Polymer composition, crosslinked polymer, and tire

Abstract

The present invention provides a polymer composition which has good processability and is suitable for the production of a tire that has an excellent balance among rebound resilience, wet grip performance, low loss tangent and tensile strength at high levels.　A polymer composition according to the present invention contains: (A) a conjugated diene polymer that is a reaction product of a compound represented by one of general formulae (1) to (3) and a polymer which is obtained by polymerizing a conjugated diene compound or a conjugated diene compound and an aromatic vinyl compound in the presence of an alkali metal compound or an alkaline earth metal compound, and which has an active polymerization end; and (B) conjugated diene polymer particles.

Description

[Technical field]

[0001] The present invention relates to a polymer composition, a crosslinked polymer, and a tire made with the crosslinked polymer. [Background technology]

[0002] In recent years, in connection with the movement towards global carbon dioxide emission regulations accompanying the growing interest in environmental issues, there has been an increasing demand for improved fuel efficiency in automobiles. In order to meet such demands, there is also a demand for reduced rolling resistance in tire performance. Conventionally, methods for optimizing tire structures have been considered as methods for reducing the rolling resistance of tires, but currently, a common method is to use polymer compositions applied to tires that have low tan δ (hereinafter also referred to as "low hysteresis loss" or "low loss") and excellent low heat generation properties.

[0003] Possible methods for obtaining such a polymer composition with low heat buildup include reducing the amount of filler such as carbon black or silica, or using carbon black with a large particle size. However, any of these methods inevitably results in a decrease in the reinforcement, abrasion resistance, and grip on wet road surfaces (hereinafter also referred to as "wet grip") of the polymer composition.

[0004] Therefore, for example, a study has been conducted on the use of a modified conjugated diene-based polymer obtained by forming an activated polymer having a metal terminal and modifying the activated polymer by introducing a specific modifier as a tire tread material (see, for example, Patent Document 1). Patent Document 1 discloses that the use of this material as a tire tread material results in excellent heat build-up, wear resistance, and wet grip properties. [Prior art documents] [Patent documents]

[0005] [Patent Document 1] Special Publication No. 2016-528369 Summary of the Invention [Problem to be solved by the invention]

[0006] However, when the modified conjugated diene-based polymer disclosed in Patent Document 1 is used as a tire tread material, there is a problem that it is difficult to obtain sufficient performance in terms of rebound resilience because the dispersibility of a filler such as silica contained in the polymer composition becomes excessively high.

[0007] Therefore, some aspects of the present invention provide a polymer composition suitable for producing a tire having good processability and excellent balance in rebound resilience, wet grip performance, low loss property and tensile strength. Also, some aspects of the present invention provide a tire having excellent balance in rebound resilience, wet grip performance, low loss property and tensile strength. [Means for solving the problem]

[0008] The present invention has been made to solve at least a part of the above-mentioned problems, and can be realized in any of the following aspects.

[0009] One embodiment of the polymer composition according to the present invention is (A) a conjugated diene polymer which is a reaction product between a polymer having an active polymerization end obtained by polymerizing a conjugated diene compound or a conjugated diene compound and an aromatic vinyl compound in the presence of an alkali metal compound or an alkaline earth metal compound, and a compound represented by any one of the following general formulas (1) to (3); (B) conjugated diene polymer particles; Contains: [ka] (In formula (1), A 2 is an imino group, an amide group, a (thio)carbonyl group, a (thio)carbonyloxy group, a sulfide or a polysulfide. 2or represents a protected primary amino group, a protected secondary amino group, a tertiary amino group, a nitrile group, a pyridyl group, a (thio)epoxy group, a (thio)isocyanate group, a (thio)formyl group, a (thio)carboxylate ester, a metal salt of a (thio)carboxylate ester, a carboxylic acid halide compound, an imidazolyl group, or a group represented by the following formula (1a): 2 and L 3 each independently represents a single bond or a hydrocarbylene group having 1 to 20 carbon atoms; R 3 and R 4 each independently represents a hydrocarbyl group having 1 to 4 carbon atoms, n2 is 0 to 3, and m1 is 0 or 1. [ka] (In formula (1a), L 3 , R 3 , R 4 and n2 are the same as in formula (1), and * is L 2 This indicates the site of binding to [ka] (In formula (2), A 3 each independently represents an imino group, an amido group, a (thio)carbonyl group, a (thio)carbonyloxy group, a secondary amino group, or a tertiary amino group; Z represents a t-valent group having 1 to 20 carbon atoms which may or may not contain a nitrogen atom; L 4 represents a single bond or a hydrocarbylene group having 1 to 20 carbon atoms; L 5 represents a hydrocarbylene group having 1 to 20 carbon atoms, R 5 and R 6 each independently represents a hydrocarbyl group having 1 to 4 carbon atoms, n3 is 0 or 1, and t is 2 or 3. [ka] (In formula (3), R 7 and R 8 each independently represents a hydrocarbyl group having 1 to 20 carbon atoms; R 9represents a hydrocarbyl group having 1 to 20 carbon atoms, a substituted alkyl group having 1 to 20 carbon atoms in which at least one of the hydrogen atoms and -CH2- groups in the alkyl group is substituted with a group containing at least one element selected from the group consisting of silicon, nitrogen, phosphorus, oxygen and sulfur, or an aromatic group having 6 to 20 carbon atoms containing at least one element selected from the group consisting of nitrogen, phosphorus, oxygen and sulfur; R 10 represents an alkanediyl group having 1 to 20 carbon atoms. n4 is 1 or 2.

[0010] In one embodiment of the polymer composition, When the entire conjugated diene polymer component contained in the polymer composition is taken as 100% by mass, the (B) conjugated diene polymer particles can be contained in an amount of 1% by mass or more and 50% by mass or less.

[0011] In any of the embodiments of the polymer composition, The (A) conjugated diene polymer may have a weight average molecular weight in terms of polystyrene measured by gel permeation chromatography of 100,000 to 2,000,000.

[0012] In any of the embodiments of the polymer composition, The (B) conjugated diene polymer particles may have a number average particle size of 10 nm or more and 800 nm or less as measured by a light scattering method.

[0013] In any of the embodiments of the polymer composition, The (B) conjugated diene polymer particles may be crosslinked particles.

[0014] In any of the embodiments of the polymer composition, Additionally, a crosslinking agent may be included.

[0015] One embodiment of the crosslinked polymer according to the present invention is The polymer composition is produced using any one of the above-mentioned embodiments.

[0016] One aspect of the tire according to the present invention is The crosslinked polymer of the above embodiment is used. Effect of the Invention

[0017] According to the polymer composition of the present invention, it is possible to produce a crosslinked polymer (tire) which has good processability and is highly well-balanced in terms of impact resilience, wet grip properties, low loss properties and tensile strength. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0018] Preferred embodiments of the present invention will be described in detail below. Note that the present invention is not limited to the embodiments described below, and should be understood to include various modified examples that are implemented within the scope of the present invention.

[0019] In this specification, a numerical range described as "X to Y" is interpreted as including the numerical value X as the lower limit and including the numerical value Y as the upper limit.

[0020] In this specification, the term "(meth)acrylic acid" includes both acrylic acid and methacrylic acid, and the term "(meth)acrylate" includes both acrylate and methacrylate.

[0021] 1. Polymer Composition A polymer composition according to one embodiment of the present invention contains (A) a conjugated diene-based polymer (hereinafter also referred to as "(A) conjugated diene-based polymer") which is a reaction product between a polymer having an active polymerization end obtained by polymerizing a conjugated diene compound or a conjugated diene compound and an aromatic vinyl compound in the presence of an alkali metal compound or an alkaline earth metal compound, and a compound represented by any one of the following general formulas (1) to (3), and (B) conjugated diene-based polymer particles.

[0022] The polymer composition according to the present embodiment is an unvulcanized polymer composition obtained by kneading (A) a conjugated diene polymer and (B) conjugated diene polymer particles, and optionally other additives. The polymer composition according to the present embodiment is a crosslinked polymer formed by, for example, a crosslinking treatment such as vulcanization.

