Techniques for distributing forces in high field magnets and related systems and methods - Patents.com

Abstract

Techniques are described for reducing strain applied to superconducting material in superconducting magnets by placing structural diaphragms between turns of superconducting material that isolate and transfer the strain to a mechanically stronger structure, such as the magnet's housing. The structural diaphragms may be formed with through-connecting slits, allowing the superconducting material to easily penetrate the diaphragms. Multiple structural diaphragms may be inserted between groups of turns of superconducting material in a magnet, allowing the diaphragms to adequately distribute forces throughout the magnet. At the same time, the number of structural diaphragms may be selected to minimize the amount of space within the magnet that is occupied by the diaphragms or that could otherwise be occupied by conductive superconducting material.

Description

[Technical field]

[0001] This disclosure relates generally to superconducting magnet coils, and more particularly to the fabrication and cooling of high temperature superconductor (HTS) magnet assemblies. [Background technology]

[0002]

[0002] A superconductor is a material that has no electrical resistance to electric current ("superconducting") below some critical temperature. For many superconductors, the critical temperature is below 30 K, so that operation of those materials in the superconducting state requires significant cooling, such as with liquid or cold gaseous helium or other cryogens.

[0003]

[0003] High field magnets are often made from superconductors due to the ability of superconductors to carry large electrical currents without resistance. Such magnets can, for example, carry currents in excess of 5 kA. Summary of the Invention [Means for solving the problem]

[0004]

[0004] According to some aspects, an HTS magnet is provided comprising a coil including a high temperature superconductor (HTS) material and a housing comprising at least a first partition, the coil is disposed within the housing, the first partition of the housing is positioned to separate a first portion of the coil from a second portion of the coil such that the windings of the first portion of the coil are disposed entirely within the first partition and the windings of the second portion of the coil are disposed entirely outside the first partition, and the first partition has a slit through which the coil passes.

[0005]

[0005] According to some aspects, a magnet assembly is provided that includes a plurality of pancakes, each of the pancakes having one or more turns of high temperature superconductor (HTS) tape that generates a magnetic field when an electric current is applied thereto, and each of the pancakes further having one or more junctions for electrically coupling the one or more turns of the HTS tape as part of an electrical circuit, and a plurality of cooling plates, each of the cooling plates having a terminal for thermally coupling the cooling plate to a cooling device, wherein the plurality of pancakes and the plurality of cooling plates are stacked in an alternating manner, each of the pancakes is electrically coupled by its one or more junctions to the junctions of either one or two nearby pancakes, thereby forming an operating current path that includes the HTS tape in each of the pancakes, and each of the pancakes is adjacent to either one or two of the cooling plates for removing heat from the pancake by thermal conduction to the cooling device.

[0006]

[0006] According to some aspects, a magnet assembly is provided having a plurality of pancakes, each of the pancakes comprising a housing, a plurality of windings of high temperature superconductor (HTS) tape disposed within the housing, one or more conductive joints coupled to the HTS tape and disposed on the exterior of the housing, and a plurality of cooling plates, each of the cooling plates having a terminal for thermally coupling the cooling plate to a cooling device, the plurality of pancakes and the plurality of cooling plates being alternately arranged in a stack, each of the pancakes in the stack being electrically coupled by its one or more conductive joints to the joints of either one or two nearby pancakes in the stack, thereby forming an operating current path through the stack including the HTS tape in each of the pancakes, and each of the pancakes being adjacent and thermally coupled to either one or two of the cooling plates.

[0007]

[0007] According to some aspects, a housing is provided for holding a wound tape to generate a magnetic field, the housing comprising a first structural plate having one or more first circular slots, one or more partitions, each partition having a through connection for winding the tape from an inner diameter of the partition to an outer diameter of the partition, each partition being removably and rotatably inserted into a corresponding one of the first circular slots, and a second structural plate having one or more second slots, each partition being removably inserted into a corresponding one of the second slots.

[0008]

[0008] According to some aspects, a method of winding conductive tape to form a magnet is provided, the method including the steps of: (a) providing a first structural plate having a surface with one or more circular slots and having a first electrical joint on an inner diameter thereof; (b) physically and electrically coupling the conductive tape to the first electrical joint; (c) circularly winding the conductive tape on the surface of the first structural plate until the conductive tape reaches one of the circular slots; (d) removably inserting a septum having a through connection into one of the circular slots, the septum being rotated within one of the circular slots whereby its through connection is aligned with an azimuthal position of the wrapped conductive tape; and (e) winding the conductive tape on the surface of the first structural plate, through the through connection, and around an outer diameter of the septum, thereby minimizing a gap between the conductive tape and the septum.

[0009]

[0009] The above apparatus and method embodiments may be implemented by any suitable combination of the aspects, features, and operations described above and in detail below. The above and other aspects, embodiments, and features of the present teachings may be more fully understood from the following description taken in conjunction with the accompanying drawings.

[0010]

[0010] Various aspects and embodiments are described with reference to the following drawings. It should be understood that the drawings are not necessarily drawn to scale. In the drawings, each identical or nearly identical component shown in various figures is represented by a like numeral. For purposes of clarity, not all components may be shown in every figure. [Brief description of the drawings]

[0011] [Figure 1] 1 is a cross-sectional view of a superconducting magnet with a structural septum according to some embodiments. [Figure 2A]

[0012] 1 is a cross-sectional view of a superconducting magnet with a structural septum disposed in a groove according to some embodiments. [Figure 2B]

[0013] FIG. 2 is a cross-sectional perspective view of an exemplary housing according to some embodiments. [Figure 2C] FIG. 2 is a cross-sectional perspective view of an exemplary housing according to some embodiments. [Figure 2D]

[0014] 1 is a photograph of a magnet with a septum and HTS tape according to some embodiments. [Figure 3A]

[0015] 11A-11C illustrate various configurations of feed-through connection slits in a structural partition according to some embodiments. [Figure 3B] 11A-11C illustrate various configurations of feed-through connection slits in a structural partition according to some embodiments. [Figure 3C] 11A-11C illustrate various configurations of feed-through connection slits in a structural partition according to some embodiments. [Figure 4A]

[0016] 1 is a cross-sectional view of a magnet assembly according to some embodiments. [Figure 4B]

[0017] FIG. 4B illustrates an enlarged portion of the cross-sectional view of FIG. 4A, according to some embodiments. [Diagram 5]

[0018] 1 is a photograph of a feed-through slit with a shim in addition to HTS tape, according to some embodiments. [Figure 6]

[0019] 1 is a flowchart of a method of assembling a magnet, according to some embodiments. [Figure 7]

[0020] FIG. 2 is an exploded view of the structural and electrical components of a finished stylized pancake according to some embodiments. [Figure 8]

[0021] FIG. 13 is a perspective view of a second type of pancake for stacking in a magnet assembly. [Figure 9]

[0022] FIG. 13 shows a portion of the first cold plate in a magnet assembly between two pancakes electrically joined along their inner diameters. [Figure 10]

[0023] FIG. 13 shows a portion of a second cold plate in a magnet assembly between two pancakes electrically joined along their outer diameters. [Figure 11A]

[0024] FIG. 2 is a cutaway view of a magnet assembly coupled to a cooling device. [Figure 11B]

[0025] FIG. 1 illustrates a portion of the cooling system highlighting the heat protective radiation shield and multi-layer insulation surrounding the magnet assembly. [Figure 12]

[0026] 1 is a cross-sectional view of layers of an exemplary coated conductor HTS tape, according to some embodiments. [Figure 13]

[0027] 1 is a three-dimensional graphic of a fusion power plant with cutaways showing various components of the power plant, according to some embodiments. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0012]

[0028] As mentioned above, high field magnets are often made from superconducting materials because of the ability of superconductors to carry large electrical currents without resistance. When the temperature is low enough that the superconducting material is below its critical temperature (the temperature below which the material's electrical resistivity drops to zero), the magnet allows electrical current to pass through its superconducting path without loss.

[0013]

[0029] High temperature superconductors (HTS) offer a particularly desirable degree of freedom for making high field superconducting magnets. Important features of HTS and HTS rare earth barium copper oxide (REBCO) superconductors compared to low temperature superconductors (LTS) include the following. First, HTS exhibits a smaller critical current sensitivity to operating temperature, allowing for a larger operating temperature margin. Second, HTS has a higher operating temperature than LTS, and at HTS operating temperatures, the heat capacity of the materials in the superconducting magnet can be significantly higher than at LTS operating temperatures. As a result, HTS magnets can have a smaller sensitivity to local heating. Third, HTS is compatible with the principles of electrically non-insulated design due to the good current sharing between bundled parts of HTS, as described in detail below. Fourth, in non-insulated superconducting magnets, small voltages (e.g., less than about 1 V) may be generated in the magnet, but unlike LTS magnets, in HTS superconducting magnets, those voltages may not require high voltage electrical insulation. And finally, HTS magnets can operate at much higher magnetic fields and exhibit less sensitivity to magnetic field strength than LTS magnets.

[0014]

[0030] Whether the superconducting magnet comprises LTS or HTS materials, generally, a superconducting magnet can have a relatively high current density (e.g., a large amount of current per unit volume or per unit cross-sectional area of ​​superconducting material) while also generating a high magnetic field. However, high current densities and high magnetic fields result in significant Lorentz loads (Lorentz forces resulting from current flowing through a magnetic field) being applied to various regions of the superconductor. Such increased Lorentz loads can lead to a reduction in the structural integrity of the magnet. For example, in high field magnets, the strain applied to the superconducting material by the Lorentz loads can be sufficient to fracture the material, reducing or preventing its ability to carry electrical current.

[0015]

[0031] The inventors have recognized and understood techniques for reducing strain applied to the superconducting material in a superconducting magnet by placing structural diaphragms between turns of superconducting material that isolate and transfer the strain to a mechanically stronger structure, such as the magnet's housing. The structural diaphragms may be formed with through-connecting slits, allowing the superconducting material to easily pass through the diaphragms. Multiple structural diaphragms may be inserted between groups of turns of superconducting material in a magnet, allowing forces to be adequately distributed by the diaphragms throughout the magnet. At the same time, the number of structural diaphragms may be selected to minimize the amount of space within the magnet that is occupied by the diaphragms or that may otherwise be occupied by conductive superconducting material.

