Resin composition, molded article, and method for manufacturing the resin composition

Abstract

To provide a resin composition comprising a polycarbonate resin and a polyester resin, making it possible to prevent the occurrence of silver streaks during its residence and improve tensile nominal strain at break, a molding and a method for producing a resin composition.SOLUTION: The present invention provides a resin composition. Relative to 100 pts.maass of a resin (C) comprising 40-95 pts.mass of a polycarbonate resin (A) and 5-60 pts.mass of a polyester resin (B), the resin composition comprises 0.001-4 pts.mass of a phosphorous transesterification inhibitor (D). Furthermore, the polyester resin (B) comprises 0.80-8.00 mass ppm of Ca element.SELECTED DRAWING: None

Description

Technical Field

[0001] The present invention relates to a resin composition, a molded body, and a method for producing the resin composition.

Background Art

[0002] As a general-purpose engineering plastic, polycarbonate resin is excellent in transparency, mechanical strength, electrical properties, heat resistance, dimensional stability, etc., and is therefore used in a wide range of fields such as electrical and electronic equipment parts, OA equipment, mechanical parts, vehicle parts, building members, various containers, leisure goods, and miscellaneous goods. In addition, resin compositions blended with polyester resins such as polyethylene terephthalate (PET) are also widely used in order to improve the chemical resistance, solvent resistance, and fluidity of polycarbonate resin. Furthermore, inorganic fillers such as talc and mica are also blended in order to improve rigidity, heat resistance, and dimensional stability (low shrinkage, low linear expansion). While the resin composition as described above is excellent in fluidity and chemical resistance compared to ordinary polycarbonate resin, it is inferior in retention heat stability, and when manufacturing a large molded body such as an automobile exterior member by injection molding, appearance defects such as silver streaks (silver) may occur due to resin retention (Patent Documents 1 to 4).

Prior Art Documents

Patent Documents

[0003]

Patent Document 1

Patent Document 2

Patent Document 3

Patent Document 4

Summary of the Invention

Problems to be Solved by the Invention

[0004] As mentioned above, resin compositions consisting of polycarbonate resin and polyester resin possess excellent properties of polycarbonate resin, as well as superior fluidity and chemical resistance. However, suppressing the generation of silver during retention is a problem. Furthermore, to ensure toughness as an automotive exterior component, improvement in tensile fracture strain is required. The present invention aims to solve the aforementioned problems and to provide a resin composition comprising a polycarbonate resin and a polyester resin, wherein the generation of silver during retention is suppressed and the tensile fracture nominal strain is improved, as well as a molded article and a method for manufacturing the resin composition. [Means for solving the problem]

[0005] Based on the above problems, the inventors conducted research and found that the above problems can be solved by combining polycarbonate resin, polyester resin with a specific Ca concentration, and a phosphorus-based transesterification inhibitor. Specifically, the above problem was solved by the following means. <1> For 100 parts by mass of resin (C) containing 40 to 95 parts by mass of polycarbonate resin (A) and 5 to 60 parts by mass of polyester resin (B), It contains 0.001 to 4 parts by mass of a phosphorus-based transesterification inhibitor (D), Furthermore, the polyester resin (B) contains 0.80 to 8.00 ppm by mass of Ca element. Resin composition. <2> The polyester resin (B) contains 0.10 to 8.00 ppm by mass of Mg element. <1> The resin composition described above. <3> The polyester resin (B) contains 200 ppm or more of Sb element. <1> or <2> The resin composition described above. <4> The polyester resin (B) includes polyethylene terephthalate resin. <1> ~ <3> A resin composition as described in any one of the following. <5> The aforementioned polyethylene terephthalate resin includes recycled materials, <4> The resin composition described above. <6> The resin (C) comprises 100 parts by mass, and an inorganic filler (E) comprises 1 to 100 parts by mass. <1> ~ <5> A resin composition as described in any one of the following. <7> The inorganic filler (E) contains 0.10 parts by mass or more of the phosphorus-based transesterification inhibitor (D) per 100 parts by mass. <6> The resin composition described above. <8> The inorganic filler (E) includes one or more selected from the group consisting of glass fibers, glass flakes, carbon fibers, talc, mica, wollastonite, and kaolin. <6> ~ <7> A resin composition as described in any one of the following. <9> <1> ~ <8> A molded article formed from any one of the resin compositions described above. <10> A resin (C) comprising 40 to 95 parts by mass of polycarbonate resin (A) and 5 to 60 parts by mass of polyester resin (B), 100 parts by mass, This includes melt-kneading 0.001 to 4 parts by mass of a phosphorus-based transesterification inhibitor (D), The polyester resin (B) contains Ca element in a proportion of 0.80 to 8.00 ppm by mass. A method for producing a resin composition. <11> The resin composition is <1> ~ <8> A resin composition described in any one of the following: <10> A method for producing the resin composition described above. [Effects of the Invention]

[0006] The present invention provides a resin composition in which the generation of silver during retention is suppressed and the tensile fracture nominal strain is improved, as well as a molded article and a method for manufacturing the resin composition. [Modes for carrying out the invention]

[0007] The following describes in detail embodiments for carrying out the present invention (hereinafter simply referred to as "this embodiment"). Note that the following embodiment is illustrative for explaining the present invention, and the present invention is not limited to this embodiment. In this specification, "~" is used to mean that the numbers before and after it are included as the lower and upper limits, respectively. In this specification, all physical properties and characteristic values ​​shall be those at 23°C unless otherwise specified. In this specification, unless otherwise specified, weight-average molecular weight and number-average molecular weight are polystyrene-converted values ​​measured by GPC (gel permeation chromatography). In this specification, ppm means mass ppm. If the measurement methods, etc., described in the standards shown herein differ from year to year, unless otherwise specified, the standards as of January 1, 2022 shall apply.

[0008] The resin composition of this embodiment is characterized by containing 0.001 to 4 parts by mass of a phosphorus-based transesterification inhibitor (D) per 100 parts by mass of resin (C), which comprises 40 to 95 parts by mass of polycarbonate resin (A) and 5 to 60 parts by mass of polyester resin (B), and further, the polyester resin (B) contains 0.80 to 8.00 ppm by mass of Ca element. With this configuration, the generation of silver during retention is suppressed and a resin composition with improved tensile fracture nominal strain can be obtained. It was estimated that by including Ca element above the lower limit in the polyester resin, the transesterification between the polycarbonate resin and the polyester resin proceeded appropriately, improving the compatibility between the polyester resin and the polycarbonate resin and thus improving the tensile fracture nominal strain. Furthermore, it was estimated that by keeping the Ca element below the upper limit, excessive transesterification was suppressed, and the generation of silver during retention was suppressed. In addition, it is thought that including a phosphorus-based transesterification inhibitor (D) (preferably an organic phosphate compound) suppressed excessive transesterification, and the generation of silver during retention was suppressed. Embodiments of the present invention will be described below.

[0009] <Polycarbonate resin (A)> The resin composition of this embodiment includes a polycarbonate resin. There are no restrictions on the type of polycarbonate resin used in this embodiment, and one type may be used alone, or two or more types may be used in any combination and ratio. The polycarbonate resin is a polymer having a basic structure with a carbonate bond, represented by the general formula: -[-O-X-O-C(=O)-]-. In the formula, X is generally a hydrocarbon group, but X with heteroatoms or hetero bonds introduced for imparting various properties may also be used.

[0010] Also, the polycarbonate resin can be classified into an aromatic polycarbonate resin in which the carbons directly bonded to the carbonate bond are each aromatic carbon, and an aliphatic polycarbonate resin in which they are aliphatic carbon, and either can be used. Among them, from the viewpoints of heat resistance, mechanical properties, electrical properties, etc., an aromatic polycarbonate resin is preferred.

[0011] There is no limitation on the specific type of the polycarbonate resin. For example, a polycarbonate polymer obtained by reacting a dihydroxy compound with a carbonate precursor can be mentioned. At this time, in addition to the dihydroxy compound and the carbonate precursor, a polyhydroxy compound or the like may be reacted. Also, a method of reacting carbon dioxide as a carbonate precursor with a cyclic ether may be used. Further, the polycarbonate polymer may be linear or branched. Furthermore, the polycarbonate polymer may be a homopolymer composed of one kind of repeating unit, or a copolymer having two or more kinds of repeating units. At this time, for the copolymer, various copolymerization forms such as a random copolymer and a block copolymer can be selected. Usually, such a polycarbonate polymer becomes a thermoplastic resin.

