Additive composition, resin composition containing the same, method for producing the same, and molded article

Abstract

Provided are an additive composition capable of imparting excellent mechanical properties to molded articles, a resin composition containing the additive composition, a production method therefor, and a molded article.　The additive composition comprises (A) a nucleator, (B) a lithium salt of a hydroxylated fatty acid, and (C) a hydrotalcite, wherein the nucleator (A) includes a metal salt of an organic oxoacid, the lithium salt of a hydroxylated fatty acid (B) is contained in an amount of 25-400 parts by mass per 100 parts by mass of the nucleator (A), and the hydrotalcite (C) is contained in an amount of 25-400 parts by mass per 100 parts by mass of the nucleator (A).

Description

[Technical Field]

[0001] The present invention relates to an additive composition, a resin composition containing the same, a method for producing the same, and a molded article, and more specifically, to an additive composition that can impart excellent mechanical properties to a molded article, a resin composition containing the same, a method for producing the same, and a molded article. [Background technology]

[0002] Polyolefin resins are among the most versatile plastic materials in terms of physical properties, moldability, and cost, and are used in a wide range of applications.

[0003] Molded articles made from polyolefin resins are sometimes required to have excellent mechanical properties. One method known for imparting mechanical properties to molded articles made from polyolefin resins is to add a nucleating agent to the polyolefin resin. As a nucleating agent to be added to polyolefin resins, for example, Patent Document 1 proposes a nucleating agent containing an aromatic phosphate ester metal salt. [Prior art documents] [Patent Documents]

[0004] [Patent Document 1] Japanese Patent Application Publication No. 63-69853 [Overview of the project] [Problems that the invention aims to solve]

[0005] However, the molded article made of polyolefin resin with the nucleating agent described in Patent Document 1 had room for further improvement in terms of mechanical properties. Therefore, it was desired to impart even better mechanical properties to molded articles made of polyolefin resin.

[0006] Therefore, the object of the present invention is to provide an additive composition that can impart excellent mechanical properties to a molded article, a resin composition containing the same, a method for producing the same, and a molded article. [Means for solving the problem]

[0007] As a result of diligent research to solve the above problems, the inventors of the present invention unexpectedly discovered that the above problems can be solved by an additive composition containing a specific nucleating agent, a fatty acid metal salt having a specific structure, and hydrotalcites in a specific ratio, and thus completed the present invention.

[0008] In other words, the additive composition of the present invention comprises (A) a nucleating agent, (B) a hydroxyl group-containing fatty acid lithium salt, and (C) hydrotalcite, wherein the (A) nucleating agent comprises an organic oxo acid metal salt, the content of the (B) hydroxyl group-containing fatty acid lithium salt is 25 to 400 parts by mass per 100 parts by mass of the (A) nucleating agent, and the content of the (C) hydrotalcite is 25 to 400 parts by mass per 100 parts by mass of the (A) nucleating agent.

[0009] In the additive composition of the present invention, it is preferable that the organic oxo acid metal salt includes an aromatic phosphate ester metal salt, an aromatic carboxylate metal salt, or an alicyclic dicarboxylate metal salt. Furthermore, in the additive composition of the present invention, it is preferable that the (B) hydroxyl group-containing fatty acid lithium salt includes at least one selected from the group consisting of lithium hydroxystearate and lithium hydroxyoleate. Moreover, in the additive composition of the present invention, it is preferable that the (C) hydrotalcites are of the following general formula (2) or the following general formula (3), TIFF0007842683000001.tif9158(In general formula (2), y1 and y2 represent numbers satisfying 0 ≤ y2 / y1 < 10 and 2 ≤ y1 + y2 ≤ 20, and p represents 0 or a positive number.) TIFF0007842683000002.tif11158(in general formula (3), A q- It is preferable that the compound contains the compound represented by (where represents a q-valent anion, and p represents 0 or a positive number).

[0010] Furthermore, the resin composition of the present invention comprises a polyolefin resin, (A) a nucleating agent, (B) a hydroxyl group-containing fatty acid lithium salt, and (C) hydrotalcite, wherein the (A) nucleating agent comprises an organic oxo acid metal salt, the content of the (B) hydroxyl group-containing fatty acid lithium salt per 100 parts by mass of the (A) nucleating agent is 25 to 400 parts by mass, the content of the (C) hydrotalcite per 100 parts by mass of the (A) nucleating agent is 25 to 400 parts by mass, and the content of the (A) nucleating agent per 100 parts by mass of the polyolefin resin is 0.001 to 10 parts by mass.

[0011] In the resin composition of the present invention, the polyolefin resin is preferably a polypropylene resin, and it is more preferable that 90% by mass or more of the monomer units constituting the polypropylene resin are propylene units.

[0012] Furthermore, the method for producing the resin composition of the present invention is characterized by including a step of blending the above-mentioned additive composition with a polyolefin resin.

[0013] Furthermore, the molded article of the present invention is characterized by being obtained by molding the above-mentioned resin composition. [Effects of the Invention]

[0014] According to the present invention, it is possible to provide an additive composition that can impart excellent mechanical properties to molded articles, a resin composition containing the same, a method for producing the same, and a molded article. [Modes for carrying out the invention]

[0015] The embodiments of the present invention will be described in detail below. First, the additive composition according to this embodiment will be described.

[0016] <Additive composition> The additive composition of this embodiment contains (A) a nucleating agent, (B) a lithium salt of a hydroxyl-containing fatty acid, and (C) hydrotalcites. And, (A) the nucleating agent contains an organic oxo acid metal salt. Further, the content of (B) the lithium salt of the hydroxyl-containing fatty acid with respect to 100 parts by mass of (A) the nucleating agent is 25 to 400 parts by mass, and the content of (C) the hydrotalcites with respect to 100 parts by mass of (A) the nucleating agent is 25 to 400 parts by mass.

[0017] According to the additive composition of this embodiment, excellent mechanical properties can be imparted to the molded product.

[0018] The reason why the additive composition of this embodiment imparts excellent mechanical properties to the molded product is not clear, but the present inventors presume as follows. That is, the organic oxo acid metal salt contained in (A) the nucleating agent, (B) the lithium salt of the hydroxyl-containing fatty acid, and (C) the hydrotalcites form some kind of aggregate by electrostatic interaction and hydrogen bonding, and this aggregate acts as a nucleating component of the polyolefin resin. Therefore, the present inventors presume that the additive composition of this embodiment can impart excellent mechanical properties to the molded product.

[0019] (A) The nucleating agent contains an organic oxo acid metal salt. Here, the organic oxo acid metal salt is a salt composed of an anion which is a conjugate base of an organic oxo acid and a metal cation. And, the organic oxo acid is an organic acid having at least one substituent containing an atom to which a hydroxyl group and an oxo group are bonded. Specific examples of the organic oxo acid include, for example, aliphatic phosphoric acid, alicyclic phosphoric acid, aromatic phosphoric acid, aliphatic phosphoric acid ester, alicyclic phosphoric acid ester, aromatic phosphoric acid ester, aliphatic carboxylic acid, alicyclic carboxylic acid, aromatic carboxylic acid, aliphatic sulfonic acid, alicyclic sulfonic acid, aromatic sulfonic acid, rosin acid, etc. Further, examples of the metal cation constituting the organic oxo acid metal salt include, for example, alkali metal ions, alkaline earth metal ions, aluminum ions, hydroxyaluminum ions, dihydroxyaluminum ions, zinc ions, etc. Here, the organic oxo acid metal salt may be contained alone or in combination of two or more.

[0020] Examples of the metal salt of aromatic phosphate ester include compounds represented by the following general formula (1). The metal salt of aromatic phosphate ester may be contained alone or in combination of two or more kinds.

[0021] TIFF0007842683000003.tif40158

[0022] In general formula (1), R 1 ~R 5 each independently represents a hydrogen atom or an alkyl group having 1 to 6 carbon atoms, n represents 1 or 2, when n is 1, M represents an alkali metal or dihydroxyaluminum, and when n is 2, M represents an alkaline earth metal, zinc or hydroxyaluminum.

