Electrodes and batteries

Abstract

This electrode 1000 is provided with: an active material layer 110 that contains an active material 112, a solid electrolyte 111 and a binder 113; and a collector 100 that comprises a substrate 101 and a coating layer 102 which covers the substrate 101, while being in contact with the active material layer 110. The binder 113 contains a block copolymer that comprises two first blocks, each of which is composed of a repeating unit that has an aromatic ring, and a second block which is positioned between the two first blocks. The block copolymer has a weight average molecular weight of 170,000 or more. The coating layer 102 contains a conductive carbon.

Description

[Technical Field]

[0001] The present disclosure relates to electrodes and batteries. [Background technology]

[0002] Patent Documents 1 to 3 disclose an electrode including a current collector and an active material layer containing an active material, a solid electrolyte, and a binder, and a battery using the electrode. In particular, Patent Document 3 discloses that a conductive carbon film is disposed on the surface of the current collector. [Prior art documents] [Patent documents]

[0003] [Patent Document 1] Japanese Patent Application Laid-Open No. 2018-125260 [Patent Document 2] Japanese Patent Application Laid-Open No. 2010-262764 [Patent Document 3] International Publication No. 2013 / 108516 Summary of the Invention

[0004] An object of the present disclosure is to provide an electrode suitable for improving the peel strength between an active material layer and a current collector.

[0005] In one aspect of the present disclosure, the electrode comprises: an active material layer including an active material, a solid electrolyte, and a binder; a current collector having a substrate and a coating layer that covers the substrate and is in contact with the active material layer; Equipped with the binder has a block copolymer including two first blocks composed of repeating units having an aromatic ring and a second block located between the two first blocks, The weight average molecular weight of the block copolymer is 170,000 or more, The coating layer contains conductive carbon.

[0006] The present disclosure provides an electrode suitable for improving the peel strength between an active material layer and a current collector. [Brief explanation of the drawings]

[0007] [Figure 1] FIG. 1 shows a cross-sectional view of an electrode according to the first embodiment. [Figure 2] FIG. 2 shows a cross-sectional view of the battery according to the second embodiment. DETAILED DESCRIPTION OF THE INVENTION

[0008] (Summary of one aspect of the present disclosure) The electrode according to the first aspect of the present disclosure comprises: an active material layer including an active material, a solid electrolyte, and a binder; a current collector having a substrate and a coating layer that covers the substrate and is in contact with the active material layer; Equipped with the binder has a block copolymer including two first blocks composed of repeating units having an aromatic ring and a second block located between the two first blocks, The weight average molecular weight of the block copolymer is 170,000 or more, The coating layer contains conductive carbon.

[0009] According to the first aspect, the active material layer is in contact with the coating layer of the current collector. At this time, an aromatic ring contained in the block copolymer of the binder in the active material layer interacts with the conductive carbon of the coating layer. This interaction tends to improve the adhesion between the active material layer and the current collector, and to improve the peel strength between the active material layer and the current collector. Thus, the electrode is suitable for improving the peel strength between the active material layer and the current collector.

[0010] In the second aspect of the present disclosure, for example, in the electrode according to the first aspect, the first block may have an average degree of polymerization of 210 or more.

[0011] According to the second aspect, the peel strength between the active material layer and the current collector can be further improved.

[0012] In the third aspect of the present disclosure, for example, in the electrode according to the first or second aspect, the second block may contain a repeating unit derived from a conjugated diene.

[0013] According to the third aspect, the peel strength between the active material layer and the current collector can be further improved.

[0014] In a fourth aspect of the present disclosure, for example, in the electrode according to any one of the first to third aspects, the block copolymer may be a triblock copolymer, and the repeating unit having the aromatic ring may include a repeating unit derived from styrene.

[0015] According to the fourth aspect, the block copolymer tends to be flexible and have high strength, which can further improve the peel strength between the active material layer and the current collector.

[0016] In a fifth aspect of the present disclosure, for example, in the electrode according to the fourth aspect, the block copolymer may be a hydrogenated product.

[0017] In a sixth aspect of the present disclosure, for example, in the electrode according to any one of the first to fifth aspects, the block copolymer may include at least one selected from the group consisting of styrene-ethylene / butylene-styrene block copolymer (SEBS), styrene-ethylene / propylene-styrene block copolymer (SEPS), and styrene-ethylene / ethylene / propylene-styrene block copolymer (SEEPS).

[0018] According to the fifth or sixth embodiment, the block copolymer tends to be more flexible and have higher strength, which can further improve the peel strength between the active material layer and the current collector.

[0019] In a seventh aspect of the present disclosure, for example, in the electrode according to any one of the first to sixth aspects, the substrate may contain aluminum or an aluminum alloy.

[0020] According to the seventh aspect, aluminum and aluminum alloys are lightweight metals with high electrical conductivity, and therefore this electrode not only improves the peel strength between the active material layer and the current collector, but also improves the weight energy density of the battery.

[0021] In an eighth aspect of the present disclosure, for example, in the electrode according to any one of the first to seventh aspects, the active material may contain a lithium-containing transition metal oxide.

[0022] According to the eighth aspect, not only is the peel strength between the active material layer and the current collector improved, but the average discharge voltage of the battery can be improved while reducing the manufacturing costs of the electrode and the battery.

[0023] In a ninth aspect of the present disclosure, for example, in the electrode according to the eighth aspect, the active material may include lithium nickel cobalt manganese oxide.

[0024] According to the ninth aspect, not only can the peel strength between the active material layer and the current collector be improved, but also the energy density of the battery can be improved.

[0025] A battery according to a tenth aspect of the present disclosure comprises: A positive electrode and a negative electrode; an electrolyte layer located between the positive electrode and the negative electrode; Equipped with At least one selected from the group consisting of the positive electrode and the negative electrode is an electrode according to any one of the first to ninth aspects.

[0026] According to the tenth aspect, in an electrode provided in a battery, not only is the peel strength between the active material layer and the current collector improved, but also excellent output characteristics can be achieved in the battery.

[0027] In an eleventh aspect of the present disclosure, for example, in the battery according to the tenth aspect, the positive electrode may be the electrode.

[0028] According to the eleventh aspect, in the electrode of the battery, not only is the peel strength between the active material layer and the current collector improved, but also better output characteristics can be achieved in the battery.

[0029] Hereinafter, embodiments of the present disclosure will be described with reference to the drawings.

[0030] (Embodiment 1) FIG. 1 shows a cross-sectional view of an electrode 1000 according to a first embodiment. The electrode 1000 of the first embodiment includes a current collector 100 and an active material layer 110. The active material layer 110 includes a solid electrolyte 111, an active material 112, and a binder 113. The current collector 100 includes a substrate 101 and a coating layer 102. The coating layer 102 coats the substrate 101 and is in contact with the active material layer 110. The binder 113 includes a block copolymer. The block copolymer in the binder 113 includes two first blocks composed of repeating units having an aromatic ring and a second block located between the two first blocks. The weight-average molecular weight of this block copolymer is 170,000 or more. The coating layer 102 includes conductive carbon.

[0031] With the above configuration, in the electrode 1000 according to the first embodiment, peeling between the active material layer 110 and the current collector 100 tends to be suppressed. Furthermore, it is possible to improve the output characteristics of a battery including the electrode 1000. The electrode 1000 can be used, for example, as an electrode for an all-solid-state secondary battery.

[0032] Patent Documents 1 and 2 disclose an electrode including an active material layer containing an active material, a solid electrolyte, and a binder, and a current collector, and a battery using the electrode. However, the electrode configurations disclosed in Patent Documents 1 and 2 do not sufficiently improve the peel strength between the active material layer and the current collector.

[0033] Patent Document 3 discloses an electrode including an active material layer containing an active material, a solid electrolyte, and a binder, and a current collector, and a battery using the electrode. In particular, Patent Document 3 discloses that a conductive carbon film is disposed on the surface of the current collector. However, the electrode configuration disclosed in Patent Document 3 does not sufficiently improve the peel strength between the active material layer and the current collector.

[0034] The present inventors have focused on the insufficient adhesion between the active material layer and the current collector in conventional electrodes and have conducted research on the active material layer and the current collector. As a result, the present inventors have newly discovered that laminating an active material layer containing a block copolymer having a high molecular weight and an aromatic ring with a current collector containing conductive carbon improves the peel strength between the active material layer and the current collector. Although the detailed mechanism behind this is not yet clear, it is believed that the interaction between the aromatic ring contained in the block copolymer and the conductive carbon plays a role. Examples of such interactions include π-π interactions. Furthermore, it is believed that pseudo-crosslinking of multiple block copolymers due to interactions between blocks composed of repeating units containing aromatic rings also affects the peel strength between the active material layer and the current collector.

[0035] Based on the above findings, the present inventors further conducted research. As a result, they newly discovered that the peel strength between the active material layer 110 and the current collector 100 in the electrode 1000 can be improved by laminating an active material layer 110 containing a block copolymer including two first blocks composed of repeating units having an aromatic ring and a second block located between the two first blocks and having a weight-average molecular weight of 170,000 or more with a current collector 100 having a coating layer 102 containing conductive carbon. As described above, in the electrode 1000 of the first embodiment, the active material layer 110 having the binder 113 containing the block copolymer contacts the coating layer 102 containing conductive carbon. As a result, in the electrode 1000 of the first embodiment, the interaction between the aromatic ring of the block copolymer contained in the binder 113 and the conductive carbon improves the adhesion between the active material layer 110 and the current collector 100. By improving the adhesion between the active material layer 110 and the current collector 100, the peel strength between the active material layer 110 and the current collector 100 tends to improve.

