Polyisocyanate compositions, two-component curable compositions, two-component curable coatings, two-component curable adhesives, laminates, packaging materials

Abstract

Provided are a two-component curable adhesive having excellent balance between reactivity and storage stability, and a polyisocyanate composition suitable for such an adhesive.　A polyisocyanate composition (X) contains: a polyurethane polyisocyanate (A1) which is a reaction product of a toluene diisocyanate and a polyol having 5-10 hydroxyl groups; and a phosphoric acid derivative (B), the phosphoric acid derivative (B) content being 10-5000 ppm. Also provided is a two-component curable adhesive containing such a polyisocyanate composition (X).

Description

Technical Field

[0001] The present invention relates to a polyisocyanate composition, a two-component curable composition, a two-component curable coating agent, a two-component curable adhesive, a laminate, and a packaging material.

Background Art

[0002] Laminates used for various packaging materials, labels, etc. are provided with design, functionality, storage stability, convenience, transport resistance, etc. by laminating various substrates such as various plastic films, metal foils, paper, etc. The packaging material formed by molding the laminate into a bag shape is used as a packaging material in various fields including foods, pharmaceuticals, detergents, etc.

[0003] Conventionally, for laminate films, the mainstream method has been to obtain them by a dry lamination method in which a two-component curable adhesive in which a polyisocyanate compound and a polyol compound are dissolved in a volatile organic solvent is applied to a film, the organic solvent is volatilized in the process of passing through an oven, and another film is laminated. In recent years, from the viewpoint of reducing environmental impact and improving the working environment, two-component curable solventless adhesives in which a polyisocyanate compound and a polyol compound do not contain a volatile organic solvent have attracted attention (Patent Document 1, Patent Document 2).

Prior Art Documents

Patent Documents

[0004]

Patent Document 1

Patent Document 2

Summary of the Invention

Problems to be Solved by the Invention

[0005] To improve productivity, there is a need to enhance the reactivity of these two-component curing adhesives. However, polyisocyanate compounds, one component of two-component curing adhesives, react with moisture in the air, so if the reactivity is too high, storage stability may decrease. Also, if the reaction proceeds too rapidly immediately after mixing the two components, the adhesion between the bonded material and the adhesive tends to decrease.

[0006] This invention has been made in view of these circumstances, and aims to provide a two-component curing adhesive with an excellent balance between reactivity and storage stability, and a polyisocyanate composition suitable for such an adhesive. [Means for solving the problem]

[0007] In other words, the present invention relates to a polyisocyanate composition (X) comprising a polyurethane polyisocyanate (A1), which is a reaction product of toluene diisocyanate and a polyol having 5 to 10 hydroxyl groups, and a phosphoric acid derivative (B), wherein the content of the phosphoric acid derivative (B) is 10 ppm to 5000 ppm, and a two-component curing adhesive containing such a polyisocyanate composition (X). [Effects of the Invention]

[0008] According to the present invention, it is possible to provide a two-component curing adhesive with an excellent balance between reactivity and storage stability, and a polyisocyanate composition suitable for such an adhesive. [Modes for carrying out the invention]

[0009] <Polyisocyanate composition (X)> (Polyurethane polyisocyanate (A1)) The polyisocyanate composition (X) of the present invention comprises a polyurethane polyisocyanate (A1), which is a reaction product of toluene diisocyanate and a polyol having 5 to 10, more preferably 5 to 8, hydroxyl groups. The toluene diisocyanate may be either 2,4'-toluene diisocyanate or 2,6'-toluene diisocyanate, or both.

[0010] Polyols having 5 to 10 hydroxyl groups that can be used in the synthesis of polyurethane polyisocyanate (A1) include low molecular weight polyols having 5 to 10 hydroxyl groups such as xylitol, triglycerol, sorbitol, dipentaerythritol, mannitol, sucrose, and polyglycerin, as well as polyether polyols obtained by addition polymerization of alkylene oxides such as ethylene oxide, propylene oxide, butylene oxide, styrene oxide, epichlorohydrin, tetrahydrofuran, and cyclohexylene using these low molecular weight polyols as initiators. These can be used individually or in combination of two or more.

[0011] A flexible coating film can be formed, and for example, when the polyisocyanate composition (X) of the present invention is used as a two-component curing adhesive described later, it is possible to obtain a polyether polyol obtained by addition polymerization of alkylene oxide to a low molecular weight polyol having 5 to 10 hydroxyl groups, or polyglycerin having 5 to 10 hydroxyl groups. It is also preferable to use a polyether polyol obtained by addition polymerization of at least one selected from ethylene oxide, propylene oxide, butylene oxide, and tetrahydrofuran to sorbitol, and at least one selected from polyglycerin having 5 to 10 hydroxyl groups.

[0012] It is preferable to use a polyol with a molecular weight of 200 g / mol or more and 3000 g / mol or less, more preferably one with a molecular weight of 400 g / mol or more and 3000 g / mol or less, and even more preferably one with a molecular weight of 440 g / mol or more and 2000 g / mol or less.

[0013] Polyurethane polyisocyanate (A1) is obtained by reacting toluene diisocyanate with a polyol under conditions in which the isocyanate groups of toluene diisocyanate are in excess of the hydroxyl groups of the polyol. The equivalent ratio of isocyanate groups to hydroxyl groups [NCO] / [hydroxyl groups] can be adjusted as appropriate, but as an example, it is between 2.0 and 20.0.

[0014] The polyisocyanate composition (X) used in the present invention preferably has a diisocyanate monomer content reduced to 1.0% by mass or less, more preferably to 0.1% by mass or less, such as the diisocyanate monomers exemplified as raw materials for the isocyanate derivative (A3) described later, i.e., aromatic diisocyanates, aromatic aliphatic diisocyanates, aliphatic diisocyanates, and alicyclic diisocyanates.

[0015] From an occupational safety and health perspective, there is a movement to regulate the use of isocyanate monomers, and the European Commission has adopted the REACH regulation, which prohibits the market placement of products containing 0.1% by mass or more of isocyanate monomers if certain requirements are not met. Products can be made compliant with such regulations by removing unreacted diisocyanate monomers until the amount of diisocyanate monomer in the polyisocyanate composition is 0.1% by mass or less.

[0016] Furthermore, when manufacturing laminates for food packaging using a two-component curing adhesive containing aromatic diisocyanate as the isocyanate derivative (A3) described later, and with a considerable amount of the aromatic diisocyanate remaining as a raw material, unreacted aromatic isocyanate monomers may remain in the adhesive layer. The isocyanate monomers react with surrounding water to form primary aromatic amines (PAAs), which may migrate through the film and leach into the contents (food). PAAs are a cause for concern due to their potential harmful effects on the human body, and various regulations have been established, including the European Commission's setting of detection limits in its regulations concerning plastic materials and products for food contact.

[0017] Since PAA reacts with unreacted aromatic isocyanates present in the surroundings, the concentration of PAA gradually decreases even when aromatic isocyanates remain in the adhesive layer. Eventually, it falls below the detection limit, but from the perspective of the manufacturing efficiency of laminates for food packaging, it is preferable that the initial value of the aromatic isocyanate monomer remaining in the adhesive layer is low. By removing the diisocyanate monomer in advance, a two-component curable adhesive with excellent manufacturing efficiency can be obtained.

[0018] The removal of the diisocyanate monomer can be carried out by distilling the diisocyanate monomer under reduced pressure using a short-path distillation apparatus, a thin-film distillation apparatus, etc. The degree of reduced pressure and the distillation temperature are appropriately adjusted according to the diisocyanate monomer to be removed. As an example, it is 0.1 mbar or less and 120°C to 190°C. The removal step of the diisocyanate monomer may be carried out multiple times.

[0019] The content of the diisocyanate monomer can be measured by gas chromatography using an internal standard, for example, in accordance with ASTM D 3432. Alternatively, it can also be measured by liquid chromatography according to the following conditions.

[0020] Apparatus: "ACQUITY UPLC H-Class" manufactured by Waters Corporation Data processing: "Empower-3" manufactured by Waters Corporation Column: "ACQUITY UPLC HSS T3" (100 mm × 2.1 mmφ, 1.8 μm) manufactured by Waters Corporation, 40°C Eluent: Ammonium formate aqueous solution / methanol, 0.3 mL / min Detector: PDA Sample preparation: 1. Dissolve 100 mg of the appropriately blocked sample in 10 ml of THF (for LC). 2. Stir for 30 seconds with a vortex. 3. Dilute appropriately with the eluent (mobile phase). 4. Pass through a 0.2 μm filtration filter to obtain a measurement sample. Calculation of area ratio: Calculated using the maximum absorption wavelength for the target material.

[0021] (Polyurethane polyisocyanate (A2)) The polyisocyanate composition (X) also preferably contains polyurethane polyisocyanate (A2), which is a reaction product of toluene diisocyanate and a bifunctional polyol. This makes it possible to obtain a polyisocyanate composition (X) with a better balance of reactivity, storage stability, and coating properties. Furthermore, when used as a two-component curing type composition as described later, it is possible to form a coating film with appropriate flexibility and improve adhesion to the substrate when applied to a flexible substrate. The toluene diisocyanate may be 2,4'-toluene diisocyanate, 2,6'-toluene diisocyanate, or both.

[0022] Examples of bifunctional polyols used in the synthesis of polyurethane polyisocyanate (A2) include aliphatic diols such as ethylene glycol, 1,2-propanediol, 1,3-propanediol, 2-methyl-1,3-propanediol, 1,4-butanediol, 1,5-pentanediol, 3-methyl-1,5-pentanediol, 1,6-hexanediol, neopentyl glycol, dimethylbutanediol, butylethylpropanediol, diethylene glycol, triethylene glycol, tetraethylene glycol, dipropylene glycol, tripropylene glycol, bishydroxyethoxybenzene, 1,4-cyclohexanediol, and 1,4-cyclohexanedimethanol, as well as polyetherdiols obtained by addition polymerization of alkylene oxides such as ethylene oxide, propylene oxide, butylene oxide, styrene oxide, epichlorohydrin, tetrahydrofuran, and cyclohexylene using these aliphatic diols as initiators. One or more of these can be used in combination.

[0023] The bifunctional polyol has a molecular weight of, for example, 8000 g / mol or less. It is more preferable that it is between 100 g / mol and 4000 g / mol.

[0024] When the polyisocyanate composition (X) contains polyurethane polyisocyanate (A2), the amount of polyurethane polyisocyanate (A1) can be adjusted as appropriate, but as an example, it is preferable that the content of polyurethane polyisocyanate (A1) in relation to the total amount of polyurethane polyisocyanate (A1) and polyurethane polyisocyanate (A2) is 40% by mass or more.

[0025] If the polyisocyanate composition (X) contains polyurethane polyisocyanate (A2), polyurethane polyisocyanate (A1) and polyurethane polyisocyanate (A2) may be synthesized separately and then mixed. Alternatively, toluene diisocyanate may be reacted with a polyol having 5 to 10 hydroxyl groups and a bifunctional polyol under conditions in which the isocyanate groups of toluene diisocyanate are in excess of the hydroxyl groups of the polyol, and then, if necessary, unreacted diisocyanate monomers may be removed to obtain a mixture of polyurethane polyisocyanate (A1) and polyurethane polyisocyanate (A2). The equivalent ratio of isocyanate groups to hydroxyl groups [NCO] / [hydroxyl groups] can be adjusted as appropriate, but as an example, it is between 2.0 and 20.0.

[0026] When polyurethane polyisocyanate (A2) is synthesized separately, it is obtained by reacting toluene diisocyanate with a bifunctional polyol under conditions in which the isocyanate groups of toluene diisocyanate are in excess of the hydroxyl groups of the bifunctional polyol, and then removing unreacted diisocyanate monomers as needed. The equivalent ratio of isocyanate groups to hydroxyl groups [NCO] / [hydroxyl groups] can be adjusted as appropriate, but as an example, it is between 2.0 and 20.0.

[0027] (Isocyanate derivative (A3)) The polyisocyanate composition (X) may contain isocyanate derivatives (A3) other than polyurethane polyisocyanate (A1) and polyurethane polyisocyanate (A2) in order to improve the storage stability and coating properties of the polyisocyanate composition (X), and to improve the flexibility of the coating film when used as a two-component curing type composition described later. Examples of isocyanate derivatives (A3) include conventionally known aromatic diisocyanates, aromatic aliphatic diisocyanates, aliphatic diisocyanates, alicyclic diisocyanates, and burette, nurate, adduct, allophanate, carbodiimide modified, uretdione modified forms of these diisocyanates, as well as polyurethane polyisocyanates other than (A1) and (A2), and can be used individually or in combination of two or more.

