Textile printing ink

Abstract

To provide an ink for printing, preventing stickiness, excellent in friction fastness and capable of improving color reproducibility and feeling.SOLUTION: An ink for printing, containing polymer particles contains first polymer particles, second polymer particles having a weight average molecular weight different from that of the first polymer particles, and a binder auxiliary for cross-linking the polymer particles on the surfaces, insides or outsides of the first polymer particles and the second polymer particles. When weight average molecular weights of polymers contained in the first polymer particles and the second polymer particles respectively are HMw1 and LMw2, a value of a ratio of the weight average molecular weight of each polymer (LMw2 / HMw1) is in a range of 0.01 to 0.20.SELECTED DRAWING: None

Description

[Technical field]

[0001] The present invention relates to a textile printing ink, and more particularly to a textile printing ink that is non-sticky, has good friction fastness, and can improve color reproducibility and texture. [Background technology]

[0002] In addition to screen printing and roller printing, inkjet printing, which processes images using a computer and allows printing essentially without plates, has become popular in recent years as a method for printing images such as letters, pictures, and designs onto woven and nonwoven fabrics.

[0003] Printing of fabric using this inkjet printing method includes a step of ejecting ink from an inkjet head and causing it to land on the fabric, a step of applying steam to the fabric on which the ink has landed to fix the dye contained in the ink to the fibers of the fabric, and a step of washing the fabric to which the steam has been applied to remove any dye that has not been fixed.

[0004] As an example of an ink used in such an inkjet printing method, Patent Document 1 discloses an aqueous ink containing first polymer particles formed from a polyester polymer (also referred to as a "polyester resin") and an acrylic polymer (also referred to as an "acrylic resin"), and second polymer particles formed from a urethane polymer having a weight-average molecular weight of 300,000 or more. However, since the water-based ink contains a urethane polymer, there is a problem in that the color fades in about three years.

[0005] Furthermore, Patent Document 2 discloses an aqueous inkjet ink in which ink-dispersible polymer particles have a weight average molecular weight of 20,000 or more and 100,000 or less, a glass transition temperature of 20°C or more and less than 80°C, and the ink-dispersible polymer particles are contained in an amount of 2.0 to 10 times the amount of pigment particles. However, the ink described in Patent Document 2 uses one type of latex and is not crosslinked, and therefore has problems such as stickiness and poor resistance to rubbing. [Prior art documents] [Patent documents]

[0006] [Patent Document 1] JP 2020-44751 A [Patent Document 2] JP 2011-116859 A Summary of the Invention [Problem to be solved by the invention]

[0007] The present invention has been made in consideration of the above problems and circumstances, and an object of the present invention is to provide a textile printing ink that prevents stickiness, has good friction fastness, and can improve color reproducibility and texture. [Means for solving the problem]

[0008] In the course of investigating the causes of the above problems in order to solve the above problems, the inventors discovered that by incorporating first polymer particles and second polymer particles having a specific ratio of weight average molecular weights, it is possible to prevent stickiness, achieve good friction fastness, and improve color reproducibility and texture, thereby arriving at the present invention. That is, the above-mentioned problems of the present invention are solved by the following means.

[0009] 1. A textile printing ink containing polymer particles, First polymer particles; second polymer particles having a weight average molecular weight different from that of the first polymer particles; A bonding aid for crosslinking polymer particles is contained on the surface, the inside or the outside of the first polymer particles and the second polymer particles, and A textile printing ink, characterized in that when the weight average molecular weights of the polymers contained in the first polymer particles and the second polymer particles are HMw1 and LMw2, respectively, the ratio of the weight average molecular weights of the polymers (LMw2 / HMw1) is within a range of 0.01 to 0.20.

[0010] 2. The textile printing ink according to item 1, wherein the second polymer particles are contained in an amount within a range of 1 to 100 parts by mass per 100 parts by mass of the first polymer particles.

[0011] 3. The textile printing ink according to item 1 or 2, wherein the glass transition temperature (Tg) of the first polymer particles and the second polymer particles is −35° C. or lower.

[0012] 4. The textile printing ink described in any one of items 1 to 3, characterized in that the binding assistant is a crosslinking monomer contained in each of the first polymer particles and the second polymer particles, and a crosslinking agent contained in the textile printing ink.

[0013] 5. The first polymer particle and the second polymer particle each contain a structural portion derived from a crosslinkable monomer, 5. The textile printing ink according to any one of items 1 to 4, characterized in that the structural portion derived from the crosslinkable monomer is contained in a range of 0.1 to 30 mass % based on the total amount of the first polymer particles and the second polymer particles.

[0014] 6. The textile printing ink according to any one of items 1 to 5, wherein the first polymer particles and the second polymer particles have an average particle size within a range of 30 to 250 nm.

[0015] 7. The textile printing ink according to any one of items 1 to 6, wherein the first polymer particles and the second polymer particles are contained in an amount within a range of 0.1 to 30% by mass relative to the textile printing ink. Effect of the Invention

[0016] According to the above-mentioned means of the present invention, it is possible to provide a textile printing ink which is prevented from becoming sticky, has good friction fastness, and can improve color reproducibility and texture. Although the mechanism by which the effects of the present invention are manifested or the mechanism by which the effects of the present invention are acted upon has not been clearly understood, it is speculated as follows. Generally, it is desirable to use polymer particles to bind the pigment and the fiber, as they become sticky and are less likely to peel off. In addition, after dyeing, cross-linking is performed to prevent stickiness, but cross-linking between polymer particles increases their strength, which impairs the texture. Therefore, by mixing first polymer particles and second polymer particles having a specific weight average molecular weight ratio value, i.e., by mixing high molecular weight polymer particles, which are the first polymer particles, with low molecular weight polymer particles, which are the second polymer particles, and bonding these polymer particles together, the mesh structure caused by bonding between the high molecular weight polymer particles is reduced, and softness (texture) and color reproducibility can be ensured. Another advantage of combining high molecular weight polymer particles with low molecular weight polymer particles (i.e., post-crosslinking) is that it can provide the function of adhering pigments and fibers before crosslinking. Furthermore, since the material is sticky as is, by crosslinking it to make it into a super-polymer, it can prevent stickiness after crosslinking and improve friction fastness.

[0017] Here, the mechanism of the crosslinking reaction between the high molecular weight polymer particles and the low molecular weight polymer particles will be described. The reaction mechanism shown below is a mechanism by which the crosslinking monomers contained in the high molecular weight polymer particles and the low molecular weight polymer particles react with the crosslinking agent contained in the ink. For example, when the monomers constituting the basic skeleton of the polymer contained in the high molecular weight polymer particles and the low molecular weight polymer particles are butyl acrylate (BA) and methyl methacrylate (MMA), and the crosslinking monomer is diacetone acrylamide (DAAM), if a crosslinking agent (adipic acid dihydrazide (ADH)) is dissolved in the ink, in the drying process, the ADH reacts with the crosslinking functional group derived from the crosslinking monomer (DAAM) in each polymer particle, and the high molecular weight polymer particles and the low molecular weight polymer particles are bonded. As a result, as described above, the stickiness of the fabric surface can be prevented, and the friction fastness can be improved and the texture and color reproducibility can be ensured. In this reaction mechanism, the structural portion derived from DAAM is bonded to a basic skeleton (for example, BA-MMA) constituting the polymer particle, although not shown.

[0018] [ka] [Brief description of the drawings]

[0019] [Figure 1] FIG. 1 is a diagram for explaining a method for measuring the weight average molecular weight of a first polymer and a second polymer particle according to the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0020] The textile printing ink of the present invention is a textile printing ink containing polymer particles, comprising first polymer particles, second polymer particles having a weight average molecular weight different from that of the first polymer particles, and a binding aid for crosslinking the polymer particles on the surfaces, interior or exterior of the first polymer particles and the second polymer particles, wherein when the weight average molecular weights of the polymers contained in the first polymer particles and the second polymer particles are HMw1 and LMw2, respectively, the ratio of the weight average molecular weights of the polymers (LMw2 / HMw1) is within the range of 0.01 to 0.20. This feature is a technical feature common to or corresponding to each of the following embodiments.