[0036] As described above, electrode 1000 in Embodiment 1 includes active material layer 110 and current collector 100. Active material layer 110 and current collector 100 will be described in detail below.

[0037] [Active material layer] Active material layer 110 in the first embodiment includes solid electrolyte 111, active material 112, and binder 113. Solid electrolyte 111, active material 112, and binder 113 will be described in detail below.

[0038] <Binder> As described above, the binder 113 has a block copolymer including two first blocks composed of repeating units having an aromatic ring and a second block located between the two first blocks. In the first block, repeating units having an aromatic ring are arranged consecutively. The repeating unit refers to a molecular structure derived from a monomer and is sometimes called a constituent unit. The block copolymer has, for example, a triblock arrangement composed of two first blocks and one second block. The block copolymer is, for example, an ABA triblock copolymer. In this triblock copolymer, the A block corresponds to the first block and the B block corresponds to the second block. The first block functions, for example, as a hard segment. The second block functions, for example, as a soft segment.

[0039] In the present disclosure, the aromatic ring refers to a cyclic structure having aromaticity. Examples of the aromatic ring contained in the first block include benzene-based aromatic rings such as a benzene ring and a naphthalene ring, non-benzene-based aromatic rings such as a tropylium ring, and heteroaromatic rings such as a pyridine ring and a pyrrole ring.

[0040] Examples of polymers constituting the first block include polystyrene, polyphenyl methacrylate, polybenzyl methacrylate, polyphenylene, polyaryl ether ketone, polyaryl ether sulfone, and polyphenylene oxide. In the first block, the repeating unit having an aromatic ring includes, for example, a repeating unit derived from styrene. In the present disclosure, a triblock copolymer in which the first block includes a repeating unit derived from styrene may be referred to as a styrene-based triblock copolymer.

[0041] The compositions of the two first blocks contained in the block copolymer may be the same or different, and the degrees of polymerization of the two first blocks may be the same or different.

[0042] The second block contains, for example, repeating units derived from a conjugated diene. Examples of conjugated dienes include butadiene and isoprene. The repeating units derived from a conjugated diene may be hydrogenated. That is, the repeating units derived from a conjugated diene may or may not have an unsaturated bond such as a carbon-carbon double bond. The second block is composed of, for example, repeating units derived from a conjugated diene.

[0043] The block copolymer contained in the binder 113 may be a styrene-based triblock copolymer. Examples of styrene-based triblock copolymers include styrene-ethylene / butylene-styrene block copolymer (SEBS), styrene-ethylene / propylene-styrene block copolymer (SEPS), styrene-ethylene / ethylene / propylene-styrene block copolymer (SEEPS), styrene-butadiene-styrene block copolymer (SBS), and styrene-isoprene-styrene block copolymer (SIS). These styrene-based triblock copolymers are sometimes called styrene-based thermoplastic elastomers. These styrene-based triblock copolymers tend to be flexible and have high strength. Therefore, when the binder 113 contains a styrene-based triblock copolymer, the peel strength between the active material layer 110 and the current collector 100 in the electrode 1000 tends to be further improved.

[0044] The block copolymer contained in the binder 113 may be a hydrogenated product. A hydrogenated product refers to a copolymer in which unsaturated bonds such as carbon-carbon double bonds contained in the block copolymer have been hydrogenated. In particular, in the second block of the block copolymer, repeating units derived from conjugated dienes may be hydrogenated. In the present disclosure, a copolymer obtained by hydrogenating a styrene-based triblock copolymer having unsaturated bonds such as carbon-carbon double bonds may be referred to as a hydrogenated styrene-based triblock copolymer. The hydrogenation rate of the block copolymer may be 90% or more, 95% or more, or even 99% or more. The hydrogenation rate of the block copolymer refers to the ratio of the number of carbon-carbon double bonds converted to single bonds by hydrogenation to the number of carbon-carbon double bonds contained in the block copolymer before hydrogenation. The hydrogenation rate of the block copolymer can be determined by proton nuclear magnetic resonance ( 1 It can be identified by H NMR measurement.

[0045] Examples of hydrogenated styrene triblock copolymers include styrene-ethylene / butylene-styrene block copolymer (SEBS), styrene-ethylene / propylene-styrene block copolymer (SEPS), and styrene-ethylene / ethylene / propylene-styrene block copolymer (SEEPS). That is, the block copolymer contained in the binder 113 may include at least one selected from the group consisting of SEBS, SEPS, and SEEPS. Hydrogenated styrene triblock copolymers tend to be more flexible and have higher strength. Therefore, when the binder 113 includes a hydrogenated styrene triblock copolymer, the peel strength between the active material layer 110 and the current collector 100 in the electrode 1000 tends to be further improved.

[0046] The block copolymer contained in the binder 113 may contain a modifying group. The modifying group refers to a functional group that chemically modifies all repeating units contained in the polymer chain, some repeating units contained in the polymer chain, or the terminal portion of the polymer chain. The modifying group can be introduced into the polymer chain by a substitution reaction, an addition reaction, or the like. The modifying group includes, for example, elements such as O and N, which have relatively high electronegativity, and Si, which have relatively low electronegativity. The modifying group containing such elements can impart polarity to the block copolymer. Examples of the modifying group include carboxylic acid groups, acid anhydride groups, acyl groups, hydroxy groups, sulfo groups, sulfanyl groups, phosphate groups, phosphonate groups, isocyanate groups, epoxy groups, silyl groups, amino groups, nitrile groups, and nitro groups. A specific example of an acid anhydride group is a maleic anhydride group. When the block copolymer contains a modifying group, interaction between the binder 113 and the metal contained in the current collector 100 may occur. This interaction tends to further improve the peel strength between active material layer 110 and current collector 100 in electrode 1000.

[0047] The block copolymer contained in the binder 113 may contain a modifying group as a nitrogen component. The modifying group containing a nitrogen component is a nitrogen-containing functional group, such as an amino group of an amine compound. The modifying group may be located at the end of the polymer chain. The block copolymer contained in the binder 113 may be, for example, a hydrogenated styrene-based triblock copolymer modified with an amine terminal.

[0048] In binder 113, the weight average molecular weight (M w) is 170,000 or more. The weight-average molecular weight of the block copolymer may be 200,000 or more, 230,000 or more, 300,000 or more, or 400,000 or more. The upper limit of the weight-average molecular weight of the block copolymer is not particularly limited, and is, for example, 1,000,000. The weight-average molecular weight can be determined by gel permeation chromatography (GPC) measurement using polystyrene as a standard sample. In other words, the weight-average molecular weight is a value converted into polystyrene. In GPC measurement, chloroform may be used as the eluent. When two or more peak tops are observed in a GPC chart, the weight-average molecular weight calculated from the entire peak range including each peak top can be considered as the weight-average molecular weight of the block copolymer.

[0049] In the binder 113, the polydispersity of the block copolymer may be 1.6 or less, 1.5 or less, 1.4 or less, or 1.3 or less. The lower limit of the polydispersity of the block copolymer is not particularly limited, and is, for example, 1.1. The polydispersity of the block copolymer is determined by the number average molecular weight (M n ) to the weight average molecular weight (M w ) ratio (M w / M n ) The number-average molecular weight of the block copolymer can be determined by the GPC measurement described above for the weight-average molecular weight. When the polydispersity of the block copolymer is 1.6 or less and the molecular weight distribution is narrow, the polymer chains of the multiple block copolymers interact more uniformly. This tends to further improve the peel strength between the active material layer 110 and the current collector 100 in the electrode 1000.

[0050] In the block copolymer of binder 113, the average degree of polymerization of the first block may be 210 or more, 230 or more, 250 or more, 270 or more, 280 or more, 300 or more, 350 or more, 400 or more, or 460 or more. The upper limit of the average degree of polymerization of the first block is not particularly limited and is, for example, 1000. When the average degree of polymerization of the first block is 210 or more, the adhesive strength between active material layer 110 and current collector 100 in electrode 1000 of embodiment 1 tends to be further improved.

[0051] In the block copolymer of the binder 113, the average degree of polymerization of the first block is the average value of the degree of polymerization per first block. For example, when the block copolymer is an ABA triblock copolymer, the average degree of polymerization of the first block corresponds to the average number of repeating units in the two A blocks contained in one polymer chain constituting the triblock copolymer. When the block copolymer is an ABA triblock copolymer, the average degree of polymerization of the first block corresponds to the number average molecular weight (M n ), the molar fraction (φ) of the repeating unit having an aromatic ring in the block copolymer, the molecular weight (M1) of the repeating unit having an aromatic ring, and the molecular weight (M2) of the repeating unit constituting the second block, can be calculated using the following formula (i):

number

[0052] In addition, in a block copolymer, when the ratio of the degree of polymerization of the repeating unit having an aromatic ring to the degree of polymerization of the repeating unit constituting the second block is m:n, the molar fraction (φ) of the repeating unit having an aromatic ring in the block copolymer can be calculated by φ=m / (m+n). The molar fraction (φ) of the repeating unit having an aromatic ring in the block copolymer can be determined, for example, by proton nuclear magnetic resonance ( 1 It can be determined by H NMR measurement.

