Adhesives for digital ink printing laminates

Abstract

A laminating adhesive with improved digital ink lamination properties comprising an isocyanate component and a polyol component. The isocyanate component comprises an isocyanate prepolymer and an aliphatic polyisocyanate. The polyol component comprises an ester-exchanged polyester polyol made from an aromatic polyester polyol and a natural oil, a polypropylene glycol, and a phosphate adhesion promoter. The isocyanate prepolymer in the isocyanate component comprises a reaction product of an isocyanate and a polyalkylene glycol polymer. The laminate structure can be made by coating at least a portion of a substrate with the adhesive and contacting the first substrate with a second substrate.

Description

[Technical field]

[0001] The present disclosure relates to laminating adhesives, and more particularly to a two-component laminating adhesive for digital ink printing laminates comprising an isocyanate component and a polyol component, wherein the isocyanate component comprises a reaction product of a modified isocyanate reacted with a polyalkylene glycol and an aliphatic polyisocyanate, and the polyol component comprises a transesterified polyester polyol made from an aromatic polyester polyol and a natural oil, a polypropylene glycol, and a phosphate adhesion promoter. [Background technology]

[0002] Digital or inkjet printing allows for economical short run print jobs for custom personalized packaging. Non-inkjet printing methods do not allow for economical short run print jobs, making it virtually impossible to produce economical personalized packaging.

[0003] The majority of packaging is created using polyethylene, polypropylene, polyester, polyamide, or cellophane substrates that are laminated together using a variety of adhesives. The lamination adhesives are generally classified as either solvent-based, water-based, or solvent-free.

[0004] Solvent-free lamination adhesives can be applied at high speeds because there is no need to dry water or organic solvents from the adhesive during application, making them preferred in applications that require rapid adhesive application, such as short run inkjet personalized packaging print jobs.

[0005] However, current lamination adhesives are not compatible with digital inks which reduces adhesion performance. Thus, there is an unmet need for lamination adhesives that are compatible with digital inks, thereby enabling inkjet printing. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0006] The present disclosure relates to a two-component solventless adhesive composition comprising an isocyanate component and a polyol component. The isocyanate component may comprise a reaction product of a modified isocyanate reacted with a polyalkylene glycol and an aliphatic polyisocyanate. The polyol component may comprise an ester-exchanged polyester polyol made from an aromatic polyester polyol and a natural oil, a polypropylene glycol, and a phosphate adhesion promoter. A coated film is also disclosed that comprises a substrate and a two-component solventless adhesive composition disposed on at least a portion of a surface of the substrate. The adhesive disposed on at least a portion of a surface on one side of the substrate may comprise an isocyanate component and a polyol component. The isocyanate component may comprise a reaction product of a modified isocyanate reacted with a polyalkylene glycol and an aliphatic polyisocyanate. The polyol component may comprise an ester-exchanged polyester polyol made from an aromatic polyester polyol and a natural oil, a polypropylene glycol, and a phosphate adhesion promoter.

[0007] As mentioned above, the two-component solventless adhesive composition according to the present disclosure includes an isocyanate component and a polyol component.

[0008] Isocyanate component: The isocyanate component includes at least one isocyanate. The at least one isocyanate can be selected from the group consisting of an isocyanate prepolymer, an isocyanate monomer, a polyisocyanate (e.g., a dimer, a trimer, etc.), and a combination of two or more thereof. As used herein, a "polyisocyanate" is any compound that includes two or more isocyanate groups. An isocyanate prepolymer is a reaction product of reactants that include at least one isocyanate and at least one polyol. As used herein, an "isocyanate prepolymer" can be a polyisocyanate itself.

[0009] At least one isocyanate comprises a functionality of 1.5 to 10, or 1.8 to 5, or 2 to 3. When used with respect to the isocyanate component, "functionality" refers to the number of hydroxyl reactive sites per molecule. Compounds having isocyanate groups, such as the isocyanate component, can be characterized by the parameter "NCO%", which is the amount of isocyanate groups by weight based on the weight of the compound. The parameter NCO% is measured by the method of ASTM D 2572-97 (2010). The disclosed isocyanate components have an NCO% of at least 3%, or at least 6%, or at least 10%. Preferably, the isocyanate component has an NCO% of not more than 25%, or 18%, or 14%.

