Rubber composition and run-flat tire

Abstract

The present invention provides a run-flat tire with outstanding high-temperature softening suppression and a rubber composition with which the tire can be manufactured. This rubber composition includes a rubber constituent, a filler, a vulcanizing agent, and a vulcanization promoter that includes a sulfenamide-based vulcanization promoter and 1.0–2.0 parts by mass of tetrabenzylthiuram disulfide relative to 100 parts by mass of the rubber constituent; the mass ratio (a / b) of the tetrabenzylthiuram disulfide content (a) and the sulfenamide-based vulcanization promoter content (b) is 0.60–1.25.

Description

[Technical field]

[0001] The present invention relates to a rubber composition and a run-flat tire. [Background technology]

[0002] 2. Description of the Related Art Conventionally, in tires, particularly in run-flat tires, a side reinforcing layer made of a rubber composition alone or a composite of a rubber composition and fibers or the like has been provided in order to improve the rigidity of the sidewall portion. In this run-flat tire, for example, in order to improve run-flat durability, a method has been disclosed in which a side reinforcing rubber layer having a predetermined tensile strength is manufactured using a rubber composition obtained by blending a rubber component, a reinforcing filler, a thermosetting resin, a thiuram vulcanization accelerator, a vulcanization accelerator other than the thiuram vulcanization accelerator, and a sulfur-containing vulcanizing agent in predetermined amounts (see, for example, Patent Documents 1 to 3).

[0003] Also, from the viewpoint of improving the extrusion processability of a rubber composition while providing a high elastic modulus and low heat generation suitable for run-flat driving, a method has been disclosed in which a rubber component containing highly crystalline syndiotactic polybutadiene-containing polybutadiene is blended with a thiuram-based vulcanization accelerator and a sulfenamide-based vulcanization accelerator in predetermined amounts to prepare a rubber composition (see, for example, Patent Document 4). [Prior art documents] [Patent documents]

[0004] [Patent Document 1] International Publication No. 2016 / 143755 [Patent Document 2] International Publication No. 2016 / 143756 [Patent Document 3] International Publication No. 2016 / 143757 [Patent Document 4] JP 2005-263916 A Summary of the Invention [Problem to be solved by the invention]

[0005] However, the tires obtained by the methods described in Patent Documents 1 to 4 are required to be further improved in terms of the ability to inhibit the vulcanized rubber from softening at high temperatures. An object of the present invention is to provide a run-flat tire excellent in suppressing high-temperature softening, and a rubber composition capable of producing the tire. [Means for solving the problem]

[0006] <1> The rubber composition includes a rubber component, a filler, a vulcanizing agent, a sulfenamide vulcanization accelerator, and a vulcanization accelerator that contains 1.0 to 2.0 parts by mass of tetrabenzyl thiuram disulfide per 100 parts by mass of the rubber component, and the mass ratio (a / b) of the content (a) of the tetrabenzyl thiuram disulfide to the content (b) of the sulfenamide vulcanization accelerator is 0.60 to 1.25.

[0007] <2> The mass ratio (a / c) of the content (a) of the tetrabenzyl thiuram disulfide to the content (c) of the vulcanizing agent is 0.22 to 0.32. <1> The rubber composition according to claim 1, <3> The total content of the vulcanization accelerator is less than the total content of the vulcanizing agent. <1> or <2> The rubber composition according to claim 1, <4> The mass ratio (d / c) of the total content (d) of the vulcanization accelerators to the total content (c) of the vulcanizing agents is 0.55 to 0.99. <1> ~ <3> The rubber composition according to any one of the above items.

[0008] <5> The filler has a nitrogen adsorption specific surface area of ​​15 to 39 m 2 / g of carbon black <1> ~ <4> The rubber composition according to any one of the above items. <6> The filler contains carbon black having a DBP oil absorption of 120 to 180 mL / 100 g. <1> ~ <5> The rubber composition according to any one of the above items. <7> The rubber composition according to any one of <1> to <6>, wherein the total content of the softening agent and the thermosetting resin is 5 parts by mass or less with respect to 100 parts by mass of the rubber component. <8> The rubber composition according to any one of <1> to <7>, wherein the total content of the softening agent and the thermosetting resin is 1 part by mass or less with respect to 100 parts by mass of the rubber component.

[0009] <9> A run-flat tire using the rubber composition according to any one of <1> to <8> for at least one member selected from the group consisting of a side reinforcing rubber layer and a bead filler.

Advantages of the Invention

[0010] According to the present invention, it is possible to provide a run-flat tire excellent in high-temperature softening suppression and a rubber composition capable of manufacturing the tire.

Brief Description of the Drawings

[0011] [Figure 1] It is a schematic diagram showing a cross section of one embodiment of the run-flat tire of the present invention.

Modes for Carrying Out the Invention

[0012] Hereinafter, the present invention will be illustrated in detail based on its embodiments. In the following description, the description of "A to B" indicating a numerical range represents a numerical range including the endpoints A and B, and represents "A or more and B or less" (when A < B), or "A or less and B or more" (when B < A). Also, parts by mass and mass% are synonymous with parts by weight and weight%, respectively.

[0013] <Rubber Composition> The rubber composition of the present invention includes a rubber component, a filler, a vulcanizing agent, a sulfenamide vulcanization accelerator, and 1.0 to 2.0 parts by mass of tetrabenzyl thiuram disulfide per 100 parts by mass of the rubber component, wherein the mass ratio (a / b) of the content of the tetrabenzyl thiuram disulfide (a) to the content of the sulfenamide vulcanization accelerator (b) is 0.60 to 1.25. The rubber composition of the present invention has the above-mentioned structure, and therefore a tire made of a vulcanized rubber obtained from the rubber composition has excellent high-temperature softening suppression properties. Although the reason for this is not clear, it is presumed to be due to the following reasons.

[0014] In vulcanized rubber obtained by vulcanizing a rubber composition, the rubber component forms a three-dimensional network structure by sulfur crosslinking, but depending on the bonding state of the network structure, the heat resistance may be reduced. When a tire is punctured and the air inside the tire is released, the tire bends and becomes hot, but run-flat tires still support the vehicle body and allow it to run. In addition, considering ride comfort, running performance, etc., even if the tire has rigidity at a time when it is likely to soften at high temperatures (e.g., 180°C), it is preferable that the rigidity does not change before and after the tire heats up. Although the tires described in Patent Documents 1 to 3 have high tensile stress at 180°C, the temperature dependency of vulcanized rubber strength has not been verified, and the tire strength cannot be maintained before and after heat generation. Patent Document 4 merely verifies the storage modulus E' of the vulcanized rubber at 100°C. Even if the vulcanized rubber described in Patent Document 4 is applied to a run-flat tire, it is considered that it is difficult to maintain rigidity at high temperatures such as 180°C.

[0015] In contrast, the rubber composition of the present invention contains tetrabenzyl thiuram disulfide and tetrabenzyl thiuram disulfide as vulcanization accelerators in the above-mentioned ranges, and is therefore believed to be able to form a network structure with a high ratio of monosulfide bonds and disulfide bonds. This is believed to result in a vulcanized rubber that is less likely to soften at high temperatures. Furthermore, it is said that a high ratio of monosulfide bonds and disulfide bonds reduces the mechanical properties of the vulcanized rubber, but on the contrary, the vulcanized rubber obtained from the rubber composition of the present invention is believed to have little deterioration in mechanical properties, and is believed to maintain its strength from before the vulcanized rubber heats up to when it heats up and at high temperatures. As a result, it is believed that a tire obtained from the rubber composition of the present invention has excellent resistance to high-temperature softening. The rubber composition will be described in detail below.

[0016] [Rubber component] The rubber composition of the present invention contains a rubber component. Examples of the rubber component include diene rubbers and non-diene rubbers. As the diene rubber, at least one selected from the group consisting of natural rubber (NR) and synthetic diene rubber is used. Specific examples of synthetic diene rubbers include polyisoprene rubber (IR), polybutadiene rubber (BR), styrene-butadiene copolymer rubber (SBR), butadiene-isoprene copolymer rubber (BIR), styrene-isoprene copolymer rubber (SIR), and styrene-butadiene-isoprene copolymer rubber (SBIR). The diene rubber is preferably natural rubber, polyisoprene rubber, styrene-butadiene copolymer rubber, polybutadiene rubber, or isobutylene-isoprene rubber, and more preferably natural rubber or polybutadiene rubber.

[0017] Examples of non-diene rubbers include ethylene propylene rubber (EPDM (also referred to as EPM)), maleic acid modified ethylene propylene rubber (M-EPM), butyl rubber (IIR), copolymers of isobutylene and aromatic vinyl or diene monomers, acrylic rubber (ACM), ionomers, and the like.

