Manufacturing method of colorant dispersion liquid

Abstract

To provide a method for producing a color material dispersion liquid which enables production of a color material dispersion liquid that is excellent in dispersion stability of a color material and is also excellent in re-dispersibility after solidification.SOLUTION: A method for producing a color material dispersion liquid that is a method for producing a color material dispersion liquid containing water and a color material includes a polymerization step of performing polymerization reaction in a liquid phase containing a hydrophobic monomer having an organic solvent having two or more hydroxyl groups and / or ether groups in the molecule, an aromatic ring or an alkyl (meth) acrylate structure, and a hydrophilic monomer having a carboxylic acid group or a sulfonic acid group, and synthesizing a dispersion resin, in which a weight average molecular weight of the dispersion resin is 5,000 or more and less than 100,000, and a content of the component (A) corresponding to the hydrophobic monomer in the total constituent monomer contained in the dispersion resin is 50 mol% or more.SELECTED DRAWING: None

Description

[Technical field]

[0001] The present invention relates to a method for producing a colorant dispersion liquid. [Background technology]

[0002] A colorant dispersion liquid in which a colorant such as a pigment or a disperse dye is dispersed is used, for example, as an inkjet ink, etc. In such a colorant dispersion liquid, excellent dispersibility of the colorant and storage stability of the colorant dispersion liquid are required.

[0003] For this purpose, for example, an aqueous pigment dispersion containing a pigment, a pigment dispersing resin, a basic compound and water, which satisfies certain parameters, has been proposed (see Patent Document 1).

[0004] Patent Document 1 discloses a method for producing such an aqueous pigment dispersion, which comprises the steps of dispersing a pigment in a non-aqueous solvent using a pigment dispersing resin synthesized by polymerizing lauryl methacrylate, styrene, and acrylic acid in methyl ethyl ketone, removing the non-aqueous solvent, adding a basic compound and water, mixing and stirring, and irradiating with ultrasonic waves, in this order. [Prior art documents] [Patent documents]

[0005] [Patent Document 1] JP 2017-226760 A Summary of the Invention [Problem to be solved by the invention]

[0006] However, with the above-mentioned methods, it is difficult to maintain a stable dispersion state of the colorant for a long period of time, and there are problems in that the ink to which the invention is applied exhibits non-Newtonian properties and has poor re-dispersibility after solidification, which is likely to induce ejection defects in the inkjet method, for example. [Means for solving the problem]

[0007] The present invention has been made to solve the above-mentioned problems, and can be realized as the following application examples.

[0008] A method for producing a colorant dispersion liquid according to an application example of the present invention is a method for producing a colorant dispersion liquid containing water and a colorant, A polymerization process in which a polymerization reaction is carried out in a liquid phase containing an organic solvent having two or more hydroxyl groups and / or ether groups in the molecule, a hydrophobic monomer having an aromatic ring or a (meth)acrylic acid alkyl ester structure, and a hydrophilic monomer having a carboxylic acid group or a sulfonic acid group to synthesize a dispersion resin. and, a water mixing step of mixing the dispersion resin with the water; having The colorant is a disperse dye, the content of components other than the organic solvent, the hydrophobic monomer, the hydrophilic monomer, and the coloring material in the liquid phase is 5.0% by mass or less, The weight average molecular weight of the dispersion resin is 5,000 or more and less than 100,000, The content of the structural unit A corresponding to the hydrophobic monomer in all the structural monomers contained in the dispersion resin is 70mol% or more and 97mol% or less Yes the content of the structural unit B corresponding to the hydrophilic monomer in all the structural monomers contained in the dispersion resin is 3 mol % or more and 30 mol % or less; below <1> , <2> At least one of the following conditions must be met: . <1> In the polymerization step, in addition to the organic solvent, the hydrophobic monomer, and the hydrophilic monomer, the coloring material is further used. <2> The method further includes a colorant mixing step of mixing the dispersion resin with the colorant at least after the polymerization step.

[0009] In the method for producing a colorant dispersion liquid according to another application example of the present invention, the organic solvent is at least one selected from the group consisting of glycol ethers and polyhydric alcohols.

[0010] In the method for producing a colorant dispersion liquid according to another application example of the present invention, both the hydrophobic monomer and the hydrophilic monomer have a polymerizable double bond.

[0011] In the method for producing a colorant dispersion liquid according to another application example of the present invention, the hydrophobic monomer is at least one selected from the group consisting of butyl (meth)acrylate and styrene.

[0012] In addition, in the method for producing a colorant dispersion liquid according to another application example of the present invention, the hydrophilic monomer is at least one selected from the group consisting of vinyl sulfonic acid, (meth)acrylic acid, (meth)allyl sulfonic acid, 2-acrylamido-2-methylpropanesulfonic acid, and salts thereof.

[0014] In the method for producing a colorant dispersion liquid according to another application example of the present invention, the dispersing resin has a dispersity of 1.05 or more and less than 2.50.

[0015] In the method for producing a colorant dispersion liquid according to another application example of the present invention, the weight average molecular weight of the dispersion resin is 7,000 or more and less than 60,000.

[0019] A method for producing a colorant dispersion liquid according to another application example of the present invention includes a colorant crushing step of crushing the colorant in a liquid containing the water, the colorant, and the dispersion resin.

[0020] Furthermore, a method for producing a colorant dispersion liquid according to another application example of the present invention includes an ink preparation step of mixing water and an organic solvent having two or more hydroxyl groups and / or ether groups in the molecule with the liquid composition obtained through the colorant crushing step, to obtain the colorant dispersion liquid to be used as an ink for inkjet recording. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0021] Preferred embodiments of the present invention will now be described in detail. [1] Method for producing colorant dispersion liquid First, the method for producing the colorant dispersion liquid of the present invention will be described.

[0022] The method for producing a colorant dispersion liquid of the present invention is a method for producing a colorant dispersion liquid containing water and a colorant, and includes a polymerization step of carrying out a polymerization reaction in a liquid phase containing an organic solvent having two or more hydroxyl groups and / or ether groups in the molecule, a hydrophobic monomer having an aromatic ring or a (meth)acrylic acid alkyl ester structure, and a hydrophilic monomer having a carboxylic acid group or a sulfonic acid group, to synthesize a dispersion resin. The weight-average molecular weight of the dispersion resin is 5,000 or more and less than 100,000, and the content of the structural unit A corresponding to the hydrophobic monomer in all the structural monomers contained in the dispersion resin is 50 mol % or more.