[0010] Further, the at least one isocyanate has a free monomer content of 0-50%, or 5-40%, or 10-30%. Further, the at least one isocyanate has an average molecular weight of 200-6,000 g / mol, or 500-5,000 g / mol, or 1000-4,000 g / mol. Still further, the isocyanate component has a viscosity at 25°C of 300-40,000 mPa·s, or 500-20,000 mPa·s, or 1,000-10,000 mPa·s, as measured by the method of ASTM D2196.

[0011] The isocyanate of the isocyanate component can be an aromatic isomer of methylene diphenyl diisocyanate ("MDI"), such as, but not limited to, 4-4-MDI, 2,2-MDI, 2,4-MDI, and toluene diisocyanate (TDI). As used herein, an aromatic isocyanate is an isocyanate that contains one or more aromatic rings.

[0012] The amount of the at least one isocyanate in the adhesive composition is at least 5% by weight, or at least 10% by weight, or at least 20% by weight, based on the weight of the adhesive composition (i.e., the total weight of the isocyanate component and the polyol component). The amount of the at least one isocyanate in the adhesive composition does not exceed 100% by weight, or does not exceed 75% by weight, or does not exceed 50% by weight, based on the weight of the adhesive composition.

[0013] The isocyanate component may also include a polyalkylene glycol reacted with an isocyanate having an NCO end group. As used herein, the polyalkylene glycol may be, but is not limited to, a polypropylene glycol, a polyethylene glycol, or an ethylene / propylene copolymer glycol. The isocyanate component may also include an aliphatic polyisocyanate. The amount of the aliphatic polyisocyanate is 0.1 to 10 or 0.1 to 5 weight percent based on the weight of the isocyanate component. An aliphatic polyisocyanate, as used herein, is an isocyanate that does not contain an aromatic ring. Examples of aliphatic polyisocyanates disclosed as suitable for use include, but are not limited to, isomers of hexamethylene diisocyanate ("HDI"), propane diisocyanate, butane diisocyanate, pentane diisocyanate, hexane diisocyanate, heptane diisocyanate, octane diisocyanate, nonane diisocyanate, nonane triisocyanate, cycloaliphatic polyisocyanates, or blends thereof.

[0014] Polyol Components: The polyol component may include an aromatic polyester polyol transesterified with a natural oil. The natural oil may be, but is not limited to, castor oil, hydrolyzed epoxidized soybean oil, hydrolyzed epoxidized linseed oil, or mixtures thereof. The transesterified aromatic polyester polyol may have an equivalent weight of 100 to 600 g / mol. Commercially available examples of transesterified aromatic polyester polyols suitable for use according to the present disclosure include, but are not limited to, products sold under the trade name MOR-FREE™ C-156 available from Dow Chemical Company. The polyol component may also include a phosphate adhesion promoter, such as MOR-FREE™ 88-138.

[0015] The content of the transesterified aromatic polyester polyol may be 5 to 50% by weight, or 10 to 40% by weight, or 20 to 35% by weight. The content of the polypropylene glycol may be 40 to 80% by weight, or 50 to 70% by weight, or 55 to 65% by weight. The content of the phosphate ester adhesion promoter may be 0.1 to 20% by weight, or 1 to 15% by weight, or 5 to 10% by weight of the total polyol component.

[0016] The process for making the two-component solventless laminating adhesive composition of the present disclosure can include mixing, admixing, or blending an isocyanate component and a polyol component. The isocyanate component can include a reaction product of a modified isocyanate and a polyalkylene glycol, and an aliphatic polyisocyanate. The polyol component can include an ester-exchanged polyester polyol made from an aromatic polyester polyol and a natural oil, a polypropylene glycol, and a phosphate adhesion promoter.

[0017] The adhesive formulation components may be mixed together by any known mixing process and equipment. The isocyanate and polyol components may be prepared and stored separately from one another as known in the art. The components may be mixed together during or immediately prior to application.

