Optimization of electrochemical cells

Abstract

A system and method for optimizing electrochemical cells containing electrodes that use coordination compounds by adjusting the water content within a desired water content profile that includes sufficient coordinated water and reduces non-coordinating water below a desired target. The process can improve the performance of cells containing one or more TMCCC materials by providing an optimal amount of residual moisture (RM) in the electrode. Too much RM can result in sufficient non-coordinating water, including mobile water, resulting in poor cell performance. Too little RM can result in poor performance of the TMCCC electrode. However, by fine-tuning the RM of the electrode, an optimal balance of electrode and cell performance characteristics can be achieved.

Description

[Technical Field]

[0001] [CROSS-REFERENCE TO RELATED APPLICATIONS] This application claims priority from U.S. Application No. 16 / 708,213, filed December 9, 2019, the contents of which are incorporated herein by reference in their entirety for all purposes.

[0002] The present invention relates generally to electrochemical cells that utilize coordination compounds in one or more electrodes, and more particularly, but not exclusively, to improving electrochemical cell operation by controlling the water content of electrochemical cells having one or more electrodes that include one or more transition metal cyanide coordination compounds. [Background technology]

[0003] Subject matter discussed in the Background section should not be assumed to be prior art merely because it is mentioned in the Background section. Similarly, problems mentioned in the Background section, or problems related to the subject matter in the Background section, should not be assumed to have been recognized in the prior art. The subject matter in the Background section merely represents various approaches that may themselves be inventions.

[0004] Electrochemical cells are often considered to use electrode materials that fall into one of two categories: (i) materials containing aqueous electrolytes or (ii) materials containing anhydrous electrolytes. Examples of the former include lead-acid cells and nickel / metal hydride cells. Examples of the latter include lithium-ion cells. It is well known that the presence of trace amounts of water impurities in cells containing anhydrous electrolytes, even at concentrations as low as parts per million, can degrade cell performance in one or more performance metrics. Therefore, the solution is to implement rigorous dry-room processes for preparing the cell components and assembling the cell. Electrode components are kept as dry as possible in an effort to remove as many traces of water as possible.

[0005] For example, each cell material is dried individually in a special room with water / moisture control (dry room). These individually dried materials are then transported to an assembly area to create individual cells, which are then assembled into stack assemblies (cell stacks). This process increases the complexity, risk, and resource costs in the manufacture of these cell stacks.

[0006] Regarding the water content of cells containing anhydrous electrolytes, reference is made to Imhof's reference [1], where Figure 6 shows that increasing the amount of ppm-level water impurities reduces the reversibility of the charge / discharge process of graphite electrodes in Li-ion cells. This is the conclusion on page 1087 of reference [1]: "Experiments with EC / DMC-based electrolytes containing various amounts of water have shown that the reversibility of the Li+ intercalation process decreases with increasing water content."

[0007] Some materials used as electrodes in electrochemical cells can include the use of transition metal cyanide coordination compounds (TMCCCs). Reference [2] treats TMCCC materials as belonging to the (ii) anhydrous category. Reference [2] describes methods for drying TMCCC electrode materials to improve cell performance. In particular, Reference [2] teaches manganese hexacyanoferrate (MnHCF) TMCCC electrode materials that are dried to a sufficiently low residual moisture (RM) that all interstitial water is removed. When this occurs, the MnHCF material undergoes a phase transition from a cubic to a rhombohedral phase (column 8). When this phase change occurs, all of the electrochemical capacity of the MnHCF electrode is captured in a single charge / discharge plateau. Having a single reaction plateau is desirable because it allows the electrochemical cell to operate over a narrower voltage range, reducing the cost and complexity of integrating the cell into other electronic systems. To achieve this result, reference [2] further describes the use of a vacuum drying process in which the vacuum pressure is less than 0.1 torr (column 7 and claim 1).

[0008] Claim 1 of Reference [2] claims a TMCCC in which water may be present over a range (z is in the range of 0-3.5). However, column 8 details that to achieve a rhombohedral phase with a single reaction plateau, all of the interstitial water must be removed from the structure. Furthermore, in Reference [3], the same inventors show that the rhombohedral phase with a single reaction plateau is completely anhydrous. Throughout Reference [3], the single-plateau phase is referred to as "anhydrous" in contrast to the "hydrated" phase with two reaction plateaus. Furthermore, in the Supplementary Information of Reference [3], Figure S2 shows that the "anhydrous" phase does not contain water. In other words, a sample of MnHCF that undergoes a phase transition upon dehydration does not contain water tightly bound to the lattice; all water present before drying is interstitial water. Therefore, one skilled in the art would view the teachings of References [2] and [3] as indicating that a single rhombohedral plateau phase is achieved when all water is removed from the structure, or, in the terms relevant to claim 1 of Reference [2], when z = 0.

[0009] It should be noted that the term "anhydride" used in Reference [3] is not a commonly used term. It is usually defined as the anhydrous form of a material that typically contains water. A reasonable interpretation of Reference [3] is that "anhydride" is synonymous with "anhydrous," meaning a material that contains no water or only negligible amounts of water as a trace impurity. In contrast, if Reference [3] were to refer to vacuum-dried MnHCF as "dehydrated," it would generally be understood to mean that either some or all of the water initially present in the material has been removed. Considering Figure S2 above, the authors' use of "anhydride" rather than "dehydrated" indicates their intention to express that all water has been removed from the material.

[0010] Contrary to these disclosures, TMCCC materials used as electrodes in electrochemical cells may not belong exclusively to these aqueous or anhydrous classes. Optimizing the operation of electrochemical cells containing TMCCC materials by managing water content may be more complex than previously understood by conventional battery manufacturing techniques.

[0011] Systems and methods for optimizing electrochemical cells that include electrodes that use coordination compounds would be beneficial. Summary of the Invention

[0012] Systems and methods for optimizing electrochemical cells including electrodes that utilize coordination compounds are disclosed. The following summary of the invention is provided to facilitate understanding of some technical features related to managing the water content of electrodes that include TMCCC materials and is not intended to be a complete description of the invention. A full understanding of the various aspects of the invention can be obtained by reading the entire specification, claims, drawings, and abstract as a whole. In addition to TMCCC materials, the present invention is applicable to other coordination compounds, particularly those that include water arranged in crystalline structure sites and water arranged in a non-coordinated manner.

[0013] One embodiment of the present invention involves a new type of battery cell based on electrodes containing transition metal cyanide coordination compound (TMCCC) materials. These TMCCC materials naturally contain water. Some of the water they contain is tightly bound within the material's crystal structure (e.g., lattice-bound), some interstitial water can reversibly enter and exit the electrode upon charging and discharging, and some water can be bound to various surfaces of the TMCCC material's particles (collectively, this non-lattice-bound water may be referred to herein as non-coordinated water). Some of the non-coordinated water can enter and exit the TMCCC material and thus undergo chemical or electrochemical reactions with other cell components, potentially causing deterioration of cell performance. Based on references [1], [2], and [3], it is expected that removing all water from the TMCCC material would improve electrode and cell performance by eliminating these undesirable reactions. However, surprising results have been demonstrated that complete dehydration of the TMCCC material, which involves removing water tightly bound within the crystal structure, actually worsens the performance of the fully dehydrated TMCCC material. It should be noted that References [1], [2], and [3] do not appear to teach or discuss non-coordinated water, i.e., any water other than pore water. Other types of water include surface water and water present in all pores within the TMCCC structure, including micropores. There are several possible reasons why these references do not discuss this type of water content, including the possibility that it was not considered relevant / impactful or its existence was not recognized.

[0014] One embodiment of the present invention describes a process by which the performance of a cell containing one or more TMCCC materials can be optimized by resulting in an electrode with an optimal amount of residual moisture (RM). Too much RM can result in sufficient non-coordinating water, including mobile water, to degrade cell performance. Too little RM can result in poor TMCCC electrode performance. However, by fine-tuning the electrode's RM, an optimal balance of electrode and cell performance characteristics can be achieved. The water content can be adjusted by partial dehydration and / or partial resorption of water to achieve a desired RM that is greater than anhydrous but less than the water content of as-synthesized, unprocessed TMCCC material. This intermediate amount or concentration of electrode water content is an aspect of some embodiments of the present invention.

[0015] An embodiment of the present invention can include improved manufacturing. Some processing steps can be simplified because the required water removal process may be less aggressive. For example, one aspect of the present invention involves assembling an entire electrochemical cell, or assembling such cells into a cell stack, detecting that the water content of the TMCCC material in at least one electrode of one or more cells is outside of a desired range, and optimizing the water content within the assembled cell or cell stack. This is in contrast to dehydrating / hydrating individual materials and then assembling using the dehydrated / hydrated materials.

[0016] An embodiment of the present invention can include a method for optimizing cell performance that includes dehydrating / hydrating at least one electrode to a controlled residual moisture. Further embodiments can include target ranges of residual moisture, dehydration / hydration conditions / apparatus, etc.

[0017] An embodiment of the present invention can include a composition of matter electrochemical cell having one or more electrodes containing a set, non-zero amount of water, where the specific amount of water (i.e., greater than zero and less than a threshold) is distinct from an electrochemical cell having one or more electrodes containing TMCCC material with an undefined amount of water, n>0.

