Implants and methods for forming implants

Abstract

Embodiments herein relate to an implant for insertion into a patient. The implant comprises a plurality of unit cells configured to form a three-dimensional lattice structure, the three-dimensional structure comprising a rest volume of the implant. The plurality of unit cells are configured to form a porous network of the three-dimensional structure, the three-dimensional structure being a reversibly compressible three-dimensional structure, and the bulk porosity of the three-dimensional structure (101) in the implant is at least 50%.

Description

[Technical field]

[0001] CROSS-REFERENCE TO RELATED APPLICATIONS This application claims priority to European Patent Application No. 19195332.2, filed with the European Patent Office on September 4, 2019, the entire contents of which are incorporated herein by reference for all purposes.

[0002] FIELD OF THE DISCLOSURE

[0002] Embodiments disclosed herein relate to the field of implants, and in particular to implants suitable for soft tissue reconstruction that are inserted into a patient, and methods of forming the implants, as well as the use of the implants for tissue reconstruction and / or tissue augmentation. [Background technology]

[0003] Breast augmentation and reconstructive mammaplasty have been performed for decades and are very popular procedures performed worldwide. While overall patient satisfaction is high, common long-term effects include breast tissue atrophy, accelerated ptosis (e.g., sagging), and inframammary fold collapse. There is growing evidence that these events are due to the continuous loads and compressive forces introduced by breast implants. For example, mechanical challenges that exceed the elastic capacity of breast tissue components ultimately lead to irreversible tissue stretching. Conventional silicone implants can be filled with non-compressible liquids and can introduce heavy loads that cause tissue stretching. Also, silicone implants can rupture over time, causing health problems and leading to additional surgery. Some implants include space-occupying structures that can be filled with liquid. For example, Patent Document 1 and Non-Patent Document 1 disclose implants that have a three-dimensional scaffold structure with voids, all of which are filled with a space-occupying structure. The space-occupying structure is removably attached to the three-dimensional scaffold structure and configured to prevent tissue infiltration and / or individual cell infiltration. After implantation (e.g., 6 to 8 weeks after implantation), the space-occupying structures are removed from the implant remnants and from the implantation site in a second surgery. [Prior art documents] [Patent documents]

[0004] [Patent Document 1] International Publication No. 2016 / 038083 [Non-patent literature]

[0005] [Non-Patent Document 1] Chhaya et al. Transformation of Breast Reconstruction via Additive Biomanufacturing. Sci. Rep. 6, 28030; doi: 10.1038 / srep28030 (2016) Summary of the Invention

[0006] Various embodiments relate to providing a lightweight implant that reduces the effects of ptosis in a patient and reduces adverse reactions by the patient to the implant.

[0007] Embodiments disclosed herein relate to an implant for insertion into a patient, the implant comprising a plurality of unit cells configured to form a three-dimensional lattice structure, the three-dimensional structure comprising a rest volume of the implant, the plurality of unit cells configured to form a porous network of the three-dimensional structure, the three-dimensional structure being a reversibly compressible three-dimensional structure, and the bulk porosity of the three-dimensional structure (101) in the implant is at least 50%.

[0008] Various embodiments further relate to an implant for insertion into a patient, the implant comprising a porous three-dimensional scaffold structure including an array of unit cells, the plurality of unit cells configured to form a porous network of a three-dimensional structure, the plurality of unit cells in the three-dimensional structure having an average pore size of at least 0.5 mm.

[0009] Various embodiments further relate to an implant for insertion into a patient, the implant comprising a three-dimensional porous scaffold structure including a plurality of hollow channels extending between a first outer surface region and a second outer surface region of the three-dimensional porous scaffold structure, the porous scaffold structure comprising a surface degradable polymeric material, the first outer surface region configured to face the chest wall of a patient receiving the implant, the shape of the second outer surface region representing the shape of a breast to be constructed by the implant, and the plurality of hollow channels configured to align with Cooper's ligaments of the patient receiving the implant.

[0010] Various embodiments relate to a method of forming an implant, the method comprising sequentially printing layers to form a three-dimensional (3D) printed structure that defines a rest volume of the implant to be formed, each printed layer comprising a lattice array of two-dimensional unit cells, the three-dimensional printed structure having a porosity such that the three-dimensional printed structure is compressible to at least 80% of its rest volume.

[0011] Finally, the present invention also relates to a method of tissue reconstruction or augmentation, comprising the step of implanting into the body of a subject an implant as disclosed herein.

[0012] The foregoing and other features of the present disclosure will be fully apparent from the following description and the appended claims, taken in conjunction with the accompanying drawings. It is understood that the accompanying drawings only illustrate some embodiments according to the present disclosure, and therefore should not be considered as limiting its scope. In order that the advantages of the present disclosure may be more readily ascertained, the present disclosure will be described with further specificity and detail using the accompanying drawings. [Brief description of the drawings]

[0013] [Figure 1A] FIG. 1 shows an implant with space-occupying structures as described in International Patent Application WO 2005 / 023366. [Figure 1B] FIG. 1 illustrates an implant of the present invention for insertion into a patient. [Figure 1C]FIG. 1 illustrates a reversibly compressible spring-like unit cell and a reversibly compressible implant of the present invention. [Figure 1D] FIG. 1 illustrates a reversibly compressible spring-like unit cell and a reversibly compressible implant of the present invention. [Figure 2A] FIG. 2 is a perspective side view of an implant for insertion into a patient. [Figure 2B] FIG. 1 is a cross-sectional side view of the implant showing the upper and lower pole pieces of the implant. [Figure 2C] FIG. 2 is a top view (plan view) of a first exterior surface region of the implant. [Figure 2D] FIG. 1 is a top view of two sublayers that may be intersected to form a unit cell. [Figure 2E] FIG. 2 is a cross-sectional longitudinal side view of the implant. [Figure 2F] FIG. 13 is a perspective side view of a lower pole portion of a second exterior surface region of the implant. [Figure 2G] FIG. 2 is a perspective top view (plan view) of a second exterior surface region of the implant. [Figure 3A] FIG. 1 is a perspective side view of an implant having multiple surface fillers. [Figure 3B] 1A-1D are perspective side and top views of an implant with surface-filling posts. [Figure 4A] FIG. 2 is a perspective longitudinal side view of the implant. [Figure 4B] FIG. 2 is a perspective top view of the implant. [Diagram 5] FIG. 1 is a perspective top view of an implant of the present invention. [Figure 6A] FIG. 1 is a graph showing the c-value, which represents the flexibility of the implant. [Figure 6B] FIG. 1 illustrates forces acting on an implant. [Figure 6C] (i)-(iii) indicate implant compressibility and overestimation of implant volume. [Figure 6D] (i)-(iii) show the effect of skin tension on the shape of the implant after insertion into the patient. [Figure 6E]FIG. 1 is a perspective view of an implant disclosed herein having the form of a hip implant. [Figure 7A] FIG. 1 shows the implant after insertion into a patient. [Figure 7B] 1 shows the anatomy of a patient's breast as constructed by the implants. [Figure 7C] 1 shows a depiction of the forces acting on the breast. [Figure 7D] 1 shows histological photographs of regenerated breast tissue. [Figure 7E] FIG. 13 illustrates the force of Cooper's ligament acting on one filament of the implant. [Figure 7F] FIG. 1 illustrates internal forces acting on breast tissue. [Figure 8] 1 shows a flow chart of a method for forming an implant. [Figure 9A] FIG. 1 shows a schematic bottom view of the implant used in the animal studies described herein, with the dimensions of the implant shown. [Figure 9B] FIG. 1 shows a schematic side view of the implant used in the animal studies described herein, also showing the dimensions of the implant. [Figure 9C] 9A and 9B depict magnetic resonance imaging (MRI) images of minipigs in treatment group 3 as described herein, with the implants depicted in FIG. 9C being inserted. The MRI image in FIG. 9C was taken two weeks after the insertion of the implants. [Figure 9D] FIG. 9C shows an MRI image of the same minipig, taken 4 weeks after implantation. [Figure 10A] FIG. 4 is a reproduction of the histological image of FIG. 4 of Non-Patent Document 1 showing areas of chronic inflammation characterized by lymphatic structures following implantation of an implant / scaffold in a miniature pig as described in Chhaya et al. and Patent Document 1. [Figure 10B]4 of Non-Patent Document 1 showing tissue components infiltrated into the pores of the implant of the present invention used in the animal study described herein. FIG 10B shows that there was no sign of chronic inflammation after implantation of the implant / scaffold of the present invention in minipigs as described herein. [Figure 11A] 1 shows a schematic diagram of a soft tissue reconstruction implant for reconstruction of a breast or breast area of ​​a patient's body. [Figure 11B] 1 shows a schematic diagram of a soft tissue reconstruction implant for reconstruction of a breast or breast area of ​​a patient's body. [Figure 11C] 1 shows a schematic diagram of a soft tissue reconstruction implant for reconstruction of a breast or breast area of ​​a patient's body. [Figure 11D] 1 shows a schematic diagram of a soft tissue reconstruction implant for reconstruction of a breast or breast area of ​​a patient's body. [Figure 11E] 1 shows a schematic diagram of a soft tissue reconstruction implant for reconstruction of a breast or breast area of ​​a patient's body. [Figure 12A] 1 shows a schematic diagram of a soft tissue reconstruction implant for reconstruction of the buccal area (or cheek) of a patient's body. [Figure 12B] 1 shows a schematic diagram of a soft tissue reconstruction implant for reconstruction of the buccal area (or cheek) of a patient's body. [Figure 12C] 1 shows a schematic diagram of a soft tissue reconstruction implant for reconstruction of the buccal area (or cheek) of a patient's body. [Figure 13A] 1 shows a schematic diagram of a soft tissue reconstruction implant for the reconstruction of the testicular region of a patient's body. [Figure 13B] 1 shows a schematic diagram of a soft tissue reconstruction implant for the reconstruction of the testicular region of a patient's body. [Figure 14A] 1B-10B show the implant in more detail. [Figure 14B] 1B-10B show the implant in more detail. [Figure 14C] 1B-10B show the implant in more detail. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0014] In the following detailed description, reference is made to the accompanying drawings, which show by way of example specific embodiments in which the claimed subject matter may be practiced. These embodiments are described in sufficient detail to enable one skilled in the art to practice the subject matter. It is understood that the various embodiments, although different, are not necessarily mutually exclusive. For example, a particular feature, structure, or characteristic described in this specification in connection with one embodiment can be implemented in other embodiments without departing from the spirit and scope of the claimed subject matter. References within this specification to "one embodiment" or "an embodiment" mean that the particular feature, structure, or characteristic described in connection with the embodiment is included in at least one embodiment encompassed herein. Thus, use of the phrases "one embodiment" or "in an embodiment" does not necessarily refer to the same embodiment. It is also understood that the location or arrangement of individual elements in each embodiment can be modified without departing from the spirit and scope of the claimed subject matter. The following detailed description is therefore not to be taken in a limiting sense, and the scope of the subject matter is defined only by the appended claims appropriately interpreted, along with the full range of equivalents to which the appended claims are entitled. In the drawings, like numerals refer to the same or similar elements or functions throughout the several views, and elements depicted herein do not necessarily correspond to one another, rather individual elements may be scaled to more easily understand the elements in the context of this specification.

[0015] As used herein, the terms "over," "to," "between," and "on" may refer to the relative location of a layer with respect to another layer. A layer that is "over" or "on" another layer may be in direct contact with the other layer or may have one or more intervening layers. A layer between layers may be in direct contact with the layer or may have one or more intervening layers.

[0016] FIG. 1B shows a diagram of an implant 100 of the present invention for insertion into a patient.

[0017] The implant 100 comprises a plurality of unit cells 102 configured to form a three-dimensional lattice structure 101. The three-dimensional structure 101 comprises a quiescent volume of the implant 100. The plurality of unit cells 102 are configured to form a porous network of the three-dimensional structure 101, where the three-dimensional structure 101 is a reversibly compressible three-dimensional structure 101.

[0018] The three-dimensional lattice structure 101 can be a mesh-like structure. For example, the implant 100 can include a plurality of lines configured to form a mesh-like structure. Each unit cell 102 in the plurality of unit cells 102 can include and / or can be formed from (e.g., forming walls surrounding the individual unit cells) intersections (or, e.g., crosses) of the plurality of lines that form and / or define the individual unit cells 102. The plurality of lines can form and / or provide an overall mesh-like three-dimensional lattice structure 101. The intersections can be arranged such that each unit cell 102 formed from the intersections includes pores having a pore size, or is referred to as a pore size. Thus, the plurality of intersections can form or define a plurality of pores in the unit cells 102. For example, the intersections can form or define the shape (e.g., shape, size, pore size) of the individual unit cells 102 (e.g., each unit cell 102) in the three-dimensional structure 101. The plurality of unit cells 102 can be configured to form a porous network of the three-dimensional structure 101. The porous network may refer to (and / or include) the pores of a plurality of unit cells 102 within the three-dimensional structure 101 .

[0019] A unit cell 102 can be the smallest and most basic unit of the three-dimensional lattice structure 101. Intersections of the multiple lines can be configured to form repeating unit cells 102 that form the three-dimensional lattice structure 101. For example, the unit cells 102 can be repeated throughout at least (equal to or greater than) 80% (or, e.g., at least 90%, or at least 95%) of the quiescent volume of the three-dimensional lattice structure 101. Thus, the lattice structure 101 can include multiple adjacent (e.g., directly adjacent) unit cells that are connected to each other throughout the lattice structure 101.