[0021] As an embodiment of the present invention, the second polymer particles are contained in a range of 1 to 100 parts by mass per 100 parts by mass of the first polymer particles, which allows the ratio of the weight average molecular weights to be controlled, and is therefore preferable from the viewpoint of manifesting the effects of the present invention.

[0022] It is preferable from the viewpoint of binding between the pigment and the fiber that the glass transition temperature (Tg) of the first polymer particles and the second polymer particles is −35° C. or lower.

[0023] It is preferable that the binding aid is a crosslinkable monomer contained in each of the first polymer particles and the second polymer particles, and a crosslinking agent contained in the textile printing ink, in that the crosslinkable monomer and the crosslinking agent of each polymer particle crosslink both polymer particles, resulting in excellent texture and color reproducibility, and also preventing stickiness and improving friction fastness.

[0024] It is preferable in terms of texture and friction resistance that the first polymer particles and the second polymer particles each contain a structural portion derived from a crosslinkable monomer, and that the first polymer particles and the second polymer particles as a whole contain the structural portion derived from the crosslinkable monomer in a range of 0.1 to 30 mass %.

[0025] From the viewpoint of ejection by inkjet printing, it is preferable that the average particle size of the first polymer particles and the second polymer particles is within a range of 30 to 250 nm.

[0026] It is preferable that the textile printing ink contains the first polymer particles and the second polymer particles in the range of 0.1 to 30 mass %, because both polymer particles are present in the gaps between fibers of a fabric, making it easy to distribute the pigment particles uniformly on the surfaces of the fibers, and providing excellent color reproducibility.

[0027] The present invention, its components, and embodiments for carrying out the present invention will be described below. In this application, the symbol "to" is used to mean that the numerical values ​​before and after the symbol "to" are included as lower and upper limits.

[0028] [Outline of the textile printing ink of the present invention] The textile printing ink of the present invention is a textile printing ink containing polymer particles, comprising first polymer particles, second polymer particles having a weight average molecular weight different from that of the first polymer particles, and a binding aid for crosslinking the polymer particles on the surfaces, interior or exterior of the first polymer particles and the second polymer particles, wherein when the weight average molecular weights of the polymers contained in the first polymer particles and the second polymer particles are HMw1 and LMw2, respectively, the ratio of the weight average molecular weights of the polymers (LMw2 / HMw1) is within the range of 0.01 to 0.20.

[0029] In the present invention, the state of the binding aid according to the present invention is as follows: (i) A state in which the first polymer particle or the second polymer particle is completely contained inside the first polymer particle or the second child polymer particle, does not appear on the surface of the polymer particle, and can appear on the surface by an external action; (ii) A state in which a part of a structural portion of a binding assistant molecule is contained on the surface or inside of the first polymer particle or the second polymer particle, and a structural portion having a crosslinkable group is present on the surface of the particle; (iii) In the case where the first polymer particle or the second polymer particle is contained in the ink outside the first polymer particle or the second polymer particle, at least three embodiments are preferable. Among these, it is preferable to use the states (ii) and (iii) in combination. For example, it is preferable that the binding aid according to the present invention is a crosslinking monomer contained in each of the first polymer particles and the second polymer particles, and a crosslinking agent contained in the textile printing ink. Other examples of the bonding aid include reactive species having a catalytic action that accelerates the reaction of the crosslinkable polymer or the crosslinking agent.

[0030] The ratio of the weight average molecular weights (LMw2 / HMw1) is within a range of 0.01 to 0.20, and more preferably within a range of 0.05 to 0.15. Therefore, the weight average molecular weight of the first polymer particles is larger than that of the second polymer particles, making them high molecular weight particles, and the weight average molecular weight of the second polymer particles is smaller than that of the first polymer particles, making them low molecular weight particles. The weight average molecular weight (HMw1) of the first polymer particles is preferably within a range of 100,000 to 3,000,000. The weight average molecular weight of the second polymer is a value such that the ratio of the weight average molecular weights (LMw2 / HMw1) is within a range of 0.01 to 0.20 depending on the weight average molecular weight of the first polymer.

[0031] <Method for measuring weight average molecular weight> The weight average molecular weight of the polymer contained in the first polymer particles or the second polymer particles was measured by a gel permeation chromatography (GPC) apparatus. Specifically, the synthesized polymer particle dispersion or ink is dried and dissolved in tetrahydrofuran (THF) to make a 1% solution. The 1% THF solution is then passed through a membrane filter with a pore size of 0.45 μm to prepare a sample liquid. Then, the measurement was carried out under the following conditions. In detail, for example, a GPC apparatus HLC-8220GPC (manufactured by Tosoh Corporation) and a column "TSKgel Super H3000" (manufactured by Tosoh Corporation) were used, and THF was passed as a carrier solvent (eluent) at a flow rate of 0.6 mL / min while maintaining the column temperature at 40°C. 100 μL of the prepared sample solution was injected into the GPC apparatus together with the carrier solvent, and the sample was detected using a differential refractive index detector (RI detector). Then, the molecular weight distribution of the sample was calculated using a calibration curve measured using 10 points of monodisperse polystyrene standard particles.

[0032] Here, the method of confirming the first polymer and the second polymer contained in the ink is, for example, as shown in Fig. 1, the first highest point (peak top) of a mountain-shaped curve that rises from the baseline through inflection point a, reaches the first highest point, and then declines is taken as HMw1 of the first polymer. Then, the second highest point of the mountain-shaped curve that declines from the first highest point, declines further through inflection point b, reaches the lowest point, then rises through a valley shape, further rises through inflection point c, reaches the second highest point, and then declines is calculated as LMw2 of the second polymer. The curve descends from the second highest point, passes through an inflection point d, and then converges to the baseline. In the present invention, the inflection point refers to a point where the curve switches from a valley to a peak (from a downward convex to an upward convex) or from a peak to a valley (from an upward convex to a downward convex). In addition, the amount of the second polymer particles at which the second highest point can be confirmed is preferably 1 part by mass or more per 100 parts by mass of the first polymer particles. Furthermore, in data analysis, when a peak due to the filter is confirmed, the baseline is set up to the peak, and the analyzed data is regarded as the molecular weight of the sample.

[0033] Measurement model: Tosoh Corporation GPC device HLC-8220GPC Column: Tosoh Corporation "TSKgelSuperH3000" Eluent:THF Temperature: Column thermostat 40.0℃ Flow rate: 0.6ml / min Concentration: 0.1mg / mL (0.1wt / vol%) Calibration curve: Standard polystyrene sample manufactured by Tosoh Corporation Injection volume: 100μL Solubility: Completely dissolved (heated at 40℃) Pretreatment: Filtration through a 0.45μm filter Detector: Differential refractometer (RI)

[0034] [Textile printing ink composition] The textile printing ink of the present invention contains first polymer particles, second polymer particles, and at least one of the above-mentioned binding assistants, and may further contain a pigment and a solvent.

[0035] <First polymer particles and second polymer particles> The first polymer particles and the second polymer particles (hereinafter, these are also collectively referred to as "polymer particles") are not particularly limited as long as they satisfy the above-mentioned weight average molecular weight ratio value, but it is preferable for the glass transition temperature (Tg) to be -35°C or lower in terms of binding between the pigment and the fiber, and more preferably within the range of -35 to 50°C.

[0036] The Tg of each polymer particle can be measured by the following method. First, the polymer particles separated from the synthesized polymer particle dispersion or ink are dried to prepare a sample. This sample is measured by differential scanning calorimetry in accordance with JIS K7121 at a temperature rise rate of 10°C / min to determine the glass transition temperature. The Tg of the polymer particles can be adjusted by the composition and degree of crosslinking of the polymers constituting the polymer particles.

[0037] Moreover, from the viewpoint of reproducing the color of the pigment particles to a high degree, the polymer particles are preferably colorless. Specifically, the colorless polymer particles refer to polymer particles that do not have a UV absorption peak at a wavelength of 400 to 700 nm in an absorption spectrum obtained by UV-Vis spectrometry.

[0038] Furthermore, the polymer particles preferably have light-transmitting properties, and more preferably are transparent, that is, the polymer particles are particularly preferably colorless and transparent.