[0053] The binder 113 may contain a binder other than a block copolymer, such as a binding agent that may generally be used as a binder for batteries. Alternatively, the binder 113 may be a block copolymer. In other words, the binder 113 may contain only a block copolymer.

[0054] Examples of binders include polyvinylidene fluoride (PVDF), polytetrafluoroethylene (PTFE), polyethylene, polypropylene, aramid resin, polyamide, polyimide, polyamideimide, polyacrylonitrile, polyacrylic acid, polyacrylic acid methyl ester, polyacrylic acid ethyl ester, polyacrylic acid hexyl ester, polymethacrylic acid, polymethacrylic acid methyl ester (PMMA), polymethacrylic acid ethyl ester, polymethacrylic acid hexyl ester, polyvinyl acetate, polyvinylpyrrolidone, polyether, polycarbonate, polyethersulfone, polyetherketone, polyetheretherketone, polyphenylene sulfide, hexafluoropolypropylene, styrene butadiene rubber, carboxymethyl cellulose, and ethyl cellulose. The binder may be a copolymer synthesized using two or more monomers selected from the group consisting of tetrafluoroethylene, hexafluoroethylene, hexafluoropropylene, perfluoroalkyl vinyl ether, vinylidene fluoride, chlorotrifluoroethylene, ethylene, propylene, butadiene, isoprene, styrene, pentafluoropropylene, fluoromethyl vinyl ether, acrylic acid ester, acrylic acid, and hexadiene. These may be used alone or in combination of two or more.

[0055] The binder may contain an elastomer from the viewpoint of excellent binding properties. Elastomer refers to a polymer having rubber elasticity. The elastomer used as the binder 113 may be a thermoplastic elastomer or a thermosetting elastomer. In addition to the styrene-based elastomers mentioned above, examples of the elastomer include butadiene rubber (BR), isoprene rubber (IR), chloroprene rubber (CR), acrylonitrile-butadiene rubber (NBR), hydrogenated isoprene rubber (HIR), hydrogenated butyl rubber (HIIR), hydrogenated nitrile rubber (HNBR), and acrylate butadiene rubber (ABR). A mixture containing two or more selected from these may also be used.

[0056] <Active material> In the first embodiment, the active material 112 is a positive electrode active material or a negative electrode active material. When the active material 112 is a positive electrode active material, the electrode 1000 can be used as a positive electrode. When the active material 112 is a negative electrode active material, the electrode 1000 can be used as a negative electrode.

[0057] The positive electrode active material as the active material 112 is, for example, a material that has the property of absorbing and releasing metal ions (e.g., lithium ions). Examples of the positive electrode active material include lithium-containing transition metal oxides, transition metal fluorides, polyanionic materials, fluorinated polyanionic materials, transition metal sulfides, transition metal oxysulfides, and transition metal oxynitrides. Examples of lithium-containing transition metal oxides include Li(Ni,Co,Al)O2, Li(Ni,Co,Mn)O2, and LiCoO2. The active material 112 includes, for example, a lithium-containing transition metal oxide. Using a lithium-containing transition metal oxide as the active material 112 can reduce the manufacturing costs of the electrode 1000 and the battery and improve the average discharge voltage of the battery.

[0058] The active material 112 may include lithium nickel-cobalt manganese oxide, which is suitable for improving the energy density of the battery. For example, the positive electrode active material as the active material 112 may be Li(Ni,Co,Mn)O.

[0059] The negative electrode active material as the active material 112 is, for example, a material that has the property of absorbing and releasing metal ions (e.g., lithium ions). Examples of the negative electrode active material include metal materials, carbon materials, oxides, nitrides, tin compounds, and silicon compounds. The metal material may be a single metal or an alloy. Examples of the metal material include lithium metal and lithium alloys. Examples of the carbon material include natural graphite, coke, partially graphitized carbon, carbon fiber, spherical carbon, artificial graphite, and amorphous carbon. The capacity density of the battery can be improved by using silicon (Si), tin (Sn), a silicon compound, a tin compound, or the like as the active material 112. The safety of the battery can be improved by using an oxide compound containing titanium (Ti) or niobium (Nb) as the active material 112.

[0060] <Solid electrolyte> In the first embodiment, a sulfide solid electrolyte, an oxide solid electrolyte, a halide solid electrolyte, a polymer solid electrolyte, a complex hydride solid electrolyte, or the like can be used as the solid electrolyte 111. The solid electrolyte 111 may include a halide solid electrolyte.

[0061] In the present disclosure, the term "oxide solid electrolyte" refers to a solid electrolyte containing oxygen. The oxide solid electrolyte may further contain anions other than sulfur and halogen elements as anions other than oxygen.

[0062] In this disclosure, the term "halide solid electrolyte" refers to a solid electrolyte containing a halogen element but not containing sulfur. In this disclosure, the term "sulfur-free solid electrolyte" refers to a solid electrolyte represented by a composition formula that does not contain sulfur. Therefore, a solid electrolyte containing only a trace amount of sulfur, for example, 0.1 mass % or less of sulfur, is included in the category of sulfur-free solid electrolyte. The halide solid electrolyte may further contain oxygen as an anion other than the halogen element.

[0063] Examples of sulfide solid electrolytes include Li2S-P2S5, Li2S-SiS2, Li2S-B2S3, Li2S-GeS2, and Li 3.25 Ge 0.25 P 0.75 S4, Li 10 GeP2S 12 These can be used in addition to LiX, Li2O, MO q , Li p MO q The element X in "LiX" is at least one element selected from the group consisting of F, Cl, Br, and I. q " and "Li p MO q "The element M is at least one element selected from the group consisting of P, Si, Ge, B, Al, Ga, In, Fe, and Zn. q " and "Li p MO q In the above formula, p and q are each independently a natural number.

[0064] The sulfide solid electrolyte may be, for example, a Li2S-P2S5-based glass ceramic. The Li2S-P2S5-based glass ceramic may contain LiX, Li2O, MO, q , Li p MO q Alternatively, two or more selected from LiCl, LiBr, and LiI may be added. Since Li2S-P2S5-based glass ceramics are relatively soft materials, a solid electrolyte sheet containing Li2S-P2S5-based glass ceramics can be used to manufacture a battery with higher durability.

[0065] Examples of oxide solid electrolytes include NASICON-type solid electrolytes, such as LiTi2(PO4)3 and its elemental substitution products, (LaLi)TiO3-based perovskite-type solid electrolytes, and Li 14 ZnGeO 16 , Li4SiO4, LiGeO4 and their element-substituted LISICON-type solid electrolytes, Li7La3Zr2O 12Garnet-type solid electrolytes, such as those substituted with LiPO4 and its N-substituted derivatives, and glasses and glass ceramics based on Li-BO compounds such as LiBO2 and LiBO3, to which LiSO4, LiCO3, etc. are added, can be used.

[0066] The halide solid electrolyte contains, for example, Li, M1, and X. M1 is at least one selected from the group consisting of metal elements and metalloid elements other than Li. X is at least one selected from the group consisting of F, Cl, Br, and I. The halide solid electrolyte has high thermal stability, thereby improving the safety of the battery. Furthermore, the halide solid electrolyte does not contain sulfur, thereby suppressing the generation of hydrogen sulfide gas. On the other hand, the halide solid electrolyte is a harder and more brittle material than the sulfide solid electrolyte. According to the electrode 1000 of the first embodiment, even when a halide solid electrolyte is used, the peel strength between the active material layer 110 and the current collector 100 can be more effectively improved.

[0067] In the present disclosure, "metalloid elements" are B, Si, Ge, As, Sb and Te.

[0068] In this disclosure, "metal element" refers to all elements in Groups 1 to 12 of the Periodic Table excluding hydrogen, and all elements in Groups 13 to 16 of the Periodic Table excluding B, Si, Ge, As, Sb, Te, C, N, P, O, S, and Se.

[0069] That is, in the present disclosure, "metalloid elements" and "metal elements" are a group of elements that can become cations when forming an inorganic compound with a halogen element.

[0070] For example, the halide solid electrolyte may be a material represented by the following composition formula (1). Li α M1 β X γ ...Equation (1)

[0071] In the above composition formula (1), α, β, and γ are each independently a value greater than 0. γ can be 4, 6, or the like.

[0072] According to the above configuration, the ionic conductivity of the halide solid electrolyte is improved, and therefore the ionic conductivity of electrode 1000 according to embodiment 1 can be improved. Therefore, when electrode 1000 according to embodiment 1 is used in a battery, the cycle characteristics of the battery can be further improved.

[0073] In the above composition formula (1), the element M1 may contain Y (=yttrium), that is, the halide solid electrolyte may contain Y as a metal element.