[0020] Implant 101 static volume (cm 3) may be the volume of the implant 101 prior to inserting the implant 101 into a patient. The rest volume of the implant 101 may be the volume of the implant 101 when only one outer surface of the implant 101 is subjected to an external force. For example, when the implant 101 is resting on (or in contact with) a carrier surface (e.g. a desk surface, or e.g. a board). For example, a first outer surface of the implant may be in contact with the carrier surface, and a second (opposite facing) outer surface may not be subjected to a compressive force. That is, the rest volume of the implant 101 may be the volume of the implant 101 without an opposing compressive force acting on the surface of the implant. When one or more outer surfaces of the implant 101 are subjected to a compressive force (physical or mechanical), the implant 101 may be compressible to at least 80% (or such as at least 70%, or such as at least 60%, or such as at least 50%, or such as at least 30%, or such as at least 20%, or such as at least 10%) of its rest volume. Compressible to at least 80% refers to the implant being able to reach 80% or less of its rest volume (due to compression forces). The rest volume of the implant 101 can be calculated based on, for example, the build volume (desired or required volume) of the breast to be built by the implant 101. The implant 101 can be configured to be compressible to at least the build volume such that the implant comprises or reaches the build volume of the breast after insertion into the patient.

[0021] Each unit cell 102 in the plurality of unit cells 102 may be a spring-like unit cell. A spring-like unit cell may be compressible to at least 80% (or, e.g., at least 70%, or, e.g., at least 60%, or, e.g., at least 50%, or, e.g., at least 30%, or, e.g., at least 20%, or, e.g., at least 10%) of its original volume. As used herein, compressible to at least 80% refers to compressible to 80% or less of its original volume. A spring-like unit cell may be reversibly compressible. By being reversibly compressible, each unit cell 102 may recover or return to its original (rest) volume after the release of a compressive force (even at the same ambient pressure and temperature). A reversibly compressible spring-like unit cell may be configured to return to at least 80% (or, e.g., at least 90%, or, e.g., at least 95%, or, e.g., at least 98%, or, e.g., up to 100%) of its original volume after the release of a compressive force acting on the implant 100. As used herein, returning to at least 80% refers to being able to return to 80% or more of its original volume.

[0022] 1C and 1D show diagrams of a reversibly compressible implant 100 with a reversibly compressible spring-like unit cell 102. FIG.

[0023] The three-dimensional structure 101 can be a reversibly compressible three-dimensional structure comprising a plurality of reversibly compressible unit cells 102. The spring-like implant 100 can provide shape stability. The spring-like implant 100 can deform when a force 103 is applied to the implant, and the implant 100 can return to its shape when or after the force is released. The ability of the implant 100 to return to its shape can avoid void closure and / or any extra force acting on the thoracic cavity that can damage the patient's tissue and / or lungs. The implant 100 can be a soft tissue reconstruction implant (e.g., an implant for and / or suitable for soft tissue reconstruction).

[0024] As shown in FIG. 1C , the reversibly compressible structure and reversibly compressible unit cells 102 of the implant 100 can transmit a force acting along one direction (e.g., an opposing compressive force 103 along the z-axis) to a different direction, such as a vertical direction 104 (e.g., along the x-direction).

[0025] 1D, when the compressive force 103 is released (indicated by the change in the direction of the arrow at 103), the energy stored during this process acts in the opposite direction (indicated by the change in the direction of the arrow at 104) to that when the compressive force 103 was applied, causing the implant 100 to spring back in shape, helping it to return to its original shape (e.g., at least 80% of its original volume).

[0026] Each spring-like unit cell 102 can be reversibly compressible in at least one Cartesian direction and / or in three Cartesian directions. Although Figures 1C and 1D show the unit cells 102 as compressible in the z-direction, it is understood that the spring-like unit cells 102 can be reversibly compressible in three Cartesian directions and / or in any direction in three-dimensional space.

[0027] 2A-2G show different views of an implant 200 of the present invention being inserted into a patient. The implant 200 can include one or more or all of the features of the implant 100 described in connection with FIGS. 1B-1D, as well as various other features.

[0028] FIG. 2A shows a perspective side view of an implant 200. The three-dimensional structure 101 of the implant 200 can include an array of layers 126. The array of layers 126 can include (or can be) multiple outer layers 126 (e.g., parallel to the xy plane) arranged successively with respect to one another in the z direction (e.g., vertical direction). For example, the implant 200 can be formed by successively printing layers 126 to form a three-dimensional (3D) printed scaffold structure 101. Arrow 117 indicates the printing direction (e.g., in the z direction) of the successive array of successive layers 126. Each outer layer 126 of the array of layers 126 can include a two-dimensional lattice array of multiple two-dimensional unit cells 102. The successive array of layers 126 (by printing) overlapping one another can lead to the formation of a three-dimensional structure 101 with edges (or peripheries) of the multiple layers 126 defining the shape and / or configuration of the second outer surface region 106.

[0029] The three-dimensional structure 101 of the implant 200 can include a first outer surface region 105 and a second (different and / or opposite facing) outer surface region 106. Outer surface region can be understood to refer to (or can be) the outermost surface, layer, and / or contour of the implant 200. The outermost surface and contour can be formed from one or more layers or lines. Outer surface region can refer to (or can be) the outermost layers of the implant 200 (e.g., a single outermost layer, or, e.g., multiple outermost layers). Outer surface region can refer to the outwardly facing surface of the implant 100.

[0030] The first outer surface region 105 of the implant 200 can include or have a first surface curvature. The first outer surface region 105 of the implant 200 can be the largest plane (or, for example, the flattest) of the implant. For example, the first outer surface region 105 can be the flattest surface of the implant and / or the surface having the least amount of curvature. As shown in FIG. 2C, the first outer surface region 105 of the implant 200 can be a plane parallel to a two-dimensional (xy) Cartesian plane. Alternatively, or optionally, the best fit plane of the first outer surface region 105 can be a plane parallel to a two-dimensional (xy) Cartesian plane.

[0031] The second outer surface region 106 of the implant 200 can include or have a second surface curvature that is different from the first surface curvature. The second surface curvature can be greater than the first surface curvature. The second outer surface region 106 of the implant 200 can be adjacent (e.g., abutting) the first outer surface region 105 of the implant 200 at a periphery 107 (e.g., perimeter) of the first outer surface region 105. For example, the second outer surface region 106 of the implant 200 can abut the first outer surface region 105 and the periphery 107 of the first outer surface region 105 can be a shared edge (or boundary) between the first outer surface region 105 and the second outer surface region 106.

[0032] The second outer surface region 106 can be shaped (e.g., shape, curvature, size) to represent the shape of the patient's breast to be constructed with the implant 200. For example, the second outer surface region 106 can include an upper pole portion 109 and a lower pole portion 111. The upper pole portion 109 can have the shape of the upper portion of the breast to be constructed with the implant 200. The upper portion of the breast can be the area of ​​the breast from the patient's nipple area upward toward the patient's head. The lower pole portion 111 can have the shape of the lower portion of the breast to be constructed with the implant 200. The lower portion of the breast can be the area of ​​the breast from the patient's nipple area downward toward the patient's feet. The upper pole portion 109 and the lower pole portion 111 can meet (or coincide) at an apex region 112 of the second outer surface region 106. The location (or position) of the apex region 112 on the second outer surface region 106 of the implant can be based on (and / or correspond to) the location (or position) of the nipple / areola of the breast to be constructed with the implant 200.

[0033] 2B shows a cross-sectional side view of implant 200. The view shows upper pole piece 109 and lower pole piece 111 of implant 200.

[0034] In the cross-sectional side view, the first outer surface region 105 can be considered as a straight line extending along (e.g., parallel to) a Cartesian x-axis (e.g., from -x to +x). The first outer surface region 105 can have a slope equal to 0, for example. In general, the (surface) curvature of the upper pole portion 109 and the (surface) curvature of the lower pole portion 111 of the second outer surface region 106 can be greater than the (surface) curvature of the first outer surface region 108, respectively. Alternatively, the curvature of the upper pole portion 109 of the second outer surface region 106 can be less than or equal to the Da curvature of the first outer surface region. The contour and shape of the upper pole portion 109 and the lower pole portion 111 of the second outer surface region 106 can be adjusted based on the desired size and shape of the implant 200.

[0035] The curvature and / or contour of the upper pole piece 109 and the lower pole piece 111 may be based on adjusting at least one of the protrusion, height, and width (symbolized by a square) of each of a plurality of sections of the second exterior surface region 106. The plurality of sections may be defined based on a plurality of points (e.g., p1-p7) in the second exterior surface region 106. Each section may lie between two points in the second exterior surface region 106. The distance between the points and the number of points may also be selectively adjusted.

[0036] The Cartesian z-axis may be located (e.g. directly) at the apex region 112 of the second outer surface region 105 (e.g. at x=0). The upper pole piece 109 of the second outer surface region 106 may be in the -x region and the lower pole piece 111 of the second outer surface region 106 may be in the +x region. In general, the sections of the upper pole piece 109 may have a positive slope with respect to the x-axis and the z-axis. A point p4 (e.g. the center point of the apex region 112) defining the apex region 112 may be located at x=0. The sections of the upper pole piece 109 closer to the apex region 112 (e.g. near point 4) may have a smaller slope, e.g. close to 0. For example, the sections p3-p4 may have a smaller slope than the sections p2-p3, and the sections p2-p3 may have a smaller slope than the sections p1-p2. In general, the sections of the lower pole piece 111 may have a negative slope with respect to the x-axis and the z-axis. A section of the bottom pole portion 111 closer to the apex region 112 (e.g., near point 4) can have a smaller slope, such as a slope closer to zero. For example, sections p4-p5 can have a smaller slope than sections p5-p6. Depending on the desired shape or geometry of the implant 200, a small section of the bottom pole portion 111 can have a positive slope (e.g., the small section between sections p6-p7). In this manner, the curvature of the bottom pole portion 111 of the second outer surface region 106 can appear to be greater than the curvature of the top pole portion 109 of the second outer surface region 106.

[0037] FIG. 2C shows a top view (plan view) of the first exterior surface region 105 of the implant 200.

[0038] In a top view, the first exterior surface region 105 can have a circular or elliptical shape. The first exterior surface region 105 can include (or can refer to) a first layer 126 of an array of layers. As shown in FIG. 2C, each outer layer 126 can include an array of two-dimensional unit cells 102. The two-dimensional unit cells 102 can be rhomboid (or diamond-shaped, or rhombus-shaped) unit cells.

[0039] FIG. 2D shows a top view of two sublayers 136A, 136B that may be intersected to form a unit cell.

[0040] Each outer layer 126 of the unit cell can include a first sublayer 136A (or a first group of sublayers) that includes lines 128 oriented in a first direction, and a second sublayer 136B (or a second group of sublayers) that includes lines 129 oriented in a second direction different from the first direction. The lines of each sublayer can be part of a continuous sublayer line that meanders continuously from a start point S of the sublayer to an end point E of the sublayer. For example, the line 128 of the first sublayer 136A can be part of a continuous sublayer line 138 that meanders continuously from a start point S of the sublayer 136A to an end point E of the sublayer. For example, the line 129 of the second sublayer 136B can be part of a continuous sublayer line 139 that meanders continuously from a start point S of the sublayer 136B to an end point E of the sublayer 136B. The intersecting lines that form the unit cell can be straight lines, or alternatively, the intersecting lines can be sinusoidal lines and the unit cell can have a "freeform" shape. The lines 128, 129 in each sublayer 136A, 136B may be parallel to one another (e.g., the acute angle between the lines in the sublayer or the lines best fit to a sine line may be within + / - 5°). The lines 128 of the first sublayer and the lines 129 of the second sublayer may intersect at crossing points or regions to form a two-dimensional lattice array of two-dimensional unit cells of the outer layer 126. The two-dimensional unit cells 102 of each layer 126 of the stacked layer array may form a three-dimensional lattice structure 101.

[0041] As shown in FIG. 2C, each unit cell 102 of the outer layer 126 can include or be formed of intersecting lines 128, 129 from adjacent sublayers 136A, 136B that define the pore size of the unit cell 102. For example, two adjacent (and parallel) lines 128 of a first sublayer 136A can intersect with two adjacent (and parallel) lines 129 of a second (adjacent) sublayer. The area of ​​the unit cell enclosed by the intersecting lines can have a rhomboid (or diamond, or rhombus) shape. In some embodiments, the minimum angle j between two intersecting lines of a unit cell can be between 5° and 90° (or, for example, between 10° and 80°, or, for example, between 30° and 60°).

[0042] Each two-dimensional unit cell 102 can have a pore diameter that defines a dimension of the unit cell 102. The pore diameter w of a unit cell 102 of a layer can be the smallest dimension (or width) of the pore, such as the smallest distance of the pore measured between two lines (e.g., oppositely facing lines) that define the unit cell 102.

[0043] The three-dimensional structure 101 of the implant 200 may be composed of a plurality of unit cells 102 with a range of different pore sizes. As shown in FIG. 2C, the first layer 126 may be the outermost layer in the first outer surface region 105. The pore size of the unit cells 102 may therefore be the surface pore size of the surface pores (openings) in the first outer surface region. The (minimal or smallest) surface pore size w of the plurality of unit cells in (or of) the first outer surface region 105 of the implant 200 may be at least (e.g. equal to or greater than) 2 mm (or e.g. at least 6 mm, or e.g. at least 8 mm). The surface pore size of at least 80% (or e.g. at least 70%, or e.g. at least 80%) of the unit cells 102 in (or of) the first outer surface region 105 may be at least 2 mm (or e.g. at least 0.75 mm, or e.g. at least 1 mm).

[0044] The size (e.g., surface pore size) of the openings at the surface of the implant 200 may vary depending on their location on the implant 200. The (average) surface pore size of the openings at (or in) the first exterior surface region 105 of the three-dimensional structure may be at least (e.g., equal to or greater than) 10% (or e.g., at least 25%, or e.g., at least 30%, or e.g., at least 35%) larger than the (average) surface pore size of the openings at the second exterior surface region 106 of the three-dimensional structure 101. Additionally or optionally, the (average) surface pore size at the first exterior surface region 105 may be larger than the (average) surface pore size at the lower pole portion 111 of the second exterior surface region 106 and may be larger than the (average) surface pore size at the upper pole portion (109).

