Sensor device with one or more optical metal dielectric filters

Description

TECHNICAL FIELD OF THE INVENTION

[0001] The present invention relates to a sensor device including metal-dielectric optical filters.BACKGROUND OF THE INVENTION

[0002] Image sensors are sensor devices that are used in imaging devices, such as cameras, scanners, and copiers, to convert optical signals into electrical signals, allowing image capture. An image sensor, generally, includes a plurality of sensor elements and a plurality of optical filters disposed over the plurality of sensor elements. A color image sensor includes a plurality of color filters disposed in an array, i.e., a color filter array (CFA). The CFA includes different types of color filters having different color passbands, e.g., red, green, and blue (RGB) filters.

[0003] Conventionally, absorption filters formed using dyes are used as color filters. Unfortunately, such dye-based color filters have relatively broad color passbands, resulting in less brilliant colors. Alternatively, dichroic filters, i.e., interference filters, formed of stacked dielectric layers may be used as color filters. Such all-dielectric color filters have higher transmission levels and narrower color passbands, resulting in brighter and more brilliant colors. However, the color passbands of all-dielectric color filters undergo relatively large center-wavelength shifts with changes in incidence angle, resulting in undesirable shifts in color.

[0004] Furthermore, all-dielectric color filters, typically, include a large number of stacked dielectric layers and are relatively thick. Consequently, all-dielectric color filters are expensive and difficult to manufacture. In particular, all-dielectric color filters are difficult to etch chemically. Lift-off processes are, therefore, preferred for patterning. Examples of lift-off processes for patterning all-dielectric CFAs are disclosed in U.S. Patent No. 5,120,622, in U.S. Patent No. 5,711,889, in U.S. Patent No. 6,238,583, in U.S. Patent No. 6,638,668, in US Patent Application No. 2008 / 0316628A1, and in U.S. Patent No. 7,648,808. However, lift-off processes are, generally, limited to a filter spacing of about twice the filter height, which makes it difficult to achieve all-dielectric CFAs suitable for smaller color image sensors.

[0005] In addition to transmitting visible light in color passbands, both dye-based and all-dielectric color filters also transmit infrared (IR) light, which contributes to noise. Therefore, a color image sensor, typically, also includes an IR-blocking filter disposed over the CFA. Conventionally, absorption filters formed of colored glass or dichroic filters formed of stacked dielectric layers are used as IR-blocking filters. Alternatively, induced transmission filters formed of stacked metal and dielectric layers may be used as IR-blocking filters. Examples of metal-dielectric IR-blocking filters are disclosed in U.S. Patent No. 5,648,653, and in U.S. Patent No. 7,133,197.

[0006] To avoid the use of an IR-blocking filter, induced transmission filters formed of stacked metal and dielectric layers may be used as color filters. Such metal-dielectric color filters are inherently IR-blocking. Typically, metal-dielectric color filters have relatively narrow color passbands that do not shift significantly in wavelength with changes in incidence angle. Furthermore, metal-dielectric color filters are, generally, much thinner than all-dielectric color filters. Examples of metal-dielectric color filters are disclosed in U.S. Patent No. 4,979,803, 1990, in U.S. Patent No. 6,031,653, in U.S. Patent Application No. 2009 / 0302407, in U.S. Patent Application No. 2011 / 0204463, and in U.S. Patent Application No. 2012 / 0085944.

[0007] Typically, the metal layers in metal-dielectric color filters are silver layers, which are environmentally unstable and which deteriorate when exposed to even small amounts of water or sulfur. Chemically etching the silver layers exposes the edges of the silver layers to the environment, allowing deterioration. Therefore, in most instances, metal-dielectric CFAs are patterned by adjusting the thicknesses of only the dielectric layers to select different color passbands for the metal-dielectric color filters. In other words, different types of metal-dielectric color filters having different color passbands are required to have the same number of silver layers as one another and the same thicknesses of the silver layers as one another. Unfortunately, these requirements severely limit the possible optical designs for the metal-dielectric color filters.