[0012] Among the monomers that are raw materials for the aromatic polycarbonate resin, examples of the aromatic dihydroxy compound include dihydroxybenzenes such as 1,2-dihydroxybenzene, 1,3-dihydroxybenzene (that is, resorcinol), 1,4-dihydroxybenzene;

[0013] dihydroxybiphenyls such as 2,5-dihydroxybiphenyl, 2,2'-dihydroxybiphenyl, 4,4'-dihydroxybiphenyl;

[0014] Dihydroxynaphthalene compounds such as 2,2'-dihydroxy-1,1'-binaphthyl, 1,2-dihydroxynaphthalene, 1,3-dihydroxynaphthalene, 2,3-dihydroxynaphthalene, 1,6-dihydroxynaphthalene, 2,6-dihydroxynaphthalene, 1,7-dihydroxynaphthalene, and 2,7-dihydroxynaphthalene;

[0015] Dihydroxydiaryl ethers such as 2,2'-dihydroxydiphenyl ether, 3,3'-dihydroxydiphenyl ether, 4,4'-dihydroxydiphenyl ether, 4,4'-dihydroxy-3,3'-dimethyldiphenyl ether, 1,4-bis(3-hydroxyphenoxy)benzene, and 1,3-bis(4-hydroxyphenoxy)benzene;

[0016] 2,2-bis(4-hydroxyphenyl)propane (i.e., bisphenol A), 1,1-Bis(4-hydroxyphenyl)propane, 2,2-Bis(3-methyl-4-hydroxyphenyl)propane (i.e., bisphenol C), 2,2-bis(3-methoxy-4-hydroxyphenyl)propane, 2-(4-hydroxyphenyl)-2-(3-methoxy-4-hydroxyphenyl)pro bread, 1,1-Bis(3-tert-butyl-4-hydroxyphenyl)propane, 2,2-bis(3,5-dimethyl-4-hydroxyphenyl)propane, 2,2-Bis(3-cyclohexyl-4-hydroxyphenyl)propane, 2-(4-hydroxyphenyl)-2-(3-cyclohexyl-4-hydroxyphenyl )propane, α,α'-bis(4-hydroxyphenyl)-1,4-diisopropylbenzene, 1,3-bis[2-(4-hydroxyphenyl)-2-propyl]benzene, Bis(4-hydroxyphenyl)methane, Bis(4-hydroxyphenyl)cyclohexylmethane, Bis(4-hydroxyphenyl)phenylmethane, Bis(4-hydroxyphenyl)(4-propenylphenyl)methane, Bis(4-hydroxyphenyl)diphenylmethane, Bis(4-hydroxyphenyl)naphthylmethane, 1,1-bis(4-hydroxyphenyl)ethane, 1,1-bis(4-hydroxyphenyl)-1-phenylethane, 1,1-bis(4-hydroxyphenyl)-1-naphthylethane, 1,1-Bis(4-hydroxyphenyl)butane, 2,2-bis(4-hydroxyphenyl)butane, 2,2-bis(4-hydroxyphenyl)pentane, 1,1-Bis(4-hydroxyphenyl)hexane, 2,2-bis(4-hydroxyphenyl)hexane, 1,1-bis(4-hydroxyphenyl)octane, 2,2-bis(4-hydroxyphenyl)octane, 4,4-bis(4-hydroxyphenyl)heptane, 2,2-bis(4-hydroxyphenyl)nonane, 1,1-bis(4-hydroxyphenyl)decane, 1,1-Bis(4-hydroxyphenyl)dodecane, Bis(hydroxyaryl)alkanes such as;

[0017] 1,1-Bis(4-hydroxyphenyl)cyclopentane, 1,1-Bis(4-hydroxyphenyl)cyclohexane, 1,1-bis(4-hydroxyphenyl)-3,3-dimethylcyclohexane, 1,1-bis(4-hydroxyphenyl)-3,4-dimethylcyclohexane, 1,1-bis(4-hydroxyphenyl)-3,5-dimethylcyclohexane, 1,1-bis(4-hydroxyphenyl)-3,3,5-trimethylcyclohexane, 1,1-Bis(4-hydroxy-3,5-dimethylphenyl)-3,3,5-trimethylcyclohexane, 1,1-Bis(4-hydroxyphenyl)-3-propyl-5-methylcyclohexane, 1,1-Bis(4-hydroxyphenyl)-3-tert-butyl-cyclohexane, 1,1-Bis(4-hydroxyphenyl)-4-tert-butyl-cyclohexane, 1,1-bis(4-hydroxyphenyl)-3-phenylcyclohexane, 1,1-Bis(4-hydroxyphenyl)-4-phenylcyclohexane, Bis(hydroxyaryl)cycloalkanes such as;

[0018] 9,9-Bis(4-hydroxyphenyl)fluorene, Bisphenols containing cardo structures, such as 9,9-bis(4-hydroxy-3-methylphenyl)fluorene;

[0019] 4,4'-Dihydroxydiphenyl sulfide, Dihydroxydiaryl sulfides such as 4,4'-dihydroxy-3,3'-dimethyldiphenyl sulfide;

[0020] Dihydroxydiaryl sulfoxides such as 4,4'-dihydroxydiphenyl sulfoxide and 4,4'-dihydroxy-3,3'-dimethyldiphenyl sulfoxide;

[0021] 4,4'-Dihydroxydiphenylsulfone, Dihydroxydiarylsulfones such as 4,4'-dihydroxy-3,3'-dimethyldiphenylsulfone; These are some examples.

[0022] Among these, bis(hydroxyaryl)alkanes are preferred, and bis(4-hydroxyphenyl)alkanes are preferred, with 2,2-bis(4-hydroxyphenyl)propane (i.e., bisphenol A) or 2,2-bis(3-methyl-4-hydroxyphenyl)propane (i.e., bisphenol C) being particularly preferred in terms of heat resistance, mechanical properties, and compatibility with polyester resins, and even more so, 2,2-bis(4-hydroxyphenyl)propane (i.e., bisphenol A). The aromatic dihydroxy compound may be used alone, or two or more may be used in any combination and ratio. Alternatively, a copolymer mainly composed of polycarbonate resin may be used, such as a copolymer with a polymer or oligomer having a siloxane structure.

[0023] Furthermore, to give an example of monomers that are raw materials for aliphatic polycarbonate resins, Alkanediols such as ethane-1,2-diol, propane-1,2-diol, propane-1,3-diol, 2,2-dimethylpropane-1,3-diol, 2-methyl-2-propylpropane-1,3-diol, butane-1,4-diol, pentane-1,5-diol, hexane-1,6-diol, and decane-1,10-diol;

[0024] Cycloalkanediols such as cyclopentane-1,2-diol, cyclohexane-1,2-diol, cyclohexane-1,4-diol, 1,4-cyclohexanedimethanol, 4-(2-hydroxyethyl)cyclohexanol, and 2,2,4,4-tetramethyl-cyclobutane-1,3-diol;

[0025] Glycols such as ethylene glycol, 2,2'-oxydiethanol (i.e., diethylene glycol), triethylene glycol, propylene glycol, and spiroglycol;

[0026] Aralkyldiols such as 1,2-benzenedimethanol, 1,3-benzenedimethanol, 1,4-benzenedimethanol, 1,4-benzenediethanol, 1,3-bis(2-hydroxyethoxy)benzene, 1,4-bis(2-hydroxyethoxy)benzene, 2,3-bis(hydroxymethyl)naphthalene, 1,6-bis(hydroxyethoxy)naphthalene, 4,4'-biphenyldimethanol, 4,4'-biphenyldiethanol, 1,4-bis(2-hydroxyethoxy)biphenyl, bisphenol A bis(2-hydroxyethyl) ether, and bisphenol S bis(2-hydroxyethyl) ether;

[0027] Examples include cyclic ethers such as 1,2-epoxyethane (i.e., ethylene oxide), 1,2-epoxypropane (i.e., propylene oxide), 1,2-epoxycyclopentane, 1,2-epoxycyclohexane, 1,4-epoxycyclohexane, 1-methyl-1,2-epoxycyclohexane, 2,3-epoxynorbornane, and 1,3-epoxypropane.

[0028] Among the monomers used as raw materials for the polycarbonate resin, examples of carbonate precursors include carbonyl halides and carbonate esters. Note that one type of carbonate precursor may be used, or two or more types may be used in any combination and ratio.

[0029] Examples of carbonyl halides include, specifically, phosgene; bischloroformates of dihydroxy compounds; monochloroformates of dihydroxy compounds; and other haloformates.

[0030] Examples of carbonate esters include diaryl carbonates such as diphenyl carbonate and dityl carbonate; dialkyl carbonates such as dimethyl carbonate and diethyl carbonate; and carbonates of dihydroxy compounds such as biscarbonates, monocarbonates, and cyclic carbonates of dihydroxy compounds.

[0031] <<Manufacturing method for polycarbonate resin>> The method for producing the polycarbonate resin used in the resin composition of this embodiment is not particularly limited, and any method can be employed. Examples include interfacial polymerization, melt transesterification, pyridine method, ring-opening polymerization of cyclic carbonate compounds, and solid-phase transesterification of prepolymers. Details of the interfacial polymerization method can be found in paragraphs 0031-0038 of International Publication No. 2020 / 013127, and these contents are incorporated herein by reference. Details of the melt transesterification method can be found in paragraphs 0039-0044 of International Publication No. 2020 / 013127, and these contents are incorporated herein by reference.

[0032] <<Physical Properties of Polycarbonate Resin>> The molecular weight of the polycarbonate resin used in the resin composition of this embodiment is arbitrary and can be appropriately selected and determined. However, the viscosity-average molecular weight [Mv] calculated from the solution viscosity is usually 10,000 or more, preferably 12,000 or more, more preferably 14,000 or more, and also usually 40,000 or less, preferably 35,000 or less, more preferably 30,000 or less, and may be 25,000 or less. By setting the viscosity-average molecular weight to be above the lower limit of the above range, the mechanical strength of the resin composition of this embodiment can be further improved, making it more preferable for applications requiring high mechanical strength. On the other hand, by setting the viscosity-average molecular weight to be below the upper limit of the above range, the decrease in fluidity of the resin composition of this embodiment can be suppressed and improved, thereby enhancing moldability and facilitating molding. In addition, in the resin composition of this embodiment, two or more polycarbonate resins with different viscosity-average molecular weights may be mixed and used. When two or more polycarbonate resins with different viscosity-average molecular weights are mixed and used, the viscosity-average molecular weight is calculated using the mixed polycarbonate resins with the following formula (1).