[0016]

[0032] According to some embodiments, the structural bulkhead may be removable from the housing or other support structure of the magnet. A removable bulkhead allows the magnet windings to be wound without the bulkhead, and then the bulkhead can be added to the magnet once the magnet is wound enough to pass through the feedthrough slits in the bulkhead. This process allows the magnet to be wound in a single plane, thereby simplifying the assembly process, and bulkheads can be added as needed as the size of the windings increases, since the windings can be made around a structure (the bulkhead or central structure of the housing) in the same plane.

[0017]

[0033] According to some embodiments, the structural diaphragm may be movable within the magnet housing or other support structure such that the position of the feedthrough slits can be adjusted during winding. In some cases, the structural diaphragm may be disposed within a groove, slot, and / or other retention mechanism within the magnet, allowing the structural diaphragm to be rotated or otherwise adjusted in position, although its position is somewhat limited by the retention mechanism. For example, the structural diaphragm may be circular and rotatable within a circular groove. In some cases, the structural diaphragm may be other than circular (e.g., rectangular) and not rotatable within the magnet. In such cases, however, small retention mechanisms may be included in the magnet housing or other support structure to reduce movement of the diaphragm during installation of the windings and diaphragm. Alternatively, the structural diaphragm may be free to move within the magnet structure, but may be held in place to some degree during winding by placing the diaphragm around a turn of the magnet that substantially fills the interior of the diaphragm. In some cases, the structural diaphragm may include multiple joint parts that can move independently while being constrained by connections to other parts. For example, the structural bulkhead may include multiple sections arranged in a loop with adjacent sections rotatably coupled to one another (eg, comparable to a bicycle chain).

[0018]

[0034] According to some embodiments, the superconducting magnet may include HTS material wound as described above and penetrating one or more structural septa. In some cases, the HTS material may include HTS tape, which is a long, flat element that includes, in addition to other layers, a layer of polycrystalline HTS. As used herein, HTS "tape" may refer to any structure that includes a layer of HTS, such as rare earth copper salt HTS (e.g., REBCO), such as tape 1200 as shown in FIG. 12, and may also include one or more other layers, such as one or more buffer layers, stabilization layers, substrates, overlay layers, and / or cladding layers.

[0019]

[0035] In some embodiments, a superconducting magnet with one or more structural septa as described herein may include HTS material wound without insulating material between at least some adjacent turns of the HTS material. In such magnets, referred to herein as non-insulated (NI) magnets (or magnets without insulation), adjacent superconducting turns of the magnet are not insulated from one another, but instead are separated by conventional conductors (i.e., not superconductors). When the magnet is operating below the critical temperature of the superconductor, current flows through the superconductor and does not cross the turns, since the superconductor has zero resistance compared to the finite resistance of the conductors present between the turns.

[0020]

[0036] In some embodiments, a superconducting magnet may comprise an HTS tape wound around a winding axis such that the x-axis of the tape is aligned parallel to the winding axis as shown in FIG. 12. Thus, for a non-insulated magnet design, for example, each HTS tape may contact the face of the adjacent tape (xy plane in FIG. 12). In some embodiments, a superconducting magnet may include windings of a stack of HTS tapes along with a non-superconducting material such as steel. For example, a stack of 10-20 HTS tapes stacked face-to-face on top of a single steel tape having the same width as the HTS tape (dimension in the x-direction in FIG. 12) may be wound together around a central structure to create a magnet, with the stack penetrating one or more structural bulkheads along the windings.

[0021]

[0037] In some embodiments, a superconducting magnet may comprise an HTS tape (or a stack of HTS tapes) arranged in a racetrack-shaped spiral, with the spiral penetrating one or more structural partitions along its windings.

[0022]

[0038] In some embodiments, the housing of a superconducting magnet may include electrically conductive joint structures configured to couple the superconducting material within the housing to an exterior surface of the housing. During winding, the superconducting material may be electrically coupled (e.g., soldered) to such joint structures. In some cases, the housing may include multiple joints, such as joints internal to the winding of superconducting material and external to the winding of superconducting material.

[0023]

[0039] In some embodiments, a superconducting magnet may include multiple individual windings of superconducting material bonded together. In some cases, the housings for each winding may be stacked or otherwise assembled with conductive joints on each housing that provide electrical coupling between the windings. As a result, a conductive path may be formed through the windings, e.g., from the inside to the outside of the winding in a first housing, through the joints to the outside of the winding in a second housing, from the outside to the inside of the winding in the second housing, etc. For at least some use cases, the housings in such assemblies may be referred to herein as "pancakes" in reference to their generally circular, flat shape.

[0024]

[0040] In some embodiments, the stack of individually housed windings as described above may be coupled to one or more cold plates. The cold plates may provide for conduction cooling and may include a thermally conductive material such as copper. In some embodiments, the cold plates may be inserted between adjacent housings, with the cold plates being electrically insulated from the joints between the adjacent housings.

[0025]

[0041] The following is a detailed description of various concepts related to techniques for reducing strain applied to superconducting materials in superconducting magnets or embodiments thereof. It should be understood that the various aspects described herein may be implemented in any of many ways. Examples of specific implementations are provided herein for illustrative purposes only. Furthermore, the various aspects described in the following embodiments may be used alone or in any combination, and are not limited to the combinations expressly described herein.

[0026]

[0042] FIG. 1 is a cross-sectional view of a superconducting magnet with a structural diaphragm, according to some embodiments. The magnet 100 includes a housing 110 with a top plate 111, a bottom plate 112, and a central structure 113 that may include an electrical joint at the inner diameter. A single continuous piece of HTS tape 115 is wound around the central structure 113. Alternatively, several joined sections of HTS tape may be wound together as a single winding. Due to the cross-sectional view shown in FIG. 1, the same HTS tape is shown with a continuous winding at a different radial location than the central structure. The magnet 100 further includes structural diaphragms (hereinafter "diaphragms") 121 and 122 through which the HTS tape 115 penetrates when wound around the central structure. The locations where the HTS tape 115 penetrates the diaphragms are not shown in FIG. 1 for clarity, but the diaphragms 121 and 122 may include feed-through slits through which the HTS tape 115 penetrates as described above.

[0027]

[0043] In some embodiments, the septa 121 and 122 may be movable within the housing 110 so that the feed-through slits in the septa may align with the HTS tape at the point where the HTS tape fills within the septa. Exemplary feed-through slits are shown in Figures 3A-3C and described in detail below. A movable septa may be beneficial during winding because the azimuthal position where the tape needs to pass through the septa may be unknown, so that the feed-through slits in the septa are located at the azimuthal position required when the tape has filled all of the space inside the septa. In some cases, the septa may still be moved correctly to the desired azimuthal position, but may be limited in movement because they are located in a slot or are otherwise somewhat restricted in movement.

[0028]

[0044] According to some embodiments, partitions 121 and 122 may be circular, and thus the same cross-sectional view of Figure 1 is applicable to any selected cross-section through the center of magnet 100 (except for cross-sections that include slits through the partitions, which may look different than in Figure 1). In some embodiments, partitions 121 and 122 may be other than circular, and instead have a shape such as a rectangle, or a rectangle with rounded corners (e.g., a racetrack shape), an ellipse, or any other suitable shape.

[0029]

[0045] According to some embodiments, the top plate 111 and the bottom plate 112 may include or be made of a high mechanical strength material, such as, but not limited to, steel, Inconel, Nitronic 40, Nitronic 50, Incoloy, or combinations thereof. In some embodiments, the bulkheads 121 and 122 may include or be made of a high mechanical strength material, such as, but not limited to, steel, Inconel, Nitronic 40, Nitronic 50, Incoloy, high entropy alloys, high strength composites, ceramics, or combinations thereof.

[0030]

[0046] According to some embodiments, the HTS tape 115 may include a rare earth barium copper oxide superconductor (REBCO), such as yttrium-based barium copper oxide (YBCO). In some embodiments, the HTS tape may comprise long, thin strands of HTS material having cross-sectional dimensions of a thickness (or height) in the range of about 0.001 mm to about 0.1 mm and a width in the range of about 1 mm to about 12 mm. According to some embodiments, each strand of the HTS tape may include an HTS material, such as REBCO, in addition to a conductive material. In some embodiments, the conductive material may be disposed on the REBCO. In some embodiments, the conductive material may be a cladding material, such as copper. In some embodiments, the HTS tape may include polycrystalline HTS and / or have high grain alignment.

[0031]

[0047] In some embodiments, the HTS tape 115 may be co-wound with a non-superconducting material such as steel or copper. A stack of HTS tapes may be co-wound with one or more layers of co-wound material. In some embodiments, additional conductive material may be included in the magnet 100 to fill potential gaps between components. For example, a soft metal such as indium may be placed between either the top plate 111 or bottom plate 112 and the HTS tape.

[0032]

[0048] 1 as being generally integral, it will be understood that the structure as shown is not a required component of magnet 100 and that, in general, a magnet may include any central structure within a housing. For example, central structure 113 may instead be cylindrical with open walls around which the HTS tape can be wound.

[0033]

[0049] FIG. 2A is a cross-sectional view of a superconducting magnet with a structural septum disposed in a groove, according to some embodiments. The magnet 250 includes a housing 260 with an upper plate 261, a lower plate 262, and a central structure 263 that may include an inner diameter electrical joint 278. A single continuous piece of HTS tape 265 is wound from the inner diameter electrical joint 278. Alternatively, several joined sections of HTS tape may be wound together as a single winding. Because of the cross-sectional view shown in FIG. 2A, the same HTS tape is shown with continuous windings at different radii from the central structure. The magnet 250 further includes septa 271 and 272 through which the HTS tape 265 penetrates when wound around the central structure. The locations where the HTS tape 265 penetrates the septa are not shown in FIG. 2A for clarity, but the septa 271 and 272 may include feed-through slits through which the HTS tape 265 penetrates as described above.

