Modifying rheology and mechanical paths for improved 3D printing of soft materials

Abstract

Methods and systems for additive manufacturing are provided. The method includes depositing a structural material onto a support material 808 through a nozzle 810 by applying a structural material to the support material such that the structural material flows through the nozzle. The structural material includes a polymer and a rheology modifier. Deposition of the structural material is repeated 814 as needed to create the object. The support material is at least partially removed from the object. In various examples, the method includes changing printing parameters from a first portion of the object to a second portion of the object, moving the nozzle away from a previously deposited layer of the object when repositioning for deposition of a subsequent layer of the object, or a combination thereof.

Description

[Technical field]

[0001] <Government support> This invention was made with Government support under Government Contract No. DGE1745016 awarded by the National Science Foundation. The Government has certain rights in this invention.

[0002] <Priority Claim> This application claims priority to U.S. Provisional Patent Application No. 62 / 973,696, filed October 18, 2019, which is incorporated by reference in its entirety. [Background technology]

[0003] There are materials that are difficult to adapt for use in additive manufacturing. For example, heat-cured thermoset polymers such as epoxies and silicones are widely used in many applications due to their combination of mechanical properties, chemical resistance, and thermal stability. However, these thermoset polymers are often two-part systems that are mixed and then can take minutes to hours to crosslink and fully cure. These thermoset polymers can be kept in a liquid state for extended periods of time. Thus, these thermoset polymers can be a challenge to additively manufacture with high fidelity, as they can flow and may not retain their intended geometries. In addition, extrusion-based direct ink writing (DIW) and fused deposition modeling (FDM) can have problems printing geometries such as overhangs and / or other free-standing structures that are difficult to print without the use of a support. These constraints on the materials and geometries that can be additively manufactured present a challenge. Summary of the Invention

[0004] In one general aspect, the present invention is directed to an additive manufacturing method. The method includes, in various embodiments, depositing a construction material onto a support material by a nozzle by applying a force to the construction material to cause the construction material to flow through the nozzle. The construction material can include a yield stress, a thixotropic property, an increase in viscosity due to a rheology modifier, or a combination thereof. Applying a force to the construction material can include applying a force of at least a yield stress to the construction material, applying a force to cause the construction material to flow through the nozzle, or a combination thereof. In certain examples, the force is at least a yield stress of the construction material, and the yield stress of the construction material is in a range of 1 Pa to 10 kPa, such as, for example, 10 Pa to 200 Pa. The construction material includes a polymer and a rheology modifier. The construction material can include, for example, 0.1 wt % to 50 wt % of the rheology modifier. The rheology modifier can include, for example, a thixotropic additive, a thixotropic additive, a particulate filler, a polymer-based additive, or a combination thereof. The polymer may include, for example, a thermoset, such as a silicone-based polymer (e.g., PDMS), an epoxy-based polymer, a urethane-based polymer, or a combination thereof. The deposition of the structural material is repeated as necessary to create the object. The structural material may be cured after deposition. The support material is at least partially removed from the object.

[0005] In another general aspect, an additive manufacturing method includes depositing a structural material onto a support material through a nozzle of an extruder assembly, and repeating the deposition of the structural material as necessary to create an object. Printing parameters of the deposition vary from a first portion of the object to a second portion of the object, or the nozzle is configured to move away from a previously deposited layer of the object as it repositions for deposition of a subsequent layer of the object, or combinations thereof. The support material is at least partially removed from the object. The printing parameters can include, for example, a flow rate of the structural material through the nozzle, an extrusion direction, an infill parameter, a translational speed of the nozzle, a layer height, a translational direction of the nozzle, a print pattern, a curing parameter, or combinations thereof. The structural material can include, for example, a polymer and a rheological modifier, and the structural material can include a yield stress in the range of 1 Pa to 10 kPa. Depositing the structural material includes applying a force to the structural material such that the structural material flows through the nozzle. The force can be at least a yield stress of the structural material.

[0006] In another general aspect, the invention is directed to a system for additive manufacturing. The system includes an extruder assembly including a nozzle configured to deposit a build material and a material deposition region configured to receive a support material. The system also includes a processor coupled to a non-transitory memory. The non-transitory memory includes machine-executable instructions that, when executed by the processor, cause the processor to control the nozzle to deposit the build material onto a support material located in the material deposition region by applying a force to the build material such that the build material flows through the nozzle. In one particular example, the build material includes a yield stress and the applied force is at least the yield stress of the build material. The non-transitory memory also includes machine-executable instructions that, when executed by the processor, cause the processor to control the nozzle to create an object and repeat deposition of the build material as needed to at least partially remove the support material from the object.

[0007] In another general aspect, an additive manufacturing method of the present invention includes receiving, by a processor, a part file of an object, and separating, by the processor, the part file into different part segments, such that each part segment includes a portion of the part file. The method also includes creating, by the processor, machine path instructions for each segment based on a design of the portion of the part file in the respective segment, and storing the machine path instructions in a memory. The machine path instructions vary between at least two segments, such as a distribution of flow of a construction material through the nozzle, a direction of extrusion, an infill parameter, a translation speed of the nozzle, a layer height, a translation direction of the nozzle, a print pattern, a curing parameter, or a combination thereof. In one particular example, the nozzle is configured to move away from a previously deposited layer of the object when repositioning for deposition of a subsequent layer of the object.

[0008] In another general aspect, a system for additive manufacturing of the invention includes a processor coupled to a non-transitory memory, the non-transitory memory including machine-executable instructions that, when executed by the processor, cause the processor to receive a part file of an object and separate the part file into different part segments, such that each part segment includes a portion of the part file. The non-transitory memory includes machine-executable instructions that, when executed by the processor, cause the processor to create machine path instructions for each segment based on a design of the portion of the part file in the respective segment and store the machine instructions in the memory. The machine path instructions vary between at least two segments.

[0009] In another general aspect, an additive manufacturing system of the invention includes an extruder assembly, a material deposition region, and a processor. The extruder assembly includes a nozzle configured to deposit a construction material. The material deposition region is configured to receive a support material. The processor is operably coupled to a non-transitory memory. The processor is configured to control deposition of the construction material through the nozzle. The processor is configured to change printing parameters from a first portion of the object to a second portion of the object, move the nozzle away from a previously deposited layer of the object when repositioning for deposition of a subsequent layer of the object, or combinations thereof. The printing parameters can include a flow rate of the construction material through the nozzle, an extrusion direction (e.g., extrusion, retraction), an infill parameter, a translation speed of the nozzle, a layer height, a translation direction of the nozzle, a print pattern, a curing parameter, or combinations thereof.

[0010] Various embodiments and implementations of the present invention provide many advantages and improvements over conventional additive printing techniques. For example, rheological modifications of structural materials can be leveraged to generate yield stress fluids more capable of maintaining their printed geometries. Additionally, intelligent machine path and careful selection of printing parameters can improve printed geometries. Specifically, interactions between the printing nozzle and the extruded filament can be minimized to prevent filament distortion. Movement can be configured to occur outside the body of the print, and retraction should be used to reduce string artifacts. A modular approach to machine path can achieve printed constructs with the highest fidelity. Additionally, robust additive manufacturing systems with robust hardware can be used to extrude thixotropic viscous fluids. These and other advantages potentially realizable through various implementations of the present invention will become apparent from the following description. [Brief description of the drawings]

[0011] The features and advantages of the embodiments of the present invention, as well as the manner in which they are accomplished, will become more apparent and the embodiments will be better understood by reference to the following description taken in conjunction with the accompanying drawings, which illustrate, by way of example, various aspects of the invention.

[0012]

[0013] [Figure 1A] 1 is an image of a rendering of an example calibration cube with infill and perimeter regions.

[0014] [Figure 1B] 13A-13C are images of an example of a filament being extruded onto a previously deposited filament, which as the filament is extruded can exert a downward force on the previous layer as well as shear stress at the interface of the layers.

[0015] [Figure 1C] 13A-13C are example images of a filament being extruded at an angle to previously deposited filaments in the infill, which can result in filament displacement as the nozzle approaches the previous layer.

[0016] [Figure 1D] FIG. 13 is an image of a top view of an example of two printed layers of PDMS with intersecting infills, where dashed circles are used to mark areas where the infill is collapsed.

[0017] [Figure 1E] 13 is an image of an exemplary calibration cube printed with PDMS on a Carbopol support material where the PDMS clumped together and did not maintain the printed geometry.

[0018] [Figure 1F] FIG. 1C is an image of a top view of the calibration cube of FIG. 1E.

[0019] [Figure 2A]1 is a graph illustrating stress ramps for various exemplary structural materials exhibiting Bingham pseudoplastic behavior, according to examples described herein.

