Circular Economy of Waste Plastics to Polyethylene and Chemicals via Refineries & Crude Units

Abstract

Provided is a continuous process for converting waste plastics for recycling for polyethylene polymerization or for linear alpha olefins. The process includes selecting waste plastics containing polyethylene and / or polypropylene and then passing the waste plastics through a pyrolysis reactor to thermally decompose at least a portion of the polyolefin waste and produce a pyrolysis effluent. The pyrolysis effluent is separated into off-gas, a naphtha / diesel fraction, a heavy fraction, and char. The naphtha / diesel fraction is passed to a crude refinery unit, from which a straight-run naphtha (C5-C8) fraction or a propane / butane (C3-C4) fraction is recovered. The straight-run naphtha fraction or the propane and butane (C3-C4) fraction is passed to a steam cracker for ethylene production. The ethylene is converted to linear alpha olefins and / or polyethylene. The heavy fraction from the pyrolysis reactor can also be combined with the heavy fraction of the linear alpha olefin stream recovered from the steam cracker. The combined heavy fraction and the heavy fraction of the normal alpha olefin stream may be passed through a wax hydrogenation zone to produce wax.

Description

[Technical field]

[0001] (background) The world has witnessed a very rapid growth in plastic production. According to PlasticsEurope Market Research Group, global plastic production was 335 million tonnes in 2016, 348 million tonnes in 2017, and 359 million tonnes in 2018. According to McKinsey & Company, the global volume of plastic waste was estimated at approximately 260 million tonnes per year in 2016 and is projected to reach 460 million tonnes per year by 2030 if the current trajectory continues. [Background technology]

[0002] Single-use plastic waste is becoming an increasingly significant environmental issue. At present, there appear to be few options for recycling polyethylene and polypropylene waste plastics into value-added chemical and fuel products. Currently, only small amounts of polyethylene and polypropylene are recycled via chemical recycling, and this recycled and cleaned polymer pellets are pyrolyzed in pyrolysis units to produce fuels (naphtha, diesel), steam cracker feedstock, or slack wax.

[0003] Processes for converting waste plastics into hydrocarbon lubricants are known. For example, US Patent No. 3,845,157 discloses the cracking of waste or virgin polyolefins to form gaseous products such as ethylene / olefin copolymers, which are further processed to produce synthetic hydrocarbon lubricants. US Patent No. 4,642,401 discloses the heating of pulverized polyolefin waste at temperatures between 150 and 500°C and pressures between 20 and 300 bar to produce liquid hydrocarbons. US Patent No. 5,849,964 discloses a process for depolymerizing waste plastic materials into volatile and liquid phases. The volatile phase is separated into a gas phase and a condensate. The liquid, condensate and gas phases are refined into liquid fuel components using standard refining techniques. US Patent No. 6,143,940 discloses a procedure for converting waste plastics into heavy wax compositions. US Patent No. 6,150,577 discloses a process for converting waste plastics into lubricating oils. EP 0 620 264 A1 discloses a process for producing lubricants from waste or virgin polyolefins by thermally cracking the waste in a fluidized bed to form a waxy product, optionally using hydrotreating, followed by catalytic isomerization and fractionation to recover the lubricants.

[0004] Other documents relating to processes for converting waste plastics into lubricants include U.S. Patent Nos. 6,288,296, 6,774,272, 6,822,126, 7,834,226, 8,088,961, 8,404,912 and 8,696,994, and U.S. Patent Application Publication Nos. 2019 / 0161683, 2016 / 0362609 and 2016 / 0264885. The aforementioned patent documents are incorporated herein by reference in their entirety.

[0005] Current methods of chemical recycling via pyrolysis are not capable of making a significant impact on the plastics industry. Current pyrolysis operations produce poor quality fuel components (naphtha and diesel range products) but in small enough quantities that these products can be blended into the fuel supply. However, to recycle the very large quantities of waste polyethylene and waste polypropylene required to address environmental concerns, such simple blending cannot continue. The raw products from pyrolysis units are too poor quality to be blended in large quantities (e.g., 5-20 vol.% blends) into transportation fuels.

[0006] More robust processes are needed to industrially recycle single-use plastics on a large scale and reduce their environmental impact. These improved processes should establish a "circular economy" for waste polyethylene and polypropylene plastics, effectively recycling post-consumer waste plastics as starting material for polymers and high-value by-products. Summary of the Invention

[0007] Provided is a continuous process for converting waste plastics to recycle for polyethylene polymerization or linear alpha olefin synthesis. The process includes first selecting waste plastics containing polyethylene and / or polypropylene. These waste plastics are then passed through a pyrolysis reactor to thermally crack at least a portion of the polyolefin waste and produce a pyrolyzed effluent. The pyrolyzed effluent is separated into off-gas, naphtha / diesel fraction, heavy fraction, and char.

[0008] The integration of this process into oil refineries is a key aspect of the process, allowing for a circular economy with single-use waste plastics such as polyethylene. Thus, the naphtha / diesel fraction is passed to a crude unit in the refinery from which a straight run naphtha fraction (C5-C8) is recovered. The straight run naphtha fraction is passed to a steam cracker for the production of ethylene.

[0009] A refinery generally has its own supply of hydrocarbons that flow through the refinery units. The volume of the naphtha / diesel stream generated from the pyrolysis of waste plastics and flowing to the refinery units can constitute any practical or accommodable volume percent (vol%) of the total flow (total flow) to the refinery units. Generally, the flow rate of the naphtha / diesel fraction generated from the pyrolysis of waste plastics can be up to about 50 vol% of the total flow (i.e., the refinery flow rate and the pyrolysis flow rate) for practical reasons. In one embodiment, the naphtha / diesel flow rate is up to about 20 vol% of the total flow rate.

[0010] The pyrolyzed naphtha / diesel fraction can alternatively be passed to a distillate treater (also known as a diesel hydrotreater) for mild hydroprocessing, from which a light naphtha fraction (C5-C8) is recovered, which is passed to a steam cracker for ethylene production.

[0011] Linear alpha olefins (NAO) are synthesized using ethylene recovered from steam crackers to produce the heavy fraction of linear alpha olefins (C 22+ The linear alpha olefins stream is separated into several fractions, including a heavy fraction of linear alpha olefins. This heavy fraction of linear alpha olefins is combined with the heavy fraction from the pyrolysis reactor. The combined heavy fraction and the heavy fraction of the linear alpha olefins stream are then passed through a wax hydrogenation zone to produce wax.