[0023] Hereinafter, each component contained in the polymer composition according to this embodiment will be described.

[0024] 1.1.(A) Conjugated diene polymer The polymer composition according to the present embodiment contains (A) a conjugated diene polymer which is a reaction product between a polymer having an active polymerization end obtained by polymerizing a conjugated diene compound or a conjugated diene compound and an aromatic vinyl compound in the presence of an alkali metal compound or an alkaline earth metal compound, and a compound represented by any one of the following general formulas (1) to (3).

[0025] [ka] (In formula (1), A 2 is an imino group, an amide group, a (thio)carbonyl group, a (thio)carbonyloxy group, a sulfide or a polysulfide. 2 or represents a protected primary amino group, a protected secondary amino group, a tertiary amino group, a nitrile group, a pyridyl group, a (thio)epoxy group, a (thio)isocyanate group, a (thio)formyl group, a (thio)carboxylate ester, a metal salt of a (thio)carboxylate ester, a carboxylic acid halide compound, an imidazolyl group, or a group represented by the following formula (1a): 2 and L 3 each independently represents a single bond or a hydrocarbylene group having 1 to 20 carbon atoms; R 3 and R 4 each independently represents a hydrocarbyl group having 1 to 4 carbon atoms, n2 is 0 to 3, and m1 is 0 or 1.

[0026] [ka] (In formula (1a), L 3 , R 3 , R 4 and n2 are the same as in formula (1), and * is L 2 This indicates the site of binding to

[0027] [ka] (In formula (2), A 3 each independently represents an imino group, an amido group, a (thio)carbonyl group, a (thio)carbonyloxy group, a secondary amino group, or a tertiary amino group; Z represents a t-valent group having 1 to 20 carbon atoms which may or may not contain a nitrogen atom; L 4 represents a single bond or a hydrocarbylene group having 1 to 20 carbon atoms; L 5 represents a hydrocarbylene group having 1 to 20 carbon atoms, R 5 and R 6 each independently represents a hydrocarbyl group having 1 to 4 carbon atoms, n3 is 0 or 1, and t is 2 or 3.

[0028] [ka] (In formula (3), R 7 and R 8 each independently represents a hydrocarbyl group having 1 to 20 carbon atoms; R 9 represents a hydrocarbyl group having 1 to 20 carbon atoms, a substituted alkyl group having 1 to 20 carbon atoms in which at least one of the hydrogen atoms and -CH2- groups in the alkyl group is substituted with a group containing at least one element selected from the group consisting of silicon, nitrogen, phosphorus, oxygen and sulfur, or an aromatic group having 6 to 20 carbon atoms containing at least one element selected from the group consisting of nitrogen, phosphorus, oxygen and sulfur; R 10 represents an alkanediyl group having 1 to 20 carbon atoms. n4 is 1 or 2.

[0029] The (A) conjugated diene polymer has a structural unit derived from a conjugated diene compound and has a structure derived from any of the compounds of the above general formulas (1) to (3) at an active polymerization end. Such a (A) conjugated diene polymer can be obtained by first polymerizing a monomer containing a conjugated diene compound in the presence of an alkali metal compound or an alkaline earth metal compound to obtain a polymer having an active polymerization end (polymerization step), and then reacting the polymer having an active polymerization end with any of the compounds of the above general formulas (1) to (3) (hereinafter also referred to as a "specific modifier") (modification step).

[0030] <Polymerization process> Examples of conjugated diene compounds that can be used in polymerization include 1,3-butadiene, isoprene, 2,3-dimethyl-1,3-butadiene, 1,3-pentadiene, 1,3-hexadiene, 1,3-heptadiene, 2-phenyl-1,3-butadiene, 3-methyl-1,3-pentadiene, and 2-chloro-1,3-butadiene. Among these, 1,3-butadiene, isoprene, and 2,3-dimethyl-1,3-butadiene are preferred. Conjugated diene compounds can be used alone or in combination of two or more.

[0031] The (A) conjugated diene polymer may be a homopolymer of a conjugated diene compound, but is preferably a copolymer of a conjugated diene compound and an aromatic vinyl compound from the viewpoint of increasing the strength of the crosslinked polymer. In particular, it is preferably a copolymer containing 1,3-butadiene and styrene in the monomer composition, in terms of high living property in anionic polymerization. When the (A) conjugated diene polymer is a copolymer of a conjugated diene compound and an aromatic vinyl compound, the (A) conjugated diene polymer typically has a random copolymerization portion in which the distribution of the conjugated diene compound and the aromatic vinyl compound is irregular, and may further have a block portion consisting of a structural unit derived from the conjugated diene compound or the aromatic vinyl compound.

[0032] Examples of aromatic vinyl compounds that can be used in the polymerization include styrene, 2-methylstyrene, 3-methylstyrene, 4-methylstyrene, α-methylstyrene, 2,4-dimethylstyrene, 2,4-diisopropylstyrene, 5-tert-butyl-2-methylstyrene, vinylethylbenzene, divinylbenzene, trivinylbenzene, divinylnaphthalene, tert-butoxystyrene, vinylbenzyldimethylamine, (4-vinylbenzyl)dimethylaminoethylether, N,N-dimethylaminoethylstyrene, N,N-dimethylaminomethylstyrene, 2-ethylstyrene, 3-ethylstyrene, 4-ethylstyrene, 2-tert-butylstyrene, 3-tert-butylstyrene, 4-tert-butylstyrene, vinylxylene, vinylnaphthalene, vinylpyridine, diphenylethylene, and tertiary amino group-containing diphenylethylene (e.g., 1-(4-N,N-dimethylaminophenyl)-1-phenylethylene). Among these, styrene and α-methylstyrene are preferred. The aromatic vinyl compounds can be used alone or in combination of two or more.

[0033] When the (A) conjugated diene polymer is a copolymer of a conjugated diene compound and an aromatic vinyl compound, the content of the aromatic vinyl compound (aromatic vinyl content) is preferably 3 to 55 mass%, more preferably 5 to 50 mass%, based on 100 mass% of the total of the conjugated diene compound and the aromatic vinyl compound used in the polymerization, from the viewpoint of achieving a good balance between the low loss property and the wet grip property of the resulting crosslinked polymer. 1 It can be measured by H-NMR.

[0034] In the polymerization, other monomers may be used in addition to the conjugated diene compound and the aromatic vinyl compound. Examples of the other monomers include acrylonitrile, methyl (meth)acrylate, ethyl (meth)acrylate, and hydroxyethyl (meth)acrylate. The amount of the other monomers used is preferably 25% by mass or less, more preferably 15% by mass or less, and particularly preferably 10% by mass or less, based on 100% by mass of the total amount of the monomers used in the polymerization.

[0035] The polymerization method used may be any of solution polymerization, gas phase polymerization, and bulk polymerization, but solution polymerization is particularly preferred. The polymerization form may be any of batch and continuous. When using solution polymerization, a specific example of the polymerization method is a method in which a monomer containing a conjugated diene compound is polymerized in an organic solvent in the presence of a polymerization initiator and a randomizer used as necessary.

[0036] As the polymerization initiator, an alkali metal compound or an alkaline earth metal compound can be used. Specific examples of these include alkyl lithium such as methyl lithium, ethyl lithium, n-propyl lithium, n-butyl lithium, sec-butyl lithium, and tert-butyl lithium, 1,4-dilithiobutane, phenyl lithium, stilbene lithium, naphthyl lithium, 1,3-bis(1-lithio-1,3-dimethylpentyl)benzene, 1,3-phenylenebis(3-methyl-1-phenylpentylidene)dilithium, 3-(dimethylamino)propyl lithium, naphthyl sodium, naphthyl potassium, di-n-butyl magnesium, di-n-hexyl magnesium, ethoxy potassium, and calcium stearate. Among these, lithium compounds are preferred. The total amount of the polymerization initiator to be used is preferably 0.2 to 20 mmol per 100 g of monomer to be used in polymerization. The polymerization initiator can be used alone or in combination of two or more.