[0018] One embodiment of the present invention can include an electrode comprising a coordination compound, an electrochemical cell having one or more electrodes of such a material, and / or an electrochemical cell stack comprising one or more such electrochemical cells, where the coordination compound (e.g., a TMCCC material) has a crystalline structure with residual water (RM) present in at least two forms, a first form bound to the crystalline structure and a second form free from the crystalline structure (e.g., non-coordinating water), and the desired RM comprises the first form fully maintained to preserve the crystalline structure and an optimally selected amount of the second form. The water content of a TMCCC material is always greater than zero, but has a maximum value necessary or desired for the crystal / lattice structure. The presence of additional non-coordinating water in a TMCCC material beyond the amount contained in the desired RM is considered an undesirable impurity, the presence of which can degrade operation and is desirably reduced, similar to other undesirable impurities.

[0019] One embodiment of the present invention involves improving the performance of an electrochemical cell having at least one electrode comprising a TMCCC material having a water content outside of a preferred water range, with a sufficient amount of residual water in a first form to maintain the crystalline structure and electrochemical properties of the material, and as little residual water in a second form as possible to minimize non-coordinating or other non-crystalline water, by adjusting the total residual water of one or more electrodes within the preferred water range.

[0020] One embodiment of the present invention can include a method of fabricating an electrochemical cell including a cell stack including one or more anodes, one or more separators, and one or more cathodes. The method includes a dehydration / hydration step of exposing the cell stack to a certain temperature and a certain pressure over a certain period of time. Either the anode or the cathode includes a first TMCCC material and includes a first residual moisture RM1. The dehydration / hydration step reduces the moisture content of the TMCCC-containing electrode to RM2 < RM1. The first TMCCC material is represented by the formula AxPy[R(CN)6]z(H2O)n, where A includes one or more alkali cations, P and R include one or more divalent or trivalent transition metal cations, 0.5 < z < 1, n = 6*(1 - z) + m, n > 0, 6*(1 - z) is the amount of lattice-bound water, m is the amount of non-coordinated water, and m ≥ 0.

[0021] A cell stack for an electrochemical cell including a plurality of layers, each of the plurality of layers including an anode electrode, a cathode electrode, and a separator intervening between both. All of the anodes within the plurality of layers are electrically connected, all of the cathodes within the plurality of layers are electrically connected, and at least one electrode includes a coordination compound material including a water content that includes a deterioration of a set of electrochemical properties when present during the electrochemical cycle of the cell stack. A method of manufacturing a cell stack, comprising: a) manufacturing an electrode set, the electrode set including an anode electrode and a cathode electrode, at least a subset of the electrode set including a coordination compound having a water content; b) assembling a cell stack using the electrode subset having a water content to produce an assembled cell stack having an electrode subset having a water content; and c) exposing the assembled cell stack having a set of electrode subsets having a water content to a process configured to Adjustment adjust the water content within a range of post-adjustment water content Adjustment such that the post-adjustment water content includes a reduction of a deterioration of a set of electrochemical properties when present during the electrochemical cycle of the assembled cell stack. adjustment The method includes a step of exposing the cell stack to a process configured to Adjustment adjust the water content within a range of post-adjustment water content such that the post-adjustment water content includes a reduction of a deterioration of a set of electrochemical properties when present during the electrochemical cycle of the assembled cell stack.

[0022] A method for manufacturing a cell stack of electrochemical cells including a plurality of layers, each layer including an anode electrode, a cathode electrode, and a separator interposed therebetween, wherein all of the anodes in the plurality of layers are in electrical communication, all of the cathodes in the plurality of layers are in electrical communication, and at least one electrode includes a coordination compound material having a residual moisture outside a desired residual moisture profile, the method comprising the steps of: a) assembling the cell stack when the residual moisture of at least one electrode of each electrochemical cell is outside the desired residual moisture profile; and thereafter, b) adjusting the cell stack to adjust the residual moisture of at least one electrode of each electrochemical cell to be within the desired residual moisture profile. adjustment and exposing the substrate to a process.

[0023] Any of the embodiments described herein can be used alone or with each other in any combination. Furthermore, the inventions encompassed herein may include embodiments that are only partially mentioned or implied in this brief summary or abstract, or not mentioned or implied at all. Various embodiments of the present invention may be motivated by various deficiencies in the prior art, which may be described or implied in one or more places herein, but an embodiment of the present invention does not necessarily address all of these deficiencies. In other words, different embodiments of the present invention may address different deficiencies that may be described herein. Some embodiments may only partially address some or only one of the deficiencies that may be described herein, and some embodiments may not address any of these deficiencies.

[0024] Other features, benefits, and advantages of the present invention will become apparent upon review of this disclosure, including the specification, drawings, and claims. [Brief explanation of the drawings]

[0025] The accompanying drawings, in which like reference numbers refer to identical or functionally similar elements throughout the different views, and which are incorporated in and form a part of this specification, further illustrate the present invention and, together with the detailed description of the invention, serve to explain the principles of the invention.

[0026] [Figure 1] 1 shows the specific capacity of an electrode containing sodium manganese hexacyanomanganate TMCCC anode material as a function of the residual moisture in the electrode after drying.

[0027] [Figure 2] 1 shows the total impedance and charge transfer resistance of an electrode containing sodium manganese hexacyanomanganate TMCCC anode material as a function of the residual moisture in the electrode after drying.

[0028] [Figure 3] Electrochemical impedance spectra of electrodes containing sodium manganese hexacyanomanganate TMCCC anode material are shown as a function of the residual moisture content of the electrode after drying.

[0029] [Figure 4] 1 shows the total impedance and charge transfer resistance of an electrode containing sodium manganese iron hexacyanoferrate TMCCC cathode material as a function of the residual moisture in the electrode after drying.

[0030] [Figure 5] For a whole cell containing a sodium manganese hexacyanomanganate TMCCC anode and a sodium manganese iron hexacyanoferrate TMCCC cathode, the specific capacity of the capacity-limiting electrode is shown, with the capacity decreasing as the weighted average residual moisture of the two electrodes decreases.

[0031] [Figure 6]The power and energy densities of the capacity-limiting electrode are shown for a whole cell containing a sodium manganese hexacyanomanganate TMCCC anode and a sodium manganese iron hexacyanoferrate TMCCC cathode, with both power and energy densities decreasing as the weighted average residual moisture of the two electrodes decreases.

[0032] [Figure 7] Electrochemical impedance spectra are shown for a whole cell containing a sodium manganese hexacyanomanganate TMCCC anode and a sodium manganese iron hexacyanoferrate TMCCC cathode as a function of the weighted average residual moisture of the two electrodes.

[0033] [Figure 8] The life in a float test at 45°C is shown for a whole cell containing a sodium manganese hexacyanomanganate TMCCC anode and a sodium manganese iron hexacyanoferrate TMCCC cathode.

[0034] [Figure 9] A table is provided containing residual moisture, coordinated water, and non-coordinating water before and after drying for selected examples of materials presented herein.

[0035] [Figure 10] 1 shows a table containing the molar compositions of various materials and further includes calculations of residual, coordinated, and non-coordinated water in mass percentages. DETAILED DESCRIPTION OF THE INVENTION

[0036] Embodiments of the present invention provide systems and methods for optimizing electrochemical cells that include electrodes that employ coordination compounds. The following description is presented to enable one of ordinary skill in the art to make and use the invention and is provided in the context of a patent application and its requirements.

[0037] Various modifications to the preferred embodiments and generic principles and features described herein will be readily apparent to those skilled in the art. Thus, the present invention is not intended to be limited to the embodiments shown, but is to be accorded the widest scope consistent with the principles and features described herein.

[0038] definition

[0039] Unless otherwise defined, all terms (including technical and scientific terms) used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this overall inventive concept belongs. Furthermore, terms such as those defined in commonly used dictionaries should be interpreted to have a meaning that is consistent with their meaning in the context of the relevant art and this disclosure, and will not be interpreted in an idealized or overly formal sense unless expressly defined herein.

[0040] The following definitions apply to some of the aspects described with respect to some embodiments of the present invention. These definitions may be expanded upon herein as well.

[0041] As used herein, the term "or" includes "and / or," which includes any and all combinations of one or more of the associated listed items. Phrases such as "at least one of," when combined with a list of elements, modify the entire list of elements and not each individual element of the list.

[0042] As used herein, the singular terms "a," "an," and "the" include plural referents unless the context makes clear otherwise. Thus, for example, a reference to an object can include a plurality of objects unless the context makes clear otherwise.

[0043] Furthermore, as used throughout this description and the claims that follow, the meaning of "in" includes "in" and "on," unless the context makes clear otherwise. When an element is referred to as being "on" another element, it will be understood that the element may be directly on the other element, or there may be intervening elements between them. In contrast, when an element is referred to as being "directly on" another element, there are no intervening elements.

[0044] As used herein, the term "set" refers to a collection of one or more objects. Thus, for example, a set of objects can include a single object or multiple objects. Objects in a set can also be referred to as members of the set. The objects in a set can be the same or different. In some cases, the objects in a set can share one or more common characteristics.

