Lubricating greases containing metal soaps and metal complex soaps based on R-10-hydroxyoctadecanoic acid

Abstract

The present invention relates to lubricating greases based on alkali and / or earth alkali metal soaps and metal complex soaps based on R-10-hydroxyoctadecanoic acid, and to their uses.

Description

[Technical field]

[0001] The present invention relates to lubricating greases based on alkali metal soaps and / or alkaline earth metal soaps and metal complex soaps based on R-10-hydroxyoctadecanoic acid and to their uses. [Background technology]

[0002] In many technical applications or friction systems, it is important to use lubricants to reduce friction and wear at the contact surfaces of moving parts. Lubricants of different viscosities are available depending on the application. Lubricating oils have a liquid, flowable consistency, while lubricating greases have a semi-solid to solid, often gel-like, consistency. Lubricating greases are characterized by a liquid oil component that is entrapped and held by a thickener component. The pasty nature and dispersible and easily plastically deformable properties of lubricating greases, together with their adhesive properties, ensure that they wet the lubrication points and that the lubricating effect occurs at the surfaces subjected to tribological stress.

[0003] Lubricating greases generally contain a thickener homogeneously dispersed in a base oil. To ensure that the thickener is stably dispersed in the base oil, further additives such as emulsifiers are often used. A wide variety of substances are known as base oils. Organic and inorganic compounds are used as thickeners. Furthermore, additives are often added to lubricating greases to improve, inter alia, wear protection, friction properties, stability over time, and corrosion protection.

[0004] The most important viscoelastic properties of lubricating greases include the pour point and shear viscosity. Both have a significant impact on the efficiency of grease-lubricated drives or bearings, especially when elastohydrodynamic lubrication (EHL) is present at high sliding or rotational speeds. The pour point and shear viscosity have a significant impact on the so-called breakaway torque and running torque of grease-lubricated parts and buildups, especially at low application temperatures.

[0005] Grease is widely used for lubrication purposes in the automotive and aerospace industries. It has many advantages from a design and maintenance standpoint compared to oil. It is therefore used to lubricate many moving parts in passenger cars and aircraft where lubrication with oil is inadequate.

[0006] The viscoelastic properties of lubricating greases also have disadvantages, which are especially noticeable when operating lubricated parts at extremely low temperatures. When starting a generally cold vehicle (winter, arctic regions), the "breakaway torque" is particularly noticeable when grease-lubricated vehicle parts such as steering systems, sunroofs, window lifts, side mirror adjustments, or door locks have to be operated manually or with low servo-electrical drive forces. Thus, in the automotive industry, lubricating greases must usually function reliably up to temperatures of at least -40°C. In the aviation industry, lubricating greases must function reliably at temperatures as low as -54°C, and in some cases even at temperatures as low as -73°C. The lubricating greases of the wheel bearings in the landing gear must function normally when landing, even if the aircraft is at high altitude for a long time and the landing gear is exposed to extremely low temperatures. The "breakaway torque" of the aircraft lubricating greases must not exceed a certain value.

[0007] In many cases, the maximum torque design of grease-lubricated parts such as gears, plain or roller bearings, and all other types of tribological pairings is determined by the quality of the lubricating grease used for lubrication. The low pour point and shear viscosity at low temperatures reduce the breakaway torque and the rotational torque, allowing the designer to choose an assembly with a relatively low driving force. This plays a particularly important role in vehicles using electric drives, such as hybrid or fully electric vehicles. The use of lubricating greases with particularly low adhesion and sliding friction at lower application temperatures, such as -40°C, reduces the electric drive force and the demand for electricity due to the reduction in the starting torque and the rotational torque, which on the one hand increases the driving range of battery-powered vehicles and on the other hand allows the use of power cables with smaller cross-sectional areas, reducing the weight in the on-board supply system.

[0008] A high degree of practical experience is required to tailor a useful lubricating grease to the lubrication and equipment requirements.

[0009] Hydroxyoctadecanoic acid, especially 12-hydroxyoctadecanoic acid (12-hydroxystearic acid), is a fatty acid that has been used for some time in the production of metal soap greases, especially lithium soap greases and lithium complex soap greases. The starting material for 12-hydroxyoctadecanoic acid or its esters or triglycerides is ricinoleic acid ((9Z,12R)-12-hydroxy-9-octadecenoic acid) and its triglycerides, i.e. the so-called castor oil, which is mainly obtained from the castor plant. For this purpose, the unsaturated hydroxy fatty acid ricinoleic acid or its triglycerides is converted to a saturated hydroxy fatty acid by hydrogenation to make it stable in storage and to increase its thermal stability. At present, other hydroxyoctadecanoic fatty acids, such as 10-hydroxyoctadecanoic acid, are of little technical importance, although they are additionally frequently cited in intellectual property rights without being used in practice. Summary of the Invention [Problem to be solved by the invention]

[0010] Disadvantages of the Prior Art and Objectives of the Invention In particular in the production of lithium greases based on 12-hydroxyoctadecanoic acid, but also in the production of other metal soap greases, a relatively high content of metal soap is required as a thickener to obtain the desired consistency. This means that such lubricating greases can increase friction losses in rolling bearing and gear applications or other grease-lubricated friction systems. The aim of the present invention is to minimize the above-mentioned disadvantages in terms of efficiency and properties at low temperatures. [Means for solving the problem]

[0011] Summary of the Invention This object is achieved by the subject matter of the independent claims. Preferred embodiments are the subject matter of the dependent claims or are described below.