[0045] Although a rhomboid (or diamond-shaped) unit cell 102 is shown in FIG. 2C, it is understood that, optionally, the plurality of two-dimensional unit cells 102 can be polygonal unit cells. For example, the plurality of two-dimensional unit cells can be triangular unit cells, diamond-shaped unit cells, rhomboid unit cells, rectangular unit cells, parallelogram unit cells, and / or hexagonal unit cells. It is understood that the implant 200 can include one or more types of unit cells throughout the volume of the implant 200, such as a mixture of unit cells. In an embodiment, the implant 200 can include primarily diamond-shaped unit cells (e.g., greater than 50%, or greater than, e.g., greater than 60%, or greater than, e.g., greater than 70%, or greater than, e.g., 80% of the unit cells can be diamond-shaped unit cells). Alternatively, instead of two-dimensional unit cells, the unit cells 102 in the plurality of unit cells 102 can include (or can be) three-dimensional unit cells having multiple planar facets. Each planar facet of the three-dimensional unit cell can define a pore and / or pore size of the three-dimensional unit cell 102. Generally speaking, each three-dimensional unit cell 102 can include at least four pores. For example, a tetrahedral three-dimensional unit cell can include at least four openings (or pores) formed by the four triangular faces of the tetrahedral unit cell. For example, a hexagonal three-dimensional unit cell can include six openings (pores) in each of the six facets of the hexagonal unit cell.

[0046] The average thickness of the plurality of lines may be 0.1 mm to 5 mm (or such as 0.1 mm to 2 mm, or such as 0.5 mm to 1.5 mm). Thus, each sublayer 136A having lines oriented in a first direction may be separated from an adjacent (or consecutive) sublayer 136A having lines oriented in the (same) first direction by a sublayer 136B having lines oriented in a second (different) direction. Thus, each sublayer 136A oriented in a first direction may be separated from an adjacent (or consecutive) sublayer 136A oriented in the (same) first direction by a separation distance of 0.1 mm to 5 mm (or such as 0.1 mm to 2 mm, or such as 0.5 mm to 1.5 mm). Similarly, each sub-layer 136B oriented in a second direction may be separated from an adjacent (or consecutive) sub-layer 136B oriented in the (same) second direction by a distance of 0.1 mm to 5 mm (or such as 0.1 mm to 2 mm, or such as 0.5 mm to 1.5 mm). This may result in an arrangement of loosely spaced layers and sub-layers, allowing free movement of individual wires relative to each other (e.g., by compression, stretching, translation).

[0047] 2E shows a longitudinal cross-section (side view) of the first exterior surface region 105 of the implant 200. This cross-sectional side view illustrates that the individual layers in the arrangement of layers can be configured such that the (two-dimensional) unit cells of successive layers form a plurality of hollow channels 118 extending between the first exterior surface region 105 and the second exterior surface region 106 of the three-dimensional structure 101. This cross-sectional side view illustrates the plurality of hollow channels 118 formed by the arrangement of the two-dimensional unit cells of successive layers within the implant 200.

[0048] One or more grooves 118 of the plurality of hollow grooves can be configured to extend from the first outer surface region 105 toward the apex region 112 of the second outer surface region 106 and / or the lower pole portion 111 of the second outer surface region 106. Additionally or alternatively, one or more further grooves 118 of the plurality of hollow grooves can be configured to extend from the upper pole portion 109 of the second outer surface region 106 toward the apex region 112 and / or the lower pole portion 111 of the second outer surface region 106. Optionally, the plurality of hollow grooves can be parallel to one another (e.g., an acute angle between sidewalls of adjacent grooves can be within + / - 5°). Alternatively, the plurality of hollow grooves can converge toward a convergent region (or point) located outside the first outer surface region 105 or the second outer surface region 106 of the three-dimensional structure. For example, the convergent point can be located on the apex region 112 of the implant 200.

[0049] The plurality of hollow grooves 118 may be inclined with respect to the first outer surface region 105 of the implant 200. The acute inclination angle k between the sidewall of the hollow groove 118 and a reference axis (e.g., x-axis) describing the first outer surface region may be less than 90°, or for example less than 60°. The reference axis may be based on a best fit plane or line of the first outer surface region 105. The plurality of hollow grooves 118 may consist of 5-1000 hollow grooves (or for example 5-60 grooves, or for example 8-20 grooves). Each inclined groove may be formed from (or may include) a column of unit cells from successive layers 126 deposited on top of each other. In the unit cells forming the column of unit cells, the unit cells of the second layer may have an outer offset (in the x-direction) with respect to the adjacent unit cells of the first layer.

[0050] The sidewalls of the column of unit cells can be formed from a plurality of outer lines (which lie substantially parallel to the xy plane) vertically stacked and oriented in the same direction in the z direction, the lines forming the sidewalls being the lines forming the individual unit cells of the column of unit cells. For example, a column of diamond-shaped unit cells can be formed by vertical stacking of diamond-shaped unit cells, the lines or walls surrounding (and defining) the individual unit cells of layer 126 can be aligned with the lines or walls surrounding (and defining) the successive unit cells of successive layers. Thus, the walls of each unit cell in the column of unit cells can form at least a portion of the sidewalls of the column of unit cells. The individual unit cells in the column of unit cells can be aligned such that the unit cells of each successive layer have an outer offset with respect to the unit cells of the (directly) previous layer within the same column. The outer offset value between the first and second unit cells can be 0%-50% (or such as 0%-20%, or such as 5%-10%) of the pore size of the unit cells. Optionally, within the same pillar, the unit cells of each layer can have the same outer offset relative to the unit cells of the directly preceding layer. Optionally, at least (e.g., equal to or greater than) 80% (or, e.g., at least 70%, or, e.g., at least 50%) of the unit cells in the same pillar (forming the same groove) can have the same pore size and the same pore shape. Alternatively, in the case of tapered grooves, the unit cells forming the same groove can have different pore sizes (e.g., the pore size of the unit cells can decrease or increase toward one point of the outer surface region). Surface porosity and different surface pore sizes are shown in Figures 2F and 2G.

[0051] FIG. 2F shows a perspective side view of the lower pole piece 111 of the second exterior surface region.

[0052] As shown in Figures 2F and 2A, the surface pore size w at the lower pole portion 111 of the second outer surface region 106 can increase (gradually, or e.g., stepwise, or e.g., layer by layer) from the lower pole boundary region 115 towards the apex region 112 of the second outer surface region 106. The lower pole boundary region 115 can be a boundary (or edge) region of the three-dimensional structure 101 where the lower pole portion 111 of the second outer surface region 106 meets a portion of the periphery 107 of the first outer surface region 105. The surface pore size w at the lower pole portion 111 of the second outer surface region 106 can increase, for example, from 0.15 mm or 2 mm at the lower pole boundary region 115 towards the apex region 112 of the second outer surface region 106 up to 6 mm, or up to 8 mm, or up to 9 mm, or up to 10 mm. The direction of increase is indicated by arrow 116. Optionally, the surface pore size can be increased from 3 mm to 7 mm (or such as from 3 mm to 6 mm, or such as from 4 mm to 8 mm, as in the implants used in the experimental examples of this application).

[0053] FIG. 2G shows a perspective top view of the second exterior surface region 106 of the implant 200.

[0054] As shown in FIG. 2G, the apex region 112 can be between (or at the boundary of) the top pole piece 109 and the bottom pole piece 111. Additionally or optionally, the (average) surface pore size in the first outer surface region 105 can be larger than the (average) surface pore size in the top pole piece 109, as shown in FIG. 2G (and FIG. 2A). The surface pore size in the top pole piece 109 of the second outer surface region 106 can increase (gradually, or e.g. in steps, or e.g. layer by layer) from the top pole boundary region 114 of the second outer surface region 106 towards the apex region 112. The direction of increase is indicated by arrow 113. The top pole boundary region 114 can be a boundary (or edge) region of the three-dimensional structure 101 where the top pole piece 109 of the second outer surface region 106 meets a portion of the perimeter 107 of the first outer surface region 105. For example, the surface pore size at the upper pole portion 109 of the second exterior region 106 may increase from 0.5 mm at the upper pole boundary region 114 of the second exterior region 106 to a maximum of 5 mm at the apex region 112. Optionally, the surface pore size may increase from 0.5 mm to 4 mm (or e.g. 0.5 mm to 2 mm, or e.g. 0.8 mm to 2 mm, or e.g. 1 mm to 2 mm). The surface pore size at the upper pole portion 109 may be achieved (or may be relied upon) by increasing the spacing between the contour lines (shown in FIGS. 4A and 4B) located at the upper pole portion 109 of the second exterior region 106.

[0055] The average surface pore diameter w of the surface pores at (or in) the apical region may be in the range 2mm to 6mm (or such as from 2mm to 4mm, or such as from 2mm to 3mm).

[0056] Generally speaking, the surface pore size of at least 50% (or, for example, at least 70%, or, for example, at least 80%) of the three-dimensional structure 101 may be at least 0.5 mm (or, for example, at least 0.75 mm, or, for example, at least 1 mm). The average surface pore size of the three-dimensional structure 101 may be at least 0.5 mm (or, for example, at least 0.75 mm, or, for example, at least 1 mm). The average surface pore size may be calculated by adding the pore sizes of the total number of openings at the outermost surface of the three-dimensional structure 101 and dividing by the total number of openings at the outermost surface of the three-dimensional structure. The surface pore area of ​​at least 50% (or, for example, at least 70%, or, for example, at least 80%) of the surface pores in the three-dimensional structure 101 may be at least 0.75 mm. 2 (or e.g. at least 1 mm 2 , or for example at least 3 mm 2 The area of ​​a surface pore may be the area enclosed by the intersecting lines that define the surface pore.

[0057] Optionally, the pore sizes of the unit cells 102 within a layer can vary from one another. For example, in the case of tapered or converging grooves, the unit cells within a layer can have the same shape but different pore sizes. Thus, the pore sizes of the unit cells at different locations of the implant 200 can be different from one another. For example, the pore sizes of the unit cells 102 within the bulk of the implant 200 (bulk pore sizes) can vary from one another depending on the location of the unit cells 102 within the implant 200.

[0058] 3A shows a perspective side three-dimensional view of an implant 200 having a plurality of surface fillers 122. This view shows a side view of a lower pole portion 111 of the implant 200. The implant 200 can include one or more or all of the features described in connection with FIGS. 1B-2G as well as various other features.

[0059] The surface infills 122 can fill openings (surface pores) in the outermost surface of the three-dimensional structure 101. Each surface infill 122 can include one or more fill lines 124 configured to at least partially fill one or more openings (surface pores) in the outermost surface of the three-dimensional structure 101. The one or more fill lines 124 of the surface infill 122 can be configured to connect (or at least partially fill the spaces between) a group of intersecting lines that define surface pores 123 in the outer surface region of the three-dimensional structure. A surface pore that is at least partially filled can be a surface pore where the fill lines fill 50%-99% (or such as 55%-95%, or such as 80%-95%) of the surface area of ​​the pore. For example, a larger percentage of the surface area of ​​pore 123A is filled than pore 123B, but both pores 123A and 123B can be considered to be at least partially filled. Optionally, at least 20% (or e.g. at least 30%, or e.g. at least 40%) of the surface pores in the exterior surface region of the three-dimensional structure 101 may be at least partially filled with surface infills 122. Optionally, surface infills 122 may be formed (or disposed) in the second exterior surface region, while the first exterior surface region may be free of surface infills 122 (e.g. all surface pores in the first exterior surface region may be open).

[0060] 3B shows a perspective side and top view of implant 200 with surface-filling posts 125. This view illustrates the surface porosity of implant 200.

[0061] Optionally, the ratio of filled (closed surface porosity) to unfilled (open surface porosity) in the second outer surface region can be 1:2. In this way, the surface porosity of the implant 200 can be defined prior to insertion into a patient. The surface porosity can represent (or can be) the void ratio or percentage (e.g., a measurement of open space) of the outermost surface of the three-dimensional structure 101. The surface porosity of the implant 200 can be expressed as the total voids (m 2) by the total surface area (m 2 ) The surface porosity of the second outer surface region can be less than the bulk porosity of the three-dimensional structure of the implant. The surface porosity of the second outer surface region can be less than the surface porosity of the first outer surface region (e.g. 0.8 times, or such as 0.5 times, or such as 0.2 times, or such as 0.1 times). For example, the surface porosity of the second outer surface of the implant 200 can be between 30% and 80% (or such as 40% and 70%, or such as 50% and 60%, or such as 54% and 66%). The bulk porosity of the three-dimensional structure 101 of the implant 200 can be at least 80% (or such as at least 20%, or such as at least 50%, or such as at least 60%, or such as at least 70%, or such as at least 85%, or such as at least 90%). Optionally, the bulk porosity of the implant can be between 80% and 99%. Bulk porosity may represent (or may be) the void ratio or percentage (e.g., a measurement of open space) of the implant 200 prior to insertion into a patient. The bulk porosity of the implant 200 is the total void space (m 3 ) to the total volume (m 3 ) can be defined as

[0062] The compressibility of the three-dimensional structure 101 in the implant can be based on (or, for example, proportional to) the bulk porosity and / or total void space of the implant. For example, the three-dimensional structure 101 can have a minimum compressed volume V based on (or, for example, proportional to) the void space of the implant. C For example, the third dimension can be compressed to V C =V T -V V can be compressed to V C is the volume of the compressed implant, and V V is the volume of the void, and V T is the total rest volume of the scaffold, i.e., the implant can be compressed by a volume based on (proportional to or equal to) the volume of the void.

[0063] A spring-like implant can be configured to return to at least 80% (e.g., 80% or more) (or e.g., at least 90%, or e.g., at least 95%, or e.g., at least 98%, or e.g., up to 100%) of its original volume after a compressive force acting on the implant is removed.