[0020] [Figure 2B] 1 is a graph depicting steady stress sweeps of various exemplary construction materials showing the increase in yield stress of various construction material compositions with increasing rheology modifier concentration;

[0021] [Figure 2C] 13 is a graph showing a power fit curve with R2=0.978 according to an embodiment described herein.

[0022] [Figure 3A] FIG. 1 shows an example of an FDM extruder nozzle extruded filament on the left and an example of an FRE extruder nozzle extruded filament on the right.

[0023] [Figure 3B] Image of a cross section of an FDM printed filament. Scale bar at bottom right is 1 mm.

[0024] [Figure 3C] FIG. 11 is an image of the cross section of an exemplary FRE printed filament; the scale bar at bottom right is 1 mm.

[0025] [Figure 3D] 1 is an image of an example frame model of a printed filament.

[0026] [Figure 3E] FIG. 11 is an image of the cross section of an exemplary FRE printed filament printed with a translation speed of 5 mm / sec and a flow fine adjustment of 1, the scale bar at the bottom right is 0.5 mm.

[0027] [Figure 3F]FIG. 13 is a graph showing the aspect ratio of an exemplary FRE printed filament versus printing speed and flow fine-tuning. The graph shows that the aspect ratio is consistently greater than 1 over a range of printing speeds (5-10 mm / sec) and flow fine-tuning (0.9-1.1).

[0028] [Figure 4A] For example, an image showing the machine path for an exemplary shell to be printed having 2 layers in the top image, 3 layers in the middle image, and 4 layers in the bottom image.

[0029] [Figure 4B] 4B is an image of an exemplary cross section of a FRE printed filament with 2 layers in the top image, 3 layers in the middle image, and 4 layers in the bottom image, printed according to the machine path of FIG. 4A. Two distinct morphologies are observed, rounded and flattened.

[0030] [Figure 4C] On the left are images of an example print that was used to examine filament morphology as a function of infill density, cut at the dashed line, and examined under a microscope to produce the image on the right. The top image is an example of a monolayer filament with 40% infill density, and the bottom image is a monolayer filament with 90% infill density, showing that filament elongation can worsen at high infill densities.

[0031] [Figure 4D] 1 is a graph showing that aspect ratio can increase with infill density.

[0032] [Figure 4E] 14A-14C are images showing cross sections of example FRE printed filaments across a range of infill densities and layer heights; asterisks indicate areas of crowning; scale bar in bottom right of each image is 1 mm.

[0033] [Diagram 5]14A-14D are side and top view images of example FRE printed calibration cubes via modification of PDMS rheology and mechanical path. The left column of images shows calibration cubes still on the support material. The top row of images shows that printing unmodified PDMS can result in clumping of the PDMS and collapse of previously printed layers, which can be manifested in air bubbles in the PDMS. The middle row shows calibration cubes printed with rheology modifiers added to the construction material. The bottom row shows calibration cubes printed with construction material containing rheology modifiers and enhanced mechanical path.

[0034] [Figure 6A] 1 shows top views of exemplary cast tensile test samples at (i) 0 wt. %, (ii) 1.0 wt. %, and (iii) 2.7 wt. % rheology modifier; scale bar at bottom right is 1 cm.

[0035] [Figure 6B] 6 is a graph of stress-strain curves for three exemplary different PDMS formulations, (i) designated as 600, (ii) designated as 602, and (iii) designated as 606 (n=6).

[0036] [Figure 6C] FIG. 1 is a graph of stress-strain curves for three different exemplary PDMS formulations, designated (i) as 600, (ii) as 602, and (iii) as 606 (n=6), over a strain range of 0-10%.

[0037] [Figure 6D] FIG. 1 is a column chart of Young's modulus for three different exemplary PDMS formulations: (i), (ii), and (iii) (Kruskall-Wallis test with post-hoc Dunn multiple comparison test, *** indicates p<0.001).

[0038] [Figure 6E]13A-13C are images of example planned machine paths for tensile test specimens with (iv) a cubic infill pattern, (v) an aligned rectilinear infill pattern, fill angle=0° (denoted as "parallel"), and (vi) an aligned rectilinear infill pattern, fill angle=90° (denoted as "perpendicular") infill pattern.

[0039] [Figure 6F] Figure 1 shows top views of exemplary FRE-printed tensile test specimens with three different infill patterns: (iv), (v), and (vi). The scale bar at the bottom right is 1 cm.

[0040] [Figure 6G] 13 is a graph of stress-strain curves for three different exemplary infill patterns: (iv), (v), and (vi), (n=6).

[0041] [Figure 6H] 13 is a graph of stress-strain curves for three different exemplary infill patterns designated as (iv) 606, (v) 608, and (vi) 610 (n=6) over strains of 0-10%.

[0042] [Figure 6I] FIG. 13 is a column chart of modulus of cast and printed example tensile test samples at 2.7 wt. % rheology modifier / PDMS (one-way ANOVA and post hoc Tukey's test, *** indicates p<0.001, **** indicates p<0.0001).

[0043] [Figure 6J] Column chart of elongation to failure as a function of infill pattern for three different exemplary infill patterns: (iv), (v), and (vi). (One-way ANOVA and post-hoc Tukey's test, **** indicates p<0.0001).

[0044] [Figure 7]Images of an exemplary 3D model to be printed, an example of a non-optimized FRE print of the exemplary 3D model, and an example of an optimized print of the 3D model. In the left column of images, the images show that generating separate machine paths (modulation of flow rate) for different regions of the print can enable the construction of hollow spheres. In the middle column of images, the images show that implementing a retract and lift movement can enable the construction of an auxetic lattice. In the right column of images, the images show that utilizing a smaller nozzle size and a more powerful motor can enable the construction of a right-handed double helix.

[0045] [Figure 8] FIG. 1 is a block diagram of an example additive manufacturing FRE system according to the present disclosure, with the x-axis coming out of the page.

[0046] [Figure 9] 1 is a flow chart of an example additive manufacturing FRE method according to the present disclosure.

[0047] The exemplifications set forth herein illustrate particular embodiments in one form, and such exemplifications should not be construed as limiting the scope of the appended claims in any manner. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0048] As used herein, "additive manufacturing" refers to a process of joining materials to create an object from 3D model data, usually layer by layer, as opposed to subtractive manufacturing methodologies. For example, additive manufacturing can include fused deposition modeling (FDM) and free-form reversible embedding (FRE). FDM can include extruding a material by heating it above its melting temperature and depositing the extruded material in a pattern to form a layer of the object. Subsequent layers can be deposited on top of previous layers as needed to form the object.

[0049] Free reversible embedding (FRE) is similar to FDM, but instead of depositing material on top of a previous deposit or support, FRE embeds a structural material near other embedded deposits within a support material and relies on triggered assembly or reorganization of the material using targeted heating, photopolymerization, crosslinking, slow reaction kinetics, application of binders, and / or other curing techniques. For example, the support material may provide divalent cations for crosslinking so that the structural material begins to harden when it contacts the support material.

[0050] In additive manufacturing techniques such as FDM, the support material is usually printed as part of the previous layer and is as rigid as the printed material, placed only under or adjacent to the printed layer to prevent deformation. In FRE, the support material can surround the extrusion nozzle and the printed material can be deposited inside the support. The support material can be a non-Newtonian fluid that allows the deposition of various materials while maintaining a buoyant force that is a physical support for the already embedded deposits of printed material. In the case of two embedded deposits of printed material with a predetermined distance inside the support material, they can be dissolved. After printing, the support material can be removed from the deposited printed material to form a fully assembled object from the deposited printed material.

[0051] With FRE, objects can be printed in any direction in 3D space and are not limited to layer-by-layer printing. For example, structures can be printed layer-by-layer in the XY plane, or in non-XY planes such as the XZ plane, or in planes offset at any angle from the XY plane. Objects can be printed using FRE in a non-planar manner, for example in curved paths such as spirals. Using FRE can enable printing of objects with different mechanical properties in the plane of printing versus orthogonal to the plane of printing or at other angles to the plane of printing. Further details regarding the FRE process are described in U.S. Patent No. 10,150,258, entitled "ADDITIVE MANUFACTURING OF EMBEDDED MATERIALS," filed January 29, 2016, which is incorporated herein by reference.

[0052] FRE printing of soft polymers such as silicone-based polymers, epoxy-based polymers, etc., presents challenges. For example, infill patterns in which each layer is extruded off-axis into the layer below are not possible due to variable filament morphology (e.g., the shape of the structural material extruded from the nozzle) and high filament deformability. Furthermore, filament morphology can affect the accuracy of prior space-filling models for machine paths when slicing part files such as STL models into G-code for printing. In addition, many soft polymers do not cure instantly, but instead cure over time or with exposure to external stimuli (heat, UV light, etc.). Thus, these soft polymers are often highly deformable after deposition and susceptible to collapse from movement of the extrusion nozzle during printing. Furthermore, the composition and surface energy of materials used in FRE may prevent dissolution unless sufficient contact and applied force between individual filaments is achieved. These challenges have limited the achievable geometries in FRE additive manufacturing with soft polymers to simple models and inhibited the use of FRE for more complex geometries.

