Inkjet printing method

Abstract

To provide an inkjet printing method which is excellent in clarity of a printed image including a dark image forming part and a light image forming part while suppressing generation of a streak on a printed matter to be obtained even in printing by a line head-type inkjet system using low liquid-absorbing printing medium.SOLUTION: Provided is an inkjet printing method for forming, on a printing medium, a printed image which includes a dark image forming part and a light image forming part, and has a larger printing duty of ink containing a coloring agent of the dark image forming part than a printing duty of ink containing a coloring agent of the light image forming part. The method includes: a step 1 of imparting pretreatment liquid to an outer edge portion of an area being a dark image forming part to obtain a printing medium having a pretreatment liquid imparting part; and a step 2 of imparting ink containing a coloring agent to an area being a dark image forming part of a surface having the pretreatment liquid imparting part of the printing medium obtained in the step 1, by a line head-type inkjet system.SELECTED DRAWING: None

Description

[Technical field]

[0001] The present invention relates to an inkjet printing method. [Background technology]

[0002] Inkjet printing has many advantages, such as the fact that it does not require plate making, it is easily adaptable to variable information, and printing onto a print medium is not contacted. In addition to being used in offices and homes, inkjet printing has recently been expanded to commercial printing applications where a much larger number of pages are to be printed. In commercial printing applications, there is a demand for improved image quality when printing on non-liquid-absorbent print media such as resin films, in addition to low-liquid-absorbent print media such as printing paper. In response, various proposals have been made.

[0003] For example, in Patent Document 1, for the purpose of providing an image forming apparatus capable of obtaining an image with high image density while suppressing bleeding between image and non-image areas, the apparatus includes a recording medium, an ink containing a coloring material, an organic solvent, and water, a liquid containing an organic solvent and water but not a coloring material, a means for applying the ink onto the recording medium to form an image area, and a means for applying the liquid to non-image areas other than the image area on the recording medium, and the static surface tension γ A and the static surface tension γ of the liquid at 25°C B satisfies a specific relationship, and the image forming apparatus does not apply the liquid to the image portion. Furthermore, Patent Document 2 describes an inkjet recording method for performing recording on a recording medium using color inks containing color materials, with the aim of preventing bleeding of the color inks regardless of the type of recording medium used, such as a recording medium with excellent ink absorption capacity or a recording medium with poor ink absorption capacity, and for recording the edge of a recording area recorded with the color inks using a clear ink that does not contain color materials and has a static surface tension and a dynamic surface tension at a lifetime of 100 milliseconds smaller than those of the color inks. [Prior art documents] [Patent documents]

[0004] [Patent Document 1] JP 2018-126972 A [Patent Document 2] JP 2009-196274 A Summary of the Invention [Problem to be solved by the invention]

[0005] In commercial printing applications, high productivity is required, so high-speed printing is performed. To accommodate this high-speed printing, line-head print heads have been developed. Conventional serial-head print heads print by operating the head (nozzle) multiple times, whereas line-head print heads are equipped with a head that can perform inkjet printing on a width equal to or greater than the length of the print medium in the direction perpendicular to the transport direction, so high-speed printing is possible by scanning only the print medium while keeping the print head fixed. On the other hand, in printing using the line-head inkjet method, unlike the serial-head type, the head cannot print by going back and forth multiple times in the print area, so that it is difficult to compensate for the deviation in the ink landing position caused by the ejection deviation, and therefore there is a problem that streaks (lines) are likely to occur. In addition, in printing in which a print image including a dark image forming portion and a light image forming portion is formed on a low-liquid-absorbent print medium, bleeding occurs at the boundary between the dark image forming portion and the light image forming portion, and the resulting print image becomes unclear. However, the technologies of Patent Documents 1 and 2 are not fully satisfactory in addressing these problems, and there is a need for the development of a technology that suppresses the occurrence of streaks while also providing excellent clarity of printed images including dark image forming areas and light image forming areas, and in particular the sharpness of printed images of cut-out characters, even in printing by a line head type inkjet method that uses a low liquid absorbency printing medium, specifically a resin film. The present invention aims to provide an inkjet printing method that suppresses the occurrence of streaks in the resulting print, even when printing by a line head type inkjet method using a low liquid absorbency printing medium, and that provides excellent clarity of printed images including a dark image forming section and a light image forming section. [Means for solving the problem]

[0006] The present inventors have discovered that the above-mentioned problems can be solved by an inkjet printing method for forming a print image including a dark image forming section and a light image forming section on a print medium, the method comprising the steps of: applying a pretreatment liquid to the outer edge of a section that will become the dark image forming section to obtain a print medium having a pretreatment liquid application section; and applying an ink containing a colorant by a line head type inkjet method to a section that will become the dark image forming section on the surface of the print medium obtained in the step that has the pretreatment liquid application section.

[0007] That is, the present invention provides an inkjet printing method including a dark image forming unit and a light image forming unit, and forming a print image on a print medium, the print duty of ink containing a colorant in the dark image forming unit being higher than the print duty of ink containing a colorant in the light image forming unit, Step 1: applying a pretreatment liquid to an outer edge of a portion that will become a dark image forming portion to obtain a print medium having a pretreatment liquid application portion; and Step 2: Applying ink containing a colorant to a portion of the surface of the printing medium obtained in step 1 having the pretreatment liquid applied thereto, which is to become a dark image forming portion, by a line head type inkjet method. Effect of the Invention

[0008] The present invention can provide an inkjet printing method that suppresses the occurrence of streaks in the resulting printed matter, even when printing using a line head inkjet method that uses a low liquid absorbency printing medium, and that provides excellent clarity of printed images that include dark image forming sections and light image forming sections. [Brief description of the drawings]

[0009] [Figure 1] 1 shows an example of a schematic diagram of a printed image including a dark image forming section and a light image forming section. In the figure, the solid line is the boundary between the dark image forming section and the light image forming section, the area surrounded by the solid line is the light image forming section, and the area surrounded by the solid line and the dotted line is the outer edge of the part that will become the dark image forming section. [Diagram 2] 1 shows an example of a schematic diagram of a printed image including a dark image forming section and a light image forming section. In the figure, the solid line is the boundary between the dark image forming section and the light image forming section, the area surrounded by the solid line indicates the light image forming section, the area surrounded by the solid line and dotted lines indicates the outer edge of the part that will become the dark image forming section, and the area surrounded by the solid line and dashed lines indicates the inner edge of the part that will become the dark image forming section. [Diagram 3] FIG. 1 is a schematic diagram of a printed image of a cut-out character formed in Examples 1 to 8, 10 to 12 and Comparative Examples 1 and 2, which is composed of a light image forming section (i) (printing duty of ink containing a colorant: 0%) and a dark image forming section (ii) (printing duty of ink containing a colorant: 100%). [Figure 4-a] FIG. 2 is an explanatory diagram showing an area to which a pretreatment liquid is applied in step 1 of Examples 1 to 10 and 12. [Figure 4-b] FIG. 13 is an explanatory diagram showing an area to which the pretreatment liquid is applied in step 1 of Example 11. [Diagram 5] FIG. 2 is an explanatory diagram showing an area to which an ink containing a colorant is applied in step 2 in Examples 1 to 12 and Comparative Examples 1 and 2. [Figure 6] 1 is a photograph of a printed image of cut-out characters obtained in Example 1. [Figure 7] 1 is a photograph of a printed image of cut-out characters obtained in Comparative Example 2. [Figure 8] FIG. 13 is a schematic diagram of a barcode printed image formed in Example 13, which is composed of a light image forming portion (i) (printing duty of ink containing a colorant: 0%) and a dark image forming portion (ii) (printing duty of ink containing a colorant: 100%). [Figure 9] FIG. 2 is an explanatory diagram showing an area to which a pretreatment liquid is applied in step 1 of Example 13. [Figure 10] 1 is a photograph of a printed image of a barcode obtained in Example 13. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0010] [Inkjet printing method] The inkjet printing method of the present invention (hereinafter also referred to as "the printing method of the present invention") is an inkjet printing method which includes a dark image forming unit and a light image forming unit, and forms a print image on a printing medium, in which the printing duty of ink containing a colorant (hereinafter also referred to as "colorant-containing ink") in the dark image forming unit is higher than the printing duty of the colorant-containing ink in the light image forming unit, Step 1: applying a pretreatment liquid to an outer edge of a portion that will become a dark image forming portion to obtain a print medium having a pretreatment liquid application portion; and Step 2: Applying a colorant-containing ink to a portion of the surface of the printing medium obtained in step 1 having the pretreatment liquid applied thereto, which is to become a dark image forming portion, by a line head type inkjet method. In the present invention, the term "printing" is a concept that includes printing for recording characters or images and printing letters.

[0011] The printing method of the present invention, even in the case of printing by a line head type inkjet method using a low liquid absorbent print medium, suppresses the occurrence of streaks in the resulting print and provides excellent clarity of the printed image including dark image forming areas and light image forming areas. The reason for this is unclear, but is thought to be as follows. In the printing method of the present invention, a printing image is formed on a printing medium, which includes a dark image forming section and a light image forming section, and the printing duty of the colorant-containing ink in the dark image forming section is greater than the printing duty of the colorant-containing ink in the light image forming section. The printing method includes, as step 1, a step of applying a pretreatment liquid to the outer edge of the part that will become the dark image forming section to obtain a printing medium having a pretreatment liquid application section, and as step 2, a step of applying a colorant-containing ink to the part that will become the dark image forming section on the surface of the printing medium obtained in step 1 having the pretreatment liquid application section by a line head type inkjet method, whereby the pretreatment liquid and the colorant-containing ink come into contact with each other at the boundary between the outer edge of the dark image forming section to which the pretreatment liquid is applied and the dark image forming section to which the colorant-containing ink is applied, thereby suppressing the wetting and spreading of the ink, and suppressing the bleeding of the ink at the boundary between the light image forming section and the dark image forming section, which is considered to improve the clarity of the printed image including the dark image forming section and the light image forming section. On the other hand, in the present invention, the pretreatment liquid is not applied to the entire surface of the printing medium. When the pretreatment liquid is applied to the entire surface of the printing medium, the dark image forming portion and the light image forming portion are printed with a colorant-containing ink by a line head type inkjet method, and the above-mentioned streaks become more noticeable due to the effect of suppressing the wetting and spreading of the pretreatment liquid that is applied in advance to the dark image forming portion and the light image forming portion. However, in the present invention, since the pretreatment liquid is not applied to most of the dark image forming portion and the light image forming portion, the occurrence of streaks is unlikely to be induced, and the effect of the pretreatment liquid can be well expressed at the boundary between the dark image forming portion and the light image forming portion. As a result, it is considered that it is possible to simultaneously suppress the occurrence of streaks and improve the clarity of the printed image including the dark image forming portion and the light image forming portion.

[0012] The present invention is an inkjet printing method that includes a dark image forming unit and a light image forming unit, and forms a print image on a printing medium in which the printing duty of the colorant-containing ink in the dark image forming unit is greater than the printing duty of the colorant-containing ink in the light image forming unit. In the present invention, the "printing duty of the colorant-containing ink" means the ratio of the area occupied by the colorant-containing ink in a predetermined area on the printing medium, that is, the ratio of the cumulative area to which the colorant-containing ink is applied. For example, the "printing duty of the colorant-containing ink is 100%" in the present invention means that when ink droplets are applied in a square lattice shape without thinning out the application area of ​​the colorant-containing ink, the ink droplets are applied so that the ends of adjacent ink dots spread in a circle on the printing medium are in contact with each other at the circumferential position, and for example, a dark image forming part where the "printing duty of the colorant-containing ink" is 100% means a solid printing part. On the other hand, the "printing duty of the colorant-containing ink is 0%" in the present invention means that no ink is applied at all in a predetermined area on the printing medium, and for example, a light image forming part where the "printing duty of the colorant-containing ink" is 0% means a non-printing part.

[0013] From the viewpoint of forming a high-quality printed image by clarifying the outline of the dark image forming portion, the printing duty of the colorant-containing ink in the dark image forming portion is preferably more than 50%, more preferably 70% or more, even more preferably 90% or more, and even more preferably 100%. From the viewpoint of obtaining a printed image of cut-out characters, the printing duty of the colorant-containing ink in the dark image forming portion is preferably 100%. The printing duty of the colorant-containing ink in the light image forming portion is 0% or more from the viewpoint of forming a high-quality printed image by clarifying the contour of the dark image forming portion, and is preferably 50% or less, more preferably 30% or less, and even more preferably 10% or less. The printing duty of the colorant-containing ink in the light image forming portion is preferably 0% from the viewpoint of obtaining a printed image of hollow characters. The difference between the printing duty of the colorant-containing ink in the dark image forming portion and the printing duty of the colorant-containing ink in the light image forming portion is preferably 50% or more, more preferably 70% or more, and even more preferably 90% or more, from the viewpoint of forming a high-quality printed image by clarifying the contour of the dark image forming portion. The difference between the printing duty of the colorant-containing ink in the dark image forming portion and the printing duty of the colorant-containing ink in the light image forming portion is preferably 100% from the viewpoint of obtaining a printed image of hollow characters.

[0014] In the present invention, examples of the printed image that can be formed include images of cut-out characters, one-dimensional codes such as bar codes, two-dimensional codes of matrix type or stack type, and extremely small characters. In the present invention, an "image of cut-out characters" means an image in which characters can be recognized by light image forming areas of a color other than the first color against a background of dark image forming areas inkjet printed in a first color. In this case, the first color and the color other than the first color may be primary colors such as yellow, magenta, cyan, and black, respectively, or may be a mixture of these primary colors, that is, a secondary color. Among these print images, from the viewpoint of improving the clarity of the print image while suppressing the occurrence of streaks in the resulting print, a cut-out character image is preferable as the print image to be formed.

[0015] <Process 1> Step 1 is a step of applying a pretreatment liquid to the outer edge of a region that will become a dark image forming region, thereby obtaining a print medium having a pretreatment liquid application region. In the present invention, the outer edge portion of the region that becomes the dark image forming portion belongs to the light image forming portion in the printed image that is formed, as shown in FIG. From the standpoint of practicality taking into account ejection distortion and misalignment in the transport of the printing medium, and from the standpoint of improving the clarity of the printed image while suppressing the occurrence of streaks in the resulting print, the outer edge portion of the part that becomes the dark image forming section is preferably at least 0.01 mm, more preferably at least 0.1 mm, even more preferably at least 0.2 mm, and preferably at most 1 mm, more preferably at most 0.7 mm, even more preferably at most 0.4 mm, calculated from the boundary between the dark image forming section and the light image forming section, on the side away from the dark image forming section. The application of the pretreatment liquid in step 1 may be at least to the outer edge of the area that will become the dark image forming area of ​​the printed image, and may be to the entire light image forming area including the outer edge of the area that will become the dark image forming area. In the printing method of the present invention, the application of the pretreatment liquid in step 1 is preferably only to the outer edge of the area that will become the dark image forming area, and when the printing duty of the colorant-containing ink in the light image forming area is 0%, the application of the pretreatment liquid in step 1 is more preferably only to the outer edge of the area that will become the dark image forming area. When the printing duty of the colorant-containing ink in the light image forming portion exceeds 0%, the pretreatment liquid may be applied to the outer edge of the portion that will become the dark image forming portion, as well as to the portion of the portion that will become the light image forming portion to which the colorant-containing ink is not applied in the step 1. In this case, in the step 2 described below, the colorant-containing ink is applied by a line head type inkjet method to the portion to which the colorant-containing ink is applied in the portion that will become the light image forming portion on the surface of the printing medium obtained in the step 1 having the pretreatment liquid application portion. In addition, when the printing duty of the colorant-containing ink in the light image forming section is more than 0%, the "part to which the colorant-containing ink is not applied" refers to a non-output part in the raster image data used for outputting the colorant-containing ink. For example, when the printing duty of the colorant-containing ink in the light image forming section is 40%, the "part to which the colorant-containing ink is not applied" refers to a non-output part of the colorant-containing ink that occupies 60% of the raster image used for outputting the colorant-containing ink in the light image forming section.

[0016] In step 1, from the viewpoint of improving the clarity of the printed image while suppressing the occurrence of streaks in the resulting printed matter, it is preferable that (1) the pretreatment liquid is not applied to the area that will become the dark image forming area, or (2) when the pretreatment liquid is applied to the area that will become the dark image forming area, the pretreatment liquid is further applied to the inner edge part of the area that will become the dark image forming area, and the pretreatment liquid is not applied to the dark image forming area other than the inner edge part of the area that will become the dark image forming area. Among these, the case of (2) is more preferable because it is possible to suppress misalignment between the application part of the pretreatment liquid in step 1 and the landing part of the colorant-containing ink in step 2, and it is possible to improve the clarity of the printed image even if it is a fine printed image. In the present invention, the inner edge portion of the portion that becomes the dark image forming portion belongs to the dark image forming portion in the printed image that is formed, as shown in FIG. From the standpoint of practicality taking into account ejection distortion and misalignment in the transport of the printing medium, and from the standpoint of suppressing misalignment of the landing position of the colorant-containing ink to further improve the clarity of the printed image, the inner edge portion of the area that becomes the dark image forming portion is preferably at least 0.01 mm, more preferably at least 0.1 mm, even more preferably at least 0.2 mm, and preferably at most 1 mm, more preferably at most 0.7 mm, even more preferably at most 0.4 mm, calculated from the boundary between the dark image forming portion and the light image forming portion, on the side away from the light image forming portion.