[0023] R 1 ~R 5 Examples of the alkyl group having 1 to 6 carbon atoms represented by ~R 1 ~R 4 include methyl group, ethyl group, n-propyl group, isopropyl group, cyclopropyl group, n-butyl group, sec-butyl group, tert-butyl group, isobutyl group, cyclobutyl group, n-amyl group, tert-amyl group, cyclopentyl group, n-hexyl group, cyclohexyl group and the like. From the viewpoint of imparting more excellent rigidity and more excellent impact resistance to the molded product, it is particularly preferable that R 5 ~R

[0024]

[0025] Specific examples of aromatic phosphate metal salts represented by general formula (1) include the following. However, aromatic phosphate metal salts represented by general formula (1) are not limited to those listed below.

[0026] TIFF0007842683000004.tif125158

[0027] Among these, sodium 2,2'-methylenebis(4,6-di-tert-butylphenyl) phosphate, lithium 2,2'-methylenebis(4,6-di-tert-butylphenyl) phosphate, hydroxyaluminum bis[2,2'-methylenebis(4,6-di-tert-butylphenyl) phosphate] or dihydroxyaluminum 2,2'-methylenebis(4,6-di-tert-butylphenyl) phosphate are preferred from the viewpoint of providing molded articles with superior rigidity and superior impact resistance, sodium 2,2'-methylenebis(4,6-di-tert-butylphenyl) phosphate or hydroxyaluminum bis[2,2'-methylenebis(4,6-di-tert-butylphenyl) phosphate] or dihydroxyaluminum 2,2'-methylenebis(4,6-di-tert-butylphenyl) phosphate are more preferred, and sodium 2,2'-methylenebis(4,6-di-tert-butylphenyl) phosphate is particularly preferred.

[0028] Examples of aromatic carboxylate metal salts include sodium benzoate, tris(4-t-butylbenzoate)aluminum, bis(4-t-butylbenzoate)hydroxyaluminum, and (4-t-butylbenzoate)dihydroxyaluminum. Among these, sodium benzoate or bis(4-t-butylbenzoate)hydroxyaluminum are preferred from the viewpoint of providing superior rigidity and impact resistance to the molded product. The aromatic carboxylate metal salt may be included alone or in combination of two or more types.

[0029] Examples of alicyclic dicarboxylate metal salts include 2,3-norbornanedicarboxylate disodium, 2,5-norbornanedicarboxylate disodium, 2,6-norbornanedicarboxylate disodium, 1,2-cyclohexanedicarboxylate calcium, 1,3-cyclohexanedicarboxylate calcium, and 1,4-cyclohexanedicarboxylate disodium. Among these, 2,3-norbornanedicarboxylate disodium or 1,2-cyclohexanedicarboxylate calcium are preferred from the viewpoint of providing molded articles with superior rigidity and impact resistance. The alicyclic dicarboxylate metal salt may be included alone or in combination of two or more types.

[0030] Examples of metal rosinate salts include sodium, calcium, and magnesium salts of rosinate, including abietic acid, palastic acid, and isopimalic acid.

[0031] In the additive composition of this embodiment, it is preferable that the organic oxo acid metal salt contained in the nucleating agent (A) includes an aromatic phosphate ester metal salt. In this case, particularly excellent rigidity and impact resistance can be imparted to the molded article.

[0032] Furthermore, it is preferable that the organic oxo acid metal salt contained in (A) the nucleating agent also contains an aromatic carboxylate metal salt. In this case, particularly excellent impact resistance can be imparted to the molded article.

[0033] Furthermore, it is preferable that the organic oxo acid metal salt contained in the nucleating agent (A) also includes an alicyclic dicarboxylate metal salt. In this case, particularly excellent rigidity can be imparted to the molded article.

[0034] In the additive composition of this embodiment, (A) the nucleating agent may further include compounds other than the above-mentioned organic oxoacid metal salts that have the function of promoting the crystallization of polyolefin resins. Examples of such compounds include polyol derivatives such as dibenzylidene sorbitol, bis(methylbenzylidene) sorbitol, bis(3,4-dimethylbenzylidene) sorbitol, bis(p-ethylbenzylidene) sorbitol, bis(dimethylbenzylidene) sorbitol, 1,2,3-trideoxy-4,6:5,7-o-bis(4-propylbenzylidene)nonitol, N,N',N”-tris[2-methylcyclohexyl]-1,2,3-propanetricarboxamide, N,N',N”-tricyclohexyl-1,3,5-benzenetricarboxamide, N,N'-dicyclohexylnaphthalenedicarboxamide, and amide compounds such as 1,3,5-tri(dimethylisopropoylamino)benzene. (A) The content of the organic oxo acid metal salt relative to the total amount of the nucleating agent may be 80 to 100% by mass, preferably 90 to 100% by mass, preferably 99 to 100% by mass, and particularly preferably 100% by mass.

[0035] (B) Examples of lithium salts of hydroxyl group-containing fatty acids include lithium salts of fatty acids having 12 to 30 carbon atoms, which contain linear or branched fatty acid residues in which 1 to 3 hydrogen atoms are substituted with hydroxyl groups. Specifically, examples include lithium salts of fatty acids such as hydroxylauric acid, hydroxymyristic acid, hydroxypalmitic acid, hydroxystearic acid, hydroxyarachidic acid, hydroxybehenic acid, hydroxymontanic acid, hydroxyoleic acid, hydroxylinoleic acid, hydroxylinolenic acid, dihydroxylauric acid, dihydroxymyristic acid, dihydroxypalmitic acid, dihydroxystearic acid, dihydroxyarachidic acid, dihydroxybehenic acid, dihydroxymontanic acid, dihydroxyoleic acid, dihydroxylinoleic acid, dihydroxylinolenic acid, trihydroxylauric acid, trihydroxymyristic acid, trihydroxypalmitic acid, trihydroxystearic acid, trihydroxyarachidic acid, trihydroxybehenic acid, trihydroxymontanic acid, trihydroxyoleic acid, trihydroxylinoleic acid, and trihydroxylinolenic acid. These may be included individually or in combination of two or more. Among these, lithium hydroxystearate or lithium hydroxyoleate is preferred from the viewpoint of providing superior rigidity and impact resistance to the molded article, and lithium 12-hydroxystearate or lithium 12-hydroxyoleate (lithium ricinoleate) is more preferred from the viewpoint of being readily available, with lithium 12-hydroxystearate being particularly preferred.

[0036] As described above, the content of (B) hydroxyl group-containing fatty acid lithium salt per 100 parts by mass of (A) nucleating agent is 25 to 400 parts by mass. From the viewpoint of imparting superior rigidity and impact resistance to the molded product, the content of (B) hydroxyl group-containing fatty acid lithium salt per 100 parts by mass of (A) nucleating agent is preferably 33 parts by mass or more, and more preferably 50 parts by mass or more. Also, from the same viewpoint, the content of (B) hydroxyl group-containing fatty acid lithium salt per 100 parts by mass of (A) nucleating agent is preferably 200 parts by mass or less, and more preferably 100 parts by mass or less.

[0037] (C) The hydrotalcite-like compounds may be composite salt compounds containing magnesium, aluminum, hydroxyl groups, carbonate groups, and optional water of crystallization, and may be natural products or synthetic products. Further, the hydrotalcite-like compounds may be those in which at least a part of magnesium or aluminum is substituted with other metals such as alkali metals and zinc, and may be those in which at least a part of hydroxyl groups and carbonate groups are substituted with other anion groups. From the viewpoint of imparting excellent rigidity and impact resistance to the molded product, the hydrotalcite-like compounds contained in the additive composition of the present embodiment preferably contain a compound represented by the following general formula (2) or the following general formula (3).

[0038] TIFF0007842683000005.tif9158

[0039] TIFF0007842683000006.tif11158

[0040] Here, in the general formula (2), y1 and y2 represent numbers satisfying 0 ≦ y2 / y1 < 10 and 2 ≦ y1 + y2 ≦ 20, and p represents 0 or a positive number. Further, in the general formula (3), A q- represents a q-valent anion, and p represents 0 or a positive number. From the viewpoint of imparting more excellent rigidity and impact resistance to the molded product, the hydrotalcite-like compound is more preferably a compound represented by the general formula (2), and further preferably a compound represented by the general formula (2) and having y2 = 0. The hydrotalcite-like compounds may be those obtained by dehydrating the water of crystallization, and may be those coated with higher fatty acids such as stearic acid, higher fatty acid metal salts such as alkali metal oleate, organic sulfonic acid metal salts such as alkali metal dodecylbenzenesulfonate, higher fatty acid amides, higher fatty acid esters, or waxes. The hydrotalcite-like compounds may be natural products or synthetic products.