[0053] Various implementations of the present invention improve FRE imparting agent manufacturing by taking advantage of or otherwise using the rheology, filament morphology, and deformability of these soft polymers to affect printing performance. For example, polydimethylsiloxane (PDMS) (e.g., Sylgard 184, PDMS prepolymer) exhibits Newtonian behavior and can flow after deposition until cured, which can take minutes to hours depending on the temperature, and can make it difficult for the deposited PDMS to resist deformation. The inventors have surprisingly discovered that by introducing a rheology modifier into the polymer (e.g., PDMS prepolymer), a yield stress fluid can be made that is more resistant to deformation after deposition onto a support material, thereby making the yield stress fluid more capable of maintaining its printed geometry. The rheology modifier is also applicable to other soft polymers other than PDMS. The rheology modifier is also applicable to other polymers that can be semi-rigid or rigid.

[0054] Additionally, filament morphology and deformability can impact the print plan and path of slicing software for FRE. Prior FDM slicing software, which takes part files (e.g., computer-aided design (CAD) models) and generates machine paths for additive manufacturing systems, assumes that the filament is flattened during extrusion and does not deform after extrusion. The inventors have discovered that FRE filament behavior is significantly different than FDM and requires different machine path instructions and parameters. For example, FRE filaments are highly deformable and do not have a consistent morphology that may depend on the local surroundings (e.g., print area, proximity to other filaments). The inventors have discovered that prior slicing software for FDM did not take these considerations into account and therefore was not optimized for FRE additive manufacturing. Based on these findings, machine path instructions and printing parameters can be optimized, and based on these optimizations, the inventors have been able to achieve complex structures with various soft polymers, such as PDMS, that were previously unattainable via typical additive manufacturing approaches. In various examples, rheological modification of structural materials, optimized machine paths, and the use of support baths can enable additive manufacturing of complex geometries with soft polymers.

[0055] 8, a block diagram illustrating an example of an additive manufacturing system 800 for FREs according to the present disclosure is provided. System 800 includes an extruder assembly 802, a computer system 804, and a material deposition area 806. Computer system 804 is in signal / data communication with extruder assembly 802 (e.g., via a wired and / or wireless data bus or link), and computer system 804 can be configured through programming to control the operation of extruder assembly 802.

[0056] The extruder assembly 802 may be a syringe-based extruder that may include a reservoir 812 (e.g., a barrel of a syringe) for receiving and storing the construction material, and a nozzle 810 (e.g., a needle) in fluid communication with the reservoir 812 and capable of receiving the construction material from the reservoir 812. The construction material may be extruded through the nozzle 810, which may be configured to deposit the extruded construction material on a support material 808 disposed at the material deposition area 806. In various examples, the extruder assembly 802 may comprise a gantry or other robotic device for supporting and / or moving the extruder assembly 802 relative to the material deposition area 806. Optionally, the extruder assembly may comprise a motor assembly or other movement assembly configured to translate and / or rotate the gantry and / or robotic device. In various examples, the extruder assembly 802 includes an actuator (e.g., a motor) configured to depress a plunger into the reservoir 812 to extrude the structural material through the nozzle 810 and onto the support material 808 as the nozzle 810 is translated through the support material 808 to generate the object 814.

[0057] The computer system 804 comprises one or more processors 820 (for simplicity, only one processor 820 and one memory 822 are shown in FIG. 8 ) operably coupled to one or more memories 822. The memory 822 may comprise primary storage (e.g., main memory directly accessible by the processor 820, such as RAM, ROM processor registers or processor cache), secondary storage (e.g., SSD or HDD not directly accessible by the processor), and / or offline storage. The memory 822 stores computer instructions (e.g., software) executed by the processor 820. The processor 820 may be configured to control (through execution of software stored in the memory 822) the deposition of the construction material through the nozzle 810. For example, the processor 820 may control (e.g., by the actuation speed of a plunger in the extruder assembly 802) the flow rate of the construction material through the nozzle 810 and / or the attitude of the extruder assembly 802 relative to the material deposition region 806.

[0058] The processor can receive a digital or electronic part file 824 of an object 814 to be manufactured by an additive manufacturing process from memory 822 or from another device (e.g., another computing device, the cloud). The object 814 can be a variety of object types, such as, for example, a soft structure, a bioprosthesis, a scaffold, a medical device, an implantable device, a gasket, a tube, a seal, an aerospace part, an automotive part, a building component, or other structures that can be additively manufactured. The part file 824 can be in a variety of different digital or electronic formats, such as an STL file, an OBJ file, an FBS file, a Collada file, a 3DS file, an IGES file, a Step file, a VRML / X3D file, a point cloud, or another 3D model file format type.

[0059] The processor 820 can be configured to separate (e.g., slice (using Slic3r, Skeinforge, KISSlicer software, etc.)) the part file 824 into different part segments 826, each segment comprising a portion of the part file 824. In various examples, the processor 820 can be configured to convert the part file 824 into a different 3D model file format prior to separation.

[0060] Each part segment 826 may be a layer 814a and 814b of the object 814 to be deposited, a portion of the layers 814a and 814b of the object 814 to be deposited, or other geometric shapes of the object 814. The segments 826 may be formed based on a design of the part file 824. For example, a segment of the segment 826 may include an overlap region 828 of the layer 814b (e.g., printed directly on top of the layer 814a), an overhang region 830 of the layer 814b, an infill region, a perimeter region, another region of the object 814, or a combination thereof. For example, the overhang region 830 may be within an overhang segment of the segment 826 that is different from the overlap segment of the segment 826 for the overlap region 828. In various examples, the perimeter region of the object 814 may be within a perimeter segment of the segment 826 that is different from the infill segment of the segment 826 for the infill region. Each segment 826 may or may not be in the XY plane, the segments may be in the XZ plane, the YZ plane, other planes offset from the XY plane, or non-XY planes, such as non-planar segments, e.g., curves. Utilizing various segments 826 for different regions of the object 814 can allow for variation in machine path instructions and / or printing parameters for each segment 826. Thus, the machine path instructions and / or printing parameters may be selected to suit the particular geometric shape to be printed with the respective segment 826.

[0061] From the segments 826, the processor 120 may be configured to create machine path instructions (e.g., G-code instructions) 832 for the segments 826 based on the design of the portion of the part file 824 within the respective segment 826. The machine path instructions 832 may be stored in the memory 822. The machine path instructions 832 may include printing parameters 834 and, when executed by the processor 820, may cause the processor 820 to control the operation (e.g., pose, extrusion) of the extruder assembly 802. In various examples, the machine path instructions 832 for at least two segments 832 may vary with the printing parameters 834, such as, for example, at least three segments 832 may vary with the printing parameters 834. The printing parameters 834 may be a flow rate of the construction material through the nozzle 810, a direction of extrusion, an infill parameter (e.g., density, pattern), a translational speed of the nozzle 810, a layer height, a translational direction of the nozzle 810, a print pattern, a curing parameter, a combination thereof, or other printing parameters.

[0062] Machine path instructions 832 and printing parameters 834 may be associated with each segment 826 and are adapted to the geometry and intended mechanical properties of the area of ​​the part file 824 within the associated respective segment 826 to be printed. The processor 820 may be configured to vary the printing parameters 834 used to control the extruder assembly 802 from a first portion of the object 814 to a second portion of the object 814. For example, the process may utilize a different flow rate of construction material through the nozzle 810 between the first portion and the second portion, a different extrusion direction, different infill parameters (e.g., density, pattern) between the first portion and the second portion, a different translation speed of the nozzle 810 between the first portion and the second portion, a different deposition height of the nozzle 810 between the first portion and the second portion, a different translation direction of the nozzle 810 between the first portion and the second portion, a different print pattern between the first portion and the second portion, different curing parameters between the first portion and the second portion, combinations of these, or may utilize various other different printing parameters. Thus, separation of part file 824 can enable machine path instructions 832 and printing parameters 834 based on the portion of object 814 being additively manufactured, thereby enabling improved printing of object 814.

