Battery cases and battery packs

Abstract

The present invention discloses a battery case comprising at least one resin-based composite layer and at least one waterproof layer, wherein the resin-based composite layer and the waterproof layer are bonded together by hot pressing. The present invention also discloses a battery pack comprising the battery case.

Description

[Technical field]

[0001] The present invention relates to the field of new energy vehicle batteries. More specifically, the present invention relates to a battery case for a new energy vehicle battery and a battery pack including the battery case. [Background technology]

[0002] The battery case for new energy vehicles in the technical field mainly adopts the combination of an aluminum alloy tray and a battery cover formed by injection molding of engineering plastics, resulting in a large battery weight and high power consumption. Therefore, reducing the weight of new energy vehicle batteries has always been one of the main focuses and difficulties of modern vehicle technology. In addition, although the existing batteries of new energy vehicles all have a completely closed structure, their waterproof effect is still insufficient; therefore, when submerged in water, these batteries potentially create a large safety hazard. Especially, in recent years, our country has often experienced heavy rains that caused floods or flooding, and sometimes new energy vehicles are submerged in water, especially rainwater. Rainwater has a stronger conductivity, so if the battery leaks, it will create a non-negligible safety problem.

[0003] Chinese Utility Model No. 209786038 (CN 209786038U) discloses a vehicle battery with good waterproof effect, including a battery body and a battery case, in which a first waterproof layer is adhered to the inner wall of the battery case, a second waterproof layer is adhered to the surface of the battery body, and a water-absorbing layer is filled between the first waterproof layer and the second waterproof layer. Although the invention achieves good waterproof performance through the combination of multiple layers of waterproof material and water-absorbing material, it has a relatively complicated structure, its productivity is low, and it is difficult to carry out large-scale continuous production.

[0004] China Utility Model No. 212810424 (CN212810424U) discloses a waterproof explosion-proof ternary lithium battery, including a battery pack, an insulating protection plate, a waterproof film and a case, in which the insulating protection plate and the waterproof film are wound on the outside of the battery pack in order and located in the case, and a waterproof adhesive is applied on the outside of both ends of the waterproof film, and a silicone layer is filled between the waterproof film and the case. This invention also has the problem of a complex structure. Moreover, the use of the waterproof adhesive not only leads to a complex manufacturing method, but also leads to the problem of total volatile organic compounds (TVOC) exceeding the prescribed limit.

[0005] Therefore, in order to better meet the performance requirements of modern new energy vehicles, there remains a demand for constantly developing novel lightweight battery packs that are characterized by simple methods, excellent mechanical strength and good waterproof performance.

[0006] Summary of the Invention In order to address the above problems, the present invention aims to provide a battery case having a simple structure, light weight, excellent mechanical strength and good waterproof effect, and a battery pack including the battery case.

[0007] The battery case according to the present invention includes at least one resin-based composite layer and at least one waterproof layer, and the resin-based composite layer and the waterproof layer are bonded together by hot pressing.

[0008] In some embodiments, the battery case includes at least two resin-based composite layers and at least one waterproof layer, and the waterproof layer is disposed between the two resin-based composite layers.

[0009] The present invention also provides a battery pack including the battery case as described above and a battery disposed inside the battery case.

[0010] Beneficial Effects The battery case of the present invention not only has a remarkable light weight effect, but also has excellent mechanical strength, good waterproof effect, and simple structure.

[0011] In order to more clearly describe the embodiments of the present invention, the drawings required in the description of said embodiments are briefly described below. Obviously, the drawings in the following description only show some embodiments of the present invention, and those skilled in the art can derive other embodiments from these drawings without creative efforts. [Brief description of the drawings]

[0012] [Figure 1] FIG. 1 is a structural diagram of a battery pack according to the prior art. [Diagram 2] FIG. 2 is a structural diagram of a battery case according to Example 1 of the present invention. [Diagram 3] FIG. 11 is a structural diagram of a battery case according to Example 2 of the present invention. [Figure 4] FIG. 2 is a structural diagram showing the use of the battery pack according to Example 1 of the present invention as an upper cover of the battery case. [Diagram 5] FIG. 11 is a structural diagram showing the use of the battery case according to Example 2 of the present invention as the upper cover of the battery pack. [Figure 6] FIG. 11 is a structural diagram showing the use of the battery case according to Example 2 of the present invention as both the upper and lower covers of the battery pack.