[0012] In another embodiment, a continuous process for converting waste plastics to recycle for polyethylene polymerization is provided. The process includes selecting waste plastics comprising polyethylene and / or polypropylene and passing the waste plastics through a pyrolysis reactor to thermally crack at least a portion of the polyolefin waste and produce a pyrolyzed effluent. The pyrolyzed effluent is separated into off-gas, a naphtha / diesel fraction, a heavy fraction, and a char. The naphtha / diesel fraction is passed to a refinery crude unit distillation column from which a portion of the propane and butane (C3-C4) fraction is recovered. The C3-C4 fraction is then passed to a steam cracker for ethylene production. The ethylene is then passed to a linear alpha olefin (NAO) synthesis unit to produce C4 to C olefins with recycle components. 22 + Generates valuable NAO chemicals in the range of linear alpha olefin streams (C 22 + ) is recovered from the linear alpha olefin synthesis unit and combined with the heavy fraction from the thermal cracking reactor.

[0013] The combined heavy fraction and the heavy fraction of the linear alpha olefin stream are passed to a wax hydrogenation zone to produce a hydrogenated wax (slack wax or paraffin wax).

[0014] Among other factors, it has been shown that waste pyrolysis oil can be upgraded to higher value products such as gasoline and diesel by adding refinery operations. It has also been shown that waste pyrolysis oil can be efficiently and effectively converted to clean naphtha (C5-C8) or (C3-C4) for the production of ultimate polyethylene polymer by adding refinery operations. Positive economics are realized throughout the process from recycled plastics to polyethylene products with product quality equivalent to virgin polymer. [Brief description of the drawings]

[0015] [Figure 1] Figure 1 shows the current practice of pyrolyzing waste plastics to produce fuel or wax (base case).

[0016] [Diagram 2] Figure 2 illustrates this process for establishing a circular economy for waste plastics.

[0017] [Diagram 3] Figure 3 shows the classification of plastic types for recycling waste plastics. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0018] This process provides a way to recycle waste polyethylene and waste polypropylene into virgin polyethylene, establishing a circular economy by combining three separate industrial processes. The majority of polyethylene and polypropylene polymers are used for single-use plastics and are discarded after use. This single-use plastic waste is becoming an increasingly significant environmental issue. At present, there appear to be few options to recycle polyethylene and polypropylene waste plastics into value-added chemical and fuel products. Currently, only a small amount of polyethylene / polypropylene is recycled via chemical recycling, and this recycled and cleaned polymer pellets are pyrolyzed in a pyrolysis unit to produce fuels (naphtha, diesel), steam cracker feedstock, or slack wax.

[0019] Ethylene is the most produced petrochemical building block. Hundreds of millions of tons of ethylene are produced annually via steam cracking. Steam crackers use either gaseous feedstocks (ethane, propane and / or butane) or liquid feedstocks (naphtha or gas oil). Steam cracking is a non-catalytic decomposition process that takes place at very high temperatures, up to 850°C.

[0020] Polyethylene is widely used in a variety of consumer and industrial products. It is the most common plastic, with over 100 million tons of polyethylene resin produced annually. Its main use is in packaging (polyethylene bags, plastic films, geomembranes, bottles and other containers). Polyethylene is produced in three main forms, which have the same chemical formula (C2H4): n However, the molecular structure is different: high density polyethylene (HDPE, approximately 0.940-0.965 g / m -3 ), linear low density polyethylene (LLDPE, approx. 0.915-0.940g / cm -3 ), low density polyethylene (LDPE, <0.930g / cm -3 HDPE has low branching and short side chains, whereas LDPE has very high branching and long side chains. LLDPE is a substantially linear polymer with a significant number of short branches and is usually made by the copolymerization of ethylene with short chain alpha olefins.

[0021] Low density polyethylene (LDPE) is produced by radical polymerization at temperatures between 150 and 300 °C and very high pressures between 1,000 and 3,000 atm. This process uses small amounts of oxygen and / or organic peroxide initiators to produce polymers with about 4,000 to 40,000 carbon atoms per average polymer molecule and with a lot of branching. High density polyethylene (HDPE) is produced in the presence of a catalyst at relatively low pressures (10 to 80 atm) and temperatures between 80 and 150 °C. Ziegler-Natta organometallic catalysts (titanium(III) chloride with aluminum alkyls) and Phillips-type catalysts (chromium(IV) oxide supported on silica) are typically used, and the production is carried out via a slurry process using a loop reactor or a gas-phase process using a fluidized bed reactor. Hydrogen is mixed with the ethylene to control the chain length of the polymer. The production conditions for linear low density polyethylene (LLDPE) are similar to those for HDPE, except for the copolymerization of ethylene with short chain alpha olefins (1-butene or 1-hexene).

[0022] Today, only a small percentage of post-consumer polyethylene products are collected for recycling, due to the inefficiencies and ineffectiveness of recycling efforts mentioned above.

[0023] Figure 1 shows a diagram of waste plastic fuel or wax pyrolysis as commonly practiced in industry today. As mentioned above, typically polyethylene and polypropylene waste are sorted together (1). The cleaned polyethylene / polypropylene waste 2 is converted to off-gas 4 and pyrolysis oil (liquid products) in pyrolysis unit 3. The off-gas 4 from the pyrolysis unit is used as fuel to operate the pyrolysis unit 3, and only the pyrolysis unit is used for commercial purposes. An on-site distillation unit separates the pyrolysis oil to produce naphtha and diesel 5 products, which are sold to the fuel market. The heavy pyrolysis oil fraction 6 is recycled to the pyrolysis unit 3 to maximize fuel yield. Char 7 is removed from the pyrolysis unit 3. The heavy fraction 6 is rich in long-chain linear hydrocarbons and is highly waxy (i.e., forms paraffinic wax when cooled to ambient temperature). Wax can be separated from the heavy fraction 6 and sold to the wax market.

[0024] The process converts large volumes of waste plastics into pyrolyzed polyethylene and / or polypropylene by integrating the waste polymer pyrolysis product stream into an oil refinery operation. The resulting process produces polymer feedstocks (naphtha or C3-C4 for ethylene crackers) and high quality gasoline and diesel fuels, and / or high quality base oils.

[0025] In general, the process provides a circular economy for polyethylene plants. Polyethylene is produced through the polymerization of pure ethylene. Clean ethylene can be produced using a steam cracker. Either naphtha or C3-C4 streams can be fed to the steam cracker. The ethylene is then polymerized to produce polyethylene.

