Compositions and methods for multilayer electrode films

Abstract

To provide energy storage device electrode films comprising multiple active layers, and methods of forming such multiple active layer energy storage device electrode films.SOLUTION: In an energy storage device, each active layer may be a self-supporting active layer comprising a binder and an active material. The binder and / or active material may be the same as or different from any other active layer. The active layers may be stacked to form an electrode film, and the electrode film may be laminated to a current collector to form an electrode.SELECTED DRAWING: Figure 2A

Description

[Technical field]

[0001] This application claims the benefit of priority to U.S. Provisional Application No. 62 / 580,956, filed November 2, 2017, and entitled “Compositions and Methods for Multilayer Electrode Films,” the disclosure of which is incorporated herein in its entirety.

[0002] The present invention relates generally to energy storage devices, and more particularly to materials and methods for multilayer electrode films. [Background technology]

[0003] Electrical energy storage batteries are widely used to power electronic, electromechanical, electrochemical and other useful devices. Such batteries include batteries, such as primary chemical cells and secondary (rechargeable) cells, fuel cells and various types of capacitors, including ultracapacitors. Increasing the operating power and energy of energy storage devices, such as capacitors and batteries, is desirable to increase energy storage performance, improve power performance and broaden practical use cases. Summary of the Invention [Problem to be solved by the invention]

[0004] Electrode films that combine complementary attributes can improve the performance of energy storage devices in practical applications. Furthermore, existing fabrication methods can impose practical limitations on various structural electrode properties. Therefore, new methods for fabricating electrode films with improved mechanical properties and improved performance are desirable. [Means for solving the problem]

[0005] For purposes of summarizing the invention and the advantages achieved over the prior art, certain objects of the invention and its advantages are described herein. Not all such objects or advantages may be achieved in a particular embodiment of the invention. Thus, for example, one skilled in the art will recognize that the invention can be embodied or practiced in a manner that achieves or optimizes one or a group of advantages taught herein without necessarily achieving other objects or advantages taught or suggested herein.

[0006] In a first aspect, a self-supporting electrode film is provided, the electrode film comprising two or more stacked active layers. In some embodiments, the self-supporting electrode film comprises a first active layer and a second active layer, the first active layer and the second active layer having different compositions relative to each other. In further embodiments, the first active layer and the second active layer are each self-supporting films. In yet another embodiment, the first active layer and the second active layer comprise different active material compositions and / or binder material compositions. In some embodiments, the electrode film is adhered to a current collector to form an electrode. In some embodiments, no separate adhesive layer is provided between the active layers of the multilayer electrode film and / or between the multilayer electrode film and the current collector.

[0007] In another aspect, a multilayer electrode film is provided. In some embodiments, the multilayer electrode film comprises a first active layer having a first active material and a first binder. In some embodiments, the multilayer electrode film comprises a second active layer having a second active material and a second binder. In some embodiments, the first and second active layers are stacked to form the multilayer electrode film. In some embodiments, the multilayer electrode film is a free-standing film.

[0008] In another aspect, a multi-layer electrode is provided. In some embodiments, the multi-layer electrode comprises a current collector having a first side and a second side. In some embodiments, the multi-layer electrode comprises a first multi-layer electrode film laminated to the first side of the current collector.

[0009] In another aspect, a double-sided multilayer electrode is provided. In some embodiments, the double-sided multilayer electrode comprises a first multilayer electrode film. In some embodiments, the double-sided multilayer electrode comprises a second multilayer electrode film laminated to a second surface of the current collector.

[0010] In another aspect, a method of making a multi-layer electrode is provided. In some embodiments, the method includes providing a first active layer having a first active material and a first binder, the first active layer being a free-standing film. In some embodiments, the method includes providing a second active layer having a second active material and a second binder, the second active layer being a free-standing film. In some embodiments, the method includes laminating the first active layer to the second active layer to form a multi-layer electrode film, the multi-layer electrode film being a free-standing film.

[0011] In another aspect, a method of making a multi-layer electrode is provided. In some embodiments, the method includes making a first multi-layer electrode film. In some embodiments, the method includes providing a current collector having a first side and a second side. In some embodiments, the method includes laminating the first multi-layer electrode film to the first side of the current collector to form a multi-layer electrode.

[0012] In another aspect, a method of making a multi-layer electrode is provided. In some embodiments, the method includes providing a first active layer having a first active material and a second binder, the first active layer being a free-standing film. In some embodiments, the method includes providing a second active layer having a second active material and a second binder, the first active layer being a free-standing film. In some embodiments, the method includes providing a current collector. In some embodiments, the method includes laminating the first active layer to the second active layer. In some embodiments, the method includes laminating the first active layer to the current collector.

[0013] All of these embodiments are intended to be within the scope of the invention disclosed herein. These and other embodiments of the invention will become readily apparent to those skilled in the art from the following detailed description of the preferred embodiments, taken in conjunction with the accompanying drawings, and the invention is not limited to the specific preferred embodiments disclosed. [Brief description of the drawings]

[0014] [Figure 1] FIG. 1 illustrates an embodiment of an energy storage device. [Figure 2A] Figures 2A and 2B show multi-layer (1 to n layers) membrane structures incorporated into an electrode: Figure 2A shows a single-sided electrode with n (3 or more) active layers in the electrode membrane; [Figure 2B] Figure 2B shows a double-sided electrode with n (three or more) active layers on each electrode film, where the active layers on both sides of the current collector have the same composition and order. [Figure 3A] Figures 3A and 3B show multilayer (1 to n and n-1 layers) membrane structures incorporated into electrodes. Figure 3A shows a double-sided electrode with n (3 or more) active layers in each electrode membrane. In Figure 3A, the active layers in the multilayer membranes on both sides of the current collector are in a different order from each other. [Figure 3B] FIG. 3B shows a double-sided electrode having n-1 (two or more) active layers in an electrode film on one side of a current collector and n (three or more) active layers in an electrode film on the opposite side. [Figure 4A] FIG. 4A shows the calendaring process for laminating the active layers together. [Figure 4B] FIG. 4B shows the calendaring process for laminating the multilayer film to the current collector. [Figure 5A] FIG. 5A shows the pressing process for laminating the active layers together. [Figure 5B] FIG. 5B shows the pressing process for laminating the multilayer film to the current collector. [Figure 6] FIG. 6 shows a flow chart illustrating a method for manufacturing the multilayer electrode film described herein. [Figure 7A]FIG. 7A shows the surface morphology of a 120 μm thick single layer graphite electrode. [Figure 7B] FIG. 7B shows the surface morphology of a three-layer graphite electrode film in which three identical active layers, each 120 μm thick, were calendered. [Figure 8A] FIG. 8A shows the capacitance of two single-layer graphite electrode films (layers 1 and 2) and a three-layer graphite electrode film (layer 121) of different compositions. [Figure 8B] FIG. 8B shows the efficiency of two single-layer graphite electrode films of different compositions (layers 1 and 2) and a three-layer graphite electrode film (layer 121). [Figure 9A] FIG. 9A shows the capacitance of the individual layers of graphite and a three-layer composite electrode (according to Example 1), where the electrode films are Layer A (Layer 1), Layer B (Layer 2) and a Si-C three-layer laminate electrode film (Layer 121). [Figure 9B] FIG. 9B shows the efficiency of the individual layers of graphite and a three-layer composite electrode (according to Example 1), where the electrode films are Layer A (Layer 1), Layer B (Layer 2) and a Si—C three-layer laminate electrode film (Layer 121). DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0015] As used herein, the terms "battery" and "capacitor" are given their ordinary and accustomed meaning to those of ordinary skill in the art. The terms "battery" and "capacitor" are not mutually exclusive. A capacitor or battery is a single electrochemical cell that operates alone or as a component of a multi-cell system.