[0064] The amount of restitution of a spring-like implant can be based on the amount of compression acting on the implant. For example, the implant can be compressed in at least one compressive direction to 30% or less. After the force is removed, the scaffold 101 can return (spring back) to 80% or more. Alternatively, the implant can be compressed to 80% or less. After the force is removed, the scaffold 101 can return to 85% or more or 90% or more of its initial projection.

[0065] Additionally, the implant 100, 200 may be reversibly compressible in one or more axial directions (e.g., two axial directions, e.g., xy, or three axial directions, e.g., xyz) simultaneously. Thus, the implant may be compressible to 80% or less (or, e.g., 70% or less, or, e.g., 60% or less, or, e.g., 50% or less, or, e.g., 30% or less, or, e.g., 20% or less, or, e.g., 10% or less) of its original size in each of one or more axial directions (e.g., height, width, length, and / or projection). The implant may be configured to return to 80% or more (e.g., 90% or more, or, e.g., 95% or more, or, e.g., 98% or more, or, e.g., 100%) of its original size in each of one, two, or three axial directions.

[0066] Optionally, the surface infilling portions may be configured to form a plurality of surface infilling pillars 125 (or strips) in the second exterior surface region 106. The surface infilling pillars 125 may include a plurality of surface infilling portions that fill adjacent surface pores (e.g., openings) of the pillars. The surface infilling pillars may be disposed adjacent to an open pillar 135. The open pillar 135 may include (or may be) a surface pore of the pillar that is devoid of a surface infilling portion. Optionally, the surface infilling pillars 125 and the open pillars 135 may be disposed in an alternating manner in the exterior surface region (e.g., in the second exterior surface region). Optionally, the surface infilling pillars and the open pillars may be disposed in a cross shape in the exterior surface region.

[0067] The surface filling posts 125 disposed in the lower pole portion of the second outer surface region can at least partially cover or close the top openings of some of the grooves of the implant 200. The surface filling posts 125 disposed in the upper pole portion of the second outer surface region can include (or form part of) the groove sidewalls of the plurality of hollow grooves.

[0068] 4A and 4B show longitudinal side and top views, respectively, of implant 200. Implant 200 can include one or more or all of the features described in connection with Figures 1B-3B, as well as various other features.

[0069] As shown in Figures 4A and 4B, the plurality of lines forming the three-dimensional structure 101 of the implant 200 can include a plurality of contour lines. A first group 119 of contour lines in the plurality of lines can be arranged around the perimeter 107 of the first outer surface region 105 (or around the perimeter 107 of one or more layers in the first outer surface region 105, for example). The first group 119 of contour lines can be arranged substantially (e.g., at least 90%, or for example, at least 95%, or for example, at least 99%, or for example, 100%) around the perimeter 107 of the first outer surface region 105, for example forming a closed circle or a closed ellipse. The first group 119 of contour lines can, for example, consist of 2 contour lines to 20 contour lines. The contour lines in the first group 119 of contour lines can be formed continuously (continuously) in a direction from the first outer surface region 105 toward the apex region 112 (e.g., in the z-direction). Optionally, the thickness or height h (measured vertically, z direction) of the first group of contours may be in the range 1 mm to 20 mm (or 2 mm to 10 mm, or such as 1.5 mm to 5 mm).

[0070] The plurality of lines forming the three-dimensional structure 101 of the implant 200 can further include a second group of contour lines 121. Unlike the first group of contour lines 119 that form a complete contour around the perimeter 107 of the first outer surface region, each contour line of the second group of contour lines 121 can form a half contour around the second outer surface region. The half contours of the second group of contour lines 121 can only extend partially (e.g., 30%-80%, or, e.g., 40%-70%, or, e.g., 50%-70%) around the perimeter of the layer. For example, the second group of contour lines 121 can be disposed at (or, e.g., around) the upper pole portion 109 of the second outer surface region 106, and the lower pole portion 111 of the second outer surface region 106 can be free of contour lines (can have no contours). The second group of contour lines 121 can be disposed continuously with respect to each other between the first outer surface region and the apex region. Optionally, the second group of contours 121 need not be formed around the perimeter of every outer layer, nor every alternating layer, or every alternating group of layers.

[0071] Optionally, the surface pore size of the openings in the surface of the upper pole piece 109 is defined by the vertical space between successive (directly adjacent) contour lines of the second group of contour lines 121. For example, the vertical space between successive contour lines of the second group of contour lines may range (or e.g. increase) from 0.5 mm in the upper pole boundary region 114 to a maximum of 5 mm in the apex region 112 of the second outer surface region 106. The direction of increase is indicated by arrow 113, as is the direction of increase in pore size. Optionally, the vertical space between successive contour lines of the second group of contour lines may increase from 0.5 mm to 4 mm (or e.g. increase from 0.5 mm to 2 mm).

[0072] The three-dimensional structure 101 of the implant 200 can be formed from a surface degradable polymer. The surface degradable polymer material can be a polymer material that degrades primarily via a surface degradation mechanism, as opposed to bulk degradation. For example, surface degradation refers to the breakdown of the exterior surface of the polymer material as opposed to the interior of the polymer material. The breakdown of the exterior surface of the polymer material can occur at least twice as fast (or, for example, at least 5 times, or, for example, at least 10 times, or, for example, at least 100 times) as the breakdown of the interior of the polymer material. Bulk degradation refers to the degradation or breakdown of both the exterior surface and the interior of the material simultaneously and at the same rate (e.g., the ratio of the rate of exterior breakdown to the rate of interior breakdown is less than 1.2). The surface degradable polymer can be, for example, a biodegradable polymer. The plurality of lines (or alternatively all lines) can include, be formed from, or consist of a biodegradable material. The biodegradable material can be, for example, a material described in U.S. Pat. No. 6,399,323. As illustrative examples, the biodegradable material may be selected from polycaprolactone, poly(1,3-trimethylene carbonate), polylactide, polyglycolide, poly(ester amide), poly(ethylene glycol) / poly(butylene terephthalate), poly(glycerol sebacate), poly(1,8-octanediol-co-citric acid), poly(1,10-decanediol-co-D,L-lactic acid), poly(diol citrate), poly(glycolide-co-caprolactone), poly(1,3-trimethylene carbonate-co-lactide), poly(1,3-trimethylene carbonate-co-caprolactone), or copolymers of at least two of these materials. Optionally, the biodegradable material may be polycaprolactone. Optionally, the biodegradable material may be a copolymer of polycaprolactone and either poly-trimethylene carbonate or polylactide. Alternatively, the wires may comprise a non-degradable material, such as nylon.

[0073] 5 shows a perspective top view of implant 200. Implant 200 can include one or more or all of the features described in connection with Figures 1B-4B, as well as various other features.

[0074] In some embodiments, the implant 200 is an implant for insertion into a patient. The implant comprises a porous three-dimensional scaffold structure comprising an array of unit cells 102, and the bulk porosity of the implant is at least 80%.

[0075] In some embodiments, the implant 200 comprises a porous three-dimensional scaffold structure 101 comprising an array of unit cells 102. The plurality of unit cells 102 are configured to form a porous network of the three-dimensional scaffold structure 101. The average pore size of the plurality of unit cells 102 in the three-dimensional structure 101 is at least about 0.5 mm (or such as at least about 0.75 mm, or such as at least about 0.8 mm, or such as at least about 1 mm, or such as at least about 1.5 mm, or such as at least about 2 mm, or such as at least about 5 mm).

[0076] In some embodiments, the implant 200 comprises a three-dimensional porous scaffold structure 101 including a plurality of hollow channels 118 extending between a first outer surface region (not shown in top view) and a second outer surface region 106 of the three-dimensional porous scaffold structure 101. The porous scaffold structure 101 includes a surface degradable polymeric material. The first outer surface region is configured to face the chest wall of a patient receiving the implant. The shape of the second outer surface region represents the shape of a breast to be constructed by the implant 200. The plurality of hollow channels 118 are configured to be aligned with Cooper's ligaments of the patient receiving the implant.

[0077] The implant 200 includes a porous three-dimensional scaffold structure 101 comprising an array of unit cells 102. The figure shows the implant 200 including, for example, a plurality of lines, contours 119, and surface infills 122. The implant 200 can include a porous three-dimensional scaffold comprising an array of unit cells. The plurality of unit cells 102 are configured to form a porous network of a three-dimensional structure. The pore size of the plurality of unit cells 102 in the three-dimensional structure can be at least 0.5 mm.

[0078] The lines (eg, intersection lines, contour lines, surface fill lines) can include a degradable (eg, surface degradable) polymeric material.

[0079] Mechanical challenges from daily activities may exceed the elastic capacity of breast tissue and may ultimately lead to irreversible tissue stretching, directly proportional to the mass introduced. Contrary to long-standing conventional wisdom, the weight of an implant, rather than its volume, may be the basis for future tissue defects and deformations. For example, elastic tissue of the breast may be represented by a spring with a constant K. When resting in an upright position, the weight of the implant may be displaced downwards in the breast with a force proportional to the weight of the implant, as described by the following force: F=m×g, where F is the force, m is the mass, and g is the standard gravitational constant. Tissue stretching may be linear (within the elastic limits of the tissue), and therefore tissue displacement may increase in a positive correlation with the weight of the implant. The displacement is described by Δx=F / K, where Δx is the displacement, F is the applied force, and K is the spring constant. A conventional heavy implant may result in an increase in force compared to a light implant, resulting in an inevitable stretching of the breast. Implant 200, being a lightweight implant, can reduce the amount of deformity and loss of breast tissue which can reduce subsequent revision surgeries, thereby further improving patient safety and satisfaction.

[0080] To alleviate the issue of weight affecting the shape of the result, the implant 200 can include a low density scaffold, which for the same volume can reduce the weight of the implant 200 and, as a result, the forces acting on the breast as well. The weight (mass) of the scaffold can be described by the following formula:

number

[0081] The implant 200 can include a low density scaffold and a highly porous scaffold. The bulk (or overall) porosity of the implant of the present invention can be described by the following formula:

number

[0082] Therefore, the volume of the scaffold is expressed as:

number

[0083] 6A shows a graphical representation 600 of the c-value representation, which represents the flexibility of the implant 200. The graphical representation shows a chart of force (N) 131 versus strain value ε (%) 132 for various amounts of compression acting on the implant 200.

[0084] The c value is expressed by the following formula:

number

[0085] As shown in FIG. 6A, the implant 200 can have a lower c value (i.e., the implant is softer) than other implants that do not have the multiple spring-like unit cells of the implant 200. The c value representing the flexibility of the implant 200 can be, for example, 20N to 200N (e.g., 20N to 150N, or, for example, 20N to 90N, or, for example, 30N to 90N, or, for example, 50N to 90N). A c value of 20N to 90N is a good range to balance mechanical integrity and patient comfort. The flexibility of the implant can be adjusted to prevent deformation due to skin tension during the wound healing process. For example, if the implant is too soft (e.g., has a c value smaller than 20N), the implant 200 may be more prone to deformation.

[0086] FIG. 6B shows a diagram of the forces acting on the implant 200.

[0087] After insertion (implantation) into the patient, the implant 200 may be in direct contact with the skin and breast tissue. The combined effects of the tension of the skin 151, 152, the weight of the breast tissue overlying the implant, and daily activity 153 (e.g., due to a woman sleeping on her stomach) create a compressive force 154 acting in the direction of the protrusion of the implant 200, resulting in deformation of the implant.

[0088] 6C(i-iii) show the compressibility of implant 200 and the overestimation of implant 200 volume.

[0089] FIG. 6C(i) illustrates that the implant 200 can have a rest volume or initial shape prior to insertion into a patient.

[0090] FIG. 6C(ii) shows an overestimation 154 of the volume of the implant 200 over the build volume. Because the implant 200 can be a folded 3D printed structure, the effect of constant compressive forces acting due to skin tension and tissue weight on the implant can result in a permanent volume loss before reaching stability. To ensure that the requested volume corresponds to the actual augmented / reconstructed breast volume, the implant volume can be overestimated (relative to the rest volume) to account for the initial collapse due to the effects of skin tension and tissue weight. For example, the volume overestimation 154 can be 20%-30% of the implant's protruding volume (build volume) 155.

[0091] FIG. 6C(iii) shows the volume of the implant 200 after insertion into the patient, where, due to the effect of skin tension, the implant volume corresponds to the original required volume (build-up volume).

[0092] 6D(i)-(iii) show the effect of skin tension on the shape of the implant 200 after insertion into a patient.

[0093] FIG. 6D(i) illustrates that the implant 200 can have a rest volume or initial shape prior to insertion into a patient.

[0094] Figure 6D(ii) shows the effect of skin tension on the implant 200. To reduce the effect of skin tension on the protrusions of the scaffold, the implant 200 is configured such that when tensioning occurs the upper pole side 109 compresses (or collapses) first (in direction 157) to provide a smooth transition between the chest wall and the nipple, while the lower pole side provides a natural breast sagging effect (in direction 156). Both of these features contribute to providing a scaffold construction volume and for said scaffold to acquire the desired aesthetic and natural shape.

[0095] 6D(iii) shows the implant 200 after insertion into a patient. The implant 200 can regain a portion of its original volume, such as at least 80% (or, for example, at least 95%) of its original volume, after being compressed during insertion of the implant 200 into a patient. Thus, the implant 200 can acquire a desired build volume and shape (e.g., an ideal natural shape) under the skin with a compressed upper pole side 109 and a hanging lower pole side 111.

[0096] FIG. 7A shows a view of the implant 200 after insertion into a patient.