[0039] Such polymer particles are not particularly limited as long as they satisfy at least the above-mentioned ratio of weight average molecular weights, but preferably contain, for example, one or more polymers selected from the group consisting of (meth)acrylic polymers, polystyrene polymers, acrylonitrile polymers, polyester polymers, and epoxy polymers. Among them, from the viewpoint of Tg being −35° C. or less and texture being less likely to be impaired, the polymer particles preferably contain a polymer selected from the group consisting of (meth)acrylic polymers and polystyrene polymers.

[0040] ((Meth)acrylic polymer) The (meth)acrylic polymer (also referred to as "(meth)acrylic resin") may be a homopolymer of at least one of a (meth)acrylic acid ester and (meth)acrylonitrile, or a copolymer of the homopolymer and another copolymerizable monomer.

[0041] The (meth)acrylic acid ester is a monofunctional (meth)acrylic acid ester, examples of which include methyl (meth)acrylate, ethyl (meth)acrylate, propyl (meth)acrylate, n-butyl (meth)acrylate, isopropyl (meth)acrylate, isobutyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, n-hexyl (meth)acrylate, etc., and is preferably methyl methacrylate. The (meth)acrylonitrile is acrylotyl or methacryloylnitrile.

[0042] The total content of the structural units derived from a (meth)acrylic acid ester and the structural units derived from a (meth)acrylonitrile can be 50% by mass or more, and preferably 60% by mass or more, based on all the structural units constituting the polymer.

[0043] The other copolymerizable monomer may be another monofunctional vinyl monomer or a polyfunctional vinyl monomer (crosslinkable vinyl monomer).

[0044] Examples of other monofunctional vinyl monomers include ethylenically unsaturated carboxylic acids (e.g., (meth)acrylic acid, maleic acid, itaconic acid, etc.), functional group-containing (meth)acrylates (e.g., quaternary ammonium group-containing (meth)acrylates such as trimethylammonium ethyl (meth)acrylate, 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, glycidyl (meth)acrylate, etc.), acrylamides (e.g., acrylamide, diacetone acrylamide), styrenes (e.g., styrene, α-methylstyrene, vinyl toluene, etc.), and saturated fatty acid vinyls (e.g., vinyl acetate, vinyl propionate, etc.). The content of structural units derived from other monofunctional vinyl monomers may be 50% by mass or less based on the total structural units constituting the polymer.

[0045] Examples of polyfunctional vinyl monomers include vinyl compounds (e.g., 1,4-divinyloxybutane, divinylbenzene, etc.), allyl compounds (e.g., diallyl phthalate, triallyl cyanurate, etc.), and polyfunctional (meth)acrylates (e.g., ethylene glycol di(meth)acrylate, diethylene glycol di(meth)acrylate, propylene glycol di(meth)acrylate, triethylene glycol di(meth)acrylate, trimethylolpropane tri(meth)acrylate, pentaerythritol tetra(meth)acrylate, etc.). The content of the structural units derived from polyfunctional vinyl monomers can be 20% by mass or less, preferably within the range of 0.5 to 10% by mass, based on the total structural units constituting the polymer.

[0046] In order to make it more difficult for the polymer particles to fuse to each other, the acrylic polymer may be crosslinked (that is, it may be a crosslinked acrylic polymer). The crosslinked acrylic polymer is a copolymer of a monofunctional vinyl monomer containing at least one of a (meth)acrylic acid ester and (meth)acrylonitrile, and a monofunctional vinyl monomer, because such a crosslinked (meth)acrylic polymer is less likely to fuse and form a film when the ink dries. In the case of the crosslinked acrylic polymer, the monofunctional vinyl monomer is preferably, for example, butyl acrylate (butyl acrylate) or methyl methacrylate, and the monofunctional vinyl monomer is preferably, for example, diacetone acrylamide. In this case, diacetone acrylamide functions as the binding assistant (crosslinkable monomer) according to the present invention.

[0047] (Polystyrene-based polymer) Polystyrene-based polymers (also referred to as "polystyrene-based resins") can be homopolymers of styrenes or copolymers of styrenes with other copolymerizable monomers.

[0048] The styrenes may be the same as those described above. The structural units derived from styrenes may be 50% by mass or more, preferably 60% by mass or more, based on the total structural units constituting the polymer. The other copolymerization monomers may be the same as those described above.

[0049] The polystyrene-based polymer may be a cross-linked polystyrene-based polymer, which is a copolymer of a monofunctional vinyl-based monomer containing styrenes and a polyfunctional vinyl-based monomer.

[0050] Among these, the polymer particles are preferably particles containing a copolymer of butyl acrylate (BA), methyl methacrylate (MMA), and diacetone acrylamide (DAAM).

[0051] (Physical properties of polymer particles) The acid value of the polymer constituting the polymer particles is not particularly limited as long as it can be well dispersed in an aqueous medium, but is, for example, 20 to 140 mgKOH / g, preferably 30 to 70 mgKOH / g. The acid value can be measured in accordance with JIS K 0070 or ISO 3961. Specifically, it can be measured as the number of mg of potassium hydroxide (KOH) required to neutralize 1 g of a sample.

[0052] The average particle diameter d2 of the first polymer particles and the second polymer particles is not particularly limited, but from the viewpoint of preventing the pigment particles from gathering in the gaps between the fibers of the fabric, it is preferable that the average particle diameter d2 is not too small compared to the average particle diameter d1 of the pigment particles. Specifically, the ratio d2 / d1 of the average particle diameter d1 of the pigment to the average particle diameter d2 of the polymer particles is preferably 0.5 to 3, and more preferably 1.1 to 2.5.

[0053] The average particle size d1 of the pigment means the average particle size of the pigment dispersed in the ink, specifically, when the ink contains a pigment dispersant, the average dispersed particle size (Z average) of the pigment particles to which the pigment dispersant is adsorbed. The average particle size d1 of the pigment may be within a range that does not impair the ejection properties by the inkjet method, and is not particularly limited, but is preferably 50 to 350 nm, and more preferably 70 to 250 nm. The dispersed particle size of the pigment can be measured by a particle size distribution measuring device using dynamic scattering. The average particle size d1 of the pigment can be adjusted mainly by the size of the pigment particles themselves, but can also be adjusted by the molecular weight and content of the pigment dispersant, the dispersion treatment conditions of the pigment particles, and the like.

[0054] The average particle size d2 of the polymer particles is preferably within a range of 30 to 250 nm, and more preferably within a range of 60 to 180 nm. The average particle size 2 of the polymer particles can be measured by a particle size distribution measuring device using dynamic scattering, in the same manner as the average particle size d1 of the pigment.

[0055] The content ratio of the first polymer particles and the second polymer particles is preferably within a range of 1 to 100 parts by mass, and more preferably within a range of 10 to 70 parts by mass, of the second polymer particles per 100 parts by mass of the first polymer particles.

[0056] The ratio M2 / M1 of the content of the polymer particles (the total content of the first polymer particles and the second polymer particles) M2 in the ink to the content of the pigment M1 is preferably 3 to 19 (mass ratio). When M2 / M1 is 3 (mass ratio) or more, the ratio of pigment particles gathering in the gaps between the fibers of the fabric when the ink is applied to the fabric can be reduced. Therefore, it is easy to distribute the pigment particles uniformly on the surface of the fibers, and sufficient image density is easily obtained. On the other hand, when M2 / M1 is 19 (mass ratio) or less, the ratio of the pigment particles in the ink is not too small, so not only is the image density unlikely to decrease, but the ratio of the polymer particles is not too large, so the texture is unlikely to be impaired. From the same viewpoint, the ratio M2 / M1 is more preferably 5 to 17 (mass ratio), and even more preferably 8 to 14 (mass ratio).

[0057] Specifically, the polymer particle content (total content of the first polymer particles and the second polymer particles) M2 is preferably within the range of 0.1 to 30% by mass, and more preferably within the range of 1 to 10% by mass, relative to the ink.

[0058] <Binding aid> The "bonding aid" according to the present invention refers to a crosslinking monomer contained in each of the first and second polymer particles as an aid for connecting the first and second polymer particles, and a crosslinking agent that is present in the ink outside the polymer particles and has a functional group capable of reacting with the crosslinking monomer to form a crosslinked bond. Note that reactive species having a catalytic action that promotes the crosslinking bond forming reaction are also included in the bonding aid according to the present invention.

