Method for producing 5-hydroxymethylfurfural

Abstract

[Problem] The present invention addresses the problem of providing conditions under which industrial production becomes possible in a method for producing 5-hydroxymethylfurfural from an aqueous solution of a saccharide such as glucose. [Solution] The present invention includes a step for heating an aqueous saccharide solution which contains dimethyl sulfoxide and / or a polar protic organic solvent in the presence of, for example, a compound in which a sulfonic acid group is covalently bound to a titanium oxide, or a step for heating the aqueous saccharide solution by irradiation with microwaves in the presence of, for example, a compound in which a sulfonic acid group is covalently bound to a titanium oxide.

Description

Method for producing 5-hydroxymethylfurfural

[0001] The present invention relates to a compound useful as a catalyst for converting sugars such as glucose or fructose into 5-hydroxymethylfurfural (hereinafter sometimes referred to as "HMF" in this specification), and a method for producing HMF from an aqueous solution of sugars such as glucose or fructose using the compound as a catalyst.

[0002] HMF is an important chemical intermediate that can be synthesized using glucose as a raw material, but its synthetic pathway is extremely complex. The raw material glucose is converted to fructose by skeletal isomerization in the presence of an acid catalyst. The resulting fructose is converted to HMF by a dehydration reaction in the presence of an acid catalyst. HMF is then further hydrolyzed by the acid catalyst in the reaction system to organic acids (formic acid, levulinic acid, etc.). Therefore, a new catalyst for highly selective production of HMF has been desired.

[0003] A solid Lewis acid containing a phosphated titanium oxide, in which phosphate residues are covalently bonded to the surface of amorphous hydrous titanium oxide obtained by treating the amorphous hydrous titanium oxide with phosphoric acid, is known as a catalyst for converting glucose or fructose to HMF (see Patent Document 1). Specifically, 0.05 g of the phosphated titanium oxide was added to a glucose solution containing 0.02 g (0.11 mmol) of D-glucose in 0.2 mL of distilled water and 1.8 mL of tetrahydrofuran (THF), and the reaction was carried out at 20°C for 2 hours, resulting in a conversion of 98% and a yield of 81.2% for HMF.

[0004] International Publication No. 2012-108472

[0005] However, the use of a large amount of THF as a solvent is problematic from an industrial standpoint, and it has been necessary to reduce the amount of organic solvent used as much as possible. An object of the present invention is to provide conditions that enable industrial production in a method for producing HMF from sugars such as glucose and fructose.

[0006] As a result of intensive research aimed at solving the above-mentioned problems, the present inventors have discovered a novel catalyst that can effectively convert sugars such as glucose and fructose. They have also found that the above-mentioned problems can be solved by using a mixed solvent of water and dimethyl sulfoxide and / or a polar protic organic solvent as a reaction solvent for converting sugars such as glucose and fructose to HMF, and by carrying out the reaction of converting sugars such as glucose and fructose to HMF under microwave irradiation, thereby completing the present invention.

[0007] That is, the present invention relates to a compound in which a sulfonic acid group is covalently bonded to titanium oxide. The BET specific surface area of ​​the compound is 200 m ２ The BET specific surface area of ​​the compound is preferably 300 m / g or more. ２ / g or less. The compound is preferably a solid Lewis acid. The compound is preferably a compound that catalyzes a chemical reaction in an aqueous solution. The chemical reaction is preferably a dehydration reaction of a sugar, preferably a reaction that produces 5-hydroxymethylfurfural from the sugar. Furthermore, the sugar is preferably glucose and / or fructose. The present invention also relates to a method for producing 5-hydroxymethylfurfural, which comprises a step of heating an aqueous sugar solution in the presence of the compound. The present invention also relates to a method for producing 5-hydroxymethylfurfural, which comprises a step of heating an aqueous sugar solution A containing dimethyl sulfoxide (hereinafter sometimes referred to as "DMSO" in this specification) and / or a polar protic organic solvent in the presence of the compound or a compound in which a phosphono group is covalently bonded to titanium oxide. The present invention also relates to a method for producing 5-hydroxymethylfurfural, which comprises a step of heating an aqueous sugar solution B by microwave irradiation in the presence of the compound or a compound in which a phosphono group is covalently bonded to titanium oxide. The aqueous saccharide solution B is preferably an aqueous solution containing dimethyl sulfoxide and / or a polar protic organic solvent. The polar protic organic solvent is preferably an alcohol having 1 to 6 carbon atoms, and more preferably an alcohol having 3 to 5 carbon atoms. The saccharide is preferably glucose and / or fructose. The compound in which a phosphono group is covalently bonded to titanium oxide is preferably a solid Lewis acid. The present invention also relates to a method for producing the compound by treating titanium oxide with sulfuric acid.

[0008] The compound and production method of the present invention can significantly reduce the amount of organic solvent used, and are therefore suitable for industrial production of HMF.