[0013] In the figure, "1" refers to the resin-based composite layer and "2" refers to the waterproof layer. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0014] In the following, the technical solutions in the embodiments of the present invention are clearly and completely described with reference to the accompanying drawings of the present invention. Obviously, the described embodiments are only a part, not all, of the embodiments of the present invention. All other embodiments obtained by those skilled in the art based on the embodiments of the present invention without creative efforts are included in the protection scope of the present invention.

[0015] In the present specification, the terms "inner", "outer", "upper", "lower", etc., indicate orientations or positions based on orientations or positions as illustrated in the drawings, and are merely for facilitating the description of the present invention, and do not indicate or suggest that the referenced members or elements must have or are configured in the particular orientation, and should not be construed as limiting the present invention. In the present specification, unless otherwise stated, the term "at least one layer" means one or more layers.

[0016] Referring to Fig. 1, Fig. 1 is a structural diagram of a battery pack 100 in the prior art, which includes a battery case (110 and 110'); the battery case can be used as an upper cover 110 and a lower cover 110' of the battery pack 100; and the upper cover 110 and the lower cover 110' jointly form a space 120 for placing an element, such as a battery or a battery module (not shown). In the present invention, the battery pack 100 includes, but is not limited to, a battery pack for a new energy vehicle.

[0017] Nevertheless, as mentioned above, current battery pack cases have the drawbacks of being too heavy, not waterproof, and / or being manufactured using complicated methods.

[0018] In order to solve these problems, the present invention provides a battery case including at least one resin-based composite layer and at least one waterproof layer, where the resin-based composite layer and the waterproof layer are bonded together by hot pressing, and the waterproof layer is disposed on a side of the resin-based composite layer closer to the battery or further away from the battery.

[0019] By using the resin-based composite layer and the waterproof layer bonded by hot pressing, the battery case of the present invention not only achieves a remarkable lightweight effect, but also has excellent mechanical strength, good waterproof effect, and simple structure.

[0020] In the present invention, the resin-based composite layer and the waterproof layer are bonded together by hot pressing to form an integral structure, which is carried out by using the bonding properties of the resin itself in the resin-based composite for bonding, which does not require additional adhesive, thus allowing the omission of adhesive application, thereby resulting in a simple method.

[0021] In the present invention, the number of the resin-based composite layers and the waterproof layers is not particularly limited, and a person skilled in the art can select the appropriate number of the layers according to the actual requirements. For example, in some embodiments, the number of the resin-based composite layers and the waterproof layers is 1-4, for example, 1, 2, 3 or 4, respectively. Preferably, the number of the resin-based composite layers is 1-3, for example, 1, 2 or 3. Preferably, the number of the waterproof layers is 1-3, for example, 1, 2 or 3.

[0022] In a preferred embodiment of the present invention, the resin-based composite layer and the waterproof layer are arranged alternately, which allows the battery case to have the advantages of excellent mechanical strength, good waterproof performance and light weight at the same time.

[0023] In the present invention, when the term "alternately" is described, it means that in the battery case, only the resin-based composite layer is bonded to the waterproof layer, and only the waterproof layer is bonded to the resin-based composite layer. Therefore, the use of the term "alternately" means that in the battery case of the present invention, there are no two waterproof layers bonded to each other, and there are no two resin-based composite layers bonded to each other. In particular, when the battery case includes only one resin-based composite layer and one waterproof layer, the term "alternately" refers to the bonding of one resin-based composite layer and one waterproof layer.

[0024] In a preferred embodiment of the present invention, the waterproof layer is disposed on the side of the resin-based composite layer closer to the battery. Therefore, the outermost layer of the battery case further away from the battery is the resin-based composite layer. Accordingly, when the battery case is subjected to external force, the resin-based composite layer as the outermost layer can play a role of shock absorption, thus avoiding damage to the waterproof layer and thereby affecting the final waterproof effect. Moreover, this arrangement can also prevent wrinkles generated in the waterproof layer during the hot pressing process from being exposed to the outside of the battery case, thereby improving the appearance of the battery case member.