[0059] As described above, the state of the binding aid according to the present invention is as follows: At least three forms are preferred: (i) the binding aid is completely contained within the first polymer particle or the second polymer particle, is not present on the surface of the polymer particle, and can be made to appear on the surface by external action; (ii) a portion of the structural component of the binding aid molecule is contained on the surface or inside of the first polymer particle or the second polymer particle, and the structural component having a crosslinkable group is made to appear on the surface of the particle; and (iii) the binding aid is contained in the ink outside the first polymer particle or the second polymer particle. Other examples of the bonding aid include reactive species having a catalytic action that accelerates the reaction of the crosslinkable polymer or the crosslinking agent.

[0060] Of the three embodiments, any of them may be used as long as the first polymer particles and the second polymer particles can be bonded to each other. In the present invention, the embodiments (ii) and (iii) are preferred. Specifically, it is preferred that a bonding aid is contained in both polymer particles (embodiment (ii)), and that another bonding aid is contained in the ink, but not in the polymer particles (embodiment (iii)).

[0061] (Crosslinking Monomer) The binding aid contained in both polymer particles includes, for example, a crosslinking monomer. Here, the "crosslinkable monomer" according to the present invention refers to a monomer that is contained in a polymer particle and has a functional group capable of linking (crosslinking) with other polymer particles or a crosslinking agent at at least one site of the molecule, for example, at the terminal end. The phrase "a crosslinkable monomer is contained in the polymer particles" refers to the above-mentioned states (i) and (ii) of the crosslinkable monomer added as a binding aid, and includes a state in which at least one site of the crosslinkable monomer is bonded to the polymer constituting the polymer particles. In other words, it includes a state in which the polymer and the crosslinkable monomer are contained by forming a bond. Such a crosslinkable monomer may be a compound having at least a functional group capable of reacting with the crosslinkable group of the crosslinking agent described below. For example, a compound having a double bond and a C=O group at the molecular end is preferable, and as described above, examples of the crosslinkable monomer include acrylamides and carboxylic acid groups.

[0062] Examples of the acrylamides include methylacrylamide, ethylacrylamide, propylacrylamide, butylacrylamide, t-butylacrylamide, t-octylacrylamide, cyclohexylacrylamide, benzylacrylamide, hydroxymethylacrylamide, methoxymethylacrylamide, butoxymethylacrylamide, methoxyethylacrylamide, phenylacrylamide, dimethylacrylamide, diethylacrylamide, β-cyanoethylacrylamide, N-(2-acetoacetoxyethyl)acrylamide, N,N'-methylenebis(acrylamide), diacetoneacrylamide, etc. Among them, N,N'-methylenebis(acrylamide) and diacetoneacrylamide (DAAM) are preferred.

[0063] Examples of the carboxylic acid group include 1,4-butanediol diacrylate, N,N'-methylenebisacrylamide, and the like.

[0064] [ka]

[0065] The crosslinkable monomer-derived structural portion contained in both polymer particles is preferably contained in an amount of 0.1 to 30 mass % relative to both polymer particles (the first polymer and the second polymer particles as a whole), and more preferably in the range of 1 to 10 mass %. The "structural portion derived from the crosslinkable monomer contained in both of the polymer particles" refers to the molecular structure portion of the crosslinkable monomer that includes a molecular structure portion other than the group or atom that dissociates upon reaction with the polymer particle constituent components, and a molecular structure portion that includes a site where the bonding state of the crosslinkable group has changed due to addition polymerization (for example, a double bond has changed to a single bond). For example, it refers to a structural portion that includes both a portion of the molecular structure of a crosslinkable monomer where the hydrogen atom of the crosslinkable group is dissociated and bonded to a polymer component constituting a polymer particle, and a portion of the other portion of the crosslinkable monomer that maintains the original molecular structure. Note that the state in which the crosslinkable monomer is contained in the polymer particle while maintaining the original molecular structure together with the polymer component is also included in the structural portion derived from the crosslinkable monomer.

[0066] (Crosslinking agent) The "crosslinking agent" according to the present invention refers to a compound that is present in the ink outside the polymer particles and has at least two functional groups capable of reacting with the crosslinking monomer to form a crosslinking bond. As the crosslinking agent, a compound having a hydrazide group, an oxazoline group, an isocyanate group, an ethyleneimine group, an aziridine group, a carbodiimide group, or a silane coupling group, which can be reacted at room temperature or a low temperature, or a compound having a blocked isocyanate group, a hydrazide group, or a diacetoneacrylamide group, which can be reacted by heating or the action of a catalyst, etc., can be used.

[0067] That is, as the crosslinking agent, compounds having a crosslinkable group such as organic acid dihydrazide compounds, oxazoline compounds, isocyanate compounds, blocked isocyanate compounds, epoxy polymer compounds, ethylene urea compounds, ethyleneimine compounds, melamine compounds, diacetone acrylamide, carbodiimide, and silane coupling agents can be used. More specifically, the crosslinking agents described in JP-A-2020-2220, JP-A-2020-203965, JP-A-2011-256477, JP-A-2011-42912, etc. can be used as reference.

[0068] In the present invention, examples of crosslinking agents that are particularly suitable for use include adipic acid dihydrazide (ADH) and N,N'-methylenebisacrylamide.

[0069] [ka]

[0070] The ink preferably contains a binding aid in an amount of 0.1 to 3 mass % based on the ink.

[0071] <Pigments> The pigment used in the textile printing ink of the present invention is not particularly limited, but is preferably, for example, an organic pigment or an inorganic pigment having the following numbers described in the Color Index.

[0072] Examples of orange or yellow pigments include CI Pigment Orange 31, CI Pigment Orange 43, CI Pigment Yellow 12, CI Pigment Yellow 13, CI Pigment Yellow 14, CI Pigment Yellow 15, CI Pigment Yellow 17, CI Pigment Yellow 74, CI Pigment Yellow 83, CI Pigment Yellow 93, CI Pigment Yellow 94, CI Pigment Yellow 128, CI Pigment Yellow 138, CI Pigment Yellow 151, CI Pigment Yellow 154, CI Pigment Yellow 155, CI Pigment Yellow 180, CI Pigment Yellow 185, and CI Pigment Yellow 213.

[0073] Examples of red or magenta pigments include Pigment Red 3, 5, 19, 22, 31, 38, 43, 48:1, 48:2, 48:3, 48:4, 48:5, 49:1, 53:1, 57:1, 57:2, 58:4, 63:1, 81, 81:1, 81:2, 81:3, 81:4, 88, 104, 108, 112, 122, 123, 144, 146, 149, 166, 168, 169, 170, 177, 178, 179, 184, 185, 208, 216, 226, 257, Pigment Violet 3, 19, 23, 29, 30, 37, 50, 88, Pigment Orange 13, 16, 20, 36.

[0074] Examples of blue or cyan pigments include Pigment Blue 1, 15, 15:1, 15:2, 15:3, 15:4, 15:6, 16, 17-1, 22, 27, 28, 29, 36, 60.

[0075] Examples of green pigments include Pigment Green 7, 26, 36, and 50. Examples of yellow pigments include Pigment Yellow 1, 3, 12, 13, 14, 17, 34, 35, 37, 55, 74, 81, 83, 93, 94, 95, 97, 108, 109, 110, 137, 138, 139, 153, 154, 155, 157, 166, 167, 168, 180, 185, and 193.

[0076] Examples of black pigments include Pigment Black 7, 28, and 26.