[0041] Methods for producing hydrotalcite include known methods described in Japanese Patent Publication No. 46-2280, Japanese Patent Publication No. 50-30039, Japanese Patent Publication No. 51-29129, Japanese Patent Publication No. 3-36839, Japanese Patent Publication No. 61-174270, Japanese Patent Publication No. 5-179052, etc. Furthermore, the crystal structure, particle shape, and particle size of the hydrotalcite are not particularly limited. In addition, the hydrotalcite may be included as a single type or as a combination of two or more types.

[0042] As described above, the content of (C) hydrotalcites per 100 parts by mass of (A) nucleating agent is 25 to 400 parts by mass. From the viewpoint of imparting superior rigidity to the molded product, the content of (C) hydrotalcites per 100 parts by mass of (A) nucleating agent is preferably 50 parts by mass or more, and more preferably 100 parts by mass or more. Also, from the same viewpoint, the content of (C) hydrotalcites per 100 parts by mass of (A) nucleating agent is preferably 200 parts by mass or less, and more preferably 150 parts by mass or less.

[0043] The content of (C) hydrotalcites per 100 parts by mass of (B) hydroxyl group-containing fatty acid lithium salt is not particularly limited, and may be, for example, 10 to 1000 parts by mass. From the viewpoint of imparting superior rigidity and impact resistance to the molded product, the content of (C) hydrotalcites per 100 parts by mass of (B) hydroxyl group-containing fatty acid lithium salt is preferably 20 to 500 parts by mass, and more preferably 25 to 400 parts by mass.

[0044] The additive composition of this embodiment may further contain, as needed, various additives such as phenolic antioxidants, phosphorus-based antioxidants, sulfur-based antioxidants, other antioxidants, hindered amine compounds, ultraviolet absorbers, fatty acid metal salts other than hydroxyl group-containing fatty acid lithium salts, flame retardants, flame retardant aids, lubricants, fillers, antistatic agents, fluorescent whitening agents, pigments, and dyes.

[0045] Examples of phenolic antioxidants include 2,6-di-tert-butyl-4-ethylphenol, 2-tert-butyl-4,6-dimethylphenol, styrenephenol, 2,2'-methylenebis(4-ethyl-6-tert-butylphenol), 2,2'-thiobis-(6-tert-butyl-4-methylphenol), 2,2'-thiodiethylenebis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate], 2-methyl-4,6-bis(octylsulfanylmethyl)phenol, 2,2'-isobutylidenebis(4,6-dimethylphenol), isooctyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl) (Nyl)propionate, N,N'-Hexane-1,6-diylbis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionamide], 2,2'-Oxamide-bis[ethyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate], 2-ethylhexyl-3-(3',5'-di-tert-butyl-4'-hydroxyphenyl)propionate, 2,2'-ethylenebis(4,6-di-tert-butylphenol), 3,5-di-tert-butyl-4-hydroxybenzenepropanoic acid and C13-15 alkyl ester, 2,5-di-tert-amylhydroquinone, polymer of hindered phenol (manufactured by ADEKA POLYMER ADDITIVES EUROPE SAS) Product name "AO.OH.98"), 2,2'-methylenebis[6-(1-methylcyclohexyl)-p-cresol], 2-tert-butyl-6-(3-tert-butyl-2-hydroxy5-methylbenzyl)-4-methylphenyl acrylate, 2-[1-(2-hydroxy-3,5-di-tert-pentylphenyl)ethyl]-4,6-di-tert-pentylphenyl acrylate, 6-[3-(3-tert-butyl-4-hydroxy-5-methyl)propoxy]-2,4,8,10-tetra-tert-butylbenz[d,f][1,3,2]-dioxaphosphobine, hexamethylenebis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate], bis[monoethyl(3,5-di-tert-butyl-4-hydroxybenzyl)phosphonate]calcium salt, 5,Reaction product of 7-bis(1,1-dimethylethyl)-3-hydroxy-2(3H)-benzofuranone and o-xylene, 2,6-di-tert-butyl-4-(4,6-bis(octylthio)-1,3,5-triazine-2-ylamino)phenol, DL-α-tocopherol (vitamin E), 2,6-bis(α-methylbenzyl)-4-methylphenol, bis[3,3-bis-(4'-hydroxy-3'-tert-butyl-phenyl)butanoic acid] glycol ester, 2,6-di-tert-butyl-p-cresol, 2,6-diphenyl Nyl-4-octadecyloxyphenol, stearyl(3,5-di-tert-butyl-4-hydroxyphenyl)propionate, distearyl(3,5-di-tert-butyl-4-hydroxybenzyl)phosphonate, tridecyl-3,5-tert-butyl-4-hydroxybenzylthioacetate, thiodiethylenebis[(3,5-di-tert-butyl-4-hydroxyphenyl)propionate], 4,4'-thiobis(6-tert-butyl-m-cresol), 2-octylthio-4,6-di(3,5-di-tert-butyl 4-hydroxyphenoxy)-s-triazine, 2,2'-methylenebis(4-methyl-6-tert-butylphenol), bis[3,3-bis(4-hydroxy-3-tert-butylphenyl)butyric acid] glycol ester, 4,4'-butylidenebis(2,6-di-tert-butylphenol), 4,4'-butylidenebis(6-tert-butyl-3-methylphenol), 2,2'-ethylidenebis(4,6-di-tert-butylphenol), 1,1,3-tris(2-methyl-4-hydroxy-5-te rt-butylphenyl)butane, bis[2-tert-butyl-4-methyl-6-(2-hydroxy-3-tert-butyl-5-methylbenzyl)phenyl]terephthalate, 1,3,5-tris(2,6-dimethyl-3-hydroxy-4-tert-butylbenzyl)isocyanurate, 1,3,5-tris(3,5-di-tert-butyl-4-hydroxybenzyl)isocyanurate, 1,3,5-tris(3,5-di-tert-butyl-4-hydroxybenzyl)-2,4,6-trimethylbenzene, 1,3,5-tris[(3,[5-di-tert-butyl-4-hydroxyphenyl)propionyloxyethyl]isocyanurate, tetrakis[methylene-3-(3',5'-tert-butyl-4'-hydroxyphenyl)propionate]methane, 2-tert-butyl-4-methyl-6-(2-acryloyloxy-3-tert-butyl-5-methylbenzyl)phenol, 3,9-bis[2-(3-tert-butyl-4-hydroxy-5-methylhydrocinnamoyloxy)-1,1-dimethylethyl]-2,4,8,10-tetraoxaspiro[5.5]undecane, triethylene glycol bis[β Examples include 3-(3,5-dialkyl-4-hydroxyphenyl)propionic acid derivatives such as -(3-tert-butyl-4-hydroxy-5-methylphenyl)propionate, stearyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate, palmityl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate, myristyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate, and lauryl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate.

