Wear-resistant hockey ball adhesive tape

Abstract

The utility model discloses a wear-resistant hockey ball adhesive tape. The wear-resistant hockey ball adhesive tape comprises a polyimide reinforcing layer 1, a first bonding layer 2, a base material layer 3 made of cotton polyester cloth, a second bonding layer 4, a PVC (Polyvinyl Chloride) grid reinforcing layer 5 and a release layer 6 which are sequentially laminated and connected. By compounding the base material and the film layer, the elasticity of the adhesive tape is increased, the friction resistance of the adhesive tape in hockey sports is improved, a club is well protected at low temperature, the impact force of the club on the ice surface is reduced, and the service life of the club is prolonged.

Description

Technical Field

[0001] The utility model relates to the technical field of adhesive tapes, in particular to a wear-resistant hockey tape. Background Art

[0002] Traditional tapes are composed of a base material and an adhesive, which connect two or more unconnected objects together through bonding. Tapes can be divided into high-temperature tapes, double-sided tapes, insulating tapes, special tapes, pressure-sensitive tapes, and die-cut tapes according to their functions. Different functions are suitable for different industry needs.

[0003] Hockey is a sport that is loved by many people. In order to better control the direction of the ball and protect the stick, the hockey stick is generally wrapped with tape. The existing hockey tape has poor wear resistance and needs to be replaced frequently. In addition, the existing hockey tape has poor stickiness and is easy to fall off during use. Utility Model Content

[0004] In order to solve the above problems, the utility model provides a wear-resistant hockey tape.

[0005] The technical solution adopted by the utility model is:

[0006] A wear-resistant hockey tape comprises a polyimide reinforcement layer 1, a first adhesive layer 2, a base material layer 3 made of cotton polyester cloth, a second adhesive layer 4, a PVC mesh reinforcement layer 5 and a release layer 6 which are sequentially stacked and connected.

[0007] Furthermore, the weight of the cotton polyester fabric is 120-140 g / m 2 , thickness is 0.05-2mm.

[0008] Furthermore, the polyimide reinforcement layer is made of a polyimide film with a thickness of 0.03-0.1 mm.

[0009] Furthermore, the PVC mesh reinforcement layer is made of PVC mesh cloth with a thickness of 0.01-0.05 mm.

[0010] Furthermore, the release layer is made of a material having a gram weight of 60-120 g / m 2 Made of glassine paper.

[0011] Further, the first adhesive layer is formed of an acrylic adhesive.

[0012] Furthermore, the second adhesive layer is formed by hot melt adhesive.

[0013] Beneficial effects of the utility model:

[0014] The present application uses cotton-polyester cloth as the base material, a polyimide film is compounded on the outside, and a PVC mesh cloth is compounded on the inside. The cotton-polyester cloth has high strength, good elastic recovery, and is resistant to high and low temperatures. The polyimide film has good wear resistance. The PVC mesh cloth has good temperature resistance, high strength, and is easy to combine with the adhesive to improve the adhesiveness of the tape. The present application increases the elasticity of the tape and improves the friction resistance of the tape in hockey sports by compounding the above-mentioned base material and the film layer. It protects the club well at low temperatures, reduces the impact force of the club on the ice surface, and extends the service life of the club. BRIEF DESCRIPTION OF THE DRAWINGS

[0015] Figure 1 This is a schematic diagram of the structure of the wear-resistant hockey tape of Example 1. DETAILED DESCRIPTION

[0016] In order to make the purpose, technical solution and advantages of the utility model clearer, the technical solution of the utility model will be clearly and completely described below in conjunction with the accompanying drawings and a preferred implementation manner.

[0017] Example 1

[0018] See also Figure 1 The present embodiment is a wear-resistant hockey tape, comprising a polyimide reinforcement layer 1, a first adhesive layer 2, a base material layer 3 made of cotton polyester cloth, a second adhesive layer 4, a PVC mesh reinforcement layer 5 and a release layer 6 which are sequentially stacked and connected.