[0018] The rubber component may be used alone or in combination of two or more kinds. The rubber component may be modified or unmodified. When two or more rubber components are used, the unmodified rubber component and the modified rubber component may be mixed and used. The rubber component may contain a diene-based rubber or a non-diene-based rubber, but from the viewpoint of obtaining a vulcanized rubber with a network structure that has excellent softening resistance and mechanical strength at high temperatures, it preferably contains at least a diene-based rubber, and more preferably consists of a diene-based rubber. In addition, the diene rubber may be either a natural rubber or a synthetic diene rubber, or both may be used. From the viewpoint of improving fracture properties such as tensile strength and elongation at break, however, it is preferable to use a combination of a natural rubber and a synthetic diene rubber.

[0019] From the viewpoint of suppressing heat generation in the vulcanized rubber, it is preferable that the rubber component does not contain styrene-butadiene copolymer rubber (the content in the rubber component is 0% by mass). Therefore, from the viewpoint of improving the high-temperature softening suppression property and low heat generation property of the tire, the rubber component is preferably composed of natural rubber, polyisoprene rubber, polybutadiene rubber, and isobutylene isoprene rubber, more preferably composed of natural rubber, polyisoprene rubber, and polybutadiene rubber, and even more preferably composed of natural rubber and polybutadiene rubber. As described above, the rubber component may be modified or unmodified, and for example, "composed of natural rubber and polybutadiene rubber" includes an embodiment using unmodified natural rubber and modified polybutadiene rubber, an embodiment using modified natural rubber and modified polybutadiene rubber, etc.

[0020] The proportion of natural rubber in the rubber component is preferably 10% by mass or more, and more preferably 20 to 80% by mass, from the viewpoint of further improving fracture properties such as tensile strength and elongation at break.

[0021] From the viewpoint of improving the low heat build-up properties of the vulcanized rubber, it is preferable to use a rubber containing a modifying group (sometimes referred to as a modified rubber) as the rubber component, and it is more preferable to use a synthetic rubber containing a modifying group. From the viewpoint of improving the reinforcing properties of the side reinforcing rubber layer, the rubber composition contains a filler, and in order to enhance the interaction with the filler (particularly, carbon black), it is preferable that the rubber component contains a polybutadiene rubber containing a modifying group (modified polybutadiene rubber) as a synthetic rubber containing a modifying group. As described later, the filler preferably contains at least carbon black, and the modified polybutadiene rubber is preferably a modified polybutadiene rubber having at least one functional group that interacts with carbon black. The functional group that interacts with carbon black is preferably a functional group having affinity for carbon black, and specifically, is preferably at least one selected from the group consisting of a tin-containing functional group, a silicon-containing functional group, and a nitrogen-containing functional group.

[0022] When the modified polybutadiene rubber is a modified polybutadiene rubber having at least one functional group selected from the group consisting of a tin-containing functional group, a silicon-containing functional group, and a nitrogen-containing functional group, the modified polybutadiene rubber is preferably modified with a modifier such as a tin-containing compound, a silicon-containing compound, or a nitrogen-containing compound, and a tin-containing functional group, a silicon-containing functional group, a nitrogen-containing functional group, or the like is introduced into the modified polybutadiene rubber. When modifying the polymerization active site of the butadiene rubber with a modifier, the modifier preferably used is a nitrogen-containing compound, a silicon-containing compound, or a tin-containing compound. In this case, a nitrogen-containing functional group, a silicon-containing functional group, or a tin-containing functional group can be introduced by the modification reaction. Such a modifying functional group may be present at any one of the polymerization initiation terminal, the main chain, and the polymerization active terminal of the polybutadiene.

[0023] The nitrogen-containing compound that can be used as the modifying agent preferably has a substituted or unsubstituted amino group, amide group, imino group, imidazole group, nitrile group, or pyridyl group. Examples of the nitrogen-containing compound suitable as the modifying agent include isocyanate compounds such as diphenylmethane diisocyanate, crude MDI, trimethylhexamethylene diisocyanate, and tolylene diisocyanate, 4-(dimethylamino)benzophenone, 4-(diethylamino)benzophenone, 4-dimethylaminobenzylideneaniline, 4-dimethylaminobenzylidenebutylamine, dimethylimidazolidinone, and N-methylpyrrolidone hexamethyleneimine.

[0024] Examples of silicon-containing compounds that can be used as the modifying agent include 3-glycidoxypropyltrimethoxysilane, 3-glycidoxypropyltriethoxysilane, N-(1-methylpropylidene)-3-(triethoxysilyl)-1-propanamine, N-(1,3-dimethylbutylidene)-3-(triethoxysilyl)-1-propanamine, N-(3-triethoxysilylpropyl)-4,5-dihydroimidazole, 3-methacryloyloxypropyltrimethoxysilane, 3-isocyanatoxin, and the like. Examples of the silicon-containing compounds include tripropyltriethoxysilane, 3-triethoxysilylpropylsuccinic anhydride, 3-(1-hexamethyleneimino)propyl(triethoxy)silane, (1-hexamethyleneimino)methyl(trimethoxy)silane, 3-diethylaminopropyl(triethoxy)silane, 3-dimethylaminopropyl(triethoxy)silane, 2-(trimethoxysilylethyl)pyridine, 2-(triethoxysilylethyl)pyridine, 2-cyanoethyltriethoxysilane, and tetraethoxysilane. These silicon-containing compounds may be used alone or in combination of two or more. In addition, partial condensates of the silicon-containing compounds may also be used.

[0025] Further, the above-mentioned modifying agent is a compound represented by the following formula (I): R 1 a ZX b(I) [In the formula, R 1 are each independently selected from the group consisting of an alkyl group having 1 to 20 carbon atoms, a cycloalkyl group having 3 to 20 carbon atoms, an aryl group having 6 to 20 carbon atoms, and an aralkyl group having 7 to 20 carbon atoms; Z is tin or silicon; X is each independently chlorine or bromine; a is 0 to 3, and b is 1 to 4, with the proviso that a+b=4. The modified polybutadiene rubber obtained by modification with the modifying agent of formula (I) has at least one type of tin-carbon bond or silicon-carbon bond.

[0026] R in formula (I) 1 Specific examples of the denaturing agent of formula (I) include methyl, ethyl, n-butyl, neophyl, cyclohexyl, n-octyl, and 2-ethylhexyl groups. Specific examples of the denaturing agent of formula (I) include SnCl4, R 1 SnCl3, R 1 2SnCl2, R 1 3SnCl, SiCl4, R 1 SiCl3, R 1 2SiCl2,R 1 3SiCl and the like are preferred, with SnCl4 and SiCl4 being particularly preferred.

[0027] Of the above, the modified polybutadiene rubber is preferably a modified polybutadiene rubber having a nitrogen-containing functional group, and more preferably an amine-modified polybutadiene rubber, from the viewpoint of reducing heat generation of the vulcanized rubber and extending the durability life.

[0028] (Modifying group of amine-modified polybutadiene rubber) In the amine-modified polybutadiene rubber, the modifying amine functional group is preferably a primary amino group or a secondary amino group, more preferably a primary amino group protected with a removable group or a secondary amino group protected with a removable group, and even more preferably a functional group containing a silicon atom is introduced in addition to these amino groups. An example of a primary amino group protected with a removable group (also called a protected primary amino group) is an N,N-bis(trimethylsilyl)amino group, and an example of a secondary amino group protected with a removable group is an N,N-(trimethylsilyl)alkylamino group. This N,N-(trimethylsilyl)alkylamino group-containing group may be either a noncyclic residue or a cyclic residue. Of the above amine-modified polybutadiene rubbers, primary amine-modified polybutadiene rubbers modified with protected primary amino groups are more preferred. Examples of the functional group containing a silicon atom include a hydrocarbyloxysilyl group and / or a silanol group in which a hydrocarbyloxy group and / or a hydroxy group is bonded to a silicon atom. Such a modifying functional group preferably has an amino group protected with a releasable group and one or more (e.g., 1 or 2) silicon atoms to which a hydrocarbyloxy group and a hydroxy group are bonded, at the polymerization terminal of the butadiene rubber, more preferably at the same polymerization active terminal.

[0029] In order to modify the active terminal of the butadiene rubber by reacting with a protected primary amine, it is preferable that at least 10% of the polymer chain of the butadiene rubber has living or pseudo-living properties. Examples of such polymerization reactions having living properties include anionic polymerization of a conjugated diene compound alone or a conjugated diene compound and an aromatic vinyl compound in an organic solvent using an organic alkali metal compound as an initiator, or coordination anionic polymerization of a conjugated diene compound alone or a conjugated diene compound and an aromatic vinyl compound in an organic solvent using a catalyst containing a lanthanum series rare earth element compound. The former is preferable because it can obtain a conjugated diene part with a higher vinyl bond content than the latter. By increasing the amount of vinyl bonds, the heat resistance of the vulcanized rubber can be improved.