[0028] Examples of aromatic diisocyanates include 2,2'-diphenylmethane diisocyanate, 2,4'-diphenylmethane diisocyanate, 4,4'-diphenylmethane diisocyanate (also known as MDI), polymethylene polyphenyl polyisocyanate (also called polymeric MDI or crude MDI), 1,3-phenylenediisocyanate, 4,4'-diphenyl diisocyanate, 1,4-phenylenediisocyanate (also known as PPDI), and 2,4-tolylene diisocyanate. Examples include, but are not limited to, annetes, 2,6-tolylene diisocyanate (also known as TDI), 4,4'-toluidine diisocyanate, 2,4,6-triisocyanate toluene, 1,3,5-triisocyanate benzene, tolidine diisocyanate (also known as TODI), dianisidine diisocyanate, naphthalene diisocyanate (also known as NDI), 4,4'-diphenyl ether diisocyanate, and 4,4',4"-triphenylmethane triisocyanate.

[0029] Aromatic aliphatic diisocyanates refer to aliphatic isocyanates having one or more aromatic rings in their molecule, and include, but are not limited to, m- or p-xylylene diisocyanate (also known as XDI) and α,α,α',α'-tetramethylxylylene diisocyanate (also known as TMXDI).

[0030] Examples of aliphatic diisocyanates include trimethylene diisocyanate, tetramethylene diisocyanate, hexamethylene diisocyanate (also known as HDI), pentamethylene diisocyanate (also known as PDI), 1,2-propylene diisocyanate, 2,3-butylene diisocyanate, 1,3-butylene diisocyanate, dodecamethylene diisocyanate, 2,4,4-trimethylhexamethylene diisocyanate, and lysine diisocyanate (also known as LDI), but are not limited to these.

[0031] Examples of alicyclic diisocyanates include, but are not limited to, 3-isocyanate-methyl-3,5,5-trimethylcyclohexyl isocyanate, isophorone diisocyanate (also known as IPDI), 1,3-cyclopentane diisocyanate, 1,3-cyclohexane diisocyanate, 1,4-cyclohexane diisocyanate, methyl-2,4-cyclohexane diisocyanate, methyl-2,6-cyclohexane diisocyanate, 4,4'-methylenebiscyclohexyl isocyanate (also known as hydrogenated MDI or HMDI), 1,3-bis(isocyanate-methyl)cyclohexane (also known as hydrogenated XDI or HXDI), hydrogenated TMXDI, norbornane diisocyanate (also known as NBDI), etc.

[0032] Polyols used in the synthesis of polyurethane polyisocyanates other than (A1) and (A2) include glycols such as ethylene glycol, 1,2-propanediol, 1,3-propanediol, 2-methyl-1,3-propanediol, 1,4-butanediol, 1,5-pentanediol, 3-methyl-1,5-pentanediol, 1,6-hexanediol, neopentyl glycol, dimethylbutanediol, butylethylpropanediol, diethylene glycol, triethylene glycol, tetraethylene glycol, dipropylene glycol, tripropylene glycol, bishydroxyethoxybenzene, 1,4-cyclohexanediol, and 1,4-cyclohexanedimethanol;

[0033] Trifunctional or tetrafunctional aliphatic alcohols such as glycerin, trimethylolpropane, and pentaerythritol; Bisphenols such as bisphenol A, bisphenol F, hydrogenated bisphenol A, and hydrogenated bisphenol F; Dimer All;

[0034] Polyether polyols obtained by addition polymerization of alkylene oxides such as ethylene oxide, propylene oxide, butylene oxide, styrene oxide, epichlorohydrin, tetrahydrofuran, and cyclohexylene in the presence of polymerization initiators such as the aforementioned glycols and trifunctional or tetrafunctional aliphatic alcohols;

[0035] Polyester polyols (1) are reaction products of polyesters obtained by the ring-opening polymerization reaction of cyclic ester compounds such as propiolactone, butyrolactone, ε-caprolactone, σ-valerolactone, and β-methyl-σ-valerolactone, and polyhydric alcohols such as glycol, glycerin, trimethylolpropane, and pentaerythritol. Polyester polyols obtained by reacting a difunctional polyol such as the glycol, dimer ol, or bisphenol with a polycarboxylic acid (2): Polyester polyols obtained by reacting a trifunctional or tetrafunctional aliphatic alcohol with a polycarboxylic acid (3); Polyester polyols obtained by reacting a bifunctional polyol with the aforementioned trifunctional or tetrafunctional aliphatic alcohol and a polycarboxylic acid (4); Polyester polyols (5), which are polymers of hydroxyl acids such as dimethylolpropionic acid and castor oil fatty acids;

[0036] A polyether polyurethane polyol obtained by increasing the molecular weight of the aforementioned polyether polyol with an isocyanate compound; A polyester polyether polyurethane polyol obtained by reacting at least one of polyester polyols (1) to (5) with a polyether polyol and an isocyanate compound; Polyester polyurethane polyols obtained by increasing the molecular weight of polyester polyols (1) to (5) with isocyanate compounds;

[0037] Examples include castor oil, dehydrated castor oil, hydrogenated castor oil (a hydrogenated form of castor oil), castor oil-based polyols such as 5-50 molar alkylene oxide adducts of castor oil, and mixtures thereof. These can be used individually or in combination of two or more.

[0038] Polycarboxylic acids used in the synthesis of polyester polyols (2) to (4) include aromatic polybasic acids such as orthophthalic acid, terephthalic acid, isophthalic acid, phthalic anhydride, 1,4-naphthalenedicarboxylic acid, 2,5-naphthalenedicarboxylic acid, 2,6-naphthalenedicarboxylic acid, 2,3-naphthalenedicarboxylic acid anhydride, naphthalic acid, trimellitic acid, trimellitic anhydride, pyromellitic acid, pyromellitic anhydride, biphenyldicarboxylic acid, 1,2-bis(phenoxy)ethane-p,p'-dicarboxylic acid, benzophenonetetracarboxylic acid, benzophenonetetracarboxylic dianhydride, 5-sodium sulfoisophthalic acid, tetrachlorophthalic anhydride, and tetrabromophthalic anhydride; Methyl esters of aromatic polybasic acids such as dimethyl terephthalic acid and dimethyl 2,6-naphthalenedicarboxylate;

[0039] Aliphatic polybasic acids such as malonic acid, succinic acid, succinic anhydride, glutaric acid, adipic acid, pimelic acid, suberic acid, azelaic acid, sebacic acid, fumaric acid, maleic acid, maleic anhydride, and itaconic acid; Alkyl esters of aliphatic polybasic acids such as dimethyl malonate, diethyl malonate, dimethyl succinate, dimethyl glutarate, dimethyl adipate, diethyl pimephosphate, diethyl sebacate, dimethyl fumarate, diethyl fumarate, dimethyl maleate, and diethyl maleate;

[0040] Examples include 1,1-cyclopentanedicarboxylic acid, 1,2-cyclopentanedicarboxylic acid, 1,3-cyclopentanedicarboxylic acid, 1,2-cyclohexanedicarboxylic acid, 1,3-cyclohexanedicarboxylic acid, 1,4-cyclohexanedicarboxylic acid, tetrahydrophthalic anhydride, 4-methylhexahydrophthalic anhydride, hexahydrophthalic anhydride, cyclohexane-1,2,4-tricarboxylic acid-1,2-anhydride, hymic anhydride, hettic anhydride, and other alicyclic polybasic acids, which can be used individually or in combination of two or more.

[0041] When the polyisocyanate composition (X) contains an isocyanate derivative (A3), it is preferable that the content of polyurethane polyisocyanate (A1) relative to the total amount of polyurethane polyisocyanate (A1) and isocyanate derivative (A3) is 40% by mass or more.

[0042] (Phosphate derivative (B)) Examples of phosphate derivatives (B) include phosphoric acid, pyrophosphate, triphosphate, methyl acid phosphate, ethyl acid phosphate, butyl acid phosphate, dibutyl phosphate, 2-ethylhexyl acid phosphate, bis(2-ethylhexyl) phosphate, isododecyl acid phosphate, butoxyethyl acid phosphate, oleyl acid phosphate, tetracosyl acid phosphate, 2-hydroxyethyl methacrylate acid phosphate, polyoxyethylene alkyl ether phosphate, etc. Phosphoric acid, pyrophosphate, triphosphate, and butyl acid phosphate are preferred.

[0043] The content of the phosphate derivative (B) in the polyisocyanate composition (X) of the present invention is 10 ppm or more and 5000 ppm or less. This makes it possible to obtain a polyisocyanate composition (X) with excellent reactivity and storage stability. The content of the phosphate derivative (B) in the polyisocyanate composition (X) is more preferably 50 ppm or more, and more preferably 1000 ppm or less.

[0044] It is preferable to add the phosphoric acid derivative (B) after the urethane formation of the polyurethane polyisocyanate (A1) is complete. If the product is manufactured through a step to remove unreacted isocyanate monomers, it may be added after the urethane formation reaction of the polyurethane polyisocyanate (A1) is complete but before the removal of unreacted isocyanate monomers, or it may be added after the removal of isocyanate monomers.

[0045] <Two-component curable composition> The polyisocyanate composition (X) of the present invention can be used as a two-component curable composition in combination with an isocyanate-reactive composition containing a compound that is reactive with isocyanate. Examples of compounds that are reactive with isocyanate include polyether polyols, polyester polyols, polyester polyether polyols, polyurethane polyols, polyester polyurethane polyols, polyether polyurethane polyols, vegetable oil polyols, sugar alcohols, polycarbonate polyols, acrylic polyols, hydroxyl group-containing olefin resins, hydroxyl group-containing fluororesins, and (poly)alkanolamines.

[0046] Such two-component curing compositions can be used, for example, in adhesives, coatings, sealants, elastomers, and the like.

[0047] <Two-component curing type coating agent> The two-component curable coating agent of the present invention comprises the polyisocyanate composition (X) described above and an isocyanate reactive composition. The coating agent of the present invention can be suitably used for various applications, but because it has excellent adhesion to metal materials, it can be particularly suitably used as a coating agent for metal substrates such as aluminum and steel plates, as an overcoat for coating films containing aluminum pigments and metal particles, for coating electrical components, and for electrical insulation.

[0048] The isocyanate-reactive composition (Y) contains a compound (C) (hereinafter also referred to as isocyanate-reactive compound (C)) having multiple functional groups that are reactive with isocyanates, such as polyester polyols (C1), polyether polyols (C2), vegetable oil polyols (C3), polyurethane polyols (C4), sugar alcohols (C5), acrylic polyols (C6), amine compounds (C7), and epoxy compounds (C8). The isocyanate-reactive compound (C) can be used alone or in combination of two or more types.

[0049] Examples of polyester polyols (C1) include polyester polyols obtained as reaction products of polyhydric alcohols and polycarboxylic acids, and lactone-based polyester polyols obtained by polycondensation reactions of aliphatic polyols with various lactones such as ε-caprolactone. It is preferable to use polyester polyols obtained as reaction products of polyhydric alcohols and polycarboxylic acids.

[0050] Examples of polyhydric alcohols include aliphatic diols such as ethylene glycol, diethylene glycol, propylene glycol, 1,3-propanediol, 1,2,2-trimethyl-1,3-propanediol, 2,2-dimethyl-3-isopropyl-1,3-propanediol, 1,4-butanediol, 1,3-butanediol, 3-methyl-1,3-butanediol, 1,5-pentanediol, 3-methyl-1,5-pentanediol, neopentyl glycol, 1,6-hexanediol, 1,4-bis(hydroxymethyl)cyclohesane, and 2,2,4-trimethyl-1,3-pentanediol;

[0051] Trimethylolethane, trimethylolpropane, glycerin, hexanetriol, pentaerythritol, and other trifunctional or more aliphatic polyols;

[0052] Bisphenols such as bisphenol A and bisphenol F; bisphenol alkylene oxide adducts obtained by adding ethylene oxide, propylene oxide, etc., to bisphenols such as bisphenol A and bisphenol F;

[0053] Examples include polyether polyols obtained by ring-opening polymerization of aliphatic diols or polyols with various cyclic ether-containing compounds such as ethylene oxide, propylene oxide, tetrahydrofuran, ethyl glycidyl ether, propyl glycidyl ether, butyl glycidyl ether, phenyl glycidyl ether, and allyl glycidyl ether, and these can be used individually or in combination of two or more.