[0033] The polycarbonate resin may contain a high molecular weight polycarbonate resin, for example, a polycarbonate resin preferably having a viscosity-average molecular weight [Mv] of more than 40,000. Including such a high molecular weight polycarbonate resin makes it easier to further improve the mechanical strength of the resin composition of this embodiment. The viscosity-average molecular weight of the high molecular weight polycarbonate resin is preferably 50,000 or more, preferably 55,000 or more, more preferably 60,000 or more, even more preferably 61,000 or more, and even more preferably 62,000 or more. The viscosity-average molecular weight of the high molecular weight polycarbonate resin is also preferably 90,000 or less, more preferably 85,000 or less, even more preferably 80,000 or less, even more preferably 75,000 or less, and even more preferably 70,000 or less.

[0034] When the high molecular weight polycarbonate resin is included, its content is preferably 5% by mass or more, more preferably 10% by mass or more, even more preferably 15% by mass or more, and even more preferably 20% by mass or more, in the total polycarbonate resin. The upper limit is preferably 40% by mass or less, and more preferably 30% by mass or less.

[0035] Here, the viscosity-average molecular weight [Mv] is calculated by using methylene chloride as the solvent, determining the intrinsic viscosity [η] (unit dL / g) at 25°C using an Ubbelohde viscometer, and then using Schnell's viscosity formula, i.e., η = 1.23 × 10⁻⁶ -4 Mv 0.83 This refers to the value calculated from [the formula shown]. Intrinsic viscosity [η] is the value calculated by measuring the specific viscosity [ηsp] at each solution concentration [C] (g / dL) and using the following formula (1).

[0036]

number

[0037] The terminal hydroxyl group concentration of the polycarbonate resin is arbitrary and can be appropriately selected and determined, but is usually 1,000 ppm by mass or less, preferably 800 ppm by mass or less, and more preferably 600 ppm by mass or less. This improves the heat retention stability and color tone of the resin composition. Furthermore, the lower limit is usually 10 ppm by mass or more, preferably 30 ppm by mass or more, and more preferably 40 ppm by mass or more, especially for polycarbonate resins produced by the melt transesterification method. This suppresses the decrease in molecular weight and further improves the mechanical properties of the resin composition. When two or more polycarbonate resins with different terminal hydroxyl group concentrations are mixed and used, the measured value obtained by the method described below using the mixed polycarbonate resin is taken as the terminal hydroxyl group concentration. The unit for terminal hydroxyl group concentration is expressed as the mass of terminal hydroxyl groups relative to the mass of polycarbonate resin, expressed in ppm (parts per million). The measurement method is colorimetric determination using the titanium tetrachloride / acetic acid method (as described in Macromol. Chem. 88 215 (1965)).

[0038] Furthermore, the polycarbonate resin is not limited to a configuration containing only one type of polycarbonate resin; two or more types of polycarbonate resins with different monomer compositions, molecular weights, terminal hydroxyl group concentrations, etc., may be mixed and used.

[0039] Furthermore, for example, to further enhance impact resistance, the polycarbonate resin may be composed of copolymers mainly composed of polycarbonate resin, such as: a copolymer with an oligomer or polymer having a siloxane structure; a copolymer with a monomer, oligomer or polymer having a phosphorus atom to further improve thermal oxidation stability; a copolymer with a monomer, oligomer or polymer having a dihydroxyanthraquinone structure to improve thermal oxidation stability; a copolymer with an oligomer or polymer having an olefin-based structure such as polystyrene to improve optical properties; or a copolymer with a polyester resin oligomer or polymer to improve chemical resistance. When a polycarbonate resin containing the above copolymer is included, the copolymer component in the polycarbonate resin is preferably 10% by mass or less, more preferably 5% by mass or less, and even more preferably 3% by mass or less. There is no particular lower limit, but 0.5% by mass or more is preferred.

[0040] Furthermore, to improve the appearance and fluidity of the molded article, the polycarbonate resin may contain polycarbonate oligomers. The viscosity-average molecular weight [Mv] of these polycarbonate oligomers is usually 1,500 or more, preferably 2,000 or more, and usually 9,500 or less, preferably 9,000 or less. When the above polycarbonate oligomers are included, the amount of polycarbonate oligomers included is preferably 30% by mass or less of the polycarbonate resin (including the polycarbonate oligomers), more preferably 15% by mass or less, even more preferably 5% by mass or less, and even more preferably 1% by mass or less. There is no particular lower limit, but 0.1% by mass or more is preferred.

[0041] Furthermore, the polycarbonate resin may be not only virgin raw material, but also polycarbonate resin recycled from used products (so-called material-recycled polycarbonate resin). Examples of the aforementioned used products include optical recording media such as optical discs; light guide plates; transparent vehicle components such as car windows, car headlamp lenses, and windshields; containers such as water bottles; eyeglass lenses; and building components such as soundproof walls, glass windows, and corrugated sheets. In addition, crushed materials obtained from non-conforming products, sprues, runners, etc., or pellets obtained by melting them can also be used.

[0042] <Polyester resin (B)> The resin composition of this embodiment includes a polyester resin containing 0.80 to 8.00 ppm by mass of Ca element. It is presumed that by including Ca element above the lower limit in the polyester resin, the compatibility is improved by moderate transesterification between the polycarbonate resin and the polyester resin, thereby improving the tensile fracture nominal strain. Furthermore, it is presumed that by including Ca element below the lower limit, excessive transesterification is suppressed, thereby suppressing the generation of silver during retention.

[0043] The polyester resin contains 0.80 to 8.00 ppm by mass of Ca element. The polyester resin preferably contains 1.10 ppm by mass or more of Ca element, more preferably 1.50 ppm by mass or more, even more preferably 2.50 ppm by mass or more, and may contain 4.00 ppm by mass or more. The polyester resin preferably contains 7.00 ppm by mass or less of Ca element, more preferably 6.50 ppm by mass or less, even more preferably 6.00 ppm by mass or less, and may contain 5.40 ppm by mass or less, or 5.00 ppm by mass or less.

[0044] The polyester resin preferably contains 0.10 to 8.00 ppm by mass of Mg element. The polyester resin preferably contains 0.30 ppm by mass or more of Mg element, more preferably 0.60 ppm by mass or more, even more preferably 0.90 ppm by mass or more, and may contain 1.60 ppm by mass or more. Containing above the lower limit tends to further improve the tensile fracture nominal strain. This is presumed to be because the compatibility improves as the transesterification between the polycarbonate resin and the polyester resin proceeds appropriately. The polyester resin preferably contains 7.00 ppm by mass or less of Mg element, more preferably 5.50 ppm by mass or less, even more preferably 4.00 ppm by mass or less, even more preferably 3.00 ppm by mass or less, and even more preferably 2.50 ppm by mass or less. Containing below the lower limit tends to further suppress the generation of silver during retention. This is presumed to be because transesterification is suppressed.

[0045] The total amount of Ca and Mg elements in the polyester resin is preferably 0.90 ppm by mass or more, more preferably 1.50 ppm by mass or more, even more preferably 1.80 ppm by mass or more, even more preferably 3.00 ppm by mass or more, and even more preferably 5.00 ppm by mass or more. Including elements above the lower limit tends to further improve the tensile fracture strain. This is presumed to be because the compatibility is improved due to a moderate transesterification of the polycarbonate resin and the polyester resin. The total amount of Ca and Mg elements in the polyester resin is preferably 16.00 ppm by mass or less, more preferably 13.00 ppm by mass or less, even more preferably 10.00 ppm by mass or less, even more preferably 8.0 ppm by mass or less, and may also be 5.0 ppm by mass or less. Including elements below the lower limit tends to further suppress the generation of silver during retention. This is presumed to be because transesterification is suppressed.

[0046] The polyester preferably contains 100 ppm by mass or more of Sb element, more preferably 200 ppm by mass or more, and more preferably 210 ppm by mass or more. By exceeding the lower limit, the generation of silver during retention tends to be further suppressed. The polyester resin preferably contains 500 ppm by mass or less of Sb element.

[0047] The Ca, Mg, and Sb content (mass ppm) in the aforementioned polyester was analyzed by ICP emission spectrometry. In this case, as a pretreatment, 200 mg of the sample was weighed, subjected to Kjeldahl wet decomposition (sulfuric acid / nitric acid, sulfuric acid / hydrogen peroxide), and diluted to a final volume of 50 mL. Subsequently, ICP emission spectrometry was performed using the acid concentration matching one-check method. ICP emission spectrometry was performed using the "iCAP76000uo" manufactured by Throm Fisher Scientific, using axial / radial photometry. Furthermore, the elements Ca, Mg, and Sb do not necessarily need to exist as individual elements in the polyester resin, but may be included as part of a compound. In this embodiment, the measured values ​​in the <Measurement of the amount of metal elements> described in the example below are used as the amounts of the metal elements.

[0048] The polyester resin in this embodiment is a polymer or copolymer obtained by a condensation reaction mainly consisting of a dicarboxylic acid component, which is composed of dicarboxylic acids or their reactive derivatives, and a diol component, which is composed of diols or their ester derivatives. Preferably, an aromatic dicarboxylic acid is used as the main acid component, and a polyester resin obtained by polycondensation reaction of this with an alcohol mainly composed of an aliphatic diol is used. The polyester resin may be used alone, or two or more may be used in any combination and ratio.