[0030] (Polymerization initiator) As the organic alkali metal compound used as an initiator of anionic polymerization, organic lithium compound is preferred.As the organic lithium compound, there is no particular limitation, but hydrocarbyl lithium and lithium amide compound are preferably used.When using the former hydrocarbyl lithium, the butadiene rubber having hydrocarbyl group at polymerization initiation end and the other end being polymerization active site is obtained.In addition, when using the latter lithium amide compound, the butadiene rubber having nitrogen-containing group at polymerization initiation end and the other end being polymerization active site is obtained.

[0031] The hydrocarbyllithium is preferably one having a hydrocarbyl group having 2 to 20 carbon atoms, and examples thereof include ethyllithium, n-propyllithium, isopropyllithium, n-butyllithium, sec-butyllithium, tert-octyllithium, n-decyllithium, phenyllithium, 2-naphthyllithium, 2-butylphenyllithium, 4-phenylbutyllithium, cyclohexyllithium, cyclopentyllithium, and a reaction product of diisopropenylbenzene with butyllithium. Of these, n-butyllithium is particularly preferred.

[0032] On the other hand, examples of the lithium amide compound include lithium hexamethyleneimide, lithium pyrrolidide, lithium piperidide, lithium heptamethyleneimide, lithium dodecamethyleneimide, lithium dimethylamide, lithium diethylamide, lithium dibutylamide, lithium dipropylamide, lithium diheptylamide, lithium dihexylamide, lithium dioctylamide, lithium di-2-ethylhexylamide, lithium didecylamide, lithium-N-methylpiberazide, lithium ethylpropylamide, lithium ethylbutylamide, lithium ethylbenzylamide, lithium methylphenethylamide, etc. Among these, from the viewpoints of the interaction effect with carbon black and the polymerization initiation ability, cyclic lithium amides such as lithium hexamethyleneimide, lithium pyrrolidide, lithium piperidide, lithium heptamethyleneimide, and lithium dodecamethyleneimide are preferred, and lithium hexamethyleneimide and lithium pyrrolidide are particularly preferred. These lithium amide compounds can generally be prepared in advance from a secondary amine and a lithium compound and used in the polymerization, but can also be prepared in situ. The amount of the polymerization initiator used is preferably selected in the range of 0.2 to 20 mmol per 100 g of monomer.

[0033] The method for producing the butadiene rubber by anionic polymerization using the organolithium compound as a polymerization initiator is not particularly limited, and any conventionally known method can be used. Specifically, in an organic solvent inert to the reaction, for example, a hydrocarbon solvent such as an aliphatic, alicyclic, or aromatic hydrocarbon compound, a conjugated diene compound or a conjugated diene compound and an aromatic vinyl compound are anionically polymerized using the lithium compound as a polymerization initiator, and optionally in the presence of a randomizer, to obtain a butadiene rubber having the desired active terminals. In addition, when an organolithium compound is used as a polymerization initiator, not only a butadiene rubber having an active end but also a copolymer of a conjugated diene compound and an aromatic vinyl compound having an active end can be efficiently obtained, as compared with the case where a catalyst containing the above-mentioned lanthanum series rare earth element compound is used.

[0034] The hydrocarbon solvent preferably has 3 to 8 carbon atoms, and examples thereof include propane, n-butane, isobutane, n-pentane, isopentane, n-hexane, cyclohexane, propene, 1-butene, isobutene, trans-2-butene, cis-2-butene, 1-pentene, 2-pentene, 1-hexene, 2-hexene, benzene, toluene, xylene, ethylbenzene, etc. These may be used alone or in combination of two or more. The monomer concentration in the solvent is preferably 5 to 50% by mass, more preferably 10 to 30% by mass. When copolymerization is carried out using a conjugated diene compound and an aromatic vinyl compound, the content of the aromatic vinyl compound in the charged monomer mixture is preferably in the range of 55% by mass or less.

[0035] (Modifier) In the present invention, a primary amine-modified polybutadiene rubber can be produced by reacting a protected primary amine compound as a modifier with the active terminal of the butadiene rubber having an active terminal obtained as described above, and a secondary amine-modified polybutadiene rubber can be produced by reacting a protected secondary amine compound. As the protected primary amine compound, an alkoxysilane compound having a protected primary amino group is preferable, and as the protected secondary amine compound, an alkoxysilane compound having a protected secondary amino group is preferable.

[0036] Examples of the alkoxysilane compound having a protected primary amino group that can be used as a modifier for obtaining the amine-modified polybutadiene rubber include N,N-bis(trimethylsilyl)aminopropylmethyldimethoxysilane, 1-trimethylsilyl-2,2-dimethoxy-1-aza-2-silacyclopentane, N,N-bis(trimethylsilyl)aminopropyltrimethoxysilane, N,N-bis(trimethylsilyl)aminopropyltriethoxysilane, N,N-bis(trimethylsilyl)aminopropylmethyldiethoxysilane, N,N-bis(trimethylsilyl)aminopropylmethyldiethoxysilane, and N,N-bis(trimethylsilyl)aminopropylmethyldimethoxysilane. Examples of the silane derivative include N,N-bis(trimethylsilyl)aminoethyltrimethoxysilane, N,N-bis(trimethylsilyl)aminoethyltriethoxysilane, N,N-bis(trimethylsilyl)aminoethylmethyldimethoxysilane, and N,N-bis(trimethylsilyl)aminoethylmethyldiethoxysilane. Preferred are N,N-bis(trimethylsilyl)aminopropylmethyldimethoxysilane, N,N-bis(trimethylsilyl)aminopropylmethyldiethoxysilane, and 1-trimethylsilyl-2,2-dimethoxy-1-aza-2-silacyclopentane.

[0037] In addition, examples of the modifier for obtaining the amine-modified polybutadiene rubber include N-methyl-N-trimethylsilylaminopropyl(methyl)dimethoxysilane, N-methyl-N-trimethylsilylaminopropyl(methyl)diethoxysilane, N-trimethylsilyl(hexamethyleneimine-2-yl)propyl(methyl)dimethoxysilane, N-trimethylsilyl(hexamethyleneimine-2-yl)propyl(methyl)diethoxysilane, and N-trimethylsilyl N-trimethylsilyl(pyrrolidin-2-yl)propyl(methyl)dimethoxysilane, N-trimethylsilyl(pyrrolidin-2-yl)propyl(methyl)diethoxysilane, N-trimethylsilyl(piperidin-2-yl)propyl(methyl)dimethoxysilane, N-trimethylsilyl(piperidin-2-yl)propyl(methyl)diethoxysilane, N-trimethylsilyl(imidazol-2-yl)propyl(methyl)dimethoxysilane, N-trimethylsilyl(imidazolyl-2-yl)propyl(methyl)dimethoxysilane alkoxysilane compounds having a protected secondary amino group, such as N-(1,3-dimethylbutylidene)-3-(triethoxysilyl)-1-propanamine, N-(1-methylethylidene)-3-(triethoxysilyl)-1-propanamine, N-(1-methylethylidene)-3-(trimethyl ... alkoxysilane compounds having an imino group, such as N-(1-methylpropylidene)-3-(triethoxysilyl)-1-propanamine, N-(4-N,N-dimethylaminobenzylidene)-3-(triethoxysilyl)-1-propanamine, and N-(cyclohexylidene)-3-(triethoxysilyl)-1-propanamine;Examples of alkoxysilane compounds having an amino group include 3-dimethylaminopropyl(triethoxy)silane, 3-dimethylaminopropyl(trimethoxy)silane, 3-diethylaminopropyl(triethoxy)silane, 3-diethylaminopropyl(trimethoxy)silane, 2-dimethylaminoethyl(triethoxy)silane, 2-dimethylaminoethyl(trimethoxy)silane, 3-dimethylaminopropyl(diethoxy)methylsilane, and 3-dibutylaminopropyl(triethoxy)silane. These modifying agents may be used alone or in combination of two or more. The modifying agent may be a partial condensate. Here, the partial condensate refers to a compound in which a part (but not all) of the SiOR (R is an alkyl group or the like) of the modifier is condensed to form an SiOSi bond.

[0038] In the modification reaction with the modifier, the amount of the modifier used is preferably 0.5 to 200 mmol / kg-butadiene rubber. The amount used is more preferably 1 to 100 mmol / kg-butadiene rubber, and particularly preferably 2 to 50 mmol / kg-butadiene rubber. Here, butadiene rubber means the mass of butadiene rubber that does not include additives such as antioxidants added during or after production. By setting the amount of the modifier used within the above range, the dispersibility of the filler, particularly carbon black, is excellent, and the fracture resistance and low heat build-up of the vulcanized rubber are improved. The method of adding the modifying agent is not particularly limited, and examples thereof include a method of adding the modifying agent all at once, a method of adding the modifying agent in portions, and a method of adding the modifying agent continuously. However, a method of adding the modifying agent all at once is preferable. The modifying agent can be bonded to either the polymer main chain or the side chain, other than the polymerization initiation end or the polymerization termination end. However, it is preferable that the modifying agent is introduced to the polymerization initiation end or the polymerization termination end, since this can suppress energy loss from the polymer end and improve low heat buildup.