[0034]

[0050] 2A, bulkheads 271 and 272 are disposed in grooves formed in top and bottom plates 261 and 262. The grooves may act as a retention mechanism to hold the bulkheads in place during assembly and / or may provide additional structural strength to the magnets, allowing forces applied to the bulkheads to be more easily transferred to plates 261 and 262. In some embodiments, the grooves formed in the faces of top and bottom plates 261 and 262 may have a circular shape. In other cases, the grooves formed in the faces of the plates may have a different shape, such as a rectangle, or a rectangle with rounded corners.

[0035]

[0051] In the example of Figure 2A, magnet 260 includes conductive bond structures (hereinafter "bonds") 278 and 279, which are structures configured to bond the HTS tape within the magnet to an outer surface as described above. During winding, HTS tape 265 may be electrically bonded (e.g., soldered) to inner bond 278 and outer bond 279. In the example of Figure 2A, inner bond 278 bonds the conductive paths of HTS tape 265 to the top surface of magnet 250, while outer bond 279 bonds the conductive paths of HTS tape 265 to the bottom surface of the magnet.

[0036]

[0052] In some embodiments, the inner joint 278 may not extend to the top of the housing as shown in FIG. 2A in each cross section. In some cases, the inner joint 278 may only extend to a portion of the top of the housing, such as around one side of the housing. Similarly, in some embodiments, the outer joint 279 may not extend to the bottom of the housing as shown in FIG. 2A in each cross section. In some cases, the outer joint 279 may only extend to a portion of the bottom of the housing, such as around one side of the housing. These configurations may have the advantage that additional elements can be inserted next to the housing while still allowing conductive paths to exit the magnet through the joint.

[0037]

[0053] 2A, it will be understood that the structure as shown is not a required component of magnet 250, and that magnets in general may include any central structure within their housing. For example, central structure 263 may instead be cylindrical, consisting only of inner diameter electrical joint 278, with an open interior wall, around which HTS tape can be wound.

[0038]

[0054] 2B and 2C are cross-sectional perspective views of an exemplary housing (or "pancake") configured as in FIG. 2A, where the housing is circular and includes a circular groove and a circular bulkhead disposed within the groove. The same structure is illustrated in both FIG. 2B and FIG. 2C, but FIG. 2B shows detail of one side of the housing. In the example of FIG. 2B-C, magnet 200 includes housing 202 including upper plate 203, lower plate 204, and bulkheads 210, 212, and 214. The magnet further includes inner joint 206 and outer joint 208.

[0039]

[0055] In the example of Figures 2B and 2C, magnet 200 includes three structural partitions 210, 212, and 214. According to some embodiments, the partitions may reduce circumferential strain accumulated in the HTS tape on multiple turns when exposed to high Lorentz forces. As shown in Figures 2B-2C, structural partitions 210, 212, and 214 are received in slots or grooves formed in upper structural plate 203 and lower structural plate 204. The radial positions of the slots and their associated structural partitions 210, 212, and 214 may be determined by computer analysis so that accumulated operational tape strain does not exceed an acceptable range. Conversely, the number of partitions can be minimized so that space within the housing is not taken up by an unnecessary number of partitions that would otherwise be occupied by the HTS tape. The spaces between the partitions where the HTS tapes may be placed, i.e., spaces 220, 222, 224, and 226 in the examples of Figures 2B and 2C, may hereinafter be referred to as "channels."

[0040]

[0056] In the example of Figures 2B and 2C, each structural bulkhead 210, 212, and 214 has a through-connection slit for transitioning the tape stack radially from one side of the bulkhead to the other. Illustrative examples of suitable through-connection slit structures are described below. Thus, as shown in Figures 2B and 2C, at least one of the pancakes in the magnet assembly may include multiple channels separated by one or more bulkheads for bearing radial loads, each channel having one or more turns of HTS tape, and each bulkhead having a through-connection connecting turns of HTS tape in nearby channels. Using this through-connection slit, a continuous length of HTS tape or tape stack can be wound from the inner diameter to the outer diameter while passing through the bulkhead but being structurally supported by the bulkhead.

[0041]

[0057] It will be appreciated that the number of septa in a pancake, and therefore the number of channels in that pancake, may be adjusted. Reasons for such adjustments include, among others, to accommodate variations in the diameter of the pancake, the materials used in the fabrication of the pancakes, including the septa themselves, the materials used in the HTS tape (or stack of HTS tapes), the magnitude of the designed material stresses, the designed operating temperature, the magnetic field, and the technical current density (or transport current), and / or other suitable factors.

[0042]

[0058] FIG. 2D is a photograph of a magnet with septa and HTS tape, according to some embodiments. Magnet 280 is an example of magnet 200 with HTS tape, with the superstructure plate removed, thereby exposing the interior of the magnet. As shown in FIG. 2D, magnet 280 includes three septa 286, 287, and 288. Each of the three septa includes a through-connection slit (not explicitly shown in FIG. 2D), and the HTS tape is wound from the interior of the magnet around central structure 285 (forming tape region 281), through septa 286 and around septa 286 (forming tape region 282), through septa 287 and around septa 287 (forming tape region 283), and through septa 288 and around septa 288 (forming tape region 284). In the example of FIG. 2D, central structure 285 consists only of an inner diameter electrical joint, as described above.

[0043]

[0059] 3A-3C illustrate various configurations of through-connection slits in structural bulkheads, according to some embodiments. Each of Figures 3A-3C illustrates a circular bulkhead disposed within a circular slot in a structural plate. It should be understood that while exemplary through-connection slits are illustrated for a circular bulkhead and a circular slot, similar slit designs are also possible in bulkheads of other shapes (e.g., rectangular) and / or bulkheads that are not disposed in a slot in a structural plate.

[0044]

[0060] In the example of FIG. 3A, the septum includes a partial slit configuration 310 where the slit does not extend the entire height of the septum. In the example of FIG. 3B, the septum includes a full slit configuration 320 where the slit extends the entire height of the septum. In the example of FIG. 3C, the septum includes a partial slit configuration 330 for the septum with a machined spiral at its outer diameter, whereby the septum is not purely circular, but rather has the shape of approximately one full turn of a spiral. The configuration of FIG. 3C can include a septum with a radially uniform thickness that can withstand radial loads equally in all azimuthal directions. Although FIG. 3C illustrates the septum having a machined spiral at its outer diameter but circular at the inner diameter, other suitable configurations for the septum may have a spiral shape at both the inner and outer diameters. It should be understood that other slit configurations can also be used in accordance with embodiments of the concepts, techniques, and structures disclosed herein, particularly to reduce radial stresses.

[0045]

[0061] As noted above, embodiments herein are not limited to a circular septum disposed within a circular slot, but may also have advantages over configurations in which the septum can rotate within the slot as the magnet is wound. Because the azimuthal position at which the tape needs to pass through the septum may be unknown, a circular septum and circular slot configuration allows the septum to rotate during winding, thereby positioning the feedthrough slit in the septum at the azimuthal position required when the tape has filled all of the space inside the septum.

[0046]

[0062] As mentioned above, in some embodiments, a high-field superconducting magnet may be formed by windings of HTS, HTS tapes, or HTS tape stacks arranged in flat layers (e.g., formed so that the interface of the layers is perpendicular to the central longitudinal axis of the magnet about which the layers are arranged), and such a configuration may be referred to as a "pancake winding" or more simply as a "pancake." The pancake thereby includes both the HTS components and the structural components for housing the HTS. When a magnet is formed by layers with windings (e.g., formed so that the interface of the layers is parallel to the central longitudinal axis of the magnet about which the layers are arranged), such a configuration may be referred to as a "layered winding approach" or simply as a "layered configuration," or more simply as "layered."

[0047]

[0063] FIG. 4A is a cross-sectional view of a magnet assembly 400 according to some embodiments, and FIG. 4B is a diagram illustrating an enlarged portion of the cross-sectional view. According to some embodiments, the magnet assembly 400 may be designed for use in high magnetic fields (e.g., 10 Tesla or greater). According to some embodiments, the magnet assembly 400 may be comprised of a conduction-cooled "cold mass" of multiple pancakes having an outer diameter (OD) electrical joint 402 and an inner diameter (ID) electrical joint 404. In the embodiments described in detail herein, the mechanical structure of each pancake that holds the HTS (hereinafter the "housing") may be formed of or include steel, or other suitable structural electrical conductor, such as an austenitic nickel-chromium alloy, such as Inconel® alloy by Special Metals Corporation, New Hartford, NY, USA, or a nitrogen-strengthened austenitic stainless steel, such as Nitronic® alloy by AK Steel, West Chester, OH, USA. However, it should be understood that in other embodiments, the housing may be formed of other structural materials that may or may not be electrical conductors. In the example of FIG. 4, the magnet assembly 400 is coupled to transfer or otherwise remove heat by thermal conduction using a cooling device at terminals 408 that are electrically insulated from the magnet assembly by electrical insulators 406 (such as high voltage fiberglass laminates).

[0048]

[0064] 4A-4B illustrate a particular non-insulated pancake design, it should be understood that many of the features and manufacturing techniques disclosed herein are applicable to magnets formed with fully or partially insulated HTS tapes or tape stacks, and one of ordinary skill in the art would understand how to adapt the concepts, techniques, and structures taught herein to fully or partially insulated designs. For example, the magnet assembly need not include the same number of bulkheads in each pancake, nor need it include pancakes at the same radial locations in each pancake, as shown in the example of FIGS. 4A-4B.

[0049]

[0065] FIG. 4B illustrates an enlarged portion of the cross-sectional view of FIG. 4A. In the example of FIG. 4B, magnet assembly 400 includes two types of pancakes, referred to herein as "standard" pancakes and "end" pancakes. Standard pancakes 410, 412, 414, 416, 418, 420, 422, and 424 may each be formed of a pair of structural plates with a structural partition therebetween. The partitions define a number of channels for holding one or more turns of an HTS tape or tape stack, as described above, and generate a magnetic field when a current is applied. (The HTS tape stack is not shown in FIGS. 4A-B to provide greater visual clarity of the structure of the pancakes themselves; i.e., only the housing is shown).