[0077] Commercially available examples of pigments include: Chromofine Yellow 2080, 5900, 5930, AF-1300, 2700L, Chromofine Orange 3700L, 6730, Chromofine Scarlet 6750, Chromofine Magenta 6880, 6886, 6891N, 6790, 6887, Chromofine Violet RE, Chromofine Red 6820, 6830, Chromofine Blue HS-3, 5187, 5108, 5197, 5085N, SR-5020, 5026, 5050, 4920, 4927, 4937, 4824, 4933GN-EP, 4940, 4973, 5205, 5208, 5214, 5221, 5000P , Chrome Fine Green 2GN, 2GO, 2G-550D, 5310, 5370, 6830, Chrome Fine Black A-1103, Seika Fast Yellow 10GH, A-3, 2035, 2054, 2200, 2270, 2300, 2400(B), 2500, 2600, ZAY-260, 2700(B), 2770 , Seika Fast Red 8040, C405(F), CA120, LR-116, 1531B, 8060R, 1547, ZAW-262, 1537B, GY, 4R-4016, 3820, 3891, ZA-215, Seika Fast Carmine 6B1476T-7, 1483LT, 3840, 3870, Seika Fast Bordeaux 10B-430, Seika Light Rose R40, Seika Light Violet B800, 7805, Seika Fast Maroon 460N, Seika Fast Orange 900, 2900, Seika Light Blue C718, A612, Cyanine Blue 4933M, 4933GN-EP, 4940, 4973 (Dainichi Seika Chemicals); KET Yellow 401, 402, 403, 404, 405, 406, 416, 424, KET Orange 501, KET Red 301, 302, 303, 304, 305, 306, 307, 308, 309, 310, 336, 337, 338, 346, KET Blue 101, 102, 103, 104, 105, 106, 111, 118, 124, KET Green 201 (manufactured by Dainippon Ink & Chemicals);Colortex Yellow 301, 314, 315, 316, P-624, 314, U10GN, U3GN, UNN, UA-414, U263, Finecol Yellow T-13, T-05, Pigment Yellow1705, Colortex Orange 202, Colortex Red101, 103, 115, 116, D3B, P-625, 102, H-1024, 105C, UFN, UCN, UBN, U3BN, URN, UGN, UG276, U456, U457, 105C, USN, Colortex Maroon601, Colortex BrownB610N, Colortex Violet600, Pigment Red 122, Colortex Blue516, 517, 518, 519, A818, P-908, 510, Colortex Green 402, 403, Colortex Black 702, U905 (Sanyo Pigment); Lionol Yellow 1405G, Lionol Blue FG7330, FG7350, FG7400G, FG7405G, ES, ESP-S (Toyo Ink Co., Ltd.); Toner Magenta E02, Permanent Rubin F6B, Toner Yellow HG, Permanent Yellow GG-02, Hostapearm Blue B2G (Hoechst Industry); Novoperm P-HG, Hostaperm Pink E, Hostaperm Blue B2G (manufactured by Clariant); Carbon black #2600, #2400, #2350, #2200, #1000, #990, #980, #970, #960, #950, #850, MCF88, #750, #650, MA600, MA7, MA8, MA11, MA100, MA100R, MA77, #52, #50, #47, #45, #45L, #40, #33, #32, #30, #25, #20, #10, #5, #44, CF9 (manufactured by Mitsubishi Chemical).

[0078] From the viewpoint of improving dispersibility in the ink, the pigment is preferably further dispersed with a pigment dispersant, which will be described later.

[0079] The pigment may be a self-dispersing pigment. A self-dispersing pigment is a pigment particle whose surface is modified with a group having a hydrophilic group, and has pigment particles and hydrophilic groups bonded to the surface of the pigment particles.

[0080] Examples of hydrophilic groups include carboxy groups, sulfonic acid groups, and phosphorus-containing groups. Examples of phosphorus-containing groups include phosphoric acid groups, phosphonic acid groups, phosphinic acid groups, phosphite groups, and phosphate groups.

[0081] Commercially available examples of self-dispersing pigments include Cabot's Cab-0-Jet® 200K, 250C, 260M, and 270V (sulfonic acid group-containing self-dispersing pigments), Cab-0-Jet® 300K (carboxylic acid group-containing self-dispersing pigments), and Cab-0-Jet® 400K, 450C, 465M, 470V, and 480V (phosphate group-containing self-dispersing pigments).

[0082] The pigment content M1 is not particularly limited, but from the viewpoint of easily adjusting the viscosity of the ink within the above range and enabling the formation of a high-density image, it is preferably within the range of 0.3 to 10% by mass of the ink. If the pigment content M1 is 0.3% by mass or more, a large amount of polymer particles can be contained, so that the color of the obtained image tends to be vivid, and if it is 5% by mass or less, the viscosity of the ink does not become too high, so that the ejection stability is not easily impaired. From the same viewpoint, it is more preferable that the pigment content M1 is 0.5 to 3% by mass of the ink.

[0083] <Solvent> The solvent is not particularly limited, but preferably contains water and further contains a water-soluble organic solvent.

[0084] The water may be ion-exchanged water, distilled water, or pure water. The water content in the ink is preferably within a range of 20 to 60% by mass, and more preferably within a range of 30 to 50% by mass.

[0085] The water-soluble organic solvent is not particularly limited as long as it is compatible with water, but from the viewpoint of making it easier for the ink to penetrate into the interior of the fabric and making it difficult for the ejection stability in the inkjet method to be impaired, it is preferable that the ink does not easily thicken due to drying. Therefore, it is preferable that the ink contains a high-boiling point solvent having a boiling point of 200° C. or more.

[0086] The high-boiling solvent having a boiling point of 200° C. or higher may be any water-soluble organic solvent having a boiling point of 200° C. or higher, and is preferably a polyol or a polyalkylene oxide.

[0087] Examples of polyols having a boiling point of 200°C or higher include dihydric alcohols such as 1,3-butanediol (boiling point 208°C), 1,6-hexanediol (boiling point 223°C), and polypropylene glycol; and trihydric or higher alcohols such as glycerin (boiling point 290°C) and trimethylolpropane (boiling point 295°C).

[0088] Examples of polyalkylene oxides having a boiling point of 200° C. or higher include ethers of dihydric alcohols such as diethylene glycol monoethyl ether (boiling point 202° C.), triethylene glycol monomethyl ether (boiling point 245° C.), tetraethylene glycol monomethyl ether (boiling point 305° C.), tripropylene glycol monoethyl ether (boiling point 256° C.) and polypropylene glycol, and ethers of trihydric or higher alcohols such as glycerin (boiling point 290° C.) and hexanetriol.

[0089] The solvent may further include other solvents in addition to the high boiling point solvent. Examples of the other solvents include polyhydric alcohols having a boiling point of less than 200° C. (e.g., ethylene glycol, propylene glycol, hexanetriol, etc.); polyhydric alcohol ethers having a boiling point of less than 200° C. (e.g., ethylene glycol monomethyl ether, ethylene glycol monobutyl ether, diethylene glycol monomethyl ether, diethylene glycol dimethyl ether, propylene glycol monomethyl ether, propylene glycol monoethyl ether); monohydric alcohols (e.g., methanol, ethanol, propanol, pentanol, hexanol, cyclohexanol, benzyl alcohol); amines (e.g., ethanolamine, N-ethyldiethanolamine, morpholine, N-ethylmorpholine, ethylenediamine, diethylenediamine, triethylenetetramine); amides (e.g., formamide, N,N-dimethylformamide, N,N-dimethylacetamide); heterocycles (e.g., 2-pyrrolidone, N-methyl-2-pyrrolidone, N-cyclohexyl-2-pyrrolidone, 2-oxazolidone, 1,3-dimethyl-2-imidazolidine), sulfoxides (e.g., dimethyl sulfoxide); and sulfones (e.g., sulfolane).

[0090] <Other ingredients> The textile printing ink of the present invention may further contain other components as necessary. Examples of the other components may include a pigment dispersant, a surfactant, a preservative, an antifungal agent, a pH adjuster, etc.

[0091] (Pigment dispersant) The pigment dispersant is present in the ink so as to surround the surface of the pigment particle or is adsorbed to the surface of the pigment particle to form a pigment dispersion and disperse the pigment well. From the viewpoint of excellent pigment dispersibility, such a pigment dispersant is preferably a polymer dispersant.

[0092] Examples of the polymer dispersant include anionic dispersants and cationic dispersants.

[0093] The anionic dispersant may be a polymer dispersant having a hydrophilic group selected from the group consisting of a carboxylic acid group, a phosphorus-containing group, and a sulfonic acid group. Among these, a polymer dispersant having a carboxylic acid group is preferred.