[0045] As used herein, the term "adjacent" refers to being near or next to one another. Adjacent objects may be separate from one another or may be in actual or direct contact with one another. In some cases, adjacent objects may be joined to one another or may be integrally formed with one another.

[0046] As used herein, the terms "connect," "connected," and "connecting" refer to a direct attachment or link. Connected objects have no intervening object or set of objects, or no substantial intervening object or set of objects, as the context indicates.

[0047] As used herein, the terms "couple," "coupled," and "coupling" refer to an operational connection or coupling. Coupled objects may be directly connected to each other or indirectly connected to each other, such as through a set of intervening objects.

[0048] The use of the term "about" applies to all numerical values, whether explicitly stated or not. This term generally refers to a range of numbers that one of ordinary skill in the art would consider a reasonable deviation from the stated numerical value (i.e., having an equivalent function or result). For example, this term can be interpreted to include a deviation of ±10% from the given numerical value, as long as such deviation does not alter the ultimate function or result of the value. Thus, a value of about 1% can be interpreted as a range of 0.9% to 1.1%.

[0049] As used herein, the terms "substantially" and "substantial" refer to a considerable degree or extent. When used in connection with an event or circumstance, these terms can refer to when the event or circumstance occurs exactly, as well as when the event or circumstance occurs to a close similarity, for example, taking into account the typical tolerance levels or variability of the embodiments described herein.

[0050] As used herein, the terms "optional" and "optionally" mean that the subsequently described event or circumstance may or may not occur, and that the description includes instances where the event or circumstance occurs and instances where it does not occur.

[0051] As used herein, the term "size" refers to a characteristic dimension of an object. Thus, for example, the size of an object that is spherical can refer to the diameter of the object. In the case of objects that are non-spherical, the size of the non-spherical object can refer to the diameter of a corresponding spherical object, where the corresponding spherical object exhibits or has a particular set of derivable or measurable properties that are substantially the same as those of the non-spherical object. Thus, for example, the size of a non-spherical object can refer to the diameter of a corresponding spherical object that exhibits substantially the same light scattering or other properties as the non-spherical object. Alternatively, or in addition, the size of a non-spherical object can refer to the average of the object's various orthogonal dimensions. That is, for example, the size of an object that is a spheroid can refer to the average of the object's major and minor axes. When a set of objects is referred to as having a particular size, it is understood that the objects can have a distribution of sizes around the particular size. Thus, as used herein, the size of a set of objects can refer to a typical size in a distribution of sizes, such as an average size, a median size, or a peak size.

[0052] As used herein, the term "residual moisture" of a coordination compound, particularly a TMCCC material, refers to the total water content of the TMCCC. Residual moisture includes the total water mass divided by the total dry mass of the TMCCC material (the mass of the metal, CN groups, and any other species, such as chelating species). For example, for a TMCCC with a dry mass of 100 g and a total water content of 10 g, the residual moisture is calculated as 10 g water / 100 g dry mass = 10%.

[0053] As used herein, the water content of a coordination compound material is complex and preferably refers to a hybrid residual water state that specifies just enough lattice-bound water content (e.g., coordinated water) to avoid degrading the desired electrochemical properties of the coordination compound material while removing as much non-lattice-bound water content (e.g., non-coordinating water) as possible. Non-lattice water, sometimes referred to herein as non-coordinating water, can exist in various ways, primarily as interstitial water and / or water bound to the surfaces of the particles of the coordination compound material and / or water present in any pores or micropores within the TMCCC particles. Non-coordinating water above a threshold contained in the optimally selected residual water is considered an undesirable impurity that degrades the desired electrochemical properties, while lattice-bound water is considered necessary and desirable. Materials in this hybrid water content state are neither aqueous nor anhydrous in bulk. As discussed herein, without sufficient care, water management processes (e.g., drying) may not adequately distinguish between coordinated and non-coordinating water in the coordination compound material. The coordination compound materials discussed herein can be used in systems containing water-containing electrolytes that may affect the water content of the coordination compound material after assembly or during use. The coordination compound materials discussed herein can be used in systems containing initially anhydrous electrolytes that may become aqueous during assembly or use as a result of partial or complete release of non-coordinating water from the coordination compound material. The more anhydrous the electrolyte, the better the water content of the electrode material can be controlled. Coordination compound manufacturing often results in excess water associated with the material, and the excess is typically included as non-coordinating water, as defined herein. Water content may be too low and may be characterized by the removal of coordinated water. Therefore, the water content can be adjusted to a desired range, preferably with sufficient coordinated water to achieve the desired electrochemical properties while minimizing non-coordinating water within a target range. A coordination compound with residual water adjusted to a desired, non-decreasing water content range is herein referred to as "coordination compound." Contains water amount tone AdjustmentSimilarly, coordination compounds with residual water outside this range are referred to herein as coordination compound materials. Contains water amount Out of sync Adjustment These are called coordination compound materials.

[0054] As used herein, the term "aqueous" in the context of an electrolyte for an electrochemical cell means an electrolyte that contains water as a solvent and one or more dissolved materials, with the water solvent having a concentration greater than 0.5%.

[0055] As used herein, the term "anhydrous" in the context of an electrolyte for an electrochemical cell means an electrolyte that contains a solvent other than water and water as a trace impurity having a concentration of less than 0.5%.

[0056] As used herein, the term "drying" in the context of removing water from a material refers to removing water to the maximum extent possible consistent with the drying process, leaving water as a trace impurity in a concentration limited by the actual drying process used. Drying transforms the material into an anhydrous state (hence, a dried material is an anhydrous material).

[0057] As used herein, the term "dehydration," in the context of altering the concentration of water in a material, refers to the controllable reduction of the water content to a desired level above trace impurities. In contrast to drying, dehydration is intended to retain water as a necessary and desirable component of the material, e.g., retaining coordinated water and removing non-coordinated water.

[0058] As used herein, the term "hydration" in the context of altering the concentration of water in a material refers to controllably increasing the water content to a desired level above trace impurities but below the aqueous level of the material, e.g., adding coordinating water without adding non-coordinating water within a target range.

[0059] As used herein, "adjustment" in the context of modifying the concentration of water content in a coordination compound such as a TMCCC material. Adjustment The term "water content" includes dehydrating or hydrating a material to achieve a desired concentration of coordinated water that allows for the desired electrochemical properties without unnecessary uncoordinated or other water content. Adjustment The aim is to optimize towards zero or near zero non-coordinated water without losing any of the coordinated water. Adjustment One way to consider this is to Adjustment The main consideration is to consider the mass fraction of water in the TMCCC material, including non-coordinated water and lattice-coordinated water, both before and after the reaction.

[0060] Described herein is a new class of battery cells based on electrodes containing transition metal cyanide coordination compound (TMCCC) materials. These TMCCC materials naturally contain water. Some of the contained water is tightly bound within the material's crystal structure, while some uncoordinated water can reversibly enter and exit the electrode during charge and discharge. Water that leaves the TMCCC material then undergoes chemical or electrochemical reactions with other cell components, causing deterioration in cell performance. Therefore, removing water from the TMCCC material is expected to eliminate these undesired reactions and thus improve electrode and cell performance. However, complete dehydration of the TMCCC material, which involves removing water tightly bound within the crystal structure, deteriorates the material's performance. Embodiments of the present invention set the water content at a preferred level that includes sufficient water content in the crystal structure while minimizing / reducing uncoordinated water.

[0061] The method taught in Reference [2] has drawbacks in both effectiveness and the performance of the resulting battery cells. As shown in Figures 8 and 9 of Reference [2], a first drying step is performed after the synthesis of the material (Figure 8) to form the water-free (z = 0) rhombohedral phase. Alternatively, the drying step can be performed after the material is fabricated into an electrode (Figure 9). TMCCC materials readily reabsorb water from the ambient environment, such as humidity in the air in storage. All processing steps after drying the TMCCC material to achieve the desired phase must be performed in a dry room, which adds cost and complexity to those steps. Therefore, to minimize the cost and complexity of manufacturing cells containing one or more TMCCC electrodes, the drying step should be performed after as many other processing steps as possible. Furthermore, when a cell contains two TMCCC electrodes (anode and cathode), performing separate drying steps for each of the two materials or for each of the two electrodes is more complicated than performing a single drying step for the assembled cell.

[0062] Disclosed herein is a simpler process for manufacturing a cell containing two TMCCC electrodes that involves processing the TMCCC material into electrodes, assembling the electrodes into a cell stack (anode, separator, and cathode electrode stack), and then performing a single drying step on the cell stack, thereby drying both electrodes simultaneously. This is one embodiment of the present invention.

[0063] The performance of electrochemical cells containing TMCCC electrodes depends on the amount of water they contain. Contrary to the teachings of References [2] and [3], some embodiments of the present invention demonstrate that removing all water from a set of TMCCC electrodes does not necessarily result in optimal cell performance. For example, lowering the RM of TMCCC electrodes through a more aggressive drying process increases the impedance of the TMCCC electrodes. Higher electrode impedance reduces the energy efficiency and power capability of the cell. Depending on the application of the battery, different performance indicators are more important than others. For applications where high energy efficiency is important, a non-zero RM in the TMCCC electrodes is optimal. On the other hand, as taught in Reference [2], for applications where operating the battery cell over a narrow voltage range is important, it is desirable to dry the TMCCC electrodes to a "waterless" (RM = 0) state. The teachings of Reference [2] can provide better performance than RM maintained in the preferred non-zero range within a specific application and narrow range of device requirements.