[0054] Examples of polycarboxylic acids include aliphatic dicarboxylic acids such as succinic acid, adipic acid, azelaic acid, sebacic acid, dodecanedicarboxylic acid, maleic anhydride, fumaric acid, 1,3-cyclopentanedicarboxylic acid, and 1,4-cyclohexanedicarboxylic acid; Aromatic dicarboxylic acids such as orthophthalic acid, isophthalic acid, terephthalic acid, 1,4-naphthalenedicarboxylic acid, 2,5-naphthalenedicarboxylic acid, 2,6-naphthalenedicarboxylic acid, naphthalic acid, biphenyldicarboxylic acid, and 1,2-bis(phenoxy)ethane-p,p'-dicarboxylic acid; and anhydrides or ester-forming derivatives of these aliphatic or dicarboxylic acids; Examples include p-hydroxybenzoic acid, p-(2-hydroxyethoxy)benzoic acid and ester-forming derivatives of their dihydroxycarboxylic acids, and polybasic acids such as dimer acids, which can be used individually or in combination of two or more.

[0055] The molecular weight of the polyester polyol (C1) is preferably 250 g / mol or more and 20,000 g / mol or less, and more preferably 500 g / mol or more and 10,000 g / mol or less. The hydroxyl value of the polyester polyol (C1) is preferably 5 mg KOH / g or more and 500 mg KOH / g or less.

[0056] Examples of polyether polyols (C2) include those obtained by addition polymerization of alkylene oxides such as ethylene oxide, propylene oxide, butylene oxide, styrene oxide, epichlorohydrin, tetrahydrofuran, and cyclohexylene in the presence of a polymerization initiator.

[0057] Polymerization initiators include glycols such as ethylene glycol, propylene glycol, 1,3-propanediol, 1,4-butanediol, 1,5-pentanediol, 3-methyl-1,5-pentanediol, 1,6-hexanediol, neopentyl glycol, methylpentanediol, dimethylbutanediol, butylethylpropanediol, diethylene glycol, triethylene glycol, tetraethylene glycol, dipropylene glycol, tripropylene glycol, bishydroxyethoxybenzene, 1,4-cyclohexanediol, 1,4-cyclohexanedimethanol, and triethylene glycol;

[0058] Trifunctional or tetrafunctional aliphatic alcohols such as glycerin, trimethylolpropane, pentaerythritol, and triol compounds of polypropylene glycol;

[0059] Examples include primary or secondary alkylamines such as ethylamine and diethylamine, amine compounds having multiple amino groups such as methylenediamine and ethylenediamine, and amine compounds having active hydrogen groups such as primary or secondary alkanolamines such as monoethanolamine and diethanolamine.

[0060] The molecular weight of the polyether polyol (C2) can be adjusted as appropriate, but it is preferably between 100 g / mol and 8000 g / mol. The hydroxyl value of the polyether polyol (C2) can be adjusted as appropriate, but as an example, it is preferably between 10 mg KOH / g and 1200 mg KOH / g.

[0061] Examples of vegetable oil polyols (C3) include castor oil, dehydrated castor oil, hydrogenated castor oil (a hydrogenated product of castor oil), and castor oil alkylene oxide adducts of 5 to 50 moles.

[0062] Polyurethane polyols (C4) are reaction products of low-molecular-weight or high-molecular-weight polyols and polyisocyanate compounds. As low-molecular-weight or high-molecular-weight polyols, those similar to the polyhydric alcohols exemplified as raw materials for polyester polyols (C1) can be used. As polyisocyanate compounds, those similar to those exemplified as raw materials for isocyanate derivatives (A3) can be used.

[0063] Examples of sugar alcohols (C5) include pentaerythritol, sucrose, xylitol, sorbitol, isomalt, lactitol, maltitol, and mannitol.

[0064] The acrylic polyol (C6) is required to be a (meth)acrylic acid ester having a hydroxyl group, and can be obtained by copolymerization with a polymerizable unsaturated monomer as needed. In this specification, (meth)acrylic acid means methacrylic acid or acrylic acid. Examples of (meth)acrylic acid esters having a hydroxyl group include hydroxyethyl (meth)acrylate, hydroxypropyl (meth)acrylate, and hydroxybutyl (meth)acrylate, which can be used individually or in combination of two or more.

[0065] Polymerizable unsaturated monomers include alkyl(meth)acrylates having alkyl groups with 1 to 22 carbon atoms, such as methyl(meth)acrylate, ethyl(meth)acrylate, n-propyl(meth)acrylate, n-butyl(meth)acrylate, isobutyl(meth)acrylate, tert-butyl(meth)acrylate, 2-ethylhexyl(meth)acrylate, and lauryl(meth)acrylate; Aralkyl(meth)acrylates such as benzyl(meth)acrylate and 2-phenylethyl(meth)acrylate; Cycloalkyl (meth)acrylates such as cyclohexyl (meth)acrylate and isobornyl (meth)acrylate; ω-alkoxyalkyl(meth)acrylates such as 2-methoxyethyl(meth)acrylate and 4-methoxybutyl(meth)acrylate; Polyfunctional (meth)acrylates such as ethylene glycol di(meth)acrylate, trimethylolpropane tri(meth)acrylate, and dipentaerythritol hexa(meth)acrylate;

[0066] (Meth)acrylic acid, maleic acid, itaconic acid, citraconic acid, mesaconic acid, maleic anhydride, 4-methylcyclohexe-4-ene-1,2-dicarboxylic acid anhydride, bicyclo[2.2.2]octo-5-ene-2,3-dicarboxylic acid anhydride, 1,2,3,4,5,8,9,10-octahydronaphthalene-2,3-dicarboxylic acid anhydride, 2-octa-1,3-diketospiro[4.4]non-7-ene, bicyclo[ 2.2.1]Hepto-5-ene-2,3-dicarboxylic acid anhydride, maleopimaric acid, tetrahydrophthalic acid anhydride, methyl-bicyclo[2.2.1]hepto-5-ene-2,3-dicarboxylic acid anhydride, methyl-norbornene-5-ene-2,3-dicarboxylic acid anhydride, norbornne-5-ene-2,3-dicarboxylic acid anhydride, sulfonated styrene, vinylbenzenesulfonamide, and other polymerizable unsaturated monomers having acid groups; Vinyl carboxylates such as vinyl acetate, vinyl propionate, vinyl pivalate, and vinyl benzoate; Alkyl esters of crotonic acid, such as methyl crotonic acid and ethyl crotonic acid; Examples include, but are not limited to, dialkyl esters of unsaturated dibasic acids such as dimethyl maleate, di-n-butyl maleate, dimethyl fumarate, and dimethyl itaconate. These may be used individually or in combination of two or more.

[0067] Amine compounds (C7) are compounds having an amino group. In this specification, an amino group refers to an NH2 group or an NHR group (where R is an alkyl group or aryl group which may have a functional group).

[0068] Any known amine compound (C7) can be used without particular limitation, including methylenediamine, ethylenediamine, isophoronediamine, 3,9-dipropanamine-2,4,8,10-tetraoxaspirodoundecane, lysine, 2,2,4-trimethylhexamethylenediamine, hydrazine, piperazine, 2-hydroxyethylethylenediamine, di-2-hydroxyethylethylenediamine, di-2-hydroxyethylpropylenediamine, 2-hydroxypropylethylenediamine, di-2-hydroxypropylethylenediamine, poly(propylene glycol)diamine, poly(propylene glycol)triamine, poly(propylene glycol)tetraamine, 1,2-diaminopropane, 1,3-diaminopropane,

[0069] 1,4-diaminobutane, 1,5-diaminopentane, 1,6-diaminohexane, 1,7-diaminoheptane, 1,8-diaminooctane, 1,9-diaminononane, 1,10-diaminodecane, diethylenetriamine, dipropylenetriamine, triethylenetetramine, tripylenetetramine, tetraethylenepentamine, tetrapropylenepentamine, pentaethylenehexamine, nonaethylenedecamine, trimethylhexamethylenediamine, tetra(aminomethyl)methane, tetrakis(2-aminoethylaminomethyl)methane, 1,3-bis(2'-aminoethylamino)propane, triethylene-bis(trimethylene)hexamine, bis(3-aminoethyl)amine, bishexamethylenetriamine, 1,4-cyclohexanediamine, 4,4'-methylenebiscyclohexylamine, 4,4'-isopropylidenebiscyclohexylamine, norbornadiamine,

[0070] Amine compounds (C7-1) having multiple amino groups, such as bis(aminomethyl)cyclohexane, diaminodicyclohexylmethane, isophoronediamine, mensendiamine, bis(cyanoethyl)diethylenetriamine, 1,4-bis-(8-aminopropyl)-piperazine, piperazine-1,4-diazacycloheptane, 1-(2'-aminoethylpiperazine), 1-[2'-(2"-aminoethylamino)ethyl]piperazine, tricyclodecanediamine, and polyureamines which are reaction products of the above-mentioned polyamines and the above-mentioned isocyanate components,

[0071] Primary or secondary alkanolamines (C7-2) such as monoethanolamine, monoisopropanolamine, monobutanolamine, N-methylethanolamine, N-ethylethanolamine, N-methylpropanolamine, diethanolamine, and diisopropanolamine,

[0072] Examples include primary or secondary amines (C7-3) such as ethylamine, octylamine, laurylamine, myristylamine, stearylamine, oleylamine, diethylamine, dibutylamine, and distearylamine.

[0073] The amount of amine compound (C7) can be adjusted as appropriate depending on the purpose, but as an example, it is preferable that the amine value of the isocyanate reactive composition (Y) be 20 to 70 mg KOH / g, more preferably 25 to 50 mg KOH / g.

[0074] In this specification, the amine value refers to the number of milligrams of KOH equivalent to the amount of HCl required to neutralize 1 g of the sample. There are no particular restrictions, and it can be calculated using known methods. If the chemical structure of the amine compound (E7) and, if necessary, the average molecular weight are known, it can be calculated using the formula: (number of amino groups per molecule / average molecular weight) × 56.1 × 1000. If the chemical structure or average molecular weight of the amine compound is unknown, it can be measured according to known amine value measurement methods, such as JIS K7237-1995.

[0075] The epoxy compound (C8) is not particularly limited as long as it is a compound having an epoxy group in its molecule, for example, polyglycidyl ether type epoxy resins of aliphatic polyols such as ethylene glycol, propylene glycol, hexanediol, neopentyl glycol, trimethylolethane, trimethylolpropane, pentaerythritol, glycerin, diglycerin, sorbitol, spiroglycol, or hydrogenated bisphenol A; Bisphenol-type epoxy resins such as bisphenol A type epoxy resin, bisphenol F type epoxy resin, bisphenol S type epoxy resin, and bisphenol AD ​​type epoxy resin;

[0076] Aromatic epoxy resins such as phenol novolac resins and novolac-type epoxy resins, which are glycidyl eres of cresol novolac resins; Polyglycidyl ethers of polyols that are ethylene oxide or propylene oxide adducts of aromatic polyhydroxy compounds such as bisphenol A, bisphenol F, bisphenol S, and bisphenol AD; Polyglycidyl ether type epoxy resins of polyether polyols such as polyethylene glycol, polypropylene glycol, or polytetramethylene glycol; cyclic aliphatic type polyepoxy resins such as bis(3,4-epoxycyclohexylmethyl) adipate and 3,4-epoxycyclohexylmethyl-3',4'-epoxycyclohexyl carboxylate;

[0077] Polyglycidyl ester type epoxy resins of polycarboxylic acids such as propanetricarboxylic acid, butanetetracarboxylic acid, adipic acid, phthalic acid, terephthalic acid, or trimellitic acid; Bis-epoxy resins of hydrocarbon dienes such as butadiene, hexadiene, octadiene, dodecadiene, cyclooctadiene, α-pinene, or vinylcyclohexene; Epoxy resins of diene polymers such as polybutadiene or polyisoprene; Glycidylamine-type epoxy resins such as tetraglycidyldiaminodiphenylmethane, triglycidylparaaminophenol, tetraglycidylbisaminomethylcyclohexane, diglycidylaniline, and tetraglycidylmetaxylylenediamine; Examples include epoxy resins containing heterocyclic rings such as triazines and hydantoins. These can be used individually or in combination of two or more types.

[0078] The isocyanate-reactive compound (C) preferably contains a bifunctional compound. This improves the flexibility of the cured coating film and allows for a coating agent with superior adhesion to the substrate. The content of the bifunctional compound in the isocyanate-reactive compound (C) can be adjusted as appropriate, but as an example, it is 50% by mass or more, and 80% by mass or more. The entire amount of the isocyanate-reactive compound (C) may be a bifunctional compound.