[0012] The lubricating grease composition according to the present invention comprises: (a) at least one base oil; (b) at least one additive; and (c) at least one thickening agent, which is or comprises a metal soap and / or metal complex soap formed from at least one alkali and / or alkaline earth metal ion and at least one carboxylate, which carboxylate is composed of C16 to C18 fatty acids, which include at least one 10-hydroxyoctadecanoic acid (R-10-hydroxystearic acid) having an enantiomeric purity for the R isomer of more than 80% by weight, preferably more than 90% by weight, in particular more than 98% by weight, and which metal complex soap, if used, comprises a complexing agent (hereinafter, in short, the metal soap and / or metal complex soap used in the present invention).

[0013] Surprisingly, it has been found that enzymatically produced R-10 hydroxyoctadecanoic acid with an enantiomeric purity of more than 80% exhibits particularly good thickening performance (100% = sum of R and S isomers). In the same base oil and additive matrix, the R-rich 10-hydroxyoctadecanoic acid thus produced clearly exhibited a thickening effect that was more than 50% better than that of, for example, 12-hydroxyoctadecanoic acid.

[0014] 10-Hydroxyoctadecanoic acid (10-hydroxystearic acid, CAS 638-26-6) can be produced enzymatically as previously described by G. Schroepfer in Biological Chemistry (1966), 241(22). Both the R and S forms can be used to produce lubricating greases.

[0015] The structural form of the R form is as follows: [ka]

[0016] The substrate for the enzymatic conversion is predominantly (9Z)-octadec-9-enoic acid (oleic acid), which can be produced, for example, from domestic "high oleic" sunflower oil with a purity of more than 92% (9Z)-octadec-9-enoic acid, and from industrial grades with a purity of more than 60% (9Z)-octadec-9-enoic acid. By-products in quality are polyunsaturated fatty acids, such as, for example, hexadecanoic acid (palmitic acid), hexadecenoic acid (palmitoleic acid), octadecanoic acid (stearic acid), or linoleic acid ((9Z,12Z)-octadeca-9,12-dienoic acid) or linolenic acid ((9Z,12Z,15Z)-octadeca-9,12,15-trienoic acid).

[0017] One advantage of this enzymatic method is the use of domestic feed ingredients and the expansion of the supply chain to include domestic starting material raw materials. In addition to "high oleic" sunflower oil, it is possible to use high-carbon wastes containing unsaturated C18 acids or esters, for example, for the production of 10-hydroxyoctadecanoic acid. In particular, high-carbon wastes can be used on the one hand as nutrients for enzyme production and on the other hand as "raw material" to yield the desired product. Used edible fats and oils, residues of biodiesel production (e.g., glycerol, fatty acids, methyl esters), as well as other industrial by-products can be used as the basis for material utilization.

[0018] 12-Hydroxyoctadecanoic acid (12-hydroxystearic acid, CAS 106-14-9) is commercially available, for example, from Sigma-Aldrich or Nidera BV. 12-Hydroxyoctadecanoic acid is chemically produced from castor oil by hydrolysis and hydrogenation. Castor oil is mainly produced in India, Brazil and China. The purity of commercially available 12-hydroxyoctadecanoic acid is usually 80-98% by weight.

[0019] In addition, a good thickening effect of R-10-hydroxyoctadecanoic acid is obtained when other fatty acids with a chain length of C16 to C18, such as, for example, hexadecanoic acid (palmitic acid) (C16:0), 9-hydroxyhexadecanoic acid, octadecanoic acid (stearic acid), (9Z)-octadec-9-enoic acid (oleic acid), or polyunsaturated fatty acids, such as, for example, linoleic acid ((9Z,12Z)-octadeca-9,12-dienoic acid) or linolenic acid ((9Z,12Z,15Z)-octadeca-9,12,15-trienoic acid) in the non-hydroxylated or hydroxylated form, are continuously used in the metal soap production, especially together with R-10-hydroxyoctadecanoic acid.

[0020] The C16 to C18 fatty acids for the preparation of the metal soaps and / or metal complex soaps used in the present invention are preferably further characterized, individually or jointly, as follows: the C16 to C18 fatty acids consist of more than 50% by weight, preferably more than 80% by weight, in particular more than 95% by weight, of 10-hydroxystearic acid; The C16 to C18 fatty acids in particular comprise more than 0.5% by weight, preferably more than 1.0% by weight, particularly preferably 1 to 10% by weight, of hexadecanoic acid. The C16 to C18 fatty acids in particular comprise more than 0.2% by weight, preferably more than 0.5% by weight, particularly preferably 1 to 10.0% by weight of hydroxyhexadecanoic acid, in particular 9-hydroxyhexadecanoic acid. The C16 to C18 fatty acids in particular comprise more than 0.2% by weight, preferably more than 0.5% by weight, particularly preferably 1 to 10.0% by weight, of octadecanoic acid. the C16 to C18 fatty acids in particular comprise more than 0.2% by weight, preferably more than 0.5% by weight, preferably from 1.0 to 10% by weight of octadecenoic acid, in particular (9Z)-octadec-9-enoic acid; The C16 to C18 fatty acids in particular comprise more than 0.2% by weight, preferably more than 0.5% by weight, particularly preferably 1 to 10% by weight of octadecadienoic acid, in particular (9Z,12Z)-octadeca-9,12-dienoic acid. the C16-C18 fatty acids comprise less than 1% by weight, preferably less than 0.2% by weight, of 12-hydroxy-9-octadecenoic acid, in particular (9Z,12R)-12-hydroxy-9-octadecenoic acid; the C16 to C18 fatty acids comprise less than 1% by weight, in particular less than 0.2% by weight, of 12-hydroxyoctadecanoic acid; -Hydroxy-substituted C16-C18 fatty acids are derived from the enzymatic conversion of the corresponding unsaturated C16-C18 fatty acids. The C16 to C18 fatty acids are obtained from edible fats, in particular from used edible fats, and / or from biodiesel, including at least one enzymatic conversion.