[0064] Embodiments of the present invention can include a process for partial or complete removal of non-coordinating water from the TMCCC structure, but not lattice-bound water. This dehydration process can be performed on individual TMCCC materials, electrodes containing them, or on fully assembled cell stacks. In some instances, TMCCC materials may have insufficient water for the lattice structure; therefore, one aspect of the present invention allows for the addition of water to meet the needs of the lattice without adding non-coordinating water.

[0065] A primary advantage of some embodiments of the present invention is that by removing a controlled amount of uncoordinated water while leaving lattice-bound water in the material, cell performance can be fully optimized with respect to multiple performance metrics, including energy efficiency, cycle life, and other metrics.

[0066] A second advantage of some embodiments of the present invention relates to the mechanical stability of the electrode during the drying process. Drying coated electrodes to a completely anhydrous state requires prolonged exposure to high temperatures (typically >130°C) and vacuum. Unfortunately, at high temperatures, the polymer binder contained in porous electrodes softens. This releases stresses accumulated in the electrode during processing, causing the electrode to warp, deform, and lose its planarity. Subsequent processing steps, such as lamination of electrodes, require the stamped electrodes to be flat. Deformed or warped electrodes are more difficult to process and can result in defects and / or yield loss. However, if the target RM of a TMCCC electrode is significantly above zero (approximately 4% or more), less aggressive drying conditions are required (<100°C), and less electrode deformation occurs during drying to the target RM. Furthermore, mechanical fixtures can be used to compress one or more electrodes or cell stacks to achieve uniform temperature, drying rate, and final RM. These mechanical fixtures can also provide mechanical stability to the electrodes or cell stacks. Therefore, these fixtures result in a consistent, homogeneous RM for large batches consisting of tens or hundreds of electrodes or cell stacks, thus resulting in a higher-quality product. Furthermore, these fixtures reduce or eliminate mechanical deformation that occurs during drying processes that do not mechanically restrain the electrodes or cell stacks.

[0067] A third advantage of some embodiments of the present invention is that the drying step can be performed on a fully assembled cell stack, with drying limited to an intermediate amount of RM, which includes retaining all lattice-bound water. By performing drying on a complete cell stack, fewer subsequent processing steps must be performed under a low RH atmosphere, thereby reducing the cost and complexity of the electrode fabrication and cell assembly process. Furthermore, if the cell stack includes a separator that is Z-folded between the punched electrodes and optionally wrapped around the outside of the cell stack, the mechanical rigidity provided by the separator limits deformation and warping of the electrodes during drying. This reduces the risk of defects associated with electrode deformation and improves yield.

[0068] Embodiments of the present invention can include methods for drying TMCCC electrodes to an optimal RM, where one or more cell performance indicators reach an optimal value. TMCCC materials have the general chemical formula AxPy[R(CN)6-p(NC)p]z(H2O)n, where A is one or more mobile cations, such as Li+, Na+, or K+; P and R are each one or more transition metal cations in the 1+, 2+, 3+, or 4+ state, such as, but not limited to, Cr, Mn, Fe, Ni, Cu, and Zn; and HO represents a water molecule. The general chemical formula is typically normalized to y=1, in which case typical compositions include 0≦x≦2, 0.5≦z≦1, 0≦p≦3, and 0≦n≦4. The moisture content of TMCCC materials can also be expressed as a percentage based on the total mass of the material, in which case it is referred to as "residual moisture" (RM). For example, a sodium manganese iron hexacyanoferrate (MnFeHCF) TMCCC material with the formula NaMnFe[Fe(CN)](HO) has n=2.6 and RM=14.5%. The RM of the TMCCC can range from about 0 to about 25% or more.

[0069] TMCCC materials have an open-framework crystal structure in which hexacyanometallate groups of formula R(CN)6-p(NC)p are octahedrally coordinated with transition metal cations of species P. This structure can consist of a cubic phase, or less commonly, a rhombohedral or monoclinic phase. In the non-cubic phase, the R-CN-P bonds are shifted off-axis relative to each other, while in the cubic phase, the R-CN-P bonds are bonded in a straight line along the same axis.

[0070] The TMCCC structure contains mobile cations, A+, and large interstitial sites where water can reside. Because the A+ cations are not strongly bound to the lattice, they can easily enter and exit the structure during electrochemical cycling of the TMCCC material. Similarly, non-coordinated water can reversibly enter and exit the TMCCC material. Removal of non-coordinated water can be achieved by exposing the TMCCC material to low ambient relative humidity (RH), by heating the material, by applying a vacuum to the material, by electrochemically or chemically inserting additional A+ cations into the material (thus occupying the interstitial space that would otherwise be occupied by water molecules), or by a combination of these or other processes. Regardless of the specific drying method, water leaves the TMCCC material until an equilibrium RM is reached. In contrast, when a low-RM "dry" TMCCC material is exposed to moisture, either by contact with liquid water or exposure to a high-RH atmosphere, the material absorbs water until a new equilibrium is reached at a higher RM. For many TMCCC materials, removal of uncoordinated water can be easily accomplished by drying the material in air or under vacuum at temperatures between 60 and 130°C.

[0071] Additionally, TMCCC materials contain water bound to the framework structure. The most common configuration of bound water is water coordinated to P-site cations adjacent to a hexacyanometallate vacancy (when z<1). The presence of that vacancy involves the absence of a CN group and therefore a vacancy in the coordination shell of each of the adjacent P-site cations. Synthesis of TMCCC materials is typically carried out in water, allowing surrounding water molecules to bind to the P cations and fill those coordination shell vacancies arising from the hexacyanometallate vacancy.

[0072] Consider the example of a TMCCC structure lacking an R(CN)6 group at its center, but with lattice-bound water, where each of the six adjacent P-site cations is coordinated to one water molecule. In such a TMCCC material, there is noncoordinated water, which may or may not be coordinated to an interstitial sodium ion, as well as lattice-bound water, where the P-site cations adjacent to the R(CN)6 vacancies each have one water molecule bound to them. If the lattice-bound water is removed by an aggressive drying process, the P-site cations would become unstable because their coordination shells are no longer filled. This results in a destabilized TMCCC electrode structure and reduced performance.

[0073] TMCCC materials can be processed into composite battery electrodes in several ways. These composite battery electrodes can further include one or more conductive additives, such as carbon, and one or more polymeric binders. The general process involves mixing TMCCC with carbon and binders in one or more organic solvents to form a viscous slurry or ink that can be coated onto a substrate. The mixing can be performed at low or high shear rates to optimize dispersion of the TMCCC, carbon, and binder in the solvent. After mixing, the resulting slurry can be coated onto a substrate such as a mesh or foil. These substrates can be metals such as aluminum, copper, or stainless steel, or surface-modified metals such as carbon-coated aluminum. Coating can be performed using a blade-over-roll coater, slot-die coater, extrusion coater, or other type of coater. After coating, the coated substrate is dried by one or more of convection heating, infrared heating, convection airflow, or other drying processes. The result of the drying process is a composite electrode on the substrate. The drying step performed after coating to form a composite electrode has the primary purpose of evaporating the solvent present in the slurry, and may optionally reduce the RM of the TMCCC material present in the coated electrode.

[0074] The composite electrode can then be densified using a roll press, such as a calendar press. Variations on this electrode fabrication process can be used to achieve higher electrode performance. These variations can include the selection of different conductive carbons or combinations of conductive carbons, such as, but not limited to, carbon black, graphite, or hard carbon, or the selection of different binders or combinations of binders, such as, but not limited to, vinyl fluoride / hexafluoropropylene copolymer, polyvinylidene fluoride (PVDF), polyacrylonitrile, polymethyl methacrylate, polytetrafluoroethylene, or styrene butadiene rubber-based polymers. Variations on this electrode fabrication process can further include the temperature, duration, and pressure used to dry the electrode.