[0016] As used herein, the voltage of an energy storage device is the operating voltage of a single battery or capacitor cell, which may be above the rated voltage, below the rated voltage under load, or may vary due to manufacturing tolerances.

[0017] As described herein, a "self-supporting" electrode film or active layer is one that incorporates a binder matrix structure sufficient to support the film or layer and maintain its shape such that the electrode film or layer is self-supporting. When incorporated into an energy storage device, a self-supporting electrode film or active layer is one that incorporates such a binder matrix structure. Typically, and depending on the method used, such an electrode film or active layer is strong enough to be used in the energy storage device manufacturing process without the use of external support elements such as current collectors or other films. For example, a "self-supporting" electrode film can be strong enough to be wound, handled, and unwound during the electrode manufacturing process without other support elements.

[0018] As described herein, a "solvent-free" electrode film is one that does not contain detectable process solvents, process solvent residues, or process solvent impurities. Process solvents or conventional solvents include organic solvents. Dry electrode films, such as cathode or anode electrode films, can be solvent-free.

[0019] A "wet" electrode or "wet process" electrode is an electrode that has been manufactured by at least one process that includes a slurry of active material, binder, and processing solvent, processing solvent residues, and / or processing solvent impurities. Wet electrodes may optionally contain additives.

[0020] Various embodiments are provided herein that incorporate an electrode film formed from multiple active layers. An electrode film used in an energy storage device may be fabricated from multiple active layers as provided herein. Additionally, the energy storage device may be constructed by a method of stacking multiple active layers to form an electrode film as provided herein.

[0021] Electrode membranes may degrade due to the mechanical properties of the membrane components and the interactions between them. For example, mechanical limitations may be due to poor adhesion between the active layer and the current collector, and poor bonding between the active layer and the binder. Such effects may lead to degraded performance in both power delivery and energy storage capacity. Without wishing to be bound by theory, it is believed that degraded performance may be due to deactivation of the active material, for example, due to loss of ionic conductivity, electrical conductivity, or a combination thereof. For example, cell resistance may increase as adhesion between the active layer and the current collector decreases. Degraded bonding between the active materials may lead to increased cell resistance and possibly loss of electrical contact, removing some active material from the ionic and electrical transfer cycle in the cell. Without wishing to be bound by theory, it is believed that volume changes in the active material contribute to such effects. For example, it may degrade further in electrodes incorporating certain active materials, such as silicon-based materials, that undergo significant volume changes during cell cycling. The lithium intercalation-deintercalation process may represent such a volume change in some systems. In general, these mechanical degradation processes may be observed in any electrode, e.g., positive or negative electrodes, or in battery electrodes, capacitor electrodes, hybrid electrodes, or energy storage devices. For example, in wet film formation processes such as spraying, slot die, extrusion, and printing, the substrate may limit the possible combinations of active layers in some circumstances.

[0022] Furthermore, wet processes can be limited in the choice of materials, and the resulting wet-processed electrode films can also have non-uniform distribution of constituent materials, e.g., active materials. The non-uniformity worsens as the film density increases, and can result in poor ionic and / or electrical conductivity. Wet processes also generally require costly and time-consuming drying steps, which become more difficult as the film becomes thicker. Thus, electrode films produced by wet processes also have thickness limitations.

[0023] Provided herein are multilayer electrode films incorporating two or more active layers. The active film may be a free-standing film that can be handled individually, with two or more active layers stacked together to form a single electrode film that is laminated to a current collector to form an electrode. Such multilayer electrode films and their associated processing techniques have been found to address some of the issues discussed above. For example, the order of the active layers may be selected such that the more adhesive film is adjacent to the current collector. As a further example, a less adhesive active layer may be sandwiched between more adhesive active layers, thereby reducing the effect of, for example, poor adhesion to the current collector. In some embodiments, the performance of the electrode film, e.g., power and / or energy performance, can be tailored by combining multiple active layers with selected properties. Advantageously, the multilayer films provided herein are cost-effective to manufacture. For example, unlike wet processes, each active layer can be designed and manufactured in parallel before assembling the final electrode film from the multiple active layers. Advantageously, electrode films with various active layers can be easily assembled and tested to find combinations with desired properties. In some cases, the active layers can be stacked in selected combinations to meet the demands of cost-effective, tailored applications.

[0024] The active films combined in the electrode film may be the same or different from each other. Advantageously, multiple stacked active layers of the same composition may allow for the production of thicker electrode films than those using conventional techniques. Advantageously, the active layers of the produced thickness may have fewer defects, e.g., non-uniformity, in the case of stacked electrode films rather than electrode films of the same composition formed as a single layer. Furthermore, some examples of multilayer electrode films with three identical active films will result in a denser electrode film compared to a conventional single layer electrode with the same material. In some embodiments, the multilayer electrode may have a similar active layer thickness. The electrode film has an improved pore structure on the surface of the electrode film compared to conventional electrode films of the composition and density. In some cases, it is more cost-effective to laminate active layers of the same composition into a single electrode film compared to forming the electrode film as a single layer. Thick electrode films are used, for example, in medical devices. Thus, the multilayer electrode films provided herein are suitable for use in medical devices.

[0025] Furthermore, the multilayer electrode films provided herein have been found to be superior to typical electrode films, e.g., electrode films having only a single layer or having substantially the same composition throughout. For example, active layers of different compositions are expected to have different electrical and ionic conductivities. Thus, the overall performance of the electrode film is improved by selecting a particular active layer according to its proximity to the current collector. Furthermore, active layers of different compositions are expected to have different energy and power performance characteristics. Combining high power and high energy active layers into a single electrode film is expected to provide each type of active layer.

[0026] Multilayer electrode films incorporating two or more active layers are generally fabricated by laminating at least one self-supporting dry electrode active layer to another active layer. In some embodiments, the active layers provided herein are structurally and / or functionally indistinguishable from an electrode film. Thus, each active layer may comprise an electrode active material and a binder. In some embodiments, each active layer is a self-supporting dry electrode active layer. The self-supporting active layers are fabricated using dry electrode fabrication techniques. Generally, the active electrode material and the binder are combined, ground, mixed, or otherwise processed to form an active layer mixture, and calendered or pressed to form the self-supporting active layer. In some embodiments, the binder is a fibrillizable polymer binder. In further embodiments, the binder includes or is based on PTFE. In further embodiments, no solvent is used at any stage of the electrode film fabrication.

[0027] Dry electrode fabrication is useful for fabricating multi-layer electrode films. Dry electrode fabrication can be self-supporting, for example, to form free-standing active layers. In general, these active layers can be combined as needed to achieve a set of desired operating characteristics. Thus, self-supporting active layers can be stacked without any restrictions as a method for fabricating individual active layers.

[0028] When the energy storage device includes a double-sided electrode, i.e., a current collector with an electrode film on both sides, the two electrode films may be of the same or different composition from each other.

[0029] In general, there is no limit to the active layers that can be combined in an electrode film. Thus, each active layer can have, for example, the same or different active material, the same or different binder, the same or different thickness, the same or different dimensions as another active layer in the same electrode film. In general, the number of active layers that can be combined in a single electrode film is not limited by fundamental physical properties such as compressibility or ionic and / or electrical conductivity, but is limited by the number of active layers in the electrode film of the energy storage device.