[0074] The halide solid electrolyte containing Y may be represented by, for example, the following composition formula (2). Li a Me b Y c X6...Formula (2)

[0075] In formula (2), a, b, and c may satisfy a+mb+3c=6 and c>0. The element Me is at least one element selected from the group consisting of metal elements and metalloid elements other than Li and Y. m represents the valence of the element Me. When the element Me contains multiple elements, mb is the sum of the products of the composition ratios of each element and the valences of the elements. For example, when Me contains the element Me1 and the element Me2, and the composition ratio of the element Me1 is b1, the valence of the element Me1 is m1, the composition ratio of the element Me2 is b2, and the valence of the element Me2 is m2, mb is represented by m1b1+m2b2. In the above composition formula (2), the element X is at least one element selected from the group consisting of F, Cl, Br, and I.

[0076] The element Me may be, for example, at least one selected from the group consisting of Mg, Ca, Sr, Ba, Zn, Sc, Al, Ga, Bi, Zr, Hf, Ti, Sn, Ta, Gd, and Nb.

[0077] As the halide solid electrolyte, for example, the following materials can be used. According to the following materials, since the ionic conductivity of the solid electrolyte 111 is further improved, the ionic conductivity of the electrode 1000 in Embodiment 1 can be further improved. Thereby, the electrode 1000 in Embodiment 1 can further improve the cycle characteristics of the battery.

[0078] The halide solid electrolyte may be a material represented by the following compositional formula (A1). Li 6-3d Y d X6 ··· Formula (A1)

[0079] In the compositional formula (A1), the element X is at least one selected from the group consisting of Cl, Br, and I. In the compositional formula (A1), d satisfies 0 < d < 2.

[0080] The halide solid electrolyte may be a material represented by the following compositional formula (A2). Li3YX6 ··· Formula (A2)

[0081] In the compositional formula (A2), the element X is at least one selected from the group consisting of Cl, Br, and I.

[0082] The halide solid electrolyte may be a material represented by the following compositional formula (A3). Li 3-3δ Y 1+δ Cl6 ··· Formula (A3)

[0083] In the compositional formula (A3), δ satisfies 0 < δ ≤ 0.15.

[0084] The halide solid electrolyte may be a material represented by the following compositional formula (A4). Li 3-3δ Y 1+δ Br6 ··· Formula (A4)

[0085] In the compositional formula (A4), δ satisfies 0 < δ ≤ 0.25.

[0086] The halide solid electrolyte may be a material represented by the following composition formula (A5). Li 3-3δ+a Y 1+δ-a Me a Cl 6-x-y Br x I y ...Formula (A5)

[0087] In the composition formula (A5), the element Me is at least one element selected from the group consisting of Mg, Ca, Sr, Ba, and Zn.

[0088] Furthermore, in the composition formula (A5), -1<δ<2, 0 <a<3、 0<(3-3δ+a), 0<(1+δ-a), 0≦x≦6, 0 ≤ y ≤ 6, and (x+y)≦6, is met.

[0089] The halide solid electrolyte may be a material represented by the following composition formula (A6): Li 3-3δ Y 1+δ-a Me a Cl 6-x-y Br x I y ...Formula (A6)

[0090] In the composition formula (A6), the element Me is at least one element selected from the group consisting of Al, Sc, Ga, and Bi.

[0091] Furthermore, in the above composition formula (A6), -1<δ<1, 0 <a<2、 0<(1+δ-a), 0≦x≦6, 0 ≤ y ≤ 6, and (x+y)≦6, is met.

[0092] The halide solid electrolyte may be a material represented by the following composition formula (A7): Li 3-3δ-a Y 1+δ-a Me a Cl 6-x-y Br x I y ...Formula (A7)

[0093] In the composition formula (A7), the element Me is at least one element selected from the group consisting of Zr, Hf, and Ti.

[0094] Furthermore, in the composition formula (A7), -1<δ<1, 0 <a<1.5、 0<(3-3δ-a), 0<(1+δ-a), 0≦x≦6, 0 ≤ y ≤ 6, and (x+y)≦6, is met.

[0095] The halide solid electrolyte may be a material represented by the following composition formula (A8). Li 3-3δ-2a Y 1+δ-a Me a Cl 6-x-y Br x I y ...Formula (A8)

[0096] In the composition formula (A8), the element Me is at least one element selected from the group consisting of Ta and Nb.

[0097] Furthermore, in the above composition formula (A8), -1<δ<1, 0 <a<1.2、 0<(3-3δ-2a), 0<(1+δ-a), 0≦x≦6, 0 ≤ y ≤ 6, and (x+y)≦6, is met.

[0098] The halide solid electrolyte may be a compound containing Li, M2, O (oxygen), and X2. The element M2 contains at least one selected from the group consisting of, for example, Nb and Ta. Also, X2 is at least one selected from the group consisting of F, Cl, Br, and I.

[0099] The compound containing Li, M2, X2, and O (oxygen) may be represented, for example, by the composition formula: Li x M2O y X2 5+x―2y where x may satisfy 0.1 < x < 7.0. y may satisfy 0.4 < y < 1.9.

[0100] More specifically, as the halide solid electrolyte, for example, Li3Y(Cl,Br,I)6, Li 2.7 Y 1.1 (Cl,Br,I)6, Li2Mg(F,Cl,Br,I)4, Li2Fe(F,Cl,Br,I)4, Li(Al,Ga,In)(F,Cl,Br,I)4, Li3(Al,Ga,In)(F,Cl,Br,I)6, Li3(Ca,Y,Gd)(Cl,Br,I)6, Li 2.7 (Ti,Al)F6, Li 2.5 (Ti,Al)F6, Li(Ta,Nb)O(F,Cl)4, etc. can be used. In the present disclosure, when an element in the formula is represented as "(Al,Ga,In)", this notation indicates at least one element selected from the group of elements within the parentheses. That is, "(Al,Ga,In)" is synonymous with "at least one selected from the group consisting of Al, Ga, and In". The same applies to other elements.

[0101] As the polymer solid electrolyte, for example, a compound of a polymer compound and a lithium salt can be used. The polymer compound may have an ethylene oxide structure. A polymer compound having an ethylene oxide structure can contain a large amount of lithium salt. Therefore, the ionic conductivity can be further improved. As the lithium salt, LiPF6, LiBF4, LiSbF6, LiAsF6, LiSO3CF3, LiN(SO2F)2, LiN(SO2CF3)2, LiN(SO2C2F5)2, LiN(SO2CF3)(SO2C4F9), LiC(SO2CF3)3, etc. can be used. One type of lithium salt may be used alone, or two or more types may be used in combination.

[0102] Examples of the complex hydride solid electrolyte that can be used include LiBH4-LiI and LiBH4-P2S5.

[0103] <Active material layer> As described above, the active material layer 110 contains the solid electrolyte 111. With this configuration, the ionic conductivity inside the active material layer 110 is improved, and the battery can operate at high power output.

[0104] When the solid electrolyte 111 contained in the active material layer 110 is particulate (for example, spherical), the median diameter of the solid electrolyte 111 may be 100 μm or less. When the median diameter of the solid electrolyte 111 is 100 μm or less, the active material 112 and the solid electrolyte 111 can be well dispersed in the active material layer 110. This improves the charge / discharge characteristics of the battery.

[0105] The median diameter of the solid electrolyte 111 contained in the active material layer 110 may be smaller than the median diameter of the active material 112. This allows the solid electrolyte 111 and the active material 112 to be dispersed well.

[0106] The median diameter of the active material 112 may be 0.1 μm or more and 100 μm or less. When the median diameter of the active material is 0.1 μm or more, the active material 112 and the solid electrolyte 111 can be well dispersed in the active material layer 110. As a result, the charge / discharge characteristics of a battery using the electrode 1000 are improved. When the median diameter of the active material 112 is 100 μm or less, the lithium diffusion rate within the active material is improved. As a result, a battery using the electrode 1000 can operate at high power.

[0107] The median diameter refers to the particle size at which the cumulative volume in the volume-based particle size distribution is equal to 50%. The volume-based particle size distribution is determined by a laser diffraction scattering method. The same applies to the other materials listed below.

[0108] In the active material layer 110, the volume ratio "v1:100-v1" of the active material 112 to the solid electrolyte 111 may satisfy 30≦v1≦95. v1 indicates the volume ratio of the active material 112 when the total volume of the active material 112 and the solid electrolyte 111 contained in the active material layer 110 is taken as 100. When 30≦v1 is satisfied, it is easy to ensure sufficient energy density for the battery. When v1≦95 is satisfied, it is easy to operate the battery at high output.

[0109] The thickness of the active material layer 110 may be 10 μm or more and 500 μm or less. When the thickness of the active material layer 110 is 10 μm or more, the battery can easily ensure a sufficient energy density. When the thickness of the active material layer 110 is 500 μm or less, the battery can more easily operate at high power.

[0110] The active material 112 may be coated with a coating material to reduce the interface resistance with the solid electrolyte 111. A material with low electronic conductivity can be used as the coating material. Examples of the coating material that can be used include an oxide material and an oxide solid electrolyte.

[0111] Examples of oxide materials that can be used for the coating material include SiO2, Al2O3, TiO2, B2O3, Nb2O5, WO3, and ZrO2.