[0094] Examples of polymeric dispersants having a carboxylic acid group include polycarboxylic acids or their salts. Examples of polycarboxylic acids include (co)polymers of monomers selected from acrylic acid or its derivatives, maleic acid or its derivatives, itaconic acid or its derivatives, and fumaric acid or its derivatives, and salts thereof. Examples of other monomers constituting the copolymer include styrene and vinylnaphthalene.

[0095] The anionic group equivalent of the anionic dispersant is not particularly limited as long as it can disperse the pigment particles sufficiently, but is preferably within the range of, for example, 1.1 to 3.8 meq / g. When the anionic group equivalent is within the above range, high pigment dispersibility is easily obtained without increasing the molecular weight of the anionic dispersant. The anionic group equivalent can be measured by the same method as the method for measuring the acid value.

[0096] Examples of the cationic group contained in the cationic dispersant include a secondary amino group (imino group), a tertiary amino group, a quaternary ammonium group, etc. The cationic dispersant is not particularly limited as long as it can form the above-mentioned pigment dispersion, and may be, for example, a cationic polymer (polymer or prepolymer).

[0097] Examples of cationic polymers include (co)polymers of ethylenically unsaturated monomers having a cationic group (a tertiary amino group or a quaternary ammonium group).

[0098] Examples of ethylenically unsaturated monomers having a tertiary amino group include dialkylaminoalkyl (meth)acrylates such as dimethyl or diethylaminoethyl (meth)acrylate, dimethyl or diethylaminopropyl (meth)acrylate, etc.; dialkylaminoalkyl (meth)acrylamides such as dimethyl or diethylaminoethyl (meth)acrylamide, dimethyl or diethylaminopropyl (meth)acrylamide, etc.; (meth)acrylamides such as acrylamide, etc.

[0099] Examples of ethylenically unsaturated monomers having a quaternary ammonium group include (meth)acryloyloxyalkyltrialkylammonium salts such as 2-(meth)acryloyloxyethyltrimethylammonium chloride and 3-(meth)acryloyloxy-2-hydroxypropyltrimethylammonium chloride; (meth)acrylamidoalkyltrialkylammonium salts such as acrylamide-2-(acryloyloxy)methyltrimethylammonium chloride, (3-(meth)acrylamidopropyltrimethylammonium chloride and 3-(meth)acryloylamino-2-hydroxypropyltrimethylammonium chloride; 2-(meth)acryloyloxyethylbenzylammonium chloride and 2-(meth)acryloyloxyethyldimethylbenzylammonium chloride, and other 2-(meth)acryloyloxyalkylbenzylammonium salts; and dialkyldiallylammonium salts such as dimethyldiallylammonium chloride.

[0100] The ethylenically unsaturated monomer having a cationic group may be one type or two or more types. For example, an ethylenically unsaturated monomer having a tertiary amino group and an ethylenically unsaturated monomer having a quaternary ammonium group may be copolymerized.

[0101] These ethylenically unsaturated monomers having a cationic group may also be copolymerized with other monomers, examples of which include (meth)acrylic acid and its esters, allyl ethers, vinyl ethers, aromatic vinyl monomers, vinyl ester monomers, olefin monomers, and diene monomers.

[0102] Examples of such cationic polymers include dimethylaminoethyl methacrylate polymer, methacrylic acid-2-dimethylaminoethyl methacrylate copolymer, butyl acrylate-dimethylaminoethyl methacrylate copolymer, acrylamide-2-(acryloyloxy)methyltrimethylammonium chloride polymer, dimethyldiallylammonium chloride-acrylamide copolymer, and the like.

[0103] The cationic group equivalent of the cationic dispersant is not particularly limited as long as it can disperse the pigment particles sufficiently, but is preferably within the range of, for example, 1 to 5 meq / g. When the cationic group equivalent is within the above range, high pigment dispersibility is easily obtained without increasing the molecular weight of the cationic dispersant. The cationic group equivalent can be measured by the same method as the method for measuring the amine value.

[0104] Among these, from the viewpoints of eliminating the need for cationic pretreatment, which is prone to causing stains, and making it easier to maintain color reproducibility for a longer period of time, it is preferable that the pigment dispersant contained in the pigment ink is a cationic dispersant.

[0105] The weight average molecular weight of the polymer dispersant is not particularly limited, but is preferably 5000 to 30000. When the weight average molecular weight of the polymer dispersant is 5000 or more, the pigment particles can be dispersed sufficiently, and when it is 30000 or less, the ink does not thicken too much, so that the permeability into the fabric is not easily impaired. The weight average molecular weight of the polymer dispersant can be measured in styrene equivalent terms by gel permeation chromatography.

[0106] The content of the polymer dispersant is not particularly limited as long as it is within a range in which the pigment particles can be sufficiently dispersed and the viscosity is sufficient not to impair the permeability into the fabric, but is preferably within a range of 20 to 100% by mass, and more preferably within a range of 25 to 60% by mass, relative to the pigment.

[0107] (Surfactant) The textile printing ink of the present invention may further contain a surfactant, if necessary.

[0108] The surfactant can reduce the surface tension of the ink and increase the wettability of the ink to the fabric. The type of the surfactant is not particularly limited, and can be, for example, an acetylene glycol surfactant, a silicone surfactant, or a fluorine surfactant.

[0109] (Preservatives, antifungal agents) Examples of preservatives or antifungal agents include aromatic halogen compounds (eg, Preventol CMK), methylene dithiocyanate, halogen-containing nitrogen-sulfur compounds, 1,2-benzisothiazolin-3-one (eg, PROXEL GXL), and the like.

[0110] (pH adjuster) Examples of pH adjusters include citric acid, sodium citrate, hydrochloric acid, sodium hydroxide, and the like.

[0111] <Ink properties> The viscosity of the textile printing ink of the present invention at 25° C. is not particularly limited as long as it provides good ejection properties in an inkjet system, but is preferably within the range of 3 to 20 mPa s, and more preferably within the range of 4 to 12 mPa s. The viscosity of the ink can be measured at 25° C. using an E-type viscometer.

[0112] [Ink preparation] The textile printing ink of the present invention can be produced by any method. For example, the textile printing ink of the present invention can be produced by 1) mixing a pigment, a pigment dispersant, and a solvent (such as water) to obtain a pigment dispersion, and 2) further mixing the obtained pigment dispersion, a dispersion containing first polymer particles, a dispersion containing second polymer particles, a binding aid (such as a crosslinking agent contained in the ink), and any other components (such as a surfactant, a high boiling point solvent, etc.). This makes it easy to obtain an ink in which the pigment is well dispersed.

[0113] In addition, the dispersion liquid containing the first polymer particles and the dispersion liquid containing the second polymer particles are prepared, for example, by heating an activator solution in which an anionic activator and sodium carbonate are dissolved in ion-exchanged water, and mixing the monomers of the polymers constituting each polymer particle, a crosslinkable monomer, and a water-soluble chain agent to prepare a monomer solution. After that, a solution in which a polymerization initiator is dissolved in ion-exchanged water is heated, and the prepared monomer solution is mixed with this solution to prepare a dispersion liquid of the polymer particles.

[0114] [Image forming method] The image forming method (textile printing method) according to the present invention includes a step of applying droplets of the textile printing ink of the present invention onto a fabric by an inkjet system. Specifically, the image forming method includes 1) a step of ejecting ink from an inkjet recording head and applying ink droplets onto a fabric (ink application step), and 2) a step of drying and fixing the ink applied to the fabric (drying and fixing step).

[0115] Regarding step 1 (ink application process) Ink is ejected from an inkjet recording head to deposit ink droplets onto the fabric.

[0116] The type of fiber material constituting the fabric is not particularly limited, and preferably includes natural fibers such as cotton (cellulose fiber), hemp, wool, and silk; and chemical fibers such as rayon, vinylon, nylon, acrylic, polyurethane, polyester, and acetate. The fabric may be any form of woven fabric, nonwoven fabric, knitted fabric, etc., made from these fibers. The fabric may also be a blended woven fabric or blended nonwoven fabric of two or more types of fibers.

[0117] For example, when the ink contains an anionic dispersant, from the viewpoint of increasing the pigment adsorption speed and fixability, the fabric preferably has cationic groups or acid groups at least on its surface. The fabric having cationic groups or acid groups at least on its surface may or may not be pretreated.