[0075] A drying process can be performed on the TMCCC material containing the first RM. The drying process can involve heating, exposure to vacuum, or both. Drying temperatures below 130°C, preferably below 100°C, are desirable to selectively remove non-coordinated water rather than lattice-bound water. Furthermore, the drying process can also be performed using a combination of heating and exposure to vacuum, where vacuum is defined as ambient pressure below 1 bar, preferably below 0.1 bar. The drying process results in a reduction of the electrode's RM to a value less than the first RM, typically about 1% to about 10% of the second RM. The rate at which drying progresses from the first RM to the second RM depends on both the temperature and the vacuum pressure. It can be advantageous to perform drying at a relatively slow rate at a temperature below 100°C so that the drying process can be stopped at a well-controlled second RM. In this situation, drying can be performed for a duration of 10 minutes to 1 hour, or 1 hour to 10 hours, or 10 to 20 hours. Drying the TMCCC material for a duration of about 1 hour or more, preferably 10 hours or more, results in a uniform drying process, ensuring that all particles of the TMCCC material in the sample reach the same RM and uniformly distributing the water within those particles. Prolonged exposure of the TMCCC material to temperatures above 100°C for durations of 20 hours or more can lead to chemical instability and undesirable chemical reactions. Therefore, drying to the desired second RM should be performed at a rate slow enough to allow uniform drying to the correct second RM, but not so slow that undesirable chemical reactions could occur. These considerations regarding drying rate also apply to the vacuum pressure applied during drying. The stronger the vacuum, the more rapid the drying at any given temperature. Therefore, the vacuum pressure should be selected in combination with the drying temperature to achieve the desired drying rate and uniformity and the desired RM. These considerations apply not only to processes performed on TMCCC materials, but also to processes performed on one or more electrodes containing one or more TMCCC materials, or on cell stacks containing one or more such electrodes.

[0076] Electrodes containing one or more TMCCC materials, each containing one or more first RMs, can undergo a drying process before assembly into a cell stack. The drying process can involve heating, exposure to vacuum, or both. For electrodes containing TMCCC materials, temperatures below 130°C, preferably below 100°C, are desirable to allow for the removal of uncoordinated water rather than lattice-bound water. This results in a reduction of the electrode's RM to a value below the initial RM, typically about 1% to about 10% of the second RM. Composite electrodes containing a polymer binder are typically calendered to reduce the porosity to a desired value. This allows for batch-to-batch control of the electrode's porosity, density, and thickness, enabling the production of reliable, high-quality cell designs. However, calendering involves mechanical deformation of the electrode, which can induce stress within the composite layers. When the polymer is heated, its Young's modulus and yield strength decrease. During the heating associated with the electrode drying process, this weakening of the polymer binder can allow the electrode to deform and release stress. One type of electrode deformation is warping, in which the edges of an originally planar porous electrode curl toward each other. The warping can be irregular, making assembly of a cell stack from warped electrodes difficult and prone to defects. To reduce electrode warping, a stack of one or more stamped electrodes can be placed between two compression plates. These plates limit electrode deformation during the drying process. By preventing warping and maintaining the planar configuration of each electrode, each electrode is exposed to the same drying conditions (temperature and local vacuum pressure), thus achieving uniform RM for all electrodes present during the drying process. Additionally, electrodes may be separated from each other by thin spacers made of sheets of metal, plastic, or other material that are flat and chemically inert under the drying conditions (temperature and vacuum pressure). These dried electrodes can then be assembled into cells using standard processing steps, such as laminating one or more anode electrodes, separators, and cathode electrodes to form a cell stack.Each subsequent processing step should be carried out under low, controlled RH until the cell stack is sealed in an impermeable cell package to prevent the electrodes from re-absorbing water and resulting in a third RM greater than the second RM achieved at the end of the drying process.

[0077] A cell stack can be assembled by arranging one or more layers of anode electrodes, separators, and cathode electrodes into a multilayer stack. These one or more layers can be arranged so that a separator is disposed between each electrode layer, and even so that every other electrode layer is either an anode or a cathode. The result of this stacking process can be a layer sequence such as... anode, separator, cathode, separator..., etc., such that a separator disposed between two electrodes is adjacent to both one anode electrode and one cathode electrode. The first and last layers in the stack can be electrodes of the same or opposite types, separators, or electrodes and separators. Individual electrodes and separators can be placed adjacent to each other to form a stack of multiple layers (see diagram). Alternatively, a single long separator can be folded or zigzagged between alternating anode and cathode electrodes (see diagram).

[0078] After the cell stack is assembled, a first tab is attached to one or more anode layers, and a second tab is attached to one or more cathode electrodes. These tabs are typically designed to protrude outside the cell packaging so that electronic contact can be made to the cell. The tab attachment process may be performed by ultrasonic welding, electron spot welding, laser welding, chemical bonding with an electronically conductive adhesive, or one or more other processes that provide intimate contact and electronic conductivity between the tab and one or more electrodes. After the tabs are attached, the cell stack can be placed in a package that is impermeable to air, water, or other chemical contaminants. One or more liquid electrolytes can be placed in the package along with the cell stack. After all internal cell components are placed in the packaging, the packaging is sealed. The packaging can include a multilayer polymer / metal laminate, a metal can or box, a metal can or box lined with an electronically insulating layer, or other types of packaging materials that are impermeable to water and air. The packaging can be sealed by a heat sealing process, a laser welding process, or one or more other sealing processes. The sealing process can be performed such that the only components of the cell extending from the inside of the packaging to the outside of the packaging are the two tabs.

[0079] Importantly, to maintain the desired second RM for the volume of one or more electrodes, each subsequent processing step until the cell packaging is sealed must be performed under controlled low RH. If one or more electrodes or one or more cell stacks are exposed to uncontrolled or high RH, they may reabsorb water, resulting in a third RM that is higher than the desired second RM. Process requirements, including controlled low RH, can increase the cost and complexity of the manufacturing process or reduce the throughput or yield of the process.

[0080] The drying process can also be performed on a cell stack including one or more anode electrodes, separators, and cathode electrodes. This cell stack drying process can be performed on cell stacks including electrodes that have been pre-dried to reach the desired second RM as described above, or on cell stacks including electrodes that have not been pre-dried. The electrodes present in the cell stack may have been calendered prior to stack assembly and may contain deformations and internal stresses. Therefore, performing the drying process on a cell stack without mechanical restraints can result in warping of the electrodes in the cell stack. This warping of the electrodes in the cell stack may be greater than, approximately equal to, or less than the warping that occurs during drying of one or more unconstrained electrodes (as described above). To minimize or eliminate warping of the electrodes in the cell stack during drying to the desired second RM, one or more cell stacks can be mechanically restrained between two compression plates. Spacers can optionally be placed between the cell stacks. Mechanically restraining the cell stack can eliminate electrode warping and maintain a planar configuration for the electrodes. This allows for a consistent drying process that achieves a uniform second RM for each anode and cathode of each cell stack.

[0081] The change in RM of one or more anode electrodes can be expressed as ΔRM(a), where ΔRM(a) is equal to the difference between a first RM, designated RM(a1), and a second RM, designated RM(a2): ΔRM(a) = RM(a1) - RM(a2). Similarly, the change in RM of one or more cathode electrodes can be expressed as ΔRM(c), where ΔRM(c) is equal to the difference between a first RM, designated RM(c1), and a second RM, designated RM(c2): ΔRM(a) = RM(c1) - RM(c2). As noted above, the first RM, such as RM(a1) or RM(c1), depends on the composition of the TMCCC material and conditions such as RH and temperature when equilibrium is reached. The second RM, such as RM(a2) or RM(c2), depends on one or more conditions of the drying process, such as temperature, vacuum pressure, and duration.

[0082] When each of RM(a1) and RM(c1) is greater than each of RM(a2) and RM(c2), that is, in other words, when RM(a1), RM(c1) > RM(a2), RM(c2), each of ΔRM(a) and ΔRM(c) is greater than 0. In this case, a net amount of water is removed from both one or more anodes and one or more cathodes, resulting in a net decrease in water for the entire cell stack. Therefore, this cell stack drying process is equivalent to a cell manufacturing process including a separate electrode drying process of drying one or more anode electrodes of a first number to RM(a2) in a first process and drying one or more cathode electrodes of a second number to RM(c2) in a second process, and then forming the cell stack by lamination under a low controlled RH. Therefore, by performing a single drying process on a fully assembled cell stack, it is possible to enable the execution of a single process and eliminate the process requirement of a low controlled RH for the cell assembly step performed between electrode drying and sealing of the cell package.

[0083] When the cell stack drying process is performed under conditions such as RM(a1) < RM(a2) < RM(c2) < RM(c1), a net amount of water may be removed from the cell stack and some water may be transferred from one or more anodes to one or more cathodes. Similarly, when the cell stack drying process is performed under conditions such as RM(c1) < RM(c2) < RM(a2) < RM(a1), a net amount of water may be removed from the cell stack and some water may be transferred from one or more cathodes to one or more anodes. Reaching the desired RM(a2) and RM(c2) through the combination of water movement between one or more anodes and one or more cathodes requires less total net water loss from the electrodes. If one or more second RMs can be achieved with less total net water loss, one or more drying processes can be performed at a lower temperature, with a less severe vacuum pressure, for a shorter period of time, or with one or more other reductions in the intensity, cost, or complexity of the drying process.

[0084] If RM(a2) and RM(c2) are arrived at under the same drying conditions with one or more anodes and one or more cathodes in communication with each other, then RM(a2) and RM(c2) are in equilibrium with each other. When RM(a2) and RM(c2) are in equilibrium with each other, there is no thermodynamic driving force for water to move from one type of electrode to the other type of electrode. If the cell assembly processing steps following the cell stack drying process are performed such that RM(a2) and RM(c2) are unchanged, they can remain in equilibrium with each other throughout these drying processes and even during cell operation. If RM(a2) and RM(c2) remain in equilibrium with each other during cell operation, water cannot be released from one or more of the electrodes and undergo undesirable chemical or electrochemical reactions. Therefore, performing drying on the cell stack rather than on the individual electrodes can result in improved cell performance.