[0023] This provides a method for producing a colorant dispersion liquid that is excellent in the dispersion stability of the colorant and excellent in redispersibility after solidification. Therefore, the colorant dispersion liquid produced using the method for producing a colorant dispersion liquid of the present invention has excellent long-term storage stability and, for example, excellent ejection stability by the inkjet method when applied to an inkjet recording ink. In addition, when a solvent is added to the colorant dispersion liquid to make it into an ink, the stable dispersion of the dispersion system can be prevented from being destroyed.

[0024] In the present invention, the colorant dispersion liquid refers to a dispersion liquid in which a colorant is dispersed in a liquid dispersion medium.

[0025] In particular, in this embodiment, in addition to the polymerization step, the process includes a water mixing step of mixing the dispersion resin with water, a colorant mixing step of mixing the dispersion resin with a colorant, a colorant crushing step of crushing the colorant in a liquid containing water, the colorant, and the dispersion resin, and an ink preparation step of mixing the liquid composition obtained as described above with water and an organic solvent having two or more hydroxyl groups and / or ether groups in the molecule to obtain the colorant dispersion liquid used as an inkjet recording ink. Each step will be described in detail below.

[0026] [1-1] Polymerization process In the polymerization process, a polymerization reaction is carried out in a liquid phase containing an organic solvent having two or more hydroxyl groups and / or ether groups in the molecule, a hydrophobic monomer having an aromatic ring or a (meth)acrylic acid alkyl ester structure, and a hydrophilic monomer having a carboxylic acid group or a sulfonic acid group, to synthesize a dispersion resin.

[0027] [1-1-1] Organic solvents The organic solvent used in the polymerization step includes those having two or more hydroxyl groups and / or ether groups in the molecule.

[0028] In this step, the organic solvent functions as a solvent that dissolves the hydrophobic monomer and the hydrophilic monomer, and allows the polymerization reaction to proceed more favorably as a homogeneous reaction. In addition, by using an organic solvent having two or more hydroxyl groups and / or ether groups in the molecule, the following effects can be obtained. That is, for example, when the finally obtained colorant dispersion liquid contains an organic solvent having two or more hydroxyl groups and / or ether groups in the molecule, the dispersion stability of the colorant in the colorant dispersion liquid, the storage stability of the colorant dispersion liquid, and the redispersibility of the colorant in the case where the colorant in the colorant dispersion liquid precipitates can be improved.

[0029] Such an organic solvent is preferably at least one selected from the group consisting of glycol ethers and polyhydric alcohols. This makes the above-mentioned effects more pronounced.

[0030] Examples of glycol ethers include alkylene glycol monoethers and alkylene glycol diethers.

[0031] Examples of alkylene glycol monoethers include ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol monoisopropyl ether, ethylene glycol monobutyl ether, ethylene glycol monohexyl ether, ethylene glycol monophenyl ether, diethylene glycol monomethyl ether, diethylene glycol monoethyl ether, diethylene glycol monobutyl ether, diethylene glycol monohexyl ether, triethylene glycol monomethyl ether, triethylene glycol monoethyl ether, triethylene glycol monobutyl ether, tetraethylene glycol monomethyl ether, tetraethylene glycol monoethyl ether, tetraethylene glycol monobutyl ether, propylene glycol monomethyl ether, propylene glycol monoethyl ether, dipropylene glycol monomethyl ether, and dipropylene glycol monoethyl ether.

[0032] Examples of alkylene glycol diethers include ethylene glycol dimethyl ether, ethylene glycol diethyl ether, ethylene glycol dibutyl ether, diethylene glycol dimethyl ether, diethylene glycol diethyl ether, diethylene glycol ethyl methyl ether, diethylene glycol dibutyl ether, diethylene glycol butyl methyl ether, triethylene glycol dimethyl ether, triethylene glycol diethyl ether, triethylene glycol dibutyl ether, triethylene glycol butyl methyl ether, tetraethylene glycol dimethyl ether, tetraethylene glycol diethyl ether, tetraethylene glycol dibutyl ether, propylene glycol dimethyl ether, propylene glycol diethyl ether, dipropylene glycol dimethyl ether, and dipropylene glycol diethyl ether.

[0033] Examples of polyhydric alcohols include alkanediols such as ethylene glycol, propylene glycol, 1,3-propanediol, 1,2-butanediol, 1,3-butanediol, 1,2-pentanediol, 1,3-pentanediol, 1,4-butanediol, 2,3-butanediol, 3-methyl-1,3-butanediol, 1,5-pentanediol, 2-methyl-2,4-pentanediol, 3-methyl-1,5-pentanediol, 1,2-hexanediol, 1,6-hexanediol, 1,2-octanediol, 2-methyl-1,3-propanediol, 2,2-dimethyl-1,3-propanediol, and 2-ethyl-1,3-hexanediol; dihydric alcohols such as diethylene glycol, triethylene glycol, tetraethylene glycol, and dipropylene glycol; and trihydric alcohols such as trimethylolpropane and glycerin.

[0034] Among the above, the organic solvent is preferably at least one selected from the group consisting of alkylene glycol monoethers and dihydric alcohols, and more preferably at least one selected from the group consisting of 1,2-butanediol, triethylene glycol monomethyl ether, and propylene glycol. This makes the above-mentioned effects more pronounced.

[0035] In addition, when the finally obtained color material dispersion liquid contains an organic solvent, it is preferable to use the same organic solvent as that contained in the finally obtained color material dispersion liquid as the organic solvent used in this step.

[0036] This makes it possible to further improve the dispersion stability of the colorant in the final colorant dispersion liquid, the storage stability of the colorant dispersion liquid, and the re-dispersibility of the colorant in the event that the colorant in the colorant dispersion liquid precipitates.

[0037] The liquid phase in which the polymerization reaction for polymerizing the dispersion resin is carried out may contain other organic solvents in addition to the organic solvent having two or more hydroxyl groups and / or ether groups in the molecule described above, such as DMF, THF, ethanol, etc.

[0038] The content of the organic solvent having two or more hydroxyl groups and / or ether groups in the molecule in the liquid phase in which the polymerization reaction is carried out is not particularly limited, but is preferably from 10% by mass to 70% by mass, more preferably from 15% by mass to 55% by mass, and even more preferably from 18% by mass to 40% by mass, based on the sum of the contents of the organic solvent, the hydrophobic monomer, and the hydrophilic monomer in the liquid phase in which the polymerization reaction is carried out.

[0039] Furthermore, the content of the organic solvent having two or more hydroxyl groups and / or ether groups in the molecule relative to the total amount of the organic solvent including other organic solvents is preferably 30% by mass or more, and more preferably 50% by mass or more.