[0008] The present invention provides a sensor device including metal-dielectric optical filters that are not subject to these requirements, and which are particularly suitable for use in image sensors and other sensor devices.SUMMARY OF THE INVENTION

[0009] Accordingly, the present invention relates to a sensor device as defined in the Claims.BRIEF DESCRIPTION OF THE DRAWINGS

[0010] The present invention will be described in greater detail with reference to the accompanying drawings wherein: FIG. 1A is a schematic illustration of a cross-section of a first optical filter for use in the present invention; FIGS. 1B to 1G are schematic illustrations of steps in a method of fabricating the optical filter of FIG. 1A; FIG. 2 is a schematic illustration of a cross-section of a second optical filter for use in the present invention; FIG. 3 is a schematic illustration of a cross-section of a plurality of optical filters; FIG. 4A is a table of layer numbers, materials, and thicknesses for an exemplary red filter; FIG. 4B is a table of layer numbers, materials, and thicknesses for an exemplary green filter; FIG. 4C is a table of layer numbers, materials, and thicknesses for an exemplary blue filter; FIG. 4D is a table of layer numbers, materials, and thicknesses for an exemplary photopic filter; FIG. 5A and 5B are plots of transmission spectra for the exemplary red, green, and blue filters of FIGS. 4A to 4C; FIG. 5C is a plot of transmission spectra at incidence angles of 0° to 60° for the exemplary photopic filter of FIG. 4D; FIG. 6A is a plot of color gamuts for the exemplary red, green, and blue (RGB) filter set of FIGS. 4A to 4C and for a conventional dye-based RGB filter set; FIG. 6B is a plot of color trajectories at incidence angles of 0° to 60° for the exemplary red filter of FIG. 4A and for a conventional all-dielectric red filter; FIG. 6C is a plot of a color trajectory at incidence angles of 0° to 60° for the exemplary photopic filter of FIG. 4D; FIG. 7 is a schematic illustration of a cross-section of a sensor device helpful in illustrating the present invention; and FIG. 8 is a schematic illustration of a cross-section of an embodiment of a sensor device of the present invention. DETAILED DESCRIPTION OF THE INVENTION

[0011] The present invention includes a metal-dielectric optical filter having protected metal layers, which is particularly suitable for use in a sensor device of the present invention. The optical filter includes a plurality of dielectric layers and a plurality of metal layers stacked in alternation. The metal layers are intrinsically protected by the dielectric layers. In particular, the metal layers have tapered edges that are protectively covered by one or more of the dielectric layers. Accordingly, the metal layers have increased resistance to environmental degradation, resulting in a more durable optical filter.

[0012] In some embodiments, the dielectric layers and the metal layers are stacked without any intervening layers. With reference to FIG. 1A, a first embodiment of the optical filter 100, disposed on a substrate 110, includes three dielectric layers 120 and two metal layers 130 stacked in alternation. The metal layers 130 are each disposed between and adjacent to two dielectric layers 120 and are, thereby, protected from the environment.

[0013] The metal layers 130 have tapered edges 131 at a periphery 101 of the optical filter 100. In other words, the metal layers 130 are substantially uniform in thickness throughout a central portion 102 of the optical filter 100, but taper off in thickness at the periphery 101 of the optical filter 100. Likewise, the dielectric layers 120 are substantially uniform in thickness throughout the central portion 102 of the optical filter 100, but taper off in thickness at the periphery 101 of the optical filter 100. Accordingly, the central portion 102 of the optical filter 100 is substantially uniform in height, whereas the periphery 101 of the optical filter 100 is sloped. In other words, the optical filter 100 has a substantially flat top and sloped sides.

[0014] The tapered edges 131 of the metal layers 130 are not exposed to the environment. Rather, the tapered edges 131 of the metal layers 130 are covered by one or more of the dielectric layers 120. The one or more dielectric layers 120 suppress environmental degradation, e.g., corrosion, of the metal layers 130, e.g., by inhibiting the diffusion of sulfur and water into the metal layers 130. The metal layers 130 are substantially encapsulated by the dielectric layers 120. The tapered edges 131 of the metal layers 130 are protectively covered by adjacent dielectric layers 120, and the metal layers 130 are substantially encapsulated by adjacent dielectric layers 120.

