One purpose of the barrier layer is to protect the electrodes and organic layers from damaging exposure to harmful species in the environment, including moisture, vapors and / or gases, etc. The barrier layer may be deposited on, under or next to the substrate, the electrodes, or on any other portion of the device, including the edges. The barrier layer may include a single layer or multiple layers. The barrier layer may be formed by various known chemical vapor deposition techniques and may include compositions having a single phase and compositions having multiple phases. Any suitable material or combination of materials may be used for the barrier layer. The barrier layer may incorporate inorganic or organic compounds or both. Preferred barrier layers include mixtures of polymeric and non-polymeric materials, as described in U.S. Pat. No. 7,968,146, PCT Patent Application Nos. PCT / US2007 / 023098 and PCT / US2009 / 042829, which are incorporated herein by reference in their entireties. To be considered a "mixture," the polymeric and non-polymeric materials that make up the barrier layer should be deposited under the same reaction conditions and / or simultaneously. The weight ratio of polymeric to non-polymeric materials can be in the range of 95:5 to 5:95. The polymeric and non-polymeric materials can be made from the same precursor materials. In one example, the mixture of polymeric and non-polymeric materials consists essentially of polymeric silicon and inorganic silicon.
[0042] Devices made according to embodiments of the invention can be incorporated into a wide variety of electronic component modules (or units) that can be incorporated into various electrical products or intermediate components. Such electrical products or intermediate components include display screens, lighting devices (such as discrete light source devices or lighting panels) that can be utilized by end-user product manufacturers. Such electronic component modules can optionally include driving electronics and / or power sources. Devices made according to embodiments of the invention can be incorporated into a wide variety of consumer products having one or more electronic component modules (or units) incorporated therein. Such consumer products include any type of product that includes one or more light sources and / or one or more display devices of some kind. Some examples of such consumer products include flat panel displays, computer monitors, medical monitors, televisions, billboards, lights for indoor or outdoor illumination and / or signaling, heads-up displays, fully or partially transparent displays, flexible displays, laser printers, telephones, mobile phones, tablets, phablets, personal digital assistants (PDAs), wearable devices, laptop computers, digital cameras, camcorders, viewfinders, microdisplays (displays less than 2 inches diagonal), 3-D displays, virtual reality or augmented reality displays, cars, video walls including multiple displays aligned together, theater or stadium screens, and signage. A variety of control mechanisms, including passive matrix and active matrix, can be used to control devices made according to the present invention. Many of the devices are intended for use within a temperature range that is comfortable for humans, such as 18 degrees Celsius to 30 degrees Celsius, and more preferably room temperature (20-25 degrees Celsius), but may also be used outside this temperature range, for example, from -40 degrees Celsius to +80 degrees Celsius.
[0043] The materials and structures described herein may have applications in devices other than OLEDs. For example, other optoelectronic devices such as organic solar cells and organic photodetectors may use the materials and structures. More generally, organic devices such as organic transistors may use the materials and structures.
[0044] As used herein, the term "halo," "halogen," or "halide" includes fluorine, chlorine, bromine, and iodine.
[0045] As used herein, the term "alkyl" refers to both straight and branched chain alkyl groups. Preferred alkyl groups contain from 1 to 15 carbon atoms and include methyl, ethyl, propyl, 1-methylethyl, butyl, 1-methylpropyl, 2-methylpropyl, pentyl, 1-methylbutyl, 2-methylbutyl, 3-methylbutyl, 1,1-dimethylpropyl, 1,2-dimethylpropyl, and 2,2-dimethylpropyl. Additionally, the alkyl groups may be substituted.
[0046] As used herein, the term "cycloalkyl" refers to a cyclic alkyl group. Preferred cycloalkyl groups contain 3 to 10 ring carbon atoms and include cyclopropyl, cyclopentyl, cyclohexyl, adamantyl, and the like. Additionally, the cycloalkyl groups may be substituted.
[0047] In the present specification, the term "alkenyl" refers to both straight-chain and branched-chain alkenyl groups. Preferred alkenyl groups are those containing 2 to 15 carbon atoms. Furthermore, the alkenyl groups may be substituted.
[0048] As used herein, the term "alkynyl" refers to both straight and branched chain alkyne groups. Preferred alkynyl groups are those containing 2 to 15 carbon atoms. Furthermore, said alkynyl groups may be substituted.
[0049] As used herein, the terms "aralkyl" and "arylalkyl" are used interchangeably and refer to an alkyl group having an aromatic group as a substituent. Additionally, said aralkyl group may be optionally substituted.
[0050] In this specification, the term "heterocyclic group" refers to aromatic and non-aromatic ring groups. Heteroaromatic ring groups also refer to heteroaryl. Preferred hetero non-aromatic ring groups are at least one heteroatom containing 3 to 7 ring atoms, including cyclic amines such as morpholino, piperidino, pyrrolidino, and cyclic ethers such as tetrahydrofuran, tetrahydropyran, and the like. Furthermore, the heterocyclic group may be substituted.
[0051] In this specification, the term "aryl" or "aromatic group" refers to monocyclic and polycyclic ring systems. A polycyclic ring can have two or more rings in which two carbons are shared by two adjacent rings (the rings are "fused"), at least one of the rings being aromatic, for example, the other rings being cycloalkyl, cycloalkenyl, aryl, heterocyclic, and / or heteroaryl. Preferred aryl groups contain 6 to 30 carbon atoms, preferably 6 to 20 carbon atoms, and more preferably 6 to 12 carbon atoms. An aryl group having 6 carbons, an aryl group having 10 carbons, or an aryl group having 12 carbons is particularly preferred. Suitable aryl groups include phenyl, biphenyl, triphenyl, triphenylene, tetraphenylene, naphthalene, anthracene, phenalene, phenanthrene, fluorene, pyrene, chrysene, perylene, and azulene, with phenyl, biphenyl, triphenyl, triphenylene, fluorene, and naphthalene being preferred. Additionally, the aryl group may be substituted.
[0052] As used herein, the term "heteroaryl" refers to a monocyclic heteroaromatic group that may contain 1-5 heteroatoms. The term heteroaryl also includes polycyclic heteroaromatic systems having two or more rings in which two atoms are shared by two adjacent rings (the rings being "fused"), at least one of the rings being heteroaryl, and the other rings may be, for example, cycloalkyl, cycloalkenyl, aryl, heterocyclic, and / or heteroaryl. Preferred heteroaryl groups are those containing 3-30 carbon atoms, preferably those containing 3-20 carbon atoms, and more preferably those containing 3-12 carbon atoms. Suitable heteroaryl groups include dibenzothiophene, dibenzofuran, dibenzoselenophene, furan, thiophene, benzofuran, benzothiophene, benzoselenophene, carbazole, indolocarbazole, pyridylindole, pyrrolodipyridine, pyrazole, imidazole, triazole, oxazole, thiazole, oxadiazole, oxatriazole, dioxazole, thiadiazole, pyridine, pyridazine, pyrimidine, pyrazine, triazine, oxazine, oxathiazine, oxadiazine, indole, benzimidazole, indazole, indoxazine, benzoxazole, benziso ... Examples of heteroaryl groups include benzothiazole, quinoline, isoquinoline, cinnoline, quinazoline, quinoxaline, naphthyridine, phthalazine, pteridine, xanthene, acridine, phenazine, phenothiazine, phenoxazine, benzofuropyridine, furodipyridine, benzothienopyridine, thienodipyridine, benzoselenophenopyridine, and selenophenodipyridine, with dibenzothiophene, dibenzofuran, dibenzoselenophene, carbazole, indolocarbazole, imidazole, pyridine, triazine, benzimidazole, 1,2-azaborine, 1,3-azaborine, 1,4-azaborine, borazine, and aza analogs thereof being preferred. Furthermore, the heteroaryl group may be optionally substituted.
[0053] The alkyl, cycloalkyl, alkenyl, alkynyl, aralkyl, heterocycle, aryl, and heteroaryl may be unsubstituted or substituted with one or more substituents selected from deuterium, halogen, alkyl, cycloalkyl, heteroalkyl, arylalkyl, alkoxy, aryloxy, amino, cyclic amino, silyl, alkenyl, cycloalkenyl, heteroalkenyl, alkynyl, aryl, heteroaryl, acyl, carbonyl, carboxylic acid, ether, ester, nitrile, isonitrile, sulfanyl, sulfinyl, sulfonyl, phosphino, and combinations thereof.
[0054] As used herein, "substituted" indicates that a substituent other than H is attached to the relevant position, such as a carbon. Thus, for example, R 1 is monosubstituted, R 1 must be something other than H. Similarly, R 1 When is disubstituted, R 1 Two of the must be non-H. Similarly, R 1 If is unsubstituted, R 1 is hydrogen at all substitution positions.
[0055] The designation "aza" in the fragments described herein, such as aza-dibenzofuran, aza-dibenzothiophene, etc., means that one or more of the CH groups in each fragment can be replaced by a nitrogen atom, for example, but not by way of limitation, azatriphenylene includes both dibenzo[f,h]quinoxaline and dibenzo[f,h]quinoline. One of ordinary skill in the art can easily imagine other nitrogen analogs of the above-mentioned aza derivatives, and all such analogs are intended to be encompassed by the terms described herein.
[0056] It is understood that when a molecular fragment is described as a substituent or as being attached to another moiety, the name may be described as either the fragment (e.g., phenyl, phenylene, naphthyl, dibenzofuryl) or the entire molecule (benzene, naphthalene, dibenzofuran). Different designations of the substituents or attached fragments are considered equivalent herein.
[0057] In this disclosure, we describe a method to achieve emitter transition dipole alignment to improve OLED device performance. Increasing the horizontal alignment of the transition dipole moment vector, which is the linchpin of photon emission in individual emitters, increases outcoupling and therefore efficiency. Increasing the aspect ratio of the emitter molecules allows anisotropic coordination of emitters in the OLED EML through increased linearity or planarity. The correlation of the transition dipole moment with this linear long axis or plane allows the emitter orientation to be transformed into a transition dipole orientation, allowing improved light outcoupling. These changes can improve light outcoupling and device efficiency by up to 50% relative to randomly oriented emitters.