[0017] (print media) As the printing medium used in the present invention, either a low-absorbency printing medium or a high-absorbency printing medium can be used, but from the viewpoint of suppressing the occurrence of streaks in the resulting printed matter and from the viewpoint of the clarity of the printed image, a low-absorbency printing medium is preferable. In the present invention, whether a printing medium has low or high liquid absorption is determined by the amount of water absorbed by the printing medium when the printing medium is in contact with pure water for 100 ms. The amount of water absorbed can be measured as the amount of transfer when the printing medium is in contact with pure water for 100 ms under conditions of 23°C and 50% relative humidity using an automatic scanning liquid absorption meter (e.g., "KM500win" manufactured by Kumagai Riki Kogyo Co., Ltd.). In the present invention, the term "low liquid absorption" is a concept including low liquid absorption and non-liquid absorption, and the water absorption amount is 0 g / m2 More than 7g / m 2 "Highly absorbent" means that the water absorption is 7 g / m or less. 2 It means to be super. Examples of low-absorbency print media include low-absorbency coated paper and non-absorbency resin film. Examples of coated paper include general-purpose glossy paper and multicolor foam gloss paper. The resin film is preferably at least one selected from the group consisting of polyester film, polyvinyl chloride film, polypropylene film, and polyethylene film, and more preferably polyester film. These resin films may be surface-treated, such as by corona treatment. Highly absorbent print media include highly absorbent plain paper. When a resin film is used as the low-liquid-absorbent printing medium, step 1 may be performed by setting areas that will become dark image forming areas and areas that will become light image forming areas based on a mirror image obtained by inverting the desired printed image so that the printed image appears as the desired image when viewed from the opposite side of the printed image forming surface of the non-liquid-absorbent film.

[0018] (Pretreatment solution) <Component (A) that suppresses wetting and spreading> The pretreatment liquid according to the present invention preferably contains a component (A) that suppresses the wetting and spreading of the colorant-containing ink used in step 2 on the printing medium (hereinafter also simply referred to as “component (A) that suppresses wetting and spreading”). Since the pretreatment liquid according to the present invention contains component (A) that suppresses wetting and spreading, at the boundary between the outer edge of the dark image forming section to which the pretreatment liquid is applied and the dark image forming section to which the colorant-containing ink is applied, component (A) that suppresses wetting and spreading prevents the colorant-containing ink from entering the light image forming section, thereby suppressing ink bleeding at the boundary between the light image forming section and the dark image forming section, and it is believed that the clarity of a printed image including the dark image forming section and the light image forming section can be improved. In the present invention, the component (A) that suppresses wetting and spreading is preferably one or more selected from the group consisting of aggregating compounds (A1) and hydrophobic compounds (A2). That is, the pre-treatment liquid according to the present invention preferably contains one or more selected from the group consisting of aggregating compounds (A1) and hydrophobic compounds (A2). These will be explained below.

[0019] [Agglutinating compound (A1)] In the present invention, the "aggregating compound (A1)" is a component that, when applied to a printing medium, causes the ink to thicken or precipitate due to the occurrence of aggregation caused by a decrease in the dispersibility of the dispersoid present in the colorant-containing ink or the decrease in the solubility of the solute, thereby preventing the ink from entering a light image forming section. In the present invention, the dispersoid present in the colorant-containing ink is an ink component such as a pigment that is currently dispersed in the ink in a solid state. In addition, the solute present in the colorant-containing ink is a component that is in a dissolved state in the ink, but its solubility is lost when it comes into contact with a printing medium treated with a pretreatment liquid, causing thickening or precipitation. Specific examples of components (solutes) that are in a dissolved state in the colorant-containing ink, but whose solubility is lost when it comes into contact with a printing medium treated with a pretreatment liquid, causing thickening or precipitation, include dyes and water-soluble resins. The aggregating compound (A1) is preferably a metal salt, an acid or a salt thereof, or a cationic compound. The aggregating compound (A1) may be used alone or in combination of two or more. Examples of the metal salt include monovalent metal salts and divalent or higher metal salts. Examples of the acid include organic acids and inorganic acids. Examples of the cationic compound include cationic resins and cationic surfactants. Among these, the aggregating compound (A1) is more preferably at least one selected from the group consisting of metal salts, acids or salts thereof, and cationic resins.

[0020] (Metal Salts) The metal salt used as the coagulating compound (A1) is preferably a polyvalent metal salt from the viewpoint of improving the sharpness of the printed image while suppressing the occurrence of streaks in the resulting print. Any polyvalent metal salt can be used as long as it is composed of a divalent or higher polyvalent metal ion and an anion (a counter ion of the polyvalent metal ion). Examples of divalent or higher polyvalent metal ions include calcium, magnesium, copper, nickel, zinc, barium, aluminum, titanium, strontium, chromium, cobalt, and iron ions. Among these, from the viewpoint of suppressing the occurrence of streaks in the resulting printed matter and improving the sharpness of the printed image, divalent or trivalent metal ions are preferred, and divalent metal ions are more preferred. Examples of divalent metal ions include ions of elements belonging to Group 2 in the periodic table of elements, and specifically, magnesium ions, calcium ions, iron (II) ions, and the like are preferred. Examples of trivalent metal ions include aluminum ions, iron (III) ions, and the like are preferred. Among these, from the viewpoint of suppressing the occurrence of streaks in the resulting printed matter while improving the clarity of the printed image, more preferred is one or more selected from the group consisting of magnesium ions, calcium ions, and aluminum ions, even more preferred is one or more selected from the group consisting of magnesium ions and calcium ions, and even more preferred is calcium ions. The anion of the polyvalent metal salt may be an inorganic ion or an organic ion. Examples of inorganic ions include monovalent anions such as nitrate ions and halide ions; and divalent anions such as sulfate ions. The organic ions include organic acid ions such as carboxylate ions. Among these, the anion is preferably an inorganic ion, more preferably one or more selected from the group consisting of a nitrate ion and a sulfate ion, and further preferably a nitrate ion.

[0021] From the viewpoint of suppressing the occurrence of streaks in the resulting printed matter while improving the clarity of the printed image, the polyvalent metal salt is preferably one or more selected from the group consisting of magnesium nitrate, magnesium sulfate, calcium nitrate, and aluminum nitrate, more preferably one or more selected from the group consisting of magnesium nitrate, calcium nitrate, and aluminum nitrate, even more preferably one or more selected from the group consisting of magnesium nitrate and calcium nitrate, and still more preferably calcium nitrate. The polyvalent metal salt may have water of hydration in the raw material form. The polyvalent metal salts may be used alone or in combination of two or more.

[0022] (acid) The acid used as the flocculating compound (A1) may be at least one selected from the group consisting of organic acids and inorganic acids. Examples of the organic acid include aliphatic carboxylic acids, aliphatic dicarboxylic acids, hydroxycarboxylic acids, carboxylic acids having a heterocyclic group, derivatives of these compounds, and salts thereof. Examples of the aliphatic carboxylic acid include formic acid and acetic acid. Examples of the aliphatic dicarboxylic acid include oxalic acid, malonic acid, succinic acid, glutaric acid, maleic acid, and fumaric acid. Examples of hydroxycarboxylic acids include glycolic acid, lactic acid, malic acid, tartaric acid, and citric acid. Examples of the carboxylic acid having a heterocyclic group include ascorbic acid, pyrrolidone carboxylic acid, pyrrone carboxylic acid, pyrrole carboxylic acid, furan carboxylic acid, pyridine carboxylic acid, coumaric acid, thiophene carboxylic acid, and nicotinic acid. Preferred examples of the inorganic acid include sulfuric acid, hydrochloric acid, nitric acid, and phosphoric acid. Among these, from the viewpoint of suppressing the occurrence of streaks in the resulting printed matter while improving the clarity of the printed image, the acid is preferably an organic acid or a salt thereof, more preferably an aliphatic dicarboxylic acid or a salt thereof, even more preferably one or more selected from the group consisting of oxalic acid, malonic acid and succinic acid, and even more preferably malonic acid. The acids may be used alone or in combination of two or more. These acids may form salts, and when the acids form metal salts, they are included in the above metal salts.

[0023] (cationic resin) Examples of the cationic compound used as the flocculant compound (A1) include cationic resins and cationic surfactants. The cationic resin preferably has a cationic group. In the present invention, the term "cationic group" refers to a cationic group or a group that can be ionized to become a cationic group. Examples of cationic groups include basic groups such as a primary amino group (-NH2), a secondary amino group (-NHR, =NH (imino group)), a tertiary amino group (-NRR'), a quaternary ammonium group, and a hydrazino group. Among these, the cationic resin preferably has one or more groups selected from the group consisting of a primary amino group, a secondary amino group, a tertiary amino group, and a quaternary ammonium group, and more preferably has a quaternary ammonium group, from the viewpoint of improving the clarity of the printed image while suppressing the occurrence of streaks in the resulting printed matter. The basic group includes those neutralized with acids such as hydrochloric acid, sulfuric acid, nitric acid, acetic acid, formic acid, maleic acid, fumaric acid, citric acid, tartaric acid, adipic acid, and lactic acid. The cationic resin may be used alone or in combination of two or more kinds.

[0024] The cationic resin has a cationic degree of preferably 0.5 meq / g or more, more preferably 3.0 meq / g or more, and preferably 10 meq / g or less, from the viewpoint of suppressing the occurrence of streaks in the resulting printed matter and improving the clarity of the printed image. The cationic degree of the cationic resin can be determined by colloid titration using potassium polyvinyl sulfate reagent. Examples of the cationic resin include cationic vinyl resins, cationic olefin resins, cationic urethane resins, and cationic amine resins.

[0025] The cationic vinyl resin includes a vinyl resin containing a structural unit derived from a vinyl monomer having a cationic group. Suitable examples of vinyl monomers having a cationic group include alkyl(meth)acrylate-based quaternary ammonium salts, alkyl(meth)acryloylamide-based quaternary ammonium salts, (meth)acrylic acid esters having a dialkylamino group, (meth)acrylamides having a dialkylamino group, styrenes having a dialkylamino group, amino group-containing heterocyclic vinyl monomers, and allylamine compounds. Examples of alkyl (meth)acrylate-based quaternary ammonium salts include (meth)acryloyloxyethyl trimethyl ammonium chloride, (meth)acryloyloxyethyl triethyl ammonium chloride, (meth)acryloyloxyethyl dimethyl benzyl ammonium chloride, (meth)acryloyloxyethyl methyl morpholino ammonium chloride, and 2-hydroxy-3-(meth)acryloyloxypropyl trimethyl ammonium chloride. Examples of the alkyl(meth)acryloylamide quaternary ammonium salt include (meth)acryloylaminoethyl triethyl ammonium chloride and (meth)acryloylaminoethyl dimethylbenzyl ammonium chloride. Examples of the (meth)acrylic acid ester having a dialkylamino group include trimethyl[(vinylphenyl)methyl]ammonium chloride, dimethylaminoethyl (meth)acrylate, diethylaminoethyl (meth)acrylate, dipropylaminoethyl (meth)acrylate, diisopropylaminoethyl (meth)acrylate, dibutylaminoethyl (meth)acrylate, diisobutylaminoethyl (meth)acrylate, and di-t-butylaminoethyl (meth)acrylate. Examples of (meth)acrylamides having a dialkylamino group include dimethylaminopropyl(meth)acrylamide, diethylaminopropyl(meth)acrylamide, dipropylaminopropyl(meth)acrylamide, diisopropylaminopropyl(meth)acrylamide, dibutylaminopropyl(meth)acrylamide, diisobutylaminopropyl(meth)acrylamide, and di-t-butylaminopropyl(meth)acrylamide. Examples of styrenes having a dialkylamino group include dimethylaminostyrene and dimethylaminomethylstyrene. Examples of the amino group-containing heterocyclic vinyl monomer include N-vinylpyrrolidine, N-vinylpyrrolidone, and N-vinylcarbazole. Examples of the allylamine compound include allylamine, dimethylallylamine, diallylamine, and methyldiallylamine.

[0026] The cationic vinyl resin may contain structural units derived from monomers other than the vinyl monomer having a cationic group. Examples of such other monomers include alkyl group-containing (meth)acrylic monomers, alkylene oxide chain-containing (meth)acrylic monomers, alkylene oxide chain-containing (meth)acrylic monomers, and aromatic ring-containing (meth)acrylic monomers. Examples of the styrene monomer include styrene and α-methylstyrene. Examples of the alkyl group-containing (meth)acrylic monomer include methyl (meth)acrylate, butyl (meth)acrylate, octyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, lauryl (meth)acrylate, and stearyl (meth)acrylate. Examples of the alkylene oxide chain-containing (meth)acrylic monomer include (poly)ethylene glycol mono(meth)acrylate, (poly)propylene glycol mono(meth)acrylate, and (poly)(ethylene glycol-propylene glycol) mono(meth)acrylate. Examples of aromatic ring-containing (meth)acrylic monomers include phenyl (meth)acrylate, benzyl (meth)acrylate, and phenoxyethyl (meth)acrylate.

[0027] Among these, the cationic vinyl resin is preferably a polyallylamine resin having a structure derived from an allylamine compound in the main skeleton, from the viewpoint of suppressing the occurrence of streaks in the resulting printed matter while improving the clarity of the printed image. Examples of the polyallylamine resin include homopolymers and copolymers of the above-mentioned allylamine compounds. Specific examples of polyallylamine resins include polyallylamine hydrochloride, polyallylamine amidosulfate, allylamine hydrochloride / diallylamine hydrochloride copolymer, allylamine acetate / diallylamine acetate copolymer, allylamine acetate / diallylamine acetate copolymer, allylamine hydrochloride / dimethylallylamine hydrochloride copolymer, allylamine / dimethylallylamine copolymer, polydiallylamine hydrochloride, polymethyldiallylamine hydrochloride, polymethyldiallylamine amidosulfate, polymethyldiallylamine acetate, polydiallyldimethylammonium chloride, diallylamine acetate / sulfur dioxide copolymer, diallylmethylethylammonium ethylsulfate / sulfur dioxide copolymer, methyldiallylamine hydrochloride / sulfur dioxide copolymer, diallyldimethylammonium chloride / sulfur dioxide copolymer, diallyldimethylammonium chloride / acrylamide copolymer, and the like.

[0028] The cationic vinyl resin may be synthesized by a known method or may be a commercially available product. Commercially available cationic vinyl resins include diallyldimethylammonium chloride polymers such as PAS-H-1L (trade name, manufactured by Nittobo Medical Co., Ltd.).

[0029] The cationic olefin resin has a structural unit derived from an olefin such as ethylene or propylene as a basic skeleton, and known ones can be appropriately selected and used. The cationic olefin resin may be used as an emulsion dispersed in a medium containing water, an organic solvent, or the like. As the cationic olefin resin, a commercially available product can be used. Examples of commercially available cationic olefin resins include Arrowbase CB-1200 and Arrowbase CD-1200 (both are product names manufactured by Unitika Ltd.).

[0030] The cationic urethane resin may be one obtained by reacting an isocyanate group of a urethane pre-resin obtained by polyaddition reaction of an organic compound (polyol) having two or more alcoholic hydroxyl groups in one molecule with a polyisocyanate, with an active hydrogen compound for introducing a cationic hydrophilic group. In the polyaddition reaction, a chain extender or a reaction terminator may be used in combination as necessary. The molecular weight can be further increased by using a chain extender. Examples of the chain extender include polyols and polyamines, and examples of the reaction terminator include monoalcohols and monoamines. The cationic urethane resin is preferably used in the form of an emulsion, and the emulsion may contain a dispersant such as a surfactant, if necessary. As the cationic urethane resin, cationic polycarbonate polyol-based urethane resin, cationic polyester polyol-based urethane resin, and cationic polyether polyol-based urethane resin are preferred. As the cationic urethane resin, commercially available products can be used. As the commercially available cationic urethane resin, Hydran CP-7010, CP-7020, CP-7030, CP-7040, CP-7050, CP-7060, CP-7610 (all of which are product names manufactured by DIC Corporation); Superflex 600, 610, 620, 630, 640, 650 (all of which are product names manufactured by Daiichi Kogyo Seiyaku Co., Ltd.); Urethane Emulsion WBR-2120C, WBR-2122C (all of which are product names manufactured by Taisei Fine Chemical Co., Ltd.) and the like can be used.

[0031] Examples of the cationic amine resin include polyamine resins and polyamide resins. The polyamine resin is a resin having an amino group in the main skeleton of the resin. Examples of the polyamine resin include polyalkyleneimines, polyethylenepolyamines, condensates of alkylamines and epihalohydrin, and condensates of alkylamines / ammonia / epihalohydrin. A polyamide resin is a resin having an amide group in the main skeleton of the resin.

[0032] As the cationic amine resin, a commercially available product can be used. Commercially available cationic amine resins include Unisense KHE103L (hexamethylenediamine / epichlorohydrin condensate), Unisense KHE104L (dimethylamine / epichlorohydrin condensate, aqueous solution with a solids concentration of 20% by mass) (all trade names, manufactured by Senka Corporation); FL-14 (trade name, manufactured by SNF Corporation); Arafix 100, 251S, 255, and 255LOX (all trade names, manufactured by Arakawa Chemical Co., Ltd.); and DK modified polyamine resins such as DK6810, DK6853, DK6885, etc.; polyamide epichlorohydrin resins or polyamine epichlorohydrin resins such as WS4010, WS4011, WS4020, WS4024, WS4027, WS4030, etc. (all of which are product names manufactured by Seiko PMC Corporation); dimethylamine / ammonia / epichlorohydrin condensates such as Papiogen P-105 (product name manufactured by Senka Corporation); Sumirez Examples of suitable epoxy resins include polyamide epoxy resins such as Resin 650(30), Resin 675A, Resin 6615, and Resin SLX-1 (all of which are product names manufactured by Taoka Chemical Co., Ltd.); Catiomaster PD-1, Catiomaster PD-7 (dimethylamine / epichlorohydrin condensate), Catiomaster PD-30, Catiomaster A, CDT-2, Catiomaster PE-10, Catiomaster PE-30 (dimethylamine / ethylenediamine / epichlorohydrin condensate), DT-EH, EPA-SK01 (polyamidepolyamine / epichlorohydrin condensate), and TMHMDA-E (all of which are product names manufactured by Yokkaichi Synthetic Co., Ltd.); and Jetfix 36N, Jetfix 38A, and Jetfix 5052 (all of which are product names manufactured by Satoda Chemical Co., Ltd.).