[0046] Examples of phosphorus-based antioxidants include triphenyl phosphite, diisooctyl phosphite, heptakis(dipropylene glycol) triphosphite, triisodecyl phosphite, diphenylisooctyl phosphite, diisooctylphenyl phosphite, diphenyltridecyl phosphite, triisooctyl phosphite, trilauryl phosphite, diphenyl phosphite, tris(dipropylene glycol) phosphite, dioleylhydrogen phosphite, trilauryltrithiophosphite, and bis(tridecyl) phosphite. Tris(isodecyl) phosphite, Tris(tridecyl) phosphite, Diphenyldecyl phosphite, Dinonylphenyl bis(nonylphenyl) phosphite, Poly(dipropylene glycol) phenyl phosphite, Tetraphenyldipropylene glycol diphosphite, Trisnonylphenyl phosphite, Tris(2,4-di-tert-butylphenyl) phosphite, Tris(2,4-di-tert-butyl-5-methylphenyl) phosphite, Tris[2-tert-butyl-4-(3-tert-butyl-4-Hyd [Loxy-5-methylphenylthio)-5-methylphenyl] phosphite, tri(decyl) phosphite, octyldiphenyl phosphite, di(decyl)monophenyl phosphite, mixture of distearyl pentaerythritol and calcium stearate, alkyl(C10) bisphenol A phosphite, tetraphenyl-tetra(tridecyl)pentaerythritol tetraphosphite, bis(2,4-di-tert-butyl-6-methylphenyl)ethyl phosphite, tetra(tridecyl)isopropylidene diphenol diphosphate Ito, Tetra(tridecyl)-4,4'-n-butylidenebis(2-tert-butyl-5-methylphenol) diphosphite, Hexa(tridecyl)-1,1,3-tris(2-methyl-4-hydroxy-5-tert-butylphenyl)butane triphosphite, Tetrakis(2,4-di-tert-butylphenyl) biphenylenediphosphonite, 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide, (1-methyl-1-propenyl-3-ylidene)tris(1,1-dimethylethyl)-5-methyl-4,1-Phenylene)Hexatridecylphosphite, 2,2'-Methylenebis(4,6-di-tert-butylphenyl)-2-ethylhexylphosphite, 2,2'-Methylenebis(4,6-di-tert-butylphenyl)-Octadecylphosphite, 2,2'-Ethylidenebis(4,6-di-tert-butylphenyl)fluorophosphite, 4,4'-Butylidenebis(3-methyl- 6-tert-butylphenyl ditridecyl) phosphite, tris(2-[(2,4,8,10-tetrakis-tert-butyldibenzo[d,f][1,3,2]dioxaphosfepin-6-yl)oxy]ethyl)amine, 3,9-bis(4-nonylphenoxy)-2,4,8,10-tetraoxa-3,9-diphosfespiro[5,5]undecane, 2,4,6-tri-tert-butyl Examples include phenyl-2-butyl-2-ethyl-1,3-propanediol phosphite, poly-4,4'-isopropylidenediphenol C12-15 alcohol phosphite, bis(diisodecyl)pentaerythritol diphosphite, bis(tridecyl)pentaerythritol diphosphite, bis(octadecyl)pentaerythritol diphosphite, bis(nonylphenyl)pentaerythritol diphosphite, bis(2,4-di-tert-butylphenyl)pentaerythritol diphosphite, bis(2,4,6-tri-tert-butylphenyl)pentaerythritol diphosphite, bis(2,6-di-tert-butyl-4-methylphenyl)pentaerythritol diphosphite, and bis(2,4-dicumylphenyl)pentaerythritol diphosphite.

[0047] Examples of sulfur-based antioxidants include tetrakis[methylene-3-(laurylthio)propionate]methane, bis(methyl-4-[3-n-alkyl(C12 / C14)thiopropionyloxy]5-tert-butylphenyl) sulfide, ditridecyl-3,3'-thiodipropionate, dilauryl-3,3'-thiodipropionate, dimyristyl-3,3'-thiodipropionate, distearyl-3,3'-thiodipropionate, lauryl / stearylthiodipropionate, 4,4'-thiobis(6-tert-butyl-m-cresol), 2,2'-thiobis(6-tert-butyl-p-cresol), and distearyl-disulfide.

[0048] Other antioxidants include nitrone compounds such as N-benzyl-α-phenylnitrone, N-ethyl-α-methylnitrone, N-octyl-α-heptylnitrone, N-lauryl-α-undecylnitrone, N-tetradecyl-α-tridecylnitrone, N-hexadecyl-α-pentadecylnitrone, N-octyl-α-heptadecylnitrone, N-hexadecyl-α-heptadecylnitrone, N-octadecyl-α-pentadecylnitrone, N-heptadecyl-α-heptadecylnitrone, N-octadecyl-α-heptadecylnitrone, N-octadecyl-α-heptadecylnitrone, 3-arylbenzofuran-2(3H)-one, 3-(alkoxyphenyl)benzofuran-2-one, 3-(acyloxyphenyl)benzofuran-2(3H)-one, and 5,7-di-ter Examples of benzofuran compounds include t-butyl-3-(3,4-dimethylphenyl)-benzofuran-2(3H)-one, 5,7-di-tert-butyl-3-(4-hydroxyphenyl)-benzofuran-2(3H)-one, 5,7-di-tert-butyl-3-{4-(2-hydroxyethoxy)phenyl}-benzofuran-2(3H)-one, 6-(2-(4-(5,7-di-tert-2-oxo-2,3-dihydrobenzofuran-3-yl)phenoxy)ethoxy)-6-oxohexyl-6-((6-hydroxyhexanoyl)oxy)hexanoate, and 5-di-tert-butyl-3-(4-((15-hydroxy-3,6,9,13-tetraoxapentadecyl)oxy)phenyl)benzofuran-2(3H)one.

[0049] Examples of hindered amine compounds include 2,2,6,6-tetramethyl-4-piperidyl stearate, 1,2,2,6,6-pentamethyl-4-piperidyl stearate, 2,2,6,6-tetramethyl-4-piperidyl benzoate, bis(2,2,6,6-tetramethyl-4-piperidyl) sebacate, tetrakis(2,2,6,6-tetramethyl-4-piperidyl)-1,2,3,4-butanetetracarboxylate, tetrakis(1,2,2,6,6-pentamethyl-4-piperidyl)-1,2,3,4-butanetetracarboxylate, and bi Su(2,2,6,6-tetramethyl-4-piperidyl) di(tridecyl)-1,2,3,4-butanetetracarboxylate, bis(1,2,2,6,6-pentamethyl-4-piperidyl) di(tridecyl)-1,2,3,4-butanetetracarboxylate, bis(1,2,2,4,4-pentamethyl-4-piperidyl)-2-butyl-2-(3,5-di-tert-butyl-4-hydroxybenzyl)malonate, 1-(2-hydroxyethyl)-2,2,6,6-tetramethyl-4-piperidinol / diethyl succinate polycondensate, 1,6-bis( 2,2,6,6-tetramethyl-4-piperidylamino)hexane / 2,4-dichloro-6-morpholino-s-triazine polycondensate, 1,6-bis(2,2,6,6-tetramethyl-4-piperidylamino)hexane / 2,4-dichloro-6-tert-octylamino-s-triazine polycondensate, 1,5,8,12-tetrakis[2,4-bis(N-butyl-N-(2,2,6,6-tetramethyl-4-piperidyl)amino)-s-triazine-6-yl]-1,5,8,12-tetraazadodecane, 1,5,8,12-tetrakis[2,4-bis(N- Butyl-N-(1,2,2,6,6-pentamethyl-4-piperidyl)amino)-s-triazine-6-yl]-1,5,8-12-tetraazadodecane, 1,6,11-tris[2,4-bis(N-butyl-N-(2,2,6,6-tetramethyl-4-piperidyl)amino)-s-triazine-6-ylamino]undecane, 1,6,11-tris[2,4-bis(N-butyl-N-(1,2,2,6,6-pentamethyl-4-piperidyl)amino)-s-triazine-6-ylamino]undecane, 3,9-bis[1,1-dimethyl-2-{tris(2,Examples include 2,6,6-tetramethyl-4-piperidyloxycarbonyl)butylcarbonyloxyethyl]-2,4,8,10-tetraoxaspiro[5.5]undecane, 3,9-bis[1,1-dimethyl-2-{tris(1,2,2,6,6-pentamethyl-4-piperidyloxycarbonyl)butylcarbonyloxy}ethyl]-2,4,8,10-tetraoxaspiro[5.5]undecane, bis(1-undecyloxy-2,2,6,6-tetramethylpiperidine-4-yl)carbonate, 2,2,6,6-tetramethyl-4-piperidylhexadecanoate, and 2,2,6,6-tetramethyl-4-piperidyloctadecanoate.