[0019] The weight of the cotton polyester fabric is 120-140 g / m 2 , thickness is 0.05-2mm.

[0020] The polyimide reinforcement layer is made of a polyimide film with a thickness of 0.03-0.1 mm.

[0021] The PVC mesh reinforcement layer is made of PVC mesh cloth with a thickness of 0.01-0.05 mm.

[0022] The release layer has a gram weight of 60-120g / m 2 Made of glassine paper.

[0023] The first adhesive layer is formed of an acrylic adhesive.

[0024] The second adhesive layer is formed by hot melt adhesive.

[0025] The preparation method of the above-mentioned adhesive tape is:

[0026] 1. Apply acrylic adhesive on the inner side of the polyimide film, and control the thickness of the adhesive layer to 0.01-0.05mm;

[0027] 2. Compounding the polyimide film coated with an adhesive on the outer side of the substrate layer 3;

[0028] 3. Apply hot melt adhesive on the inner side of the substrate layer 3, and control the thickness of the adhesive layer to be 0.04-0.08 mm;

[0029] 4. A PVC mesh cloth is laminated on the inner side of the base material layer 3, and the hot melt adhesive passes through the holes of the PVC mesh cloth to form an adhesive layer on the surface of the PVC mesh cloth;

[0030] 5. Compound a layer of glassine paper on the adhesive layer of the PVC mesh cloth.

[0031] When the utility model is used:

[0032] Method 1: Cut a piece of tape, tear off the release layer 6, start from the root of the racket head, wrap the tape vertically around the racket head, and move the tape backward along the axis of the club. Each wrapping overlaps the previous one, and the overlap does not exceed 6 mm. Pinch the outermost tape of the racket head with your fingers and cut off the excess with scissors.

[0033] Method 2: Cut a piece of tape, tear off the release layer 6, and stick the tape parallel to the outer edge of the top of the racket head. Then, starting from the root of the racket head, wrap the tape perpendicularly to the racket head and move the tape backward along the axis of the club. Each wrapping overlaps the previous one, and the overlap does not exceed 6 mm. Pinch the outermost tape of the racket head with your fingers and cut off the excess with scissors.

[0034] Method 3: Cut five or six short pieces of tape, tear off the release layer 6, and stick the tape vertically to the top of the racket head, wrap the racket head, and then wrap it vertically with the racket head from the root of the racket head, moving the tape backward along the axis of the club, and each wrapping overlaps with the previous one, and the overlap does not exceed 6 mm. Pinch the outermost tape of the racket head with your fingers and cut off the excess with scissors.

[0035] The above is only a preferred embodiment of the present invention. It should be pointed out that a person skilled in the art can make several improvements and modifications without departing from the principle of the present invention, and these improvements and modifications are also within the protection scope of the present invention.

Claims

1. A wear-resistant hockey tape, characterized in that: It comprises a polyimide reinforcement layer (1), a first adhesive layer (2), a base material layer (3) made of cotton polyester cloth, a second adhesive layer (4), a PVC mesh reinforcement layer (5) and a release layer (6) which are sequentially stacked and connected.

2. A wear-resistant hockey tape according to claim 1, characterized in that: The cotton polyester fabric has a grammage of 120-140 g / m 2 , thickness is 0.05-2mm.

3. The wear-resistant hockey tape according to claim 1, characterized in that: The polyimide reinforcement layer (1) is made of a polyimide film with a thickness of 0.03-0.1 mm.

4. The wear-resistant hockey tape according to claim 1, characterized in that: The PVC mesh reinforcement layer (5) is made of PVC mesh cloth with a thickness of 0.01-0.05 mm.

5. The wear-resistant hockey tape according to claim 1, characterized in that: The release layer (6) has a gram weight of 60-120 g / m 2 Made of glassine paper.

6. The wear-resistant hockey tape according to claim 1, characterized in that: The first adhesive layer (2) is formed of an acrylic adhesive.

7. The wear-resistant hockey tape according to claim 1, characterized in that: The second adhesive layer (4) is formed by hot melt adhesive.