Electrode assembly

Abstract

The present application provides an electrode assembly.

Description

[Technical field]

[0001] This application claims priority to Korean Patent Application No. 10-2021-0090596 filed on July 9, 2021, Korean Patent Application No. 10-2021-0090592 filed on July 9, 2021, Korean Patent Application No. 10-2021-0090597 filed on July 9, 2021, and Korean Patent Application No. 10-2021-0090598 filed on July 9, 2021, the entire contents of which are incorporated herein by reference.

[0002] The present invention relates to an electrode assembly. [Background technology]

[0003] Unlike primary batteries, secondary batteries are rechargeable and have the potential to be small and have large capacity, so they have been the subject of much research and development in recent years. As technological development and demand for mobile devices increases, the demand for secondary batteries as an energy source is growing rapidly.

[0004] Secondary batteries are classified into coin-type batteries, cylindrical batteries, square batteries, and pouch-type batteries according to the shape of the battery case. The electrode assembly attached inside the battery case of a secondary battery is a power generating element capable of charging and discharging, which is made of a laminated structure of electrodes and a separator.

[0005] The electrode assemblies can be generally classified into a jelly-roll type, a stack type, and a stack-and-folding type. In the jelly-roll type, a separator is interposed between a sheet-like anode and cathode coated with an active material, and the entire arrangement is wound up. In the stack type, a number of anodes and cathodes are stacked in sequence with a separator interposed therebetween. In the stack-and-folding type, stacked unit cells are wound up with a long length of separator film. [Prior art documents] [Patent documents]

[0006] [Patent Document 1] Korean Patent Publication No. 10-2013-0132230 Summary of the Invention [Problem to be solved by the invention]

[0007] First, the present invention provides an electrode assembly that reduces variations in adhesion and air permeability across layers while maintaining adequate adhesion and air permeability. [Means for solving the problem]

[0008] An exemplary aspect of the present invention provides an electrode assembly, the electrode assembly according to such aspect of the present invention preferably including a plurality of electrodes arranged in a stack along a stacking axis, with respective separator membrane portions positioned between each of the electrodes in the stack.

[0009] The plurality of electrodes includes an upper electrode located at an upper portion of the laminate along the lamination axis, and the plurality of electrodes includes a lower electrode located at a lower portion of the laminate along the lamination axis. The separation membrane portion includes an upper separation membrane portion in contact with the upper electrode and a lower separation membrane portion in contact with the lower electrode. The upper separation membrane portion and the lower separation membrane portion may each have an air permeability value of 80 sec / 100 ml to 120 sec / 100 ml per square inch of the separation membrane portion at a pressure of 0.05 MPa and room temperature.

[0010] According to some aspects of the invention, the separator sections may be part of a long separator sheet that may be folded between each separator section such that the long separator sheet extends between each successive electrode in the stack along a serpentine path that traverses back and forth along the transverse dimension perpendicular to the stack axis. Effect of the Invention

[0011] The electrode assembly according to an embodiment of the present invention is preferable in that it can prevent side effects such as lithium (Li) precipitation in the electrode assembly and non-filling of the electrode assembly. The electrode assembly according to an embodiment of the present invention can also have uniform performance. [Brief description of the drawings]

[0012] [Figure 1] 1 is a cross-sectional view illustrating an example of an electrode assembly according to an embodiment of the present invention. [Diagram 2] FIG. 2 is a cross-sectional view of the electrode assembly of FIG. 1, showing the location of the upper surface, lower surface and middle portion of the electrode assembly. [Diagram 3] 1 is a top view showing an electrode assembly manufacturing apparatus for manufacturing an electrode assembly according to the present invention; [Figure 4] A front elevational view conceptually illustrating an apparatus for manufacturing the electrode assembly of FIG. 3 is shown. [Diagram 5] 6 is a photograph showing the results of checking whether or not lithium (Li) was precipitated when the electrode assemblies of Comparative Example 1 and Example 1 were disassembled after completion of charging. [Figure 6] 6 is a photograph showing the results of checking whether or not lithium (Li) was precipitated when the electrode assemblies of Comparative Example 1 and Example 1 were disassembled after completion of charging. [Figure 7] 1 is a schematic diagram showing a method for manufacturing an electrode assembly according to the present invention; [Figure 8] 1 is a perspective view of a separation membrane heating section of a separation membrane supply section according to an embodiment of the present invention; DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0013] The object, specific advantages, and novel features of the present invention will become more apparent from the following detailed description in conjunction with the accompanying drawings and embodiments. In this specification, when adding reference numbers to components in each drawing, it should be noted that the same components are given the same numbers even if they are displayed in different drawings. Furthermore, the present invention may be embodied in several different forms and is not limited to the embodiments described in this specification. In addition, in describing the present invention, detailed descriptions of related known technologies that may unnecessarily obscure the gist of the present invention will be omitted.