[0025] In one embodiment of the present invention, the battery case includes at least two resin-based composite layers and at least one waterproof layer, and the waterproof layer is disposed between the two resin-based composite layers. Therefore, both the outermost layer away from the battery and the innermost layer closer to the battery of the battery case are resin-based composite layers, that is, the arrangement can better protect the waterproof layer. At the same time, this arrangement can avoid wrinkles generated in the waterproof layer during the hot pressing process from being exposed to the outside of the battery case, thereby improving the overall appearance of the battery case members. Moreover, the mechanical strength of the battery case can be further increased by disposing two layers of resin matrix composite.

[0026] In one embodiment, the resin-based composite layer is a resin-based porous material layer. The resin-based porous material is a material known in the art, and includes a porous material and a resin covering the porous material. In the resin-based porous material, the resin is filled into the gaps or pores of the porous material, or the porous material is immersed in the resin.

[0027] Moreover, the resin and the porous material in the resin-based porous material are also materials known in the art.

[0028] In a preferred embodiment, the resin-based porous material layer has a porous structure. Preferably, the porous structure is derived from cells generated by foaming of the resin in the resin-based porous material layer. The cell structure formed by foaming of a resin is known to those skilled in the art. Therefore, in some embodiments, the resin-based porous material layer, particularly its cross section, has a porous structure similar to the cells.

[0029] In the present invention, the "cell" refers to the minimum structural unit constituting one small cavity of a foamed resin, and is formed during foaming of the resin by mechanical introduction of a foaming agent, gas, or dissolution of a soluble substance. The foaming includes, for example, physical foaming and chemical foaming. The physical foaming refers to foaming through gasification of a physical foaming agent. The chemical foaming refers to foaming by generating a gas (e.g., carbon dioxide) through a chemical reaction of a chemical foaming agent, for example, water and isocyanate. Methods for forming cells are known to those skilled in the art.

[0030] In some embodiments, the resin in the resin-based porous material layer includes polyurethane or polyurea, epoxy resin, or unsaturated resin; preferably, the resin is a polyurethane resin. In some embodiments, the resin is a foamed resin, such as a foamed polyurethane resin. By using a foamed resin, the battery case can be further lightened. In some embodiments, the resin has a density of 100 to 1200 g / L, preferably 100 to 500 g / L.

[0031] In some embodiments, the porous material in the resin-based porous material layer has a density of 100 to 2400 g / m 2 In the present invention, the "single layer surface density" refers to the mass per unit area in the porous material forming one resin-based porous material layer. Methods for measuring the single layer surface density are known to those skilled in the art.

[0032] As known in the art, the porous material is also called reinforced material. For example, the porous material includes fiber materials, such as glass fiber (GF), carbon fiber, natural fibers (e.g. bamboo fiber), especially natural fibers in the form of cloth, nonwoven fabric, and perforated (permeable or non-permeable) flake-like materials, such as perforated metal plates, wood plates and plastic plates, such as aluminum foam and honeycomb panels. In a preferred embodiment, the porous material is a fiber reinforced material, especially glass fiber (GF). Preferably, the porous material is a glass fiber material in the form of felt, such as glass fiber felt.

[0033] In some embodiments, the waterproof layer comprises a metal sheet or a plastic sheet as known in the art. Preferably, the metal sheet is selected from aluminum alloy, iron, steel and aluminum. Preferably, the plastic sheet is selected from at least one of the following materials: polyethylene (PE), polyvinyl chloride (PVC), polyethylene terephthalate (PET), polybutylene terephthalate (PBT), polypropylene (PP), thermoplastic polyurethane (TPU), polyurethane (PU), polyamide (PA), polyvinyl butyral (PVB) and ethylene-vinyl acetate copolymer (EVA). In a preferred embodiment, the plastic sheet is selected from polyurethane (PU), more preferably thermoplastic polyurethane (TPU).

