Solvent Application of Anhydromevalonolactone

Abstract

This paper describes solvents and cosolvents containing anhydromevalonolactone (aMVL), as well as various industrial applications of such solvents. aMVL has several advantageous properties for use in solvents, such as a high boiling point, low melting point, low viscosity, non-flammability, water solubility, very low volatility, and excellent solvation ability. Exemplary industrial applications of solvents containing aMVL include polymer production, polymer recycling, mold making, fiber making, membrane making, thermosetting coating production, paint production, paint removal, paint strippers, cleaning products, degreasing products, nitrile synthesis, alkylation, synthesis gas production, carbon-carbon cross-coupling reactions, metal-organic framework synthesis, halogenation reactions, pharmaceutical formulations, fungicide and / or herbicide formulations, seed treatment products, bioregulators, and battery or capacitor electrolytes.

Description

[Technical field]

[0001] CROSS-REFERENCE TO RELATED APPLICATIONS This application claims priority benefit to U.S. Provisional Application No. 62 / 757,905, entitled SOLVENT APPLICATIONS OF ANHYDROMEVALONOLACTONE, filed November 9, 2019, which is incorporated by reference in its entirety.

[0002] The present invention is generally directed to solvents comprising anhydromevalonolactone and various industrial uses thereof. [Background technology]

[0003] Solvents are ubiquitous in the chemical industry. They are used in various concentrations and under different conditions in a variety of industries, from paper and pulp processing to pharmaceuticals. Depending on the application, they are applied as cleaning fluids, working fluids or recycling fluids.

[0004] Two of the most widely used solvents today are NMP and DCM, with a combined market size of 1.4 million tons per year in 2014. The largest uses of NMP and DCM are polymer dissolution and paint stripping, respectively. However, the use of these two solvents poses serious health hazards, including acute neurotoxicity, organ damage, carcinogenicity, teratogenicity, and muscle deformation [EPA-740-R1-7005, EPA-740-R1-7004]. Summary of the Invention

[0005] Herein, anhydromevalonolactone (4-methyl-5,6-dihydro-2H-pyran-2-one or aMVL), a bio-derived molecule, is described for its performance as a solvent for various applications. This polar molecule has many attractive properties, such as a high boiling point (200-250 °C), low melting point (-40-20 °C), low viscosity (3-5 mPas), non-flammability, water solubility (approximately 600-900 g / L), very low volatility (vapor pressure: 30-40 Pa, 67 °C), and excellent solvation ability (according to Hansen solubility parameters). aMVL can be produced inexpensively by dehydration of mevalonolactone (MVL), a biointermediate that can be produced in high yields by fermentation using a variety of biomass feedstocks, making aMVL a green and easily accessible bio-based molecule [U.S. Patent Application Publication No. 2016 / 0145227, incorporated herein in its entirety]. aMVL behaves similarly to DCM and NMP in terms of solvating capacity, based on the Hansen solubility parameters, a system that quantifies the potential for one material to dissolve in another.

[0006] The objective of the present invention is to demonstrate the performance and applicability of aMVL for various solvent applications and its use in place of more hazardous polar aprotic solvents such as NMP, DCM and / or ethers. The aforementioned applications include, but are not limited to, the use of aMVL as a solvent, reaction medium, dehydrating agent, diluent, extractant, cleaning agent, degreaser, absorbent and / or dispersant. Additionally, the present invention uses aMVL as a paint remover, battery electrolyte, and metalworking fluid.

[0007] In one embodiment, a solvent for one or more industrial applications is provided. The solvent comprises anhydromevalonolactone.

[0008] In another embodiment, a process for producing a solvent for industrial use is provided, the process comprising: (a) forming a solvent comprising anhydromevalonolactone; and (b) providing the solvent for industrial use.

[0009] In another embodiment, a process for producing or recycling a polymer is provided, the process comprising: (a) providing a solvent comprising anhydromevalonolactone; and (b) producing the polymer or recycling the polymer in the presence of the solvent.

[0010] In another embodiment, an electrolytic capacitor is provided. The electrolytic capacitor includes an anode, a cathode, and an electrolyte. The electrolyte includes a solvent. The solvent includes anhydromevalonolactone.

[0011] In another embodiment, a process for removing oil, grease, paint, coating, or stains from a surface is provided, the process comprising the steps of (a) providing a solvent comprising anhydromevalonolactone, and (b) applying the solvent to a surface.

[0012] In another embodiment, there is provided the use of anhydromevalonolactone as a solvent in one or more industrial applications.

[0013] In another embodiment, a process for recycling a polymer is provided, the process comprising at least: (a) dissolving at least one waste polymer in a solvent selected from the group consisting of anhydromevalonolactone, methyl ethyl ketone, benzyl acetate, ethyl benzoate, cyclohexanone, cyclopentyl methyl ether, dichloromethane, and co-solvent mixtures thereof, thereby forming a polymer mixture; (b) contacting the reaction mixture with an absorbent or adsorbent to form a purified polymer mixture; (c) contacting the purified polymer mixture with at least one anti-solvent, thereby recovering dissolved polymer and a residue stream comprising the solvent and the anti-solvent; (d) separating the retentate stream into a recovered solvent stream and a recovered anti-solvent stream; (e) filtering the dissolved polymer to form a first filtered polymer; (f) washing the first filtered polymer to form a washed polymer; (g) filtering the washed polymer to form a second filtered polymer; (h) drying the second filtered polymer to form the final polymer product. [Brief description of the drawings]