[0049] Examples of aromatic dicarboxylic acids include terephthalic acid, isophthalic acid, orthophthalic acid, 1,5-naphthalenedicarboxylic acid, 2,6-naphthalenedicarboxylic acid, 4,4'-biphenyldicarboxylic acid, 4,4'-biphenyletherdicarboxylic acid, 4,4'-biphenylmethanedicarboxylic acid, 4,4'-biphenylsulfondicarboxylic acid, 4,4'-biphenylisopropylidenedicarboxylic acid, 1,2-bis(phenoxy)ethane-4,4'-dicarboxylic acid, 2,5-anthracenedicarboxylic acid, 2,6-anthracenedicarboxylic acid, 4,4'-p-ta-phenylenedicarboxylic acid, and 2,5-pyridinedicarboxylic acid. Substitutes of these (e.g., alkyl-substituted compounds such as 5-methylisophthalic acid) and reactive derivatives (e.g., alkyl ester derivatives such as dimethyl terephthalate and diethyl terephthalate) can also be used.

[0050] Of these, terephthalic acid, 2,6-naphthalenedicarboxylic acid, and their alkyl ester derivatives are more preferred, and terephthalic acid and its alkyl ester derivatives are particularly preferred. These aromatic dicarboxylic acids may be used individually or in combination of two or more, and it is also possible to use one or more aliphatic dicarboxylic acids such as adipic acid, azelaic acid, sebacic acid, and dodecanedioic acid, or alicyclic dicarboxylic acids such as cyclohexanedicarboxylic acid in combination with aromatic dicarboxylic acids.

[0051] Examples of diols include aliphatic diols such as ethylene glycol, diethylene glycol, 1,2-propylene glycol, 1,3-propanediol, triethylene glycol, 1,4-butanediol, neopentyl glycol, 1,5-pentanediol, 1,6-hexanediol, decamethylene glycol, and 2,2-dimethyl-1,3-propanediol; alicyclic diols such as 1,4-cyclohexanedimethanol, 1,3-cyclohexanedimethanol, cyclohexanediol, and trans- or cis-2,2,4,4-tetramethyl-1,3-cyclobutanediol; and aromatic diols such as p-xylenediol, bisphenol A, tetrabromobisphenol A, and tetrabromobisphenol A-bis(2-hydroxyethyl ether). Substitutes of these diols can also be used.

[0052] Of these, aliphatic diols are preferred in terms of heat resistance and dimensional stability, ethylene glycol, 1,4-butanediol, and 1,4-cyclohexanedimethanol are more preferred, and ethylene glycol is particularly preferred.

[0053] Diols may be used alone or in combination of two or more. Furthermore, one or more long-chain diols with molecular weights of 400 to 6,000, such as polyethylene glycol, poly-1,3-propylene glycol, and polytetramethylene glycol, may be copolymerized in combination with the above-mentioned diols.

[0054] Furthermore, the polyester resin used in the resin composition of this embodiment can be copolymerized with hydroxycarboxylic acids such as parahydroxybenzoic acid, other carboxylic acids, and alcohols other than the diols mentioned above, and such copolymerized resins can also be used in the present invention. However, it is preferable that such copolymerized components be present in small amounts, and it is preferable that 80% or more, and more preferably 90% or more, of the polyester resin (B) consists of components from aromatic dicarboxylic acids and aliphatic diols. It is also preferable that one compound accounts for 80 mol% or more, and more preferably 90 mol% or more, of each aromatic dicarboxylic acid and aliphatic diol.

[0055] The polyester resin used in the resin composition of this embodiment is preferably polyalkylene terephthalate. Here, polyalkylene terephthalate refers to a resin containing alkylene terephthalate structural units, and may be a copolymer of alkylene terephthalate structural units and other structural units.

[0056] Examples of polyalkylene terephthalates include polyethylene terephthalate (PET), polypropylene terephthalate, polybutylene terephthalate (PBT), polyethylene naphthalate (PEN), polybutylene naphthalate (PBN), poly(cyclohexane-1,4-dimethylene terephthalate), and polytrimethylene terephthalate. Among these, polyethylene terephthalate (PET) and polybutylene terephthalate (PBT) are preferred, and polyethylene terephthalate (PET) is more preferred.

[0057] In addition to the above, other examples of polyalkylene terephthalate include alkylene terephthalate copolymers, which mainly consist of alkylene terephthalate constituent units, and polyalkylene terephthalate mixtures, which mainly consist of polyalkylene terephthalate. Furthermore, those containing or copolymerized with elastomer components such as polyoxytetramethylene glycol (PTMG) can also be used.

[0058] Examples of alkylene terephthalate copolyesters include copolyesters composed of two or more diol components and terephthalic acid, and copolyesters composed of a diol component, terephthalic acid, and a dicarboxylic acid other than terephthalic acid. When using two or more diol components, they can be appropriately selected from the diol components mentioned above, but it is preferable to limit the monomer units copolymerized to alkylene terephthalate, which is the main structural unit, to 25% by mass or less, as this improves heat resistance.

[0059] For example, in addition to alkylene terephthalate copolyesters whose main constituent unit is alkylene terephthalate, such as ethylene glycol / isophthalic acid / terephthalic acid copolymer (isophthalic acid copolymer polyethylene terephthalate) and 1,4-butanediol / isophthalic acid / terephthalic acid copolymer (isophthalic acid copolymer polybutylene terephthalate), other examples include 1,4-butanediol / isophthalic acid / decanedicarboxylic acid copolymer, among which alkylene terephthalate copolyesters are preferred.

[0060] In this embodiment, when using an alkylene terephthalate copolyester, the above-mentioned isophthalic acid copolymerized polyethylene terephthalate or isophthalic acid copolymerized polybutylene terephthalate are preferred as the polyester resin, and among these, those with an isophthalic acid component of 25% by mass or less are particularly preferred from the viewpoint of heat resistance.

[0061] <<Polyethylene terephthalate resin>> In this embodiment, polyethylene terephthalate is particularly preferred as the polyester resin in terms of compatibility with polycarbonate resin and mechanical properties. Here, polyethylene terephthalate is a polyester resin having a structure in which terephthalic acid units and ethylene glycol units are ester-bonded, and includes polyethylene terephthalate copolymers containing other copolymer components other than terephthalic acid units and ethylene glycol units, as well as mixtures of homopolymers and polyethylene terephthalate copolymers, in addition to polyethylene terephthalate resin (homopolymer).

[0062] The polyethylene terephthalate resin may contain one or more dicarboxylic acid units other than terephthalic acid. Other specific examples of dicarboxylic acids include aromatic dicarboxylic acids such as isophthalic acid, orthophthalic acid, 1,5-naphthalenedicarboxylic acid, 2,5-naphthalenedicarboxylic acid, 2,6-naphthalenedicarboxylic acid, biphenyl-2,2'-dicarboxylic acid, biphenyl-3,3'-dicarboxylic acid, biphenyl-4,4'-dicarboxylic acid, bis(4,4'-carboxyphenyl)methane, anthracenedicarboxylic acid, and 4,4'-diphenyletherdicarboxylic acid; alicyclic dicarboxylic acids such as 1,4-cyclohexanedicarboxylic acid and 4,4'-dicyclohexyldicarboxylic acid; and aliphatic dicarboxylic acids such as adipic acid, sebacic acid, azelaic acid, and dimer acid. In this embodiment, the polyethylene terephthalate resin preferably contains terephthalic acid units accounting for 80 mol% or more of the total dicarboxylic acid units, more preferably 90 mol% or more, even more preferably 95 mol% or more, and may also contain 99 mol% or more.

[0063] The diol unit may include one or more other diol units in addition to ethylene glycol. Other specific examples of diol units include aliphatic glycols such as 1,2-propanediol, 1,3-propanediol, 1,4-butanediol, pentamethylene glycol, hexamethylene glycol, and neopentyl glycol, alicyclic glycols such as cyclohexanedimethanol, and aromatic dihydroxy compound derivatives such as bisphenol A and bisphenol S. In this embodiment, the polyethylene terephthalate resin preferably contains ethylene glycol units accounting for 80 mol% or more of the total diol units, more preferably 90 mol% or more, even more preferably 95 mol% or more, and may also contain 99 mol% or more.

[0064] Furthermore, the polyethylene terephthalate resin may be copolymerized with a branched component, such as a trifunctional or tetrafunctional acid like tricarbaryl acid, trimellicinic acid, trimellitic acid, or pyromellitic acid, or a trifunctional or tetrafunctional alcohol like glycerin, trimethylolpropane, or pentaerythritol, in an amount of, for example, 1.0 mol% or less, preferably 0.5 mol% or less, and more preferably 0.3 mol% or less.

[0065] The polyethylene terephthalate resin used in the resin composition of this embodiment is preferably a polyethylene terephthalate homopolymer in which terephthalic acid units and ethylene glycol units are ester-bonded. Alternatively, it may be a polyethylene terephthalate copolymer containing one or more dicarboxylic acids other than terephthalic acid as carboxylic acid units and / or one or more diols other than ethylene glycol as diol units. In the polyethylene terephthalate resin, terephthalic acid units and ethylene glycol units preferably account for 85 mol% or more of the total units excluding the terminal groups, more preferably 90 mol% or more, even more preferably 95 mol% or more, even more preferably 98 mol% or more, and even more preferably 99 mol% or more.

[0066] When the polyethylene terephthalate resin is a polyethylene terephthalate resin modified by copolymerization, isophthalic acid copolymerized polyethylene terephthalate resin is preferred. In particular, isophthalic acid copolymer polyethylene terephthalate resin is preferred in which units derived from isophthalic acid (hereinafter sometimes referred to as "isophthalic acid units") account for 0.5 mol% to 15 mol% of the total units derived from the dicarboxylic acid component. Using such a specific polyethylene terephthalate resin tends to further improve the tensile fracture strain of the molded article.