[0021] The metal soap and / or metal complex soap used in the present invention is, in particular, - Lithium soap or lithium complex soap, or - Lithium / calcium soap or lithium / calcium complex soap, or - Calcium soap or calcium complex soap.

[0022] Surprisingly, it has thus been found that lubricating greases based on R-10-hydroxyoctadecanoic acid have a significantly lower thickener content at the same consistency, preferably requiring at least 30% by weight less thickener and at least 30% by weight less lithium hydroxide monohydrate in the preparation.

[0023] The lubricating greases produced in this manner have significantly lower flow pressures, lower pour points, and significantly lower breakaway torques, especially at low temperatures, in plain bearings, roller bearings, and gears. The reduced use of lithium hydroxide monohydrate, especially in the case of lithium soap and lithium complex soap greases, can reduce production costs.

[0024] Also, in the case of lithium soap thickened lubricating greases, the use of R-10 hydroxyoctadecanoic acid instead of 12-hydroxyoctadecanoic acid significantly reduces the cost of using the Li salt, since up to 62% less lithium hydroxide monohydrate is required to form the lithium hydroxyoctadecanoate soap, which is a significant cost factor in grease production, especially against the background of increasing lithium demand in battery production and electric vehicles.

[0025] Preferably, the lithium R-10-hydroxyoctadecanoate soap is prepared in situ, i.e., by reacting lithium hydroxide monohydrate with R-10-hydroxyoctadecanoic acid, but lithium 10-hydroxyoctadecanoate prepared in a separate step can also be mixed into the base oil and thickened by subsequent thermal and mechanical treatment.

[0026] It can also be shown that in the case of steel / steel contact, the sliding friction coefficient of lubricating greases based on R-10-hydroxyoctadecanoic acid is, for example, up to 37% lower than that of comparable lubricating greases based on 12-hydroxyoctadecanoic acid. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0027] The composition of the present invention comprises at least (a) preferably from 55 to 98% by weight, in particular from 70 to 97% by weight, of a base oil or a base oil mixture, preferred base oils being, for example, polyalphaolefins, mineral oils, and / or esters, (b) preferably 0.5 to 40% by weight, in particular 2 to 20% by weight, of an additive, (c) It contains a thickener, and the thickener is or contains a metal soap or metal complex soap containing R-10 hydroxyoctadecane metal soap, and the metal soap or metal complex soap used in the present invention (including a complexing agent) used in the present invention is preferably contained in an amount of 1.5 to 25% by weight, preferably 3 to 10% by weight, or 1.5 to 40% by weight of the metal complex soap (in the metal soap), contains 0.1 to 20% by weight of a complexing agent, preferably 0.1 to 10% by weight of a complexing agent, and the metal soap salt used in the production is an alkali metal hydroxide and / or an alkaline earth hydroxide (the metal soap used in the present invention).

[0028] The weight percentages specified relate to the total composition and each applies independently of the other.

[0029] Standard lubricating oils which are liquid at room temperature are suitable as base oils. In particular, the base oils have a viscosity of 14 to 2500 mm at 40°C in each case. 2 / s, preferably 30 to 500 mm 2 / s kinematic viscosity.

[0030] Base oils can be classified as mineral or synthetic oils. Mineral oils are considered to be naphthenic and paraffinic mineral oils in the API Group I classification. Also suitable are chemically modified low aromatic and low sulfur mineral oils classified according to API Groups II, III, III+, which have a low content of saturates and improved viscosity / temperature properties compared to Group I oils, as well as synthetic oils produced from natural gas in the so-called Gas-to-Liquids process (GTL oils).

[0031] Examples of synthetic oils are di- or polyethers, esters, polyalphaolefins, polyglycols, and alkylaromatic compounds, and mixtures thereof. Diether compounds can be compounds with aliphatic and / or aromatic residues (e.g., alkylated diphenyl ethers). Polyether compounds can have free hydroxyl groups, but they can also be fully etherified or end-group esterified, and / or made from starting compounds with one or more hydroxy and / or carboxyl groups (-COOH). Also, diphenyl ethers or polyphenyl ethers, alkylated as appropriate, can be the only component, or more preferably, the mixed component. Suitable esters are esters of aromatic di-, tri- or tetracarboxylic acids with one or a mixture of C2-C30 alcohols, esters of adipic acid, sebacic acid, trimethylolpropane, neopentyl glycol, pentaerythritol or dipentaerythritol with aliphatic, branched or unbranched, saturated or unsaturated C2-C22 carboxylic acids, C18 dimer acid esters with C2-C22 alcohols, complex esters, either as individual components or in any desired mixture.

[0032] Particularly suitable base oils are or contain polyalphaolefins, for example those resulting from polymerizing C4 and C14 LAO (LAO=linear alpha olefin), C6 and C16 LAO, C8, C10 and C12 LAO, C8 and C14 LAO, C6, C10 and C14 LAO, C4 and C12 LAO, optionally with the aid of metallocene catalysts, as copolymers or as mixtures of the respective homopolymers.