[0009] The compound of the present invention contains titanium oxide and a sulfonic acid group (—SO ３The titanium oxide is a compound in which two or more metals (H) are covalently bonded to each other. The titanium oxide is not particularly limited, but specific examples include crystalline titanium oxides such as rutile, anatase, and brookite; amorphous titanium oxide; hydrous titanium oxides such as orthotitanic acid and metatitanic acid; titanium hydroxide; composite oxides of titanium and different metals such as lithium titanate, barium titanate, and strontium titanate; and hydrolysis products of titanium oxide precursors. These may be used alone or in combination of two or more.

[0010] The titanium oxide may or may not be doped with a metal element (excluding titanium; the same applies hereinafter), and may or may not be coated with a compound containing a metal element. Examples of the metal element include aluminum, gallium, indium, thallium, magnesium, manganese, calcium, niobium, tantalum, zirconium, silicon, zinc, cerium, iron, tungsten, molybdenum, and vanadium. When the titanium oxide is doped with a metal element, the doping rate of the metal element relative to the number of moles of titanium atoms is preferably 10 mol% or less, more preferably 5 mol% or less, even more preferably 1 mol% or less, and particularly preferably 0.5 mol% or less.

[0011] The titanium oxide can be obtained, for example, by hydrolysis of a titanium oxide precursor. Examples of the titanium oxide precursor include inorganic titanium compounds such as titanium hydroxide, titanic acid, titanium trichloride, titanium tetrachloride, titanium tetrabromide, titanium sulfate, and titanium oxysulfate; titanium alkoxide compounds such as tetraisopropoxytitanium, tetra-n-butoxytitanium, tetrakis(2-ethylhexyloxy)titanium, and tetrastearyloxytitanium; titanium acylate compounds; titanium chelate compounds such as diisopropoxybis(acetylacetonato)titanium, isopropoxy(2-ethyl-1,3-hexanediolato)titanium, and hydroxybis(lactato)titanium; organic acid titanium compounds such as titanium oxalate and titanium tetraacetate; and water-soluble titanium complexes. Among these, the titanium oxide precursor is preferably at least one selected from the group consisting of titanium chloride, titanium oxalate, titanium sulfate, and titanium alkoxide.

[0012] The number of carbon atoms constituting the alkoxy group in the titanium alkoxide is preferably 1 to 6, more preferably 2 to 4. The alkoxy group may be linear, branched, or cyclic.

[0013] The hydrolysis reaction of the titanium oxide precursor can be carried out by reacting the titanium oxide precursor with water in the presence of an acid catalyst or a base catalyst as necessary. The temperature during the hydrolysis reaction is preferably 10 to 100° C., more preferably 20 to 50° C. The time required for the hydrolysis reaction can be appropriately set depending on the reaction temperature, reaction scale, etc., but is preferably 0.5 to 48 hours, more preferably 10 to 24 hours.

[0014] The hydrolysis reaction can be repeated multiple times. Examples of acids used in the hydrolysis reaction include hydrochloric acid, sulfuric acid, and nitric acid. Examples of bases used in the hydrolysis reaction include ammonia, sodium hydroxide, and potassium hydroxide.

[0015] The mixing ratio of the titanium oxide precursor to the acid catalyst or the base catalyst is not particularly limited, but is usually preferably in the molar ratio range of 1:0.1 to 1:10, and more preferably 1:1 to 1:5. In addition, in the hydrolysis reaction, the initial concentration of the titanium oxide precursor in the entire reaction mixture including water is preferably in the range of 1 to 50 mass %, and more preferably 10 to 20 mass %.

[0016] The hydrolysis product of the titanium oxide precursor is preferably an amorphous hydrous titanium oxide. Whether the amorphous hydrous titanium oxide contains water molecules can be confirmed by surface measurement using an infrared spectrophotometer or by weight loss due to heat dehydration treatment under vacuum. Whether the amorphous titanium oxide is amorphous can also be determined by X-ray diffraction.

[0017] In the present invention, "amorphous" means including an amorphous portion that can be confirmed by X-ray diffraction, and includes not only amorphous hydrous titanium oxides that are amorphous as a whole, but also those that are partially amorphous. The amorphous pattern confirmed by X-ray diffraction specifically refers to a broad wave pattern without a clear crystalline diffraction pattern.

[0018] The compound of the present invention is a compound in which a sulfonic acid group is covalently bonded to the titanium oxide. The compound can be obtained, for example, by treating the titanium oxide with sulfuric acid. Specifically, the sulfuric acid treatment can be carried out by immersing the titanium oxide in an aqueous sulfuric acid solution (for example, a 0.5 to 2 M aqueous sulfuric acid solution) and stirring it.

[0019] The temperature of the sulfuric acid treatment is preferably in the range of 10° C. to 100° C., more preferably in the range of 20° C. to 40° C. The time of the sulfuric acid treatment is the time required for producing the desired compound and is appropriately selected depending on the conditions such as the treatment temperature, but is preferably in the range of 1 hour to 96 hours, more preferably in the range of 24 hours to 72 hours.

[0020] The titanium oxide treated with sulfuric acid can be dried by heating if necessary. The heating temperature is not particularly limited, but a temperature at which adhering water can be removed is preferred, and 100° C. or higher is preferable. When vacuum drying by heating is performed, the temperature can be adjusted appropriately depending on the degree of vacuum.