[0033] (Cationic Surfactant) The cationic compound used as the aggregating compound (A1) may be a cationic surfactant. In the present invention, the term "cationic surfactant" refers to a compound having a hydrophobic group and a cationic group as a hydrophilic group, and having no repeating structure derived from a monomer. Preferred examples of the hydrophobic group of the cationic surfactant include alkyl groups having 10 to 22 carbon atoms. Examples of the cationic surfactant include alkylamine salts and alkyl quaternary ammonium salts. Examples of the alkylamine salt include alkylamine acetates such as laurylamine acetate and stearylamine acetate. Examples of the alkyl quaternary ammonium salt include alkyl trimethyl ammonium salt, dialkyl dialkyl ammonium salt, and alkyl benzyl dimethyl ammonium salt. Among these, the cationic surfactant is preferably an alkyl quaternary ammonium salt, and more preferably an alkyltrimethylammonium chloride having an alkyl group having 10 to 22 carbon atoms.

[0034] [Hydrophobic compound (A2)] In the present invention, the “hydrophobic compound (A2)” is a compound that contains a hydrophobic structure and does not cause thickening or precipitation of the colorant-containing ink, but is a component that inhibits the ink from entering a light image forming section due to its low affinity for the ink resulting from the hydrophobic structure at the boundary between the outer edge portion of the dark image forming section to which the pretreatment liquid is applied and the dark image forming section to which the colorant-containing ink is applied. The hydrophobic compound (A2) is preferably at least one selected from the group consisting of anionic resins and hydrophobic surfactants.

[0035] (anionic resin) The "anionic resin" used as the hydrophobic compound (A2) refers to an anionic resin that, when dried at 105°C for 2 hours to reach a constant weight, is dissolved in 100 g of water at 25°C until saturation is reached, the amount of dissolution is 10 g or less. In addition, when the anionic resin has an anionic group and the anionic group is neutralized with a neutralizing agent, the amount of dissolution is determined by the amount of dissolution measured under conditions in which the neutralizing agent is present and the mass ratio of the anionic resin to the neutralizing agent is the same as that in the pretreatment liquid. From the viewpoints of blendability with the pretreatment liquid and dispersion stability in the pretreatment liquid, the anionic resin is preferably a resin having an anionic group. In the present invention, the term "anionic group" refers to an anionic group or a group that can be ionized to become an anionic group. Examples of the anionic group include a carboxy group (-COOM), a sulfonic acid group (-SO3M), and a phosphate group (-OPO3M2). In the above chemical formula, M represents a hydrogen atom, an alkali metal, ammonium, or an organic ammonium. Among these, the anionic resin preferably has a carboxy group as the anionic group, and M is preferably ammonium. Examples of the anionic resin include anionic vinyl resin, anionic urethane resin, and anionic silicone resin. The anionic resins may be used alone or in combination of two or more.

[0036] The anionic vinyl resin is preferably a vinyl resin containing a structural unit derived from a vinyl monomer having an anionic group. The vinyl monomer having an anionic group is preferably one or more selected from the group consisting of acrylic acid, methacrylic acid, crotonic acid, itaconic acid, maleic acid, fumaric acid, and citraconic acid, more preferably one or more selected from the group consisting of acrylic acid and methacrylic acid, and even more preferably acrylic acid.

[0037] The anionic vinyl resin may be either a homopolymer or a copolymer, but is preferably a vinyl resin that further contains a constituent unit derived from a hydrophobic vinyl monomer in addition to a constituent unit derived from a vinyl monomer having an anionic group. Preferred examples of the hydrophobic vinyl monomer include one or more selected from the group consisting of alkyl(meth)acrylates having a linear, branched, or cyclic alkyl group with 1 to 22 carbon atoms, aryl group-containing (meth)acrylates having an aryl group with 6 to 22 carbon atoms, and styrene-based monomers. Preferred examples of alkyl(meth)acrylates having an alkyl group having 1 to 22 carbon atoms include alkyl(meth)acrylates having one or more straight-chain or branched-chain alkyl groups selected from the group consisting of methyl(meth)acrylate, ethyl(meth)acrylate, propyl(meth)acrylate, isopropyl(meth)acrylate, butyl(meth)acrylate, isobutyl(meth)acrylate, hexyl(meth)acrylate, 2-ethylhexyl(meth)acrylate, octyl(meth)acrylate, dodecyl(meth)acrylate, and stearyl(meth)acrylate; and cycloalkyl(meth)acrylates selected from the group consisting of cyclopentyl(meth)acrylate, cyclohexyl(meth)acrylate, and cycloheptyl(meth)acrylate. Preferred examples of the aryl group-containing (meth)acrylate having an aryl group having 6 to 22 carbon atoms include one or more selected from the group consisting of phenyl (meth)acrylate, benzyl (meth)acrylate, phenoxyethyl (meth)acrylate, and phenoxydiethylene glycol (meth)acrylate. The styrene-based monomer is preferably at least one selected from the group consisting of styrene, α-methylstyrene, vinyltoluene, and vinylnaphthalene. Among these, the hydrophobic vinyl monomer is more preferably one or more selected from the group consisting of alkyl(meth)acrylates having a linear or branched alkyl group having from 1 to 8 carbon atoms, cycloalkyl(meth)acrylates, and styrene-based monomers, and even more preferably one or more selected from the group consisting of methyl(meth)acrylate, ethyl(meth)acrylate, butyl(meth)acrylate, isobutyl(meth)acrylate, cyclohexyl(meth)acrylate, styrene, and α-methylstyrene.

[0038] The content of vinyl monomers having an anionic group in the raw material monomers constituting the anionic vinyl resin, or the content of structural units derived from vinyl monomers having an anionic group in the anionic vinyl resin, is preferably 5 mass% or more, more preferably 10 mass% or more, even more preferably 15 mass% or more, and is preferably 40 mass% or less, more preferably 36 mass% or less, even more preferably 32 mass% or less. The content of hydrophobic vinyl monomers in the raw material monomers constituting the anionic vinyl resin, or the content of structural units derived from hydrophobic vinyl monomers in the anionic vinyl resin, is preferably 60 mass% or more, more preferably 64 mass% or more, even more preferably 68 mass% or more, and is preferably 95 mass% or less, more preferably 90 mass% or less, even more preferably 85 mass% or less.

[0039] The anionic vinyl resin preferably has a crosslinked structure from the viewpoint of suppressing the occurrence of streaks in the resulting printed matter and improving the clarity of the printed image. From the same viewpoint as above, the anionic vinyl resin having a crosslinked structure is preferably obtained by reacting an anionic vinyl resin containing a structural unit derived from a vinyl monomer having an anionic group and a structural unit derived from a hydrophobic vinyl monomer with a crosslinking agent. In this case, the anionic vinyl resin having a crosslinked structure has a structure derived from a crosslinking agent in addition to the structural unit derived from a vinyl monomer having an anionic group and the structural unit derived from a hydrophobic vinyl monomer. As the crosslinking agent, from the viewpoint of suppressing the occurrence of streaks in the resulting printed matter while improving the clarity of the printed image, a polyglycidyl ether compound of a polyhydric alcohol having a hydrocarbon group having from 3 to 8 carbon atoms is preferred, more preferably one or more compounds selected from the group consisting of pentaerythritol polyglycidyl ether and trimethylolpropane polyglycidyl ether, and even more preferably trimethylolpropane polyglycidyl ether.

[0040] The crosslinking rate of the anionic vinyl resin having a crosslinked structure is preferably 20 mol% or more, more preferably 30 mol% or more, even more preferably 40 mol% or more, and preferably 80 mol% or less, more preferably 70 mol% or less, even more preferably 60 mol% or less. When the anionic vinyl resin having a crosslinked structure is obtained by reacting an anionic vinyl resin containing a constituent unit derived from a vinyl monomer having an anionic group and a constituent unit derived from a hydrophobic vinyl monomer with a crosslinking agent, the crosslinking rate is calculated from the equivalent of the anionic group of the anionic vinyl resin before crosslinking and the equivalent of the crosslinkable functional group of the crosslinking agent, and is expressed as "the molar equivalent number of the crosslinkable functional group of the crosslinking agent / the molar equivalent number of the anionic group of the anionic vinyl resin before crosslinking".

[0041] The anionic vinyl resin may be a synthetically prepared one or a commercially available product. The anionic vinyl resin may be produced by copolymerizing raw material monomers by a known polymerization method. The anionic vinyl resin is preferably used in the form of a dispersion.

[0042] The acid value of the anionic vinyl resin is preferably 40 mgKOH / g or more, more preferably 80 mgKOH / g or more, even more preferably 100 mgKOH / g or more, still more preferably 120 mgKOH / g or more, and preferably 320 mgKOH / g or less, more preferably 280 mgKOH / g or less, even more preferably 240 mgKOH / g or less, still more preferably 200 mgKOH / g or less. The weight average molecular weight of the anionic vinyl resin is preferably 5,000 or more, more preferably 8,000 or more, even more preferably 10,000 or more, and is preferably 3,000,000 or less, more preferably 1,000,000 or less, even more preferably 200,000 or less. The acid value and weight average molecular weight of the anionic vinyl resin are measured by the method described in the Examples. The acid value of the anionic vinyl resin can also be calculated from the mass ratio of the monomers that constitute the anionic vinyl resin. When the anionic vinyl resin has a crosslinked structure, the acid value of the anionic vinyl resin can also be calculated from the mass ratio of the monomers and crosslinking agent that constitute the anionic vinyl resin.

[0043] Anionic urethane resin is a resin having a constitutional unit derived from an organic compound (polyol) having two or more alcoholic hydroxyl groups in one molecule, a constitutional unit derived from a polyisocyanate, and a constitutional unit derived from a dialkanol carboxylic acid. The anionic urethane resin is obtained by polyaddition reaction of a polyol, a polyisocyanate, and a dialkanol carboxylic acid.

[0044] The polyol constituting the anionic urethane resin is not particularly limited as long as it is a compound having two or more alcoholic hydroxyl groups in one molecule, and is preferably a polycarbonate polyol, a polyester polyol, or a polyether polyol, and more preferably a polycarbonate polyol or a polyester polyol. That is, the anionic urethane resin is preferably a polycarbonate polyurethane or a polyester polyurethane.

[0045] The polycarbonate polyol is a compound obtainable by reacting a carbonate compound with a diol, that is, a diol having a carbonate structure. Examples of the carbonate compound include dimethyl carbonate, diethyl carbonate, diphenyl carbonate, ethylene carbonate, and diethylene carbonate. Examples of the diol include aliphatic diols which may be substituted with lower alcohols, alicyclic diols such as cyclohexanediol and hydrogenated xylylene glycol, and aromatic diols such as xylylene glycol. Among these, aliphatic diols are preferred, and aliphatic diols having a carbon chain length of 4 to 9, such as 1,4-butanediol, 3-methyl-1,5-pentanediol, 1,6-hexanediol, heptanediol, octanediol, and nonanediol, are more preferred.

[0046] The polyester polyol is a compound obtainable by condensing a low molecular weight diol with a dicarboxylic acid, that is, a diol having an ester structure. Examples of low molecular weight diols include diols having 2 to 6 carbon atoms, such as ethylene glycol, diethylene glycol, propylene glycol, dipropylene glycol, and 1,4-butanediol. Among these, ethylene glycol, propylene glycol, and 1,4-butanediol are preferred. Examples of dicarboxylic acids include aliphatic dibasic acids such as succinic acid, glutaric acid, adipic acid, pimelic acid, suberic acid, azelaic acid, sebacic acid, and brassylic acid, and aromatic dibasic acids such as isophthalic acid, terephthalic acid, and naphthalenedicarboxylic acid. Among these, aliphatic dibasic acids are preferred, and dibasic acids with a methylene chain length of 4 to 8, such as adipic acid, pimelic acid, suberic acid, azelaic acid, and sebacic acid, are more preferred.

[0047] Examples of polyether polyols include polyethylene glycol, polypropylene glycol, and polytetramethylene glycol.

[0048] Examples of the polyisocyanate constituting the anionic urethane resin include chain-like aliphatic diisocyanates, aliphatic diisocyanates having a cyclic structure, aliphatic diisocyanates having an aromatic ring, aliphatic diisocyanates having an aromatic ring, aromatic diisocyanates, and modified products of these diisocyanates (carbodiimide, uretdione, uretoimine-containing modified products, etc.). Examples of the chain aliphatic diisocyanate include tetramethylene diisocyanate, 1,6-hexamethylene diisocyanate, dodecamethylene diisocyanate, trimethylhexamethylene diisocyanate, and lysine diisocyanate. Examples of the aliphatic diisocyanate having a cyclic structure include isophorone diisocyanate, hydrogenated xylylene diisocyanate, and dicyclohexylmethane 4,4'-diisocyanate. Examples of the aliphatic diisocyanate having an aromatic ring include xylylene diisocyanate and tetramethylxylylene diisocyanate. Examples of aromatic diisocyanates include tolylene diisocyanate and diphenylmethane diisocyanate. Among these, at least one selected from the group consisting of aliphatic diisocyanates and aromatic diisocyanates is preferred.

[0049] Examples of dialkanol carboxylic acids constituting the anionic urethane resin include dimethylolbutanoic acid, dimethylolpropionic acid, and salts thereof.

[0050] The anionic urethane resin may be used in combination with a chain extender or a reaction terminator, if necessary. The use of a chain extender can further increase the molecular weight. Examples of the chain extender include polyols and polyamines, and examples of the reaction terminator include monoalcohols and monoamines. The anionic urethane resin is preferably used as an emulsion, and the emulsion may contain a dispersing agent such as a surfactant, if necessary.

[0051] The acid value of the anionic urethane resin is preferably 3 mgKOH / g or more, more preferably 5 mgKOH / g or more, even more preferably 7 mgKOH / g or more, and preferably 50 mgKOH / g or less, more preferably 40 mgKOH / g or less, even more preferably 35 mgKOH / g or less.

[0052] An anionic silicone resin is a resin having a silicone structure and an anionic group in the resin structure. The silicone structure may be present in the main chain structure of the resin, or may be present as a side chain of the resin. In the present invention, when an anionic resin has a polyurethane structure or a vinyl structure in addition to a silicone structure, it is classified as an anionic silicone resin if it has a silicone structure in the resin structure. Commercially available examples of anionic silicone resins include Chaline FE-230N (silicone / acrylic graft polymerization type, aqueous emulsion, acid value: 7.7 mg KOH / g), Chaline FE-502 (silicone / acrylic graft polymerization type, aqueous emulsion, acid value: 17.3 mg KOH / g), and Chaline RU-911 (blend type (with urethane), acid value: 2.2 mg KOH / g), all manufactured by Nissin Chemical Industry Co., Ltd.

[0053] The acid value of the anionic silicone resin is preferably 2 mgKOH / g or more, more preferably 4 mgKOH / g or more, even more preferably 6 mgKOH / g or more, and is preferably 20 mgKOH / g or less, more preferably 10 mgKOH / g or less, even more preferably 5 mgKOH / g or less.

[0054] (Hydrophobic surfactant) The "hydrophobic surfactant" used as the hydrophobic compound (A2) refers to a surfactant that does not form a single phase when mixed with ion-exchanged water in a mass ratio of 1:1 at 25° C. Cationic surfactants that meet this condition are not included in the hydrophobic surfactants. The hydrophobic surfactant used as the hydrophobic compound (A2) is preferably a nonionic one. Preferred examples of the nonionic hydrophobic surfactant include one or more surfactants selected from the group consisting of acetylene glycol surfactants and silicone surfactants. An acetylene glycol surfactant is a diol having a carbon-carbon triple bond in the center of its structure and a hydroxyl group on each carbon atom adjacent to the carbon-carbon triple bond, or an ethylene oxide (hereinafter also referred to as "EO") adduct of the diol. The acetylene glycol surfactant can be synthesized by reacting acetylene with a ketone or aldehyde corresponding to the desired acetylene glycol, and can be obtained, for example, by the method described in Takehiko Fujimoto, revised edition, "New Introduction to Surfactants" (published by Sanyo Chemical Industries, Ltd., 1992), pages 94 to 107, etc. The HLB value of the acetylene glycol surfactant is preferably not more than 8. Here, the HLB (hydrophile-lipophile balance) value indicates the affinity of a surfactant to water and oil, and the HLB value of the acetylene glycol surfactant can be calculated from the following formula by the Griffin method. HLB value = 20 x [(total formula weight of hydrophilic groups contained in surfactant) / (molecular weight of surfactant)] Examples of the hydrophilic group contained in the surfactant include a hydroxy group and an ethyleneoxy group. Preferred examples of the acetylene glycol surfactant include one or more selected from the group consisting of 2,4,7,9-tetramethyl-5-decyne-4,7-diol, 3,6-dimethyl-4-octyne-3,6-diol, 2,5-dimethyl-3-hexyne-2,5-diol, and EO adducts thereof. Among these, one or more selected from the group consisting of 2,4,7,9-tetramethyl-5-decyne-4,7-diol and an EO adduct thereof is more preferable, one or more selected from the group consisting of 2,4,7,9-tetramethyl-5-decyne-4,7-diol and those having an average EO addition mole number of 6 or less is even more preferable, and one or more selected from the group consisting of 2,4,7,9-tetramethyl-5-decyne-4,7-diol, an EO adduct of 2,4,7,9-tetramethyl-5-decyne-4,7-diol with an average of 1.3 moles, and an EO adduct of 2,4,7,9-tetramethyl-5-decyne-4,7-diol with an average of 3 moles. Commercially available acetylene glycol surfactants include Surfynol 104PG-50 (2,4,7,9-tetramethyl-5-decyne-4,7-diol, 50% propylene glycol solution with average EO added moles: 0, HLB value: 3.0 (calculation formula: 20×(34 / 226)))) and Surfynol 420 (2,4,7,9-tetramethyl-5-decyne-4,7-diol with average EO added moles of 1.3, HLB value: 6.4 (calculation formula: 20×((34+44×1.3) / (226+44×1.3))))) from Nissin Chemical Industry Co., Ltd. and Air Products & Chemicals.