[0039] (Condensation accelerator) In the present invention, it is preferable to use a condensation promoter in order to promote the condensation reaction involving the alkoxysilane compound having a protected primary amino group used as the above-mentioned modifying agent. As such a condensation promoter, a compound containing a tertiary amino group or an organic compound containing one or more elements belonging to any of Groups 3, 4, 5, 12, 13, 14, and 15 of the periodic table (long period type) can be used. Furthermore, as the condensation promoter, an alkoxide, carboxylate, or acetylacetonate complex salt containing at least one metal selected from the group consisting of titanium (Ti), zirconium (Zr), bismuth (Bi), aluminum (Al), and tin (Sn) is preferable. The condensation accelerator used here can be added before the modification reaction, but is preferably added to the modification reaction system during and / or after the modification reaction. If added before the modification reaction, a direct reaction with the active terminal occurs, and a hydrocarbyloxy group having a protected primary amino group may not be introduced at the active terminal. The timing of adding the condensation promoter is usually 5 minutes to 5 hours after the start of the modification reaction, and preferably 15 minutes to 1 hour after the start of the modification reaction.

[0040] Specific examples of the condensation promoter include tetramethoxytitanium, tetraethoxytitanium, tetra-n-propoxytitanium, tetraisopropoxytitanium, tetra-n-butoxytitanium, tetra-n-butoxytitanium oligomer, tetra-sec-butoxytitanium, tetra-tert-butoxytitanium, tetra(2-ethylhexyl)titanium, bis(octanediolate)bis(2-ethylhexyl)titanium, tetra(octanediolate)titanium, titanium Titanium lactate, titanium dipropoxy bis(triethanol aminate), titanium dibutoxy bis(triethanol aminate), titanium tributoxy stearate, titanium tripropoxy stearate, titanium ethylhexyl diolate, titanium tripropoxy acetylacetonate, titanium dipropoxy bis(acetylacetonate), titanium tripropoxy ethyl acetoacetate, titanium propoxy acetylacetonate bis(ethyl acetoacetate), titanium Titanium tributoxy acetylacetonate, titanium dibutoxy bis(acetylacetonate), titanium tributoxy ethyl acetoacetate, titanium butoxy acetylacetonate bis(ethyl acetoacetate), titanium tetrakis(acetylacetonate), titanium diacetylacetonate bis(ethyl acetoacetate), bis(2-ethylhexanoate) titanium oxide, bis(laurate) titanium oxide, bis(naphthenate) titanium oxide, Examples of titanium-containing compounds include titanium bis(stearate)titanium oxide, titanium bis(oleate), titanium bis(linoleate), titanium tetrakis(2-ethylhexanoate), titanium tetrakis(laurate), titanium tetrakis(naphthenate), titanium tetrakis(stearate), titanium tetrakis(oleate), titanium tetrakis(linoleate), and titanium tetrakis(2-ethyl-1,3-hexanediolato).

[0041] Also, for example, tris(2-ethylhexanoate)bismuth, tris(laurate)bismuth, tris(naphthenate)bismuth, tris(stearate)bismuth, tris(oleate)bismuth, tris(linoleate)bismuth, tetraethoxyzirconium, tetra-n-propoxyzirconium, tetraisopropoxyzirconium, tetra-n-butoxyzirconium, tetra-sec-butoxyzirconium, tetra-tert-butoxyzirconium, tetra(2-ethylhexyl)zirconium, zirconium tributoxystearate, zirconium tributoxyacetylacetonate, zirconium dibutoxybis(acetylacetonate), zirconium tributoxyethylacetoacetate, zirconium butoxyacetylacetonate bis(ethylacetoacetate), Examples of compounds containing bismuth or zirconium include tetrakis(2-ethylhexanoate)zirconium oxide, bis(laurate)zirconium oxide, bis(naphthenate)zirconium oxide, bis(stearate)zirconium oxide, bis(oleate)zirconium oxide, bis(linoleate)zirconium oxide, tetrakis(2-ethylhexanoate)zirconium, tetrakis(laurate)zirconium, tetrakis(naphthenate)zirconium, tetrakis(stearate)zirconium, tetrakis(oleate)zirconium, and tetrakis(linoleate)zirconium.

[0042] Further examples of aluminum-containing compounds include triethoxyaluminum, tri-n-propoxyaluminum, triisopropoxyaluminum, tri-n-butoxyaluminum, tri-sec-butoxyaluminum, tri-tert-butoxyaluminum, tri(2-1-ethylhexyl)aluminum, aluminum dibutoxystearate, aluminum dibutoxyacetylacetonate, aluminum butoxybis(acetylacetonate), aluminum dibutoxyethylacetoacetate, aluminum tris(acetylacetonate), aluminum tris(ethylacetoacetate), tris(2-ethylhexanoate)aluminum, tris(laurate)aluminum, tris(naphthenate)aluminum, tris(stearate)aluminum, tris(oleate)aluminum, and tris(linoleate)aluminum.

[0043] Among the above-mentioned condensation promoters, titanium compounds are preferred, and titanium metal alkoxides, titanium metal carboxylates, and titanium metal acetylacetonate complex salts are particularly preferred. The amount of the condensation promoter used is preferably such that the molar ratio of the number of moles of the compound to the total amount of hydrocarbyloxy groups present in the reaction system is 0.1 to 10, and particularly preferably 0.5 to 5. By setting the amount of the condensation promoter used within the above range, the condensation reaction proceeds efficiently. The condensation reaction time is usually about 5 minutes to 10 hours, and preferably about 15 minutes to 5 hours. By setting the condensation reaction time within the above range, the condensation reaction can be smoothly completed. The pressure of the reaction system during the condensation reaction is usually 0.01 to 20 MPa, and preferably 0.05 to 10 MPa.

[0044] From the viewpoint of improving the low heat build-up property and high-temperature softening resistance of the vulcanized rubber, the content of the modified rubber in the rubber component is preferably from 10 to 90 mass %, more preferably from 20 to 80 mass %.

[0045] [Filler] The rubber composition of the present invention contains a filler from the viewpoints of increasing the rigidity of the vulcanized rubber and obtaining softening resistance at high temperatures. Examples of the filler include metal oxides such as alumina, titania, and silica, clay, calcium carbonate, and reinforcing fillers such as carbon black, and silica and carbon black are preferably used. From the viewpoint of suppressing heat generation of the vulcanized rubber even when the air in the tire is released and the side reinforcing rubber layer, the bead filler, etc. are bent and the vulcanized rubber constituting these parts generates heat, it is preferable to use a filler with low heat generation.

[0046] (Carbon Black) When the rubber composition contains carbon black, the strength of the vulcanized rubber can be improved. Furthermore, from the viewpoint of improving the low heat generation property of vulcanized rubber, carbon black is used with a nitrogen adsorption specific surface area (N2SA) of 15 to 39 m 2 In this specification, it is preferable that the nitrogen adsorption specific surface area is 39 m 2 / g or less is referred to as large particle size carbon black. Nitrogen adsorption specific surface area is 39m 2 / g or less, heat generation caused by carbon black can be suppressed, and heat generation of vulcanized rubber can be suppressed. 2 From the viewpoint of improving the low heat generation and reinforcing properties of the vulcanized rubber and improving the high-temperature softening suppression properties of the tire, the nitrogen adsorption specific surface area of ​​the carbon black is 18 to 37 m 2 / g is more preferable, and 21 to 35m 2 It is more preferable that the molecular weight is / g.

[0047] The carbon black also preferably has a DBP oil absorption (dibutyl phthalate oil absorption) of 120 to 180 mL / 100 g. DBP oil absorption is used as an index of the degree of development of the aggregate structure of carbon black (sometimes referred to as "structure"). The higher the DBP oil absorption, the larger the aggregates tend to be. In this specification, carbon black with a DBP oil absorption of 120 mL / 100 g or more is referred to as high-structure carbon black. A DBP oil absorption of 120 mL / 100 g or more can improve the tensile strength and compression resistance of the vulcanized rubber and improve the high-temperature softening resistance of the tire. A DBP oil absorption of 180 mL / 100 g or less can suppress heat generation and improve the high-temperature softening resistance of the tire. The DBP oil absorption of the carbon black is more preferably from 122 to 170 mL / 100 g, and further preferably from 125 to 165 mL / 100 g.

[0048] The rubber composition of the present invention preferably contains carbon black having a large particle size and high structure. Generally, the larger the particle size of carbon black, the lower the structure of the carbon black. However, by using carbon black having a large particle size but high structure, heat generation can be suppressed and tensile strength and compressive strength can be improved, so that the softening resistance of run-flat tires at high temperatures can be improved. Specifically, the rubber composition of the present invention has a nitrogen adsorption specific surface area of ​​15 to 39 m 2 / g and the DBP oil absorption is preferably 120 to 180 mL / 100 g.