[0118] In addition, when the ink contains a cationic dispersant, from the viewpoint of increasing the adsorption speed and fixability of the pigment, it is preferable that the fabric has an anionic group at least on the surface. That is, a fabric containing a fiber having an anionic group (e.g., cotton or a polyester having an anionic group) has an anionic group as it is, and therefore does not necessarily have to be provided with an anionic group by pretreatment. On the other hand, a fabric not containing a fiber having an anionic group does not have an anionic group as it is, and therefore it is preferable that an anionic group is provided by pretreatment.

[0119] In the present invention, when the ink is applied, the polymer particles contained in the ink gather to a certain extent in the gaps between the fibers, so that the pigment particles are less likely to gather excessively in the gaps between the fibers and are more likely to be distributed uniformly on the surface of the fibers.

[0120] Regarding step 2 (drying and fixing process) In the drying step, the ink applied to the fabric is dried to remove the solvent component in the ink, thereby fixing the pigment to the fabric.

[0121] The drying method is not particularly limited and may be a method using a heater, a hot air dryer, a heated roller, etc. Among them, it is preferable to dry the fabric by heating both sides thereof using a hot air dryer and a heater.

[0122] The drying temperature and drying time are preferably set to a level that allows the solvent component in the ink to evaporate while preventing the polymer particles from forming a film. Specifically, the drying temperature is preferably (Tg+50)°C (Tg means the Tg of the polymer particles) or lower. The drying temperature may be room temperature. The drying time depends on the drying temperature, but may be, for example, about 0.5 to 30 minutes.

[0123] In the present invention, since the Tg of the polymer particles applied to the fabric is appropriately high, the polymer particles are unlikely to fuse together excessively when the ink dries, and are unlikely to form a film. Therefore, the gaps between the fibers are not bonded, and the image-formed product (also called "printed fabric" or "printed product") is unlikely to become hard.

[0124] Furthermore, the image forming method according to the present invention may further include 3) a step of pretreating the fabric (pretreatment step), if necessary.

[0125] Regarding step 3 (pre-treatment step) In the pretreatment step, a pretreatment agent is applied to the fabric.

[0126] The type of pretreatment agent is not particularly limited and can be selected according to the composition of the ink. For example, when the ink contains an anionic dispersant, the pretreatment agent is preferably a pretreatment agent containing a compound having an acid group or a cationic group. When the ink contains a cationic dispersant, the pretreatment agent is preferably an anionic pretreatment agent containing a compound having an anionic group.

[0127] The compound having an anionic group is not particularly limited, and may be the same as an anionic surfactant, or may be a polymer compound having an anionic group, etc. Examples of the polymer compound having an anionic group include plant skins such as pectinic acid, cellulose derivatives such as carboxymethyl cellulose, processed starches such as carboxymethyl starch and carboxyethyl starch, and synthetic glues such as acrylic polymers having acrylic acid as a copolymerization component, such as acrylic acid-acrylic acid ester copolymers and styrene-acrylic acid copolymers.

[0128] The pretreatment agent may further contain, as necessary, a pH adjuster, a preservative, etc. As the preservative, the same preservatives as those exemplified for the inkjet textile printing ink can be used.

[0129] The method for applying the pretreatment agent to the fabric is not particularly limited, and may be, for example, a pad method, a coating method, a spray method, an inkjet method, or the like.

[0130] The pretreatment agent applied to the fabric can also be heated and dried using hot air, a hot plate, or a heat roller.

[0131] In order to facilitate obtaining a uniform image, natural impurities (such as fats and oils, waxes, pectins, and natural pigments) attached to the fabric fibers, residues of chemicals used in the fabric manufacturing process (such as glues), and dirt attached to the fabric may be washed away before the pretreatment agent is applied to the fabric.

[0132] The resulting image-formed product includes a fabric and an image layer disposed on the surface thereof. The image layer includes a dried product of an ink containing pigment particles and polymer particles. In the dried product of the ink, most of the polymer particles are not coated, at least a part of the polymer particles retain their particle shape, and the fibers of the fabric are not bonded together. As a result, the image-formed product is less likely to become hard, and the texture of the fabric can be well maintained. EXAMPLES

[0133] The present invention will be specifically described below with reference to examples, but the present invention is not limited thereto. In the following examples, unless otherwise specified, the operations were performed at room temperature (25°C). Furthermore, unless otherwise specified, "%" and "parts" mean "% by mass" and "parts by mass", respectively.

[0134] 1. Ink materials (1) Preparation of polymer particle dispersion (Preparation of polymer particle dispersion A) A surfactant solution prepared by dissolving 1.68 g of anionic surfactant (sodium dodecylbenzenesulfonate: SDS) and 0.34 g of sodium carbonate in 554 g of ion-exchanged water was added to a separable flask equipped with a stirrer, a temperature sensor, a cooling tube, and a nitrogen introducing device, and the internal temperature was raised to 80°C while stirring at a stirring speed of 330 rpm under a nitrogen stream. Meanwhile, a monomer solution was prepared by dissolving 99.75 g (71.25 parts by mass) of n-butyl acrylate (BA), 33.25 g (23.75 parts by mass) of methyl methacrylate (MMA), 7.0 g (5 parts by mass) of diacetone acrylamide (DAAM) as a crosslinkable monomer, and 0.07 g (0.0005 parts by mass) of 1-octanethiol (NOM) as a water-soluble chain transfer agent. Next, a solution of 0.14 g (0.001 parts by mass) of a polymerization initiator (potassium persulfate: KPS) dissolved in 2.66 g of ion-exchanged water was added and heated to 80°C, and the adjusted monomer solution was added dropwise over 60 minutes and stirred to produce polymer microparticles. After the dropwise addition was completed, the mixture was heated and stirred for 60 minutes, after which a solution of 0.14 g of a polymerization initiator (potassium persulfate: KPS) dissolved in 2.66 g of ion-exchanged water was added and stirred for 60 minutes, and then cooled to 40°C to obtain a dispersion of polymer microparticles (polymer particle dispersion A). The parts by mass of KPS listed in Table I indicate the parts by mass of KPS added the first time.

[0135] (Preparation of polymer particle dispersions B to H) Polymer particle dispersions B to H were obtained in the same manner as in the preparation of polymer particle dispersion A, except that n-butyl acrylate (BA), methyl methacrylate (MMA), diacetone acrylamide (DAAM), potassium persulfate (KPS) and 1-octanethiol (NOM) added in the first addition were mixed in the amounts of parts by mass shown in Table I below.

[0136] (Preparation of polymer particle dispersion I) A dispersion of polyurethane resin particles, Superflex 840 (manufactured by Daiichi Kogyo Co., Ltd.), was used, and this was designated as polymer particle dispersion I.

[0137] (Measurement of weight average molecular weight of polymer particles) The weight average molecular weight of the polymer particles in each of the polymer particle dispersions prepared above was measured. Specifically, the synthesized polymer particle dispersion was dried and dissolved in tetrahydrofuran (THF) to make a 1% solution. The 1% THF solution was then passed through a membrane filter with a pore size of 0.45 μm to prepare a sample solution. Then, using the following GPC device and column, THF was run as a carrier solvent (eluent) at a flow rate of 0.6 mL / min while maintaining the column temperature at 40° C. 100 μL of the prepared sample solution was injected into the GPC device together with the carrier solvent, and the sample was detected using a differential refractive index detector (RI detector). Then, the molecular weight distribution of the sample was calculated using a calibration curve measured using 10 points of monodisperse polystyrene standard particles. Measurement model: Tosoh Corporation GPC device HLC-8220GPC Column: Tosoh Corporation "TSKgelSuperH3000" Eluent:THF Temperature: Column thermostat 40.0℃ Flow rate: 0.6ml / min Concentration: 0.1mg / mL (0.1wt / vol%) Calibration curve: Standard polystyrene sample manufactured by Tosoh Corporation Injection volume: 100μL Solubility: Completely dissolved (heated at 40℃) Pretreatment: Filtration through a 0.45μm filter Detector: Differential refractometer (RI)

[0138] (Measurement of Glass Transition Temperature of Polymer Particles) The glass transition temperature (Tg) of the polymer particles in each of the polymer particle dispersions prepared above was measured. Specifically, the sample obtained by drying the synthesized polymer particle dispersion was measured using a Hitachi High-Tech Science DSC7000X. The measurement was performed at a temperature rise rate of 10°C / min to determine the glass transition temperature.