[0030] In some embodiments, each active layer of the multilayer electrode film provided herein comprises at least one active material and at least one binder. In further embodiments, each active layer of the multilayer electrode film provided herein is a self-supporting layer. The at least one active material can be any active material known in the art. The at least one active material may include, for example, a carbon material, such as a graphitic material, graphite, a graphene-containing material, activated carbon, hard carbon, soft carbon, and / or carbon nanotubes. The at least one active material may include, for example, a battery active material, such as a metal oxide, a metal sulfide, or a lithium metal oxide. For example, the battery active material may include a lithium metal oxide, a lithium metal sulfide, a lithium metal oxide ... The lithium metal oxide may include lithium nickel manganese cobalt oxide (NMC), lithium manganese oxide (LMO), lithium nickel manganese oxide (LNMO), lithium iron phosphate (LFP), lithium cobalt oxide (LCO), lithium titanate and / or lithium nickel cobalt aluminum oxide (NCA). The carbon may be porous carbon, graphite, conductive carbon or combinations thereof. The binder may be PTFE, polyolefin, poly(ethylene oxide) (PEO), styrene-butadiene, polyvinylidene chloride, polyvinylidene chloride (PVDC), polyvinyl chloride (PVC), poly(phenylene oxide) (PPO), polyethylene block-poly(ethylene glycol), polydimethylsiloxane (PDMS), polydimethylsiloxane-coalkylmethylsiloxane, copolymers thereof and / or mixtures thereof. In some embodiments, the one or more polyolefins may include polyethylene (PE), polypropylene (PP), polyvinylidene fluoride (PVDF), copolymers thereof, and / or mixtures thereof. The binder may include a cellulose, such as, for example, carboxymethyl cellulose (CMC). In certain embodiments, the binder includes or is based on PTFE. In some embodiments, the binder includes a fibrillizable polymer.

[0031] Multilayer electrode films incorporating two or more active layers as described herein can advantageously exhibit improved performance, e.g., coulombic efficiency, capacity, or conductivity, compared to those with only a single active layer.

[0032] The materials and methods provided herein can be implemented in a variety of energy storage devices. As provided herein, the energy storage device can be a capacitor, a lithium ion capacitor (LIC), an ultracapacitor, a battery, or a hybrid energy storage device combining two or more of the above aspects. In some embodiments, the device is a battery. The energy storage device can be characterized by an operating voltage. In some embodiments, the energy storage device described herein can have an operating voltage of about 2.2V to about 3.8V. In further embodiments, the operating voltage can be about 2.7V to about 3V, about 3.6V to about 3.7V, about 2.7V to about 4.2V, about 2.7V to about 4.3V, about 2.7V to about 4.4V, or any value selected therebetween. In some embodiments, the operating voltage can be about 2.7V, about 3V, about 3.6V, about 3.7V, about 4.2V, about 4.3V, about 4.4V, or about 4.5V, or any range of values ​​therebetween.

[0033] The energy storage device provided herein comprises one or more electrodes. The electrodes generally comprise an electrode film and a current collector. The electrode film can be composed of stacked active layers, each of which can be formed from an active layer mixture of one or more binders and one or more active electrode materials. It has been found that the electrode binders and electrodes comprising the binders provided herein can be used in various embodiments with any of a number of energy storage devices and systems, such as one or more batteries, capacitors, capacitor-battery hybrids, fuel cells or other energy storage systems or devices, and combinations thereof. In some embodiments, the active layer mixtures and electrodes made from the active layer mixtures described herein can be components of lithium ion capacitors, lithium ion batteries, ultracapacitors, or hybrid energy storage devices combining two or more of the above aspects.

[0034] The energy storage devices provided herein may be of any suitable shape, such as, for example, planar, spirally wound, button-shaped, or pouch-shaped. The energy storage devices provided herein may be used in, for example, power generation systems, uninterruptible power supply systems (UPS), solar It may also be a component of a system such as a power generation system, e.g., an energy recovery system for use in industrial machinery and / or transportation. The energy storage devices provided herein can be used to power a variety of electronic devices and / or automobiles, including hybrid electric vehicles (HEVs), plug-in hybrid electric vehicles (PHEVs) and / or electric vehicles (EVs).

[0035] The energy storage devices described herein are advantageously characterized by a reduced increase in equivalent series resistance over the life of the device, which can provide a device with increased power density over the life of the device. The energy storage devices described herein are advantageously characterized by a reduced increase in equivalent series resistance over the life of the device, which can provide a device with increased power density over the life of the device. In some embodiments, the energy storage devices described herein are characterized by a reduced loss in capacity over the life of the device. Further improvements that can be realized in various embodiments include improved cycling performance, including improved storage stability and reduced capacity fade during cycling.

[0036] 1 illustrates a cross-sectional schematic side view of an example energy storage device 100. Energy storage device 100 may be classified as, for example, a capacitor, a battery, a capacitor-battery hybrid, or a fuel cell.

[0037] The device can have a first electrode 102, a second electrode 104, and a separator 106 disposed between the first electrode 102 and the second electrode 104. The first electrode 102 and the second electrode 104 can be disposed adjacent opposing surfaces of the separator 106. The energy storage device 100 can include an electrolyte 118 to facilitate ionic communication between the electrodes 102, 104 of the energy storage device 100. For example, the electrolyte 118 can be in contact with the first electrode 102, the second electrode 104, and the separator 106. The electrolyte 118, the first electrode 102, the second electrode 104, and the separator 106 can be encased within a housing 120 of the energy storage device. One or more of the first electrode 102, the second electrode 104, and the separator 106, or components thereof, can include a porous material. The pores in the porous material can provide reduced and / or increased surface area for reactivity with the electrolyte 118 within the housing 120. The energy storage device housing 120 can be sealed around the first electrode 102, the second electrode 104, and the separator 106, and may be physically sealed from the surrounding environment.

[0038] In some embodiments, the first electrode 102 can be an anode (negative electrode) and the second electrode 104 can be a cathode (positive electrode). The separator 106 can be configured to electrically insulate two adjacent electrodes, such as the first electrode 102 and the second electrode 104, on opposite sides of the separator 106 while allowing ionic communication between the two adjacent electrodes. The separator 106 can include a suitable porous, electrically insulating material. In some embodiments, the separator 106 can include a polymeric material. For example, the separator 106 can include a cellulosic material (e.g., paper), a polyethylene (PE) material, a polypropylene (PP) material, and / or a polyethylene and polypropylene material.

[0039] Generally, the first electrode 102 and the second electrode 104 each include a current collector and an electrode film. The electrodes 102 and 104 each include an electrode film 112 and 114. The electrode films 112 and 114 can have any suitable shape, size, and thickness. For example, the electrode films can have a thickness of about 30 microns (μm) to about 250 microns, e.g., about 50 microns, about 100 microns, about 150 microns, about 200 microns, about 250 microns, or any range of values ​​therebetween. The electrode films generally include one or more active materials. In some embodiments, the electrode films 112 and 114 include a binder material. and an active layer including at least one active material. In some embodiments, the at least one active material can include a carbon-based material or a battery material. In some embodiments, the battery active material can include lithium metal oxide and / or lithium sulfide. In some embodiments, the battery active material can include lithium nickel manganese cobalt oxide (NMC), lithium manganese oxide (LMO), lithium nickel manganese oxide (LNMO), lithium iron phosphate (LFP), lithium cobalt oxide (LCO), lithium titanate, and / or lithium nickel cobalt cobalt oxide (NCA). The electrode films 112 and / or 114 can be multi-layer electrode films as provided herein and have beneficial properties such as beneficial thicknesses as provided herein. The first electrode 102 and / or the second electrode 104 can be double-sided electrodes as provided herein, each electrode including an electrode film on both sides of a current collector.

[0040] The carbon-based material can be selected from graphitic carbon, porous carbon, activated carbon, carbon black, conductive carbon, graphene-containing carbon, graphite, and combinations thereof. The activated carbon is obtained from a steam process or an acid / etch process. In some embodiments, the graphitic carbon can be a surface-treated carbon.

