Method for producing a granulation additive

Abstract

The invention relates to a method for producing an additive for improving fertiliser granulation, which consists essentially in using a static turbulence reactor (B) having a preferably spatial geometric configuration with downward tangential injection of a diluted acid (4), generating a high-turbulence vortex (Reynolds number (Re) > 4000) on which a solid raw material (5) containing calcium and magnesium is poured, and subsequently pouring the resulting primary reaction product (6) on a moving bed reactor (C) in which the product is kept static, without agitation, for a long residence time to control the different reaction states, desired hydration level and gradual release of reaction gases, ensuring a homogenous and dry end product (10).

Description

[0001] MANUFACTURING PROCEDURE FOR A GRANULATION ADDITIVE

[0002] OBJECT OF THE INVENTION

[0003] The present invention relates to the process for manufacturing an additive to improve the granulation of fertilizers, particularly fertilizers that require maintaining a low free moisture content.

[0004] BACKGROUND OF THE INVENTION

[0005] Currently, granulated fertilizers are the most widely used compared to those in powder or crystalline form, due to their improved application, both in terms of uniformity and convenience.

[0006] Methods for obtaining magnesium salts, primarily sulfates, have been described (see patent application ES144857A1). These methods are primarily based on the calcination of carbonates or the utilization of the byproducts of such calcination.

[0007] The stability of granulated fertilizers during manufacturing and storage depends on numerous factors, among which is essential to avoid excessive free moisture. The characteristics displayed by certain salts that form multiple hydrates indicate the ability to sequester a certain amount of moisture in the form of water of crystallization. Since the water of crystallization is bound to the soluble salt, forming a stable solid, it does not participate as free water and therefore does not cause problems such as deterioration of grain hardness, the possibility of undesirable chemical reactions, the possibility of grain agglomeration ("caking"), etc.

[0008] Therefore, it would be desirable to have a specific additive to improve the granulation and stability of fertilizers that also acts as a fertilizer itself by supplying magnesium, calcium, and sulfur through direct assimilation by crops and through simultaneous delayed release.

[0009] In this sense, several patent documents have been published, among which we highlight the following: Document CA 2392088 A1 by NORSK HYDRO ASA, discloses a composition for use as an additive in the granulation of fertilizers comprising the following components expressed as percentages by weight: 35-60% magnesium sulfate, 5-35% calcium sulfate, 10-35% of a mixture of magnesium and calcium carbonates and up to 5% water, in a free state, bound or as water of crystallization and the remaining amount of magnesium oxide to meet the balance.

[0010] The process for obtaining the aforementioned composition includes mixing magnesium oxides and magnesium and / or calcium carbonates with sulfuric acid in a fluidized bed reactor operated with hot air.

[0011] On the other hand, it anticipates a fertilizer composition that incorporates, in addition to the granulation additive, other substances such as diammonium phosphate and potassium chloride.

[0012] Document GB 2237800 A (WILLET & SON) describes a granulation process for fertilizer materials characterized by the use of a composition comprising one or more hydrated salts to aid granulation. The composition preferably includes hydrated calcium and magnesium sulfates and more preferably hemihydrated and dihydrated calcium sulfates. This composition finds particular use in granulation processes for nitrogen fertilizers whose nitrogen contribution comes from compounds such as ammonium sulfate, ammonium nitrate, and urea.

[0013] This document highlights the role played by the crystallization of calcium sulfate dihydrate formed in a crystalline lattice matrix in which other fertilizer ingredients are bound.

[0014] Document US2020 / 00398332 A1 (BAUCKE GUIDO et al) includes a granulated composition of hydrated magnesium sulphates and the process for obtaining a fertiliser composition comprising said sulphates mixed with urea, the resulting mixture being stable for storage under ambient conditions. Magnesium sulphates are obtained by digesting magnesium oxide with concentrated sulphuric acid at 50-90% by weight, giving rise to a mixture that mainly comprises magnesium sulphate monohydrate, hydrated magnesium sulphate (5 / 4) and magnesium sulphate dihydrate.

[0015] Although the cited documents describe additives that meet, at least in part, the indicated characteristics, only document CA 2392088 A1 of NORSK HYDRO ASA describes a manufacturing process for the additive using a fluidized bed reactor.

[0016] The facilities and equipment required for an industrial plant based on a fluidized bed reactor using hot air as the fluidizing medium are bulky, require a high investment, and require maintenance. Example 1 of said document indicates the need for a flow rate of approximately 1000 Nm. 3 of air heated to 140 e C per ton of final product. Furthermore, heating this air requires between 30,000 and 40,000 kcal / t of final product. The power of the air compressor described is also high, around 60 kW depending on the air flow rate and pressure mentioned.