[0021] In the FT-IR spectrum, the titanium oxide not treated with sulfuric acid had a peak at 1180 cm －１ In contrast, the solid Lewis acid of the present invention has a signal (peak) at 1180 cm due to the stretching vibration of the S—O bond. －１ This is because sulfonic acid groups are covalently bonded to hydroxyl groups (Ti—OH) on the surface of the titanium oxide skeleton, forming Ti—O—SO ２ This indicates that a chemical structure of (OH) is formed. Furthermore, the compound is preferably a compound that functions as a solid Lewis acid.

[0022] The compound of the present invention may also be bonded to functional groups other than sulfonic acid groups. However, it is preferable that sulfonic acid groups have the largest molar fraction among the functional groups covalently bonded to the titanium oxide, and the number of sulfonic acid groups in the total number of functional groups covalently bonded to the titanium oxide is preferably 60% or more, more preferably 80% or more, even more preferably 95% or more, and particularly preferably 99% or more, in terms of molar fraction. Note that when the titanium oxide is bonded to both sulfonic acid groups and phosphono groups, this titanium oxide is treated as the compound of the present invention, not as a titanium oxide phosphate.

[0023] The titanium oxide in the compound may or may not be doped with a metal element, and may or may not be coated with a compound containing a metal element. Examples of the metal element include aluminum, gallium, indium, thallium, magnesium, manganese, calcium, niobium, tantalum, zirconium, silicon, zinc, cerium, iron, tungsten, molybdenum, and vanadium. When the titanium oxide is doped with the metal element, the doping ratio of the metal element to titanium atoms is preferably 10 mol% or less, more preferably 5 mol% or less, and even more preferably 1 mol% or less.

[0024] The BET specific surface area of ​​the compound of the present invention is not particularly limited, but in order to carry out the chemical reaction described below more efficiently, it is preferred that the BET specific surface area be 100 m ２ / g or more, and ２ / g or more. This is the BET specific surface area of ​​100 m ２ The present inventors presume that this is because, by setting the saturation concentration at or above 1 / g, the number of active sites that can come into contact with the target substance (e.g., sugars such as glucose and fructose) that promotes the chemical reaction described below is sufficiently increased.

[0025] The BET specific surface area of ​​the compound of the present invention is 400 m from the viewpoint of superior durability (performance stability) when used as a catalyst for a chemical reaction described below. ２ / g or less, and ２ This is because the BET specific surface area is 400 m / g or less. ２The present inventors presume that this is because, by setting the pore size of the catalyst of the present invention to be 0.01 / g or less, the pore size of the catalyst of the present invention is maintained within an appropriate range, substances generated in or introduced into the pores can be released from the pores, and the activity of the catalyst can be easily maintained.

[0026] The BET specific surface area was determined by adsorbing nitrogen gas onto the surface of a target object (for example, the compound of the present invention) at liquid nitrogen temperature and then determining the adsorption / desorption isotherm based on the adsorption / desorption of nitrogen gas at -196°C. The sample was treated under vacuum at 150°C for 3 hours before measurement. The analysis conditions were as follows. [Measurement conditions] Measurement device: High-speed specific surface / pore distribution measurement device BELSORP-mini2 (manufactured by MicrotracBEL) Adsorbed gas: Nitrogen 99.99995% by volume Adsorption temperature: Liquid nitrogen temperature (-196°C)

[0027] The compound of the present invention can be used as a catalyst for various chemical reactions. The catalytic activity of the compound of the present invention is not lost in the presence of water molecules, and therefore the compound can be used as a catalyst for promoting various chemical reactions, particularly in aqueous solutions. Specific examples of the various chemical reactions include various dehydration reactions, allylation reactions, aldol condensation reactions, Michael addition reactions, alkylation reactions, isomerization reactions, hydrolysis reactions, and the like. Among these, preferred examples of the various chemical reactions include skeletal isomerization reactions of saccharides and dehydration reactions of saccharides. More specific examples include reactions for producing HMF from saccharides.

[0028] The saccharides may be D-isomers, L-isomers, or a mixture thereof. In the mixture, the content of the D-isomer is preferably 20% by mass or more but less than 100% by mass, more preferably 90% by mass or more but less than 100% by mass, even more preferably 99% by mass or more but less than 100% by mass, and particularly preferably 99.9% by mass or more but less than 100% by mass, based on the total mass of the D-isomers and the L-isomers.

[0029] Specific examples of the sugars include allose, talose, gulose, glucose, altrose, mannose, galactose, idose, psicose, fructose, sorbose, and tagatose, with glucose and fructose being preferred. These sugars can be used alone or in combination of two or more.

[0030] When the compound of the present invention is used as a catalyst for various chemical reactions, the form of the compound of the present invention is not limited, but is preferably particulate. When a chemical reaction using the compound of the present invention is carried out in a batch system, the particle size of the compound of the present invention measured by X-ray diffraction (XRD) or small angle X-ray scattering (SAXS) is preferably in the range of 1 nm to 250 nm, more preferably in the range of 3 to 50 nm, and even more preferably in the range of 5 to 10 nm.