[0026] By adding refining operations to upgrade the waste pyrolysis oil to higher value products (gasoline, jet and diesel) and to produce clean LPG and naphtha for the steam cracker for the production of ultimate polyethylene polymer, positive economics can be generated throughout the process from recycled plastics to a polyethylene product with quality equivalent to virgin polymer.

[0027] The pyrolysis unit produces low quality products containing contaminants such as calcium, magnesium, chlorides, nitrogen, sulfur, dienes, and heavy components, which cannot be used in large quantities for blending transportation fuels. It has been found that by passing these products through a refinery unit, the contaminants can be captured in a pre-treatment unit and their adverse effects can be mitigated. The fuel components can be further upgraded in a suitable refinery unit with chemical conversion processes, and the final transportation fuel produced by the integrated process can be of higher quality and meet the fuel quality requirements. The integrated process produces a much cleaner naphtha stream as a steam cracker feedstock for ethylene production and polyethylene production. The mass production of these products on spec makes a "circular economy" of recycled plastics feasible.

[0028] The carbon going in and out of the refinery is “transparent,” meaning that not all molecules from the waste plastics are cycled back to the polyolefin plant and become the exact olefin product, but it is nevertheless considered a “credit” since the net “green” carbon going in and out of the refinery is positive. These integrated processes result in a significant reduction in the amount of virgin feedstock required for a polyethylene plant.

[0029] FIG. 2 shows the present integrated process integrating refining operations with recycling for efficient polyethylene production. In FIG. 2, mixed waste plastics are sorted together (21). The cleaned waste plastics 22 are converted in a pyrolysis unit 23 into off-gas 24 and pyrolysis oil (liquid product) and optionally wax (solid product at ambient temperature). The off-gas 24 from the pyrolysis unit can be used as fuel to operate the pyrolysis unit 23. The pyrolysis oil is typically separated into a naphtha / diesel fraction 25 and a heavy fraction 26 in an on-site distillation unit. After completion of the pyrolysis process, char 27 is removed from the pyrolysis unit 23.

[0030] The pyrolysis unit can be located near the waste plastic collection site, which can be remote from the refinery, near the refinery, or within the refinery. If the pyrolysis unit is located remote from the refinery, the pyrolysis oils (naphtha / diesel and heavy oils) can be transported to the refinery by truck, barge, rail car, or pipeline. However, it is preferred that the pyrolysis unit be located at the plastic collection site or within the refinery.

[0031] The preferred starting material for the process is sorted waste plastics containing mainly polyethylene and polypropylene (plastic recycling classification types 2, 4, and 5). The pre-sorted waste plastics are washed, shredded or pelletized, and fed to a pyrolysis unit for pyrolysis. Figure 3 shows the plastic type classification for waste plastic recycling. Classification types 2, 4, and 5 are high density polyethylene, low density polyethylene, and polypropylene, respectively. Polyethylene and polypropylene waste plastics can be used in any combination. It is preferred to use at least some polyethylene waste plastics in the process.

[0032] Proper sorting of waste plastics is very important to minimize contaminants such as N, Cl, and S. Plastic waste including polyethylene terephthalate (Plastic Recycle Classification Type 1), polyvinyl chloride (Plastic Recycle Classification Type 3) and other polymers (Plastic Recycle Classification Type 7) should be sorted to less than 5%, preferably less than 1%, and most preferably less than 0.1%. The process can tolerate moderate amounts of polystyrene (Plastic Recycle Classification Type 6). Waste polystyrene should be sorted to less than 30%, preferably less than 20%, and most preferably less than 5%.

[0033] Washing of waste plastics removes metallic contaminants such as sodium, calcium, magnesium, aluminum, and non-metallic contaminants from other waste sources. Non-metallic contaminants include contaminants from Group IV of the periodic table such as silica, contaminants from Group V such as phosphorus and nitrogen compounds, contaminants from Group VI such as sulfur compounds, and halide contaminants from Group VII such as fluorides, chlorides, iodides, etc. Residual metal, non-metallic contaminants, and halides should be removed to less than 50 ppm, preferentially less than 30 ppm, and most preferentially less than 5 ppm.

[0034] If washing does not adequately remove the metal, non-metallic contaminants, and halide impurities, a separate guard bed can be used to remove the metal and non-metallic contaminants.

[0035] Pyrolysis is carried out by contacting the plastic material feedstock under pyrolysis conditions in a pyrolysis zone, where at least a portion of the feedstock is decomposed, thereby forming a pyrolysis zone effluent containing olefins and paraffins. The pyrolysis conditions include a temperature of about 400°C to about 700°C, preferably about 450°C to about 650°C. Conventional pyrolysis techniques teach operating conditions at pressures above atmospheric pressure (see, for example, U.S. Pat. No. 4,642,401). Furthermore, it has been found that the yield of desired products can be controlled by adjusting the pressure downward (see, for example, U.S. Pat. No. 6,150,577). Thus, in some embodiments where such control is desired, the pyrolysis pressure is below atmospheric pressure.

[0036] 2 shows the integrated process, where only the naphtha / diesel fraction 25 of the thermal cracking unit is sent to a crude unit desalter 28 to produce C5-C8 naphtha, preferentially C5-C7 naphtha, and most preferentially C5-C6 naphtha, which is used for steam cracker 35 feedstock for ethylene production. The ethylene is passed to a polymerization unit 40 and the polyethylene polymer product is used for polyethylene consumer products 41. The heavy naphtha / diesel / gas oil 30 is sent to a suitable refining unit 31 for upgrading to clean gasoline, diesel, or jet fuel.

[0037] Refinery crude units separate crude oil into multiple fractions such as liquefied petroleum gas (LPG), naphtha, kerosene, diesel, and gas oil for further processing into useful petroleum products. Refinery crude units include a crude oil processing section, commonly known as a desalter, and a crude oil distillation section or crude oil fractionation section. The distillation section typically includes atmospheric and vacuum distillation units.

[0038] The naphtha / diesel fraction from the thermal cracking unit is fed to a desalter, which removes salts and solids contained in the oil to protect downstream equipment from the harmful effects of contaminants. To remove the salts, water is mixed with the oil and typically heated to a temperature of about 215°F to about 280°F and separated in the desalter.