[0017] Therefore, it is of great industrial interest to manufacture this additive using a more economically viable process, without additional thermal energy input, minimal electrical consumption, and requiring minimal maintenance.

[0018] DESCRIPTION OF THE INVENTION

[0019] The present invention relates to a manufacturing process that allows for the economical production of a product that can be used primarily as an additive to improve the granulation and stability of other fertilizers. As an additional benefit, it can also serve as a fertilizer that supplies magnesium, calcium, and sulfur, partly for direct assimilation by crops and partly for delayed release. Such an additive must meet the following characteristics:

[0020] • Sequester moisture in the form of water of crystallization, so that the residual free moisture of the granulated fertilizer remains below the desired limits.

[0021] • A crystalline skeleton is formed that strongly binds the grain components, thus providing extra hardness that prevents plastic deformation of the fertilizer grain and its “caking.”

[0022] • The components of the additive are all fertilizer nutrients for plants.

[0023] • These nutrients are available in two forms: a rapidly soluble portion and a slow-solubility portion, which is becoming increasingly important in preventing the eutrophication of lakes, rivers, and groundwater. The present invention essentially relates to the process for manufacturing the aforementioned additive by using a static turbulence reactor in which the finely ground solid raw material is added to a powerful acid vortex. By mixing the finely ground solid material within a turbulent vortex, a very intimate mixture between the acid and the solid is ensured, allowing for a rapid reaction of the raw materials within just a few seconds.

[0024] The reaction achieved with the process of the invention is sufficiently complete and does not require the use of additional thermal energy (unlike those cited in other patent documents); the enthalpy of reaction between the acid and the carbonates of the calcium-magnesium materials used is sufficient. This reactor is completely static and compact, with no moving parts, making it a device that requires virtually no maintenance.

[0025] The manufacturing process of a granulation additive, as described in claim 1, comprises the following steps: preparation of a dilute acid, at a concentration between 69% and 75% w / w. resulting from the dissolution of a concentrated sulfuric acid (96-98%) with water, introduction of the diluted acid into a static swirl reactor configured to generate a powerful diluted acid vortex, introduction of a finely ground solid raw material, comprising calcium-magnesium materials, into the interior of the static swirl reactor and specifically into the diluted acid vortex for mixing with said diluted acid, reacting in a very short time (2 to 5 seconds) and giving rise to a primary reaction product, pouring the primary reaction product onto a moving bed reactor, for kinetic reasons, where it remains static without stirring for a residence time of between 15 and 60 minutes,ensuring a homogeneous and dry final product without external heat input, aspiration of the gases produced in the moving bed reactor by means of an extraction hood located above the moving bed reactor, which allows the introduction of air at room temperature onto the primary reaction product located in the moving bed reactor for cooling the product, giving rise to a product cake, and comminution of the product cake by means of a comminutor to obtain a powdery final product. DESCRIPTION OF THE DRAWINGS,

[0026] To complement the description being made and in order to help better understand the characteristics of the invention, in accordance with a preferred example of practical implementation thereof, a set of drawings is attached as an integral part of said description, in which the following has been represented for illustrative and non-limiting purposes:

[0027] Figure 1.- Shows a schematic representation of an installation that can be used for the application of the process according to the invention.

[0028] Figure 2.- Shows a diagram of the formation of the described vortex.

[0029] PREFERRED EMBODIMENT OF THE INVENTION

[0030] A preferred embodiment of the manufacturing process of a granulation additive that constitutes the object of this invention is described below.

[0031] As can be seen in Figure 1, the installation comprises a dilution tower (A) in which the concentrated sulfuric acid (96-98%) (1) is diluted with water (2) to obtain a diluted acid (4) at a concentration between 69% and 75% w / w.

[0032] Subsequently, said diluted acid (4) together with the finely ground solid raw material (5) which are calcium-magnesium materials, are taken to a static turbulence reactor (B) in which the finely ground solid raw material (5) is added to a powerful vortex of the diluted acid (4) created in the static turbulence reactor (B) due to its configuration, as observed in figure 2.

[0033] The dilution tower (A) can be dispensed with if diluted acid (4) is already available at the aforementioned concentrations, by introducing it directly into the static turbulence reactor (B) as shown in the dashed line.

[0034] It is contemplated that the static turbulence reactor (B) can adopt various geometric configurations that can serve to generate the necessary vortex, but in this case, preferably, a conical configuration is used with downward tangential injection of the acid until the vortex is formed, in which the solid raw material (5) is added. In this static turbulence reactor (B) the mixing of the solid raw material (5) is carried out in a very short time, between 2 and 5 seconds, and in it the reaction of the solid raw material (5) with the diluted acid (4) begins, giving rise to a primary reaction product (6).