[0014] 1 is a cross-sectional view of an example of an electrode assembly according to an embodiment of the present invention. That is, referring to FIG. 1, an electrode assembly 10 according to an embodiment of the present invention includes an electrode stack of one or more first electrodes 11 alternating with one or more second electrodes 12. Each electrode in the stack is separated from the others by an intervening separator membrane 14, which may be one long separator membrane 14 that is folded to repeat around each successive electrode along a serpentine or zigzag path.

[0015] The electrode assembly 10 is a chargeable and dischargeable power generating element, and the first electrode may be an anode and the second electrode may be a cathode. Alternatively, however, the first electrode may be a cathode and the second electrode may be an anode. The electrode assembly 10 may be provided in a form in which the outermost periphery is surrounded by a separation membrane 14, for example, in a form in which the electrode assembly 10 assembled as shown in FIG. 1 surrounds the separation membrane. For the electrode assembly including the electrode assembly and the separation membrane, commonly used materials may be used.

[0016] As discussed further herein, the "top surface" of the electrode assembly 10 refers to the topmost position in the stacking direction of the electrode assembly 10, designated by reference number 2 in Fig. 2. Thus, the "top surface air permeability" subsequently referred to relates to the air permeability of the separator 14 that contacts the topmost electrode in the electrode assembly. Similarly, the "top surface adhesive strength" subsequently referred to refers to the adhesive strength between the abutting portion of the topmost electrode and the separator 14 in the electrode assembly.

[0017] Furthermore, as discussed herein, the "lower surface" of the electrode assembly 10 refers to the lowermost position in the stacking direction of the electrode assembly 10, designated by reference number 3 in Fig. 2. Therefore, the "lower surface air permeability" subsequently referred to relates to the air permeability of the separator 14 in contact with the lowest electrode in the electrode assembly. Similarly, the "lower surface adhesive strength" subsequently referred to refers to the adhesive strength between the abutting portion of the separator 14 and the lowest electrode in the electrode assembly.

[0018] Finally, as discussed herein, the "middle" of the electrode assembly 10 refers to a middle position between the top and bottom surfaces of the electrode assembly 10 in the stacking direction of the electrode assembly 10, as designated by reference number 1 in FIG. 2. For example, when the electrode assembly 10 consisting of nine electrodes is viewed from the side as in FIG. 2, the "middle" position relates to the position of the fifth electrode in the stack. Thus, the "middle air permeability" subsequently referred to relates to the air permeability of the separator 14 that contacts the middle electrode in the electrode assembly. Similarly, the "middle adhesion" subsequently referred to refers to the adhesion between the abutting portion of the middle electrode and the separator 14 in the electrode assembly.

[0019] 3 and 4, an apparatus 100 for manufacturing an electrode assembly according to an embodiment of the present invention includes a stack table 110, a separation membrane supply unit 120 for supplying a separation membrane 14, a first electrode supply unit 130 for supplying a first electrode 11, a second electrode supply unit 140 for supplying a second electrode 12, a first electrode stack unit 150 for stacking the first electrode 11 on the stack table 110, a second electrode stack unit 160 for stacking the second electrode 12 on the stack table 110, and a press unit 180 for bonding the first electrode 11, the separation membrane 14, and the second electrode 12 to each other. In addition, the apparatus 100 for manufacturing an electrode assembly according to an embodiment of the present invention includes a holding mechanism 170 for fixing the stack (including the first electrode 11, the second electrode 12, and the separation membrane 14) to the stack table 110 by assembling the stack.

[0020] The separation membrane supply unit 120 may have a passage through which the separation membrane 14 passes toward the stack table 110. In particular, the separation membrane supply unit 120 may include a separation membrane heating unit (separation membrane heating unit 121) that defines a passage through which the separation membrane 14 passes toward the stack table 110. As shown in FIG. 8, the separation membrane heating unit 121 includes a pair of bodies 121a, each of which may be configured in a rectangular block shape, and the bodies 121a may be spaced apart by a distance that defines one of the dimensions of the passage through which the separation membrane 14 passes. At least one or both of the bodies 121a may further include a separation membrane heater 121b that transfers heat to the separation membrane 14 by heating the respective bodies 121a.

[0021] The separation membrane supply unit 120 may further include a separation membrane roll 122 on which the separation membrane 14 is wound. Thus, the separation membrane 14 wound on the separation membrane roll 122 can be supplied to the stack table 110 by passing through the passage formed by gradually unwinding.