[0055] A silicone-based surfactant has a silicone structure and a structure exhibiting hydrophilicity, and the hydrophilic structure can be exemplified by a polyether group. The HLB value of the silicone surfactant is preferably not more than 7. Here, the HLB value of the silicone surfactant may be the value given in the catalog. Preferred examples of commercially available silicone surfactants include KF-6015 (polyether modified silicone (straight-chain type), HLB value: 4.5 (catalog value)), KF-6017 (polyether modified silicone (straight-chain type), HLB value: 4.5 (catalog value)), KF-6028 (polyether modified silicone (branched type), HLB value: 4.0 (catalog value)), KF-6038 (polyether modified silicone (branched type, alkyl co-modified type), HLB value: 3.0 (catalog value)), and KF-6048 (polyether modified silicone (straight-chain type, alkyl modified type), HLB value: 3.5 (catalog value)).

[0056] Among these, from the viewpoint of improving the sharpness of a printed image while suppressing the occurrence of streaks in the obtained printed matter, the pretreatment liquid according to the present invention preferably contains, as component (A) that suppresses wetting and spreading, one or more selected from the group consisting of a metal salt, an organic acid or a salt thereof, a cationic resin, an anionic resin, and a hydrophobic surfactant, more preferably contains one or more selected from the group consisting of a metal salt, an organic acid or a salt thereof, a cationic resin, and an anionic resin, and even more preferably contains one or more selected from the group consisting of a metal salt, an organic acid or a salt thereof, a cationic resin, and an anionic resin having a crosslinked structure.

[0057] <Organic solvent (B)> From the viewpoints of improving the sharpness of the printed image while suppressing the occurrence of streaks in the resulting print, it is preferable that the pretreatment liquid according to the present invention further contains an organic solvent (B). The organic solvent (B) can be used alone or in combination of two or more kinds. The static surface tension of the organic solvent (B) measured at 25°C is, from the viewpoint of suppressing the occurrence of streaks in the resulting printed matter while improving the clarity of the printed image, preferably 40 mN / m or less, more preferably 38 mN / m or less, and preferably 18 mN / m or more, more preferably 20 mN / m or more, even more preferably 22 mN / m or more, and still more preferably 24 mN / m or more. The static surface tension of the organic solvent (B) at 25° C. is measured by the method described in the Examples. When two or more organic solvents are used as the organic solvent (B), the static surface tension of the organic solvent (B) is a weighted average value weighted by the content (mass %) of each organic solvent.

[0058] The boiling point of the organic solvent (B) under atmospheric pressure is preferably 280°C or lower, more preferably 260°C or lower, and even more preferably 240°C or lower, from the viewpoint of promoting evaporation from the printing medium and improving the clarity of the printed image while suppressing the occurrence of streaks in the resulting printed matter, and is preferably 140°C or higher, more preferably 160°C or higher, and even more preferably 180°C or higher, from the viewpoint of suppressing excessive acceleration of the evaporation rate and suppressing uneven distribution of the components that suppress wetting and spreading, thereby suppressing the occurrence of streaks in the resulting printed matter and improving the clarity of the printed image. When two or more organic solvents are used as the organic solvent (B), the boiling point of the organic solvent (B) is a weighted average value weighted by the content (mass %) of each organic solvent.

[0059] Examples of the organic solvent (B) include polyhydric alcohols, ethers such as polyhydric alcohol alkyl ethers, polyhydric alcohol aryl ethers, and polyhydric alcohol aralkyl ethers, nitrogen-containing heterocyclic compounds, amides, amines, and sulfur-containing compounds. Among these, at least one selected from the group consisting of polyhydric alcohols and polyhydric alcohol alkyl ethers is preferred.

[0060] Examples of polyhydric alcohols include diols such as ethylene glycol, diethylene glycol, propylene glycol (1,2-propanediol), 1,3-propylene glycol, dipropylene glycol (mixture of isomers), 1,3-butanediol, 1,4-butanediol, 2,3-butanediol, triethylene glycol, polyethylene glycol, and polypropylene glycol.

[0061] Examples of polyhydric alcohol alkyl ethers include (poly)alkylene glycol monoalkyl ethers such as ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol monopropyl ether, ethylene glycol monoisopropyl ether, ethylene glycol monobutyl ether, ethylene glycol monoisobutyl ether, ethylene glycol monohexyl ether, ethylene glycol mono-2-ethylhexyl ether, diethylene glycol monomethyl ether, diethylene glycol monoethyl ether, diethylene glycol monoisopropyl ether, diethylene glycol monobutyl ether, diethylene glycol monoisobutyl ether, diethylene glycol dimethyl ether, diethylene glycol diethyl ether, diethylene glycol methylethyl ether, triethylene glycol monobutyl ether, triethylene glycol dimethyl ether, tetraethylene glycol monomethyl ether, propylene glycol monomethyl ether, propylene glycol monopropyl ether, propylene glycol monobutyl ether, dipropylene glycol monomethyl ether, dipropylene glycol monoethyl ether, dipropylene glycol monopropyl ether, dipropylene glycol monobutyl ether, and dipropylene glycol dimethyl ether. Examples of polyhydric alcohol aryl ethers include ethylene glycol monophenyl ether, and examples of polyhydric alcohol aralkyl ethers include ethylene glycol monobenzyl ether.

[0062] Examples of the nitrogen-containing heterocyclic compound include 2-pyrrolidone, N-methyl-2-pyrrolidone, N-hydroxyethyl-2-pyrrolidone, 1,3-dimethyl-2-imidazolidinone, and ε-caprolactam. Examples of amides include formamide, N-methylformamide, N,N-dimethylformamide, 3-methoxy-N,N-dimethylpropionamide, and 3-butoxy-N,N-dimethylpropionamide. Examples of the amines include monoethanolamine, diethanolamine, triethanolamine, and triethylamine. Examples of sulfur-containing compounds include dimethyl sulfoxide, sulfolane, and thiodiethanol. Other examples of organic solvents include propylene carbonate and ethylene carbonate.

[0063] 〔water〕 The pretreatment liquid according to the present invention preferably further contains water. The pretreatment liquid according to the present invention is preferably water-based. The pretreatment liquid according to the present invention being "water-based" means that water accounts for the largest proportion by mass of the liquid components contained in the pretreatment liquid. The water is preferably pure water or ultrapure water, such as ion-exchanged water, ultrafiltered water, reverse osmosis water, or distilled water, from which ionic impurities have been removed as much as possible.

[0064] The pretreatment liquid according to the present invention may further contain other components, as necessary, such as surfactants other than the above-mentioned cationic surfactants and hydrophobic surfactants, pH adjusters, fixing aids, colorants, defoamers, antiseptics and antifungals, and rust inhibitors.

[0065] The pretreatment liquid according to the present invention preferably further contains a surfactant other than the above-mentioned cationic surfactant and hydrophobic surfactant. The surfactant other than the above-mentioned cationic surfactant and hydrophobic surfactant is preferably a hydrophilic nonionic surfactant. In the present invention, the "hydrophilic nonionic surfactant" refers to a surfactant that becomes one phase when mixed with ion-exchanged water at 25°C in a mass ratio of 1:1. Examples of hydrophilic nonionic surfactants include hydrophilic polyoxyalkylene alkyl ether surfactants, acetylene surfactants, polyhydric alcohol surfactants, fatty acid alkanolamides, silicone surfactants, and fluorine surfactants. Among these, preferred is at least one selected from the group consisting of hydrophilic acetylene surfactants and hydrophilic silicone surfactants. The HLB value of the hydrophilic acetylenic surfactant is preferably greater than 8. Here, the HLB value of the hydrophilic acetylenic surfactant can be determined from the above formula according to the Griffin method. Examples of hydrophilic acetylene surfactants include one or more ethylene oxide (EO) adducts selected from the group consisting of 2,4,7,9-tetramethyl-5-decyne-4,7-diol, 3,6-dimethyl-4-octyne-3,6-diol, 3,5-dimethyl-1-hexyne-3-ol, and 2,4-dimethyl-5-hexyne-3-ol. The average number of moles (n) of EO added in the EO adduct is preferably more than 8, and is preferably 20 or less, more preferably 10 or less. As the hydrophilic silicone surfactant, polyether-modified silicone surfactant is preferred.As the polyether group of polyether-modified silicone surfactant, for example, polyethyleneoxy group, polypropyleneoxy group, ethyleneoxy group and propyleneoxy group (trimethyleneoxy group or propane-1,2-diyloxy group) are preferably added in block form or random form to polyalkyleneoxy group, and can use the compound in which polyether group is grafted to silicone main chain, and the compound in which polyether group is bonded to both ends of silicone main chain in block form. The HLB value of the hydrophilic silicone surfactant is preferably more than 8. Here, the HLB value of the hydrophilic silicone surfactant may be a value listed in the catalog. Examples of commercially available hydrophilic nonionic surfactants include the "Surfynol" series manufactured by Nissin Chemical Industry Co., Ltd. and Air Products & Chemicals, and the "KF" series manufactured by Shin-Etsu Chemical Co., Ltd. The hydrophilic nonionic surfactant may be used alone or in combination of two or more. Among these, it is preferable to use a hydrophilic acetylene glycol surfactant in combination with a hydrophilic silicone surfactant from the viewpoint of improving the clarity of the printed image while suppressing the occurrence of streaks in the resulting printed matter.

[0066] The pretreatment liquid according to the present invention may contain a pH adjuster. The pH adjuster refers to an agent that suppresses pH fluctuations due to environmental changes and keeps the pH of the pretreatment liquid constant. The pH adjuster can be selected from any known agents depending on the pH of the pretreatment liquid according to the present invention.

[0067] The pretreatment liquid according to the present invention may contain a colorant within a range that does not impair the effects of the present invention. Examples of such colorants include those used in the colorant-containing ink described below. When the pretreatment liquid according to the present invention contains a colorant, the colorant is preferably a pigment or a hydrophobic dye from the viewpoint of water resistance, and is preferably a pigment from the viewpoint of achieving high weather resistance. From the viewpoint of improving the clarity of the printed image, the content of the colorant in the pretreatment liquid is preferably 2% by mass or less, more preferably 1% by mass or less, even more preferably 0.1% by mass or less, still more preferably 0.01% by mass or less, and even more preferably no colorant is contained.

[0068] [Composition of pretreatment solution] The content of the component (A) that suppresses wetting and spreading in the pretreatment liquid according to the present invention is preferably 0.5% by mass or more, more preferably 1% by mass or more, and even more preferably 2% by mass or more, from the viewpoints of suppressing the occurrence of streaks in the obtained printed matter and improving the clarity of the printed image, and from the same viewpoints as above, it is preferably 10% by mass or less, more preferably 7% by mass or less, and even more preferably 5% by mass or less.

[0069] The content of the organic solvent (B) in the pretreatment liquid according to the present invention is, from the viewpoints of suppressing the occurrence of streaks in the obtained printed matter while improving the clarity of the printed image, preferably 10% by mass or more, more preferably 15% by mass or more, even more preferably 20% by mass or more, and still more preferably 25% by mass or more, and from the same viewpoints as above, is preferably 50% by mass or less, more preferably 45% by mass or less, even more preferably 40% by mass or less, and still more preferably 35% by mass or less.

[0070] The mass ratio of the content of the component (A) that inhibits wetting and spreading to the content of the organic solvent (B) in the pretreatment liquid according to the present invention [component (A) that inhibits wetting and spreading / organic solvent (B)] is, from the viewpoints of improving the clarity of the printed image while inhibiting the occurrence of streaks in the obtained printed matter, preferably 0.01 or more, more preferably 0.03 or more, even more preferably 0.05 or more, and still more preferably 0.07 or more, and from the same viewpoints as above, is preferably 1 or less, more preferably 0.5 or less, and even more preferably 0.3 or less.

[0071] The water content in the pretreatment liquid according to the present invention is preferably 40% by mass or more, more preferably 50% by mass or more, even more preferably 60% by mass or more, and is preferably 85% by mass or less, more preferably 80% by mass or less, even more preferably 75% by mass or less, and still more preferably 70% by mass or less. When the polyvalent metal salt is used in the form of a hydrate having water of hydration as the raw material form of the polyvalent metal salt, the water content in the pretreatment liquid according to the present invention means the amount including the water content from the hydrate of the polyvalent metal salt.

[0072] When the pretreatment liquid according to the present invention contains a hydrophilic nonionic surfactant, the content of the hydrophilic nonionic surfactant in the pretreatment liquid is preferably 0.01% by mass or more, more preferably 0.1% by mass or more, even more preferably 0.5% by mass or more, and is preferably 3% by mass or less, more preferably 2% by mass or less, even more preferably 1% by mass or less. The content of the colorant in the pretreatment liquid according to the present invention is preferably 2% by mass or less, more preferably 1% by mass or less, even more preferably 0.5% by mass or less, still more preferably 0.1% by mass or less, and even more preferably 0% by mass.

[0073] The pretreatment liquid according to the present invention is preferably prepared by appropriately mixing the component (A) for suppressing wetting and spreading, the organic solvent (B), and, if necessary, water and the other components described above. The pH of the pretreatment liquid can be appropriately adjusted with the pH adjuster described above.

[0074] From the viewpoint of improving the clarity of the printed image, the pretreatment liquid according to the present invention is preferably applied to the printing medium in a solid state, that is, so that the printing duty of the pretreatment liquid is 100%. Here, the "printing duty of the pretreatment liquid" refers to the proportion of the area that the pretreatment liquid occupies within a specific area on the printing medium, that is, the ratio of the cumulative area to which the pretreatment liquid is applied. The method for applying the pretreatment liquid to the printing medium is preferably, for example, by a spray, a brush, or an inkjet method. Among these, the application of the pretreatment liquid is more preferably by an inkjet method from the viewpoint of ease of adjusting the application position of the pretreatment liquid and from the viewpoint of improving the clarity of the printed image while suppressing the occurrence of streaks in the resulting printed matter. From the viewpoint of being able to perform steps 1 and 2 continuously, the device used to apply the pretreatment liquid to the printing medium is preferably one in which the means for applying the pretreatment liquid used in step 1 and the means for applying the colorant-containing ink used in step 2 are integrated, and it is more preferable that the means for applying the pretreatment liquid used in step 1 and the means for applying the colorant-containing ink used in step 2 use a line head type inkjet system.

[0075] The amount of the pretreatment liquid applied to the printing medium is preferably 0.003 g / m from the viewpoint of suppressing the occurrence of streaks in the printed matter and improving the clarity of the printed image. 2 More preferably, 0.01 g / m 2 More preferably, 0.1 g / m 2From the same viewpoint as above, it is preferably 10 g / m 2 Less than 5g / m, more preferably 2 More preferably, 1 g / m 2 Less than 0.5 g / m 2 The following is the result. The amount of the component (A) contained in the pretreatment liquid that suppresses wetting and spreading to be applied to the printing medium is preferably 0.0001 g / m from the viewpoint of suppressing the occurrence of streaks in the printed matter and improving the clarity of the printed image. 2 More preferably, 0.0005 g / m 2 More preferably, 0.001 g / m 2 From the same viewpoint as above, it is preferably 0.1 g / m 2 Less than 0.01 g / m, more preferably 0.01 g / m 2 More preferably, 0.001 g / m or less 2 The following is the result.

[0076] The printing method of the present invention preferably includes, in step 1, a step of applying the pretreatment liquid to the printing medium, and then holding the printing medium to which the pretreatment liquid has been applied at a temperature of 25° C. or higher. This step has the effect of removing volatile components in the pretreatment liquid from the printing medium to which the pretreatment liquid has been applied, and can dry the printing medium (hereinafter, the step of holding the printing medium to which the pretreatment liquid has been applied in step 1 at 25° C. or higher is also referred to as the "drying step of step 1"). The printing method of the present invention preferably includes a step of drying the print medium to which the pretreatment liquid has been applied in step 1. The printing method of the present invention preferably includes a step of fixing the pretreatment liquid application portion in step 1. That is, the drying step of step 1 is preferably a step of keeping the print medium to which the pretreatment liquid has been applied at 25° C. or higher and drying the print medium to which the pretreatment liquid has been applied, and more preferably a step of keeping the print medium to which the pretreatment liquid has been applied at 25° C. or higher and drying the print medium to which the pretreatment liquid has been applied, thereby fixing the area to which the pretreatment liquid has been applied. This can further improve the clarity of the printed image. In step 1, preferred methods for maintaining the print medium to which the pretreatment liquid has been applied at 25° C. or higher include leaving it still, blowing air, heating, reducing pressure, etc. In the printing method of the present invention, application of active energy rays such as ultraviolet rays and radiation is not included in the drying step in step 1 of the present invention. The temperature at which the print medium is held in the drying step of step 1 is preferably 120°C or lower, more preferably 110°C or lower, and even more preferably 100°C or lower, from the viewpoint of suppressing deformation of the print medium, and is preferably 25°C or higher, more preferably 30°C or higher, and even more preferably 40°C or higher, from the viewpoint of drying in a short period of time and further improving the clarity of the printed image. The time for which the holding temperature is maintained (holding time) in the drying step of step 1 is preferably 0.5 seconds or more, more preferably 1 second or more, even more preferably 1.5 seconds or more, and preferably 30 minutes or less, more preferably 20 minutes or less, even more preferably 10 minutes or less, and even more preferably 1 minute or less.