[0079] The isocyanate-reactive compound (C) preferably contains one with a glass transition temperature (Tg) of 15°C or higher. This allows for a coating agent with suppressed blocking. The upper limit of the glass transition temperature of the isocyanate-reactive compound (C) can be adjusted as appropriate depending on the purpose, but one example is 80°C or lower.

[0080] The coating agent of the present invention may contain a solvent. Examples of solvents that can be used in the coating agent of the present invention include esters such as ethyl acetate, butyl acetate, and cellosolve acetate; ketones such as acetone, methyl ethyl ketone, isobutyl ketone, and cyclohexanone; ethers such as tetrahydrofuran and dioxane; aromatic hydrocarbons such as toluene and xylene; halogenated hydrocarbons such as methylene chloride and ethylene chloride; dimethyl sulfoxide and dimethyl sulfamide, and can be used individually or in combination of two or more.

[0081] The coating agent of the present invention may contain additives such as urethane catalysts, organic fillers, inorganic fillers, organic pigments, inorganic pigments, extender pigments, viscosity minerals, waxes, surfactants, stabilizers, flow regulators, leveling agents, rheology control agents, ultraviolet absorbers, antioxidants, and plasticizers. The urethane catalyst and pigments can be the same as those used in the two-component curing adhesive described later.

[0082] The method of applying the coating agent is not particularly limited, and conventionally known methods can be used. Examples of various coating methods include spray coating, direct gravure coating, gravure kiss reverse coating, offset guavia coating, flexo coating, offset coating, bar coating, roll kiss coating, forward rotation roll coating, reverse roll coating, slot die coating, vacuum die coating, (micro) chamber doctor coating, air doctor coating, blade coating, knife coating, spin coating, and dipping coating.

[0083] The amount of coating agent applied can be adjusted as appropriate depending on the application, but one example is 10 g / m². 2 More than 100g / m 2 The following applies:

[0084] The two-component curable coating agent of the present invention is preferably used in such a way that the ratio [NCO] / [isocyanate-reactive functional groups] between the number of moles of isocyanate groups [NCO] contained in the polyisocyanate composition (X) and the number of moles of functional groups that are reactive with isocyanate [isocyanate-reactive functional groups] contained in the isocyanate-reactive composition (Y) is 0.5 to 5.0, more preferably 1.0 to 3.0. This makes it possible to obtain appropriate curability regardless of the ambient humidity during coating.

[0085] <Two-part curing adhesive> The two-component curing adhesive of the present invention comprises the polyisocyanate composition (X) and the polyol composition (Y) described above.

[0086] When the adhesive of the present invention is used as a solvent-free adhesive, the viscosity of the polyisocyanate composition (X) is adjusted to a range suitable for the non-solvent laminating method. For example, the viscosity at 40°C is adjusted to be in the range of 100 to 50,000 mPas, more preferably 500 to 20,000 mPas. The viscosity of the polyisocyanate composition (X) can be adjusted, for example, by the structure of the polyurethane polyisocyanate (A1) (the polyol used). The viscosity of the polyisocyanate composition (X) is measured, for example, using a rotational viscometer with a cone-plate: 1° × diameter 50 mm, shear rate: 100 sec. -1 It can be measured at 40℃±1℃.

[0087] When the adhesive of the present invention is used as a solvent-type adhesive, the viscosity of the polyisocyanate composition (X) can be adjusted by diluting it with a solvent as described later.

[0088] (Isocyanate-reactive composition (Y)) The isocyanate-reactive composition (Y) contains an isocyanate-reactive compound (C). As the isocyanate-reactive compound (C), one or more types similar to those used in the coating agent described above can be used.

[0089] The isocyanate-reactive compound (C) preferably contains a bifunctional compound. This improves the flexibility of the cured coating film of the adhesive, resulting in an adhesive with superior adhesion and bonding to the substrate. The content of the bifunctional compound in the isocyanate-reactive compound (C) can be adjusted as appropriate, but examples include 50% by mass or more, and 80% by mass or more. The entire amount of the isocyanate-reactive compound (C) may be a bifunctional compound.

[0090] The isocyanate-reactive compound (C) preferably contains one with a glass transition temperature (Tg) of 40°C or lower. This allows for an adhesive with excellent adhesion. The lower limit of the glass transition temperature of the isocyanate-reactive compound (C) can be adjusted as appropriate depending on the purpose, but one example is -50°C or higher.

[0091] (Monool compound (D)) The isocyanate-reactive composition (Y) may contain a monool compound (D) having one alcoholic hydroxyl group. The main chain of the monool compound (D) is not particularly limited and examples include vinyl resins, acrylic resins, polyesters, epoxy resins, urethane resins, etc., all having one hydroxyl group. Aliphatic alcohols, alkylalkylene glycols, etc., can also be used. The main chain of the monool compound (D) may be linear or branched. The bonding position of the hydroxyl group is not particularly limited, but it is preferably located at the end of the molecular chain.

[0092] Specific examples of monool compounds (D) include methanol, ethanol, propanol, butanol, pentanol, hexanol, heptanol, octanol, nonanol, decanol, lauryl alcohol, myristyl alcohol, pentadecanol, cetyl alcohol, heptadecanol, stearyl alcohol, nonadecanol, other alkanols (C20-C50), oleyl alcohol, and aliphatic monools such as their isomers.

[0093] Cyclohexanol, methylcyclohexanol, 4-butylcyclohexanol, 4-pentylcyclohexanol, 4-hexylcyclohexanol, cyclodecanol, cyclododecanol, cyclopentadecanol, 4-isopropylcyclohexanol, 3,5,5-trimethylcyclohexanol, menthol, 2-norbornanol, borneol, 2-adamantanol, dicyclohexylmethanol, decatol, 2-cyclohexylcyclohexanol, 4-cyclohexylcyclohexanol, 4-(4-propylcyclohexyl)cyclohexanol, 4-(4-pentylcyclohex Sil-cyclohexanol, α-ambrinol, deoxycorticosterone, 11-dehydrocorticosterone, cholesterol, β-sitosterol, campesterol, stigmasterol, brassicasterol, lanosterol, ergosterol, β-cholestanol, testosterone, estrone, digitoxygenin, dehydroepiandrosterone, coprostanol, pregnenolone, epicholestanol, 7-dehydrocholesterol, estradiol benzoate, tigogenin, hecogenin, methandienone, cortisone acetate, stenolone, and alicyclic monools such as their isomers.

[0094] Aromatic aliphatic monools such as benzyl alcohol,

[0095] Examples include polyoxyalkylene monools obtained by ring-opening addition polymerization of alkylene oxides such as ethylene oxide, propylene oxide, butylene oxide, and tetrahydrofuran, using an alkyl compound containing one active hydrogen atom as an initiator.

[0096] When the adhesive of the present invention is provided in a solvent-free form, the viscosity of the isocyanate-reactive composition (Y) is adjusted to a range suitable for the non-solvent laminating method. For example, the viscosity at 40°C is adjusted to be in the range of 100 to 50,000 mPas, more preferably 100 to 20,000 mPas. The viscosity of the isocyanate-reactive composition (Y) can be adjusted by the skeleton of the isocyanate-reactive compound (C) or by plasticizers, as described later.

[0097] (Other components of the adhesive) The two-component curing adhesive of the present invention may contain components other than those described above. These other components may be included in either or both of the polyisocyanate composition (X) and the isocyanate reactive composition (Y), or they may be prepared separately and mixed with the polyisocyanate composition (X) and the isocyanate reactive composition (Y) immediately before application of the adhesive. Each component will be described below.

[0098] (catalyst) Examples of catalysts include metal catalysts, amine catalysts, aliphatic cyclic amide compounds, and quaternary ammonium salts.

[0099] Examples of metal catalysts include metal complex catalysts, inorganic metal catalysts, and organometallic catalysts. Examples of metal complex catalysts include acetylacetonate salts of metals selected from the group consisting of Fe (iron), Mn (manganese), Cu (copper), Zr (zirconium), Th (thorium), Ti (titanium), Al (aluminum), and Co (cobalt), such as iron acetylacetonate, manganese acetylacetonate, copper acetylacetonate, and zirconia acetylacetonate.

[0100] Examples of inorganic metal catalysts include those selected from Sn, Fe, Mn, Cu, Zr, Th, Ti, Al, Co, and the like.

[0101] Examples of organometallic catalysts include organozinc compounds such as zinc octoate, zinc neodecanoate, and zinc naphthenate; organotin compounds such as stanus diacetate, stanus dioctoate, stanus dioleate, stanus dilaurate, dibutyltin diacetate, dibutyltin dilaurate, dioctyltin dilaurate, dibutyltin oxide, and dibutyltin dichloride; organonickel compounds such as nickel octoate and nickel naphthenate; organocobalt compounds such as cobalt octoate and cobalt naphthenate; organobismuth compounds such as bismuth octoate, bismuth neodecanoate, and bismuth naphthenate; tetraisopropyloxytitanate, dibutyltitanium dichloride, tetrabutyltitanium trichloride, butoxytitanium trichloride; aliphatic diketones; aromatic diketones; and titanium compounds such as titanium chelate complexes with at least one alcohol having 2 to 10 carbon atoms as a ligand.

[0102] Amine-based catalysts include triethylenediamine, 2-methyltriethylenediamine, quinuclidine, 2-methylquinuclidine, N,N,N',N'-tetramethylethylenediamine, N,N,N',N'-tetramethylpropylenediamine, N,N,N',N",N"-pentamethyldiethylenetriamine, N,N,N',N",N"-pentamethyl-(3-aminopropyl)ethylenediamine, N,N,N',N",N"-pentamethyldipropylenetriamine, N,N,N',N'-tetramethylhexamethylenediamine, bis(2-dimethylaminoethyl) ether, dimethylethanolamine, dimethylisopropanolamine, dimethylaminoethoxyethanol, N,N-dimethyl-N'-(2-hydroxyethyl)ethylenediamine, N,N-dimethyl-N'-(2-hydroxyethyl)propanediamine, bis(dimethylaminopropyl)amine, bis(dimethylaminopropyl)isopropanediamine Lopanolamine, 3-Quinuclidinol, N,N,N',N'-Tetramethylguanidine, 1,3,5-Tris(N,N-dimethylaminopropyl)hexahydro-S-triazine, 1,8-Diazabicyclo[5.4.0]undecene-7, N-Methyl-N'-(2-dimethylaminoethyl)piperazine, N,N'-Dimethylpiperazine, Dimethylcyclohexylamine, N-Methylmorpholine, N-Ethylmorpholine, 1-Methylimidazole, 1 Examples include 2-dimethylimidazole, 1-isobutyl-2-methylimidazole, 1-dimethylaminopropylimidazole, N,N-dimethylhexanolamine, N-methyl-N'-(2-hydroxyethyl)piperazine, 1-(2-hydroxyethyl)imidazole, 1-(2-hydroxypropyl)imidazole, 1-(2-hydroxyethyl)-2-methylimidazole, and 1-(2-hydroxypropyl)-2-methylimidazole.

[0103] Examples of aliphatic cyclic amide compounds include δ-valerolactam, ε-caprolactam, ω-enanthollactam, η-capryllactam, and β-propiolactam. Among these, ε-caprolactam is most effective in promoting curing.

[0104] Examples of quaternary ammonium salts include alkylammonium, aromatic ammonium, hydroxy salts, alkylates, and halide salts. Examples include, but are not limited to, tetramethylammonium hydroxide, tetraethylammonium hydroxide, tetrapropylammonium hydroxide, tetrabutylammonium hydroxide, benzyltrimethylammonium hydroxide, tetrabutylammonium fluoride, tetrabutylammonium chloride, tetrabutylammonium bromide, tetrabutylammonium iodide, benzyltriethylammonium chloride, and hexadecyltrimethylammonium bromide.

[0105] (Coupling agent) Examples of coupling agents include silane coupling agents, titanate-based coupling agents, and aluminum-based coupling agents.

[0106] Examples of silane coupling agents include aminosilanes such as γ-aminopropyltriethoxysilane, γ-aminopropyltrimethoxysilane, N-β(aminoethyl)-γ-aminopropyltrimethoxysilane, N-β(aminoethyl)-γ-aminopropyltrimethyldimethoxysilane, N-phenyl-γ-aminopropyltrimethoxysilane, bis[3-(trimethoxysilyl)propyl]amine, and bis[3-(triethoxysilyl)propyl]amine; epoxysilanes such as β-(3,4-epoxycyclohexyl)ethyltrimethoxysilane, γ-glycidoxypropyltrimethoxysilane, and γ-glycidoxypropyltriethoxysilane; vinylsilanes such as vinyltris(β-methoxyethoxy)silane, vinyltriethoxysilane, vinyltrimethoxysilane, and γ-methacryloxypropyltrimethoxysilane; and hexamethyldisilazane and γ-mercaptopropyltrimethoxysilane.