[0039] A refinery generally has its own supply of hydrocarbons that flow through the refinery units. The volume of the naphtha / diesel stream generated from the pyrolysis of waste plastics and flowing to the refinery unit (e.g., the refinery-crude unit in the present process) can constitute any practical or containable volume percent (vol%) of the overall flow (total flow) to the refinery unit. In general, the flow rate of the naphtha / diesel fraction generated from the pyrolysis of waste plastics can be up to about 50 vol% of the total flow (i.e., refinery flow rate and pyrolysis flow rate) for practical reasons. In one embodiment, the pyrolysis naphtha / diesel flow rate is up to about 20 vol% of the total flow rate. In another embodiment, the pyrolysis naphtha / diesel flow rate is up to about 10 vol% of the total flow rate. It has been found that about 20 vol% is a very practical amount in terms of impact on the refinery, while at the same time providing excellent results and being a containable amount. Of course, the amount of naphtha / diesel generated from pyrolysis can be controlled so that the fraction passed to the refinery unit provides the desired volume percent of the flow rate.

[0040] The desalted oil is sent to an atmospheric distillation unit where it is heated to about 340-372 °C (644-700 °F) at the bottom of the distillation tower, and liquids are removed at various points in the fractional distillation tower to produce various fuels. Fuel from the crude unit is sent to various upgrading units in the refinery to remove impurities (nitrogen, sulfur) and to catalytically convert fractions to improve product properties such as octane and cetane numbers. The bottoms from the atmospheric distillation tower (also known as atmospheric resid) are sent to a vacuum distillation tower to produce vacuum gas oil (650-1050 °F) and vacuum resid. Vacuum gas oil can be used to produce base oils or further cracked to produce gasoline, jet, and diesel fuels. The overall process produces LPG (<80 °F), gasoline (80-400 °F), jet fuel (360-500 °F), and diesel fuel (300-700 °F). The boiling points of these fractions are adjusted according to seasonal and regional specifications.

[0041] Alternatively, the naphtha / diesel fraction may be passed to a distillate hydrotreater (also known as a diesel hydrotreater) for mild hydrotreating. The hydrotreating step saturates a portion of the olefins, dienes, and aromatics to improve fuel quality. Typical hydrotreating conditions used to remove contaminants while avoiding cracking include temperatures ranging from about 190°C (374°F) to about 340°C (644°F), pressures ranging from about 400 psig to about 3000 psig, and a 0.1 hr. -1 ~About 20 hours -1 The hydrotreating catalysts include those conventionally used in hydrotreating units, including metals such as Ni, Mo, Co, W, and porous supports such as alumina, silica, or silica-alumina. A light naphtha fraction (C5-C8) is recovered from the hydrotreater and then passed to a steam cracker for ethylene production.

[0042] Linear alpha olefins are synthesized in a linear alpha olefin synthesis unit 36 ​​using ethylene recovered from the steam cracker 35. Various fractions of linear alpha olefins are recovered. The linear alpha olefin (NAO) production process converts ethylene into linear alpha olefins via ethylene oligomerization. Ethylene is oligomerized to produce C4-C 30 There are several commercial processes for linear alpha olefins with a wide distribution of carbon numbers ranging from 0.1 to 1.0. In the most common Ziegler process, excess ethylene is fed into a plug flow reactor using triethylaluminum as the catalyst. The reaction is carried out at high pressure and temperature. The excess ethylene is flashed off. The triethylaluminum catalyst is washed from the product with caustic and the linear alpha olefins are separated.

[0043] The heavy waxy fraction of pyrolysis oil from the pyrolysis unit 26 is a heavy C 2 O 3 fraction recovered from the NAO synthesis unit 36. 22+ The NAO is combined with a linear alpha olefins (NAO) unit product stream 37. The combined heavy NAO stream is then hydrotreated (38) to produce wax, either slack wax or paraffin wax.

[0044] The ethylene polymerization unit is preferably located near the refinery so that the feedstocks (propane, butane, naphtha) can be transported via pipeline. For petrochemical plants located remotely from the refinery, the feedstocks can be delivered via truck, barge, rail car, or pipeline.

[0045] In another embodiment, the C3-C4 fraction 32 is recovered from the refinery and crude unit 28. This stream can also be fed to a steam cracker 35 for the production of ethylene. The ethylene is passed to a polymerization unit 40 and the polyethylene product is used for consumer polyethylene production 41.

[0046] The benefits of a circular economy and effective and efficient recycling campaigns are realised through this integrated process.

[0047] The following examples are provided to further illustrate the present process and its advantages. These examples are intended to be illustrative and not limiting. EXAMPLES

[0048] Example 1: Characterization of pyrolysis oils and waxes from commercial sources

[0049] Pyrolysis oil and wax samples were obtained from commercial sources. Their properties are summarized in Table 1. These pyrolysis samples were prepared from waste plastics, mainly containing polyethylene and polypropylene, via pyrolysis in a pyrolysis reactor at approximately 400-600 °C and near atmospheric pressure without the addition of gas or catalyst. Pyrolysis units typically produce gas, liquid oil products, optional wax products, and char. The overhead gas stream of the pyrolysis unit containing the thermally decomposed hydrocarbons was cooled and the condensate was collected as pyrolysis oil (liquid at ambient temperature) and / or pyrolysis wax (solid at ambient temperature). Pyrolysis oil is the primary product of the pyrolysis unit. Some pyrolysis units produce pyrolysis wax as a separate product in addition to pyrolysis oil. [Table 1]

[0050] Specific gravity measurements were performed using ASTM D4052 method. Simulated boiling point distribution curves were obtained using ASTM D2887 method. Carlo-Erba analysis for carbon and hydrogen was performed according to ASTM D5291 method. Bromine number measurements were performed according to ASTM D1159 method. Hydrocarbon type analysis was performed using a high resolution magnetic mass spectrometer, scanning the magnet from 40 to 500 Daltons. Total sulfur was determined using XRF according to ASTM D2622 method. Nitrogen was determined using chemiluminescence detection according to modified ASTM D5762 method. Total chloride content was measured using a combustion ion chromatography instrument according to modified ASTM 7359 method. Oxygen content in the boiling range of naphtha and distillate was estimated using GC with GC / MS measurement equipped with an electron ionization detector with an m / Z range of 29 to 500. Trace metal and nonmetallic elements in the oils were determined using inductively coupled plasma atomic emission spectrometry (ICP-AES).