[0018] A method for forming a laminate structure using the two-component solventless adhesive composition of the present disclosure may include the steps of: (1) applying a layer of the adhesive composition to a surface of a first substrate; (2) contacting the layer of adhesive with a surface of a second substrate to form a laminate structure with a laminator; and (3) curing the adhesive composition to bond the surface of the first substrate and the surface of the second substrate together at ambient temperature or, optionally, at an elevated temperature.

[0019] A method for forming a laminate structure is disclosed herein. In the method of the present disclosure, an isocyanate component can be mixed with a polyol component. The isocyanate component can include a reaction product of a modified isocyanate with a polyalkylene glycol polyol or a mixture of two or more polyalkylene glycols, and an aliphatic polyisocyanate. The polyol component can include an ester-exchange polyester polyol made from an aromatic polyester polyol and a natural oil, a polypropylene glycol, and a phosphate adhesion promoter.

[0020] The lamination adhesive thus formed can be applied to at least a portion of a surface of at least one substrate, which can then be contacted with a surface of at least one second substrate to form a laminated structure by a laminator. The adhesive composition can then be cured to bond the substrates together.

[0021] The two-component solventless lamination adhesive composition of the present disclosure can be in a liquid or semi-solid state at 25°C. If in a semi-solid state at 25°C, the solventless lamination adhesive of the present disclosure can be heated until the solventless lamination adhesive is in a liquid state. A layer of the mixed adhesive composition can be applied to a surface of a first substrate, such as a polymeric film. A "film" is any structure having one dimension that is 2 millimeters (mm) or less and two other dimensions that are both 1 centimeter (cm) or more. A "polymeric film" is a film made from a single polymer or a mixture of two or more polymers. In addition, the film can be a metallized polymeric film and foil. The weight ratio of the isocyanate component to the polyol component in the curable adhesive mixture is 1:1.5 to 2:1, and the NCO index is 1.6 to 1.

[0022] A surface of a second substrate or film can be contacted with a layer of the curable adhesive mixture on the first substrate prior to curing of the adhesive to form an uncured laminate. The uncured laminate can be pressed, for example, by passing through nip rollers, which may or may not be heated. The uncured laminate may be heated to accelerate the curing reaction.

[0023] Suitable substrates (e.g., first and second substrates) for use according to the present disclosure include, but are not limited to, films, such as paper, woven and nonwoven fabrics, metal foils, polymeric films, and metal-coated polymeric films. The film optionally has a surface on which an image is printed with ink. The ink may be contacted with the adhesive composition.

[0024] The laminate may be dual substrates bonded together, triple substrates bonded together, or multiple substrates bonded together with an adhesive.

[0025] Generally, the bonding of substrates using the solventless laminating adhesive composition of the present disclosure can be carried out on an industrial scale for the production of large quantities of laminated products. Advantageously, the two components are filled and stored in separate containers, such as drums or hob bocks, until the components are ready to be used. As mentioned above, before the application of the adhesive composition, the two components are stored separately and the two components are mixed with each other only during or immediately before the application of the adhesive. During application, the components are pushed from the storage containers using a feed pump and metered through a feed line into a mixing device such as is commonly used for mixing two-component adhesives in industrial production. For example, the mixing of the two components can be carried out via a static mixer or by a dynamic mixer. When mixing the two components, care is taken to ensure that the two components are mixed as homogeneously as possible. If the two components are not mixed well, there will be local deviations from the favorable mixing ratio, which can have an impact on the deterioration of the mechanical properties of the resulting product made using the adhesive. It may be advantageous if the two components have two different colors to visually check the mixing quality. The mixing is considered good when the mixed adhesive has a homogeneous mixed color without visible streaks or stains. It is preferable to control and maintain the mixing ratio of the two components to achieve the desired target performance of the adhesive.