[0014] [Figure 1] FIG. 1 is a schematic diagram of a process for recovering and recycling waste polymers using aMVL and / or other co-solvents, according to one embodiment of the present invention. [Diagram 2] 1 is a graph showing FTIR data of recovered polycarbonate by aMVL and comparison with a control according to one embodiment of the present invention. [Diagram 3] 1 is a graph showing comparative results of volatility testing of aMVL, DCM, and NMP. [Figure 4] 1 is a set of photographs showing paint removal by aMVL solvent compared to DCM solvent. [Figure 5A] FIG. 1 is a perspective view of an electrolytic capacitor according to one embodiment of the present invention. [Figure 5B] FIG. 5B is a close-up view of the electrodes and electrolyte interface of the electrolytic capacitor of FIG. 5A. [Figure 5C] FIG. 5B is a schematic diagram of the inside of a casing portion of the electrolytic capacitor of FIG. 5A. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0015] Embodiments of the invention are generally directed to solvents comprising anhydromevalonolactone (aMVL) and their use in one or more industrial applications. The solvent may be substantially pure aMVL, or a co-solvent comprising a mixture of aMVL and one or more other components. In certain embodiments, the solvent comprises aMVL and / or more co-solvents selected from the group consisting of methyl ethyl ketone, benzyl acetate, ethyl benzoate, cyclohexanone, cyclopentyl methyl ether, and dichloromethane. In certain other embodiments, the solvent consists of (or consists essentially of) aMVL. In certain embodiments, the solvent comprises about 10 to about 100% by weight, preferably about 50 to about 99% by weight, of aMVL. In certain embodiments, the solvent comprises at least about 1, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, or 99% by weight of aMVL. The solvent generally has a boiling point of about 200 to about 250°C, preferably about 225 to about 240°C. The solvent generally has a melting point of about -40 to about 20°C, preferably about -30 to about -10°C. The solvent generally has a viscosity of about 3 to about 5 mPa.s at standard ambient temperature and pressure. The solvent generally has a water solubility of about 600 to about 900 g / L, preferably about 750 to about 850 g / L, at standard ambient temperature and pressure. The solvent generally has a vapor pressure of about 30 to about 40 Pa at 67°C.

[0016] Solvents comprising aMVL may be used in a variety of different industrial applications, some of which are described in more detail herein. Exemplary industrial applications include polymer manufacturing processes, polymer recycling processes, mold making processes, fiber making processes, membrane manufacturing processes, thermosetting coating manufacturing processes, coating manufacturing processes, paint removal, paint strippers, cleaning products, degreasing products, nitrile synthesis, alkylation, synthesis gas production, carbon-carbon cross-coupling reactions, metal organic framework synthesis, halogenation reactions, pharmaceutical formulations, fungicide and / or herbicide formulations, seed treatment products, bioregulators, battery or capacitor electrolytes, or combinations thereof. Accordingly, certain embodiments of the present invention are directed to a process for producing a solvent for industrial applications. The process includes (a) forming a solvent comprising aMVL, and (b) providing the solvent to an industrial application. Certain industrial applications using aMVL solvents are described in the following description and examples.

[0017] Polymer manufacturing applications In one or more embodiments of the present invention, the solvent is used in a process for producing, modifying, and / or recycling a polymer (including a copolymer). In certain embodiments, the solvent is used in a process for producing a polymer, comprising the steps of (a) providing a solvent comprising aMVL, and (b) producing a polymer in the presence of the solvent. The polymer can be produced using a variety of techniques, depending on the properties of the solvent, including aMVL, with or without other co-solvents.

[0018] In one embodiment, a solvent comprising aMVL can be used to dissolve one or more polymers. In certain embodiments, the one or more polymers comprise (consist of, or consist essentially of) a polymer selected from the group consisting of polysulfones, polyesters, polycarboxylic acids, polyanhydrides, polyacrylates, polyacrylamides, polyacrylonitriles, polyvinyl chlorides, polyvinyl esters, polyamides, polyimides, polyamideimides, polyvinyl acetals, polyoxyalkylenes, polystyrenes, polycarbonates, polyurethanes, polyureas, and copolymers thereof. Because aMVL has high solubility with the corresponding monomers, conventional organic solvents, and water, an optimal solvent mix specific to a given application can be used. Thus, in certain embodiments, a process for producing a polymer comprises dissolving a polymer in a solvent comprising aMVL.

[0019] In one embodiment, a solvent comprising aMVL is used to prepare molded articles. The solvents described herein are particularly useful for such applications because aMVL is non-corrosive, non-flammable, and can produce concentrated solutions of moldable compounds from a range of polymers. Thus, in certain embodiments, the process of producing a polymer includes forming a concentrated solution comprising the polymer in a solvent. In certain such embodiments, the polymer is selected from the group consisting of polyacrylonitrile, polyvinyl chloride, polystyrene, and combinations thereof. Solvents comprising aMVL can also be used for cold wetting of plastics due to their swelling and solubilizing action.

[0020] In one embodiment, aMVL-containing solvents readily dissolve polymers such as polyacrylonitrile, aromatic polyamides, polyureas, polyvinyl esters, and alcohols, and / or copolymers thereof. Thus, in certain preferred embodiments, the process of producing a polymer includes dissolving one or more of the above polymers and / or copolymers in aMVL-containing solvent. Most of these are insoluble or only slightly soluble in other solvents. Thus, the use of aMVL, with or without additives, is an excellent medium to solvate these polymers for spinning and extrusion into fibers.

[0021] In another embodiment, polymers such as polysulfone and polycarbonate are widely used to manufacture membranes in separation processes such as ultrafiltration, permeation, and gas purification. aMVL can be used as a solvent to produce such membranes due to the high solvation ability of the polymeric material. Thus, in a particular preferred embodiment, the process of producing the polymer includes dissolving one or both of polysulfone and polycarbonate in a solvent containing aMVL.

[0022] In another embodiment, aMVL is a non-corrosive, high boiling compound with excellent solvation ability and chemical resistance, and is therefore an advantageous solvent for baked coatings that cure at temperatures between about 80°C and about 150°C. aMVL can improve rheological properties, which leads to coatings and finishes with excellent flowability and higher covering power. Thus, coatings are more homogeneous and non-porous, more resistant to chemicals, and have higher mechanical strength. aMVL is an excellent solvent for most coating ingredients, including, but not limited to, acrylates, polyurethanes, polyvinyl chloride-based, polyamide-imide-based wire enamels, water-based coatings, and printing inks, optionally containing UV-curable resins. Thus, in certain preferred embodiments, the process for producing the polymer includes dissolving one or more of the above components in a solvent containing aMVL.