[0067] The proportion of isophthalic acid units is preferably 0.7 mol% or more, more preferably 0.9 mol% or more, even more preferably 1.1 mol% or more, even more preferably 1.3 mol% or more, and even more preferably 1.5 mol% or more, out of the total units derived from the dicarboxylic acid component. Furthermore, the proportion of isophthalic acid units is preferably 10.0 mol% or less, 8.0 mol% or less, 5.0 mol% or less, 4.0 mol% or less, and 3.5 mol% or less, out of the total units derived from the dicarboxylic acid component, in that order, more preferably 3.0 mol% or less, even more preferably 2.5 mol% or less, even more preferably 2.3 mol% or less, and even more preferably 2.0 mol% or less.

[0068] The intrinsic viscosity of the polyethylene terephthalate resin used in the resin composition of this embodiment is preferably 0.50 dL / g or more, more preferably 0.60 dL / g or more, even more preferably 0.65 dL / g or more, even more preferably 0.70 dL / g or more, even more preferably 0.73 dL / g or more, even more preferably greater than 0.76 dL / g, even more preferably 0.78 dL / g or more, and may also be 0.80 dL / g or more. Setting it above the lower limit tends to further improve the tensile fracture nominal strain of the molded article. Furthermore, the intrinsic viscosity of the polyethylene terephthalate resin is preferably 2.0 dL / g or less, more preferably 1.5 dL / g or less, even more preferably 1.2 dL / g or less, even more preferably 0.95 dL / g or less, and even more preferably 0.85 dL / g or less. By keeping the value below the aforementioned upper limit, the melt viscosity during melt mixing and molding tends to be kept from becoming too high, thereby reducing the load on the extruder and molding machine. If the resin composition of this embodiment contains two or more types of polyethylene terephthalate resin, the intrinsic viscosity shall be the intrinsic viscosity of the mixture.

[0069] In this invention, the intrinsic viscosity of polyethylene terephthalate is the value measured at 30°C using a mixed solvent of phenol / tetrachloroethane (weight ratio 1 / 1).

[0070] Furthermore, the amount of terminal carboxyl groups in the polyethylene terephthalate resin used in the resin composition of this embodiment can be appropriately selected and determined, but is usually 60 eq / ton or less, preferably 50 eq / ton or less, and more preferably 30 eq / ton or less. The concentration of terminal carboxyl groups in the polyethylene terephthalate resin is determined by dissolving 0.5 g of polyethylene terephthalate resin in 25 mL of benzyl alcohol and titrating with a 0.01 mol / L benzyl alcohol solution of sodium hydroxide. The amount of terminal carboxyl groups can be adjusted by any conventionally known method, such as adjusting polymerization conditions like the raw material ratio, polymerization temperature, and reduced pressure method during polymerization, or by reacting with a chelating agent.

[0071] The concentration of terminal carboxyl groups in polyethylene terephthalate can be determined by dissolving 0.5 g of polyethylene terephthalate in 25 mL of benzyl alcohol and titrating it with a 0.01 mol / L benzyl alcohol solution of sodium hydroxide.

[0072] The polyethylene terephthalate resin used in this embodiment preferably contains 0.50% by mass or less of cyclic trimers, more preferably 0.40% by mass or less, and even more preferably 0.30% by mass or less. By keeping the amount below the upper limit, the generation of silver during retention tends to be further reduced. There is no specific lower limit, but 0.1% by mass or more is practical. The amount of cyclic trimer was determined by dissolving 0.1 g of polyethylene terephthalate resin in a solvent such as chloroform, performing dissolution and reprecipitation, filtering the supernatant, and measuring it by high-performance liquid chromatography (HPLC). Quantitative analysis was performed using a single-point absolute calibration curve method, and the value was expressed in terms of DMT (dimethyl terephthalate).

[0073] Such polyethylene terephthalate resin (hereinafter sometimes referred to as "PET") can be virgin (hereinafter sometimes referred to as "virgin PET"), recycled (hereinafter sometimes referred to as "recycled PET"), bio-derived (hereinafter sometimes referred to as "bio-PET"), or mixtures thereof. Bio-PET refers to polyethylene terephthalate resin in which at least a portion of the raw material is derived from biological resources (biomass). The polyester resin used in this embodiment may be virgin, recycled, bio-derived, or a combination thereof, but recycled is preferred in terms of reducing environmental impact. Recycled PET can be obtained through material recycling, where collected used PET bottles and films are crushed, alkaline-washed, and reused as fibers, as well as through chemical recycling (chemical decomposition method) and mechanical recycling. Chemical recycling involves chemically decomposing collected used PET bottles and films to return them to their raw material level and resynthesize polyethylene terephthalate resin. Mechanical recycling, on the other hand, is a method that makes it possible to reliably remove contaminants from polyethylene terephthalate resin more effectively than material recycling by performing alkaline cleaning more rigorously or by vacuum drying at high temperatures. For example, after foreign matter is removed from used PET bottles, they are crushed and washed, then pelletized using an extruder, crystallized in an environment of approximately 120-150°C, and then solid-phase polymerized in an environment of approximately 210°C under a nitrogen stream or high reduced pressure to obtain recycled PET. Bio-PET includes PET manufactured by replacing monoethylene glycol, a raw material for PET, with bio-based raw materials derived from sugarcane.

[0074] <Blending ratio of resin (C)> In the resin composition of this embodiment, 100 parts by mass of resin (C) contains 40 to 95 parts by mass of polycarbonate resin (A) and 5 to 60 parts by mass of polyester resin (B). In the resin composition of this embodiment, the proportion of polycarbonate resin (A) in 100 parts by mass of resin (C) is preferably 50 parts by mass or more, more preferably 55 parts by mass or more, even more preferably 60 parts by mass or more, even more preferably 65 parts by mass or more, and may also be 70 parts by mass or more, 80 parts by mass or more, or 85 parts by mass or more. Furthermore, in the resin composition of this embodiment, the proportion of polycarbonate resin (A) in 100 parts by mass of resin (C) is preferably 90 parts by mass or less, more preferably 85 parts by mass or less, and may also be 80 parts by mass or less. In the resin composition of this embodiment, the proportion of polyester resin (B) in 100 parts by mass of resin (C) is preferably 10 parts by mass or more, more preferably 15 parts by mass or more, and may be 20 parts by mass or more. Furthermore, in the resin composition of this embodiment, the proportion of polyester resin (B) in 100 parts by mass of resin (C) is preferably 50 parts by mass or less, more preferably 45 parts by mass or less, even more preferably 40 parts by mass or less, even more preferably 35 parts by mass or less, and may be 30 parts by mass or less, 20 parts by mass or less, or 15 parts by mass or less. In the resin composition of this embodiment, the mass ratio (A) / (B) of polycarbonate resin (A) to polyester resin (B) in 100 parts by mass of resin (C) is preferably 95 / 5 to 40 / 60. The mass ratio (A) / (B) is more preferably 90 / 10 to 45 / 55, even more preferably 85 / 5 to 50 / 50, and even more preferably 80 / 20 to 60 / 40.

[0075] In the resin composition of this embodiment, the total amount of polycarbonate resin (A) and polyester resin (B) in resin (C) is preferably 50% by mass or more, more preferably 70% by mass or more, even more preferably 80% by mass or more, even more preferably 90% by mass or more, even more preferably 95% by mass or more, and may be 99% by mass or more. Setting it above the lower limit tends to further improve the tensile fracture nominal strain. The upper limit is the amount at which the entire amount of resin (C) consists of polycarbonate resin (A) and polyester resin (B), which is 100% by mass. Setting it below the upper limit tends to further suppress the generation of silver during retention. The above resin (C) may contain only one type of polycarbonate resin and one type of polyester resin, or two or more types. When two or more types are included, it is preferable that the total amount is within the above range.

[0076] The resin (C) content in the resin composition of this embodiment is preferably 50% by mass or more, more preferably 60% by mass or more, even more preferably 70% by mass or more, even more preferably 75% by mass or more, and may be 80% by mass or more. Setting it above the lower limit tends to further improve the tensile fracture nominal strain. The upper limit of resin (C) is the amount in the resin composition other than the phosphorus-based transesterification inhibitor (D) that becomes resin (C), for example, 99.9% by mass or less. Setting it below the upper limit tends to further suppress the generation of silver during retention.

[0077] <Phosphorus-based transesterification inhibitor (D)> The resin composition of this embodiment contains 0.001 to 4 parts by mass of a phosphorus-based transesterification inhibitor (D) per 100 parts by mass of resin (C), which comprises 40 to 95 parts by mass of polycarbonate resin (A) and 5 to 60 parts by mass of polyester resin (B). The phosphorus-based transesterification inhibitor is a compound that plays a role in suppressing transesterification between the polyester resin and the polycarbonate resin.

[0078] Examples of phosphorus-based transesterification inhibitors (D) include organic phosphate compounds. Examples of organic phosphate compounds include alkyl acid phosphates, alkenyl acid phosphates, and their metal salts. The alkyl acid phosphate or alkenyl acid phosphate of the phosphate compound is preferably represented by the following formula (I). That is, the alkyl acid phosphate or alkenyl acid phosphate is represented by the following formula (I), and the alkyl acid phosphate metal salt or alkenyl acid phosphate metal salt is preferably a metal salt such as a zinc salt or aluminum salt of the alkyl acid phosphate or alkenyl acid phosphate represented by the following formula (I). O=P(OH) n (OR) 3-n …(I) (In formula (I), R is an alkyl group having 8 to 30 carbon atoms or an alkenyl group having 8 to 30 carbon atoms, and n is an integer of 1 or 2. When n is 1, the two Rs may be the same or different.) The alkyl group represented by R in formula (I) above may be a linear alkyl group or a branched alkyl group. Specific examples of the alkyl group R include octyl, nonyl, isononyl, decyl, isodecyl, dodecyl, tridecyl, isotridecyl, tetradecyl, hexadecyl, octadecyl(stearyl), eicosyl, and tetracosyl groups. The alkenyl group represented by R may also be a linear alkenyl group or a branched alkenyl group. Specific examples of the alkenyl group R include oleyl. n is 1 or 2, or a mixture thereof. The number of carbon atoms in the alkyl or alkenyl group represented by R in formula (I) above is more preferably 12 to 24, and even more preferably 18. The alkyl acid phosphate is particularly preferably a mixture of the distearyl acid phosphate with n=1 and the monostearyl acid phosphate with n=2, represented by the following formula (II). O=P(OH) n (OC 18 H 37 ) 3-n …(II) Furthermore, as the metal salt of the alkyl acid phosphate, a mixture of distearyl acid phosphate zinc salt represented by the following formula (IIIa) and monostearyl acid phosphate zinc salt represented by the following formula (IIIb) is preferred.

