Polyesteramide copolymer with high glass transition temperature

Abstract

Disclosed herein are polyesteramide random copolymers having high glass transition temperatures, methods of forming such polymers, devices, formulations, and medical devices comprising such polymers, and methods of using such polymers in combination with bioactive agents to treat mammals suffering from various conditions. In one embodiment, the random copolymers may have a Tg greater than body temperature, about 37°C, and may achieve longer release durations, different release rates, improved barrier properties, or other advantages relative to polymers having a Tg less than 37°C.

Description

Detailed Description of the Invention

[0001] [CROSS-REFERENCE TO RELATED APPLICATIONS] This application is an international application claiming priority to U.S. Provisional Patent Application No. 62 / 934028, filed November 12, 2019, and European Patent Application Publication No. 19214978.9, filed December 10, 2019, the entire contents of each of which are incorporated herein by reference.

[0002] [Field] The disclosed invention relates to certain polymers, methods of forming such polymers, devices containing such polymers, and methods of using such polymers in combination with bioactive agents to treat mammals suffering from a variety of conditions.

[0003] [background] Polymers have proven to be useful excipients for delivering certain bioactive agents to mammals by injection or implantation. The polymer can be formed into a specific shape or present as a coating, depending on the desired method of injection or implantation. Delivery of the bioactive agent occurs when the bioactive agent leaches out of the polymer or when the polymer degrades. Drug delivery devices containing degradable polymers may be preferred because they may not require a separate procedure to remove the polymer after the bioactive agent is used up.

[0004] However, the use of degradable polymers for drug delivery by injection or implantation presents many challenges. For example, it is often difficult to achieve the desired release rate for an application, whether burst, zero-order, or a combination of the two, in combination with a specified release duration. Furthermore, certain polymers may be more or less compatible with certain drugs, which also affects the release profile. Therefore, polymers that provide the desired compatibility with certain drugs and achieve a specific release profile are desirable.

[0005] [overview] Numerous properties are important for a polymer to be useful for drug delivery in the mammalian body. These properties include the polymer's degradation rate, the drug's solubility in the polymer, and biocompatibility. The barrier properties of a polymer are also important for its function as an excipient in drug delivery formulations. However, the barrier properties of a polymer below its glass transition temperature (Tg) are significantly different from the barrier properties of a polymer above its Tg. Furthermore, a polymer is in a "wet" state when present in physiological fluids within the body. A polymer typically has a wet Tg that is lower than its dry Tg.

[0006] Certain biocompatible polymers, such as poly(L-lactic acid) (PLLA), have a wet Tg above body temperature, but such biocompatible polymers may lack other properties that are more favorable for long-term drug delivery and may be incompatible with certain active pharmaceutical ingredients (APIs).

[0007] Other known biocompatible polymers, such as certain polyesteramides (PEAs), may offer better compatibility with certain APIs, but known PEAs can be plasticized in aqueous environments and have a wet Tg below body temperature.

[0008] U.S. Patent Application Publication No. 2008 / 0299174 discloses the following formula IV: [ka] (wherein m is from about 0.01 to about 0.99, p is from about 0.99 to about 0.01, and q is from about 0.99 to 0.01, and n is from about 5 to about 100; R 1 (C2~C 20 ) alkylene, (C2-C 20 ) alkenylene, and combinations thereof; R of a single comonomer m or p is independently selected from the group consisting of 3 and R 4is hydrogen, (C1-C6) alkyl, (C2-C6) alkenyl, (C2-C6) alkynyl, (C6-C 10 )aryl(C1-C6)alkyl and —(CH2)2S(CH3); R 5 is represented by structural formula (II) [ka] R is selected from the bicyclic fragments of 1,4:3,6-dianhydrohexitols; 6 (C2~C 20 ) alkylene, (C2-C 20 ) selected from the group consisting of alkenylene or alkyloxy; R 7 is hydrogen, (C6-C 10 ) aryl(C1-C6) alkyl or a protecting group; and R 8 is (C1~C 20 ) alkyl or (C2-C 20 ) alkenyl) discloses a PEA copolymer.

[0009] U.S. Pat. No. 9,963,549 discloses a compound of formula V: [ka] (wherein m+p varies from 0.9 to 0.1, and q varies from 0.1 to 0.9; m+p+q=1, whereby m or p can be 0; and n varies from 5 to 300; R 1 (C2~C 20 ) alkylene, (C2-C 20 ) alkenylene, -(R9-CO-OR 10 -O-CO-R9)-, -CHR 11 -O-CO-R 12 -COOCR 11 - and combinations thereof; R of a single main chain unit m or p 3 and R 4is hydrogen, (C1-C6) alkyl, (C2-C6) alkenyl, (C2-C6) alkynyl, (C6-C 10 )Aryl, (C1~C6)alkyl, -(CH2)SH, -(CH2)2S(CH3), -CH2OH, -CH(OH)CH3, -(CH2)4NH3+, -(CH2)3NHC(=NH2+)NH2, -CH2COOH, -(CH2)COOH, -CH2-CO-NH 2, -CH2CH2-CO-NH2, -CH2CH2COOH, CH3-CH2-CH(CH3)-, (CH3)2-CH-CH2-, H2N-(CH2)4-, Ph-CH2-, CH=C-CH2-, HO-p-Ph-CH2-, (CH3)2-CH-, Ph-NH-, [ka] each independently selected from the group consisting of: R 5 (C2~C 20 ) alkylene, (C2-C 20 ) selected from the group consisting of alkenylene, alkyloxy or oligoethylene glycol; R 6 is represented by structural formula (II) [ka] bicyclic fragments of 1,4:3,6-dianhydrohexitols; R 7 (C6~C 10 ) aryl(C1-C6) alkyl; R8 is -(CH2)4-; R9 or R 10 is C2~C 12 Alkylene or C2-C 12 alkenylene; R 11 or R 12 H, methyl, C2-C 12 Alkylene or C2-C 12 alkenylene; whereby a is at least 0.05, b is at least 0.05, and a+b=1. discloses polyesteramide copolymers.

[0010] By incorporating a PEA with a Tg greater than body temperature, about 37°C, longer release duration, different release rates, improved barrier properties, or other advantages can be achieved relative to a PEA with a Tg less than 37°C.

[0011] According to one embodiment, the random copolymer has formula I: [ka] (In the formula, m is 0 to 0.20, n is 0.80 to 0.95, q is 0 to 0.20, and m+n+q=1, where m, n, and q represent the equivalent weights of corresponding units in the random copolymer; p is about 5 to about 300; R 1 is C2~C 20 is alkylene; R 4 is hydrogen, (C1-C6) alkyl, (C2-C6) alkenyl, (C2-C6) alkynyl, (C6-C 10 )Aryl, -CH2SH, -(CH2)2S(CH3), -CH2OH, -CH(OH)CH3, -(CH2)4NH3+, -(CH2)3NHC(=NH2+)NH2, -CH2COOH, -CH2-CO-NH2, -CH 2CH2-CO-NH2, -CH2CH2COOH, CH3-CH2-CH(CH3)-, (CH3)2CH-CH2-, H2N-(CH2)4-, Ph-CH2-, CH=C-CH2-, (CH3)2-CH-, Ph-NH-, [ka] and; R 6 is represented by formula II or formula III [ka] is due to; R 7 (C6~C 10 ) aryl(C1-C6) alkylene; and R 8 is a C3-C8 alkylene) This is due to the following.

[0012] The disclosed polymers, implants and methods may achieve advantages in bioactive agent release, such as better release duration, more uniform daily dose delivery or more desirable daily dose, better compatibility with certain types of bioactive agents, such as acid-sensitive bioactive agents, or improved implant morphology during degradation. [Brief explanation of the drawings]

[0013] [Figure 1] FIG. 1 is a schematic diagram of a wet Tg test apparatus. [Figure 2] FIG. 1 is a schematic diagram of a dry Tg test apparatus. [Figure 3] 1 is a reaction scheme for forming a random copolymer according to Formula VI. [Figure 4] 1 is a reaction scheme for forming PEA III AcBz. [Figure 5] 1 is a graph of Mn as a percentage of initial Mn in days relating to Example 1. [Figure 6] 1 is a graph of cumulative release over time relating to Example 2a. [Figure 7] 1 is a graph of extrapolated daily dose (μg / day) over time relating to Example 2a. [Figure 8] 1 is a composite of optical microscope images of PEA 85D15L X50 implants (2a-2) at three time periods related to Example 2a. [Figure 9] 1 is a composite of optical microscope images of PEA 85D15L X25 implants (2a-3) at three time periods related to Example 2a. [Figure 10] 1 is a graph of cumulative release over time relating to Example 2b. [Figure 11] 1 is a graph of extrapolated daily dose (μg / day) over time relating to Example 2b. [Figure 12] 1 is a composite of optical microscope images of PEA85D15L X25 implants (2b-1) at two time periods related to Example 2b. [Figure 13] 1 is a graph of cumulative release over time relating to Example 2c. [Figure 14] 1 is a light microscope image showing the typical appearance of an implant having the composition of Example 2c-1 (PEA III X25 core, PLGA shell) after several weeks of release in phosphate buffer at 37° C. [Figure 15] 1 is a graph of extrapolated daily dose (μg / day) over time relating to Example 2d.