[0031] When a chemical reaction using the compound of the present invention is carried out in a flow system, the lower limit of the volume average particle diameter of the compound of the present invention can be appropriately selected depending on the chemical reaction. From the viewpoint of reducing the back pressure of a column packed with catalyst particles, the lower limit of the volume average particle diameter of the compound of the present invention is preferably 1 μm or more, more preferably 5 μm or more, even more preferably 10 μm or more, still more preferably 20 μm or more, particularly preferably 30 μm or more, and most preferably 40 μm or more.

[0032] The upper limit of the volume average particle size is not particularly limited and can be appropriately selected depending on the chemistry.From the viewpoint of increasing the surface area per unit volume, the upper limit of the volume average particle size is preferably 500 μm or less, more preferably 200 μm or less, and even more preferably 100 μm or less.When the chemical reaction using the compound of the present invention is carried out by flow reaction, the compound of the present invention can be granulated to a volume average particle size as required using a granulation method such as extrusion molding or tumbling granulation, which is the same as the particles used when the chemical reaction is carried out in a batch system.

[0033] The production of HMF of the present invention involves a step of heating an aqueous saccharide solution in the presence of the compound of the present invention. Hereinafter, the aqueous saccharide solution will be referred to as the "reaction solution of the present invention," and the mixture obtained by adding the compound of the present invention to the reaction solution will be referred to as the "mixture of the present invention." The production method of HMF can be carried out by either a batch system or a flow system.

[0034] When the HMF production method is carried out batchwise, the concentration of the saccharide in the mixture is not particularly limited, but is preferably in the range of 0.01 to 90 mass / volume (wt / v)%, more preferably 1.0 to 85 mass / volume%, even more preferably 2.0 to 80 mass / volume%, and particularly preferably 3.0 to 70 mass / volume%, relative to the volume of the mixture.

[0035] When the HMF production method is carried out by a flow system, the concentration of the saccharide in the reaction solution is preferably in the range of 0.5 to 50% by mass, more preferably in the range of 1 to 40% by mass, and even more preferably in the range of 5 to 30% by mass.

[0036] When the HMF production method is carried out in a batch system, the concentration of the compound in the present mixed solution is not particularly limited, but is preferably in the range of 0.05 to 300% by mass, more preferably 1 to 200% by mass, relative to the saccharide.

[0037] When the HMF production method is carried out in a batch system or a flow system, the reaction temperature (i.e., the temperature at which the reaction solution of the present invention is brought into contact with the compound; the same applies hereinafter in this specification) is preferably in the range of 80 to 180°C, more preferably in the range of 100 to 170°C.

[0038] When the HMF production method is carried out in a batch system, the reaction time is the time during which the conversion rate of glucose or fructose, the yield of HMF, and the like reach desired values, and is appropriately selected depending on conditions such as the reaction temperature. The reaction time is preferably in the range of 10 minutes to 24 hours, and more preferably in the range of 2 hours to 6 hours.

[0039] When the HMF production method is carried out by a flow system, the reaction time is preferably in the range of 1 minute to 2 hours, more preferably in the range of 5 minutes to 30 minutes.

[0040] In carrying out the HMF production method, any means capable of carrying out a reaction at high temperature and pressure may be appropriately employed, whether a batch system or a flow system is employed.

[0041] Furthermore, the method A for producing HMF of the present invention comprises a step of heating an aqueous saccharide solution A containing dimethyl sulfoxide and / or a polar protic organic solvent in the presence of the compound of the present invention or a compound in which a phosphono group (-PO3H2) is covalently bonded to a titanium oxide (hereinafter sometimes referred to as "phosphated titanium oxide" in the specification). Hereinafter in the specification, the compound of the present invention and the phosphated titanium oxide are collectively referred to as the "specific compound."

[0042] Hereinafter, in the HMF production method A of the present invention, the saccharide aqueous solution A containing dimethyl sulfoxide and / or a polar protic organic solvent is also referred to as the "specific reaction solution," and the mixture obtained by adding a specific compound to the specific reaction solution is also referred to as the "specific mixed solution." Note that, in this specification, the specific reaction solution and the specific mixed solution may be separated into an aqueous phase and an oil phase. The HMF production method can be carried out by either a batch system or a flow system.

[0043] The titanium phosphate oxide can be produced by using phosphoric acid instead of sulfuric acid in the production method of the compound of the present invention. The titanium phosphate oxide also has the same properties as the compound of the present invention, and the details are the same as those described above for the compound of the present invention.

[0044] Whether or not a phosphono group is covalently bonded to titanium oxide in the titanium phosphate compound can be confirmed by the contents described in WO 2012 / 108472.

[0045] When the HMF production method A is carried out in a batch system, the content of dimethyl sulfoxide in the specific mixed solution is preferably in the range of 0.1 to 1.0 M, more preferably in the range of 0.2 to 0.8 M, even more preferably in the range of 0.3 to 0.7 M, and particularly preferably in the range of 0.4 to 0.6 M.