[0079] [ka] These phosphate compounds may be used individually or as a mixture of two or more. Specific examples of such phosphate compounds include "JP-518Zn" manufactured by Johoku Chemical Industry Co., Ltd. and "AX-71" manufactured by ADEKA Corporation.

[0080] The content of the phosphorus-based transesterification inhibitor (D) in the resin composition of this embodiment is 0.001 to 4 parts by mass per 100 parts by mass of resin (C) containing 40 to 95 parts by mass of polycarbonate resin (A) and 5 to 60 parts by mass of polyester resin (B). By setting the content above the lower limit, the generation of silver during retention tends to be further suppressed. By setting the content below the upper limit, the tensile fracture strain tends to be further improved, and thermal stability also tends to be further improved. The content of the phosphorus-based transesterification inhibitor (D) is preferably 0.005 parts by mass or more, more preferably 0.01 parts by mass or more, even more preferably 0.05 parts by mass or more, even more preferably 0.075 parts by mass or more, and even more preferably 0.1 parts by mass or more, per 100 parts by mass of the resin. Furthermore, the content of the phosphorus-based transesterification inhibitor (D) is preferably 3 parts by mass or less, more preferably 2 parts by mass or less, even more preferably 1 part by mass or less, and even more preferably 0.5 parts by mass or less, per 100 parts by mass of the resin. The resin composition of this embodiment may contain only one phosphorus-based transesterification inhibitor (D), or it may contain two or more. When two or more are included, it is preferable that the total amount is within the above range.

[0081] <Inorganic filler (E)> The resin composition of this embodiment may or may not contain an inorganic filler. Including an inorganic filler tends to improve the mechanical strength of the molded article made from the resin composition of this embodiment. Any known inorganic filler can be used. Specifically, examples include wollastonite, xonotlite, talc, mica, clay, montolilonite, smectite, kaolin, calcium carbonate, magnesium carbonate, barium carbonate, silica, ceramic particles, ceramic fibers, ceramic balloons, potassium titanate, boron nitride, aluminum borate, magnesium sulfate, calcium sulfate, barium sulfate, titanium dioxide, zinc oxide, glass fibers (chopped strands), glass fibers, glass flakes, glass beads, carbon fibers, carbon short fibers, and carbon nanotubes. These inorganic fillers may be included individually or in combination of two or more. In particular, it is preferable to include one or more selected from the group consisting of glass fibers, glass flakes, carbon fibers, talc, mica, wollastonite, and kaolin, with talc being especially preferred from the viewpoint of rigidity and dimensional stability.

[0082] The inorganic filler can take the form of a fibrous or non-fibrous material (such as a needle, plate, or sphere). Among these, a non-fibrous inorganic filler is preferred.

[0083] The inorganic filler may be treated with a known surface treatment agent to improve its adhesion to the resin. Examples of surface treatment agents include silane-based coupling agents and titanate-based coupling agents containing amino groups or epoxy groups. Such surface treatment agents may be applied to the surface of the inorganic filler beforehand, or they may be added when mixing the resin and the inorganic filler. Examples of coupling agents include silane-based, chromium-based, and titanium-based coupling agents, with those containing silane-based coupling agents such as epoxysilanes like γ-glycidoxypropyltrimethoxysilane, vinyltrichlorosilane, and aminosilanes like γ-aminopropyltriethoxysilane being particularly preferred.

[0084] <<Talc>> As the inorganic filler used in this embodiment, talc is particularly preferred because it offers a good balance between appearance and mechanical strength. Examples of talc are given in paragraphs 0021 to 0039 of Japanese Patent Application Publication No. 2020-45419, and these contents are incorporated herein by reference.

[0085] In the resin composition of this embodiment, the inorganic filler (E) is preferably contained in an amount of 1 to 100 parts by mass per 100 parts by mass of resin (C) which contains 40 to 95 parts by mass of polycarbonate resin (A) and 5 to 60 parts by mass of polyester resin (B). Setting the value above the lower limit tends to further improve mechanical strength. Setting the value below the upper limit tends to further suppress the generation of silver during retention. The content of the inorganic filler is preferably 2.5 parts by mass or more, more preferably 5 parts by mass or more, even more preferably 10 parts by mass or more, and even more preferably 15 parts by mass or more, based on 100 parts by mass of the resin (C). Furthermore, the content of the inorganic filler is preferably 80 parts by mass or less, more preferably 65 parts by mass or less, even more preferably 50 parts by mass or less, even more preferably 30 parts by mass or less, and may also be 25 parts by mass or less, based on 100 parts by mass of the resin (C). In the resin composition of this embodiment, the content of the inorganic filler (E) is preferably 5% by mass or more, more preferably 10% by mass or more, preferably 45% by mass or less, more preferably 35% by mass or less, and even more preferably 25% by mass or less. The resin composition of this embodiment may contain only one type of inorganic filler (E), or it may contain two or more types. When it contains two or more types, it is preferable that the total amount is within the above range.

[0086] <Mixing ratio of phosphorus-based transesterification inhibitor (D) and inorganic filler (E)> The resin composition of this embodiment preferably contains 0.1 parts by mass or more of a phosphorus-based transesterification inhibitor (D) per 100 parts by mass of an inorganic filler (E). Generally, the incorporation of inorganic fillers into a resin composition can reduce its thermal stability and make it more prone to generating silver during retention. In particular, because talc has alkaline properties, it is presumed that when incorporated into a resin containing polycarbonate resin and polyester resin, it promotes the decomposition of the resin and causes the generation of silver during retention. However, it is presumed that by using such a blending ratio of inorganic filler (E) to phosphorus-based transesterification inhibitor (D), the decomposition of the resin by the inorganic filler is suppressed, and the generation of silver during retention tends to be further suppressed. The phosphorus-based transesterification inhibitor (D) is preferably present in an amount of 0.20 parts by mass or more, more preferably 0.40 parts by mass or more, even more preferably 0.60 parts by mass or more, and may be present in an amount of 1.00 parts by mass or more, 2.00 parts by mass or more, or 4.00 parts by mass or more per 100 parts by mass of the inorganic filler (E). Setting the amount above the lower limit tends to further suppress the generation of silver during retention. It is preferable that the phosphorus-based transesterification inhibitor (D) is contained in an amount of 30.00 parts by mass or less, more preferably 20.00 parts by mass or less, even more preferably 10.00 parts by mass or less, even more preferably 5.00 parts by mass or less, even more preferably 2.00 parts by mass or less, and may also be 1.50 parts by mass or less, 1.00 parts by mass or less, or 0.90 parts by mass or less. By keeping the amount below the above upper limit, the tensile fracture nominal strain tends to improve, and the thermal stability also tends to improve.

[0087] <Other ingredients> The resin composition of this embodiment may contain other components as needed, as long as they do not significantly impair the desired physical properties. Examples of other components include various resins and resin additives. The other components may be present individually, or two or more in any combination and ratio. Specifically, these include thermoplastic resins other than polycarbonate resin and polyester resin, elastomers, mold release agents, stabilizers other than phosphorus-based transesterification inhibitors (heat stabilizers, light stabilizers), colorants (pigments, dyes), reactive compounds, nucleating agents, flame retardants, flame retardant additives, fillers other than inorganic fillers, antistatic agents, antifogging agents, antiblocking agents, flow improvers, plasticizers, dispersants, and antibacterial agents. The resin composition of this embodiment is formulated so that the total amount of polycarbonate resin (A), polyester resin (B), phosphorus-based transesterification inhibitor (D), and other components added as needed is 100% by mass. In the resin composition of this embodiment, the total amount of polycarbonate resin (A), polyester resin (B), phosphorus-based transesterification inhibitor (D), and inorganic filler (E) added as needed is preferably 80% by mass or more, more preferably 90% by mass or more, even more preferably 95% by mass or more, and may be 98% by mass or more, or 99% by mass or more. The upper limit is 100% by mass.

[0088] <<Elastomer>> The resin composition of this embodiment may also contain an elastomer. As the elastomer, a copolymer obtained by graft copolymerizing a rubber component with a monomer component copolymerizable thereto is preferred. The method for producing such a graft copolymer may be any of the following methods: bulk polymerization, solution polymerization, suspension polymerization, emulsion polymerization, etc., and the copolymerization method may be single-stage grafting or multi-stage grafting. Specifically, as elastomers, refer to paragraphs 0129 to 0133 of Japanese Patent Publication No. 2020-164869, the contents of which are incorporated herein by reference.