[0139] (Measurement of average particle size d2 of polymer particles) The dispersed particle size (Z average) of the polymer particles in each of the polymer particle dispersions prepared above was measured by a Zataizer NanoS90 manufactured by Melvern, and was taken as the average particle size d2.

[0140] [Table 1]

[0141] (2) Preparation of anionic pigment dispersion As a pigment dispersant, 7 parts by mass of styrene-butyl acrylate-methacrylic acid copolymer (anionic dispersant, weight average molecular weight 16000, anionic group equivalent weight 3.5meq / g) was mixed with 78 parts by mass of water, and then heated and stirred to prepare a neutralized pigment dispersant. 15 parts by mass of CI Pigment Blue 15:3 was added to this mixture, premixed, and then dispersed using a sand grinder filled with 50% by volume of 0.5mm zirconia beads to obtain a cyan pigment dispersion with a pigment concentration of 15% by mass.

[0142] (3) Other ingredients Olfin E-1010 (manufactured by Nissin Chemical Co., Ltd., acetylene glycol surfactant) Proxel GXL (manufactured by Lonza Japan, preservative) Ethylene glycol Propylene glycol Glycerin Ion-exchanged water Adipic dihydrazide (ADH)

[0143] 2. Ink Preparation (Preparation of Ink 1) Next, the following components were mixed to a total of 100 parts by mass to obtain ink 1. Anionic pigment dispersion (pigment concentration 15% by mass): 10 parts by mass (solid concentration 1.5 parts by mass) Polymer particle dispersion A (solid content concentration 30% by mass): 24 parts by mass (solid content concentration 7.2 parts by mass) Polymer particle dispersion F (solid content concentration 30% by mass): 6 parts by mass (solid content concentration 1.8 parts by mass) Adipic acid dihydrazide (ADH): 0.7 parts by mass Ethylene glycol: 30 parts by weight Propylene glycol: 10 parts by weight Glycerin: 10 parts by weight Olfin E1010 (acetylene glycol surfactant manufactured by Nissin Chemical Industry): 0.5 parts by mass Proxel GXL (manufactured by Lonza Japan): 0.5 parts by weight Ion exchange water: remainder (8.3 parts by mass)

[0144] The dispersed particle size of the polymer particles in the obtained ink was approximately the same as that of the polymer particles in the polymer particle dispersion liquid.

[0145] (Preparation of Inks 2 to 9) Inks 2 to 9 were obtained by mixing the components in the same manner as in the preparation of Ink 1, except that the type and content of the polymer particle dispersion was changed as shown in Table II below. The "content" shown in Table II is the mass ratio of each polymer particle dispersion.

[0146] 3. Evaluation (Image formation test) An image formation test was carried out using the obtained ink. First, an inkjet head (Konica Minolta head #204) was prepared as an image forming apparatus. Next, the inks shown in Table II were ejected from the nozzles of the inkjet head of the image forming apparatus to form an image on a cotton cloth as a fabric. Specifically, the image was formed in the following manner.

[0147] (Ink application process) The obtained ink was set in an image forming apparatus. A solid image was formed on the above-mentioned fabric using the obtained ink at 540 dpi in the main scanning direction and 720 dpi in the sub-scanning direction. Note that dpi refers to the number of ink droplets (dots) per 2.54 cm. The ejection frequency was 22.4 kHz.

[0148] (drying process) The fabric to which the ink was applied was dried at 120° C. for 5 minutes in a belt conveyor dryer.

[0149] (evaluation) When an image formation test was carried out using each ink, the color reproducibility, texture (hardness), stickiness and abrasion resistance of the resulting image-formed product were evaluated by the following methods.

[0150] (color reproducibility) The obtained image-formed product was visually evaluated for color reproducibility according to the following criteria. ◎: Excellent color density and vividness ○: The color density is slightly low or the color vividness is slightly inferior, but it is at a good level. △: The color density is a little thin or the color vividness is a little inferior, but there is no problem in practical use. ×: The color density is low or the color is dull, to a level that is problematic for practical use. If it was △ or higher, it was considered to be within the acceptable range.

[0151] (Texture) The obtained image-formed product was subjected to a sensory evaluation using a touch and was rated according to the following criteria. ◎: Soft and the boundary between the print surface and the fabric is difficult to distinguish. Good: Soft, but you can see the boundary between the print surface and the fabric. △: Not stiff, but the boundary between the print surface and the fabric is clearly visible. ×: Feels stiff and hard. If it was equal to or greater than ○, it was considered to be within the acceptable range.

[0152] (Sticky) The obtained image-formed product was subjected to a sensory evaluation using a touch and was rated according to the following criteria. ◎: No problem with touch 〇: It feels like it is being printed, but there are no problems △: When touched, it feels like there is a polymer. ×: Sticky to the touch. If it was △ or higher, it was considered to be within the acceptable range.

[0153] (Abrasion resistance and durability) Each image-formed product was left for one month under conditions of 25°C and 50% RH using a xenon lamp (Super Xenon Weather Meter SX75, Suga Test Instruments Co., Ltd.). After that, a Gakushin-type rub fastness tester (product name: AB-301, Tester Sangyo Co., Ltd.) was used to perform 100.0 round trips under conditions of a load of 200.0 g and a speed of 10.0 cm / s. After that, a JIS color fastness test white cloth (JIS L 0803:2011 compliant No. 3-1) was soaked in pure water to measure the dye transfer optical density value (hereinafter also referred to as the "dye transfer OD value"), and the rub fastness was evaluated according to the following evaluation criteria. The lower the dye transfer OD value, the better the wet rub fastness. ⊚: The dye transfer density OD value is 0.15 or less. ◯: The dye transfer concentration OD value is greater than 0.15 and less than 0.20. △: The dye transfer concentration OD value is more than 0.20 and 0.25 or less. ×: The OD value of the dye transfer concentration is more than 0.25. If it was △ or higher, it was considered to be within the acceptable range.

[0154] [Table 2]

[0155] As shown by the above results, it is evident that by using the ink of the present invention, stickiness can be prevented, the friction fastness is good, and the color reproducibility and texture can be improved. [Explanation of symbols]

[0156] HMw1 weight average molecular weight of the first polymer particles LMw2 Weight average molecular weight of the second polymer particles

Claims

1. A textile printing ink containing polymer particles, First polymer particles; second polymer particles having a weight average molecular weight different from that of the first polymer particles; A bonding aid for crosslinking polymer particles is contained on the surface, the inside or the outside of the first polymer particles and the second polymer particles, and The weight average molecular weights of the polymers contained in the first polymer particles and the second polymer particles are respectively represented by HMw １ and L.M.W. ２ When the weight average molecular weight ratio of each polymer is ２ / HMw １ ) is within the range of 0.01 to 0.

20.

2. 2. The textile printing ink according to claim 1, wherein the second polymer particles are contained in an amount within a range of 1 to 100 parts by mass with respect to 100 parts by mass of the first polymer particles.

3. 3. The textile printing ink according to claim 1, wherein the first polymer particles and the second polymer particles each have a glass transition temperature (Tg) of −35° C. or lower.

4. 4. The textile printing ink according to claim 1, wherein the binding assistant is a crosslinkable monomer contained in each of the first polymer particles and the second polymer particles, and a crosslinking agent contained in the textile printing ink.

5. the first polymer particles and the second polymer particles each contain a structural portion derived from a crosslinkable monomer, 5. The textile printing ink according to claim 1, wherein the first polymer particles and the second polymer particles as a whole contain a structural portion derived from the crosslinkable monomer in a range of 0.1 to 30 mass %.

6. 6. The textile printing ink according to claim 1, wherein the first polymer particles and the second polymer particles have an average particle size within a range of 30 to 250 nm.

7. 7. The textile printing ink according to claim 1, wherein the first polymer particles and the second polymer particles are contained in an amount within a range of 0.1 to 30 mass % relative to the textile printing ink.