[0063] The infill regions of the object 814 are typically repeating geometric shape patterns with defined porosity that are utilized to occupy what would otherwise be space within the object 814. Infill density may be expressed as a percentage, for example, from 0-100%, with 0% representing a completely hollow space and 100% representing a solid object. The infill density may affect the weight, strength, and other mechanical properties of the object 814. Additionally, the infill regions of the object 814 may be machined in a variety of different patterns, such as grids, lines, honeycomb structures, and other patterns. Various infill patterns may be more suitable for different shaped structures and / or alter the mechanical properties of the structure (e.g., provide non-uniform strength characteristics). The object 814 may be machined to have non-uniform infill density and / or patterns throughout the object 814 based on the machine path instructions 832 and parameters 834. Thus, different regions of the object 814 may have different weights, strengths, and mechanical properties.

[0064] The mechanical properties of the object 814 can also be customized by controlling the direction and / or pattern in which the structural material is deposited by the nozzle 810. During additive manufacturing of the object 814, the structural material can be deposited by the nozzle 810 as a series of successive planes or any 3D striations that are ultimately fused together to form the object 814. The longitudinal axis of the striations can be orthogonal to the direction in which the layers or striations are added. The striations can be anisotropic, exhibiting different mechanical properties (e.g., tensile strength) along their longitudinal axis than their transverse axis, which affects the mechanical properties of the object 814. Thus, controlling the direction in which the striations are deposited to form the object 814 can control the mechanical properties of the object 814. For example, if it is desired that the object 814 exhibit higher tensile strength in a particular direction, the nozzle 810 can be controlled to deposit the structural material such that the longitudinal axis of the striations is aligned with that desired direction. Furthermore, as mentioned above, the direction in which the striations are deposited can be any 3D motion and is not limited to planar motion.

[0065] Based on the machine path instructions 832, the nozzle 810 may be configured to move away from a previously deposited layer of the object 814 when repositioning for deposition of a subsequent layer of the object 814. For example, after printing of layer 814a, the nozzle 810 may perform a non-printing move at the XY coordinates where layer 814a was not deposited. After printing of layer 814a, the non-printing move may include moving the nozzle 810 to a starting position for printing layer 814b without extruding any structural material. Moving over a previous layer may disrupt the shape of the previous layer because the nozzle 810 must translate through the support material 808. Minimizing movement over a previous layer during a non-printing move may enable improved printing of the object 814.

[0066] The nozzle 810 can be configured to deposit the structural material onto the support material 808 by applying a force to the structural material in the reservoir 812 such that the structural material can flow from the reservoir 812 through the nozzle 810. The structural material can include a yield stress, thixotropic properties, an increase in viscosity due to a rheology modifier (e.g., compared to a structural material without a rheology modifier), or a combination thereof. In various examples, the structural material includes both a yield stress and a thixotropic property. In examples where the structural material includes a yield stress, the applied force can be at least a yield stress. In certain examples, applying a force to the structural material can cause the structural material to flow through the nozzle. For example, if the viscosity increases, the force can overcome the increased viscosity and cause the material to flow through the nozzle. In examples where the structural material includes a thixotropic property, the thixotropic property can cause the time scale for the structural material to begin to flow to be longer than the printing process.

[0067] In various examples, the plunger can translate through a reservoir 812. In various examples, the force can be applied pneumatically or the deposition can be controlled by a cavity pump. The application of force can transform the construction material from a solid or semi-solid state to a fluid state (e.g., liquid) such that the construction material can be deposited on the support material 808. The construction material can be suspended in the support material 808 where the construction material is deposited by the nozzle 810 within the support material 808. The processor 820 can control the extruder assembly 802 and the nozzle 810 such that the deposition of the construction material by the nozzle 810 can be based on machine path instructions 832 and associated printing parameters 834 executed by the processor 820.

[0068] The extruder assembly 802 can move the nozzle 810 in two dimensions when depositing the structural material, similar to FDM, or in three dimensions when depositing material, i.e., simultaneously in the X, Y, and Z directions. Additionally, the extruder assembly 802, the nozzle 810, and / or the material deposition area 806 can be rotatable. Machine path instructions can be defined according to both Cartesian and rotational coordinates, which can make it possible to produce objects with complex geometric shapes or very specific mechanical properties. The 3D movement of the nozzle 810 during deposition of the structural material can enable, for example, additive manufacturing of a helical spring in one constant motion. In various examples, other complex geometric shapes are achievable with a robotic arm assembly that can control movement simultaneously in six degrees of freedom (i.e., in any Cartesian or rotational direction).

[0069] The deposition of the structural material can be repeated as necessary to create the object. For example, the processor 820 can control the nozzle 810 to deposit the structural material in layers, such as layers 814a and 814b, to create the object 814 in the support material 808 based on the part file 824, another planar, and / or non-planar movement. In some examples, the layer 814a can be deposited before the layer 814b. The layer 814a may not be partially and / or fully cured before the deposition of the layer 814b. Thus, the processor 820 can control the nozzle 810 to deposit the layer 814b near (e.g., adjacent to, in contact with, directly on) the layer 814a, such that the deposition of the layer 814b deforms the layer 814a. For example, the deposition of the layer 814b can change the shape of at least a portion of the layer 814a. The changed shape of at least a portion of the layer 814a can be one that cannot be achieved by simply extruding from the nozzle 810. Changing the shape of layer 814a by the deposition of layer 814b increases the contact surface area between layers 814a and 814b, reduces the voids between layers 814a and 814b, improves adhesion between layers 814a and 814b, or a combination thereof.

[0070] The structural material may include a yield stress material that transitions from a fluid (e.g., liquid) state to a solid or semi-solid state upon application of pressure. For example, the structural material may be in a solid or semi-solid state within the extruder assembly 802, and pressure may be applied to the structural material to transition it to a fluid state, causing it to flow through the nozzle 810 and be deposited onto the support material 808. After exiting the nozzle 810, the pressure applied to the structural material is removed, causing the structural material to transition to a solid or semi-solid state, thereby resisting deformation while in the material deposition region 806.

[0071] The structural material may include a polymer and a rheology modifier. The polymer may include a polymer resin (e.g., a prepolymer resin), a hardener, and other additives. For example, the polymer may include an alginate material, a collagen material, a fibrin material, a hyaluronic acid material, a protein material, a polysaccharide hydrogel material, a synthetic gel material, an elastomeric polymer material, a rigid polymer material, or a combination thereof. In various examples, the polymer may include a thermosetting polymer. The polymer may include, for example, a silicone-based polymer, such as polydimethylsiloxane (PDMS), an epoxy-based polymer, a urethane-based polymer, or a combination thereof. The structural material may include at least 70% polymer based on the total weight of the structural material, for example, at least 80% polymer based on the total weight of the structural material, or at least 90% polymer based on the total weight of the structural material. The polymer, when cured, may have an elastic modulus in the range of 0.1 kPa to 10 GPa, such as 0.1 Mpa to 50 Mpa or 0.1 Mpa to 10 Mpa.

[0072] The rheology modifier can be added to the construction material in an effective amount to modify the construction material to have a yield stress. The construction material can include at least 0.1% rheology modifier based on the total weight of the construction material, such as at least 0.5% rheology modifier, at least 1% rheology modifier, at least 2% rheology modifier, at least 5% rheology modifier, or at least 10% rheology modifier, based on the total weight of the construction material. The construction material can include 50% or less rheology modifier, such as 20% or less rheology modifier, 10% or less rheology modifier, 9% or less rheology modifier, 5% or less rheology modifier, or 3% or less rheology modifier, based on the total weight of the construction material. For example, the construction material may include a rheology modifier in the range of 0.1% to 50% based on the total weight of the construction material, such as, for example, 0.1 to 20%, 0.1% to 10%, 1% to 10%, 0.5% to 3%, 0.5% to 5%, 1% to 5%, or 5% to 10%, based on the total weight of the construction material. The rheology modifier may include a thixotropic additive, a particle filler (e.g., nanoparticles, microparticles, nanofibers, microfibers), a polymer-based additive, or other viscosity modifier. The polymer-based additive may form a temporary bond (e.g., hydrogen bond) that may be broken under the applied shear force. The temporary bond may be between the polymer-based additive itself, between the polymer-based additive and the construction material, or a combination thereof.

[0073] The yield stress of the structural material can be greater than 1 Pascal (Pa), such as greater than 10 Pa, greater than 20 Pa, greater than 30 Pa, greater than 40 Pa, greater than 50 Pa, greater than 100 Pa, or greater than 1 kPa. The yield stress of the structural material can be 10 kPa or less, such as 1 kPa or less, 500 Pa or less, 400 Pa or less, 300 Pa or less, 200 Pa or less, 175 Pa or less, 150 Pa or less, 125 Pa or less, or 100 Pa or less, etc. For example, the yield stress of the structural material can be in the range of 1 Pa to 10 kPa, such as, for example, 1 Pa to 500 Pa, 10 Pa to 400 Pa, 10 Pa to 200 Pa, 20 Pa to 200 Pa, 50 Pa to 200 Pa, 50 Pa to 150 Pa, or 50 Pa to 100 Pa.