[0089] When the resin composition of this embodiment contains an elastomer, it is preferable to include 0.5 parts by mass or more, more preferably 1.0 part by mass or more, and even more preferably 2.0 parts by mass or more, per 100 parts by mass of resin (C) which contains 40 to 95 parts by mass of polycarbonate resin (A) and 5 to 60 parts by mass of polyester resin (B). Including an amount above the upper limit tends to further improve the tensile fracture nominal strain. Furthermore, it is preferable to include 15 parts by mass or less, more preferably 10 parts by mass or less, and even more preferably 7.5 parts by mass or less, per 100 parts by mass of the resin. Including an amount below the lower limit tends to further suppress the generation of silver during retention. The resin composition of this embodiment may contain only one type of elastomer, or it may contain two or more types. When it contains two or more types, it is preferable that the total amount is within the above range.

[0090] <<Stabilizers other than phosphorus-based transesterification inhibitors (D)>> The resin composition of this embodiment may also contain stabilizers other than the phosphorus-based transesterification inhibitor (D) (light stabilizers and / or heat stabilizers). Examples of stabilizers include phosphorus compounds other than phosphorus transesterification inhibitors (D), phenolic compounds, hindered amine compounds, and sulfur-based stabilizers. Among these, phosphorus compounds other than phosphorus transesterification inhibitors (D) and phenolic compounds are preferred.

[0091] Other phosphorus compounds besides the phosphorus transesterification inhibitor (D) include phosphorus oxoacids such as phosphoric acid, phosphonic acid, phosphinic acid, and polyphosphate; acidic pyrophosphate metal salts such as sodium acidic pyrophosphate, potassium acidic pyrophosphate, and calcium acidic pyrophosphate; phosphates such as potassium phosphate, sodium phosphate, cesium phosphate, and zinc phosphate; organic phosphite compounds, organic phosphonite compounds, and the like. Among these, organic phosphite compounds are preferred. The phosphorus compounds other than the aforementioned phosphorus transesterification inhibitor (D) may consist of only one type or two or more types.

[0092] The phenolic compounds mentioned above are preferably hindered phenolic stabilizers, such as pentaerythritol tetrakis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate], octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate, thiodiethylenebis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate], N,N'-hexane-1,6-diylbis[3-(3,5-di-tert-butyl-4-hydroxyphenylpropionamide), 2,4-dimethyl-6-(1-methylpentadecyl)phenol, diethyl[[3,5-bis(1,1-dimethylethyl)-4-hydroxyphenyl]methyl]phosphoate, 3,3',3”,5,5',5”-hexa-tert-butyl-a,a',a -(mesitylene-2,4,6-triyl)tri-p-cresol, 4,6-bis(octylthiomethyl)-o-cresol, ethylenebis(oxyethylene)bis[3-(5-tert-butyl-4-hydroxy-m-tolyl)propionate], hexamethylenebis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate], 1,3,5-tris(3,5-di-tert Examples include -butyl-4-hydroxybenzyl)-1,3,5-triazine-2,4,6(1H,3H,5H)-trione, 2,6-di-tert-butyl-4-(4,6-bis(octylthio)-1,3,5-triazine-2-ylamino)phenol, and 2-[1-(2-hydroxy-3,5-di-tert-pentylphenyl)ethyl]-4,6-di-tert-pentylphenyl acrylate. The phenolic stabilizer may consist of only one type or two or more types.

[0093] Specifically, as stabilizers, reference can be made to paragraphs 0066-0075 of Japanese Patent Publication No. 2021-063196, paragraphs 0047-0057 of Japanese Patent Publication No. 2018-070722, paragraphs 0030-0036 of Japanese Patent Publication No. 2019-056035, and paragraphs 0053-59 of Japanese Patent Publication No. 2020-045419, the contents of which are incorporated herein by reference.

[0094] If the resin composition of this embodiment contains a stabilizer, its content is preferably 0.001 parts by mass or more, more preferably 0.005 parts by mass or more, even more preferably 0.01 parts by mass or more, and even more preferably 0.05 parts by mass or more, per 100 parts by mass of resin (C) containing 40 to 95 parts by mass of polycarbonate resin (A) and 5 to 60 parts by mass of polyester resin (B). Setting the content above the lower limit tends to further improve the effect of suppressing thermal degradation and oxidative degradation of the resin during melt mixing, molding, and use as a molded article. Furthermore, the upper limit of the stabilizer content is preferably 2.0 parts by mass or less, and more preferably 1.5 parts by mass or less, per 100 parts by mass of the resin. Setting the content below the upper limit effectively suppresses adverse effects on appearance and physical properties due to aggregation of additives such as stabilizers. The resin composition of this embodiment may contain only one stabilizer or two or more stabilizers. When two or more stabilizers are included, it is preferable that the total amount is within the above range.

[0095] <<Release agent>> The resin composition of this embodiment may contain a mold release agent. Examples of mold release agents include aliphatic carboxylic acids, esters of aliphatic carboxylic acids and alcohols, aliphatic hydrocarbon compounds with a number average molecular weight of 200 to 15,000, and polysiloxane-based silicone oils. As for the aforementioned release agent, specific examples can be found in paragraphs 0083 to 0092 of Japanese Patent Publication No. 2015-199852, the contents of which are incorporated herein by reference.

[0096] When the resin composition of this embodiment contains a release agent, the amount is preferably 0.01 parts by mass or more, more preferably 0.05 parts by mass or more, and even more preferably 0.1 parts by mass or more, per 100 parts by mass of resin (C) containing 40 to 95 parts by mass of polycarbonate resin (A) and 5 to 60 parts by mass of polyester resin (B). Including above the lower limit tends to further improve moldability. Furthermore, the upper limit of the release agent content is preferably 5.0 parts by mass or less, and more preferably 1.0 part by mass or less, per 100 parts by mass of the resin. Including below the upper limit tends to further suppress the generation of silver. The resin composition of this embodiment may contain only one type of release agent, or it may contain two or more types. When it contains two or more types, it is preferable that the total amount is within the above range.

[0097] <Method for producing resin compositions> The present invention also discloses a method for producing a resin composition. The method for producing the resin composition of this embodiment includes melt-kneading 100 parts by mass of resin (C) containing 40 to 95 parts by mass of polycarbonate resin (A) and 5 to 60 parts by mass of polyester resin (B), and 0.001 to 4 parts by mass of phosphorus-based transesterification inhibitor (D), wherein the polyester resin (B) contains Ca element in a proportion of 0.80 to 8.00 ppm by mass. The resin composition of this embodiment can be manufactured by first mixing a polycarbonate resin (A), a polyester resin (B), a phosphorus-based transesterification inhibitor (D), and, if necessary, an inorganic filler (E) and other additives using various mixers such as a tumbler or a Henschel mixer, and then melt-kneading them using a Banbury mixer, rolls, brabender, single-screw extruder, twin-screw extruder, kneader, etc. Furthermore, the resin composition can be manufactured by supplying the components to the extruder using a feeder, either without pre-mixing them or by pre-mixing only some of the components, and then melt-kneading them. Alternatively, some components, such as colorants, may be melt-kneaded with a thermoplastic resin to prepare a masterbatch, and then the remaining components may be added to this masterbatch and melt-kneaded to manufacture the resin. When using inorganic fillers, it is also preferable to supply them from a side feeder in the middle of the extruder cylinder. The heating temperature during melt-kneading can usually be appropriately selected from the range of 240 to 330°C. If the temperature is too high, it may cause decomposition gases or a decrease in strength due to a decrease in molecular weight. Therefore, it is desirable to select a screw configuration that takes shear heating into consideration. To suppress decomposition during kneading and subsequent molding processes, it is desirable to use antioxidants and heat stabilizers.

[0098] <Properties of resin compositions> <<Silver during stay>> The resin composition of this embodiment suppresses the generation of silver during retention. Specifically, it is as follows: Using the resin composition of this embodiment, a three-stage plate of 50mm x 90mm x 3mmt, 2mmt, and 1mmt was molded in 10 consecutive shots under normal conditions of a 45-second cycle using an injection molding machine (cylinder temperature 290°C, mold temperature 80°C). Then, the cooling time was extended to change the retention conditions to a 180-second cycle, and silver during retention was checked on the plate after the 5th consecutive shot. A score from 0 to 9 was assigned visually according to the degree of silver during retention. A higher number indicates a larger area of ​​silver streaks during retention. The score is preferably 7 or less, more preferably 6 or less, and even more preferably 5 or less. The score is most preferably 0, where no silver during retention is visually observed. The amount of silver generated during retention is evaluated according to the description in the examples below.

[0099] <<Tensile fracture specified strain>> The resin composition of this embodiment exhibits improved tensile fracture strain. Specifically, when a dumbbell test piece (A1) conforming to JIS K 7139 is molded using the resin composition, and the tensile fracture strain measured by the method of JIS K 7161 is preferably 10.0% or higher, and more preferably 10.5% or higher. There is no particular upper limit for the tensile fracture strain, but 100.0% or lower is practical.

[0100] <Molded articles of resin compositions> This embodiment also includes molded articles formed from the resin composition of this embodiment. The pellets obtained by pelletizing the resin composition of this embodiment can be molded into molded bodies using various molding methods. Alternatively, the resin composition, which is melt-kneaded in an extruder, can be directly molded into molded bodies without going through the pellet stage. There are no particular restrictions on the shape of the molded body, and it can be appropriately selected according to the application and purpose of the molded body. Examples include plate-shaped, rod-shaped, sheet-shaped, film-shaped, cylindrical, annular, circular, elliptical, gear-shaped, polygonal, irregularly shaped, hollow, frame-shaped, box-shaped, panel-shaped, and cap-shaped molded bodies. The molded body in this embodiment may be a finished product, a part, or welded parts.