[0041] In some embodiments, the porous carbon may comprise activated carbon. In some embodiments, the porous carbon may comprise hierarchical carbon. In some embodiments, the porous carbon may comprise structured carbon nanotubes, structured carbon nanowires, and / or structured carbon nanosheets. In some embodiments, the porous carbon may comprise graphene sheets. In some embodiments, the porous carbon may be surface-treated carbon.

[0042] The first electrode film 112 and / or the second electrode film 114 may also include an active layer that includes one or more binders provided herein. In some embodiments, the binder may include one or more polymers. In some embodiments, the binder may include one or more fibrillizable binder components. The binder components may fibrillize to provide a multitude of fibrils that provide the desired mechanical support to one or more other components of the membrane. It is believed that the fibrils may form a matrix, lattice, or web to provide mechanical structure to the electrode membrane. In some embodiments, the binder components may include one or more of a variety of suitable fibrillizable polymeric materials.

[0043] In general, the active layer and / or electrode film described herein can be manufactured using a modified dry manufacturing process. For example, some steps provided herein may be as described in U.S. Patent Publication Nos. 2005 / 0266298 and 2006 / 0146479. These and other external documents described herein are incorporated herein by reference in their entirety. As used herein, a dry manufacturing process can refer to a process in which no or nearly no solvent is used in forming the electrode film. For example, the components of the active layer or electrode film, including the carbon material and binder, may include dry particles. The dry particles to form the active layer or electrode film can be combined to provide a dry particle active layer mixture. In some embodiments, the active layer or electrode film may be formed from a dry particle active layer mixture such that the weight percentages of the components of the active layer or electrode film and the weight percentages of the components of the dry particle active layer mixture are substantially the same. In some embodiments, the active layer or electrode film formed from the dry particle active layer mixture using a dry manufacturing process is free or substantially free of processing additives such as solvents and solvent residues resulting therefrom. In some embodiments, the resulting active layer or electrode film is a self-supporting film formed from the dry particle mixture using a dry process. In some embodiments, the resulting active layer or The electrode film is a free-standing film formed using a dry process from a dry particle mixture. The process for forming the active layer or electrode film may include fibrillating a fibrillizable binder component such that the film comprises a fibrillated binder. In a further embodiment, the free-standing active layer or electrode film may be formed in the absence of a current collector. In yet another embodiment, the active layer or electrode film may include a fibrillated polymer matrix such that the film is self-supporting.

[0044] As shown in FIG. 1, the first electrode 102 and the second electrode 104 each include a first current collector 108 in contact with the first electrode film 112 and a second current collector 110 in contact with the second electrode film 114. The first current collector 108 and the second current collector 110 can facilitate an electrical connection between each corresponding electrode film and an external electrical circuit (not shown). The first current collector 108 and / or the second current collector 110 can include one or more conductive materials and have any suitable shape and size selected to facilitate the transfer of charge between the corresponding electrode and the external electrical circuit. For example, the current collector can include metallic materials such as aluminum, nickel, copper, rhenium, niobium, tantalum, and materials including precious metals such as silver, gold, platinum, palladium, rhodium, osmium, iridium, and alloys and combinations thereof. For example, the first current collector 108 and / or the second current collector 110 can include aluminum foil. The aluminum foil can have a rectangular or nearly rectangular shape sized to provide for the transfer of charge between the corresponding electrodes and an external electrical circuit.

[0045] In some embodiments, the cathode electrode film of the lithium ion battery or hybrid energy storage device may comprise at least one active material at about 70% to about 95% by weight, including about 70% to about 92% by weight, or about 70% to about 88% by weight. In some embodiments, the cathode electrode film may comprise a porous carbon material at about 5% by weight, or about 1% to about 5% by weight, including about 1% to about 5% by weight. In some embodiments, the cathode electrode film comprises a conductive additive at about 5% by weight, including about 1% to about 3% by weight. In some embodiments, the cathode electrode film comprises a binder at about 20% by weight, including about 1.5% to 10% by weight, about 1.5% to 5% by weight, or about 1.5% to 3% by weight. In some embodiments, the cathode electrode film comprises a binder at about 1.5% to about 3% by weight.

[0046] In some embodiments, the anode electrode film can include at least one active material, a binder, and an optional conductive additive. In some embodiments, the conductive additive can include a conductive carbon additive, such as carbon black. In some embodiments, the at least one active material of the anode can include synthetic graphite, natural graphite, hard carbon, soft carbon, graphene, mesoporous carbon, silicon, silicon oxide, tin, tin oxide, germanium, lithium titanate, mixtures, or composites of the above materials. In some embodiments, the anode electrode film can include about 80% to about 94% by weight, including about 80% to about 92% by weight, or about 80% to about 90% by weight, of the at least one active material. In some embodiments, the anode electrode film includes up to about 5% by weight, including about 1% to about 3% by weight, of the conductive additive. In some embodiments, the anode electrode film comprises up to about 20% by weight of the binder, including about 1.5% to 10% by weight, about 1.5% to 5% by weight, or about 1.5% to 3% by weight. In some embodiments, the anode electrode film comprises about 1.5% to about 3% by weight of the binder. In some embodiments, the anode electrode film may be free of conductive additives.

[0047] Some embodiments include an electrode membrane, such as an anode and / or a cathode, having one or more active layers that include a polymer binder material. In some embodiments, the binder can include PTFE and optionally one or more additional binder components. In some embodiments, the binder may include one or more polyolefins and / or copolymers thereof, and PTFE. In some embodiments, the binder may include PTFE and one or more celluloses, polyolefins, polyethers, precursors of polyethers, polysiloxanes, copolymers thereof, and / or mixtures thereof. In some embodiments, the binder may include branched polyethers, polyvinyl ethers, copolymers thereof, and / or the like. The binder may include polysiloxanes and copolymers of polysiloxanes, and / or copolymers of polyether precursors. For example, the binder may include poly(ethylene oxide) (PEO), poly(phenylene oxide) (PPO), polyethylene block poly(ethylene glycol), polydimethylsiloxane (PDMS), polydimethylsiloxane-coalkylmethylsiloxane, copolymers thereof, and / or mixtures thereof. In some embodiments, the one or more polyolefins may include polyethylene (PE), polypropylene (PP), polyvinylidene fluoride (PVDF), copolymers thereof, and / or mixtures thereof. The binder may include a cellulose, such as carboxymethyl cellulose (CMC). The mixture of polymers may include an interpenetrating network of the aforementioned polymers or copolymers.

[0048] The binder may include various suitable ratios of the polymer components, for example, the PTFE may include up to about 98% by weight, including about 20% to about 80% by weight, about 30% to about 70% by weight, or about 30% to about 50% by weight, such as about 20% to about 95% by weight, about 20% to about 90% by weight.

[0049] In some embodiments, the at least one active material comprises a treated carbon material, the treated carbon material comprising a reduced number of hydrogen-containing, nitrogen-containing and / or oxygen-containing functional groups, as described in U.S. Patent Publication No. 2014 / 0098464. For example, the treated carbon particles may comprise a reduced number of one or more functional groups on one or more surfaces of the treated carbon, e.g., about 10% to about 60%, including about 20% to about 50%, of the one or more functional groups compared to an untreated carbon surface. The treated carbon may comprise a reduced number of hydrogen-containing, nitrogen-containing and / or oxygen-containing functional groups. The treated carbon may comprise a reduced number of hydrogen-containing, nitrogen-containing and / or oxygen-containing functional groups. In some embodiments, the treated carbon material comprises less than about 1%, including less than about 0.5%, of functional groups containing hydrogen. In some embodiments, the treated carbon material comprises less than about 0.5%, including less than about 0.1%, of functional groups containing nitrogen. In some embodiments, the treated carbon material contains less than about 5%, including less than about 3%, of oxygen-containing functional groups. In further embodiments, the treated carbon material contains about 30% fewer hydrogen-containing functional groups than the untreated carbon material.