[0023] In another embodiment, aMVL can be used as a medium during the production of thermosetting coatings for electrical insulation. Amide-group-containing polyisocyanates can be formed in a condensation reaction between aMVL solution of a polybasic carboxylic anhydride and a monomeric polyisocyanate. The resulting polyisocyanate finish results in a coating with excellent mechanical and dielectric properties, especially on copper conductors. aMVL in this application serves two purposes, firstly as a reaction medium in the manufacturing process and secondly as a viscosity modifier that remains in the final coating. Thus, in certain preferred embodiments, the process of producing a polymer includes reacting aMVL with precursors (e.g., polybasic carboxylic anhydrides and monomeric polyisocyanates) to form a reaction product (e.g., a polyisocyanate) in a solvent containing aMVL.

[0024] Since aMVL is non-corrosive, has a high boiling point, and is relatively inert under most conditions, in one embodiment, it can serve as an excellent solvent for polymerization reactions. Most free radical polymerization initiators (AIBN, BPO, TMA, and DTBP) show no effect on aMVL. In addition, aMVL only opens its ring under very basic conditions or under high temperature and H2 pressure, making it applicable as a solvent for ring-opening polymerization reactions. In particular, aMVL can be used to produce polycarboxylic acids, polyesters, polyvinyl esters, polycarbonates, polysulfones, polyamides, and polyamideimides. Thus, in certain preferred embodiments, the process of producing a polymer includes mixing a polymerization initiator and / or one or more monomers in a solvent containing aMVL. Exemplary monomers include MMA and styrene.

[0025] In certain embodiments, all or part of the forming step is carried out at a temperature of about 20 to about 200°C, preferably about 40 to about 180°C, more preferably about 60 to about 150°C. In certain embodiments, all or part of the forming step is carried out at a pressure of about 0.01 to about 20 MPa, preferably about 0.05 to about 15 MPa, more preferably about 0.1 to about 10 MPa. In certain embodiments, particularly when the polymer is dissolved in a solvent containing aMVL, the polymer is present in the solution as a concentration of about 1 to about 90% by weight, preferably about 2 to about 50% by weight, more preferably about 5 to about 25% by weight. In certain embodiments, the contact time to achieve dissolution of the polymer in the solvent is about 0.5 to about 48 hours, preferably about 1 to about 24 hours, more preferably about 2 to about 12 hours. In certain embodiments, particularly in polymer synthesis embodiments, the monomer concentration in the reaction mixture containing the solvent is about 0.1 to about 90% by weight, preferably about 0.2 to about 49% by weight, more preferably about 5 to about 25% by weight. In certain such embodiments, the reaction mixture comprises an initiator at a concentration of from about 0.1 to about 10% by weight, preferably from about 1 to about 5% by weight.

[0026] Polymer recycling applications In one or more embodiments of the present invention, a solvent, and in certain embodiments, a solvent comprising aMVL, can be used to recover and recycle waste polymers. The process generally includes the steps of (a) providing a solvent, and (b) recycling the polymer in the presence of the solvent. In certain embodiments, the solvent is selected from the group consisting of aMVL, methyl ethyl ketone, benzyl acetate, ethyl benzoate, cyclohexanone, cyclopentyl methyl ether, dichloromethane, and co-solvent mixtures thereof. In certain embodiments, the solvent comprises substantially pure aMVL. In certain embodiments, the solvent comprises aMVL and a co-solvent selected from the group consisting of methyl ethyl ketone, benzyl acetate, ethyl benzoate, cyclohexanone, cyclopentyl methyl ether, and dichloromethane. In certain such embodiments, the solvent comprises at least about 10, 50, 80, 90, or 99% by weight of aMVL, with the total weight of the solvent (including the co-solvent) being 100% by weight. However, in other such embodiments, the solvent comprises less than about 1, 0.5, or 0.1 wt.% aMVL, based on 100 wt.% total weight of the solvent (including co-solvent). The polymer recycling process may incorporate one or more of the techniques described above and may utilize the same or different temperatures, pressures, contact times, and / or concentrations as described for polymer production.

[0027] An exemplary polymer recycling process is shown in Figure 1. Waste polymer P is dissolved in a solvent solution S in a unit operation 10 under conditions optimal for dissolution to form a polymer mixture. In certain preferred embodiments, the waste polymer is a polymer or copolymer selected from the group consisting of polymers and / or copolymers are polysulfones, polyesters, polycarboxylic acids, polyanhydrides, polyacrylates, polyacrylamides, polyacrylonitriles, polyvinyl chlorides, polyvinyl esters, polyamides, polyimides, polyamideimides, polyvinyl acetals, polyoxyalkylenes, polystyrenes, polycarbonates, polyurethanes, polyureas, and copolymers thereof.

[0028] The solution containing the polymer mixture is then passed through bed 12 to contact an adsorbent or absorbent to remove color, dyes, fillers, and other impurities, thereby forming a purified polymer mixture. In certain embodiments, the adsorbent or absorbent comprises one or more of silica, activated carbon, ion exchange resin, diatomaceous earth, montmorillonite, and zeolite. The solution containing the purified polymer mixture is then contacted with an anti-solvent of choice AS in tank 14 to recover the dissolved polymer and generate a residue stream comprising the solvent and the anti-solvent. In certain embodiments, the anti-solvent is selected from the group consisting of water, inorganic acid solution, inorganic alkaline solution, alcohol, aromatic compounds, esters, ethers, aldehydes, amines, ketones, organic halides, amides, lactones, lactams, C5-C10 olefins, C5-C10 hydrocarbons, and C5-C15 terpenes, or mixtures thereof. In preferred embodiments, the anti-solvent comprises water and / or ethanol. In certain embodiments, the ratio of solvent to anti-solvent is from about 10:1 to about 1:10, preferably from about 5:1 to about 1:5, and more preferably from about 4:1 to about 1:4.