[0026] The two-component polyurethane adhesives of the present disclosure can be used in all classes of laminates, including, for example, film-film or film-foil composites or film-paper laminates, and the adhesives can be used in packaging applications requiring three performance levels: "general purpose", "medium performance", and "high performance" laminates. Typically, the final packaged product and its filling process will determine the type of adhesive material used in various applications. For example, general purpose laminates include film-film or film-paper composites and are typically used to package dry foods that are stored at room temperature. Medium performance laminates are typically used in packaging fatty or acidic foods, temperature processing up to pasteurization temperatures, and on foils. High performance laminates are typically used in boil-in-bag applications, hot-fill, sterilization processes at elevated temperatures such as up to 140°C, pharmaceuticals, etc. EXAMPLES

[0027] All raw materials and digital ink printing films are listed in Table 1.

[0028] [Table 1]

[0029] Prepolymer 1: The formulation of Prepolymer 1 is shown in Table 2 below. Prepolymer 1 is prepared by first purging a dry 2L 3-neck flask connected to a condenser, overhead mixer, thermocouple temperature controller, and nitrogen bubbler with nitrogen. ISONATE™ 125M and ISONATE™ 143L are then charged into a reactor preheated to 45°C, followed by VORANOL™ 232-034N and VORANOL CP-1055 polyols. Nitrogen is then bubbled continuously through the system for at least 2 minutes, after which the reactor is gradually heated to 78°C. The reactor temperature is maintained at 78°C for 2 hours, after which the reaction is stopped and the product is poured into a glass bottle. Prepolymer 1 has an NCO% of 11% based on total weight.

[0030] [Table 2]

[0031] Coreactant 1: Prepare coreactant 1 by mixing the ingredients in Table 3 using a high speed mixer at 1,800 rpm for 2 minutes.

[0032] [Table 3]

[0033] Prepolymer 2: Prepolymer 2 is prepared by mixing Prepolymer 1 with 2 weight percent C-33 aliphatic polyisocyanate, based on the weight of Prepolymer 1, using a high speed mixer at 1,800 rpm for 2 minutes.

[0034] Prepolymer 3 is prepared by mixing Prepolymer 1 with 5% by weight of C-33 aliphatic polyisocyanate.

[0035] Prepolymer 4 is prepared by mixing Prepolymer 1 with 10% by weight of C-33 aliphatic polyisocyanate.

[0036] Example 1 in the table below is prepared by reacting prepolymer 1 with coreactant 1 at room temperature after mixing, coating, and lamination. Example 2 is prepared by reacting prepolymer 2 with coreactant 1 at room temperature after mixing, coating, and lamination. Example 3 is prepared by reacting prepolymer 3 with coreactant 1 at room temperature after mixing, coating, and lamination. Example 4 is prepared by reacting prepolymer 4 with coreactant 1 at room temperature after mixing, coating, and lamination.

[0037] Comparative Example 1 is MOR-FREE™ L75-164 / C-411 and Comparative Example 2 is PACACEL™ L75-191 / CR88-141. NCO% is determined by titration method according to ASTM D2572-70 at ambient temperature.

[0038] The pot life of the two-component polyurethane adhesives of the present disclosure is determined by measuring the viscosity change with cure time using a DV II Brookfield Viscometer with spindle 27 at a running speed of 20 rpm at 40°C. The pot life of the adhesive is defined as the cure time at which the viscosity reaches twice the mixed viscosity or when the viscosity of the mixed adhesive reaches 4000 MPa·s. The mixed viscosity is defined as the minimum viscosity of the adhesive after mixing and stabilizing at 40°C.

[0039] Table 4 shows the mixed viscosity and pot life (curing time at twice the mixed viscosity) of the adhesives of the present disclosure.

[0040] [Table 4]

[0041] [Table 5]

[0042] As seen in the examples, the four higher levels of aliphatic polyisocyanates result in longer cure times with only slight performance gains. Adhesion performance is evaluated by both hand lamination and pilot laminator testing with digital ink printed BOPP / GF-19 and digital ink printed PET / EVOH-PE. Hand lamination testing is performed on digital ink printed BOPP / GF-19 constructions with a hot oil hand laminator at a speed of 27 in / min, a nip temperature of 150°F, and a nip pressure of 40 psi. Pilot laminator testing is performed on a LABO-COMBI™ 400 laminator available from Nordmeccanica Group with digital ink printed PET / EVOH-PE at 100 ft / min, a nip temperature of 120°F, and a metering roll temperature of 100°F.