[0077] The drying rate of the pretreatment liquid in the drying step of step 1, i.e., the removal rate of volatile components in the pretreatment liquid, is preferably 40% by mass or more, more preferably 50% by mass or more, even more preferably 60% by mass or more, and still more preferably 80% by mass or more, from the viewpoint of improving the clarity, and in particular the sharpness, of the printed image. In the present invention, the "drying rate of the pretreatment liquid" is the percentage of the ratio of the total mass of components actually removed by the drying step in step 1 to the total mass of components contained in the pretreatment liquid that can be removed by the drying step, and is calculated using the following formula, where M0 is the mass of the printing medium, M1 is the mass of the printing medium immediately after application of the pretreatment liquid in step 1, M2 is the mass of the printing medium after the step of maintaining the printing medium at 25°C or higher, and X% by mass is the proportion of the total mass of components in the pretreatment liquid that can be removed by the drying step in step 1. Drying rate (mass%) = (M1-M2) / [(M1-M0)×X / 100]×100 In the present invention, the proportion X (mass %) of the total mass of components in the pre-treatment liquid that can be removed by the drying step in step 1 is preferably the water content (mass %) in the pre-treatment liquid.

[0078] <Process 2> Step 2 is a step of applying a colorant-containing ink by a line head type inkjet method to a portion of the surface of the printing medium obtained in step 1 having the pretreatment liquid applied thereon, which is to become a dark image forming portion. When the printing duty of the colorant-containing ink in the light image forming portion is 0%, it is preferable not to apply the colorant-containing ink to the light image forming portion in step 2. That is, in this case, step 2 is preferably step 2-1 described below. Step 2-1: A step of applying a colorant-containing ink by a line head type inkjet method only to a portion that will become a dark image forming portion on the surface of the printing medium obtained in step 1 having the pretreatment liquid applied portion.

[0079] Furthermore, when the printing duty of the colorant-containing ink in the light image forming portion exceeds 0%, in step 2, the colorant-containing ink is applied not only to the portion that will become the dark image forming portion on the surface having the pretreatment liquid application portion of the printing medium obtained in step 1, but also to the portion to which the colorant-containing ink is applied in the portion that will become the light image forming portion. That is, in this case, step 2 becomes step 2-2 described below. Step 2-2: A step of applying a colorant-containing ink to a portion to be applied to a dark image forming portion and a portion to be applied to a light image forming portion of the surface of the printing medium obtained in step 1 having a pretreatment liquid application portion, using a line head type inkjet method.

[0080] (Ink containing colorant) The ink containing the colorant according to the present invention (colorant-containing ink) will be described. The colorant-containing ink according to the present invention is preferably one or more inks selected from the group consisting of black inks and chromatic inks.

[0081] [Coloring Agent] The colorant used in the colorant-containing ink according to the present invention may be either a dye or a pigment. Among these, it is preferable to use a pigment as the colorant from the viewpoint of water resistance, light resistance, weather resistance, gas resistance, etc. The pigment may be any of known organic and inorganic pigments. The pigment may be used alone or in combination of two or more kinds, or may be a mixed crystal. Examples of inorganic pigments include titanium oxide, iron oxide, calcium carbonate, barium sulfate, aluminum hydroxide, barium yellow, cadmium red, chrome yellow, and carbon black. Examples of organic pigments include azo pigments, polycyclic pigments, dye chelates, nitro pigments, nitroso pigments, aniline black, etc. Examples of polycyclic pigments include phthalocyanine pigments, perylene pigments, perinone pigments, anthraquinone pigments, quinacridone pigments, dioxazine pigments, indigo pigments, thioindigo pigments, isoindolinone pigments, quinophthalone pigments, etc. Examples of dye chelates include basic dye chelates, acid dye chelates, etc. Specific examples of pigments for black ink include carbons, metals, and organic pigments. Carbons include lamp black (CI Pigment Black 6), furnace black, acetylene black, channel black, and other carbon blacks (CI Pigment Black 7). Metals include copper-chromium oxide (CI Pigment Black 28), iron oxide (CI Pigment Black 11), and titanium oxide (CI Pigment Black 35). Organic pigments include aniline black (CI Pigment Black 1). Specific examples of pigments for chromatic inks include one or more product numbers selected from the group consisting of CI Pigment Yellow, CI Pigment Orange, CI Pigment Red, CI Pigment Violet, CI Pigment Blue, and CI Pigment Green.

[0082] The dye is not particularly limited, and examples thereof include acid dyes, basic dyes, direct dyes, reactive dyes, etc. The dyes may be used alone or in combination of two or more kinds. Examples of the dye include products having product numbers selected from the group consisting of CI Acid Yellow, CI Acid Red, CI Acid Blue, CI Acid Black, CI Food Black, CI Direct Yellow, CI Direct Red, CI Direct Blue, CI Direct Black, CI Reactive Red, and CI Reactive Black.

[0083] When the colorant-containing ink contains a pigment, the pigment is dispersed in a medium in the ink. The form of the pigment in the colorant-containing ink includes a form in which the pigment is dispersed with a resin (hereinafter also referred to as "pigment dispersion resin") or a surfactant as a dispersant, and a form of a self-dispersed pigment dispersed without using a dispersant. Among these, the form of the pigment in the colorant-containing ink is preferably a form in which the pigment is dispersed with a pigment dispersion resin. The pigment dispersing resin may be either a water-soluble resin or a water-insoluble resin. Here, regarding "water-soluble" and "water-insoluble" resins, when a resin that has reached a constant weight after drying at 105°C for 2 hours is dissolved in 100 g of water at 25°C until saturation is reached, if the amount dissolved exceeds 10 g, it is judged to be "water-soluble," and if it is 10 g or less, it is judged to be "water-insoluble." Furthermore, as described below, when the resin has an anionic group, the amount dissolved is the amount dissolved when measured in the presence of a neutralizer under conditions where the mass ratio of the resin to the neutralizer is the same as that in a colorant-containing ink.

[0084] Specific examples of the form of the pigment in the colorant-containing ink, from the viewpoint of improving the dispersion stability of the pigment, include preferably (a) a form in which a water-soluble resin is adsorbed onto the pigment surface, (b) a form in which a water-soluble surfactant or a water-dispersible surfactant is adsorbed onto the pigment surface, (c) a form of a self-dispersing pigment in which a hydrophilic functional group is chemically or physically introduced onto the pigment surface and the pigment is dispersed without using a pigment dispersing resin or a surfactant, and (d) a form in which the pigment is coated with a water-insoluble resin.

[0085] The pigments having the above-mentioned forms (a) to (d) are preferably anionic. In form (a), the water-soluble resin preferably has an anionic group, in form (b), the water-soluble surfactant or water-dispersible surfactant preferably has an anionic group, in form (c), the hydrophilic functional group introduced onto the pigment surface preferably has an anionic group, and in form (d), the water-insoluble resin preferably has an anionic group. The anionic group is as defined in the anionic resin of the hydrophobic compound (A2). Examples of the anionic group include a carboxy group (-COOM), a sulfonic acid group (-SO3M), and a phosphate group (-OPO3M2). In the above chemical formula, M represents a hydrogen atom, an alkali metal, ammonium, or an organic ammonium. Among these, the anionic resin preferably has a carboxy group as the anionic group, and M is preferably an alkali metal.

[0086] Among these, the form of the pigment in the colorant-containing ink is such that, when the component (A) contained in the pretreatment liquid for suppressing wetting and spreading is an aggregating compound (A1), the dispersibility of the dispersoid present in the ink is reduced, thereby efficiently exhibiting the aggregation effect. Also, when the component (A) contained in the pretreatment liquid for suppressing wetting and spreading is a hydrophobic compound (A2), excessive wetting and spreading of the ink can be prevented. This increases the efficiency of preventing wetting and spreading, and improves the clarity of the printed image while suppressing the occurrence of streaks in the resulting printed matter. From this viewpoint, the form is preferably one or more forms selected from the group consisting of form (c) and form (d), and more preferably form (d). When the pigment in the colorant-containing ink is in the form (d), the form in which the pigment is coated with the water-insoluble resin includes a form in which the water-insoluble resin encapsulates the pigment, a form in which the pigment is uniformly dispersed in the water-insoluble resin, a form in which the pigment is exposed from the surface of the water-insoluble resin particles, a form in which the water-insoluble resin is adsorbed to the pigment, and the like. When the pigment in the colorant-containing ink has the form (d), the pigment is preferably coated with a water-insoluble resin having a crosslinked structure. In the case where the pigment is coated with a water-insoluble resin having a crosslinked structure, the water-insoluble resin preferably has a structure containing a polymer component having a linear two-dimensional structure that may have a branched chain and a component derived from a crosslinking agent. It is considered that such a crosslinked structure is a three-dimensional structure of a polymer having a linear two-dimensional structure that may have a branched chain and a component derived from a crosslinking agent.

[0087] [Pigment Dispersion Resin] When the colorant-containing ink is in the form of (d), the type of water-insoluble resin used as the pigment dispersing resin for dispersing the pigment in the colorant-containing ink is not particularly limited. Specific examples of the water-insoluble resin include (meth)acrylic resin, styrene / (meth)acrylic resin, maleic acid resin, styrene / maleic acid resin, urethane resin, and polyester resin. In addition, when the pigment in the colorant-containing ink is in the form of (d) and the pigment is coated with a water-insoluble resin having a crosslinked structure, the constituent component of the polymer having a linear two-dimensional structure that may have a branched chain is preferably one or more selected from the group consisting of (meth)acrylic resin, styrene / (meth)acrylic resin, urethane resin, and polyester resin, from the viewpoint of forming a high-quality printed image, and more preferably one or more selected from the group consisting of (meth)acrylic resin and styrene / (meth)acrylic resin. The water-insoluble resin may be synthesized by a known method, or a commercially available product may be used. The water-insoluble resin may be used alone or in combination of two or more kinds.

[0088] The number average molecular weight of the pigment dispersing resin is preferably 5,000 or more, more preferably 7,000 or more, even more preferably 10,000 or more, and is preferably 100,000 or less, more preferably 50,000 or less, even more preferably 30,000 or less. The number average molecular weight of the pigment dispersing resin is measured by the method described in the examples. When the colorant-containing ink is in the form of (d) in which the pigment is coated with a water-insoluble resin having a crosslinked structure, the number average molecular weight of the constituent component of the polymer having a linear two-dimensional structure which may have a branched chain, which is the water-insoluble resin used to disperse the pigment as a pigment dispersing resin, is preferably 5,000 or more, more preferably 7,000 or more, even more preferably 10,000 or more, and is preferably 100,000 or less, more preferably 50,000 or less, even more preferably 30,000 or less. The acid value of the pigment dispersing resin is preferably 5 mgKOH / g or more, more preferably 50 mgKOH / g or more, even more preferably 70 mgKOH / g or more, still more preferably 90 mgKOH / g or more, and is preferably 800 mgKOH / g or less, more preferably 500 mgKOH / g or less, even more preferably 300 mgKOH / g or less. The acid value of the pigment dispersion resin can be determined by the method described in the Examples, but can also be calculated from the mass ratio of the constituent monomers. When the pigment dispersion resin has a crosslinked structure, the acid value of the pigment dispersion resin can also be calculated from the mass ratio of the constituent monomers and crosslinking agent.

[0089] [Fixing resin] From the viewpoint of forming a high-quality printed image, the colorant-containing ink may contain a resin that functions as a fixing aid (hereinafter, also referred to as a "fixing resin"). The fixing resin in the colorant-containing ink is preferably in the form of a resin that does not coat the pigment, and more preferably in the form of resin particles that do not contain a pigment. The fixing resin is not particularly limited and can be appropriately selected depending on the purpose. Specific examples of the fixing resin include urethane resin, polyester resin, acrylic resin, vinyl acetate resin, styrene resin, butadiene resin, styrene / butadiene resin, vinyl chloride resin, styrene / acrylic resin, and acrylic silicone resin. The ink can be obtained by mixing a particulate fixing resin with a colorant, water, an organic solvent, etc. The fixing resin to be used may be a synthesized product or a commercially available product. The fixing resin may be used alone or in combination of two or more kinds.

[0090] 〔wax〕 The colorant-containing ink may contain wax from the viewpoint of forming a high-quality printed image. In this specification, "wax" refers to an organic substance that is solid or semi-solid at room temperature (25°C) and becomes liquid when heated. Here, "wax is semi-solid" means that the wax deforms and flows when force is applied to it, but can maintain a certain shape when no force is applied to it. In addition, the temperature at which the wax becomes liquid when heated, that is, the melting point of the wax, is in the temperature range of 45°C or higher. The wax may be either a natural wax or a synthetic wax. Examples of natural waxes include petroleum waxes such as paraffin wax and microcrystalline wax; vegetable waxes such as carnauba wax, candelilla wax and rice wax; and animal waxes such as lanolin and beeswax. Examples of synthetic waxes include synthetic hydrocarbon waxes such as polyolefin wax and Fischer-Tropsch wax, silicone waxes, and modified waxes such as paraffin wax derivatives, montan wax derivatives, and microcrystalline wax derivatives. Among these, polyolefin waxes containing an olefin monomer as a main component are preferred. The waxes can be used alone or in combination of two or more.

[0091] The colorant-containing ink preferably contains wax as a dispersion (hereinafter also referred to as a "wax dispersion"). The wax dispersion is not particularly limited, and examples thereof include those obtained by emulsifying wax with a known surfactant, such as a nonionic surfactant or an anionic surfactant. Examples of the nonionic surfactant include ethylene oxide adducts of higher alcohols and ethylene oxide adducts of alkylated phenols. Examples of the anionic surfactant include sulfates and phosphates based on ethylene oxide adducts of higher alcohols; and alkylated benzenesulfonates. Among these, from the viewpoint of improving the ink ejection stability and image fastness of printed matter, etc., the wax dispersion is preferably a nonionic wax dispersion obtained by emulsifying wax with a nonionic surfactant, and more preferably a nonionic polyolefin wax dispersion. Suitable examples of commercially available wax dispersions include the "Hi-Tech E" series manufactured by Toho Chemical Industry Co., Ltd., the "AQUACER" series manufactured by BYK, the "Cellosol" series manufactured by Chukyo Yushi Co., Ltd., and the "Chemipearl" series manufactured by Mitsui Chemicals, Inc.

[0092] 〔water〕 The medium of the colorant-containing ink is preferably an aqueous medium, that is, the colorant-containing ink is preferably an aqueous ink that contains water. Here, "water-based" means that water accounts for the largest proportion by mass of the medium of the colorant-containing ink. The water contained in the colorant-containing ink is preferably ion-exchanged water, ultrafiltered water, reverse osmosis water, or distilled water.

[0093] [Water-soluble organic solvent] The colorant-containing ink may further contain a water-soluble organic solvent as an aqueous medium. Examples of the water-soluble organic solvent contained in the ink include polyhydric alcohols, ethers such as polyhydric alcohol alkyl ethers, polyhydric alcohol aryl ethers, and polyhydric alcohol aralkyl ethers, nitrogen-containing heterocyclic compounds, amides, amines, and sulfur-containing compounds. From the viewpoint of environmental friendliness, the water content in the aqueous medium of the colorant-containing ink is preferably 51% by mass or more, more preferably 55% by mass or more, even more preferably 60% by mass or more, still more preferably 65% ​​by mass or more, and is preferably 95% by mass or less, more preferably 90% by mass or less, even more preferably 85% by mass or less, and still more preferably 80% by mass or less.

[0094] The colorant-containing ink may contain surfactants, antifoaming agents, antiseptic and antifungal agents, rust inhibitors, pH adjusters, and the like, as necessary.

[0095] [Composition of Colorant-Containing Ink] From the viewpoint of improving the image density of printed matter, the content of the colorant in the colorant-containing ink is preferably 2% by mass or more, more preferably 3% by mass or more, and is preferably 20% by mass or less, more preferably 15% by mass or less, and even more preferably 10% by mass or less. When the colorant-containing ink contains a pigment as a colorant, the content of the pigment in the ink is, from the viewpoint of improving the image density of the printed matter, preferably 2% by mass or more, more preferably 3% by mass or more, and preferably 20% by mass or less, more preferably 15% by mass or less, and even more preferably 10% by mass or less. When the colorant-containing ink contains a pigment dispersion resin, the content of the pigment dispersion resin in the ink is preferably 2% by mass or more, and more preferably 4% by mass or more, from the viewpoint of pigment dispersion stability and of forming a high-quality printed image, and is preferably 20% by mass or less, more preferably 15% by mass or less, and even more preferably 10% by mass or less, from the viewpoint of improving the image density of the printed matter. When the colorant-containing ink contains a pigment dispersion resin, the mass ratio of the pigment content to the pigment dispersion resin content in the ink [pigment / pigment dispersion resin] is preferably 0.30 or more, more preferably 0.50 or more, and even more preferably 0.70 or more, from the viewpoint of improving the image density of the printed matter, and is preferably 1.00 or less, more preferably 0.90 or less, and even more preferably 0.80 or less, from the viewpoint of pigment dispersion stability and forming a high-quality printed image. When the colorant-containing ink contains a fixing resin, the content of the fixing resin in the ink is preferably 0.5% by mass or more, more preferably 1% by mass or more, and even more preferably 3% by mass or more, from the viewpoint of forming a high-quality printed image, and is preferably 10% by mass or less, more preferably 7% by mass or less, from the viewpoint of improving the image density of the printed matter. When the colorant-containing ink contains a wax, from the viewpoint of forming a high-quality printed image, the content of the wax in the ink is preferably 0.3% by mass or more, more preferably 0.5% by mass or more, even more preferably 0.8% by mass or more, and is preferably 7% by mass or less, more preferably 5% by mass or less, even more preferably 3% by mass or less. When the colorant-containing ink contains a water-soluble organic solvent, the content of the water-soluble organic solvent in the ink is, from the viewpoint of forming a high-quality printed image, preferably 5% by mass or more, more preferably 10% by mass or more, even more preferably 15% by mass or more, and is preferably 45% by mass or less, more preferably 40% by mass or less, even more preferably 30% by mass or less, and still more preferably 20% by mass or less. From the viewpoint of environmental friendliness, the water content in the colorant-containing ink is preferably 40% by mass or more, more preferably 45% by mass or more, even more preferably 50% by mass or more, still more preferably 60% by mass or more, and is preferably 85% by mass or less, more preferably 80% by mass or less, and even more preferably 75% by mass or less.