[0022] The first electrode supply unit 130 may further include a first electrode roll 133 on which the first electrode 11 is wound in a sheet state, a first cutter 134 which cuts the sheet-like first electrode 11 wound around the first electrode roll 133 at regular intervals to form first electrodes 11 of a predetermined size when the sheet-like first electrode 11 is unwound and supplied, a first conveyor belt 135 which moves the first electrodes 11 cut by the first cutter 134, and a first electrode supply head 136 which picks up (e.g., by vacuum suction) the first electrodes 11 transported by the first conveyor belt 135 and places them on the first electrode placing table 131.

[0023] The second electrode supply unit 140 may further include a second electrode roll 143 on which the second electrode 12 is wound in sheet form, a second cutter 144 which cuts the sheet-like second electrode 12 wound around the second electrode roll 143 at regular intervals to form second electrodes 12 of a predetermined size when the sheet-like second electrode 12 is unwound and supplied, a second conveyor belt 145 which moves the second electrode 12 cut by the second cutter 144, and a second electrode supply head 146 which picks up (e.g., by vacuum suction) the second electrode 12 transported by the second conveyor belt 145 and places it on the second electrode placing table 141.

[0024] The first electrode stacking unit 150 may be configured to stack the first electrodes 11 on the stack table 110. The first electrode stacking unit 150 may include a first suction head 151 and a first moving unit 153. The first suction head 151 picks up the first electrode 11 placed on the first electrode placement table 131 by vacuum suction via one or more vacuum suction ports (not shown) formed on the bottom surface 151b, and then the first moving unit 153 moves the first suction head 151 to the stack table 110 so that the first suction head 151 can stack the first electrode 11 on the stack table 110.

[0025] The second electrode stacking unit 160 may be configured to stack the second electrodes 12 on the stack table 110. The second electrode stacking unit 160 may have the same structure as the first electrode stacking unit 150 described above. In this case, the second electrode stacking unit 160 may include a second suction head 161 and a second moving unit 163. The second suction head 161 may pick up the second electrode 12 placed on the second electrode placement table 141 through vacuum suction. Then, the second moving unit 163 may move the second suction head 161 to the stack table 110 so that the second suction head 161 can stack the second electrode 12 on the stack table 110.

[0026] The stack table 110 may be rotatable between positions facing the first electrode stack unit 150 and the second electrode stack unit 160. By rotating the stack table 110, the holding mechanism 170 can grip the stack (including the first electrode 11, the second electrode 12, and the separation membrane 14) being assembled to fix the position of the stack relative to the stack table 110. For example, the holding mechanism 170 can apply downward pressure to the upper surface of the stack to press it toward the stack table 110. The holding mechanism 170 may include, for example, a first holder 171 and a second holder 172 that fix opposing sides of the first electrode 11 or the second electrode 12. The holders 171, 172 may each be in the form of one or more clamps or other clamping mechanisms.

[0027] As a result, the first electrode 11 is supplied from the first electrode supply unit 130 to the first electrode stacking unit 150, and the first electrode stacking unit 150 stacks the first electrode 11 on the upper surface of the separation film 14 stacked on the stacking table 110. The holding mechanism 170 then presses the upper surface of the first electrode 11 to fix the position of the first electrode 11 on the stacking table 110. Thereafter, the separation film 14 is continuously supplied, and the stack table 110 is rotated toward the second electrode stacking unit 160 to cover the upper surface of the first electrode 11. Meanwhile, the second electrode 12 is supplied from the second electrode supply unit 140, and is stacked by the second electrode stacking unit 160 on the portion where the separation film 14 covers the upper surface of the first electrode 11. Thereafter, the holding mechanism 170 releases the upper surface of the first electrode 11, and then presses the upper surface of the second electrode 12 to fix the position of the stack S to be stacked on the stacking table 110. Thereafter, the process of stacking the first electrodes 11 and the second electrodes 12 is repeated, whereby the separator 14 is folded in a zigzag pattern to form a laminate S located between successive first electrodes 11 and second electrodes 12.

[0028] After the components of the electrode assembly are stacked, the electrode assembly may undergo one or more heat press operations. In particular, the electrode assembly may be moved to a press section 180 where heated pressure blocks 181, 182 advance toward each other across the stack to apply heat and pressure to the laminate. As a result, the components of the laminate (i.e., the electrodes and separator) are thermally bonded to each other, preferably preventing the completed electrode assembly from becoming dislodged or the components of the electrode assembly from shifting positions within the stack.

[0029] The heat pressing operation applied to the electrode assembly may include a first heat pressing operation and a second heat pressing operation. The first heat pressing operation relates to the stack being heated and pressed after the first and second electrodes are alternately stacked between the folded separator to form a stack and the stack is gripped by the gripper. The second heat pressing operation relates to an operation after the first heat pressing operation, in which the stack is heated and pressed again after the gripper stops gripping the stack.