[0015] With reference to FIGS. 1B to 1G, the first embodiment of the optical filter 100 may be fabricated by a lift-off process. With particular reference to FIG. 1B, in a first step, the substrate 110 is provided. With particular reference to FIG. 1C, in a second step, a photoresist layer 140 is applied onto the substrate 110. Typically, the photoresist layer 140 is applied by spin coating or spray coating.

[0016] With particular reference to FIG. 1D, in a third step, the photoresist layer 140 is patterned to uncover a region of the substrate 110 where the optical filter 100 is to be disposed, i.e., a filter region. Other regions of the substrate 110 remain covered by the patterned photoresist layer 140. Typically, the photoresist layer 140 is patterned by first exposing a region of the photoresist layer 140 covering the filter region of the substrate 110 to ultraviolet (UV) light through a mask, and then developing, i.e., etching, the exposed region of the photoresist layer 140 by using a suitable developer or solvent.

[0017] The photoresist layer 140 is patterned in such a manner that an overhang 141, i.e., an undercut, is formed in the patterned photoresist layer 140 surrounding the filter region. Typically, the overhang 141 is formed by chemically modifying, e.g., by using a suitable solvent, a top portion of the photoresist layer 140, so that the top portion develops more slowly than a bottom portion of the photoresist layer 140. Alternatively, the overhang 141 may be formed by applying a dual-layer photoresist layer 140, consisting of a top layer that develops more slowly and a bottom layer that develops more quickly, to the substrate 110.

[0018] With particular reference to FIG. 1E, in a fourth step, a multilayer stack 103 is deposited onto the patterned photoresist layer 140 and the filter region of the substrate 110. A portion of the multilayer stack 103 disposed on the filter region of the substrate 110 forms the optical filter 100. The layers of the multilayer stack 103, which correspond to the layers of the optical filter 100, may be deposited by using a variety of deposition techniques, such as: evaporation, e.g., thermal evaporation, electron-beam evaporation, plasma-assisted evaporation, or reactive-ion evaporation; sputtering, e.g., magnetron sputtering, reactive sputtering, alternating-current (AC) sputtering, direct-current (DC) sputtering, pulsed DC sputtering, or ion-beam sputtering; chemical vapor deposition, e.g., plasma-enhanced chemical vapor deposition; and atomic layer deposition. Moreover, different layers may be deposited by using different deposition techniques. For example, the metal layers 130 may be deposited by sputtering of a metal target, and the dielectric layers 120 may be deposited by reactive sputtering of a metal target in the presence of oxygen.

[0019] Because the overhang 141 shadows a periphery of the filter region of the substrate 110, the deposited layers taper off in thickness towards the periphery 101 of the optical filter 100. When a dielectric layer 120 is deposited onto a metal layer 130, the dielectric layer 120 covers not only the top surface of the metal layer 130, but also the tapered edges 131 of the metal layer 130, thereby, protecting the metal layer 130 from the environment.

[0020] With particular reference to FIG. 1F, in a fifth step, a portion of the multilayer stack 103 on the patterned photoresist layer 140 is removed, i.e., lifted off, together with the photoresist layer 140. Typically, the photoresist layer 140 is stripped by using a suitable stripper or solvent. The optical filter 100 remains on the filter region of the substrate 110. The substrate 110 may, for example, be a conventional sensor element.

[0021] It should be noted that the lift-off process of FIGS. 1B to 1F may also be used to simultaneously form a plurality of optical filters 100 of the same type, i.e., having the same optical design, on the substrate 110. Moreover, the lift-off process may be repeated to subsequently form one or more optical filters of a different type, i.e., having a different optical design, on the same substrate 110. Thereby, an optical filter array may be formed on the substrate 110. The substrate 110 may, for example, be a conventional sensor array.