[0050] The multi-layer electrodes described herein can be used separately or in combination in energy storage devices to enable operation under selected conditions.

[0051] Lithium-ion Energy Storage Device In some embodiments, the energy storage device 100 may be a lithium ion energy storage device, such as a lithium ion capacitor or a lithium ion battery. In some embodiments, an electrode film of an electrode of a lithium ion energy storage device can include one or more carbon materials and a fibrillated binder matrix provided herein.

[0052] In some embodiments, the electrode film of the anode of a lithium-ion battery or hybrid energy storage device can include an anode active material, such as an intercalation material (such as carbon, graphite, and / or graphene), alloy / non-alloy material, or a combination of both. The anode active materials may include metals (such as silicon, silicon oxide, tin, and / or tin oxide), metal alloys or compounds (such as Si-Al, and / or Si-Sn), and / or conversion materials (such as manganese oxide, molybdenum oxide, nickel oxide, and / or copper oxide). The anode active materials may be used alone or mixed to form multiphase materials (such as Si-C, Sn-C, SiOx-C, SnOx-C, Si-Sn, Si-SiOx, Sn-SnOx, Si-SiOx-C, Sn-SnOx-C, Si-Sn-C, SiOx-SnOx-C, Si-SiOx-Sn, or Sn-SiOx-SnOx).

[0053] In some embodiments, the electrode membrane of the cathode of a lithium ion battery or hybrid energy storage device can include a cathode active material, a binder, an optional porous carbon material, and an optional conductive additive. In some embodiments, the conductive additive can include a conductive carbon additive such as carbon black. In some embodiments, the porous carbon material can include activated carbon. In some embodiments, the cathode active material can include lithium metal oxide and / or lithium sulfide. In some embodiments, the cathode active material can include lithium nickel manganese cobalt oxide (NMC), lithium manganese oxide (LMO), lithium nickel manganese oxide (LNMO), lithium iron phosphate (LFP), lithium cobalt oxide (LCO), lithium titanate, and / or lithium nickel cobalt aluminum oxide (NCA). The cathode active material can include sulfur or a material containing sulfur, such as lithium sulfide (Li2S), or other sulfur-based materials, or mixtures thereof. In some embodiments, the cathode membrane includes a material including sulfur or a sulfur active material in a concentration of at least 50% by weight. In some embodiments, the cathode membrane comprising a material containing sulfur or a sulfur active material has a capacity of at least 10 mAh / cm 2 In some embodiments, the cathode membrane comprising a material comprising sulfur or a sulfur active material has an areal capacity of 1 g / cm 3 In some embodiments, the cathode membrane comprising a material comprising sulfur or a sulfur active material further comprises a binder. In some embodiments, the binder of the cathode membrane comprising a material comprising sulfur or a sulfur active material is selected from polytetrafluoroethylene (PTFE), polyvinylidene fluoride (PVDF), poly(ethylene oxide) (PEO), polyethylene (PE), polyacrylic acid (PAA), gelatin, other thermoplastic resins, or any combination thereof.

[0054] In some embodiments, the electrode film of the electrode of the lithium ion energy storage device includes an active material configured to reversibly intercalate lithium ions. In some embodiments, the lithium intercalation active material is graphite, hard carbon, and / or soft carbon. For example, the electrode film of the electrode can include a binder material, one or more of graphite, graphene-containing carbon, hard carbon, and soft carbon, and an electrical conduction facilitating material. In some embodiments, the electrode is pre-doped with lithium ions.

[0055] In further embodiments, the energy storage device 100 is charged with a suitable lithium-containing electrolyte. For example, the device 100 can include a lithium salt and a solvent, such as a non-aqueous or organic solvent. Generally, the lithium salt includes an anion that is redox stable. In some embodiments, the anion can be monovalent. In some embodiments, the lithium salt can be hexafluorophosphate (LiPF6), lithium tetrafluoroborate (LiBF4), lithium perchlorate (LiClO4), lithium bis(trifluoromethanesulfonyl)imide (LiN(SO2CF3)2), lithium trifluoromethanesulfonate (LiSO3CF3), lithium bis(pentafluoroethanesulfonyl)imide (CF4CF4), lithium ... 10 LiNO4S2) (LiBETI), lithium bis(fluorosulfonyl)imide (F2LiNO4S2) (LiFSI), and combinations thereof. In some embodiments, the electrolyte comprises a quaternary ammonium cation and The electrolyte may include an anion selected from the group consisting of hexafluorophosphate, tetrafluoroborate, and iodide. In some embodiments, the salt concentration may be about 0.1 mol / L (M) to about 5M, about 0.2M to about 3M, or about 0.3M to about 2M. In further embodiments, the electrolyte salt concentration may be about 0.7M to about 1M. In certain embodiments, the electrolyte salt concentration may be about 0.2M, about 0.3M, about 0.4M, about 0.5M, about 0.6M, about 0.7M, about 0.8M, about 0.9M, about 1M, about 1.1M, about 1.2M, about 1.3M, about 1.4M, about 1.5M, or any range of values ​​therebetween.

[0056] In some embodiments, the energy storage devices provided herein can include a liquid solvent. The solvents provided herein need not dissolve all components of the electrolyte, nor need to completely dissolve any components. In further embodiments, the solvent can be an organic solvent. In some embodiments, the solvent can include one or more functional groups selected from carbonates, ethers, and / or esters. In some embodiments, the solvent can include a carbonate. In further embodiments, the carbonate can be selected from cyclic carbonates, such as, for example, ethylene carbonate (EC), propylene carbonate (PC), vinyl ethylene carbonate (VEC), vinylene carbonate (VC), fluoroethylene carbonate (FEC), and combinations thereof, or acyclic carbonates, such as, for example, dimethyl carbonate (DMC), diethyl carbonate (DEC), ethyl methyl carbonate (EMC), and combinations thereof. In certain embodiments, the electrolyte can include LiPF6 and one or more carbonates.

[0057] In some embodiments, the energy storage device 100 is a lithium ion battery or a hybrid energy storage device that includes a cathode that includes at least one cathode active material. In some embodiments, the lithium ion battery is configured to operate at about 2 to 4.5 V, about 3 to 4 V, or about 3.6 to 3.7 V.

[0058] In some embodiments, the energy storage device is a battery comprising one or more multilayer electrodes as described herein and configured for operation at temperatures from -30°C to about 70°C, e.g., -30°C, -20°C, -10°C, 0°C, 10°C, 20°C, 30°C, 40°C, 50°C, 60°C, 70°C, or any range of values ​​therebetween. In some embodiments, the energy storage device is configured to operate at temperatures greater than 70°C.

[0059] Ultracapacitor In some embodiments, energy storage device 100 may be an ultracapacitor configured to operate at approximately 2.7V, 2.8V, 2.9V, 3V, or greater than 3V, or any range of values ​​therebetween.