[0085] Example

[0086] For each of the following examples, a porous electrode containing TMCCC material was fabricated by first mixing TMCCC powder, nanoparticle carbon black powder, and a styrene-butadiene binder in a xylene and butyl alcohol solution in a mass ratio of approximately 85:7.5:7.5 to form a viscous slurry. This slurry was coated onto an aluminum foil substrate using a slot die coater to form a coated electrode with a target solids mass loading of approximately 20 mg / cm. The coated electrode was heated at a temperature of 100°C or less for 10 minutes to remove the organic solvent, thereby forming a dried electrode with a first porosity of greater than 50%. The dried electrode was then calendered to a second porosity of less than 30% to form a porous electrode. The porous electrode was then punched into sheets of desired dimensions ranging from approximately 2 x 2 cm to approximately 20 x 20 cm for use in battery cells with various form factors to form punched anode electrodes.

[0087] 1. Drying the Single-Layer Electrode

[0088] The anode and cathode can be dried at the electrode level to achieve optimal RM.

[0089] Example 1.

[0090] Anode electrodes were fabricated. The as-fabricated anodes contained 9.1% of the first RM, as measured using a Karl Fischer volumetric titrator. Six 15 cm2 anode electrodes were placed flat in a single layer on the center shelf of a vacuum oven preheated to 70°C. The vacuum oven was evacuated, and the electrodes were dried under dynamic vacuum for 20 minutes, achieving a final pressure of 0.67 torr in the vacuum oven after 20 minutes. The oven was then refilled with nitrogen, and the anode electrodes were removed from the oven. After drying, the anodes contained 7.1% of the second RM, based on the mass of the electrode composite, as measured using a Karl Fischer volumetric titrator.

[0091] Example 2.

[0092] A cathode electrode was fabricated. The as-fabricated cathode contained 18.2% of the first RM, as measured using a Karl Fischer volumetric titrator. Six 15 cm2 cathode electrodes were placed flat in a single layer on the center shelf of a vacuum oven preheated to 110°C. The vacuum oven was evacuated, and the electrodes were dried under dynamic vacuum for 60 minutes, achieving a final pressure of 0.37 torr in the vacuum oven after 60 minutes. The oven was then refilled with nitrogen, and the cathode electrode was removed from the oven. The dried cathode contained 6.9% of the second RM, as measured using a Karl Fischer volumetric titrator. The dried anode and cathode electrodes were then stacked into a cell in a humidity-controlled environment. The resulting cell showed optimal performance.

[0093] Below is a general paragraph about this type of drying that was used to generate the data shown in Figures 1-4.

[0094] Anodes are typically dried at temperatures ranging from 60°C to 100°C, while cathodes, which naturally contain more water than anodes, are typically dried at temperatures ranging from 100°C to 120°C. Care must be taken to avoid drying at temperatures so high that the electrode or active material may thermally degrade. Thus, it is important to understand the thermal properties of the electrode components before developing a drying method. For both electrodes, drying times typically range from 20 minutes to 2 hours. For both electrodes, the final vacuum oven pressure achieved during drying typically ranges from 0.2 to 1.0 torr. The RM of the undried electrode, the residual slurry solvent content in the undried electrode, and the vapor pressure of the aforementioned volatile materials significantly affect the drying temperature and drying time required to achieve the optimal RM for each electrode. These factors can vary depending on the powder synthesis conditions, slurry composition, and slurry application and drying conditions. Furthermore, the drying batch size or the total mass of electrodes in the vacuum oven for one drying cycle can affect the drying temperature and drying time required to achieve the optimal RM.

[0095] 2. Drying the powder

[0096] Another route to achieving optimal RM in the final product is to perform the drying step upstream from the electrodes, i.e., at the powder level.

[0097] Example 1.

[0098] Anode powder was synthesized. The as-synthesized anode powder contained 8.7% of the first RM as measured by a Karl Fischer volumetric titrator. 20 grams of the anode powder was spread on a glass dish and covered with a Kim wipe, which was then secured to the glass container using a rubber band. The glass container was placed on the center shelf of a vacuum oven preheated to 70°C. The anode powder was dried under dynamic vacuum for 16 hours. The dried anode powder contained 7.1% of the second RM as measured by a Karl Fischer volumetric titrator.

[0099] Example 2.

[0100] Cathode powder was synthesized. The as-synthesized cathode powder contained 16.3% of the first RM as measured by a Karl Fischer volumetric titrator. 20 grams of the cathode powder was spread on a glass dish and covered with a Kim wipe, which was then secured to the glass container using a rubber band. The glass container was placed on the center shelf of a vacuum oven preheated to 100°C. The cathode powder was dried under dynamic vacuum for 16 hours. The dried cathode powder contained 7.0% of the second RM as measured by a Karl Fischer volumetric titrator.

[0101] Comments on the powder after drying process:

[0102] The dried powder was then mixed into a slurry with conductive additives and binders and coated onto an electrode sheet. The slurry formulation was adjusted to account for the different rheological behavior of the dried powder compared to the typical wet state. The coated electrode was then dried at low temperature to evaporate the slurry solvent. The resulting electrode contained optimal moisture content and did not require additional vacuum drying. The electrode was then stacked into a cell, which demonstrated optimal performance. This drying route requires that all subsequent processing steps after vacuum drying of the powder be performed in a moisture-controlled environment to ensure the dried powder remains in its optimal RM state and does not reabsorb moisture from the processing environment.

[0103] 3. Drying process of electrode stacks – a typical example

[0104] Example 1: Drying of Electrodes. Stacks of electrodes containing 5-30 pieces are prepared and weighed. The electrodes are dried under dynamic vacuum in a vacuum oven at temperatures between 80-120°C for 90-480 minutes depending on the material, batch size, and desired target residual moisture.

[0105] Example 2: Drying of Electrodes. A stack of 30 or fewer electrodes is placed in a vacuum oven and preheated plates, each weighing 2 pounds or more, are placed on the electrode stack. The electrodes are dried under dynamic vacuum at temperatures between 80 and 120°C for times between 90 and 480 minutes, depending on the material, batch size, and desired target residual moisture of the material.

[0106] To improve the uniformity of heat transfer in a stack having multiple electrodes, it may be advantageous to apply pressure to the electrodes in the stack or to restrain the electrodes in the stack. This can be accomplished by using heavy plates of similar surface area as the electrodes, or by placing the electrodes between plates that are bolted together with fixtures to provide the desired amount of pressure.

[0107] The electrodes can be equivalently dried in a vacuum oven or a convection oven under an inert atmosphere such as nitrogen.

[0108] Example 3: Drying of Electrodes. Electrodes containing >13.4% first RM1 are dried in a vacuum oven at 120°C under dynamic vacuum for 360-600 minutes, depending on batch size, to a second RM2 of <6.7%. The electrodes are then laminated into cells under controlled RH of <10%. Measurements taken after cell lamination show that these electrodes reached a third RM3 of between 6.7% and 7.2%, where RM3 > RM2 and RM3 is the desired final material moisture content.

[0109] Example 4: Drying of Electrodes. The electrodes are placed in a convection oven at a temperature of 80-120°C, and the oven is purged with N2 at a flow rate of up to 150 SCFM during drying. The electrodes are dried for 50-90 minutes depending on the material, batch size, and desired residual moisture.

[0110] 4. Drying process of electrode stacks - specific examples

[0111] Example 5: Drying of Cathode Electrodes. The residual moisture of cathode electrodes comprising sodium manganese iron hexacyanoferrate TMCCC material was measured using a Karl Fischer to be 18.4% of the electrode composite mass. Eight stacks of 14 cathode electrodes, each with an area of ​​approximately 385 cm, were evenly spaced horizontally on two shelves of a vacuum oven. The stacks were covered with an approximately 500 g aluminum plate. Both the oven and plate were preheated to 120°C. The electrodes were dried under active vacuum for 6 hours. The final moisture was measured by Karl Fischer to be 7.0% of the electrode composite mass.

[0112] Example 6: Drying of Anode Electrodes. The residual moisture of anode electrodes comprising sodium manganese hexacyanomanganate TMCCC material was measured using a Karl Fischer to be 8.1% of the electrode composite mass. Eight stacks of 12 anode electrodes, each with an area of ​​approximately 369 cm, were placed horizontally and evenly spaced on two shelves of a vacuum oven. The stacks were covered with an approximately 500 g aluminum plate. Both the oven and plate were preheated to 80°C. The electrodes were dried under active vacuum for 80 minutes. The final moisture was measured by Karl Fischer to be 7.1% of the electrode composite mass.

[0113] Cell Drying Process - Typical Example

[0114] Example 7: Cell Drying. Cells consisting of stacked anode and cathode electrodes with a separator in between, placed inside unsealed laminate packaging, can be arranged in a single layer or stacked 2-3 cells high and dried in a vacuum oven. The cells are dried under dynamic vacuum at 95°C for 60-120 minutes, depending on the batch size and desired target residual moisture.