[0050] Examples of UV absorbers include 2-hydroxybenzophenones such as 2,4-dihydroxybenzophenone and 5,5'-methylenebis(2-hydroxy-4-methoxybenzophenone); 2-(2-hydroxy-5-methylphenyl)benzotriazole, 2-(2-hydroxy-5-tert-octylphenyl)benzotriazole, 2-(2-hydroxy-3,5-di-tert-butylphenyl)-5-chlorobenzotriazole, 2-(2-hydroxy-3-tert-butyl-5-methylphenyl)-5-chlorobenzotriazole, 2-( 2-Hydroxy-3,5-Dicumylphenyl)benzotriazole, 2,2'-Methylenebis(4-tert-octyl-6-benzotriazolylphenol), polyethylene glycol ester of 2-(2-hydroxy-3-tert-butyl-5-carboxyphenyl)benzotriazole, 2-[2-Hydroxy-3-(2-acryloyloxyethyl)-5-methylphenyl]benzotriazole, 2-[2-Hydroxy-3-(2-methacryloyloxyethyl)-5-tert-butylphenyl]benzotriazole, 2-[2-Hydroxy- 3-(2-methacryloyloxyethyl)-5-tert-octylphenyl]benzotriazole, 2-[2-hydroxy-3-(2-methacryloyloxyethyl)-5-tert-butylphenyl]-5-chlorobenzotriazole, 2-[2-hydroxy-5-(2-methacryloyloxyethyl)phenyl]benzotriazole, 2-[2-hydroxy-3-tert-butyl-5-(2-methacryloyloxyethyl)phenyl]benzotriazole, 2-[2-hydroxy-3-tert-amyl-5-(2-methacryloyloxyethyl) 2-(2-hydroxyphenyl)benzotriazoles such as phenyl]benzotriazole, 2-[2-hydroxy-3-tert-butyl-5-(3-methacryloyloxypropyl)phenyl]-5-chlorobenzotriazole, 2-[2-hydroxy-4-(2-methacryloyloxymethyl)phenyl]benzotriazole, 2-[2-hydroxy-4-(3-methacryloyloxy-2-hydroxypropyl)phenyl]benzotriazole, and 2-[2-hydroxy-4-(3-methacryloyloxypropyl)phenyl]benzotriazole;Phenyl salicylate, resorcinol monobenzoate, 2,4-di-tert-butylphenyl-3,5-di-tert-butyl-4-hydroxybenzoate, octyl(3,5-di-tert-butyl-4-hydroxy)benzoate, dodecyl(3,5-di-tert-butyl-4-hydroxy)benzoate, tetradecyl(3,5-di-tert-butyl-4-hydroxy)benzoate, hexadecyl(3,5-di-tert-butyl-4-hydroxy) Benzoates such as benzoate, octadecyl(3,5-di-tert-butyl-4-hydroxy)benzoate, behenyl(3,5-di-tert-butyl-4-hydroxy)benzoate; substituted oxanilides such as 2-ethyl-2'-ethoxyoxanilide, 2-ethoxy-4'-dodecyloxanilide; cyanoacrylates such as ethyl-α-cyano-β,β-diphenylacrylate, methyl-2-cyano-3-methyl-3-(p-methoxyphenyl)acrylate. Rates; 2-(4,6-diphenyl-1,3,5-triazine-2-yl)-5-hexyloxyphenol, 2-(2-hydroxy-4-octoxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine, trioctyl-2,2',2”-((1,3,5-triazine-2,4,6-triyl)tris(3-hydroxybenzene-4-,1-diyl)tripropionate), 2-(4,6-diphenyl-1,3,5-triazine-2- Examples include triazines such as (yl)-5-[2-(2-ethylhexanoyloxy)ethoxy]phenol, 2,4,6-tris(2-hydroxy-4-hexyloxy-3-methylphenyl)-1,3,5-triazine, and 1,12-bis[2-[4-(4,6-diphenyl-1,3,5-triazine-2-yl)-3-hydroxyphenoxy]ethyl]dodecanediate; various metal salts or metal chelates, especially nickel and chromium salts or chelates.

[0051] Examples of fatty acid metal salts other than hydroxyl group-containing lithium fatty acid salts include metal salts of fatty acids having 12 to 30 carbon atoms, including linear or branched fatty acid residues. Examples of metal ions constituting fatty acid metal salts include sodium ions, potassium ions, lithium ions, dihydroxyaluminum ions, calcium ions, zinc ions, barium ions, magnesium ions, and hydroxyaluminum ions, among which sodium ions, potassium ions, lithium ions, and calcium ions are preferred. Examples of fatty acids constituting fatty acid metal salts include lauric acid, myristic acid, palmitic acid, stearic acid, oleic acid, linoleic acid, linolenic acid, arachidic acid, arachidonic acid, behenic acid, lignoceric acid, cerotic acid, montanic acid, and melissic acid, among which myristic acid and stearic acid are preferred.

[0052] Examples of flame retardants include triphenyl phosphate, tricresyl phosphate, trixylenyl phosphate, cresyl diphenyl phosphate, cresyl-2,6-dixylenyl phosphate, resorcinol bis(diphenyl phosphate), (1-methylethylidene)-4,1-phenylenetetraphenyl diphosphate, 1,3-phenylenetetrakis(2,6-dimethylphenyl) phosphate, and ADEKA Corporation's product names "ADEKA Stab FP-500", "ADEKA Stab FP-600", and "ADEKA Stab Tab FP-800 contains aromatic phosphate esters, phosphonic acid esters such as divinyl phenylphosphonate, diallyl phenylphosphonate, and phenylphosphonic acid (1-butenyl), phosphinic acid esters such as phenyl diphenylphosphinate, methyl diphenylphosphinate, and 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide derivatives, phosphazene compounds such as bis(2-allylphenoxy)phosphazene and dicresylphosphazene, melamine phosphate, melamine pyrophosphate, and melamine polyphosphate. Phosphorus-based flame retardants such as ammonium polyphosphate, ammonium polyphosphate, piperazine phosphate, piperazine pyrophosphate, piperazine polyphosphate, phosphorus-containing vinylbenzyl compounds and red phosphorus, metal hydroxides such as magnesium hydroxide and aluminum hydroxide, brominated bisphenol A type epoxy resin, brominated phenol novolac type epoxy resin, hexabromobenzene, pentabromotoluene, ethylenebis(pentabromopenyne), ethylenebistetrabromophthalimide, 1,2-dibromo-4-(1,2-dibromoethin Examples of brominated flame retardants include cyclohexane, tetrabromocyclooctane, hexabromocyclododecane, bis(tribromophenoxy)ethane, brominated polyphenylene ether, brominated polystyrene, and 2,4,6-tris(tribromophenoxy)-1,3,5-triazine, tribromophenylmaleimide, tribromophenyl acrylate, tribromophenyl methacrylate, tetrabromobisphenol A type dimethacrylate, pentabromobenzyl acrylate, and brominated styrene. These flame retardants are preferably used in combination with drip inhibitors such as fluororesins and flame retardant additives such as polyhydric alcohols and hydrotalcite.

[0053] Examples of lubricants include unsaturated fatty acid amides such as oleamide and erucamide; saturated fatty acid amides such as behenamide and stearamide; butyl stearate; stearyl alcohol; monoglyceride stearate; sorbitan monopalmitate; sorbitan monostearate; mannitol; stearic acid; hydrogenated castor oil; stearin amide; oleamide; ethylenebisstearate amide, etc.

[0054] Examples of fillers include talc, mica, calcium carbonate, calcium oxide, calcium hydroxide, magnesium carbonate, magnesium hydroxide, magnesium oxide, magnesium sulfate, aluminum hydroxide, barium sulfate, glass powder, glass fibers, clay, dolomite, silica, alumina, potassium titanate whiskers, wollastonite, and fibrous magnesium oxysulfate. The particle size (or fiber diameter, fiber length, and aspect ratio in the case of fibrous materials) can be appropriately selected. Among these fillers, talc is particularly preferred because it provides excellent rigidity and is readily available. Furthermore, the filler may be surface-treated as needed.

[0055] Examples of antistatic agents include low-molecular-weight antistatic agents such as nonionic, anionic, cationic, or amphoteric surfactants, and high-molecular-weight antistatic agents such as polymer compounds. Examples of nonionic surfactants include polyethylene glycol-type nonionic surfactants such as higher alcohol ethylene oxide adducts, fatty acid ethylene oxide adducts, higher alkylamine ethylene oxide adducts, and polyolefin glycol ethylene oxide adducts; and polyhydric alcohol-type nonionic surfactants such as fatty acid esters of polyethylene oxide and glycerin, fatty acid esters of pentaerythritol, fatty acid esters of sorbitol or sorbitan, alkyl ethers of polyhydric alcohols, and aliphatic amides of alkanolamines. Examples of anionic surfactants include carboxylates such as alkali metal salts of higher fatty acids; sulfate esters such as higher alcohol sulfates and higher alkyl ether sulfates; sulfonates such as alkylbenzene sulfonates, alkyl sulfonates, and paraffin sulfonates; and phosphate esters such as higher alcohol phosphates. Examples of cationic surfactants include quaternary ammonium salts such as alkyltrimethylammonium salts. Examples of amphoteric surfactants include amino acid-type amphoteric surfactants such as higher alkylaminopropionates, and betaine-type amphoteric surfactants such as higher alkyldimethyl betaine and higher alkyldihydroxyethyl betaine. Among these, anionic surfactants are preferred, and sulfonates such as alkylbenzene sulfonates, alkyl sulfonates, and paraffin sulfonates are particularly preferred.