[0040] This allows the polymerization reaction to proceed more smoothly, and improves the dispersion stability of the colorant in the final colorant dispersion liquid, the storage stability of the colorant dispersion liquid, and the re-dispersibility of the colorant in the case where the colorant in the colorant dispersion liquid precipitates.

[0041] [1-1-2] Hydrophobic monomer The hydrophobic monomer used in the polymerization step is a compound having an aromatic ring or a (meth)acrylic acid alkyl ester structure in the molecule.

[0042] The hydrophobic monomer may have the above-mentioned chemical structure, and the polymerization method is not particularly limited. Examples of the polymerization method of the hydrophobic monomer include addition polymerization, condensation polymerization, and ring-opening polymerization, and the addition polymerization is preferable, and the hydrophobic monomer preferably has a polymerizable double bond.

[0043] This makes it possible to improve the dispersion stability of the colorant in the finally obtained colorant dispersion liquid, the storage stability of the colorant dispersion liquid, and the like.

[0044] Examples of the hydrophobic monomer include (meth)acrylic acid alkyl esters such as methyl (meth)acrylate, ethyl (meth)acrylate, propyl (meth)acrylate, butyl (meth)acrylate, pentyl (meth)acrylate, and hexyl (meth)acrylate; vinyl aromatic compounds such as styrene and 2-vinylnaphthalene; and one or more selected from these may be used in combination. Among these, the hydrophobic monomer is preferably at least one selected from the group consisting of butyl (meth)acrylate and styrene.

[0045] This makes it possible to improve the reactivity in this step, while also improving the dispersion stability of the colorant in the finally obtained colorant dispersion liquid, the storage stability of the colorant dispersion liquid, and the re-dispersibility of the colorant in the case where the colorant in the colorant dispersion liquid precipitates.

[0046] The content of the hydrophobic monomer in the liquid phase in which the polymerization reaction is carried out is not particularly limited, but the ratio of the amount of the hydrophobic monomer to the sum of the amounts of the hydrophobic monomer and the hydrophilic monomer in the liquid phase in which the polymerization reaction is carried out is preferably 50 mol% or more and 99 mol% or less, more preferably 60 mol% or more and 98 mol% or less, and even more preferably 70 mol% or more and 97 mol% or less.

[0047] This makes it possible to improve the reactivity in this step, while also improving the dispersion stability of the colorant in the finally obtained colorant dispersion liquid, the storage stability of the colorant dispersion liquid, and the re-dispersibility of the colorant in the case where the colorant in the colorant dispersion liquid precipitates.

[0048] [1-1-3]Hydrophilic monomer The hydrophilic monomer used in the polymerization step is a compound having a carboxylic acid group or a sulfonic acid group in the molecule.

[0049] The hydrophilic monomer may have the above-mentioned chemical structure, and the polymerization method is not particularly limited. Examples of the polymerization method of the hydrophilic monomer include addition polymerization, condensation polymerization, and ring-opening polymerization, and the addition polymerization is preferable, and the hydrophilic monomer preferably has a polymerizable double bond.

[0050] This makes it possible to improve the dispersion stability of the colorant in the finally obtained colorant dispersion liquid, the storage stability of the colorant dispersion liquid, and the like.

[0051] Examples of hydrophilic monomers include vinyl sulfonic acid, (meth)acrylic acid, (meth)allyl sulfonic acid, vinyl carboxylate, 2-acrylamido-2-methylpropanesulfonic acid, and salts thereof. One or a combination of two or more selected from these can be used. Among these, at least one selected from the group consisting of vinyl sulfonic acid, (meth)acrylic acid, (meth)allyl sulfonic acid, 2-acrylamido-2-methylpropanesulfonic acid, and salts thereof is preferred, and (meth)acrylic acid and (meth)allyl sulfonic acid are more preferred.

[0052] This makes it possible to improve the reactivity in this step, while also improving the dispersion stability of the colorant in the finally obtained colorant dispersion liquid, the storage stability of the colorant dispersion liquid, and the re-dispersibility of the colorant in the case where the colorant in the colorant dispersion liquid precipitates.

[0053] The content of the hydrophilic monomer in the liquid phase in which the polymerization reaction is carried out is not particularly limited, but the content of the hydrophilic monomer relative to the sum of the amounts of the hydrophobic monomer and the hydrophilic monomer in the liquid phase in which the polymerization reaction is carried out is preferably 1 mol% or more and 50 mol% or less, more preferably 2 mol% or more and 40 mol% or less, and even more preferably 3 mol% or more and 30 mol% or less.

[0054] This makes it possible to improve the reactivity in this step, while also improving the dispersion stability of the colorant in the finally obtained colorant dispersion liquid, the storage stability of the colorant dispersion liquid, and the re-dispersibility of the colorant in the case where the colorant in the colorant dispersion liquid precipitates.

[0055] The ratio of the amount of (meth)acrylic acid to the sum of the amounts of all monomer components in the liquid phase in which the polymerization reaction is carried out is preferably 1 mol% or more and 49 mol% or less, more preferably 2 mol% or more and 30 mol% or less, and even more preferably 3 mol% or more and 20 mol% or less.

[0056] This makes it possible to improve the reactivity in this step, while also improving the dispersion stability of the colorant in the finally obtained colorant dispersion liquid, the storage stability of the colorant dispersion liquid, and the re-dispersibility of the colorant in the case where the colorant in the colorant dispersion liquid precipitates.

[0057] [1-1-4] Coloring materials The polymerization step may be carried out in a liquid phase containing the organic solvent, the hydrophobic monomer, and the hydrophilic monomer. For example, the liquid phase in which the polymerization step is carried out may further contain a coloring material.

[0058] This allows the dispersion resin to adhere more suitably to the surface of the colorant. Also, for example, the colorant mixing step described below can be omitted, or even if the colorant mixing step is performed, the amount of colorant to be mixed in the colorant mixing step can be reduced. The coloring material will be described in detail later.

[0059] As will be described in detail later, the coloring material may be mixed after the polymerization step, in which case the coloring material does not need to be contained in the liquid phase in the polymerization step.

[0060] [1-1-5] Other ingredients The liquid phase in which the polymerization step is carried out may contain components other than those described above. Hereinafter, in [1-1-5], such components are also referred to as "other components".

[0061] Examples of the other components include monomer components other than the hydrophobic monomer and the hydrophilic monomer, a polymerization initiator such as azobisisobutyronitrile, and a pH adjuster.

[0062] However, the water content in the liquid phase in which the polymerization reaction is carried out is preferably 2.0% by mass or less, more preferably 1.0% by mass or less, and even more preferably 0.5% by mass or less.