[0115] To improve the efficiency, yield, or cost of the drying process and downstream processes (collectively, manufacturing considerations), or to reach a desired final RM, it may be advantageous to dry stacked cells as a unit, rather than drying individual electrodes or several anode or cathode electrodes.

[0116] For manufacturing considerations or to reach a desired final RM, it may be advantageous to pre-dry one or more anode or cathode electrodes prior to cell assembly and then subsequently dry the fully assembled cell stack. In certain cases, due to moisture transfer between the anode and cathode electrodes during the cell drying step, an electrode can be pre-dried from a first RM to a second RM and then dried in the cell drying step to an additional third RM, which may be larger or smaller than the second RM. In this way, the final moisture target for both electrodes can be designed and achieved by complementary drying steps.

[0117] Additionally, due to manufacturing considerations or desired final material moisture content, it may be advantageous to select drying conditions that remove more water from the electrode material than the desired end goal, to allow for re-absorption of moisture in subsequent processing steps.

[0118] 5. Cell Drying Process – Specific Examples

[0119] Example 8: Cell Drying. A large number of eight stacked cells in unsealed laminate pouches were fabricated. Prior to drying, representative electrode samples were measured by Karl Fischer. The cathode was found to have a first RM, i.e., RMc(1), of 18.4%, and the anode was found to have a first RM, i.e., RMa(1), of 8.1%. The cell was placed in a vacuum oven and covered with an aluminum compression plate weighing approximately 500 g. Both the oven and plate were preheated to 90°C. The cell was dried under active vacuum for 90 minutes before being removed from the oven. The cell was disassembled, and samples were taken for Karl Fischer moisture measurement. The second RM of the electrodes was measured. For the cathode, the second RMc(2) was measured to be 14.0%, and for the anode, the second RMa(2) was measured to be 5.8%. A net loss of RM was observed for each of the two electrodes.

[0120] 6. General Concepts of the Embodiments:

[0121] 1. Equipment settings

[0122] The drying system consists of a vacuum oven connected to a vacuum pump with a solvent trap along the vacuum line between the oven and the pump. A digital pressure gauge is used to accurately monitor the pressure achieved in the vacuum oven during drying. Prior to drying, the oven should be preheated and stabilized at the desired temperature, and the solvent trap must be pre-frozen. With the pre-frozen solvent trap and the preheated oven under maximum vacuum, a pressure below 0.2 torr should be achieved when the oven is empty. This confirms that all seals in the system are in good condition.

[0123] 2. Resorption

[0124] Dry electrodes are highly hygroscopic and tend to reabsorb moisture from the environment. In particular, the electrodes can reabsorb moisture from humidity in the air or can absorb moisture from other electrodes when they come into contact with each other during cell stacking.

[0125] It may be advantageous to pre-dry the electrode to a moisture content below the optimum RM in anticipation of the electrode re-absorbing moisture from the humid air during downstream processes.

[0126] It may be advantageous to dry an electrode set to a moisture content a that is less than the optimum RM moisture content b for that electrode set (anode or cathode), and then stack that electrode set into a cell in which the other electrode has a moisture content x that is greater than the optimum RM moisture content y for that electrode set (anode or cathode). Moisture transfer between the electrodes during cell stacking can bring both electrode sets to their optimum RM moisture content b and y. If moisture transfer from the cell stack is insufficient, subsequent drying of the cell stack can enhance moisture transfer between the electrode sets.

[0127] FIG. 1 shows the specific capacity of electrodes containing sodium manganese hexacyanomanganate TMCCC anode material as a function of the residual moisture in the electrode after drying.

[0128] FIG. 2 shows the total impedance and charge transfer resistance of an electrode containing sodium manganese hexacyanomanganate TMCCC anode material as a function of the residual moisture in the electrode after drying.

[0129] FIG. 3 shows the electrochemical impedance spectra of electrodes containing sodium manganese hexacyanomanganate TMCCC anode material as a function of the residual moisture content of the electrode after drying.

[0130] FIG. 4 shows the total impedance and charge transfer resistance of an electrode containing sodium manganese iron hexacyanoferrate TMCCC cathode material as a function of the residual moisture in the electrode after drying.

[0131] 1 to 3 show that the specific capacitance of the anode electrode is lower for drier and lower RM electrodes. Furthermore, the total impedance and charge transfer resistance are higher for drier and lower RM anodes. This indicates that the lower the RM, the greater the degradation of the anode electrode performance.

[0132] Figure 4 shows that the total impedance and charge transfer resistance increase for drier and lower RM cathodes. The onset of performance degradation, as evidenced by increases in total impedance and charge transfer resistance, occurs at RMs below 3% for the cathode and 7% for the anode. This indicates that the drying conditions for optimizing the performance of TMCCC electrodes depend on the composition of the TMCCC material contained in the electrode.

[0133] Figure 5 shows the specific capacity of the capacity-limiting electrode for a whole cell containing a sodium manganese hexacyanomanganate TMCCC anode and a sodium manganese iron hexacyanoferrate TMCCC cathode. The capacity decreases as the weighted average residual moisture of the two electrodes decreases.

[0134] Figure 6 shows the power and energy densities of the capacity-limiting electrode for a whole cell containing a sodium manganese hexacyanomanganate TMCCC anode and a sodium manganese iron hexacyanoferrate TMCCC cathode. Both power and energy densities decrease as the weighted average residual moisture of the two electrodes decreases.

[0135] FIG. 7 shows the electrochemical impedance spectra for a whole cell containing a sodium manganese hexacyanomanganate TMCCC anode and a sodium manganese iron hexacyanoferrate TMCCC cathode as a function of the weighted average residual moisture of the two electrodes.

[0136] Figure 8 shows the lifespan of whole cells containing a sodium manganese hexacyanomanganate TMCCC anode and a sodium manganese iron hexacyanoferrate TMCCC cathode in a float test at 45°C. In this test, the cells were continuously floated at a maximum voltage of 1.859V and fully discharged at a rate of 1C once per day. The cell with the lowest weighted average residual moisture was the most stable and had the longest lifespan.

[0137] Figures 5-7 show that the trends observed for the individual cathodes and anodes also hold true for the whole cell. The drier the electrodes in the whole cell, the lower the cell's capacity, power, and energy, and the higher the impedance. However, Figure 8 shows that the cells containing the driest electrodes achieve the longest life. Therefore, the optimal cell contains electrodes with an intermediate amount of residual moisture that strikes an optimal balance between performance indicators such as cell life (favoring drier electrodes) and high capacity and low resistance (favoring wetter electrodes).

[0138] Figure 9 tabulates the initial and final residual moisture, coordinated water, and noncoordinating water for selected examples. In each case, the noncoordinating water is reduced during sample processing, including a dehydration step. The temperature used in the dehydration step was 120°C or less, allowing for the selective removal of noncoordinating water from the TMCCC samples without removing the coordinated water.

[0139] Inductively coupled plasma (ICP) and Karl Fischer (KF) analyses were performed to determine the composition of each TMCCC material. The ICP data was analyzed using the KF data for oxygen values, and then a charge balance was forced to the known initial charge state of the TMCCC material. The coordinated water content was then assumed to be directly proportional to the vacancy mole fraction. The non-water component of the material is expressed as a 100% mass basis, and water is expressed as an additional mass percentage relative to this basis. Measured KF values ​​for electrodes are converted from the % total electrode mass as a function of sample weight (regardless of water content) to instead reflect the mass percentage of water relative to the non-water TMCCC mass, which is always normalized to 100%. The stoichiometric ratio of coordinated and non-coordinated water is used to determine the wet fraction of water measured by KF. For these calculations, it is assumed that all non-coordinated water is removed during drying before the coordinated water.

[0140] Figure 10 tabulates exemplary compositions of two TMCCC materials on a molar basis and shows an exemplary calculation of residual water on a mass percent basis from these molar compositions. While coordinated water is proportional to the vacancy content of each TMCCC material, non-coordinated water depends on synthesis and processing conditions prior to composition determination.

[0141] conclusion

[0142] References [2] and [3] teach that trace amounts of water in a cell result in deterioration of cell performance. Embodiments of the present invention are believed to be novel and non-obvious, at least in part, because they dry TMCCC electrodes to a non-zero RM, and the presence of some water within the described range in the material actually improves cell performance, thus allowing for optimization of cell performance.

[0143] The concept of performing a single dehydration / hydration process on a fully assembled cell stack is also believed to be novel and non-obvious. Such a process is practical, at least in part, because a non-zero RM is desired and implemented. This is because the composition of the TMCCC material determines its affinity for water, reaching an equilibrium RM at a specific ambient temperature and pressure. When two electrodes, each containing a unique TMCCC material, are placed in close proximity to each other, the electrode with a higher affinity for water and a higher equilibrium RM will absorb water from the other electrode until the two electrodes reach equilibrium. Therefore, performing a drying / hydration step on a cell stack containing two TMCCC electrodes can result in water migration from one electrode to the other, in addition to the net water loss observed in conventional drying processes. Furthermore, this water migration between electrodes can degrade the performance of the electrochemical cell.