[0014] [Detailed explanation] According to one embodiment, the random copolymer has formula I: [ka] (In the formula, m is 0 to 0.20, n is 0.80 to 0.95, q is 0 to 0.20, and m+n+q=1, where m, n, and q represent the equivalent weights of corresponding units in the random copolymer; p is about 5 to about 300; R 1 is C2~C 20 is alkylene; R 4 is hydrogen, (C1-C6) alkyl, (C2-C6) alkenyl, (C2-C6) alkynyl, (C6-C 10)Aryl, -CH2SH, -(CH2)2S(CH3), -CH2OH, -CH(OH)CH3, -(CH2)4NH3+, -(CH2)3NHC(=NH2+)NH2, -CH2COOH, -CH2-CO-NH2, -CH 2CH2-CO-NH2, -CH2CH2COOH, CH3-CH2-CH(CH3)-, (CH3)2CH-CH2-, H2N-(CH2)4-, Ph-CH2-, CH=C-CH2-, (CH3)2-CH-, Ph-NH-, [ka] and; R 6 is represented by formula II or formula III [ka] is due to; R 7 (C6~C 10 ) aryl(C1-C6) alkylene; and R 8 is a C3-C8 alkylene) This is due to the following.

[0015] As used herein, the term "alkyl" means a monovalent straight or branched chain hydrocarbon radical, including methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, tert-butyl, n-hexyl, and the like.

[0016] As used herein, the term "alkylene" refers to a divalent branched or unbranched hydrocarbon chain, such as -CH2-, -(CH2)2-, -(CH2)3-, -(CH2)4-, -(CH2)5-, and the like.

[0017] As used herein, the term "alkenyl" refers to a monovalent straight or branched chain hydrocarbon group containing at least one unsaturated bond in its main chain or in one side chain.

[0018] As used herein, "alkenylene" means a divalent branched or unbranched hydrocarbon chain containing at least one unsaturated bond in its main chain or in one side chain.

[0019] As used herein, "alkynyl" means a straight or branched hydrocarbon chain having at least one carbon-carbon triple bond.

[0020] As used herein, "aryl" means a phenyl radical or an ortho-fused bicyclic carbocyclic radical having about 9 to 10 ring atoms in which at least one ring is aromatic. Examples of aryl include, but are not limited to, phenyl, naphthyl, and nitrophenyl.

[0021] As used herein, "biodegradable" refers to a material that is capable of completely or substantially breaking down or eroding when exposed to an in vivo environment. For example, a polymer can be degraded or eroded when it can be gradually broken down, resorbed, absorbed, and / or eliminated by hydrolysis, enzymatic degradation, oxidation, metabolic processes, bulk or surface erosion, etc.

[0022] As used herein, "random copolymer" means a copolymer in which two or more individual polymer units are randomly distributed throughout the copolymer. According to Formula I, each of the units m, n, and q is randomly distributed throughout the copolymer.

[0023] In one embodiment, n is 0.80, 0.81, 0.82, 0.825, 0.83, 0.835, 0.84, 0.845, or 0.85 to 0.95, 0.945, 0.94, 0.935, 0.93, 0.925, 0.92, 0.915, 0.91, 0.905, or 0.90. In one embodiment, q is zero. In one embodiment, the ratio of m:q is 10:1, 9:1, 8:1, 7:1, 6:1, 5:1, 4:1, 3:1, or 2:1 to 1:6, 1:5, 1:4, 1:3, 1:2, or 1:1. In one embodiment, m is equal to or greater than q.

[0024] In one embodiment, p is 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, or 75 to 300, 290, 280, 270, 260, 250, 240, 230, 220, 210, 200, 190, 180, 170, 160, or 150. In one embodiment, the random copolymer of Formula I has a number average molecular weight (Mn) of at least 15,000 g / mol, at least 20,000 g / mol, at least 25,000 g / mol, at least 30,000 g / mol, or at least 35,000 g / mol. In one embodiment, the random copolymer of Formula I has an Mn of at most 250,000 g / mol, at most 225,000 g / mol, at most 200,000 g / mol, at most 175,000 g / mol, at most 150,000 g / mol, at most 125,000 g / mol, at most 100,000 g / mol, or at most 75,000 g / mol, as measured by GPC in THF using polystyrene as a standard.

[0025] In one embodiment, R 4 is hydrogen, (C1-C6) alkyl, CH3-CH2-CH(CH3)-, (CH3)2CH-CH2-, Ph-CH2-, or (CH3)2CH-. In one embodiment, R 7 is Caryl-CH- (i.e., benzyl). In one embodiment, R 8 is -(CH2)4-.

[0026] Polyesteramide random copolymers are synthesized using techniques known in the art. R. Katsarava, V. Beridze, N. Arabuli, D. Kharadze, CCC Hu, CY Won J Polym Sci A: Polym Chem 37:391-407 (1999). Briefly, the polymers are prepared by solution polycondensation of di-p-toluenesulfonate or hydrochloride salts of bis-(α-amino acid) α,ω-diol diesters, lysine benzyl ester, and di-N-hydroxysuccinimide esters of lysine and / or sebacic acid in anhydrous DMSO. Typically, the salts are converted to free amines by the addition of triethylamine, and these amines are further reacted with diacid derivatives. The use of preactivated acids in the reaction allows polymerization at relatively low temperatures, such as 65°C, resulting in polycondensates without by-products and predictable decomposition products. The resulting reaction mixture is then purified by aqueous precipitation, followed by organic precipitation and filtration. Drying under reduced pressure yields a polyesteramide random copolymer.

[0027] For example, such a polymer can be prepared by reacting lysine, lysine benzyl ester, and hexahydrofuro[3,2-b]furan-3,6-diylbis(2-amino-4-methylpentanoate) with di-N-hydroxysuccinimide ester-activated sebacic acid in DMSO for 24 hours. The polymer is then isolated from the reaction mixture in two precipitation steps and characterized by proton NMR and THF-based GPC relative to polystyrene standards.

[0028] In one embodiment, the random copolymer according to Formula I has a wet Tg of 36°C or greater. A wet Tg of 36°C or greater corresponds to a polymer that may remain solid (glassy) upon injection or implantation into a mammal. In contrast, if the wet Tg is, for example, 32°C or less, the polymer may behave as a viscous liquid upon injection or implantation. In one embodiment, the random copolymer has a wet Tg of 36°C, 36.5°C, 37°C, 37.5°C, 38°C, or 39°C to 45°C, 44°C, 43°C, 42°C, 41°C, 40°C, 39°C, 38°C, or 37°C.

[0029] In one embodiment, the initial wet Tg of the random copolymer differs from the wet Tg of the random copolymer after 35 days in PBS at 37° C. by at most + / −10%, + / −9%, + / −8%, + / −7%, + / −6%, or + / −5%. In one embodiment, q is 0.05 to 0.20, the initial wet Tg of the random copolymer differs from the wet Tg of the random copolymer after 35 days in PBS at 37° C. by at most + / −10%, + / −9%, + / −8%, + / −7%, + / −6%, or + / −5%, and the Mn after 35 days in PBS at 37° C. is 50%, 55%, 60%, or 65% to 70%, 75%, or 80% of the initial Mn.

[0030] In one embodiment, the drug delivery device comprises a random copolymer and a bioactive agent. In one embodiment, the drug delivery device provides controlled and / or extended release of the bioactive agent. The drug delivery device can be a pharmaceutical product or a medical device. A pharmaceutical product is a medical product that is administered to a patient and achieves its intended purpose through pharmacological action. A medical device is a medical instrument, device, apparatus, machine, apparatus, implant, extracorporeal reagent, or other similar or related article, including their component parts or accessories, that does not achieve its intended purpose through pharmacological action.

[0031] In one embodiment, the bioactive agent comprises a nutrient, a pharmaceutical, a small molecule drug, a protein, a peptide, a vaccine, genetic material (such as polynucleotides, oligonucleotides, plasmids, DNA and RNA), a diagnostic agent, or an imaging agent. The bioactive agent can be a drug, a prodrug or codrug thereof, a metabolite thereof, and / or a prodrug of a metabolite.

[0032] In one embodiment, the bioactive agent is capable of stimulating or inhibiting a biological response. In one embodiment, the bioactive agent is selected from one or more of growth factors (VEGF, FGF, MCP-1, PlGF, antibiotics (e.g., B-lactams, penicillins such as chloramphenicol), anti-inflammatory compounds, anti-thrombogenic compounds, anti-occlusive agents, anti-arrhythmic agents, anti-atherosclerotic agents, antihistamines, cancer therapeutics, vascular agents, ophthalmic agents, amino acids, vitamins, hormones, neurotransmitters, neurohormones, enzymes, signaling molecules, antiviral agents, and psychotropic agents.