[0107] Examples of titanate-based coupling agents include tetraisopropoxytitanium, tetra-n-butoxytitanium, butyl titanate dimer, tetrastearyl titanate, titanium acetylacetonate, titanium lactate, tetraoctylene glycol titanate, titanium lactate, and tetrastearoxititanium.

[0108] Examples of aluminum-based coupling agents include acetalkoxyaluminum diisopropylate.

[0109] (Pigment) There are no particular restrictions on the pigments used, and examples include organic and inorganic pigments such as extender pigments, white pigments, black pigments, gray pigments, red pigments, brown pigments, green pigments, blue pigments, metal powder pigments, luminescent pigments, pearlescent pigments, and even plastic pigments, as listed in the 1970 edition of the Paint Raw Materials Handbook (compiled by the Japan Paint Manufacturers Association).

[0110] Examples of extender pigments include precipitated barium sulfate, granite, precipitated calcium carbonate, calcium bicarbonate, limestone, alumina white, silica, hydrated fine silica (white carbon), ultrafine anhydrous silica (aerosil), silica sand, talc, precipitated magnesium carbonate, bentonite, clay, kaolin, and yellow ochre.

[0111] Specific examples of organic pigments include various insoluble azo pigments such as Benzidine Yellow, Hansa Yellow, and Laked 4R; soluble azo pigments such as Laked C, Carmine 6B, and Bordeaux 10; various (copper) phthalocyanine pigments such as phthalocyanine blue and phthalocyanine green; various chlorinated dye lakes such as rhodamine lake and methyl violet lake; various mordant dyes such as quinoline lake and fast sky blue; various vat dyes such as anthraquinone pigments, thioindigo pigments, and perinone pigments; various quinacridone pigments such as Syncasia Red B; various dioxazine pigments such as dioxazine violet; various condensed azo pigments such as chromophthal; and aniline black.

[0112] Inorganic pigments include various chromates such as lead yellow, zinc chromate, and molybdate orange; various ferrocyanide compounds such as Prussian blue; various metal oxides such as titanium dioxide, zinc oxide, mapo yellow, iron oxide, red iron oxide, chrome green oxide, and zirconium oxide; various sulfides or selenides such as cadmium yellow, cadmium red, and mercury sulfide; various sulfates such as barium sulfate and lead sulfate; various silicates such as calcium silicate and ultramarine; various carbonates such as calcium carbonate and magnesium carbonate; various phosphates such as cobalt violet and manganese purple; various metal powder pigments such as aluminum powder, gold powder, silver powder, copper powder, bronze powder, and brass powder; metal flake pigments and mica flake pigments; metallic pigments and pearl pigments such as mica flake pigments coated with metal oxides and mica-like iron oxide pigments; graphite, carbon black, etc.

[0113] Examples of plastic pigments include "Grandeur PP-1000" and "PP-2000S" manufactured by DIC Corporation.

[0114] The pigments used can be selected appropriately depending on the purpose, but for example, inorganic oxides such as titanium dioxide and zinc oxide are preferred as white pigments because they have excellent durability, weather resistance, and design properties, and carbon black is preferred as a black pigment.

[0115] The amount of pigment added is, for example, 1 to 400 parts by mass per 100 parts by mass of the total non-volatile content of the polyol composition (X) and the polyisocyanate composition (Y), and is more preferably 10 to 300 parts by mass to improve adhesion and blocking resistance.

[0116] (Plasticizer) Examples of plasticizers include phthalate-based plasticizers, fatty acid-based plasticizers, aromatic polycarboxylic acid-based plasticizers, phosphate-based plasticizers, polyol-based plasticizers, epoxy-based plasticizers, polyester-based plasticizers, and carbonate-based plasticizers.

[0117] Examples of phthalate-based plasticizers include phthalate ester plasticizers such as dimethyl phthalate, diethyl phthalate, dibutyl phthalate, diisobutyl phthalate, dihexyl phthalate, diheptyl phthalate, di-(2-ethylhexyl) phthalate, di-n-octyl phthalate, dinonyl phthalate, diisononyl phthalate, didecyl phthalate, diisodecyl phthalate, ditridecyl phthalate, diundecyl phthalate, dilauryl phthalate, distearyl phthalate, diphenyl phthalate, dibenzyl phthalate, butylbenzyl phthalate, dicyclohexyl phthalate, octyldecyl phthalate, dimethyl isophthalate, di-(2-ethylhexyl) isophthalate, and diisooctyl isophthalate, as well as tetrahydrophthalate ester plasticizers such as di-(2-ethylhexyl)tetrahydrophthalate, di-n-octyltetrahydrophthalate, and diisodecyltetrahydrophthalate.

[0118] Examples of fatty acid-based plasticizers include adipic acid-based plasticizers such as di-n-butyl adipate, di-(2-ethylhexyl) adipate, diisodecyl adipate, diisononyl adipate, di(C6-C10 alkyl) adipate, and dibutyldiglycol adipate; azelaic acid-based plasticizers such as di-n-hexyl azelate, di-(2-ethylhexyl) azelate, and diisooctyl azelate; and di-n-butyl sebacate, di-(2 Sebacate-based plasticizers such as -ethylhexyl) sebacate and diisononyl sebacate; maleic acid-based plasticizers such as dimethyl maleate, diethyl maleate, di-n-butyl maleate, and di-(2-ethylhexyl) maleate; fumaric acid-based plasticizers such as di-n-butyl fumarate and di-(2-ethylhexyl) fumarate; monomethyl itaconate, monobutyl itaconate, dimethyl itaconate, diethyl itaconate, dibutyrate Examples of plasticizers include itaconic acid-based plasticizers such as ruitaconate and di-(2-ethylhexyl)itaconate; stearic acid-based plasticizers such as n-butyl stearate, glycerin monostearate, and diethylene glycol distearate; oleic acid-based plasticizers such as butyl oleate, glyceryl monooleate, and diethylene glycol monooleate; citrate-based plasticizers such as triethyl citrate, tri-n-butyl citrate, acetyl triethyl citrate, acetyl tributyl citrate, and acetyl tri-(2-ethylhexyl) citrate; ricinoleic acid-based plasticizers such as methylacetyl ricinoleate, butylacetyl ricinoleate, glyceryl monoricinoleate, and diethylene glycol monoricinoleate; and other fatty acid-based plasticizers such as diethylene glycol monolaurate, diethylene glycol diperargonate, and pentaerythritol fatty acid esters.

[0119] Examples of aromatic polycarboxylic acid plasticizers include trimellitic acid plasticizers such as tri-n-hexyl trimellitate, tri-(2-ethylhexyl) trimellitate, tri-n-octyl trimellitate, triisooctyl trimellitate, triisononyl trimellitate, tridecyl trimellitate, and triisodecyl trimellitate, as well as pyromellitic acid plasticizers such as tetra-(2-ethylhexyl) pyromelitate and tetra-n-octyl pyromelitate.

[0120] Examples of phosphate-based plasticizers include triethyl phosphate, tributyl phosphate, tri-(2-ethylhexyl) phosphate, tributoxyethyl phosphate, triphenyl phosphate, octyldiphenyl phosphate, cresyldiphenyl phosphate, cresylphenyl phosphate, tricresyl phosphate, trixylenyl phosphate, tris(chloroethyl) phosphate, tris(chloropropyl) phosphate, tris(dichloropropyl) phosphate, and tris(isopropylphenyl) phosphate.

[0121] Examples of polyol-based plasticizers include glycol-based plasticizers such as diethylene glycol dibenzoate, dipropylene glycol dibenzoate, triethylene glycol dibenzoate, triethylene glycol di-(2-ethyl butyrate), triethylene glycol di-(2-ethylhexoate), and dibutylmethylene bisthioglycolate, as well as glycerin-based plasticizers such as glycerol monoacetate, glycerol triacetate, and glycerol tributyrate.

[0122] Examples of epoxy plasticizers include epoxidized soybean oil, epoxybutyl stearate, di-2-ethylhexyl epoxyhexahydrophthalate, diisodecyl epoxyhexahydrophthalate, epoxy triglycerides, octyl epoxidized oleate, and decyl epoxidized oleate.

[0123] Examples of polyester-based plasticizers include adipic acid-based polyesters, sebaciate-based polyesters, and phthalate-based polyesters.

[0124] Examples of carbonate-based plasticizers include propylene carbonate and ethylene carbonate.

[0125] Other plasticizers include partially hydrogenated terphenyl, adhesive plasticizers, and polymerizable plasticizers such as diallyl phthalate, acrylic monomers, and oligomers. These plasticizers can be used individually or in combination of two or more.

[0126] (acid anhydride) Examples of acid anhydrides include cyclic aliphatic acid anhydrides, aromatic acid anhydrides, and unsaturated carboxylic acid anhydrides, and one or more can be used in combination. More specifically, examples include maleic anhydride, phthalic anhydride, trimellitic anhydride, pyromellitic anhydride, benzophenonetetracarboxylic anhydride, dodecenyl succinic anhydride, polyadipic anhydride, polyazelaic anhydride, polysebacic anhydride, poly(ethyloctadecanediic acid) anhydride, poly(phenylhexadecanedioic acid) anhydride, tetrahydrophthalic anhydride, methyltetrahydrophthalic anhydride, methylhexahydrophthalic anhydride, hexahydrophthalic anhydride, methylhymic anhydride, and trialkyltetrahydrophthalic acid Examples include anhydrides, methylcyclohexenedicarboxylic acid anhydride, methylcyclohexenetetracarboxylic acid anhydride, ethylene glycol bistrimellitate dianhydride, hetic acid anhydride, nadic acid anhydride, methylnadic acid anhydride, 5-(2,5-dioxotetrahydro-3-furanyl)-3-methyl-3-cyclohexane-1,2-dicarboxylic acid anhydride, 3,4-dicarboxy-1,2,3,4-tetrahydro-1-naphthalenesuccinic acid dianhydride, 1-methyl-dicarboxy-1,2,3,4-tetrahydro-1-naphthalenesuccinic acid dianhydride, etc.

[0127] As the acid anhydride, the above-mentioned compounds modified with glycol may be used. Examples of glycols that can be used for modification include alkylene glycols such as ethylene glycol, propylene glycol, and neopentyl glycol; and polyether glycols such as polyethylene glycol, polypropylene glycol, and butyltetramethylene ether glycol. Furthermore, copolymer polyether glycols of two or more of these glycols and / or polyether glycols can also be used.

[0128] Alternatively, as the acid anhydride, a homopolymer or copolymer of a compound having a polymerizable unsaturated group, such as maleic anhydride, from among the compounds mentioned above may be used. Compounds that can copolymerize with a compound having an acid anhydride group and a polymerizable unsaturated group include α-olefins such as ethylene, propylene, 1,3-butadiene, and cyclopentylethylene; vinyl compounds having an aromatic ring such as styrene, 1-ethynyl-4-methylbenzene, divinylbenzene, 1-ethynyl-4-methylethylbenzene, benzonitrile, acrylonitrile, p-tert-butylstyrene, 4-vinylbiphenyl, 4-ethynylbenzyl alcohol, 2-ethynylnaphthalene, and phenanthrene-9-ethynyl; and fluoroolefins such as vinylidene fluoride, tetrafluoroethylene, hexafluoropropylene, and chlorotrifluoroethylene. These can be used individually or in combination of two or more. It is preferable to use styrene and p-tert-butylstyrene, which are vinyl compounds having an aromatic ring.

[0129] (Phosphate compounds) Examples of phosphate compounds include phosphoric acid, pyrophosphate, triphosphate, methyl acid phosphate, ethyl acid phosphate, butyl acid phosphate, dibutyl phosphate, 2-ethylhexyl acid phosphate, bis(2-ethylhexyl) phosphate, isododecyl acid phosphate, butoxyethyl acid phosphate, oleyl acid phosphate, tetracosyl acid phosphate, 2-hydroxyethyl methacrylate acid phosphate, and polyoxyethylene alkyl ether phosphate. In the adhesive of the present invention, since the polyisocyanate composition (X) contains a phosphate compound, it is not necessary to add a phosphate compound when forming the adhesive.