[0074] Material deposition area 806 can be configured to mechanically support support material 808 during FRE additive manufacturing. For example, material deposition area 806 can include a vessel in which support material 808 is placed and a platform on which the vessel is supported. Material deposition area can include motors and / or actuators that can move the platform in 3D space as needed.

[0075] Support material 808 can mechanically support at least a portion of the embedded structural material (i.e., object 814), maintain the intended geometric shape of the embedded structural material, and inhibit deformation of the structural material during the FRE additive manufacturing process. For example, the embedded structural material can be held in place within support material 808 until the structural material hardens. Support material 808 can be at rest at applied stress levels below a threshold stress level and can flow at applied stress levels equal to or greater than the threshold stress level during the FRE additive manufacturing process.

[0076] The support material 808 may be a viscoplastic material with Bingham plastic-like rheological behavior. The support material 808 may exhibit significant shear thinning behavior such that the support material 808 acts like a solid material during deposition of the structural material and then acts like a fluid when the nozzle 810 is moved through the support material 808 such that the movement of the nozzle 810 does not disturb the deposited structural material. The reduction in viscosity of the support material 808 under dynamic loads may make the support material 808 suitable for FRE. For example, in a FRE, dynamic loads may be caused by the force of the nozzle 810 through the support material 808, affecting the support material 808 in several ways. The extruder assembly 802 may be configured to alter the support material 808 by imposing mechanical loads via shear, pressure, or vibration. The extruder assembly 802 may be configured to irradiate or heat the support material 808 to thin it. In various examples, the support material 808 may reduce in viscosity under vibration, heat, or irradiation generated locally in the extruder assembly 802 .

[0077] The support material 808 can include other materials with viscoplastic behavior, such as Herschel-Bulkley fluids. Bingham plastics and Herschel-Bulkley fluids are viscoplastic materials that fall into the "shear thinning" or "yield stress fluid" category. Below a certain shear stress, these materials appear as solid materials. Above a threshold shear force, these materials behave as fluids. Bingham plastics are not necessarily "shear thinning" but rather may behave like Newtonian fluids once they begin to flow. In contrast, Herschel-Buckley fluids undergo shear thinning once they begin to flow.

[0078] The object 814 may be at least partially cured within the support material 808 after deposition of the construction material. In various examples, the construction material may be at least partially cured prior to removal of the support material 808. In some examples, the construction material may not be cured until after removal of the support material 808. As used herein, the terms "curing" and "hardening" refer to the chemical cross-linking of components in the construction material. Thus, the terms "curing" and "hardening" do not encompass only the physical drying of the construction material by solvent or carrier evaporation. In this regard, the term "hardened" as used herein refers to a state of the construction material in which the components of the construction material forming the object 814 have chemically reacted to form new covalent bonds (e.g., new covalent bonds formed between a polymeric resin and a hardener), new ionic bonds, new hydrogen bonds, new VanderWaal bonds, or combinations thereof, in the construction material.

[0079] For example, hardening of the object 814 can include crosslinking. The object 814 can be treated through various crosslinking techniques to selectively increase the stiffness of the entire object 814 or portions thereof. Crosslinking can be induced by various mechanisms, such as, for example, photo-mechanisms (e.g., exposing the construction material to UV light), ionic mechanisms, enzymatic mechanisms, pH mechanisms (e.g., exposing the construction material to different pHs), or thermally driven mechanisms (e.g., cooling, heating). In various examples, the support material 808 can include a crosslinking agent or pH suitable for hardening the construction material when deposited on the support material 808. In some examples involving construction materials including PDMS, the construction material can then be hardened at room temperature for 48 hours while in the support material 808 before being removed by heating the support material 808 to 37 degrees Celsius.

[0080] By controlling the amount of curing that occurs within the object 814, the mechanical properties of the object 814 can be controlled. For example, the machine path instructions 832 can be adjusted to control the amount of crosslinking that occurs within each segment 826 of the object 814. For example, the extruder assembly 802 can be equipped with a UV light, and the embedded structural material can be selectively exposed to the UV light as desired.

[0081] The object 814 may be at least partially removed from the support material 808. Removing the support material 808 may include heating the support material 808, cooling the support material 808, removing cations to disrupt crosslinks in the support material 808, physically removing the support material 808, irradiating with vibration, ultraviolet, infrared, or visible light, applying a constant or oscillating electric or magnetic field, other mechanisms, or combinations thereof.

[0082] Methods for additive manufacturing herein, as described in FIG. 9 below, may be implemented in whole or in part as computer executable instructions stored in non-transitory memory 822 of computer system 804 that, when executed by processor 820 of computer system 804, cause computer system 804 to perform the recited steps. The computer instructions may be implemented as one or more software modules 816 stored in memory 822, each programmed to cause processor 820 to perform one or more separate steps of a process or other functions described herein. For example, modules 816 may comprise a separation module programmed to convert part files 824 into segments, a conversion module programmed to convert segments 826 into computer instructions (e.g., G-code) to control movement of extruder assembly 802 to process object 814, a modeling module programmed to receive, store, create, and / or modify part files of an object to be processed, and a robotics control module programmed to control extruder assembly 802 according to instructions generated by the conversion module to process object 814. Various other modules may be implemented in addition to or in place of the modules described above. In certain examples, the processes described herein may be performed across multiple computer systems communicatively connected together in a network, computer systems communicatively connected to a cloud computing system configured to perform one or more of the described steps, etc.

[0083] Referring to FIG. 9, a flow chart illustrating an additive manufacturing method according to a particular implementation of the present invention is provided. The method includes, in step 902, receiving by a processor 820 a part file of an object 814. In step 904, the processor 820 executing a separation module software can separate (e.g., slice) the part file into different part segments. Each part segment includes a portion of the part file. The method further includes, in step 906, by executing a conversion module, the processor 820 generates machine path instructions (e.g., G-code instructions) for each segment based on the design of the portion of the part file in the respective segment, and stores the machine path instructions in memory 822. The method can include, in step 908, depositing a structural material by a nozzle 810 onto a support material 808 by applying a force to the structural material to flow through the nozzle 810. In step 910, deposition of the structural material can be repeated as necessary to create the object 814.

[0084] The printing parameters may be changed from a first portion of the object to a second portion of the object. The nozzle 810 may be configured to move away from a previously deposited layer of the object when repositioning for deposition of a subsequent layer of the object.

[0085] Thereafter, in step 912, the structural material may be at least partially cured after deposition, and then in step 914, the support material may be at least partially removed from the object 814. The curing may occur before, during, after the removal of the support material in step 914, or a combination thereof.

[0086] <Example>

[0087] Various aspects, advantages, and features potentially realizable through the implementation of the present invention will be more fully understood by reference to the following examples, which provide illustrative, non-limiting aspects of the invention. It should be understood that the invention described herein is not necessarily limited to the examples described in this section.

[0088] [Preparation of Carbopol Support Bath]

[0089] A 0.2% (w / v) Carbopol support bath was prepared by slowly adding 4 grams of Carbopol 940 (Lubrizol) to 2 liters of distilled water and mixing for 15 minutes in a KitchenAid mixer. The bath was then neutralized to pH 7.0-7.1 using sodium hydroxide (1.0 N) (EMD Millipore) to induce immediate gelation. The bath was mixed for an additional 5 minutes to ensure homogeneity. Prior to additive manufacturing, the Carbopol gel was mixed in a planetary centrifugal mixer (Thinky) for 2 minutes at 2000 RPM, followed by degassing for 2 minutes at 2000 RPM. Alternatively, the Carbopol was centrifuged at 2000 G for 20 seconds.

[0090] [Preparation of PDMS composite ink for use as a structural material]

[0091] Sylgard 184 elastomer (Dow Corning) was prepared per manufacturer's instructions by mixing 10 parts base resin to 1 part hardener in a planetary centrifugal mixer (Thinky) for 2 minutes at 2000 RPM, followed by degassing for 2 minutes at 2000 RPM. Using the same mixing and degassing cycle, five different PDMS composite inks were made by mixing HS II thixotropic additive (DOWSIL) at 1.0, 2.7, 5.0, 8.3, and 10.0% (w / w) with Sylgard 184. Silc Pig silicone color pigment (Smooth-On, Inc.) was used for contrast and was incorporated into the PDMS prepolymer with the HS II thixotropic additive prior to mixing.