[0022] With reference to FIG. 1G, in an optional sixth step, an additional dielectric coating 150 is deposited onto the optical filter 100. The dielectric coating 150 may be deposited by using one of the deposition techniques mentioned heretofore. The dielectric coating 150 covers both the central portion 102 and the periphery 101 of the optical filter 100, i.e., all exposed portions of the optical filter 100, thereby, protecting the optical filter 100 from the environment.

[0023] According to the invention, the optical filter includes a plurality of corrosion-suppressing layers, disposed between the dielectric layers and the metal layers, which further protect the metal layers. With reference to FIG. 2, a second embodiment of the optical filter 200, disposed on a substrate 210, is similar to the first embodiment of the optical filter 100, but further includes four corrosion-suppressing layers 260 inserted between the three dielectric layers 220 and the two metal layers 230.

[0024] The metal layers 230 are each disposed between and adjacent to two corrosion-suppressing layers 260 and are, thereby, further protected from the environment. The corrosion-suppressing layers 260 suppress corrosion of the metal layers 230, principally during the deposition process. In particular, the corrosion-suppressing layers 260 protect portions of the metal layers 230 in the optical path, inhibiting degradation of the optical properties of the metal layers 230. The tapered edges 231 of the metal layers 230 are protectively covered by adjacent corrosion-suppressing layers 260, as well as by nearest dielectric layers 220. Thus, the metal layers 230 are, substantially encapsulated by adjacent corrosion-suppressing layers 260, as well as by nearest dielectric layers 220.

[0025] The second embodiment of the optical filter 200 may be fabricated by a lift-off process similar to that used to fabricate the first embodiment of the optical filter 100. However, the layers of the multilayer stack deposited in the fourth step correspond to the layers of the optical filter 200. In particular, corrosion-suppressing layers 260 are deposited before and after each metal layer 230. Advantageously, the corrosion-suppressing layers 260 suppress corrosion, i.e., oxidation, of the metal layers 230 during deposition of the dielectric layers 220.

[0026] The corrosion-suppressing layers 260 may be deposited as metal compound, e.g., metal nitride or metal oxide, layers by using one of the deposition techniques mentioned heretofore. Alternatively, the corrosion-suppressing layers 260 may be formed by first depositing suitable metal layers, by using one of the deposition techniques mentioned heretofore, and subsequently oxidizing the metal layers. Preferably, the corrosion-suppressing layers 260 are each formed by first depositing a suitable metal layer, oxidizing the metal layer, and then depositing a metal oxide layer. For example, the corrosion-suppressing layers 260 may be formed by sputtering of a suitable metal target followed by oxidation, followed by reactive sputtering of a suitable metal target in the presence of oxygen. Further details of methods of forming corrosion-suppressing layers are disclosed in U.S. Patent No. 7,133,197.

[0027] The optical filter useable in the present invention may have a variety of optical designs. The optical designs of exemplary optical filters will be described in further detail hereafter. In general, the optical design of the optical filter is optimized for a particular passband by selecting suitable layer numbers, materials, and / or thicknesses.

[0028] Typically, the optical filter includes 2 to 6 metal layers, 3 to 7 dielectric layers, and, optionally, 4 to 12 corrosion-suppressing layers. In general, increasing the number of metal layers provides a passband with steeper edges, but with a lower in-band transmittance.

[0029] The first layer in the optical design, i.e., the first layer deposited on the substrate, may be a metal layer or a dielectric layer. The last layer in the optical design, i.e., the last layer deposited on the substrate, is usually a dielectric layer. When the first layer is a metal layer, the optical filter may consist of n metal layers (M) and n dielectric layers (D) stacked in a sequence of (M / D) n , where n ≥ 2. Alternatively, the optical filter may consist of n metal layers (M), n dielectric layers (D), and 2n corrosion-suppressing layers (C), stacked in a sequence of (C / M / C / D) n , where n ≥ 2. When the first layer is a dielectric layer, the optical filter may consist of n metal layers (M) and n + 1 dielectric layers (D) stacked in a sequence of D(M / D) n , where n ≥ 2. Alternatively, the optical filter may consist of n metal layers (M), n + 1 dielectric layers (D), and 2n corrosion-suppressing layers (C), stacked in a sequence of D(C / M / C / D) n , where n ≥ 2.