[0030] As shown in FIG. 7, the method may first include a stacking process in which first and second electrodes are alternately stacked on a separation membrane to assemble a stack (stack cell) on a stack table, in which the separation membrane is continuously supplied and folded in sequence on the previously stacked. Before the subsequent electrode of the first and second electrodes is stacked, one of the first and second electrodes is stacked. After the stacking process, the stack can be moved away from the stack table. During this time, the separation membrane is pulled, and after the separation membrane is pulled by a certain length, the separation membrane is cut. Then, a predetermined length of the cut end of the separation membrane is wound around the stack cell. The movement of the stack away from the stack table may be preferably performed by a gripper, which is a movable part, that can grip the stack on the stack table and then move the stack to the press unit 180 where the heat press operation is performed. Then, a first heat press operation is performed with the wound stack cell gripped by the gripper. When the first heat press operation is completed, the grip of the stack cell by the gripper is released. After the gripper is removed, a second heat press operation is performed. Once the second heat pressing operation is complete, a finished electrode assembly can be completed.

[0031] If the temperature, pressure, and time conditions described herein are not met, the components of the electrode assembly may not be firmly attached, the electrode assembly may become detached, or the components of the electrode assembly may become misaligned within the assembly, especially when the electrode assembly is moved prior to insertion into the battery case, and problems with the separator being too breathable may occur.

[0032] On the other hand, when the heat pressing operation disclosed herein is performed (including meeting each pressure, temperature and time condition), the electrode assembly may be produced without the need to separately heat and / or press each step of the electrode assembly (i.e., heat and / or press each electrode and separator pair at each step of the process) to bond the components together. Such separate heating and pressing at each step may result in detrimental effects of the heat and / or pressure building up on the lower separator of the stack as already stacked layers subsequently experience the applied heat and / or pressure, respectively. This may adversely affect such portions of the separator, for example, by reducing porosity (and breathability). In contrast, the present invention may simultaneously bond the entire electrode assembly, improving uniformity above all else. Thus, appropriate levels of adhesion between the electrodes and a separator having appropriate breathability may be simultaneously achieved while minimizing damage to the unit electrodes.

[0033] In this application, the "air permeability" of an electrode assembly refers to the air permeability of the separator component of the electrode assembly. Furthermore, unless otherwise specified, "air permeability" refers to the air permeability of all separators comprising the electrode assembly, where the air permeability of each separator may be independently the same or different.

[0034] In general, when the air permeability is less than 40sec / 100ml, the lithium ion migration rate in the separator increases, but there is a problem that the safety of the electrode assembly may be rapidly reduced, and there is also a problem that the migration rate of the lithium ions in the electrodes in the electrode assembly may not match the migration rate of the lithium ions in the separator. In addition, when the air permeability is more than 120sec / 100ml, the lithium ion migration rate in the separator decreases, and the efficiency and performance of the charge / discharge cycle may decrease. Therefore, regardless of the position in the electrode assembly, the separator preferably has a permeability in the range of 40sec / 100ml to 120sec / 100ml.

[0035] The electrode assembly according to the present invention preferably has higher air permeability than conventional electrode assemblies, thereby improving the safety of the electrode assembly. Specifically, the upper surface air permeability and the lower surface air permeability of the electrode assembly according to the present invention may be independently 80 sec / 100 ml to 120 sec / 100 ml.

[0036] In the present invention, the method for measuring the air permeability of a separation membrane is not particularly limited. The methods further utilized and discussed in this specification can be measured by methods commonly used in the art. For example, the air permeability was measured by the JIS Gurley measurement method of the Japanese Industrial Standards using a Gurley type densitometer (No. 158) manufactured by Toyo Seiki. That is, the air permeability of a separation membrane can be obtained by measuring the time it takes for 100 ml (or 100 cc) of air to pass through 1 square inch of separation membrane under a pressure of 0.05 MPa at room temperature (i.e., 20°C to 25°C).

[0037] According to one embodiment of the present invention, the intermediate air permeability of the electrode assembly may be in the range of 70sec / 100ml to 85sec / 100ml, preferably 75sec / 100ml to 85sec / 100ml.

[0038] According to one embodiment of the present invention, the upper surface air permeability of the electrode assembly may be in the range of 80sec / 100ml to 120sec / 100ml, preferably 80sec / 100ml to 110sec / 110ml, and more preferably 80sec / 100ml to 100sec / 100ml.