[0046] When the HMF production method A is carried out by a flow system, the concentration of dimethyl sulfoxide in the specific reaction solution is preferably in the range of 0.1 to 1.0 M, more preferably in the range of 0.2 to 0.8 M, even more preferably in the range of 0.3 to 0.7 M, and particularly preferably in the range of 0.4 to 0.6 M.

[0047] When the HMF production method A is carried out in a batch system, the content of the polar protic organic solvent in the specific mixed solution is preferably in the range of 20 to 200% by volume, more preferably in the range of 50 to 150% by volume, even more preferably in the range of 70 to 130% by volume, and particularly preferably in the range of 80 to 120% by volume, relative to the total volume of the specific mixed solution.

[0048] When the HMF production method A is carried out in a flow system, the content of the polar protic organic solvent in the specific reaction solution is preferably in the range of 20 to 200% by volume, more preferably in the range of 50 to 150% by volume, even more preferably in the range of 70 to 130% by volume, and particularly preferably in the range of 80 to 120% by volume, relative to the total volume of the specific reaction solution.

[0049] Specific examples of the polar protic organic solvent contained in the specific reaction solution or the specific mixed solution include alcohols, aliphatic amines, alicyclic amines, acid amides, and carboxylic acids. These may be used alone or in combination of two or more.

[0050] The polar protic organic solvent is preferably an alcohol having 1 to 6 carbon atoms. Specific examples of alcohols having 1 to 6 carbon atoms include methanol, ethanol, n-propanol, isopropanol, cyclopropanol, n-butanol, isobutanol, s-butanol, cyclobutanol, n-pentanol, isopentanol, s-pentanol, neopentyl alcohol, cyclopentanol, n-hexanol, isohexanol, s-hexanol, 2,2-dimethyl-1-butanol, and cyclohexanol. Of these, alcohols having 3 to 5 carbon atoms are preferred. These may be used alone or in combination of two or more.

[0051] Dimethyl sulfoxide and the polar protic organic solvent can be used alone, but it is more preferable to use them as a mixture.

[0052] The specific mixed solution or the specific reaction solution may or may not contain a component other than water, a sugar, the compound of the present invention, the titanium oxide phosphate, dimethyl sulfoxide, or the polar protic organic solvent (hereinafter also referred to as "other component"). The content of the other component is preferably 0 to 200% by mass, more preferably 0 to 20% by mass, even more preferably 0 to 5% by mass, and particularly preferably 0 to 1% by mass, based on the total mass of the specific mixed solution or the specific reaction solution.

[0053] When the HMF production method A is carried out in a batchwise manner, the concentration of the saccharide in the specific mixed solution is not particularly limited, but is preferably in the range of 0.01 to 90 mass / volume (wt / v)%, more preferably 1.0 to 85 mass / volume%, even more preferably 2.0 to 80 mass / volume%, and particularly preferably 3.0 to 70 mass / volume%, relative to the volume of the specific mixed solution.

[0054] When the HMF production method A is carried out in a flow system, the concentration of the saccharide in the specific reaction solution is preferably in the range of 0.5 to 50% by mass, more preferably in the range of 1 to 40% by mass, and even more preferably in the range of 5 to 30% by mass.

[0055] When the HMF production method A is carried out in a batchwise manner, the concentration of the specific compound in the specific mixed solution is not particularly limited, but is preferably in the range of 0.05 to 300% by mass, more preferably 1 to 200% by mass, relative to the saccharide. The specific compound is the compound of the present invention alone, the titanium phosphate oxide alone, or a mixture of the compound of the present invention and the titanium phosphate oxide in an appropriate ratio.

[0056] When the HMF production method A is carried out in a batch or continuous manner, the reaction temperature is preferably in the range of 80 to 180°C, more preferably in the range of 100 to 170°C.

[0057] The reaction time when the HMF production method A is carried out in a batch system is the time during which the sugar conversion rate, HMF yield, and the like reach desired values, and is appropriately selected depending on conditions such as the reaction temperature. The reaction time is preferably in the range of 10 minutes to 24 hours, and more preferably in the range of 2 hours to 6 hours.

[0058] When the HMF production method A is carried out by a flow system, the reaction time is preferably in the range of 1 minute to 2 hours, more preferably in the range of 5 minutes to 30 minutes.

[0059] In carrying out the HMF production method A, whether a batch system or a flow system is employed, the reaction vessel can be a vessel capable of carrying out a reaction at high temperature and pressure, as appropriate.

[0060] Furthermore, the method B for producing HMF of the present invention comprises a step of heating the aqueous saccharide solution B by irradiating it with microwaves in the presence of the compound of the present invention or the titanium phosphate oxide.

[0061] Specific examples of the chemical reaction apparatus that performs a chemical reaction by irradiating microwaves include those disclosed in Japanese Patent Application Laid-Open Nos. 2011-235262, 2011-235263, and 2011-240213.

[0062] The frequency of the microwaves to be irradiated can be set arbitrarily depending on the reaction temperature and reaction time to be set, but specifically, it is preferably in the range of 300 MHz to 300 GHz, more preferably in the range of 900 MHz to 50 GHz, and more specifically, examples thereof include 2.45 GHz, 5.8 GHz, 24 GHz, 913 MHz, etc. Furthermore, heating may be performed by irradiating microwaves of two or more frequencies.