[0030] The metal layers are each composed of silver or silver alloy. For example, a silver alloy consisting essentially of about 0.5 wt% gold, about 0.5 wt% tin, and a balance of silver may provide improved corrosion resistance. Typically, the metal layers each have a physical thickness between about 5 nm and about 50 nm, preferably, between about 10 nm and about 35 nm.

[0031] The dielectric layers are each composed of a dielectric material. Typically, the dielectric layers are each composed of a high-index dielectric material, i.e., a dielectric material having a refractive index greater than about 1.65 at 550 nm, that is transparent in the visible spectral region. Suitable examples of high-index dielectric materials include titanium dioxide (TiO 2 ), zirconium dioxide (ZrO 2 ), niobium pentoxide (Nb 2 O 5 ), tantalum pentoxide (Ta 2 O 5 ), and mixtures thereof. Preferably, the high-index dielectric material is also UV-absorbing, i.e., absorbing in the near-UV spectral region. For example, a high-index dielectric material including or consisting of TiO 2 and / or Nb 2 O 5 may provide enhanced UV blocking, i.e., lower out-of-band transmittance in the near-UV spectral region. Preferably, the high-index dielectric material has a refractive index greater than about 2.0 at 550 nm, more preferably, greater than about 2.35 at 550 nm. A higher refractive index is usually desirable. However, the transparent high-index dielectric materials that are currently available, generally, have refractive indices less than about 2.7 at 550 nm.

[0032] Generally, but not necessarily, the dielectric layers are composed of the same dielectric material, but have different thicknesses. Typically, the dielectric layers each have a physical thickness between about 20 nm and about 300 nm. This physical thickness is selected to correspond with a quarter wave optical thickness (QWOT) required by an optical design. The QWOT is defined as 4nt, where n is the refractive index of the dielectric material and t is the physical thickness. Typically, the dielectric layers each have a QWOT between about 200 nm and about 2400 nm.

[0033] The optional corrosion-suppressing layers are each composed of a corrosion-suppressing material. Typically, the corrosion-suppressing layers are composed of a corrosion-suppressing dielectric material. Examples of suitable corrosion-suppressing dielectric materials include silicon nitride (Si 3 N 4 ), TiO 2 , Nb 2 O 5 , zinc oxide (ZnO), and mixtures thereof. Preferably, the corrosion-suppressing dielectric material is a compound, e.g., a nitride or an oxide, of a metal having a higher galvanic potential than the metal or alloy of the metal layers.

[0034] The corrosion-suppressing layers are, generally, suitably thin to substantially avoid contributing to the optical design of the optical filter, especially when they are absorbing in the visible spectral region. Typically, the corrosion-suppressing layers each have a physical thickness between about 0.1 nm and about 10 nm, preferably, between about 1 nm and about 5 nm. Further details of suitable corrosion-suppressing layers are disclosed in U.S. Patent No. 7,133,197.

[0035] The optional dielectric coating is composed of a dielectric material. The dielectric coating may be composed of the same dielectric materials and may have the same range of thicknesses as the dielectric layers. Typically, the dielectric coating is composed of the same dielectric material as the last dielectric layer and has a thickness that is a portion of the design thickness, i.e., the thickness required by the optical design, of the last dielectric layer. In other words, the last dielectric layer of the optical design is split between a dielectric layer and a dielectric coating. For example, if the last dielectric layer has a design thickness t d and the dielectric coating has a coating thickness t c , e.g., 250 QWOT, the actual thickness t a of the last dielectric layer is given by: t a = t d - t c .