[0097] The implant 200 can be configured such that the first outer surface region 105 of the implant 200 can be configured to face the chest wall 141 of the patient receiving the implant 200. Optionally, the implant 200 can be positioned such that the first outer surface region 105 faces the pectoral muscle 143 (e.g., the implant can be positioned above the pectoral muscle). The apex region 112 of the second outer surface region 106 of the implant can be located at (or e.g., directly facing, or e.g., directly below) the nipple / areola of the breast that will be created by the implant 200. The first outer surface region 105, which has the largest average surface pore size, can be configured to face the vascular source of the patient. Body fluids or blood vessels from the patient can infiltrate the porous network of the implant 200 in a direction guided by the direction of the grooves 118 in the implant 200. Alternatively, the implant 200 can be positioned below the pectoral muscle 143. For example, the first outer surface region 105 of the implant can be configured to face the chest wall 141 of the patient, and the muscle can be positioned on the second outer surface region 106.

[0098] FIG. 7B shows the anatomical structure of a patient's breast (eg, augmentation, or eg, breast reduction, or eg, breast revision) that may be constructed with implant 200.

[0099] After the implant 200 is inserted into the patient, the scaffold (e.g., three-dimensional structure) can be resorbed, leaving behind regenerated tissue. The regenerated tissue can be fibrovascular tissue and have a similar weight to the silicone implant as healthy tissue. The constant forces exerted by the weight of this tissue can cause irreversible tissue stretching. Therefore, the number of grooves and the slope of the grooves can be selected to reduce tissue stretching.

[0100] Figure 7C shows a representation of the forces acting on the breast. The breast can be designed as a semi-ellipsoid beam of length L. The mass of the breast forms a force that is aligned with gravity (W_breast). F represents the reaction forces acting in the muscle (F_pectoral fascia) and rib (F_rib) regions, which helps the system to maintain the shape of the breast.

[0101] However, an important role (e.g. the most important role) in providing support and maintaining shape is played by the force acting in tension against gravity (F_Cooper). In young and healthy breast tissue, this effect is brought about by fibrous threads called suspensory ligaments or Cooper's ligaments, which emerge from the pectoral fascia and pass around the periphery of the breast tissue to firmly attach the breast to the overlying skin. When using conventional silicone implants, their weight is almost the same as regenerated and healthy tissue, but there is no system of attachment to the pectoral fascia.

[0102] By depositing the material of the implant 200 in a way that orients the filaments (grooves) in the direction of the tensile forces required to support the structure so that the tissue maintains its shape and is not affected by weight, the regenerated tissue can be reinforced without considering any additional material that may cause safety issues. While the material degrades in the body, the tissue area directly surrounding the scaffold fibers consists of a tightly packed regular connective tissue aligned along the surface of the strut, which is the same composition as tendons and ligaments. It is therefore possible to have a self-made structure (e.g. a template scaffold structure) while fixing the scaffold to the surrounding tissue, providing stability to the shape over time. Thus, although the implant 200 is described here first with respect to a breast implant, such implants are also useful in other parts of the body such as the chest, buttocks (also known as hips), calves, parts of the face such as the cheeks (or cheeks), or even genital areas such as the testicular region, to name only a few exemplary body areas. The implant of the present invention can therefore adopt any optimal form simply corresponding to the tissue to be reconstructed or augmented. The implant may have the form of, for example, a buttock implant as described in US Pat. No. 10,004,585 (a perspective view of a buttock implant having a form as described in US Pat. No. 10,004,585 is shown in FIG. 6E), a breast (see breast implant shown in FIGS. 11A-11E for reconstruction of the breast or breast area of ​​a patient's body), a cheek or buccal (see FIGS. 12A-12C which show a schematic diagram of a soft tissue reconstruction implant for reconstruction of the buccal (or buccal) area of ​​a patient's body), or a testicular area (see FIGS. 13A-13B which show a schematic diagram of a soft tissue reconstruction implant for reconstruction of the testicular area of ​​a patient's body).

[0103] FIG. 7D shows a histological photograph of the regenerated breast tissue.

[0104] The tissue that regenerates within the grooves 118 of the implant 200 after insertion into the patient may be free in nature, with a high degree of vascularization and randomness in terms of the alignment of the collagen fibers (panels (i) and (ii)). However, the tissue areas directly surrounding the scaffold fibers are regular connective tissue, with the same organization as tendons and ligaments, and aligned along the surface of the struts (panels (iii) and (iv)). Thus, by using 3D printing techniques to form the grooves 118 of the implant 200, it is possible to tailor where the stiffest areas of tissue will grow.

[0105] During daily activities (e.g., standing, running, jumping, and walking) in healthy tissue, the greatest forces can be borne by Cooper's ligaments 144, which are anatomically considered as the structural framework that holds the constructed breast. The hollow grooves 118 can be configured to align with Cooper's ligaments 144 of the patient receiving the implant 200, so that after insertion of the implant 200 into the patient, bodily fluids or blood vessels can infiltrate the pores (e.g., hollow grooves) of the implant 200 to form long, aligned tissue fibers in the hollow grooves, mimicking the arrangement of the patient's Cooper's ligaments 144 prior to insertion of the implant 200. The hollow grooves 118 can be oriented such that the regenerated tissue is fully embedded into the surrounding tissue, and the denser tissue aligns with Cooper's ligaments (e.g., from muscle 143 to nipple 142), exerting tensile forces that act as support for the new tissue (FIG. 7A) that provides and improves the structural stability of the implant 200.

[0106] FIG. 7E shows the force of Cooper's ligament acting on one filament (or for example one groove with resorbed tissue).

[0107] The number of grooves 118 in the implant 200 and the inclination angle of the grooves 118 in the implant 200 can be determined by testing the forces from daily activities and the tensile strength of the ligaments.

[0108] Assuming that the mass of the breast m = 1 kg and the jump angle α = 60° (in the extreme case), the force that the Cooper's ligament can undergo (Fクーパー ) can be 50N to 60N. After absorption of the threads into the hollow grooves 118, the areas of dense tissue are roughly similar to the filaments. For example, the filaments (grooves) of the implant 200 have a diameter of 200 μm and a density of 314×10 -10 m 2 has a surface area of

[0109] The force acting on a single dense connective tissue filament is

number

[0110] The maximum force exerted by a single filament is:

number

[0111] In the worst case (fiber diameter 200 μm, m=1 kg and α=60° at jump), generating a force of 60 N may require a total number of filaments of:

number

[0112] In healthy breast tissue, the tilt angle α can range from 45° to 60°. Therefore, it is possible to calculate the theoretical maximum and minimum values ​​of α that can be used for filaments inside a three-dimensional structure.

[0113] FIG. 7F shows a diagram illustrating the internal forces acting on breast tissue during running, jumping, walking, and standing.

[0114] d2 represents the effective radius of curvature of the breast, d1 represents the center of gravity of the breast (reasonably assumed as a semicircle), α is the dorsal insertion angle of the breast, and O is the reference point at the base of the breast.

[0115] The forces exerted when standing, walking, running, and jumping are expressed as follows:

[0116] [Table 1]

[0117] m is the mass of the breast, and W(W 乳房 ) is the force generated by the weight of the breast.

[0118] To calculate the force, m is in the range of 0.5kg to 1kg.

number

[0119] The acceleration can be considered as follows:

[0120] [Table 2]

[0121] The force can be calculated as follows:

[0122] [Table 3]

[0123] In the following example, we assume an extreme case scenario of a breast weight of 1 kg suspended during jumping without a bra, with a small amount of implant (100 ml) with, say, 65 filaments. It is important that equilibrium is maintained so that the breast maintains its shape and prevents sagging. This equilibrium is:

number

number

number

[0124] Assuming all filaments work in tension, the maximum force that can be exerted is:

number

[0125] For example, the maximum value of α can therefore be calculated as follows:

number

[0126] Assuming that only half the filaments are working in tension, the maximum force that can act is:

number

[0127] For example, the minimum value of α can therefore be calculated as follows:

number

[0128] Thus, the acute inclination angle k between the sidewall of the hollow groove in the plurality of hollow grooves and a reference axis (e.g., the x-axis) representing the first outer surface region can be in the range of 3° to 87°, or 3° to 54° (or for example 10° to 50°, or for example 25° to 45°).

[0129] The implant 200 allows tissue regeneration and can keep alive the adipose tissue once injected into the scaffold and nutrients are needed. The four main blood sources of the breast are the internal thoracic artery, the external thoracic artery, the anterior intercostal artery, and the thoracoacromial artery. The scaffold structure and / or porous network in the unit cells 102 of the implant 200 can therefore provide space for vessels to infiltrate and live in the scaffold, especially at the interface between the scaffold and the major blood sources. However, it is important in the implant 200 to have adequate space throughout the scaffold, allowing the vessels to reach from all places. However, highly porous implants can lead to patient discomfort. For example, the more porous the implant, the higher the surface roughness, which can cause discomfort to the patient. The implant 200 provides space for exchange of materials (allowing potentially harmful materials that may be trapped inside the scaffold to escape and allowing materials that may help tissue regeneration to enter the scaffold) and also allows for patient comfort (e.g., by reducing tissue irritation and / or infection). The implant 200 addresses patient comfort and scaffold security by providing a smooth interface between the scaffold and tissue despite the scaffold being porous (via space-filling and contouring).

[0130] To aid in vascularization of the scaffold, the implant 200 can be considered to have the highest pore size of the scaffold facing the major blood supply (e.g., FIG. 7A) and to have a highly porous scaffold. Different porosities (e.g., two or more different porosities and / or pore ranges) can be considered to compromise the surface roughness and provide space for blood vessels to infiltrate and distribute throughout the entire scaffold (FIGS. 2A-2E). For example, the top surface porosity and / or pore size range can be smaller than the bulk porosity value, but facing the tissue area where the minor blood supply is located. For example, the bulk porosity and / or pore size range can be higher than the surface value, providing space for all blood vessels to migrate throughout the scaffold. With the possibility of tuning the fiber deposition, the implant grooves can be aligned toward the major blood supply, with the largest pore size at the interface between the scaffold and the muscle, and the smallest pore size at the interface between the scaffold and the nipple / breast tissue. For example, pore size at the bottom is 8mm and pore size at the top is 2mm, the projection of the groove on the underside of the implant has a range of 6mm to 2mm.

[0131] Due to the possibility of tailoring the fiber deposition, the implant 200 can include a full contour at the bottom to ensure implant stability and a semi-contour in the remaining part of the scaffold to maintain porosity in the lower pole of the scaffold (FIGS. 4A-4B). The semi-contour is used to smooth the surface for patient comfort, while at the same time maintaining a certain porosity required to allow for material exchange and vascular infiltration. In some embodiments, the implant 200 can include a top pole surface with a porosity of approximately 83%, and the pore size of the top pole surface can be 0 mm to 6 mm. The bulk porosity can be 95%, and the bulk pore size can be 0 mm to 8 mm.

[0132] Unlike implant 200, conventional silicone implants can be filled with a non-compressible liquid. However, over time, silicone implants can rupture and cause health problems, potentially leading to additional surgery.

[0133] The implant 200 can be formed using 3D printing to tailor fiber (groove) deposition, create a reversibly compressible structure, and create an implant 200 that is comfortable for the patient. The implant 200 can be configured to provide shape stability while retaining the flexibility of the implant. The implant 200 can accommodate the required shape and ensure that the final shape of the breast after insertion into the patient is ideal and natural.

[0134] The implant 200 provides shape stability to the scaffold by using a spring-like system that deforms when a force is applied and returns to its shape when it is released (FIGS. 1C-1D), avoiding pore obstruction and any extra force acting on the thoracic cavity that may cause damage to the tissue or, in the most severe cases, the lung. The reversibly compressible structure can transmit the force acting along one direction to a vertical direction (FIG. 1C). When the force is released, the energy stored during this process acts in the opposite direction (FIG. 1D), helping the shape spring back and return to its original shape in less than 8 hours.

[0135] The shape stability and flexibility of the implant is important to ensure patient comfort. The implant 200 can have anisotropic mechanical properties, which can include a combination of spring-like unit cells and grooves aligned towards the nipple area. The spring-like unit cells allow the implant 200 to be soft in the lateral direction to ensure a natural feel. The combination of the spring-like unit cells and groove orientation allows the implant 200 to still be soft along the printing direction, while still being rigid enough to maintain shape under tissue weight and other forces.

[0136] To ensure shape stability and desired flexibility of the implant 200, the anisotropic mechanical properties may include a combination of both the effect of spring-like unit cells and grooves aligned in the direction of the major force. The implant 200 may be formed by considering the forces acting on the scaffold after insertion into the patient to ensure that the volume of the scaffold in the body is the same as the required volume, and a certain percentage of additional volume (or additional size) may be considered during manufacturing. Depending on the shape to be achieved and the forces acting on the breast, adjustments to the contour may be considered in advance to achieve the desired result after the force is applied, to provide a natural result.

[0137] FIG. 8 shows a flow chart of a method 800 of forming an implant of the present invention.

[0138] The method 800 includes a step 830 of successively printing layers to form a three-dimensional (3D) printed structure. The three-dimensional printed structure defines a rest volume of the implant to be formed. Each printed layer includes a lattice array of two-dimensional unit cells. The three-dimensional printed structure can have porosity such that (or where) the three-dimensional printed structure is compressible to at least 80% of its rest volume.

[0139] Method 800 can optionally include determining a build volume of the implant 810 prior to successively printing the layers. Method 800 can further include determining a rest volume of the implant 820 based on the build volume of the implant. For example, the rest volume of the printed implant can be an overestimate of the build volume of the implant.

[0140] In the method 800, the step 830 of successively printing layers can include printing a first layer to form a first outer surface region of the 3D printed structure, and printing successive layers on the first layer according to a printing direction. The printing direction (e.g., z-direction) can be a direction perpendicular to the plane of the first layer. A successive edge region of the successive printed layer can form a second outer surface region of the 3D printed structure adjacent to the first outer surface region. The second outer surface region can define a shape of a breast to be constructed by the implant, and a region between the first outer surface region and the second outer surface region can define a rest volume of the implant before implantation into a patient.