[0051] Industrial pyrolysis processes of sorted plastics, sourced primarily from polyethylene and polypropylene waste, have produced high-quality hydrocarbon streams with specific gravities in the range of 0.7-0.9 and boiling points in the range of 18-1100°F, as in the case of pyrolysis oil or pyrolysis wax.

[0052] The pyrolysis products are fairly pure hydrocarbons consisting mainly of carbon and hydrogen. The hydrogen to carbon molar ratio varies from 1.7 to nearly 2.0. The bromine numbers range from 14 to 60, indicating varying degrees of unsaturation due to olefins and aromatics. The aromatic content ranges from 5 to 23 vol%, with more severe pyrolysis units producing more aromatics. Depending on the process conditions of the pyrolysis unit, the pyrolysis products show paraffin contents ranging from the mid-20s to the mid-50s vol.%. The pyrolysis products contain significant amounts of olefins. Samples A and B are pyrolysis oils produced under more severe conditions, such as higher pyrolysis temperatures and / or longer residence times, which result in higher aromatics and less paraffin, with H / C molar ratios of about 1.7 and high bromine numbers of 50 to 60. Samples C and D were produced under less severe conditions and their pyrolysis oils are more paraffinic, resulting in H / C molar ratios closer to 2.0 and bromine numbers around 40. Sample E (pyrolysis wax) is mostly paraffinic saturated hydrocarbons with a significant amount of linear (as opposed to branched) hydrocarbons and a bromine number of only 14.

[0053] The following Examples 2 to 5 show the evaluation of waste plastic pyrolysis oil as a transportation fuel.

[0054] [Example 2] Fractional distillation of pyrolysis oil for evaluation as a transportation fuel

[0055] Sample D was distilled to separate multiple fractions of hydrocarbons, namely, gasoline (350° F. - ) fraction, jet (350-572°F) fraction, diesel (572-700°F) fraction, and heavy (700°F + Table 2 summarizes the boiling point distribution and impurity distribution of each fraction of the distillation product. [Table 2]

[0056] [Example 3] Evaluation of pyrolysis oil fractions for gasoline fuel

[0057] Sample F (a fraction of pyrolysis oil with a boiling point range for gasoline fuel) was evaluated for its potential use as gasoline fuel. The carbon number range of sample F is C5 to C12, which is typical for gasoline fuel.

[0058] Because pyrolysis oils are olefinic in nature, oxidation stability (ASTM D525) and gum formation tendency (ASTM D381) were identified as the most important properties to be investigated. Research Octane Number (RON) and Motor Octane Number (MON) are also important properties for engine performance. RON and MON values ​​were estimated from detailed GC analysis of the hydrocarbons. [Table 3]

[0059] Sample F (a fraction of pyrolysis oil in the boiling range of gasoline fuel) is of poor quality and cannot be used alone as a gasoline fuel for motor vehicles. The gasoline fraction from pyrolysis oil showed very poor oxidation stability in that sample F failed after only 90 minutes compared to the target stability of over 1440 minutes. The pyrolysis gasoline exceeded the wash gum target of 4 mg / 100 mL, indicating a strong tendency for gum formation. The pyrolysis gasoline has a lower octane number compared to the reference gasoline. Premium unleaded gasoline was used as the reference gasoline.

[0060] We also investigated the possibility of blending limited amounts of pyrolysis gasoline fractions into the reference gasoline. Our work showed that up to 15% by volume of sample F could potentially be blended into refined gasoline while still achieving the fuel property targets. By integrating pyrolysis gasoline products with refined fuels, the overall product quality can be maintained.

[0061] These results indicate that the as-produced gasoline fraction of pyrolysis oil has limited usefulness as a gasoline fuel. Upgrading in a refinery unit is preferred to convert this gasoline fraction of pyrolysis oil into hydrocarbons that meet gasoline fuel property targets.

[0062] [Example 4] Evaluation of pyrolysis oil fractions for jet fuel

[0063] Sample G (a fraction of pyrolysis oil with a boiling point range equivalent to jet fuel) was evaluated for its potential use as jet fuel. The carbon number range of sample G is C9 to C18, which is typical of jet fuel.

[0064] Due to the olefinic nature of pyrolysis oil, the jet fuel thermal oxidation test (D3241) was considered the most important test. Sample G, which is the pure jet fraction of pyrolysis oil, had an oxidation stability of only 36 minutes, indicating that the pure pyrolysis jet fraction is unsuitable for use as jet fuel.

[0065] We prepared a 5% by volume blend of the pyrolysis jet fraction (Sample G) into refinery produced jet fuel. This blend still failed the jet fuel oxidation test, as shown in Table 4. [Table 4]

[0066] These results indicate that the as-produced jet fraction of pyrolysis oil is completely unsuitable for jet fuel and that upgrading in a refining unit is necessary to convert this jet fraction of pyrolysis oil into hydrocarbons that meet the property targets for jet fuel.

[0067] [Example 5] Evaluation of pyrolysis oil fractions for diesel fuel

[0068] Sample H (a fraction of pyrolysis oil with a boiling point range for diesel fuel) was evaluated for its potential use as diesel fuel. The carbon number range of Sample H is C14 to C24, which is typical for diesel fuel.

[0069] Sample H contains a significant amount of normal hydrocarbons, which tend to exhibit wax-like properties, so cold flow properties such as pour point (ASTM D5950-14) and cloud point (ASTM D5773) were considered the most important tests.

[0070] We prepared two blends of Sample H at 10% and 20% by volume in refinery produced diesel fuel, but both blends still failed the target pour point of less than -17.8°C (0°F). [Table 5]

[0071] These results indicate that pyrolysis oil as is is completely unsuitable for diesel fuel and that upgrading in a refinery unit is required to convert the diesel fraction of pyrolysis oil into hydrocarbons that meet the property targets for diesel fuel.

[0072] [Example 6] Co-processing of pyrolysis oil into crude or desalting units

[0073] The results in Table 1 show that the industrial pyrolysis process of sorted plastics, mainly sourced from polyethylene and polypropylene waste, produces high quality pyrolysis oil or pyrolysis wax, composed mainly of carbon and hydrogen. With good sorting and efficient operation of the pyrolysis unit, nitrogen and sulfur impurities are at sufficiently low levels that modern refineries can handle cofeeding of pyrolysis feedstock to processing units without detrimental effects.

