Abstract

To provide a process for reducing the content of oxygen in metallic copper.SOLUTION: The content of oxygen in molten metallic copper is reduced during the copper refining process by adding pure carbon monoxide, produced by electrolysis of carbon dioxide in a solid oxide electrolysis cell (SOEC), thereby removing oxygen through the reduction of CuO to Cu. In this way, the purity of the metallic copper is increased.SELECTED DRAWING: None

Description

[Technical field]

[0001] The present invention relates to a method for reducing the oxygen content in metallic copper. More specifically, the present invention deals with the reduction of the oxygen content in metallic copper using carbon monoxide. [Background technology]

[0002] Metallic copper is prepared industrially in a variety of ways. Copper ore, which usually contains only 1%-2% copper, is concentrated to 20-40% copper, then typically first roasted to remove some of the sulfur and other impurities, and then smelted with iron oxide to produce copper matte, a molten solution of copper sulfide mixed with small amounts of iron sulfide. The matte is transferred to a converter, where it is processed by blowing air through it to remove the sulfur (as sulfur dioxide) and iron (as a slag of ferrous oxide). The resulting copper is 98%-99% pure. It is referred to as blistered copper because its surface is blistered by the escape of gases as the metal solidifies during casting.

[0003] Most copper is further refined by electrolysis. Blister copper is smelted in furnaces and cast into anodes. Thin sheets of pure copper are used as the cathode. A solution of copper sulfide and sulfuric acid is used as the electrolyte. The anode and cathode are immersed in the electrolyte and an electric current is passed through them, causing the anode to dissolve in the electrolyte and ultra-pure copper metal to be deposited on the cathode. Soluble impurities, usually nickel and arsenic, remain dissolved in the electrolyte. Insoluble impurities, often including silver, gold and other precious metals, precipitate from the electrolyte. These can be recovered and purified.

[0004] Most metals find their main industrial application in the form of alloys, but this is not the case for copper, and there are only a few prior art documents disclosed on copper alloys. Thus, WO 2004 / 087976 (Patent Document 1), US 2004 / 0096353 (Patent Document 2) and China Patent No. 1628924 (Patent Document 3) deal with Cu alloys with Mg, Sn and Ag, respectively.

[0005] Metallic copper is most widely used as a conductor and in heating or cooling radiators, both of which require high conductivity, electrical conductivity in conductors and thermal conductivity in heating or cooling radiators, as well as very high purity. Commercial production of pure copper poses numerous metallurgical problems. Electrolytic refining reduces the metallic impurity content in copper to an acceptable low level, leaving oxygen (which is inevitably introduced during melting of the cathode copper) as the main impurity in the metal. Oxygen-free copper can be produced by adding phosphorus to the liquid metal, but the residual phosphorus content usually reduces the conductivity of the metal below that required for electrical applications. Oxygen-free high conductivity (OFHC) copper is melted and cast under a carbon monoxide atmosphere and is used in a variety of electrical applications. The refining of copper and the process for producing oxygen-free copper are well disclosed in U.S. Pat. No. 3,281,236 (Patent Document 4), U.S. Pat. No. 2,479,311 (Patent Document 5), U.S. Pat. No. 3,528,803 (Patent Document 6), U.S. Pat. No. 4,118,256 (Patent Document 7), U.S. Pat. No. 4,059,437 (Patent Document 8), U.S. Pat. No. 4,814,235 (Patent Document 9), China Patent No. 102994786 (Patent Document 10) and WO 2006 / 029162 (Patent Document 11), the latter of which deals with a continuous pyrometallurgical refining process for copper.

[0006] The exact method of copper smelting depends on the type of mineral it is bound to: copper ores high in sulfur are processed by pyrometallurgy, while copper ores high in oxygen are refined by hydrometallurgy.

[0007] In pyrometallurgy, the concentrate is dried and then heated in a furnace. Chemical reactions that occur during the heat treatment separate the copper concentrate into two layers of material: a matte layer and a slag layer. The lower matte layer contains the copper, and the upper slag layer contains the impurities.

[0008] The slag is discarded and the matte is collected and transferred to a cylindrical converter. Various chemicals are added to the converter and these react with the copper. The result is the converted copper, the blister copper mentioned above. The blister copper is collected and then pyrometallurgically refined.

[0009] In the hydrometallurgical process, copper oxide ore is leached with sulfuric acid, after which the metal can be further refined by one of several methods.

[0010] A much less common method is cementation, where an acidic solution of copper is deposited on the scrap iron in an oxidation-reduction reaction. Once a sufficient amount of copper has been plated, the copper is then further refined.

[0011] The more commonly used refining processes are solvent extraction and electrowinning. This new technology became widely adopted in the 1980s, and about 20% of the world's copper is produced this way.