[0033] The bioactive agent may have antiproliferative or anti-inflammatory properties, or may have other properties such as antitumor, antiplatelet, anticoagulant, antifibrinogen, antithrombotic, antimitotic, antibacterial, antiallergic, or antioxidant properties. Examples of antiproliferative agents include rapamycin and its functional or structural derivatives, 40-O-(2-hydroxy)ethyl-rapamycin (everolimus) and its functional or structural derivatives, and paclitaxel and its functional or structural derivatives. Examples of rapamycin derivatives include ABT-578, 40-O-(3-hydroxy)propyl-rapamycin, 40-O-[2-(2-hydroxy)ethoxy]ethyl-rapamycin, and 40-O-tetrazole-rapamycin. Examples of paclitaxel derivatives include docetaxel. Examples of antineoplastic and / or antimitotic agents include methotrexate, azathioprine, vincristine, vinblastine, fluorouracil, doxorubicin hydrochloride (e.g., Adriamycin® manufactured by Pharmacia AND Upjohn, Peapack, NJ), and mitomycin (e.g., Mutamycin® manufactured by Bristol-Myers Squibb Co., Stamford, Conn.).Examples of such antiplatelet agents, anticoagulants, antifibrins, and antithrombins include sodium heparin, low molecular weight heparin, heparinoids, hirudin, argatroban, forskolin, vapiprost, prostacyclin and prostacyclin analogs, dextran, D-phe-pro-arg-chloromethylketone (synthetic antithrombin), dipyridamole, glycoprotein Hb / nia platelet membrane receptor antagonist antibodies, recombinant hirudin, thrombin inhibitors such as Angiomax (Biogen, Inc., Cambridge, Mass.), calcium channel blockers (such as nifedipine), colchicine, fibroblast growth factor (FGF) antagonists, fish oil (omega-3 fatty acids), histamine antagonists, lovastatin (an inhibitor of HMG-CoA reductase, a cholesterol-lowering drug, manufactured by Merck and Co., Inc., Whitehouse Examples of anti-inflammatory drugs include those manufactured by Station, NJ under the trade name Mevacor®, monoclonal antibodies (such as antibodies specific for the platelet-derived growth factor (PDGF) receptor), nitroprusside, phosphodiesterase inhibitors, prostaglandin inhibitors, suramin, serotonin blockers, steroids, thioprotease inhibitors, triazolopyrimidines (PDGF antagonists), superoxide dismutase, superoxide dismutase mimics, 4-amino-2,2,6,6-tetramethylpiperidine-1-oxyl (4-amino-TEMPO), estradiol, anticancer drugs, dietary supplements such as various vitamins, and combinations thereof. Examples of anti-inflammatory drugs, including steroidal and non-steroidal anti-inflammatory drugs, include biolimus, tacrolimus, dexamethasone, clobetasol, corticosteroids, or combinations thereof. Examples of such cytostatics include angiotensin-converting enzyme inhibitors such as angiopeptin, captopril (e.g., Capoten® and Capozide® manufactured by Bristol-Myers Squibb Co., Stamford, Conn.), cilazapril, or lisinopril (e.g., Prinivil® and Prinzide® manufactured by Merck and Co., Inc., Whitehouse Station, NJ). An example of an antiallergic agent is permirolast potassium.Other therapeutic substances or agents that may be appropriate include alpha-interferon, pimecrolimus, imatinib mesylate, midostaurin, and genetically engineered epithelial cells.

[0034] Further examples of specific bioactive agents include nervous system agents (amphetamines, methylphenidate), alpha 1 adrenergic receptor antagonists (prazosin, terazosin, doxazosin, ketensin, urapidil), alpha 2 blockers (arginine, nitroglycerin), antihypertensives (clonidine, methyldopa, moxonidine, hydrazine minoxidil), bradykinin, angiotensin receptor blockers (benzepryl, captopril, cilazepril, enalapril, fosinopril, lisinopril, perindopril, quinapril, ramipril, trandolapril), and the like. ol, zofenopril), angiotensin-1 blockers (candesartan, eprosartan, irbesartan, losartan, telmisartan, valsartan), endopeptidase (omapatrilate), beta-2 antagonists (acebutolol, atenolol, bisoprolol, celiprolol, esmodol, metoprolol, nebivolol, betaxolol), beta-2 blockers (carvedilol, labetalol, oxprenolol, pindolol, propanolol), diuretics (chlorthalidone, chlorothiazide, epithizide, hydrochloride) Thiazides, indapamide, amiloride, triamterene), calcium channel blockers (amlodipine, barnidipine, diltiazem, felodipine, izradipine, lacidipine, lercanidipine, nicardipine, nifedipine, nimodipine, nitrezinpine, verapamil), anti-alimentary active drugs (amiodarone, solatol, diclofenac, flecainide) or ciprofloxacin, latanoprost, flucloxacillin, rapamycin and analogues, and limus derivatives, paclitaxel, taxol, cyclosporine, heparin, adrenal cortex These include hormones (triamcinolone acetonide, dexamethasone, fluocinolone acetonide), anti-angiogenic agents (iRNA, VEGF antagonists: bevacizumab, ranibizumab, pegaptanib), growth factors, zinc finger transcription factors, triclosan, insulin, salbutamol, estrogen, norcantharidin, microlysyl analogs, prostaglandins, statins, chondroitinates, diketopiperazines, macrocyclic compounds, neuregulin, osteopontin, alkaloids, immunosuppressants, antibodies, avidin, biotin, and clonazepam.

[0035] In one embodiment, the bioactive agent is useful for treating glaucoma, ocular hypertension, wet age-related macular degeneration (AMD), diabetic retinopathy, diabetic macular edema, or other diseases of the eye. In one embodiment, the bioactive agent comprises latanoprost, bimatoprost, or travoprost.

[0036] In one embodiment, the bioactive agent comprises a chemotherapeutic agent, a JAK kinase inhibitor, an antipsychotic agent, or an antiviral agent.

[0037] In one embodiment, the bioactive agent comprises one or more of sorafenib, pazopanib, axitinib, regorafenib, cabozantinib, lenvatinib, sunitinib, nintedanib, crizotinib, ceritinib, alectinib, brigatinib, bosutinib, dasatinib, imatinib, nilotinib, ponatinib, vemurafenib, dabrafenib, ibrutinib, palbociclib, ribociclib, gefitinib, erlotinib, lapatinib, afatinib, osimertinib, or trametinib.

[0038] In one embodiment, the bioactive agent comprises one or more of tofacitinib, ruxolitinib, oclacitinib, baricitinib, peficitinib, fedratinib, upadacitinib, filgotinib, cerdulatinib, gandotinib, lestaurtinib, momelotinib, or pacritinib.

[0039] In one embodiment, the bioactive agent comprises one or more of aripiprazole, brexiprazole, olanzapine, quetiapine, or ziprasidone.

[0040] In one embodiment, the bioactive agent comprises one or more of tenofovir, emtricitabine, efavirenz, elvitegravir, cobicistat, ribavirin, daclatasvir, sofosbuvir, velpatasvir, voxilaprevir, glecaprevir, pibrentasvir, elbasvir, grazoprevir, simeprevir, or ledipasvir.

[0041] Drug delivery devices can take a variety of forms. In one embodiment, the drug delivery device comprises a random copolymer formed into a particular shape. In one embodiment, the drug delivery device comprises a random copolymer coated onto a substrate, such as the surface of a stent. In one embodiment, the drug delivery device comprises an injectable formulation comprising the random copolymer in a solution containing, for example, microparticles or nanoparticles comprising the random copolymer and a bioactive agent. In one embodiment, the drug delivery device is in the shape of a cylinder, disk, sphere, or coating, or multiple cylinders, disks, spheres, or coatings.

[0042] In one embodiment, the drug delivery device is in the shape of a cylinder having a diameter of from 100, 150, 200, or 250 micrometers to 1000, 900, 800, 700, 600, or 500 micrometers. In one embodiment, the drug delivery device is in the shape of a cylinder having a length of from 0.5, 1, 1.5, 2, 2.5, 3, 3.5, 4, 4.5, or 5 millimeters to 30, 25, 20, 15, 10, 5, 4, or 3 millimeters.

[0043] In one embodiment, the drug delivery device is cylindrical in shape with a diameter of 1, 2, 3, 4, or 5 to 4, 5, 6, 7, 8, 9, or 10 mm. In one embodiment, the drug delivery device is cylindrical in shape with a length of 10, 15, 20, 25, or 30 mm to 150, 120, 100, or 80 mm. In one embodiment, the drug delivery device is cylindrical in shape with a diameter of 1 to 5 mm and a length of 20 to 100 mm.

[0044] In one embodiment, the drug delivery device comprises a core comprising a random copolymer and a bioactive agent, and a shell comprising a shell polymer. In one embodiment, both the core and the shell comprise a bioactive agent. In one embodiment, only the core comprises a bioactive agent. In one embodiment, the core and the shell comprise the same polymer.