[0058] Alignment of the emission transition dipole moment: The methods described herein improve OLED performance by maximizing light outcoupling through molecular alignment. Despite the very high exciton conversion efficiency and luminescence quantum yield achieved by phosphorescent OLED materials, device efficiency is ultimately limited by light extraction efficiency. Extraction of photons emitted from the light-emitting layer (EML) of an OLED stack is highly dependent on the photon emission direction. Photons propagating perpendicular to the device substrate have a high probability of extraction. On the other hand, photons propagating at high angles to the substrate perpendicular direction are more likely to be lost or not extracted due to internal reflection, coupling to waveguide modes, and surface plasmon modes.
[0059] In each individual emitter compound, light emission occurs perpendicular to the triplet to ground state transition dipole moment (TDM). Thus, an increase in the number of molecules of the emitter compound whose TDM vector is aligned horizontally to the OLED substrate leads to higher light extraction efficiency and thus higher device efficiency (external quantum efficiency - EQE). This horizontal alignment factor can be statistically described for an ensemble of emitter molecules by the ratio θ of the horizontal component of the TDM vector to the sum of the vertical component (TDM⊥) and the horizontal component (TDM||). In other words, θ=TDM|| / (TDM⊥+TDM||). Said ratio θ is hereafter referred to as the horizontal dipole ratio (HDR).
[0060] The horizontal dipole ratio θ can be measured by angle-dependent photoluminescence measurements. By comparing the measured emission pattern of a photoexcited thin-film sample with a computationally modeled pattern as a function of polarization, the TDM vector orientation can be determined for a given sample. The horizontal dipole ratio θ has a very significant effect on the resulting device efficiency. In a typical bottom-emission device structure (shown in Figure 10) without microcavities or other optical enhancements and with a material refractive index of about 1.5-2.0, randomly oriented emitters (θ = 0.67) give quantitative emission and charge recombination efficiencies (at very low current densities <1 mA / cm). 2 Assuming a θ=1 angle (achievable at θ=1), a maximum device EQE of about 28% can be achieved. For a perfectly horizontal emitter, where θ=1, an EQE of over 40% is achievable in an OLED device with 100% PLQY and 100% charge recombination efficiency.
[0061] In general, the increase in luminous outcoupling depends on two factors: (1) triplet-ground state TDM vector alignment in the emitter compound molecules; and (2) molecular alignment of emitters within the EML structure. Thus, it is necessary to control both factors in unison to effectively achieve alignment of the TDM vectors and enhance OLED performance. Furthermore, neither factor is separate, but rather a distribution of alignment. Near-degenerate luminous optical transitions can result in a distribution of differently oriented TDM vectors, described by Boltzmann statistics. Structurally, the molecular alignment of emitters in the amorphous EML medium can result in a distribution of emitter alignments, varying throughout the EML layers. Thus, through preferential emission from a single optical transition within the device EML and strong alignment of this transition, enhanced device performance can be realized.
[0062] Single TDM vector molecular alignment: To achieve a linear (aligned) TDM vector in the device, preferential (selective) emitter alignment must be instilled in the host and emitter materials. Primarily, this can be achieved through high aspect ratio emitter molecules. In nominally amorphous films prepared by methods such as thermal evaporation, spin coating, inkjet printing, and organic vapor jet printing, it is found that high aspect ratio rod-like or disk-like structures can be preferentially oriented.
[0063] In emitters with a single preferential emission transition, a rod-like structure can be selected to optimize alignment with the TDM vector while still minimizing molecular weight. This can be achieved in emitters similar in structure to tris(2-phenylpyridine)iridium (Ir(ppy)3, FIG. 3) by the creation of a long molecular axis that runs through the iridium metal center. The directionality of the long molecular axis can depend on the orientation of the TDM vector, as described below.
[0064] With reference to FIG. 4, for emitters in which the TDM vector is roughly aligned with the iridium-nitrogen bond (indicated by the dashed arrow), the pyridine 4-position (R 1 A molecular long axis can be generated by appropriate substitution with iridium-nitrogen bond R. For example, an aryl, heteroaryl, alkyl, or cycloalkyl substituent can be introduced at this position to promote the formation of a high aspect ratio rod-like structure in which the molecular long axis passes roughly through the iridium-nitrogen bond and the substituent. We aim to align the TDM vector axis with this high aspect ratio molecular long axis, with the angle between these two axes preferably being less than 30°, more preferably less than 10°. The substituent R 1 The preferred lengths of range from 3 Å to 15 Å, more preferably from 4 Å to 9 Å. By judicious selection of the substituents and applying the above molecular design, we are able to achieve HDRs up to 0.85 and thereby a large increase in EQE.
[0065] Similarly, rod-like structures can be used for emitters that contain a single preferential TDM vector that roughly bisects the bidentate emitting ligand (see FIG. 5, shown by the dashed line). In this case, elongation with aryl, heteroaryl, alkyl, or cycloalkyl substitution at pyridine 3- and 4-positions, in combination with substitution at phenyl 5- and 6-positions, can be used to generate a molecular long axis that roughly bisects the bidentate emitting ligand. For example, alkyl substitution at pyridine 4-position and fused heteroaryl substitution at phenyl 5- and 6-positions results in a net elongation in the TDM vector direction. Similarly, twisted aryl substitution at phenyl 6-position results in a more rod-like elongation in this TDM vector axis. We aim to align the TDM vector axis with this high aspect ratio molecular long axis, with the angle between these two axes preferably less than 30°, more preferably less than 10°. Substituent R 1 / R 2 and R 3 / R 4The preferred length of ranges from 3 Å to 15 Å, more preferably from 4 Å to 9 Å. Since this substitution pattern can induce a larger planar shape and align with the EML surface, we expect a further improved HDR of up to 0.9.
[0066] Ligand energy gap: In homoleptic iridium emitters, the three bidentate ligands are all the same, and the degeneracy of the three optical transitions results in random transition dipole orientations. In homoleptic emitters, the emission may be distributed among degenerate or near-degenerate transitions. These transitions may be clustered on different ligands, which may in large part have orthogonal TDM vectors. This results in an overall scrambling of any emission alignment that may result from molecular alignment.
[0067] We note that the very small energy gap between almost identical phenylpyridine-based ligands leads to large isotropic emission in Ir(ppy)3-type emitters, even in strongly oriented rod-like structures. In these cases, Boltzmann statistics mainly describe the possibility of emission from near-degenerate transitions. Thus, it turns out that the localization of the emissive transitions is very sensitive to the energy gap between the various transitions under consideration. In order to strongly localize the emission and improve the TDM alignment, the preferred energy gap between the emitting ligands of the emissive center with respect to the auxiliary ligands is higher than 0.05 eV, more preferably 0.10 eV.
[0068] Furthermore, any preferential alignment induced by the long axis located along one of the ligands that does not primarily contribute to the emissive transition may result in a low horizontal dipole ratio θ. This case of applying one of the alignment motifs mentioned above to one of the emitter ancillary ligands should be avoided, as it may result in HDR values lower than 0.67 (isotropic orientation).
[0069] Symmetry and geometry of TDM vectors: In some cases where a large energy gap cannot be achieved by energy tuning of the emitting and ancillary ligand structures, as is the case for many high energy blue and green emitters, symmetry and molecular geometry are used to generate highly aligned emission from multiple ligands. Note the largely orthogonal nature of the degenerate TDM vectors of Ir(ppy)3 and the perfectly parallel nature of those of the diketone-coordinated red emitters with symmetric emitting ligands. In the case of degenerate emission, these perpendicular and parallel relationships result in the negation and enhancement of any aligned emission by molecular alignment in the EML, respectively.
[0070] In these diketone-coordinated iridium emitters, the preferential trans orientation of the iridium-nitrogen bond results in a C2 axis symmetry in the structure, see FIG. 6. We propose to use this C2 axis to enhance the alignment induced by the elongation of the TDM vector axis, see FIG. 7. The non-ketone ligands are designed with (1) the TDM vector and (2) the steric long axis aligned with the Ir-N bond, and the C2 symmetry enhances the alignment with the parallel TDM vectors on the two emitting ligands. This allows very high HDR values of over 0.85.
[0071] For tris-substituted compounds, it is preferred to align (1) the TDM vector and (2) the long axis with a plane that contains the 3-fold symmetry compound such that emission can be focused equally or nearly equally at each of the three ligands. In these homoleptic fac compounds, this C3 plane roughly bisects the angle between the two metal-ligand bonds of each bidentate ligand. See FIG. 8. Thus, the TDM vectors of these complexes roughly bisect this angle, and the angle between the C3 plane and the TDM vector is less than 20°, more preferably less than 10°.
[0072] The resulting planar or near-planar arrangement of the three TDM vectors contributes to gains in efficiency, if the change in aspect ratio induces preferential horizontal alignment in this plane. Lengthening each ligand along this C3 plane results in a very flat structure with a high aspect ratio. One such structure is shown in FIG. 9, where R is alkyl, cycloalkyl, aryl, or heteroaryl. The same R can also be placed in a similar position on the pyridine ring. The molecular aspect ratio is defined by the radius between the metal center and the end of the R group, and is preferably longer than 4 Å, more preferably longer than 8 Å. Furthermore, it is preferred to have the vector between the metal center and the end of the R group in the C3 plane with an angle between the vector and the plane less than 20°, more preferably less than 10°.
[0073] Emitters can be developed that contain two identical emitter ligands, or more generally, two ligands that contribute primarily to emission, where the long axis and the TDM vector are not orthogonal. For each ligand, the long axis and the TDM vector can be collinear, as described above. When this long axis of one ligand is at a large angle (φ) to that of the second emitting ligand, an enhancement in device efficiency can be observed. In this case, the emissive molecular alignment can be described by a distribution of orientations in the amorphous EML, so that a bent shape of 90°<φ<180° leads to an enhancement in device efficiency, with both TDM vectors roughly aligned with the long axis formed between the two ligands. This is achieved by the TDM vector preferably bisecting the bidentate ligand and being slightly outside the plane of the ligand. We propose to use near-degenerate or degenerate emitting ligands with quasi-symmetric orientation of the TDM, resulting in HDR values above 0.7, more preferably 0.8.
