Power storage device

Abstract

To provide a power storage device which can improve gas permeability of an outer package composed of a laminate film.SOLUTION: A power storage device includes an electrode body, and an outer package which stores the electrode body and is composed of a laminate film 21. The laminate film 21 has a barrier layer 32 as a metal layer, and a sealing layer 31 laminated on a surface opposite to the electrode body of the barrier layer 32. In the barrier layer 32, a through hole 34 penetrating through the barrier layer 32 in a thickness direction is formed. A diameter of the through hole 34 is 3 mm or more and 10 mm or less. The laminate film 21 further has a resin part 35 arranged in the through hole 34.SELECTED DRAWING: Figure 4

Description

[Technical field]

[0001] The present disclosure relates to an electricity storage device. [Background technology]

[0002] Japanese Patent Application Laid-Open No. 2017-10946 (Patent Document 1) discloses a lithium secondary battery including an electrode laminate and a battery case that houses the electrode laminate. The battery case is made of a laminate sheet in which a large number of pores are formed. Gas generated from the electrode laminate is discharged to the outside through the pores of the laminate sheet. [Prior art documents] [Patent documents]

[0003] [Patent Document 1] JP 2017-10946 A Summary of the Invention [Problem to be solved by the invention]

[0004] In the battery described in the above document, the internal pressure may increase due to gas generation inside the battery case. This increase in internal pressure is a factor that affects the life of the battery. In order to mitigate the increase in internal pressure, there is a demand for improving the permeability of the generated gas to the outside of the battery case.

[0005] The present disclosure proposes an electricity storage device that can improve the gas permeability of an exterior body made of a laminate film. [Means for solving the problem]

[0006] According to the present disclosure, there is proposed an energy storage device comprising an electrode body and an exterior body made of a laminate film that houses the electrode body, the laminate film having a metal layer and a resin layer laminated on the surface of the metal layer facing the electrode body, the metal layer having a through hole formed therein that penetrates the metal layer in the thickness direction, the through hole having a diameter of 3 mm or more and 10 mm or less, and the laminate film further having a resin portion disposed within the through hole.

[0007] By forming a through hole in the metal layer and setting the diameter of the through hole to 3 mm or more and 10 mm or less, the gas permeability of the exterior body can be improved. The resin part can prevent moisture from entering the interior of the exterior body through the through hole from the outside.

[0008] In the above-described electricity storage device, a part of the resin layer protruding into the through hole may serve as a resin part, which makes it possible to easily form the resin part and reliably seal the through hole.

[0009] In the above-described energy storage device, the resin portion may contain a resin material different from the material forming the resin layer, whereby appropriate resin materials that fulfill required functions can be selected as the material forming the resin layer and the material forming the resin portion.

[0010] In the above-described power storage device, the resin portion may include a resin material having a lower moisture permeability than the material forming the resin layer, thereby more reliably preventing moisture from passing through the through holes and entering the inside.

[0011] In the above-mentioned energy storage device, the area ratio of the through holes to the area of ​​the metal layer may be 3% or more and 40% or less. By making the area ratio of the through holes 3% or more, the gas permeation speed can be ensured, and the effect of improving the gas permeability of the exterior body can be reliably obtained. By making the area ratio of the through holes 40% or less, the mechanical strength of the laminate film can be ensured.

[0012] In the electricity storage device, it is preferable that the resin layer does not have any macroscopically visible holes, which can reliably prevent liquid inside the electricity storage device from leaking to the outside. Effect of the Invention

[0013] According to the electricity storage device of the present disclosure, the gas permeability of the exterior body can be improved. [Brief description of the drawings]

[0014] [Figure 1] 1 is a cross-sectional view showing a schematic configuration of a power storage device according to an embodiment. [Diagram 2] 2 is a plan view of the electricity storage device as viewed in the direction of arrow II shown in FIG. [Diagram 3] 2 is an enlarged cross-sectional view of an exterior body showing a region III shown in FIG. 1. [Figure 4] FIG. 11 is a cross-sectional view showing another example of an exterior body. [Diagram 5] 1 is a table showing evaluation results of examples and comparative examples. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0015] Hereinafter, an embodiment will be described with reference to the drawings. In the following description, the same components are denoted by the same reference numerals. Their names and functions are also the same. Therefore, detailed description thereof will not be repeated.