[0039] According to one embodiment of the present invention, the underside air permeability of the electrode assembly may be in the range of 80sec / 100ml to 120sec / 100ml, preferably 80sec / 100ml to 110sec / 110ml, and more preferably 80sec / 100ml to 100sec / 100ml.

[0040] According to one embodiment of the present invention, the lower surface air permeability may be equal to or lower than the upper surface air permeability. Also, the intermediate air permeability may be equal to or lower than the lower surface air permeability.

[0041] That is, the magnitudes of the top surface air permeability, bottom surface air permeability and middle surface air permeability can satisfy the following mathematical formula 1. [Mathematical formula 1] Top air permeability ≧ Bottom air permeability ≧ Intermediate air permeability The air permeability value of Equation 1 relates to the air permeability of the separator within the electrode assembly after the heating and pressurizing steps are completed.

[0042] According to one embodiment of the present invention, the adhesive strength between the separator and the electrode at any position (ie, the upper surface, the middle surface, and the lower surface) in the electrode assembly may be in the range of 5 gf / 20 mm to 75 gf / 20 mm.

[0043] In the present invention, the method of measuring the adhesive strength of the separator is not particularly limited. For example, samples of the lower, middle and upper parts of the electrode assembly may be separated from the laminate. Such samples may include an anode and a separator, or a cathode and a separator. The samples, which may be 55 mm wide and 20 mm long, are attached to respective glass slides with the electrodes positioned on the adhesive surfaces of the glass slides. Next, the samples were tested by carrying out a 90° peel test at a speed of 100 mm / min according to the test method specified in ASTM-D6862. That is, the edge of the separator is pulled upward at 90° to the glass slide at a speed of 100 mm / min, and the separator is peeled off from the electrodes along the width direction of the sample (i.e., peeling from 0 mm to 55 mm).

[0044] According to one embodiment of the present invention, the intermediate adhesive strength of the electrode assembly may be 5gf / 20mm to 35gf / 20mm, preferably 5gf / 20mm to 15gf / 20mm.

[0045] According to one embodiment of the present invention, the upper surface adhesive strength of the electrode assembly may be 5gf / 20mm to 75gf / 20mm, preferably 6gf / 20mm to 30gf / 20mm.

[0046] According to one embodiment of the present invention, the lower surface adhesive strength of the electrode assembly may be 5gf / 20mm to 75gf / 20mm, preferably 9gf / 20mm to 30gf / 20mm.

[0047] According to one embodiment of the present invention, the bottom adhesive force and the top adhesive force may be greater than the middle adhesive force.

[0048] According to an embodiment of the present invention, the adhesive strength between the anode and the separator and the adhesive strength between the cathode and the separator may be the same or different.

[0049] According to one embodiment of the present invention, the deviation between the middle adhesive strength of the electrode assembly and the upper adhesive strength or the lower adhesive strength of the electrode assembly may be 10gf / 20mm to 35gf / 20mm, preferably 10gf / 20mm to 20gf / 20mm.

[0050] According to an embodiment of the present invention, a deviation between the intermediate air permeability of the electrode assembly and either the upper surface air permeability or the lower surface air permeability of the electrode assembly may be 3 sec / 100 ml to 15 sec / 100 ml.

[0051] When the above conditions of air permeability and adhesive strength are satisfied, not only cleaning and process handling are easy, but also wetting of the separator with the electrolyte is easy, so that an electrode assembly with uniform performance can be manufactured. Also, side effects such as lithium (Li) deposition in the electrode assembly and non-charging of the electrode assembly can be prevented.

[0052] The withstand voltage of the electrode assembly of the present invention may be 1.56 kV to 1.8 kV. Since the electrode assembly of the present invention is manufactured by a manufacturing method for an electrode assembly including a first heat press and a second heat press, it is possible to simultaneously obtain superior adhesive strength and superior withstand voltage compared to a case where only the first heat press is performed.

[0053] According to an exemplary embodiment of the present invention, when the thickness of the top electrode is assumed to be 100%, an electrode assembly can be provided in which the thickness of all electrodes is 70% to 120% of the thickness of the top electrode.

[0054] According to an exemplary embodiment of the present invention, a minimum thickness of the electrodes of the electrode assembly may be 8.2 mm or greater.

[0055] According to an exemplary embodiment of the present invention, the electrode thickness deviation of the electrode assembly may be 0.013 mm to 0.035 mm.

[0056] If the electrodes constituting the electrode assembly have a small thickness and a small variation in thickness between the electrodes, the electrode assembly may be structurally more stable and tend to be more stable during use. As a result of the present invention, it is advantageously possible to manufacture an electrode assembly in which the electrodes comprising the electrode assembly have a small thickness and a small variation in thickness between the electrodes.