[0096] (Line head inkjet method) The inkjet method used in the printing method of the present invention is carried out using a line head type print head. Line head print heads are equipped with a head that can inkjet print over a width equal to or greater than the length perpendicular to the transport direction of the print medium, enabling high-speed printing by scanning only the print medium while keeping the print head fixed. The line head type print head may be a plurality of single heads arranged in a line, and it is preferable that a line head type print head is provided for each color of ink containing colorant.

[0097] From the viewpoint of forming high-quality printed images, the nozzle spacing of a line head type print head is preferably 120 npi or more, more preferably 180 npi or more, even more preferably 300 npi or more, and even more preferably 600 npi or more, and from the same viewpoints as above, it is preferably 6000 npi or less, more preferably 3600 npi or less, even more preferably 2400 npi or less, and even more preferably 1600 npi or less. In the present invention, the unit "npi" indicating the nozzle spacing of a line head type print head means the number of nozzles per inch in the longitudinal direction of the nozzle row of the print head.

[0098] There are various types of print head ejection methods, but in the printing method of the present invention, either a piezo type using a piezoelectric element or a thermal type using a thermal element may be used. Among these, the print head ejection method is preferably a piezo type from the viewpoint of forming a high-quality printed image.

[0099] In the present invention, the transport speed of the printing medium is preferably 10 m / min or more, more preferably 15 m / min or more, and even more preferably 20 m / min or more, from the viewpoint of efficiently obtaining printed matter, and is preferably 100 m / min or less, more preferably 80 m / min or less, and even more preferably 60 m / min or less, from the viewpoint of forming a high-quality printed image.

[0100] In the present invention, from the viewpoint of forming a high-quality printed image, the amount of ejected droplets of the colorant-containing ink is preferably 1 pL or more, more preferably 1.5 pL or more, even more preferably 2 pL or more, and is preferably 15 pL or less, more preferably 10 pL or less, even more preferably 7.5 pL or less, and even more preferably 5 pL or less. Here, "pL (picoliter)" is 10 of "L (liter)". -12 means. The amount of ink droplets ejected containing colorant can be set by an inkjet head control device.

[0101] In the present invention, the resolution in a direction parallel to the transport direction of the printing medium, i.e., the density of ink dots on the printing medium, is preferably 600 dpi or more, more preferably 800 dpi or more, even more preferably 1000 dpi or more, and from the same viewpoints as above, is preferably 3600 dpi or less, more preferably 2400 dpi or less, even more preferably 1800 dpi or less, and even more preferably 1200 dpi or less. In the present invention, the resolution in a direction perpendicular to the transport direction of the printing medium, i.e., the density of ink dots on the printing medium, is preferably 600 dpi or more, more preferably 800 dpi or more, even more preferably 1000 dpi or more, and from the same viewpoints as above, is preferably 3600 dpi or less, more preferably 2400 dpi or less, even more preferably 1800 dpi or less, and even more preferably 1200 dpi or less. In the present invention, the unit of resolution "dpi" means the number of ink dots per inch in a direction parallel or perpendicular to the transport direction of the print medium. When the resolution differs for each ink color, the highest resolution is regarded as the resolution in the present invention.

[0102] In the present invention, the diameter of the ink dots that land on the printing medium (hereinafter simply referred to as "ink dot diameter") is preferably 20 μm or more, more preferably 23 μm or more, and even more preferably 25 μm or more, from the viewpoint of forming a high-quality printed image, and from the same viewpoint as above, it is preferably 60 μm or less, more preferably 55 μm or less, and even more preferably 50 μm or less. As described in the Examples, the diameter of the ink dots that have landed on the printing medium can be determined by observing 10 ink dots under a microscope after applying ink by inkjet printing, and taking the average value as the diameter of the ink dots.

[0103] The amount of the colorant-containing ink applied to the portion that will become the dark image forming portion in step 2 is preferably 1 g / m from the viewpoint of improving the clarity of the printed image while suppressing the occurrence of streaks in the resulting printed matter. 2 More preferably, 3 g / m 2 More preferably, 4.5 g / m 2 From the same viewpoint as above, it is preferably 10 g / m 2 Less than 7g / m 2 More preferably, 5 g / m or less 2 The following is the result.

[0104] <Process 3> In the present invention, from the viewpoint of forming a high-quality printed image by clarifying the contours of the dark image forming parts, it is preferable to further include a step 3 before step 1 or after step 2, in which a white ink containing a white pigment (hereinafter also simply referred to as "white ink") is applied to the printing medium or the surface of the printing medium to which the colorant-containing ink has been applied. When the method further includes step 3, it is preferable to apply a white ink after step 2 to the side of the printing medium opposite to the side to which the colorant-containing ink has been applied (i.e., the printing medium) or to the side of the printing medium to which the colorant-containing ink has been applied. When a resin film is used as the low-liquid-absorbent printing medium, and a mirror image of the desired printed image is formed on the printing medium so that the desired image appears when viewed from the opposite side of the printed image-forming surface of the non-liquid-absorbent film, it is preferable that step 3 be applied to the entire surface of the printing medium on which the colorant-containing ink has been applied.

[0105] Pigments for white ink include white inorganic pigments such as titanium oxide, zinc oxide, zinc sulfide, antimony oxide, and zirconium oxide. From the viewpoint of increasing the whiteness and enhancing the sharpness of cut-out characters, one or more selected from the group consisting of titanium oxide and zinc oxide are preferred, and titanium oxide (CI Pigment White 6) is more preferred. Titanium oxide may be untreated, but from the viewpoint of obtaining good dispersibility, surface-treated titanium oxide is preferred. Surface treatment of titanium oxide may be performed using an inorganic substance, or using an organic substance such as a titanium coupling agent, a silane coupling agent, or silicone oil, and surface treatment using an inorganic substance is preferred.

[0106] In the present invention, the white pigment is dispersed in a medium in the white ink. The form of the white pigment in the white ink may be a form in which the white pigment is dispersed using the above-mentioned pigment dispersion resin or a surfactant as a dispersant, or a form of a self-dispersed pigment dispersed without using a dispersant. Among these, the form of the pigment in the white ink is preferably a form in which the pigment is dispersed using a pigment dispersion resin. The pigment dispersion resin is preferably the same as the resin exemplified in the above-mentioned colorant-containing ink. The white ink may further contain the above-mentioned fixing resin.

[0107] The medium for the white ink is preferably an aqueous medium, that is, the white ink is preferably an aqueous ink that contains water. Here, "water-based" means that water accounts for the largest proportion by mass of the white ink medium. The water contained in the white ink is preferably ion-exchanged water, ultrafiltered water, reverse osmosis water, or distilled water. Furthermore, the white ink may also contain wax, a water-soluble organic solvent, a surfactant, an antifoaming agent, an antiseptic / antifungal agent, an antirust agent, a pH adjuster, and the like, as necessary. The preferred range of the content of each component, such as the white pigment, in the white ink is the same as the preferred range of the content of each component, such as the colorant, in the colorant-containing ink described above.

[0108] Examples of the method for applying the white ink in step 3 include application by roller, application by spray, application by brush, application by inkjet system, etc. Among these, from the viewpoint of applying the white ink simply and uniformly, one selected from the group consisting of application by roller and application by inkjet system is preferred. Specific examples of rollers used for coating with a roller include an offset gravure coater, a gravure coater, a doctor coater, a bar coater, a blade coater, a flexo coater, and a roll coater. Among these, one or more types selected from the group consisting of a doctor coater, a bar coater, and a roll coater are preferred. As a specific example of application by the inkjet method, a line type inkjet method is preferably used. Furthermore, from the viewpoint of being able to perform steps 1, 2, and 3 continuously, the device that applies the white ink to the print medium or the print image forming surface in step 3 is preferably one that is integrated with a means for applying the pretreatment liquid used in step 1 and a means for applying the colorant-containing ink used in step 2. In this case, for example, the inkjet printing device may have a means for applying the white ink, such as a roller coater, built in, or the inkjet printing device may have an inkjet head that applies the white ink built in.

[0109] In order to form a high-quality printed image, the amount of white ink applied to the printing medium in step 3 is preferably 1 g / m 2 More preferably 5 g / m 2 More preferably, 10 g / m 2From the same viewpoint as above, it is preferably 50 g / m 2 Less than 30 g / m 2 More preferably, 15 g / m or less 2 The following is the result.

[0110] When the printing method of the present invention includes step 3, from the viewpoint of forming a high-quality printed image, step 3 preferably includes a step of applying a white ink to a printing medium or a surface of a printing medium to which a colorant-containing ink has been applied, and then holding the printing medium to which the white ink has been applied at 25° C. or higher. This step has the effect of removing volatile components in the white ink from the printing medium or printed matter to which the white ink has been applied, and can dry the printing medium or printed matter (hereinafter, the step of holding the printing medium to which the white ink has been applied at 25° C. or higher in step 3 is also referred to as the "drying step of step 3"). In step 3, methods for maintaining the print medium to which the white ink has been applied at 25° C. or higher include leaving it still, blowing air, heating, reducing pressure, etc. In the printing method of the present invention, application of active energy rays such as ultraviolet rays and radiation is not included in the drying step in step 3 of the present invention. The temperature at which the printing medium is held in the drying step of step 3 is preferably 120°C or lower, more preferably 100°C or lower, even more preferably 90°C or lower, and even more preferably 80°C or lower, from the viewpoint of preventing deformation of the printing medium, and is preferably 25°C or higher, more preferably 30°C or higher, from the viewpoint of drying in a short period of time. The time for which the holding temperature is maintained (holding time) in the drying step of step 3 is preferably 0.5 seconds or more, more preferably 1 second or more, even more preferably 3 seconds or more, still more preferably 5 seconds or more, and preferably 30 minutes or less, more preferably 20 minutes or less, even more preferably 10 minutes or less, and still more preferably 1 minute or less.

[0111] The inkjet printing apparatus of the present invention is an inkjet printing apparatus used in the inkjet printing method of the present invention, and has an inkjet head filled with a pretreatment liquid and an inkjet head filled with an ink containing a colorant. In the inkjet printing apparatus of the present invention, the ink containing a pretreatment liquid and a colorant is the same as the ink containing a pretreatment liquid and a colorant used in the printing method of the present invention described above. In the inkjet printing apparatus of the present invention, the inkjet head filled with the ink containing a colorant may be one inkjet head or multiple inkjet heads. However, from the viewpoint of using ink containing multiple colorants, it is preferable to use multiple inkjet heads. Furthermore, the inkjet printing device of the present invention preferably has an inkjet head filled with a pretreatment liquid, an inkjet head filled with an ink containing a colorant, and an inkjet head filled with a white ink containing a white pigment. That is, the inkjet printing device of the present invention preferably has an inkjet head filled with a pretreatment liquid, an inkjet head filled with an ink containing a colorant, and an inkjet head filled with a white ink containing a white pigment, and it is more preferable that the inkjet printing device of the present invention has an inkjet head filled with a pretreatment liquid, a plurality of inkjet heads filled with ink containing a colorant, and an inkjet head filled with a white ink containing a white pigment. The inkjet printing apparatus of the present invention can be preferably used in the above-mentioned printing method of the present invention or the method of producing a printed matter of the present invention described below.

[0112] The ink set for ink-jet printing of the present invention is an ink set for ink-jet printing used in the ink-jet printing method of the present invention, and includes a pretreatment liquid and an ink containing a colorant. In the ink set for ink-jet printing of the present invention, the ink containing a pretreatment liquid and a colorant has the same meaning as the ink containing a pretreatment liquid and a colorant used in the printing method of the present invention described above. In the ink set for inkjet printing of the present invention, the ink containing a colorant may be one or more, but is preferably more than one. Also, the ink set for inkjet printing of the present invention preferably further comprises a white ink containing a white pigment in addition to the pretreatment liquid and the ink containing a colorant. That is, the ink set for inkjet printing of the present invention preferably comprises a pretreatment liquid, an ink containing a colorant, and a white ink containing a white pigment, and more preferably comprises a pretreatment liquid, an ink containing multiple colorants, and a white ink containing a white pigment. The ink set for ink-jet printing of the present invention can be preferably used in the printing method of the present invention described above or the method for producing a printed matter of the present invention described below.

[0113] [Manufacturing method for printed matter] The printed matter according to the present invention can be obtained by the printing method according to the present invention described above. That is, the method for producing a printed matter of the present invention is a method for producing a printed matter, which includes a dark image forming unit and a light image forming unit, and forms a print image on a printing medium, the print duty of the ink containing the colorant in the dark image forming unit being higher than the print duty of the ink containing the colorant in the light image forming unit, Step 1: applying a pretreatment liquid to an outer edge of a portion that will become a dark image forming portion to obtain a print medium having a pretreatment liquid application portion; and Step 2: A method for producing a printed matter, comprising the steps of: applying an ink containing a colorant to a portion of the surface of the printing medium obtained in step 1 having the pretreatment liquid applied thereto, which is to become a dark image forming portion, using a line head type inkjet method.

[0114] In the method for producing a printed matter of the present invention, steps 1 and 2 are the same as steps 1 and 2 in the printing method of the present invention. Moreover, the method for producing a printed matter of the present invention preferably further includes step 3 of applying a white ink to the printing medium or the surface of the printing medium to which the colorant-containing ink has been applied, before step 1 or after step 2. In the method for producing a printed matter of the present invention, step 3 is synonymous with step 3 in the printing method of the present invention described above. The method for producing a printed matter of the present invention has the above-mentioned characteristics, and therefore the occurrence of streaks in the resulting printed matter is suppressed, while the printed image including dark image formed areas and light image formed areas has excellent clarity.

[0115] The present invention further includes the following aspects. <1> 1. An inkjet printing method including a dark image forming unit and a light image forming unit, the method forming a print image on a print medium, the print duty of ink containing a colorant in the dark image forming unit being higher than the print duty of ink containing a colorant in the light image forming unit, Step 1: applying a pretreatment liquid to an outer edge of a portion that will become a dark image forming portion to obtain a print medium having a pretreatment liquid application portion; and Step 2: applying an ink containing a colorant to a portion of the surface of the printing medium obtained in step 1 having the pretreatment liquid applied thereto, which is to become a dark image forming portion, by a line head type inkjet method. <2> 1. An inkjet printing method including a dark image forming unit and a light image forming unit, the method forming a print image on a print medium, the print duty of ink containing a colorant in the dark image forming unit being higher than the print duty of ink containing a colorant in the light image forming unit, Step 1: applying a pretreatment liquid to an outer edge of a portion that will become a dark image forming portion, and maintaining the print medium to which the pretreatment liquid has been applied at 25° C. or higher to obtain a print medium having a pretreatment liquid application portion; and Step 2: applying an ink containing a colorant to a portion of the surface of the printing medium obtained in step 1 having the pretreatment liquid applied thereto, which is to become a dark image forming portion, by a line head type inkjet method. <3> 1. An inkjet printing method including a dark image forming unit and a light image forming unit, the method forming a print image on a print medium, the print duty of ink containing a colorant in the dark image forming unit being higher than the print duty of ink containing a colorant in the light image forming unit, Step 1: applying a pretreatment liquid to an outer edge of a portion that will become a dark image forming portion, and drying the print medium to which the pretreatment liquid has been applied, to obtain a print medium having a pretreatment liquid applied portion; and Step 2: applying an ink containing a colorant to a portion of the surface of the printing medium obtained in step 1 having the pretreatment liquid applied thereto, which is to become a dark image forming portion, by a line head type inkjet method. <4> 1. An inkjet printing method including a dark image forming unit and a light image forming unit, the method forming a print image on a print medium, the print duty of ink containing a colorant in the dark image forming unit being higher than the print duty of ink containing a colorant in the light image forming unit, Step 1: applying a pretreatment liquid to an outer edge of a region that will become a dark image forming region, thereby fixing the pretreatment liquid application region and obtaining a print medium having a pretreatment liquid application region; and Step 2: applying an ink containing a colorant to a portion of the surface of the printing medium obtained in step 1 having the pretreatment liquid applied thereto, which is to become a dark image forming portion, by a line head type inkjet method. <5> The print medium is a low liquid absorbent print medium. <1> ~ <4> 13. The inkjet printing method according to any one of claims 1 to 12. <6> The non-liquid-absorbent printing medium is a resin film. <5> 2. The inkjet printing method according to claim 1 . <7> The resin film is a polyester film. <6> 2. The inkjet printing method according to claim 1 . <8> The step 1 further comprises a step of maintaining the print medium to which the pretreatment liquid has been applied at 25° C. or higher. <1> and <3> ~ <7> 13. The inkjet printing method according to any one of claims 1 to 12. <9> The method further comprises a step of drying the print medium to which the pretreatment liquid has been applied in the step 1. <1> , <2> and <4> ~ <7> 13. The inkjet printing method according to any one of claims 1 to 12. <10> The method includes a step of fixing the pretreatment liquid application portion in the step 1. <1> ~ <3> and <5> ~ <7> 13. The inkjet printing method according to any one of claims 1 to 12. <11> In step 1, the printing medium to which the pretreatment liquid has been applied is held at a temperature of 40° C. or higher and 100° C. or lower for 1.5 seconds to 1 minute to dry the pretreatment liquid and fix the pretreatment liquid. <1> ~ <10> 13. The inkjet printing method according to any one of claims 1 to 12. <12> The pretreatment liquid contains at least one compound selected from the group consisting of an aggregating compound (A1) and a hydrophobic compound (A2). <1> ~ <11> 13. The inkjet printing method according to any one of claims 1 to 12. <13> The aggregating compound (A1) is at least one selected from the group consisting of metal salts, organic acids or salts thereof, and cationic resins. <12> 2. The inkjet printing method according to claim 1 . <14> The coagulant compound (A1) is calcium nitrate. <13> 2. The inkjet printing method according to claim 1 . <15> The aggregating compound (A1) is malonic acid. <13> 2. The inkjet printing method according to claim 1 . <16> The aggregating compound (A1) is a diallyldimethylammonium chloride polymer. <13> 2. The inkjet printing method according to claim 1 . <17> The hydrophobic compound (A2) is at least one selected from the group consisting of anionic resins and hydrophobic surfactants. <12> 2. The inkjet printing method according to claim 1 . <18> The anionic resin is at least one selected from the group consisting of anionic vinyl resins, anionic urethane resins, and anionic silicone resins. <13> 2. The inkjet printing method according to claim 1 . <19> The hydrophobic compound (A2) is a crosslinked acrylic acid / styrene resin. <12> 2. The inkjet printing method according to claim 1 . <20> the outer edge of the dark image forming section is an area of ​​0.01 mm to 1 mm away from the boundary between the dark image forming section and the light image forming section; <1> ~ <19> 13. The inkjet printing method according to any one of claims 1 to 12. <21> the outer edge portion is an area of ​​0.1 mm to 0.4 mm away from the boundary between the dark image forming portion and the light image forming portion; <20> 2. The inkjet printing method according to claim 1 . <22> In step 1, the pretreatment liquid is further applied to an inner edge portion of a portion that will become a dark image forming portion. <1> ~ <21> 13. The inkjet printing method according to any one of claims 1 to 12. <23> the inner edge of the portion that will become the dark image forming portion is an area that is 0.01 mm to 1 mm away from the boundary between the dark image forming portion and the light image forming portion; <1> ~ <22> 13. The inkjet printing method according to any one of claims 1 to 12. <24> the inner edge portion is an area of ​​0.2 mm to 0.4 mm away from the boundary between the dark image forming portion and the light image forming portion, the area being located on the side away from the light image forming portion; <23> 2. The inkjet printing method according to claim 1 . <25> the difference between the print duty of the ink containing the colorant in the dark image forming portion and the print duty of the ink containing the colorant in the light image forming portion is 50% or more; <1> ~ <24> 13. The inkjet printing method according to any one of claims 1 to 12. <26> the difference between the print duty of the ink containing the colorant in the dark image forming portion and the print duty of the ink containing the colorant in the light image forming portion is 90% or more; <25> 2. The inkjet printing method according to claim 1 . <27> the difference between the print duty of the ink containing the colorant in the dark image forming portion and the print duty of the ink containing the colorant in the light image forming portion is 100%; <25> 2. The inkjet printing method according to claim 1 . <28> the printing duty of the ink containing the colorant of the light image forming portion is 0%; <1> ~ <27> 13. The inkjet printing method according to any one of claims 1 to 12. <29> The printed image is an image of cut-out characters. <1> ~ <28> 13. The inkjet printing method according to any one of claims 1 to 12. <30> The method further includes a step 3 of applying a white ink containing a white pigment to the printing medium or to a surface of the printing medium to which the ink containing a colorant has been applied, before the step 1 or after the step 2. <1> ~ <29> 13. The inkjet printing method according to any one of claims 1 to 12. <31> the printing duty of the ink containing the colorant in the light image forming portion is more than 0%, and the pretreatment liquid in the step 1 is applied not only to the outer edge of the portion that will become the dark image forming portion, but also to a portion of the portion that will become the light image forming portion where the ink containing the colorant is not applied; <1> ~ <30> 13. The inkjet printing method according to any one of claims 1 to 12. <32> The above <1> ~ <31> An inkjet printing apparatus for use in the inkjet printing method according to any one of claims 1 to 5, An inkjet printing apparatus having an inkjet head filled with the pretreatment liquid and an inkjet head filled with ink containing the colorant. <33> The above <1> ~ <32> The ink set for inkjet printing is used in the inkjet printing method according to any one of claims 1 to 5, An ink set for ink-jet printing comprising the pretreatment liquid and an ink containing the colorant. <34> A method for producing a printed matter, comprising: forming a print image on a print medium, the print image including a dark image forming unit and a light image forming unit, the print duty of the dark image forming unit being higher than the print duty of the ink containing the colorant of the light image forming unit, the method comprising: Step 1: applying a pretreatment liquid to an outer edge of a portion that will become a dark image forming portion to obtain a print medium having a pretreatment liquid application portion; and Step 2: A method for producing a printed matter, comprising the step of applying an ink containing a colorant to a portion of the surface of the printing medium obtained in step 1 having the pretreatment liquid applied thereto, which is to become a dark image forming portion, by a line head type inkjet method. EXAMPLES