[0037] The polymerization reaction may be carried out in the presence of a compound (hereinafter also referred to as a "modified initiator") obtained by mixing an alkali metal compound or an alkaline earth metal compound with a compound having a functional group that interacts with silica. By carrying out the polymerization in the presence of a modified initiator, a functional group that interacts with silica can be introduced into the polymerization initiation terminal of the conjugated diene polymer (A). In this specification, "interaction" means forming a covalent bond between molecules or forming an intermolecular force weaker than a covalent bond (for example, an electromagnetic force acting between molecules such as an ion-dipole interaction, a dipole-dipole interaction, a hydrogen bond, or a van der Waals force). The "functional group that interacts with silica" preferably has at least one selected from the group consisting of a nitrogen atom, a sulfur atom, a phosphorus atom, and an oxygen atom.

[0038] The modified initiator is preferably a reaction product of a lithium compound such as an alkyl lithium and a nitrogen-containing compound such as a secondary amine compound. Specific examples of the nitrogen-containing compound include dimethylamine, diethylamine, dipropylamine, dibutylamine, dodecamethyleneimine, N,N'-dimethyl-N'-trimethylsilyl-1,6-diaminohexane, piperidine, pyrrolidine, hexamethyleneimine, heptamethyleneimine, dicyclohexylamine, N-methylbenzylamine, di-(2-ethylhexyl)amine, diallylamine, morpholine, N-(trimethylsilyl)piperazine, N-(tert-butyldimethylsilyl)piperazine, 1,3-ditrimethylsilyl-1,3,5-triazinane, etc. In addition, when polymerization is performed in the presence of a modified initiator, an alkali metal compound or an alkaline earth metal compound may be mixed in advance with a compound having a functional group that interacts with silica to prepare a modified initiator, and the prepared modified initiator may be added to the polymerization system to perform polymerization. Alternatively, an alkali metal compound or an alkaline earth metal compound and a compound having a functional group that interacts with silica may be added to the polymerization system, and the two may be mixed in the polymerization system to prepare a modified initiator and perform polymerization. Alternatively, a nitrogen-containing alkyl lithium compound may be used. A specific example of a nitrogen-containing alkyl lithium compound is a reaction product of 3-dimethylaminopropyl lithium and isoprene.

[0039] The randomizer can be used for the purpose of adjusting the vinyl bond content, which indicates the content of vinyl bonds (1,2-bonds and 3,4-bonds) in the polymer. Examples of the randomizer include dimethoxybenzene, tetrahydrofuran, dimethoxyethane, diethylene glycol dibutyl ether, diethylene glycol dimethyl ether, 2,2-di(tetrahydrofuryl)propane, 2-(2-ethoxyethoxy)-2-methylpropane, triethylamine, pyridine, N-methylmorpholine, and tetramethylethylenediamine. These can be used alone or in combination of two or more.

[0040] The organic solvent used in the polymerization may be any organic solvent inert to the reaction, and may be, for example, an aliphatic hydrocarbon, an alicyclic hydrocarbon, or an aromatic hydrocarbon. Among them, a hydrocarbon having 3 to 8 carbon atoms is preferred, and specific examples thereof include, for example, propane, n-butane, isobutane, n-pentane, isopentane, n-hexane, cyclohexane, propene, 1-butene, isobutene, trans-2-butene, cis-2-butene, 1-pentyne, 2-pentyne, 1-hexene, 2-hexene, benzene, toluene, xylene, ethylbenzene, heptane, cyclopentane, methylcyclopentane, methylcyclohexane, 1-pentene, 2-pentene, and cyclohexene. The organic solvent may be used alone or in combination of two or more.

[0041] When solution polymerization is used, the monomer concentration in the reaction solvent is preferably 5 to 50% by mass, more preferably 10 to 30% by mass, from the viewpoint of maintaining a balance between productivity and ease of polymerization control. The temperature of the polymerization reaction is preferably -20°C to 150°C, more preferably 0°C to 120°C, and particularly preferably 20°C to 100°C. The polymerization reaction is preferably carried out under a pressure sufficient to keep the monomers substantially in a liquid phase. Such a pressure can be obtained by a method such as pressurizing the inside of a reactor with a gas inert to the polymerization reaction. A conjugated diene-based polymer having an active polymerization terminal can be obtained by such a polymerization reaction.

[0042] In the conjugated diene polymer having an active polymerization end, the vinyl bond content in the structural units derived from the conjugated diene compound is preferably 30 to 65 mol%, more preferably 33 to 62 mol%, and particularly preferably 35 to 60 mol%. If the vinyl bond content is less than 30 mol%, the grip properties tend to be too low, and if it exceeds 65 mol%, the abrasion resistance of the resulting crosslinked polymer tends to be easily deteriorated. In this specification, the "vinyl bond content" is a value indicating the content ratio of structural units having vinyl bonds to all structural units derived from the conjugated diene compound in the conjugated diene polymer, 1 The values ​​were measured by H-NMR.

[0043] <Denaturation process> Next, the active polymerization terminals of the conjugated diene polymer obtained by the polymerization reaction are reacted with compounds (specific modifiers) represented by the following general formulas (1) to (3). Through these steps, a conjugated diene polymer (A) that has been terminally modified with a specific modifier can be obtained. The conjugated diene polymer (A) that has been terminally modified with such a specific modifier has a stronger interaction with the filler at the terminal modified site, and therefore has improved wet grip properties and low loss properties, and also has improved tensile strength and processability due to the branching properties of the imine.

[0044] [ka] (In formula (1), A 2 is an imino group, an amide group, a (thio)carbonyl group, a (thio)carbonyloxy group, a sulfide or a polysulfide. 2 or represents a protected primary amino group, a protected secondary amino group, a tertiary amino group, a nitrile group, a pyridyl group, a (thio)epoxy group, a (thio)isocyanate group, a (thio)formyl group, a (thio)carboxylate ester, a metal salt of a (thio)carboxylate ester, a carboxylic acid halide compound, an imidazolyl group, or a group represented by the following formula (1a): 2 and L 3each independently represents a single bond or a hydrocarbylene group having 1 to 20 carbon atoms; R 3 and R 4 each independently represents a hydrocarbyl group having 1 to 4 carbon atoms, n2 is 0 to 3, and m1 is 0 or 1.

[0045] [ka] (In formula (1a), L 3 , R 3 , R 4 and n2 are the same as in formula (1), and * is L 2 This indicates the site of binding to

[0046] In the above formula (1), L 2 and L 3 Examples of the hydrocarbylene group having 1 to 20 carbon atoms include a linear or branched alkanediyl group having 1 to 20 carbon atoms, a cycloalkylene group having 3 to 20 carbon atoms, and an arylene group having 6 to 20 carbon atoms. 3 and R 4 Examples of the hydrocarbyl group having 1 to 4 carbon atoms include a linear or branched alkyl group having 1 to 4 carbon atoms and a cycloalkyl group having 3 to 4 carbon atoms.

[0047] Specific examples of the compound represented by the above general formula (1) include N,N-bis(trimethoxysilylpropyl)aminopropyl-3-imidazole, N,N-bis(triethoxysilylpropyl)aminopropyl-1-imidazole, N,N-bis(trimethoxysilyl)aminopropylmethyldiethylsilane, N,N,N-tris(triethoxysilylpropyl)amine, and N,N,N',N'-tetrakis(3-triethoxysilylpropyl)-1,3-diaminopropane.

[0048] [ka] (In formula (2), A 3each independently represents an imino group, an amido group, a (thio)carbonyl group, a (thio)carbonyloxy group, a secondary amino group, or a tertiary amino group; Z represents a t-valent group having 1 to 20 carbon atoms which may or may not contain a nitrogen atom; L 4 represents a single bond or a hydrocarbylene group having 1 to 20 carbon atoms; L 5 represents a hydrocarbylene group having 1 to 20 carbon atoms, R 5 and R 6 each independently represents a hydrocarbyl group having 1 to 4 carbon atoms, n3 is 0 or 1, and t is 2 or 3.