[0101] The method for forming the molded body is not particularly limited, and conventionally known molding methods can be employed. For example, injection molding, ultra-high-speed injection molding, injection compression molding, multi-color injection molding, gas-assisted injection molding, molding using a heat-insulating mold, molding using a rapidly heating and cooling mold, foam molding (including supercritical fluid), insert molding, IMC (in-mold coating) molding, extrusion molding, sheet molding, thermoforming, rotational molding, lamination molding, and press molding can be employed. Furthermore, for various injection molding methods, a molding method using a hot runner system can also be selected. Furthermore, the mold temperature during mold molding, such as injection molding, is preferably 40 to 100°C.

[0102] <Application> The resin composition of this embodiment is used as a molded article formed from the resin composition. The applications of the resin composition or molded article are not particularly limited, but it is preferably used in electrical and electronic equipment / components, office automation equipment / components, information terminal equipment / components, machine parts, home appliances, vehicle parts (automobile interior and exterior), building materials, various containers, leisure goods and miscellaneous goods, lighting equipment, etc. [Examples]

[0103] The present invention will be described in more detail below with reference to examples. The materials, amounts used, proportions, processing content, and processing procedures shown in the following examples can be modified as appropriate, as long as they do not depart from the spirit of the present invention. Therefore, the scope of the present invention is not limited to the specific examples shown below. If the measuring instruments used in the examples are difficult to obtain due to discontinuation or other reasons, measurements can be taken using other instruments with equivalent performance.

[0104] 1. Raw materials The raw materials shown in Tables 1-3 below were used. [Table 1] [Table 2] [Table 3]

[0105] 2. Examples 1-9, Comparative Examples 1-6 <Measurement of the amount of metallic elements> The calcium, magnesium, and sorbite content (mass ppm) in polyester resin was analyzed by ICP emission spectrometry. As a pretreatment, 200 mg of the sample was weighed, subjected to Kjeldahl wet decomposition (sulfuric acid / nitric acid, sulfuric acid / hydrogen peroxide), and diluted to 50 mL. Subsequently, ICP emission spectrometry was performed using the acid concentration matching one-check method. ICP emission spectrometry was performed using Thrmo Fisher Scientific's "iCAP76000uo" with axial / radial photometry.

[0106] <Measurement of the amount of cyclic trimer> The amount of cyclic trimers in polyester resin was determined by dissolving 0.1 g of polyethylene terephthalate resin in a solvent such as chloroform, performing dissolution and reprecipitation, filtering the supernatant, and measuring by high-performance liquid chromatography (HPLC). Quantitative analysis was performed using a single-point absolute calibration curve method, and the value was expressed in terms of DMT (dimethyl terephthalate).

[0107] <Manufacturing of resin compositions> (Examples 1-7, Comparative Examples 1-6) Each component shown in Tables 1-3 above was blended in the proportions (all parts by mass) indicated in Tables 4 or 5 below, mixed in a tumbler for 20 minutes, and then supplied to a twin-screw extruder (TEM26SS) manufactured by Shibaura Machine Co., Ltd. The mixture was kneaded under the conditions of a screw rotation speed of 250 rpm, a discharge rate of 30 kg / hour, and a barrel temperature of 260°C. The molten resin composition extruded into strands was rapidly cooled in a water bath and pelletized using a pelletizer to obtain resin composition pellets. (Examples 8 and 9) Of the components shown in Tables 1-3 above, the polycarbonate resin, polyester resin, and other raw materials were weighed in the proportions shown in Table 6 and mixed separately in a tumbler for 20 minutes. The resin composition pellets were produced in the same manner as described above (Examples 1-7, Comparative Examples 1-6), except that the polycarbonate resin and polyester resin were fed from the base of the extruder, and the other raw materials were fed separately.

[0108] <Silver's evaluation during stay> The pellets obtained above were dried in a hot air dryer at 120°C for 5 hours. Then, using a Japan Steel Works injection molding machine (J-55ADS), three 50mm x 90mm plates with thicknesses of 3mm, 2mm, and 1mm were molded under the following conditions: cylinder temperature 290°C, mold temperature 80°C, injection speed 10mm / s, and holding pressure 80MPa. After 10 consecutive shots under normal conditions of a 45-second cycle, the cooling time was extended to change to a 180-second cycle, and the silver streak during stagnation was checked on the 5th consecutive shot plate. The resulting molded bodies were visually inspected and scored on a scale of 0 to 9 according to the degree of silver streak during stagnation. A higher number indicates a larger area of ​​silver streak during stagnation. Five experts evaluated the results, and the majority vote was used. A standard was set so that Example 1 would receive a score of "5".

[0109] <Measurement of tensile fracture strain> The pellets obtained as described above were dried in a hot air dryer at 120°C for 5 hours. Then, using an injection molding machine (NEX80III) manufactured by Nissei Plastic Industrial Co., Ltd., a JIS K7139 multi-purpose test specimen (A1) with a thickness of 4 mm was molded under the conditions of cylinder temperature 280°C, mold temperature 80°C, injection speed 33 mm / s, and holding pressure 80 MPa. Using the test specimens obtained above, the tensile fracture strain (unit: %) was measured according to the method described in JIS K 7161.

[0110] <Measurement of Charpy strength retention rate after moist heat treatment> The 4mm thick JIS K7139 multipurpose test specimen (A1) obtained above was cut into a specimen measuring 80mm in length, 10mm in width, and 4mm in thickness using a notching tool manufactured by Toyo Seiki Co., Ltd., and a notch with a tip radius r=0.25mm was made. Subsequently, it was subjected to moist heat treatment for 500 hours in a moist heat environment of 85°C and 85%. The Charpy impact strength was measured using the specimens obtained above, both before and after moist heat treatment, according to the method of JIS K 7111-1. The Charpy impact strength retention rate after moist heat was calculated according to the following formula (2). Formula (2) Charpy impact strength retention rate after moist heat treatment (%) = [(Charpy impact strength after moist heat treatment) / (Charpy impact strength before moist heat treatment)] × 100

[0111] <Measuring ΔDTUL> The pellets obtained above were dried in a hot air dryer at 120°C for 5 hours. Then, using an injection molding machine (NEX80III) manufactured by Nissei Plastic Industrial Co., Ltd., 20 consecutive shots were molded under normal conditions of 45-second cycles with a cylinder temperature of 280°C, mold temperature of 80°C, injection speed of 33 mm / s, and holding pressure of 80 MPa, to form a 4 mm thick JIS K7139 multipurpose test specimen (A1). Subsequently, the cooling time was extended to change the retention condition to a 600-second cycle, and 3 consecutive shots were molded to form a multipurpose test specimen (A2) under retention conditions. From the 4mm thick JIS K7139 multipurpose test specimens (A1, A2) obtained above, 80mm x 10mm x 4mm test specimens were cut out. Subsequently, using the test specimen under normal conditions (A1) and the test specimen under retention conditions (A2), the temperature of deflection under load (DTUL, unit: °C) was measured using a Toyo Seiki Auto HDT TESTER 6A-2 according to the method of JIS K 7191 at a load of 1.8 MPa. ΔDTUL was calculated according to equation (3) below. Formula (3) ΔDTUL = (DTUL of the 3rd consecutive shot (A2) under dwell conditions) - (DTUL under normal conditions (A1))

[0112] The results are shown in Tables 4-6 below. [Table 4]

[0113] [Table 5]

[0114] [Table 6]

[0115] As is clear from the results above, the resin composition of this embodiment suppresses the generation of silver during retention and improves the tensile fracture strain.

Claims

1. To 100 parts by mass of resin (C) containing 40 to 95 parts by mass of polycarbonate resin (A) and 5 to 60 parts by mass of polyester resin (B), It contains 0.001 to 4 parts by mass of a phosphorus-based transesterification inhibitor (D), Furthermore, the polyester resin (B) contains 0.80 to 8.00 ppm by mass of Ca element, The total amount of Ca and Mg elements in the polyester resin (B) is 1.50 ppm by mass or more and 13.00 ppm by mass or less. Resin composition.

2. The resin composition according to claim 1, wherein the content of Mg element in the polyester resin (B) is 0.10 to 4.00 ppm by mass.

3. The resin composition according to claim 1 or claim 2, wherein the polyester resin (B) contains 200 ppm by mass or more of the element Sb.

4. The resin composition according to any one of claims 1 to 3, wherein the polyester resin (B) comprises polyethylene terephthalate resin.

5. The resin composition according to claim 4, wherein the polyethylene terephthalate resin includes recycled material.

6. The resin composition according to any one of claims 1 to 5, comprising 1 to 100 parts by mass of an inorganic filler (E) per 100 parts by mass of the resin (C).

7. The resin composition according to claim 6, comprising 0.10 parts by mass or more of the phosphorus-based transesterification inhibitor (D) per 100 parts by mass of the inorganic filler (E).

8. The resin composition according to claim 6 or 7, wherein the inorganic filler (E) comprises one or more selected from the group consisting of glass fiber, glass flakes, carbon fiber, talc, mica, wollastonite, and kaolin.

9. A molded article formed from the resin composition according to any one of claims 1 to 8.

10. A resin (C) comprising 40 to 95 parts by mass of polycarbonate resin (A) and 5 to 60 parts by mass of polyester resin (B), 100 parts by mass, This includes melt-kneading 0.001 to 4 parts by mass of a phosphorus-based transesterification inhibitor (D), The polyester resin (B) contains Ca element in a proportion of 0.80 to 8.00 ppm by mass, The total amount of Ca and Mg elements in the polyester resin (B) is 1.50 ppm by mass or more and 13.00 ppm by mass or less. A method for producing a resin composition.

11. A method for producing a resin composition according to claim 10, wherein the resin composition is the resin composition according to any one of claims 1 to 8.