[0063] The microwave irradiation output can be determined arbitrarily depending on the type and scale of the reaction, etc. The microwave irradiation method may be a multimode method or a single mode method. The microwave irradiation may be performed continuously or intermittently (discontinuously).

[0064] The microwave irradiation time is preferably 10 to 100%, more preferably 50 to 100%, and even more preferably 80 to 100% of the total reaction time. In the HMF production method B, the reaction time is, for example, preferably in the range of 1 minute to 2 hours, and more preferably in the range of 5 minutes to 30 minutes.

[0065] In the HMF production method B, the reaction vessel may be a vessel capable of carrying out a reaction at high temperature and pressure as appropriate. The microwave output may be adjusted as appropriate to achieve a desired reaction temperature. In the HMF production method B, the heat source for the reaction may be microwaves alone, or other heat sources may be used in combination.

[0066] In the HMF production method B, the saccharide aqueous solution B preferably contains dimethyl sulfoxide and / or a polar protic organic solvent. The amounts of dimethyl sulfoxide and the polar protic organic solvent used, and specific examples of the polar protic organic solvent are as described above.

[0067] The HMF production method B can be carried out either by a batch system or a flow system. In each of the HMF production methods B, the sugars are specifically as described above, but glucose and fructose are particularly preferred. These sugars can be used alone or in combination of two or more.

[0068] In the HMF production method of the present invention and HMF Production Methods A and B of the present invention, glucose is skeletal isomerized by the compound of the present invention to form fructose, which is then converted to HMF by successive dehydration reactions. The compound of the present invention functions in aqueous solvents without being deactivated, and can therefore be used as a catalyst for chemical reactions in aqueous solutions.

[0069] It is presumed that the compound of the present invention has a Brønsted acid function due to the titanium oxide having a sulfonic acid group, which promotes the dehydration reaction without the use of DMSO or the polar protic organic solvent, resulting in a compound with good reactivity. Furthermore, it is presumed that the use of DMSO or the polar protic organic solvent in the HMF production method of the present invention and HMF Production Methods A and B of the present invention makes it possible to lower the activation energy of the dehydration reaction, further facilitating the reaction.

[0070] Next, the present invention will be described in more detail using examples, but the scope of the present invention is not limited to these examples.

[0071] (High-Performance Liquid Chromatography (HPLC) Measurement Method) Analysis was performed using a photodiode array (PDA; 254 nm, 283 nm) and a refractive index (RI) detector under the following conditions: HPLC: LC-2000 (Jasco) Aminex HPX-87H column (7.8 mm diameter x 300 mm, Bio-Rad Laboratories Inc. Co. Ltd.) Eluent (0.5 mM H ２ SO ４(0.5 mol / L sulfuric acid (1N) reagent solution (Kanto Chemical Cat. No. 37880-08) diluted 100 times) Flow rate (0.5 mL / min) Column temperature (308 K) The measurement sample was diluted with water, and 10 μL was injected and measured, and the retention time of HMF was 41.7 minutes. Quantitation was performed using the calibration curve method.

[0072] Unless otherwise specified below, the treatments and steps in each test were carried out at 25°C.

[0073] 36 g of anatase-type titanium oxide (product name: ST-01, manufactured by Ishihara Sangyo Kaisha, Ltd., X-ray particle size: 7 nm) was added to 1800 ml of a 1 M aqueous sulfuric acid solution and stirred for 48 hours. The reaction solution was filtered, and the residue was washed with distilled water until the pH of the filtrate reached 3 to 4. The resulting white solid was dried at 120°C for 16 hours to obtain 32 g of a compound in which sulfonic acid groups were covalently bonded to titanium oxide as a white solid (the pH was measured at 25°C). The BET surface area of ​​the resulting compound was measured and found to be 280 m ２ / g.

[0074] When the FT-IR spectrum was measured, the titanium oxide without sulfuric acid treatment showed a peak at 1180 cm －１ In contrast, in the compound of the present invention, a signal (peak) due to the stretching vibration of the S—O bond is present at 1180 cm －１ This is because sulfonic acid groups are covalently bonded to hydroxyl groups (Ti—OH) on the surface of the titanium oxide skeleton, forming Ti—O—SO ２ This indicates that the chemical structure of (OH) is formed.

[0075] [Reference Example] 18 ml of nitric acid (specific gravity 1.38) and 36 g of anatase-type titanium oxide (product name: ST-01, manufactured by Ishihara Sangyo Kaisha, Ltd., X-ray particle size: 7 nm) were added to 1800 ml of a 1 M aqueous phosphoric acid solution, and the mixture was stirred for 48 hours. The reaction solution was filtered, and the residue was washed with distilled water until the pH of the filtrate reached 3 to 4. The resulting white solid was dried at 120°C for 16 hours, yielding 32 g of a white solid Lewis acid in which a phosphono group was covalently bonded to titanium oxide. The BET surface area of ​​the resulting solid Lewis acid was measured and found to be 290 m ２ / g.