[0029] The precipitated polymer is then filtered 16, washed 18, and filtered again 20. The filtered polymer is then dried in unit 22 to recover the final polymer. The residue stream, which comprises the solvent and anti-solvent (S / AS) mixture, is then processed in unit 24 in a separation step that may include, but is not limited to, flash distillation, continuous distillation, extractive distillation, azeotropic distillation, evaporation, absorption, membrane separation, or liquid-liquid extraction, thereby producing a recovered solvent stream and a recovered anti-solvent stream from separator unit 24. The recovered solvent stream can be recycled and combined with the solvent during dissolution in unit operation 10. The anti-solvent stream can be recycled and combined with the anti-solvent during contacting in anti-solvent mixture tank 14.

[0030] Other Solvent Applications In one or more embodiments, a solvent comprising aMVL can be used to remove oil, grease, paint, coating, or stains from a surface. The process includes the steps of (a) providing a solvent comprising anhydromevalonolactone and (b) applying the solvent to a surface. Particular embodiments of this and other uses (as well as related compositions and processes) are described below.

[0031] In one embodiment, aMVL can be successfully employed as a cleaning and degreaser component due to its high solvating power for oils and greases. Its miscibility with water and most conventional organic solvents allows for the production of highly effective products that can be tailored for use in different applications. Solvents containing aMVL can be used alone or mixed and / or with additives to remove oil, carbon deposits, and other tar-like polymeric residues from metal, glass, ceramic, wood, and other surfaces. Mixtures of aMVL can be used to clean articles or surfaces soiled with oil, grease, soot, glue, etc. by immersion in the bath. In another embodiment, aMVL can be used to degrease metals prior to surface treatment. In certain embodiments, aMVL-based cleaning products can be used on exterior / interior walls for graffiti removal and for ultrasonic cleaning of items such as optical lenses or dental prostheses.

[0032] In one embodiment, aMVL can be used as a low-VOC, recyclable paint stripper. In this embodiment, a paint stripper is defined as any solvent or mixture of solvents that can successfully dissolve industrial or commercial paints within a reasonably acceptable time frame. The high boiling point and high solubility of the solvent in water allows for efficient recycling, reducing costs as well as environmental impacts. aMVL has a higher boiling point and favorable toxicity profile while having similar performance to DCM. It can be mixed with other additives such as esters, alcohols, ethers, and water to modify the activity of the paint for a particular application. In addition, aMVL can be mixed with other solvents to produce a foaming type paint stripper that is useful for removing a variety of paints, varnishes, lacquers, and other coatings or finishes, especially from relatively large surfaces. These paint strippers are easy to use, have low volatility, are environmentally friendly, and have reduced fire hazards. In particular, aMVL can be used in concentrations of about 0.1 to about 99% by weight with other additives for use as a paint stripper.

[0033] Because aMVL is a chemically stable, strong polar solvent, in one embodiment it can be used as a reaction medium for chemical reactions where an inert medium is desirable. Thus, the present invention, in certain embodiments, is directed to processes in which chemical reactions are carried out in the presence of a solvent, diluent, or dispersant that includes aMVL. Some of these applications include, but are not limited to, alkylation of acetylides, synthesis of nitriles, and reaction media for producing syngas. aMVL can also be used as a dipolar aprotic solvent for carbon-carbon cross-coupling reactions [Sonogashira, Suzuki-Miyaura, Heck] halogenation reactions, and metal-organic framework (MOF) synthesis. Solvents commonly used for these reactions are NMP and N,N-dimethylformamide (DMF).

[0034] In another embodiment, aMVL can be used as a solvent or co-solvent for the formation of compounds used in, but not limited to, pharmaceuticals, insecticides, fungicides, herbicides, seed treatment products, and bioregulators where highly polar solvents are required.

[0035] In one embodiment, aMVL blend with common solvents may be utilized to clean and degrease single crystal silicon wafers for ICs. In another embodiment, aMVL may be used as a solvent to remove fluxing agent residues after soldering to prevent corrosion of circuit boards. This may be accomplished with an aMVL-based solvent blend. In another embodiment, aMVL may be used to selectively remove polymer coatings from specific areas on a printed circuit board.

[0036] In one or more embodiments, aMVL is used in processes for modifying polymers, including the production of molded articles, inks, pigments, resins, dyes, fibers, wires, thin films, coatings, microparticles, nanoparticles, and membranes. In a preferred embodiment, the solvent is used in the production of batteries and wires, particularly battery separators and wire enamels. Solvents containing aMVL are particularly useful as electrolyte solutions in the presence of insoluble organic and inorganic solids. In certain embodiments, the solids are graphene and / or graphite. Solvents containing aMVL are also particularly useful in the production of membranes with different porosity.

[0037] In a preferred embodiment, aMVL is an advantageous electrolyte in a battery or capacitor due to its high dielectric constant, low melting point, and high boiling point. aMVL can be used as an electrolyte in a lithium-ion or lithium-air battery, or as an electrolyte in an aluminum electrolytic capacitor for electronics or automotive applications. An exemplary electrolytic capacitor 100 is shown in Figures 5A, 5B, and 5C. The capacitor 100 includes leads 104 and a case 102 that contains an electrolyte solution including a solvent composition according to an embodiment of the present invention. The case 102 prevents leakage of the solvent electrolyte solution 114 and allows the solvent 114 to evaporate to the interface between the separator film 110 and the electrodes 106, 108. The anode 106 and the cathode 108 may include, for example, aluminum foil. The anode 106 further includes an oxide film 116 formed on the rough surface facing the separator film 110. An element closing tape 112 may also be included adjacent to the cathode 108.

[0038] Additional advantages of various embodiments of the present invention will become apparent to those skilled in the art upon review of the disclosure herein and the examples below. It will be understood that the various embodiments described herein are not necessarily mutually exclusive, unless otherwise stated herein. For example, features described or illustrated in one embodiment may be included in other embodiments, but are not necessarily included. Thus, the present invention encompasses various combinations and / or integrations of the specific embodiments described herein.

[0039] As used herein, the phrase "and / or," when used in a list of two or more items, means that any one of the listed items may be employed alone, or any combination of two or more of the listed items may be employed. For example, if a composition is described as including or excluding components A, B, and / or C, the composition may include or exclude A only, B only, C only, a combination of A and B, a combination of A and C, a combination of B and C, or a combination of A, B, and C.

