Battery shell with reinforcing nonwoven fabric, manufacturing method, and drive battery

Abstract

The present invention relates to a battery shell having a reinforcing nonwoven fabric made of long cut fibers and a polymer matrix, and to a method for manufacturing such a battery shell.

Description

[Technical field]

[0001] The present invention relates to a battery shell having a reinforcing nonwoven fabric, a manufacturing method, and a traction battery.

[0002] Batteries, in particular traction batteries for storing energy in motor vehicles, consist of a number of components, where a battery casing with at least one battery shell serves, inter alia, to secure and protect the battery modules and other required components.

[0003] Due to the relatively large mass of today's battery casings, flat battery casings, especially battery casings for use in electric vehicles, are required to support the large mass of the battery modules reliably and robustly at relatively high acceleration values.

[0004] Furthermore, there are demands placed on the batteries of electric vehicles that the battery modules should be protected from damage in the event of an accident.

[0005] Various implementations of plastic battery shells are known in the prior art.

[0006] The problem on which the invention is based is to provide an improvement or alternative to the state of the art.

[0007] According to a first aspect of the present invention, the above problems are solved by a battery shell, in particular a battery shell for a traction battery, the battery shell having a bottom and a side wall, the battery shell having an inner surface and an outer surface, the battery shell having a reinforcing nonwoven fabric made of long cut fibers and a polymer matrix.

[0008] In this regard, the following concepts are explained: First, it should be noted that within the framework of this specification, indefinite articles such as "a / one" and "two" and numerical expressions should normally be interpreted as meaning "at least", i.e., "at least one", "at least two", unless it is clear from the context that they may mean "exactly one", "exactly two", etc., or unless it is obvious to a person skilled in the art, or unless it is technically necessary.

[0009] Within the framework of this specification, the expression "in particular" is always to be understood as introducing any preferred features with this expression. This expression should not be interpreted as "and" and "i.e."

[0010] By "traffic battery" is understood an energy store, in particular an energy store for electric current. In particular, the traction battery is suitable for installation in an electric vehicle and also for driving the electric vehicle. In particular, the traction battery is suitable for use in battery electric vehicles and / or vehicles with a battery electric drive and an internal combustion engine.

[0011] By "battery shell" is understood a casing component of a battery, in particular a traction battery.

[0012] In particular, the battery shell is designed to accommodate the components of the battery and accordingly has an accommodation space for accommodating the components, so that these components can be protected from external influences by the battery shell and / or can be at least indirectly fixed within the battery shell.

[0013] In particular, a battery shell is understood to mean a lower battery shell or an upper battery shell, in which case the lower battery shell and the upper battery shell together form, in particular, an essential component of the casing of the traction battery.

[0014] By "reinforcing nonwoven fabric" is understood a structure consisting of finite length fibres arranged in a random orientation and interconnected to form a fibre layer, the reinforcing nonwoven fabric being designed to reinforce components consisting of fibre-reinforced plastic composites, in particular in a crystallised polymer matrix, which can increase the stiffness and puncture resistance of the fibre-reinforced plastic composites.

[0015] By "long cut fibres" it is understood that fibres of finite length have a length of 0.5 mm or more. Fibres having a length of less than 0.5 mm are called short cut fibres.

[0016] By "polymer matrix" is understood the plastic that surrounds the reinforcing nonwoven fabric in a fiber-reinforced plastic composite, the fibers of which are bonded to the polymer matrix by adhesive interactions.

[0017] Here, a battery shell is proposed as a fiber-reinforced plastic composite, in which the fiber parts have a reinforcing nonwoven fabric or consist of a reinforcing nonwoven fabric.

[0018] The use of a reinforcing nonwoven fabric provides a battery shell with high stiffness at a relatively low weight. Furthermore, a particularly good puncture resistance of the battery shell can be achieved by the reinforcing nonwoven fabric.

[0019] In the manufacture of the battery shells proposed here, inter alia, a pressing method is used, which realizes the distribution of the molten molding material to form battery shells with complex geometric shapes, in particular the typical geometric shapes of battery shells. The reinforcing nonwoven fabric proposed here is a shaped product of randomly oriented long-cut fibers, which are bonded to one another in a crystalline and / or molten polymer matrix by adhesion. This realizes that the molten molding material is distributed in the press together with the long-cut fibers contained therein. As soon as the molding material hardens in the press, it bonds with the long-cut fibers, which results in a battery shell with a relatively uniformly distributed reinforcing nonwoven fabric with a relatively uniform fiber volume fraction.