[0049] The carbon black preferably has a toluene coloring transmittance of 50% or more. A toluene color transmission of 50% or more suppresses the tar content, particularly aromatic components, present on the carbon black surface, and can adequately reinforce the rubber component, improving the abrasion resistance of the vulcanized rubber. The toluene color transmission of carbon black is more preferably 60% or more, and even more preferably 75% or more. The toluene color transmission of carbon black may be 100%, but is usually less than 100%. The toluene coloring transmittance is measured by the method described in JIS K 6218:1997, Section 8, Method B, and is expressed as a percentage of pure toluene.

[0050] The content of carbon black in the rubber composition is preferably 30 to 100 parts by mass, more preferably 35 to 80 parts by mass, and even more preferably 40 to 70 parts by mass, per 100 parts by mass of the rubber component, from the viewpoint of further improving the softening resistance of the vulcanized rubber at high temperatures and thereby further improving the run-flat durability.

[0051] (silica) The silica is not particularly limited, and examples thereof include wet silica (hydrated silicic acid), dry silica (anhydrous silicic acid), colloidal silica, etc. The silica may be a commercially available product, and is available, for example, as NIPSIL AQ (trade name) from Tosoh Silica Corporation, Zeosil 1115MP (trade name) from Rhodia, and VN-3 (trade name) from Evonik Degussa. In addition, when silica is used as a filler, the rubber composition may further contain a silane coupling agent in order to strengthen the bond between the silica and the rubber component to increase the reinforcing property and to improve the dispersibility of the silica in the rubber composition.

[0052] The filler may be used alone or in combination of two or more. The filler may contain either carbon black or silica, or both, but preferably contains at least carbon black, and more preferably uses carbon black alone or in combination of two or more. The content (total amount) of the filler in the rubber composition of the present invention is preferably 30 to 100 parts by mass, more preferably 30 to 100 parts by mass, more preferably 35 to 80 parts by mass, and even more preferably 40 to 70 parts by mass, per 100 parts by mass of the rubber component, from the viewpoint of further improving the softening resistance of the vulcanized rubber at high temperatures and thereby further improving the run-flat durability.

[0053] [Vulcanizing agent] The rubber composition of the present invention contains a vulcanizing agent. The vulcanizing agent is not particularly limited, and sulfur is usually used. Examples of the vulcanizing agent include powdered sulfur, precipitated sulfur, colloidal sulfur, surface-treated sulfur, and insoluble sulfur. The content of the vulcanizing agent in the rubber composition is preferably 2 to 12 parts by mass per 100 parts by mass of the rubber component. When the content is 2 parts by mass or more, the vulcanization can proceed sufficiently, and when the content is 12 parts by mass or less, the aging resistance of the vulcanized rubber can be suppressed. The content of the vulcanizing agent in the rubber composition is more preferably 3 to 10 parts by mass, and further preferably 4 to 8 parts by mass, per 100 parts by mass of the rubber component.

[0054] [Vulcanization accelerator] The rubber composition contains a sulfenamide vulcanization accelerator and tetrabenzyl thiuram disulfide as vulcanization accelerators, wherein the content of the tetrabenzyl thiuram disulfide in the rubber composition is 1.0 to 2.0 parts by mass per 100 parts by mass of the rubber component, and the mass ratio (a / b) of the content (a) of the tetrabenzyl thiuram disulfide to the content (b) of the sulfenamide vulcanization accelerator is 0.60 to 1.25. The rubber composition of the present invention contains the sulfenamide vulcanization accelerator and tetrabenzyl thiuram disulfide in the above amounts as vulcanization accelerators, and therefore the run-flat tire obtained from the rubber composition of the present invention is considered to have excellent high-temperature softening suppression, and as a result, excellent run-flat durability. This is considered to be because the use of the vulcanization accelerator in the above composition allows the vulcanized rubber to form a network structure with a high ratio of monosulfide bonds and disulfide bonds, which makes the vulcanized rubber excellent in softening resistance at high temperatures and maintains rigidity even when the vulcanized rubber is compressed or pulled at high temperatures.

[0055] If the content (a) of trabenzyl thiuram disulfide in the rubber composition is less than 1.0 part by mass per 100 parts by mass of the rubber component, sufficient inhibition of softening at high temperatures cannot be obtained, while if the content (a) exceeds 2.0 parts by mass, rubber burning is likely to occur and the mechanical strength of the vulcanized rubber decreases. From the viewpoint of further improving the high-temperature softening suppression property of the tire, the content (a) is preferably from 1.2 to 1.8 parts by mass, and more preferably from 1.3 to 1.7 parts by mass. If the mass ratio (a / b) of the content of tetrabenzyl thiuram disulfide (a) to the content of sulfenamide vulcanization accelerator (b) is less than 0.60, the vulcanized rubber will not have high softening resistance at high temperatures, and therefore will not have run-flat durability. If the mass ratio (a / b) exceeds 1.25, the fracture properties will decrease. From the viewpoint of further improving the high-temperature softening suppression property of the tire, the mass ratio (a / b) is preferably from 0.62 to 1.22, and more preferably from 0.64 to 1.20.

[0056] The mass ratio (a / c) of the content (a) of the tetrabenzyl thiuram disulfide to the content (c) of the vulcanizing agent is preferably 0.22 to 0.32. When the mass ratio (a / c) is within the above range, the vulcanized rubber has excellent resistance to softening at high temperatures, and therefore has excellent run-flat durability. The mass ratio (a / c) is more preferably from 0.25 to 0.32, and further preferably from 0.27 to 0.32.

[0057] Furthermore, in the rubber composition of the present invention, the total content of the vulcanization accelerator is preferably less than the total content of the vulcanizing agent. More specifically, the mass ratio (d / c) of the total content (d) of the vulcanization accelerator to the total content (c) of the vulcanizing agent is preferably 0.55 to 0.99. Generally, in order to increase the ratio of monosulfide bonds and disulfide bonds in the network structure of vulcanized rubber, the total content of vulcanization accelerators is made larger than the total content of vulcanizing agents, but in the present invention, it is preferable to make the total content of vulcanization accelerators smaller than the total content of vulcanizing agents. Furthermore, it is said that vulcanized rubbers using thiuram vulcanization accelerators and having a large ratio of monosulfide bonds and disulfide bonds have excellent heat resistance but low mechanical strength. However, in the present invention, it is possible to achieve both softening resistance and mechanical strength at high temperatures. Although the reason for this is unclear, it is believed that in the present invention, softening resistance and mechanical strength at high temperatures can be achieved due to the inclusion of a sulfenamide vulcanization accelerator and tetrabenzyl thiuram disulfide as vulcanization accelerators in the specific amounts described above. From the viewpoint of further improving the high-temperature softening suppression property of the tire, the mass ratio (d / c) is more preferably from 0.55 to 0.95, even more preferably from 0.55 to 0.90, and even more preferably from 0.55 to 0.85.

[0058] (Sulfenamide vulcanization accelerator) Examples of the sulfenamide vulcanization accelerator include N-cyclohexyl-2-benzothiazolyl sulfenamide, N,N-dicyclohexyl-2-benzothiazolyl sulfenamide, N-tert-butyl-2-benzothiazolyl sulfenamide, N-oxydiethylene-2-benzothiazolyl sulfenamide, N-methyl-2-benzothiazolyl sulfenamide, N-ethyl-2-benzothiazolyl sulfenamide, N-propyl-2-benzothiazolyl sulfenamide, N-butyl-2-benzothiazolyl sulfenamide, N-pentyl-2-benzothiazolyl sulfenamide, N-hexyl-2-benzothiazolyl sulfenamide, N-heptyl-2-benzothiazolyl sulfenamide, N-octyl-2-benzothiazolyl sulfenamide, N-2-ethylhexyl-2-benzothiazolyl sulfenamide, N-decyl-2-benzothiazolyl sulfenamide, N -Dodecyl-2-benzothiazolylsulfenamide, N-Stearyl-2-benzothiazolylsulfenamide, N,N-Dimethyl-2-benzothiazolylsulfenamide, N,N-Diethyl-2-benzothiazolylsulfenamide, N,N-Dipropyl-2-benzothiazolylsulfenamide, N,N-Dibutyl-2-benzothiazolylsulfenamide, N,N-Dipentyl-2-benzothiazolylsulfenamide, N,N-Dihexyl 2-benzothiazolylsulfenamide, N,N-diheptyl-2-benzothiazolylsulfenamide, N,N-dioctyl-2-benzothiazolylsulfenamide, N,N-di-2-ethylhexylbenzothiazolylsulfenamide, N,N-didecyl-2-benzothiazolylsulfenamide, N,N-didodecyl-2-benzothiazolylsulfenamide, and N,N-distearyl-2-benzothiazolylsulfenamide. The sulfenamide vulcanization accelerators may be used alone or in combination of two or more.