[0116] In the following Preparation Examples, Production Examples, Examples and Comparative Examples, "parts" and "%" are "parts by mass" and "% by mass" unless otherwise specified. The methods for measuring each physical property are as follows. The physical properties of the resin and the like were measured by the following methods.

[0117] [Measurement of number average molecular weight and weight average molecular weight of resin] The measurement was performed by gel permeation chromatography under the following conditions. GPC equipment: Tosoh Corporation "HLC-8320GPC" Columns: Tosoh Corporation's "TSKgel SuperAWM-H", "TSKgel SuperAW3000", and "TSKgel guardcolum Super AW-H" Eluent: N,N-dimethylformamide with phosphoric acid and lithium bromide dissolved at concentrations of 60mmol / L and 50mmol / L, respectively. Flow rate: 0.5mL / min Standard material: Monodisperse polystyrene kit with known molecular weight [PStQuick B (F-550, F-80, F-10, F-1, A-1000), PStQuick C (F-288, F-40, F-4, A-5000, A-500)] (manufactured by Tosoh Corporation) Measurement sample: 0.1 g of resin was mixed with 10 mL of the eluent in a glass vial, stirred with a magnetic stirrer at 25°C for 10 hours, and filtered with a syringe filter "DISMIC-13HP" (PTFE, 0.2 µm, Advantec Co., Ltd.) to calculate the number average molecular weight or weight average molecular weight of the resin.

[0118] [Measurement of resin acid value] Using an automatic potentiometric titrator (Kyoto Electronics Manufacturing Co., Ltd., electric burette, model number: APB-610), in the case of a resin that does not have a crosslinked structure, the resin was dissolved in a titration solvent made of a mixture of toluene and acetone (2:1), and in the case of a resin that has a crosslinked structure, the resin was dispersed in the titration solvent and titrated with a 0.1N potassium hydroxide / ethanol solution by potentiometric titration, with the inflection point on the titration curve being the end point. The acid value (mgKOH / g) was calculated from the titration amount up to the end point of the potassium hydroxide solution.

[0119] [Measurement of solid concentration] 10.0 g of sodium sulfate, which had been kept constant in a desiccator, was weighed out into a 30 mL polypropylene container (φ=40 mm, height=30 mm), and about 1.0 g of the sample was added and mixed, then accurately weighed, and the mixture was kept at 105°C for 2 hours to remove volatile matter, and then left in the desiccator for 15 minutes, after which the mass was measured. The mass of the sample after removing the volatile matter was taken as the solid content, and divided by the mass of the sample added to obtain the solid content concentration (%).

[0120] [Measurement of the average particle size of resin particles not containing pigment and resin particles containing pigment] Cumulant analysis was performed using a laser particle analysis system "ELS-8000" (manufactured by Otsuka Electronics Co., Ltd.), and the obtained cumulant average particle size was taken as the average particle size of the resin particles that did not contain pigment or the resin particles that contained pigment. The measurement sample had a particle concentration of 5 × 10 -3 A dispersion liquid diluted with water to a mass % (solid content conversion) was used. The measurement conditions were a temperature of 25°C, an angle between the incident light and the detector of 90°, and 100 cumulative measurements. The refractive index of water (1.333) was entered as the refractive index of the dispersion medium.

[0121] [Measurement of static surface tension of organic solvent (B) at 25°C] A platinum plate was immersed in a cylindrical polyethylene container (diameter 3.6 cm × depth 1.2 cm) containing 5 g of sample adjusted to 25°C, and the static surface tension at 25°C was measured by the Wilhelmy method using a surface tensiometer (manufactured by Kyowa Interface Science Co., Ltd., "CBVP-Z").

[0122] Production Example 1 (Production of acrylic acid / styrene resin) A monomer mixture was prepared by mixing 31 parts of acrylic acid and 69 parts of styrene. Into a reaction vessel, 10 parts of methyl ethyl ketone (hereinafter referred to as "MEK"), 0.2 parts of 2-mercaptoethanol as a polymerization chain transfer agent, and 10% of the monomer mixture were placed and mixed, and the inside of the vessel was thoroughly replaced with nitrogen gas. On the other hand, a mixture of the remainder of the monomer mixture (90% of the monomer mixture), 0.13 parts of the polymerization chain transfer agent, 30 parts of MEK, and 1.1 parts of 2,2'-azobis(2,4-dimethylvaleronitrile) ("V-65" manufactured by Fujifilm Wako Pure Chemical Industries, Ltd.) as an azo-based radical polymerization initiator was placed in a dropping funnel, and the monomer mixture in the reaction vessel was heated to 65°C while stirring under a nitrogen atmosphere, and the mixture in the dropping funnel was dropped over 3 hours. After 2 hours at 65°C from the end of the dropping, a solution in which 0.1 parts of the polymerization initiator was dissolved in 2 parts of MEK was added, and the mixture was further aged at 65°C for 2 hours and 70°C for 2 hours, and then dried under reduced pressure to obtain an acrylic acid / styrene resin (number average molecular weight: 19,000, acid value: 240mgKOH / g).

[0123] Production Example 2 (Production of Water Dispersion of Crosslinked Acrylic Acid / Styrene Resin) 15.3 parts of the acrylic acid / styrene resin obtained in Production Example 1 was mixed with 63.5 parts of ion-exchanged water, and 1.8 parts of 25% ammonia water was added to neutralize the resin so that the ratio of the number of moles of ammonia to the number of moles of carboxyl groups in the acrylic acid / styrene resin was 40% (neutralization degree: 40 mol%). The neutralized product was heated to 90°C using a warm bath and stirred for 1 hour to disperse the acrylic acid / styrene resin in water, and then cooled to room temperature (25°C) to obtain a dispersion of the acrylic acid / styrene resin. The obtained dispersion of acrylic acid / styrene resin was added with 4.6 parts of trimethylolpropane polyglycidyl ether (Nagase Chemtex Corporation's "Denacol EX-321LT", epoxy equivalent: 140) as a crosslinking agent, sealed, and heated at 90 ° C for 1.5 hours while stirring with a stirrer. At this time, crosslinking treatment was performed with an amount of crosslinking agent of an epoxy amount that can react with 50% of the total number of carboxyl groups contained in the acrylic acid / styrene resin (crosslinking rate: 50%). Thereafter, the dispersion was cooled to room temperature (25 ° C), filtered with a 25 mL needleless syringe (Terumo Corporation) equipped with a membrane filter (Sartorius Corporation's "Minisart", material: cellulose acetate) with a pore size of 5 μm, and ion-exchanged water was added to adjust the solid concentration to 20%, to obtain an aqueous dispersion of crosslinked acrylic acid / styrene resin (acid value: 120 mg KOH / g).

[0124] Preparation Examples 1 to 8 Each component of the pretreatment liquid was added to a container equipped with a stirrer according to the composition shown in Table 1, mixed at 25°C for 1 hour, and then filtered using the membrane filter with a pore size of 5 μm and the needleless syringe described above to obtain each pretreatment liquid. The components shown in Table 1 are as follows. <Component (A) that suppresses wetting and spreading> [Agglutinating compound (A1)] (cationic resin) Cationic vinyl resin A1-1: "PAS-H-1L" (diallyldimethylammonium chloride polymer) manufactured by Nittobo Medical Co., Ltd. (Metal Salts) Calcium nitrate: Calcium nitrate tetrahydrate (Tokyo Chemical Industry Co., Ltd., Reagent) The amount of calcium nitrate shown in Table 1 is the amount in anhydrous form. (organic acid) Malonic acid: (Reagent manufactured by Fujifilm Wako Pure Chemical Industries, Ltd.) [Hydrophobic compound (A2)] (anionic resin) Anionic vinyl resin A2-1: Water dispersion (solids concentration: 20%) of the crosslinked acrylic acid / styrene resin (acid value: 120 mg KOH / g) obtained in Production Example 2 Anionic vinyl resin A2-2: BASF "Joncryl 7100" (styrene / acrylic acid resin emulsion, acid value: 51 mg KOH / g, effective content: 48%) Anionic urethane resin A2-3: Covestro's "NeoRez R-600" (aliphatic urethane resin aqueous dispersion, acid value: 7 mg KOH / g, effective content: 38%) Anionic silicone resin A2-4: "Chaline Ru-911" manufactured by Nissin Chemical Industry Co., Ltd. (blend type (with urethane), form: water-based emulsion, acid value: 2.2 mg KOH / g, active content: 36%) The amounts of the anionic resins (A2-1 to A2-4) are the amounts as effective components. (Hydrophobic surfactant) Surfynol 420: Surfynol 420 manufactured by Nissin Chemical Industry Co., Ltd. (2,4,7,9-tetramethyl-5-decyne-4,7-diol with an average 1.3 moles of EO adduct, HLB value: 6.4 (calculation formula: 20 x ((34 + 44 x 1.3) / (226 + 44 x 1.3))) <Organic solvent (B)> Diethylene glycol monobutyl ether: (Fujifilm Wako Pure Chemical Corporation, Reagent, Static surface tension at 25°C: 26.2 mN / m) Propylene glycol: (Fujifilm Wako Pure Chemical Co., Ltd., Reagent, static surface tension at 25°C: 36.0 mN / m) (hydrophilic nonionic surfactant) Surfynol 465: Surfynol 465 manufactured by Nissin Chemical Industry Co., Ltd. (2,4,7,9-tetramethyl-5-decyne-4,7-diol with an average of 10 moles of EO adduct, HLB value: 14.2 (calculation formula: 20 x ((34 + 44 x 10) / (226 + 44 x 10))) KF-6011: Shin-Etsu Chemical Co., Ltd. "KF-6011" (PEG-11 methyl ether dimethicone (side-chain polyether modified linear silicone), HLB value: 14.5 (catalog value))

[0125] [Table 1]

[0126] Production Example 3 (Production of Water Dispersion of Crosslinked Resin Particles Containing Black Pigment) 100 parts of the acrylic acid / styrene resin obtained in Production Example 1 was mixed with 78.6 parts of MEK, and 41.2 parts of a 5N aqueous sodium hydroxide solution (sodium hydroxide content: 16.9%) was added as a neutralizing agent to neutralize (neutralization degree: 40 mol%). 800 parts of ion-exchanged water was further added, and 100 parts of black pigment (CB, CI Pigment Black 7, Cabot Chemical's "Monarch 717") was added thereto, and the mixture was stirred for 60 minutes at 20°C using a disperser (Asada Iron Works' "Ultra Disperser") with the disperser blade rotating at 7000 rpm. The mixture was then dispersed 10 times using a Microfluidizer (Microfluidics' product name) at a pressure of 200 MPa. Next, 250 parts of ion-exchanged water was added to the obtained dispersion, and after stirring, MEK was removed under reduced pressure at 60°C, and further a part of the water was removed to adjust the pigment concentration to 10%. 35.7 parts of trimethylolpropane polyglycidyl ether (Nagase Chemtex Corporation's "Denacol EX-321", epoxy equivalent: 140) was added as a crosslinking agent to the dispersion, the mixture was sealed, and the mixture was heated at 70°C for 5 hours while stirring with a stirrer, and then cooled to room temperature (25°C) to obtain an aqueous dispersion of crosslinked resin particles (crosslinking rate: 60 mol%) containing a black pigment (solid concentration: 23.4%, pigment content: 9.7%, acid value: 96 mgKOH / g (calculated value)).

[0127] Production Example 4 (Production of Water Dispersion of Resin Particles Containing No Pigment) In a reaction vessel equipped with a dropping funnel, the monomers shown in "Initial Charge Monomer Solution" in Table 2, sodium polyoxyethylene alkyl ether sulfate (Kao Corporation's "Latemul E-118B") as a surfactant (hereinafter referred to as "Latemul E-118B"), potassium persulfate (FUJIFILM Wako Pure Chemical Industries, Ltd.) as a polymerization initiator, and ion-exchanged water were mixed and replaced with nitrogen gas to obtain an initial charge monomer solution. In addition, the monomers shown in "Dropped Monomer Solution" in Table 2, surfactants, polymerization initiators, and ion-exchanged water were mixed to obtain a dropped monomer solution, which was placed in a dropping funnel and replaced with nitrogen gas. Under a nitrogen atmosphere, the initial monomer solution in the reaction vessel was heated from room temperature (25°C) to 80°C over 30 minutes while stirring, and while maintaining the temperature at 80°C, the monomer in the dropping funnel was gradually dropped into the reaction vessel over 3 hours. After the dropping was completed, the mixture was stirred for 1 hour while maintaining the temperature inside the reaction vessel. It was then filtered through a 200 mesh to obtain an aqueous dispersion of resin particles not containing a pigment (solid concentration: 44.1%, average particle size: 94 nm). The weight average molecular weight of the resin constituting the pigment-free resin particles was 750,000 and the acid value was 16 mgKOH / g. [Table 2]

[0128] Production Example 5 (Production of Black Ink Bk1) 33.0 parts of an aqueous dispersion of crosslinked resin particles containing a black pigment obtained in Production Example 3 (solid content concentration: 23.4%, pigment content: 9.7%), 11.3 parts of an aqueous dispersion of resin particles not containing a pigment obtained in Production Example 4 (solid content concentration: 44.1%), 11.5 parts of propylene glycol (manufactured by FUJIFILM Wako Pure Chemical Industries, Ltd.), 3.5 parts of diethylene glycol monoisobutyl ether (manufactured by FUJIFILM Wako Pure Chemical Industries, Ltd.), polyether-modified silicone surfactant ("Silface SAG005" manufactured by Nissin Chemical Industry Co., Ltd., HLB value: 7 (catalog value), kinetic viscosity: 170 mm 2

[0113] To the mixture obtained, 0.2 parts of a propylene glycol surfactant ("Surfynol 104PG-50" manufactured by Nissin Chemical Industry Co., Ltd., a propylene glycol solution of 2,4,7,9-tetramethyl-5-decyne-4,7-diol, active content: 50%, HLB value: 3.0 (calculation formula: 20 × (34 / 226))) and ion exchanged water were added to make a total amount of 100 parts, and the resulting mixture was filtered using the membrane filter and needleless syringe to obtain black ink Bk1.