[0016] FIG. 1 is a cross-sectional view showing a schematic configuration of a power storage device 1 according to an embodiment. The power storage device 1 is, for example, a non-aqueous secondary battery such as a lithium ion battery. The power storage device 1 is mounted on a vehicle for use, for example. Examples of the vehicle include a hybrid vehicle, a plug-in hybrid vehicle, an electric vehicle, and a fuel cell vehicle. A battery pack in which a plurality of power storage devices 1 are arranged to form a single assembly is mounted on the vehicle.

[0017] As shown in FIG. 1, the energy storage device 1 includes an electrode body 10. The electrode body 10 includes a positive electrode 11, a negative electrode 12, and a separator 13. The positive electrode 11 may include a positive electrode collector and a positive electrode active material layer. The positive electrode collector may include aluminum foil. The negative electrode 12 may include a negative electrode collector and a negative electrode active material layer. The negative electrode collector may include copper foil. The separator 13 is disposed between the positive electrode 11 and the negative electrode 12. The separator 13 is formed of an insulating material such as a resin, and electrically insulates the positive electrode 11 and the negative electrode 12. The electrode body 10 is immersed in an electrolyte (not shown).

[0018] Fig. 2 is a plan view of the energy storage device 1 as viewed from the direction of arrow II shown in Fig. 1. The energy storage device 1 includes an exterior body 20. The exterior body 20 contains an electrode assembly 10 and an electrolyte solution therein. The exterior body 20 is made of a laminate film. The exterior body 20 includes a first laminate film 21 and a second laminate film 22. The exterior body 20 is formed by welding a peripheral portion of the first laminate film 21 and a peripheral portion of the second laminate film 22 to each other.

[0019] The positive electrode tab 25 protrudes to the outside from the exterior body 20. The positive electrode tab 25 is electrically connected to the positive electrode 11 of the electrode assembly 10. The negative electrode tab 26 protrudes to the outside from the exterior body 20. The negative electrode tab 26 is electrically connected to the negative electrode 12 of the electrode assembly 10.

[0020] Fig. 3 is an enlarged cross-sectional view of the exterior body 20 showing an area III shown in Fig. 1. Fig. 3 illustrates the first laminate film 21 to explain the configuration of the laminate film, but the second laminate film 22 also has the same configuration as the first laminate film 21. The laminate film constituting the exterior body 20 includes a sealing layer 31, a barrier layer 32, and a protective layer 33.

[0021] The sealing layer 31 is formed of a resin material. The sealing layer 31 may be formed of, for example, non-oriented polypropylene (CPP), polyethylene (PE), or the like. The sealing layer 31 constitutes the inner surface of the exterior body 20. The sealing layer 31 has an inner surface facing the electrode body 10 and an outer surface facing the outside of the electricity storage device 1. The sealing layer 31 corresponds to an example of a resin layer.

[0022] The barrier layer 32 is made of a metal material. The barrier layer 32 may be made of aluminum, for example. The barrier layer 32 is disposed on the outside of the sealing layer 31. The barrier layer 32 has an inner surface facing the electrode body 10 and an outer surface facing the outside of the energy storage device 1. The outer surface of the sealing layer 31 and the inner surface of the barrier layer 32 face each other. The sealing layer 31 is laminated on the inner surface of the barrier layer 32. The barrier layer 32 corresponds to an example of a metal layer.