[0074] Host-induced dopant alignment: Because the alignment of emitters in the EML arises from various interactions of the emitters with the EML materials and deposition media (vacuum, air, inert gas, solvents, etc.), interactions between the host and emitter materials are expected to have an effect on the resulting orientation of the emitter TDM vectors. Electrostatic interactions act to flatten high aspect ratio emitter molecules into the EML structure, and other strong host-emitter interactions can be used to affect alignment. These interactions can include donor-acceptor pi interactions, which are acted upon by pi-stacking, hydrogen bonding, the use of functional groups with strong interactions (including polar, non-polar, fluorinated, or alkyl groups that can interact between the host / dopant or drive intercalation or segregation effects), and interactions between electron-rich and electron-deficient aromatic moieties.
[0075] Optimization of emitter-host interactions to induce dopant alignment strongly depends on the planarity of the dopant and / or host molecules. In particular, when strong pi-stacking interactions induce alignment, increased planarity of these molecules is expected to result in stronger interactions and thus a higher degree of alignment. In this case, it is preferable to judiciously introduce a bifacial twist of the pi plane to increase the number of aromatic rings bi-aligned in the molecule and increase the overall planarity of the dopant. Through the same strategy, it is desirable to increase not only the planarity of the host molecule, but also the conjugation length, the charge transfer properties in the host, and the inter- and intramolecular hydrogen bonds. These differences in host-induced emitter alignment can be directly measured by photoluminescence techniques in emitter:host samples for emitter:mCP (mCP is 1,3-bis(N-carbazolyl)benzene, a disordered non-oriented host).
[0076] To the extent that the underlying layers of the device stack influence the alignment of host or dopant materials near the interface, it may also be preferable to incorporate these alignment or template motifs into electron blocking layers (EBLs) or other underlying layers.
[0077] According to an embodiment of the present disclosure, a compound having a metal coordination complex structure is disclosed, which can function as an emitter in an OLED at room temperature. For the purposes of this description, room temperature means a temperature range of 20° C. to 25° C. The compound has at least two ligands coordinated to the metal; the compound has a first substituent R at one site around the ligand. 1 a first distance between the metal and R 1 is defined as the distance between one of the atoms in the R 1 the first distance being greater than any other atom-metal distance between the metal and any other atom in the compound; a sphere having a radius r having its center at the metal, the radius r being greater than the radius of the R 1 If the sphere defined above is defined as the smallest radius that allows for enclosing all atoms that are not part of R, then the first distance is at least 2.9 Å longer than the radius r, where 2.9 Å represents the diameter of a phenyl ring. 1 In this specification, "surrounded by the sphere" means that the atoms are located at a distance from the metal equal to or less than the radius r.
[0078] In some embodiments of the compound, the first distance is at least 4.3 Å longer than the radius r. In some embodiments of the compound, the first distance is at least 7.3 Å longer than the radius r.
[0079] In some embodiments of the compound, the compound has a second substituent R 2 and the second distance is between the metal and R 2is defined as the distance between one of the atoms in the R 2 the radius r is the radius of the sphere that is the radius of the R 1 or R 2 When the second distance is the smallest radius that allows for enclosing all atoms that are not part of r, the second distance is at least 1.5 Å longer than r.
[0080] The second substituent R 2 In some embodiments of the compound having R 1 and R 2 are on different ligands. In some embodiments of the compound, the second distance is at least 2.9 Å longer than r. In some embodiments, the second distance is at least 4.3 Å longer than r. In some embodiments, the second distance is at least 7.3 Å longer than r. In some embodiments, the first distance and the second distance are both at least 4.3 Å longer than r. In some embodiments, the first distance and the second distance are both at least 7.3 Å longer than r.
[0081] The second substituent R 2 In some embodiments of the compound having R 1 is bonded to an aromatic ring having a first coordination atom, and R 2 is attached to an aromatic ring having a second coordination atom, said first coordination atom being in a trans configuration with respect to said metal and with respect to said second coordination atom.
[0082] In some embodiments of the compound, the compound includes a third substituent R 3 and the third distance is between the metal and R 3 is defined as the distance between one of the atoms in the R 3 the radius r is the radius of the sphere that is the radius of the R 1 , R 2 , or R 3When the third distance is the smallest radius that allows for enclosing all atoms that are not part of r, the third distance is at least 1.5 Å longer than r.
[0083] The third substituent R 3 In some embodiments of the compound having the substituent R 1 , R 2 , and R 3 are on different ligands. In some embodiments of the compounds, the third distance is at least 2.9 Å longer than r. In some embodiments, the third distance is at least 4.3 Å longer than r. In some embodiments, the third distance is at least 7.3 Å longer than r.
[0084] Table 1 below shows the maximum linear length for various substituents defined along the long axis. This maximum linear length is defined as the distance between the two atoms furthest apart along the long axis of a particular substituent. The values shown are used to estimate how far in a coordination complex a given substituent at one point around the ligand extends beyond the radius r of the sphere that encloses all atoms in the coordination complex that are not part of the particular substituent. For example, the first substituent R 1 In embodiments of the coordination complex having only one substituent R 1 The amount of the second substituent R 2 and a third substituent R 3 When the group has additional substituents such as the above, the substituent R 2 or R 3By considering the specific substituents included in the , the distance between the second distance or the third distance and the radius r can be estimated. The difference between two substituents can be calculated using Table 1 below. For example, if the first substituent is phenyl and the second substituent is tolyl, the second substituent is one C-C bond (i.e., 1.5 Å) longer than the first substituent. In another example, if the second substituent is biphenyl, the second substituent is C-C6H5 (i.e., 4.3 Å) longer than the first substituent. Any two or more of the following fragments can be linked together and the distance can be calculated by simply adding these values to the total length of the single C-C bond distances used to connect them. [Table 1]
[0085] The third substituent R 3 In some embodiments of the compound having the formula: the first distance, the second distance, and the third distance are all at least 4.3 Å longer than r. In some embodiments, the first distance, the second distance, and the third distance are all at least 7.3 Å longer than r. In some embodiments, the first distance, the second distance, and the third distance are each independently at least one distance greater than r as shown in Table 1. In some further embodiments, the first distance, the second distance, and the third distance are all at least one distance greater than r as shown in Table 1.
[0086] The third substituent R 3 In some embodiments of a compound having the formula: 1 , R 2 , and R 3Each atom in has a point-to-plane distance to said first plane of less than 5 Å. A "point-to-plane" distance refers to the shortest distance between a plane and a point that is not in said plane.
[0087] R 3 In some embodiments of the compound having R 1 , R 2 , and R 3 Any atom in has a point-to-plane distance of less than 4 Å relative to the first plane. 1 , R 2 , and R 3 Any atom in has a point-plane distance to said first plane that is less than r.
[0088] In some embodiments of the compound, the compound has a transition dipole moment axis; and the transition dipole moment axis and R 1 is less than 40°. A "transition dipole moment axis" is an axis along the transition dipole moment. In some embodiments, the angle between the transition dipole moment axis and the axis along the first distance is less than 30°. In some embodiments, the angle between the transition dipole moment axis and the axis along the first distance is less than 20°. In some embodiments, the angle between the transition dipole moment axis and the axis along the first distance is less than 15°. In some embodiments, the angle between the transition dipole moment axis and the axis along the first distance is less than 10°. In some embodiments, the angle between the transition dipole moment axis and the axis along the first distance is less than 35°. In some embodiments, the angle between the transition dipole moment axis and the axis along the first distance is less than 25°. In some embodiments, the angle between the transition dipole moment axis and the axis along the first distance is less than 5°.
[0089] R 1 The first distance in R 2 The second distance in and R 3significantly longer than the third distance in 2 or R 3 In some embodiments of the compounds that are free of R, the free energy difference between the emissions collected on three different ligands is taken into account. 1 To compare the free energy of the ligand with R 1 A first homoleptic metal complex consisting of the same ligand having the ligand having the formula: will have a triplet energy that is at least 0.02 eV lower than the triplet energy of a second homoleptic metal complex consisting of a ligand that is any of the other ligands in the compound. In other embodiments, the triplet energy of the first homoleptic metal complex is at least 0.05 eV lower than the triplet energy of the second homoleptic metal complex. In other embodiments, the triplet energy of the first homoleptic metal complex is at least 0.1 eV lower than the triplet energy of the second homoleptic metal complex. In other embodiments, the triplet energy of the first homoleptic metal complex is at least 0.15 eV lower than the triplet energy of the second homoleptic metal complex.
[0090] In some embodiments of the compounds, the substituent R 1 , R 2 , and R 3 are each independently selected from the group consisting of: [ka] [ka] [ka] [ka]
[0091] In some embodiments of the compounds, the compounds can function as phosphorescent, fluorescent, or delayed fluorescent emitters in organic light emitting devices at room temperature.
[0092] In some embodiments of the compounds, the compounds are capable of emitting light from a triplet excited state to the ground singlet state at room temperature.
[0093] In some embodiments of the compound, the compound has a metal-carbon bond.
[0094] In some embodiments of the compound, the metal is selected from the group consisting of Ir, Rh, Re, Ru, Os, Pt, Pd, Au, Ag, and Cu. In some embodiments, the metal is Ir. In some embodiments, the metal is Pt.
[0095] In some embodiments of the compound, the compound has a neutral charge.
[0096] In some embodiments of the compound, each ligand in the compound is different from the others.
[0097] In some embodiments of the compound, the compound has an octahedral coordination geometry consisting of three bidentate ligands, two tridentate ligands, one tetradentate ligand and one bidentate ligand, or one hexadentate ligand.
[0098] In some embodiments of the compounds, the compounds have a tetrahedral coordination geometry consisting of two bidentate ligands or one tetradentate ligand.