[0057] Although the present invention has been described in detail with reference to specific exemplary embodiments, it is to be understood that the present invention is not limited thereto, and that various implementations are possible within the technical concept of the present invention by those skilled in the art.

[0058] 1) Example 1 Nineteen anode sheets, 20 cathode sheets and a long separation membrane were supplied to the stack table from the anode supply section, cathode supply section and separation membrane supply section, respectively.

[0059] More specifically, the anode and cathode were supplied in the form of cuts from an anode sheet and a cathode sheet, respectively, and the long separator was supplied in the form of a separator sheet. Then, as described above, the stack table was rotated to stack the anode and cathode, and the supplied separator was folded. At this time, a holding mechanism was used to press and stabilize the stack on the stack table, producing a stack including 39 electrodes.

[0060] After preparing the laminate, the laminate was gripped with a gripper and pressed for 15 seconds under heating conditions of a temperature of 70° C. and a pressure of 1.91 MPa to perform a first heat press step.

[0061] After the first heat pressing step, the stack table was heated to a temperature of 70° C. as shown in Table 1 below, and a pressure of 2.71 MPa (pressure condition) was applied to the laminate by the press block of the press for 10 seconds (press time), thereby preparing the electrode assembly of Example 1.

[0062] In the process of manufacturing the electrode assembly, the above-mentioned contents regarding the present invention can be applied.

[0063] 2) Examples 2 and 3 Electrode assemblies of Examples 2 and 3 were produced in the same manner as in Example 1, except that the method of Example 1 was carried out under the temperature conditions, pressure conditions and pressing times shown in Table 1 below.

[0064] [Table 1]

[0065] 3) Comparative Examples 1 to 7 The electrode assemblies of Comparative Examples 1 to 7 were manufactured in the same manner as in Example 1, except that the temperature conditions, pressure conditions, and pressing time of the first heat pressing step in Example 1 were as shown in Table 2 below, and the second heat pressing step was not performed.

[0066] [Table 2]

[0067] 3) Experimental Example 1 - Air permeability evaluation The electrode assemblies of Examples 1 to 3 and Comparative Example 1 were evaluated for air permeability.

[0068] Specifically, after collecting the separation membrane from the electrode assemblies of Examples 1 to 3 and Comparative Example 1, the separation membrane was cut to prepare a separation membrane sample having a size of 5 cm x 5 cm (width x length), and then the separation membrane sample was washed with acetone.

[0069] Thereafter, in accordance with the JIS Gurley measurement method, the time required for 100 ml (or 100 cc) of air to pass through 1 square inch of the separation membrane was measured using a Toyoseiki Gurley type Densometer (No. 158) at room temperature and a pressure of 0.05 MPa, thereby measuring the air permeability of Examples 1 to 3 and Comparative Example 1.

[0070] The results are shown in Table 3.

[0071] [Table 3]

[0072] From the results of Table 3, it was confirmed that the upper surface air permeability and the lower surface air permeability of the electrode assembly according to the present invention are each independently 80 sec / 100 ml or more. In addition, it was confirmed that the upper surface air permeability and the lower surface air permeability of the electrode assembly according to the present invention do not exceed 120 sec / 100 ml. In other words, it was confirmed that the electrode assembly according to the present invention has an appropriate level of air permeability for use as an electrode assembly.

[0073] It was also confirmed that the deviation in air permeability between each position was less than 20 sec / 100 ml, and it was determined to be substantially uniform.

[0074] On the other hand, in the case of Comparative Example 1, the deviation in air permeability by position was smaller than in the example, but the upper and lower air permeabilities were each independently less than 80 sec / 100 ml, which confirmed that the safety was lower than that of the electrode assembly according to the present invention. This is believed to be due to the fact that only the first heat press operation was performed.

[0075] 4) Experimental Example 2 - Adhesion strength evaluation and voltage resistance evaluation After disassembling the electrode assemblies of Examples 1 to 3 and Comparative Examples 1 to 7, the separated layers were analyzed to measure the adhesive strength at the top, bottom and middle. Specifically, the adhesive strength between the separator located at the bottom of the laminate and the cathode was measured. Also, the adhesive strength between the cathode located at the top of the laminate and the separator was measured. Finally, the adhesive strength between the cathode located at the middle position along the stacking direction of the laminate and the separator was measured.

[0076] The width and length of the sampled cathode and separator for each of the separated electrode assemblies were 55 mm and 20 mm. The sampled sample was attached to a glass slide so that the electrode was located on the adhesive surface of the glass slide. Then, the glass slide to which the sample was attached was placed on the adhesion measuring device, and a 90° peel test was performed at a speed of 100 mm / min according to the test method specified in ASTM-D6862 as described above. That is, the edge of the separator was pulled 90° upward relative to the glass slide at a speed of 100 mm / min, and the separator was peeled off from the electrode along the width direction of the sample (i.e., peeling from 0 mm to 55 mm). After discounting initial significant fluctuations, the force (g / mm) applied per sample width while the separator was peeled off from the electrode was measured. The value when the separator was peeled off from the electrode was measured by pulling the separator in a direction perpendicular to the plane on which the glass slide was placed.