[0063] The content of other components in the liquid phase in which the polymerization reaction is carried out is preferably 6.0% by mass or less, and more preferably 5.0% by mass or less. The lower limit of the content of other components is 0 mass %.

[0064] [1-1-6]Reaction conditions The polymerization step may be carried out under any conditions so long as the monomer components including the hydrophobic monomer and the hydrophilic monomer are polymerized.

[0065] Although it depends on the type of monomer component, the polymerization step is usually carried out by heating the liquid phase in the presence of a polymerization initiator.

[0066] The heating temperature in the polymerization step is not particularly limited, but is preferably from 40°C to 90°C, more preferably from 45°C to 85°C, and even more preferably from 50°C to 80°C.

[0067] The reaction time in the polymerization step is not particularly limited, but is preferably from 1 hour to 24 hours, more preferably from 2 hours to 18 hours, and even more preferably from 3 hours to 16 hours.

[0068] The polymerization step may be carried out as a one-stage reaction or as a two or more stage reaction.

[0069] The dispersion resin obtained in this step is a copolymer containing the structural unit A corresponding to the hydrophobic monomer and the structural unit B corresponding to the hydrophilic monomer.

[0070] The weight average molecular weight of the dispersion resin obtained as described above may be from 5,000 to less than 100,000, and is preferably from 7,000 to less than 60,000. This makes the above-mentioned effects more pronounced.

[0071] Furthermore, the content of the structural unit A corresponding to the hydrophobic monomer in all the constituent monomers contained in the dispersed resin obtained as described above may be 50 mol% or more, but is preferably 50 mol% or more and 99 mol% or less, more preferably 60 mol% or more and 98 mol% or less, and even more preferably 70 mol% or more and 97 mol% or less. This makes the above-mentioned effects more pronounced.

[0072] In addition, the dispersing resin obtained by the polymerization reaction in the polymerization step preferably satisfies the following conditions.

[0073] In other words, the content of the structural unit B corresponding to the hydrophilic monomer in all the structural monomers contained in the dispersion resin is preferably 1 mol% or more and 50 mol% or less, more preferably 2 mol% or more and 40 mol% or less, and even more preferably 3 mol% or more and 30 mol% or less.

[0074] In addition, the dispersity of the dispersed resin, i.e., the weight average molecular weight Mw of the dispersed resin divided by the number average molecular weight Mn of the dispersed resin, is preferably 1.05 or more and less than 2.50, more preferably 1.20 or more and less than 2.40, and even more preferably 1.25 or more and less than 2.35.

[0075] This makes it possible to improve the dispersion stability of the colorant in the final colorant dispersion liquid, the storage stability of the colorant dispersion liquid, and the re-dispersibility of the colorant in the event that the colorant in the colorant dispersion liquid precipitates.

[0076] The dispersion resin synthesized as described above may be used in the steps described below in the liquid phase state of the polymerization step, but it is preferable to use it in the steps described below after purification.

[0077] The dispersion resin may be purified by any method, but can be purified, for example, as follows.

[0078] First, after the polymerization reaction is completed, the liquid phase, which is the reaction product, is diluted with a solvent as necessary, and then the diluted liquid is dropped into a poor solvent for the dispersed resin to precipitate the dispersed resin. The precipitated dispersed resin is then separated from the liquid phase by centrifugation or the like. The dispersed resin separated from the liquid phase is then dried. By such a method, the dispersed resin can be suitably purified.

[0079] When carrying out the above-mentioned purification, for example, tetrahydrofuran or the like can be used as the dilution solvent, and for example, hexane or the like can be used as the poor solvent.

[0080] [1-2]Water mixing process In the water mixing step, the dispersed resin obtained in the polymerization step is mixed with water. By including such a step, even if the polymerization step is carried out in a liquid phase that does not contain water or in a liquid phase with a relatively low water content, the water content in the finally obtained colorant dispersion can be adjusted to a suitable range, and the colorant dispersion can have suitable fluidity and viscosity. In addition, by carrying out this step before the colorant mixing step, the colorant mixing step can be carried out more suitably.

[0081] The amount of water mixed with the dispersion resin in this step is not particularly limited, but the amount of water mixed in this step per 100 parts by mass of the dispersion resin is preferably 200 parts by mass or more and 2000 parts by mass or less, more preferably 250 parts by mass or more and 1000 parts by mass or less, and even more preferably 300 parts by mass or more and 700 parts by mass or less. This makes the above-mentioned effects more pronounced.

[0082] In this step, other components may be mixed together with the dispersion resin and water. Examples of such components include pH adjusters such as triethanolamine and ammonia.

[0083] When a pH adjuster is used in this step, the pH of the composition obtained in this step is preferably 5.5 to 8.5, more preferably 6.0 to 8.0, and even more preferably 6.5 to 7.7.

[0084] This makes it possible to further improve the dispersion stability of the colorant in the final colorant dispersion liquid, the storage stability of the colorant dispersion liquid, and the re-dispersibility of the colorant in the event that the colorant in the colorant dispersion liquid precipitates.

[0085] In this step, the dispersion resin and water may be mixed in two or more stages. For example, this process may include a first process of mixing a dispersion resin with water, a second process of adding a pH adjuster to the composition obtained in the first process to adjust the pH, and a third process of mixing the composition obtained in the second process with water.

[0086] In this step, a heat treatment may be carried out, if necessary. The heating temperature in this step is not particularly limited, but is, for example, preferably from 40°C to 95°C, more preferably from 45°C to 90°C, and even more preferably from 50°C to 85°C.

[0087] [1-3] Color material mixing process In the colorant mixing step, the dispersion resin obtained in the polymerization step is mixed with the colorant.

[0088] This makes it possible to obtain a colorant dispersion liquid containing a sufficient content of colorant even when the previous polymerization step is carried out in a liquid phase containing no colorant or having a low content of colorant. This also makes it possible to effectively prevent the reaction rate of the intended polymerization reaction from decreasing and the progression of undesirable side reactions involving the colorant in the polymerization step.

[0089] In particular, in this embodiment, the composition obtained in the water mixing step described above, i.e., the composition containing water together with the dispersion resin, is mixed with the colorant. In other words, in this embodiment, the water mixing step is followed by the colorant mixing step.

[0090] This allows the colorant and the dispersing resin to be mixed more uniformly, and allows the dispersing resin to be more suitably attached to the surface of the colorant.

[0091] The colorant may be any colorant that can be contained in a dispersed state in the final colorant dispersion liquid, and examples of the colorant include acid dyes, reactive dyes, disperse dyes, sublimation dyes, and pigments, with disperse dyes being preferred.