[0033] It has further been found that, in contrast to conventional 12-hydroxyoctadecanoate metallic greases, lubricating greases based on metallic R-10-hydroxyoctadecanoates, especially in base oils containing or consisting of polyalphaolefins, exhibit unexpected advantages in terms of low temperature properties and efficiency, in which the soaps used in the present invention differ significantly from conventional 12-hydroxyoctadecanoate soaps.

[0034] Optionally, in addition to the C16-C18 fatty acids as mentioned above, other fatty acids can also be reacted with metal salts, such as metal hydroxides, to obtain further metal soaps. These may be alkali or alkaline earth salts of one or more saturated or unsaturated monocarboxylic acids having 10-15 and / or 19-24 carbon atoms, optionally substituted as in the preferred corresponding hydroxycarboxylic acids. Suitable carboxylic acids are, for example, lauric acid, myristic acid or behenic acid. In addition to the fatty acids with unbranched chains mentioned, fatty acids with branched chains, saturated or unsaturated, can also be used. Also naphthenic acid, neodecanoic acid or equivalent neo acids can also be used.

[0035] Also, simple, mixed or complex soaps based on Al-, Bi-, Ti-salts and carboxylic acids, or Li-, Na-, Mg-, Ca-, Al-, Bi-, Ti-salts and sulfonic acids can be added as further metal soaps during the preparation of the base fat or later as additives, or these soaps can also be formed in situ during the preparation of the metal soaps used in the present invention.

[0036] Instead of fatty acids with free acid groups, suitable triglycerides of acids / hydroxy acids and suitable saponified lower alcohol esters, such as methyl-, ethyl-, propyl-, isopropyl- or sec-butyl acetate, can also be used in the preparation of the respective metal soaps to obtain better dispersion.

[0037] In the embodiment of the metal complex soap, in addition to the metal soap already described, a complexing agent is used in the preparation. The complexing agent within the meaning of the present invention is (a) optionally substituted in each case alkali and / or alkaline earth salts of saturated or unsaturated monocarboxylic or further hydroxycarboxylic acids having 2 to 8, in particular 2 to 4, carbon atoms, or alkali and / or alkaline earth salts of dicarboxylic acids having 2 to 16, in particular 2 to 12, carbon atoms, and / or (b) reaction products of alkali or alkaline earth salts of boric acid and / or phosphoric acid, in particular with LiOH and / or Ca(OH)2, or reaction products of alkali or alkaline earth hydroxides, in particular with LiOH and / or Ca(OH)2, and / or esters of boric acid or phosphoric acid, and / or (c) Boric and phosphoric acid esters having unbranched or branched alkyl groups having 2 to 32 carbon atoms, preferably 8 to 32 carbon atoms. Preferably, the complexing agent is (a).

[0038] Particularly suitable monocarboxylic acids are acetic acid and propionic acid. Also suitable are hydroxybenzoic acids, such as parahydroxybenzoic acid, salicylic acid, 2-hydroxy-4-hexylbenzoic acid, metahydroxybenzoic acid, 2,5-dihydroxybenzoic acid (gentisic acid), 2,6-dihydroxybenzoic acid (gamma-resorcylic acid) or 4-hydroxy-4-methoxybenzoic acid. Particularly suitable dicarboxylic acids are adipic acid (CH 10 O4), Sebacic acid (C 10 H 18 O4), azelaic acid (C9H 16 O4), and / or 3-tert-butyl adipic acid (C 10 H 18 O4).

[0039] For example, orthoborates such as metaborates, diborates, tetraborates or monolithium orthoborates can be used as borates (b). Possible phosphates are the dihydrogen phosphates, hydrogen phosphates or pyrophosphates of the alkali (preferably lithium) and alkaline earth (preferably calcium) or calcium or lithium hydroxyapatites. The esters of boric and phosphoric acid can have unbranched or branched alkyl groups with 2 to 32, preferably 8 to 32 carbon atoms.

[0040] Optionally, bentonites, such as montmorillonites (wherein the sodium ions may be replaced or partially replaced by organically modified ammonium ions, if desired), aluminosilicates, aluminas, hydrophobic and hydrophilic silicas, oil-soluble polymers (e.g. polyolefins, poly(meth)acrylates, polyisobutylene, polybutene, or polystyrene copolymers), polyureas, or polyurea-polyurethanes, or PTFE, may also be used as auxiliary thickeners. Bentonites, aluminosilicates, aluminas, silicas, and / or oil-soluble polymers may be added to produce the base fat or added later as additives in a second step.

[0041] Lignin derivatives can also be added as auxiliary thickeners or additives during or after the production of the metal or metal complex soaps. Lignin derivatives are effective components in lubricating greases and can be used to improve wear protection and corrosion load properties.

[0042] In that respect, lignin derivatives represent multifunctional components. Due to their large number of polar groups and aromatic structures, their polymeric structure and their low solubility in all kinds of lubricating oils, powdered lignin and / or lignosulfonates are also suitable as solid lubricants in lubricating greases and pastes. Furthermore, the phenolic hydroxy groups contained in lignin and lignosulfonates provide an anti-aging effect. In the case of lignosulfonates, the sulfur content in the lignosulfonates promotes the EP / AW effect in the grease. Preferably, lignin and / or calcium and / or sodium lignosulfonates or mixtures thereof are used. However, kraft lignin, soda lignin or organosol lignin can also be used. The addition of biologically based oligomers or polymers, such as triterpenes, cellulose or modified cellulose, chitin and / or chitosan, as solid lubricants or auxiliary thickeners is also possible.