[0092] [Rheology]

[0093] To measure the rheological properties of the PDMS composite inks, each formulation was loaded into a rheometer (Discovery Hybrid Rheometer [DHR-2], TA Instruments) equipped with a 1° cone with a diameter of 40 mm. A stress ramp was performed from 0.1 to 1000 Pa to obtain flow curves. For yield stress analysis, a steady stress sweep was performed in the range of 5 to 500 Pa, and the yield stress value was designated as the last data point before a significant decrease in viscosity. These values ​​were fitted to power curves in MATLAB. All curves were plotted in GraphPad Prism 8.4.2.

[0094] [FRE3D Printing (Additive Manufacturing)]

[0095] Additive manufacturing of the PDMS composite ink was carried out on a MakerGear printer modified with a custom-designed syringe pump extruder (Replistruder4). 3D models for printing were obtained from the Thingiverse database (https: / / www.thingiverse.com). All STL files were processed by Slic3r (https: / / slic3r.org) software. Custom G-code was generated by generating G-code for each print region of interest (with modifiers in Slic3r) and merging the code in a text editor (Sublime Text). For investigation of filament morphology and deformability, the Z-step was adjusted to 60% of the layer height to obtain dissolution using a custom MATLAB script. Prior to printing, the PDMS composite ink was transferred into a 5.0 mL airtight glass syringe (Hamilton) and mounted on the Replistruder4. The syringe was fitted with a needle (Jensen Global) and primed. All needles were equipped with 1-inch stainless steel cannulas. Most printing was performed with either a 635 μm or 406 μm ID needle. Carbopol was prepared and added to an acrylic container large enough to accommodate the printed construct. The container was secured to the printing platform with a thin layer of vacuum grease. The needle was positioned in the center of the container and lowered into the support, leaving a small gap between the needle and the bottom of the container. Duet Wifi or Pronterface software was used to initiate printing. Once printing was complete, the print container was removed from the printing platform and cured in an oven overnight at 65 °C. After curing, sodium chloride was sprayed onto the Carbopol support to induce liquefaction and allow for print removal.

[0096] [Analysis of FRE-printed PDMS structures]

[0097] To evaluate filament and print morphology, window frame models were printed across a range of print speeds (5-10 mm / s), flow fine-tuning (0.9-1.1), infill densities (10-90%), and print heights (1-5 print layers). Additionally, hollow cylinders were printed with 2-4 layers. These constructs were sliced ​​down the middle and the filament cross sections were examined under a stereo microscope. Aspect ratios were analyzed by measuring the height and width of each filament using ImageJ (https: / / imagej.net / Welcome) software. Surface plots of aspect ratio as a function of print speed and flow fine-tuning were generated in MATLAB, and aspect ratio as a function of infill density was plotted in GraphPad Prism 8.4.2.

[0098] [Mechanical properties]

[0099] Three PDMS formulations (0 wt%, 1.0 wt%, and 2.7 wt% thixotropic additive) were cast into 150 mm Petri dishes to a thickness of approximately 3 mm and allowed to partially cure overnight at room temperature. Full cure was obtained by placing the PDMS formulations in a 65 °C oven for 4 h. Tensile bar strips were laser cut with a Rabbit Laser Cutter (Model: RL-80-1290, Rabbit Laser USA). Additionally, tensile bar strips were FRE additively fabricated with 2.7 wt% thixotropic additive with three infill densities (cubic, aligned straight, fill angle = 0°, aligned straight, 90°). Uniaxial tensile tests were performed on all samples using an Instron 5943 (Instron) for a total of six samples per condition. Samples were stretched at a rate of 2.00 mm / min until failure. Modulus was determined from a simple linear regression of the 0-10% stress-strain curves. Statistical analysis was performed using GraphPad Prism 8.4.2.

[0100] [Challenges of FRE printing using deformable ink]

[0101] The high material deformability inherent to FRE presents challenges not present in FDM. Previously printed layers can easily collapse as the direction of shear stress is directly related to the direction of the machine path. To demonstrate this, a PDMS cube was printed. FRE printing, like all FDM-based printing techniques, has a standard perimeter (outer shell) and infill (inner core) as two main regions of the print, as shown in Figure 1A. Both contribute to the structural integrity of the print, with larger shell thickness and infill density resulting in stronger parts. The construction of lattice structures or models consisting of only the perimeter has been demonstrated with embedded printing systems, although some geometries involve infill.

[0102] When printing a PDMS calibration cube, it becomes clear that the forces exerted on the perimeter are fundamentally different from those in the fill. In the perimeter, layer n is extruded first and layer n+1 is extruded on top of it along the same or similar path as shown in Figure 1B. Shear stresses are generated along the layer interface and in the direction of the two filaments, resulting in minimal material collapse and displacement occurring along the print path. In the infill, layer n+1 often traces a path at an angle to layer n, as shown in Figure 1C. Here, shear stresses can displace material in the direction of layer n+1, which often deviates from the print path. These effects are especially evident when printing PDMS prepolymers or other soft materials that exhibit Newtonian behavior and flow easily. When printing the first few layers of the calibration cube, the perimeter remains intact, but the filaments in the infill break apart due to interactions with the printing nozzle, as shown in Figure 1D. Each pass through the nozzle creates further perturbations of the previously extruded ink, making it difficult to maintain the printed geometry. Once the print is complete, it is apparent that these collapses intermingle over time, resulting in extensive PDMS aggregation throughout the construct, as shown in Figures 1E and 1F. Due to the opposing wettability, PDMS aggregation of Carbopol is energetically favorable, and the motion of the printing nozzle provides sufficient driving force to make this possible.

[0103] [Modification of PDMS rheology by thixotropic additives]

[0104] The rheology of the PDMS prepolymer, specifically, its Newtonian profile and low viscosity, are the source of its high flowability and therefore the ease of strain exhibited during printing. To counter this behavior, a rheology modifier, HS II thixotropic additive (hereafter referred to as the "additive"), was added to the PDMS prepolymer to create a yield stress fluid, i.e., one that flows only when exposed to a stress above a threshold value (known as the yield stress). Due to the desirable properties of PDMS elastomers, such as high extensibility and low modulus, low additive concentrations were chosen between 1.0 and 10.0% w / w (1.0, 2.7, 5.0, 8.3, and 10.0% w / w) to minimize the degree of modification. The stress ramp at each concentration revealed that the composite ink was indeed a yield stress fluid, as indicated by the non-zero y-intercept at each concentration, as shown in Figure 2A.

[0105] This rheological profile may be desirable for embedded printing, where passing through a yield stress induces flow and allows the fluid to resist deformation upon interaction with the printing nozzle. Steady stress sweeps show that the yield stress, which is the last value of stress before a significant drop in viscosity, increases with additive concentration, as shown in Figure 2B. This behavior can be explained by a power fit: y = 37.9 × 0.4937, as shown in Figure 2C, where the yield stress plateaus at larger additive concentrations, suggesting that there is a power law dependence as the jamming transition is approached. A concentration of 2.7% (w / w) additive was chosen for all prints to induce sufficient yield stress to substantially reduce flow during printing while minimizing denaturation of the native PDMS.

[0106] [FDM slicer software assumptions are insufficient for FRE]

[0107] Rheological modification results in a yield stress in the PDMS precursor that reduces its flowability, but this alone may not be sufficient to produce a robust embedded printing platform. Another factor that determines the success of printing is the filament morphology, as this can affect the machine path. FDM slicing software assumes that (1) the filament is flattened on the printing platform during extrusion, resulting in an elliptical cross-section with an aspect ratio (filament height divided by width) of less than 1, and (2) fine filament deformability is present after extrusion, as shown in Figures 3A and 3B. In FDM, a thermoplastic filament is heated above its melting temperature into the rubbery regime of the polymer, allowing the filament to be easily extruded and flattened. After extrusion, the filament is rapidly cooled and returned to a glassy state, where it is effectively solid and does not deform for the duration of the print. The prepolymers used in FREs are typically not thermoplastic and therefore do not have the same material properties. Additionally, in FREs, a yield stress support bath (e.g., a support material in the material deposition area) replaces the printing platform. These differences warrant investigation into filament morphology to determine whether the software's fundamental assumptions hold true for embedded additive manufacturing systems.

[0108] As shown in Figure 3A, an FDM system is shown on the left and an FRE system is shown on the right. An example of a filament morphology for an FDM filament is shown in Figure 3B, and an example of a filament morphology for an FRE is shown in Figure 3C.