[0060] The energy storage device 100 can be charged with any suitable electrolyte. For example, the device 100 can include a solvent and a salt including a cation and an anion. The cation can be a quaternary ammonium cation. In some embodiments, the quaternary ammonium cation can be selected from tetraalkylammonium. In some embodiments, the tetraalkylammonium cation can be selected from cyclic ammonium, such as, for example, spiro-(1,1')-bipyrrolidinium, and non-cyclic ammonium, such as, for example, triethylmethylammonium, triethylbenzylammonium, and tetraethylammonium. The quaternary ammonium salt can include an anion selected from the group consisting of hexafluorophosphate, tetrafluoroborate, and iodide. The cation of the electrolyte salt can include a symmetrical cation, such as, for example, the cation spiro-(1,1')-bipyrrolidinium. In some embodiments, In the present invention, the cation of the electrolyte salt can include an asymmetric cation, such as, for example, triethylmethylammonium. In some embodiments, the salt can include a spiro compound, such as, for example, a symmetric or asymmetric spiro compound. For example, the spiro compound can be an N-spiro bicyclic compound containing one or more 4-, 5-, 6-, or 7-membered rings. The symmetric spiro cation can be spiro-(1,1')-bipyrrolidinium tetrafluoroborate. In some embodiments, the salt can include an asymmetric spiro compound having unequal sized rings, or different substitutions on equal sized rings. In some embodiments, the salt concentration can be about 0.1 mol / L (M) to about 5M, about 0.2M to about 3M, or about 0.3M to about 2M. In further embodiments, the salt concentration of the electrolyte can be about 0.7M to about 1M. In certain embodiments, the electrolyte salt concentration may be about 0.2M, about 0.3M, about 0.4M, about 0.5M, about 0.6M, about 0.7M, about 0.8M, about 0.9M, about 1M, about 1.1M, about 1.2M, or any range of values ​​therebetween.

[0061] In some embodiments, the energy storage devices provided herein can include a liquid solvent. The solvents provided herein need not dissolve all components of the electrolyte, nor need to completely dissolve any components. In further embodiments, the solvent can be an organic solvent. In some embodiments, the solvent can include one or more functional groups selected from nitriles, carbonates, ethers, and / or esters. In some embodiments, the solvent can include a nitrile, such as, for example, acetonitrile. In some embodiments, the solvent can include a carbonate. In further embodiments, the carbonate can be selected from cyclic carbonates, such as, for example, ethylene carbonate (EC), propylene carbonate (PC), vinyl ethylene carbonate (VEC), vinylene carbonate (VC), and combinations thereof, or acyclic carbonates, such as, for example, dimethyl carbonate (DMC), diethyl carbonate (DEC), ethyl methyl carbonate (EMC), and combinations thereof. In certain embodiments, the electrolyte can include a quaternary ammonium salt and acetonitrile.

[0062] In a further embodiment, the ultracapacitor includes an electrolyte comprising a quaternary ammonium salt at a concentration of less than 1 Molar (M), as described in U.S. Patent Publication No. 2014 / 0104752, the entire contents of which are incorporated herein by reference. In yet another embodiment, the ultracapacitor includes a protective coating disposed on an inner surface of the housing, as described in U.S. Patent Publication No. 2014 / 0098463, the entire contents of which are incorporated herein by reference. In yet another embodiment, the ultracapacitor includes a positive electrode or a negative electrode comprising a carbon-based layer having a selected porosity, e.g., mesoporous or microporous, as described in U.S. Patent Publication No. 2014 / 0098465, the entire contents of which are incorporated herein by reference. In some embodiments, the ultracapacitor includes an amount of electrolyte selected to correspond to a saturation amount of a component of the ultracapacitor, as described in U.S. Patent Publication No. 2014 / 0368973, the entire contents of which are incorporated herein by reference.

[0063] In some embodiments, the energy storage device is an ultracapacitor including one or more multi-layer electrodes described herein configured to operate at 3 volts or greater. In further embodiments, the ultracapacitor is configured to operate at 2.7 volts or greater. In some embodiments, the ultracapacitor is configured to operate at selected conditions of voltage and temperature. For example, the ultracapacitor can be configured to operate at temperatures of 50° C., 55° C., 60° C., 65° C., 70° C., 75° C., 80° C., 85° C., 90° C., 95° C., 100° C., or greater, or any range of values ​​therebetween. The ultracapacitor can be configured to operate at temperatures of 2.7V (60 to 85° C.), 2.8V (60 to 85° C.), 3.0V (60 to 85° C.), 4.0V (60 to 85° C.), 5.0V (60 to 85° C.), 6.0V (60 to 85° C.), 7.0V (60 to 85° C.), 8.0V (60 to 85° C.), 9.0V (60 to 85° C.), 10.0V (60 to 85° C.), 10.0V (60 to 85° C.), 11.0V (60 to 85° C.), 12.0V (60 to 85° C.), 13.0V (60 to 85° C.), 14.0V (60 to 85° C.), 15.0V (60 to 85° C.), 16.0V (60 to 85° C.), 17.0V (60 to 85° C.), 18.0V ), 2.9V (60 to 85° C.), or 3V (60 to 85° C.), or any selected temperature value therebetween. In some embodiments, the voltage and temperature conditions are about 2.7V and about 85° C., about 2.8V and about 80° C., about 2.9V and about 75° C., about 3V and about 70° C., or about 3.1V and about 65° C. In some embodiments, the ultracapacitor is configured for an operating voltage of about 2.7 to 3 volts at a temperature of at least about 65° C. for at least about 500k cycles. In some embodiments, the ultracapacitor does not experience significant degradation of the electrodes after about 1500 hours of operation and / or at least 500k cycles, significance being determined by the intervention of deleterious effects necessitating operation below the rated conditions of the device.

[0064] The ultracapacitor may include one or more multi-layer electrodes, as described herein, to enable the ultracapacitor to maintain a capacitance greater than about 80% of the initial capacitance and / or less than 200% of the initial equivalent series resistance for about 1500 hours, at a voltage of about 2.7 to 3 volts, and / or for at least 500k cycles, and at a temperature of at least about 65° C. In other embodiments, the ultracapacitor is configured to maintain at least 75%, 85%, 90%, 95%, or 99% of the initial capacity when operated at about 65° C. or greater for at least 1500 hours and / or for at least 500k cycles.

[0065] multilayer electrode film Provided herein are compositions and methods for electrode films comprised of multiple active layers.

[0066] Various embodiments of the multilayer electrode films provided herein are presented in Figures 2A-2B and Figures 3A-3B. Figures 2A and 2B show multilayer (layer 1 to layer n) film structures incorporated into electrodes. Figure 2A shows a single-sided electrode containing at least three active layers in the electrode film, and Figure 2B shows a double-sided electrode containing at least three active layers in each electrode film. In Figure 2B, the active layers on both sides of the current collector have the same composition and order. Figure 2B shows a symmetric double-sided electrode containing a multilayer electrode film.

[0067] 3A and 3B show multilayer (layer 1 to layer n) membrane structures incorporated into electrodes. FIG. 3A shows a double-sided electrode including n layers, at least 3 layers of active layers in each electrode film. In FIG. 3A, the order of the active layers of the multilayer films on both sides of the current collector is different from each other. For example, the active layers directly adjacent to each corresponding side of the current collector of each corresponding multilayer film can have different compositions relative to each other. FIG. 3B shows a double-sided electrode including n-1 layers, at least 2 layers of active layers in the electrode film on one side of the current collector, and n layers, at least 3 layers of active layers in the electrode film on the opposite side. Thus, FIG. 3B shows a double-sided multilayer electrode with a first multilayer electrode film including a different number of layers from the second multilayer electrode film. FIG. 3A and 3B show an asymmetric double-sided electrode including a multilayer electrode film. It will be understood from the drawings that FIG. 2B, 3A, and 3B can be modified to include a different number of layers. For example, a multilayer electrode film shown to have three or more layers may have two or more layers. Some embodiments may have only a single (non-multilayer) active film on one side of the current collector and a multilayer film on the other side. Additionally, any of the layers shown may have the same or different composition relative to each other. For example, as shown in FIG. 2B, "layer 1" is depicted adjacent to the current collector, showing different layers on each side of the current collector, and the chemical composition of each layer 1 may be the same or different from the other. Also, bipolar multilayer configurations for use in bipolar energy storage device configurations, such as the embodiment shown in FIGS. 2B through 3B, are within the scope of the present invention as well. For example, layers 1, 2, and n shown above the current collector in FIG. 2B can be positive polarity, while layers 1, 2, and n shown below the current collector in FIG. 2B can be negative polarity, and vice versa, as well as for FIGS. 3A and 3B. In a bipolar energy storage device configuration, the cells are stacked in a sandwich configuration, so that the negative polarity of one cell is not affected by the other. The current collector of one cell is also used as the positive current collector of the next cell. In this way, the bifacial electrode is shared by two series-coupled electrochemical cells, with one side of the bifacial electrode acting as the anode of one cell and the other side of the bifacial electrode acting as the cathode of the next cell. The anode and cathode polarities of the bifacial electrode are separated by a current collector that acts as an electronically conducting membrane and a partition that acts as a series connection and prevents the flow of ions between the cells.