[0040] The present description also uses numerical ranges to quantify certain parameters related to various embodiments of the present invention. When numerical ranges are provided, it should be understood that such ranges are to be interpreted as providing literal support for claim limitations that recite only the lower limit of the range, as well as for claim limitations that recite only the upper limit of the range. For example, a disclosed numerical range of about 10 to about 100 provides literal support for claims that recite "about 10 or more" (no upper limit) and claims that recite "about 100 or less" (no lower limit). EXAMPLES

[0041] The following examples and prophetic examples illustrate experiments using solvents according to embodiments of the present invention, however, it should be understood that these examples are provided by way of illustration and not as limiting the overall scope of the invention.

[0042] Example 1 Polymer solubility in aMVL A Q-Tube glass pressure vessel was charged with 2.17±0.2 g (2 mL) of aMVL and approximately 10 wt. % of the test polymer. The vessel was equipped with a stir bar and placed on a hot plate. The aMVL and polymer containing solution was stirred at 500 RPM at 80° C. under ambient conditions for 24 hours. After 24 hours, the solution was cooled to room temperature and filtered using filter paper placed in a Buchner funnel. The remaining polymer solids were rinsed using water, filtered, and quenched with N 2 The solid was dried under gas. The dried solid was finally weighed to determine the change in weight after contact with aMVL. Table 1 shows the results of this experiment. [Table 1]

[0043] Example 2 Effect of temperature on polymer solubility The procedure described in Example 1 was carried out at two temperatures, 80° C. and 150° C. The higher dissolution temperature allowed for the dissolution of certain polymers, such as nylon 12. A comparison of polymer solubility in aMVL between these two temperatures is shown in Table 2. [Table 2]

[0044] Example 3 Polymer solubility in aMVL and other cosolvents A 50:50 mixture of aMVL and other co-solvents and neat solutions were placed in a 20 mL scintillation glass vial with a working volume of 15 mL. 5% by weight of waste polycarbonate was added to the solution. In the case of low boiling point co-solvents, the mixture was heated to 38 °C, whereas in the case of high boiling point (>150 °C) co-solvents, the solution was heated to 80 °C, 100 °C, or 120 °C. The mixture was left stirring for 12 h. After 12 h, the mixtures were visually analyzed for solubility. The data for the mixtures are shown in Table 3. [Table 3]

[0045] Example 4 Removing color and other impurities from polymer solutions The solution of dissolved polymer from Example 3 was contacted with DARCO 20-40 mesh granular activated carbon. The low viscosity solution was gravity fed through 2 g of charcoal packed in a glass pipette. The high viscosity solution was contacted with 2 g of charcoal and gently shaken for 1 minute. After contact, the high viscosity solution was filtered through a fritted filter. After the adsorption process, a colorless polymer solution was obtained. Visual inspection data is shown in Table 3 above.

[0046] Example 5 Polymer recovery by antisolvent Polymers found to have dissolved in any of the mixtures from Examples 1-4, formed liquid solutions or gels, and / or been treated with activated carbon were investigated for recovery using water, ethanol, or methanol as anti-solvent at a ratio of 10:1 of anti-solvent to dissolved solution. The dissolved polymer solutions from Examples 1, 2, 3, and 4 were added dropwise to a stirred beaker containing 10 times the anti-solvent to the mass of the solvent solution (provided ratios above). The mixture was stirred for 30 minutes, after which the polymer precipitate was removed by gravity filtration. After the initial filtration was completed, the polymer was washed with anti-solvent. The polymers analyzed and the results are shown in Table 4. [Table 4]

[0047] Example 6 Polymer recovery by evaporating the solvent The DCM polycarbonate solution of Example 3 was placed in a 100 mL round bottom flask in a rotary evaporator. The evaporator was set to a vacuum pressure of 12 mmHg and the water bath was kept at 40°C. The evaporator was stirred at 60 rpm. Approximately half of the DCM was evaporated. After this evaporation, approximately 15 mL of deionized water was added to the round bottom flask. The majority of this solution was then evaporated under the same conditions. After this evaporation, the residual polymer was washed with 10 mL of deionized water, which was also removed via rotary evaporation. The residual polymer was dried overnight in an oven at 50°C.

[0048] Example 7 Analysis of polymer recovered after color removal Polycarbonate samples from Example 4 were precipitated in Example 5 and analyzed by Differential Scanning Calorimetry (DSC), Fourier Transform Infrared Spectroscopy (FTIR), and Gel Permeation Chromatography (GPC). These samples were compared to the waste polycarbonate starting material. Data from the GPC and DSC measurements are summarized in Table 3 above. FTIR data of the recovered polycarbonate from aMVL compared to the control is shown in Figure 2.

[0049] Example 8 Effect of polymerization initiators on aMVL Approximately 0.2 g of aMVL was mixed with approximately 0.2 g of styrene, methyl methacrylate (MMA), or prepared neat with approximately 10 mg of one or a mixture of the following polymerization initiators: azobisisobutyronitrile (AIBN), benzoyl peroxide (BPO), trimethylaluminum (TMA), or di-tert-butyl peroxide (DTBP), or a 4:1 mixture of BPO:TMA. The mixture was solvated with 1 mL of solvent (deuterated chloroform, CDCl3, or deuterated benzene, C6D6), sealed in an NMR tube in a glove box, and heated to 75 °C. At different time intervals, the reaction mixture was analyzed by proton (1H) NMR to identify the polymerization activity.