[0050]

[0066] In the example of FIG. 4B, pancake 410 includes three bulkheads 425, 426, 427 from the inner diameter outward, and this bulkhead design is replicated in the other stylized pancakes of stacked magnet assembly 400. The windings of the HTS stack form a continuous spiral in the channel of each pancake, electrically connecting its inner diameter to its outer diameter. According to some embodiments, at least one HTS tape of a pancake may include a rare earth copper oxide, such as REBCO. It should be understood that other superconducting materials may be used in magnet assembly 400 to generate a magnetic field in accordance with embodiments of the concepts, techniques, and structures disclosed herein.

[0051]

[0067] According to some embodiments, the HTS tape and co-wound materials in the magnet assembly 400 can be free-standing and densely packed in a pancake configuration, whereby one or more turns of the HTS tape stack in each of the channels substantially fills the volume of the channel. Alternatively, the HTS tape of at least one of the pancakes is soldered to at least one of the channels and soldered to one or more bonding bodies. It should be understood that other methods may be used to secure the superconducting tape or tape stack in the magnet assembly 400 according to embodiments of the concepts, techniques, and structures disclosed herein.

[0052]

[0068] According to some embodiments, copper co-wraps may be added in those critical regions to enhance quench stability due to small resistive heating in the joints, potential over-distortion and / or over-stress of the tapes in the joints, and the inter-channel transitions through the structural diaphragm in each pancake. To reduce quench-related temperature rise due to inductive pickup eddy current heating of the copper components in the joints, current leads, and inter-channel transitions, the HTS tape stack may be reinforced by adding HTS tapes in series to achieve a larger current carrying capacity. Additionally, to reduce potential kinking of the HTS tape stack in the joints, current leads, and inter-channel transitions, the HTS tape stack may be reinforced by steel tape co-wraps. Additional co-wraps may be added. For example, copper co-wraps may be added to improve normal conduction propagation through the diaphragm during a quench, or for other purposes.

[0053]

[0069] According to some embodiments, each of the pancakes of the magnet assembly 400 may include one or more joints for electrically coupling one or more turns of HTS tape as part of an electrical circuit. More specifically, ring-shaped joints embedded in the structural plate may be located at the inner and outer diameters of each shaped pancake to terminate the superconducting electrical path. These joints may include or consist of copper and / or other electrically conductive materials and / or may include or consist of superconducting materials. As an example, the shaped pancake 422 has an inner diameter joint 440 and an outer diameter joint 442. The spirals of the HTS tape stack continue into the grooves of those joints. In an exemplary embodiment, the spirals may terminate after multiple complete 360 ​​degree rotations, while in other embodiments, the grooves may terminate before or after one complete rotation.

[0054]

[0070] According to some embodiments, the inner diameter joint 440 and the outer diameter joint 442 may each be embedded in the structural plate of each pancake, so that they are flush with or extend slightly above the plane of the structural plate on opposite sides thereof. In particular, the joints may extend above the structural plate to provide adjacent space for a cooling plate, as described below. According to the modular design disclosed herein, the number of standard pancakes can be any number of pancakes greater than or equal to one to generate the desired magnetic field.

[0055]

[0071] In the example of Figures 4A and 4B, multiple identical shaped pancakes may be stacked together with alternating axial orientations of the HTS tape filled channels. This arrangement may provide a continuous electrical path between the exposed joints of the two outermost pancakes through the spiral of HTS tape and the mated ID-to-OD joints of all pancakes of the magnet assembly 400. In particular, a pattern of alternating housings may be repeated in which one of the pancakes is electrically coupled by a joint on its outer diameter to a joint on the outer diameter of the second one of the pancakes, and the first one of the pancakes is electrically coupled by a joint on its inner diameter to a joint on the inner diameter of the third one of the pancakes. 4B, the outer diameter joint of the first pancake 412 and the outer diameter joint of the second pancake 414 mate via electrical bonding area 446, and the inner diameter joint of the first pancake 412 and the inner diameter joint of the third pancake 410 mate via electrical bonding 444. To promote better electrical contact of the joints between the pancakes, a conductive (e.g., indium) gasket may be inserted between the respective mating surfaces of the joints of two stacked side-by-side pancakes during manufacture.

[0056]

[0072] Note that in Figure 4B, bond region 446 includes a portion of a cold plate 452 inserted between the joints in pancakes 412 and 414. In the exemplary magnet assembly of Figures 4A and 4B, the outer joints between the plates are in contact only on half of the pancakes, while the other half has a cold plate inserted between them. This difference is evident when comparing the joint region 402 on the left side of Figure 4A, which shows the joints in contact with each other, to the joint region 402 on the right side of Figure 4A, which shows the joints with a cold plate therebetween.

[0057]

[0073] 4A and 4B, the electrical paths of the HTS tape windings are completed by the two outermost end pancakes 430 and 432. The end pancakes 430, 432 represent an integral structural plate with a single ring-shaped joint located at either the ID or OD at the same radial position as the regular pancake with which it electrically contacts. That is, each pancake at the top of the stack and at the bottom of the stack has an inner surface with a joint at either its outer diameter or its inner diameter that is electrically coupled to the joint of the other (regular) pancake, and a parallel outer surface that has no joint.

[0058]

[0074] In the example of Figures 4A and 4B, both end pancakes 430, 432 have respective joints 434, 436 at the OD, but only on their inner surfaces. The ring-shaped joints 434, 436 of the end pancakes 430, 432 are connected continuously with a conductive plate of the same conductor and extend radially outward, usually in the direction of the HTS current lead (e.g., conductor 406 as shown in Figures 4A and 4B). The HTS tape stack starts inside the joint ring, forms a 360 degree loop in the joint groove, and then fits into the groove of the extension plate. Each of the pancakes (both regular and end) is thereby electrically coupled by its one or more joints to the joints of one or two nearby pancakes, thereby forming a working current path that includes the HTS tape in each of the pancakes.

[0059]

[0075] According to some embodiments, although the ID and OD joints are described above as being executed in the shape of a continuous circular ring, the joints may alternatively be configured as discontinuous plates formed as extensions from their respective pancakes and positioned about the pancakes, thereby fitting together in an assembly that can be pressed and secured individually, one joint at a time, or all together in the cold mass assembly as described above.

[0060]

[0076] According to some embodiments, the pancakes are independent of each other and connected for electrical operation only at the junctions, so the shapes of the individual pancakes can be different as long as the junctions of adjacent pancakes have mating surfaces. In general, the cold mass and HTS windings can be shaped as solenoids or racetracks, or have different shapes that topologically match either of them. Thus, at least two of the pancakes may have different sizes or shapes. It is expected that one skilled in the art can conceive of other sizes or shapes without departing from the concepts and techniques disclosed herein.

[0061]

[0077] According to some embodiments, the cold mass may be conductively cooled by a thermally conductive (e.g., copper, aluminum, silver, gold, graphite, etc.) cold plate inserted between the pancakes in the spaces not yet filled by the bond. In the example of Figures 4A and 4B, a copper cold plate 450 is placed between adjacent shaped pancakes 422 and 424, and this design of alternating pancakes and cold plates is repeated throughout the magnet assembly 400 as shown. In some embodiments, the copper cold plate may be electrically insulated to prevent electrical shorting between the pancakes. This insulation may be achieved by coating each side with a layer of an electrical insulator such as polytetrafluoroethylene (PTFE) or similar and solidifying the insulator. It should be understood that other coatings may also be used.

[0062]

[0078] Each of the copper cold plates 450 may be thermally conductive and may be positioned between the pancakes, through a layer of electrical insulation, and to a terminal to thermally couple the cold plate to a cooling device. In the example of Figures 4A and 4B, the copper cold plate 450 has a terminal 452 that is in thermal contact with a terminal 470 of the cooling device. In this manner, each of the pancakes is adjacent to either one or two of the cold plates, allowing the pancake to cool to an operating temperature and allowing the pancake to transfer heat generated in the pancake to the cooling device by thermal conduction. Specifically, each end pancake is adjacent to one of the cold plates and each regular pancake is adjacent to two of the cold plates.

[0063]

[0079] According to some embodiments, when the HTS penetrates a feedthrough slit in the structural bulkhead, additional material other than the HTS tape may be provided to fill any gaps in the feedthrough. This additional material may mitigate degradation of the tape due to deformation caused by pressure and / or other forces during operation of the magnet. Because the HTS tape in the slit may be relatively thin, it may be particularly susceptible to deformation, which may be avoided by adding a "shimming" material placed in the feedthrough.

[0064]

[0080] FIG. 5 is a photograph of a feed-through slit with shims in addition to HTS tape, according to some embodiments. In the example of FIG. 5, the magnet is shown with the top plate removed and the HTS tape wound inside and between the septa as described in various embodiments above. In the example of FIG. 5, a septum 520 separates an area 511 of HTS tape windings from an area 512 of HTS tape windings, which passes through a slit in the septum 520. In the example of FIG. 5, the septum 520 is of the type shown in FIG. 3C, which has the shape of a spiral with approximately one full turn. Additional shimming material 522 and 523 are inserted on either side of the septum to fill gaps that may otherwise appear as the turns of HTS tape 518 pass through the septum 520.

[0065]

[0081] Shimming material 522 and 523 may include additional pieces of HTS tape and / or additional strips of conductive material (e.g., copper strips and / or steel strips). Multiple strips of various materials may be inserted as desired (e.g., multiple strips of HTS tape, multiple strips of copper tape, and multiple strips of steel tape may all be inserted together as a single shim or "co-wrap").

[0066]

[0082] Figure 6 is a flow chart of a method of assembling a magnet according to some embodiments. For illustrative purposes, method 600 is described with reference to an exploded view of a magnet as shown in Figure 7, but it should be understood that method 600 is not limited to assembling a magnet with the particular components of Figure 7. In particular, while Figure 7 illustrates a circular bulkhead and a circular structural plate with a circular slot, method 600 may be practiced with bulkheads and plates of any suitable shape, including plates without slots, or with slots other than circular.

[0067]

[0083] With respect to the elements of Figure 7, the figure shows an exploded view of the structural and electrical components of a complete stylized pancake 500, such as the pancake included in magnet assembly 400 shown in Figures 4A and 4B, or magnet 200 of Figures 2B and 2C. The design shown in Figure 7 facilitates a convenient process of making the pancake and winding the HTS tape stack onto the structural plate of the pancake. The HTS tape stack may be a tape stack as described above in connection with Figures 4A and 4B. The fabrication of the end pancakes is similar, with differences noted below.