[0059] Of the above sulfenamide vulcanization accelerators, from the viewpoint of achieving both high-temperature softening resistance and mechanical strength of the vulcanized rubber and further improving run-flat durability, N-cyclohexyl-2-benzothiazolylsulfenamide and N-tert-butyl-2-benzothiazolylsulfenamide are preferred, and N-tert-butyl-2-benzothiazolylsulfenamide is more preferred. The sulfenamide vulcanization accelerator can be freely used within the range of the mass ratio (a / b) described above of 0.60 to 1.25, but the content of the sulfenamide vulcanization accelerator in the rubber composition is preferably 0.80 to 3.33 parts by mass per 100 parts by mass of the rubber component. From the viewpoint of further improving the high-temperature softening suppression property, the content of the sulfenamide vulcanization accelerator is more preferably 1.00 to 3.00 parts by mass, and further preferably 1.10 to 2.80 parts by mass per 100 parts by mass of the rubber component.

[0060] The rubber composition of the present invention may further contain a vulcanization accelerator such as a guanidine-based, aldehyde-amine-based, aldehyde-ammonia-based, thiazole-based, thiourea-based, dithiocarbamate-based, or xanthate-based vulcanization accelerator in addition to a thiuram-based vulcanization accelerator other than tetrabenzylthiuram disulfide. However, in a component composition in which the total content of the vulcanization accelerator is less than the total content of the vulcanizing agent, the ratio of monosulfide bonds and disulfide bonds is increased to increase the softening resistance of the vulcanized rubber at high temperatures while improving its mechanical strength, so that the vulcanization accelerator preferably consists of tetrabenzyl thiuram disulfide and a sulfenamide-based vulcanization accelerator.

[0061] (vulcanization retarder) The rubber composition of the present invention may contain a vulcanization retarder. By containing the vulcanization retarder in the rubber composition, rubber burning caused by overheating of the rubber composition during preparation of the rubber composition can be suppressed. In addition, the scorch stability of the rubber composition can be improved, and the rubber composition can be easily extruded from a kneader. The rubber composition of the present invention has a Mooney viscosity (ML 1+4, 130°C) is preferably 40 to 100, more preferably 50 to 90, and further preferably 60 to 85. When the Mooney viscosity is within the above range, sufficient physical properties of the vulcanized rubber, including fracture resistance, can be obtained without impairing manufacturing processability. Examples of the vulcanization retarder include phthalic anhydride, benzoic acid, salicylic acid, N-nitrosodiphenylamine, N-(cyclohexylthio)-phthalimide (CTP), sulfonamide derivatives, diphenylurea, bis(tridecyl)pentaerythritol-diphosphite, etc. Commercially available vulcanization retarders may be used, such as Monsanto's product name "Santoguard PVI" [N-(cyclohexylthio)-phthalimide]. Among the above, N-(cyclohexylthio)-phthalimide (CTP) is preferably used as the vulcanization retarder. When a vulcanization retarder is used, from the viewpoint of suppressing rubber burning of the rubber composition without interfering with the vulcanization reaction and improving scorch stability, the content of the vulcanization retarder in the rubber composition is preferably 0.1 to 1.0 part by mass per 100 parts by mass of the rubber component.

[0062] [Softener, thermosetting resin] The rubber composition of the present invention preferably does not substantially contain a softener and a thermosetting resin. Specifically, the content of each of the softener and the thermosetting resin is preferably 5 parts by mass or less per 100 parts by mass of the rubber component, the total content of the softener and the thermosetting resin is more preferably 5 parts by mass or less per 100 parts by mass of the rubber component, and the total content is further preferably 1 part by mass or less, and it is particularly preferable that the rubber composition does not contain a softener and a thermosetting resin (the total content of the softener and the thermosetting resin is 0 parts by mass per 100 parts by mass of the rubber component).

[0063] (Softener) Since the rubber composition does not substantially contain a softener, the ratio of the elastic modulus of the vulcanized rubber at high temperature to the elastic modulus at room temperature can be increased. Therefore, when the vulcanized rubber is applied to the side reinforcing rubber of a tire, the deflection of the tire sidewall can be suppressed. Therefore, from the viewpoint of improving durability during run-flat driving, it is preferable that the rubber composition does not contain a softener. Examples of the softener include process oil and thermoplastic resin. Examples of process oils include mineral oils derived from minerals, aromatic oils derived from petroleum, paraffin oils, naphthenic oils, and palm oils derived from natural products. Thermoplastic resins include resins that soften or become liquid at high temperatures and make vulcanized rubber flexible. Specific examples include various petroleum-based resins such as C5-based (including cyclopentadiene-based resins and dicyclopentadiene-based resins), C9-based, and C5 / C9 mixed resins, terpene-based resins, terpene-aromatic compound-based resins, rosin-based resins, phenolic resins, and tackifiers (not including curing agents) such as alkylphenol resins.

[0064] (thermosetting resin) Since the rubber composition is substantially free of thermosetting resin, the vulcanized rubber becomes flexible, and the static vertical spring constant of a run-flat tire using the rubber composition of the present invention becomes small, resulting in good ride comfort of the run-flat tire. Examples of the thermosetting resin include phenol resin, melamine resin, urea resin, epoxy resin, etc. Examples of the hardener for the phenol resin include hexamethylenetetramine, etc.

[0065] The rubber composition of the present invention may contain, together with the above-mentioned components, compounding agents that are compounded and used in ordinary rubber compositions, such as vulcanization accelerator aid zinc oxide (zinc oxide), stearic acid, antioxidants, compatibilizers, workability improvers, lubricants, tackifiers, dispersants, homogenizers, and other various compounding agents that are generally compounded.

[0066] The antioxidant may be any known one and is not particularly limited, but examples thereof include phenol-based antioxidants, imidazole-based antioxidants, amine-based antioxidants, etc. The amount of these antioxidants to be added is usually 0.5 to 10 parts by mass, preferably 1 to 5 parts by mass, per 100 parts by mass of the rubber component.

[0067] [Method for producing rubber composition] In this way, the rubber composition of the present invention is obtained by kneading the above-mentioned components. The kneading method may be a method normally used by those skilled in the art. A kneading machine such as a roll, an internal mixer, or a Banbury rotor may be used for kneading. Furthermore, when molding into a sheet or strip, a known molding machine such as an extrusion molding machine or a press machine may be used. For example, all components other than sulfur, a vulcanization accelerator (and, if necessary, a vulcanization retarder), and zinc oxide may be kneaded at 100 to 200°C, and then sulfur, a vulcanization accelerator, and zinc oxide (and, if necessary, a vulcanization retarder) may be added, and the mixture may be kneaded at 60 to 130°C using a kneading roll machine or the like.

[0068] <Run-flat tires> The run-flat tire of the present invention uses the rubber composition of the present invention in at least one member selected from the group consisting of a side reinforcing rubber layer and a bead filler. An example of the structure of a run-flat tire having a side reinforcing rubber layer will be described below with reference to FIG. 1 is a schematic diagram showing a cross section of one embodiment of a run-flat tire of the present invention, and illustrates the arrangement of each member such as a bead filler 7 and a side reinforcing rubber layer 8. Note that a run-flat tire may be simply referred to as a tire.

[0069] In FIG. 1, a preferred embodiment of a tire of the present invention includes a carcass layer 2 consisting of at least one radial carcass ply that is connected in a toroidal shape between a pair of bead cores 1, 1' (1' is not shown) and has both ends wound up around the bead core 1 from the inside to the outside of the tire, a side rubber layer 3 that is disposed axially outward of the side region of the carcass layer 2 to form an outer portion, a tread rubber layer 4 that is disposed radially outward of the crown region of the carcass layer 2 to form a ground contact portion, and a reinforcing rubber layer that is disposed between the tread rubber layer 4 and the crown region of the carcass layer 2 to form a ground contact portion. The tire comprises a belt layer 5 forming a belt, an inner liner 6 arranged on the entire inner surface of the carcass layer 2 to form an airtight membrane, a bead filler 7 arranged between a main body portion of the carcass layer 2 extending from one bead core 1 to the other bead core 1' and a wound-up portion wound up around the bead core 1, and at least one side reinforcing rubber layer 8 having a substantially crescent-shaped cross section along the tire rotation axis, between the carcass layer 2 and the inner liner 6 from a side of the bead filler 7 in the side region of the carcass layer to a shoulder region 10. The run-flat tire of the present invention has excellent high-temperature softening suppression properties and, as a result, excellent run-flat durability, by using the rubber composition of the present invention in at least one member selected from the side reinforcing rubber layer 8 and the bead filler 7. The vulcanized rubber of the rubber composition of the present invention may be used in portions other than the bead filler 7 and the side reinforcing rubber layer 8, such as the tread rubber layer 4.

[0070] The carcass layer 2 of the tire of the present invention is composed of at least one carcass ply, but may be composed of two or more carcass plies. The reinforcing cord of the carcass ply may be arranged at an angle of substantially 90° with respect to the tire circumferential direction, and the end count of the reinforcing cord may be 35 to 65 cords / 50 mm. The belt layer 5, which is composed of two layers, a first belt layer 5a and a second belt layer 5b, is arranged on the tire radial outer side of the crown region of the carcass layer 2, but the number of the belt layers 5 is not limited to this. The first belt layer 5a and the second belt layer 5b may be formed by embedding a plurality of steel cords in rubber that are not twisted together and are aligned in parallel in the tire width direction. For example, the first belt layer 5a and the second belt layer 5b may be arranged so as to cross each other between the layers to form a cross belt.