[0050] In the case of a neat solution of aMVL with the polymerization initiators, the aMVL did not undergo any reaction during the course of the experiment, indicating that none of the polymerization initiators interacted with the aMVL (Table 5, entries 1-5). Polymerizations of styrene (Table 5, entries 6-9) and MMA (Table 5, entries 10-12) using aMVL as the solvent were comparable to polymerizations using chloroform as well as benzene as the solvent. The results are summarized in Table 5. [Table 5]

[0051] Example 9 Measurement of the dielectric constant of aMVL The impedance of pure aMVL was measured using an Agilent 4284A Precision LCR Meter. All electrodes of the LCR meter were immersed in 120 mL of pure anhydrous aMVL solution. The LCR meter was set in series circuit mode to calculate the capacitance of the solution. This capacitance was then converted to a dielectric constant using the following formula:

number

[0052] Example 10 Use of aMVL in Aluminum Electrolytic Capacitors (Prophetic) The capacitor element is formed by winding up an anode foil and a cathode foil with a separator inserted between them. The anode foil used is an aluminum foil obtained by chemically or electrochemically etching 99.9% pure aluminum foil in an acidic solution to increase its surface area and then chemically treating it in an ammonium adipate aqueous solution so as to form an anodic oxide film layer on its surface. The cathode foil used is an aluminum foil with a purity of 99.9% that has been etched to increase its surface area.

[0053] The capacitor element constructed in this manner is impregnated with a pure anhydrous aMVL solution for driving the electrolytic capacitor. The capacitor element impregnated with the electrolyte is housed in an aluminum cylindrical housing with a bottom, and a sealing member made of butyl rubber is inserted into the open end of the housing, which is then retracted to seal the aluminum electrolytic capacitor. The assembly is shown in Figures 5A, 5B, and 5C.

[0054] The aluminum electrolytic capacitor constructed in this way can be subjected to high temperature service life tests. The aluminum electrolytic capacitor has a rating of 50WV, 100mF. The test conditions are 125°C, 1,000 hours under rated voltage load, and 125°C, 1,000 hours without load.

[0055] Example 11 paint removal Consumer paints, including Krayton spray paint and Rust-Oleum latex paint, were spot painted onto metal surfaces and allowed to dry for 12 hours. Paint removability was compared using aMVL and dichloromethane (DCM) by adding 100uL of each solution to the surface and gently wiping the metal surface with a paper towel. Figure 4 shows the visual paint removability with aMVL compared to DCM.

[0056] Example 12 Volatility of aMVL for recycling paint strippers. Experiments comparing the volatility of aMVL with that of NMP (N-methyl-2-pyrrolidone) and DCM (dichloromethane) were conducted by preparing samples of each solvent in 20 mL scintillation vials. Samples were kept uncapped in a fume hood and weighed at intervals to determine the rate of mass loss. As shown in Figure 3, aMVL is non-volatile compared to DCM and NMP. This allows for higher recovery and less loss when recycled into paint removal applications.

[0057] Example 13 Effect of additives on paint removal (predictive) Paint stripper compositions can be prepared by combining aMVL and oils of vegetable, animal, or petrochemical origin with any solvent or thickener components and mixing until a homogenous mixture is obtained. The additives tested are as follows: Aluminum panels (3" x 6") can be painted with either Krayton's Kraft paint or Rust-Oleum's latex paint. One coat of paint approximately 1.5 mm thick can be applied. Each panel can then be treated with the aforementioned mixture in three different spots. Each spot can be approximately 0.5 to 1.0 inch in diameter. The time required for the paint in each spot to completely bubble off the substrate can then be measured.

[0058] The composition was also tested for its ability to remove multiple coats of commercial paint from wood. Pressure treated pine wood was painted sequentially with the following paints: (a) one coat of white shellac (aged 14 hours), (b) two coats of white alkyd semi-gloss paint (aged 1 week), (c) two coats of red flat exterior acrylic paint (aged 1 week), (d) one coat of black exterior alkyd semi-gloss paint (aged 4 days), (e) one coat of white shellac (aged 1 day), and (f) one coat of white flat vinyl acrylic paint (aged 1 month). Additives: ·Soybean oil Corn oil Peanut oil Olive oil Inedible animal fat Turpentine Xylene Mineral oil ·Dipropylene glycol methyl ether acetate Methyl tert-butyl ether

[0059] Example 14 Stain Removal and Household Cleaning (Prophetic) Solutions of various concentrations of aMVL (0.5-100% by weight) can be prepared in water. Cotton fabrics can develop a variety of carbonaceous deposits, fatty residues, vegetable oil, and wine stains up to 2x2 inches in size. aMVL solutions can be applied to these stains and left for 24 hours at different temperatures (20°C, 40°C, 60°C). After 24 hours, these fabric patches are washed with water and then dried in a vacuum oven at 80°C for 2-4 hours. After drying, these fabric samples can be compared to commercial stain removers and control samples for a qualitative measurement of stain removal.

[0060] Example 15 Polyimide coating formation (predictive) To 2 g of aMVL containing a small amount of water (approximately 0.05-0.1%), 1.6 g of 2,2-bis(4-(3,4-dicarboxyphenoxy)-)phenylpropane (4,4'-BPATA), and 0.72 g of 4,4'-methylenedianiline (MDA) can be added with stirring. Stirring is continued for 3-4 hours while the mixture of ingredients is heated to 45°C and maintained at that temperature to form a clear, homogeneous, moderately viscous solution. A portion of the above prepared solution can be poured onto aluminum foil and heated at 120°C for 5 minutes, 140°C for 5 minutes, and 160°C for 15 minutes. A 3 mil thin film of the cured polymer can be produced.

[0061] Example 16 Preparation of polyamide-imide coatings (predictive) It can be synthesized by adding 237.5 g of 4,4'-MDI (as an isocyanate component) and 192 g (1.0 mol) of trimeric acid anhydride (TMA) (as an acid component) to 12.5 g of 2,4'-diphenylmethane diisocyanate (MDI) and reacting with aMVL (1000 g). The solution is then further diluted with 300 g of N,N-dimethylformamide (DMF). Thus, a polyamideimide resin-based insulating varnish with a resin component concentration of about 25% by mass is prepared. The varnish can then be applied around a copper wire with a diameter of 0.8 mm and baked.