[0109] A window frame test model with a single filament printed across the center of the frame was designed to allow for filament cross-section analysis, as shown in Figure 3D. The printed construct is sectioned through the center and the filament cross-section is imaged as shown in Figure 3E. The aspect ratio of each filament is quantified by dividing the height by the width. The effect of various printing parameters on the filament morphology is of interest, and printing speed (e.g., nozzle translation speed) and flow fine-tuning are demonstrated here. Printing speed dictates the print time and quality, while flow fine-tuning (also known as extrusion multiplier) is an adjustment (multiplier) to the material flow rate. This printing parameter helps to fine-tune the material flow rate and can correct defects such as crowning (excess of material) or under-extrusion. For example, a flow fine-tuning of 0.9 results in under-extrusion where the final flow rate is 90% of the original flow rate, and similarly, a flow fine-tuning of 1.1 results in over-extrusion where the final flow rate is 110% of the original flow rate. The constructs were printed at three printing speeds (5, 7.5, and 10 mm / s) and flow fine adjustments (0.9, 1.0, 1.1). Additionally, the layer height was set equal to the extrusion width (equal to the inner diameter of the extrusion nozzle) and kept constant to ensure that the material flow rate was consistent for all prints.

[0110] Image analysis revealed that the aspect ratio was greater than 1 throughout the parameter space, inconsistent with FDM. This is surprising since the individual filaments were expected to have the same circular geometry as the extruded holes, especially since the extrusion width and layer height are held constant. This suggests that there is a region of low pressure immediately after the printing nozzle, and the PDMS ink fills this area until it is immobilized by the support bath. These results demonstrate that the filament geometry in embedded printing such as FRE systems deviates from the FDM filament geometry. Assuming an incorrect FDM-like geometry of the extruded filament in FRE, the slicing software may misposition the filament in the generation of the machine path for the build, resulting in printing defects such as under- or over-extrusion. This ultimately results in poor fidelity of the print. With this in mind, the printing parameters should be selected and the machine path generated.

[0111] [Ink deformability and morphology depend on the local environment]

[0112] Due to the slow cure times and viscous nature of these inks, material deformability is another property that may deviate from FDM. Specifically, interactions between adjacent filaments are of interest as they can inform optimal filament placement (packing). These interactions are examined in both ambient and infill contexts. To determine how the ambient filaments deform, hollow cylinders with 2, 3, and 4 layers were printed and sectioned in half, as shown in Figure 4A. Initially, insufficient or nonexistent interlayer dissolution caused the cylinders to fall apart upon decomposition of Carbopol. To counter this, the interlayer distance (or Z-step taken by the extruder nozzle after a layer change) was reduced within the G-code to achieve dissolution. The original Z-step (Z0) was equal to the layer height and extrusion width of 0.635 mm. The Z-step was adjusted to 50, 60, 70, 80, and 90% of Z0, and evaluation of the filament cross-sections revealed that a step equal to 60% of Z0 was sufficient to achieve interfilament dissolution. The filaments possessed both rounded and flattened morphologies, indicated by the green and red arrows, respectively, as shown in Figure 4B. In the absence of neighboring filaments, for example at the bottom surface of the bottom layer or the top surface of the top layer, the filaments are elongated in the up and down directions in the same manner as observed in Figures 3C and 3E. In contrast, filaments in the middle layer deform their neighbors during deposition, effectively flattening the adjacent surfaces in a manner similar to FDM.

[0113] To investigate filament deformability in the infill, the window frame model in Figure 3D was modified to have single-layer infill densities from 10 to 90 percent. At 40% infill, the filament has an aspect ratio greater than 1, as expected from the single filament morphology shown in Figure 3, and at higher infill densities, the aspect ratio increases dramatically, as shown in Figures 4C and 4D. At these infill densities, the printing nozzle approaches the previously extruded filament in increasingly close proximity, thereby displacing the support laterally and stretching the nearby filament in the up-down direction. The degree of stretching is tightly coupled to the infill density. To see if the observed morphologies present in the perimeter and infill were consistent in prints containing both, the same frame model was printed at increasing infill densities (30, 50, and 70%) and increasing print heights (2, 3, 4, and 5 layers). By examining the morphology in 3D, it is clear that the behavior seen previously is present: stacked filaments (both perimeter and infill) are flattened against each other, and lateral filaments packed against each other are stretched in the up-down direction in Z, as shown in Figure 4E. At high infill densities (seen at 70% for builds with more than two layers), this translates to crowning, a print defect (indicated by an asterisk) where there is an unwanted excess of material in an area of ​​the print, resulting from the displacement of the ink by the extruder nozzle. This indicates that while the Z-step had to be adjusted for single perimeter or one-layer builds to achieve dissolution, this is not necessary for 3D builds, likely due to the increased material deposited, and the increased frequency of interactions with the print nozzle that can promote dissolution. Indeed, this reduction in Z-step most likely contributed to the crowning observed at 70% infill density. For all future prints, the Z-step was not changed in the G-code.

[0114] [Print calibration reveals difficulties printing with deformable inks]

[0115] In classical FDM additive manufacturing, a simple cube is used as a test model to calibrate and fine-tune extruder and print settings. We chose a calibration cube as a model to determine the general range of print settings suitable for embedded printing, as shown in Figure 5. As previously mentioned, when printing unmodified PDMS prepolymer, there is widespread clumping throughout the structure. Despite this, the support bath maintains the general shape of the cube, but upon carbopol dissolution and print removal, the cube breaks apart, leaving behind a mass of hardened PDMS, as shown in the top row of Figure 5. By incorporating HS II thixotropic additive (2.7% w / w) and setting the layer height to 50% of the extrusion width and the infill density to 100%, the filament maintains its printed geometric shape and even exhibits characteristic FDM features such as individual layers. Release from the support bath confirms that the layers have dissolved and the cube remains intact, but closer inspection reveals that the print is riddled with defects such as crowning (indicated by asterisks) and inconsistent dissolution (indicated by arrows), as shown in the middle row of Figure 5.

[0116] As shown in Figure 4E, due to the deformability of the material present in the FRE, material displacement can result in these defects. The filaments can flatten as they are stacked on top of each other, which is consistent with the filament profile used in the slicing software algorithm. At the same time, as the filaments pack together at a high infill density, material can be displaced vertically into adjacent layers and then shifted by the print nozzle during the move, resulting in crowning. Once a layer is completed, the print nozzle was observed to drag the ink from one corner of the cube to the other as it moves up in Z and transitions to printing the next layer. Due to the morphology and deformability inherent to this system, material is often displaced from its intended location, resulting in melting that may not be consistent across the print (visually represented by the change in opacity in Figure 5). In areas containing crowning, excess material packs together to form an essentially solid part. However, in other areas, the infill is not melted into the shell. The lack of melting at the infill / ambient interface is also a result of the elasticity of the support bath. This causes the ink to recoil slightly when the printing nozzle reverses direction, which often occurs where the infill meets its surroundings. If the two areas do not achieve physical contact, dissolution may not be achieved.

[0117] Here, the challenges of printing with deformable inks in an embedded printing system are clear: dissolution relies on contact with adjacent filaments, but these interactions, in addition to interactions with the passing print nozzle, often disrupt the ink and displace it from its intended location. Intelligent machine paths are another factor that can affect the fidelity and success of a print. From these observations, several guidelines are made for embedded printing. First, movements (movements that do not involve ink extrusion and therefore play no role in dissolution) should be made outside the body of the print (e.g., in the XY coordinates of the object being built) to minimize material displacement. Additionally, to account for the elasticity of the support bath, the overlap between the infill and the surroundings can be adjusted to 125% or more. Finally, an infill density of 90% or less is generally sufficient to prevent crowning when the extrusion width is 50% of the layer height, which may vary depending on the feature size. With these adjustments, dimensionally accurate calibration cubes with good interlayer dissolution were printed. These guidelines were used to inform the printing parameter selection and machine paths in all future prints.

[0118] Mechanical properties of cast and printed constructs.

[0119] After demonstrating the ability to print the modified inks, the mechanical properties of both the cast and printed constructs were of interest. To determine the effect of the rheology modifier on PDMS properties, three PDMS+HS II formulations ((i) 0%, (ii) 1.0%, and (iii) 2.7% w / w HS II) were cast and laser cut into tensile bar specimens for uniaxial tensile testing (Figure 6A). These tests revealed that the modulus decreased with increasing additive concentration, suggesting that the additive behaves as a plasticizer within the PDMS network, decreasing crosslink density (Figure 6B,C,D).

[0120] Next, the effect of infill pattern was examined. Infill patterns may be selected based on the desired structural integrity. Three infill patterns were selected: (iv) cubic, (v) aligned straight line, fill angle = 0°, perpendicular to the direction of the uniaxial tensile test (labeled "parallel"), and (vi) aligned straight line, fill angle = 90°, perpendicular to the direction of the test (labeled "perpendicular") (Figure 6E,F). Straight infill patterns are very commonly used in additive manufacturing and can typically be printed faster than more complex patterns. The fill angle was selected to determine how filament directionality affects mechanical properties. Cubic infill was selected because it can be used for functional additive manufacturing that requires strength in multiple directions. Perpendicular constructs were printed as rectangular prisms as opposed to the traditional dog-bone shape due to limitations in current slicing software. Testing showed that the parallel construct had a significantly larger modulus compared to the other two constructs (Figure 6G,H,I). Additionally, parallel and cubic constructs showed greater elongation to failure compared to perpendicular constructs. The effect of filament orientation on mechanical properties is consistent with traditional FDM, where constructs are weaker between layers (Figure 6J).