[0036] With reference to FIG. 3, the optical filter 300, typically, has a filter height h, i.e., a height of the central portion of the optical filter 300 from the substrate 310, of less than 1 µm, preferably, of less than 0.6 µm. Also typically, the optical filter 300 has a filter width w, i.e., a width of the central portion of the optical filter 300, of less than 2 µm, preferably, of less than 1 µm. Advantageously, the relatively small filter height allows a smaller filter spacing when a plurality of optical filters 300 are formed by a lift-off process. Typically, the optical filters 300 have a filter spacing d, i.e., a spacing between the central portions of nearest optical filters 300, of less than 2 µm, preferably, of less than 1 µm.

[0037] The optical filter is a metal-dielectric bandpass filter, i.e., an induced transmission filter, having a high in-band transmittance and a low out-of-band transmittance. Typically, the optical filter has a maximum in-band transmittance of greater than about 50 %, an average out-of-band transmittance of less than about 2 % between about 300 nm and about 400 nm, i.e., in the near-UV spectral region, and an average out-of-band transmittance of less than about 0.3 % between about 750 nm and about 1100 nm, i.e., in the infrared (IR) spectral region. Generally, the optical filter also has a low angle shift, i.e., center-wavelength shift with change in incidence angle from 0°. Typically, the optical filter has an angle shift at an incidence angle of 60° of less than about 5% or about 30 nm in magnitude for an optical filter centered at 600 nm.

[0038] In some embodiments, the optical filter is a color filter having a relatively narrow color passband in the visible spectral region. For example, the optical filter may be a red, green, blue, cyan, yellow, or magenta filter. In other embodiments, the optical filter is a photopic filter having a photopic passband, i.e., a passband that mimics the spectral response of the human eye to relatively bright light, in the visible spectral region. In yet other embodiments, the optical filter is an IR-blocking filter having a relatively broad passband in the visible spectral region.

[0039] Optical designs, i.e., layer numbers, materials, and thicknesses, for exemplary red, green, and blue filters, i.e., an exemplary RGB filter set, are tabulated in FIG. 4A, 4B, and 4C, respectively. An optical design for an exemplary photopic filter is tabulated in FIG. 4D. The layers of each optical design are numbered starting from the first layer deposited on the substrate.

[0040] The metal layers are each composed of silver, and have physical thicknesses between about 13 nm and about 34 nm. The dielectric layers are each composed of a high-index dielectric material (H), and have QWOTs between about 240 nm and about 2090 nm. For example, the high-index dielectric material may be a mixture of Nb 2 O 5 and TiO 2 having a refractive index of about 2.43 at 550 nm. The corrosion-suppressing layers are each composed of ZnO and each have a physical thickness of about 2 nm.

[0041] When the high-index dielectric material has a refractive index of about 2.43 at 550 nm, the filter height of the red filter is 606 nm, that of the green filter is 531 nm, that of the blue filter is 252 nm, and that of the photopic filter is 522 nm. These filter heights are considerably smaller than those of conventional all-dielectric optical filters.

[0042] Transmission spectra 570, 571, and 572 for the exemplary red, green, and blue filters are plotted in FIGS. 5A and 5B. The transmission spectrum 570 for the exemplary red filter includes a red passband centered at about 620 nm, the transmission spectrum 571 for the exemplary green filter includes a green passband centered at about 530 nm, and the transmission spectrum 572 for the exemplary blue filter includes a blue passband centered at about 445 nm.

[0043] Transmission spectra 573 and 574 for the exemplary photopic filter at incidence angles of 0° to 60° are plotted in FIG. 5C. The transmission spectrum 573 for the exemplary photopic filter at an incidence angle of 0° includes a photopic passband centered at about 555 nm. In the transmission spectrum 574 for the exemplary photopic filter at an incidence angle of 60°, the photopic passband is centered at about 520 nm. In other words, the angle shift of the exemplary photopic filter at an incidence angle of 60° is about -25 nm.