[0043] In particular, thickeners (metal soaps according to the invention, further metal soaps and auxiliary thickeners) are used so that the composition contains sufficient thickener to obtain a cone consistency value (worked consistency) of 210 to 475 mm / 10 (at 25° C.), preferably 230 to 385 mm / 10 (at 25° C.) (measured according to DIN ISO 2137 or ASTM D 0217-97).

[0044] The composition according to the invention may further contain additives as further substances. Typical additives within the meaning of the invention are antioxidants, antiwear agents, corrosion inhibitors, detergents, pigments, lubricity promoters, adhesion promoters, viscosity additives, friction modifiers, high pressure additives and metal deactivators.

[0045] Examples of these are: Primary antioxidants, such as amine compounds (e.g. alkylamines or 1-phenyl-aminonaphthalene), aromatic amines such as phenyl-naphthylamine or diphenylamine, or polymeric hydroxyquinolines (e.g. TMQ), phenolic compounds (e.g. 2,6-di-tert-butyl-4-methylphenol), zinc dithiocarbamates, or zinc dithiophosphates. Secondary antioxidants, for example phosphites, such as tris(2,4-di-tert-butylphenyl phosphite), or bis(2,4-di-tert-butylphenyl)-pentaerythritol diphosphite. High pressure additives, such as organic chlorine compounds, sulfur or organic sulfur compounds, phosphorus compounds, inorganic or organic boron compounds, zinc dithiophosphates, organic bismuth compounds. Active ingredients that improve "oiliness" such as C2-C6 polyols, fatty acids, fatty acid esters, or animal or vegetable oils. Corrosion inhibitors, for example, petroleum sulfonates, dinonylnaphthalene sulfonates, or sorbitan esters; disodium sebacate; metal deactivators such as neutral or overbased calcium sulfonates, magnesium sulfonate, sodium sulfonate, calcium and sodium naphthalene sulfonates, calcium salicylates, amine phosphates, succinates, benzotriazoles or sodium nitrite. Viscosity enhancers, such as polymethacrylates, polyisobutylenes, oligo-dec-1-enes, polystyrenes. Wear protection additives and friction modifiers, such as organomolybdenum complexes (OMC), molybdenum-di-alkyl-dithiophosphates, molybdenum-di-alkyl-dithiocarbamates, or molybdenum-di-alkyl-dithiocarbamates, in particular molybdenum-di-n-butyl-dithiocarbamate and molybdenum-di-alkyl-dithiocarbamates (Mo 2m Sn(dialkyl-carbamate)2, where m=0-3 and n=4-1), zinc dithiocarbamate, or zinc dithiophosphate; or a trinuclear molybdenum compound corresponding to the formula: Mo3Sk L n Q z where L is an independently selected ligand having an organic group containing carbon atoms as disclosed in US Pat. No. 6,172,013 to render the compound soluble or dispersible in oil, n is in the range of 1 to 4, k is in the range of 4 to 7, Q is selected from the group of neutral electron donor compounds consisting of amines, alcohols, phosphines, and ethers, z is in the range of 0 to 5, including non-stoichiometric values ​​(see DE 102007048091 A1). Friction modifiers, for example organic compounds based on functional polymers, such as oleylamide, polyethers and amides, such as alkyl polyethylene glycol tetradecylene glycol ethers, polyisobutylene succinimides, polyisobutylene succinimides (PIBSI) or polyisobutylene succinic anhydrides (PIBSA). Furthermore, the lubricating grease composition according to the invention contains the usual additives for protection against corrosion and oxidation and against the effects of metals acting as chelating compounds, radical scavengers, UV converters, reactive layer formers, etc. Additives such as carbodiimides or epoxides which improve the resistance of the ester base oils to hydrolysis can be added. Solid lubricants which can be used are, for example, polymer powders such as polyamides, polyimides or PTFE, melamine cyanurate, graphite, metal oxides, boron nitride, silicates such as magnesium silicate hydrate (talcum), sodium tetraborate, potassium tetraborate, metal sulfides such as molybdenum disulfide, tungsten disulfide or mixed sulfides based on tungsten, molybdenum, bismuth, tin and zinc, inorganic salts of alkali and alkaline earth metals such as calcium carbonate, sodium phosphate and calcium phosphate. Similarly, carbon black or other carbon-based solid lubricants, such as nanotubes, can be used. Lignin derivatives can also be used as thickener components or solid lubricants. Biologically based oligomers or polymers, such as triterpenes, modified cellulose, chitin, chitosan, or polypeptides, are also possible.

[0046] The lubricating greases according to the invention are particularly suitable for use in plain and roller bearings, gears and / or constant velocity joint shafts in industrial and automotive applications. It is a particular aspect of the invention to obtain low-friction lubricating greases, especially at low temperatures, when low breakaway and running torques are required and low pour points and shear viscosities are advantageous. In the particular case of lubrication of plain and roller bearings, and gears and constant velocity joint shafts in the automotive industry, smaller and lighter drives can thus be used, with efficiency advantages. The lubricating greases produced according to the invention have pour points (measured with an oscillatory rheometer according to DIN 51810-2) up to 43% lower and shear viscosities (measured with a shear viscometer according to DIN 51810-1) up to 50% lower than comparable lubricating greases, especially at -35°C. In the flow pressure test according to DIN 51805-2, the lubricating greases produced according to the invention show values ​​at -40°C that are at least 50% lower than comparable lubricating greases. Furthermore, the lubricating greases according to the invention have a sliding friction coefficient in steel / steel contact that is up to 37% lower than that of comparable lubricating greases based on 12-hydroxyoctadecanoic acid.