[0068] In general, the active layer may include one active material or may be a composite active layer including two or more active materials. For example, the composite active layer may include a high energy active material such as silicon along with a high power material such as carbon, such as graphite. For example, silicon may have about 4000 mA-h / g, or up to about 4200 mA-h / g, and graphite may have about 300 mA-h / g, or up to about 370 mA-h / g. These materials may be used in a multilayer electrode film in different ratios for the two different active layers, as further described herein. For example, the first layer may have increased silicon compared to the second layer for increased energy, and the second layer may have increased graphite compared to the first layer for increased power.

[0069] Generally, a multi-layer electrode film is made by stacking and / or laminating multiple active layers to form an electrode film, which can be laminated to a current collector. A self-supporting electrode film can be assembled from stacked active layers, for example, before being laminated to a current collector, or the active layers can be laminated to the current collector individually, in groups, and / or in sequence. For example, two active layers can be stacked to form a self-supporting electrode film, and the electrode film can be laminated to a current collector to form an electrode. Alternatively, or in addition, a single first active layer can be laminated to a current collector, and a second active layer can be laminated onto the first active layer to form an electrode film in contact with the current collector. Generally, the assembly steps described herein can be performed on a current collector of a double-sided electrode or a single-sided electrode. Thus, the lamination steps can be performed on a current collector in contact with one or more active layers or electrode films. The active layers or electrode films can be on the same side or on opposite sides of the current collector.

[0070] The multilayer electrode film can have a selected thickness suitable for a particular application. The thickness of the operable multilayer electrode film can be greater than the thickness of the electrode film prepared by conventional processes. In some embodiments, the multilayer electrode film can have a thickness of about 250 microns, about 300 microns, about 350 microns, about 400 microns, about 450 microns, about 500 microns, about 750 microns, or about 1 mm, or at least these values, or any range of values ​​therebetween. An electrode including one or more multilayer electrode films can have a thickness of about 500 microns, about 750 microns, or about 1 mm, or at least these values, or any range of values ​​therebetween.

[0071] The active layers provided herein can be made from two or more stacked identical or substantially identical active pre-layers. In some embodiments, the active pre-layer can be a free-standing, self-supporting film, as provided herein.

[0072] The multilayer electrode film may include, for example, a high-power active layer, a high-energy active layer, a high-load active layer, a hybrid active layer, or a combination thereof. The high-energy active layer may include an active material characterized by a relatively large capacity. The high-power active layer may include an active material characterized by a relatively large ejection performance. The high-load active layer may include a high content of active material in the active layer and / or a high load of active material in the electrode film compared to electrode films prepared using conventional materials and methods. The hybrid active layer may include two or more materials selected from high energy, high power, or high load. The high-power active material may include, for example, hard carbon. The high-energy active material may include, for example, Si or Si-C. The hybrid layer may include, for example, Sn, S It may include nC, Si, or Si-C.

[0073] In general, the stacking order of the active layers in the electrode film is not particularly limited, and the composition of any active layer may be the same or different from the composition of other active layers in the electrode film. Thus, a bilayer film of a current collector and two active layers A and B may have the following order: current collector-AB, or current collector-BA. Furthermore, active layers A and B may have the same or different compositions. A trilayer film of a current collector and three active layers A, B, and C may have the following order: current collector-ABC, current collector-ACB, current collector-BCA, current collector-BAC, current collector-CBA, or current collector-CAB. Furthermore, in each order of the active layers above, A may have the same or different composition as B or C, B may have the same or different composition as C or A, and C may have the same or different composition as A or B. In certain embodiments, A, B, and / or C may be selected from high-power active layers, high-energy active layers, high-load active layers, hybrid active layers, or combinations thereof.

[0074] Generally, each stacking and / or lamination step may be performed at a different temperature. In general, the compression ratio, the number of lamination iterations, and the lamination temperature also affect the properties of the final electrode film. For example, it is believed that the adhesion between layers is affected by the lamination temperature.

[0075] The active layer mixture can be processed by high shear and / or high pressure processes. High shear and / or high pressure processes can include jet milling, blending, etc. Processing time and / or feed rate generally affect the final particle size of the binder and / or active material. In some embodiments, the active layer and / or electrode film so formed is a self-supporting active layer and / or electrode film.

[0076] In some embodiments, the active layer mixture can include binder particles having a selected size. In some embodiments, the binder particles can be about 50 nm, about 100 nm, about 150 nm, about 200 nm, about 250 nm, about 300 nm, about 350 nm, about 400 nm, about 450 nm, about 500 nm, about 1 μm, about 5 μm, about 10 μm, about 50 μm, or any range of values ​​therebetween.

[0077] In some embodiments, the number of layers in a multi-layer electrode film may be selected from the desired thickness of the electrode film and the thickness of each active layer.

[0078] In some embodiments, the active layer mixture is subjected to one or more dry electrode processes, such as those described in U.S. Patent Publication No. 2015 / 0072234. In some embodiments, dry electrodes are provided, which are not treated with contaminants such as solvents, and thus are prepared by the methods and materials provided herein.

[0079] In some embodiments, electrodes manufactured using the materials and methods described herein can be characterized by improved performance. In further embodiments, the capacity of the multilayer electrode film including the first active layer and the second active layer is greater than either the first active layer or the second active layer, respectively. In further embodiments, the Coulombic efficiency of the multilayer electrode film including the first active layer and the second active layer is greater than either the first active layer or the second active layer, respectively.

[0080] In some embodiments, a method of manufacturing an energy storage device including a multilayer electrode film is provided. In further embodiments, the method includes stacking a first free-standing active layer and a second free-standing active layer to form a laminate, pressing or calendaring the laminate to form the multilayer electrode film, and optionally laminating the multilayer electrode film to a current collector to form an electrode. Methods of calendaring or pressing the stacked active layers to form an electrode film, and methods of laminating the stacked active layers to a current collector are generally known in the art.

[0081] Figure 4A shows a rolling process, such as a calendering process, for stacking the active layers on top of each other, and Figure 4B shows a rolling process, such as a calendering process, for laminating the multilayer film to a current collector.

[0082] Figure 5A shows the pressing process for stacking the active layers on top of each other, and Figure 5B shows the pressing process for laminating the multilayer film to the current collector.

[0083] In general, the process for producing the active layer is no different from the process for producing an electrode film using dry electrode manufacturing techniques. For example, such techniques may be as described in U.S. Patent Publication No. 2005 / 0266298 and / or U.S. Patent Publication No. 2006 / 0146479. These and other references to external documents herein are incorporated by reference in their entirety.

[0084] In some embodiments, a self-supporting electrode film is provided, the electrode film comprising stacked active layers as provided herein. In further embodiments, the first active layer and the second active layer are self-supporting films. In some further embodiments, the self-supporting electrode film comprises a first active layer and a second active layer, the first active layer and the second active layer having different compositions. In yet another embodiment, the first active layer and the second active layer comprise different active material compositions and / or binder material compositions.