[0044] The exemplary optical filters each have a maximum in-band transmittance of greater than about 60 %. Advantageously, the exemplary optical filters provide improved IR blocking relative to conventional dye-based and all-dielectric optical filters, reducing noise caused by IR leaking. Specifically, the exemplary optical filters each have an average out-of-band transmittance of less than about 0.3 % between about 750 nm and about 1100 nm, i.e., in the IR spectral region. The exemplary optical filters, particularly the exemplary red filter, also provide improved UV blocking relative to some conventional metal-dielectric color filters, reducing noise caused by UV leaking. Specifically, the exemplary optical filters each have an average out-of-band transmittance of less than about 2 % between about 300 nm and about 400 nm, i.e., in the near-UV spectral region.

[0045] A color gamut 680 for the exemplary RGB filter set is plotted on a CIE xy chromaticity diagram in FIG. 6A, along with a color gamut 681 for a conventional dye-based RGB filter set for comparison. Advantageously, the color gamut 680 of the exemplary RGB filter set is considerably larger than the color gamut 681 of the conventional dye-based RGB filter set.

[0046] A color trajectory 682 for the exemplary red filter at incidence angles of 0° to 60° is plotted on a CIE xy chromaticity diagram in FIG. 6B, along with a color trajectory 683 for a conventional all-dielectric red filter at incidence angles of 0° to 60°. A color trajectory 684 for the exemplary photopic filter at incidence angles of 0° to 60° is plotted on a CIE xy chromaticity diagram in FIG. 6C. Advantageously, the angle shift of the exemplary optical filters is considerably smaller than the angle shift of conventional all-dielectric optical filters.

[0047] The optical filter is part of a sensor device of the present invention. The sensor device may be any type of sensor device including a plurality of sensor elements, in addition to a plurality of optical filters described herein. For example, the sensor device may be an ambient light sensor, a proximity sensor, or an image sensor. The sensor elements may be any type of conventional sensor elements. Typically, the sensor elements are photodetectors, such as photodiodes, charge-coupled device (CCD) sensor elements, or complementary metal-oxide semiconductor (CMOS) sensor elements. The sensor elements may be front- or back-illuminated.

[0048] The optical filters are disposed over the one or more sensor elements, so that the optical filters filter light provided to the sensor elements. Typically, each optical filter is disposed over one sensor element. In other words, each pixel of the sensor device, typically, includes one optical filter and one sensor element. Preferably, the optical filters are disposed directly on the sensor elements. For example, the optical filters may be formed on the sensor elements by a lift-off process. However, in some instances, there may be one or more coatings disposed between the optical filters and the sensor elements.

[0049] For reference purposes, FIG. 7 shows a sensor device 790 including a sensor element 711 and an optical filter 700 disposed on the sensor element 711. For example, the sensor device 790 may be an ambient light sensor, the sensor element 711 may be a photodiode, and the optical filter 700 may be a photopic filter, such as the exemplary photopic filter of FIG. 4D, or an IR-blocking filter.

[0050] According to the present invention, the sensor device includes a plurality of sensor elements, and a plurality of optical filters disposed over the plurality of sensor elements. The sensor elements are disposed in an array. In other words, the sensor elements form a sensor array, such as a photodiode array, a CCD array, a CMOS array, or any other type of conventional sensor array. The optical filters are also disposed in an array. In other words, the optical filters form an optical filter array, such as a color filter array (CFA). ,The sensor array and the optical filter array are corresponding two-dimensional arrays, i.e., mosaics. For example, the arrays may be rectangular arrays having rows and columns.

[0051] Usually, the optical filters are substantially separate from one another. In other words, the peripheries of the optical filters are not usually in contact with one another. However, in some instances, the dielectric layers of the optical filters may unintentionally touch, while the metal layers, particularly, the tapered edges, remain separate from one another.

[0052] The plurality of optical filters includes different types of optical filters having different passbands from one another. For example, the plurality of optical filters may include color filters, such as red, green, blue, cyan, yellow, and / or magenta filters, photopic filters, IR-blocking filters, or a combination thereof. In some embodiments, the plurality of optical filters includes different types of color filters, forming a CFA. For example, the plurality of optical filters may include red, green, and blue filters, such as the exemplary red, green, and blue filters of FIGS. 4A to 4C, forming an RGB filter array, such as a Bayer filter array.