[0112] Examples of oxide solid electrolytes used in coating materials include Li-Nb-O compounds such as LiNbO3, Li-BO compounds such as LiBO2 and Li3BO3, Li-Al-O compounds such as LiAlO2, Li-Si-O compounds such as Li4SiO4, Li-SO compounds such as Li2SO4, and Li4Ti5O 12 Examples of usable oxide solid electrolytes include Li-Ti-O compounds such as Li2ZrO3, Li-Zr-O compounds such as Li2MoO3, Li-VO compounds such as LiV2O5, and Li-WO compounds such as Li2WO4. Oxide solid electrolytes have high ionic conductivity and high potential stability. Therefore, using oxide solid electrolytes as coating materials can further improve the charge / discharge efficiency of batteries.

[0113] The coating material that coats the active material 112 may further contain the above-mentioned halide solid electrolyte in addition to the above-mentioned oxide solid electrolyte. The active material layer 110 may contain the active material 112 coated with this coating material and a sulfide solid electrolyte as the solid electrolyte 111.

[0114] In the active material layer 110, the ratio of the binder 113 to the solid electrolyte 111 may be 0.5% by mass or more and 10% by mass or less, 1% by mass or more and 6% by mass or less, or 1% by mass or more and 5% by mass or less. When the ratio of the binder 113 to the solid electrolyte 111 is 0.5% by mass or more, the binder 113 tends to bind more particles of the solid electrolyte 111 together. This can improve the film strength of the active material layer 110. When the ratio of the binder 113 to the solid electrolyte 111 is 10% by mass or less, the contact between particles of the solid electrolyte 111 in the active material layer 110 tends to improve. This can improve the ionic conductivity of the active material layer 110.

[0115] [Current collector] Current collector 100 in embodiment 1 has substrate 101 and coating layer 102. Coating layer 102 coats substrate 101 and is in contact with active material layer 110. Coating layer 102 contains conductive carbon. As described above, with this configuration, in electrode 1000 in embodiment 1, an interaction occurs between the aromatic ring of the block copolymer contained in binder 113 in active material layer 110 and the conductive carbon contained in coating layer 102 in current collector 100. This interaction can improve the adhesion between active material layer 110 and current collector 100.

[0116] <Coating layer> The covering layer 102 in the first embodiment may cover the entire main surface of the substrate 101, or may cover only a portion of the main surface of the substrate 101. The "main surface" refers to the surface of the substrate 101 that has the largest area. The covering layer 102 is located between the substrate 101 and the active material layer 110, and is in contact with both the substrate 101 and the active material layer 110. The shape of the covering layer 102 may be dot-like, striped, or the like.

[0117] Examples of conductive carbon contained in the coating layer 102 include graphites such as natural graphite and artificial graphite, carbon blacks such as acetylene black (AB) and ketjen black (KB), vapor grown carbon (VGCF (registered trademark)), and conductive fibers such as carbon nanotubes (CNT).

[0118] The content of conductive carbon in the coating layer 102 is not particularly limited and may be, for example, 5% by mass or more and 80% by mass or less, or may be 10% by mass or more and 60% by mass or less, or may be 15% by mass or more and 45% by mass or less. When the content of conductive carbon is 5% by mass or more, the electrical conductivity of the coating layer 102 is improved, thereby enabling a higher output battery. When the content of conductive carbon is 80% by mass or less, the presence of a sufficient amount of a binder, etc., as described below, tends to prevent peeling of the coating layer 102.

[0119] The coating layer 102 may contain elements or components other than conductive carbon. These elements or components may be added to the coating layer 102 due to contamination or other reasons. For example, an unavoidable oxide film or the like may be formed on a portion of the surface of the coating layer 102. That is, the coating layer 102 may contain unavoidable oxides or the like. Furthermore, the coating layer 102 may contain a binder. A coating layer 102 containing a binder tends to be easily maintained on the substrate 101. The binder is not particularly limited, and the binders described above may be used. Examples of binders that may be used include fluororesins such as polytetrafluoroethylene (PTFE), tetrafluoroethylene-perfluoroalkyl vinyl ether copolymer (PFA), and polyvinylidene fluoride (PVDF). Because fluororesins have excellent solvent resistance, peeling of the coating layer 102 can be suppressed even when the active material layer 110 is fabricated by a wet coating method.

[0120] The coating layer 102 can be produced, for example, by a method of sputtering the material of the coating layer 102 onto the surface of the substrate 101. The coating layer 102 may also be produced by applying a solution or dispersion containing the material of the coating layer 102 to the surface of the substrate 101. The solution or dispersion can be applied using a gravure coater, a die coater, or the like.

[0121] When a solution or dispersion containing the material of the coating layer 102 is applied to the surface of the substrate 101, the coating weight of the material of the coating layer 102 is not particularly limited, and may be, for example, 0.01 g / m 2 More than 5g / m 2 less than or equal to 0.1 g / m 2 More than 3g / m 2 The coating weight may be 0.01 g / m or less. 2 When the coating weight is 5 g / m or more, contact between the substrate 101 and the active material layer 110 can be sufficiently prevented, thereby suppressing corrosion of the substrate 101. 2 If it is equal to or less than this, the electrical resistance of the coating layer 102 is reduced, and the battery can be easily operated at high power.

[0122] The thickness of the coating layer 102 is not particularly limited and may be, for example, 0.001 μm or more and 5 μm or less, or 0.1 μm or more and 2 μm or less. When the thickness of the coating layer 102 is 0.001 μm or more, contact between the substrate 101 and the active material layer 110 can be sufficiently prevented, thereby suppressing corrosion of the substrate 101. When the thickness of the coating layer 102 is 5 μm or less, the electrical resistance of the coating layer 102 decreases, allowing the battery to easily operate at high power.

[0123] <Substrate> The substrate 101 has, for example, a plate shape. The material of the substrate 101 may be a metal or an alloy. Examples of metals include aluminum, iron, nickel, and copper. Examples of metal alloys include aluminum alloys and stainless steel (SUS). The substrate 101 may contain aluminum or an aluminum alloy.

[0124] The substrate 101 may contain aluminum as a main component. "The substrate 101 contains aluminum as a main component" means that the aluminum content in the substrate 101 is 50% by mass or more. Aluminum is a lightweight metal with high electrical conductivity. Therefore, an electrode 1000 including a substrate 101 containing aluminum as a main component can improve the weight energy density of a battery. The substrate 101 containing aluminum as a main component may further contain elements other than aluminum. Note that if the substrate 101 consists only of aluminum, that is, if the aluminum content in the substrate 101 is 100%, the strength of the substrate 101 may be reduced. Therefore, the substrate 101 may contain elements other than aluminum. The aluminum content in the substrate 101 may be 99% by mass or less, or may be 90% by mass or less.

[0125] The substrate 101 may contain an aluminum alloy. Aluminum alloys are lightweight and have high strength. Therefore, an electrode 1000 including a substrate 101 containing an aluminum alloy can realize a battery that achieves both high energy density per weight and high durability. The aluminum alloy is not particularly limited, and examples thereof include an Al-Cu alloy, an Al-Mn alloy, an Al-Mn-Cu alloy, and an Al-Fe-Cu alloy.

[0126] An Al-Mn alloy may be used as the material for substrate 101 in the first embodiment. Al-Mn alloys have high strength, as well as excellent formability and corrosion resistance. Therefore, an electrode 1000 including a substrate 101 containing an Al-Mn alloy can improve the cycle characteristics of a battery.

[0127] The thickness of the substrate 101 is not particularly limited and may be, for example, 0.1 μm to 50 μm, or 1 μm to 30 μm. When the thickness of the substrate 101 is 0.1 μm or more, the strength of the substrate 101 is improved, and therefore damage to the substrate 101 is suppressed. When the thickness of the substrate 101 is 50 μm or less, the electrical resistance of the substrate 101 is reduced, and the battery can easily operate at high power.

[0128] <Current collector> The current collector 100 has, for example, a plate shape. The thickness of the current collector 100 may be 0.1 μm or more and 1 mm or less. When the thickness of the current collector 100 is 0.1 μm or more, the strength of the current collector 100 is improved, and breakage of the current collector 100 is suppressed. When the thickness of the current collector 100 is 1 mm or less, the electrical resistance of the electrode 1000 is reduced, and the battery can easily operate at high power. In other words, by appropriately adjusting the thickness of the current collector 100, batteries can be manufactured stably and the battery can operate at high power.

[0129] [Electrode manufacturing method] The electrode 1000 of the first embodiment can be fabricated, for example, by the following method. First, a dispersion containing a solid electrolyte 111, an active material 112, and a binder 113 for forming the active material layer 110 is prepared. The dispersion may be a slurry in which the solid electrolyte 111, the active material 112, and the binder 113 are dispersed in a solvent. The solvent may be a solvent that does not react with the solid electrolyte 111, such as an aromatic hydrocarbon solvent such as toluene. Next, the dispersion is applied to the coating layer 102 of the current collector 100. Examples of methods for applying the dispersion include die coating, gravure coating, doctor blade coating, bar coating, spray coating, and electrostatic coating. The active material layer 110 is formed by drying the resulting coating, thereby obtaining the electrode 1000. The method for drying the coating is not particularly limited. For example, the coating may be dried by heating the coating at a temperature of 80°C or higher for at least one minute. The coating may be dried in a vacuum or reduced-pressure atmosphere. The method of forming active material layer 110 by applying a dispersion onto coating layer 102 is sometimes called a wet coating method.