[0062] Example 17 Formation of microporous polysulfone membranes (predictive). The source solution for forming the membrane can be prepared by homogeneously dissolving 15 parts of polysulfone, 69 parts of aMVL, 15 parts of polyvinylpyrrolidone, and 1 part of water. This solution is sprayed onto a glass plate using a pour coater so that the thickness of the sprayed solution is 100 to 200 μm, and hot air at 40 ° C is blown onto the surface of the sprayed solution sample. The sample is immediately immersed in a solidification bath containing 20 ° C water to obtain a microporous membrane.

[0063] The average pore size of each resulting membrane can be determined in accordance with ASTM-f-316-03, and the depth of the dense layer forming the surface can be measured by electron microscopy.

[0064] Example 18 Formation of porous polysulfone membranes (predictive). A thin film-forming stock solution can be prepared by homogeneously mixing 15 parts of polysulfone, 66 parts of aMVL, 15 parts of polyvinylpyrrolidone, 2 parts of lithium chloride, and 2 parts of water. The solution is cast onto a glass plate using a modified blade to a thickness of about 200 μm on a dry basis, and air at 25° C. is blown onto the surface of the cast thin film at a speed of 1.0 m / s. The thin film is then immediately immersed in a coagulation bath filled with water at 25° C. to obtain a microporous membrane.

[0065] The average pore size of each resulting membrane can be determined in accordance with ASTM-f-316-03, and the depth of the dense layer forming the surface can be measured by electron microscopy.

[0066] Example 19 Preparation of polycarbonate membranes (prophetic) A composition of 52 wt.% tetrabromobisphenol A polycarbonate, 32.5 wt.% aMVL (solvent), and 15.5 wt.% triethylene glycol (TEG) (non-solvent) (solvent to non-solvent ratio of approximately 2:1) can be fed to the melt pot of a melt pot extruder. Dichloromethane (DCM) in an amount equal to 30 wt.% of the total composition is added to the melt pot. The mixture is heated to 95°C at least until the mixture is a homogenous solution. Most of the DCM flashes off during this heating step. A nitrogen purge is passed through the melt pot at 500 cm3 per minute, drawing the nitrogen with the volatilized DCM from the melt pot. The mixture is passed from the melt pot to a transfer line and pumped to a hollow fiber spinneret apparatus at a flow rate of approximately 15 g per minute.

[0067] The transfer line and spinneret face equipment are maintained at a temperature of 75°C. The mixture is extruded into hollow fibers through a 254 micron annulus with an outside diameter of approximately 1800 microns while a core gas pin delivers a core gas of nitrogen into the bore at a rate of 8.8 standard cm3 per minute. The line speed is 100 feet per minute. The hollow fibers are extruded into a 1 foot long air quench zone at ambient temperature. The fibers are passed through a 4°C water quench bath with a 2 second residence time. The fibers are captured and then placed in a 90°C water bath for 10 minutes. The fibers are hung vertically and dried by passing air over the fibers at a flow rate of 100 feet per minute for 2 hours.

[0068] The prepared hollow fiber membranes can be examined by scanning electron microscopy (SEM) and the average pore size can be measured according to ASTM-f-316-03. Such membranes have porous outer and inner surfaces.

[0069] Example 20 Preparation of graphene-PHB nanocomposite (predictive) The biopolymer polyhydroxybutyrate (PHB) can be dissolved in aMVL at a solvent concentration of 33 mg / mL with stirring at 120 °C. A graphene dispersion is prepared without centrifugation to maximize the amount of dispersed graphene / graphite (5 mL). This is then deposited under suction onto a 0.2 μm FluoroporeTM membrane, leaving a graphene / graphite thin film on the membrane. The polymer solution is then poured on top and allowed to cool, creating a bilayer thin film. The sample is first washed thoroughly with water. It is then placed in a vacuum oven at 120 °C for 24 hours to remove any residual moisture.

[0070] Example 21 Preparation of polylactic acid resin microparticles (predictive) 1.5 g of polylactic acid (molecular weight about 160,000), 2.5 g of hydroxypropyl cellulose as a polymer different from polylactic acid, and 46 g of aMVL can be placed in a 100 mL autoclave and heated to 50 °C and stirred until the polymer is completely dissolved. After cooling to room temperature, 50 g of deionized water, a poor solvent, is added by dropping at a rate of 0.4 g per minute with a pump while stirring at 500 RPM. After the entire amount of water is added, stirring is continued for another 30 minutes, and the resulting suspension is filtered and washed three times with 50 g of deionized water. The filtered material is then dried under vacuum at 80 °C for 10 hours to obtain about 0.5 g of a powdery white solid. The resulting powder can be analyzed via scanning electron microscope (SEM) to measure the average particle size and particle size distribution index.

[0071] Example 22 Preparation of PAN thin films for use as battery separators (prophetic) The battery separator can be formed by a thermally induced phase separation method in which polyacrylonitrile (PAN) is dissolved in a miscible mixture of 95 wt% aMVL and 5 wt% water at 80°C to form a single-phase solution containing 10 wt% PAN. Particles of Aerosil R805 (hydrophobized fumed silica particles) are then added to the single-phase polymer solution. The amount of these particles added is 10 wt% based on the weight of the PAN. A thin film of the polymer solution is then cast onto a flat glass plate and cooled. During cooling, the PAN precipitates and the thin film changes from transparent to opaque. The aMVL is then extracted by washing the solid PAN precipitate with water. The solid PAN precipitate is then dried by heat to evaporate the residual water and produce the separator.

[0072] Example 23 Preparation of polyethersulfone (prophetic). In a reactor having an internal volume of 100 mL, 1.141 g of bisphenol A, 0.835 g of aqueous sodium hydroxide solution (48.40% by weight), and 5 mL of aMVL can be added. After flushing the air in the reaction system with nitrogen, the mixture is heated to 150° C. while stirring at 300 RPM and maintained at that temperature for 10 minutes. Then, the reaction mixture is cooled to a temperature below 100° C., and 0.647 g of sodium sulfide (purity: 60%) and 20 mL of chlorobenzene are added. The mixture is heated again and the water present in the reaction mixture is continuously removed as an azeotrope with chlorobenzene. After the chlorobenzene is completely distilled off, the reaction mixture is heated to 150° C. for 10 minutes. Then, the reaction mixture is cooled to 40° C. and 2.872 g of 4,4'-dichlorodiphenyl sulfone and 5 mL of aMVL are added. After thoroughly flushing the inside of the reaction system with nitrogen, the mixture is heated to 150° C. and reacted for 14 hours. The reaction product thus obtained is poured into a large amount of methanol, whereby a white polymer is precipitated. The polymer is collected by filtration, washed twice with methanol, twice with hot water, and dried under reduced pressure at 100° C. for 5 hours. Approximately 3 g of a solid white polymer powder is obtained.