[0099] In some embodiments of the compound, the compound comprises a first benzene ring coordinated to the metal, the first benzene ring fused with a second aromatic ring, in some embodiments the second aromatic ring is fused with a third aromatic ring, in some embodiments the third aromatic ring is fused with a fourth aromatic ring.
[0100] In some embodiments of the compound, the compound is M(L 1 ) x (L 2 ) y (L 3 ) z It is expressed by the formula: L 1 , L 2 , and L 3 may be the same or different; x is 1, 2, or 3; y is 0, 1, or 2; z is 0, 1, or 2; x+y+z is the oxidation state of the metal M; L 1 , L 2 , and L 3 are each independently selected from the group consisting of: [ka] [ka] [ka] [ka] In the formula, X 1 ~X 17 are each independently selected from the group consisting of carbon and nitrogen; Z 1 , Z 2 , and Z 3 are each independently carbon or nitrogen; X is selected from the group consisting of BR', NR', PR', O, S, Se, C=O, S=O, SO2, CR'R'', SiR'R'', and GeR'R''; R' and R'' may be fused or joined to form a ring; R a , R b , R c , and R d represents the maximum number of substitutions possible, from monosubstitution to no substitution; R', R'', R a , R b , R c , R d , R e are each independently selected from the group consisting of hydrogen, deuterium, halide, alkyl, cycloalkyl, heteroalkyl, arylalkyl, alkoxy, aryloxy, amino, silyl, alkenyl, cycloalkenyl, heteroalkenyl, alkynyl, aryl, heteroaryl, acyl, carbonyl, carboxylic acid, ester, nitrile, isonitrile, sulfanyl, sulfinyl, sulfonyl, phosphino, and combinations thereof; Any two R a , R b , R c , and R d may be fused or linked to form a ring or to form a multidentate ligand; R a , R b , R c , and R d At least one of the following is R 1 Includes.
[0101] Said M(L 1 ) x (L 2 ) y (L 3 ) z In some embodiments of the compound represented by the formula a , R b , R c , and R d At least one pair of is bonded and fused to form a ring.
[0102] Said M(L 1 ) x (L 2 ) y (L 3 ) z In some embodiments of the compound represented by the formula a , R b , R c , and R d At least one pair of is bonded and fused to form a ring.
[0103] Said M(L 1 ) x (L 2 ) y (L 3 ) z In some embodiments of the compound represented by the formula 1 )2(L 2 ) is expressed by the formula:
[0104] The Ir(L 1 )2(L 2 In some embodiments of the compound represented by the formula: 1 is below: [ka] represented by a formula selected from the group consisting of: L 2 is below: [ka] It is expressed as: In some embodiments, L 2 is below: [ka] Represented by; In the formula, R e , R f , R h , and R i is independently selected from the group consisting of alkyl, cycloalkyl, aryl, and heteroaryl; Re , R f , R h , and R i at least one of has at least two carbon atoms; R g is selected from the group consisting of hydrogen, deuterium, halogen, alkyl, cycloalkyl, heteroalkyl, arylalkyl, alkoxy, aryloxy, amino, silyl, alkenyl, cycloalkenyl, heteroalkenyl, alkynyl, aryl, heteroaryl, acyl, carbonyl, carboxylic acid, ester, nitrile, isonitrile, sulfanyl, sulfinyl, sulfonyl, phosphino, and combinations thereof.
[0105] Said M(L 1 ) x (L 2 ) y (L 3 ) z In some embodiments of the compound represented by the formula 1 )(L 2 )(L 3 ), Ir(L 1 )2(L 2 ), and Ir(L 1 )3; L 1 , L 2 , and L 3 are different and each independently selected from the group consisting of: [ka] [ka]
[0106] Said M(L 1 ) x (L 2 ) y (L 3 ) z In some embodiments of the compound represented by the formula, the compound is Pt(L 1 )2 or Pt(L 1)(L 2 In some embodiments, L 1 is another L 1 Or L 2 and forms a tetradentate ligand.
[0107] Said M(L 1 ) x (L 2 ) y (L 3 ) z In some embodiments of the compound represented by the formula 1 )2 or M(L 1 )(L 2 ) wherein M is Ir, Rh, Re, Ru, or Os; L 1 and L 2 are different tridentate ligands.
[0108] In some embodiments of the compound, the compound is selected from the group consisting of: [ka] [ka] [ka] [ka] [ka] [ka] [ka] [ka] [ka] [ka] [ka] [ka] [ka] [ka] [ka] [ka] [ka] [ka] [ka] [ka] [ka] [ka]
[0109] According to another aspect of the present disclosure, an OLED is disclosed, the OLED comprising: an anode; a cathode; and an organic layer disposed between the anode and the cathode, the organic layer comprising a compound having a metal coordination complex structure; The compound is capable of functioning as an emitter in an organic light emitting device at room temperature; The compound comprises at least two ligands coordinated to the metal; The compound has a first substituent R 1 having; The first distance is between the metal and the R 1 is the distance between the atoms in said first distance being greater than any distance between said metal and any other atom in said compound; A sphere having a radius r is centered on the metal, and the radius r is the R 1 When r is defined as the smallest radius that allows for enclosing all atoms that are not part of the molecule, the first distance is at least 2.9 Å longer than the radius r.
[0110] In some embodiments of the OLED, the organic layer is an emissive layer, and the compound having a metal coordination complex structure is an emissive dopant or a non-emissive dopant.
[0111] In some embodiments of the OLED in which the organic layer further comprises a host, the host comprises a triphenylene containing benzo-fused thiophene or a benzo-fused furan; The optional substituents in the host are independently selected from the group consisting of C n H 2n+1 , O.C. n H 2n+1 , OAr1, N(C n H 2n+1 )2, N(Ar1)(Ar2), CH=CH-C n H 2n+1 , C≡CC n H 2n+1 , Ar1, Ar1-Ar2, and C n H 2n -Ar1 is a non-fused substituent selected from the group consisting of, or the host is unsubstituted; n is from 1 to 10; Ar1 and Ar2 are independently selected from the group consisting of benzene, biphenyl, naphthalene, triphenylene, carbazole, and heteroaromatic analogs thereof.
[0112] In some embodiments of the OLED in which the organic layer further comprises a host, the host comprises at least one chemical group selected from the group consisting of triphenylene, carbazole, dibenzothiophene, dibenzofuran, dibenzoselenophene, azatriphenylene, azacarbazole, aza-dibenzothiophene, aza-dibenzofuran, and aza-dibenzoselenophene.
[0113] In some embodiments of the OLED in which the organic layer further comprises a host, the host is selected from the group consisting of: [ka] [ka]
[0114] In some embodiments of the OLED in which the organic layer further comprises a host, the host comprises a metal complex.
[0115] In some embodiments of the OLED, the compound having a metal coordination complex structure has a HDR of at least 0.7. In some embodiments of the OLED, the compound having a metal coordination complex structure has a HDR of at least 0.75. In some embodiments of the OLED, the compound having a metal coordination complex structure has a HDR of at least 0.8. In some embodiments of the OLED, the compound having a metal coordination complex structure has a HDR of at least 0.85. In some embodiments of the OLED, the compound having a metal coordination complex structure has a HDR of at least 0.9. In some embodiments of the OLED, the compound having a metal coordination complex structure has a HDR of at least 0.95.
[0116] In some embodiments of the OLED, the organic layer further comprises a host; the compound has a higher HDR by at least 5% when compared to an identical device having mCP (1,3-bis(N-carbazolyl)benzene) as the host. In some embodiments of the OLED, the compound has a higher HDR by at least 10% when compared to an identical device having mCP as the host. In some embodiments of the OLED, the compound has a higher HDR by at least 20% when compared to an identical device having mCP as the host. In some embodiments of the OLED, the compound has a higher HDR by at least 30% when compared to an identical device having mCP as the host. In some embodiments of the OLED, the compound has a higher HDR by at least 40% when compared to an identical device having mCP as the host.
[0117] According to another aspect of the present disclosure, an OLED is disclosed, the OLED comprising: an anode; a cathode; and an organic layer disposed between the anode and the cathode, the organic layer comprising a phosphorescent light-emitting compound; the phosphorescent light-emitting compound has a characteristic emission spectrum with a FWHM value of 45 nm or less, and the OLED has a light emission efficiency of 0.1 mA / cm at room temperature when a voltage is applied across the device. 2and has an EQE of at least 25%. In some embodiments, the FWHM value of the intrinsic emission spectrum of the phosphorescent compound is 43 nm or less. In some embodiments, the FWHM value of the intrinsic emission spectrum of the phosphorescent compound is 41 nm or less. In some embodiments, the FWHM value of the intrinsic emission spectrum of the phosphorescent compound is 39 nm or less. In some embodiments, the FWHM value of the intrinsic emission spectrum of the phosphorescent compound is 37 nm or less. In some embodiments, the FWHM value of the intrinsic emission spectrum of the phosphorescent compound is 35 nm or less. In some embodiments, the FWHM value of the intrinsic emission spectrum of the phosphorescent compound is 33 nm or less. In some embodiments, the FWHM value of the intrinsic emission spectrum of the phosphorescent compound is 31 nm or less. In some embodiments, the FWHM value of the intrinsic emission spectrum of the phosphorescent compound is 29 nm or less. In some embodiments, the FWHM value of the intrinsic emission spectrum of the phosphorescent compound is 27 nm or less. In some embodiments, the OLED has an EQE of at least 27%. In some embodiments, the OLED has an EQE of at least 29%. In some embodiments, the OLED has an EQE of at least 31%. In some embodiments, the device lifetime to 95% brightness is less than 20 mA / cm. 2 400nm ≤ λ measured at max <8 hours for 500 nm emitters, 80 mA / cm 2 500nm ≤ λ measured at max < 80mA / cm for 30 hours with 590nm emitter 2 Measured at 590 nm ≤ λ max For <750 nm emitters, it is 150 hours. In some embodiments, the device lifetime to 95% brightness is 20 mA / cm 2 400nm ≤ λ measured at max < 80mA / cm for 12 hours for 500nm emitter 2 500nm ≤ λ measured at max< 80mA / cm for 45 hours with 590nm emitter 2 Measured at 590 nm ≤ λ max For <750 nm emitters, it is 225 hours. In some embodiments, the device lifetime to 95% brightness is 20 mA / cm 2 400nm ≤ λ measured at max < 16 hours for 500 nm emitters, 80 mA / cm 2 500nm ≤ λ measured at max < 80mA / cm for 60 hours with 590nm emitter 2 Measured at 590 nm ≤ λ max <300 hours for 750 nm emitters. In some embodiments, device lifetime to 95% brightness is 20 mA / cm 2 400nm ≤ λ measured at max < 80mA / cm for 20 hours for 500nm emitters 2 500nm ≤ λ measured at max < 75 hours for 590 nm emitter, 80 mA / cm 2 Measured at 590 nm ≤ λ max For <750 nm emitters, it is 375 hours.