[0034] In the present invention, the waterproof layer has a thickness of 0.01-1 mm, preferably 0.02-0.3 mm. A thickness within the above range on the one hand ensures good adhesion between the resin-based composite layer and the waterproof layer when they are hot-pressed into an integral structure, and on the other hand also ensures that the obtained battery case has excellent physical properties, especially waterproof performance.

[0035] The battery case of the present invention has a thickness of 1.0 to 50 mm, preferably 1.0 to 10 mm. 3 , preferably 1.1 to 1.8 g / m3 Therefore, the battery case of the present invention has a significant weight-saving effect. The "total density" described in this specification refers to the ratio of the total mass of the battery case itself to its total volume, as determined in accordance with GB / T 1033.1-2008.

[0036] The present invention also provides a battery pack including the battery case as described above and a battery inside the battery case.

[0037] In one embodiment of the present invention, the battery case is the upper cover and / or the lower cover of the battery pack. Preferably, the upper cover and the lower cover of the battery pack are joined together in a manner known in the art (e.g., by bolting). The upper cover and the lower cover together form a space for placing a battery.

[0038] In a preferred embodiment, the battery case has a shape adapted to the battery.

[0039] In the following, certain embodiments of the present invention are illustrated by way of example, but it will be understood that the invention is not limited to these examples. EXAMPLES

[0040] Test Method Total density: GB / T 1033.1-2008 Tensile strength: GB / T 1447-2005 Waterproof performance: GB 38031-2020.

[0041] Battery case manufacturing Example 1 Figure 2 illustrates a battery case according to Example 1 of the present invention. As shown in Figure 2, the battery case had a two-layer structure. Specifically, the structure included a resin-based composite layer 1 and a waterproof layer 2. The waterproof layer 2 was located on the side of the resin-based composite layer 1 closer to the battery (not shown).

[0042] The battery case of this embodiment is manufactured by the following steps: step 1) firstly spray polyurethane resin material on both sides (or one side) of glass fiber felt through a nozzle; step 2) place a waterproof layer made of thermoplastic polyurethane TPU in a mold, and place the uncured resin-based glass fiber felt obtained in step 1) on the surface of the waterproof layer; and step 3) clamp the upper mold and the lower mold together, and then cure by hot pressing to form an integral part.

[0043] In this embodiment, the waterproof layer 2 had a thickness of 0.05 mm and the battery case had a thickness of 1.6 mm. The resulting battery case had a weight of 1.5 g / m 3 and a tensile strength of 165 MPa. Therefore, the battery case of the present invention not only had a significant lightweight effect, but also had excellent mechanical strength.

[0044] Example 2 FIG. 3 illustrates a battery case according to Example 2 of the present invention. As shown in FIG. 3, the battery case had a three-layer structure. Specifically, the structure included two resin-based composite layers 1 and one waterproof layer 2. The waterproof layer 2 was located between the two resin-based composite layers 1. The two resin-based composite layers 1 and the one waterproof layer 2 were bonded by hot pressing.

[0045] The battery case of this embodiment is manufactured by the following steps: step 1) prepare two layers of glass fiber felt; step 2) place a waterproof layer made of thermoplastic polyurethane TPU between the two layers of glass fiber felt; step 3) spray polyurethane resin material onto the surfaces of the two layers of glass fiber felt respectively through a nozzle; and step 4) clamp the upper mold and the lower mold together, and then harden them by hot pressing to form an integral part.

[0046] In this embodiment, the waterproof layer 2 had a thickness of 0.05 mm and the battery case had a thickness of 1.3 mm. The resulting battery case had a weight of 1.7 g / m3 and a tensile strength of 223 MPa. Therefore, the battery case of the present invention not only had a remarkable lightweight effect, but also had excellent mechanical strength.

[0047] Battery pack manufacturing and waterproof testing Figure 4 illustrates the use of a battery case according to Example 1 of the present invention as the top cover of the battery pack. Figure 5 illustrates the use of a battery case according to Example 2 of the present invention as the top cover of the battery pack. Figure 6 illustrates the use of a battery case according to Example 2 of the present invention as both the top and bottom covers of the battery pack. The top and bottom covers of the battery pack were joined by bolts. The top and bottom covers together form a space for placing a battery (not shown).