[0130] (Form of adhesive) The two-component curing adhesive of the present invention may be in either a solvent-type or solvent-free form. In this specification, a "solvent-type" adhesive refers to a form used in a method in which the adhesive is applied to a substrate, heated in an oven or the like to volatilize the organic solvent in the coating film, and then bonded to another substrate, a method known as the dry lamination method. Either one or both of the polyisocyanate composition (X) and the isocyanate reactive composition (Y) contain an organic solvent capable of dissolving (diluting) the components of the polyisocyanate composition (X) and isocyanate reactive composition (Y) used in the present invention.

[0131] Examples of organic solvents include esters such as ethyl acetate, butyl acetate, and cellosolve acetate; ketones such as acetone, methyl ethyl ketone, isobutyl ketone, and cyclohexanone; ethers such as tetrahydrofuran and dioxane; aromatic hydrocarbons such as toluene and xylene; halogenated hydrocarbons such as methylene chloride and ethylene chloride; dimethyl sulfoxide; and dimethyl sulfamide. The organic solvent used as a reaction medium in the production of the components of the polyisocyanate composition (X) and the isocyanate reactive composition (Y) may also be used as a diluent during painting.

[0132] In this specification, "solvent-free" adhesive refers to an adhesive used in a method of bonding with another substrate without a step of heating in an oven or the like to volatilize the solvent after coating the substrate with the adhesive, in the so-called non-solvent laminating method. The polyisocyanate composition (X) and isocyanate reactive composition (Y) substantially do not contain esters such as ethyl acetate, butyl acetate, and cellosolve acetate, ketones such as acetone, methyl ethyl ketone, isobutyl ketone, and cyclohexanone, ethers such as tetrahydrofuran and dioxane, aromatic hydrocarbons such as toluene and xylene, halogenated hydrocarbons such as methylene chloride and ethylene chloride, and highly soluble organic solvents such as dimethyl sulfoxide and dimethyl sulfamide, especially ethyl acetate or methyl ethyl ketone. If trace amounts of organic solvent remain in the polyisocyanate composition (X) or isocyanate reactive composition (Y) due to incomplete removal of components or organic solvents used as reaction media during the manufacturing of their raw materials, it is considered that the composition is substantially free of organic solvents. Furthermore, if the isocyanate reactive composition (Y) contains low molecular weight alcohol, the low molecular weight alcohol reacts with the polyisocyanate composition (X) to become part of the coating film, and therefore does not need to be volatilized after coating. Consequently, this form is also treated as a solvent-free adhesive, and the low molecular weight alcohol is not considered an organic solvent.

[0133] The two-component curing adhesive of the present invention is preferably formulated so that the ratio [NCO] / [isocyanate-reactive functional groups] between the number of moles of isocyanate groups [NCO] contained in the polyisocyanate composition (X) and the number of moles of functional groups that are reactive with isocyanate [isocyanate-reactive functional groups] contained in the isocyanate-reactive composition (Y) is 0.5 to 5.0, more preferably 1.0 to 3.0. This makes it possible to obtain appropriate curing properties regardless of the ambient humidity during coating.

[0134] <Laminate> The laminate of the present invention can be obtained, for example, by a two-component mixing step in which a polyisocyanate composition (X) and an isocyanate-reactive composition (Y) are mixed in advance, applied to a first substrate, then laminated onto the coated surface with a second substrate, and the adhesive layer is cured; or by a two-component fractional coating step in which the polyisocyanate composition (X) and the isocyanate-reactive composition (Y) are applied separately to a first substrate and a second substrate, then the coated surfaces are brought into contact and pressed together to laminate the first substrate and the second substrate, and the adhesive layer is cured. There are no particular restrictions on the film used, and a film can be appropriately selected according to the application.

[0135] For example, for food packaging, examples include polyethylene terephthalate (PET) film, polystyrene film, polyamide film, polyacrylonitrile film, polyethylene film (LLDPE: low-density polyethylene film, HDPE: high-density polyethylene film, MDOPE: uniaxially oriented polyethylene film, OPE: biaxially oriented polyethylene film), polypropylene film (CPP: unoriented polypropylene film, OPP: biaxially oriented polypropylene film), ethylene vinyl alcohol copolymer, and gas barrier heat-seal films such as polyolefin films, polyvinyl alcohol films, and ethylene-vinyl alcohol copolymer films, which have an olefin-based heat-sealable resin layer on one or both sides of a gas barrier resin such as polyvinyl alcohol.

[0136] Furthermore, it is also preferable to use biomass films, biodegradable films, or recycled plastic films formed from materials containing biomass-derived components, biodegradable components, or recycled components. Biomass films, biodegradable films, and recycled plastic films are sold by various companies. In addition, films certified in each country can be used, such as film sheets listed in the biomass certified product list of the Japan Organic Resources Association, films listed in the Eco Mark certified product list of the Japan Environment Association, and films bearing the symbol mark set by the Japan Bioplastics Association.

[0137] (Biomass film) A well-known example of a biomass film is one that uses biomass-derived ethylene glycol as a raw material. Biomass-derived ethylene glycol is made from ethanol (biomass ethanol) produced from biomass. For example, biomass-derived ethylene glycol can be obtained by conventionally known methods, such as a method that produces ethylene glycol via ethylene oxide from biomass ethanol. Alternatively, commercially available biomass ethylene glycol may be used; for example, the biomass ethylene glycol commercially available from India Glycol can be suitably used.

[0138] For example, as an alternative to conventional polyethylene terephthalate films using petroleum-based raw materials, films containing biomass polyesters, biomass polyethylene terephthalate, etc., which use biomass-derived ethylene glycol as the diol unit and fossil fuel-derived dicarboxylic acid as the dicarboxylic acid unit are known.

[0139] The dicarboxylic acid units in biomass polyesters use dicarboxylic acids derived from fossil fuels. Aromatic dicarboxylic acids, aliphatic dicarboxylic acids, and their derivatives can be used without restriction as dicarboxylic acids. Furthermore, in addition to the diol and dicarboxylic acid components mentioned above, a copolymerized polyester may also be obtained by adding a copolymerizing component as a third component, such as a bifunctional oxycarboxylic acid or at least one polyfunctional compound selected from the group consisting of trifunctional or more polyhydric alcohols, trifunctional or more polyhydric acids and / or their anhydrides, and trifunctional or more oxycarboxylic acids, in order to form a crosslinked structure.

[0140] Furthermore, as an alternative to conventional polyolefin films using petroleum-based raw materials, biomass polyolefin films such as biomass polyethylene films and biomass polyethylene-polypropylene films, which contain polyethylene resins made from biomass-derived ethylene glycol, are also known. The polyethylene resin is not particularly limited except for the use of biomass-derived ethylene glycol as part of the raw materials. Examples include ethylene homopolymers and copolymers of ethylene and α-olefins with ethylene as the main component (ethylene-α-olefin copolymers containing 90% by mass or more of ethylene units). These can be used individually or in combination of two or more types.

[0141] The α-olefin constituting the copolymer of ethylene and α-olefin is not particularly limited, and examples include α-olefins having 4 to 8 carbon atoms, such as 1-butene, 4-methyl-1-pentene, 1-hexene, and 1-octene. Known polyethylene resins such as low-density polyethylene resin, medium-density polyethylene resin, and linear low-density polyethylene resin can be used. Among these, linear low-density polyethylene resin (LLDPE) (a copolymer of ethylene and 1-hexene, or a copolymer of ethylene and 1-octene) is preferred from the viewpoint of making it even less likely for damage such as punctures or tears to occur when the films rub against each other, and has a density of 0.910 to 0.925 g / cm³. 3 A linear low-density polyethylene resin is more preferable.

[0142] Biomass films are also available that use biomass raw materials classified by the biomass plasticity level specified in ISO 16620 or ASTM D6866. Radioactive carbon-14C exists in the atmosphere at a rate of 1 in 10¹² atoms, and this rate does not change even in atmospheric carbon dioxide. Therefore, this rate does not change in plants that fix carbon dioxide through photosynthesis. For this reason, the carbon in plant-derived resins contains radioactive carbon-14C. In contrast, the carbon in fossil fuel-derived resins contains almost no radioactive carbon-14C. Therefore, by measuring the concentration of radioactive carbon-14C in the resin using an accelerator mass spectrometer, the proportion of plant-derived resin in the resin, i.e., the biomass plasticity level, can be determined.

[0143] Examples of plant-derived low-density polyethylene (PPE) biomass plastics with a biomass plastic content of 80% or more, preferably 90% or more, as defined by ISO 16620 or ASTM D6866, include Braskem's product names "SBC818," "SPB608," "SBF0323HC," "STN7006," "SEB853," and "SPB681," and films made from these materials can be suitably used.

[0144] Films and sheets containing biomass raw materials such as starch and polylactic acid are also known. These can be selected and used as appropriate depending on the application.

[0145] The biomass film may be a laminate formed by stacking multiple biomass films, or it may be a laminate formed by combining a conventional petroleum-based film with a biomass film. Furthermore, these biomass films may be unstretched or stretched films, and their manufacturing method is not limited.

[0146] (Biodegradable film) Well-known biodegradable films include those made from readily available biodegradable resins. Examples include polycaprolactone, polyvinyl alcohol, polyamide, cellulose ester, lactic acid-based polyester resin, aliphatic polyester resin, or aliphatic aromatic polyester resin. These biodegradable resins may be used individually or in combination of two or more. Among these, aliphatic polyester resin or aliphatic aromatic polyester resin is preferred. Aliphatic polyester resins include aliphatic polyesters obtained by polycondensation reactions of aliphatic diols and aliphatic dicarboxylic acids. Examples of aliphatic diols include ethylene glycol, 1,3-propanediol, 1,4-butanediol, 1,5-pentanediol, 1,6-hexanediol, 1,4-cyclohexanediol, and 1,4-cyclohexanedimethanol. These may be used individually or in mixtures. Among these, 1,4-butanediol is preferred. Examples of aliphatic dicarboxylic acids include oxalic acid, succinic acid, glutanoic acid, adipic acid, sebacic acid, suberic acid, and dodecanedioic acid, and their derivatives, such as acid anhydrides, may also be used. Among these, succinic acid or succinic anhydride, or mixtures of these with adipic acid, are preferred. Specifically, examples include polybutylene succinate (PBS) obtained from 1,4-butanediol and succinic acid (e.g., BioPBS from PPT MCC Biochem), and polybutylene succinate adipate (PBSA) obtained by copolymerizing PBS with adipic acid.

[0147] Aliphatic aromatic polyester resins include copolymers containing aliphatic dicarboxylic acid units, aromatic dicarboxylic acid units, and linear aliphatic and / or alicyclic diol units. The diol component that provides the diol units usually has 2 to 10 carbon atoms, and examples include ethylene glycol, 1,3-propanediol, 1,4-butanediol, and 1,4-cyclohexanedimethanol. Among these, diols with 2 to 4 carbon atoms are preferred, with ethylene glycol and 1,4-butanediol being preferred, and 1,4-butanediol being even more preferred. The dicarboxylic acid component that provides the dicarboxylic acid units usually has 2 to 10 carbon atoms, and examples include succinic acid, adipic acid, suberic acid, sebacic acid, and dodecanedioic acid. Among these, succinic acid or adipic acid are preferred. Examples of aromatic dicarboxylic acid components that provide aromatic dicarboxylic acid units include terephthalic acid, isophthalic acid, and naphthalenedicarboxylic acid. Among these, terephthalic acid and isophthalic acid are preferred, with terephthalic acid being even more preferred. Specifically, examples include PBAT (for example, Ecoflex manufactured by B.A.S.F.), which is a copolymer of 1,4-butanediol, adipic acid, and terephthalic acid.

[0148] Other examples include aliphatic polyester copolymers obtained from hydroxyalkanoic acid and polycarboxylic acid, such as poly(3-hydroxyalkanoate) (in particular, poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) (PHBH) (e.g., Aonirex manufactured by Kaneka Corporation) and polylactic acid (PLA) (e.g., REVODE manufactured by Kaisei Biomaterials Co., Ltd., and Ingeo manufactured by NatureWorks Inc.).

[0149] The biodegradable film may be a laminate formed by stacking multiple biodegradable films, or a laminate formed by combining a conventional petroleum-based film with a biodegradable film. Furthermore, these biodegradable films may be unstretched or stretched films, and their manufacturing method is not limited.

[0150] The film may be stretched. A common stretching method involves melting and extruding the resin into a sheet using methods such as extrusion film formation, followed by simultaneous biaxial stretching or sequential biaxial stretching. In the case of sequential biaxial stretching, it is common to first perform longitudinal stretching, followed by transverse stretching. Specifically, a method combining longitudinal stretching using the speed difference between rolls and transverse stretching using a tenter is frequently used.