[0035] The acid concentration is precisely adjusted so that the heat generated in the reaction evaporates the water to the point of maintaining the precise concentration to obtain calcium sulphate hemihydrate (CaSO4-0.5 H2O), hydrated magnesium sulphate (MgSO4-xH2O), where x represents the average water of crystallization and has a value between 1 and 5, and a free moisture content between 0 and 1.5% w / w.

[0036] For kinetic reasons, the primary reaction product (6) is immediately poured onto a moving bed reactor (C) where it remains static without stirring for a high residence time, between 15 and 60 minutes.

[0037] In this way, it is possible to control the various stages of reaction, the desired degree of hydration and the gradual release of the reaction gases (8), mainly CO2 and H2O, in order to ensure the obtaining of a homogeneous and dry final product (7) without the need for external heat input (the heat of reaction itself is sufficient to evaporate the water).

[0038] The aspiration of these reaction gases (8) is done through a gas extraction hood (D) which are subsequently washed with decontamination equipment (F).

[0039] At the same time as the aspiration is produced, the entry of air at room temperature (9) into a moving bed reactor (C) is facilitated, for the cooling of the primary reaction product (6) giving rise to a product cake (7),

[0040] At the exit of the moving bed reactor (C) there is a shredder (E) for shredding the product cake (7) and obtaining a final powdery product (10).

[0041] Finally, the product is transported to a final product warehouse (G). The composition of the manufactured granulation additive is:

[0042] MgSO4-x H20 35-45% w / w, where x has a value between 1 and 5

[0043] CaSO4-0.5 H20 25-40% w / w

[0044] MgCO3. 10-20% w / w CaCO3.. 10-20% w / w

[0045] Free moisture .0-1 .5 % w / w

[0046] The product thus obtained is suitable for direct use as an additive to promote the granulation of fertilizers using any conventional granulation process (drum, plate, fluid bed, etc.).

[0047] EXAMPLES

[0048] The invention will then be illustrated by tests carried out by the inventors, which demonstrate the effectiveness of the process described in the invention.

[0049] Example 1: Additive manufacturing

[0050] In a facility like the one described above, the following chemical components were used: MgCO3, CaCO3 (said carbonates with a purity of 99%) and 72% sulfuric acid.

[0051] The MgCO3 and CaCO3 were thoroughly mixed and reacted vigorously with the sulfuric acid, reaching a Re greater than 4000 for a time no longer than 5 seconds. The resulting mass was then allowed to rest for 25 minutes.

[0052] The process conditions were:

[0053] - Solid matter ratio (MgCO3 and CaCO3) / final product = 0.66 kg / kg

[0054] - 72% sulfuric acid / final product ratio = 0.27 liters / kg

[0055] - Residence time in secondary reactor = 25 minutes

[0056] - Flow rate = 12.48 Tons / h

[0057] 9.94 Tm / h of a final product with the following composition was obtained:

[0058] MgSO4-3H2O 42.09% w / w (smo)

[0059] CaSO4'0.5H2O 30.78% w / w (smo)

[0060] MgCO31 1.68% w / w (smo)

[0061] CaCO313.36% w / w (smo)

[0062] Free moisture 1.0% w / w (smo). Example 2: Use of the additive for fertilizer granulation

[0063] In order to verify the improvement achieved with the product manufactured according to the invention in the granulation of an NPK fertilizer, 80 t of an NPK 20-10-10 were first manufactured by mixing in a Granulator Plate 1.59 t / h of potassium chloride, 2.52 t / h of urea, 2.10 t / h of ammonium sulfate, 2.10 t / h of diammonium phosphate (DAP), 0.7 t / h of single superphosphate (SSP) and 1.0 t / h of clay.

[0064] Approximately 14% of the fluid phase (a saturated solution of salts from the raw materials used, generated by adding water) was added to this mixture. The granulation temperature was maintained at approximately 48°C. e C. After a drying process at 90 e C in a Trome (in co-current with a mixture of air and natural gas combustion gases) a product with the following characteristics is obtained:

