Start-up process for the Fischer-Tropsch process

Abstract

The present invention relates generally to a Fischer-Tropsch process, and more particularly to a Fischer-Tropsch process for converting a feedstock comprising a mixture of hydrogen and carbon monoxide gases, preferably in the form of a synthesis gas mixture, into hydrocarbons by contacting the mixture with a cobalt-containing Fischer-Tropsch synthesis catalyst in a reactor at a pressure of at least 4.0 MPa absolute, the process comprising: i) supplying a feedstock comprising a mixture of hydrogen and carbon monoxide, preferably in the form of a synthesis gas mixture, to a reactor containing a cobalt-containing Fischer-Tropsch synthesis catalyst, wherein the pressure in the reactor is 3.5 MPa absolute or less; ii) maintaining the feed to the reactor, removing the hydrocarbon-containing product stream, and maintaining the pressure in the reactor at 3.5 MPa absolute or less for at least 15 hours, preferably at least 50 hours; The process begins with a start-up procedure that includes steps: [Selection diagram] None

Description

[Technical field]

[0001] The present invention relates to a process for converting a mixture of hydrogen and carbon monoxide into hydrocarbons, in particular to a Fischer-Tropsch process, which process begins with a start-up procedure to produce a catalyst with improved activity, thereby 5+ Improved selectivity to hydrocarbons and improved conversion can be obtained.The present invention further relates to catalysts produced by said start-up procedure, as well as methods and uses comprising such catalysts.

[0002] The conversion of synthesis gas to hydrocarbons by the Fischer-Tropsch process has been known for many years. The growing importance of alternative energy sources has seen renewed interest in the Fischer-Tropsch process as one of the more attractive, direct and environmentally acceptable routes to high quality transportation fuels.

[0003] Many metals, such as cobalt, nickel, iron, molybdenum, tungsten, thorium, ruthenium, rhenium and platinum, are known to be catalytically active, either alone or in combination, in the conversion of synthesis gas to hydrocarbons and their oxygenated derivatives. Of said metals, cobalt, nickel and iron have been most widely studied. Generally, metals are used in combination with support materials, the most common of which are alumina, silica and carbon.

[0004] In the preparation of cobalt-containing Fischer-Tropsch catalysts, a solid support is typically impregnated with a cobalt-containing compound (e.g., which may be an organometallic compound or an inorganic compound (e.g., Co(NO3)2·6H2O) by contacting it with a solution of the compound. The particular form of the cobalt-containing compound is generally selected such that it is capable of forming a cobalt oxide (e.g., CoO, Co2O3 or Co3O4) after a subsequent calcination / oxidation step. Following the generation of the supported cobalt oxide, a reduction step is required to form pure cobalt metal as the active catalytic species. The reduction step is therefore also commonly referred to as the activation step.

[0005] A variety of different methods have been proposed to activate new or regenerate spent Fischer-Tropsch catalysts. Historically, supported cobalt oxide catalyst precursors were reduced with hydrogen at high temperatures before being transferred to the reactor under inert conditions. Typically, reduction in the presence of hydrogen is carried out at temperatures above 300° C. For example, WO 03 / 035257 and WO 06 / 075216 disclose a two-stage reduction of Fischer-Tropsch catalyst precursors with hydrogen, with the final reduction stage being carried out with pure hydrogen gas at temperatures between 300° C. and 600° C.

[0006] C in the Fischer-Tropsch synthesis reaction 5+ It is generally understood that the selectivity of hydrocarbons is increased by operating at lower temperatures. By providing a more active catalyst, the same synthesis gas conversion can be achieved at lower temperatures while improving C 5+ Hydrocarbon selectivity can be benefited from. Thus, more active catalysts also represent a means to modify the selectivity of the Fischer-Tropsch synthesis by allowing for a reduction in the operating temperature.

[0007] In a typical Fischer-Tropsch process, a reactor is loaded with catalyst and a stream of synthesis gas is fed to the reactor. The temperature and pressure are then increased to obtain the desired reaction conditions, which are maintained throughout the process. It is generally understood that increased pressure can aid performance by increasing the partial pressure of the reactants within the pores of the catalyst. If a higher operating pressure is desired to achieve a particular activity, this pressure is used from the start of the process and maintained throughout.

[0008] Surprisingly, by implementing a start-up procedure in a Fischer-Tropsch reaction in which a pressure of 3.5 MPa or less is initially maintained and then the process is operated at a pressure of 4.0 MPa or greater, it has been found that the C 5+ It has been found that improved selectivity to hydrocarbons and improved conversion can be obtained.