[0023] The protective layer 33 is formed of a resin material. The protective layer 33 is formed of a material different from the resin material constituting the sealing layer 31. The protective layer 33 may be formed of, for example, polyethylene terephthalate (PET). The protective layer 33 constitutes the outer surface of the exterior body 20. The protective layer 33 has an inner surface facing the electrode body 10 and an outer surface facing the outside of the energy storage device 1. The outer surface of the barrier layer 32 and the inner surface of the protective layer 33 face each other. The protective layer 33 is laminated on the outer surface of the barrier layer 32.

[0024] An adhesive layer or an underlayer for improving adhesion may be provided between the sealing layer 31 and the barrier layer 32. An adhesive layer or an underlayer may also be provided between the barrier layer 32 and the protective layer 33.

[0025] A plurality of through holes 34 are formed in the barrier layer 32. The through holes 34 penetrate the barrier layer 32 in the thickness direction. The through holes 34 may be formed by machining the barrier layer 32 or may be formed chemically. The through holes 34 can be formed in the barrier layer 32 before the sealing layer 31 and the protective layer 33 are laminated on the barrier layer 32.

[0026] The through holes 34 are, for example, round holes, but the shape of the through holes 34 is not limited. The through holes 34 may be formed in any other shape than a circle. The multiple through holes 34 may be arranged in a lattice pattern as shown in Fig. 2, for example, but may also be arranged in a staggered pattern or in any other arrangement. The multiple through holes 34 may be arranged at equal intervals or at different intervals.

[0027] The diameter of each through hole 34 is 3 mm or more and 10 mm or less. The through holes 34 have a size that is visible to the naked eye. When the through holes 34 have a circular shape as shown in Fig. 2, the diameter of the through holes 34 is 3 mm or more and 10 mm or less. When the through holes 34 have a shape other than a circle, the maximum diameter dimension of the through holes 34 is 3 mm or more and 10 mm or less.

[0028] The area ratio of the through holes 34 to the area of ​​the barrier layer 32 is 3% or more and 40% or less. For example, in the range where the electrode body 10 and the exterior body 20 overlap when the power storage device 1 is viewed in plan as shown in Fig. 2, the area ratio of the through holes 34 to the barrier layer 32 may be 3% or more and 40% or less.

[0029] While through-holes 34 are formed in the barrier layer 32, no voids penetrating the sealing layer 31 are formed in the sealing layer 31. No voids penetrating the protective layer 33 are formed in the protective layer 33. Since the sealing layer 31 and the protective layer 33 are formed of a resin material, they may have porosity microscopically, but no pores visible macroscopically are formed in the sealing layer 31 and the protective layer 33.

[0030] A resin part 35 made of a resin material is disposed in the through hole 34. A part of the sealing layer 31 laminated on the barrier layer 32 protrudes into the through hole 34, and the part of the sealing layer 31 protruding into the through hole 34 constitutes the resin part 35. Therefore, the resin part 35 is formed of the same material as the sealing layer 31.

[0031] The resin portion 35 shown in FIG. 3 fills the entire through hole 34 and blocks the entire through hole 34. The resin portion 35 contacts the entire inner circumferential surface of the through hole 34. The tip surface of the resin portion 35 contacts the inner surface of the protective layer 33. The resin portion 35 does not necessarily have to contact the protective layer 33, and a gap may be formed between the resin portion 35 and the protective layer 33. The resin portion 35 may fill only a portion of the through hole 34. The resin portion 35 may be present in a portion of the through hole 34, and the other portion of the through hole 34 may be a hollow space.

[0032] The resin portion 35 may be formed of the same material as the protective layer 33. A part of the protective layer 33 may constitute the resin portion 35.

[0033] 4 is a cross-sectional view showing another example of exterior body 20. Resin portion 35 may be formed of a resin material different from the material forming either one or both of sealing layer 31 and protective layer 33. For example, the resin material forming resin portion 35 may have lower moisture permeability than the resin material forming sealing layer 31 and lower moisture permeability than the resin material forming protective layer 33. Resin portion 35 may be formed of, for example, PVdF (polyvinylidene fluoride), FEP (tetrafluoroethylene-hexafluoropropylene copolymer), or the like.