[0043] T-peel bond strength is measured after 1, 6, and 14 days of cure on a Thwing-Albert tensile tester with a 200N load cell using 1 inch sample strips and a speed of 10 in / min. Three strips are tested for each laminate and the high and average strengths are recorded along with the failure mode. For film tear, film stretch, and ink transfer (full or partial ink transfer), the average high value is reported, while for the other failure modes (adhesive transfer, adhesive failure, and adhesive separation), the average T-peel bond strength is reported. Typical failure modes include: AF- Adhesive failure (adhesive on primary). AT-Adhesive Transfer (Adhesive on Secondary). AS-Adhesive separation (cohesive failure of adhesive). FT-Film tearing (destruction of bond). IT- Overall ink transfer. PIT-Partial ink transfer.

[0044] [Table 6]

[0045] [Table 7]

[0046] [Table 8]

[0047] After curing for 9 days, the laminate is heat sealed at 320° F., 40 psi pressure, and 1.0 second seal time. Heat seal resistance is determined by pulling 1 inch wide strips at a pull rate of 12 in / min for 1.5 inches. The average of triplicate data is reported below.

[0048] [Table 9]

[0049] The degradation of PAA is tested after 2 and 3 days of curing at 25°C and 50% relative humidity by diazotizing the PAA in the presence of food simulants so that the concentration of PAA can be determined colorimetrically. The aromatic amines present in the test solution are diazotized in a chloride solution and subsequently coupled with N-(1-naphthyl)-ethylenediamine dihydrochloride to give a purple solution. Concentration of the color is carried out using a stationary phase extraction column. The amount of PAA is determined photometrically at a wavelength of 550 nm.

[0050] The laminate is prepared as described above. Pouches are formed by cutting strips approximately 30.5 cm by 16.5 cm wide from the central portion of the laminate. Each strip is folded to form a surface area of ​​14 cm by 16.3 cm, and approximately 1 cm edges are heat sealed along each open longitudinal edge of the folded strip to form pouches with an internal surface area of ​​14 cm by 14.3 cm. The equipment used to heat seal the edges is a Brugger HSG-C. Sealing conditions for the laminate are 1.3-1.5 bar and 130-160°C.

[0051] Four pouches (two blanks and two test pouches) each having an internal surface area of ​​about 14.0 cm x 14.3 cm are used for each exemplary film in this test. Each pouch is formed two days after the time of formation of the respective laminate. The pouches are formed after storing the laminate at room temperature under ambient atmosphere.

[0052] Each pouch is filled with 100 ml of 3% acetic acid in water, used as a food simulant. The pouches are stored at 70°C for 2 hours in an air-circulating oven. After the pouches have cooled to room temperature, 100 ml of the test solution is mixed with 12.5 ml of hydrochloric acid solution (1N) and 2.5 ml of sodium nitrite solution (0.5 g per 100 ml of solution) and the contents are allowed to react for 10 minutes. Ammonium sulfamate (5 ml, 2.5 g per 100 ml of aqueous solution) is added and allowed to react for 10 minutes. A coupling reagent (5 ml, 1 g of N-(1-naphthyl)-ethylenediamine dihydrochloride per 100 g of aqueous solution) is added and allowed to react for 2 hours. After each addition, the resulting mixture is stirred with a glass rod. For the blank pouch, 100 ml of the test solution, excluding sodium nitrite, is mixed with the derivatizing reagent discussed above.

[0053] The solution is concentrated by elution through an ODS solid phase extraction column (ODS reverse phase, C18 endcap) and the absorbance is measured at 550 nm using a Spectrophotometer Lambda (Perkin Elmer).