[0045] In one embodiment, the core and shell comprise different polymers. In one embodiment, the shell polymer comprises poly(lactic acid), poly(glycolic acid), poly(lactide-co-glycolide), polycaprolactone, or a combination thereof. In one embodiment, each of the core and shell comprises a random polymer according to Formula I.

[0046] The core-shell arrangement can take a variety of forms, such as a coating with an inner core layer closer to the substrate than the shell layer, with other layers being closer to the substrate than the core layer, between the core and shell layers, or more distal than the shell layer.

[0047] In one embodiment, the drug delivery device is cylindrical in shape and includes a cylindrical core at least partially surrounded by a cylindrical shell, which may surround the entire cylindrical core, only one end of the cylindrical core, or not further surround either end of the cylindrical core.

[0048] In embodiments, the drug delivery device is an injectable formulation comprising a plurality of microparticles and / or nanoparticles comprising a random copolymer and a bioactive agent. In one embodiment, the microparticles and / or nanoparticles comprise a core comprising the random copolymer and the bioactive agent, and a shell surrounding the core.

[0049] In one embodiment, the injectable formulation comprises a plurality of microparticles comprising a random copolymer and a bioactive agent, the microparticles having an average particle diameter of 10 to 500 micrometers. In one embodiment, the injectable formulation comprises a plurality of microparticles comprising a random copolymer and a bioactive agent, the microparticles having an average particle diameter of 10, 20, 30, 40, 50, 60, 70, 80, 90, or 100 micrometers to 500, 475, 450, 425, 400, 375, 350, 325, or 300 micrometers. In one embodiment, the injectable formulation comprises a plurality of nanoparticles comprising a random copolymer and a bioactive agent, the nanoparticles having an average particle diameter of 50, 100, 150, 200, 250, 300, 350, 400, 450, or 500 nanometers to 1000, 950, 900, 850, or 800 nanometers. The average particle diameter is measured by laser diffraction using a Malvern Mastersizer 2000.

[0050] In one embodiment, the drug delivery device further comprises another polymer other than the random copolymer of Formula I. Examples of such biocompatible polymers are poly(orthoesters), poly(anhydrides), poly(D,L-lactic acid), poly(L-lactic acid), poly(glycolic acid), copolymers of poly(lactic acid) and glycolic acid, poly(L-lactide), poly(D,L-lactide), poly(glycolide), poly(D,L-lactide-co-glycolide), poly(L-lactide-co-glycolide), poly(phosphoesters), poly(trimethylene carbonate), poly(oxa-esters), poly(oxa-amides), poly(ethylene carbonate), poly(propylene carbonate), poly(phosphoesters), poly(phosphazenes), poly(tyrosine-derived carbonates), poly(tyrosine-derived arylates), poly(tyrosine-derived iminocarbonates), copolymers of these polymers with poly(ethylene glycol) (PEG), or combinations thereof. These additional polymers may be present as a blend with the random copolymer of Formula I, or may form part or all of a separate layer or portion of the drug delivery device.

[0051] In one embodiment, the drug delivery device includes fibers. The fibers can be produced via an extrusion process, such as melt extrusion, in which a biodegradable polymer and additional compounds are homogenized using a Retsch cryogenic grinder. The resulting powder is then loaded into a preheated DSM Xplore microextruder with a 5 cc barrel and twin screws connected to a microfiber spinning device. The biodegradable polymer preferably has a residence time of 5 to 10 minutes at 120 to 140°C before being stretched into fibers with diameters ranging from 100 to 250 μm. Extrusion is typically carried out under an inert atmosphere to minimize oxidative degradation of the polymer during the process. It is then cooled at room temperature under tension. The resulting fibers can then be cut into, for example, 4 mm long segments and sterilized with gamma radiation.

[0052] Alternatively, such fibers can be prepared by injection molding. In this process, fibers are formed in an injection molding apparatus at temperatures of 50-200°C, preferably 100-200°C, resulting in fibers approximately 200 μm in diameter. The mold can then be cooled to room temperature before opening and removing the fibers.

[0053] If the drug delivery device includes one or more bioactive agents, loading of the bioactive agents can be achieved by forming the drug delivery device into the desired shape in the presence of or after the bioactive agents. If the bioactive agent is affected by the process of forming the drug delivery device into the desired shape, the drug delivery device can be loaded with the bioactive agent after it has been formed into the desired shape. This can be achieved by contacting the drug delivery device with the bioactive agent and allowing the bioactive agent to diffuse into the drug delivery device and / or adhere to or absorb onto its surface.

[0054] Drug delivery devices comprising the random copolymers can be used for drug delivery in the medical field, particularly in the fields of pain management, MSK, ophthalmology, cancer treatment, vaccine delivery compositions, dermatology, cardiovascular and orthopedics, spinal, intestinal, pulmonary, nasal or auricular.

[0055] The following examples further illustrate embodiments of the present invention but, of course, should not be construed as in any way limiting the scope of the claims.

[0056] [Example] [Measurement method] [Wet Tg] The samples are immersed in Dulbecco's PBS buffer at 37° C. for 4 days. Typically, the samples float on top of the buffer for the first approximately 3 days, and then become saturated enough that they sink into the buffer for the last 24 hours or so of the immersion process.

[0057] A schematic diagram of the modified geometry of the test setup is shown in Figure 1. Measurements are performed on an ARES2-rheometer. The sample 1 is placed between parallel plates 2 with a diameter of 15 mm. The ARES2-rheometer has been modified to include PBS buffer 3 to create a saturated atmosphere.

[0058] The temperature ramp is from 70°C to 0°C with a cooling rate of 5°C / min, an angular frequency of 1 Hz (6.28 rad / s), and an initial variable strain of 0.1% (automatic strain control enabled). The gap is manually controlled to apply a constant axial (compressive) force to the specimen (F N (approximately 30 grams). This constant compressive force is necessary to prevent loss of contact between the sample and the parallel plates.

[0059] [Dry Tg] A schematic diagram of the test setup is shown in Figure 2. The measurements are carried out on an ARES2-Rheometer. The parallel plates 2 have approximately the same dimensions as the test sample 1, in this case 4 mm in diameter. The measurements are carried out in a N2 atmosphere.

[0060] The sample is dried at 25 °C under a 200 mbar nitrogen atmosphere for 7 days. The temperature ramp is from 90 °C to 0 °C (cooling rate 5 °C / min) with an angular frequency of 1 Hz (6.28 rad / s) and an initial variable strain of 0.1% (automatic strain control enabled). The gap is manually controlled to apply a constant axial (compressive) force to the sample (F N(approximately 30 grams). This constant compressive force is necessary to prevent loss of contact between the sample and the parallel plates.

[0061] [Molecular weight] Mn is determined on dried samples by GPC using THF as the mobile phase. Molecular weights are relative to polystyrene standards.

[0062] Preparation of copolymers used in the examples Test samples are prepared according to the following procedure.

[0063] A random copolymer according to Formula VI was prepared by the following procedure. Triethylamine (30 mL, 0.215 mol) and DMSO (52 mL, 0.732 mol) were added to a mixture of di-N-hydroxysuccinimide ester of sebacic acid (di-NHS-sebacic acid) (38.541 g, 0.097 mol), L-leucine-(DAS)-2TosOH (59.244 g, 0.083 mol), and L-lysine (Bz)-2TosOH (8.469 g, 0.014 mol) in a nitrogen-filled 500 mL round-bottom flask equipped with an overhead stirrer at room temperature. The mixture was then heated to 60°C and the reaction proceeded as monitored by GPC analysis in THF. After 36 hours, a stable molecular weight was obtained. The mixture was then allowed to cool to room temperature. Acetic anhydride (1.89 mL, 0.0199 mol) was added at room temperature to acylate the amino-functional end groups of the polymer. The mixture was stirred at room temperature for 24 hours. The general reaction scheme is shown in Figure 3.

[0064] The resulting crude polymer mixture is precipitated in water at a ratio of 10:1 (water:reaction mixture). The polymer is recovered and dissolved in ethanol (500 mL, 8.57 mol) before being precipitated a second time. The polymer is again dissolved in ethanol (500 mL, 8.57 mol) and precipitated in ethyl acetate (5000 mL, 50.91 mol) by dropwise addition to the stirred solution. The precipitated polymer is washed with ethyl acetate (100 mL, 1.00 mol), the supernatant is removed, and the precipitate is washed again with ethyl acetate (100 mL, 1.00 mol). After removing the supernatant, the precipitate is dried, dissolved in ethanol (500 mL, 8.57 mol), and filtered through a 0.2 μm PTFE membrane filter. The filtered polymer solution is dried at 65°C under reduced pressure. Yield 75%, Mn=108 kDa (gel permeation chromatography (GPC) in THF against polystyrene standards).