[0118] The intrinsic emission spectrum of a phosphorescent compound is defined as the photoluminescence spectrum of a thermally evaporated thin film of the emitter doped with <1%-10% of the same host material used in the OLED stack. One skilled in the art will recognize that the doping rate should be restricted to a regime that minimizes aggregation quenching and broadening. It is worth noting that the emission spectrum can show slight broadening or narrowing in OLEDs due to optical and chemical factors.
[0119] Benzoannulation of the ligand-containing ring was found to significantly reduce the photoluminescence full width at half maximum (FWHM) of the emitter. Narrowing of the emitter's photoluminescence spectrum improves device performance, such as EQE. For example, when compound A (FWHM: 65 nm in solution) is condensed with an additional benzene ring, the aromatized compound B has a FWHM of 19 nm, significantly narrower than compound A. Similarly, in solid-state PMMA thin films, compound B has a FWHM of 21 nm, 47 nm narrower than compound A (FWHM: 68 nm) in a 5% doped PMMA solid film. [ka]
[0120] In some embodiments of the OLED, the phosphorescent compound is a metal coordination complex and the metal is selected from the group consisting of Ir, Rh, Re, Ru, Os, Pt, Pd, Au, Ag, and Cu. In some embodiments, the metal is Ir. In some embodiments, the metal is Pt.
[0121] In some embodiments of OLEDs in which the phosphorescent compound is a metal coordination complex, the phosphorescent compound is a benzene ring coordinated to the metal; the benzene ring is fused with a second aromatic ring. In some embodiments, the second aromatic ring is fused with a third aromatic ring. In some embodiments, the third aromatic ring is fused with a fourth aromatic ring.
[0122] The phosphorescent emitting compound in the OLED has a characteristic emission spectrum with a FWHM value of 45 nm or less, and a specific emission spectrum of 0.1 mA / cm at room temperature when a voltage is applied across the device. 2In some embodiments of the OLED having an EQE of at least 25% measured at 1000 nm, the phosphorescent compound has an HDR of at least 0.7. In some embodiments of the OLED, the phosphorescent compound has an HDR of at least 0.75. In some embodiments of the OLED, the phosphorescent compound has an HDR of at least 0.8. In some embodiments of the OLED, the phosphorescent compound has an HDR of at least 0.85. In some embodiments of the OLED, the phosphorescent compound has an HDR of at least 0.9. In some embodiments of the OLED, the phosphorescent compound has an HDR of at least 0.95.
[0123] In some embodiments of the OLED, in which the phosphorescent compound in the OLED has a characteristic emission spectrum with a FWHM value of 45 nm or less and an EQE of at least 25% at room temperature when a voltage is applied across the device, the emissive layer further comprises a host; the compound has a horizontal dipole ratio that is increased by at least 5% when compared to an identical device having mCP (1,3-bis(N-carbazolyl)benzene) as the host. In some embodiments, the compound has a horizontal dipole ratio that is increased by at least 10% when compared to an identical device having mCP (1,3-bis(N-carbazolyl)benzene) as the host.
[0124] In some embodiments of the OLED, the phosphorescent compound in the OLED has a unique emission spectrum with a FWHM value of 45 nm or less and an EQE of at least 25% at room temperature when a voltage is applied across the device, the phosphorescent compound is a compound having a metal coordination complex structure; the compound is capable of functioning as an emitter in an organic light emitting device at room temperature; the compound has at least two ligands coordinated to the metal; and the compound has a first substituent R 1 a first distance between the metal and a distance R furthest from the metal; 1said first distance being greater than any distance between said metal and any other atom in said compound; a sphere having a radius r at its center, said radius r being greater than any distance between said metal and any other atom in said compound; 1 When r is defined as the smallest radius that allows for enclosing all atoms that are not part of the molecule, the first distance is at least 2.9 Å longer than the radius r.
[0125] According to another aspect of the present disclosure, a consumer product is disclosed that includes an OLED, the OLED includes an anode, a cathode, and an organic layer disposed between the anode and the cathode, the organic layer including a compound having a metal coordination complex structure, the compound being capable of functioning as an emitter in an organic light emitting device at room temperature, the compound including at least two ligands coordinated to the metal, and the compound including a first substituent R at one site around the ligand. 1 a first distance between the metal and a furthest distance R 1 the first distance is greater than any distance between the metal and any other atom in the compound; a sphere having a radius r is centered at the metal and the radius r is greater than any distance between the metal and any other atom in the compound; 1 When r is defined as the smallest radius that allows for enclosing all atoms that are not part of the molecule, the first distance is at least 2.9 Å longer than the radius r.
[0126] According to another aspect of the present disclosure, a consumer product is disclosed that includes an OLED comprising: an anode; a cathode; and an organic layer disposed between the anode and the cathode that includes a phosphorescent light-emitting compound; the phosphorescent light-emitting compound has a characteristic emission spectrum with a FWHM value of 45 nm or less, and a light emission current of 0.1 mA / cm at room temperature when a voltage is applied across the device. 2 has an EQE of at least 25% as measured by
[0127] In some embodiments, the consumer product referred to above is selected from the group consisting of a flat panel display, a computer monitor, a medical monitor television, a billboard, a light for indoor or outdoor illumination and / or signaling, a heads-up display, a fully or partially transparent display, a flexible display, a laser printer, a telephone, a mobile phone, a tablet, a phablet, a personal digital assistant (PDA), a wearable device, a laptop computer, a digital camera, a camcorder, a viewfinder, a micro-display, a 3-D display, a virtual reality or augmented reality display, a car, a large area wall, a theater or stadium screen, or a sign.
[0128] Working Example
[0129] As shown previously, the average transition dipole moment (TDM) alignment of a given representative EML structure can be determined by angle-dependent photoluminescence measurements. The angular dependence of p-polarized emission is very sensitive to the HDR. Thus, the HDR of an emitter-doped EML sample 300 can be determined by comparing the measured p-polarized emission e as a function of detection angle φ as shown in FIG. 11 with the simulated angular dependence based on the optical properties of the sample and the contributions of the two in-plane and out-of-plane transition dipole modes.
[0130] Photoluminescence measurements of compound 152 confirm the increased horizontal alignment of TDMs with the substitution pattern described above. As shown in Figure 12, the substitution pattern of compound 152 produces preferentially horizontally ordered EMLs (HDR = 0.73), in contrast to the randomly oriented nature of tris(2-phenylpyridine)iridium (HDR = 0.67).
[0131] Synthesis of compound 152
[0132] Process 1 [ka] CC-2 (2.3 g, 2.71 mmol) was dissolved in dry dichloromethane (400 ml). The mixture was degassed with N2 and cooled to 0° C. 1-Bromopyrrolidine-2,5-dione (0.81 g, 2.71 mmol) was dissolved in DCM (300 mL) and added dropwise. After addition, the temperature was gradually raised to room temperature and the reaction was stirred for 12 h. Saturated NaHCO3 (20 mL) solution was added. The organic phase was separated and collected. The solvent was removed and the residue was applied to Celite and purified on a column of silica gel eluted with toluene / heptane 70 / 30 (v / v) to give the product CC-2-Br (0.6 g, 24%).
[0133] Process 2 [ka] CC-2-Br (0.72 g, 0.775 mmol) was dissolved in a mixture of toluene (40 ml) and water (4 ml). The mixture was purged with N2 for 10 min. K3PO4 (0.411 g, 1.937 mmol), SPhos (0.095 g, 0.232 mmol), Pd2dba3 (0.043 g, 0.046 mmol), and phenylboronic acid (0.189 g, 1.55 mmol) were added. The mixture was heated at 110 °C under N2 for 12 h. After that, the reaction was cooled to room temperature and the product was extracted with DCM. The organic phase was separated and collected. The solvent was removed and the residue was applied to Celite and purified on a column of silica gel eluted with toluene / heptane 70 / 30 (v / v). The product was further purified by recrystallization from toluene / MeOH to give compound 152 (0.7 g).
[0134] Synthesis of compound 153 [ka] CC-2-Br-2 (0.6 g, 0.646 mmol) was dissolved in a mixture of toluene (100 ml) and water (10 ml). The mixture was purged with N2 for 10 min. K3PO4 (0.343 g, 1.61 mmol), SPhos (0.080 g, 0.19 mmol), Pd2dba3 (0.035 g, 0.039 mmol), and [1,1-biphenyl]4-ylboronic acid (0.256 g, 1.29 mmol) were added. The mixture was heated at 110 °C under N2 for 12 h. After that, the reaction was cooled to room temperature, the product was extracted with DCM, and the organic phase was separated. The solvent was removed and the residue was applied to Celite and purified on a column of silica gel eluted with toluene / heptane 70 / 30 (v / v). The product was further purified by recrystallization from toluene / MeOH to give compound 153 (0.64 g).
[0135] Synthesis of compound 154
[0136] Process 1 [ka] CC-1 (2.04 g, 2.500 mmol) was dissolved in dry dichloromethane (400 ml). The mixture was degassed with N2 and cooled to 0°C. 1-Bromopyrrolidine-2,5-dione (0.445 g, 2.500 mmol) was dissolved in DCM (200 mL) and added dropwise. After addition, the temperature was gradually raised to room temperature and stirred for 16 h. Saturated NaHCO3 (20 mL) solution was added. The organic phase was separated and collected. The solvent was removed and the residue was applied to Celite and purified on a column of silica gel eluted with 70 / 30 toluene / heptane to give the product CC-Br (0.6 g).