[0009] The present invention thus provides a Fischer-Tropsch process for converting a feedstock comprising a mixture of hydrogen and carbon monoxide, preferably in the form of a synthesis gas mixture, into hydrocarbons by contacting a cobalt-containing Fischer-Tropsch synthesis catalyst with the mixture of hydrogen and carbon monoxide in a reactor at a pressure of at least 4.0 MPa absolute, the process being commenced by a start-up procedure comprising the steps of:

[0010] i) supplying a feedstock comprising a mixture of hydrogen and carbon monoxide, preferably in the form of a synthesis gas mixture, to a reactor containing a cobalt-containing Fischer-Tropsch synthesis catalyst, the pressure in the reactor being equal to or less than 3.5 MPa absolute; ii) maintaining the feed to the reactor, removing a product stream comprising hydrocarbons and maintaining the pressure in the reactor below 3.5 MPa absolute for at least 15 hours, preferably at least 50 hours.

[0011] The Fischer-Tropsch process of the present invention, which employs lower start-up pressures and higher operating pressures, has a substantially improved C2O3 content compared to comparable processes which operate only at lower or higher pressures, respectively, employed in the start-up procedure or subsequent operation of the Fischer-Tropsch process. 5+ It has been found to result in improved hydrocarbon selectivity and improved conversion.

[0012] Without wishing to be bound by any particular theory, it is believed that, despite the use of an at least partially preactivated catalyst, a final activation step to form the final state of the cobalt-containing catalyst occurs during the initial stages of the start-up procedure upon exposure to hydrogen and carbon monoxide. It is believed that by providing milder pressure conditions during this final activation of the catalyst, a more active catalyst is formed. Thus, when the catalyst is subsequently deployed in a Fischer-Tropsch process operated at a higher operating pressure, it may perform better than a comparable catalyst deployed in a Fischer-Tropsch process operated under comparable conditions that have not undergone a lower pressure start-up procedure. In particular, the low pressure start-up procedure may result in the production of increased levels of available active cobalt metal, or an otherwise favorable distribution of available active cobalt metal on the catalyst surface (i.e., physical differences in catalyst topography and / or morphology), resulting in superior C catalysis in subsequent Fischer-Tropsch reactions. 5+ This is particularly surprising as conventional processes using the same initial catalyst composition but at elevated pressures (i.e., the higher operating pressures used following the start-up procedure of the present invention) would be expected to exhibit comparable catalytic activity. The method of the present invention also outperforms processes that always operate at the initial low pressures used in the start-up procedure of the present invention, indicating that the combination of a particular start-up procedure and final operating pressure is important to achieve the benefits of the present invention.

[0013] Any suitable pressure less than 3.5 MPa may be used in steps i) and ii) of the process. In some embodiments, the pressure during steps i) and ii) of the start-up procedure is 3.3 MPa absolute or less, preferably 2.5 MPa or less, for example 1.5 MPa or less. Preferably, the pressure during steps i) and ii) of the start-up procedure is greater than 0.2 MPa, preferably greater than 0.5 MPa, for example greater than 1.0 MPa.

[0014] In a preferred embodiment, the pressure in the reactor for the Fischer-Tropsch process after completion of the start-up procedure is from 0.5 MPa to 3.5 MPa higher than the pressure in step i) and / or step ii), preferably from 0.5 MPa to 2.5 MPa higher, more preferably from 0.5 MPa to 1.5 MPa higher, most preferably from 0.75 MPa to 1.25 MPa higher, such as greater than 1.0 MPa.

[0015] Unless otherwise stated, it should be understood that pressures referred to herein are absolute pressures, with atmospheric pressure being 0.1 MPa.

[0016] The pressure in the reactor during step ii) of the start-up procedure can be maintained for any suitable amount of time, provided it is for a period of at least 15 hours, preferably at least 50 hours. It is understood that the exact time can vary depending on the other reaction conditions used. In general, it is desirable for steady state conditions to be obtained during step ii) of the start-up procedure. In a preferred embodiment, the pressure in the reactor in step ii) of the start-up procedure is maintained for 100 to 600 hours, more preferably 200 to 500 hours.

[0017] In some embodiments, the pressure and / or temperature in the reactor during step i) of the start-up procedure is different from the pressure and / or temperature in the reactor during step ii) of the start-up procedure.

[0018] In a preferred embodiment, the temperature in the reactor during the start-up procedure is different to the temperature in the reactor for the Fischer-Tropsch process carried out after completion of the start-up procedure, preferably the temperature in the reactor for the Fischer-Tropsch process carried out after completion of the start-up procedure is lower than the temperature in the reactor during the start-up procedure.

[0019] It will be appreciated that any suitable temperature may be used during the start-up procedure or subsequent Fischer-Tropsch processing that provides adequate conversion and does not risk thermal deformation of the catalyst. Suitably, the start-up procedure and / or the Fischer-Tropsch processing after the start-up procedure is carried out at a temperature between 100 and 400 oC, preferably 150 to 350 o C, more preferably 150 to 250 o C, and the temperature may be varied over the course of the start-up procedure and / or the Fischer-Tropsch process after the start-up procedure. For example, the temperature may be increased incrementally until the desired level of conversion is achieved. Alternatively, a substantially constant temperature may be applied.