[0048] The above battery pack shown in Figures 4-6 was tested for waterproof performance according to GB 38031-2020. The battery pack was placed in a water tank 3 with a water depth of 1.5 m for 30 minutes, and no air bubbles were observed and no water leaked into the battery pack. During the following hour, no air bubbles or water leakage were observed.

[0049] It should be noted that although the waterproof layer 2 in the battery case shown in FIG. 4 above is positioned on the side of the resin-based composite layer 1 closer to the battery, those skilled in the art will understand that the battery case will also have excellent waterproof performance when the waterproof layer 2 is positioned on the side of the resin-based composite layer 1 further away from the battery.

[0050] The above results show that the battery case of the present invention not only has a remarkable lightweight effect, but also is characterized by excellent mechanical strength, excellent waterproof performance, and a simple manufacturing method.

[0051] The basic principle and exemplary embodiments of the present invention are described above. It should be understood by those skilled in the art that the above description is only illustrative of the present invention, and the present invention is not limited to the above embodiments. Many modifications and variations can be made to the present invention without departing from the spirit and scope of the present invention. All such modifications and variations are within the protection scope of the present invention. [Explanation of symbols]

[0052] 1 resin composite material layer, 2 waterproof layer, 100 battery pack, 110 upper cover, 110' lower cover, 120 space

Claims

1. A battery case comprising at least one resin-based composite material layer (1) and at least one waterproof layer (2), wherein the resin-based composite material layer (1) and the waterproof layer (2) are bonded to each other by hot pressing.

2. 2. The battery case according to claim 1, wherein the number of said resin-based composite material layers (1) and said waterproof layers (2) is 1 to 4, respectively.

3. 2. The battery case according to claim 1, wherein the resin-based composite material layer (1) and the waterproof layer (2) are alternately arranged.

4. 2. The battery case according to claim 1, wherein the waterproof layer (2) is disposed on the side of the resin-based composite material layer (1) closer to the battery.

5. 2. The battery case according to claim 1, characterized in that the battery case comprises at least two resin-based composite layers (1) and at least one waterproof layer (2), and the waterproof layer (2) is disposed between the two resin-based composite layers (1).

6. 2. The battery case according to claim 1, wherein the resin-based composite material layer (1) is a resin-based porous material layer containing a porous material and a resin covering the porous material.

7. The battery case according to claim 6 , wherein the resin-based porous material layer has a porous structure.

8. 7. The battery case according to claim 6, wherein the resin is polyurethane, polyurea, or epoxy resin; and the porous material is glass fiber, carbon fiber, natural fiber, or a perforated metal plate, wood plate, or plastic plate.

9. The porous material has a density of 100 to 2400 g / m ２ 7. The battery case of claim 6, having a monolayer surface density of 0.1 to 0.5 μm.

10. 2. The battery case according to claim 1, characterized in that the waterproof layer (2) comprises a metal sheet or a plastic sheet.

11. 11. The battery case according to claim 10, wherein the metal sheet is selected from aluminum alloy, iron, steel, and aluminum, and the plastic sheet is selected from polyethylene PE, polyvinyl chloride PVC, polyethylene terephthalate PET, polybutylene terephthalate PBT, polypropylene PP, polyurethane PU, polyamide PA, polyvinyl butyral PVB, and ethylene-vinyl acetate copolymer EVA.

12. 12. The battery case according to claim 11, wherein the plastic sheet is thermoplastic polyurethane (TPU).

13. 2. The battery case according to claim 1, wherein the waterproof layer (2) has a thickness of 0.01 mm to 1 mm.

14. 2. The battery case according to claim 1, wherein the battery case has a thickness of 1.0 mm to 50 mm.

15. The battery case according to any one of claims 1 to 14; and A battery disposed inside the battery case A battery pack comprising:

16. 16. The battery pack according to claim 15, wherein the battery case is an upper cover and / or a lower cover of the battery pack.