[0020] Advantageously, therefore, a battery shell having relatively uniform material properties can be achieved despite the irregular orientation of the long cut fibers within the reinforcing nonwoven fabric.

[0021] According to a preferred embodiment, the height of the side wall as viewed in the normal direction of the bottom of the battery shell is greater than 50 mm, preferably greater than 80 mm, more preferably greater than 110 mm, and particularly preferably greater than 140 mm.

[0022] Particularly preferably, the battery shell is integrally formed, whereby the battery shell is manufactured as a single component, in one continuous piece and without seams.

[0023] Optionally, the long cut fibres have a length between 0.5mm and 20mm, preferably between 1.0mm and 15mm, preferably between 1.0mm and 10mm.

[0024] It is proposed here, inter alia, that the long-cut fibers have a length between 0.5 mm and 20 mm, the lengths of the individual fibers being distributed either substantially equally or with different lengths, which has been shown in tests to be advantageously particularly uniform material properties with relatively high tensile strengths in the relatively complex component geometries of the battery shell.

[0025] It is expressly noted here that the above values ​​for the length of the long cut fibers should not be construed as strict limits, but rather may be exceeded or exceeded on an engineering scale without departing from the above-mentioned aspects of the invention. In brief, the above values ​​provide a guide to the size of the proposed range of lengths of the long cut fibers.

[0026] Preferably, the battery shell has a fibre volume fraction of 20% or more, preferably 30% or more, particularly preferably 40% or more.

[0027] In this regard, the following concepts are explained: "Fiber volume fraction" is understood to be the ratio of the volume of fibers to the total volume of the fiber reinforcing material.

[0028] The battery shell in particular has a fibre volume fraction of 45% or more, preferably 50% or more, particularly preferably 55% or more.

[0029] Furthermore, the battery shell in particular has a fibre volume fraction of 60% or more, preferably 70% or more, particularly preferably 80% or more.

[0030] Advantageously, the proposed range of fiber volume fraction allows for good distribution of the molding material, which results in particularly uniform material properties for the battery shell and at the same time a relatively high tensile strength.

[0031] It is expressly noted here that the above values ​​for the fiber volume fraction should not be construed as strict limits, but rather may be exceeded or exceeded on an engineering scale without departing from the above-mentioned aspects of the invention. In short, the above values ​​provide an indication of the magnitude of the proposed range of fiber volume fractions.

[0032] According to a preferred embodiment, the polymeric matrix consists of a thermoplastic, in particular polypropylene, PA6 or PA6.6.

[0033] In this regard, the following concepts are explained: By "plastic" is understood a material that consists essentially of polymers.

[0034] In particular, the plastic is a thermoplastic, which can be deformed over a temperature range depending on the material, and the process is reversible and can be repeated any number of times by cooling and reheating to the molten state.

[0035] In particular, thermoplastic is understood to mean polyamide 6 (PA6) or polyamide 6.6 (PA6.6).

[0036] This makes it possible advantageously to achieve a particularly stiff battery shell made of a thermoplastic which exhibits a particularly high elastic modulus and / or a high degree of crystallinity.

[0037] According to a preferred embodiment, the polymer matrix consists of a thermosetting plastic, whereby a particularly hard and rigid battery shell can be achieved.

[0038] Preferably, the long cut fibres comprise glass fibres and / or carbon fibres and / or aramid fibres.

[0039] It is proposed here that the long cut fibres consist of one fibre material or of a mixture of different fibre materials. Since the material properties of glass fibres, carbon fibres and / or aramid fibres are different, the fibre selection and / or fibre composition can be optimally adapted to the individual requirements of the battery shell.

[0040] According to a particularly preferred embodiment, the battery shell has a metal insert for fastening the battery shell, in particular a metal insert with an internal thread.

[0041] In this regard, the following concepts are explained: By "metal insert" is understood a metal body designed as a connecting means for fastening the battery shell.