[0054] Condition the column using first 10 ml of methanol, then 10 ml of elution solvent, then 10 ml of aqueous hydrochloric acid (0.1 N). Add each derivatized sample to the column using a glass beaker that has previously been rinsed twice with 3 ml of aqueous hydrochloric acid (0.1 N). Apply vacuum (approximately 2.5 mm Hg) to the column for 1 minute to remove all rinses. Then add 5 ml of elution solvent to the column and repeat this process until 10 ml of elution solution has been collected.

[0055] To determine the concentration of PAA, the absorbance of the reaction product is measured at 550 nm in a 5 cm cell against a reagent blank solution and a series of standards with known concentrations of aniline hydrochloride run in parallel.

[0056] As can be seen in the table below, the breakdown of PAA is significantly faster in Example 2 than in Comparative Example 1.

[0057] [Table 10]

Claims

1. 1. A two-component solventless adhesive composition comprising: a. at least one isocyanate component comprising an isocyanate prepolymer and an aliphatic polyisocyanate, wherein the isocyanate prepolymer further comprises the reaction product of an isocyanate and a polyalkylene glycol polymer; b. a two-component solventless adhesive composition comprising: castor oil, polypropylene glycol, and at least one polyol component comprising a transesterified polyester polyol made from an aromatic polyester polyol reacted with a phosphate adhesion promoter.

2. A coated film, a. base material, b. a two-component solventless adhesive composition, the two-component solventless adhesive being disposed on at least a portion of a surface of the substrate, the two-component solventless adhesive composition comprising: i. at least one isocyanate component comprising the reaction product of an isocyanate and a polyalkylene glycol and an aliphatic polyisocyanate; ii. A coated film comprising a two-component solventless adhesive composition comprising at least one polyol component comprising a transesterified polyester polyol made from an aromatic polyester polyol and castor oil, polypropylene glycol, and a phosphate adhesion promoter.

3. A laminated structure, a. a first substrate; b. a second substrate; c. a two-component solventless adhesive composition, the two-component solventless adhesive being disposed between the first substrate and the second substrate, the two-component solventless adhesive composition comprising: i. at least one isocyanate component comprising an isocyanate prepolymer and an aliphatic polyisocyanate, wherein the isocyanate prepolymer further comprises the reaction product of an isocyanate and a polyalkylene glycol polymer; ii. A laminate structure comprising a two-component solventless adhesive composition comprising at least one polyol component comprising a transesterified polyester polyol made from an aromatic polyester polyol and castor oil, polypropylene glycol, and a phosphate adhesion promoter.

4. 10. The two-component solventless adhesive composition of claim 1, wherein the amount of the aliphatic polyisocyanate is 0.1 to 5 weight percent based on the weight of the isocyanate component.

5. 3. The coated film of claim 2, wherein the amount of the aliphatic polyisocyanate is 0.1 to 5 weight percent based on the weight of the isocyanate component.

6. 4. The laminate structure of claim 3, wherein the bond strength is greater than 200 g / in.

7. 4. The laminate structure of claim 3, wherein after 3 days of cure, the PAA concentration is less than 0.200 ppb.

8. The laminate structure of claim 3, wherein the heat seal resistance bond strength is from 3,000 to 6,000 g / in.

9. 9. The two-component solventless adhesive composition of claim 1 or 4, the coated film of claim 2 or 5, or the laminate structure of claim 3, 6, 7, or 8, wherein the amount of the phosphate adhesion promoter is 0.1 to 20 weight percent, based on the weight of the at least one polyol component.

10. 1. A method of forming a laminate structure, comprising: a. providing at least one isocyanate component comprising an isocyanate prepolymer and an aliphatic polyisocyanate, wherein the isocyanate prepolymer further comprises the reaction product of an isocyanate and a polyalkylene glycol polymer; b. providing at least one polyol component comprising a transesterified polyester polyol made from an aromatic polyester polyol and castor oil, polypropylene glycol, and a phosphate adhesion promoter; c. combining the at least one isocyanate component and the at least one polyol component to form a solventless adhesive composition; d. applying a layer of the solventless adhesive composition to a surface of a first substrate; e. contacting the layer of adhesive with a surface of a second substrate to form a laminate structure with a laminator; f. curing the adhesive composition to bond the surface of the first substrate and the surface of the second substrate together.