[0077] The results are shown in Table 4 below.

[0078] [Table 4]

[0079] Furthermore, the withstand voltages of the electrode assemblies of Examples 1 to 3 and Comparative Example 1 were also measured.

[0080] The results are shown in Table 5 below.

[0081] [Table 5]

[0082] From the results in Table 4, it was confirmed that the adhesive strength of Examples 1 to 3 was superior to that of Comparative Example 1 in which only the first heat press was carried out under the same conditions as those of the Example.

[0083] Furthermore, looking at the results in Table 5, it was confirmed that the withstand voltages of Examples 1 to 3, in which the first heat press was performed under higher temperature and pressure conditions than the comparative example, were in the range of 1.56 kV or more and 1.8 kV or less.

[0084] That is, the electrode assembly of the present invention has excellent adhesive strength, and at the same time, has a characteristic in terms of withstand voltage suitable for use as an electrode assembly, and a withstand voltage of 1.8 kV or less was confirmed.

[0085] This is believed to be because the electrode assembly of the present invention is manufactured by a manufacturing method including a first and a second heat pressing step.

[0086] 5) Experimental Example 3 After the electrode assemblies of Example 1 and Comparative Example 1 were completely filled, they were disassembled to check for the presence or absence of lithium (Li) deposition, and the results were as shown in Figures 5 and 6 below.

[0087] In the case of the electrode assembly of Comparative Example 1, it was confirmed that lithium (Li) was precipitated when the electrode assembly was disassembled after the filling was completed as shown in FIG.

[0088] Meanwhile, in the case of the electrode assembly of Example 1, it was confirmed that lithium (Li) was not precipitated when the electrode assembly was completely filled and then disassembled, as shown in FIG.

[0089] This is believed to be because the electrode assembly of the present invention is manufactured by a manufacturing method including a first and a second heat pressing step. Through the above Experimental Examples 1 to 3, it was confirmed that the electrode assembly according to the present invention has excellent stability and adhesive strength, as well as an appropriate withstand voltage, and can prevent side effects such as lithium (Li) deposition in the electrode assembly and non-filling of the electrode assembly.

[0090] 6) Experimental Example 4 - Thickness measurement The maximum thickness, minimum thickness, average thickness and electrode thickness deviation of the electrodes constituting the electrode assemblies of Examples 1 to 3 and Comparative Example 1 were measured using a flat plate thickness measuring device with a load cell.

[0091] Specifically, the thickness when the upper plate of the flat plate thickness gauge descended and contacted the lower plate was determined as 0 mm. Then, the electrode assembly whose thickness was to be measured was placed inside the flat plate thickness gauge, and the plate was lowered to apply a force of 90 kgf for 3 seconds. In Example 1, the area when a force of 90 kgf was applied was 554.1 cm2. 2 It is.

[0092] The results are shown in Table 6.

[0093] [Table 6]

[0094] From the results of Table 6, it was confirmed that the electrode assembly according to the present invention has a thin electrode and maintains an appropriate level of thickness variation between electrodes. This is believed to be because the electrode assembly according to the present invention is manufactured by a manufacturing method including a first and second heat pressing steps. [Explanation of symbols]

[0095] 10...electrode assembly 11...1st electrode 11a First electrode tab 12...Second electrode 12a Second electrode tab 14...Separation membrane 100 Manufacturing apparatus for electrode assembly 110 Stack Table 120...Separation membrane supply section 121 Separation membrane heating section 121a: Torso 121b Separation membrane heater 122 Separation membrane roll 130...First electrode supply section 131 First electrode placement table 133 First electrode roll 134 First cutter 135 No. 1 Conveyor Belt 136 First electrode supply head 140...Second electrode supply section 141 Second electrode placement table 143 Second electrode roll 144 No. 2 cutter 145 - Second conveyor belt 146 Second electrode supply head 150 First electrode stack section 151 1st suction head 151a Vacuum inlet 151b...Bottom surface 153 First moving part 160 Second electrode stack section 161 Second suction head 163 Second moving part 170 ···Holding mechanism 171 First holder 172 2nd Holder 180 ···Press Department 181, 182: Pressure block S ···Laminate