[0071] Furthermore, in the tire of the present invention, a belt reinforcing layer (not shown) may be disposed on the tire radially outer side of the belt layer 5. The reinforcing cord of the belt reinforcing layer is intended to ensure tensile rigidity in the tire circumferential direction, and therefore it is preferable to use a cord made of a highly elastic organic fiber. As the organic fiber cord, organic fiber cords such as aromatic polyamide (aramid), polyethylene naphthalate (PEN), polyethylene terephthalate, rayon, Zylon (registered trademark) (polyparaphenylene benzobisoxazole (PBO) fiber), aliphatic polyamide (nylon), etc. can be used.

[0072] Furthermore, in the tire of the present invention, in addition to the side reinforcing layer, reinforcing members such as inserts and flippers (not shown) may be arranged. Here, the insert is a reinforcing material arranged in the tire circumferential direction from the bead portion to the side portion, in which a plurality of highly elastic organic fiber cords are arranged and rubber-coated (not shown). The flipper is a reinforcing material arranged between the main body portion of the carcass ply extending between the bead cores 1 or 1' and the folded-back portion folded back around the bead cores 1 or 1', in which a plurality of highly elastic organic fiber cords are arranged and rubber-coated, and which includes at least a part of the bead cores 1 or 1' and the bead fillers 7 arranged on the outer side of the bead cores 1 or 1' in the tire radial direction. The angle of the insert and the flipper is preferably 30 to 60° with respect to the circumferential direction.

[0073] The bead cores 1, 1' are embedded in the pair of bead portions, respectively, and the carcass layer 2 is folded back around the bead cores 1, 1' from the inside to the outside of the tire and secured thereto, but the method of securing the carcass layer 2 is not limited thereto. For example, at least one of the carcass plies constituting the carcass layer 2 may be folded back around the bead cores 1, 1' from the inside to the outside in the tire width direction, and the folded back end may be positioned between the belt layer 5 and the crown portion of the carcass layer 2, forming a so-called envelope structure. Furthermore, a tread pattern may be appropriately formed on the surface of the tread rubber layer 4, and an inner liner 6 may be formed on the innermost layer. In the tire of the present invention, the gas filled in the tire may be normal air or air with a changed oxygen partial pressure, or an inert gas such as nitrogen.

[0074] (Manufacturing method of run-flat tires) The run-flat tire of the present invention is produced by a normal run-flat tire production method using the vulcanized rubber of the rubber composition of the present invention for either or both of the bead filler 7 and the side reinforcing rubber layer 8. That is, the rubber composition containing various chemicals is processed into each component in the unvulcanized stage, and these are attached and molded in a tire building machine in a normal manner to form a green tire. This green tire is then heated and pressurized in the vulcanizer to obtain a run-flat tire. EXAMPLES

[0075] <Examples 1 to 5 and Comparative Examples 1 to 7> [Preparation of Rubber Composition] The rubber compositions of Examples 1, 3 to 5, and Comparative Examples 1 to 7 were prepared by kneading the components according to the compounding compositions shown in Tables 1 and 2 below. The rubber composition of Example 2 was also prepared by kneading the components according to the compounding compositions shown in Table 1. Note that Comparative Example 4 shown in Table 1 and Comparative Example 6 shown in Table 2 have the same rubber composition, but are given different numbers because the vulcanized rubber used in the fracture property (EB×TB) evaluation described below and the tire size used in the run-flat durability evaluation are different. The modified polybutadiene rubbers used in preparing the rubber compositions of Examples 1, 3 to 5, and Comparative Examples 1 to 7, and the modified polybutadiene rubber used in preparing the rubber composition of Example 2 were produced by the following method.

[0076] [Production of primary amine modified polybutadiene rubber P] (1) Production of unmodified polybutadiene In a nitrogen-substituted 5L autoclave, 1.4 kg of cyclohexane, 250 g of 1,3-butadiene, and 0.285 mmol of 2,2-ditetrahydrofurylpropane were poured as a cyclohexane solution under nitrogen, and 2.85 mmol of n-butyl lithium (BuLi) was added to the solution, followed by polymerization for 4.5 hours in a 50°C warm water bath equipped with a stirrer. The reaction conversion rate of 1,3-butadiene was nearly 100%. A part of the polymer solution was extracted into a methanol solution containing 1.3 g of 2,6-di-tert-butyl-p-cresol to terminate the polymerization, and the solvent was removed by steam stripping and dried with a roll at 110°C to obtain unmodified polybutadiene. The microstructure (vinyl bond amount) of the obtained unmodified polybutadiene was measured, and the vinyl bond amount was found to be 30% by mass.

[0077] (2) Manufacture of primary amine modified polybutadiene rubber P The polymer solution obtained in (1) above was kept at a temperature of 50°C without deactivating the polymerization catalyst, and 1,129 mg (3.364 mmol) of N,N-bis(trimethylsilyl)aminopropylmethyldiethoxysilane in which the primary amino group was protected was added to carry out a modification reaction for 15 minutes. Thereafter, 8.11 g of tetrakis(2-ethyl-1,3-hexanediolato)titanium, a condensation promoter, was added, and the mixture was stirred for an additional 15 minutes. Finally, 242 mg of silicon tetrachloride was added as a metal halide compound to the polymer solution after the reaction, and 2,6-di-tert-butyl-p-cresol was added. Next, the solvent was removed by steam stripping and the protected primary amino groups were deprotected, and the rubber was dried on a hot roll adjusted to 110°C to obtain primary amine-modified polybutadiene rubber P. The microstructure (vinyl bond content) of the resulting modified polybutadiene was measured, and the vinyl bond content was found to be 30% by mass.

[0078] The details of each component other than the modified polybutadiene rubber (primary amine-modified polybutadiene rubber P) are as follows. (1) Rubber component Natural rubber: RSS#1

[0079] (2) Filler Carbon black 1: Asahi Carbon Co., Ltd., product name "Asahi #52" [Nitrogen adsorption specific surface area: 28 m 2 / g, DBP oil absorption 128ml / 100g, toluene coloring transmittance = 65%] Carbon black 2: Asahi Carbon Co., Ltd., product name "Asahi #60" [Nitrogen adsorption specific surface area: 40 m 2 / g, DBP oil absorption 114ml / 100g, toluene coloring transmittance = 80%] Carbon black 3: Tokai Carbon Co., Ltd., product name "Seast FY" [Nitrogen adsorption specific surface area: 29 m 2 / g, DBP oil absorption 152ml / 100g, toluene coloring transparency = 80%] Carbon black 4: Cabot Corporation, product name "SP5000A" [Nitrogen adsorption specific surface area: 28 m 2 / g, DBP oil absorption 120ml / 100g, toluene coloring transparency = 99%]

[0080] (3) Resin Thermosetting resin: Phenolic resin, manufactured by Sumitomo Bakelite Co., Ltd., product name "Sumilite Resin PR-50731" Hardener: Hexamethoxymethylmelamine, Fujifilm Wako Pure Chemical Industries, Ltd.

[0081] (4) Vulcanization accelerators, vulcanizing agents, vulcanization retarders Vulcanization accelerator 1 (TOT): Tetrakis(2-ethylhexyl)thiuram disulfide, manufactured by Ouchi Shinko Chemical Industry Co., Ltd., product name "Noccela TOT-N" Vulcanization accelerator 2 (TBzTD): Tetrabenzyl thiuram disulfide, manufactured by Sanshin Chemical Industry Co., Ltd., product name "Suncerer TBzTD" Vulcanization accelerator 3 (NS): Nt-butyl-2-benzothiazylsulfenamide, manufactured by Ouchi Shinko Chemical Industry Co., Ltd., product name "Noccela NS" Vulcanization retarder (PVI): Monsanto's product name "Santoguard PVI" [N-(cyclohexylthio)-phthalimide] Sulfur: Tsurumi Chemical Industry Co., Ltd., product name "Powdered sulfur"

[0082] (5) Various ingredients Stearic acid: New Japan Chemical Co., Ltd., product name "Stearic acid 50S" Zinc oxide: Manufactured by Hakusui Tech Co., Ltd., product name "No. 3 zinc oxide" Antioxidant (6C): N-phenyl-N'-(1,3-dimethylbutyl)-p-phenylenediamine, manufactured by Ouchi Shinko Chemical Industry Co., Ltd., product name "Nocrac 6C"

[0083] [Manufacturing of run-flat tires, measurement and evaluation of physical properties of vulcanized rubber] (A) Manufacturing of size A tires The obtained rubber composition was disposed in the side reinforcing rubber layer 8 and the bead filler 7 shown in Fig. 1, and radial run-flat tires for passenger cars having a tire size of 255 / 65F18 (size A) were manufactured according to a standard method. The maximum thickness of the side reinforcing rubber layer of each prototype tire was 14.0 mm, and the shape of the side reinforcing rubber layer was the same for all of them.