[0049] In the above formula (2), Z is a divalent or trivalent group having 1 to 20 carbon atoms which may contain a nitrogen atom, and preferably contains a nitrogen atom. 4 A hydrocarbylene group having 1 to 20 carbon atoms and L 5 Examples of the hydrocarbylene group having 1 to 20 carbon atoms include a linear or branched alkanediyl group having 1 to 20 carbon atoms, a cycloalkylene group having 3 to 20 carbon atoms, and an arylene group having 6 to 20 carbon atoms. In the above formula (2), R 5 and R 6 Examples of the hydrocarbyl group having 1 to 4 carbon atoms include a linear or branched alkyl group having 1 to 4 carbon atoms and a cycloalkyl group having 3 to 4 carbon atoms.

[0050] Specific examples of the compound represented by the above general formula (2) include compounds represented by the following formulae (M-1) to (M-4).

[0051] [ka] In the above formula (M-1), R 11 represents a hydrogen atom or an alkyl group having 1 to 20 carbon atoms, and n5 represents an integer of 1 to 10.

[0052] [ka] (In formula (3), R 7and R 8 each independently represents a hydrocarbyl group having 1 to 20 carbon atoms; R 9 represents a hydrocarbyl group having 1 to 20 carbon atoms, a substituted alkyl group having 1 to 20 carbon atoms in which at least one of the hydrogen atoms and -CH2- groups in the alkyl group is substituted with a group containing at least one element selected from the group consisting of silicon, nitrogen, phosphorus, oxygen and sulfur, or an aromatic group having 6 to 20 carbon atoms containing at least one element selected from the group consisting of nitrogen, phosphorus, oxygen and sulfur; R 10 represents an alkanediyl group having 1 to 20 carbon atoms. n4 is 1 or 2.

[0053] In the above formula (3), R 7 and R 8 Examples of the hydrocarbyl group having 1 to 20 carbon atoms include a linear or branched alkyl group having 1 to 20 carbon atoms, a cycloalkyl group having 3 to 20 carbon atoms, and an aryl group having 6 to 20 carbon atoms.

[0054] Specific examples of the compound represented by the above general formula (3) include N-phenyl-2,2-dimethoxy-1-aza-2-silacyclopentane, N-(3-triethoxysilylpropyl)-2,2-dimethoxy-1-aza-2-silacyclopentane, and the like.

[0055] In the modification reaction of the conjugated diene polymer having an active polymerization terminal, the specific modifier may be used alone, or a modifier other than the specific modifier (hereinafter also referred to as "other modifier") may be used together with the specific modifier. The other modifier is not particularly limited as long as it has a functional group that interacts with the filler and can react with the active polymerization terminal of the polymer.

[0056] The above modification reaction can be carried out, for example, as a solution reaction. This solution reaction may be carried out using a solution containing unreacted monomers after the polymerization reaction is completed, or the conjugated diene polymer contained in the solution may be isolated and dissolved in a suitable solvent such as cyclohexane before the reaction. The modification reaction may be carried out either batchwise or continuously. In this case, the method of adding the modifier is not particularly limited, and examples of the method include a method of adding the modifier all at once, a method of adding the modifier in portions, and a method of adding the modifier continuously.

[0057] The proportion of the specific modifier used (the total amount when two or more types are used) is preferably 0.2 mol or more, more preferably 0.4 mol or more, per mol of the metal atom involved in the polymerization reaction of the polymerization initiator. By making it 0.2 mol or more, the modification reaction of the polymer terminal by the specific modifier can be sufficiently advanced, and the interaction with the filler at the modified terminal site can be sufficiently strengthened. In addition, in order to reduce unreacted matter in the solution after the modification reaction, the upper limit of the proportion of the specific modifier used is preferably less than 1.5 mol, more preferably less than 1.2 mol, per mol of the metal atom involved in the polymerization reaction of the polymerization initiator.

[0058] In addition, when the specific modifier and other modifiers are used in combination in the modification reaction, the proportion of the other modifier used is preferably 30 mol % or less, more preferably 20 mol % or less, and particularly preferably 10 mol % or less, based on the total proportion of the specific modifier and other modifiers used, from the viewpoint of sufficiently proceeding the reaction between the conjugated diene polymer and the specific modifier.

[0059] The temperature of the modification reaction is usually the same as the temperature of the polymerization reaction, and is preferably -20°C to 150°C, more preferably 0°C to 120°C, and particularly preferably 20°C to 100°C. If the temperature of the modification reaction is low, the viscosity of the modified conjugated diene polymer tends to increase. On the other hand, if the temperature of the modification reaction is high, the active terminal of the polymer is easily deactivated. The reaction time of the modification reaction is preferably 1 minute to 5 hours, and more preferably 2 minutes to 1 hour.

[0060] The conjugated diene polymer (A) contained in the reaction solution can be isolated by a known solvent removal method such as steam stripping and drying such as heat treatment. The obtained conjugated diene polymer (A) may be adjusted in Mooney viscosity by adding an extender oil or the like as necessary. This treatment can improve processability. Examples of the extender oil include aromatic oil, naphthenic oil, and paraffin oil. The amount of the extender oil to be added may be appropriately determined depending on the monomers used in polymerization, and is, for example, 10 to 50 parts by mass relative to 100 parts by mass of the conjugated diene polymer.

[0061] In this way, the conjugated diene polymer (A) can be obtained. The conjugated diene polymer (A) can improve compatibility with fillers, and can provide a polymer composition with improved processability. By using such a polymer composition containing the conjugated diene polymer (A), a tire (crosslinked polymer) can be obtained that is excellent in heat buildup, tensile strength, abrasion resistance, fuel economy, wet grip, and the like, required for applications such as automobile tires, while also having excellent low loss properties.

[0062] The (A) conjugated diene polymer preferably has a structure derived from any of the compounds of the above general formulas (1) to (3) at least at one end of the polymer. When the (A) conjugated diene polymer has such a structure, the dispersibility of fillers such as carbon black and silica is further improved when the polymer is applied to, for example, tires, and this is preferable in that it provides a higher improvement in low loss properties and wet grip properties.

[0063] The weight average molecular weight (Mw) of the conjugated diene polymer (A) measured by gel permeation chromatography (GPC) in terms of polystyrene is preferably 100,000 to 2,000,000. If the Mw is less than 100,000, the crosslinked polymer of the polymer composition according to the present embodiment tends to have low loss properties and abrasion resistance that are easily reduced, and if it is more than 2,000,000, the processability of the polymer composition tends to be easily reduced. The weight average molecular weight (Mw) of the resulting conjugated diene polymer (A) is more preferably 150,000 to 1,500,000, and even more preferably 200,000 to 1,000,000.

[0064] The molecular weight distribution of the (A) conjugated diene polymer, i.e., the ratio (Mw / Mn) of the weight average molecular weight (Mw) to the number average molecular weight (Mn), is preferably 1.5 to 3.0, more preferably 1.5 to 2.5, and particularly preferably 1.5 to 2.2. When the (A) conjugated diene polymer has a molecular weight distribution within the above range, it is easy to obtain better low loss properties, abrasion resistance, wet grip performance, and mechanical properties.

[0065] 1.2.(B) Conjugated diene polymer particles The polymer composition according to the present embodiment contains (B) conjugated diene polymer particles. By containing (B) conjugated diene polymer particles, the abrasion resistance and impact resilience of the obtained crosslinked polymer (tire) are improved.

[0066] The (B) conjugated diene polymer particles are preferably crosslinked particles, and examples thereof include particles of at least one type of polymer selected from a rubber polymer (hereinafter also referred to as a "specific rubber polymer") selected from the group consisting of isoprene rubber, butadiene rubber, styrene-butadiene copolymer rubber, styrene-isoprene copolymer rubber, butadiene-isoprene copolymer rubber, styrene-butadiene-isoprene copolymer rubber, styrene-acrylonitrile-butadiene copolymer rubber, acrylonitrile-butadiene copolymer rubber, ethylene-α-olefin diene copolymer rubber, chloroprene rubber, and halogenated butyl rubber, and a graft polymer (hereinafter also referred to as a "specific rubber graft polymer") obtained by graft polymerizing a conjugated diene compound (hereinafter also referred to as a "conjugated diene monomer") and / or a styrene compound (hereinafter also referred to as a "styrene monomer") to the specific rubber polymer.