[0068]

[0084] The pancake may be assembled by first installing and bolting the ID joints 720 under the structural plate 710. The HTS stacks may be pre-soldered into grooves in the ID joints 720 or, optionally, soldered in place after installation of the joints in operation 602. At this stage in the assembly process, the radial space outside the ID joints 720 is open, and in particular, there are no bulkheads installed in the slots in the sub-structural plate 710.

[0069]

[0085] In operation 604, the stacked HTS tape can then be wound in a single plane outward from the ID joint 720, similar to how tape is wound onto a cassette reel. This "reel-to-reel" approach to reel-to-pancake winding of HTS tape greatly simplifies the winding process. Winding continues until the deposited radial structure reaches the slot 712 of the first bulkhead 730.

[0070]

[0086] Optionally, the first bulkhead 730 may be insertable during the winding process rather than being fixed to the substructure plate 710. In such a case, the bulkhead may be inserted into the first bulkhead slot 712 at the appropriate time during the winding of the HTS tape around the ID joints 720 in operation 606. In such a case, the bulkhead 730 may be inserted into the slot 712 in the substructure plate 710 so that the gap between the tape and the bulkhead 730 is as small as possible. In the case of a circular (tubular) winding, this is achieved by rotating the bulkhead 730 to place its feedthrough in the best azimuthal position that minimizes said gap, i.e., just as the circumferential winding of the HTS tape reaches the slot 712 in operation 608.

[0071]

[0087] In operation 610, the HTS tape stack, with any of the local co-wound materials described above (e.g., copper, steel and / or HTS tape) to mitigate the formation of kinks in the transition region, may be driven through the gap in the septum 730 to the outer diameter of the septum 730, which is then rotated within the slot 712 to feed the tape through the feedthrough until the volume inside the septum 730 is entirely filled with tape. At this time, the septum 730 is held in position and the "reel to reel" winding continues around the outside of the septum 730.

[0072]

[0088] According to some embodiments, the first bulkhead 730 and the other bulkheads 740 and 750 include feedthrough slits through which the HTS tape stack passes, as shown in any of Figures 3A, 3B, or 3C, or using other configurations with feedthrough connections.

[0073]

[0089] The process of operation 604 and optionally operation 606, as well as operations 608 and 610, may be repeated for each bulkhead 730, 740, and 750 until the winding reaches the location of the OD joint 760. After its placement, the HTS tape stack (with co-windings) is inserted into the gap at the OD joint 760 and soldered. Potential gaps between the winding and the bulkhead 730, 740, 750 or joints 720, 760 may be shimmed with solid copper or steel or may be constructed with one or more thin tape shims. In this manner, the interior of each shaped pancake may be monolithic, with the HTS tape stack fixed in place against radial forces.

[0074]

[0090] According to some embodiments, each of the bulkheads 730, 740, 750 may extend above the top of the HTS tape windings, i.e., the bulkheads 730, 740, 750 may have a height slightly above the wound HTS tape. In such a case, a layer of indium may be added to the space above the wound HTS tape before it is finally covered with the upper structural plate. Finally, the upper structural plate 770 is installed flush with the top of the HTS tape, the bulkheads, and the assembly. During installation, the bulkheads 730, 740, 750 are inserted into the lower slots of the upper structural plate 770, which are in the same radial position as the slots 712, 714, 716 of the lower structural plate 710, thereby providing support to the bulkheads against radial forces built up during operation.

[0075]

[0091] Fabrication of the end pancake may include inserting the OD joint 760 and copper extension plate, and soldering the HTS tape stack into the grooves of the joint.

[0076]

[0092] Thus, a housing for holding a wound tape to generate a magnetic field is disclosed. The housing comprises a first structural plate 710 having one or more first circular slots 712, 714, 716. The housing further comprises one or more bulkheads 730, 740, 750, each of which has a through-connection for winding the tape from the inner diameter of the bulkhead to the outer diameter of the bulkhead. Each bulkhead 730, 740, 750 is removably and rotatably inserted into a corresponding one of the first circular slots. That is, because the slots are circular and the bulkheads are designed to be housed within the slots, the bulkheads are advantageously rotatable within each slot, whereby their through-connections have a desired azimuthal position, facilitating winding, i.e., rotating the through-connections in the slot to ensure that the entire volume within the bulkhead is filled with tape. The housing further comprises a second structural plate 770 having one or more second slots, each of which is removably inserted into a corresponding one of the second slots. One of the bulkheads 730, 740, 750 may have a through connecting slit according to any of the configurations 310, 320, or 330 shown in Figures 3A-3C, or any other configuration that facilitates passing a wrapped tape from one side of the bulkhead to the other.

[0077]

[0093] That is, a method of winding conductive tape to form a magnet is disclosed. The method 600 includes providing a first structural plate 710 having a surface with one or more circular slots 712, 714, 716 and having a first electrical connection 720 at its inner diameter. The method then optionally includes operation 602 in which a conductive tape is physically and electrically coupled to the first electrical connection 720. The method proceeds to operation 604, where a conductive tape is circularly wound on the surface of the first structural plate 710 until the conductive tape reaches one of the circular slots (e.g., circular slot 712). The method then optionally includes operation 606 in which a septum (e.g., septum 730) having a through-connection slit is removably inserted into one of the circular slots 712, where the septum 730 may be optionally rotated within one of the circular slots 712 so that its through-connection is aligned with the azimuthal position of the wound conductive tape. The method proceeds to operation 608 where the HTS tape is aligned with the feedthrough slits (by rotating the septum or otherwise), and then in operation 610, conductive tape is wrapped onto the surface of the first structural plate 710, through the feedthroughs, and around the outer diameter of the septum 730, thereby minimizing the gap between the conductive tape and the septum 730.

[0078]

[0094] The method may continue by repeating operations 604-610 for each additional slot of the one or more circular slots (e.g., for additional circular slots 714 and 716 using bulkheads 740 and 750, respectively). If first structural plate 710 has a second electrical contact at its outer diameter (e.g., contact 760), the method may include physically and electrically bonding the conductive tape to second electrical contact 760. The method may further include adding a layer of indium adjacent to the wrapped conductive tape.

[0079]

[0095] Method 600 may, in some embodiments, further include providing a second structural plate (e.g., plate 770) having a surface with a second circular slot, and placing second structural plate 770 flush with the wrapped conductive tape, thereby creating a pancake with a complete structural housing and wrapped tape, by removably inserting a bulkhead (in this case bulkhead 730) into the second circular slot. It should be understood that the second structural plate may have slots to accommodate additional bulkheads (e.g., bulkheads 740 and 750), and placing second structural plate 770 may further removably insert those additional bulkheads into corresponding slots of the second structural plate. As discussed above, the conductive tape may be co-wound with copper, steel, or both copper and steel.

[0080]

[0096] FIG. 8 is a perspective view of an end pancake 800 that may be used in a magnet assembly such as magnet assembly 400 shown in FIGS. 4A-4B. End pancake 800 includes a structural plate 802 and a single electrical connection 804 that is used to carry electrical current to and from the magnet assembly via electrical conductor 806. End pancake 800 is shown with electrical connection 804 along its outer diameter. As noted above, it is also contemplated to provide an end pancake with a single connection along its inner diameter, for example, for use in magnet assemblies having an odd number of regular pancakes. Such an alternative end pancake may require electrical conductors radially outward from the inner diameter for coupling to an external circuit, and one of ordinary skill in the art would understand how to fabricate such conductors.

[0081]

[0097] Since the continuous inter-pancake electrical pathway alternates between the inner and outer diameters of the stack over its entire length, there are two types of copper cold plates shaped accordingly. Thus, FIG. 9 shows a copper cold plate 900 used between pancakes mated along their inner diameter as illustrated by electrical bond interface 910, such as between the connection between pancakes 410 and 412 at electrical bond 444 as shown in FIG. 4B, and similar connections between pancakes 414 and 416, between pancakes 418 and 420, and between pancakes 422 and 424. In particular, copper cold plate 450 may be implemented as copper cold plate 900 of FIG. 9. It should be understood that in designs where an end pancake has a ring-shaped electrical joint along its inner diameter to mate with a regular pancake, copper cold plate 900 or a plate of similar design should be used at the interface.

[0082]

[0098] Similarly, Fig. 10 shows a copper cold plate 1000 used between pancakes mated along their outer diameters as illustrated by electrical coupling interface 1010, such as the connection between pancakes 412 and 414 at electrical coupling 446 as shown in Fig. 4B, as well as similar connections between pancakes 416 and 418 and between pancakes 420 and 422. In particular, copper cold plate 454 may be implemented as copper cold plate 1000 of Fig. 10. In the exemplary design of Figs. 4A and 4B, where each of end pancakes 430 and 432 has a single ring-shaped joint, copper cold plate 1000 may be used for the connections between pancakes 430 and 410 and between pancakes 424 and 432.

[0083]

[0099] It should be understood that in designs with an odd number of sized pancakes, one end pancake will have an electrical connection along its inner diameter and the other end pancake will have an electrical connection along its outer diameter. In such a case, the first end pancake is adjacent to copper cold plate 900 and the second end pancake is adjacent to copper cold plate 1000.

[0084]

[0100] According to some embodiments, a thermally conductive member may be inserted between one of the pancakes and the adjacent stacked cold plate to increase thermal conductivity when the magnet assembly is under vacuum and to facilitate cooling of the pancake incorporating the HTS tape. By way of example, the thermally conductive member may be indium foil, or a cryogenic high vacuum grease such as Apiezon® N grease by M&I Materials Limited, Manchester, UK, or a mesh of conductive wires.

[0085]

[0101] To complete the fabrication of the magnet assembly 400 shown in Figures 4A-4B, regular and end pancakes with a number appropriate to the operational requirements are stacked with insulated copper cold plates as described above, and the stack of pancakes with intermediate cold plates can be joined together by bolts at both its inner diameter and its outer diameter. Optionally, the magnet assembly 400 includes additional structural plates 480, 482 at the top and bottom of the stack, which are bolted together, and the stacked plates are instead (or additionally) pressed together by those additional structural plates 480, 482. At a later point in time, the magnet assembly 400 can be disassembled by removing the fastening bolts to separate the individual pancakes. The cold mass can then be reassembled with more or fewer regular pancakes to achieve different operational magnetic fields, as needed. Thus, it should be understood that the design of magnet assembly 400 is beneficially both modular and conduction cooled, allowing for easy assembly and disassembly, and that the use of ten pancakes and nine cooling plates in the embodiment shown in Figures 4A and 4B is merely exemplary.