[0144] Therefore, performing a single drying step on the cell stack is advantageous for two reasons. First, it is a simpler process than performing separate drying steps on each of the two electrodes before assembly into the cell stack. Second, a single drying step results not only in a net loss of water (net drying) throughout the cell stack, but also in a net movement of water between the two electrodes until they reach equilibrium with each other. Chemical equilibrium represents the most stable state of a system under a particular set of conditions (temperature, pressure, etc.). A cell stack in which each of the two electrodes contains an equilibrium amount of water will be most stable, with the least amount of that water being chemically active. Therefore, by equilibrating the two electrodes with each other through a single drying step, optimal RM for optimal cell performance can be achieved, while at the same time, each RM of the two electrodes can reach equilibrium, where it is most chemically stable and least reactive.

[0145] Figure 9 shows the residual moisture, coordinated water, and non-coordinating water for selected examples described herein before and after drying. Expressing residual moisture in this manner allows for consideration of water in the material's composition of matter. Figure 10 shows selected compositions for examples described herein. For both the anode and cathode, the material compositions are reported in moles. Additionally, the residual moisture, coordinated water, and non-coordinating water are calculated in mass percentages. Therefore, the measured residual moisture for each sample herein relates back to the composition of the TMCCC material for those examples. For example, the composition of the as-synthesized anode includes n=1.6 and m=1.1 (following the compositional notation used herein). In this case, m=1.1 corresponds to 7% non-coordinating water in the as-synthesized material, which is reduced during processing described herein. For example, in Example 1, the final non-coordinating water is 6.1%, corresponding to m=0.96.

[0146] As initially produced, TMCCC materials may have non-coordinating water in the range of about 5-15%, roughly corresponding to m = 1.0-2.0. Figure 10 shows that for each of the included examples, after processing, the non-coordinating water is reduced to about 0-10%, or roughly m = 0-1.5.

[0147] References - expressly incorporated herein by reference:

[0148] References [1] - Imhof, R. In Situ Investigation of the Electrochemical Reduction of Carbonate Electrolyte Solutions at Graphite Electrodes.J.Electrochem.Soc.,145,1081-1087(1998)

[0149] Reference [2] - U.S. Patent No. 9,099,718 (Lu'718)

[0150] Reference [3] - Wu, J, et al, J. Am. Chem. Soc., 139, 18358-18364 (2017)

[0151] The above systems and methods have been described in general terms to aid in understanding the details of preferred embodiments of the present invention. In the description herein, numerous specific details, such as example components and / or methods, are presented to provide a thorough understanding of embodiments of the present invention. Some features and advantages of the present invention may be realized in such a manner, but not required in all cases. However, one skilled in the art will recognize that embodiments of the present invention can be practiced without one or more of the specific details, or can be practiced with other devices, systems, assemblies, methods, components, materials, parts, etc. In other instances, well-known structures, materials, or operations are not specifically shown or described in detail to avoid obscuring aspects of embodiments of the present invention.

[0152] Throughout this specification, references to "one embodiment," "an embodiment," or "a particular embodiment" mean that a particular feature, structure, or characteristic described in connection with that embodiment is included in at least one embodiment of the invention, but not necessarily in all embodiments. Thus, the appearances of the phrases "in one embodiment," "in an embodiment," or "a particular embodiment" in various places throughout this specification do not necessarily refer to the same embodiment. Furthermore, the particular features, structures, or characteristics of any particular embodiment of the invention may be combined in any suitable manner with one or more other embodiments. It should be understood that other variations and modifications of the embodiments of the invention described and illustrated herein are possible in light of the teachings herein and should be considered as part of the spirit and scope of the invention.

[0153] It will also be understood that one or more of the elements shown in the drawings / figures may be implemented in a more separate or more integrated manner, or may be eliminated or rendered non-functional in certain cases, as may be useful depending on the particular application.

[0154] Furthermore, any signal arrows in the drawings / diagrams should be considered only as examples and not as limitations unless otherwise stated. Also, combinations of components or steps will be considered as referred to when the terminology does not predict that they are separable or combinable.

[0155] The foregoing description of illustrated embodiments of the present invention, including what is set forth in the Abstract, is not intended to be exhaustive or to limit the invention to the precise form disclosed herein. While specific embodiments of, and examples for, the present invention have been described herein for illustrative purposes only, various equivalent modifications are possible within the spirit and scope of the present invention, as those skilled in the art will recognize and understand. As will be shown, these modifications can be made to the present invention in light of the foregoing description of illustrated embodiments of the invention and are to be included within the spirit and scope of the present invention.

[0156] Thus, while the invention has been described herein with reference to specific embodiments thereof, it will be understood that a degree of freedom of modification, alteration, and substitution is contemplated in the foregoing disclosure, and that in some cases, some features of the embodiments of the invention may be employed without the corresponding use of other features without departing from the scope and spirit of the invention as described. Accordingly, many modifications may be made to adapt a particular situation or material to the essential scope and spirit of the invention. The invention is not limited to the specific terms used in the following claims and / or to the particular embodiment disclosed as the best mode contemplated for carrying out the invention; rather, the invention is intended to include any and all embodiments and equivalents falling within the scope of the appended claims. The scope of the invention, therefore, should be determined solely by the appended claims. [Prior art documents] [Patent documents]

[0157] [Patent Document 1] U.S. Patent No. 9,099,718 [Non-patent literature]

[0158] [Non-Patent Document 1] Imhof, R. In Situ Investigation of the Electrochemical Reduction of Carbonate Electrolyte Solutions at Graphite Electrodes.J.Electrochem.Soc.,145,1081-1087(1998) [Non-patent document 2] Wu,J,et al,J.Am.Chem.Soc.,139,18358-18364(2017)

Claims

1. 1. A method of manufacturing a cell stack for an electrochemical cell comprising a plurality of layers, each of the plurality of layers including an anode electrode, a cathode electrode, and a separator interposed therebetween, wherein all of the anodes in the plurality of layers are in electrical communication, all of the cathodes in the plurality of layers are in electrical communication, and at least one electrode includes a coordination compound material including a moisture content that, when present during electrochemical cycling of the cell stack, includes a deterioration in a set of electrochemical properties, the method comprising: a) fabricating an electrode set, the electrode set including the anode electrode and the cathode electrode, all of the anode electrode and the cathode electrode having the coordination compound having the water content; b) assembling the cell stack using the electrode set including the water content to produce an assembled cell stack having the electrode set including the water content; c) exposing the assembled cell stack having the electrode set with the water content to a conditioning process configured to adjust the water content of the electrodes of the electrode set to within a range of adjusted water contents; Including, the adjusted water content comprises a reduction in the degradation of the set of electrochemical properties when present during electrochemical cycling of the assembled cell stack; the adjusted moisture content comprises 4 percent or more residual moisture for all electrodes of the electrode set; the electrode set contains both non-zero coordinating and non-coordinating water when the residual moisture is 4 percent or greater for all electrodes of the electrode set; The electrode is Formula: A ｘ P ｙ [R(CN) ６ ｚ (H ２ O) ｎ ​ the coordination compound material having the adjusted water content comprising: A is one or more alkali cations; P and R are one or more divalent or trivalent transition metal cations; 0.5<z<1, n=6*(1−z)+m and n>0, 6*(1-z) is the amount of lattice-bound water, m is the amount of non-coordinated water, m≧0, A method wherein 0≦x≦2 and y=1.

2. 10. The method of claim 1, wherein the step of exposing the assembled cell stack is performed in an environmentally controlled chamber configured for the conditioning process to be applied to the assembled cell stack, and the step of assembling the cell stack is performed outside of the environmentally controlled chamber.

3. 1. A method of manufacturing a cell stack for an electrochemical cell, the cell stack including a plurality of layers, each layer including an anode electrode, a cathode electrode, and a separator interposed therebetween, wherein all of the anodes in the plurality of layers are in electrical communication, and all of the cathodes in the plurality of layers are in electrical communication, and each of the electrodes includes a coordination compound material having a residual moisture outside of a desired residual moisture profile, the method comprising: a) assembling the cell stack when the residual moisture of the electrodes of each electrochemical cell is outside the desired residual moisture profile; and thereafter b) exposing the cell stack to a conditioning process to adjust the residual moisture of the electrodes of each electrochemical cell to within the desired residual moisture profile of 4 percent or greater; Including, the electrodes contain both non-zero coordinating and non-coordinating water when the residual moisture for all of the electrodes is 4 percent or greater; The electrode is Formula: A ｘ P ｙ [R(CN) ６ ｚ (H ２ O) ｎ ​ and A is one or more alkali cations; P and R are one or more divalent or trivalent transition metal cations; 0.5<z<1, n=6*(1−z)+m and n>0, 6*(1-z) is the amount of lattice-bound water, m is the amount of non-coordinated water, m≧0, A method where 0≦x≦2 and y=1.

4. 4. The method of claim 3, wherein the coordination compound material comprises a TMCCC material having a first amount of coordinated water and a second amount of non-coordinated water, and the residual moisture profile comprises the first amount of coordinated water located within a first target range and the second amount of non-coordinated water located below a second target range.

5. The method of claim 4 , wherein the anode electrode comprises the TMCCC material, the TMCCC material comprising manganese hexacyanomanganate.

Images