[0092] When a disperse dye is used as a coloring material, the above-mentioned problems may occur significantly. In contrast, in the present invention, even when a disperse dye is used as a coloring material, the redispersibility can be improved and the above-mentioned problems can be effectively prevented. In other words, when the coloring material is a disperse dye, the effects of the present invention are more pronounced.

[0093] The disperse dye is not particularly limited, but specific examples thereof include the following.

[0094] Examples of yellow disperse dyes include CI Disperse Yellow 3, 4, 5, 7, 9, 13, 23, 24, 30, 33, 34, 42, 44, 49, 50, 51, 54, 56, 58, 60, 63, 64, 66, 68, 71, 74, 76, 79, 82, 83, 85, 86, 88, 90, 91, 93, 98, 99, 100, 104, 108, 114, 116, 118, 119, 122, 124, 126, 135, 140, 141, 149, 160, 162, 163, 164, 165, 179, 180, 182, 183, 184, 186, 192, 198, 199, 202, 204, 210, 211, 215, 216, 218, 224, 227, 231, 232, etc.

[0095] Examples of orange disperse dyes include CI Disperse Orange 1, 3, 5, 7, 11, 13, 17, 20, 21, 25, 29, 30, 31, 32, 33, 37, 38, 42, 43, 44, 45, 46, 47, 48, 49, 50, 53, 54, 55, 56, 57, 58, 59, 61, 66, 71, 73, 76, 78, 80, 89, 90, 91, 93, 96, 97, 119, 127, 130, 139, and 142.

[0096] Examples of red disperse dyes include CI Disperse Red 1, 4, 5, 7, 11, 12, 13, 15, 17, 27, 43, 44, 50, 52, 53, 54, 55, 56, 58, 59, 60, 65, 72, 73, 74, 75, 76, 78, 81, 82, 86, 88, 90, 91, 92, 93, 96, 103, 105, 106, 107, 108, 110, 111, 113, 117, 118, 121, 122, 126, 127, 128, 131, 132, 134, 135, 137, 143, 145, 146, 151, 152, 153, 154, 157, 159, 164, 167, 169, 177, 179, 181, 183, 184, 185, 188, 189, 190, 191, 192, 200, 201, 202, 203, 205, 206, 207, 210, 221, 224, 225, 227, 229, 239, 240, 257, 258, 277, 278, 279, 281, 288, 298, 302, 303, 310, 311, 312, 320, 324, 328, etc.

[0097] Examples of violet disperse dyes include CI Disperse Violet 1, 4, 8, 23, 26, 27, 28, 31, 33, 35, 36, 38, 40, 43, 46, 48, 50, 51, 52, 56, 57, 59, 61, 63, 69, 77, and the like.

[0098] An example of a green disperse dye is CI Disperse Green 9.

[0099] Examples of brown disperse dyes include CI Disperse Brown 1, 2, 4, 9, 13, 19, and the like.

[0100] Examples of blue disperse dyes include CI Disperse Blue 3, 7, 9, 14, 16, 19, 20, 26, 27, 35, 43, 44, 54, 55, 56, 58, 60, 62, 64, 71, 72, 73, 75, 79, 81, 82, 83, 87, 91, 93, 94, 95, 96, 102, 106, 108, 112, 113, 115, 118, 120, 122, 125, 128, 130, 139, 141, 142, 143, 146, 148, 149, 153, 154, 158, 165, 167, 171, 173, 174, 176, 181, 183, 185, 186, 187, 189, 197, 198, 200, 201, 205, 207, 211, 214, 224, 225, 257, 259, 267, 268, 270, 284, 285, 287, 288, 291, 293, 295, 297, 301, 315, 330, 333, etc.

[0101] Examples of black disperse dyes include CI Disperse Black 1, 3, 10, 24, and the like.

[0102] In the present invention, for example, one or a combination of two or more selected from the above coloring materials can be used.

[0103] [1-4] Color material crushing process In the coloring material crushing step, the coloring material is crushed in a liquid containing water, the coloring material, and a dispersion resin.

[0104] This allows the particle size of the colorant to be reduced, and allows the dispersion resin to be more suitably attached to the surface of the colorant particles, resulting in improved dispersion stability of the colorant in the final colorant dispersion, storage stability of the colorant dispersion, and redispersibility of the colorant in the case where the colorant in the colorant dispersion precipitates. This step can be suitably carried out using, for example, a ball mill, a bead mill, or the like.

[0105] In this specification, the average particle size refers to the average particle size based on volume, and can be determined, for example, by adding a sample to methanol, dispersing the sample for 3 minutes using an ultrasonic disperser, and measuring the dispersion using a Coulter Counter particle size distribution measuring instrument (TA-II model manufactured by COULTER ELECTRONICS INS) with an aperture of 50 μm.

[0106] [1-5] Ink mixing process In the ink preparation process, the liquid composition obtained through the colorant pulverization process is mixed with water and an organic solvent having two or more hydroxyl groups and / or ether groups in the molecule to obtain a colorant dispersion liquid to be used as an ink for inkjet recording.

[0107] This can improve the moisture retention of the colorant dispersion liquid used as an inkjet recording ink, and more effectively prevent the colorant dispersion liquid from drying in an inkjet head or the like when ejecting the colorant dispersion liquid by an inkjet method, and the solid content of the colorant dispersion liquid from unintentionally precipitating due to this, etc. The viscosity of the colorant dispersion liquid can be more suitably adjusted. As a result, the ejection stability of the colorant dispersion liquid by the inkjet method can be improved.

[0108] The organic solvent used in this step may be any one having two or more hydroxyl groups and / or ether groups in the molecule, but it is preferable that the organic solvent contains the same compound as the organic solvent used in the polymerization step.

[0109] This makes it possible to further improve the dispersion stability of the colorant in the final colorant dispersion liquid, the storage stability of the colorant dispersion liquid, and the re-dispersibility of the colorant in the event that the colorant in the colorant dispersion liquid precipitates.

[0110] [2] Colorant dispersion liquid Next, the colorant dispersion liquid according to the present invention will be described. The colorant dispersion according to the present invention contains water, a colorant, and the above-mentioned dispersion resin.

[0111] The colorant dispersion liquid according to the present invention may be used as an ink as it is, or may be used as a raw material for an ink. Also, the colorant dispersion liquid according to the present invention may be used as a paint, for example.

[0112] In addition, the colorant dispersion liquid according to the present invention preferably contains an organic solvent having two or more hydroxyl groups and / or ether groups in the molecule, and more preferably contains an organic solvent containing the same compound as that used in the polymerization step described above.