[0042] In particular, the metal insert has an internal thread and / or a profile on its outer surface, the internal thread being designed in such a way that it can establish a threaded connection under interaction with a corresponding thread, and the profile on the outer surface being designed in such a way that it can create a form-fit with the plastic of the battery shell that surrounds the metal insert, thereby allowing a better transmission of forces between the battery shell and the metal insert.

[0043] Particularly preferably, the metal insert is a helicoil, more particularly formed as a spring screw, which can be inserted into the cavity prior to forming the battery shell and molded in with the molding material during formation of the battery shell.

[0044] Advantageously, the metal insert makes it possible to achieve a robust, load-bearing connection between the battery shell and its surroundings, in particular the body of a specified vehicle and / or adjacent battery shells.

[0045] Particularly preferably, at least one side wall of the battery shell has a varying height.

[0046] In load tests of a battery casing consisting of two battery shells with a reinforcing nonwoven fabric, it was found that the battery casing is particularly robust and resistant to external loads if at least one side wall of the battery shells has a height different from that of the other side wall. According to an advantageous embodiment, the battery casing can be made up of two battery shells, each of which has a side wall with a height different from that of the opposite side wall, so that an angularly offset mating surface is created with respect to the respective bottom of the battery shells.

[0047] It is particularly advantageous for a loaded battery casing if a connecting surface extends between the two battery shells that is slightly offset in angle with respect to the respective bottoms of the battery shells. In particular, the battery shells have, both on their side walls that have different heights relative to the opposite side walls, respectively, connection means with a specified surrounding body shell of a specified vehicle, in particular in the immediate vicinity of the specified connecting surface. This advantageously makes it possible to achieve a particularly advantageous transfer of loads from the battery shell to the specified surrounding body shell and from the specified surrounding body shell to the battery shell, respectively.

[0048] Load introduction by means of connection elements in the vicinity of the joining surfaces of the battery shell, in particular in the vicinity of joining surfaces that are angled relative to the bottom of the battery shell, has proven to be particularly advantageous, whereby a very lightweight battery shell can be achieved.

[0049] In other words, a battery shell is proposed here, which has two side walls with constant but different heights and two side walls with a diagonally extending height level, so that the height level between the two side walls with constant but different heights can be compensated by the side wall with the diagonally extending height level, thereby achieving a battery casing with abutment surfaces that are slightly offset in angle with respect to the respective bottom of the battery shell.

[0050] Vehicles are often asymmetrical with respect to the fastening points used to connect the battery shell proposed here as specified to the vehicle structure. The battery shell proposed here has side walls of different heights. This advantageously allows for an ideal adaptation of the battery shell to vehicles that are asymmetrical with respect to the fastening points. Here, the different heights of the side walls are designed in such a way that the battery shell can be placed on a body that is asymmetrically arranged in the specified vehicle by means of a collar extending on the upper edge of the side walls and can also be fixed to said body, in particular at least indirectly, by means of one or more collars. Advantageously, horizontal forces occurring during operation of the specified vehicle can be ideally introduced into the battery shell proposed here.

[0051] According to a second aspect of the present invention, the above problem is solved by a method for manufacturing a battery shell, in particular a battery shell according to the first aspect of the present invention, the method comprising the following steps: a) forming a battery shell from a preform having a polymer matrix and a reinforcing nonwoven fabric made of long cut fibers using a press molding machine having a cavity, particularly using a shear edge type tool; and b) Taking out the battery shell.

[0052] In this regard, the following concepts are explained: By "preform" is understood a preformed molding material having a polymer matrix and a reinforcing nonwoven fabric surrounded by the polymer matrix, in particular the polymer matrix consisting of a thermoplastic, in particular polypropylene, PA6 or PA6.6.

[0053] Compression molding is a manufacturing method for processing thermoplastic or thermosetting plastics into molded articles using a "press molder" that is specifically configured as a shear edge tool. The molder has a cavity and a core that are designed to form a cavity for forming the article. The cavity can be opened or closed by relative movement between the cavity and the core.

[0054] To produce a product, in particular a battery shell, the molding material, in particular in the form of a preform, is introduced into the cavity of a molding machine. In particular, the molding machine is thermostated. The cavity is then closed using a pressure piston. Due to the pressure, the molding material takes on the shape set by the cavity of the molding machine.