[0067] The specific rubber graft polymer includes a graft polymer obtained by graft polymerization of a conjugated diene monomer, a graft polymer obtained by graft polymerization of a styrene monomer, a graft polymer obtained by graft polymerization of a conjugated diene monomer and a styrene monomer, single Examples of the graft polymer include a graft polymer obtained by graft polymerization of a monomer.

[0068] Among these, butadiene rubber and styrene-butadiene copolymer rubber are preferred from the viewpoint of compounding processability.

[0069] The number average particle diameter of the (B) conjugated diene polymer particles is preferably 10 to 800 nm, more preferably 30 to 700 nm. Here, the number average particle diameter of the (B) conjugated diene polymer particles is a value measured by a light scattering method. When the (B) conjugated diene polymer particles have a number average particle diameter within the above range, the abrasion resistance and impact resilience of the resulting crosslinked polymer (tire) can be highly well-balanced.

[0070] Such conjugated diene polymer particles (B) can be produced by an emulsion polymerization method or a suspension polymerization method.

[0071] Specifically, when the (B) conjugated diene polymer particles are made of a specific rubber polymer, a monomer for obtaining the specific rubber polymer (hereinafter also referred to as a "monomer for forming rubber particles") can be polymerized in a medium using a polymerization initiator, an emulsifier, and a suspension stabilizer as necessary, to obtain rubber particles made of the specific rubber polymer.

[0072] In addition, when the (B) conjugated diene polymer particles are composed of a specific graft polymer, rubber particles composed of the graft polymer can be obtained by graft polymerizing a conjugated diene monomer and / or a styrene monomer to a specific rubber polymer obtained by emulsion polymerization or suspension polymerization.

[0073] As the monomer for forming rubber particles, an appropriate compound is used depending on the type of polymer to be formed. In order to form a crosslinked structure, for example, a polyfunctional compound having a polymerizable unsaturated group (hereinafter also referred to as a "compound for forming a crosslinked structure") is used.

[0074] Examples of the crosslinked structure forming compound include divinylbenzene, diallyl phthalate, ethylene glycol di(meth)acrylate, diethylene glycol di(meth)acrylate, propylene glycol di(meth)acrylate, propanediol di(meth)acrylate, butanediol di(meth)acrylate, hexanediol di(meth)acrylate, trimethylolpropane di(meth)acrylate, trimethylolpropane tri(meth)acrylate, pentaerythritol tri(meth)acrylate, pentaerythritol tetra(meth)acrylate, hydroquinone, polyethylene glycol di(meth)acrylate, polypropylene glycol di(meth)acrylate, etc. Among these, divinylbenzene and trimethylolpropane trimethacrylate are preferred from the viewpoint of versatility, i.e., cost reduction.

[0075] The ratio of the crosslinked structure forming compound in the rubber particle forming monomer is preferably 0.5 to 5 parts by mass with respect to 100 parts by mass of the total of the monomers (rubber particle forming monomers) to be polymerized. When the ratio of the crosslinked structure forming compound is within the above range, the resilience of the resulting crosslinked polymer (tire) may be good.

[0076] In addition, as the monomer for forming rubber particles, a functional group-containing compound (hereinafter also referred to as a "dispersibility improving compound") may be used for the purpose of improving the dispersibility of the (B) conjugated diene polymer particles in the rubber composition. That is, the (B) conjugated diene polymer particles may have a structural unit derived from the functional group-containing compound.

[0077] Specific examples of the dispersibility improving compound include hydroxyethyl methacrylate, hydroxypropyl methacrylate, hydroxybutyl methacrylate, ethylene glycol dimethacrylate, trimethylolpropane trimethacrylate, pentaerythritol tetramethacrylate, tert-butoxydimethylsilylstyrene, and isopropoxydimethylsilylstyrene. Among these, hydroxyethyl methacrylate is preferred from the viewpoint of the rolling resistance of the resulting crosslinked polymer (tire). Ethylene glycol dimethacrylate, trimethylolpropane trimethacrylate, and pentaerythritol tetramethacrylate also act as the crosslinked structure forming compound.

[0078] The proportion of the dispersibility improving compound used is preferably 0.5 to 10 parts by mass per 100 parts by mass of the total of the monomers (monomers for forming rubber particles) to be polymerized. When the proportion of the dispersibility improving compound used is within the above range, the resulting crosslinked polymer (tire) can have a highly well-balanced low loss property and impact resilience.

[0079] In the emulsion polymerization method, a radical polymerization initiator is used as a polymerization initiator. Examples of the radical polymerization initiator include organic peroxides such as benzoyl peroxide, lauroyl peroxide, tert-butyl hydroperoxide, cumene hydroperoxide, p-menthane hydroperoxide, di-tert-butyl peroxide, and dicumyl peroxide; Zo Diazo compounds such as bisisobutyronitrile, inorganic peroxides such as potassium persulfate, and redox catalysts such as combinations of these peroxides with ferrous sulfate can be used.

[0080] In the emulsion polymerization method, a polymerization initiator is used in combination with, for example, mercaptans such as tert-dodecyl mercaptan and n-dodecyl mercaptan, carbon tetrachloride, thioglycols, J Chain transfer agents such as terpenes, terpinolenes, and γ-terpinenes may also be used in combination.

[0081] The emulsifier used in the emulsion polymerization method may be an anionic surfactant, a nonionic surfactant, a cationic surfactant, an amphoteric surfactant, or a fluorine-based surfactant. The emulsifier may be used alone or in combination of two or more.

[0082] Examples of the suspension stabilizer used in the suspension polymerization method include polyvinyl alcohol, sodium polyacrylate, hydroxyethyl cellulose, etc. The suspension stabilizer may be used alone or in combination of two or more.

[0083] The content of the (B) conjugated diene polymer particles in the polymer composition according to the present embodiment is preferably 1 to 50 mass%, more preferably 3 to 40 mass%, and particularly preferably 5 to 30 mass%, when the total conjugated diene polymer components contained in the polymer composition are taken as 100 mass%. When the content of the (B) conjugated diene polymer particles is within the above range, the impact resilience of the resulting crosslinked polymer (tire) is likely to be improved.

[0084] 1.3.Other Ingredients The polymer composition according to the present embodiment may contain optional components as necessary in addition to the essential components, that is, (A) the conjugated diene polymer and (B) the conjugated diene polymer particles.

[0085] In the polymer component, other than the essential components (A) conjugated diene polymer and (B) conjugated diene polymer particles, other optional components such as natural rubber, butadiene rubber, butyl rubber, synthetic isoprene rubber, styrene-butadiene copolymer rubber, ethylene-α-olefin copolymer rubber, ethylene-α-olefin-diene copolymer rubber, acrylonitrile-butadiene copolymer rubber, chloroprene rubber, halogenated butyl rubber, and mixtures thereof may be contained. Among these, it is preferable to contain natural rubber or butadiene rubber because the obtained crosslinked polymer (tire) can achieve a high balance between low loss and wet grip properties while maintaining abrasion resistance. The proportion of other polymer components used is preferably 10 to 45 mass% in 100 mass% of the polymer component.

[0086] Examples of optional components other than the polymer component include fillers such as silica and carbon black, silane coupling agents, acidic compounds, crosslinking agents such as sulfur, extender oils, antioxidants, vulcanization assistants such as zinc oxide, vulcanization accelerators, waxes, and the like.

[0087] <Silica> As the silica, silica generally used as a filler can be used, but in order to obtain a crosslinked polymer (tire) having a highly well-balanced low loss property and impact resilience, synthetic silicic acid having a primary particle size of 50 nm or less is preferred.

[0088] The proportion of silica used is preferably 20 to 100 parts by mass relative to 100 parts by mass of the polymer component. When the silica content is within the above range, the resulting crosslinked polymer (tire) can have a highly well-balanced low loss property and impact resilience.

[0089] <Carbon black> Carbon black may be any carbon black commonly used as a filler. Specific examples of carbon black include GPF, FEF, HAF, ISAF, and SAF. Among these, ISAF, SAF, and HAF are preferred, and ISAF is more preferred.