[0047] Various laboratory test methods are available for testing the pour point and shear viscosity of lubricating greases. One method for measuring the pour point using an oscillatory rheometer is DIN 51810-2. The flow pressure method according to DIN 51805-2 is also used to measure the low service temperature of lubricating greases. The flow pressure is the pressure difference from the ambient pressure required to extrude a grease line from a test nozzle under the conditions specified in this standard. This is a measure of the hardness of the lubricating grease at the respective test temperature and can be used in addition to the test according to DIN 51810-2 as a measure of the pour point.

[0048] IP186 and ASTM D1478 describe the measurement of starting and running torque of ball bearings. These test methods allow the functionality of lubricating greases to be tested at low temperatures, e.g. -40°C or -73°C.

[0049] These test methods are therefore part of numerous standards and user standards for the automotive and aerospace industries (civil and military aircraft). They have proven to be useful test methods for many years. Furthermore, DIN 51805-2 for flow pressure measurement is primarily used in Germany as the national method for determining the low service temperatures of lubricating greases.

[0050] Lubricating greases can be prepared, for example, by mixing a salt / metal compound with a carboxylic acid compound (which may optionally be extended with a complexing agent and optionally with a base oil component), optionally simultaneously heating the mixture to a temperature above 100° C., in particular above 170° C., to form a viscous lubricating grease product, cooling the lubricating grease product, and optionally adding water, subjecting the mixture to shear forces, for example in a toothed colloid mill, a high pressure homogenizer, and / or a three-roll mill. In a further embodiment of the invention, the thickener is synthesized in situ in the base oil under pressure and at elevated temperature in a closed reaction vessel such as an autoclave.

[0051] The lubricating grease composition can be used to lubricate gears, constant velocity joint shafts, plain and roller bearings, sliding guides, spindle drives, linear drives, ball screws, especially at low operating temperatures below -20°C and / or in automobiles, aircraft, drones or helicopters. Other applications include the lubrication of steering systems, sunroofs, window lifts, side mirror adjustments, door locks, bearings for chassis wheels, especially in automobiles, aircraft, drones or helicopters. The lubricating grease composition is also suitable for lubricating bearings for electric motors, especially in hybrid or fully electric vehicles. EXAMPLES

[0052] Demonstration Examples Example A (reference) Lithium-12-hydroxyoctadecanoate fatty acid with polyalphaolefins 171 g of polyalphaolefin (PAO6:PAO150=3:1 mixture) and 45.25 g of 12-hydroxyoctadecanoic acid as racemate were placed in a stirred tank reactor and heated to 86° C. Then, 6.31 g of lithium hydroxide monohydrate, previously dissolved in 25 g of distilled water, was added. The material was then heated to 210° C., cooled to below 100° C. for 20 minutes, and the additives were added.

[0053] The lubricating grease was then homogenized on a three-roll mill and adjusted to the desired consistency by gradually adding additional polyalphaolefin. The lubricating grease thus produced had a thickener content of 12.13% by weight and a worked consistency of 332 0.1 mm.

[0054] Examples B1, B2, B3 (invention) Lithium-10-hydroxyoctadecanoate fatty acid with polyalphaolefins 171 g of polyalphaolefin (a 3:1 mixture of PAO6 (metallocene based):PAO150) and 35.16 g of R-10-hydroxyoctadecanoic acid were placed in a stirred tank reactor and heated to 91° C. Then, 5.07 g of lithium hydroxide monohydrate, previously dissolved in 21 g of distilled water, was added. The material was then heated to 210° C., before being cooled to below 100° C. for 20 minutes and additives were added. The lubricating grease was then homogenized on a three-roll mill and adjusted to the desired consistency by gradually adding more polyalphaolefin. The lubricating greases thus produced had thickener contents of 4.64% by weight (B1), 4.97% by weight (B2), and 5.06% by weight (B3) and worked consistencies of 339 0.1 mm (B1), 332 0.1 mm (B2), and 320 0.1 mm (B3).

[0055] Example C (reference) Lithium-12-hydroxyoctadecanoic acid complex fat with polyalphaolefins 171 g of polyalphaolefin (PAO6:PAO150=3:1 mixture) and 45.25 g of 12-hydroxyoctadecanoic acid as racemate were placed in a stirred tank reactor and heated to 91° C. Then, 6.31 g of lithium hydroxide monohydrate, previously dissolved in 25 g of distilled water, were added. The material was then heated to 210° C. and cooled to below 122° C. for 15 minutes. Then, 1.25 g of (tris(2-ethylhexyl)orthoborate was added, cooled to below 100° C., and additives were added. The lubricating grease was then homogenized on a three-roll mill and adjusted to the desired consistency by gradually adding more polyalphaolefin. The grease thus produced had a thickener content of 10.52% by weight and a mixed consistency of 328 0.1 mm, as well as a dropping point above 300° C.

[0056] Example D (Invention) Lithium R-10-hydroxyoctadecanoate complex fat with polyalphaolefins 171 g of polyalphaolefin (a 3:1 mixture of PAO6:PAO150) and 35.16 g of R-10-hydroxyoctadecanoic acid were placed in a stirred tank reactor and heated to 91°C.