[0076] A 5 ml mixed solution was prepared by dissolving 1.0 g of the compound obtained in Example 1, 0.5 g of D-glucose, and distilled water, and the resulting mixed solution was placed in a pressure-resistant glass container and sealed. Next, the pressure-resistant glass container was kept sealed, and the mixed solution was heated and reacted at 120°C for 4 hours while stirring. The resulting reaction solution was quantified by high-performance liquid chromatography, confirming that 94 mM of HMF was obtained in the reaction solution. However, when quantifying the reaction solution by high-performance liquid chromatography, the compound obtained in Example 1 was removed from the reaction solution by filtration beforehand, and the value of the HMF concentration in the reaction solution is the concentration of HMF in the reaction solution from which the compound obtained in Example 1 was removed, and this also applies to the following test examples. In the solution of this example, the amount of the compound obtained in Example 1 was 200% by mass relative to the total mass of D-glucose, and the amount of D-glucose was 10% by mass / volume relative to the volume of the mixed solution.

[0077] The same procedure as in Example 2 was carried out except that 2.2 mmol of dimethyl sulfoxide (DMSO) (corresponding to a DMSO concentration of 0.43 M in the solution to which DMSO was added) was further added to the mixed solution in Example 2, and it was confirmed that HMF was obtained at 108 mM in the reaction solution.

[0078] The same procedure as in Example 2 was carried out, except that 5 ml of n-butanol was further added to the mixed solution in Example 2, and HMF was obtained at 148 mM. Note that although the reaction solution separated into an aqueous phase and an oil phase, the concentration of HMF obtained in the reaction solution described here is the concentration of the entire reaction solution separated into the aqueous phase and the oil phase (i.e., the average concentration of the aqueous phase and the oil phase). The same applies hereinafter to the case where the reaction solution separates into the aqueous phase and the oil phase.

[0079] The same procedure as in Example 4 was carried out except that the amount of D-glucose added was changed to 1.25 g, and HMF was obtained at 271 mM in the reaction solution.

[0080] The same procedure as in Example 4 was carried out except that the amount of D-glucose added was changed to 2.0 g, and HMF was obtained at 382 mM.

[0081] The same procedure as in Example 2 was carried out except that 2.2 mmol of dimethyl sulfoxide (DMSO) and 5 ml of n-butanol were further added to the mixed solution in Example 2, and HMF was obtained at 150.1 mM.

[0082] The same procedure as in Example 7 was carried out except that the amount of D-glucose added was changed to 1.25 g, and HMF was obtained at 285.5 mM.

[0083] The same procedure as in Example 7 was carried out except that the amount of D-glucose added was changed to 2.0 g, and HMF was obtained at 390.4 mM.

[0084] The compound obtained in Example 1 was packed into a cylindrical pressure column with an inner diameter of 7.6 mm and a height of 150 mm, and the temperature was maintained at 160 ° C. A 25% by mass glucose aqueous solution (reaction solution) was passed through this cylindrical pressure column maintained at 160 ° C. at a flow rate of 0.5 mL / min for 4 hours. The number of times the solution was passed was one time. After passing the reaction solution, the reaction solution was quantified by high performance liquid chromatography, and it was confirmed that 125 mM HMF was obtained. In this example, the average contact time between the reaction solution and the compound of the present invention was 13.6 minutes.

[0085] A 5 ml mixed solution was prepared by mixing 1.0 g of the compound obtained in Example 1, 2.0 g of D-glucose, and distilled water, and the resulting mixed solution was placed in a pressure-resistant glass container and sealed. Next, while maintaining the pressure-resistant glass container sealed, the mixed solution inside was irradiated with 2.45 GHz microwaves for 10 minutes while stirring. The microwave output was set so that the temperature of the mixed solution during irradiation was 160°C. Quantitation of the resulting reaction solution by high-performance liquid chromatography revealed that 271 mM HMF was obtained in the reaction solution. In this example, the amount of the compound of the present invention in the mixed solution was 50% by mass relative to the total mass of D-glucose, and the amount of D-glucose was 40% by mass / volume relative to the total volume of the mixed solution.

[0086] The same procedure as in Example 11 was carried out except that 2.2 mmol of dimethyl sulfoxide (DMSO) (corresponding to a concentration of 0.43 M in the mixed solution) was further added to the mixed solution in Example 11, thereby obtaining 392 mM HMF.

[0087] The same procedure as in Example 11 was carried out except that 5 ml of n-butanol was further added to the mixed solution in Example 11, and HMF was obtained at 485 mM.

[0088] The same procedure as in Example 11 was carried out except that the amount of D-glucose added was changed to 0.5 g and 5 ml of n-butanol was further added, and HMF was obtained at 170 mM.

[0089] The same procedure as in Example 11 was carried out except that the amount of D-glucose added was changed to 1.25 g and 5 ml of n-butanol was further added, and HMF was obtained at 322 mM.

[0090] 1 g of the compound obtained in Reference Example, 0.5 g of D-glucose, and distilled water were mixed to make 5 ml of solution, and the mixture containing 5 mL of n-butanol was placed in a pressure-resistant glass vessel and sealed. The mixture was reacted at 120°C for 4 hours while stirring. The resulting reaction solution was quantified by high-performance liquid chromatography, revealing that 148.8 mM HMF was obtained.