[0056] Examples of polymeric antistatic agents include ionomers and block polymers with polyethylene glycol as the hydrophilic portion. An example of an ionomer is the ionomer described in Japanese Patent Publication No. 2010-132927. Examples of polymers with polyethylene glycol as the hydrophilic portion include the polyether ester amide described in Japanese Patent Publication No. 7-10989, the polymer consisting of polyolefin and polyethylene glycol described in U.S. Patent No. 6,552,131, and the polymer consisting of polyester and polyethylene glycol described in Japanese Patent Publication No. 2016-023254.

[0057] Fluorescent whitening agents are compounds that enhance the whiteness and blueness of molded products through fluorescence, which occurs when they absorb ultraviolet light from sunlight or artificial light and radiate it as visible light ranging from purple to blue. Examples of fluorescent whitening agents include benzoxazole compounds (CIFluorescent Brightener 184), coumarin compounds (CIFluorescent Brightener 52), and diaminostilbenndisulfonic acid compounds (CIFluorescent Brightener 24, 85, 71).

[0058] The pigments are not particularly limited, and commercially available pigments can also be used. Specific examples of pigments include, for example, Pigment Red 1, 2, 3, 9, 10, 17, 22, 23, 31, 38, 41, 48, 49, 88, 90, 97, 112, 119, 122, 123, 144, 149, 166, 168, 169, 170, 171, 177, 179, 180, 184, 185, 192, 200, 202, 209, 215, 216, 217, 220, 223, 224, 226, 227, 228, 240, 254; Pigment Orange 13, 31, 34, 36, 38, 43, 46, 48, 49, 51, 52, 55, 59, 60, 61, 62, 64, 65, 71; Pigment Yellow 1, 3, 12, 13, 14 ,16,17,20,24,55,60,73,81,83,86,93,95,97,98,100,109,110,113,114,117,120,125,126,127,129,137,138,139,147,148,150,151,152,153,154,166,168,175, Examples include 180, 185; pigment green 7, 10, 36; pigment blue 15, 15:1, 15:2, 15:3, 15:4, 15:5, 15:6, 22, 24, 29, 56, 60, 61, 62, 64; and pigment violet 1, 15, 19, 23, 27, 29, 30, 32, 37, 40, 50.

[0059] Examples of dyes include azo dyes, anthraquinone dyes, indigoid dyes, triarylmethane dyes, xanthene dyes, alizarin dyes, acridine dyes, stilbene dyes, thiazole dyes, naphthol dyes, quinoline dyes, nitro dyes, indamine dyes, oxazine dyes, phthalocyanine dyes, cyanine dyes, and others.

[0060] The additive composition of this embodiment may also be a one-pack composite additive that has been granulated by further blending a binder, wax, solvent, silica, or other granulation aid. Alternatively, the additive composition of this embodiment may also be a masterbatch containing a polyolefin resin.

[0061] Examples of polyolefin resins included in the masterbatch include polyethylene resins such as low-density polyethylene, linear low-density polyethylene, high-density polyethylene, crosslinked polyethylene, and ultra-high molecular weight polyethylene; polypropylene resins such as homopolypropylene, random copolymer polypropylene, block copolymer polypropylene, impact copolymer polypropylene, high-impact copolymer polypropylene, and maleic anhydride-modified polypropylene; α-olefin polymers such as polybutene-1, cycloolefin polymer, poly-3-methyl-1-butene, poly-3-methyl-1-pentene, and poly-4-methyl-1-pentene; and α-olefin copolymers such as ethylene-methyl methacrylate copolymer and ethylene-vinyl acetate copolymer. These polyolefin resins may be used individually or in combination of two or more. The polyolefin resins may also be alloyed. Among these, polypropylene resins are particularly preferred as the polyolefin resins included in the masterbatch. The molecular weight, degree of polymerization, density, softening point, proportion of insoluble matter in the solvent, degree of stereoregularity, presence or absence of catalyst residue, type and blending ratio of monomers used as raw materials, and type of catalyst used for polymerization (e.g., Ziegler catalyst, metallocene catalyst, etc.) of the polyolefin resin are not particularly limited and are selected as appropriate.

[0062] When the additive composition is a masterbatch containing a polyolefin resin, the content of the polyolefin resin in the masterbatch may be, for example, 90% by mass or less, preferably 80% by mass or less, and more preferably 60% by mass or less. Alternatively, the content of the polyolefin resin in the masterbatch may be, for example, 20% by mass or more.

[0063] Next, the resin composition according to this embodiment will be described. <Resin composition> The resin composition of this embodiment comprises a polyolefin resin, (A) a nucleating agent, (B) a hydroxyl group-containing lithium fatty acid salt, and (C) hydrotalcite. Here, (A) the nucleating agent includes an organic oxo acid metal salt. The content of (B) the hydroxyl group-containing lithium fatty acid salt is 25 to 400 parts by mass per 100 parts by mass of (A) the nucleating agent, and the content of (C) hydrotalcite is 25 to 400 parts by mass per 100 parts by mass of (A) the nucleating agent. Furthermore, the content of (A) the nucleating agent is 0.001 to 10 parts by mass per 100 parts by mass of the polyolefin resin. According to the resin composition of this embodiment, molded articles with excellent mechanical properties can be obtained.

[0064] The polyolefin resin included in the resin composition of this embodiment is the same as that included in the masterbatch described above. Among these, polypropylene resin is preferred. In this case, the molded article will have excellent heat resistance. Furthermore, from the viewpoint of improving the rigidity and impact resistance of the molded article, it is preferable that 90% by mass or more of the monomer units constituting the polypropylene resin are propylene units. From the viewpoint of further improving the rigidity and impact resistance of the molded article, it is more preferable that 95% by mass or more of the monomer units constituting the polypropylene resin are propylene units, even more preferable that 99% by mass or more of the monomer units constituting the polypropylene resin are propylene units, and particularly preferable that 100% by mass of the monomer units constituting the polypropylene resin are propylene units, i.e., the polypropylene resin is homopolypropylene. Furthermore, from the viewpoint of improving the rigidity and impact resistance of the molded article, the melt flow rate of the polypropylene resin at a cylinder temperature of 230°C and a load of 2.16 kg is preferably 40 g / 10 min or less, more preferably 10 g / 10 min or less, and even more preferably 5 g / 10 min or less. Furthermore, the melt flow rate of the polypropylene resin at a cylinder temperature of 230°C and a load of 2.16 kg is preferably 0.1 g / 10 min or more, more preferably 1 g / 10 min or more, and even more preferably 2 g / 10 min or more.

[0065] The (A) nucleating agent, (B) hydroxyl group-containing fatty acid lithium salt, and (C) hydrotalcite contained in the resin composition of this embodiment are the same as those contained in the additive composition described above. As described above, the content of (B) hydroxyl group-containing fatty acid lithium salt per 100 parts by mass of (A) nucleating agent is 25 to 400 parts by mass. From the viewpoint of obtaining a molded product with better rigidity and impact resistance, the content of (B) hydroxyl group-containing fatty acid lithium salt per 100 parts by mass of (A) nucleating agent is preferably 33 parts by mass or more, and more preferably 50 parts by mass or more. Also, from the same viewpoint, the content of (B) hydroxyl group-containing fatty acid lithium salt per 100 parts by mass of (A) nucleating agent is preferably 200 parts by mass or less, and more preferably 100 parts by mass or less.