[0084] (B) Manufacturing of size B tires The obtained rubber composition was disposed in the side reinforcing rubber layer 8 and the bead filler 7 shown in Fig. 1, and radial run-flat tires for passenger cars having a tire size of 235 / 65R17 (size B) were manufactured according to a standard method. The maximum thickness of the side reinforcing rubber layer of each prototype tire was 11.8 mm, and the shape of the side reinforcing rubber layer was the same for all of them.

[0085] 1.High temperature softening degree The dynamic tensile storage modulus E' of the vulcanized rubber obtained by vulcanizing the rubber compositions of Examples 1, 3 to 5, and Comparative Examples 1 to 7 was measured at 25°C to 180°C under conditions of an initial tensile strain of 5%, a dynamic tensile strain of 1%, and a frequency of 52 Hz. max ) and dynamic tensile storage modulus E' at 180°C (E' 180℃ ) and the difference (ΔE'=E' max -E' 180℃ ) was calculated as the high-temperature softening degree. The high-temperature softening degree ΔE' of each Example and Comparative Example shown in Tables 1 and 2 was indexed, assuming that the high-temperature softening degree ΔE' of Comparative Example 1 was 1.000. The smaller the high-temperature softening degree ΔE', the more difficult the vulcanized rubber is to soften at high temperatures and the more the mechanical strength is maintained.

[0086] The high-temperature softening degree evaluation of Example 2 is carried out as follows. The dynamic tensile storage modulus E' of the vulcanized rubber obtained by vulcanizing the rubber composition is measured at 25°C to 180°C under conditions of an initial tensile strain of 5%, a dynamic tensile strain of 1%, and a frequency of 52 Hz. max ) and dynamic tensile storage modulus E' at 180°C (E' 180℃ ) and the difference (ΔE'=E'max -E' 180℃ ) is calculated as the high temperature softening degree. The high temperature softening degree ΔE' of Comparative Example 1 is set as 1.000, and the high temperature softening degree ΔE' is indexed. The smaller the high temperature softening degree ΔE', the more difficult the vulcanized rubber is to soften at high temperatures and the more the mechanical strength is maintained.

[0087] 2. Run-flat durability In Examples 1, 4, and 5 and Comparative Examples 2 to 4 in Table 1, prototype tires of size A were used, and in Comparative Examples 6 and 7 in Table 2, prototype tires of size B were used. The tires were run on a drum (speed 80 km / h) without internal pressure, and the drum running distance until the tire became unable to run was recorded as the run-flat running distance. In Table 1 (Examples 1, 4, 5 and Comparative Examples 2 to 4), the run-flat mileage of the run-flat tire of Comparative Example 4 is expressed as an index, which is set to 100, and in Table 2 (Comparative Examples 6 and 7), the run-flat mileage of the run-flat tire of Comparative Example 6 is expressed as an index, which is set to 100. The higher the index, the better the run-flat durability of the run-flat tire. In addition, in Example 2, Example 3, Comparative Example 1 and Comparative Example 5, run-flat durability evaluation was not performed.

[0088] 3. Breakdown characteristics (EB×TB) In Examples 1, 3 to 5 and Comparative Examples 1 to 5 in Table 1, vulcanized rubber was prepared under vulcanization conditions of 145°C and 26 minutes. In Comparative Examples 6 and 7 in Table 2, vulcanized rubber was prepared under vulcanization conditions of 160°C and 12 minutes. Each vulcanized rubber was processed into a dumbbell-shaped No. 8 test piece, and the breaking elongation (EB) and tensile strength (TB) were determined using a tensile testing device (Shimadzu Corporation).

[0089] The breaking elongation (EB) was determined by pulling a test piece at 25°C at a rate of 100 mm / min, measuring the length at which the test piece broke, and calculating the length (unit: %) relative to the length before pulling (100%). The tensile strength (TB) was determined based on JIS K 6251 (2017) by pulling the test piece until it broke at a specified speed (500 ± 25 mm / min) at 25°C, and was calculated as the maximum tensile force (unit: MPa) required to break the test piece. In the examples and comparative examples, the breaking elongation (EB) (%) and the tensile strength (TB) (MPa) obtained were multiplied to calculate EB×TB.

[0090] In Table 1 (Examples 1, 3 to 5 and Comparative Examples 1 to 5), the EB×TB values ​​are expressed as indexes with the EB×TB value of Comparative Example 4 set to 100. In Table 2 (Comparative Examples 6 and 7), the EB×TB values ​​are expressed as indexes with the EB×TB value of Comparative Example 6 set to 100. The higher the index, the more excellent the fracture properties of the vulcanized rubber.

[0091] In Example 2 of Table 1, vulcanized rubber is prepared under vulcanization conditions of 145°C and 26 minutes. Each vulcanized rubber is processed into a dumbbell-shaped No. 8 test piece, and the breaking elongation (EB) and tensile strength (TB) are determined using a tensile testing device (Shimadzu Corporation).

[0092] The breaking elongation (EB) is determined by pulling a test piece at 25° C. at a rate of 100 mm / min, measuring the length at which the test piece breaks, and calculating the length (unit: %) relative to the length before pulling (100%). Tensile strength (TB) is determined based on JIS K 6251 (2017) by pulling a test piece at a specified speed (500±25mm / min) at 25°C until it breaks, and is calculated as the maximum tensile force (unit: MPa) required to break the test piece. The breaking elongation (EB) (%) is multiplied by the tensile strength (TB) (MPa) to calculate EB×TB.

[0093] The EB×TB value is expressed as an index, with the EB×TB value of Comparative Example 4 taken as 100. The larger the index, the more excellent the fracture properties of the vulcanized rubber.

[0094] [Table 1]

[0095] [Table 2]

[0096] From Tables 1 and 2, it can be seen that the rubber composition of the present invention, which contains 1.0 to 2.0 parts by mass of vulcanization accelerator 2 (tetrabenzyl thiuram disulfide) per 100 parts by mass of the rubber component and has a ratio (a / b) of 0.60 to 1.25, has a lower high-temperature softening degree of the vulcanized rubber than the comparative examples. This shows that the vulcanized rubber of the rubber composition of the present invention is less likely to soften at high temperatures and maintains its mechanical strength. In addition, the run-flat durability indexes of Examples 1, 4, and 5 exceed 100, so that tires using vulcanized rubber with a low high-temperature softening degree are excellent in run-flat durability. [Industrial Applicability]

[0097] The vulcanized rubber of the rubber composition of the present invention is resistant to softening at high temperatures and has excellent mechanical strength, and is therefore suitable for use in various tires, particularly in side reinforcing rubber and bead fillers of run-flat tires. [Explanation of symbols]

[0098] 1 Bead Core 2 Carcass layer 3 Side rubber layer 4 Tread rubber layer 5 Belt Layer 6 Inner Liner 7 Bead Filler 8 Side reinforcement rubber layer 10 Shoulder Area

Claims

1. A rubber component, A filler; A vulcanizing agent; a sulfenamide vulcanization accelerator and a vulcanization accelerator comprising 1.0 to 2.0 parts by mass of tetrabenzyl thiuram disulfide per 100 parts by mass of the rubber component, wherein a mass ratio (a / b) of a content of the tetrabenzyl thiuram disulfide (a) to a content of the sulfenamide vulcanization accelerator (b) is 0.60 to 1.25, The rubber composition includes a modified polybutadiene rubber, A rubber composition comprising a vulcanization accelerator having a total content less than a total content of the vulcanizing agents.

2. The rubber composition according to claim 1, wherein the mass ratio (a / c) of the content (a) of the tetrabenzyl thiuram disulfide to the content (c) of the vulcanizing agent is 0.22 to 0.

32.

3. The rubber composition according to claim 1 or 2, wherein the mass ratio (d / c) of the total content (d) of the vulcanization accelerator to the total content (c) of the vulcanizing agent is 0.55 to 0.

99.

4. The filler has a nitrogen adsorption specific surface area of ​​15 to 39 m ２ The rubber composition according to any one of claims 1 to 3, further comprising carbon black having a molecular weight of 1 / g.

5. The rubber composition according to any one of claims 1 to 4, wherein the filler contains carbon black having a DBP oil absorption of 120 to 180 mL / 100 g.

6. The rubber composition according to any one of claims 1 to 5, wherein a total content of the softener and the thermosetting resin is 5 parts by mass or less based on 100 parts by mass of the rubber component.

7. The rubber composition according to any one of claims 1 to 6, wherein a total content of the softener and the thermosetting resin is 1 part by mass or less based on 100 parts by mass of the rubber component.

8. A run-flat tire comprising the rubber composition according to any one of claims 1 to 7, which is used in at least one member selected from the group consisting of a side reinforcing rubber layer and a bead filler.