[0057] Then, 5.07 g of lithium hydroxide monohydrate, previously dissolved in 21 g of distilled water, was added. The material was then heated to 210° C. and then cooled to less than 122° C. for 15 minutes. Then, 1.19 g of (tris(2-ethylhexyl)orthoborate was added, cooled to less than 100° C., and additives were added. The lubricating grease was then homogenized on a three-roll mill and adjusted to the desired consistency by gradually adding more polyalphaolefin. The grease thus produced had a thickener content of 4.68% by weight and a worked consistency of 335 0.1 mm, and a dropping point of 293° C.

[0058] Example E (reference) Lithium-12-hydroxyoctadecanoate fatty acid with mineral oil 107.48 g of mineral oil, Group II (kinematic viscosity = 110 mm at 40°C) 2 22.08 g of 12-hydroxyoctadecanoic acid (racemic) were placed in a stirred tank reactor and heated to 91° C. Then, 3.18 g of lithium hydroxide monohydrate, previously dissolved in 15 g of distilled water, were added. The material was then heated to 210° C., then cooled to below 100° C. for 20 minutes, and the additives were added. The lubricating grease was then homogenized on a three-roll mill and adjusted to the desired consistency by gradually adding more mineral oil, Group II SN600. The lubricating grease thus produced had a thickener content of 8.3% and a worked consistency of 317 0.1 mm.

[0059] Example F (Invention) Lithium-10-hydroxyoctadecanoate fatty acid with mineral oil 107.12 g of mineral oil, Group II (kinematic viscosity = 110 mm at 40°C) 222.04 g of R-10-hydroxyoctadecanoic acid were placed in a stirred tank reactor and heated to 91° C. Then, 3.17 g of lithium hydroxide monohydrate, previously dissolved in 15 g of distilled water, were added. The material was then heated to 210° C., then cooled to below 100° C. for 20 minutes, and the additives were added. The lubricating grease was then homogenized on a three-roll mill and adjusted to the desired consistency by gradually adding more mineral oil, Group II SN600. The lubricating grease thus produced had a thickener content of 4.21% by weight and a worked consistency of 328 0.1 mm.

[0060] Example G (Reference) Lithium-12-hydroxyoctadecanoate fatty acid with ester oil 107.48 g of pentaerythritol ester (96 mm at 40°C) 2 12.08 g of 12-hydroxyoctadecanoic acid (viscosity of 1.0 g / s) was placed in a stirred tank reactor and heated to 91°C.

[0061] Then, 3.18 g of lithium hydroxide monohydrate, previously dissolved in 15 g of distilled water, was added. The material was then heated to 210° C., then cooled to below 100° C. for 20 minutes, and the additives were added. The lubricating grease was then homogenized on a three-roll mill and adjusted to the desired consistency by gradually adding more pentaerythritol ester. The lubricating grease thus produced had a thickener content of 6.13% and a worked consistency of 328 0.1 mm.

[0062] Example H (Invention) Lithium R-10-hydroxyoctadecanoate fatty acid with ester oil 107.12 g of pentaerythritol ester (96 mm at 40°C) 222.04 g of 12-hydroxyoctadecanoic acid (viscosity of 1.0 g / s) were placed in a stirred tank reactor and heated to 91° C. Then, 3.17 g of lithium hydroxide monohydrate, previously dissolved in 15 g of distilled water, were added. The material was then heated to 210° C., before being cooled to below 100° C. for 20 minutes and the additives were added. The lubricating grease was then homogenized on a three-roll mill and adjusted to the desired consistency by gradually adding more pentaerythritol ester. The lubricating grease thus produced had a thickener content of 4.08% by weight and a worked consistency of 335 0.1 mm.

[0063] In the same base oil and additive matrix, the lubricating greases according to the present invention made with R-10-hydroxyoctadecanoic acid showed up to 62% better thickening effect than those with 12-hydroxyoctadecanoic acid.

[0064] 1 shows a table of examples. [Table 1] JPEG0007623296000003.jpg218128 [Table 2] JPEG0007623296000005.jpg236128 [Table 3] JPEG0007623296000007.jpg245164 [Table 4] JPEG0007623296000009.jpg253169

Claims

1. (a) at least one base oil; (b) at least one additive; and (c) at least one thickening agent; the at least one thickening agent is a metal soap and / or metal complex soap comprised of at least one alkali or alkaline earth metal ion and / or at least one carboxylate formed from a C16-C18 fatty acid, the C16-C18 fatty acid comprising at least R-10-hydroxyoctadecanoic acid, the 10-hydroxyoctadecanoic acid having an enantiomeric purity for the R isomer of greater than 80% by weight; the C16-C18 fatty acids consist of greater than 50% by weight of 10-hydroxyoctadecanoic acid; (a) 55 to 98 wt. % of said base oil; (b) 0.5 to 40% by weight of said additive, and (c1) 1.5 to 25% by weight of said metal soap, or (c2) 1.5 to 40% by weight of the metal complex soap containing 0.1 to 20% by weight of a complexing agent, or (c3) A lubricating grease composition comprising both 1.5 to 25% by weight of said metal soap and 1.5 to 40% by weight of said metal complex soap containing 0.1 to 20% by weight of said complexing agent.