[0065] A random copolymer according to Formula VII was prepared by the following procedure. Triethylamine (30 mL, 0.215 mol) and DMSO (52 mL, 0.732 mol) were added to a mixture of di-N-hydroxysuccinimide ester of sebacic acid (di-NHS-sebacic acid) (38.541 g, 0.097 mol), L-leucine-(DAS)-2TosOH (59.244 g, 0.083 mol), L-lysine.2HCl (1.598 g, 0.007 mol), and L-lysine(Bz)-2TosOH (4.235 g, 0.007 mol) in a nitrogen-filled 500 mL round-bottom flask equipped with an overhead stirrer at room temperature. The mixture was then heated to 60°C and the reaction proceeded as monitored by GPC analysis in THF. After 36 hours, a stable molecular weight was obtained. The mixture was then allowed to cool to room temperature. Acetic anhydride (1.89 mL, 0.0199 mol) was added at room temperature to acylate the amino functional end groups of the polymer, and the mixture was stirred at room temperature for 24 hours.

[0066] The resulting crude polymer mixture is precipitated in water at a ratio of 10:1 (water:reaction mixture). The polymer is recovered and dissolved in ethanol (500 mL, 8.57 mol) before being precipitated a second time. The polymer is again dissolved in ethanol (500 mL, 8.57 mol) and precipitated in ethyl acetate (5000 mL, 50.91 mol) by dropwise addition to the stirred solution. The precipitated polymer is washed with ethyl acetate (100 mL, 1.00 mol), the supernatant is removed, and the precipitate is washed again with ethyl acetate (100 mL, 1.00 mol). After removing the supernatant, the precipitate is dried, dissolved in ethanol (500 mL, 8.57 mol), and filtered through a 0.2 μm PTFE membrane filter. The filtered polymer solution is dried at 65° C. under reduced pressure. Yield: 75%, Mn=62 kDa (gel permeation chromatography (GPC) in THF against polystyrene standards).

[0067] PEA III AcBz according to formula VIII is obtained as follows: To a mixture of di-N-hydroxysuccinimide ester of sebacic acid (di-NHS-sebacic acid) (39.940 g, 0.1008 mol, 1.0 equiv.), L-leucine(6)-2TosOH (20.823 g, 0.0302 mol, 0.30 equiv.), L-leucine-(DAS)-2TosOH (32.503 g, 0.0453 mol, 0.45 equiv.), and L-lysine(Bz)-2TosOH (14.628 g, 0.0252 mol, 0.25 equiv.) in a nitrogen-filled 500 mL round-bottom flask equipped with an overhead stirrer, triethylamine (30.9 mL, 0.222 mol, 2.2 equiv.) and N,N-dimethylformamide (53.07 mL, 0.689 mol) were added at room temperature. The mixture was then heated to 60 °C to allow the reaction to proceed and monitored by GPC analysis in THF. After 36 h, a stable molecular weight was achieved, followed by the addition of a portion of L-leucine(6)-2TosOH (4.338 g, 0.0063 mol) along with triethylamine (1.76 mL, 0.0126 mol) and N,N-dimethylformamide (4.54 mL, 0.0590 mol) to terminate the polymerization reaction. After heating the mixture for an additional 24 h, the viscous solution was diluted with additional N,N-dimethylformamide (407.85 g, 5.301 mol) and allowed to cool to room temperature. Acetic anhydride (1.89 mL, 0.0199 mol) was added at room temperature to acylate the amino-functional end groups of the polymer. The mixture was stirred at room temperature for 24 h. The general reaction scheme is shown in Figure 4.

[0068] The resulting crude polymer mixture is precipitated in water at a ratio of 10:1 (water:reaction mixture). The polymer is recovered and dissolved in ethanol (500 mL, 8.57 mol) before being precipitated a second time. The polymer is again dissolved in ethanol (500 mL, 8.57 mol) and precipitated in ethyl acetate (5000 mL, 50.91 mol) by dropwise addition to the stirred solution. The precipitated polymer is washed with ethyl acetate (100 mL, 1.00 mol). After removing the ethyl acetate, the polymer is washed again with ethyl acetate (100 mL, 1.00 mol). The polymer is then dried, dissolved in ethanol (500 mL, 8.57 mol), and filtered through a 0.2 μm PTFE membrane filter. The filtered polymer solution is dried at 65° C. under reduced pressure. Yield: 75%, Mn=43.3 kDa (gel permeation chromatography (GPC) in THF against polystyrene standards).

[0069] PEA III X25 according to Formula IX can be obtained as follows: Triethylamine (31 mL, 0.222 mol) and DMSO (54 mL, 0.76 mol) are added to a mixture of di-N-hydroxysuccinimide ester of sebacic acid (di-NHS-sebacic acid) (39.336 g, 0.099 mol), L-leucine-(DAS)-2TosOH (32.876 g, 0.045 mol), L-leucine(6)-2TosOH (21.062 g, 0.030 mol), L-lysine.2HCl (1.396 g, 0.006 mol), and L-lysine(Bz)-2TosOH (4.235 g, 0.018 mol) in a nitrogen-filled 500 mL round-bottom flask equipped with an overhead stirrer at room temperature. The mixture is then heated to 60°C to allow the reaction to proceed and is monitored by GPC analysis in THF. After 36 hours, a stable molecular weight is obtained. The reaction mixture is diluted with 250 mL of DMSO and allowed to cool to room temperature. Acetic anhydride (1.89 mL, 0.0199 mol) is added at room temperature to acylate the amino-functional end groups of the polymer. The mixture is then stirred at room temperature for 24 hours.

[0070] The resulting crude polymer mixture is precipitated in water at a ratio of 10:1 (water:reaction mixture). The polymer is recovered and dissolved in ethanol (500 mL, 8.57 mol) before being precipitated a second time. The polymer is again dissolved in ethanol (500 mL, 8.57 mol) and precipitated in ethyl acetate (5000 mL, 50.91 mol) by dropwise addition to the stirred solution. The precipitated polymer is washed with ethyl acetate (100 mL, 1.00 mol), the supernatant is removed, and the precipitate is washed again with ethyl acetate (100 mL, 1.00 mol). After removing the supernatant, the precipitate is dried, dissolved in ethanol (500 mL, 8.57 mol), and filtered through a 0.2 μm PTFE membrane filter. The filtered polymer solution is dried at 65° C. under reduced pressure. A typical yield is 75%. The Mn is typically in the range of 45-70 kDa (gel permeation chromatography (GPC) in THF against polystyrene standards).

[0071] The copolymers formed are listed in Table 0.1 below. For each copolymer according to Formula I, R 1 is -(CH2)8- and R 4 is (CH3)2CH-CH2-; R 5 is -(CH2)6- and R 6 is according to formula II; R 7 is C aryl-CH—, and R 8 is -(CH2)4-.

[0072] [Table 1]

[0073] PEA 85D15L is according to formula VI. [ka]

[0074] PEA 85D15L X50 is according to Formula VII. [ka]

[0075] PEA III AcBz is a random copolymer according to Formula VIII. [ka]

[0076] PEA III X25 is a random copolymer according to formula IX. [ka]

[0077] Example 1 - Tg The polymer is compression molded into disk-shaped samples with a diameter of 25 mm and a thickness of 0.5 mm using a Fontijne TP200 table press. During molding, the press chamber is constantly filled with N2 gas. A sheet of Teflon™ foil is placed on the surface of the mold to prevent the material from sticking to the surface of the mold. Molding is carried out according to the procedure in Table 1.1.

[0078] [Table 2]

[0079] Smaller disks with a diameter of 4 mm and a thickness of 0.5 mm are then punched out from the larger disk with a diameter of 25 mm. The initial dry Tg, initial wet Tg and initial Mn are measured. The results are shown in Table 1.2.

[0080] [Table 3]

[0081] Samples of PEA III AcBz, PEA 85D15L, PEA 85D15L X50, and PEA 100D are placed in PBS buffer at 37°C. Wet Tg and Mn are measured at the indicated time periods over 35 days. The results of the wet Tg measurements over time are shown in 1.3. Mn (kDa) over time (as a percentage of initial Mn) is plotted in Figure 5.

[0082] [Table 4]

[0083] The wet Tg remains fairly constant over the test period. The predicted reason for the decrease in Mn of 85D15L X50 is the hydrolysis of unprotected carboxylic acid groups, which is not present in the other copolymers. Surprisingly, the decrease in Mn does not affect the wet Tg stability. The wet Tg stability and degradation profile are expected to be useful for long-term drug delivery applications.

[0084] Example 2 - In vitro release Cylindrical implants are formed by injection molding. First, a powder is prepared as follows: A formulation of polymer and bioactive agent is dissolved in ethanol at 1-30% solids depending on the bioactive agent and polymer. The formulation is cast onto an FEP (fluorinated ethylene propylene) plate. The resulting film is dried under vacuum at 37°C. The film is then cryo-milled to obtain a powder.

[0085] The resulting powder is used to injection mold implants according to the following procedure: a Thermo Fisher Scientific HAAKE MiniJet Pro is fitted with custom mode. The molding temperature is 90-130°C. The resulting implants are either 250 μm in diameter if the implant is uncoated, or 230 μm in diameter if a coating layer is added.