[0130] (Embodiment 2) The following describes the second embodiment. Explanations that overlap with the first embodiment will be omitted where appropriate.

[0131] FIG. 2 shows a cross-sectional view of a battery 2000 according to the second embodiment.

[0132] The battery 2000 in the second embodiment includes a positive electrode 201 , a negative electrode 203 , and an electrolyte layer 202 .

[0133] At least one selected from the group consisting of the positive electrode 201 and the negative electrode 203 is the electrode 1000 in the above-described first embodiment. That is, at least one selected from the group consisting of the positive electrode 201 and the negative electrode 203 includes the active material layer 110 and the current collector 100 described in the first embodiment.

[0134] The electrolyte layer 202 is located between the positive electrode 201 and the negative electrode 203 .

[0135] With the above configuration, the battery 2000 of the second embodiment can improve the output characteristics.

[0136] As shown in FIG. 2, in a battery 2000 according to the second embodiment, the positive electrode 201 may be the electrode 1000 according to the first embodiment. In this case, the positive electrode 201 includes the active material layer 110 and the current collector 100 described in the first embodiment. The following describes a battery 2000 in which the positive electrode 201 is the electrode 1000. However, the battery 2000 according to the second embodiment is not limited to the following configuration. In the battery 2000, the negative electrode 203 may be the electrode 1000 according to the first embodiment.

[0137] According to the above configuration, the output characteristics of the battery 2000 can be further improved.

[0138] The electrolyte layer 202 is a layer containing an electrolyte material. Examples of the electrolyte material include solid electrolytes. That is, the electrolyte layer 202 may be a solid electrolyte layer. The solid electrolyte contained in the electrolyte layer 202 may be any of the solid electrolytes exemplified as the solid electrolyte 111 in the first embodiment, and examples of the solid electrolyte that may be used include sulfide solid electrolytes, oxide solid electrolytes, halide solid electrolytes, polymer solid electrolytes, and complex hydride solid electrolytes. The solid electrolyte may be a halide solid electrolyte. Halide solid electrolytes have high thermal stability, and therefore can improve the safety of the battery 2000.

[0139] The electrolyte layer 202 may contain a solid electrolyte as a main component. The electrolyte layer 202 may contain 70% or more (70 mass % or more) of the solid electrolyte in terms of mass ratio relative to the entire electrolyte layer 202.

[0140] According to the above configuration, the charge and discharge characteristics of the battery 2000 can be improved.

[0141] The electrolyte layer 202 contains a solid electrolyte as a main component, and may further contain unavoidable impurities, or starting materials, by-products, decomposition products, and the like used in synthesizing the solid electrolyte.

[0142] The electrolyte layer 202 may contain a solid electrolyte in a mass ratio of 100% (100 mass %) relative to the entire electrolyte layer 202, excluding unavoidable impurities.

[0143] According to the above configuration, the charge and discharge characteristics of the battery 2000 can be further improved.

[0144] The electrolyte layer 202 may contain two or more of the materials listed as solid electrolytes. For example, the electrolyte layer 202 may contain a halide solid electrolyte and a sulfide solid electrolyte.

[0145] The thickness of the electrolyte layer 202 may be 1 μm or more and 300 μm or less. When the thickness of the electrolyte layer 202 is 1 μm or more, the possibility of short-circuiting between the positive electrode 201 and the negative electrode 203 decreases. When the thickness of the electrolyte layer 202 is 300 μm or less, the battery 2000 can easily operate at high power. That is, when the thickness of the electrolyte layer 202 is appropriately adjusted, the safety of the battery 2000 can be sufficiently ensured, and the battery 2000 can be operated at high power.

[0146] The shape of the solid electrolyte contained in the battery 2000 is not particularly limited. The shape of the solid electrolyte may be needle-like, spherical, oval-spherical, etc. The shape of the solid electrolyte may also be particulate.

[0147] The negative electrode 203 may contain an electrolyte material, for example, a solid electrolyte. As the solid electrolyte, any of the solid electrolytes exemplified as materials constituting the electrolyte layer 202 may be used. With the above configuration, ion conductivity (e.g., lithium ion conductivity) inside the negative electrode 203 is improved, and the battery 2000 can operate at high power.

[0148] The negative electrode 203 contains, for example, a material having the property of absorbing and releasing metal ions (for example, lithium ions) as a negative electrode active material. The materials exemplified in the above-mentioned first embodiment may also be used as the negative electrode active material.

[0149] The median diameter of the negative electrode active material may be 0.1 μm or more and 100 μm or less. When the median diameter of the negative electrode active material is 0.1 μm or more, the negative electrode active material and the solid electrolyte can be well dispersed in the negative electrode 203. This improves the charge / discharge characteristics of the battery 2000. When the median diameter of the negative electrode active material is 100 μm or less, the lithium diffusion rate within the negative electrode active material improves. This allows the battery 2000 to operate at high power.

[0150] The median diameter of the negative electrode active material may be larger than the median diameter of the solid electrolyte, which allows the solid electrolyte and the negative electrode active material to be dispersed well.

[0151] In the negative electrode 203, the volume ratio "v2:100-v2" of the negative electrode active material to the solid electrolyte may satisfy 30≦v2≦95. v2 indicates the volume ratio of the negative electrode active material when the total volume of the negative electrode active material and solid electrolyte contained in the negative electrode 203 is taken as 100. When 30≦v2 is satisfied, it is easy to ensure sufficient energy density for the battery 2000. When v2≦95 is satisfied, it is easy to operate the battery 2000 at high output.

[0152] The thickness of the negative electrode 203 may be 10 μm or more and 500 μm or less. When the thickness of the negative electrode 203 is 10 μm or more, a sufficient energy density can be easily ensured for the battery 2000. When the thickness of the negative electrode 203 is 500 μm or less, the battery 2000 can more easily operate at high power.

[0153] The negative electrode active material may be coated with a coating material to reduce the interfacial resistance with the solid electrolyte. A material with low electronic conductivity may be used as the coating material. An oxide material, an oxide solid electrolyte, or the like may be used as the coating material. The materials exemplified in the first embodiment may also be used as the coating material.

[0154] At least one selected from the group consisting of the electrolyte layer 202 and the negative electrode 203 may contain a binder to improve adhesion between particles. As the binder, the materials exemplified in embodiment 1 can be used.

[0155] As the binder, an elastomer may be used from the viewpoint of excellent binding properties. The materials exemplified in the first embodiment may be used as the elastomer. Two or more selected from these may be mixed and used as the binder. When the binder contains a thermoplastic elastomer, for example, high filling of the electrolyte layer 202 or the negative electrode 203 can be achieved by thermal compression during the production of the battery 2000.

[0156] In the positive electrode 201, the binder 113 of the active material layer 110 may or may not further contain the above-mentioned binding agent in addition to the above-mentioned block copolymer.

[0157] At least one selected from the group consisting of the active material layer 110 of the positive electrode 201, the electrolyte layer 202, and the negative electrode 203 may contain a non-aqueous electrolyte, a gel electrolyte, or an ionic liquid in order to facilitate the exchange of lithium ions and improve the output characteristics of the battery 2000.

[0158] The nonaqueous electrolyte contains a nonaqueous solvent and a lithium salt dissolved in the nonaqueous solvent. Examples of nonaqueous solvents that can be used include cyclic carbonate ester solvents, chain carbonate ester solvents, cyclic ether solvents, chain ether solvents, cyclic ester solvents, chain ester solvents, and fluorine-containing solvents. Examples of cyclic carbonate ester solvents include ethylene carbonate, propylene carbonate, and butylene carbonate. Examples of chain carbonate ester solvents include dimethyl carbonate, ethyl methyl carbonate, and diethyl carbonate. Examples of cyclic ether solvents include tetrahydrofuran, 1,4-dioxane, and 1,3-dioxolane. Examples of chain ether solvents include 1,2-dimethoxyethane and 1,2-diethoxyethane. Examples of cyclic ester solvents include γ-butyrolactone. Examples of chain ester solvents include methyl acetate. Examples of fluorine-containing solvents include fluoroethylene carbonate, methyl fluoropropionate, fluorobenzene, fluoroethyl methyl carbonate, fluorodimethylene carbonate, etc. As the non-aqueous solvent, one non-aqueous solvent selected from these may be used alone, or a mixture of two or more non-aqueous solvents selected from these may be used.

[0159] The non-aqueous electrolyte may contain at least one fluorine solvent selected from the group consisting of fluoroethylene carbonate, methyl fluoropropionate, fluorobenzene, fluoroethyl methyl carbonate, and fluorodimethylene carbonate.

[0160] Examples of lithium salts include LiPF6, LiBF4, LiSbF6, LiAsF6, LiSO3CF3, LiN(SO2F)2, LiN(SO2CF3)2, LiN(SO2C2F5)2, LiN(SO2CF3)(SO2C4F9), and LiC(SO2CF3)3. As the lithium salt, one type of lithium salt selected from these may be used alone, or a mixture of two or more types of lithium salts selected from these may be used. The concentration of the lithium salt in the nonaqueous electrolyte may be 0.5 mol / L or more and 2 mol / L or less.