2. (i) the C16 to C18 fatty acids consist of greater than 80% by weight of 10-hydroxyoctadecanoic acid; or (ii) The lubricating grease composition according to claim 1, wherein the 10-hydroxyoctadecanoic acid has an enantiomeric purity for the R isomer of greater than 90% by weight, or satisfies both (i) and (ii) above.

3. 3. The lubricating grease composition according to claim 1 or 2, wherein the C16 to C18 fatty acids comprise more than 0.5 wt.% hexadecanoic acid.

4. 4. The lubricating grease composition according to claim 1, wherein the C16 to C18 fatty acids comprise more than 0.2 wt.% of hydroxyhexadecanoic acid.

5. 5. The lubricating grease composition according to any one of claims 1 to 4, wherein the C16 to C18 fatty acids comprise more than 0.2 wt.% of octadecanoic acid.

6. A lubricating grease composition according to any one of claims 1 to 5, wherein the C16 to C18 fatty acids comprise more than 0.2 wt.% of octadecenoic acid.

7. A lubricating grease composition according to any one of claims 1 to 6, wherein the C16 to C18 fatty acids comprise more than 0.2 wt% of octadecadienoic acid.

8. A lubricating grease composition according to any one of claims 1 to 7, wherein the C16 to C18 fatty acids comprise less than 1 wt% of 12-hydroxy-9-octadecenoic acid.

9. A lubricating grease composition according to any one of claims 1 to 8, wherein the C16 to C18 fatty acids comprise less than 1 wt% of 12-hydroxyoctadecanoic acid.

10. 10. The lubricating grease composition according to any one of claims 1 to 9, wherein the C16 to C18 fatty acids comprise hydroxy-substituted C16 to C18 fatty acids obtained from the enzymatic conversion of corresponding unsaturated C16 to C18 fatty acids.

11. A lubricating grease composition according to any one of claims 1 to 10, wherein the C16 to C18 fatty acids are obtained from edible fats, including at least one enzymatic conversion.

12. The metal soap or metal complex soap is - Lithium soap or lithium complex soap, or A composition according to any one of claims 1 to 11, which is a lithium / calcium soap or a lithium / calcium complex soap.

13. The complexing agent is (i) optionally substituted in each occurrence, (a) of a saturated or unsaturated monocarboxylic acid or hydroxycarboxylic acid having 2 to 8 carbon atoms, or (b) an alkali or alkaline earth salt, or both, of a dicarboxylic acid having from 2 to 16 carbon atoms, or (ii) an alkali or alkaline earth salt of boric acid or phosphoric acid, or a reaction product of an alkali or alkaline earth hydroxide with an ester of boric acid or phosphoric acid, or (iii) esters of boric or phosphoric acid having unbranched or branched alkyl groups having 2 to 32 carbon atoms, or (iv) A lubricating grease composition according to any one of claims 1 to 12, selected from mixtures of (i) to (iii) above.

14. The composition comprises: (a) 70 to 95 wt. % of said base oil, (b) 2 to 20% by weight of said additive, and (c1) 3 to 10% by weight of said metal soap, or (c2) 1.5 to 40% by weight of the metal complex soap containing 0.1 to 10% by weight of the complexing agent, or (c3) The composition according to any one of claims 1 to 13, comprising both 3 to 10% by weight of the metal soap and 1.5 to 40% by weight of the metal complex soap containing 0.1 to 10% by weight of the complexing agent.

15. 15. The lubricating grease composition according to any one of the preceding claims, comprising a further metal soap or a further metal complex soap of a saturated or unsaturated mono- or hydroxycarboxylic acid having from 10 to 15 and / or from 19 to 24 carbon atoms, optionally comprising a complexing agent.

16. 16. The lubricating grease composition according to any one of the preceding claims, further comprising an auxiliary thickener selected from one or more members of the group: aluminosilicates, alumina, hydrophobic and hydrophilic silica, polymers, di / polyureas, di / polyurea polyurethanes, and PTFE.

17. 17. The lubricating grease composition according to any one of the preceding claims, wherein the composition has a cone consistency value as worked consistency, measured according to ISO 2137, of 210 to 475 mm / 10 (at 25°C).

18. The base oil has a viscosity of 14 to 2500 mm at 40° C. ２ The lubricating grease composition according to any one of claims 1 to 17, having a kinematic viscosity of 1 / 2 g / s.

19. The additive is - antioxidants, - high pressure additives, - C2-C6 polyols, fatty acids, fatty acid esters or animal or vegetable oils, - corrosion inhibitors, - metal deactivators, - viscosity enhancers, - wear protection additives, - Friction modifiers, and - solid lubricants.

20. Use of a lubricating grease composition according to any one of claims 1 to 19 for lubricating a gear, a constant velocity joint shaft, a plain bearing, a roller bearing, a sliding guide, a spindle drive, a linear drive, or a ball screw.

21. Use of a lubricating grease composition according to any one of claims 1 to 19 for lubricating a steering system, a sunroof, a window lifting device, a side mirror adjustment device, a door lock, or a chassis wheel bearing.

22. Use of a lubricating grease composition according to any one of claims 1 to 19 for lubricating electric motor bearings.

23. (a) at least one base oil; (b) at least one additive; and (c) a method for preparing a lubricating grease composition according to at least one of claims 1 to 19 by combining with at least one thickener which is a metal soap or metal complex soap composed of alkali or alkaline earth metal ions and R-10-hydroxyoctadecanoic acid, said metal soap or metal complex soap being prepared in said base oil while heating to at least 170°C, and said additive being added after cooling below 100°C.