[0073] Example 24 Preparation of poly(vinyl cinnamate) (prophetic) 11 g of highly hydrolyzed polyvinyl alcohol of medium molecular weight can be gradually added to 100 mL of aMVL at room temperature with stirring in a 500 ml three-neck flask equipped with a stirrer, thermometer and condenser fitted with a drying tube. The mixture is heated and stirred overnight in a steam bath at 90 ° C. The next morning, another 100 mL of aMVL is added at 90 ° C and the solution of polyvinyl alcohol is cooled to 50 ° C. 50 g of molten cinnamoyl chloride is added to the reaction mixture using a heated dropping funnel for 20 minutes at about 50 ° C. The temperature is maintained at 50 ° C for 4 hours. The reaction mixture is slowly poured into a solution of 64 g of sodium carbonate and 2 liters of water with rapid stirring. The precipitated polymer is chopped several times with water in a Waring blender and after each treatment the product is filtered through a Büchner funnel. After drying in a vacuum oven at 60 ° C, about 40 g of cinnamic ester of polyvinyl alcohol is obtained.

Claims

1. 1. A process for producing or recycling a polymer, comprising: (a) providing a solvent comprising at least 25% by weight of anhydromevalonolactone; (b) producing a polymer or recycling said polymer in the presence of said solvent.

2. 2. The process of claim 1, wherein the generating or recycling is carried out at a temperature of from 20 to 200°C.

3. 10. The process of claim 1, wherein said producing comprises forming a reaction mixture comprising said solvent and 0.1 to 90 weight percent of one or more monomers.

4. 2. The process of claim 1, wherein the producing comprises dissolving at least one waste polymer in the solvent to form a polymer mixture.

5. 5. The process of claim 4, further comprising contacting the polymer mixture with an absorbent to form a purified polymer mixture.

6. 6. The process of claim 5, further comprising contacting the purified polymer mixture with at least one anti-solvent, thereby recovering dissolved polymer and a residue stream comprising the solvent and the anti-solvent.

7. 7. The process of claim 6, further comprising separating the retentate stream into a recovered solvent stream and a recovered anti-solvent stream.

8. 8. The process of claim 7, wherein the separation comprises flash distillation, continuous distillation, extractive distillation, azeotropic distillation, evaporation, absorption, membrane separation, or liquid-liquid extraction.

9. The process of claim 6, further comprising filtering the dissolved polymer to form a first filtered polymer.

10. 10. The process of claim 9, further comprising washing the first filtered polymer to form a washed polymer.

11. 11. The process of claim 10, further comprising filtering the washed polymer to form a second filtered polymer.

12. 12. The process of claim 11, further comprising drying the second filtered polymer to form a final polymer.

13. An electrolytic capacitor, (a) an anode; (b) a cathode; and (c) an electrolyte comprising a solvent, the solvent comprising at least 25% by weight of anhydromevalonolactone.

14. 14. The electrolytic capacitor of claim 13, further comprising a separator positioned between the anode and the cathode.

15. 15. The electrolytic capacitor of claim 14, wherein the electrolyte is in contact with the anode, the cathode, and the separator.

16. 1. A process for removing oil, grease, paint, coating, or stains from a surface, comprising: (a) providing a solvent comprising at least 25% by weight of anhydromevalonolactone; (b) applying said solvent to said surface.

17. 17. The process of claim 16, wherein the solvent comprises 30 to 100% by weight of anhydromevalonolactone.

18. 1. A process for recycling polymers, comprising: (i) dissolving at least one waste polymer in a solvent comprising at least 25 wt.% anhydromevalonolactone, thereby forming a polymer mixture; (j) contacting the polymer mixture with an absorbent or adsorbent to form a purified polymer mixture; (k) contacting the purified polymer mixture with at least one anti-solvent, thereby recovering dissolved polymer and a residue stream comprising the solvent and the anti-solvent; (l) separating said retentate stream into a recovered solvent stream and a recovered anti-solvent stream; (m) filtering the dissolved polymer to form a first filtered polymer; (n) washing the first filtered polymer to form a washed polymer; (o) filtering the washed polymer to form a second filtered polymer; (p) drying the second filtered polymer to form a final polymer product.

19. 20. The process of claim 18, wherein the solvent comprises anhydromevalonolactone and a co-solvent selected from the group consisting of methyl ethyl ketone, benzyl acetate, ethyl benzoate, cyclohexanone, cyclopentyl methyl ether, and dichloromethane.

20. 20. The process of claim 19, wherein the solvent comprises at least 30% by weight of anhydromevalonolactone, based on 100% by weight of the total weight of the solvent.

21. 20. The process of claim 18, wherein the separation comprises flash distillation, continuous distillation, extractive distillation, azeotropic distillation, evaporation, absorption, membrane separation, or liquid-liquid extraction.

22. 20. The process of claim 18, wherein the absorbent or adsorbent comprises one or more of silica, activated carbon, ion exchange resins, diatomaceous earth, montmorillonite, and zeolites.

23. 20. The process of claim 18, wherein the anti-solvent is selected from the group consisting of water, inorganic acid solution, inorganic alkali solution, alcohol, aromatic compound, ester, ether, aldehyde, amine, ketone, organohalogen compound, amide, lactone, lactam, C5-C10 olefin, C5-C10 hydrocarbon, and C5-C15 terpene, or mixtures thereof.

24. (q) recycling the recovered solvent stream so that it is combined with the solvent during the dissolution of step (a); (r) recycling said recovered anti-solvent stream so that it is combined with said anti-solvent during said contacting of step (c).