[0034] The resin material forming the sealing layer 31 or the protective layer 33 has necessary functions such as mechanical strength, chemical resistance, and processability, while having relatively high moisture permeability. When a part of the sealing layer 31 constitutes the resin part 35 shown in Fig. 3, the function of suppressing moisture penetration into the inside of the electricity storage device 1 may become insufficient.

[0035] On the other hand, resin materials with low moisture permeability such as PVdF and FEP are difficult to use as materials for forming the sealing layer 31 or the protective layer 33 from the viewpoints of mechanical strength, chemical resistance, processability, cost, etc. By using a resin material with low moisture permeability as the material filled in the through holes 34 formed in the barrier layer 32, the required functions of the sealing layer 31 and the protective layer 33 can be fulfilled and the intrusion of moisture into the inside of the electricity storage device 1 can be reliably suppressed.

[0036] 3 and 4, in the energy storage device 1 of the embodiment described above, the first laminate film 21 has a sealing layer 31 which is a resin layer and a barrier layer 32 which is a metal layer. The barrier layer 32 has a through hole 34 formed therein, which penetrates the barrier layer 32 in the thickness direction.

[0037] Gas may be generated inside the exterior body 20 due to decomposition of the electrolyte, etc. The generated gas is dissolved in the sealing layer 31 of the exterior body 20. The gas cannot permeate the barrier layer 32, which is a metal layer. The gas that moves through the sealing layer 31 and reaches the through-hole 34 passes through the barrier layer 32 via the through-hole 34 and is released to the outside. Compared to a conventional electricity storage device including a laminate film in which no through-holes are formed in the metal layer, in the electricity storage device 1 of the embodiment in which the through-holes 34 are formed in the barrier layer 32, the gas permeability of the exterior body 20 is improved.

[0038] A resin portion 35 is disposed in the through hole 34, and the through hole 34 is sealed by the resin portion 35. Even if the through hole 34 is formed penetrating the barrier layer 32, by sealing the through hole 34 with the resin portion 35, leakage of the electrolyte through the through hole 34 to the outside of the exterior body 20 is suppressed, and infiltration of moisture from the outside through the through hole 34 into the interior of the exterior body 20 is suppressed.

[0039] By making the diameter of the through hole 34 3 mm or more, gas that reaches the through hole 34 can be easily released to the outside, thereby improving the gas permeability of the exterior body 20. When the area ratio of the through hole 34 to the area of ​​the barrier layer 32 is constant, if the diameter of the through hole 34 is too large, the distance that the gas travels in the sealing layer 31 before reaching the through hole 34 becomes long, and the gas permeation rate decreases. By making the diameter of the through hole 34 10 mm or less, the distance that the gas travels in the sealing layer 31 can be shortened and the gas permeation rate can be ensured, thereby improving the gas permeability of the exterior body 20.

[0040] 3, a part of the sealing layer 31 protruding into the through hole 34 may constitute the resin part 35. When the sealing layer 31 is laminated and integrated with the barrier layer 32 during production of the laminate film, a part of the sealing layer 31 enters the through hole 34 to form the resin part 35. This makes it possible to easily form the resin part 35 and to reliably seal the through hole 34 with the resin part 35.

[0041] The protective layer 33 laminated on the outer surface of the barrier layer 32 is provided for the purpose of physically protecting the exterior body 20. The sealing layer 31 laminated on the inner surface of the barrier layer 32 serves to prevent leakage of the electrolyte to the outside. For this reason, it is preferable to adopt a configuration in which a part of the sealing layer 31 forms the resin part 35 as shown in FIG. 3, rather than a configuration in which a part of the protective layer 33 forms the resin part 35.

[0042] 4, the resin part 35 may contain a resin material of a different type from the material forming the sealing layer 31. In this way, the exterior body 20 can be formed by selecting appropriate resin materials that fulfill the required functions as the material forming the sealing layer 31 and the material forming the resin part 35.