[0161] The gel electrolyte may be a polymer material containing a non-aqueous electrolyte, such as polyethylene oxide, polyacrylonitrile, polyvinylidene fluoride, polymethyl methacrylate, or a polymer having an ethylene oxide bond.

[0162] The cations constituting the ionic liquid may be aliphatic chain quaternary cations such as tetraalkylammonium and tetraalkylphosphonium, aliphatic cyclic ammoniums such as pyrrolidiniums, morpholiniums, imidazoliniums, tetrahydropyrimidiniums, piperaziniums, and piperidiniums, and nitrogen-containing heterocyclic aromatic cations such as pyridiniums and imidazoliums. The anions constituting the ionic liquid may be PF6 - , BF4 - , SbF6 - , AsF6 - , SO3CF3 - , N(SO2F)2 - , N(SO2CF3)2 - , N(SO2C2F5)2 - , N(SO2CF3)(SO2C4F9) - , C(SO2CF3)3 - The ionic liquid may contain a lithium salt.

[0163] At least one selected from the group consisting of the active material layer 110 of the positive electrode 201 and the negative electrode 203 may contain a conductive additive to improve electronic conductivity. Examples of conductive additives include graphites such as natural graphite and artificial graphite, carbon blacks such as acetylene black and ketjen black, conductive fibers such as carbon fiber and metal fiber, conductive powders such as carbon fluoride and aluminum, conductive whiskers such as zinc oxide and potassium titanate, conductive metal oxides such as titanium oxide, and conductive polymers such as polyaniline, polypyrrole, and polythiophene. Using a carbon material as a conductive additive can reduce costs.

[0164] The shape of the battery 2000 may be coin type, cylindrical type, square type, sheet type, button type, flat type, laminated type, or the like.

[0165] Battery 2000 in Embodiment 2 can be manufactured, for example, by the following method. First, current collector 100, materials for forming active material layer 110, materials for forming electrolyte layer 202, materials for forming negative electrode 203, and a current collector for negative electrode 203 are prepared. Using these, a laminate in which positive electrode 201, electrolyte layer 202, and negative electrode 203 are arranged in this order is fabricated by a known method. Battery 2000 can be manufactured in this manner. [Example]

[0166] Hereinafter, the present disclosure will be described in detail using examples and comparative examples. Note that the electrodes and batteries of the present disclosure are not limited to the following examples.

[0167] <Example 1-1> [Preparation of halide solid electrolytes] In an argon glove box with a dew point of -60°C or less, raw material powders of YCl3, LiCl, and LiBr were weighed in a molar ratio of YCl3:LiCl:LiBr = 1:1:2. These raw material powders were then mixed. The resulting mixture was calcined in an electric furnace at 520°C for 2 hours to obtain a halide solid electrolyte, Li3YBr2Cl4 (hereinafter referred to as "LYBC").

[0168] [solvent] In all the following steps, commercially available dehydrated solvents or solvents dehydrated by nitrogen bubbling were used as solvents, and the water content in the solvents was 10 ppm by mass or less.

[0169] [Preparation of binder solution] A binder solution was prepared by adding a solvent to the binder and dissolving or dispersing the binder in the solvent. The binder concentration in the binder solution was adjusted to 5% by mass or more and 6% by mass or less. Next, the binder solution was dehydrated by nitrogen bubbling until the water content reached 10 ppm by mass or less.

[0170] In Example 1-1, p-chlorotoluene was used as the solvent for the binder solution. SEBS (Tuftec (registered trademark) N504, manufactured by Asahi Kasei Corporation), a hydrogenated styrene-based thermoplastic elastomer, was used as the block copolymer constituting the binder. In this SEBS, the mole fraction of repeating units having an aromatic ring was 0.21.

[0171] [Electrode preparation] LYBC was pulverized using a dry jet mill in a dry room with a dew point of -40°C or less to obtain pulverized LYBC powder. Next, in an argon glove box with a dew point of -60°C or less, a binder solution was added dropwise to mix the LYBC and the binder. LYBC and SEBS were mixed at a mass ratio of LYBC:SEBS = 100:3. p-Chlorotoluene was added to the resulting mixture to adjust the solid content to 56% by mass. Next, a slurry was produced by kneading the mixture at 1600 rpm for 3 minutes using a rotation-revolution mixer (THINKY, ARE-310). Next, a current collector with a coating layer was prepared by applying carbon black to an aluminum alloy foil (A1N30 foil, thickness: 15 μm). The slurry was applied to the coating layer of this current collector, and the resulting coating film was dried at 100°C for 1 hour in a vacuum atmosphere to produce the electrode of Example 1-1.

[0172] <Example 1-2> The electrode of Example 1-2 was produced in the same manner as in Example 1-1, except that SEEPS (Septon (registered trademark) 4099, manufactured by Kuraray Co., Ltd.) was used as the block copolymer constituting the binder. In the SEEPS used in Example 1-2, the molar fraction of repeating units having an aromatic ring was 0.21.

[0173] <Examples 1-3> The electrode of Example 1-3 was produced in the same manner as in Example 1-1, except that SEPS (Septon (registered trademark) 2006, manufactured by Kuraray Co., Ltd.) was used as the block copolymer constituting the binder. In the SEPS used in Example 1-3, the molar fraction of repeating units having an aromatic ring was 0.24.

[0174] <Examples 1-4> The electrode of Example 1-4 was produced in the same manner as in Example 1-1, except that SBS (Asaprene (registered trademark) T-411, manufactured by Asahi Kasei Corporation) was used as the block copolymer constituting the binder. In the SBS used in Example 1-4, the mole fraction of repeating units having an aromatic ring was 0.17.

[0175] <Comparative Example 1-1> An electrode of Comparative Example 1-1 was produced in the same manner as in Example 1-1, except that an aluminum alloy foil (A1N30 foil, thickness: 15 μm) was used as the current collector.

[0176] <Comparative Example 1-2> An electrode of Comparative Example 1-2 was produced in the same manner as in Example 1-1, except that SEBS (Dynaron (registered trademark) 8903P, manufactured by JSR Corporation) was used as the block copolymer constituting the binder. In the SEBS used in Comparative Example 1-2, the mole fraction of repeating units having an aromatic ring was 0.22.

[0177] <Comparative Example 1-3> An electrode of Comparative Example 1-3 was produced in the same manner as in Example 1-1, except that SBR (Tufden (registered trademark) 2100R, manufactured by Asahi Kasei Corporation) was used as the polymer constituting the binder. The SBR was a random copolymer.

[0178] [Measurement of the weight-average molecular weight of the block copolymer, the mole fraction of repeating units having an aromatic ring in the block copolymer, and the average degree of polymerization of the first block of the block copolymer] The weight-average molecular weight of the block copolymer constituting the binder was measured by gel permeation chromatography (GPC) using a high-speed GPC device (HLC-832-GPC manufactured by Tosoh Corporation). The measurement sample was prepared by dissolving the binder in chloroform and filtering it using a filter with a pore size of 0.2 μm. Two Super HM-H columns manufactured by Tosoh Corporation were used. A differential refractometer (RI) was used for the GPC measurement. The GPC measurement was carried out at a flow rate of 0.6 mL / min and a column temperature of 40°C. Monodisperse polystyrene (Tosoh Corporation) was used as the standard sample. The number-average molecular weight (M n ), weight average molecular weight (M w ), and dispersity (M w / M n ) was identified.

[0179] The molar fraction of repeating units having an aromatic ring in the block copolymers used in Examples 1-1 to 1-4 and Comparative Examples 1-1 and 1-2 was determined by the following method. First, a measurement sample containing the block copolymer was subjected to proton nuclear magnetic resonance (NMR) analysis using a nuclear magnetic resonance apparatus (AVANCE500 manufactured by Bruker). 1 H NMR measurements were performed. The block copolymer was dissolved in CDCl3, which contained 0.05% TMS. 1The H NMR measurement was performed at a resonance frequency of 500 MHz and a measurement temperature of 23°C. From the obtained NMR spectrum, the integral value of the peak derived from the styrene skeleton and the integral value of the peak derived from skeletons other than the styrene skeleton were determined. The determined integral values ​​were used to determine the mole fraction of repeating units having an aromatic ring in the block copolymer.

[0180] The block copolymers used in Examples 1-1 to 1-4 and Comparative Examples 1-1 and 1-2 were measured for number average molecular weight (M n ), the molar fraction (φ) of the repeating unit having an aromatic ring, the molecular weight (M1) of the repeating unit having an aromatic ring, and the molecular weight (M2) of the repeating unit constituting the second block, the average degree of polymerization of the block composed of repeating units having an aromatic ring (first block) was calculated using the following formula (i):

number

[0181] [Peel strength measurement] The peel strength of the electrodes of Examples 1-1 to 1-4 and Comparative Examples 1-1 to 1-3 was measured by the following method.