[0113] This makes it possible to further improve the dispersion stability of the colorant in the colorant dispersion, the storage stability of the colorant dispersion, and the redispersibility of the colorant in the case where the colorant in the colorant dispersion precipitates.

[0114] In the colorant dispersion liquid according to the present invention, each component constituting the colorant dispersion liquid according to the present invention preferably satisfies the same conditions as those described above. This provides the same effect as described above.

[0115] The content of the colorant in the colorant dispersion according to the present invention is not particularly limited, but is preferably from 1.0% to 50% by mass, and more preferably from 2.5% to 30% by mass.

[0116] This makes it possible to sufficiently increase the content of the colorant in the colorant dispersion liquid, while further improving the dispersion stability of the colorant in the colorant dispersion liquid, the storage stability of the colorant dispersion liquid, and the re-dispersibility of the colorant in the event of precipitation of the colorant in the colorant dispersion liquid.

[0117] In particular, when the colorant dispersion liquid according to the present invention is an ink for inkjet recording itself, the content of the colorant in the colorant dispersion liquid is preferably 1.0% by mass or more and 8.0% by mass or less, and more preferably 2.5% by mass or more and 6.0% by mass or less.

[0118] Furthermore, when the colorant dispersion liquid according to the present invention is a colorant dispersion liquid used for preparing an ink for inkjet recording, that is, a colorant dispersion liquid in the narrow sense or a paint, the content of the colorant in the colorant dispersion liquid is preferably 7% by mass or more and 50% by mass or less, and more preferably 10% by mass or more and 30% by mass or less.

[0119] The content of the dispersing resin in the colorant dispersion liquid according to the present invention is not particularly limited, but is preferably from 0.1% by mass to 25% by mass, and more preferably from 0.5% by mass to 15% by mass.

[0120] This makes it possible to further improve the dispersion stability of the colorant in the colorant dispersion, the storage stability of the colorant dispersion, and the redispersibility of the colorant in the case where the colorant in the colorant dispersion precipitates.

[0121] In particular, when the colorant dispersion liquid according to the present invention is an ink for inkjet recording itself, the content of the dispersion resin in the colorant dispersion liquid is preferably 0.1% by mass or more and 4% by mass or less, and more preferably 0.2% by mass or more and 3% by mass or less.

[0122] Furthermore, when the colorant dispersion liquid according to the present invention is a colorant dispersion liquid used for preparing an ink for inkjet recording, i.e., a colorant dispersion liquid in the narrow sense or a paint, the content of the dispersion resin in the colorant dispersion liquid is preferably 0.7% by mass or more and 25% by mass or less, and more preferably 1.0% by mass or more and 15% by mass or less.

[0123] When the colorant dispersion liquid according to the present invention is an ink for inkjet recording itself, the content of the organic solvent in the colorant dispersion liquid is not particularly limited, but is preferably from 2% by mass to 20% by mass, and more preferably from 3% by mass to 10% by mass.

[0124] Furthermore, when the colorant dispersion liquid according to the present invention contains the organic solvent, the proportion of the organic solvent having a hydroxyl group in the molecule to the total organic solvent contained in the colorant dispersion liquid is preferably 33 mass % or more, and more preferably 50 mass % or more.

[0125] This improves the redispersibility of the colorant in the colorant dispersion liquid when the colorant precipitates.

[0126] When the content of the colorant in the colorant dispersion liquid of the present invention is XC [% by mass] and the content of the dispersion resin in the colorant dispersion liquid of the present invention is XD [% by mass], it is preferable to satisfy the relationship of 0.10≦XD / XC≦1.00, it is more preferable to satisfy the relationship of 0.20≦XD / XC≦0.70, and it is even more preferable to satisfy the relationship of 0.30≦XD / XC≦0.60.

[0127] This makes it possible to sufficiently increase the content of the colorant in the colorant dispersion liquid, while further improving the dispersion stability of the colorant in the colorant dispersion liquid, the storage stability of the colorant dispersion liquid, and the re-dispersibility of the colorant in the event of precipitation of the colorant in the colorant dispersion liquid.

[0128] The colorant dispersion liquid according to the present invention may contain components other than those described above. Hereinafter, in [2], such components are also referred to as “other components”. Examples of such components include pH adjusters, chelating agents, preservatives, antifungal agents, rust inhibitors, flame retardants, dispersants other than the above-mentioned dispersing resins, surfactants, antioxidants, ultraviolet absorbers, oxygen absorbers, dissolution aids, and penetrating agents.

[0129] Examples of the chelating agent include ethylenediaminetetraacetate, etc. Examples of the preservatives and antifungal agents include sodium benzoate, sodium pentachlorophenol, sodium 2-pyridinethiol-1-oxide, sodium sorbate, sodium dehydroacetate, 1,2-dibenzisothiazolin-3-one, 4-chloro-3-methylphenol, etc. Examples of the rust inhibitors include benzotriazole, etc.

[0130] As the preservative / antifungal agent, for example, a compound having an isothiazolinone ring structure in the molecule can be suitably used.

[0131] As the surfactant, various surfactants such as anionic surfactants, cationic surfactants, and nonionic surfactants can be used.

[0132] The content of other components is preferably 3.0% by mass or less, and more preferably 2.0% by mass or less. The lower limit of the content of other components is 0 mass %.

[0133] When the colorant dispersion liquid according to the present invention contains other components, such components may be added, for example, in the above-mentioned steps or in a step other than the above-mentioned steps.

[0134] The viscosity of the colorant dispersion liquid according to the present invention at 25°C is preferably from 2 mPa·s to 10 mPa·s, more preferably from 3 mPa·s to 8 mPa·s, and even more preferably from 4 mPa·s to 6 mPa·s.

[0135] This makes it possible to improve the ejection stability of the colorant dispersion liquid according to the present invention when it is ejected by the inkjet method.

[0136] The viscosity was measured at 25°C using a viscoelasticity tester (e.g., Atago Co., Ltd., VISCO 6800) at a shear rate of 10 [s -1 The viscosity can be measured by reading the viscosity at

[0137] Although the preferred embodiments of the present invention have been described above, the present invention is not limited to these.

[0138] For example, in the above-mentioned embodiment, a method in which the polymerization step, the water mixing step, the colorant mixing step, the colorant pulverization step, and the ink preparation step are performed in this order has been typically described, but in the method for producing a colorant dispersion liquid of the present invention, at least some of the steps other than the polymerization step may be omitted, the order of the steps may be changed, or the treatment described as being performed in a plurality of separate steps may be performed in the same step. More specifically, when the colorant dispersion liquid is something other than ink, for example, when the colorant dispersion liquid is not ink itself but a colorant dispersion liquid used in preparing ink, the ink preparation step described above may be omitted.