[0012] Solvent extraction begins with an organic solvent that separates the copper from impurities and unwanted materials. Sulfuric acid is then added to strip the copper from the organic solvent and produce the electrolyte.

[0013] This solution is then subjected to an electrowinning process which simply plates the copper in the solution onto a cathode which can be sold as is or made into rods or seed plates for use in other electrolytic cells.

[0014] In pyrometallurgy, air and natural gas are blown through the copper to remove any remaining sulfur and oxygen, leaving refined copper for processing into copper cathodes.

[0015] This copper is cast into copper anodes and placed in an electrolytic cell. Once charged, pure copper accumulates on the cathode and is removed as a 99% pure product.

[0016] Two chemical reactions are involved in the refining of copper: sulfur removal and oxygen removal. The oxygen concentration in freshly desulfurized molten copper is about 0.3% by mass. Most of this dissolved oxygen precipitates as solid Cu2O inclusions during casting and must therefore be removed to low levels.

[0017] Copper oxide precipitation is minimized by removing most of the oxygen from the molten Cu with injected gas or liquid hydrocarbons. The typical reaction for removing dissolved oxygen is: H2C(s,l,g)+2|O|→H2O(g)+CO(g)(1) CO(g) + |O| → CO2(g)(2) H2(g) + |O| → H2O(g)(3) and Reaction (2) is particularly suitable for the present invention.

[0018] The presence of oxygen as an impurity in copper poses two problems in terms of the mechanical properties of the metal: if the metal is heated in an atmosphere containing hydrogen, the ductility decreases slightly and embrittlement can result.

[0019] In his 1922 paper "The Reduction of Copper Oxide by Carbon Monoxide and the Catalytic Oxidation of Carbon Monoxide in the Presence of Copper and Copper Oxide" (Non-Patent Document 1), Howard A. Jones showed that the reduction of CuO by CO is an autocatalytic process with elemental copper being the autocatalyst, that the mechanism of the combination of carbon monoxide-oxygen mixture on copper oxide is the alternate reduction and oxidation of copper oxide, and that the two-phase (Cu / CuO) interface plays an important role in the reduction of CuO by CO. The end result is the reaction CuO+CO→Cu+CO2 It is.

[0020] Carbon monoxide (CO) is therefore used in the copper industry as an effective agent to reduce the oxygen content in copper and obtain higher grades of material. In many industries, coke or hydrocarbon fuels, such as diesel, are added to copper during smelting to reduce the oxygen content. However, all these solutions imply the introduction of other components in addition to CO, such as hydrogen and coke due to incomplete oxidation of the hydrocarbons, as well as sulfur and water. Furthermore, if diesel fuel is added to the furnace, small amounts of nitrogen impurities (approximately the same level as sulfur, depending on the quality of the diesel) can also be expected.

[0021] Kang et al., Transactions of the Indian Institute of Metals, Vol. 67(5), pp. 617-622 (2014) (Non-Patent Document 2) studied the deoxidation of molten copper by CO gas bubbling to produce oxygen-free copper. Pure (about 99.9%) copper samples were melted by induction melting under an argon atmosphere. Once the sample was completely melted, CO gas was introduced into the melt to deoxidize it. The oxygen concentration in the melt was reduced to less than 6 ppm.

[0022] The use of pure CO to reduce the oxygen content in copper has several advantages. One important advantage is that hydrogen, which would otherwise promote embrittlement of the produced copper, is avoided. Many copper smelting plants currently in operation purposefully use high purity CO from cylinders or tube trailers to avoid hydrogen and other harmful impurities.

[0023] The production of carbon monoxide (CO) by electrolysis of carbon dioxide (CO2) has inherent advantages and this method is surprisingly suitable for obtaining CO to reduce the oxygen content in copper. In WO 2014 / 154253, the applicant disclosed a method carried out in a solid oxide electrolysis cell (SOEC) or in a SOEC stack consisting of many solid oxide cells typically separated by interconnects. The main element in the cell is the electrolyte, i.e. the current (e -) can dissociate oxygen ions from H2O or CO2. CO2+2e - →CO+O 2- or H2O+2e - →H2+O 2-

[0024] In the method, CO2 is conducted to the fuel side of the stack by an applied current, excess oxygen is transported to the oxygen side of the stack, the oxygen side is optionally flushed with air or nitrogen, and the product stream from the SOEC containing CO mixed with CO2 is subjected to a separation process. The method further includes heating the inlet gases of both the fuel side and the oxygen side by separate heating units to supply heat to the SOEC, where the operating temperature of said heating units is at least equal to the operating temperature of the cell stack -50°C, and preferably at least equal to the operating temperature of the cell stack. The production of high purity CO based on SOEC electrolysis of CO2 in combination with a high purity CO2 feedstock is disclosed in WO2013 / 131778 (Patent Document 13), also belonging to the present applicant.