[0053] Advantageously, the different types of optical filters may have different numbers of metal layers and / or different thicknesses of the metal layers from one another. In some embodiments, at least two of the different types of optical filters include different numbers of metal layers from one another. In the same or other embodiments, at least two of the different types of optical filters have different metal-layer thicknesses from one another. For example, the exemplary blue filter of FIG. 4C has a different number of metal layers from the exemplary red and green filters of FIGS. 4A and 4B. Moreover, all of the exemplary red, green, and blue filters of FIGS. 4A to 4C have different metal-layer thicknesses from one another.

[0054] With reference to FIG. 8, an embodiment of the sensor device 890 includes a plurality of sensor elements 811 and a plurality of optical filters 800 and 804 disposed on the plurality of sensor elements 811. The plurality of optical filters 800 and 804 includes a first type of optical filter 800 having a first passband, and a second type of optical filter 804 having a second passband, different from the first passband. For example, the sensor device 890 may be an image sensor, the plurality of sensor elements 811 may form a CCD array, and the plurality of optical filters 800 and 804 may form a Bayer filter array, of which only a portion of one row is illustrated. The first type of optical filter 800 may be a green filter, such as the exemplary green filter of FIG. 4B, and the second type of optical filter 804 may be a blue filter, such as the exemplary blue filter of FIG. 4C.

Claims

1. A sensor device (890) comprising: a plurality of sensor elements ( 811); and a plurality of optical filters (200) disposed over the the plurality of sensor elements (811), wherein each of the optical filters (200) includes: a plurality of dielectric layers (220); and a plurality of silver or silver alloy metal layers (230) stacked in alternation with the plurality of dielectric layers (220), wherein each of the plurality of metal layers (230) is substantially uniform in thickness throughout a central portion (102) of the optical filter (200), and tapers off in thickness at a periphery (101) of the optical filter (200) to has a tapered edge (231), at the periphery (201) of the optical filter (200,), that is protectively covered by one or more of the plurality of dielectric layers (220), and each of the plurality of metal layers (230) is separated from a substrate (210) of an optical filter (200), of the one or more optical filters, using at least one the plurality of dielectric layers (220), and each of the plurality of metal layers (230) is encapsulated by two nearest of the plurality of dielectric layers (220); and wherein each of the one or more optical filters (200) further includes a plurality of corrosion-suppressing layers (260) disposed between the plurality of dielectric layers (220) and the plurality of metal layers (230), and the metal layers are encapsulated by the corrosion-suppressing layers, characterised in that the plurality of sensor elements (811) are disposed in a two-dimensional array, and the plurality of optical filters (200) are disposed in a corresponding two-dimensional array, and the plurality of optical filters (200) includes different types of optical filters (200) having different passbands from one another.

2. The sensor device (890) of claim 1, wherein the one or more optical filters (200) are disposed on the one or more sensor elements (811).

3. The sensor device (890) of claim 2, wherein the one or more optical filters (200) were formed on the one or more sensor elements (811) by a lift-off process.

4. The sensor device (890) of claim 1, wherein the one or more optical filters (200) have substantially flat tops and sloped sides.

5. The sensor device (890) of claim 1, wherein each of the plurality of dielectric layers (220) is composed of a high-index dielectric material having a refractive index greater than 2.0 at 550 nm.

6. The sensor device (890) of claim 5, wherein the high-index dielectric material is ultraviolet-absorbing, and wherein the one or more optical filters (200) each have an average out-of-band transmittance of less than about 2 % between about 300 nm and about 400 nm.

7. The sensor device (890) of claim 1, wherein the one or more optical filters (200) are one or more color filters, photopic filters, infrared-blocking filters, or a combination thereof.

8. The sensor device (890) of claim 1, wherein the plurality of optical filters (300, 800, 804) are substantially separate from one another.

9. The sensor device (890) of claim 1, wherein at least two of the different types of optical filters (800, 804) include different numbers of metal layers from one another.

10. The sensor device (890) of claim 1, wherein at least two of the different types of optical filters (800, 804) have different metal-layer thicknesses from one another.