[0137] Process 2 [ka] CC-Br (1.16 g, 1.296 mmol) was dissolved in a mixture of toluene (120 ml) and water (12.00 ml). The mixture was purged with N2 for 10 min. K3PO4 (0.688 g, 3.24 mmol), SPhos (0.160 g, 0.389 mmol), Pd2dba3 (0.071 g, 0.078 mmol), and phenylboronic acid (0.316 g, 2.59 mmol) were added. The mixture was heated at 110 °C under N2 for 16 h. After the reaction was cooled to room temperature, the product was extracted with DCM. The organic phase was separated and collected. The solvent was removed and the residue was applied to Celite and purified on a column of silica gel eluted with 70 / 30 toluene / heptane. The product was further purified by recrystallization from toluene / MeOH to give compound 154 (1.0 g).
[0138] Synthesis of compound 155
[0139] Process 1 [ka] Under nitrogen, 2-chloro-5-methylpyridine (10.03 g, 79 mmol), (3-chloro-4-methylphenyl)boronic acid (13.4 g, 79 mmol), and potassium carbonate (21.74 g, 157 mmol) were dissolved in a mixture of DME (150 ml) and water (20 ml) to give a colorless suspension. Pd(PPh3)4 (0.909 g, 0.786 mmol) was added to the reaction mixture, after which the reaction mixture was degassed and heated to 95° C. for 12 h. It was then cooled to room temperature, the organic layer was separated and evaporated. The residue was subjected to silica gel column chromatography eluted with heptane / THF 9 / 1 (v / v) and crystallized from heptane to give 10 g of a white solid (yield 58%).
[0140] Process 2 [ka] 2-(3-chloro-4-methylphenyl)-5-methylpyridine (10 g, 45.9 mmol), ((methyl-d3)sulfonyl)methane-d3 (92 g, 919 mmol), and sodium 2-methylpropan-2-olate (2.65 g, 27.6 mmol) were dissolved together under nitrogen to give a dark solution. The reaction mixture was heated to 80° C. under nitrogen for 12 h, cooled, diluted with ethyl acetate, washed with water, dried over sodium sulfate, filtered, and evaporated. Purification by silica gel column chromatography eluted with heptane / THF 9 / 1 (v / v) gave a white solid, which was then crystallized from heptane to give a colorless crystalline material (9.1 g, 81% yield).
[0141] Process 3 [ka] Under nitrogen, 2-(3-chloro-4-(methyl-d3)phenyl)-5-(methyl-d3)pyridine (7.45 g, 33.3 mmol), phenylboronic acid (6.09 g, 49.9 mmol), potassium phosphate (15.34 g, 66.6 mmol), Pd2(dba)3 (0.305 g, 0.333 mmol) and dicyclohexyl(2',6'-dimethoxy-[1,1'-biphenyl]-2-yl)phosphane (SPhos, 0.273 g, 0.666 mmol) were dissolved in a mixture of DME (150 ml) and water (25 ml) to give a red suspension. The reaction mixture was degassed under nitrogen and heated to reflux. After heating overnight, about 80% conversion was achieved. Further addition of Ph boronic acid and catalyst did not improve the conversion. Purification by silica gel column chromatography eluted with heptane / THF 9 / 1, followed by crystallization from heptane gave a white solid (6.2 g, 70% yield).
[0142] Process 4 [ka] Under nitrogen, 4,5-bis(methyl-d3)-2-phenylpyridine (1.427 g, 7.54 mmol), 5-(methyl-d3)-2-(6-(methyl-d3)-[1,1'-biphenyl]-3-yl)pyridine (2 g, 7.54 mmol), and [IrCl(COD)]2 (2.53 g, 3.77 mmol) were dissolved in ethoxyethanol (50 ml) under nitrogen to give a red solution. The reaction mixture was heated to reflux for 1 h, after which a precipitate formed. An additional 30 mL of ethoxyethanol was added and reflux continued for 48 h, after which the reaction mixture was cooled to room temperature. The crude material was used in the next step without further purification.
[0143] Process 5 [ka] The iridium dimer suspended in ethoxyethanol in 50 ml of methanol under nitrogen was mixed with pentane-2,4-dione (2.59 g, 25.9 mmol) and sodium carbonate (3.43 g, 32.3 mmol), stirred under nitrogen at 55° C. for 24 hours and evaporated. The yellow residue was subjected to silica gel column chromatography eluted with a gradient mixture heptane / toluene to give 5 g of the desired complex (yield 36%).
[0144] Process 6 [ka] The acac complex (5 g, 6.72 mmol) was dissolved in DCM (20 mL), then HCl in ether (16.80 ml, 33.6 mmol) was added in one portion, stirred for 10 min, and evaporated. The residue was triturated with methanol. The solid was filtered and washed with methanol and heptane to give a yellow solid (4.55 g, 100% yield).
[0145] Process 7 [ka] Ir dimer (4.55 g, 3.34 mmol) and (((trifluoromethyl)sulfonyl)oxy)silver (2.062 g, 8.03 mmol) were suspended in 50 ml of a 1 / 1 (v / v) mixture of DCM / methanol and stirred at room temperature for 72 h, filtered through Celite and evaporated to give a yellow solid (4.75 g, 83% yield).
[0146] Process 8 [ka] A mixture of triflate (3 g, 3.5 mmol) and 8-(4-(2,2-dimethylpropyl-1,1-d2)pyridin-2-yl)-2-(methyl-d3)benzofuro[2,3-b]pyridine (2.56 g, 7.7 mmol) in 30 mL of methanol was stirred at 65° C. under nitrogen for 5 days. The material was then cooled and the methanol was evaporated. The residue was subjected to silica gel column chromatography eluting with 2% ethyl acetate in toluene to give two isomers of the product (higher R f 1.7 g of complex with low R f (0.7 g of complex with low R f The complex having the formula: is the target compound 155.
[0147] Device Example
[0148] All of the devices in the examples were fabricated under high vacuum (<10 -7The devices were fabricated by thermal evaporation at 1000 Å (1000 Torr). The anode electrode was 750 Å indium tin oxide (ITO). The cathode consisted of 10 Å Liq (8-hydroxyquinoline lithium) and 1,000 Å Al. All devices were encapsulated with a glass lid sealed with epoxy resin in a nitrogen glove box (H2O and O2 <1 ppm) immediately after fabrication, and a moisture getter was packaged. The organic stack of the device example consisted of, from the ITO surface, 100 Å HAT-CN as a hole injection layer (HIL); 450 Å HTM as a hole transport layer (HTL); and a 400 Å thick light emitting layer (EML). The light emitting layer included H-host (H1):E-host (H2) in a ratio of 6:4 and 12 wt % green emitter. As ETL, 350 Å of Liq (8-hydroxyquinoline lithium) was doped with 40% ETM. The device structure is shown in Table 2 below. Table 2 shows the schematic device structure. The chemical structures of the device materials are shown below. [ka] [ka]
[0149] For the fabricated device, DC80mA / cm 2 The EL, JVL, and lifetime were measured. The device performance is shown in Table 3. The voltage, LE, EQE, PE, and LT97% were all based on the comparison compound. [Table 2] Schematic device structure [Table 3] Device performance
[0150] Comparing Compound 152 and Compound 153 with the Comparative Example, the efficiency of both Compound 152 and Compound 153 is higher than that of the Comparative Example. Presumably, Compound 152 and Compound 153 have a higher horizontal emitting dipole orientation than the Comparative Example. The extended planar substituents with high electrostatic potential increase the surface area for interaction between the Ir complex and the host molecule, thereby stacking the Ir complex parallel to the film surface and enhancing the outcoupling efficiency. Furthermore, the efficiency of both Compound 152 and Compound 153 is higher than 80 mA / cm. 2 LT in 97% is superior to that of the comparative example, suggesting that the extended substituents not only increase the efficiency but also enhance the stability of the complex in the device.
[0151] A summary of device data recorded at 9000 nits for the device examples is provided below in Table 4. EQE values are based on device C-2. [Table 4] The data in Table 4 show that devices using the inventive compounds as emitters achieved higher efficiency compared to the comparative example, albeit with the same color. Notably, the only difference between the inventive compound (compound 154) and the comparative compound (CC-1) is that the inventive compound has a phenyl moiety replacing one of the protons in the comparative compound, thereby increasing the distance between the terminal atoms in one direction across the Ir metal center. The device results show that a larger aspect ratio of the emitter molecules appears to be important in achieving higher device efficiency. Combination with other materials
[0152] The materials described herein as useful for a particular layer in an organic light-emitting device can be used in combination with a wide variety of other materials present in the device.For example, the emissive dopants disclosed herein can be used in conjunction with a wide variety of hosts, transport layers, blocking layers, injection layers, electrodes, and other layers that may be present.The materials described or referenced below are non-limiting examples of materials that may be useful in combination with the compounds disclosed herein, and those skilled in the art can easily consult the literature to identify other materials that may be useful in combination.
[0153] Conductive dopants: The charge transport layer is doped with a conductive dopant to significantly change the density of charge carriers and therefore its conductivity. The conductivity can be increased by creating charge carriers in the matrix material or, depending on the type of dopant, a change in the Fermi level of the semiconductor can also be achieved. The hole transport layer can be doped with a p-type conductive dopant and an n-type conductive dopant is used in the electron transport layer.
[0154] Non-limiting examples of conductive dopants that can be used in OLEDs in combination with the materials disclosed herein are illustrated below along with references that disclose these materials. EP01617493, EP01968131, EP2020694, EP2684932, US20050139810, US20070160905, US20090167167, US2010288362, WO 06081780, WO2009003455, WO2009008277, WO2009011327, WO2014009310, US2007252140, US2015060804, US2012146012 [ka] HIL / HTL:
[0155] The hole injection / transport material used in the embodiments of the present invention is not particularly limited, and any compound may be used as long as the compound is typically used as a hole injection / transport material. Examples of materials include phthalocyanine or porphyrin derivatives; aromatic amine derivatives; indolocarbazole derivatives; polymers containing fluorocarbons; polymers with conductive dopants; conductive polymers such as PEDOT / PSS; self-assembly monomers derived from compounds such as phosphonic acid and silane derivatives; MoO x p-type semiconducting organic compounds such as 1,4,5,8,9,12-hexaazatriphenylene hexacarbonitrile; metal complexes, and crosslinkable compounds.