[0025] Thus, according to the Applicant's above mentioned international publication, CO is produced from high purity CO2 (food or beverage grade) and electricity. The resulting gas is a pure mixture of CO and CO2, the only source of undesirable impurities being the traces of hydrocarbons and water present in the CO2 feed. These traces are converted into traces of hydrogen.

[0026] In plants for the production of high purity CO based on SOEC electrolysis of CO, feed CO is converted to a mixture of CO and CO. The product gas is then typically further purified by a series of processing unit operations, the most common of which consists in compression of the product mixture from electrolysis, followed by a pressure swing adsorption (PSA) step, and for high purity CO a polishing step with applied temperature swing adsorption (TSA). [Prior art documents] [Patent documents]

[0027]

Patent Document 1

Patent document 2

Patent document 3

Patent document 4

Patent document 5

Patent document 6

Patent document 7

Patent document 8

Patent Document 9

Patent document 10

Patent document 11

Patent document 12

Patent document 13

Non-licensed literature

[0028] [Non-licensed document 1] Howard A. Jones, "The Reduction of Copper Oxide by Carbon Monoxide and the Catalytic Oxidation of Carbon Monoxide in the Presence of Copper and Copper Oxide," 1992

Non-licensed Document 2

[0029] However, importantly, in the case of oxygen removal from copper, further removal of CO2 from the gases produced in the electrolysis step is completely unnecessary, as CO2 is inert to the copper smelting process. This means that the mixture of CO and CO2 obtained by electrolysis of CO2 can be fed directly to the copper smelting process, which significantly reduces the cost and complexity of the CO generation plant. [Means for solving the problem]

[0030] The present invention therefore relates to a method for reducing the content of oxygen present as copper oxide in molten metallic copper, obtained in a manner known per se and subjected to a copper smelting process, comprising the steps of: Carbon monoxide, which is produced from carbon dioxide in a solid oxide fuel cell (SOEC) stack, is added to the refining process to produce the product CuO+CO→Cu+CO2 and thereby increasing the purity of the copper metal. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0031] Preferably, the product gas from the SOEC stack is compressed and added to the copper melt through an injection system that distributes the reducing gas in the form of small bubbles throughout the copper melt. In this way, the gas / solid contact surface is maximized.

[0032] It is also preferred that the gas from the SOEC stack be purified to greater than 99% pure carbon monoxide and mixed with nitrogen before being injected into the copper melt.

[0033] Preferably, the product gas from the SOEC stack contains at least 10% CO, with the remainder being CO2 or inert gases. The amount of CO in the product gas may of course be higher, such as 20%, 30%, 40% or more.

Claims

1. 1. A method for reducing the content of oxygen present as copper oxide in molten metallic copper obtained in a manner known per se and subjected to a copper smelting process, comprising the steps of: CO ２ to a solid oxide electrolysis cell (SOEC) stack to produce a product gas comprising carbon monoxide and carbon dioxide; adding said product gas directly to a refining process and removing oxygen from the molten copper metal with CO; The method thereby increases the purity of metallic copper.

2. 1. A method for reducing the content of oxygen present as copper oxide in molten metallic copper obtained in a manner known per se and subjected to a copper smelting process, comprising the steps of: adding carbon monoxide produced from electrolysis of carbon dioxide in a solid oxide electrolysis cell (SOEC) stack into the smelting process to remove oxygen; This increases the purity of the metallic copper, CO is high purity CO ２ It is produced from CO and CO ２ A pure mixture of CO ２ CO and CO obtained by electrolysis of ２ The mixture of the above can be fed directly to a copper smelting process.

3. 3. The method according to claim 1 or 2, wherein the gas from the SOEC stack is compressed and added to the copper melt through an injection system.

4. The gas from the SOEC stack contains at least 10% CO, the remainder being CO ２ The method according to claim 1 or 2, wherein the gas is an inert gas.

5. The gas from the SOEC stack contains at least 20% CO, the remainder being CO ２ or an inert gas.

6. The gas from the SOEC stack contains at least 30% CO, the remainder being CO ２ or an inert gas.

7. The gas from the SOEC stack contains at least 40% CO, the remainder being CO ２ or an inert gas.

8. Product gas produced from solid oxide electrolysis cell (SOEC) stack 1. Use of a copper smelter for reducing the content of oxygen present as copper oxide in molten metallic copper obtained in a manner known per se and subjected to a copper smelting process, comprising: CO ２ to a solid oxide electrolysis cell (SOEC) stack to produce a product gas comprising carbon monoxide and carbon dioxide; The product gas is directly added to a refining process, and oxygen is removed from the molten copper metal by CO, thereby increasing the purity of the copper metal.