[0141] Successive layers can be disposed relative to one another such that unit cells of the layers can form a plurality of hollow channels in the 3D printed structure. The plurality of hollow channels can extend between a first exterior surface region and a second exterior surface region of the three-dimensional structure (e.g., in a direction from the first exterior surface region toward the second exterior surface region).

[0142] Optionally, layers can be printed sequentially to form multiple three-dimensional unit cells (e.g., tetrahedral unit cells) of the 3D structure. Optionally, the two-dimensional unit cells of the layers can be considered as facets (or planes) of the three-dimensional unit cells.

[0143] The method 800 may further include forming a plurality of surface infills 840 after forming the successive printed layer. Forming the surface infills may include forming one or more fill lines to at least partially fill one or more openings (surface pores) in an outermost surface of the three-dimensional structure.

[0144] The method 800 may further include forming 850 a plurality of contour lines after the successive printing of the layers. Forming the plurality of contour lines may include forming a first group of contour lines around a perimeter of the first exterior surface region and / or a second group of contour lines. Unlike the first group of contour lines forming a complete contour around the perimeter of the first exterior surface region, each contour line in the second group of contour lines may form a half contour around the second exterior surface region.

[0145] It can be understood that the features described with respect to the various embodiments herein can be combined with each other. The method 800 can include one or more or all of the features already described with respect to Figures 1B-7F.

[0146] Experimental Example 1: Long-term implantation study of the present invention in combination with autologous fat grafting (AFG) in a large animal (Elegaard-Göttingen minipig) model 3D printed medical grade polycaprolactone resorbable implants (scaffolds) as described herein, complying with ISO 11137 (sterilization), 13485 (quality systems), 11607 (packaging) and 14644-1 (clean room) standards, have been used to evaluate the safety of the finished implants, including: 1. Long-term evaluation of immune responses 2. Long-term evaluation of AFG persistence 3. Device (implant) performance 4. Device operability during surgical procedures

[0147] Ellegard Göttingen minipigs obtained from Ellegard GmbH, Dalmoose, Denmark, were selected for this study. 3 A scaffold of this type was used for small sized animals and had the following dimensions (see also Figures 9A and 9B): Height: 84mm ·Width: 91mm ·Protrusion: 31.5mm Pore ​​size at the base and apex of the implant: 4mm (base), 8mm (apex), meaning the average pore size is greater than 4mm.

[0148] The size of the mini-pig employed in this study is approximately 1.5 times smaller than the size of an average human female. Taking into account the difference in size, the equivalent dimensions of the scaffold for an average human female are as follows: Height: 126mm ·Width: 136.5mm ·Protrusion: 47.25mm Pore ​​size at the base and apex of the implant: 4mm (base), 8mm (apex), meaning the average pore size is greater than 4mm.

[0149] Therefore, the implant (scaffold) size selected for the mini pig was 300 cm, which is the size of a human female with an average body size. 3 It should be noted, however, that the implants used in the present animal study are intended to be employed in human patients as well, i.e., female patients with smaller than average body size.

[0150] The trial will include a total of 32 animals randomized into three time point groups: a 6-week pilot study, and 12 and 24 month main studies. 12 month time point → 16 animals 24 month time point → 16 animals (n=32 treatments)

[0151] Four treatment groups were selected for this study: 1. Group 1 is a negative control group in which only the implant of the present invention is implanted (i.e., no AFG). 2. In group 2, immediately after implantation of the implant (scaffold) of the present invention, AFG (50 cm 3 ) is carried out. 3. In group 3, autologous fat injection (50 cm) was performed 4 weeks after the insertion of the implant of the present invention. 3 ) is executed. 4. Group 4 is a positive control in which only AFG is performed and corresponds, as far as practicable, to the standard AFG procedure performed in humans.

[0152] The tissue infiltration of the implants of the invention was evaluated by magnetic resonance imaging (MRI). Figure 9C shows partial tissue infiltration of the implant 2 weeks after implantation in minipigs of treatment group 3, while Figure 9D shows that complete and rapid tissue infiltration of the implant in minipigs occurs already 4 weeks after implantation. In this context, in implants as described in patent document 1 and non-patent document 1, complete tissue infiltration was only observed after 24 weeks. Thus, the implants of the invention provide faster tissue infiltration, thereby offering an important advantage over known implants.

[0153] For example, compared to implant (scaffold) designs as described in US Pat. No. 5,399,433 and US Pat. No. 5,499,433, the following additional functional differences were found in this study:

[0154] Pore ​​size and porosity All published literature related to soft tissue engineering, including Patent Document 1 and Non-Patent Document 1, describes scaffolds with an average pore size of 1 mm or less. In contrast, it has been found in the present invention that in order to regenerate large volumes of tissue (>50 ml) in a clinically relevant setting, large pores (>1 mm) are required to allow efficient infiltration of angiogenesis into the central region of the implant. The implant of the present invention used in this study, with a pore size of 8 mm at the base and 4 mm at the apex (apex), meets this need and therefore allows efficient infiltration of angiogenesis into the central region of the implant.

[0155] mechanical properties Studies such as "Patent Document 1" aimed at regenerating large volumes of soft tissue have described the use of a combination of small pore sizes (<0.5 mm) and a rigid porous structure. The rigid structure has been shown to cause inflammation in the tissue. This inflammatory problem has been shown to result in mild chronic inflammation within the pores of the device, as shown in Figure 4 of "Patent Document 1" (reproduced herein as Figure 10A), characterized by invasion of lymphatic structures in the tissue.

[0156] In contrast, the highly porous, spring-like compressible implants produced using the design features identified herein did not result in inflammation or chronic inflammation, as shown in Figure 10B. Thus, the ability of the implants of the present invention to avoid inflammation after implantation due to these mechanical properties, along with the very fast tissue infiltration and lightweight nature of the implants, makes them ideal candidates for tissue restoration and tissue augmentation.

[0157] 11A-11E show several views of a soft tissue reconstruction implant 300 for reconstruction of the chest or chest region of a patient's body, such as in the case of congenital pectus excavatum. The implant 300 can include one or more or all of the features described in connection with FIGS. 1B-10B, as well as various other features.

[0158] 11A and 11B show respective bottom views of a thoracic implant 300. The thoracic implant can include a first exterior surface region 105, which can be the largest planar (or, e.g., flattest) surface of the implant. The unit cells of the successive layers can form a plurality of hollow channels extending between the first exterior surface region 105 and the second exterior surface region 106 in the three-dimensional structure 101 of the thoracic implant 300.

[0159] 11C and 11D show perspective side and top views of pectoral implant 300. The contour and shape of second exterior surface region 106 can be based on the desired size and shape of pectoral implant 300.

[0160] FIG. 11E illustrates a cross-sectional side view of a thoracic implant showing a plurality of hollow channels extending between first outer surface region 105 and second outer surface region 106 in three-dimensional structure 101 of thoracic implant 300.

[0161] Experimental Case 2: Phase 1 Clinical Trial of Breast Implants Soft tissue reconstruction implants as described herein (such as chest implant 300) are absorbable soft tissue reconstruction scaffolds that are used to reconstruct the chest or chest region of a patient's body, such as in cases of congenital pectus excavatum. The impact of surgery is reported at https: / / www.abc.net.au / news / 2020-07-21 / world-first-3d-chest-scaffold-funnel-chest-queensland / 12477704.

[0162] Currently, three main surgical options exist for reconstruction of the breast base following mastectomy or for congenital defects such as pectus excavatum. Reconstruction using silicone implants is associated with several drawbacks, including capsular contracture. Furthermore, silicone implants are also subject to potential rupture, displacement, deformity, and chronic seroma or hematoma. Free tissue transfer procedures such as latissimus dorsi, pedicle transverse rectus abdominis myocutaneous flap, or deep inferior epigastric artery perforator flap often take 8-9 hours and are associated with extended hospital stays and extended recovery periods. The main complication associated with these is sometimes the formation of thrombi in the veins draining the flap or in the arteries supplying the flap. Both cases can result in necrosis of the flap tissue. Finally, autologous fat transfer or lipofilling is associated with a 40%-60% reduction in graft volume due to tissue resorption and necrosis, leading to poor clinical results in large volume reconstructions (greater than 100cc). Two other methods exist for pectus excavatum defects: the Nass technique and the Vacuum Bell technique. A key step in the Nass technique is the introduction of a curved bar that elevates the sternum. Complications with this technique include chronic pain, reoperations requiring removal of the bar after several years, possible damage to the heart or lungs during surgery, and incorrect positioning of the bar. An alternative solution, the vacuum bell, which uses suction cups to elevate the sternum without surgical intervention, has produced poor clinical results in some cases of pectus excavatum and cannot be used in patients with cardiac injury.

[0163] A clinical trial using the chest implant described herein was performed by a plastic and reconstructive surgeon for the congenital pectus excavatum deformity. Pectus excavatum (pectus excavatum syndrome) is a chest deformity characterized by a central or lateral sternal depression. Pectus excavatum syndrome may occur in 1% to 2% of the population and is the most common congenital thoracic deformity. The surgery to insert the implant into the patient's body was designed as a minimally invasive method that does not touch the bone and is expected to result in less painful recovery than other procedural approaches, and the use of an absorbable scaffold offers simplicity compared to other techniques that use silicone. The patient had a pectus excavatum deformity and was born with lymphatic obstruction affecting the chest wall and upper limbs and limb hypertrophy. This set of conditions is known as Klippel-Trenoret syndrome. A 6 cm old scar that had previously been used to insert a tissue expander was used to access the anterior aspect of the sternum. This entailed the removal of the sternocostal portion of the ipsilateral pectoralis major muscle as is routinely done in breast augmentation surgery. A cavity for the implant was created and the implant was inserted. Fat grafts were also harvested from the patient's thighs and abdomen. The fat was prepared using standard Coleman fat grafting techniques and then injected directly into the implant using standard fat injection needles. The key part of the procedure is to inject the patient's own fat into the scaffold at the time of implant insertion or several weeks later. This stimulates the regeneration of a highly porous scaffold with a significant amount of the patient's own tissue (e.g., more than 70%, or more than 80%, or more than 90%). The wound was then closed in a standard two-layer technique. No surgical drains were required. Light compression dressing was applied as is routinely done in breast implant surgery. A significant difference was observed when using a camouflage 3D printed scaffold to hide deformities such as pectus excavatum. The patient had already undergone 17 surgeries for chest deformities, which affected her heart and lung function. The procedure allowed the deformities to be hidden without harming her organs. Furthermore, the implant material allows the implant to disappear completely after some time.

[0164] The implants as described herein are implanted by minimally invasive methods. The absorbable (e.g. fully absorbable) porous scaffold exhibits very specific topology and design features and serves as a base for injecting adipose tissue harvested using standard liposuction surgery. The absorbable polymer aids in natural breast tissue regeneration after implantation. Tissue can be regenerated from the patient's own body fat without the need for cultured stem cells or products of animal origin. The implant is absorbed over a period of time (e.g. 2 years) providing a stable base for the injected adipose tissue to mature, adapt and stabilize in its environment. Other implants may not be compressible or malleable and / or designed to disappear. For example, silicone implants need to be replaced due to complications such as capsular contracture, silicone implants are not lifelong devices. For example, patients with silicone implants require up to three revision procedures at some point in their lives. The implants described herein avoid these revision procedures by providing a porous network that can regenerate the patient's own tissue after implantation at the surgical site. Additionally, the incompressibility and spring-like properties of the implant allow for folding and / or compressing of the scaffold so that only very small incisions are required, minimizing trauma and / or surgical scarring or scarring to the patient's body.

[0165] Further Examples of Use of the Soft Tissue Reconstruction Implant of the Present Invention 12A-12C show several views of a soft tissue reconstruction implant 400 for reconstruction of the buccal region (or cheek) of a patient's body. The implant 400 can include one or more or all of the features described in connection with FIGS. 1B-11E, as well as various other features.

[0166] 12A and 12B show perspective top views of the cheek implant 400. FIG. 12C shows a side view of the cheek implant 400. The cheek implant may include a plurality of hollow grooves extending between the first outer surface region 105 and the second outer surface region 106 in the three-dimensional structure 101 of the cheek implant 400. The cheek implant may further include a contour line 421 forming a complete and / or partial contour around the periphery of the first outer surface region 105 and the second outer surface region 106. The cheek implant may optionally include an apex region 112. The distance between the apex region 112 of the second outer surface region 105 and the first outer surface region 105 may be the maximum height between any portion of the second outer surface region 105 and the first outer surface region 105.

[0167] The spring-like, reversibly compressible implant allows the cheek implant to mimic the flexibility and reversible compressibility of a patient's cheek (such as the stiffness of human fat and tissue).

[0168] 13A-13B show perspective side and top views, respectively, of a soft tissue reconstruction implant 500 for reconstruction of the testicular region of a patient's body. The implant 500 can include one or more or all of the features described in connection with FIGS. 1B-12C, as well as various other features.

[0169] The testicular implant 500 can optionally be spherical and / or ovoid. The testicular implant can include a plurality of hollow grooves extending between the first outer surface region 105 and the second outer surface region 106 in the three-dimensional structure 101 of the testicular implant 500. Optionally, the hollow grooves can be zigzag or sinusoidal grooves. The implant 500 can further include a contour line 521 forming a complete and / or partial contour around the periphery of the first outer surface region 105 and the second outer surface region 106. The testicular implant 500 can optionally include an apex region 112 in the second outer surface region 106.

[0170] Testicular implants can be performed in the case of testicular surgery or cosmetic. Testicular implant 500 can have a desired size of testis (e.g., the size of an average human testis) and can be implanted in a patient in the absence of one or both testicles. Testicular implant 500 can have dimensions that allow the testicular implant to fit within the scrotum after implantation in the scrotum. A pair of testicular implants 500 can be used to create or restore testicular symmetry, such as in cases where the patient's original testicles differ significantly in size from one another.