[0156] Examples of aromatic amine derivatives used in the HIL or HTL include, but are not limited to, the following general structure: [ka]
[0157] Ar 1 From Ar 9each of which is a group consisting of aromatic hydrocarbon ring compounds such as benzene, biphenyl, triphenyl, triphenylene, naphthalene, anthracene, phenalene, phenanthrene, fluorene, pyrene, chrysene, perylene, and azulene; dibenzothiophene, dibenzofuran, dibenzoselenophene, furan, thiophene, benzofuran, benzothiophene, benzoselenophene, carbazole, indolocarbazole, pyridyl indole, pyrrolodipyridine, pyrazole, imidazole, triazole, oxazole, thiazole, oxadiazole, oxatriazole, dioxazole, thiadiazole, pyridine, pyridazine, pyrimidine, pyrazine, triazine, oxazine, oxathiazine, oxadiazine, indole, benzimidazole, indazole, indole, and aromatic heterocyclic compounds such as xazine, benzoxazole, benzisoxazole, benzothiazole, quinoline, isoquinoline, cinnoline, quinazoline, quinoxaline, naphthyridine, phthalazine, pteridine, xanthene, acridine, phenazine, phenothiazine, phenoxazine, benzofuropyridine, furodipyridine, benzothienopyridine, thienodipyridine, benzoselenophenopyridine and selenophenodipyridine; and aromatic hydrocarbon ring groups and aromatic heterocyclic groups having 2 to 10 cyclic structural units of the same or different types, which are bonded to each other directly or via at least one of an oxygen atom, a nitrogen atom, a sulfur atom, a silicon atom, a phosphorus atom, a boron atom, a chain structural unit and an aliphatic cyclic group. Each Ar can be unsubstituted or substituted with a substituent selected from the group consisting of deuterium, halide, alkyl, cycloalkyl, heteroalkyl, arylalkyl, alkoxy, aryloxy, amino, silyl, alkenyl, cycloalkenyl, heteroalkenyl, alkynyl, aryl, heteroaryl, acyl, carbonyl, carboxylic acid, ester, nitrile, isonitrile, sulfanyl, sulfinyl, sulfonyl, phosphino, and combinations thereof.
[0158] In one embodiment, Ar 1 From Ar9 teeth, [ka] are independently selected from the group consisting of: where k is an integer from 1 to 20; 101 From X 108 is C (including CH) or N; Z 101 is NAr 1 , O, or S; Ar 1 has the same radical as defined above.
[0159] Examples of metal complexes used in the HIL or HTL include, but are not limited to, those of the general formula: [ka] where Met is a metal that may have an atomic weight greater than 40; 101 -Y 102 ) is a bidentate ligand, and Y 101 and Y 102 is independently selected from C, N, O, P, and S; L 101 is an ancillary ligand; k' is an integer value from 1 to the maximum number of ligands that may be attached to the metal; and k'+k'' is the maximum number of ligands that may be attached to the metal.
[0160] In one embodiment, (Y 101 -Y 102 In another embodiment, (Y 101 -Y 102 In another embodiment, Met is selected from Ir, Pt, Os, and Zn. In a further embodiment, the metal complex is + For the / Fc couple, it has a minimum oxidation potential of less than about 0.6 V in solution.
[0161] Non-limiting examples of HIL and HTL materials that can be used in OLEDs in combination with the materials disclosed herein are illustrated below along with references that disclose these materials. CN102702075、DE102012005215、EP01624500、EP01698613、EP01806334、EP01930964、EP01972613、EP01997799、EP02011790、EP02055700、EP02055701、EP1725079、EP2085382、EP2660300、EP650955、JP07-073529、JP2005112765、JP2007091719、JP2008021687、JP2014-009196、KR20110088898、KR20130077473、TW201139402、US06517957、US20020158242、US20030162053、US20050123751、US20060182993、US20060240279、US20070145888、US20070181874、US20070278938、US20080014464、US20080091025、US20080106190、US20080124572、US20080145707、US20080220265、US20080233434、US20080303417、US2008107919、US20090115320、US20090167161、US2009066235、US2011007385、US20110163302、US2011240968、US2011278551、US2012205642、US2013241401、US20140117329、US2014183517、US5061569、US5639914、WO05075451、WO07125714、WO08023550、WO08023759、WO2009145016、WO2010061824、WO2011075644、WO2012177006、WO2013018530、WO2013039073、WO2013087142、WO2013118812、WO2013120577、WO2013157367、WO2013175747、WO2014002873、WO2014015935、WO2014015937、WO2014030872、WO2014030921、WO2014034791、WO2014104514、WO2014157018 [ka] [ka] [ka] [ka] [ka] [ka] [ka] [ka] EBL:
[0162] Electron blocking layers (EBLs) can be used to reduce the number of electrons and / or excitons that leave the emissive layer. The presence of such a blocking layer in a device can result in significantly higher efficiency and / or longer lifetime compared to a similar device lacking a blocking layer. Blocking layers can also be used to confine emission to desired regions of an OLED. In some embodiments, the EBL material has a higher LUMO (closer to the vacuum level) and / or a higher triplet energy than the emitter closest to the EBL interface. In some embodiments, the EBL material has a higher LUMO (closer to the vacuum level) and / or a higher triplet energy than one or more of the hosts closest to the EBL interface. In one aspect, the compound used in the EBL contains the same molecule or the same functional group as one of the hosts described below. host:
[0163] The light-emitting layer of the organic EL device of the present invention preferably contains at least a metal complex as a light-emitting material, and may contain a host material that uses the metal complex as a dopant material. The host material is not particularly limited, and any metal complex or organic compound may be used as long as the triplet energy of the host is greater than that of the dopant. Any host material may be used with any dopant as long as the triplet criterion is met.
[0164] Examples of metal complexes used as host materials preferably have the general formula: [ka] where Met is a metal; 103 -Y 104 ) is a bidentate ligand, and Y 103 and Y 104 is independently selected from C, N, O, P, and S; L 101 is another ligand; k' is an integer value from 1 to the maximum number of ligands that may be attached to the metal; and k'+k'' is the maximum number of ligands that may be attached to the metal.
[0165] In one embodiment, the metal complex is a complex: [ka] where (ON) is a bidentate ligand with the metal coordinated to atoms O and N.
[0166] In another embodiment, Met is selected from Ir and Pt. 103 -Y 104 ) is a carbene ligand.
[0167] Examples of other organic compounds used as the host material include the group consisting of aromatic hydrocarbon cyclic compounds such as benzene, biphenyl, triphenyl, triphenylene, tetraphenylene, naphthalene, anthracene, phenalene, phenanthrene, fluorene, pyrene, chrysene, perylene, and azulene; dibenzothiophene, dibenzofuran, dibenzoselenophene, furan, thiophene, benzofuran, benzothiophene, benzoselenophene, carbazole, indolocarbazole, pyridyl indole, pyrrolodipyridine, pyrazole, imidazole, triazole, oxazole, thiazole, oxadiazole, oxatriazole, dioxazole, thiadiazole, pyridine, pyridazine, pyrimidine, pyrazine, triazine, oxazine, oxathiazine, oxadiazine, indole, and benzimidazoline. and aromatic heterocyclic compounds such as benzofuropyridine, indazole, indoxazine, benzoxazole, benzisoxazole, benzothiazole, quinoline, isoquinoline, cinnoline, quinazoline, quinoxaline, naphthyridine, phthalazine, pteridine, xanthene, acridine, phenazine, phenothiazine, phenoxazine, benzofuropyridine, furodipyridine, benzothienopyridine, thienodipyridine, benzoselenophenopyridine and selenophenodipyridine; and aromatic hydrocarbon ring groups and aromatic heterocyclic groups, which may be of the same or different types and are bonded to each other directly or via at least one of an oxygen atom, a nitrogen atom, a sulfur atom, a silicon atom, a phosphorus atom, a boron atom, a chain structural unit and an aliphatic ring group. Each option in each group can be unsubstituted or substituted with a substituent selected from the group consisting of deuterium, halide, alkyl, cycloalkyl, heteroalkyl, arylalkyl, alkoxy, aryloxy, amino, silyl, alkenyl, cycloalkenyl, heteroalkenyl, alkynyl, aryl, heteroaryl, acyl, carbonyl, carboxylic acid, ester, nitrile, isonitrile, sulfanyl, sulfinyl, sulfonyl, phosphino, and combinations thereof.
[0168] In one embodiment, the host compound contains at least one of the following groups in the molecule: [ka] In the formula, R 101 From R 107 is independently selected from the group consisting of hydrogen, deuterium, halide, alkyl, cycloalkyl, heteroalkyl, arylalkyl, alkoxy, aryloxy, amino, silyl, alkenyl, cycloalkenyl, heteroalkenyl, alkynyl, aryl, heteroaryl, acyl, carbonyl, carboxylic acid, ester, nitrile, isonitrile, sulfanyl, sulfinyl, sulfonyl, phosphino, and combinations thereof, and when it is aryl or heteroaryl, has the same definition as that of Ar mentioned above. k is an integer from 0 to 20 or 1 to 20; k''' is an integer from 0 to 20. X 101 From X 108 is selected from C (including CH) or N. Z 101 and Z 102 is NR 101 , O, or S.