[0086]

[0102] Thus, a magnet assembly 400 is disclosed that includes multiple cold plates (of which cold plates 450 and 454 are examples), each having a terminal (e.g., terminal 452) for thermally coupling the cold plate to a cooling device 470. As shown in Figures 4A and 4B, multiple pancakes and multiple cold plates are arranged in an alternating stack, with each pancake in the stack electrically coupled by its one or more junctions to the junctions of either one or two nearby pancakes in the stack, thereby forming an operating current path through the stack that includes the HTS tape in each of the pancakes, and each of the pancakes is adjacent and thermally coupled to either one or two of the cold plates.

[0087]

[0103] For operation of the magnet assembly 400, the operating current may be defined by the current carrying capacity of the HTS tape stack specific to a given operating temperature and maximum magnetic field in the conductor. Optionally, tilting of the HTS tape stack may be effected by varying the number of tapes in the stack, since the peak magnetic field differs between turns. This helps to reduce the total amount of tape in the magnet assembly 400. To illustrate, the critical current of the HTS tape is smaller at the inner diameter (ID) than at the outer diameter (OD) because the magnetic field is higher at the ID and lower at the OD. To compensate for the difference, more tape is needed at the ID, i.e., the HTS tape stack is "tipped". This is accomplished by starting the winding at the ID with the maximum required number of tapes, and then terminating some of the tapes at a given radial location, which may be done in the winding process as described above. It should be noted that this simplified explanation does not account for the dependence of the critical current on the direction of the magnetic field relative to the tape plane, but is sufficient for the present disclosure.

[0088]

[0104] There are several nominal modes for operating the magnet assembly 400: charge, steady state, slow rate and fast discharge, along with uncontrolled quench, each of which is described below.

[0089]

[0105] The charging and slow discharge modes are performed by varying the transport current controlled by an external power source (not shown). Unlike conventional magnets wrapped with insulated cables, charging of non-insulated magnets takes much longer and is driven by inductive voltage driven inter-turn current sharing and the resulting heating. The faster the charging rate dl / dt, the stronger those radial currents are, and the more resistive heating power stored inside the structure needs to be removed by conductive cooling to avoid temperature rise of the cold mass structure and HTS tape. To speed up charging, in this magnet assembly 400, the charging rate can be controlled and dynamically adjusted to maintain the temperature measured at the warmest location (i.e., the location furthest from the cooling source) at the highest acceptable value. The highest acceptable temperature is defined by the approximation of the transport current to the critical current for the current combination of peak magnetic field and temperature.

[0090]

[0106] The heat loss in steady state mode operation at a given constant current is very small and is easily managed by the available cooling power of the cooling source described in connection with Figures 11A and 11B.

[0091]

[0107] The fast discharge is used to drive the current and magnetic field of the magnet assembly 400 to zero in emergency situations. This is accomplished by opening the current supply circuit. This action triggers strong induced eddy currents in the radially outermost turns of the axially outermost pancake, tending to shield the magnetic flux in the magnet assembly 400. The outer diameter joint 402 provides a convenient circumferential path for these currents, facilitating substantially uniform heating along the edges of the turns. This heat wave propagates radially deeper into the magnet assembly 400, quenching the turns of the HTS tape one by one until the entire pancake is quenched. At this time, most of the transport current changes its path from azimuthally along the turns of the helical HTS tape to a more resistive path radially through the structural plate and the substrate of the HTS tape itself (which may be, for example, a corrosion-resistant alloy such as Hastelloy® nickel-based alloy from Haynes International, Inc., Kokomo, Indiana, USA). The lost flux of the quenched pancake is picked up by the next pancake and triggers a similar process in it. This process continues until the entire pancake is quenched and all the stored electromagnetic energy is deposited in the cold mass in the form of heat.

[0092]

[0108] The advantage of this method of quenching the magnet is that the quench is initiated, predictable, propagates very uniformly and does not form localized overheating points. This is achieved essentially due to the joints forming a path for the induced current. The quench time depends on the size of the magnet assembly 400 and is expected to be very fast, less than one second. This differs from insulated magnets known in the field of the invention, which are quenched by dumping the current through an external resistor. In this case, the quench time is defined by the terminal voltage and is usually very long. A notable feature of quenching in non-insulated magnets is the low voltage, on the order of 1 V or less, generated between the components comprising the magnet. This feature significantly reduces the requirements to insulation and allows the use of the insulation techniques mentioned above.

[0093]

[0109] Uncontrolled quenching usually occurs due to the local formation of a quench initiation zone, where the transport current exceeds the critical current for some reason. In non-insulated magnets, including the present design, this situation locally radially redistributes part of the series winding current, thereby changing the magnetic flux distribution and creating a condition similar to that described above for emergency shutdown with controlled quenching. Copper cladding in the form of copper joints serves a similar purpose and leads in the present design to a more controlled quench propagation, resulting in more uniform Joule heating. Alternatively, with sufficient cooling power, the normal conduction band can return to a superconducting state.

[0094]

[0110] According to some embodiments, the cold mass of the magnet assembly may be surrounded by an insulating vacuum and enclosed in a cryostat, with a thermal radiation shield inserted between the cryostat wall and the cold mass. Conduction cooling may be achieved by cryocoolers, cryofridges, heat exchangers utilizing a continuous flow of cryogenic liquid, or other conventionally used approaches. In general, however, the cooling device acts as a heat sink for the thermal energy generated in the cold mass. Additionally, the cooling device, together with its insulation, provides cooling of the cold mass of the magnet to the operating temperature, facilitates charging / discharging of the magnet assembly, and physically supports the magnet assembly during operation and, if necessary, during transportation.

[0095]

[0111] In this regard, Figure 11A is a cutaway view of a magnet assembly 1100 coupled to a portion of a cooling device 1110, and Figure 11B illustrates the portion 1110 highlighting the different thermally protective layers surrounding the magnet assembly 1100. The magnet assembly 1100 may be, for example, the magnet assembly 400 of Figures 4A and 4B.

[0096]

[0112] Thermal insulation can be achieved in several forms. The first form is e.g. -4The first involves pumping out the cryostat to an adiabatic vacuum, which can be a pressure below 1000 MPa. The second involves placing a thermal radiation shield 1120 around the cold mass that is cooled to some intermediate temperature between the cryostat wall temperature and the cold mass temperature. The third involves encasing the cold mass and radiation shield 1120 in a multi-layer insulation (MLI) 1130, shown in more detail in FIG. 11B.

[0097]

[0113] The radiation shield 1120 that surrounds the magnet assembly 1100 and the entire cold mass comprises a thermally conductive metal, typically copper, that has good thermal contact with an intermediate temperature source of cooling, which may be a separate cryocooler, or the first stage of a cryocooler that cools the magnet, or any other source of the required temperature and cooling power, such as liquid nitrogen or cryogenic gas from a cryofridge, or any combination thereof.

[0098]

[0114] Depending on the fringing magnetic field at the location of the radiation shield 1120 and the rate of change of the magnetic field during magnet quenching, the radiation shield 1120 may be cut off for electrical isolation in portions 1122 to limit eddy currents in the material of the shield 1120 and to limit Lorentz forces interacting between the quenching magnet and the shield 1120. Such forces may deform or even destroy the radiation shield 1120. The thermally conductive material of the shield 1120 may be reinforced by strong metallic or non-metallic structures for similar reasons.

[0099]

[0115] Very fast, sub-second quench onset times are specific to the non-insulated coils disclosed herein, during which the coil current and the high magnetic field generated by this current change from their operating values ​​to zero. These changes can result in strong Lorentz forces in the radiation shield 1120 that are so strong that typical measures similar to those described above are not sufficient to protect the integrity of the shield 1120 during a quench.

[0100]

[0116] 11B, in order to reduce and limit eddy currents and forces acting on the radiation shield 1120 in the disclosed cooling device, the conductive material (e.g., copper) of the radiation shield 1120 is cut into narrow strips at least in a portion 1122. The size of these strips is determined by the tolerable forces on the structure of the shield 1120. The strips in the portion 1122 are electrically insulated from each other. By way of example, the strips may be implemented as 10 mm wide copper strips with an insulating gap of 0.5-1.0 mm between them. The strips are bonded to an underlying shield structure 1124, which may be formed of a non-conductive material such as fiberglass G11-CR. Alternatively, if the forces generated during the quench permit, the underlying shield structure 1124 may be formed of a less conductive but stronger metal such as stainless steel.

[0101]

[0117] Bonding of the copper strips in section 1122 to the structure 1124 of the shield 1120 may be accomplished by gluing, riveting, or screwing. An electrically insulating film may be used to insulate the copper strips from the stainless steel body, if present. Any strips attached to the radiation shield 1120 parallel to the top and bottom faces of the magnet assembly 1100 need to be bonded to the outer surface of the shield structure. During a quench, in this position, the strips are pushed into the shield structure, towards the magnet assembly 1100.

[0102]

[0118] At least a portion of the radiation shield 1120 is located away from the magnet assembly 1100 so that the magnetic field level allows for the normal design of the shield (i.e., not being cut by the strips). Thermally conductive copper strips are bonded to the thermally conductive portion of the shield by application of indium shims or Apiezon® N grease to reduce the thermal resistance of the joint in the surrounding vacuum.

[0103]

[0119] Alternatively, the radiation shield 1120 can be formed as a fiberglass dash with imprinted copper strips of the required shape. A similar circuit board can be used to route the instrumentation wires.