[0066] Furthermore, as mentioned above, the content of (C) hydrotalcites per 100 parts by mass of (A) nucleating agent is 25 to 400 parts by mass. From the viewpoint of obtaining a molded product with superior rigidity, the content of (C) hydrotalcites per 100 parts by mass of (A) nucleating agent is preferably 50 parts by mass or more, and more preferably 100 parts by mass or more. Also, from the same viewpoint, the content of (C) hydrotalcites per 100 parts by mass of (A) nucleating agent is preferably 200 parts by mass or less, and more preferably 150 parts by mass or less.

[0067] The content of (C) hydrotalcites per 100 parts by mass of (B) hydroxyl group-containing fatty acid lithium salt is not particularly limited, and may be, for example, 10 to 1000 parts by mass. From the viewpoint of obtaining molded articles with better rigidity and impact resistance, the content of (C) hydrotalcites per 100 parts by mass of (B) hydroxyl group-containing fatty acid lithium salt is preferably 20 to 500 parts by mass, and more preferably 25 to 400 parts by mass.

[0068] As described above, in the resin composition of this embodiment, the content of (A) nucleating agent per 100 parts by mass of polyolefin resin is 0.001 to 10 parts by mass. If the content of (A) nucleating agent per 100 parts by mass of polyolefin resin is less than 0.001 parts by mass, a molded product with sufficient mechanical properties cannot be obtained. Also, if the content of (A) nucleating agent per 100 parts by mass of polyolefin resin exceeds 10 parts by mass, bloom may occur on the surface of the molded product or migration of (A) nucleating agent may occur. From the viewpoint of providing excellent rigidity and impact resistance of the molded product and sufficiently suppressing bloom and migration of (A) nucleating agent, the content of (A) nucleating agent per 100 parts by mass of polyolefin resin is preferably 0.005 to 5 parts by mass, more preferably 0.01 to 1 part by mass, even more preferably 0.01 to 0.5 parts by mass, and even more preferably 0.02 to 0.2 parts by mass. Furthermore, in the resin composition of this embodiment, the content of (B) hydroxyl group-containing fatty acid lithium salt per 100 parts by mass of polyolefin resin may be, for example, 0.001 to 10 parts by mass, preferably 0.005 to 5 parts by mass, more preferably 0.01 to 1 part by mass, even more preferably 0.01 to 0.5 parts by mass, and even more preferably 0.02 to 0.2 parts by mass. Furthermore, in the resin composition of this embodiment, the content of (C) hydrotalcites per 100 parts by mass of polyolefin resin may be, for example, 0.001 to 10 parts by mass, preferably 0.005 to 5 parts by mass, more preferably 0.01 to 1 part by mass, even more preferably 0.01 to 0.5 parts by mass, and even more preferably 0.02 to 0.2 parts by mass.

[0069] The resin composition of this embodiment may comprise a polyolefin resin and the above-mentioned additive composition, wherein the content of the additive composition per 100 parts by mass of the polyolefin resin may be 0.001 to 10 parts by mass.

[0070] Furthermore, the resin composition of this embodiment may optionally contain various additives such as phenolic antioxidants, phosphorus-based antioxidants, sulfur-based antioxidants, other antioxidants, hindered amine compounds, ultraviolet absorbers, fatty acid metal salts other than hydroxyl group-containing fatty acid lithium salts, flame retardants, flame retardant aids, lubricants, fillers, antistatic agents, fluorescent whitening agents, pigments, and dyes. Examples of these various additives are the same as those exemplified as additives that may be included in the additive composition described above.

[0071] Next, a method for producing the resin composition according to this embodiment will be described. <Method for producing resin compositions> The method for producing the resin composition of this embodiment includes a step of blending the above-described additive composition with a polyolefin resin. The method for producing the resin composition of this embodiment may include steps other than the step of blending the above-described additive composition with a polyolefin resin. For example, it may include a preparatory step of preparing the polyolefin resin, the additive composition, and other optional additives in advance.

[0072] According to the resin composition produced by the method for producing the resin composition of this embodiment, a molded article with excellent mechanical properties can be obtained.

[0073] (preparation process) First, prepare the polyolefin resin and the additive composition described above.

[0074] (Blending process) Next, the additive composition is blended into the polyolefin resin. The blending method is not particularly limited, and examples include adding the polyolefin resin, the additive composition, and the various additives mentioned above as needed, and then mixing them using a mixing device such as a Henschel mixer, mill roll, Banbury mixer, or super mixer. Here, at least one component of the additive composition and the various additives mentioned above may be added before or during the polymerization of the polyolefin resin monomer or oligomer, and the remaining components may be added to the resulting polymer.

[0075] The resin composition is manufactured as described above. The method for manufacturing the resin composition may include a step of blending a polyolefin resin with (A) a nucleating agent, (B) a hydroxyl group-containing fatty acid lithium salt, (C) hydrotalcites, and, if necessary, the various additives described above. The method for manufacturing the resin composition may also include a melt-kneading step in which the mixture obtained by the above method is further melt-kneaded using a melt-kneading apparatus such as a single-screw extruder or a twin-screw extruder. Here, the melt-kneading temperature may be, for example, 220 to 280°C. Furthermore, the method for manufacturing the resin composition may also include a granulation step in which the kneaded product obtained by melt-kneading is granulated. The method of granulation is not particularly limited, and examples include using a granulation apparatus such as a pelletizer. The shape of the resin composition obtained by granulation is not particularly limited, and may be, for example, pelletized.

[0076] Next, embodiments of the molded article of the present invention will be described. <Molded products> The molded article of this embodiment is obtained by molding the resin composition described above. This molded article has excellent mechanical properties.

[0077] Examples of molded products in this embodiment include injection molded products, fibers, flat yarn, biaxially oriented films, uniaxially oriented films, unoriented films, sheets, thermoforming molded products, extruded blow molded products, injection blow molded products, injection stretched blow molded products, shaped extruded products, rotationally molded products, etc. More specifically, examples include automobile exterior parts, automobile interior parts, housings, containers, piping, etc. Examples of automotive exterior parts include bumpers, radiator grilles, front grilles, front panels, fenders, pillars, pillar covers, door mirror stay covers, glass run channels, door mirror housings, lamp housings, wheel covers, spoilers, air spoilers, weatherstrips, window moldings, belt moldings, sunroofs, front end modules, door modules, back door modules, and body panels. Examples of automotive interior parts include instrument panels, door trim panels, pillar trims, door trims, pillar garnishes, package trays, rear trays, console boxes, and air conditioning ducts. Examples of enclosures include home appliance enclosures, arcade game machine enclosures, home game console enclosures, portable game console enclosures, camera enclosures, and mobile phone enclosures. Examples of containers include smartphone casings, electronic device casings, secondary battery casings, and safety breaker casings. Examples of containers include tableware, prepared food containers, frozen food containers, microwave oven heat-resistant containers, frozen storage containers, retort containers, cups, frozen dessert cups and other food containers, beverage bottles, infusion bottles, medical hollow bottles and other bottle containers, physicochemical test containers such as beakers and graduated cylinders, pharmaceutical containers, medical containers, detergent containers, cosmetic containers, perfume containers, and toner containers. Examples of piping include water pipes, gas pipes, infrastructure pipes, factory utility pipes, vehicle fuel delivery pipes, vehicle air intake pipes and other various pipes, cosmetic / perfume spray tubes, medical tubes, infusion tubes and other various tubes, water hoses, vehicle air duct hoses and other various hoses.

[0078] The molding method for the molded product of the present invention is not particularly limited and includes methods such as injection molding, extrusion molding, blow molding, rotational molding, vacuum molding, inflation molding, calendering, slush molding, dip molding, and thermoforming. [Examples]

[0079] The present invention will be described in more detail below with reference to examples, but the present invention is not limited in any way by the following examples.

[0080] The polyolefin resin, (A) nucleating agent, (B) hydroxyl group-containing fatty acid lithium salt, and (C) hydrotalcite used in this example are as follows.