[0020] Suitably, the pressure in the reactor during the Fischer-Tropsch process after completion of the start-up procedure is less than 10.0 MPa (absolute), preferably less than 7.5 MPa (absolute), more preferably less than 5.0 MPa (absolute).

[0021] Preferably, the start-up procedure is carried out in the same reactor in which the Fischer-Tropsch process is carried out after completion of the start-up procedure, although it will be appreciated that it is possible for these steps to be carried out in separate reactors.

[0022] In a preferred embodiment, the C during the Fischer-Tropsch process is performed after the start-up step is completed. 5+ The selectivity is at least 70%, preferably at least 75%, more preferably at least 80%.

[0023] In a preferred embodiment, the C during the Fischer-Tropsch process is performed after the start-up procedure is completed. 5+ The productivity is at least 90 g / Lh, preferably at least 100 g / Lh, more preferably at least 110 g / Lh. The productivity of the catalyst is determined by the amount of products containing 5 or more carbon atoms (C 5+ ) (grams) / catalyst volume (liters) / reaction time (hours).

[0024] In a preferred embodiment, the CH4 selectivity during the Fischer-Tropsch process performed after the start-up steps are completed is less than 15%, more preferably less than 13%.

[0025] In a preferred embodiment, the CO conversion during the Fischer-Tropsch process after completion of the start-up procedure is greater than 60%, preferably greater than 63%, more preferably greater than 65%.

[0026] CO conversion, CH4 selectivity, C 5+ Selectivity, and C 5+ It will be understood that productivity values ​​are average values ​​obtained at steady state, typically over a run time of about 200 to 700 hours.

[0027] At least prior to the start-up procedure of the method of the invention, the cobalt-containing catalyst referred to herein comprises at least partially reducible cobalt species, i.e. the main catalytic species, which can be converted to cobalt metal when reduced. In particular, it is preferred that the cobalt-containing catalyst comprises at least partially cobalt in the form of oxides, e.g. CoO, Co2O3 and / or Co3O4, at least prior to the start-up step. In some embodiments, prior to the start-up procedure of the method of the invention, the catalyst is partially reduced by any suitable method, e.g. using a hydrogen-containing stream, preferably a hydrogen / nitrogen stream. The partial reduction may be carried out before transferring the catalyst to the reactor in which the start-up procedure will be carried out, or may be carried out in the same reactor prior to the start-up procedure.

[0028] The cobalt-containing catalyst for use according to the method of the present invention may be a freshly prepared catalytic material. Alternatively, the cobalt-containing catalyst may be obtained from a cobalt-containing material that has previously been used to catalyze a Fischer-Tropsch reaction. If necessary, the cobalt-containing material that has previously been used to catalyze a Fischer-Tropsch reaction is subjected to a passivation step in order to convert at least a portion of the cobalt contained in the material to the oxide form.

[0029] Generally, cobalt-containing materials previously used in Fischer-Tropsch reactions can be passivated by treatment with a gas containing molecular oxygen, such as air, at elevated temperatures prior to use in accordance with the present invention. Such passivation desirably increases the proportion of cobalt oxide in the cobalt-containing materials previously used in Fischer-Tropsch reactions. The elevated temperatures for this passivation typically range from 30° C. to 500° C., preferably from 60° C. to 150° C. The treatment can be carried out at any desired pressure, with atmospheric pressure being preferred.

[0030] The optimum treatment time will depend on the history of the cobalt-containing material, the oxygen content of the gas used, and the treatment conditions. The treatment time should generally be long enough to remove any carbonaceous residues present on the cobalt-containing material, and is therefore particularly useful with cobalt-containing materials that have previously been used in Fischer-Tropsch reactions. Treatment times of at least 30 minutes, preferably 1 to 48 hours, are preferred.

[0031] The cobalt-containing Fischer-Tropsch catalyst may be unsupported or the support material may be supported on a conventional refractory support material such as silica, alumina, silica / alumina, ceria, titania, gallia, zirconia, magnesia, zinc oxide, and the like and mixtures thereof.

[0032] The cobalt-containing Fischer-Tropsch catalyst can be prepared by any suitable method known to those skilled in the art, for example, by impregnation, precipitation or gelation. Suitable Fischer-Tropsch catalysts can also be prepared by kneading or blending a support material such as alumina, silica or zirconia with either a soluble or insoluble cobalt compound before extruding, drying and calcining the product.