[0086] If the implant is coated, the coating is prepared by dip coating. The implant is secured with a metal paper clip held in an Ametek CS225 Force Tester. The coating solution is a 12.3 wt% solution of the polymer in acetone for polyester coating or a 15 wt% solution of the polymer in ethanol for PEA coating. The immersion speed is 1.5 cm / sec for polyester coating, a maximum of 0.83 cm / sec, and a minimum of 0.33 cm / sec for PEA coating.

[0087] The implants are trimmed to a length of 2 mm and each implant has a mass of approximately 100 μg.

[0088] Bioactive agent loading is confirmed by UPLC-UV. Samples are soluble in ethanol (typically 1 mL of solution for 100 μg of sample) and run on a Waters UPLC-UV (Ultra Performance Liquid Chromatography) using the following settings: Eluent: 60% acetonitrile - 40% MQ water, 0.01% v / v trifluoroacetic acid Flow rate: 0.4mL / min Run Time: 4 minutes Column: Acquity C18 BEH 1.7μ 2.1*50mm Detection wavelength: 210 nm Injection volume: 10 μL for release samples and 2 μL for loading confirmation.

[0089] In vitro release experiments were performed by placing 2 mm implants in silanized HPLC vials containing 0.5–1.8 mL of phosphate buffer. Using silanized vials, the adsorption behavior of travoprost / latanoprost onto glass can be minimized by diluting the release samples as follows: First, dilute the samples from the release experiments by adding acetonitrile to the HPLC vial in a 1:1 volume ratio. Analyze the samples using UPLC-UV as described above.

[0090] Samples are taken mainly according to the following scheme: days 1, 2, 3, 4, 7, 9, 11, 14, 17, 21 and thereafter once weekly sampling.

[0091] Results are presented either as cumulative release in % of payload and / or as extrapolated daily dose. For the extrapolated daily dose, a constant release rate is assumed over the two sampling periods.

[0092] Example 2a - In vitro release of travoprost The aforementioned polymers are used to form implants as described above. All implants are uncoated. The bioactive agent is travoprost ester (CAS#157283-68-6). Three sets of implants are made.

[0093] [Table 5]

[0094] The cumulative release (%) over time is shown in Figure 6. The extrapolated daily dose (μg / day) over time is shown in Figure 7. Figures 8 and 9 are composites of optical microscope images at three time periods for 2a-2 and 2a-3, respectively.

[0095] The release of travoprost is shown for up to about 130 days. For both Experiments 2a-2 and 2a-3, a second burst is observed, resulting in a rapid release of the remaining travoprost. This second burst appears to correlate with a change in implant shape. See Figures 8 and 9, where 2a-2 and 2a-3 undergo substantial flattening of the implant at about day 100, leading to a high release rate of the remaining travoprost within 30 to 40 days.

[0096] Example 2b - Release rate of travoprost at different loading rates Implants are formed as described above using the polymers described above. All implants are uncoated. The bioactive agent is travoprost ester (CAS#157283-68-6). Two sets of implants are made.

[0097] [Table 6]

[0098] The cumulative release (%) over time is shown in Figure 10. The extrapolated daily dose (μg / day) over time is shown in Figure 11. Figure 12 is a composite of optical microscope images of samples from Set 2b-1 at 31 and 133 days.

[0099] The release rate, as a percentage of total loading, is lower for the 10 wt% formulation than for the 15 wt% formulation. Translated into daily dose, the difference is significant and does not directly correlate with the travoprost loading. The 10 wt%-loaded implants also do not exhibit the second burst observed with the 15 wt% formulation. Indeed, the 10 wt% implants certainly maintain their shape for a longer period than the 15 wt% implants; this is illustrated by comparing Figure 9, where substantial flattening is observed, with Figure 12, where the implants maintain their shape. The residual concentrations of travoprost in the implants at 100 days are approximately 7.5 wt% for the 15 wt% travoprost implants and approximately 7 wt% for the 10 wt% travoprost implants. Based on these calculations, no direct correlation can be found between the concentration of travoprost at a particular time later in the polymer degradation process and either the shape change or the second burst.

[0100] Due to an unexpectedly low release rate, one implant from the 10 wt% travoprost batch is extracted at approximately day 80 to verify mass balance. A residual amount of travoprost comparable to the expected amount is recovered from the implant.

[0101] Example 2c - In vitro release of latanoprost Implants are formed as described above using the aforementioned polymer. Only PEA III X25-based implants are coated. The coating polymer is PLGA. The bioactive agent is latanoprost (CAS#130209-82-4). Three sets of implants are made.

[0102] [Table 7]

[0103] In this study, suboptimal sampling methods were used during the first few weeks, potentially resulting in adsorption of latanoprost to the glass vials. Therefore, only the release duration, as opposed to the daily dose, can be accurately measured, as this is not affected by potential loss due to adsorption.

[0104] The cumulative release (%) over time is shown in Figure 13. Figure 14 shows optical microscope images showing the typical appearance of implants with the composition 2c-1 after several weeks in phosphate buffer at 37°C.

[0105] Each of the 2c-1, 2c-2, and 2c-3 polymer grades allows for sustained release of latanoprost for several months. PEA 85D15L X50 exhibits sustained release over two months, and PEA 85D15L X25 exhibits sustained release over three months. A slow burst is observed for PEA 85D15L X25 around day 90. For PEA 85D15L X50, the implant appears to have released all of the latanoprost before reaching this point. These curves do not reach 100% release, which can be explained by the possibility of partial loss of latanoprost due to adsorption. A PLGA coating can further increase the release time. However, as shown in Figure 14, the implant shape changes, and the plasticized polymer is released from the tip of the implant. The implant shape increases in length during this time. In the ocular chamber, the limited chamber volume may require an implant with limited volume and stability (or reduced time), and implants that change shape in this way may not be suitable for use in intraocular administration.

[0106] Example 2d - Effect of Coating PEA 85D15L on Latanoprost Release To reduce the burst during the first few days, we will coat the implant with a polymer layer that does not contain a bioactive agent. Previous results have shown that coating with polymers such as PLGA or PLA significantly reduces the burst. However, such coatings are expected to reduce the release of latanoprost from the PEA 85D15L formulation to levels below the desired daily dose. Therefore, we will attempt to coat the implant with the same polymer used for the core.

[0107] The aforementioned polymer is used to form implants as described above. The bioactive agent is latanoprost (CAS#130209-82-4). Two sets of implants are made.

[0108] [Table 8]

[0109] The extrapolated daily dose (μg / day) for the first 30 days of release is shown in Figure 15. Compared to uncoated implants, coated implants release less in the first 2 days. This is theorized to be due to the rapid migration of latanoprost through the polymer matrix. Since the daily doses of both sets of implants reach approximately the same level at about 6 days, it is expected that there will be no significant difference in release duration between coated and uncoated implants. However, coating may be useful for suppressing burst release.

[0110] Additional Description of Exemplary Embodiments 1. A random copolymer having Formula I: [ka] (In the formula, m is 0 to 0.20, n is 0.80 to 0.95, q is 0 to 0.20, and m+n+q=1, where m, n, and q represent the equivalent weights of corresponding units in the random copolymer; p is about 5 to about 300; R 1 is C2~C 20 is alkylene; R 4 is hydrogen, (C1-C6) alkyl, (C2-C6) alkenyl, (C2-C6) alkynyl, (C6-C 10)Aryl, -CH2SH, -(CH2)2S(CH3), -CH2OH, -CH(OH)CH3, -(CH2)4NH3+, -(CH2)3NHC(=NH2+)NH2, -CH2COOH, -CH2-CO-NH2, -CH 2CH2-CO-NH2, -CH2CH2COOH, CH3-CH2-CH(CH3)-, (CH3)2CH-CH2-, H2N-(CH2)4-, Ph-CH2-, CH=C-CH2-, (CH3)2CH-, Ph-NH-, [ka] and; R 6 is represented by formula II or formula III [ka] is due to; R 7 (C6~C 10 ) aryl(C1-C6) alkylene; and R 8 is a C3-C8 alkylene) Random copolymers by. 2. The random copolymer of exemplary embodiment 1, wherein n is 0.8 to 0.9. 3. The random copolymer of any one of the preceding exemplary embodiments, wherein m is from 0 to 0.15, and q is from 0 to 0.15. 4. The random copolymer of any one of the preceding exemplary embodiments, wherein m is 0.1 to 0.2. 5. The random copolymer of any one of the preceding exemplary embodiments, wherein m is 0.05 to 0.15. 6. The random copolymer of any one of the preceding exemplary embodiments, wherein the ratio m:q is from 5:1 to 1:5. 7. The random copolymer of any one of the preceding exemplary embodiments, wherein the ratio m:q is from 4:1 to 1:4. 8. The random copolymer of any one of the preceding exemplary embodiments, wherein m is greater than or equal to q. 9. The random copolymer of any one of the preceding exemplary embodiments, wherein q is 0. 10. The random copolymer of any one of the preceding exemplary embodiments, wherein p is 50 to 200. 11. The random copolymer of any one of the preceding exemplary embodiments, having a wet Tg of 36°C or greater. 12. The random copolymer of any one of the preceding exemplary embodiments, having a wet Tg of 36°C, 36.5°C, 37°C, 37.5°C, 38°C, or 39°C to 45°C, 44°C, 43°C, 42°C, 41°C, 40°C, 39°C, 38°C, or 37°C. 13. The random copolymer of any one of the preceding exemplary embodiments, wherein the initial wet Tg of the random copolymer and the wet Tg of the random copolymer after 35 days of storage in PBS at 37°C differ by at most + / - 10%, + / - 9%, + / - 8%, + / - 7%, + / - 6%, or + / - 5%. 14. The random copolymer of any one of the preceding exemplary embodiments, wherein q is 0.05 to 0.20, the initial wet Tg of the random copolymer differs from the wet Tg of the random copolymer after 35 days in PBS at 37°C by at most + / -10%, + / -9%, + / -8%, + / -7%, + / -6%, or + / -5%, and the Mn after 35 days in PBS at 37°C is 50%, 55%, 60%, or 65% to 70%, 75%, or 80% of the initial Mn. 15. The random copolymer of any one of the preceding exemplary embodiments, wherein R1 is —(CH2)8— or —(CH2)4—. 16.R 4 is hydrogen, (C1-C6) alkyl, CH3-CH2-CH(CH3)-, (CH3)2CH-CH2-, Ph-CH2-, or (CH3)2CH-. 17.R 6