[0043] 4, the resin part 35 may contain a resin material having a lower moisture permeability than the material forming the sealing layer 31. This can reliably prevent moisture from penetrating from the outside of the electricity storage device 1 through the through holes 34 and into the inside. Even a resin material that is usually difficult to use as a material for forming the sealing layer 31 or the protective layer 33 can be used as a material for forming the resin part 35.

[0044] 2, by setting the area ratio of the through holes 34 to the area of ​​the barrier layer 32 to be 3% or more, the gas permeation rate can be ensured, and the effect of improving the gas permeability of the exterior body 20 can be reliably obtained. As the area ratio of the through holes 34 to the area of ​​the barrier layer 32 increases, the mechanical strength of the laminate film decreases, and when the area ratio exceeds a predetermined value, the rate of increase in gas permeability becomes small. By setting the area ratio of the through holes 34 to the area of ​​the barrier layer 32 to be 40% or less, the mechanical strength of the laminate film can be ensured to enable it to function as the exterior body 20, and the effect of improving gas permeability can be appropriately obtained.

[0045] 3 and 4, no macroscopically visible holes are formed in the sealing layer 31. If holes are formed in the sealing layer 31, there is a possibility that the electrolyte may leak to the outside through the holes. By preventing holes from being formed in the sealing layer 31, it is possible to reliably prevent the electrolyte from leaking to the outside of the exterior body 20. EXAMPLES

[0046] The following is a description of the examples. First, a laminate film for evaluation was prepared. Commercially available aluminum foil was used as the base material. Through holes were formed in this base material so as to have a specified diameter and area ratio. A resin film made of CPP was welded to both sides of the part of the base material where the through holes were formed, to prepare a laminate film.

[0047] The laminate film in which different resin materials are filled into the through holes of the base material was created by forming the through holes in the same manner as described above, placing a resin material of the same diameter as the through hole in the through hole, and then welding a CPP resin film to both sides of the base material.

[0048] Next, simulated gas was created to simulate the gas components generated inside the exterior body 20 of the electricity storage device 1. Assuming that hydrogen, carbon monoxide, and methane were the main gas components, adjustments were made so that hydrogen was 4 vol%, carbon monoxide was 48 vol%, and methane was 48 vol%. Taking into account the combustion ratio, hydrogen gas was set to 4 vol% or less.

[0049] Next, in order to measure the gas permeation rate of the laminate film, a simulated cell filled with a simulated gas was created. The simulated cell was created by forming the laminate film into the shape of the exterior body of the electricity storage device in a glove box filled with the simulated gas. An internal pressure sensor was inserted inside the simulated cell to enable measurement of the internal pressure of the simulated cell.

[0050] The amount of gas components in the simulated cells was measured by gas chromatography immediately after the simulated gas was filled and after 120 days of storage. The change in the amount of gas components immediately after filling and after 120 days of storage was taken as the amount of permeated gas, and the gas permeation rate was calculated from the number of days that had passed.

[0051] Fig. 5 is a table showing the evaluation results of the examples and the comparative examples. Fig. 5 shows the results of investigating the relationship between the diameter of the through holes formed in the base material, the area ratio of the through holes to the area of ​​the base material, the internal structure of the through holes, and the gas permeation rate.

[0052] A base material without through holes was used as Comparative Example 1. In Comparative Examples 2-5, the diameter of the through holes formed in the base material was set to less than 3 mm. In Examples 1-9, the diameter of the through holes formed in the base material was set to a constant 3 mm, and the density of the through holes was changed to change the area ratio of the through holes. In Examples 10-14, the area ratio of the through holes was set to a constant 20%, and the diameter of the through holes was changed. In Examples 15-20, the inside of the through holes was filled with a resin material (FEP, PVdF) different from the CPP forming the resin film.