[0129] Production Example 6 (Production of Water Dispersion of Resin Particles Containing White Pigment) In a 5L plastic container, 2500g of polyacrylic acid ("Aron A-10SL" manufactured by Toa Gosei Co., Ltd., weight average molecular weight: 6,000, acid value: 735mgKOH / g, solid content concentration: 40%) and 3.57g of ion-exchanged water were added, the container was cooled in an ice bath, and the solution was neutralized by slowly adding 1666.43g of 5N aqueous sodium hydroxide solution while stirring at 100 rpm. Ion-exchanged water was added to the neutralized aqueous solution to adjust the solid content concentration to 20%, and a neutralized aqueous solution of polyacrylic acid was obtained (neutralization degree: 53 mol%, acid value: 735mgKOH / g). Next, 33.0 g of a neutralized aqueous solution of polyacrylic acid (solid concentration: 20%), 300 g of titanium oxide as a white pigment (Ishihara Sangyo Kaisha, Ltd. "Tipake CR-80", CI Pigment White 6, rutile type, Al·Si treatment, average particle size: 250 nm (catalog value)), and 300 g of water were added to a 2 L plastic container (Nikko Hansen J Bottle, round type, wide mouth, natural). 1000 g of zirconia beads were added and dispersed for 8 hours using a tabletop pot mill stand (As One Corporation). The zirconia beads were removed using a metal mesh, and the solid concentration was adjusted with ion-exchanged water to obtain an aqueous dispersion of resin particles containing a white pigment (solid concentration: 51%, pigment content: 50%, polyacrylic acid content: 1%, average particle size 280 nm, pH: 7.6).

[0130] Production Example 7 (Production of White Ink W2) 20.0 g of the aqueous dispersion of resin particles containing the white pigment obtained in Production Example 6 (solid content concentration: 51%), styrene / acrylic acid resin emulsion ("Joncryl" manufactured by BASF) The mixture was filtered using the membrane filter and needleless syringe to obtain a white ink W2. The mixture was then filtered using the membrane filter and needleless syringe to obtain a white ink W3. The mixture was filtered using the membrane filter and needleless syringe to obtain a white ink W4. The mixture was filtered using the membrane filter and needleless syringe to obtain a white ink W5. The mixture was filtered using the membrane filter and needleless syringe to obtain a white ink W6. The mixture was filtered using the membrane filter and needleless syringe to obtain a white ink W7. The mixture was filtered using the membrane filter and needleless syringe to obtain a white ink W8. The mixture was filtered using the membrane filter and needleless syringe to obtain a white ink W9. The mixture was filtered using the membrane filter and needleless syringe to obtain a white ink W1. The mixture was filtered using the membrane filter and needleless syringe to obtain a white ink W2. The mixture was filtered using the membrane filter and needleless syringe to obtain a white ink W1.

[0131] Examples 1 to 12, Comparative Examples 1 to 2 Inkjet printing was performed as described below using the combinations of printing medium, pretreatment liquid, application area of ​​the pretreatment liquid, and whether or not a drying process for the pretreatment liquid on the printing medium was performed, as shown in Table 3, and the following evaluations were performed. (Process 1) In an environment of a temperature of 25±1° C. and a relative humidity of 30±5%, a printing evaluation device (manufactured by Tritec Corporation) equipped with multiple inkjet heads (Kyocera Corporation, “KJ4B-HD06MHG-STDV”, piezoelectric type) was filled with each of the pretreatment liquids shown in Table 3 and the black ink Bk1 obtained in Production Example 5 as a colorant-containing ink. The head voltage was set to 26 V, the frequency to 26 kHz, the head temperature to 32°C, the resolution to 1200 dpi, the number of flushings before ejection to 200, and the negative pressure to -4.0 kPa. The print medium was fixed to the conveying table under reduced pressure so that the longitudinal direction of the print medium was the same as the conveying direction. At this time, the print medium was provided with a non-absorbent film, PET film FE2001 (manufactured by Futamura Chemical Co., Ltd., water absorption: 0 g / m 2 ) or coated paper, OK topcoat paper (Oji Paper Co., Ltd., water absorption: 4.9 g / m 2 ) was used. In Examples 1 to 8 and 10, step 1 was performed using a mirror image of the cut-out characters shown in Figure 4-a so that, when viewed from the opposite side of the printed image forming surface of the non-absorbent film, a printed image of cut-out characters of size 12 was formed, consisting of a light image forming section (i) (printing duty of the colorant-containing ink: 0%) and a dark image forming section (ii) (printing duty of the colorant-containing ink: 100%) as shown in Figure 3. Similarly, in Example 9, a mirror image of the cut-out characters shown in Figure 4-a was used, so the printed image formed in Example 9 is an inverted image of the printed images formed in Examples 1 to 8 and 10. In step 1 of Examples 1 to 10, the pretreatment liquid was applied to the printing medium in a solid form (printing duty of the pretreatment liquid: 100%) with a droplet volume of 1.5 pL to the outer edge portion (iii) of the portion (ii') that will become the dark image forming portion in FIG. 4-a. The outer edge portion (iii) of the portion (ii') that will become the dark image forming portion in FIG. 4-a corresponds to the outer edge portion of the dark image forming portion (ii) in FIG. 3, and belongs to the light image forming portion (i) in FIG. 3. The outer edge portion (iii) of the portion (ii') that will become the dark image forming portion in FIG. 4-a was set to an area within 0.3 mm on the side away from the dark image forming portion, calculated from the boundary between the dark image forming portion and the light image forming portion. The portion (i') that will become the light image forming portion in FIG. 4-a corresponds to the light image forming portion (i) in FIG. 3. In Example 11, the printed image was a cut-out character printed image shown in FIG. 3 formed in Examples 1 to 8 and 10, with a character size of class 8, and the pretreatment liquid was applied to the printing medium in a solid form (printing duty of the pretreatment liquid 100%) with a discharge droplet volume of 1.5 pL to both the outer edge portion (iii) and the inner edge portion (iv) of the portion (ii') that becomes the dark image forming portion in FIG. 4-b. The outer edge portion (iii) of the portion (ii') that becomes the dark image forming portion in FIG. 4-b corresponds to the outer edge portion of the dark image forming portion (ii) in FIG. 3, and belongs to the light image forming portion (i) in FIG. 3. The outer edge portion (iii) of the portion (ii') that becomes the dark image forming portion in FIG. 4-b was set to an area within 0.3 mm on the side away from the dark image forming portion, calculated from the boundary between the dark image forming portion and the light image forming portion. The portion (i') that becomes the light image forming portion in FIG. 4-b corresponds to the light image forming portion (i) in FIG. 3. Moreover, the inner edge portion (iv) of the region (ii') that becomes the dark image forming region in Fig. 4-b corresponds to the inner edge portion of the dark image forming region (ii) in Fig. 3, and belongs to the dark image forming region (ii) in Fig. 3. The inner edge portion (iv) of the region (ii') that becomes the dark image forming region in Fig. 4-b is an area within 0.3 mm on the side away from the light image forming region, counting from the boundary line between the dark image forming region and the light image forming region. Furthermore, in Example 12, the character size of the printed image of the cut-out characters shown in FIG. 3 formed in Examples 1 to 8 and 10 was set to Class 8, the area to which the pretreatment liquid was applied and the amount of ejected droplets were the same as in Examples 1 to 10, and the pretreatment liquid was applied solidly (printing duty of the pretreatment liquid: 100%) to the printing medium. In Comparative Example 1, the pretreatment liquid was applied solidly (printing duty of the pretreatment liquid: 100%) to the entire surface of the printing medium with an ejection droplet volume of 1.5 pL, and in Comparative Example 2, the pretreatment liquid was not applied to the printing medium. After the pretreatment liquid was applied, a drying step was performed in which the temperature of the surface of the print medium to which the pretreatment liquid was applied was kept at 100°C for 1.5 seconds using hot air to dry the pretreatment liquid. At this time, the temperature of the print medium was confirmed with a non-contact thermometer. Note that in Example 10, after the pretreatment liquid was applied, the above-mentioned drying step was not performed, and the print medium was left to stand for 3 seconds in an environment with a temperature of 25±1°C and a relative humidity of 30±5%.

[0132] (Process 2) On the surface of the printing medium obtained in step 1 having the pretreatment liquid application area, black ink was applied to the area (ii'') that would become the dark image formation area using an inkjet head filled with the black ink Bk1 obtained in Manufacturing Example 5 of the device used in step 1, with an ejection droplet volume of 2 pL and a print duty of 100%, so that the area (i'') that would become the light image formation area in Figure 5 would become the area (i') that would become the light image formation area in Figure 4-a or Figure 4-b used in step 1. In Comparative Example 2, black ink was applied to the print medium at a location (ii'') that would become the dark image formation area in FIG. 5, with an ejection droplet volume of 2 pL and a print duty of 100%. 5, a portion (ii'') which becomes a dark image forming portion to which a colorant-containing ink is applied corresponds to the dark image forming portion (ii) in FIG. (Step 3) The white ink W2 obtained in Production Example 7 was filled into a printing device similar to that used in step 1, and the white ink was applied to the entire surface of the printing medium to which the black ink obtained in step 2 had been applied, with an ejection droplet volume of 5 pL and a print duty of 100%. Note that step 3 was not performed in Example 9, and white ink was not applied. Photographs of the printed images of the cut-out characters obtained in Example 1 and Comparative Example 2 are shown in Figures 6 and 7, respectively. Note that Figures 6 and 7 are photographs taken from the opposite side of the non-liquid-absorbent film to the side on which the printed image is formed.

[0133] Example 13 Printing was carried out in the same manner as in Example 1, except that the print image was changed to a barcode. In Example 13, step 1 was performed using an inverted mirror image of the barcode shown in Figure 9 so that a barcode printed image consisting of a light image forming section (i) (printing duty of the colorant-containing ink: 0%) and a dark image forming section (ii) (printing duty of the colorant-containing ink: 100%) shown in Figure 8 was formed when viewed from the opposite side of the printed image forming surface of the non-absorbent film. In process 1, the pretreatment liquid was applied to the print medium in a solid manner (printing duty of the pretreatment liquid: 100%) with an ejection droplet volume of 1.5 pL to the portion shown in the outer edge portion (iii) of the portion (ii') that will become the dark image forming portion in Fig. 9, and in the drying process, the temperature of the surface of the print medium to which the pretreatment liquid was applied was kept at 100°C for 1.5 seconds by using hot air to dry the pretreatment liquid. At this time, the temperature of the print medium was confirmed with a non-contact thermometer. Next, in step 2, using an inkjet head filled with the black ink Bk1 obtained in Manufacturing Example 5 of the device used in step 1, black ink was applied to the surface of the printing medium obtained in step 1 having the pretreatment liquid application portion, with an ejection droplet volume of 2 pL and a printing duty of 100%, to the area (ii'') (not shown) that would become the dark image forming area, so that the area (i'') (not shown) that would become the light image forming area became the area (i') that would become the light image forming area in Figure 9 used in step 1.Furthermore, in step 3, a printing device similar to that used in step 1 was filled with the white ink W2 obtained in Manufacturing Example 7, and white ink was applied to the entire surface of the printing medium to which the black ink obtained in step 2 had been applied, with an ejection droplet volume of 5 pL and a printing duty of 100%. In FIG. 9, the outer edge portion (iii) of the part (ii') which becomes the dark image forming portion corresponds to the outer edge portion of the dark image forming portion (ii) in FIG. 8, and belongs to the light image forming portion (i) in FIG. A photograph of the printed image of the barcode obtained in Example 13 is shown in Fig. 10. Note that Fig. 10 is a photograph taken from the opposite side of the non-liquid-absorbent film to the side on which the printed image is formed.

[0134] <Evaluation of streaks> The black ink portion of the obtained print was observed, and streaks were visually evaluated. (Evaluation Criteria) 4: No streaks, uniform and good. 3: Slight streaks are visible. 2: Streaks are visible, but not to the level that would cause a practical problem. 1: Streaks are clearly observed, and are problematic for practical use. In practical use, a rating of 2 or higher on the above criteria is sufficient.

[0135] <Evaluation of the clarity of printed images (sharpness of cut-out characters and sharpness of barcode edges)> The cut-out characters or barcode portions of the obtained prints were observed, and the clarity of the printed images (sharpness of the cut-out characters and sharpness of the edges of the barcode) was evaluated visually. (Evaluation Criteria) 4: The cut-out characters or barcode can be clearly identified. 3: The cut-out characters or barcode are blurred, but the cut-out characters or barcode can be identified. 2: The cut-out characters or barcodes are blurred and difficult to identify, but the level is not so severe that it is a practical problem. 1: The cut-out characters or barcodes are covered by black ink and cannot be recognized. In practical use, a rating of 2 or higher on the above criteria is sufficient.

[0136] [Table 3]

[0137] From Table 3, it can be seen that the printed matter obtained in the Examples has excellent clarity of the printed image (sharpness of cut-out characters or barcodes) while suppressing the occurrence of streaks, as compared to the Comparative Examples. [Industrial Applicability]

[0138] According to the present invention, even when printing using a line head type inkjet method that uses a low liquid absorbency printing medium, it is possible to obtain a printed matter that has excellent clarity of the printed image, including dark image forming areas and light image forming areas, while suppressing the occurrence of streaks. [Explanation of symbols]

[0139] (i) Light image forming section (ii) Dark image forming section (i') Part that becomes the light image forming part (ii') Part that will become the dark image forming part (iii) The outer edge portion of the portion (ii') which becomes the dark image forming portion (iv) The inner edge portion of the portion (ii') which becomes the dark image forming portion (i'') Part that becomes the light image forming part (ii'') A portion that becomes a dark image forming portion

Claims

1. 1. An inkjet printing method including a dark image forming unit and a light image forming unit, the method forming a print image on a print medium, the print duty of ink containing a colorant in the dark image forming unit being higher than the print duty of ink containing a colorant in the light image forming unit, Step 1: applying a pretreatment liquid to an outer edge of a portion that will become a dark image forming portion to obtain a print medium having a pretreatment liquid application portion; and Step 2: applying an ink containing a colorant to a portion of the surface of the printing medium obtained in step 1 having the pretreatment liquid applied thereto, which is to become a dark image forming portion, by a line head type inkjet method.

2. The inkjet printing method of claim 1 , wherein the print medium is a low liquid absorbency print medium.

3. The inkjet printing method according to claim 1 , further comprising a step of holding the printing medium to which the pretreatment liquid has been applied at a temperature of 25° C. or higher in step 1.

4. The inkjet printing method according to claim 1 or 2, further comprising a step of drying the printing medium to which the pretreatment liquid has been applied in step 1.

5. The inkjet printing method according to claim 1 , further comprising the step of fixing the pretreatment liquid application portion in step 1 .

6. The inkjet printing method according to claim 1 or 2, wherein the pretreatment liquid contains at least one compound selected from the group consisting of an aggregating compound (A1) and a hydrophobic compound (A2).

7. The inkjet printing method according to claim 6, wherein the aggregating compound (A1) is at least one member selected from the group consisting of metal salts, organic acids or salts thereof, and cationic resins.

8. The inkjet printing method according to claim 6, wherein the hydrophobic compound (A2) is at least one selected from the group consisting of anionic resins and hydrophobic surfactants.

9. 3. The inkjet printing method according to claim 1, wherein the outer edge of the portion that becomes the dark image forming portion is an area of ​​0.01 mm to 1 mm away from the boundary line between the dark image forming portion and the light image forming portion.

10. The inkjet printing method according to claim 1 or 2, wherein in step 1, the pretreatment liquid is further applied to an inner edge portion of a portion that will become a dark image forming portion.

11. The inkjet printing method according to claim 10, wherein the inner edge of the portion that becomes the dark image forming portion is an area of ​​0.01 mm to 1 mm away from the boundary line between the dark image forming portion and the light image forming portion.

12. 3. The inkjet printing method according to claim 1, wherein a difference between a print duty of the ink containing the colorant in the dark image forming portion and a print duty of the ink containing the colorant in the light image forming portion is 50% or more.

13. 3. The inkjet printing method according to claim 1, wherein the printing duty of the ink containing the colorant in the light image forming portion is 0%.

14. The inkjet printing method according to claim 1 or 2, wherein the printed image is an image of cut-out characters.

15. 3. The inkjet printing method according to claim 1, further comprising a step 3, before step 1 or after step 2, of applying a white ink containing a white pigment to the printing medium or to a surface of the printing medium to which the ink containing the colorant has been applied.

16. 3. The inkjet printing method according to claim 1, wherein a printing duty of the ink containing the colorant in the light image forming portion exceeds 0%, and the pretreatment liquid in step 1 is applied not only to an outer edge of a portion that will become a dark image forming portion, but also to a portion of the portion that will become a light image forming portion to which the ink containing the colorant is not applied.

17. An inkjet printing apparatus for use in the inkjet printing method according to claim 1 or 2, An inkjet printing apparatus having an inkjet head filled with the pretreatment liquid and an inkjet head filled with ink containing the colorant.

18. An ink set for ink jet printing used in the ink jet printing method according to claim 1 or 2, An ink set for ink-jet printing comprising the pretreatment liquid and an ink containing the colorant.

19. A method for producing a printed matter, comprising: forming a print image on a print medium, the print image including a dark image forming unit and a light image forming unit, the print duty of an ink containing a colorant in the dark image forming unit being higher than the print duty of an ink containing a colorant in the light image forming unit, Step 1: applying a pretreatment liquid to an outer edge of a portion that will become a dark image forming portion to obtain a print medium having a pretreatment liquid application portion; and Step 2: applying an ink containing a colorant to a portion of the surface of the printing medium obtained in step 1 having the pretreatment liquid applied thereto, which is to become a dark image forming portion, by a line head type inkjet method.

Images