[0023] The random copolymer of any one of the preceding exemplary embodiments, wherein 18.R 7

[0023] The random copolymer of any one of the preceding exemplary embodiments, wherein is C6 aryl-CH2-. 19.R 8

[0023] The random copolymer of any one of the preceding exemplary embodiments, wherein is -(CH2)4-. 20. The random copolymer of any one of the preceding exemplary embodiments, wherein the wet Tg is the initial wet Tg after immersion in PBS buffer at 37° C. for 4 days. 21. A drug delivery device comprising the random copolymer of any one of the preceding exemplary embodiments and a bioactive agent. 22. The drug delivery device of exemplary embodiment 21, which is in the shape of a cylinder, a disk, or a sphere. 23. The drug delivery device of exemplary embodiment 21, which is in the shape of a cylinder having a diameter of 100, 150, 200, or 250 micrometers to 1000, 900, 800, 700, 600, or 500 micrometers. 24. The drug delivery device of exemplary embodiment 21 or 23, which is in the shape of a cylinder having a length of 0.5, 1, 1.5, 2, 2.5, 3, 3.5, 4, 4.5, or 5 millimeters to 30, 25, 20, 15, 10, 5, 4, or 3 millimeters. 25. The drug delivery device of exemplary embodiment 21, which is in the shape of a cylinder having a diameter of 1, 2, 3, 4 or 5 to 4, 5, 6, 7, 8, 9 or 10 mm. 26. The drug delivery device of exemplary embodiment 21 or 25, which is in the shape of a cylinder having a length of 10, 15, 20, 25, or 30 mm to 150, 120, 100, or 80 mm. 27. The drug delivery device of exemplary embodiment 21, which is in the shape of a cylinder having a diameter of 1 to 5 mm and a length of 20 to 100 mm. 28. The drug delivery device of any one of the preceding exemplary embodiments, comprising a core comprising the random copolymer of any one of the preceding exemplary embodiments and a bioactive agent, and a shell comprising a shell polymer. 29. The drug delivery device of exemplary embodiment 28, wherein the shell polymer comprises poly(lactic acid), poly(glycolic acid), poly(lactide-co-glycolide), polycaprolactone, or a combination thereof. 30. The drug delivery device of exemplary embodiment 28, wherein the shell polymer comprises the random copolymer of any one of the preceding exemplary embodiments. 31. The drug delivery device of any one of the preceding exemplary embodiments, wherein the drug delivery device is cylindrical in shape and comprises a cylindrical core and a cylindrical shell. 32. The drug delivery device of exemplary embodiment 31, wherein the cylindrical shell does not surround one end of the cylindrical core. 33. The drug delivery device of exemplary embodiment 31, wherein the cylindrical shell does not surround both ends of the cylindrical core. 34. A drug delivery device according to any one of exemplary embodiments 28-33, wherein the shell does not contain a bioactive agent. 35. An injectable formulation comprising a plurality of microparticles or nanoparticles comprising a random copolymer according to any one of exemplary embodiments 1-20 and a bioactive agent. 36. The injectable formulation of exemplary embodiment 35, comprising a plurality of microparticles comprising a random copolymer and a bioactive agent, and having an average particle diameter of 10 to 500 micrometers. 37. The injectable formulation of exemplary embodiment 35, comprising a random copolymer and a bioactive agent, and comprising a plurality of microparticles having an average particle diameter of 10, 20, 30, 40, 50, 60, 70, 80, 90, or 100 micrometers to 500, 475, 450, 425, 400, 375, 350, 325, or 300 micrometers. 38. The injectable formulation of exemplary embodiment 35, comprising a random copolymer and a bioactive agent, and comprising a plurality of nanoparticles having an average particle diameter of 50, 100, 150, 200, 250, 300, 350, 400, 450, or 500 nanometers to 1000, 950, 900, 850, or 800 nanometers. 39. A medical device comprising a coating comprising the random copolymer described in any one of exemplary embodiments 1-20. 40. The medical device of exemplary embodiment 39, further comprising a bioactive agent in the coating. 41. A medical device comprising a coating comprising a first layer and a second layer over the first layer, wherein the first layer comprises a random copolymer described in any one of exemplary embodiments 1-20 and a bioactive agent, and the second layer comprises a second polymer. 42. The medical device of exemplary embodiment 41, wherein the second polymer is a random copolymer of any one of exemplary embodiments 1-20. 43. The drug delivery device, injectable formulation, or medical device of any one of the preceding exemplary embodiments, wherein the bioactive agent is useful for treating glaucoma, ocular hypertension, wet age-related macular degeneration (AMD), diabetic retinopathy, diabetic macular edema, or other diseases of the eye. 44. The drug delivery device, injectable formulation, or medical device of any one of the preceding exemplary embodiments, wherein the bioactive agent comprises latanoprost, bimatoprost, or travoprost. 45. The drug delivery device, injectable formulation, or medical device of any one of the preceding exemplary embodiments, wherein the bioactive agent comprises latanoprost, bimatoprost, or travoprost at a loading of at least 10%, 11%, 12%, 13%, 14%, or 15% by weight, based on the total weight of the (core) random copolymer plus the bioactive agent. 46. ​​The drug delivery device, injectable formulation, or medical device of any one of the preceding exemplary embodiments, wherein the bioactive agent comprises latanoprost, bimatoprost, or travoprost at a loading of up to 30% by weight or 25% by weight, based on the total weight of the (core) random copolymer plus bioactive agent. 47. The drug delivery device, injectable formulation, or medical device of any one of the preceding exemplary embodiments, wherein the bioactive agent comprises latanoprost, bimatoprost, or travoprost at a loading of up to 22%, 21%, 20%, 19%, 18%, or 17% by weight, based on the total weight of the (core) random copolymer plus bioactive agent. 48. The drug delivery device, injectable formulation, or medical device of any one of the preceding exemplary embodiments, wherein the bioactive agent comprises latanoprost, bimatoprost, or travoprost at a loading of 11% to 17% by weight, based on the total weight of the (core) random copolymer plus bioactive agent. 49. The drug delivery device, injectable formulation, or medical device of any one of the preceding exemplary embodiments, wherein the bioactive agent is released in vitro for at least 100 days or at least 110 days. 50. The drug delivery device, injectable formulation, or medical device of any one of the preceding exemplary embodiments, wherein the bioactive agent is released in vivo over a period of at least 100 days or at least 110 days. 51. The drug delivery device, injectable formulation, or medical device of any one of the preceding exemplary embodiments, wherein the bioactive agent is released in vitro over a period of up to 180 days, up to 170 days, up to 160 days, up to 150 days, up to 140 days, up to 130 days, or up to 120 days. 52. The drug delivery device, injectable formulation, or medical device of any one of the preceding exemplary embodiments, wherein the bioactive agent is released in vivo over a period of up to 180 days, up to 170 days, up to 160 days, up to 150 days, up to 140 days, up to 130 days, or up to 120 days. 53. The drug delivery device, injectable formulation, or medical device of any one of the preceding exemplary embodiments, wherein the bioactive agent comprises a chemotherapeutic agent, a JAK kinase inhibitor, an antipsychotic agent, or an antiviral agent. 54. The drug delivery device, injectable formulation, or medical device of any one of the preceding exemplary embodiments, wherein the bioactive agent comprises one or more of sorafenib, pazopanib, axitinib, regorafenib, cabozantinib, lenvatinib, sunitinib, nintedanib, crizotinib, ceritinib, alectinib, brigatinib, bosutinib, dasatinib, imatinib, nilotinib, ponatinib, vemurafenib, dabrafenib, ibrutinib, palbociclib, ribociclib, gefitinib, erlotinib, lapatinib, afatinib, osimertinib, or trametinib. 55. The drug delivery device, injectable formulation, or medical device of any one of the preceding exemplary embodiments, wherein the bioactive agent comprises one or more of tofacitinib, ruxolitinib, oclacitinib, baricitinib, peficitinib, fedratinib, upadacitinib, filgotinib, cerdulatinib, gandotinib, lestaurtinib, momelotinib, or pacritinib. 56. The drug delivery device, injectable formulation, or medical device of any one of the preceding exemplary embodiments, wherein the bioactive agent comprises one or more of aripiprazole, brexiprazole, olanzapine, quetiapine, or ziprasidone. 57. The drug delivery device, injectable formulation, or medical device of any one of the preceding exemplary embodiments, wherein the bioactive agent comprises one or more of tenofovir, emtricitabine, efavirenz, elvitegravir, cobicistat, ribavirin, daclatasvir, sofosbuvir, velpatasvir, voxilaprevir, glecaprevir, pibrentasvir, elbasvir, grazoprevir, simeprevir, or ledipasvir. 58. The drug delivery device, injectable formulation, or medical device of any one of the preceding exemplary embodiments, wherein the bioactive agent is a drug, a prodrug or codrug thereof, a metabolite thereof, and / or a prodrug of a metabolite. 59. A method of treating a human or animal patient, comprising implanting into the patient a drug delivery device, an injectable formulation or a medical device according to any one of the preceding exemplary embodiments. 60. A method of treating a human or animal patient suffering from glaucoma, ocular hypertension, wet age-related macular degeneration (AMD), diabetic retinopathy or diabetic macular edema by implanting a drug delivery device described in any one of the preceding exemplary embodiments into the patient's eye. 61. A method of treating a human or animal patient suffering from glaucoma, ocular hypertension, wet age-related macular degeneration (AMD), diabetic retinopathy or diabetic macular edema by implanting a drug delivery device described in any one of the preceding exemplary embodiments into a position within the intraocular chamber of the patient's eye. 62. Use of a drug delivery device according to any one of the preceding exemplary embodiments for treating glaucoma, ocular hypertension, wet age-related macular degeneration (AMD), diabetic retinopathy or diabetic macular edema. 63. A drug delivery device according to any one of the preceding exemplary embodiments for use in the treatment of glaucoma, ocular hypertension, wet age-related macular degeneration (AMD), diabetic retinopathy or diabetic macular edema.