[0139] The method for producing a colorant dispersion liquid of the present invention may have a configuration other than that described above. EXAMPLES

[0140] Next, specific examples of the present invention will be described. [3] Preparation of colorant dispersion (Dispersion 1) In a sidearm flask, 16 parts by mass of butyl acrylate as a hydrophobic monomer, 16 parts by mass of sodium methallyl sulfonate as a hydrophilic monomer, 5 parts by mass of acrylic acid as a hydrophilic monomer, 2 parts by mass of 2-{[(carboxymethyl)sulfanylthiocarbonyl]sulfanyl}propanoic acid, and 1 part by mass of azobisisobutyronitrile as a polymerization initiator were placed. 60 parts by mass of 1,2-butanediol as an organic solvent was added thereto to dissolve each component, and a Dimroth condenser was attached. Then, the mixture was reacted at 75°C for 6 hours while stirring with a stirrer.

[0141] After the reaction was completed, the reaction product was diluted with tetrahydrofuran and dropped into hexane to precipitate a yellow solid. The yellow precipitate was collected by centrifugation and then vacuum dried at 50°C for 10 hours to obtain 50 parts by mass of a dispersion resin as a copolymer. The obtained dispersion resin had a weight average molecular weight of 8200.

[0142] Next, a 1L eggplant-shaped flask was set, 15 parts by mass of the dispersion resin as the copolymer obtained as described above and 70 parts by mass of pure water were added, and a Dimroth condenser was attached. Then, the mixture was heated to 80°C while stirring with a stirrer. Triethanolamine was added to the mixture until the pH became 7.6, and the mixture was adjusted to 100 parts by mass with pure water. After cooling to 25°C, the dissolved aqueous solution was obtained as a varnish liquid.

[0143] Next, 50 parts by weight of the above varnish liquid, 15 parts by weight of CI Disperse Yellow 232 as a water-insoluble colorant, and 35 parts by weight of pure water were added and ground in a bead mill for 1 hour to obtain a colorant dispersion containing 6% by weight of copolymer and 12% by weight of colorant.

[0144] (Dispersion 2) A colorant dispersion was produced in the same manner as in Dispersion 1, except that a mixed solvent of 30 parts by weight of triethylene glycol monomethyl ether and 30 parts by weight of THF was used instead of 60 parts by weight of 1,2-butanediol as the organic solvent.

[0145] (Dispersion 3) A colorant dispersion was produced in the same manner as in Dispersion 1, except that propylene glycol was used as the organic solvent instead of 1,2-butanediol.

[0146] (Dispersion 4) A colorant dispersion was produced in the same manner as in Dispersion 1, except that 21 parts by mass of styrene and 16 parts by mass of acrylic acid were used instead of 16 parts by mass of butyl acrylate, 16 parts by mass of sodium methallyl sulfonate, and 5 parts by mass of acrylic acid.

[0147] (Dispersion 5) A colorant dispersion was produced in the same manner as in Dispersion 2, except that 21 parts by mass of styrene and 16 parts by mass of acrylic acid were used instead of 16 parts by mass of butyl acrylate, 16 parts by mass of sodium methallyl sulfonate, and 5 parts by mass of acrylic acid.

[0148] (Dispersion 6) A colorant dispersion was produced in the same manner as Dispersion 3, except that 21 parts by mass of styrene and 16 parts by mass of acrylic acid were used instead of 16 parts by mass of butyl acrylate, 16 parts by mass of sodium methallyl sulfonate, and 5 parts by mass of acrylic acid.

[0149] (Dispersion 7) A colorant dispersion was produced in the same manner as in Dispersion 1, except that 16 parts by mass of butyl acrylate, 16 parts by mass of acrylamido-2-methylpropanesulfonic acid, and 5 parts by mass of acrylic acid were used instead of 16 parts by mass of butyl acrylate, 16 parts by mass of sodium methallylsulfonate, and 5 parts by mass of acrylic acid.

[0150] (Dispersion 8) A colorant dispersion was produced in the same manner as in Dispersion 2, except that 16 parts by weight of butyl acrylate, 16 parts by weight of acrylamido-2-methylpropanesulfonic acid, and 5 parts by weight of acrylic acid were used instead of 16 parts by weight of butyl acrylate, 16 parts by weight of sodium methallylsulfonate, and 5 parts by weight of acrylic acid.

[0151] (Dispersion 9) A colorant dispersion was produced in the same manner as in Dispersion 3, except that 16 parts by weight of butyl acrylate, 16 parts by weight of acrylamido-2-methylpropanesulfonic acid, and 5 parts by weight of acrylic acid were used instead of 16 parts by weight of butyl acrylate, 16 parts by weight of sodium methallylsulfonate, and 5 parts by weight of acrylic acid.

[0152] (Dispersion 10) A colorant dispersion was produced in the same manner as in Dispersion 1, except that tetrahydrofuran was used as the organic solvent instead of 1,2-butanediol.

[0153] (Dispersion 11) A colorant dispersion was produced in the same manner as in Dispersion 4, except that tetrahydrofuran was used as the organic solvent instead of 1,2-butanediol.

[0154] The conditions of the dispersion resin contained in the colorant dispersion liquid obtained in each of the Examples and Comparative Examples are summarized in Table 1, and the conditions of the colorant dispersion liquid obtained in each of the Examples and Comparative Examples are summarized in Table 2. In the table, butyl acrylate is indicated as "BA", styrene is indicated as "St", acrylic acid is indicated as "AA", sodium methallyl sulfonate is indicated as "NaMPS", acrylamido-2-methylpropanesulfonic acid is indicated as "ATBS", CI Disperse Yellow 232 is indicated as "DY232", 1,2-butanediol is indicated as "1,2-BD", ethylene glycol monomethyl ether is indicated as "EGME", propylene glycol is indicated as "PG", tetrahydrofuran is indicated as "THF", weight average molecular weight is indicated as Mw, and number average molecular weight is indicated as Mn.

[0155] [Table 1]

[0156] [4] Preparation of ink composition Other components were mixed with each of the dispersions prepared in the above [3] so as to obtain the compositions shown in Table 2, and the ink compositions of Examples 1 to 9 and Comparative Examples 1 and 2 were produced.