[0033] Suitable impregnation methods include, for example, impregnating the support material with a compound of cobalt that is thermally decomposable to the oxide form. Any suitable impregnation technique can be used, including the incipient wetness technique or the excess solution technique, both of which are well known in the art. The incipient wetness technique is so called because it requires that the volume of the impregnation solution be predetermined to provide the minimum volume of solution required just to wet the entire surface of the support without excess liquid. As the name suggests, the excess solution technique requires an excess of impregnation solution, after which the solvent is removed, usually by evaporation.

[0034] The impregnation solution may suitably be either an aqueous or non-aqueous organic solution of the thermally decomposable cobalt compound. Suitable non-aqueous organic solvents include, for example, alcohols, ketones, liquid paraffinic hydrocarbons and ethers. Alternatively, an aqueous organic solution of the thermally decomposable cobalt compound may be used, for example an aqueous alcohol solution.

[0035] Suitable soluble compounds include, for example, the nitrates, acetates or acetylacetonates of cobalt, preferably the nitrates. It is preferable to avoid the use of cobalt halides, as these halides have been found to be harmful.

[0036] Impregnation can be carried out with the support material in powder, granule or pelletized form, or impregnation can be carried out with the support material in the form of a shaped extrudate.

[0037] It will be appreciated that where a preformed support or extrudate is impregnated, the support may be contacted with the impregnation solution by any suitable means including, for example, vacuum impregnation, incipient wetness or immersion in excess liquid.

[0038] If a powder or granules of the carrier material is impregnated, the powder or granules may be mixed with the impregnation solution by any suitable means known to those skilled in the art, such as adding the powder or granules to a container of the impregnation solution and stirring. If an extrusion step follows immediately after the impregnation of the powder or granules, the mixture of the powder or granules and the impregnation solution may be further processed if it is not yet in a suitable form for extrusion. For example, the mixture may be kneaded to reduce the presence of larger particles that may not be easily extruded or that would otherwise impair the physical properties of the resulting extrudate. Kneading typically involves forming a paste suitable for shaping by extrusion. Any suitable kneading or kneading equipment known to those skilled in the art may be used for kneading in the context of the present invention. For example, a pestle and mortar may be suitably used in some applications, or a Simpson muller may be suitably used. Kneading is typically carried out for a period of 3 to 90 minutes, preferably 5 to 30 minutes. Kneading may suitably be carried out over a range of temperatures including ambient temperature. A preferred temperature range for kneading is 15°C to 50°C. The kneading may suitably be carried out at ambient pressure. It will be appreciated that complete removal of the binding solvent from the impregnation solution may be carried out to effect complete precipitation after extrusion.

[0039] In embodiments where the impregnated powder or granules are subjected to a calcination step to completely remove the solvent of the impregnation solution, the calcined powder or granules may also be further processed to form a mixture suitable for extrusion. For example, an extrudable paste may be formed by combining the calcined powder or granules with a suitable solvent, such as the solvent used for impregnation, preferably an aqueous solvent, and kneading as described above.

[0040] In some embodiments, the extrudate or preformed support is converted to a powder or granules. This can be accomplished by any suitable means known to those skilled in the art. For example, the impregnated support material may be a dry extrudate in some embodiments, and may be crushed and / or ground / milled. In a preferred embodiment, the powder formed has a median particle size (d50) of less than 50 μm, preferably less than 25 μm. If granules are formed instead, the median particle size (d50) of the granules is preferably 300-600 μm. The particle size (d50) can be suitably determined using a particle size analyzer (e.g., Microtrac S3500 Particle size analyzer).

[0041] Suitable precipitation methods for producing cobalt-containing catalysts include, for example, (1) precipitating cobalt with the formation of its insoluble pyrolyzable compounds using a precipitating agent comprising ammonium hydroxide, ammonium carbonate, ammonium bicarbonate, tetraalkylammonium hydroxide, or an organic amine at a temperature in the range of 0° C. to 100° C., and (2) recovering the precipitate obtained in step (1).

[0042] In contrast to the impregnation method, any soluble salt of cobalt can be used. Suitable salts include, for example, carboxylates, chlorides and nitrates. It is preferred to use an aqueous solution of the cobalt salt, although, if desired, for example, an aqueous alcoholic solution may be used.

[0043] Concerning the precipitating agent, in addition to ammonium carbonate, ammonium bicarbonate and ammonium hydroxide, tetraalkylammonium hydroxide and organic amines can also be used. The alkyl group of the tetraalkylammonium hydroxide can suitably be a C1-C4 alkyl group. A suitable organic amine is cyclohexylamine. Experiments have shown that the use of alkali metal precipitating agents results in very poor catalysts. It is therefore preferable to avoid the presence of alkali metals in the catalyst composition. Compositions free of alkali metals can be suitably prepared using either ammonium carbonate or ammonium bicarbonate, more preferably ammonium bicarbonate, as precipitating agent. Ammonium carbonate can be suitably used in commercial formulations that include a mixture of ammonium hydrogen carbonate and ammonium carbonate. Instead of using preformed carbonate or bicarbonate, it is possible to use precursors of these salts, such as soluble salts and carbon dioxide.