[0053] As shown in Examples 1-9, the gas permeation rate increased as the area ratio of the through holes increased. The gas permeation rate tended to increase proportionally when the area ratio of the through holes was in the range of up to 40%. When the area ratio of the through holes exceeded 40%, the increase rate of the gas permeation rate decreased, and the effect of increasing the area ratio became small. This is thought to be because when the area ratio of the through holes increases to a certain level or more, the partial pressure of the gas inside the simulated cell decreases. In addition, the mechanical strength of the laminate film decreases as the area ratio of the through holes increases. Considering the role of the laminate film as an exterior body for the power storage device, it is thought to be preferable to set the area ratio of the through holes to 40% or less.

[0054] In Example 1, when the area ratio of the through holes was 1%, the gas permeation rate was not sufficient. In order to sufficiently increase the gas permeation rate, it is preferable that the area ratio of the through holes be 3% or more. In Comparative Example 2-5, when the diameter of the through holes was less than 3 mm, the gas permeation rate was not sufficient. In order to sufficiently increase the gas permeation rate, it is preferable that the diameter of the through holes be 3 mm or more.

[0055] As shown in Examples 5 and 10-14, when the diameter of the through hole is changed, the gas permeation rate hardly changes when the diameter of the through hole is in the range of 10 mm or less, but when the diameter exceeds 10 mm, the gas permeation rate tends to gradually decrease. This is thought to be due to the increase in the average distance to the through hole in the laminate film by increasing the diameter while keeping the area ratio of the through hole constant. Since the gas permeation in the laminate film is carried out in the process of dissolving the gas in the resin on the inner periphery of the cell, diffusing, and releasing it to the outside, when the average distance to the through hole is long, the distance required for diffusion becomes long, and as a result, the gas permeation rate is thought to decrease. Therefore, it is thought that the diameter of the through hole is preferably 10 mm or less.

[0056] In the case of Example 1-14, when the inside of the through-hole was left vacant, the amount of moisture that penetrated from the outside tended to increase. As shown in Examples 15-20, it was shown that by filling the through-hole with a resin material with low moisture permeability, it is possible to increase the internal gas permeation rate while suppressing the permeation of moisture from the outside.

[0057] The embodiments and examples disclosed herein are illustrative in all respects and should not be considered as limiting. The scope of the present invention is defined by the claims, not the above description, and is intended to include the meaning equivalent to the claims and all modifications within the scope. [Explanation of symbols]

[0058] 1 energy storage device, 10 electrode body, 11 positive electrode, 12 negative electrode, 13 separator, 20 exterior body, 21 first laminate film, 22 second laminate film, 25 positive electrode tab, 26 negative electrode tab, 31 sealing layer, 32 barrier layer, 33 protective layer, 34 through hole, 35 resin portion.

Claims

1. An electrode body; An electric storage device comprising an exterior body made of a laminate film that houses the electrode body, the laminate film includes a metal layer having an inner surface facing the electrode body and an outer surface facing the outside of the power storage device, a resin layer laminated on the inner surface of the metal layer, and a protective layer laminated on the outer surface of the metal layer; a plurality of through holes penetrating the metal layer in a thickness direction are formed at intervals in a range where the electrode body and the exterior body overlap when viewed from the power storage device in a stacking direction of the laminate film, The diameter of the through hole is 3 mm or more and 10 mm or less, The laminate film further has a resin portion disposed in the through hole, the resin portion includes a resin material different from a material forming the resin layer and different from a material forming the protective layer, An electricity storage device, wherein the protective layer is free of holes that are macroscopically visible.

2. The power storage device according to claim 1 , wherein the resin portion includes a resin material having a lower moisture permeability than a material forming the resin layer.

3. The power storage device according to claim 2 , wherein the resin portion includes a resin material having a lower moisture permeability than a material forming the protective layer.

4. The power storage device according to claim 1 , wherein an area ratio of the through holes to an area of ​​the metal layer is equal to or greater than 3% and equal to or less than 40%.

5. The power storage device according to claim 1 , wherein the resin layer is free of any pores that are macroscopically visible.