[0090] The amount of carbon black used is preferably 0.5 to 100 parts by mass, and more preferably 1 to 50 parts by mass, based on 100 parts by mass of the polymer component.

[0091] <Silane coupling agent> Examples of the silane coupling agent include bis(3-triethoxysilylpropyl)tetrasulfide, bis(3-triethoxysilylpropyl)trisulfide, bis(3-triethoxysilylpropyl)disulfide, bis(2-triethoxysilylethyl)tetrasulfide, bis(3-trimethoxysilylpropyl)tetrasulfide, bis(2-trimethoxysilylethyl)tetrasulfide, 3-mercaptopropyltrimethoxysilane, 3-mercaptopropyltriethoxysilane, 2-mercaptoethyltrimethoxysilane, 2-mercaptoethyltriethoxysilane; 3-trimethoxysilylpropyl-N,N-dimethylthiocarbamoyltetrasulfide, 3-triethoxysilylpropyl-N,N-dimethylthiocarbamoyltetrasulfide, Examples of the compounds include bis(3-diethoxymethylsilylpropyl)tetrasulfide, 3-mercaptopropyldimethoxymethylsilane, dimethoxymethylsilylpropyl-N,N-dimethylthiocarbamoyl tetrasulfide, dimethoxymethylsilylpropyl-N,N-dimethylthiocarbamoyl tetrasulfide, dimethoxymethylsilylpropyl-benzothiazolyl tetrasulfide, 3-octanoylthio-1-propyltriethoxysilane, etc. These compounds can be used alone or in combination of two or more. Among these, bis(3-triethoxysilylpropyl) trisulfide, bis(3-triethoxysilylpropyl) disulfide, and 3-trimethoxysilylpropyl benzothiazolyl tetrasulfide are preferred from the viewpoint of improving reinforcing properties.

[0092] The proportion of the silane coupling agent used is preferably 0.5 to 20 parts by mass relative to 100 parts by mass of the filler component. When the proportion of the silane coupling agent used is within the above range, sufficient reinforcement and fracture resistance can be imparted to the crosslinked polymer formed from the polymer composition, and the abrasion resistance of the crosslinked polymer can be improved in some cases.

[0093] <Acidic compounds> As the acidic compound, saturated fatty acids having 12 to 24 carbon atoms and their metal salts are preferably used. Specific examples of the acidic compound include lauric acid, tridecylic acid, myristic acid, pentadecylic acid, palmitic acid, margaric acid, stearic acid, nonadecylic acid, arachidic acid, henicosylic acid, behenic acid, tricosylic acid, lignoceric acid, and calcium salts and zinc salts of these saturated fatty acids. These acidic compounds can be used alone or in combination of two or more. Among these, stearic acid is preferred. The proportion of the acidic compound used is preferably 0.3 to 15 parts by mass based on 100 parts by mass of the polymer component.

[0094] <Crosslinking agent> Examples of the crosslinking agent include sulfur, sulfur halides, organic peroxides, quinone dioximes, organic polyamine compounds, and alkylphenol resins having a methylol group. Among these, sulfur is usually used as the crosslinking agent. The proportion of the crosslinking agent used is preferably 0.1 to 10 parts by mass, more preferably 0.5 to 5 parts by mass, based on 100 parts by mass of the polymer component.

[0095] <Other additives> Examples of the extender oil include aromatic oil, naphthenic oil, paraffin oil, etc. The ratio of the extender oil used is preferably 0 to 50 parts by mass with respect to 100 parts by mass of the polymer component.

[0096] Examples of the antioxidant include N-(1,3-dimethylbutyl)-N'-phenyl-p-phenylenediamine, N-phenyl-N'-isopropyl-p-phenylenediamine, etc. The proportion of the antioxidant used is preferably 0.5 to 5 parts by mass based on 100 parts by mass of the polymer component.

[0097] An example of the vulcanization aid is zinc oxide, etc. The proportion of the vulcanization aid used is preferably 1 to 5 parts by mass with respect to 100 parts by mass of the polymer component.

[0098] As a vulcanization accelerator, Niji Examples of the vulcanization accelerator include compounds such as amines, aldehydes-amines, aldehydes-ammonias, thiazoles, sulfenamides, thioureas, thiurams, dithiocarbamates, and xanthates. Specific examples of preferred vulcanization accelerators include sulfenamide vulcanization accelerators such as N-cyclohexyl-2-benzothiazylsulfenamide (CBS) and N-tetra-butyl-2-benzothiazylsulfenamide (TBBS). The proportion of the vulcanization accelerator used is appropriately determined in consideration of the type and proportion of the basic compound, and is preferably 0.5 to 5 parts by mass relative to 100 parts by mass of the polymer component.

[0099] 1.4. Method for producing polymer composition The polymer composition according to the present embodiment can be prepared by kneading the above-mentioned components using a kneader such as a plastomill, a Banbury mixer, a roll, an internal mixer, etc. For example, it is preferably prepared by the following method.

[0100] <First stage mixing> In the first stage of kneading, it is preferable to knead the (A) conjugated diene polymer and (B) conjugated diene polymer particles together with a filler and a silane coupling agent, which are added as necessary. In addition, in the first stage of kneading, other polymers, extender oils, antiaging agents, etc. are also kneaded together as necessary. In addition, in the first stage of kneading, an acidic compound, which is considered to be preferably kneaded in the second stage of kneading, may be kneaded together.

[0101] By subjecting the filler to the first stage of kneading, the dispersibility of the filler tends to be improved, and the fuel economy performance of a tire (crosslinked polymer) formed from the obtained polymer composition may be improved.

[0102] In addition, when a silane coupling agent is used in the first stage of kneading, it is preferable to first knead (A) the conjugated diene polymer, (B) the conjugated diene polymer particles, other polymers, and, if necessary, a filler, and then add (post-add) the silane coupling agent and further knead.

[0103] By adding the silane coupling agent in the first mixing stage, the resulting polymer composition has better processability, and the crosslinked polymer formed from the polymer composition has better low loss properties. In addition, when the polymer composition contains silica as a filler, the dispersibility of the silica can be improved.

[0104] In the case of post-adding the silane coupling agent, the timing of adding the silane coupling agent is appropriately determined in consideration of the use ratios of (A) the conjugated diene-based polymer, (B) the conjugated diene-based polymer particles and other polymers depending on the type of silica, the use ratio of silica, and the kneading conditions.

[0105] In addition, in the case of post-adding the silane coupling agent, it is preferable to mix (A) the conjugated diene polymer, (B) the conjugated diene polymer particles, and other polymers and knead them for 0.5 to 10 minutes, and then add the silane coupling agent and knead them for 0.5 to 10 minutes.

[0106] The kneading machine used in the first stage of kneading may be an open or closed type kneading machine such as a plastomill, a Banbury mixer, a roll, an internal mixer, etc. In the first stage of kneading, the kneading temperature is 30°C to 180°C, and preferably 50°C to 160°C.

[0107] In addition, when a silane coupling agent is used in the first stage of kneading, the method is not limited to adding the silane coupling agent later and kneading, and the silane coupling agent may be kneaded together with all other components to be kneaded in the first stage to obtain a kneaded product containing the silane coupling agent. Also, a method may be used in which a master batch is prepared in which (A) a conjugated diene polymer, (B) conjugated diene polymer particles, silica as a filler, and a silane coupling agent are kneaded, and then other polymers and additives are added.

[0108] <Second stage mixing> The second stage of kneading is a step of adding at least a crosslinking agent to the kneaded product obtained in the first stage of kneading, and kneading the kneaded product and the crosslinking agent to obtain a polymer composition. In the second stage of kneading, it is preferable that an acidic compound is kneaded together with the kneaded product obtained in the first stage of kneading and the crosslinking agent. In addition, in the second stage of kneading, zinc oxide and a vulcanization accelerator are also kneaded together as necessary. In the second stage of kneading, the polymer composition is usually obtained by a method of simultaneously kneading all the components to be subjected to the second stage of kneading (specifically, the kneaded product obtained in the first stage of kneading, the crosslinking agent, and other components such as an acidic compound, zinc oxide, and a vulcanization accelerator, which are provided as necessary).