[0081] <Polyolefin resins> (P-1): Melt flow rate of 3g / 10min of homopolypropylene at cylinder temperature of 230℃ and load of 2.16kg. <(A) Nuclear agent> (A-1) Sodium 2,2'-methylenebis(4,6-di-tert-butylphenyl)phosphate (A-2) Hydroxyaluminum bis[2,2'-methylenebis(4,6-di-tert-butylphenyl)phosphate] (A-3) Sodium benzoate (A-4) Bis(4-t-butylbenzoate)hydroxyaluminum (A-5) Disodium 2,3-norbornanedicarboxylate (A-6) Calcium 1,2-cyclohexanedicarboxylate <(B) Lithium salt of hydroxyl group-containing fatty acid> (B-1)12-Lithium Hydroxystearate (C) Hydrotalcite (C-1) Hydrotalcite manufactured by Kyowa Chemical Industry Co., Ltd., product name "DHT-4V"

[0082] <Preparation of resin composition> (Examples 1-68, Reference Examples 1 and 2) To 100 parts by mass of polyolefin resin, the following were added: (A) nucleating agent, (B) hydroxyl group-containing fatty acid lithium salt, and (C) hydrotalcites as listed in Tables 1 to 13 in the amounts specified in Tables 1 to 13; 0.05 parts by mass of a phenolic antioxidant (tetrakis[methylene-3-(3',5'-tert-butyl-4'-hydroxyphenyl)propionate]methane); 0.1 parts by mass of a phosphorus-based antioxidant (tris(2,4-di-tert-butylphenyl)phosphite); and 0.05 parts by mass of a fatty acid metal salt (calcium stearate). The mixture was then mixed for 1 minute at a rotation speed of 1000 rpm using a Henschel mixer (FM200, manufactured by Mitsui Mining Co., Ltd.). The resulting mixture was melt-kneaded using a twin-screw extruder (TEX-28V, manufactured by Japan Steel Works, Ltd.) under processing conditions of a melting temperature of 230°C and a screw speed of 150 rpm, and then granulated to obtain pellets. The obtained pellets were dried at 60°C for 8 hours before being used for characterization. In Tables 1-13, the unit of composition is parts by mass.

[0083] (Comparative Example 1) A pellet of Comparative Example 1 was obtained in the same manner as in Example 57, except that (A) the nucleating agent, (B) the hydroxyl group-containing lithium fatty acid salt, and (C) hydrotalcites were not included.

[0084] (Comparative Example 2) A pellet for Comparative Example 2 was obtained in the same manner as in Example 57, except that (B) hydroxyl group-containing lithium fatty acid salt and (C) hydrotalcite were not included.

[0085] (Comparative Example 3) (B) A pellet of Comparative Example 3 was obtained in the same manner as in Example 57, except that a lithium salt containing a hydroxyl group was not included.

[0086] (Comparative Example 4) A pellet of Comparative Example 4 was obtained in the same manner as in Example 57, except that (b) lithium stearate (b-1) was added as a lithium fatty acid salt that does not contain a hydroxyl group, instead of (b) lithium fatty acid salt containing a hydroxyl group.

[0087] (Comparative Example 5) A pellet of Comparative Example 5 was obtained in the same manner as in Example 57, except that (c) hydrotalcite was replaced with (c-1) talc manufactured by Hayashi Chemical Co., Ltd. (product name: Micron White 5000S) as talc.

[0088] <Characteristic Evaluation> (Flexural modulus) After drying the pellets from Examples 1-68, Reference Examples 1 and 2, and Comparative Examples 1-5 at 60°C for 8 hours, they were molded using an injection molding machine (Toshiba Machine Co., Ltd. EC-220) under conditions of resin temperature 230°C and mold temperature 50°C to create 80mm × 10mm × 4mm bending test specimens. These specimens were left to stand in a constant temperature and humidity chamber at 23°C and 50% humidity for 168 hours, and then the bending modulus of elasticity (MPa) of the specimens was measured using a bending tester (Shimadzu Corporation AG-IS) in accordance with ISO 178. The results are shown in Tables 1-14.

[0089] (Charpy impact strength) After drying the pellets from Examples 1-68, Reference Examples 1 and 2, and Comparative Examples 1-5 at 60°C for 8 hours, they were molded using an injection molding machine (NEX80, manufactured by Nissei Plastic Industrial Co., Ltd.) under conditions of resin temperature 230°C and mold temperature 50°C to produce 80mm x 10mm x 4mm Charpy impact strength test specimens with a V-shaped notch in the center. These test specimens were left standing in a constant temperature and humidity chamber at 23°C and 50% humidity for 168 hours, and then the Charpy impact strength (kJ / m²) of the test specimens was measured in accordance with ISO 179-1. 2 The following measurements were taken. The results are shown in Tables 1-14.

[0090] [Table 1]

[0091] [Table 2]

[0092] [Table 3]

[0093] Table 4

[0094] Table 5

[0095] Table 6

[0096] Table 7

[0097] Table 8

[0098] Table 9

[0099] Table 10

[0100] Table 11

[0101] Table 12

[0102] Table 13

[0103] [Table 14]

[0104] As shown in Tables 1-14, the molded articles obtained by molding the pellets of Examples 1-68 and Reference Examples 1 and 2 had excellent rigidity and impact resistance. On the other hand, the molded articles obtained by molding the pellets of Comparative Examples 1-5 did not have sufficient rigidity or impact resistance.

[0105] Based on the above, it has been confirmed that the additive composition of the present invention can impart excellent mechanical properties to molded articles.

Claims

1. (A) Nuclear agent and, (B) Lithium salt of hydroxyl group-containing fatty acid, (C) Hydrotalcites and Includes, The aforementioned (A) nucleating agent contains an organoxo acid metal salt, The content of (B) hydroxyl group-containing fatty acid lithium salt is 25 to 400 parts by mass per 100 parts by mass of (A) nucleating agent, The content of (C) hydrotalcites per 100 parts by mass of (A) nucleating agent is 25 to 400 parts by mass. The aforementioned metal oxoacid salt is at least one selected from the group consisting of aromatic phosphate ester metal salts and aromatic carboxylate metal salts. The aromatic phosphate ester metal salt includes a compound represented by the following general formula (1): An additive composition characterized by being for use with polyolefin resins. (In general formula (1), R1 to R5 each independently represent a hydrogen atom or an alkyl group having 1 to 6 carbon atoms, n represents 1 or 2, if n is 1, M represents an alkali metal, and if n is 2, M represents an alkaline earth metal or zinc.)

2. The additive composition according to claim 1, wherein the (B) hydroxyl group-containing fatty acid lithium salt comprises at least one selected from the group consisting of lithium hydroxystearate and lithium hydroxyoleate.

3. The above (C) hydrotalcite is the following general formula (2) or the following general formula (3), (In general formula (2), y1 and y2 represent numbers satisfying 0 ≤ y2 / y1 < 10 and 2 ≤ y1 + y2 ≤ 20, and p represents 0 or a positive number.) The additive composition according to claim 1 or 2, comprising a compound represented by the general formula (3) (wherein Aq- represents a q-valent anion, and p represents 0 or a positive number).

4. Polyolefin resins, (A) Nuclear agent and, (B) Lithium salt of hydroxyl group-containing fatty acid, (C) Hydrotalcites and Includes, The aforementioned (A) nucleating agent contains an organoxo acid metal salt, The content of (B) hydroxyl group-containing fatty acid lithium salt is 25 to 400 parts by mass per 100 parts by mass of (A) nucleating agent, The content of (C) hydrotalcites per 100 parts by mass of (A) nucleating agent is 25 to 400 parts by mass. The content of the nucleating agent (A) per 100 parts by mass of the polyolefin resin is 0.001 to 10 parts by mass. The aforementioned metal oxoacid salt is at least one selected from the group consisting of aromatic phosphate ester metal salts and aromatic carboxylate metal salts. A resin composition characterized in that the aromatic phosphate ester metal salt contains a compound represented by the following general formula (1). (In general formula (1), R1 to R5 each independently represent a hydrogen atom or an alkyl group having 1 to 6 carbon atoms, n represents 1 or 2, if n is 1, M represents an alkali metal, and if n is 2, M represents an alkaline earth metal or zinc.)

5. The resin composition according to claim 4, wherein the polyolefin resin is a polypropylene resin.

6. The resin composition according to claim 5, wherein 90% by mass or more of the monomer units constituting the polypropylene resin are propylene units.

7. A method for producing a resin composition, characterized by comprising the step of blending a polyolefin resin with an additive composition according to any one of claims 1 to 3.

8. A molded article characterized by being obtained by molding a resin composition according to any one of claims 4 to 6.

Images