[0055] By "shear edge tool" is understood a press having at least partially circumferentially extending shear edges for guiding the core and / or sealing the cavity, in particular configured as replaceable shear edge strips.

[0056] In particular, shear edge tools, especially variable capacity shear edge tools, can be used to manufacture battery shells in which the flash, if any, is directed toward the molding machine.

[0057] Here, a method is proposed for producing a battery shell, in which a preform is formed into a battery shell in a press. After forming, the polymer matrix crystallizes and, after opening of the press, the hardened battery shell can be removed.

[0058] The preforms used consist of a molding material having a polymer matrix and a reinforcing nonwoven fabric consisting of long cut fibers which are non-uniformly oriented within the molding material.

[0059] During forming using a press molding machine, pressure is transmitted from the press molding machine to the preform, which causes the preform to expand into the cavity of the press molding machine, thus creating a relatively uniform distribution of the non-uniformly oriented long cut fibers in the cavity, and thus the reinforcing nonwoven fabric is also relatively uniformly distributed in the cavity of the press molding machine.

[0060] The cavity according to the proposed manufacturing method has a negative shape for the battery shell, so that the battery shell can be formed. Due to the relatively uniform distribution of the molding material, the finished battery shell also has relatively uniform material properties.

[0061] By reaching the required internal molding pressure, sufficient compression of the molding material can be achieved, thereby supporting a robust structure of the reinforcing nonwoven fabric.

[0062] Advantageously, the proposed manufacturing method makes it possible to manufacture a large number of battery shells as fiber-reinforced plastic components with relatively uniform material properties at high process speeds and therefore at relatively low costs.

[0063] In particular, when using a shear edge tool, it can be advantageously achieved that the metered molding material is not extruded again from the cavity of the molding machine, and in this case, due to the small tolerances of the cavity and the piston, the cavity is simultaneously vented during molding of the molding material, so that complete filling of the cavity with the molding material can be achieved, especially in complex molding machines and long flow paths.

[0064] In particular, the use of a shear edge tool further enables battery shells to be formed in the manner proposed herein that have no or minimal burrs, thereby avoiding or reducing subsequent machining that may be required in some cases.

[0065] Preferably, the moulding material for the preform is provided by mixing a molten polymer, in particular a molten thermoplastic, with long cut fibres, in particular by means of an extruder.

[0066] In this regard, the following concepts are explained: By "molding material" is meant a mixture of long-cut fibers and a polymer matrix, in which the long-cut fibers are already surrounded by the polymer matrix and in which the long-cut fibers are already assembled in a random orientation into the fibrous material and are connected to one another by means of the polymer matrix and by adhesive interactions.

[0067] According to the first variant proposed here, the molding material is obtained by mixing the molten streams of the polymer material and the long-cut fibers with one another in the second extruder, which furthermore already results in a random orientation of the long-cut fibers in the molding material used to form the reinforcing nonwoven in the second extruder.

[0068] Prior to mixing in the second extruder with the first extruder, according to a first variant, the polymer material is melted, optionally homogenized and provided as a molten stream which is mixed together with the long cut fibres in the second extruder to form the moulding material.

[0069] According to the second variant proposed here, the molding material is processed in a single extruder with two sections: in the first section, the polymer material is melted and, if necessary, homogenized, then the long-cut fibers are fed into the melt stream at the beginning of the following second section, where they are carried by the extruder and by the melt stream already present therein, and mixed with the melt stream by the extruder, which homogenizes the molding material.

[0070] Optionally, the preform may be preformed prior to forming the battery shell. - formed by an extruder nozzle; and / or -Brought to press forming machines, especially shear edge type tools.

[0071] Here, according to a first alternative, it is proposed that the preform is formed from the molding material by means of an extruder nozzle, in which case the preform is brought directly into an open press by the extruder nozzle.

[0072] For this purpose, for example, the extruder nozzle is guided by a suitable mechanism, in particular by means of a manipulator, through the open press during the formation of the preform, so that the formed preform is placed in the press simultaneously with its formation.