[0044] Regardless of the method for preparing the cobalt-containing material, it is usually necessary to convert the cobalt-containing material to a catalyst comprising cobalt in oxide form, which can then be partially reduced and / or used in accordance with the present invention. Calcination may be used to provide a catalyst comprising cobalt in oxide form, for example by causing thermal decomposition of a previously formed pyrolyzable compound of cobalt. Calcination may be carried out by any method known to those skilled in the art, for example in a fluidized bed or rotary kiln, suitably at a temperature in the range of 200° C. to 700° C. In some embodiments, calcination may be carried out as part of an integrated process that also includes reductive activation, or may be carried out in the same reactor.

[0045] In a preferred embodiment, the cobalt-containing Fischer-Tropsch synthesis catalyst comprises one or more promoters, dispersing aids, strength aids and / or binders.

[0046] The promoter, which may promote the reduction of the oxide of cobalt to cobalt metal, preferably at lower temperatures, is preferably selected from the list consisting of ruthenium, palladium, platinum, rhodium, rhenium, manganese, chromium, nickel, iron, molybdenum, boron, tungsten, zirconium, gallium, thorium, lanthanum, cerium and mixtures thereof.

[0047] The promoters are typically used at cobalt to promoter atomic ratios of up to 250:1, more preferably up to 125:1, even more preferably up to 25:1, and most preferably up to 10:1. The promoted catalysts can be prepared by a variety of methods including impregnation, extrusion, precipitation or gelation.

[0048] The promoter may be added at one or more of the catalyst preparation stages, including during precipitation as a soluble compound; precipitation by incipient wetness impregnation; or after calcination of the cobalt-containing precipitate.

[0049] The cobalt-containing catalyst may also be a composition further comprising zinc oxide, for example as described in U.S. Patent No. 4,826,800. Such compositions are preferably prepared by the preferred methods described therein.

[0050] Following the start-up procedure according to the method of the present invention, the Fischer-Tropsch process is carried out to convert a feedstock comprising a mixture of hydrogen and carbon monoxide gases into hydrocarbons, such as diesel or aviation fuels or precursors thereof. The Fischer-Tropsch synthesis of hydrocarbons from synthesis gas can be represented by Equation 1:

[0051]

number

[0052] As described above, the method of the present invention surprisingly achieves high C 5+ It has been found that cobalt-containing Fischer-Tropsch catalysts provide particularly active hydrocarbon selectivity, the hydrocarbon distribution being preferably from C5 to C9 gasoline and C10 -C 20 Includes diesel fraction.

[0053] In the feed gas used in steps i) and ii) and during the subsequent Fischer-Tropsch process, the volume ratio of hydrogen to carbon monoxide (H2:CO) in the feed (e.g., feed and / or reactor inlet) is preferably 0.5:1 to 5:1, more preferably 1:1 to 3:1, and most preferably 1.6:1 to 2.2:1. The gaseous reactant stream may also contain other diluent / inert gas components such as nitrogen, carbon dioxide, water, methane, and other saturated and / or unsaturated light hydrocarbons. In some embodiments, such diluent / inert gas components may be present in a concentration of 1% to 75% by volume, 5% to 60% by volume, or 10% to 50% by volume. In other embodiments, diluent / inert gas components that may be present in the gaseous reactant stream in addition to the reactant gas are present in a concentration of less than 50% by volume, such as less than 30% by volume, or less than 20% by volume. As will be appreciated, the diluent / inert gas in the product effluent stream obtained from the reactor may be recycled to the gaseous reactant stream or may be used in other downstream processes if desired.

[0054] The gaseous reactants for the start-up procedure and / or the subsequent Fischer-Tropsch process following the start-up procedure may be fed to the reactor separately or premixed (e.g., as in the case of synthesis gas). They may all initially contact the solid catalyst at the same portion of the solid catalyst or may be added at different locations on the solid catalyst. The initial point of contact of one or more reactants with the solid catalyst is the point at which all reactants first contact each other in the gas phase and in the presence of the solid catalyst. Preferably, one or more gaseous reactants flow cocurrently over the solid catalyst.

[0055] The gaseous reactant mixture used in the start-up procedure and / or in a subsequent Fischer-Tropsch process following the start-up procedure may comprise recycled materials extracted from elsewhere, for example unreacted reactants separated from any preceding catalytic reduction step.