[0169] Non-limiting examples of host materials that can be used in OLEDs in combination with the materials disclosed herein are illustrated below along with references that disclose these materials. EP2034538, EP2034538A, EP2757608, JP2007254297, KR20100079458, KR20120088644, KR20120129733, KR201301 15564, TW201329200, US20030175553, US20050238919, US20060280965, US20090017330, US20090030202, US20090 167162, US20090302743, US20090309488, US20100012931, US20100084966, US20100187984, US2010187984, US201 2075273, US2012126221, US2013009543, US2013105787, US2013175519, US2014001446, US20140183503, US201402 25088, US2014034914, US7154114, WO2001039234, WO2004093207, WO2005014551, WO2005089025, WO2006072002, WO2006114966, WO2007063754, WO2008056746, WO2009003898, WO2009021126, WO2009063833, WO2009066778, WO20 09066779, WO2009086028, WO2010056066, WO2010107244, WO2011081423, WO2011081431, WO2011086863, WO201212 8298, WO2012133644, WO2012133649, WO2013024872, WO2013035275, WO2013081315, WO2013191404, WO2014142472
change
change
change
change
[0170] One or more additional emitter dopants can be used together with the compounds of the present disclosure.The example of additional emitter dopant is not particularly limited, and any compound can be used as long as the compound is typically used as an emitter material.Suitable emitter materials include, but are not limited to, compounds that can generate luminescence via phosphorescence, fluorescence, thermally activated delayed fluorescence, i.e. TADF (also called E-type delayed fluorescence), triplet-triplet annihilation, or a combination of these processes.
[0171] Non-limiting examples of emitter materials that can be used in OLEDs in combination with the materials disclosed herein are illustrated below along with references that disclose these materials. CN103694277、CN1696137、EB01238981、EP01239526、EP01961743、EP1239526、EP1244155、EP1642951、EP1647554、EP1841834、EP1841834B、EP2062907、EP2730583、JP2012074444、JP2013110263、JP4478555、KR1020090133652、KR20120032054、KR20130043460、TW201332980、US06699599、US06916554、US20010019782、US20020034656、US20030068526、US20030072964、US20030138657、US20050123788、US20050244673、US2005123791、US2005260449、US20060008670、US20060065890、US20060127696、US20060134459、US20060134462、US20060202194、US20060251923、US20070034863、US20070087321、US20070103060、US20070111026、US20070190359、US20070231600、US2007034863、US2007104979、US2007104980、US2007138437、US2007224450、US2007278936、US20080020237、US20080233410、US20080261076、US20080297033、US200805851、US2008161567、US2008210930、US20090039776、US20090108737、US20090115322、US20090179555、US2009085476、US2009104472、US20100090591、US20100148663、US20100244004、US20100295032、US2010102716、US2010105902、US2010244004、US2010270916、US20110057559、US20110108822、US20110204333、US2011215710、US2011227049、US2011285275、US2012292601, US20130146848, US2013033172, US2013165653, US2013181190, US2013334521, US20140246656, US 2014103305, US6303238, US6413656, US6653654, US6670645, US6687266, US6835469, US6921915, US7279704, US73 32232, US7378162, US7534505, US7675228, US7728137, US7740957, US7759489, US7951947, US8067099, US8592586 , US8871361, WO06081973, WO06121811, WO07018067, WO07108362, WO07115970, WO07115981, WO08035571, WO200201 5645, WO2003040257, WO2005019373, WO2006056418, WO2008054584, WO2008078800, WO2008096609, WO2008101842 , WO2009000673, WO2009050281, WO2009100991, WO2010028151, WO2010054731, WO2010086089, WO2010118029, WO20 11044988, WO2011051404, WO2011107491, WO2012020327, WO2012163471, WO2013094620, WO2013107487, WO201317 4471, WO2014007565, WO2014008982, WO2014023377, WO2014024131, WO2014031977, WO2014038456, WO2014112450,
change
change
change
change
[0172] A hole blocking layer (HBL) can be used to reduce the number of holes and / or excitons that leave the emissive layer. The presence of such a blocking layer in a device can result in significantly higher efficiency and / or longer lifetime compared to a similar device lacking a blocking layer. A blocking layer can also be used to confine emission to a desired region of an OLED. In some embodiments, the HBL material has a lower HOMO (further away from the vacuum level) and / or a higher triplet energy than the emitter closest to the HBL interface. In some embodiments, the HBL material has a lower HOMO (further away from the vacuum level) and / or a higher triplet energy than one or more of the hosts closest to the HBL interface.
[0173] In one embodiment, the compounds used in the HBL contain the same molecules as those used as hosts described above.
[0174] In another embodiment, the compound used in the HBL contains at least one of the following groups in the molecule: [ka] where k is an integer from 1 to 20; L 101 is another ligand, and k' is an integer from 1 to 3. ETL:
[0175] The electron transport layer (ETL) may include a material capable of transporting electrons. The electron transport layer may be intrinsic (undoped) or doped. Doping may be used to enhance conductivity. Examples of ETL materials are not particularly limited, and any metal complex or organic compound may be used as long as it is typically used to transport electrons.
[0176] In one embodiment, the compound used in the ETL contains at least one of the following groups in the molecule: [ka] JPEG0007622316000087.jpg27154In formula, R 101 is selected from the group consisting of hydrogen, deuterium, halide, alkyl, cycloalkyl, heteroalkyl, arylalkyl, alkoxy, aryloxy, amino, silyl, alkenyl, cycloalkenyl, heteroalkenyl, alkynyl, aryl, heteroaryl, acyl, carbonyl, carboxylic acid, ester, nitrile, isonitrile, sulfanyl, sulfinyl, sulfonyl, phosphino, and combinations thereof, and when it is aryl or heteroaryl, has the same definition as that of Ar mentioned above. 1 From Ar 3 has the same definition as that of Ar mentioned above. k is an integer from 1 to 20. X 101 From X 108 is selected from C (including CH) or N.
[0177] In another embodiment, the metal complex used in the ETL comprises, but is not limited to, the following general formula: [ka] In the formula, (ON) or (NN) is a bidentate ligand having a metal coordinated to the atoms O, N or N, N; 101 is another ligand; and k' is an integer value between 1 and the maximum number of ligands that can be attached to the metal.
[0178] Non-limiting examples of ETL materials that can be used in OLEDs in combination with the materials disclosed herein are illustrated below along with references that disclose these materials. CN103508940, EP01602648, EP01734038, EP01956007, JP2004-022334, JP2 005149918, JP2005-268199, KR0117693, KR20130108183, US20040036077, U S20070104977, US2007018155, US20090101870, US20090115316, US20090140637, US20090179554, US2009218940, US2010108990, US2011156017, US20 11210320, US2012193612, US2012214993, US2014014925, US2014014927, US20140284580, US6656612, US8415031, WO2003060956, WO2007111263, WO20 09148269, WO2010067894, WO2010072300, WO2011074770, WO2011105373, WO 2013079217, WO2013145667, WO2013180376, WO2014104499, WO2014104535. [ka] [ka] [ka] Charge Generation Layer (CGL)
[0179] In tandem or stacked OLEDs, the CGL plays an important role in performance and consists of n-doped and p-doped layers for the injection of electrons and holes, respectively. The electrons and holes are supplied from the CGL and electrodes. The consumed electrons and holes in the CGL are replenished by electrons and holes injected from the cathode and anode, respectively, after which the bipolar current gradually reaches a steady state. Typical CGL materials contain n-type and p-type conductive dopants used in the transport layers.
[0180] In any of the above-mentioned compounds used in each layer of an OLED device, the hydrogen atoms may be partially or fully deuterated. Thus, any of the specifically mentioned substituents, such as but not limited to methyl, phenyl, pyridyl, etc., can be their non-deuterated, partially deuterated, and fully deuterated versions. Similarly, the classes of substituents, such as but not limited to alkyl, aryl, cycloalkyl, heteroaryl, etc., can be their non-deuterated, partially deuterated, and fully deuterated versions.
[0181] It is understood that the various embodiments described herein are merely exemplary and are not intended to limit the scope of the invention. For example, many of the materials and structures described herein can be substituted with other materials and structures without departing from the spirit of the invention. Thus, the invention as claimed may include variations from the specific examples and preferred embodiments described herein, as will be apparent to those skilled in the art. It is understood that the various theories of why the invention works are not intended to be limiting. [Prior art documents] [Patent documents]
[0182] [Patent Document 1] U.S. Pat. No. 5,844,363 [Patent Document 2] U.S. Patent No. 6,303,238 [Patent Document 3] U.S. Patent No. 5,707,745 [Patent Document 4] U.S. Patent No. 7,279,704 [Explanation of symbols]
[0183] 100 Organic Light Emitting Device 110 Substrate 115 Anode 120 Hole injection layer 125 Hole transport layer 130 Electron Blocking Layer 135 Light-emitting layer 140 Hole Blocking Layer 145 Electron transport layer 150 Electron injection layer 155 Protective layer 160 Cathode 162 First conductive layer 164 Second Conductive Layer 170 Barrier Layer 200 Inverted OLED, device 210 Substrate 215 Cathode 220 Light-emitting layer 225 Hole transport layer 230 Anode 300 EML samples
Claims
1. A compound having a metal coordination complex structure; The compound is selected from the group consisting of: 【Chemistry 1】 【Chemistry 2】 【Chemistry 3】 【Chemistry 4】 【Chemistry 5】 【Chemistry 6】 【Chemistry 7】 【Chemistry 8】 【Chemistry 9】 【Chemistry 10】 【Chemistry 11】 【Chemistry 12】 【Chemistry 13】 【Chemistry 14】 【Chemistry 15】 【Chemistry 16】 【Chemistry 17】 【Chemistry 18】 【Chemistry 19】 【Chemistry 20】
2. an anode; A cathode; an organic layer disposed between the anode and the cathode, the organic layer comprising a compound having a metal coordination complex structure, An organic light emitting device (OLED) characterized in that the compound is a compound according to claim 1.
3. A consumer product comprising an organic light emitting device (OLED) according to claim 2.
Citation Information
Patent Citations
Light-emitting compound containing lanthanide ion
JP2006299230A
Metal complex and organic light emitting element
JP2008007500A
Method for producing imidazole compound, organic electroluminescent element, displaying device and illuminating device
JP2010120893A
Phosphorescent substances
JP2013521280A
Organic electroluminescent element, display device, and lighting device
JP2014099539A