[0171] Similar to saline breast implants, current testicular implants may be filled with saline, and thus present similar challenges as those presented by saline implants. After implantation, saline testicular implants may result in a hardening of the capsule around the implant. Additionally, there is the possibility of infection, migration of the implant within the body, and scarring from the incision. The reversibly compressible testicular implant 500 allows for the smallest possible scarring and reduced recovery time. Thus, the testicular implant procedure may be performed as an outpatient surgery, reducing anesthesia.

[0172] Each implant described herein can be a spring-like reversibly compressible implant that, after the compressive force is released, can return (recover) or return (return) to its original (rest) volume (without changing the ambient pressure and temperature). The spring-like implant can be compressible to at least (e.g., equal to or greater than) 80% (or e.g., at least 70%, or e.g., at least 60%, or e.g., at least 50%, or e.g., at least 30%) of its original volume. The spring-like implant can be configured to return to at least 80% (e.g., 80% or more) (or e.g., at least 90%, or e.g., at least 95%, or e.g., at least 98%, or e.g., up to 100%) of its original volume after the compressive force acting on the implant is released. The surface filling line 122 and the contour lines 119, 121, 421 also provide comfort to the user to prevent inflammation. Thus, a spring-like and smooth implant for insertion into a patient is provided without using an external coating (such as in the case of a saline implant). The implant can be biodegradable. Optionally, after implantation, depending on the desired softness of the implantation area, fat can be injected into the implant to soften the implantation area. Alternatively, it is also possible not to perform fat injection during implantation. The tissue infiltrates the inserted implant, and after a few weeks, the implant biodegrades.

[0173] Figures 14A - 14C show more detailed implants 100, 200 described in relation to Figures 1B - 10B and can be soft tissue reconstruction implants for the reconstruction of the breast region of a patient's body. The soft tissue reconstruction implants 100, 200 can be spring-like reversibly compressible implants.

[0174] The implant 100, 200 includes a plurality of unit cells 102 configured to form a spring-like three-dimensional lattice structure 101, which comprises the rest volume of the implant. The plurality of unit cells 102 are configured to form a porous network of the three-dimensional structure. The bulk porosity of the three-dimensional structure 101 in the implant is at least 50%, or at least 60%, or at least 70%.

[0175] The individual unit cells 102 can be reversibly compressible spring-like unit cells that can be compressed to at least (e.g., equal to or less than) 10% or 20% of their original volume and return to at least (e.g., equal to or greater than) 80% of their original volume.

[0176] The surface porosity of the second exterior region 106 may be less than the bulk porosity of the three-dimensional structure of the implant 100, 200. The implant material density may be less than 0.1 gr / cm 3 ~2gr / cm 3 It can be said that:

[0177] The present invention is further characterized by the following:

[0178] Item 1: An implant for insertion into a patient, the implant comprising a plurality of unit cells configured to form a three-dimensional lattice structure, the three-dimensional structure comprising a rest volume of the implant, the plurality of unit cells configured to form a porous network of the three-dimensional structure, the three-dimensional structure being a reversibly compressible three-dimensional structure.

[0179] Item 2: The implant of item 1, wherein each unit cell in the plurality of unit cells comprises a reversibly compressible unit cell.

[0180] Item 3: The implant according to item 1 or 2, wherein the unit cell in the plurality of unit cells is a three-dimensional unit cell.

[0181] Item 4: The implant of any of items 2 or 3, wherein the reversibly compressible unit cell is compressible to at least 50%, or at least 60%, or at least 70%, or at least 80% of its original volume and returns to at least 80% of its original volume.

[0182] Item 5: An implant according to any one of items 1 to 4, wherein the rest volume of the implant is based on a construction volume of a breast to be constructed by the implant, and the implant is configured to be reversibly compressible to at least the construction volume.

[0183] Item 6: An implant according to any one of items 1 to 5, wherein each unit cell includes intersecting lines in a plurality of lines, and the intersecting lines of the unit cells are configured to form a plurality of pores in the unit cells.

[0184] Item 7: The implant according to any one of items 1 to 6, wherein the intersection lines of the unit cells define the pore size of the unit cells.

[0185] Item 8: The subject matter of any of Examples 1-7, wherein the average pore size of the unit cells in the three-dimensional structure is at least 0.5 mm.

[0186] Item 9: The implant according to any one of items 1 to 8, wherein the pore size of at least 50% of the unit cells in the three-dimensional structure is at least 0.5 mm.

[0187] Item 10: The three-dimensional structure is a first outer surface region of the implant having a first surface curvature; a second outer surface region of the implant having a second surface curvature; a second outer surface region of the implant adjacent the first outer surface region of the implant at a periphery of the first outer surface region; 10. The implant according to any one of items 1 to 9, wherein the shape of the second outer surface region represents the shape of a breast to be constructed by the implant.

[0188] Item 11: The second outer surface region is an upper pole portion having a shape of an upper portion of a breast to be constructed by the implant; a lower pole portion having a shape of a lower portion of the breast to be constructed by the implant; Item 11. The implant of item 10, wherein the upper pole portion and the lower pole portion coincide at an apex region of the second outer surface region of the three-dimensional structure.

[0189] Item 12: the first outer surface region comprises a surface of minimal curvature on the implant; the curvature of the upper pole portion of the second exterior surface region is greater than the curvature of the first exterior surface region; and Item 12. The implant of item 11, wherein the curvature of the lower pole portion of the second outer surface region is equal to or greater than the curvature of the upper pole portion of the second outer surface region.

[0190] Item 13: The implant according to any of items 1 to 13, wherein the average pore size of the openings in the first outer surface region of the three-dimensional structure is at least 25% larger than the average pore size of the openings in the second outer surface region of the three-dimensional structure.

[0191] Item 14: The implant according to any of items 10 to 13, wherein the average pore size of the openings in the first outer surface region of the implant is at least 2 mm.

[0192] Item 15: The pore size of the upper pole portion of the second outer surface region increases from 0.5 mm in the upper pole boundary region to a maximum of 5 mm in the apex region of the second outer surface region; 15. The implant according to any one of items 11 to 14, wherein the upper pole boundary region is a boundary region of a three-dimensional structure where the upper pole portion of the second outer surface region meets a portion of the periphery of the first outer surface region.

[0193] Item 16: the pore size of the lower pole portion of the second outer surface region increases from 0.15 mm or 2 mm at the lower pole boundary to up to 6 mm, or up to 8 mm, or up to 9 mm, or up to 10 mm toward the apex region of the second outer surface region; 16. The implant according to any one of items 11 to 15, wherein the lower pole boundary region is a boundary region of a three-dimensional structure where the lower pole portion of the second outer surface region meets a portion of the periphery of the first outer surface region.

[0194] Item 17: The implant according to any of items 10 to 16, wherein the surface porosity of the second outer surface region is less than the bulk porosity of a three-dimensional structure in the implant.

[0195] Item 18: An implant according to any of items 1 to 17, wherein the bulk porosity of the three-dimensional structure in the implant is at least 50%, or at least 60%, or at least 70%, or at least 80%.

[0196] Item 19: The implant according to item 18, wherein the bulk porosity of the implant is between 50%, or at least 60%, or at least 70%, or at least 80%, and 99%.

[0197] Item 20: The implant material density is 0.1gr / cm 3 ~2gr / cm 3 20. The implant according to any one of items 1 to 19,

[0198] Item 21: The implant according to any one of Items 1 to 20, wherein the plurality of unit cells includes a plurality of three-dimensional unit cells, and the three-dimensional unit cells are tetrahedral unit cells.

[0199] Item 22: The three-dimensional structure includes an arrangement of layers including a plurality of outer layers disposed contiguously with one another; 21. The implant of any of items 1-20, wherein each outer layer of the array of layers comprises a lattice array comprising a plurality of two-dimensional unit cells.

[0200] Item 23: The implant of item 22, wherein the plurality of two-dimensional unit cells is at least one of a triangular unit cell, a diamond-shaped unit cell, a rhomboidal unit cell, a rectangular unit cell, and a hexagonal unit cell.

[0201] Item 24: The three-dimensional structure comprises a first exterior region including a first layer of the arrangement of layers; the two-dimensional unit cells of successive layers of the array of layers form a plurality of hollow channels extending between the first exterior surface region and the second exterior surface region of the three-dimensional structure; 24. The implant of any of items 22 or 23, wherein the second outer surface region is adjacent to the first outer surface region at a periphery of the first outer surface region.

[0202] Item 25: The implant according to Item 24, wherein the hollow grooves are parallel to one another.

[0203] Item 26: An implant described in either of items 24 or 25, wherein the first outer surface region is configured to face the chest wall of a patient receiving the implant and the plurality of hollow grooves are configured to align with Cooper's ligaments of the patient receiving the implant.

[0204] Item 27: An implant according to any one of items 24 to 26, wherein the plurality of hollow grooves are inclined relative to the first outer surface region of the implant, and an acute inclination angle between the plurality of hollow grooves and a reference axis representing the first outer surface region is less than 60°.

[0205] Item 28: An implant described in any of items 24 to 27, wherein the multiple hollow grooves are configured to converge toward a convergent region, the convergent region being located outside the first outer surface region or the second outer surface region in the three-dimensional structure.

[0206] Item 29: The second outer surface region has an upper pole portion having a shape of an upper part of a breast to be constructed by an implant; a lower pole portion having a shape of a lower portion of the breast to be constructed by the implant; the upper pole portion and the lower pole portion meet at a tip region of the second outer surface region; 29. The implant of any of items 24-28, wherein one or more of the plurality of hollow grooves are configured to extend from the first outer surface region toward at least one of the apex region of the second outer surface region and the lower pole portion of the second outer surface region.

[0207] Item 30: The implant of item 29, wherein one or more additional grooves of the plurality of hollow grooves are configured to extend from an upper pole portion of the second outer surface region toward at least one of an apex region and a lower pole portion of the second outer surface region.

[0208] Item 31: The implant of any of items 1 to 30, wherein a first group of contour lines in the plurality of lines are disposed around a periphery of a first outer surface region of the implant.

[0209] Item 32: the plurality of lines includes a second group of contour lines; each contour line in the second group of contour lines forms a semi-contour around a second outer surface region of the implant; 32. The implant of claim 31, wherein the second group of contour lines are disposed continuously with respect to one another between the apical region of the first outer surface region and the second outer surface region.

[0210] Item 33: The implant of item 32, wherein the second group of contour lines is disposed at an upper pole portion of the second outer surface region and a lower pole portion of the second outer surface region is free of contour lines.

[0211] Item 34: The implant of item 22, comprising a plurality of surface filling portions, the surface filling portions comprising one or more filling lines configured to at least partially fill openings in the outer surface region of the three-dimensional structure.

[0212] Item 35: The implant of item 34, wherein one or more fill lines of the surface fill portion are configured to connect to a group of intersecting lines that define unit cells at the outermost surface of the three-dimensional structure.

[0213] Item 36: The three-dimensional structure is a first group of unit cells at an outermost surface of the three-dimensional structure having a surface infill that blocks openings of the first group of unit cells; and a second group of unit cells at an outermost surface of the three-dimensional structure that is devoid of surface infill.

[0214] Item 37: The implant of any of items 34 to 36, wherein at least 20% of the unit cells at the outermost surface of the three-dimensional structure are at least partially filled with the surface filling portion.

[0215] Item 38: The surface filling pillars and the open pillars are alternately arranged in the outer surface region; the openings of the surface filling pillars at the outermost surface of the three-dimensional structure are at least partially filled with the surface filling portion; and 38. The implant according to item 37, wherein the openings of the open posts at the outermost surface of the three-dimensional structure are free of surface filling.

[0216] Item 39: The implant of item 38, wherein the surface filling posts include side walls of the grooves in the plurality of hollow grooves.

[0217] Item 40: The implant according to any one of items 1 to 39, wherein the c value representing the flexibility of the implant is 20N to 200N.

[0218] Item 41: The implant of any of items 6 to 40, wherein the plurality of wires comprises a surface degradable polymer material.

[0219] Item 42: The implant of any of items 6 to 40, wherein the plurality of wires comprises a non-degradable material.

[0220] Item 43: The implant according to any one of Items 24 to 42, wherein the plurality of hollow grooves consists of 5 to 1000 hollow grooves.

[0221] Item 44: An implant for insertion into a patient, the implant comprising: An implant comprising a porous three-dimensional scaffold structure comprising an array of unit cells, the bulk porosity of the implant being at least 50%, or at least 60%, or at least 70%.

[0222] Item 45: The implant according to item 44, wherein the bulk porosity of the implant is 75% to 99%.

[0223] Item 46: The implant according to any one of Items 44 to 45, wherein the surface porosity of the implant is 30% to 80%.

[0224] Item 47: The implant according to any of Items 44 to 46, wherein the surface porosity of the implant is 40% to 70%.

[0225] Item 48: The implant according to any of Items 44 to 47, wherein the surface porosity of the implant is 50% to 60%.

[0226] Item 49: The density of the implant material is 0.1gr / cm 3 ~2gr / cm 3 49. The implant according to any one of items 44 to 48,

[0227] Item 50: The implant according to any of Items 44 to 48, wherein each unit cell in the plurality of unit cells is a spring-like unit cell, and the spring-like unit cell is reversibly compressible.

[0228] Item 51: The three-dimensional structure is a first outer surface region of the implant having a first surface curvature; a second outer surface region of the implant having a second surface curvature; a second outer surface region of the implant adjacent the first outer surface region of the implant at a periphery of the first outer surface region; 52. The implant according to any one of items 45 to 51, wherein the shape of the second outer surface region represents the shape of a breast to be constructed by the implant.