[0056] The feed gas used in steps i) and ii) of the start-up process and during the subsequent Fischer-Tropsch process is preferably used for 100 to 10,000 h. -1 (Gas volume converted to standard temperature and standard pressure) range, preferably 125 to 9000h -1 In some preferred embodiments, the feed gas is passed over the catalyst bed at a gas hourly space velocity (GHSV) in the range of 5000 to 9000 h -1 , for example 6000~8000h -1 In another preferred embodiment, the feed gas is passed over the catalyst bed at a gas hourly space velocity (GHSV) of 1000 to 2000 h -1 , more preferably 1200 to 1500 hours -1 , e.g. 1250 h -1 The catalyst bed is passed over at a gas hourly space velocity (GHSV) of 1000 MPa.

[0057] As is well known in the art, the synthesis gas preferably used for the Fischer-Tropsch reaction mainly contains carbon monoxide and hydrogen, and possibly small amounts of carbon dioxide, nitrogen and other inert gases, depending on its origin and degree of purity. Methods for preparing synthesis gas are well established in the art and usually involve partial oxidation of carbonaceous materials, such as coal. Alternatively, synthesis gas can be prepared, for example, by catalytic steam reforming of methane. The ratio of carbon monoxide to hydrogen present in the synthesis gas can be appropriately modified by the addition of either carbon monoxide or hydrogen, or can be adjusted by so-called shift reactions, well known to those skilled in the art.

[0058] The start-up procedure and / or the subsequent Fischer-Tropsch process following the start-up procedure is preferably carried out continuously in a fixed bed, fluidized bed or slurry phase reactor. When the cobalt-containing Fischer-Tropsch catalyst is used in a fixed bed process, the particle size should be of a shape and dimension such that an acceptable pressure drop is achieved over the catalyst bed. A person skilled in the art can determine the optimum particle size for use in such a fixed bed reactor. Particles of the desired shape and size can be obtained by extrusion of a slurry, to which an extrusion aid and / or binder can optionally be added.

[0059] Naturally, C. 5+ Cobalt-containing Fischer-Tropsch synthesis catalysts may be advantageously used in subsequent Fischer-Tropsch processes where improved hydrocarbon activity or selectivity is desired.

[0060] Thus, according to a further aspect of the present invention there is provided a cobalt-containing Fischer-Tropsch synthesis catalyst, preferably obtained by the start-up procedure described hereinbefore.

[0061] It will be understood that the cobalt-containing Fischer-Tropsch synthesis catalyst may be an unsupported catalyst or a supported catalyst, as previously described herein.

[0062] According to a further aspect of the present invention, C 5+ There is provided the use of a cobalt-containing Fischer-Tropsch synthesis catalyst as defined herein above for increasing the selectivity of a Fischer-Tropsch process for the production of hydrocarbons and / or for increasing the conversion in a Fischer-Tropsch process.

[0063] According to yet another aspect of the present invention, in a Fischer-Tropsch process, 5+There is provided a process for increasing the selectivity and / or increasing the conversion of a Fischer-Tropsch process for the production of hydrocarbons, the process comprising the step of feeding a cobalt-containing Fischer-Tropsch synthesis catalyst as defined herein above to the Fischer-Tropsch process.

[0064] The invention will now be further described by reference to the following examples, which are merely illustrative. In the examples, CO conversion is defined as moles of CO used / moles of CO fed x 100, and carbon selectivity is defined as moles of CO attributable to a particular product / moles of CO converted x 100. Unless otherwise stated, temperatures referred to in the examples are application temperatures and not catalyst / bed temperatures. Unless otherwise stated, pressures referred to in the examples are absolute pressures.

[0065] Example 1 Catalyst preparation

[0066] The catalyst was prepared by impregnating a zinc oxide support with a sufficient amount of aqueous cobalt nitrate solution to achieve a cobalt loading of 10.5 wt. % (which is 10.5 wt. % of cobalt atoms compared to the total mass of the calcined but not yet reduced catalyst). The impregnated powder was extruded, dried and calcined.

[0067] Example 2 (present invention) Startup procedure 3.3MPa, operation 4.3MPa

[0068] 10 mL of the catalyst prepared in Example 1 was loaded into a microreactor and the reduction was completed under hydrogen in the microreactor to form an at least partially reduced catalyst (10 h, 240 °C, 50% H2 / N2, 0.7 MPa). A mixture of hydrogen and carbon monoxide (H2 / CO = 1.8) containing an additional 18 vol.% nitrogen was then added and this was cooled to 1250 h. -1The gas was introduced into the reactor at a gas hourly space velocity (GHSV) of 10 ...

[0069] Example 3 (Comparative Example) 4.3MPa steady operation

[0070] The procedure of Example 2 was followed except that a temperature of 216° C. and a pressure of 4.3 MPa were maintained from start-up and throughout the Fischer-Tropsch synthesis.