[16] Interestingly, when comparing the stress-strain traces of printed and cast constructs, there was a greater deviation in the cast construct, indicating that the casting and laser cutting processes created inconsistencies in the tensile specimens. At the same time, this indicates that printing produces consistent and uniform constructs. Together, these results demonstrate that mechanical properties can be tuned by altering additive concentration and infill pattern.

[0121] [Improving FRE by changing machine paths and printing process parameters]

[0122] To explore the geometric limits of the FRE platform, three test geometries were selected: hollow sphere, auxetic lattice, and double helix (Figure 7). The first attempt to print hollow spheres was moderately successful as most of the layers were fused together, except for layer separation that was mostly present in the top quarter of the sphere (Figure 7, left column). This supports previous observations that a single wall of filament is difficult to obtain fusion without decreasing the Z-step. Furthermore, the larger needle size (ID = 635 μm) prevented the slicing software from slicing the sphere without a large gap between the top and bottom layers. To improve layer fusion, a modular modification approach was taken. Specifically, the G-code was modified for each region of interest. The entire construct originally had four perimeters used, and by the addition of a modifier in Slic3r introducing six perimeters in the top 3 mm, as well as the use of a smaller needle (ID = 305 μm) and a flow fine adjustment of 125%, fused spheres were created. The addition of extra perimeter, as well as a higher flow rate, results in more ink being extruded, which allows for dissolution.

[0123] Next, an auxetic lattice was chosen to demonstrate the importance of retraction and smart transfer. Retraction is a print command that pulls material back into the nozzle to prevent unwanted material from oozing out of the nozzle and creating stringing artifacts. A lift command can be implemented in conjunction with retraction during transfer, which causes the extruder nozzle to lift a specified distance in Z above the layer currently being printed. This ensures that the nozzle does not drag material from one area of ​​the print to another, which is especially important with FREs where up-down filament stretching in Z (as demonstrated in Figure 4) can displace material upwards into upcoming layers. The first print (without retraction and lift commands) demonstrated many stringing events, especially outside of the build. These most likely result from ink oozing out of the nozzle during transfer, as well as displacement of ink by the nozzle. By implementing and optimizing retraction and lift commands, stringing events are greatly reduced, there is interlayer melting, and the lattice can be repeatedly stretched. Finally, a double helix was chosen as the last print. This structure is extremely difficult to cast or print via extrusion-based methods. Initial attempts to produce this structure failed - resulting in up-and-down stringing events when the nozzle was lifted for retraction. Early printer hardware was not robust enough for rapid retraction, and the large needle size limited the minimum feature size. By switching to a smaller nozzle (ID=406 μm) and using a custom-designed, more robust syringe adapter with a larger motor, larger retraction was possible, producing a double helix with a solid base, small features, and some stringing events.

[0124] These builds show more guidance for embedded printing. First, a modular approach to the machine path may need to be taken, and the G-code should be modified by the print area as necessary. Also, the importance of implementing movements that occur outside of the print is emphasized again. Interactions with the print nozzle and deformable inks have a detrimental effect on print fidelity. Finally, these prints show the importance of retraction and the need for robust hardware that can deal with thixotropic, viscous fluids. The FRE printing platform is not limited to the geometries shown here, and with modifications of these machine paths, complex geometries can be obtained, which is promising for the future of polymer additive manufacturing.

[0125] [Conclusion]

[0126] It is clear that many factors influence the success of printing soft polymers with FREs. Rheological modifications of structural materials can be leveraged to generate yield stress fluids that are more capable of maintaining their printed geometries. Additionally, intelligent machine path and careful selection of printing parameters can improve printed geometries. Specifically, interactions between the printing nozzle and the extruded filament can be minimized to prevent filament distortion. Movements should be configured to occur outside the body of the print, and retractions should be used to reduce string artifacts. A modular approach to machine path can achieve printed constructs with the highest fidelity. Additionally, robust additive manufacturing systems with robust hardware can be used to extrude thixotropic viscous fluids. The guidance provided in the examples herein can be extended to other material systems, greatly expanding the ability to utilize FREs to print soft polymers.

[0127] Any patent, publication, or other disclosure material identified herein is incorporated herein by reference in its entirety unless otherwise indicated, unless the incorporated material conflicts with existing definitions, descriptions, or other disclosure material explicitly set forth herein. Thus, to the extent necessary, the express disclosure set forth herein supersedes any conflicting material incorporated herein by reference. Any material, or portion thereof, that is said to be incorporated herein by reference but conflicts with existing definitions, descriptions, or other disclosure material set forth herein, is incorporated only to the extent that no conflict occurs between the incorporated material and the existing disclosure material. Applicant reserves the right to amend this specification to explicitly list any subject matter, or portion thereof, incorporated herein by reference.

[0128] In this specification, unless otherwise indicated, all numerical parameters should be understood to be prefaced in all instances by the term "about" and subject to the inherent variability characteristic of the underlying measuring technique used to determine the numerical value of the parameter. At the very least, and not as an attempt to limit the application of the doctrine of equivalents to the scope of the claims, each numerical parameter set forth herein should at least be construed in light of the number of reported significant digits and by applying ordinary rounding techniques.

[0129] Also, any numerical range recited herein includes all subranges contained within the recited range. For example, a range of "1 to 10" includes all subranges between (and including) the recited minimum value of 1 and the recited maximum value of 10, i.e., subranges having a minimum value of 1 or more and a maximum value of 10 or less. Any maximum numerical limitation recited herein is intended to include all lower numerical limitations contained therein, and any minimum numerical limitation recited herein is intended to include all higher numerical limitations contained therein. Accordingly, applicants reserve the right to amend this specification, including the claims, to expressly recite any subranges contained within an expressly recited range. All such ranges are inherently described herein.

[0130] Those skilled in the art will recognize that the articles and methods described herein and the accompanying discussion are used as examples for conceptual clarity, and various configuration modifications are contemplated. Thus, as used herein, the specific examples / embodiments described and the accompanying discussion are intended to be representative of their more general classes. In general, the use of any particular example is intended to represent its class, and the absence of specific components, devices, operations / actions, and objects should not be considered limiting. While the present disclosure provides descriptions of various specific aspects for the purpose of illustrating various aspects of the disclosure and / or its potential applications, it is understood that variations and modifications will occur to those skilled in the art. Thus, the inventions described herein should be understood to be at least as broad as they are claimed, and not more narrowly defined by the specific exemplary aspects provided herein.

Claims

1. 1. An additive manufacturing method comprising: depositing the building material onto a support material by applying a force to the building material through the nozzle that is at least a yield stress of the building material, by applying a force to the building material such that the building material flows through the nozzle, the building material comprising a polymer and a rheology modifier, the yield stress of the building material being in the range of 1 Pa to 10 kPa; repeating the deposition of the structural material to create an object; and and at least partially removing the support material from the object.

2. The method of claim 1, wherein the structural material comprises 0.1% to 50% by weight of the rheology modifier.

3. The method of any one of claims 1 to 2, further comprising curing the structural material after said depositing.

4. the structural material comprises a yield stress, and applying the force to the structural material comprises applying a force to the structural material of at least the yield stress; or the construction material includes thixotropic properties, and applying the force to the construction material includes applying a force that causes the construction material to flow through the nozzle; or the rheology modifier increases the viscosity of the build material and applying the force to the build material includes applying a force to cause the build material to flow through the nozzle; or The method according to any one of claims 1 to 3, which is a combination thereof.

5. The method of claim 1, wherein the yield stress of the structural material is in the range of 10 Pa to 200 Pa.

6. The method of any one of claims 1 to 5, wherein the polymer comprises a thermoset.

7. The method of any one of claims 1 to 6, wherein the polymer comprises a silicone-based polymer, an epoxy-based polymer, a urethane-based polymer, or a combination thereof.

8. The method of any one of claims 1 to 7, wherein the polymer comprises polydimethylsiloxane.

9. The method of any one of claims 1 to 8, wherein the rheology modifier comprises a thixotropic additive, a particulate filler, a polymeric additive, or a combination thereof.

10. 10. The method of any one of claims 1 to 9, wherein repeating the deposition of the structural material to fabricate an object comprises depositing a first layer of structural material and depositing a second layer of structural material proximate to the first layer such that deposition of the second layer of structural material deforms the first layer of structural material.