[0074] However, some pyrolysis oils or waxes may still contain significant amounts of metals (Ca, Fe, Mg) and other non-metals (P, Si, Cl, O) that can adversely affect the performance of the refinery's conversion units. In pyrolysis, products with high impurity levels are preferentially fed to a desalter before the crude unit, which effectively removes most of the impurities.

[0075] By feeding the pyrolysis feedstock to a crude unit or a desalting unit before the crude unit, the pyrolysis oil is fractionated into multiple components, which are then further converted in subsequent conversion units, including a paraffin isomerization unit, a jet hydrotreater unit, a diesel hydrotreater unit, a fluid catalytic cracking unit (FCC), an alkylation unit, a hydrocracking unit, and / or a coker unit, to produce gasoline, jet, and diesel fuels with satisfactory product properties. The conversion units (FCC or hydrocracking units) also convert the heavy fraction (corresponding to sample I) into high-quality transportation fuels.

[0076] After the crude unit, the pyrolysis oil is further converted in the subsequent crude unit. Example 7 below demonstrates the conversion of waste plastic pyrolysis oil into high-quality transportation fuel in a refinery conversion unit (using an FCC unit as an example).

[0077] [Example 7] Conversion of pyrolysis oil in FCC

[0078] To study the effect of coprocessing waste plastic pyrolysis oil on FCC, a series of laboratory tests were carried out using Sample A and Sample C. Vacuum gas oil (VGO) is a typical feedstock for FCC. The FCC performance of a 20% blend of pyrolysis oil with VGO and pure pyrolysis oil was compared with that of pure VGO feedstock.

[0079] FCC experiments were performed in a Model C ACE (advanced cracking evaluation) unit manufactured by Kayser Technology Inc., using regenerated equilibrium catalyst (Ecat) from a refinery. The reactor was a fixed flow reactor using N2 as the fluidizing gas. Catalytic cracking experiments were performed at atmospheric pressure and a reactor temperature of 900°F. The catalyst / oil ratio was varied between 5 and 8 by varying the amount of catalyst. Gas products were collected and analyzed using a refinery gas analysis unit (RGA) equipped with a GC with FID detector. In-situ regeneration of spent catalyst was performed in the presence of air at 1300°F, and the regenerated flue gas was passed through a LECO to determine the coke yield. Liquid products were weighed and analyzed by GC for simulated distillation (D2887) and C5 - Compositional analysis was performed. Mass balance showed that the crude oil was composed of coke, dry gas components, LPG components, gasoline (C5, ~430°F), light cycle oil (LCO, 430-650°F), and heavy cycle oil (HCO, 650°F). + The yield of 1,2-dichloro-1,2-diphenyl-2,3-diphenyl-1,4-tetrahydrofuran (1,2-diphenyl-2,4-diphenyl-1,5-dimethyl-2,6-dimethyl-2,7-dimethyl-2,8-diphenyl-1,5 ...7- [Table 6]

[0080] The results in Table 6 show that co-feeding up to 20% by volume of pyrolysis oil only results in a negligible change in the performance of the FCC unit, indicating that co-processing up to 20% of pyrolysis oil is readily feasible. Blending 20% ​​by volume of Sample A or Sample C resulted in a negligible decrease in coke and dry gas yields, a slight increase in gasoline yield, and a slight decrease in LCO and HCO, which are favorable in most situations. Because pyrolysis oil is paraffinic, blending 20% ​​of Sample A or Sample C resulted in a decrease in octane number of about 3-5. Depending on the operational flexibility of the refinery, these octane losses can be compensated for by adjusting the blending or feed position.

[0081] By co-feeding the pyrolysis oil through an FCC process unit with a zeolite catalyst, the oxygen and nitrogen impurities in the fuel range were significantly reduced from about 300-1400 ppm nitrogen (N) to about 30 ppm and from about 250-540 ppm oxygen (O) to about 60-80 ppm. The hydrocarbon compositions of all these co-feed products are well within the range of typical FCC gasoline.

[0082] FCC operation of 100% pyrolysis oil showed a significant octane minus (minus about 13–14), indicating that co-processing of pyrolysis oil is preferable over processing of pure 100% pyrolysis oil.

[0083] [Example 8] Feedstock for C3-C4 and / or naphtha production via co-feeding waste plastic pyrolysis products to refinery and crude units

[0084] The pyrolysis oil is fractionated into components by feeding the entire pyrolysis oil to the crude unit or by feeding it to a desalting unit prior to the crude unit. With the pyrolysis oil co-feed, the refinery crude unit produces significant amounts of clean propane, butane, and naphtha streams, as well as other streams for the refinery conversion units.

[0085] [Example 9] Feeding recycled C3-C4 and / or naphtha to a steam cracker for the production of ethylene and subsequent production of recycled polyethylene resin and polyethylene consumer products

[0086] Propane, butane, and naphtha streams are produced via co-feeding the pyrolysis products to a crude unit (Example 8). These streams are suitable raw materials to be co-fed to a steam cracker to produce ethylene with recycled content. At least some, if not all, of these streams are fed to the steam cracker. The ethylene is processed in a polymerization unit to produce polyethylene resins containing recycled polyethylene / polypropylene derived material. The quality of the newly produced polyethylene is indistinguishable from virgin polyethylene made entirely from virgin petroleum resources. This polyethylene resin containing recycled material is further processed to produce a variety of polyethylene products for consumer product needs. Although these polyethylene consumer products contain chemically recycled circular polymers, the quality of these products is indistinguishable from those made entirely from virgin polyethylene polymers. These chemically recycled polymer products are different from mechanically recycled polymer products, which are of inferior quality to polymer products made from virgin polymers.

[0087] [Example 10] Production of cyclic linear alpha olefins and petroleum wax

[0088] Propane, butane, and naphtha streams are produced via co-feeding the pyrolysis products to a crude unit (Example 8). These streams are suitable feedstocks to be co-fed to a steam cracker to produce ethylene with recycled content. The ethylene is processed in an ethylene oligomerization unit to produce linear alpha olefins (NAO) of various carbon chain lengths, including recycled polyethylene / polypropylene derived materials. The quality of the newly produced NAO is indistinguishable from virgin NAO made entirely from virgin petroleum resources. These linear alpha olefins with recycled content are further converted to produce various chemicals such as polyalphaolefins (PAO), copolymerization agents, etc. Although these chemical products contain chemically recycled materials from waste plastics, the quality of those chemical products is indistinguishable from those made entirely from virgin ethylene.