[0182] Peel strength measurements were performed in a dry room with a dew point of -40°C or lower using a benchtop tension-compression tester (MCT-2150 manufactured by A&D Corporation) using the following method. First, a 15 mm-wide electrode was cut and attached to a Unilate® plate using double-sided tape. Specifically, the active material layer of the electrode was attached to the Unilate plate using the double-sided tape. Next, the current collector was peeled from the active material layer fixed to the Unilate plate using the tester at a peel angle of 90° and a peel rate of 10 mm / min. After starting the measurement, the measurements for the first 2 mm of the active material layer peeled from the current collector were ignored, and the average value of the measurements (unit: N) continuously recorded for the 8 mm length of the active material layer peeled from the current collector was determined. This average value divided by the width of the electrode was considered to be the peel strength (unit: N / m) between the active material layer and the current collector.

[0183] The results of the above measurements are shown in Table 1. The binder types A to F in Table 1 correspond to the following polymers, respectively. A: Hydrogenated styrene-based thermoplastic elastomer (SEBS) Tuftec N504 B: Hydrogenated styrene thermoplastic elastomer (SEEPS) Septon 4099 C: Hydrogenated styrene thermoplastic elastomer (SEPS) Septon 2006 D: Styrene-based thermoplastic elastomer (SBS) Asaprene T-411 E: Hydrogenated styrene-based thermoplastic elastomer (SEBS) Dynaron 8903P F: Styrene-based elastomer (SBR) Tufuden 2100R

[0184] [Table 1]

[0185] As can be seen from Table 1, when a block copolymer having a triblock sequence is used as the binder and carbon black is used as the material for the coating layer, the weight average molecular weight (M w ) correlates with peel strength. In particular, M w In the electrodes of the examples containing a block copolymer having a molecular weight of 170,000 or more, the peel strength between the active material layer and the current collector layer was high. From this result, it can be said that the electrodes of the examples are suitable for improving the peel strength between the active material layer and the current collector.

[0186] <Example 2-1> [Preparation of halide solid electrolyte dispersion] p-Chlorotoluene was added to LYBC in a dry room with a dew point of -40°C or less. LYBC was pulverized using a wet-type micro-pulverizer / disperser equipped with a bead mill and dispersed in a solvent to obtain a LYBC dispersion. The solid concentration in the LYBC dispersion was 35% by mass.

[0187] [Preparation of active material] First, Li(Ni,Co,Mn)O2 coated with LiNbO3 was prepared. Next, in an argon glove box with a dew point below -60°C, LiNbO3-coated Li(Ni,Co,Mn)O2, LYBC dispersion, vapor-grown carbon fiber (VGCF), and p-chlorotoluene were weighed in a mass ratio of LiNbO3-coated Li(Ni,Co,Mn)O2:LYBC:VGCF = 100:7.5:0.41. Next, these materials were kneaded using a benchtop kneader to prepare the active material. In the active material, Li(Ni,Co,Mn)O2 was coated with LYBC and LiNbO3.

[0188] [Preparation of electrode mixture] In an argon glove box with a dew point of -60°C or less, the above active material, LYBC, sulfide solid electrolyte Li2S-P2S5-based glass ceramics (LPS), and VGCF were weighed out in a mass ratio of active material:LYBC:LPS:VGCF = 85.0:6.4:8.6:1. These were mixed in an agate mortar to prepare an electrode composite.

[0189] [Electrode preparation] The binder solution was added dropwise to the electrode composite and mixed in an argon glove box with a dew point of -60°C or less. The block copolymer constituting the binder was SEBS (Tuftec® N504, manufactured by Asahi Kasei Corporation), a hydrogenated styrene-based thermoplastic elastomer. The binder solution and electrode composite were mixed in a mass ratio of LYBC+LPS:SEBS = 100:2.7. Mixed xylene was further added to the resulting mixture to adjust the solids concentration to 80% by mass. The mixed xylene was a mixed solvent containing o-xylene, m-xylene, p-xylene, and ethylbenzene in a mass ratio of 24:42:18:16. Next, the mixture was kneaded at 1600 rpm for 3 minutes using a planetary centrifugal mixer (ARE-310, manufactured by THINKY Corporation) to produce a slurry. Next, a current collector having a coating layer was prepared by applying carbon black to an aluminum alloy foil (A3003 foil, thickness: 15 μm). The slurry was applied onto the coating layer of this current collector, and the resulting coating film was dried in a vacuum atmosphere at 100°C for 1 hour to prepare the electrode of Example 2-1.

[0190] <Example 2-2> An electrode of Example 2-2 was produced in the same manner as in Example 2-1, except that the binder solution and the electrode mixture were mixed in a mass ratio of LYBC+LPS:SEBS=100:5.3.

[0191] <Comparative Example 2-1> An electrode of Comparative Example 2-1 was produced in the same manner as in Example 2-1, except that SBR (Tufden (registered trademark) 2100R, manufactured by Asahi Kasei Corporation) was used as the polymer constituting the binder. The SBR was a random copolymer.

[0192] <Comparative Example 2-2> An electrode of Comparative Example 2-2 was produced in the same manner as in Comparative Example 2-1, except that the binder solution and the electrode mixture were mixed in a mass ratio of LYBC+LPS:SEBS=100:5.3.

[0193] [Peel strength measurement] The electrodes of Examples 2-1 and 2-2 and Comparative Examples 2-1 and 2-2 were subjected to the measurement of peel strength by the method described above.

[0194] The results of the above measurements are shown in Table 2. Resin binder types A and F in Table 2 correspond to the following polymers, respectively. A: Hydrogenated styrene-based thermoplastic elastomer (SEBS) Tuftec N504 F: Styrene-based elastomer (SBR) Tufuden 2100R

[0195] [Table 2]

[0196] Table 2 shows that the electrode of Example 2-1 exhibited improved peel strength between the active material layer and the current collector layer compared to the electrode of Comparative Example 2-1, which had the same binder to solid electrolyte ratio. Similarly, the electrode of Example 2-2 exhibited improved peel strength between the active material layer and the current collector layer compared to the electrode of Comparative Example 2-2, which had the same binder to solid electrolyte ratio. As can be seen from Table 2, when a block copolymer having a triblock sequence and a weight-average molecular weight of 170,000 or more was used as the binder and carbon black was used as the coating layer material, the peel strength between the active material layer and the current collector layer was improved. These results suggest that the electrodes of the examples are suitable for improving the peel strength between the active material layer and the current collector.

[0197] <Consideration> A comparison of the results of Example 1-1 and Comparative Example 1-1 shown in Table 1 reveals that when conductive carbon is used as the material for the coating layer, the peel strength between the active material layer and the current collector layer is improved.

[0198] A comparison of the results of Examples 1-1 to 1-4 shown in Table 1 with the results of Comparative Examples 1-2 and 1-3 reveals that the peel strength between the active material layer and the current collector layer is improved when a block copolymer having a triblock arrangement and a weight-average molecular weight of 170,000 or more is used as the binder.

[0199] From the above, it has been confirmed that the electrode of the present disclosure is suitable for suppressing peeling between the active material layer and the current collector. an active material layer including an active material, a solid electrolyte, and a binder; a current collector having a substrate and a coating layer that covers the substrate and is in contact with the active material layer; Equipped with the binder has a block copolymer including two first blocks composed of repeating units having an aromatic ring and a second block located between the two first blocks, The weight average molecular weight of the block copolymer is 170,000 or more, The coating layer contains conductive carbon. It is an electrode. [Industrial Applicability]

[0200] The electrode of the present disclosure can be used, for example, in all-solid-state lithium-ion secondary batteries. [Explanation of symbols]

[0201] 100 Current collector 101 Substrate 102 Covering layer 110 Active material layer 111 Solid electrolyte 112 Active material 113 Binder 201 Positive electrode 202 Electrolyte layer 203 Negative electrode 1000 electrodes 2000 batteries

Claims

1. an active material layer including an active material, a solid electrolyte, and a binder; a current collector having a substrate and a coating layer that covers the substrate and is in contact with the active material layer; Equipped with the binder has a block copolymer including two first blocks constituted by repeating units having an aromatic ring and a second block located between the two first blocks, The weight average molecular weight of the block copolymer is 170,000 or more, the polydispersity of the block copolymer is 1.1 or more and 1.5 or less, The coating layer contains conductive carbon. electrode.

2. the first block has an average degree of polymerization of 210 or more; 10. The electrode of claim 1.

3. the second block contains a repeating unit derived from a conjugated diene, 3. The electrode according to claim 1 or 2.

4. the block copolymer is a triblock copolymer, The repeating unit having an aromatic ring includes a repeating unit derived from styrene.

10. The electrode of claim 1.

5. The block copolymer is a hydrogenated product.

5. The electrode of claim 4.

6. The block copolymer includes at least one selected from the group consisting of styrene-ethylene / butylene-styrene block copolymer (SEBS), styrene-ethylene / propylene-styrene block copolymer (SEPS), and styrene-ethylene / ethylene / propylene-styrene block copolymer (SEEPS); 10. The electrode of claim 1.

7. the substrate comprises aluminum or an aluminum alloy; 10. The electrode of claim 1.

8. The active material includes a lithium-containing transition metal oxide.

10. The electrode of claim 1.

9. The active material includes lithium nickel cobalt manganese oxide.

9. The electrode of claim 8.

10. A positive electrode and a negative electrode; an electrolyte layer located between the positive electrode and the negative electrode; Equipped with At least one selected from the group consisting of the positive electrode and the negative electrode is the electrode according to claim 1. battery.

11. The positive electrode is the electrode. The battery of claim 10.