[0071] Example 4 (present invention) Startup procedure 3.3MPa, operation 4.3MPa

[0072] The procedure of Example 2 was followed except that the applied temperatures were 229° C. during the start-up procedure and 219° C. during the subsequent Fischer-Tropsch synthesis.

[0073] Example 5 (Comparative Example) 4.3MPa steady operation

[0074] The procedure of Example 3 was followed except that the application temperature was 219°C throughout.

[0075] Example 6 (present invention) Startup procedure 3.3MPa, operation 4.3MPa

[0076] The procedure of Example 2 was followed, except that the temperature during the start-up procedure was 212°C and the temperature during the Fischer-Tropsch synthesis was 213°C.

[0077] Example 7 (present invention) Startup procedure 3.3MPa, operation 4.3MPa

[0078] The process of Example 2 was monitored on-stream for 1560 hours at an application temperature of 210°C.

[0079] Example 8 (Comparative Example) 4.3MPa steady operation

[0080] The process of Example 3 was monitored on-stream for 1560 hours at an application temperature of 214°C.

[0081] Example 9 (Comparative Example) Steady operation at 4.3MPa, then reduced to 3.3MPa

[0082] The process of Example 8, operating at 4.3 MPa, was adjusted to reduce the pressure from 4.3 MPa to 3.3 MPa. Data from Example 9 relates to time at 3.3 MPa.

[0083] Example 10 (Comparative Example) 3.3MPa steady operation

[0084] The procedure of Example 3 was followed except that the temperature was 213° C. and the pressure was 3.3 MPa throughout.

[0085] Example 11 (present invention) Startup procedure 1.3MPa, operation 4.3MPa

[0086] Pressure: 1.3MPa, temperature: 220℃, GHVS startup operation: 800 h -1 The procedure of Example 2 was followed, except that the temperature was 208°C.

[0087] Example 12 (present invention) Startup procedure 2.3MPa, operation 4.3MPa

[0088] The procedure of Example 2 was followed except that the pressure was 2.3 MPa, the temperature was 220° C. during the start-up procedure and 205° C. during the Fischer-Tropsch synthesis.

[0089] CO conversion, CH4 selectivity, and C 5+ Selectivity data was compiled and the results for the above examples are shown in Table 1 below. The effluent gases were sampled and analyzed by on-line mass spectrometry. 5+ Selectivity is determined by the difference between the C1-C4 components in the gas phase. CH4 selectivity is determined by the difference between the C1-C4 components in the gas phase. 2+ The CO conversion, CH4 selectivity, and C 5+ Selectivity values ​​are average values ​​obtained at steady state over a period of 200 to 700 hours.

[0090] [Table 1]

[0091] The results in Table 1 show that significant improvements can be obtained by using the start-up procedure at pressures below 3.5 MPa, followed by operation at pressures of 4.0 MPa or higher. For example, at comparable levels of CO conversion, processes using the start-up method of the present invention advantageously achieve a C 5+ For example, comparing Examples 2 and 3, when the start-up method of the present invention (i.e., Example 3) is not followed, a higher reaction temperature is required to achieve the same CO conversion, which results in higher CH4 selectivity and lower C 5+ As mentioned above, this reduction in CH4 selectivity and the 5+ Increased selectivity is essential to improve the commercial viability of Fischer-Tropsch. Comparison of Examples 7 and 8 also shows that this advantageous selectivity is maintained over longer periods of time, with improvements still observed after 1560 hours of operation.

[0092] Furthermore, a comparison of Examples 4 and 5 shows that when the same elevated temperature is used during Fischer-Tropsch synthesis, but the present start-up procedure is used (Example 4), all parameters show improvements over the constant pressure process (Example 5). Example 6 also demonstrates improved results at intermediate temperatures between Examples 2 and 4.

[0093] Example 9 shows that by moving from a constant 4.3 MPa process to 3.3 MPa, the conversion rate was significantly reduced and 5+ Selectivity is poor, confirming that the start-up procedure is important, not the process pressure itself. Similarly, Example 10 shows that by simply starting the process at 3.3 MPa and maintaining this pressure, C 5+ This indicates that the selectivity decreases and the CH4 selectivity increases.

[0094] Examples 11 and 12 show that the start-up procedure can be equally carried out at lower pressures of 1.3 MPa and 2.3 MPa, respectively, and shows improved selectivity compared to the start-up procedure at 3.3 MPa.

[0095] Comparing Example 10 with Examples 3 and 5, it is shown that higher methane selectivity is observed for the process at 3.3 MPa, but the overall catalyst activity is higher, requiring lower temperatures to reach the same level of conversion. This indicates that the catalyst undergoes better final activation at 3.3 MPa than at 4.3 MPa, which is exploited in the present invention by subsequently increasing the pressure after the initial low pressure start-up procedure.