[0091] The same procedure as in Example 16 was carried out except that 2.2 mmol of dimethyl sulfoxide (DMSO) was further added to the mixed solution in Example 16, and HMF was obtained at 180.9 mM.

[0092] The same procedure as in Example 10 was carried out using the compound obtained in the Reference Example, except that DMSO was added to a 25% glucose aqueous solution so that the DMSO concentration in the entire solution to which DMSO was added was 0.43 M, and HMF was obtained at 151 mM.

[0093] The same procedure as in Example 2 was carried out except that D-fructose was used instead of D-glucose, and HMF was obtained at 154.2 mM.

[0094] Comparative Example 1 The same procedure as in Example 10 was carried out except that the compound obtained in Reference Example was used, and HMF was obtained at 113 mM.

[0095] Comparative Example 2 The same procedure as in Example 2 was carried out except that D-fructose was used instead of D-glucose and anatase-type titanium oxide (product name: ST-01, manufactured by Ishihara Sangyo Kaisha, Ltd., X-ray particle size: 7 nm) was used instead of the compound obtained in Example 1, and 89.8 mM HMF was obtained.

[0096] Comparative Example 3 The same procedure as in Example 4 was carried out except that anatase-type titanium oxide (product name: ST-01, manufactured by Ishihara Sangyo Kaisha, Ltd., X-ray particle size: 7 nm) was used instead of the compound obtained in Example 1, and HMF was obtained at 55.3 mM.

[0097] Comparative Example 4 The same procedure as in Example 4 was carried out except that tetrahydrofuran was used instead of n-butanol and heating was carried out at 70° C., whereby 0.5 mM HMF was obtained.

[0098] The method for producing HMF of the present invention is useful as a method for industrially producing HMF from sugars such as glucose.

Claims

1. A compound formed by covalently bonding a sulfonic acid group to titanium oxide.

2. The BET specific surface area of ​​the compound is 200 m ２ The compound according to claim 1, wherein the molecular weight of the compound is 1 / g or more.

3. The BET specific surface area of ​​the compound is 300 m ２ The compound according to claim 1 or 2, wherein the molecular weight of the compound is 1 / g or less.

4. The compound according to claim 1 or 2, wherein the compound is a solid Lewis acid.

5. The compound according to claim 1 or 2, wherein the compound is a compound that catalyzes a chemical reaction in an aqueous solution.

6. The compound according to claim 5, wherein the chemical reaction is a dehydration reaction of a saccharide.

7. The compound according to claim 5, wherein the chemical reaction is a reaction for producing 5-hydroxymethylfurfural from sugars.

8. The compound according to claim 6, wherein the saccharide is glucose and / or fructose.

9. The compound according to claim 7, wherein the saccharide is glucose and / or fructose.

10. A method for producing 5-hydroxymethylfurfural, comprising the step of heating an aqueous saccharide solution in the presence of the compound according to claim 1 or 2.

11. A method for producing 5-hydroxymethylfurfural, comprising the step of heating an aqueous saccharide solution containing dimethyl sulfoxide and / or a polar protic organic solvent in the presence of the compound according to claim 1 or 2 or a compound in which a phosphono group is covalently bonded to titanium oxide.

12. A method for producing 5-hydroxymethylfurfural, comprising the step of heating an aqueous saccharide solution by irradiating it with microwaves in the presence of the compound according to claim 1 or 2 or a compound in which a phosphono group is covalently bonded to titanium oxide.

13. A method for producing 5-hydroxymethylfurfural according to claim 12, wherein the aqueous saccharide solution is an aqueous solution containing dimethyl sulfoxide and / or a polar protic organic solvent.

14. The method for producing hydroxymethylfurfural according to claim 11, wherein the polar protic organic solvent is an alcohol having 1 to 6 carbon atoms.

15. The method for producing hydroxymethylfurfural according to claim 13, wherein the polar protic organic solvent is an alcohol having 1 to 6 carbon atoms.

16. The method for producing 5-hydroxymethylfurfural according to claim 11, wherein the polar protic organic solvent is an alcohol having 3 to 5 carbon atoms.

17. The method for producing 5-hydroxymethylfurfural according to claim 13, wherein the polar protic organic solvent is an alcohol having 3 to 5 carbon atoms.

18. A method for producing 5-hydroxymethylfurfural according to claim 10, wherein the sugar is glucose and / or fructose.

19. A method for producing 5-hydroxymethylfurfural according to claim 11, wherein the sugar is glucose and / or fructose.

20. A method for producing 5-hydroxymethylfurfural according to claim 12, wherein the sugar is glucose and / or fructose.

21. The method for producing 5-hydroxymethylfurfural according to claim 11, wherein the compound in which a phosphono group is covalently bonded to a titanium oxide is a solid Lewis acid.

22. The method for producing 5-hydroxymethylfurfural according to claim 12, wherein the compound in which a phosphono group is covalently bonded to a titanium oxide is a solid Lewis acid.

23. A method for producing the compound according to claim 1 or 2, comprising treating titanium oxide with sulfuric acid.