[0065] Granulometry

[0066] > 4 mm 27.37%

[0067] 3 - 4 mm 46.84%

[0068] 2 - 3 mm 18.68% 1 - 2 mm 2.10% < 1 mm 5.00%

[0069] Hardness 34.24 N

[0070] The quantity of inert (clay) is then replaced by the additive manufactured according to example n e1 of the invention. During the granulation process, the additive intervenes in the hydration process by sequestering the moisture from the mixture in the form of crystallization water, forming soluble and stable magnesium salts. Depending on the amount of water sequestered by the additive and after the drying process at 90 ° C, e C in a trommel (in co-flow with a mixture of air and natural gas flue gases), the resulting salts turned out to be a mixture of MgSO4-4H2O (starkeyrite), MgSO4-5H2O (pentahydrite), MgSO4-6H2O (hexahydrite), or MgSO4-7H2O (epsomite). The resulting product has the following characteristics:

[0071] Granulometry

[0072] > 4 mm 17.67%

[0073] 3 - 4 mm 57.33%

[0074] 2 - 3 mm 23.67% 1 - 2 mm 1.33% < 1 mm 0.00%

[0075] Hardness 40.02 N

[0076] It is observed that the use of the additive obtained according to the process of the invention improves the granulation by 23.63%, the granulometry between 2 and 4 mm, and the grain hardness by 16.88%.

[0077] Below is a list of the references used in the figures:

[0078] A Acid dilution tower

[0079] B Static turbulence reactor

[0080] C Moving bed reactor

[0081] D Fume hood

[0082] And Shredder

[0083] F Gas scrubber

[0084] G Final Product Warehouse

[0085] 1 Sulfuric acid (96-98%)

[0086] 2 Dilution water

[0087] 4 Sulfuric acid (69-75%)

[0088] 5 Calcium-magnesium raw material

[0089] 6 Primary reaction product

[0090] 7 Product cake

[0091] 8 Reaction gases

[0092] 9 Air at room temperature

[0093] 10 Powdery final product

Claims

CLAIMS 1. Process for manufacturing a granulation additive comprising the steps of: preparing a dilute acid (4) at a concentration of between 69% and 75% w / w resulting from the dissolution of a concentrated sulfuric acid (96-98%) (1) with water (2), introducing the dilute acid (4) into a static swirl reactor (B) configured to generate a powerful dilute acid vortex (4), introducing a finely ground solid raw material (5) comprising calcium-magnesium materials into the interior of the static swirl reactor and specifically into the dilute acid vortex for mixing with the dilute acid (4), reacting and giving rise to a primary reaction product (6), pouring the primary reaction product (6) onto a moving bed reactor (C) where it remains static without stirring for a residence time of between 15 and 60 minutes,aspiration of the gases produced in the moving bed reactor (C) by means of an extraction hood (D) located above the moving bed reactor (C), which allows the introduction of air at room temperature (9) onto the primary reaction product (6) located in the moving bed reactor (C) for cooling the primary reaction product (6), giving rise to a product cake (7), and comminution of the product cake (7) by means of a comminutor (E) to obtain a final powdery product (10). 2.- The method of claim 1 in which the calcium-magnesium materials do not incorporate magnesium oxide supplementation. 3.- The method of claim 1 in which the static turbulence reactor (B) is of conical configuration and the introduction of the diluted acid is done with a downward tangential injection until the vortex is formed. 4.- The method of claim 3 in which the tangential injection generates the high turbulence vortex overcoming the transient laminar state defined by the Reynolds number (Re) (Re > 4000). 5.- The method of claim 1 wherein the mixing time is less than 5 seconds 6.- The method of claim 5 wherein the mixing time is between 2 and 5 seconds 7.- The method of claim 1 wherein the moving bed reactor (C) is a conveyor belt resistant to sulfuric acid and temperatures of 110-120 e C 8.- The method of claim 1 in which the gases aspirated by the extraction hood are washed with decontamination equipment (F). 9.- The method of claim 1 wherein the shredder is a squirrel cage shredder. 10.- The method of claim 1 additionally comprising the step of regulating: - the flow of solid raw material (5), - the flow rate of the diluted acid (4), - the concentration of the diluted acid (4), - the translation speed of the primary reaction product (6) on the moving bed reactor (C), to adjust the final humidity of the product cake between 0 and 1.5% w / w and to obtain calcium sulfate hemihydrate (CaSO4-0.5 H2O), magnesium sulfate hydrate (MgSO4-xH2O), where x represents the average water of crystallization and has a value between 1 and 5. 11.- The method of claim 1 wherein the dissolution of a concentrated sulfuric acid (96-98%) (1) with water (2) is carried out in a dilution tower (A). 12.- Granulation additive obtained according to the process of any one of claims 1 to 11 comprising the following composition: MgSO4-x H2O 35-45% w / w, where x has a value between 1 and 5 CaSO4-0.5 H20 25-40% w / w MgCO3. 10-20% w / w CaCO310-20% w / w and free moisture content of 0-1.5% w / w