[0073] According to a second variant, it is proposed that the preform is first formed by means of a fixed extruder nozzle and then transferred to an open press, which can be done, inter alia, manually or by means of a manipulator.

[0074] According to a preferred embodiment, the extruder nozzle is a wide slit nozzle.

[0075] Advantageously, this allows a substantially rectangular preform to be formed, which can be transported to the press by simple means or can be placed in the press using a mobile extruder.

[0076] Preferably the cavity of the press, particularly the shear edge tool, has a variable volume.

[0077] In this regard, the following concepts are explained: When the press, in particular the shear edge tool, has a "variable volume", this is understood to mean that the cavity of the press does not have a defined end position, in particular that the movable half of the press does not have a defined end position relative to the fixed half of the press. In many cases, only one half of the press, in particular the upper half, is supported movably, so that the upper half of the press does not have a defined end position relative to the lower half of the press (lower half). In other words, the material thickness of the battery shell depends on the amount of molding material brought to the press.

[0078] Advantageously, the amount of molding material used in the battery shell can be scaled to a wider tolerance range than in presses that do not have a variable volume, and in this case, it is proposed, among other things, to specify a minimum amount of molding material to be used in achieving a battery shell having at least the required component stiffness.

[0079] Additionally, variable volume presses, particularly shear edge tools, allow for the formation of fine details in the battery shell without the risk of overfilling and / or underfilling the press.

[0080] According to an optional embodiment, an insert is provided in the cavity prior to formation of the battery shell.

[0081] In this regard, the following concepts are explained: By "insert part" is understood a preformed part which is brought into the cavity of the molding machine in addition to the preform and which is formed together with the preform into a product.

[0082] In particular, the insert part is a metal insert which is connected with the molding material by adhesive interaction.

[0083] In particular, the insert is a plastic component which is connected with the molding compound by gluing and / or mixing.

[0084] Particularly preferably, before the formation of the battery shell, a metal insert for fastening the battery shell, in particular a metal insert having an internal thread, is brought into the cavity, in particular the metal insert being operatively connected with a holding device in the cavity.

[0085] A "retention device" is understood to be a device within the cavity designed to secure the metal insert during formation of the battery shell, thereby allowing the metal insert to be positioned in a precise location in the formed battery shell.

[0086] It is proposed here that a battery shell is formed in one cycle together with its connection means, which are in particular designed to allow connection of components and / or other attachments for a specified traction battery to the battery shell inside the battery shell, in particular designed for connecting the battery shell to its surroundings, in particular to a specified vehicle.

[0087] In particular, the metal insert is a helicoil insert, in particular embodied as a spring screw. The metal insert can be inserted into the cavity prior to forming the battery shell, so that the metal insert can be molded with the molding material during formation of the battery shell.

[0088] It is expressly mentioned that the subject matter of the second aspect may be advantageously combined with the subject matter of the above-mentioned aspects of the invention, either individually or cumulatively in any combination.

[0089] According to a third aspect of the present invention, the above problem is solved by a battery shell, in particular a battery shell for a traction battery, the battery shell having a bottom and a side wall, the battery shell having an inner surface and an outer surface, the battery shell being manufactured by a method according to the second aspect of the present invention.

[0090] It will be appreciated that the advantages of the method for manufacturing a battery shell according to the second aspect of the present invention relate directly to the battery shell being manufactured by the method for manufacturing a battery shell according to the second aspect of the present invention, as described above.

[0091] It is expressly mentioned that the subject matter of the third aspect may be advantageously combined with the subject matter of the above-mentioned aspects of the invention, either individually or cumulatively in any combination.

[0092] According to a fourth aspect of the present invention, the above object is achieved by a traction battery, in particular a traction battery for a motor vehicle, having a battery shell according to the first aspect of the present invention or the third aspect of the present invention.

[0093] It will be appreciated that the advantages of the battery shell according to the first aspect of the present invention or the third aspect of the present invention relate directly to a traction battery having a battery shell according to the first aspect of the present invention or the third aspect of the present invention, as described above.