[0104]

[0120] In some embodiments, the radiation shield 1120 is wrapped in a multi-layer insulation (MLI) 1130 to reduce the temperature drop and heat load on the shield due to heat transfer from the warm cryostat walls. The MLI 1130 is 100% thermally insulated for good thermal performance of the cryostat. -5 From 10 -7 It is used for insulation in vacuum environments at reduced pressures of 1000 MPa. The MLI1130 consists of alternating layers of low emissivity radiation shield and low thermal conductivity spacer material. The most commonly used low emissivity radiation shield is a Mylar® substrate with a vacuum deposited aluminum coating on one or both sides of the sheet. The spacer material can vary, most commonly polyester. The MLI1130 blanket may consist of many layers, for example 32 layers, and often two blankets are used for better insulation of the shield.

[0105]

[0121] The thickness of the evaporated aluminum is, for example, 350 angstroms, i.e., 3.5*10 -5The thickness of the blanket is very small, for example, mm. In this example, the total thickness of the aluminum in the blanket with 32 double aluminized layers is 0.00224 mm. At the same time, the deposited material may be very high purity aluminum (according to the expression used in the publication) with a residual resistance ratio (RRR) of approximately 1000 or more. RRR is the ratio of the resistance of the material at room temperature to a cryogenic temperature of about 20 K. These properties mean that at the operating temperature of the radiation shield 1120, 60-80 K, the combined effect of eddy currents in the MLI blanket during a quench of a non-electrically insulating magnet can generate significant forces applied to the radiation shield 1120, which the blanket of the MLI 1130 envelops. This force may damage the radiation shield and may also damage the MLI 1130.

[0106]

[0122] For high-field, non-electrically insulating magnet cooling devices, the deposition of aluminum on the Mylar film (or film of other material) of the MLI 1130 is done with interruptions located at different locations on both sides of the aluminized film. The narrow interruptions provide the necessary electrical insulation when dividing the aluminized layer into strips. During quenching of the magnet, the interruptions limit the eddy currents in the aluminized film and reduce the Lorentz forces applied to the shield 1120 to acceptable levels. At the same time, the thermal performance of the MLI 1130 is not significantly degraded. This is due to the small surface area of ​​the interruptions in the aluminum film and the absence of transparent locations in the double aluminized film.

[0107]

[0123] The above description assumes that the cold mass is cooled using a dry, conductive cooling scheme. Alternatively, the cold mass may be cooled by a cryogenic reservoir scheme, in which case it is surrounded by a sealed case containing a cryogenic liquid, e.g., helium, neon, argon, hydrogen, etc. In the latter case, one skilled in the art will understand how to modify some of the features described above to implement this change in cooling device design.

[0108]

[0124] For illustrative purposes, Figure 12 is a cross-sectional view of layers of an exemplary coated conductor HTS tape, according to some embodiments. The following description is applicable to the above-mentioned HTS tape disposed in a magnet or magnet assembly, in some embodiments. Rare earth barium copper oxide ("REBCO") is a ceramic-based HTS. Although ceramic-based HTS was first discovered in 1987, large-scale manufacturing of REBCO HTS conductors was not possible until relatively recently due to the difficulty in producing long strands of REBCO that still maintained high performance.

[0109]

[0125] FIG. 12 is an example of an HTS tape 1200 fabricated as a coated conductor, where the HTS layer 1210 is a layer of REBCO. As noted above, "REBCO" is an acronym for "rare-earth barium copper oxide." As used herein, at least in some instances, "REBCO" may be used to more generally refer to any rare-earth copper salt HTS. Thus, unless expressly noted, barium may be present in the REBCO, but its presence is not required. However, in the example of FIG. 12, the REBCO layer is provided as an example of an HTS layer and is not intended to limit the illustrated structure to a particular HTS use.

[0110]

[0126] In the example of Figure 12, the exemplary tape 1200 further includes a buffer layer 1212, a Hastelloy layer 1214, and a copper layer 1216 and a silver layer 1218 disposed above and below the REBCO layer, respectively. The copper layer may be referred to as a "stabilizer" layer. Exemplary dimensions of the tape are shown in Figure 12, with the tape having a width (dimension in the X-direction) of approximately 2-12 mm and a thickness (dimension in the Y-direction) of approximately 0.1 mm.

[0111]

[0127] In some embodiments, the HTS tapes can have an aspect ratio (which is the ratio of the width of the tape to its thickness) that is greater than or equal to 10, 20, 40, 60, 80, 100, 120, or 150. In some embodiments, the HTS tapes can have an aspect ratio that is less than or equal to 150, 120, 100, 80, 60, 40, 20, or 10. Any suitable combination of the above-mentioned ranges is also possible (e.g., aspect ratios greater than or equal to 60 and less than or equal to 100).

[0112]

[0128] In some embodiments, the HTS tape may have a thickness of 0.005 mm, 0.01 mm, 0.05 mm, 0.1 mm, 0.15 mm, or 0.2 mm or more. In some embodiments, the HTS tape may have a thickness of 0.5 mm, 0.2 mm, 0.15 mm, 0.1 mm, 0.05 mm, or 0.01 mm or less. Any suitable combination of the above-mentioned ranges (e.g., thicknesses of 0.01 mm or more and 0.1 mm or less) is also possible.

[0113]

[0129] FIG. 13 is a three-dimensional graphic of a power plant with cutaway portions showing various components of the fusion power plant, according to some embodiments. The fusion power plant may include a magnet or magnet assembly fabricated as described above. FIG. 13 shows a cross section of the power plant, including magnet coils 1314, neutron shield 1312, and core region 1311. According to some embodiments, magnet coils 1314 may be, or form part of, a toroidal field coil. In some embodiments, magnet coils 1313 may be fabricated from, or otherwise include, a superconducting magnet fabricated as discussed and described above. According to some embodiments, magnet coils 1313 may be, or form part of, a central solenoid and / or other poloidal field solenoid wound coils.

[0114]

[0130] Those skilled in the art may recognize other embodiments of the concepts, results, and techniques disclosed herein. It is recognized that superconducting magnets constructed according to the concepts and techniques described herein may be useful for a wide range of applications. For example, one such application is performing nuclear magnetic resonance (NMR) studies, for example, on solid physics, physiology, or proteins. Another application is performing clinical magnetic resonance imaging (MRI) for medical scanning of organisms or parts thereof, where a small high-field magnet is required. Yet another application is high-field MRI, where a large-bore solenoid is required. Still another application is for performing magnetic studies in physics, chemistry, and materials science. Further applications are in particle accelerators for material processing or research, generators, medical accelerators generally for proton therapy, radiation therapy, and radiation generation, superconducting energy storage, magnetohydrodynamic (MHD) generators, and magnets for material separation, such as mining, semiconductor fabrication, and recycling. It is to be understood that the above list of applications is not exhaustive, and there are further applications to which the concepts, processes, and techniques disclosed herein are applied without departing from their scope.

[0115]

[0131] As used herein, the expressions "HTS material" or "HTS superconductor" refer to a superconducting material that has a critical temperature above 30° K at zero self-field.

[0116]

[0132] Having thus described several aspects of at least one embodiment of this invention, it is to be appreciated that various alterations, modifications, and improvements will readily occur to those skilled in the art.

[0117]

[0133] Such alterations, modifications, and improvements are intended to be part of this disclosure and are intended to be within the spirit and scope of the present invention. Furthermore, while advantages of the present invention are shown, it should be understood that not every embodiment of the technology described herein includes every advantage described. Some embodiments may not implement any of the features described herein as being beneficial, and in some instances, one or more of the described features may be implemented to achieve further embodiments. Thus, the above description and drawings are by way of example only.

[0118]

[0134] In the above detailed description, various features of the embodiments are grouped together in one or more individual embodiments for the purpose of streamlining the disclosure. This method of disclosure is not to be interpreted as reflecting an intention that the claims require more features than are expressly recited herein. Rather, novel aspects may reside in less than all features in each disclosed embodiment.

[0119]

[0135] The above-described embodiments of the technology described herein may be implemented in any of many ways. Various aspects of the invention may be used alone, in combination, or in various configurations not specifically described in the above-described embodiments, and therefore are not limited in their application to the details and configurations of components set forth in the above description or illustrated in the drawings. For example, aspects described in one embodiment may be combined in any manner with aspects described in other embodiments.

[0120]

[0136] The invention may also be embodied as a method, of which an example has been provided. The operations performed as part of the method may be ordered in any suitable manner. Accordingly, embodiments may be constructed in which operations are performed in an order different from that shown, and which may include performing some operations simultaneously, even when shown as sequential operations in the example embodiments.

[0121]

[0137] Additionally, some actions are described as being performed by a "user." It should be understood that a "user" need not be a single individual, and that in some embodiments actions attributed to a "user" may be performed by a team of individuals and / or an individual in combination with computer-assisted tools or other mechanisms.

[0122]

[0138] The use of ordinal terms such as "first," "second," "third," etc. in the claims to modify claim elements does not in itself imply any priority, precedence, or ordering of a claim element relative to other orders or temporal orders in which method operations are performed, but is used solely as an indication to distinguish one claim element having a particular name from other elements having the same name (because of the use of ordinal terms) to distinguish claim elements.

[0123]

[0139] The terms "approximately" and "about" may be used in some embodiments to mean within ±20% of a target value, in some embodiments within ±10% of a target value, in some embodiments within ±5% of a target value, and even in some embodiments within ±2% of a target value. The terms "approximately" and "about" may include the target value. The term "approximately equal" may be used to refer to values ​​that are in some embodiments within ±20% of each other, in some embodiments within ±10% of each other, in some embodiments within ±5% of each other, and even in some embodiments within ±2% of each other.

[0124]

[0140] The term "approximately" may be used to refer to values ​​that are within ±20%, in some embodiments within ±10%, in some embodiments within ±5%, and even in some embodiments within ±2% of a comparative measurement in some embodiments. For example, a first direction that is "approximately" perpendicular to a second direction may refer to a first direction that is within ±20% of forming a 90° angle with the second direction in some embodiments, within ±10% of forming a 90° angle with the second direction in some embodiments, within ±5% of forming a 90° angle with the second direction, and even in some embodiments within ±2% of forming a 90° angle with the second direction.

[0125]

[0141] Also, the phraseology and terminology used herein is for the purpose of description and should not be regarded as limiting. The use of "including," "comprising," or "having," "containing," "involving," and variations thereof herein are intended to encompass the items listed before it, as well as equivalents thereof, and additional items.