[0111] The terms "a," "an," "the," and similar uses in connection with the description of the present invention (particularly in connection with the claims that follow) are to be construed as including both the singular and the plural, unless otherwise indicated herein or clearly contradicted by context. The terms "comprise," "have," "include," and "contain" are to be construed as open-ended terms (i.e., meaning "including, but not limited to"), unless otherwise specified. The recitation of ranges of values ​​herein is merely intended to serve as a shorthand method of individually referring to each separate value falling within the range, unless otherwise stated herein, and each separate value is incorporated herein as if it were individually set forth herein. Unless otherwise claimed, the use of any and all examples or exemplary language (e.g., "such as") provided herein is intended merely to better clarify the invention and does not pose a limitation on the scope of the invention. No language in the specification should be construed as indicating any non-claimed element essential to the practice of the invention.

[0112] Preferred embodiments of the present invention, including the best mode known to the inventors for carrying out the invention, are described herein. Variations of these preferred embodiments may become apparent to those of ordinary skill in the art upon reading the foregoing description. The inventors expect that skilled artisans will take advantage of such variations, and the inventors intend that the invention may be practiced otherwise than as specifically described herein. Accordingly, this invention includes all modifications and equivalents of the subject matter recited in the claims appended hereto as permitted by applicable law. While specific optional features are described as embodiments of the invention, the description is meant to include and specifically disclose all combinations of these embodiments unless specifically indicated otherwise or physically impossible.

Claims

1. A random copolymer having the formula I: 【Chemistry 1】 (In the formula, m is 0.05 to 0.20, n is 0.80 to 0.95, q is 0 to 0.15, and m+n+q=1, where m, n, and q represent the equivalent weights of corresponding units in the random copolymer; p is from about 5 to about 300; R １ is C ２ ~C ２０ alkylene; R ４ is hydrogen, (C １ ~C ６ ) alkyl, (C ２ ~C ６ ) alkenyl, (C ２ ~C ６ ) alkynyl, (C ６ ~C １０ ) aryl, —CH ２ SH, -(CH ２ ) ２ S (CH ３ ), -CH ２ OH, -CH(OH)CH ３ , -(CH ２ ) ４ NH ３ +, - (CH ２ ) ３ NHC (=NH ２ +)NH ２ , -CH ２ COOH, -CH ２ —CO—NH ２ , -CH ２ CH ２ —CO—NH ２ , -CH ２ CH ２ COOH, CH ３ -CH ２ -CH(CH ３ ) -, (CH ３ ) ２ CH-CH ２ -, H ２ N-(CH ２ ) ４ -, Ph-CH ２ -, CH=C-CH ２ -, (CH ３ ) ２ CH-, Ph-NH-, 【Chemistry 2】 and R ６ is represented by formula II 【Transformation 3】 is due to; R ７ is (C ６ ~C １０ ) aryl (C １ ~C ６ ) alkyl; and R ８ is C ３ ~C ８ alkylene) and a random copolymer having a wet Tg of 37°C or greater.

2. 2. The random copolymer of claim 1, wherein n is 0.8 to 0.

9.

3. 3. The random copolymer according to claim 1, wherein m is from 0.05 to 0.

15.

4. The random copolymer according to any one of claims 1 to 3, wherein q is 0.

5. 5. The random copolymer of claim 1, wherein the wet Tg is the initial wet Tg after immersion in PBS buffer for 4 days.

6. The random copolymer according to any one of claims 1 to 5, having a wet Tg of from 37°C to 44°C.

7. 7. The random copolymer according to any one of claims 1 to 6, wherein the initial wet Tg of the random copolymer and the wet Tg of the random copolymer after 35 days of storage in PBS at 37°C differ by at most + / - 10%.

8. 4. The random copolymer according to claim 1, wherein q is between 0.05 and 0.15, the initial wet Tg of the random copolymer differs from the wet Tg of the random copolymer after 35 days in PBS at 37°C by at most + / - 10%, and the Mn after 35 days in PBS at 37°C is at least 50% of the initial Mn.

9. R ４ is hydrogen, (C １ ~C ６ ) alkyl, CH ３ -CH ２ -CH(CH ３ ) -, (CH ３ ) ２ CH-CH ２ -, Ph-CH ２ - or (CH ３ ) ２ The random copolymer according to any one of claims 1 to 8, wherein the copolymer is CH-.

10. R ７ is C ６ Aryl-CH ２ The random copolymer according to any one of claims 1 to 9, wherein

11. A drug delivery device comprising the random copolymer of any one of claims 1 to 10 and a bioactive agent.

12. 12. The drug delivery device of claim 11, which is in the shape of a cylinder having a diameter of 1 to 10 mm and a length of 10 to 150 mm.

13. 13. The drug delivery device of claim 11 or 12, comprising a core comprising the random copolymer of any one of claims 1 to 10 and a bioactive agent, and a shell comprising a shell polymer, wherein the shell polymer comprises the random copolymer of any one of claims 1 to 10.

14. The drug delivery device of any one of claims 11 to 13, wherein the bioactive agent is a drug, a prodrug or codrug thereof, a metabolite thereof and / or a prodrug of said metabolite.

15. 15. The drug delivery device of any one of claims 11 to 14, wherein the bioactive agent comprises latanoprost, bimatoprost, or travoprost at a loading of 11% to 17% by weight based on the total weight of the random copolymer plus bioactive agent.

16. The drug delivery device of any one of claims 11 to 15, wherein the bioactive agent is released in vitro for at least 100 days.

17. The drug delivery device of any one of claims 11 to 16, wherein the bioactive agent is released in vivo for at least 100 days.

18. A drug delivery device according to any one of claims 11 to 17, for implantation into a human or animal patient for treatment.

19. 18. The drug delivery device of any one of claims 11 to 17, which is implanted into the eye of a human or animal patient for the treatment of glaucoma, ocular hypertension, wet age-related macular degeneration (AMD), diabetic retinopathy or diabetic macular edema.

20. 18. The drug delivery device of any one of claims 11 to 17, for use in implantation into an intraocular chamber of the eye of a human or animal patient for the treatment of glaucoma, ocular hypertension, wet age-related macular degeneration (AMD), diabetic retinopathy or diabetic macular edema.

21. 18. A drug delivery device according to any one of claims 11 to 17 for use in the treatment of glaucoma, ocular hypertension, wet age-related macular degeneration (AMD), diabetic retinopathy or diabetic macular edema.