[0089] [Example 11] Manufacturing of slack wax and paraffin wax (including recycled content)

[0090] The waste plastic pyrolysis wax (sample E) is a linear alpha olefin (C22 + The combined heavy fraction and the heavy fraction of the linear alpha olefin stream may then be passed through a wax hydrogenation zone to produce wax.

[0091] To characterize the recycled wax, sample E (crude pyrolysis wax) was vacuum distilled to 680°F. + and produced a pyrolysis slack wax (Sample J). Sample E was hydrogenated in a continuous fixed bed unit containing NiMo / alumina catalyst at a reactor temperature of 635°F and a pressure of 1200 psig. The catalyst bed volume was hydrogenated at a rate of 1.5 hr. -1 A liquid feed flow rate of 2,500 scf / bbl and a H2 / hydrocarbon flow rate of 2500 scf / bbl were used to produce a mostly waxy hydrogenated product (Sample K). This hydrogenated product was vacuum distilled and extracted at 650° F. as hydrogenated pyrolysis paraffin wax (Sample L). +The results are summarized in Table 7. [Table 7]

[0092] Slack wax from waste plastic pyrolysis (sample J) shows a light brown color due to trace impurities in the sample. This sample contains traces of nitrogen, phosphorus, iron and silicon, but generally has good wax qualities.

[0093] Upon hydrogenation, all trace impurities are completely removed. The resulting paraffinic wax (sample L) is white in color and has good wax quality. This example shows that high-quality pure paraffinic wax can be effectively produced from waste plastics, mainly containing polyethylene and polypropylene. Based on these results, it is expected that the combination of heavy fractions from NAO and heavy fractions from waste plastic pyrolysis wax will produce high-quality wax after hydrogenation.

[0094] As used in this disclosure, the words "comprises" or "comprising" are intended as open-ended transitional phrases, meaning the inclusion of the indicated elements, but not necessarily the exclusion of other unspecified elements. The phrase "consists essentially of" or "consisting essentially of" is intended to mean excluding other elements that are essential to the composition. The phrase "consisting of" or "consists of" is intended as a transitional phrase, meaning the exclusion of all other than the recited elements, except for only trace impurities.

[0095] All patents and publications referenced herein are incorporated herein by reference to the extent not inconsistent therewith. It will be understood that the specific above-described structures, functions, and operations of the above-described embodiments are not necessary to practice the present invention, but are included in the description merely to complete the exemplary embodiment or embodiments. It will be further understood that the specific structures, functions, and operations described in the above-referenced patents and publications can be practiced in combination with the present invention, but are not essential to its practice. Thus, it should be understood that the present invention can be practiced as specifically described without actually departing from the spirit and scope of the present invention, as defined by the appended claims. The contents of the invention according to the claims as originally filed in this application are as follows: [Section 1] 1. A continuous process for converting waste plastics into a recycle for linear alpha olefins, comprising: (a) selecting waste plastics comprising polyethylene and / or polypropylene; (b) passing the waste plastic from (a) through a pyrolysis reactor to thermally decompose at least a portion of the polyolefin waste and produce a pyrolyzed effluent; (c) separating the pyrolyzed effluent into an off-gas, a naphtha / diesel fraction, a heavy fraction, and a char; (d) passing the naphtha / diesel fraction through a crude unit of a refinery; (e) From the crude unit, straight run naphtha fraction (C 5 -C 8 ), (f) passing the straight run naphtha fraction through a steam cracker for the production of ethylene; (g) passing the ethylene through a linear alpha olefin synthesis unit to produce linear alpha olefins; The above process comprising: [Section 2] The process of claim 1, wherein the naphtha / diesel fraction of (c) is passed directly to a refinery crude unit and contaminants are removed in a crude unit desalter. [Section 3] Item 1. The process of item 1, wherein contaminants are removed at the pyrolysis site. [Section 4] Item 1. The process of item 1, wherein the volumetric flow rate of the naphtha / diesel fraction flowing to the crude unit of the refinery constitutes up to 50 volume percent of the total hydrocarbon flow rate flowing to the crude unit. [Section 5] Item 5. The process of item 4, wherein the naphtha / diesel flow rate comprises up to 20% by volume. [Section 6] A continuous process for converting waste plastics into recycling for polyethylene polymerization, comprising: (a) selecting waste plastics comprising polyethylene and / or polypropylene; (b) passing the waste plastic from (a) through a pyrolysis reactor to thermally decompose at least a portion of the polyolefin waste and produce a pyrolyzed effluent; (c) separating the pyrolyzed effluent into an off-gas, a naphtha / diesel fraction, a heavy fraction, and a char; (d) passing the naphtha / diesel fraction through a crude unit of a refinery; (e) From the crude unit, straight run naphtha fraction (C 5 -C 8 ), (f) passing the straight run naphtha fraction through a steam cracker for the production of ethylene; (g) passing ethylene through a linear alpha olefin synthesis unit to produce linear alpha olefins and producing a heavy end (C 22+ recovering a linear alpha olefin stream of (h) the heavy fraction from (c) is mixed with the heavy fraction from (g) (C 22+ with a linear alpha olefin stream of (i) passing the combined heavy fraction and a heavy fraction of the linear alpha olefin stream from (g) through a wax hydrogenation zone to produce wax; The above process comprising: [Section 7] The process of claim 6, wherein the naphtha / diesel fraction of (c) is passed directly to a refinery crude unit and contaminants are removed in a crude unit desalter. [Section 8] Item 7. The process of item 6, wherein contaminants are removed at the pyrolysis site. [Section 9] 7. The process of claim 6, wherein the heavy fraction of the linear alpha olefin stream in (g) is taken from linear alpha olefins produced using ethylene produced in a steam cracker. [Section 10] The process according to item 6, wherein the ethylene produced in (f) is then polymerized. [Section 11] Item 11. The process of item 10, wherein the polyethylene product is prepared from polymerized ethylene. [Section 12] Item 7. The process of item 6, wherein heavy naphtha / diesel / atmospheric gas oil is recovered from the crude unit and further processed in a refinery into clean gasoline, diesel, or jet fuel. [Section 13] Item 7. The process of item 6, wherein heavy naphtha / diesel / atmospheric gas oil is recovered from the crude unit and further processed in a refinery into clean gasoline, diesel, or jet fuel. [Section 14] Item 13. The process of item 12, wherein the amount of unused crude oil processed by the crude unit is reduced with recycled pyrolysis oil. [Section 15] 5. The process of claim 4, wherein the waste plastics selected in (a) are from plastic classification groups 2, 4, and / or 5. [Section 16] 7. The process of claim 6, wherein the volumetric flow rate of the naphtha / diesel fraction flowing to the crude unit of the refinery constitutes up to 50 volume percent of the total hydrocarbon flow rate flowing to the crude unit. [Section 17] Item 17. The process of item 16, wherein the naphtha / diesel flow rate comprises up to 20% by volume. [Section 18] A continuous process for converting waste plastics into recycling for polyethylene polymerization, comprising: (a) selecting waste plastics comprising polyethylene and / or polypropylene; (b) passing the waste plastic from (a) through a pyrolysis reactor to thermally decompose at least a portion of the polyolefin waste and produce a pyrolyzed effluent; (c) separating the pyrolyzed effluent into an off-gas, a naphtha / diesel fraction, a heavy fraction, and a char; (d) passing the naphtha / diesel fraction through a crude unit of a refinery; (e) Propane and butane (C 3 -C4 ) recovering a portion of the fraction; (f) Above (C 3 -C 4 ) passing the fraction through a steam cracker for the production of ethylene; (g) The heavy fraction from (c) is mixed with the heavy fraction from (g) (C 22+ with a linear alpha olefin stream of (h) the combined heavies and the heavies of the linear alpha olefin stream from (g) (C 22+ ) through a wax hydrogenation zone to produce wax; The above process comprising: [Section 19] The process of claim 18, wherein the naphtha / diesel fraction of (c) is passed directly to a refinery crude unit and contaminants are removed in a crude unit desalter. [Section 20] 20. The process of claim 18, wherein contaminants are removed at the pyrolysis site. [Section 21] Item 19. The process of item 18, wherein the heavy fraction of the linear alpha olefin stream in (g) is synthesized from ethylene produced in a steam cracker. [Section 22] Item 19. The process of item 18, wherein the ethylene produced in (f) is then polymerized. [Section 23] 23. The process of claim 22, wherein the polyethylene product is prepared from polymerized ethylene. [Section 24] 20. The process of claim 18, wherein heavy naphtha / diesel / atmospheric gas oil is recovered from the crude unit and further processed in a refinery into clean gasoline, diesel, or jet fuel. [Section 25] Item 19. The process of item 18, wherein the waste plastics selected in (a) are from plastic classification groups 2, 4, and / or 5. [Section 26] A process for converting waste plastics into chemicals useful for the preparation of polyethylene and wax, comprising: (a) selecting waste plastics comprising polyethylene and / or polypropylene; (b) pyrolyzing the waste plastics to recover a naphtha / diesel fraction and a heavy fraction; (c) passing the naphtha / diesel fraction through a crude unit of a refinery; (d) passing the heavy fraction from (b) into a wax hydrogenation zone; The above process comprising:

Claims

1. A continuous process for converting waste plastics into recycling for polyethylene polymerization, comprising: (a) selecting waste plastics comprising polyethylene and / or polypropylene; (b) passing the waste plastic from (a) through a pyrolysis reactor to thermally decompose at least a portion of the polyolefin waste and produce a pyrolyzed effluent; (c) separating the pyrolyzed effluent into an off-gas, a naphtha / diesel fraction, a heavy fraction, and a char; (d) passing the naphtha / diesel fraction through a crude unit of a refinery; (e) a straight run naphtha fraction (C ５ -C ８ ) recovering said (f) passing the straight run naphtha fraction through a steam cracker for producing ethylene; (g) passing ethylene into a linear alpha olefin synthesis unit to produce linear alpha olefins and producing a heavy fraction (C ２２＋ recovering a linear alpha olefin stream of (h) removing the heavy fraction from (c) from the heavy fraction from (g) (C ２２＋ with a linear alpha olefin stream of (i) passing the combined heavy fraction and a heavy fraction of the linear alpha olefin stream from (g) through a wax hydrogenation zone to produce wax; The above process comprising:

2. 2. The process of claim 1, wherein the naphtha / diesel fraction of (c) is passed directly to said crude unit and contaminants are removed in a crude unit desalter.

3. 10. The process of claim 1, wherein the ethylene produced in (f) is subsequently polymerized to prepare polymerized ethylene and a polyethylene product is prepared from the polymerized ethylene.

4. 2. The process of claim 1, wherein heavy naphtha / diesel / atmospheric gas oil is recovered from the crude unit and further processed in a refinery into clean gasoline, diesel, or jet fuel.

5. 2. The process of claim 1, wherein the waste plastics selected in (a) are from plastic classification groups 2, 4, and / or 5.

6. 10. The process of claim 1, wherein the volumetric flow rate of the naphtha / diesel fraction flowing to a crude unit of the refinery constitutes up to 50 volume percent of the total hydrocarbon flow rate flowing to the crude unit, or the naphtha / diesel flow rate constitutes up to 20 volume percent of the total hydrocarbon flow rate flowing to the crude unit.

7. A continuous process for converting waste plastics into recycling for polyethylene polymerization, comprising: (a) selecting waste plastics comprising polyethylene and / or polypropylene; (b) passing the waste plastic from (a) through a pyrolysis reactor to thermally decompose at least a portion of the polyolefin waste and produce a pyrolyzed effluent; (c) separating the pyrolyzed effluent into an off-gas, a naphtha / diesel fraction, a heavy fraction, and a char; (d) passing the naphtha / diesel fraction through a crude unit of a refinery; (e) Propane and butanes (C ３ -C ４ ) recovering a portion of the fraction; (f) The above (C ３ -C ４ ) passing the fraction through a steam cracker for the production of ethylene; (g) separating the heavy fraction from (c) into a heavy fraction of a linear alpha olefin stream (C ２２＋ ) to form a combined heavy fraction; (h) passing the combined heavy fraction from (g) through a wax hydrogenation zone to produce wax; The above process comprising:

8. 8. The process of claim 7, wherein the naphtha / diesel fraction of (c) is passed directly to the crude unit and contaminants are removed in a crude unit desalter.

9. 8. The process of claim 7, wherein the ethylene produced in (f) is subsequently polymerized and a polyethylene product is prepared from the polymerized ethylene.

10. 8. The process of claim 7, wherein heavy naphtha / diesel / atmospheric gas oil is recovered from the crude unit and further processed in a refinery into clean gasoline, diesel, or jet fuel.