[0157] In Table 2, CI Disperse Yellow 232 is indicated as "DY232," 1,2-butanediol as "1,2-BD," triethylene glycol monomethyl ether as "TEGMME," propylene glycol as "PP," 1,2 diethylene glycol as "1,2-DEG," carboxymethylcellulose sodium salt (manufactured by Fuji Film Wako Pure Chemical Industries, Ltd.) as "CMCNa," the silicone-based surfactant BYK-348 (manufactured by BYK-Chemie) as "BYK-34," and triethanolamine as "TEA."

[0158] [Table 2]

[0159] [5] Evaluation The ink compositions obtained in the above Examples and Comparative Examples were evaluated as follows.

[0160] [5-1] Changes in particle size distribution First, 30 mL of each of the ink compositions obtained in the examples and comparative examples was placed in a predetermined container and allowed to stand in an environment of 60° C. for 5 days.

[0161] Then, using a Coulter counter particle size distribution measuring instrument (TA-II model manufactured by COULTER ELECTRONICS INS) with an aperture of 50 μm, the average particle size of the colorant contained in each colorant dispersion liquid after standing for 5 days in an environment of 60°C was determined and evaluated according to the following criteria. It can be said that the smaller the increase rate of the average particle size, the better the dispersion stability of the colorant and the storage stability of the colorant dispersion liquid. B or higher was considered to be a good level.

[0162] A: The increase in average particle size is less than 10%. B: The increase rate of the average particle size is 10% or more and less than 30%. C: The increase rate of the average particle size is 30% or more.

[0163] [5-2]Viscosity First, the ink compositions obtained in the above-mentioned respective Examples and Comparative Examples were subjected to a viscoelasticity test at a shear rate of 10 [s -1 The viscosity was measured at this time and evaluated according to the following criteria. B or higher was considered to be good.

[0164] A: Shear rate 10 [s -1 ] is 4 mPa s or more and 6 mPa s or less. B: Shear rate 10 [s -1 ] is more than 6 mPa·s and less than 10 mPa·s. C: Shear rate 10 [s -1 ] is more than 10 mPa s.

[0165] [5-3] Viscosity change First, 30 mL of each of the ink compositions obtained in the examples and comparative examples was placed in a predetermined container and allowed to stand in an environment of 60° C. for 5 days.

[0166] Then, at 25°C, a viscoelasticity tester (Pysica, MCR-300) was used to measure the shear rate of 10 [s -1 The viscosity was measured at this time and evaluated according to the following criteria. B or higher was considered to be good.

[0167] A: Shear rate 10 [s -1 ] is 4 mPa s or more and 6 mPa s or less. B: Shear rate 10 [s -1 ] is more than 6 mPa·s and less than 10 mPa·s. C: Shear rate 10 [s -1 ] is more than 10 mPa s.

[0168] [5-4] Redispersibility First, the ink compositions obtained in each of the Examples and Comparative Examples were dropped onto a slide glass, dried, and solidified. Then, the slide glass was immersed in a sample bottle containing ink water, taking great care not to stir the ink water, and the behavior of redispersion of the solid matter was visually confirmed and evaluated according to the following criteria. B or higher was determined to be a good level. Note that, as the ink water, a liquid having a composition in which the colorant and dispersion resin were removed from each ink composition was used for each of the Examples and Comparative Examples.

[0169] A: Dispersed in the ink water. B: The ink is slightly dispersed in the water. C: The ink is not dispersed in the water.

[0170] These results are shown in Table 3 together with the average particle size of the colorant contained in each ink composition.

[0171] [Table 3]

[0172] As is clear from Table 3, excellent results were obtained in the present invention. In contrast, satisfactory results were not obtained in the comparative examples.

Claims

1. A method for producing a colorant dispersion liquid containing water and a colorant, comprising the steps of: a polymerization step of synthesizing a dispersion resin by carrying out a polymerization reaction in a liquid phase containing an organic solvent having two or more hydroxyl groups and / or ether groups in the molecule, a hydrophobic monomer having an aromatic ring or a (meth)acrylic acid alkyl ester structure, and a hydrophilic monomer having a carboxylic acid group or a sulfonic acid group; and a water mixing step of mixing the dispersion resin with the water, The colorant is a disperse dye, a content of components other than the organic solvent, the hydrophobic monomer, the hydrophilic monomer, and the coloring material in the liquid phase is 5.0% by mass or less, The weight average molecular weight of the dispersion resin is 5,000 or more and less than 100,000, the content of the structural unit A corresponding to the hydrophobic monomer in all the constituent monomers contained in the dispersion resin is 70 mol% or more and 97 mol% or less, and the content of the structural unit B corresponding to the hydrophilic monomer in all the constituent monomers contained in the dispersion resin is 3 mol% or more and 30 mol% or less, A method for producing a colorant dispersion liquid, which satisfies at least one of the following conditions <1> and <2>: <1> In the polymerization step, in addition to the organic solvent, the hydrophobic monomer, and the hydrophilic monomer, the coloring material is further used. <2> The method further includes a colorant mixing step of mixing the dispersion resin with the colorant at least after the polymerization step.

2. The method for producing a colorant dispersion liquid according to claim 1 , wherein the organic solvent is at least one selected from the group consisting of glycol ethers and polyhydric alcohols.

3. The method for producing a colorant dispersion liquid according to claim 1 , wherein both the hydrophobic monomer and the hydrophilic monomer have a polymerizable double bond.

4. 4. The method for producing a colorant dispersion liquid according to claim 1, wherein the hydrophobic monomer is at least one selected from the group consisting of butyl (meth)acrylate and styrene.

5. The method for producing a colorant dispersion liquid according to any one of claims 1 to 4, wherein the hydrophilic monomer is at least one selected from the group consisting of vinyl sulfonic acid, (meth)acrylic acid, (meth)allyl sulfonic acid, 2-acrylamide-2-methylpropanesulfonic acid, and salts thereof.

6. The method for producing a colorant dispersion liquid according to claim 1 , wherein the dispersing resin has a dispersity of 1.05 or more and less than 2.

50.

7. The method for producing a colorant dispersion liquid according to claim 1 , wherein the dispersion resin has a weight average molecular weight of 7,000 or more and less than 60,000.

8. The method for producing a colorant dispersion liquid according to claim 1 , further comprising a colorant crushing step of crushing the colorant in a liquid containing the water, the colorant, and the dispersion resin.

9. 9. The method for producing a colorant dispersion liquid according to claim 8, further comprising an ink preparation step of mixing water and an organic solvent having two or more hydroxyl groups and / or ether groups in the molecule with the liquid composition obtained through the colorant pulverization step, to obtain the colorant dispersion liquid to be used as an ink for inkjet recording.