[0109] By providing an acidic compound in the second stage kneading, the resulting polymer composition has better processability, and the crosslinked polymer formed from the polymer composition has better low loss properties.

[0110] In the second stage of kneading, the kneading machine used in the first stage of kneading is used. In addition, in the second stage of kneading, the kneading temperature is set to 30°C to 130°C, and preferably 50°C to 110°C.

[0111] The polymer composition obtained by the above-mentioned production method is an unvulcanized polymer composition, and a crosslinked polymer is formed by subjecting it to a crosslinking treatment such as vulcanization.

[0112] 1.5.Applications The crosslinked polymer formed from the polymer composition according to the present embodiment is preferably used as a tire, specifically as a tire tread. The tire formed from the polymer composition according to the present embodiment has high strength in the tread and a desired shape in the tread, so that excellent performance can be obtained. The crosslinked polymer formed from the polymer composition according to the present embodiment can also be used as tire components other than the tread, anti-vibration rubber, fenders, belts, hoses, and other industrial products.

[0113] 2. Working Example Specific examples of the present invention will be described below, but the present invention is not limited to these examples. In the following Production Examples, Examples, and Comparative Examples, "%" is based on mass unless otherwise specified.

[0114] 2.1. (A) Production examples and physical property measurements of conjugated diene polymers <Production Example 1> In a nitrogen-purged autoclave reactor having an internal volume of 5 liters, 2500 g of cyclohexane, 50 g of tetrahydrofuran as a vinyl group content regulator (randomizer), and 125 g of styrene and 365 g of 1,3-butadiene as monomers were charged. After adjusting the temperature of the contents of the reactor to 10°C, 5.20 mmol of n-butyllithium was added as a polymerization initiator to start polymerization. The polymerization was carried out under adiabatic conditions, and the maximum temperature reached 85°C. When the polymerization conversion rate reached 99% (25 minutes after the start of polymerization), 10 g of 1,3-butadiene was added over 1 minute, and then 0.575 mmol of N,N,N',N'-tetrakis(3-triethoxysilylpropyl)-1,3-diaminopropane was added as a modifier and the reaction was carried out for 15 minutes. 4.40 g of 2,6-di-tert-butyl-p-cresol was added to the resulting polymer solution containing the modified conjugated diene copolymer. Next, the solvent was removed by steam stripping, and the mixture was dried with a heated roll adjusted to 110°C to obtain a modified conjugated diene copolymer (hereinafter also referred to as "SBR-1").

[0115] <Production Example 2> The same procedure was carried out as in Production Example 1, except that 1.15 mmol of N-(3-imidazolylpropyl)-N,N-bis(3-trimethoxysilylpropyl)amine was added instead of N,N,N',N'-tetrakis(3-triethoxysilylpropyl)-1,3-diaminopropane, to obtain a modified conjugated diene copolymer (hereinafter also referred to as "SBR-2").

[0116] <Production Example 3> The same procedure was carried out as in Production Example 1, except that 2.30 mmol of N,N-dimethylaminopropyltrimethoxysilane was added instead of N,N,N',N'-tetrakis(3-triethoxysilylpropyl)-1,3-diaminopropane, to obtain a conjugated diene copolymer (hereinafter also referred to as "SBR-3").

[0117] <Measurement of number average molecular weight (Mn) and weight average molecular weight (Mw)> For each of the polymers produced above, the polystyrene-equivalent number average molecular weight (Mn) and weight average molecular weight (Mw) were calculated from the retention time corresponding to the apex of the maximum peak in the GPC curve obtained under the following GPC conditions using gel permeation chromatography (GPC) ("HLC-8120" manufactured by Tosoh Corporation). (GPC conditions) Column: 2 pieces of "GMHXL" (manufactured by Tosoh Corporation) Column temperature: 40℃ Mobile phase: Tetrahydrofuran Flow rate: 1.0ml / min Sample concentration: 10mg / 20ml

[0118] <Measurement of vinyl content and bound styrene content> Vinyl content (%): 400MHz 1 It was measured by H-NMR measurement. Bound styrene content (%): 400MHz 1 The bound styrene content was measured by H-NMR measurement. The bound styrene content is a parameter equivalent to the aromatic vinyl content.

[0119] 2.2. (B) Example of production of conjugated diene polymer particles <Production Example 1> First, 200 parts by mass of water and 4.5 parts by mass of rosin acid soap were charged into a polymerization vessel, along with 63 parts by mass of 1,3-butadiene as monomers, 35 parts by mass of styrene, and 2 parts by mass of divinylbenzene as a crosslinking structure forming compound. After adjusting the temperature of this polymerization vessel to 5°C, 0.1 parts by mass of hydroperoxymethane, 0.07 parts by mass of sodium ethylenediaminetetraacetate, 0.05 parts by mass of ferrous sulfate heptahydrate, and 0.15 parts by mass of sodium formaldehyde sulfoxylate were added as radical polymerization initiators, and polymerization was carried out for 12 hours to obtain a polymer particle dispersion containing polymer particles made of styrene-butadiene copolymer. Next, the obtained polymer particle dispersion liquid was coagulated with sulfuric acid and a salt to form crumbs, and then dried with a hot air dryer to obtain conjugated diene-based polymer particles (hereinafter also referred to as "polymer particles (B1)") having an average particle size of 200 nm.

[0120] <Production Example 2> Conjugated diene-based polymer particles (hereinafter also referred to as "polymer particles (B2)") made of a styrene-butadiene copolymer and having an average particle size of 180 nm were obtained by the same method as in Production Example 1 of Polymer Particles (B1), except that in Production Example 1, 60 parts by mass of 1,3-butadiene, 33 parts by mass of styrene, 2 parts by mass of divinylbenzene as a compound for forming a crosslinked structure, and 5 parts by mass of hydroxyethyl methacrylate as a compound for improving dispersibility were used as monomers.

[0121] <Production Example 3> In the above Production Example 1, 60 parts by mass of 1,3-butadiene, 33 parts by mass of styrene, 2 parts by mass of trimethylolpropane trimethacrylate as a compound for forming a crosslinked structure and a compound for improving dispersibility, and 5 parts by mass of hydroxyethyl methacrylate as a compound for improving dispersibility were used as monomers. The same method as in Production Example 1 of polymer particles (B1) was used to obtain conjugated diene-based polymer particles (hereinafter also referred to as "polymer particles (B3)") having an average particle size of 200 nm, which are made of a styrene-butadiene copolymer.

[0122] <Production Example 4> Conjugated diene-based polymer particles made of butadiene rubber and having an average particle size of 200 nm (hereinafter also referred to as "polymer particles (B4)") were obtained in the same manner as in Production Example 1 of Polymer Particles (B1), except that in Production Example 1, 100 parts by mass of 1,3-butadiene was used as the monomer, 2 parts by mass of divinylbenzene as the compound for forming a crosslinked structure, and 5 parts by mass of hydroxyethyl methacrylate as the compound for improving dispersibility were used.

[0123] 2.3. Examples 1 to 6 and Comparative Examples 1 to 4 2.3.1. Preparation of polymer compositions and crosslinked polymers A polymer composition was produced by blending the components according to the blending recipe shown in Table 3 below and kneading them. The kneading was carried out in the following manner.

[0124] In the first stage of kneading, the polymer components shown in Table 3 below, silica, extender oil, carbon black, silane coupling agent, stearic acid, antioxidant, and zinc oxide were kneaded at a filling rate of 72% and a rotation speed of 60 rpm using a plastomill (capacity: 250 cc) equipped with a temperature control device. Next, in the second stage of kneading, the kneaded product obtained above was cooled to room temperature, and then sulfur and a vulcanization accelerator were kneaded to obtain the polymer compositions of Examples 1 to 6 and Comparative Examples 1 to 4.

[0125] Next, each of the obtained polymer compositions was molded and vulcanized in a vulcanizing press at 160° C. for a predetermined time to obtain each crosslinked polymer having a predetermined shape to be subjected to the following evaluation tests.

[0126] 2.3.2. Evaluation of cross-linked polymers The following evaluation tests were carried out on each of the obtained crosslinked polymers, and the results are shown in Table 3 below.