Claims

1. A Fischer-Tropsch process for converting a feedstock comprising a mixture of hydrogen and carbon monoxide gases into hydrocarbons, the process comprising: i) supplying a feedstock comprising a mixture of hydrogen and carbon monoxide gas to a reactor containing a cobalt-containing Fischer-Tropsch synthesis catalyst, the pressure in the reactor being equal to or less than 3.5 MPa absolute; ii) commencing the Fischer-Tropsch process by a start-up procedure comprising the steps of maintaining the feed to the reactor, removing a product stream comprising hydrocarbons and maintaining the pressure in the reactor at or below 3.5 MPa absolute for at least 15 hours; Further, the cobalt-containing Fischer-Tropsch synthesis catalyst is contacted in a reactor with a mixture of hydrogen and carbon monoxide at a pressure of at least 4.0 MPa absolute and at a temperature below the temperature in the reactor at the start of the start-up procedure, wherein prior to step i), the cobalt-containing Fischer-Tropsch synthesis catalyst is only partially activated and comprises one or more reducible cobalt species, and wherein the feed used in steps i) and ii) of the start-up procedure and during the subsequent Fischer-Tropsch process is a Fischer-Tropsch process conducted having a volumetric ratio of H 2 :CO in the range of 1.6:1 to 2.2:

1.

2. C in step ii) ５＋ Selectivity is C in a comparative method carried out under the conditions of step ii) without prior carrying out step i). ５＋ The method of claim 1, wherein the selectivity is greater than or equal to 100%.

3. 2. The method according to claim 1, wherein the pressure during steps i) and ii) of the start-up procedure is less than or equal to 3.3 MPa absolute and / or the pressure during steps i) and ii) of the start-up procedure is greater than 0.2 MPa.

4. 2. The process of claim 1, wherein the pressure in the reactor for the Fischer-Tropsch process after completion of the start-up procedure is from 0.5 MPa to 3.5 MPa higher than the pressure in step i) and / or step ii).

5. The process according to any one of claims 1 to 4, wherein the pressure in the reactor in step ii) of the start-up procedure is maintained for a period of from 100 to 600 hours.

6. The process of any one of claims 1 to 5, wherein the pressure in the reactor during the Fischer-Tropsch process after completion of the start-up procedure is less than 10.0 MPa absolute.

7. A process according to any one of the preceding claims, wherein the start-up procedure and / or the Fischer-Tropsch process following the start-up procedure is carried out in the range of from 100 to 400°C.

8. The process of any one of claims 1 to 7, wherein the start-up procedure is carried out in the same reactor in which the Fischer-Tropsch process is carried out after completion of the start-up procedure.

9. A process according to any one of claims 1 to 8, wherein the cobalt-containing Fischer-Tropsch synthesis catalyst is a supported catalyst.

10. 10. The method of claim 9, wherein the support material comprises a material selected from any of silica, alumina, silica / alumina, ceria, titania, gallia, zirconia, magnesia, zinc oxide, and mixtures thereof.

11. A process according to any one of claims 1 to 10, wherein the cobalt-containing Fischer-Tropsch synthesis catalyst comprises one or more promoters, dispersing aids, strength aids and / or binders.

12. In a Fischer-Tropsch process carried out after completion of the start-up procedure, ５＋ and / or C ５＋ Productivity is at least 90 g / L.h. and / or CH ４ The process according to any one of claims 1 to 11, wherein the selectivity is less than 15%.

13. The process of any one of claims 1 to 12, wherein the CO conversion is greater than 60% in the Fischer-Tropsch process carried out after completion of the start-up procedure.

14. A process according to any one of the preceding claims, wherein the mixture of hydrogen and carbon monoxide gases is in the form of a synthesis gas mixture.

15. C ５＋ Use of a cobalt-containing Fischer-Tropsch synthesis catalyst obtainable by the start-up procedure according to any one of claims 1 to 5 or claim 14 or the cobalt-containing Fischer-Tropsch synthesis catalyst which is the supported catalyst according to claim 9 or claim 10 for improving the selectivity of a Fischer-Tropsch process for the production of hydrocarbons and / or for improving the conversion in a Fischer-Tropsch process.

16. A process for producing a Fischer-Tropsch synthesis catalyst, comprising the step of: supplying a cobalt-containing Fischer-Tropsch synthesis catalyst obtained by the starting means according to any one of claims 1 to 5 or claim 14, or the cobalt-containing Fischer-Tropsch synthesis catalyst which is the supported catalyst according to claim 9 or claim 10, to a Fischer-Tropsch process. ５＋ A method for improving the selectivity of a Fischer-Tropsch process for the production of hydrocarbons and / or for improving the conversion in a Fischer-Tropsch process.