Claims

1. 1. A high temperature superconductor (HTS) magnet, comprising: a coil including an HTS material; a housing having at least a first partition; Equipped with The coil is disposed within the housing, a first bulkhead of the housing is positioned to separate the first portion of the coil from the second portion of the coil such that the turns of the first portion of the coil are disposed generally within the first bulkhead and the turns of the second portion of the coil are disposed generally outside the first bulkhead; the first partition wall has a slit through which the coil passes, Before the coil is wound, the first bulkhead is free to move within the housing. High temperature superconductor (HTS) magnets.

2. 2. The magnet of claim 1, wherein the housing comprises a first structural plate and a second structural plate, the coil is disposed between the first structural plate and the second structural plate, and the first bulkhead comprises a wall extending between the first structural plate and the second structural plate.

3. The magnet of claim 2 , wherein said first structural plate includes a first circular slot, and said first bulkhead is disposed within said first circular slot.

4. 4. The magnet of claim 3, wherein said first bulkhead is removably inserted within said first circular slot, and said first bulkhead is freely rotatable within said first circular slot.

5. The magnet according to claim 1 , wherein the slit extends to a height of the first partition wall.

6. 2. The magnet of claim 1, wherein an outer shape of the first partition is a helical shape, and the slits in the first partition are gaps between adjacent turns of the helical shape of the first partition.

7. The magnet of claim 1 , wherein the HTS material is an HTS tape.

8. The magnet of claim 7 further comprising a conductive material disposed between at least some of the turns of the coil.

9. 9. The magnet of claim 8, wherein the coil is formed from multiple layers of HTS tape wound into multiple turns and the layer of conductive material.

10. 8. The magnet of claim 7, wherein the coil includes turns of the HTS tape arranged such that turns of the HTS tape contact faces of the HTS tape in adjacent turns.

11. 10. The magnet of claim 1, further comprising a first conductive ring coupled to an inner end of the coil and a second conductive ring coupled to an outer end of the coil.

12. 2. The magnet of claim 1, wherein the housing includes a second partition disposed outside the first partition and having a slit through which the coil extends, and wherein the turns of the first portion of the coil and at least some of the turns of the second portion of the coil are disposed entirely within the second partition of the coil.

13. The magnet of claim 1 , wherein each of the housing and the first bulkhead comprises steel, an austenitic nickel-chromium alloy, and / or a nitrogen-strengthened austenitic stainless steel.

14. A magnet assembly comprising a plurality of magnets according to claim 1.

15. a plurality of pancakes, each of the pancakes having one or more turns of high temperature superconductor (HTS) tape that generates a magnetic field when an electric current is applied to the pancake, each of the pancakes further having one or more joints for electrically coupling the one or more turns of the HTS tape as part of an electric circuit; a plurality of cooling plates, each of the cooling plates having a terminal for thermally coupling the cooling plate to a cooling device; A magnet assembly comprising: the plurality of pancakes and the plurality of cold plates are stacked in an alternating fashion, each of the pancakes being electrically coupled by its one or more joints to the joints of either one or two nearby pancakes, thereby forming an operating current path including the HTS tape in each of the pancakes, each of the pancakes being adjacent to either one or two of the cold plates for removing heat from the pancake by thermal conduction to the cooling device; At least one of the pancakes comprises a housing having a first partition; Before the coil containing the HTS tape is wound, the first bulkhead is free to move within the housing. Magnet assembly.

16. 16. The magnet assembly of claim 15, wherein each of the pancakes comprises steel, or an austenitic nickel-chromium alloy, or a nitrogen-strengthened austenitic stainless steel.

17. The magnet assembly of claim 15 , wherein the HTS tape of at least one of the pancakes comprises rare earth copper oxide.

18. The magnet assembly of claim 15 , wherein the one or more bonding bodies of at least one of the pancakes comprises copper.

19. 16. The magnet assembly of claim 15, wherein the one or more abutments of each of the pancakes are located on at least a portion of an inner diameter of the pancake, or a portion of its outer diameter, or a portion of both the inner diameter and the outer diameter.

20. 16. The magnet assembly of claim 15, wherein a first one of the pancakes comprises a first face having a joint on an outer diameter thereof and a second parallel face having a joint on an inner diameter thereof.

21. 21. The magnet assembly of claim 20, wherein the first one of the pancakes is electrically coupled to a mating body on the outer diameter of a second one of the pancakes by the mating body on its outer diameter, and the first one of the pancakes is electrically coupled to a mating body on the inner diameter of a third one of the pancakes by the mating body on its inner diameter.

22. 16. The magnet assembly of claim 15, wherein each pancake at the top of the stack and each pancake at the bottom of the stack has an inner surface with a joint on either its outer diameter or its inner diameter that is electrically coupled to the joint of the other pancake, and parallel outer surfaces that have no joint.

23. 16. The magnet assembly of claim 15, wherein at least one of the pancakes comprises a plurality of channels separated by one or more removable bulkheads for withstanding radial loads, each channel having one or more turns of the HTS tape, each removable bulkhead having a feed-through connecting the turns of the HTS tape in nearby channels.

24. 24. The magnet assembly of claim 23, wherein the HTS tape of the at least one of the pancakes is soldered to at least one of the plurality of channels, or soldered to the one or more bonding bodies, or both.

25. 24. The magnet assembly of claim 23, wherein the one or more turns of HTS tape in each of the channels approximately fills a volume of the channel.

26. 16. The magnet assembly of claim 15, further comprising a conductive gasket between the joints of each of two adjacent stacked pancakes.

27. 16. The magnet assembly of claim 15, further comprising a thermally conductive foil, or grease, or wire mesh between one of the pancakes and an adjacent stacked cold plate.

28. The magnet assembly of claim 15 , wherein the plurality of pancakes and the plurality of cold plates are connected by bolts at both the inner diameter and the outer diameter of the stack.

29. 16. The magnet assembly of claim 15, further comprising additional structural plates at the top and bottom of said plates stacked and bolted together, said stacked plates being pressed together by said additional structural plates.

30. 16. The magnet assembly of claim 15, wherein the HTS tape in at least one of the pancakes is co-wound with copper, steel, or both copper and steel.

31. The magnet assembly of claim 15 , wherein at least two of the pancakes have different sizes or shapes.

32. 16. A magnet assembly as claimed in claim 15, wherein said cooling device comprises a cryo-cooler, or cryo-refrigerator, or heat exchanger utilising a continuous flow of cryogenic liquid and / or gas.

33. The magnet assembly of claim 15 further comprising a thermal radiation shield.

34. The magnet assembly of claim 33 , wherein the thermal radiation shield comprises copper and / or aluminum.

35. 35. The magnet assembly of claim 34, wherein the copper is cut to limit eddy currents and to limit Lorentz forces during magnet quench.

36. The magnet assembly of claim 33 wherein said thermal radiation shield is encased in multiple layers of insulation.

37. 37. The magnet assembly of claim 36, wherein said multi-layer insulation includes alternating layers of spacer material and a substrate having an aluminum coating deposited thereon having a barrier thereon.

38. 1. A magnet assembly comprising a plurality of pancakes, each of said pancakes comprising: a housing having a first partition; a plurality of turns of high temperature superconductor (HTS) tape disposed within the housing; one or more conductive joints coupled to the HTS tape and disposed on the exterior of the housing; a plurality of cooling plates, each of the cooling plates having a terminal for thermally coupling the cooling plate to a cooling device; the plurality of pancakes and the plurality of cold plates are arranged in an alternating stack, each of the pancakes in the stack being electrically coupled by its one or more conductive joints to the joints of either one or two nearby pancakes in the stack, thereby forming an operating current path through the stack including the HTS tape in each of the pancakes, each of the pancakes being adjacent and thermally coupled to either one or two of the cold plates; Before the coil containing the HTS tape is wound, the first bulkhead is free to move within the housing. Magnet assembly.

39. A housing for holding a wound tape for generating a magnetic field, said housing comprising: a first structural plate having one or more first circular slots; one or more bulkheads, each bulkhead having a feedthrough connection for winding the tape from an inner diameter of the bulkhead to an outer diameter of the bulkhead, each bulkhead removably and rotatably inserted into a corresponding one of the first circular slots; a second structural plate having one or more second slots, each bulkhead being removably inserted into a corresponding one of the second slots; and A housing comprising:

40. 40. The housing of claim 39, wherein one of the partitions includes a through-connection slit that does not extend the entire height of the partition.

41. 40. The housing of claim 39, wherein one of the partitions includes a through-connection slit that extends the entire height of the partition.

42. 40. The housing of claim 39, wherein one of the partitions comprises a spiral having a radially uniform thickness.

43. 40. The housing of claim 39, wherein each bulkhead has a feedthrough for holding a wound tape for generating a magnetic field, the wound tape being co-wound with copper, or steel, or both copper and steel.

44. A method of winding a high temperature superconductor (HTS) conductive tape to form an HTS magnet, the method comprising: (a) providing a first structural board having a first electrical connection; (b) physically and electrically coupling the HTS conductive tape to the first electrical joint; (c) wrapping the conductive tape in a circular shape on the surface of the first structural plate; (d) removably inserting a bulkhead having a feedthrough into the first structural plate, the bulkhead moving within the first structural plate such that the feedthrough aligns with an azimuthal position of the wrapped conductive tape; (e) wrapping the conductive tape on the surface of the first structural plate, through the feedthrough, and around an outer diameter of the septum, thereby minimizing a gap between the HTS conductive tape and the septum; The method includes:

45. The method of claim 44, further comprising repeating steps (c) to (e) for each additional slot in the partition having a through connection.

46. The method described in claim 44, wherein the first structural plate has a surface having one or more circular slots, the first structural plate having a second electrical joint on its outer diameter, and the method further includes the step of physically and electrically coupling the conductive tape to the second electrical joint.

47. 45. The method of claim 44, further comprising adding a layer of indium adjacent to the wrapped conductive tape.

48. providing a second structural plate having a surface with a second circular slot; positioning the second structural plate flush with the wrapped conductive tape such that the bulkhead is removably inserted into the second circular slot; 45. The method of claim 44, further comprising:

49. 45. The method of claim 44, wherein the conductive tape is co-wound with copper, steel, or both copper and steel.