[0127] <Rebound elasticity> A Tripso type resilience tester (manufactured by Toyo Seiki Seisakusho) was used to measure at 50° C. Table 3 below shows the index when the value of the crosslinked polymer according to Comparative Example 1 is taken as 100, and according to the index, the larger the value, the greater and more favorable the resilience.

[0128] <Wet grip performance (0℃ tan δ)> Measurements were performed using a dynamic spectrometer (manufactured by Rheometrics, Inc., USA) under conditions of a tensile dynamic strain of 0.14%, an angular velocity of 100 radians per second, and a temperature of 0° C. Table 3 below shows the index when the value of the crosslinked polymer of Comparative Example 1 is taken as 100. According to the index, a larger value indicates a higher and more favorable wet skid resistance.

[0129] <Low hysteresis loss performance (50℃ tan δ)> A dynamic spectrometer (manufactured by Rheometrics, Inc., USA) was used to measure under conditions of a tensile dynamic strain of 0.7%, an angular velocity of 100 radians per second, and a temperature of 50° C. Table 3 below shows the index when the value of the crosslinked polymer of Comparative Example 1 is taken as 100, and according to the index, the larger the value, the greater the low hysteresis loss property and the better it is.

[0130] <Tensile strength> The crosslinked polymer obtained above was used as a measurement sample, and the 300% modulus (M300) was measured according to JIS K6251: 2010. Table 3 below shows the index when the value of the crosslinked polymer according to Comparative Example 1 is set to 100, and according to the index, the larger the value, the higher and more favorable the tensile strength is.

[0131] <Processability (compound Mooney viscosity)> The polymer composition before vulcanization was used as a measurement sample, and the Mooney viscosity was measured in accordance with JIS K6300-1:2013 using an L rotor under the conditions of 1 minute preheating, 4 minutes rotor operation time, and a temperature of 100° C. Table 3 below shows the index when the value of the polymer composition according to Comparative Example 1 is taken as 100, and according to the index, the larger the value, the better the processability.

[0132] 2.4.Evaluation Results The physical properties of each of the conjugated diene polymers synthesized above are shown in Table 1 below. The compounds used in the production of each of the conjugated diene polymer particles synthesized above and their usage ratios are shown in Table 2 below. The composition and evaluation results of each polymer composition are shown in Table 3 below.

[0133] [Table 1]

[0134] [Table 2]

[0135] [Table 3]

[0136] In Table 3, the numerical values ​​of each component in the polymer composition represent parts by mass. The following products were used as the materials shown in Table 3. BR: JSR Corporation, product name "BR-01", non-particle polybutadiene rubber Silica: Tosoh Silica Corporation, product name "Nipsil AQ", average primary particle size 15 nm Extension oil: Sankyo Yuka Kogyo Co., Ltd., product name "SNH46" Carbon black: Mitsubishi Chemical Corporation, product name "Diablack N339" Silane coupling agent: Evonik, product name "Si-69", bis(triethoxysilylpropyl)tetrasulfane Stearic acid: NOF Corporation, product name "Beads Stearic Acid Tsubaki" Anti-aging agent: Ouchi Shinko Chemical Industry Co., Ltd., product name "Nocrac 810NA", N-phenyl-N'-isopropyl-p-phenylenediamine Zinc oxide: Manufactured by Mitsui Mining & Smelting Co., Ltd., product name "Zinc Oxide No. 1" Vulcanization accelerator CZ: Manufactured by Ouchi Shinko Chemical Industry Co., Ltd., product name "Noccera CZ", N-cyclohexyl-2-benzothiazolyl sulfenamide Vulcanization accelerator D: Ouchi Shinko Chemical Industry Co., Ltd., product name "Noccera D", 1,3-diphenylguanidine Sulfur: Tsurumi Chemical Industry Co., Ltd., product name "Kinka-in oil-filled fine powder sulfur"

[0137] The results in Table 3 above show that the polymer compositions of Examples 1 to 6 containing (A) a conjugated diene polymer and (B) conjugated diene polymer particles have improved not only the rebound resilience, wet grip properties, and low hysteresis loss, but also the tensile strength and processability due to the branching characteristics of the imine, compared to the polymer composition of Comparative Example 1.

[0138] The present invention is not limited to the above-described embodiments, and various modifications are possible. The present invention includes configurations that are substantially the same as those described in the embodiments (for example, configurations with the same functions, methods, and results, or configurations with the same purpose and effect). The present invention also includes configurations in which non-essential parts of the configurations described in the above-described embodiments are replaced with other configurations. Furthermore, the present invention also includes configurations that have the same effects as the configurations described in the above-described embodiments, or that can achieve the same purpose. Furthermore, the present invention also includes configurations in which publicly known technology is added to the configurations described in the above-described embodiments.

Claims

1. (A) a conjugated diene polymer which is a reaction product between a polymer having an active polymerization terminal obtained by polymerizing a conjugated diene compound or a conjugated diene compound and an aromatic vinyl compound in the presence of an alkali metal compound or an alkaline earth metal compound, and a compound represented by any one of the following general formulas (1) to (3); (B) conjugated diene polymer particles which are crosslinked particles; A polymer composition comprising: 【Chemistry 1】 (In formula (1), A ２ is an imino group, an amide group, a (thio)carbonyl group, a (thio)carbonyloxy group, a sulfide or a polysulfide; ２ or represents a protected primary amino group, a protected secondary amino group, a tertiary amino group, a nitrile group, a pyridyl group, a (thio)epoxy group, a (thio)isocyanate group, a (thio)formyl group, a (thio)carboxylate ester, a metal salt of a (thio)carboxylate ester, a carboxylic acid halide compound, an imidazolyl group, or a group represented by the following formula (1a): ２ and L ３ each independently represents a single bond or a hydrocarbylene group having 1 to 20 carbon atoms; R ３ and R ４ each independently represents a hydrocarbyl group having 1 to 4 carbon atoms, n2 is 0 to 2, and m1 is 0 or 1. 【Chemistry 2】 (In formula (1a), L ３ , R ３ , R ４ and n2 are the same as in formula (1), and * is L ２ The binding site is shown.) 【Chemistry 3】 (In formula (2), A ３ each independently represents an imino group, an amide group, a secondary amino group, or a tertiary amino group; Z represents a t-valent group having 1 to 20 carbon atoms which may or may not contain a nitrogen atom; L ４ represents a single bond or a hydrocarbylene group having 1 to 20 carbon atoms; L ５ represents a hydrocarbylene group having 1 to 20 carbon atoms; R ５ and R ６ each independently represents a hydrocarbyl group having 1 to 4 carbon atoms, n3 is 0 or 1, and t is 2 or 3. 【Chemistry 4】 (In formula (3), R ７ and R ８ each independently represents a hydrocarbyl group having 1 to 20 carbon atoms; R ９ represents a hydrogen atom or a —CH ２ At least one of - represents a substituted alkyl group having 1 to 20 carbon atoms substituted with a group containing at least one element selected from the group consisting of silicon, nitrogen, phosphorus, oxygen, and sulfur, or represents an aromatic group having 6 to 20 carbon atoms containing at least one element selected from the group consisting of nitrogen, phosphorus, oxygen, and sulfur; R １０ represents an alkanediyl group having 1 to 20 carbon atoms. n4 is 1 or 2.

2. The polymer composition according to claim 1, wherein the conjugated diene polymer particles (B) are contained in an amount of 1% by mass or more and 50% by mass or less when the entire conjugated diene polymer component contained in the polymer composition is taken as 100% by mass.

3. 3. The polymer composition according to claim 1, wherein the conjugated diene polymer (A) has a weight average molecular weight in terms of polystyrene measured by gel permeation chromatography of 100,000 to 2,000,000.

4. 4. The polymer composition according to claim 1, wherein the conjugated diene polymer particles (B) have a number average particle size of 10 nm or more and 800 nm or less as measured by a light scattering method.

5. The polymer composition according to claim 1 , further comprising a crosslinking agent.

6. A crosslinked polymer produced using the polymer composition according to claim 5.

7. A tire using the crosslinked polymer according to claim 6.