[0151] Various surface treatments, such as flame treatment or corona discharge treatment, may be applied to the film surface as needed to ensure that an adhesive layer free from defects such as film breakage or repulsion is formed.

[0152] Alternatively, a film containing a vapor-deposited layer of metal such as aluminum, a metal oxide such as silica or alumina, or a barrier film containing a gas barrier layer such as polyvinyl alcohol, ethylene-vinyl alcohol copolymer, or vinylidene chloride may be used in combination. By using such films, a laminate can be made that has barrier properties against water vapor, oxygen, alcohol, inert gases, volatile organic compounds (fragrances), etc.

[0153] As for the paper, any known paper substrate can be used without particular limitation. Specifically, it is manufactured using known papermaking natural fibers such as wood pulp and papermaking machines, but the papermaking conditions are not particularly specified. Examples of natural fibers for papermaking include wood pulp such as softwood pulp and hardwood pulp, non-wood pulp such as Manila hemp pulp, sisal hemp pulp, and flax pulp, and pulps that have been chemically modified. As for the type of pulp, chemical pulps produced by sulfate pulping, acidic, neutral, and alkaline sulfite pulping, soda salt pulping, etc., as well as gland pulp, chemigland pulp, thermomechanical pulp, etc. can be used. In addition, various commercially available fine papers, coated papers, backing papers, impregnated papers, cardboard, and paperboard can also be used.

[0154] More specifically, the configuration of the laminate is as follows: (1) Substrate 1 / Adhesive layer 1 / Sealant film (2) Substrate 1 / Adhesive layer 1 / Metal vapor-deposited unstretched film (3) Substrate 1 / Adhesive layer 1 / Metal vapor-deposited stretched film (4) Transparent vapor-deposited stretched film / adhesive layer 1 / sealant film (5) Substrate 1 / Adhesive layer 1 / Substrate 2 / Adhesive layer 2 / Sealant film (6) Substrate 1 / Adhesive layer 1 / Metal vapor-deposited stretched film / Adhesive layer 2 / Sealant film (7) Substrate 1 / Adhesive layer 1 / Transparent vapor-deposited stretched film / Adhesive layer 2 / Sealant film (8) Substrate 1 / Adhesive layer 1 / Metal layer / Adhesive layer 2 / Sealant film (9) Substrate 1 / Adhesive layer 1 / Substrate 2 / Adhesive layer 2 / Metal layer / Adhesive layer 3 / Sealant film (10) Substrate 1 / Adhesive layer 1 / Metal layer / Adhesive layer 2 / Substrate 2 / Adhesive layer 3 / Sealant film Examples include, but are not limited to, those listed above.

[0155] Examples of substrates 1 used in composition (1) include MDOPE film, OPE film, OPP film, PET film, nylon film, and paper. Alternatively, a substrate 1 coated with a coating for purposes such as improving gas barrier properties or ink receptivity when providing the printing layer described later may be used. Commercially available coated substrate films 1 include K-OPP film, K-PET film, and K-nylon film. The adhesive layer 1 is a cured coating of the adhesive of the present invention. Examples of sealant films include CPP film, LLDPE film, easy-open heat-seal film, and gas-barrier heat-seal film. The printing layer may be provided on the side of the substrate 1 facing the adhesive layer 1 (or, if a coated substrate film 1 is used, on the side of the coating layer facing the adhesive layer 1) or on the side opposite to the adhesive layer 1. The printing layer is formed using various printing inks such as gravure ink, flexographic ink, offset ink, stencil ink, and inkjet ink, using general printing methods conventionally used for printing on polymer films and paper.

[0156] Examples of substrate 1 used in configurations (2) and (3) include MDOPE film, OPE film, OPP film, PET film, paper, etc. The adhesive layer 1 is a cured coating of the adhesive of the present invention. Examples of unstretched metal-deposited films include CPP film, LLDPE film, VM-CPP film, VM-LLDPE film, etc., which are gas barrier heat seal films with metal deposition of aluminum or the like. Examples of stretched metal-deposited films include VM-MDOPE film, VM-OPE film, VM-OPP film, etc., which are MDOPE film, OPE film, or OPP film with metal deposition of aluminum or the like. A printed layer may be provided on any surface of the substrate 1 in the same manner as in configuration (1).

[0157] Examples of transparent vapor-deposited stretched films used in configuration (4) include MDOPE films, OPE films, OPP films, PET films, nylon films, etc., on which silica or alumina vapor deposition has been applied. Films with a coating applied to the vapor-deposited layer may also be used for purposes such as protecting the inorganic vapor-deposited layer of silica or alumina. The adhesive layer 1 is a cured coating film of the adhesive of the present invention. The sealant film is the same as that of configuration (1). A printed layer may be provided on the side of the transparent vapor-deposited stretched film facing the adhesive layer 1 (or, if a film with a coating applied to the inorganic vapor-deposited layer is used, on the side of the coating layer facing the adhesive layer 1). The method for forming the printed layer is the same as in configuration (1).

[0158] Examples of substrate 1 used in configuration (5) include PET film and paper. Examples of substrate 2 include nylon film. At least one of adhesive layer 1 and adhesive layer 2 is a cured coating film of the adhesive of the present invention. Examples of sealant film are the same as those in configuration (1). A printed layer may be provided on any surface of substrate 1 in the same manner as in configuration (1).

[0159] The base material 1 of configuration (6) is the same as that of configurations (2) and (3). Examples of metal vapor-deposited stretched films include VM-MDOPE film, VM-OPE film, VM-OPP film, and VM-PET film, which are obtained by vapor deposition of aluminum or other metal onto MDOPE film, OPE film, OPP film, or PET film. At least one of adhesive layer 1 and adhesive layer 2 is a cured coating film of the adhesive of the present invention. Examples of sealant films are the same as those of configuration (1). A printed layer may be provided on any surface of the base material 1 in the same manner as in configuration (1).

[0160] Examples of the substrate 1 in configuration (7) include PET film and paper. Examples of the transparent vapor-deposited stretched film include those the same as in configuration (4). At least one of the adhesive layers 1 and 2 is a cured coating film of the adhesive of the present invention. Examples of the sealant film include those the same as in configuration (1). A printed layer may be provided on any surface of the substrate 1 in the same manner as in configuration (1).

[0161] Examples of the base material 1 in configuration (8) include PET film and paper. Examples of the metal layer include aluminum foil. At least one of the adhesive layers 1 and 2 is a cured coating film of the adhesive of the present invention. Examples of the sealant film are the same as those in configuration (1). A printed layer may be provided on any surface of the base material 1 in the same manner as in configuration (1).

[0162] Examples of base material 1 in configurations (9) and (10) include PET film and paper. Examples of base material 2 include nylon film. Examples of metal layers include aluminum foil. At least one layer of adhesive layers 1, 2, and 3 is a cured coating of the adhesive of the present invention. Examples of sealant films are the same as those in configuration (1). A printed layer may be provided on any surface of base material 1 in the same manner as in configuration (1).

[0163] The laminate of the present invention may further include other films or substrates in addition to the above-described configurations (1) to (10). As other substrates, in addition to the stretched film, unstretched film, and transparent vapor-deposited film described above, porous substrates such as paper, wood, and leather, as described later, may also be used. The adhesive used when bonding the other substrates may be the adhesive of the present invention or not.

[0164] The "other layer" may contain known additives and stabilizers, such as antistatic agents, easy-adhesion coating agents, plasticizers, lubricants, and antioxidants. The "other layer" may also have its surface pretreated by corona treatment, plasma treatment, ozone treatment, chemical treatment, solvent treatment, etc., to improve adhesion when laminated with other materials.

[0165] The laminate of the present invention can be suitably used in a variety of applications, such as packaging materials for food, pharmaceuticals, and household goods; lids; paper tableware such as paper straws, paper napkins, paper spoons, paper plates, and paper cups; protective wall materials; roofing materials; solar panel materials; battery packaging materials; window materials; outdoor flooring materials; lighting protection materials; automotive components; signs; stickers and other outdoor industrial applications; decorative sheets used in injection molding simultaneous decoration methods; and packaging materials for laundry detergents, kitchen detergents, bath detergents, bath soaps, liquid shampoos, liquid conditioners, and the like.

[0166] <Packaging material> The laminate of the present invention can be used as a multilayer packaging material for the purpose of protecting food, pharmaceuticals, and other products. When used as a multilayer packaging material, the layer configuration may be changed depending on the contents, usage environment, and usage form. Furthermore, the packaging of the present invention may be appropriately provided with an easy-open treatment or resealing means.

[0167] As an example of a specific embodiment of the packaging material of the present invention, a packaging material made by forming a bag from a laminate having a sealant film, such as the laminate configuration examples (1), (4) to (10) described above, can be mentioned. The laminate is folded or overlapped so that the inner layers (sealant film surfaces) face each other, and the peripheral edges are heat-sealed to form a bag. Methods for forming the bag include heat sealing methods such as side seal type, two-side seal type, three-side seal type, four-side seal type, envelope seal type, gusset seal type, pleated seal type, flat-bottom seal type, square-bottom seal type, gusset type, and other heat-seal types. The packaging material of the present invention can take various forms depending on the contents, usage environment, and usage form. Self-standing packaging materials (standing pouches) are also possible. Known heat sealing methods include bar seal, rotary roll seal, belt seal, impulse seal, high-frequency seal, and ultrasonic seal.

[0168] Products using the packaging material of the present invention are manufactured by filling the packaging material with contents through its opening and then heat-sealing the opening. Examples of contents that can be filled include, for example, food products such as rice crackers, bean snacks, nuts, biscuits / cookies, wafers, marshmallows, pies, semi-baked cakes, candies, and snack foods; staple foods such as bread, instant noodles, dried noodles, pasta, aseptically packaged rice, rice porridge, packaged mochi, and cereal foods; processed agricultural products such as pickles, boiled beans, natto, miso, frozen tofu, tofu, enoki mushrooms, konjac, processed wild vegetables, jams, peanut cream, salads, frozen vegetables, and processed potato products; processed livestock products such as ham, bacon, sausages, processed chicken products, and corned beef; and fish ham. Examples of processed seafood products include sausages, processed seafood products, fish cakes, seaweed, preserved foods, dried bonito flakes, salted seafood, smoked salmon, and spicy cod roe; fruits such as peaches, oranges, pineapples, apples, pears, and cherries; vegetables such as corn, asparagus, mushrooms, onions, carrots, radishes, and potatoes; frozen and chilled prepared foods such as hamburgers, meatballs, fried seafood, dumplings, and croquettes; dairy products such as butter, margarine, cheese, cream, instant creamy powder, and infant formula; liquid seasonings; retort curry; and pet food.

[0169] Furthermore, as a non-food product, it can be used as a packaging material for various items such as cigarettes, disposable hand warmers, pharmaceuticals such as intravenous fluid packs, liquid laundry detergent, liquid dish soap, liquid bath detergent, liquid bath soap, liquid shampoo, liquid conditioner, cosmetics such as lotions and emulsions, vacuum insulation materials, and batteries. [Examples]

[0170] The present invention will be described in more detail below with reference to specific synthesis examples and embodiments, but the present invention is not limited to these embodiments. In the following examples, "parts" and "%" represent "parts by mass" and "mass%", respectively, unless otherwise specified.

[0171] <Preparation of polyisocyanate composition (X)> (Polyisocyanate composition (X-1)) 720.0 parts of tolylene diisocyanate (TDI) were added to a reaction vessel equipped with a stirrer, thermometer, nitrogen gas inlet tube, and condenser, and heated to 40°C while stirring under a nitrogen gas stream. Then, 182.0 parts of polyoxypropylene sorbitol ether (Sanyo Chemical Industries, Ltd., Sannix SP-750) and 98.0 parts of bifunctional polyethylene glycol with a molecular weight of 400 were added, taking care to avoid exothermic reactions, and the mixture was then heated to 60°C. The reaction was continued at 60°C until the NCO% no longer changed, and 0.2 parts of butyl acid phosphate were added to terminate the reaction. Next, using a thin-film distillation apparatus, the TDI in the urethane prepolymer, which is the reaction product of TDI and polyol, was purified to 0.05% by mass of the solid content at a pressure of approximately 0.02 Torr and a temperature of 160°C. This was dissolved and diluted with ethyl acetate to obtain a polyisocyanate composition (X-1) with a non-volatile content of 80% by mass. The NCO% of the polyisocyanate composition (X-1) was 10.5%.