[0094] It is expressly mentioned that the subject matter of the fourth aspect may be advantageously combined with the subject matter of the above-mentioned aspects of the invention, either individually or cumulatively in any combination. Further advantages, details and features of the invention will become apparent from the examples described below. [Brief description of the drawings]

[0095] [Figure 1] 1 shows a schematic representation of a portion of a battery shell. [Diagram 2] 1 shows a schematic diagram of a portion of a battery shell in a portion of a press molding machine, which is typically separated. [Diagram 3] 13A-B are schematic diagrams of a portion of a battery shell in a portion of a shear edge type tool;

[0096] The battery shell 100 in FIG. 1 is integrally molded from a thermoplastic (not shown) that encases a reinforcing nonwoven fabric (not shown).

[0097] The battery shell 100 has a bottom 102, at least one sidewall 104, and a collar 120 extending therearound.

[0098] Furthermore, the battery shell 100 has an inner reinforcing member 140 for reinforcing the battery shell 100, which is also formed integrally with the battery shell 100 and therefore also has a reinforcing nonwoven fabric (not shown).

[0099] The inner reinforcing member 140 has reinforcing ribs 141 on both sides (only one side is visible) which provide additional reinforcement to the battery shell 100, and also has a reinforcing nonwoven fabric (not shown).

[0100] Collar 120 also has a reinforcing nonwoven fabric (not shown) therein.

[0101] The collar 120 of the battery shell 100 further includes at least one metal insert 110 that can be used to secure the battery shell 100 and / or to connect to another battery shell (not shown) to form a battery casing (not shown).

[0102] The bottom 102 of the battery shell 100 also has at least one metal insert 110 that can be used to connect designated components (not shown) in the battery shell 100 .

[0103] 2 illustrates a portion of a battery shell 100 in a portion of a standard segmented, multi-piece press (160). As can be seen, a possible flash 150 of the battery shell 100 extends into the segmented area (not shown) of the standard segmented press (160).

[0104] 3 illustrates a portion of a battery shell 100 in a portion of a multi-piece shear edge tool (170) where a potential burr 150 on the battery shell 100 extends in a direction (not shown) that allows the shear edge tool (170) to be opened and closed. [Explanation of symbols]

[0105] 100 Battery Shells 102 Bottom 104 Side wall 110 Metal Insert 120 Color 140 Inner reinforcement member 141 Reinforcing rib 150 Bali 160 Standard split press molding machine 170 Shear Edge Tool

Claims

1. A method for manufacturing a battery shell (100) having a bottom (102), side walls (104), an inner surface, and an outer surface, the battery shell having a reinforcing nonwoven fabric and a polymer matrix made of long cut fibers having a length of 0.5 mm to 20 mm, comprising: The method comprises the steps of: c) forming the battery shell (100) from a preform comprising a reinforcing nonwoven fabric of the long cut fibers and a polymer matrix using a press (160) having a cavity configured as a shear edge tool (170); and d) removing the battery shell (100).

2. 2. The method of claim 1, wherein the molding material for the preform is provided by mixing a molten polymer with long cut fibers.

3. The preform, prior to the formation of the battery shell (100), formed by an extruder nozzle; and / or The method according to claim 1 or 2, characterized in that the press (160) is configured as a shear edge tool (170).

4. 4. The method of claim 3, wherein the extruder nozzle is a wide slit nozzle.

5. The method according to any one of claims 1 to 4, characterized in that the cavity of the press (160) has a variable volume.

6. 6. The method according to claim 1, characterized in that an insert is brought into the cavity before the formation of the battery shell (100).

7. 7. The method according to claim 1, characterized in that before the formation of the battery shell (100), a metal insert for fixing the battery shell (100) is provided in a cavity.

8. 8. The method according to claim 1, wherein the long cut fibres have a length between 1.0 mm and 15 mm.

9. 9. The method according to any one of the preceding claims, characterized in that the battery shell (100) has a fibre volume fraction of 20% or more.

10. 10. The method according to claim 1, wherein the polymer matrix consists of a thermoplastic.

11. 11. The method according to any one of claims 1 to 10, characterized in that the long cut fibres comprise glass fibres and / or carbon fibres and / or aramid fibres.

12. The method according to any one of the preceding claims, characterized in that the battery shell (100) has a metal insert for fixing the battery shell (100).

13. 13. The method according to any one of claims 1 to 12, characterized in that at least one side wall of the battery shell (100) has a different height.