[0229] Item 52: The second outer surface region is an upper pole portion having a shape of an upper portion of a breast to be constructed by the implant; a lower pole portion having a shape of a lower portion of the breast to be constructed by the implant; Item 52. The implant of item 51, wherein the upper pole portion and the lower pole portion coincide at an apex region of the second outer surface region of the three-dimensional structure.

[0230] Item 53: An implant according to either of items 51 or 52, wherein the surface porosity of the second outer surface region is less than the surface porosity of the first outer surface region.

[0231] Item 54: An implant for insertion into a patient, the implant comprising: a porous three-dimensional scaffold structure including an array of unit cells; the plurality of unit cells are configured to form a three-dimensional porous network; The implant, wherein the unit cells in the three-dimensional structure have an average pore size of at least 0.5 mm.

[0232] Item 55: The implant of Item 54, wherein the average pore size of a plurality of unit cells in the three-dimensional structure is at least 3 mm.

[0233] Item 56: The implant of any of items 54 or 55, wherein the pore size of at least 50% of the unit cells in the three-dimensional structure is at least 0.5 mm.

[0234] Item 57: Three-dimensional structure a first outer surface region of the implant having a first surface curvature; a second outer surface region of the implant having a second surface curvature; the second outer surface region of the implant is adjacent to the first outer surface region of the implant at a periphery of the first outer surface region; and 57. The implant according to any one of items 54 to 56, wherein the shape of the second outer surface region represents the shape of a breast to be constructed by the implant.

[0235] Item 58: The second outer surface area is an upper pole portion having a shape of an upper portion of a breast to be constructed by the implant; a lower pole portion having a shape of a lower portion of the breast to be constructed by the implant; Item 58. The implant of item 57, wherein the upper pole portion and the lower pole portion coincide at an apex region of the second outer surface region of the three-dimensional structure.

[0236] Item 59: The implant according to any of Items 55 to 58, wherein the average pore size in the first outer surface region of the three-dimensional structure is at least 25% larger than the average pore size in the second outer surface region of the three-dimensional structure.

[0237] Item 60: The implant of any of items 58 or 59, wherein the average pore size in the first outer surface region of the implant is at least 8 mm.

[0238] Item 61: The pore size of the upper pole portion of the second outer surface region increases from 0.5 mm in the upper pole boundary region to 5 mm in the tip region of the second outer surface region; 59. The implant according to any of items 55 to 58, wherein the upper pole boundary region is a boundary region of a three-dimensional structure, and the upper pole portion of the second outer surface region intersects with a portion of the periphery of the first outer surface region.

[0239] Item 62: The pore size of the lower pole portion of the second outer surface region increases from 2 mm at the lower pole boundary region to a maximum of 6 mm toward the apex region of the second outer surface region; 62. The implant according to any of items 58 to 61, wherein the lower pole boundary region is a boundary region of a three-dimensional structure, and the lower pole portion of the second outer surface region intersects with a portion of the periphery of the first outer surface region.

[0240] Item 63: An implant according to any of items 54 to 62, wherein the pore size of the opening in the second outer surface region of the implant increases from 0.5 mm in the upper pole boundary region to 2 mm in the apex region of the second outer surface region.

[0241] Item 64: The implant according to any of items 54 to 63, wherein the pore size of the opening in the second outer surface region of the implant increases from 2 mm in the lower pole boundary region to a maximum of 6 mm toward the apex region.

[0242] Item 65: An implant for insertion into a patient, the implant comprising: a three-dimensional porous scaffold comprising a plurality of hollow channels extending between a first exterior surface region and a second exterior surface region of the three-dimensional porous scaffold; The porous scaffold comprises a surface degradable polymeric material; the first exterior surface region is configured to face a chest wall of a patient receiving the implant; The shape of the second outer surface region represents the shape of the breast to be constructed by the implant; and The implant, wherein the plurality of hollow grooves are configured to align with Cooper's ligaments of a patient receiving the implant.

[0243] Item 66: The three-dimensional porous scaffold comprises a plurality of outer layers disposed contiguously with one another, each outer layer of the array of layers comprising a lattice array of a plurality of two-dimensional unit cells; Item 66. The implant of item 65, wherein the two-dimensional unit cells in successive layers of the plurality of outer layers are configured to form a plurality of hollow channels extending between the first outer surface region and the second outer surface region of the three-dimensional porous scaffold.

[0244] Item 67: An implant described in either item 65 or 66, wherein the second outer surface region is adjacent to the first outer surface region at a periphery of the first outer surface region.

[0245] Item 68: The subject matter described in any of items 65 to 67, wherein the plurality of hollow grooves are inclined relative to the first outer surface region of the implant, and an acute inclination angle between the plurality of hollow grooves and a reference axis representing the first outer surface region is less than 60°.

[0246] Item 69: The subject matter described in any of Items 65 to 68, wherein the multiple hollow grooves are configured to converge toward a converging region, the converging region being located outside the first outer surface region or the second outer surface region in the three-dimensional structure.

[0247] Item 70: The second outer surface region has an upper pole portion having a shape of an upper part of a breast to be constructed by an implant; a lower pole portion having a shape of a lower portion of the breast to be constructed by the implant, the upper pole portion and the lower pole portion meeting at an apex region of the second outer surface region; 68. The subject matter of any of items 63-67, wherein one or more of the plurality of hollow grooves are configured to extend from the first exterior surface region toward at least one of the apex region of the second exterior surface region and the lower pole portion of the second exterior surface region.

[0248] Item 71: The implant described in Item 70, wherein one or more additional grooves of the plurality of hollow grooves are configured to extend from the upper pole portion of the second outer surface region toward at least one of the apex region and the lower pole portion of the second outer surface region.

[0249] Item 72: The bulk porosity of the implant is at least 50%, or at least 60%, or at least 70%, or at least 80%, and the total porosity is described by the formula:

number

[0250] Item 73: A method for forming an implant, the method comprising: printing successive layers to form a three-dimensional (3D) printed structure that defines a rest volume of the implant to be formed; Each printed layer comprises a lattice array of two-dimensional unit cells; The method, wherein the three dimensional printed structure has bulk porosity such that the three dimensional printed structure is compressible to at least 80% of its original volume.

[0251] Item 74: The method of item 73, wherein the average pore size of a plurality of unit cells in the three-dimensional structure is at least 0.5 mm.

[0252] Item 75: The step of successively printing layers includes: printing a first layer to form a first exterior region of a 3D scaffold structure; 75. The method according to any of items 73 or 74, comprising printing a successive layer on top of the first layer according to the printing direction, wherein an edge region of the successive layer forming a second outer surface region of the 3D scaffold structure is adjacent to the first outer surface region.

[0253] Item 76: The method of any of items 73 to 75, wherein the unit cells of the layer of the 3D scaffold structure form a plurality of hollow channels extending between the first and second outer surface regions of the three-dimensional structure.

[0254] Item 77: The method of any of items 73 to 76, wherein the layers are printed sequentially to form a plurality of three-dimensional unit cells in a three-dimensional (3D) printed scaffold structure.

[0255] Item 78: A method for forming an implant, the method comprising: printing (830) successive layers to form a three-dimensional (3D) printed structure that defines a rest volume of the implant to be formed; Each printed layer comprises a lattice array of two-dimensional unit cells; The method, wherein the three dimensional printed structure has bulk porosity such that the three dimensional printed structure is compressible to at least 80% of its original volume.

[0256] Item 79: A method for tissue reconstruction or augmentation, the method comprising the step of implanting into the body of a subject an implant as defined in any one of items 1 to 72 or produced by the method as defined in any one of items 73 to 78.

[0257] Item 80: The method according to item 79, comprising reconstruction of a body part.

[0258] Item 81: The method of item 80, wherein the body part is selected from the group consisting of the buttocks area, the calf, and a part of the face, chest, or genital area.

[0259] Item 82: The method according to Item 81, wherein the part of the face is a cheek.

[0260] Item 83: The method according to any of items 80 to 82, comprising chest reconstruction or breast reconstruction.

[0261] Item 84: The method of item 83, wherein the breast reconstruction is performed after lumpectomy or mastectomy.

[0262] Item 85: The method of item 83, wherein the chest reconstruction includes reconstruction of the chest or chest area of ​​the patient's body.

[0263] Item 86: The method of item 85, wherein the chest reconstruction includes treatment of congenital pectus excavatum.

[0264] Although detailed embodiments of the present invention have been described, it will be understood that the present invention, as defined by the appended claims, is susceptible of many easy modifications without departing from its spirit or scope, and is not to be limited by the specific details set forth above.

Claims

1. A soft tissue reconstruction implant (100, 200, 300, 400, 500) for insertion into a patient, the implant comprising: a plurality of repeating unit cells (102) connected to each other to form a three-dimensional lattice structure (101), said unit cells (102) being basic units of said three-dimensional lattice structure, said three-dimensional lattice structure comprising a quiescent volume of said implant; the plurality of unit cells (102) are configured to form a porous network of the three-dimensional lattice structure, the three-dimensional lattice structure (101) being a reversibly compressible three-dimensional lattice structure, the bulk porosity of the three-dimensional lattice structure (101) in the implant being at least 50%; a plurality of surface infills configured to form a plurality of surface infill columns in the exterior region; a plurality of open posts in said outer surface region that are devoid of surface filling.

2. 2. The implant of claim 1, wherein each unit cell in the plurality of unit cells is a reversibly compressible spring-like unit cell, and the three-dimensional lattice structure is compressible to at least 80% of its rest volume.

3. comprising layers of said unit cells successively deposited on top of one another; The implant of claim 1 or 2, wherein edge regions of the layers in the three-dimensional lattice structure form an outer surface region of the implant, the outer surface region representing the shape of a portion of the patient's body that is to be constructed by the implant.

4. The implant of any one of claims 1 to 3, wherein the average pore size of the openings in the first outer surface region (105) of the three-dimensional lattice structure (101) is at least 25% greater than the average pore size of the openings in the second outer surface region (106) of the three-dimensional lattice structure (101).

5. The three-dimensional lattice structure (101) is a first outer surface region (105) of said implant having a first surface curvature; a second outer surface region (106) of the implant having a second surface curvature; a second outer surface region (106) of the implant adjacent to a first outer surface region (105) of the implant at a periphery (107) of the first outer surface region (105); The implant according to any one of claims 1 to 4, wherein the shape of the second external surface area (106) represents the shape of the breast area, cheeks, buttocks or testicular area to be constructed by the implant.

6. The second outer surface region (106) is an upper pole portion (109) having the shape of the upper part of the breast to be constructed by the implant; a lower pole portion (111) having the shape of the lower portion of the breast to be constructed by the implant; 6. The implant of claim 5, wherein the upper pole portion (109) and the lower pole portion (111) coincide at an apex region (112) of the second outer surface region (106) of the three-dimensional lattice structure (101).

7. 7. The implant of claim 6, wherein the pore size of the openings in the second outer surface region (106) of the implant increases from 0.5 mm in the upper pole interface region (114) to 2 mm or 5 mm in the apex region of the second outer surface region and decreases from a maximum of 10 mm, or 8 mm, or 6 mm in the lower pole interface region (115) to 0.5 mm towards the apex region (112).

8. 7. The implant of claim 6, wherein the pore size of the openings in the second outer surface region (106) of the implant increases from 0.5 mm in the upper pole interface region (114) to 2 mm or 5 mm in the apex region of the second outer surface region and increases from 0.5 mm in the lower pole interface region (115) to a maximum of 6 mm, or a maximum of 8 mm, or a maximum of 10 mm towards the apex region (112).

9. The implant of any one of claims 4 to 8, wherein the surface porosity of the second exterior surface region is less than the bulk porosity of the three-dimensional lattice structure of the implant.

10. The material density of the implant is 0.1 gr / cm ３ ~2gr / cm ３ The implant according to any one of claims 1 to 9,

11. The three-dimensional lattice structure (101) is a first exterior region (105) comprising a first layer (126) of an array of layers (126); 11. The implant of any one of claims 1 to 10, wherein each layer (126) of the array of layers comprises a lattice array comprising a plurality of two-dimensional unit cells (102), the two-dimensional unit cells of successive layers of the array of layers forming a plurality of hollow channels (118) extending between a first outer surface region (105) and a second outer surface region (106) of the three-dimensional lattice structure.

12. a first group of contour lines (119) in a plurality of lines forming a complete contour around a periphery of the first outer surface region of the implant; and a second group of contour lines (121) in a plurality of lines; each contour line of the second group of contour lines (121) forms a semi-contour around a second outer surface region of the implant; The implant according to any one of claims 1 to 11, wherein the second group of contour lines (121) are arranged continuously with respect to each other between an apex region (112) of the first outer surface region (105) and the second outer surface region (106) of the implant.

13. An implant as described in any one of claims 1 to 12, wherein the surface filling portion (122) has one or more filling lines (124) configured to at least partially fill openings in the outer surface region of the three-dimensional lattice structure.

14. The c value representing the flexibility of the implant is 20N to 200N; The c value is represented by the following formula: [0010] F ２０％ is the force value in N at 20% compression, F １０％ is the force value in N at 10% compression, ε １０％ is the strain value at 10% compression, and ε ２０％ The implant according to any one of claims 1 to 13, wherein m is the strain value at 20% compression.

15. 1. A method (800) of forming a soft tissue reconstruction implant, the method comprising: printing (830) successive layers to form a three-dimensional (3D) printed lattice structure comprising repeating unit cells, the unit cells being a fundamental unit of the three-dimensional lattice structure, the 3D printed lattice structure defining a rest volume of the implant to be formed; Each printed layer comprises a lattice array of two-dimensional unit cells; the three dimensional printed lattice structure has a bulk porosity of at least 50% such that the three dimensional printed lattice structure is reversibly compressible; the plurality of surface infills are configured to form a plurality of surface infilling columns in the exterior surface region; The method, wherein the plurality of open posts in the exterior surface region are free of surface infills.