[0172] (Polyisocyanate composition (X-2)) 819.1 parts of tolylene diisocyanate (TDI) were added to a reaction vessel equipped with a stirrer, thermometer, nitrogen gas inlet tube, and condenser, and heated to 40°C while stirring under a nitrogen gas stream. Then, 180.9 parts of polyoxypropylene sorbitol ether (Sanyo Chemical Industries, Ltd., Sannix SP-750) were added carefully to avoid exothermic reaction, and the mixture was heated to 60°C. The reaction was continued at 60°C for 4 hours, and 1.0 part of polyphosphate was added to terminate the reaction. Next, using a thin-film distillation apparatus, the TDI in the urethane prepolymer, which was the reaction product of TDI and polyol, was purified to 0.05% by mass of the solid content at a pressure of approximately 0.02 Torr and a temperature of 160°C. This was dissolved and diluted with ethyl acetate to obtain a 76% by mass non-volatile content solution to obtain polyisocyanate composition (X-2). The NCO% of polyisocyanate composition (X-2) was 10.5%.

[0173] (Polyisocyanate composition (X-3)) 788.7 parts of tolylene diisocyanate (TDI) were added to a reaction vessel equipped with a stirrer, thermometer, nitrogen gas inlet tube, and condenser, and heated to 40°C while stirring under a nitrogen gas stream. Then, 147.9 parts of polyoxypropylene sucrose ether (Sanyo Chemical Industries, Ltd., Sannix HS-209) and 63.4 parts of bifunctional polyethylene glycol with a molecular weight of 400 were added, taking care to avoid exothermic reactions, and the mixture was then heated to 60°C. The reaction was further carried out at 60°C for 4 hours, and 0.2 parts of butyl acid phosphate were added to terminate the reaction. Next, using a thin-film distillation apparatus, the TDI in the urethane prepolymer, which is the reaction product of TDI and polyol, was purified to 0.05% by mass of the solid content at a pressure of approximately 0.02 Torr and a temperature of 160°C until the TDI content in the urethane prepolymer was 0.05% by mass of the solid content, thereby obtaining polyisocyanate composition (X-3). The NCO% of polyisocyanate composition (X-3) was 12.9%.

[0174] (Polyisocyanate composition (X'-4)) 500.0 parts of tolylene diisocyanate (TDI) were added to a reaction vessel equipped with a stirrer, thermometer, nitrogen gas inlet tube, and condenser, and heated to 60°C while stirring under a nitrogen gas stream. Then, 657.6 parts of bifunctional polypropylene glycol (AGC Exenol 420) were added carefully, taking care to avoid exothermic reactions, and the mixture was heated to 80°C and reacted at 80°C for 2 hours. Next, using a thin-film distillation apparatus, the TDI in the urethane prepolymer, which is the reaction product of TDI and polypropylene glycol, was purified to 0.05% by mass of the solid content at a pressure of approximately 0.02 Torr and a temperature of 160°C to obtain polyisocyanate composition (X'-4). The NCO% of polyisocyanate composition (X'-4) was 8.9%.

[0175] (Polyisocyanate composition (X'-5)) 500.0 parts of tolylene diisocyanate (TDI) were added to a reaction vessel equipped with a stirrer, thermometer, nitrogen gas inlet tube, and condenser, and heated to 40°C while stirring under a nitrogen gas stream. Then, 657.6 parts of bifunctional polypropylene glycol (AGC Exenol 420) were added carefully to avoid exothermic reaction, and the mixture was heated to 60°C. The reaction was continued at 60°C for 4 hours, and 1.0 part of polyphosphate was added to terminate the reaction. Next, using a thin-film distillation apparatus, the TDI in the urethane prepolymer, which is the reaction product of TDI and polypropylene glycol, was purified to 0.05% by mass of the solid content at a pressure of approximately 0.02 Torr and a temperature of 160°C to obtain polyisocyanate composition (X'-5). The NCO% of polyisocyanate composition (X'-5) was 9.0%.

[0176] (Polyisocyanate composition (X'-6)) 720.0 parts of tolylene diisocyanate (TDI) were added to a reaction vessel equipped with a stirrer, thermometer, nitrogen gas inlet tube, and condenser, and heated to 40°C while stirring under a nitrogen gas stream. Then, 182.0 parts of polyoxypropylene sorbitol ether (Sanyo Chemical Industries, Ltd., Sannix SP-750) and 98.0 parts of bifunctional polyethylene glycol with a molecular weight of 400 were added, taking care to avoid exothermic reactions, and the mixture was then heated to 60°C. The reaction was further carried out at 60°C for 4 hours, and 10.0 parts of polyphosphate were added to terminate the reaction. Next, using a thin-film distillation apparatus, the TDI in the urethane prepolymer, which is the reaction product of TDI and polyol, was purified to 0.05% by mass of the solid content at a pressure of approximately 0.02 Torr and a temperature of 160°C until the TDI content in the urethane prepolymer was 0.05% by mass of the solid content. This was dissolved and diluted with ethyl acetate to obtain a polyisocyanate composition (X'-6) with a non-volatile content of 80% by mass. The NCO% of the polyisocyanate composition (X'-6) was 10.4%.

[0177] (Polyisocyanate composition (X'-7)) 899.4 parts of tolylene diisocyanate (TDI) were added to a reaction vessel equipped with a stirrer, thermometer, nitrogen gas inlet tube, and condenser, and heated to 40°C while stirring under a nitrogen gas stream. Then, 100.6 parts of polyglycerin 10 (polymer of 10 glycerin molecules) were added carefully to avoid exothermic reactions, and the mixture was heated to 60°C. The reaction was continued at 60°C for 4 hours, and 1.0 part of polyphosphate was added to terminate the reaction. Next, using a thin-film distillation apparatus, the TDI in the urethane prepolymer, which is the reaction product of TDI and polyol, was purified to 0.05% by mass of the solid content at a pressure of approximately 0.02 Torr and a temperature of 160°C. This was dissolved and diluted with ethyl acetate to obtain a 75% by mass non-volatile content solution to obtain polyisocyanate composition (X'-7). The NCO% of polyisocyanate composition (X'-7) was 12.0%.

[0178] <Preparation of isocyanate-reactive composition (Y)> (Isocyanate-reactive composition (Y-1)) In a polyester reaction vessel equipped with a stirrer, thermometer, nitrogen gas inlet tube, rectification tube, etc., 130 parts terephthalic acid, 130 parts isophthalic acid, 150 parts adipic acid, 50 parts dimer acid, 70 parts ethylene glycol, 65 parts diethylene glycol, 65 parts neopentyl glycol, and 60 parts 1,6-hexanediol were added, and an esterification reaction was carried out at an internal temperature of 250°C. After the dehydration reaction, an intermediate polyester polyol with an acid value of 1 mg KOH / g was obtained. This was dissolved and diluted with ethyl acetate to obtain a solution with a non-volatile content of 65% by mass. Furthermore, 4 parts isophorone diisocyanate were added to 100 parts of the solid content of the intermediate polyester polyol, and the urethane reaction was carried out by heating to 80°C until the free NO groups were substantially eliminated, to obtain an isocyanate reactive composition (Y-1) with a non-volatile content of 65% by mass and a hydroxyl value of 6.

[0179] <Rating> (Storage stability of polyisocyanate composition (X)) 15 ml glass bottles were filled with the prepared polyisocyanate compositions (X-1) to (X-3) and (X'-4) to (X'-7), respectively, and stored at room temperature for a certain period. The state of the polyisocyanate composition (X) after storage was evaluated in two stages according to the following criteria, and the results are summarized in Table 1. ○: Did not solidify for more than 30 days ×: Solidified within 30 days

[0180] [Table 1]

[0181] (Preparation of adhesive) Polyisocyanate composition (X) and isocyanate-reactive composition (Y) were mixed according to the formulations shown in Table 2 to prepare adhesives for the examples and comparative examples. Polyisocyanate composition (X'-7) solidified and therefore could not be evaluated as an adhesive.

[0182] (Heat seal strength) A two-component curing adhesive (solid content 3 g / m²) is formulated by combining a 15 μm thick biaxially oriented nylon film and a 30 μm thick linear low-density polyethylene (LLDPE) film as a sealant film, in combination as shown in the examples or comparative examples. 2 The layers were bonded together and aged at 40°C for 6 hours to obtain a laminated film.

[0183] Align the sealant film surfaces of the laminated films and seal them with a 1cm wide sealing bar at 180℃ and 1kgf / cm². 2 The test specimens were heat-sealed for 1 second and cut into 15 mm wide strips. Using a tensile testing machine, the ambient temperature was set to 25°C and the peeling speed to 300 mm / min. The peak tensile strength measured at both ends of the test specimen was defined as the heat-seal strength (N / 15 mm). The results were evaluated according to the following criteria and summarized in Table 2. ○: 50N / 15mm or more ×: Less than 50N / 15mm

[0184] (Lamination strength) A two-component curing adhesive (solid content 3g / m²) is formulated by combining a 50μm biaxially oriented PET film and a 30μm aluminum foil in the combinations shown in the examples or comparative examples. 2 The materials were bonded together and aged at 40°C for 72 hours to obtain a laminated film.

[0185] Test specimens were cut from the laminated film in 15 mm widths, and the adhesive strength (N / 15 mm) was measured using a tensile testing machine at an ambient temperature of 25°C, a peeling speed of 300 mm / min, and a 180-degree peel. The results were evaluated according to the following criteria and are summarized in Table 2. ○: 5.0N / 15mm or more ×: 5.0N / less than 15mm

[0186] [Table 2]

Claims

1. Polyurethane polyisocyanate (A1), which is a reaction product of toluene diisocyanate and a polyol having 5 to 10 hydroxyl groups, It contains a phosphate derivative (B), A polyisocyanate composition (X) having a content of the phosphate derivative (B) of 10 ppm or more and 5000 ppm or less.

2. The polyisocyanate composition (X) according to claim 1, wherein the molecular weight of the polyol is 200 g / mol or more and 3000 g / mol or less.

3. The polyisocyanate composition (X) according to claim 1, wherein the polyol is at least one selected from xylitol, triglycerol, sorbitol, dipentaerythritol, mannitol, sucrose, and polyglycerin, modified with at least one selected from ethylene oxide, propylene oxide, butylene oxide, and tetrahydrofuran to form a polyether polyol, and at least one selected from polyglycerin.

4. The polyisocyanate composition (X) according to claim 1, wherein the polyol is a polyether polyol obtained by modifying sorbitol with at least one selected from ethylene oxide, propylene oxide, butylene oxide, and tetrahydrofuran, and at least one selected from polyglycerin.

5. The polyisocyanate composition (X) according to claim 1, further comprising polyurethane polyisocyanate (A2), which is a reaction product of toluene diisocyanate and a bifunctional polyol.

6. The polyisocyanate composition (X) according to claim 5, wherein the bifunctional polyol is at least one selected from diethylene glycol and polyetherdiol.

7. The polyisocyanate composition (X) according to claim 5, wherein the bifunctional polyol is polyethylene glycol.

8. The polyisocyanate composition (X) according to claim 5, wherein the molecular weight of the bifunctional polyol is 100 g / mol or more and 4000 g / mol or less.

9. The polyisocyanate composition (X) according to claim 5, wherein the content of the polyurethane polyisocyanate (A2) in the polyisocyanate composition (X) is 10% by mass or more and 60% by mass or less.

10. The polyisocyanate composition (X) according to claim 1, wherein the content of diisocyanate monomer is 0.1% by mass or less.

11. A polyisocyanate composition (X) according to any one of claims 1 to 10, A two-component curable composition comprising an isocyanate-reactive composition (Y) containing an isocyanate-reactive compound (C), and

12. A polyisocyanate composition (X) according to any one of claims 1 to 10, A two-component curable coating agent comprising an isocyanate-reactive composition (Y) containing an isocyanate-reactive compound (C), and

13. A polyisocyanate composition (X) according to any one of claims 1 to 10, A two-component curing adhesive comprising an isocyanate-reactive composition (Y) containing an isocyanate-reactive compound (C), and

14. The two-component curing adhesive according to claim 13, wherein the isocyanate-reactive compound (C) comprises at least one selected from polyester polyol (C1), polyether polyol (C2), vegetable oil polyol (C3), polyurethane polyol (C4), sugar alcohol (C5), acrylic polyol (C6), amine compound (C7), and epoxy compound (C8).

15. A laminate comprising a first substrate, a second substrate, and an adhesive layer disposed between the first substrate and the second substrate, wherein the adhesive layer is a cured coating film of the two-component curing adhesive described in claim 13.

16. A packaging material comprising the laminate described in claim 15.

Images