Claims

1. an electrode assembly including a plurality of electrodes arranged along a stacking axis of the stack, each of the electrodes being disposed between respective electrodes in the stack, the plurality of electrodes including an upper electrode located at an upper portion of the stack along the stacking axis, and a lower electrode located at a lower portion of the stack along the stacking axis, the separation membrane portion including an upper separation membrane portion in contact with the upper electrode and a lower separation membrane portion in contact with the lower electrode, The upper separation membrane portion and the lower separation membrane portion each have an air permeability value of 80 sec / 100 ml to 120 sec / 100 ml per square inch at a pressure of 0.05 MPa and room temperature, the upper separation membrane part is bonded to the upper electrode to such an extent that a peeling force of 5 gf / 20 mm to 75 gf / 20 mm is required to peel the upper separation membrane part from the upper electrode at a speed of 100 mm / min along the lamination axis, the lower separation membrane part is adhered to the lower electrode to such an extent that a peeling force of 5 gf / 20 mm to 75 gf / 20 mm is required to peel the lower separation membrane part from the lower electrode at a speed of 100 mm / min along the lamination axis; Electrode assembly.

2. 2. The electrode assembly of claim 1, wherein the separator sections are portions of a long separator sheet, the long separator sheet being folded between each separator section such that the long separator sheet extends between each successive electrode in the stack along a serpentine path that traverses back and forth along a transverse dimension perpendicular to the stacking axis.

3. the plurality of electrodes includes an intermediate electrode among the plurality of electrodes located between the upper electrode and the lower electrode along the stacking axis, The separation membrane part is an electrode assembly including an intermediate separation membrane part in contact with the intermediate electrode, 2. The electrode assembly of claim 1, wherein the intermediate separator has an air permeability value of 70 sec / 100 ml to 85 sec / 100 ml per square inch of each separator at a pressure of 0.05 MPa and room temperature.

4. 2. The electrode assembly of claim 1, wherein the plurality of electrodes includes an intermediate electrode among the plurality of electrodes between the upper electrode and the lower electrode along the stacking axis, the separation membrane portion includes an intermediate separation membrane portion in contact with the intermediate electrode, and the intermediate separation membrane portion is adhered to the intermediate electrode to such an extent that a peel force of 5 gf / 20 mm to 35 gf / 20 mm is required to peel the intermediate separation membrane portion from the intermediate electrode at a speed of 100 mm / min along the stacking axis.

5. 2. The electrode assembly of claim 1, wherein the upper separator has an air permeability value of 80 sec / 100 ml to 110 sec / 100 ml per square inch at a pressure of 0.05 MPa and room temperature.

6. The electrode assembly of claim 1 , wherein the lower separation membrane portion has an air permeability value lower than that of the upper separation membrane portion.

7. 7. The electrode assembly of claim 6, wherein the plurality of electrodes includes an intermediate electrode among the plurality of electrodes between the upper electrode and the lower electrode along the stacking axis, and the separation membrane portion includes an intermediate separation membrane portion in contact with the intermediate electrode, wherein the intermediate separation membrane portion has a second air permeability value per square inch of each of the separation membrane portions at a pressure of 0.05 MPa and room temperature, and the second air permeability value is equal to or smaller than the air permeability value of the lower separation membrane portion.

8. 2. The electrode assembly of claim 1, wherein the plurality of electrodes includes an intermediate electrode among the plurality of electrodes between the upper electrode and the lower electrode along the lamination axis, the separation membrane portion includes an intermediate separation membrane portion in contact with the intermediate electrode, the intermediate separation membrane portion is bonded to the intermediate electrode to a degree that a first peeling force per 20 mm width is required to peel the intermediate separation membrane portion from the intermediate electrode at a speed of 100 mm / min along the lamination axis, and the upper separation membrane portion and the lower separation membrane portion are bonded to the upper electrode and the lower electrode, respectively, to a degree that a second peeling force per 20 mm width is required to peel the upper separation membrane portion and the lower separation membrane portion from the upper electrode and the lower electrode, respectively, at a speed of 100 mm / min along the lamination axis, and a deviation between the first peeling force and the second peeling force is 3 gf / 20 mm to 15 gf / 20 mm.

9. 9. The electrode assembly according to claim 1, wherein the plurality of electrodes includes an intermediate electrode among the plurality of electrodes between the upper electrode and the lower electrode along the stacking axis, the separation membrane portion includes an intermediate separation membrane portion in contact with the intermediate electrode, the intermediate separation membrane portion has a second air permeability value per square inch of each separation membrane portion at a pressure of 0.05 MPa and room temperature, and the second air permeability value is a deviation of the air permeability value per square inch of each separation membrane portion at a pressure of 0.05 MPa and room temperature of 10 sec / 100 ml to 35 sec / 100 ml.

Images