[0085] FIG. 6 is a flow chart illustrating a method 200 for manufacturing a multilayer electrode film provided herein. In box 205, a first free-standing active layer is manufactured. The first free-standing active layer may be manufactured by any suitable method. In general, the manufacturing method may be a dry electrode manufacturing process. In general, the manufacturing method of the free-standing dry active layer is similar to the manufacturing method of the free-standing dry electrode film. In some embodiments, the first free-standing active layer may be a high energy layer, a high power layer, a high load layer, or a hybrid layer provided herein.

[0086] In box 210, a second free-standing active layer is fabricated. The second free-standing active layer may be fabricated by any suitable method. In general, the fabrication method may be a dry electrode fabrication process. The second free-standing active layer may be of the same or different composition as the first free-standing active layer. In some embodiments, the second free-standing active layer may be a high energy layer, a high power layer, a high load layer, or a hybrid layer provided herein.

[0087] In box 220, the first and second free-standing active layers are laminated. Lamination of the first layer to the second layer refers to adhering the layers to each other without an intervening layer between them that is used on the same side of the current collector of the electrode. Lamination may include laminating the first and second layers to each other. Lamination may include laminating one two layers to the other two layers without a current collector, or may include laminating the first layer to the second layer that is pre-laminated to the current collector in a separate step. Laminating the first and second free-standing active layers may include a calendaring or pressing step to adhere the two layers to each other. The combined multilayer film may have a thickness that is approximately the sum of the thicknesses of the two layers before lamination, or less than the sum of the thicknesses of the two layers.

[0088] In box 230, an electrode is formed from the stacked active layers. Forming the electrode can include laminating the stacked active layers formed in box 220 to a current collector. In some embodiments, forming the electrode from the stacked active layers can include laminating the stacked active layers to a current collector, including an adhesive layer. The method may include laminating the stacked active layers to a current collector, for example by gluing. In further embodiments, forming an electrode from the stacked active layers may include laminating the stacked active layers to a current collector without the use of an adhesive. In further embodiments, forming an electrode from the stacked active layers may include laminating the stacked active layers to a current collector using an adhesive. Method 200 may include additional steps of forming a third or more free-standing layers (such as steps 205 and 210) and / or laminating a third or more additional free-standing active layers (such as step 220). The final multi-layer electrode film may be formed upon completion of step 220 or, in the case of an electrode film having two or more layers, after the additional free-standing active layers have been laminated onto the first and second layers. In some embodiments, steps 220 and 230 may be completed simultaneously. For example, the first and second free-standing active layers may be formed in steps 205 and 210, and one of these two layers may then be attached to a current collector before performing the lamination step 220. The first and second layers, along with a current collector attached to one of the two layers, can then be laminated together to complete the lamination step 220 and electrode film formation step 230.

[0089] Example 1 The first free-standing single layer electrode film had a thickness of 120 μm and contained graphite as an active material and was fabricated by a typical dry electrode technique as a comparative sample. The second free-standing multilayer electrode film contained three identical active layers, each 120 μm thick and containing graphite active material, and was fabricated according to the present disclosure. SEM images of the first electrode film, as shown in FIG. 7A, and the second electrode film, as shown in FIG. 7B, were taken and show uniform surface morphology. As shown in FIGS. 7A and 7B, the multilayer electrode (FIG. 7B) shows open pores on the surface of the electrode film, which are important for wetting with liquid electrolyte and are expected to improve electrode performance. The conventional single layer electrode (FIG. 7A) had fewer pores on the surface, which is expected to limit the diffusion of electrolyte to the intermediate layer of the electrode film. The multilayer electrode film in FIG. 7B retained its density despite showing a desirable pore structure.

[0090] Example 2 Three graphite electrode films were prepared as follows: the first electrode film included graphite, 3 wt% CMC, and 3 wt% PTFE ("Layer 1"), and the second electrode film included graphite, 3 wt% polyvinyl chloride (PVC), and 3 wt% PTFE ("Layer 2"). A third multilayer electrode film was prepared containing three active layers in the following configuration: Layer 1-Layer 2-Layer 1 ("Layer 121"). The thicknesses of the electrode films Layer 1, Layer 2, and Layer 121 were 132 μm, 132 μm, and 256 μm, respectively. Figures 8A and 8B provide capacity and efficiency data measured for the Layer 1, Layer 2, and Layer 121 electrode films.

[0091] As seen in Figure 8A, layer 1 had a charge capacity of about 325 mAh / g and a discharge capacity of about 275 mAh / g, layer 2 had a charge capacity of about 350 mAh / g and a discharge capacity of about 300 mAh / g, and layer 121 had a charge capacity of about 400 mAh / g and a discharge capacity of about 350 mAh / g. As shown in Figure 8B, the efficiency of layer 1 was about 81.5%, the efficiency of layer 2 was about 83%, and the efficiency of layer 121 was about 85%.

[0092] Example 3 A self-supporting free-standing electrode film was fabricated according to the present disclosure. The Si-C three-layer electrode film was fabricated by fabricating two active layers, a first active layer and a second active layer. The first active layer (A) contained 94% graphite and 6% binder, and the second active layer (B) contained 89.5% graphite, 4.5% nano-sized silicon and 6% binder. The binder in each electrode film contained 3 wt% CMC and 3 wt% PTFE. Three identical pre-layers were stacked and calendared to form the first active layer. The electrode film was formed by stacking the second active layer (B) between two first active layers (A) with a thickness of 120 μm. Thus, the order of the active layers was ABA. The resulting stacked active layers were calendared to form an electrode film. Figures 9A and 9B provide capacity and efficiency data for the AB-A three-layer stacked electrode film of Example 3.

[0093] As shown in Figure 9A, it was found that the charge capacity of layer 1 was about 250mAh / g, the discharge capacity was about 200mAh / g, the charge capacity of layer 2 was about 350mAh / g, the discharge capacity was about 275mAh / g, and the charge capacity of layer 121 was about 375mAh / g, and the discharge capacity was about 300mAh / g. As shown in Figure 9B, it was found that the efficiency of layer 1 was about 83.5%, the efficiency of layer 2 was about 77.5%, and the efficiency of layer 121 was about 82%.

[0094] Although specific embodiments of the present invention have been described, these embodiments are presented by way of example only and are not intended to limit the scope of the present disclosure. Indeed, the novel methods and systems described herein may be embodied in a variety of other forms. Furthermore, various omissions, substitutions, and modifications in the systems and methods described herein may be made without departing from the spirit of the present disclosure. The appended claims and their equivalents are intended to cover such forms or modifications as fall within the scope and spirit of the present disclosure. Thus, the scope of the present invention is defined solely by reference to the appended claims.

[0095] It should be understood that features, materials, properties, or groups described in connection with a particular aspect, embodiment, or example may be applied to any other aspect, embodiment, or example described in this section or elsewhere in this specification, unless incompatible. All features disclosed herein (including the accompanying claims, abstract, and drawings), and / or all steps of a method or process so disclosed, may be in any combination, except combinations in which at least some of such features and / or steps are mutually exclusive. Protection is not limited to the details of the foregoing embodiments. Protection extends to new or novel combinations of features disclosed herein (including the accompanying claims, abstract, and drawings), or new or novel combinations of method or process steps.

[0096] Moreover, certain features that are described in the disclosure in the context of separate implementations can also be implemented in combination in a single implementation. Conversely, various features that are described in the context of a single implementation can also be implemented separately in multiple implementations or in any suitable subcombination. Furthermore, although features are described above as acting in a particular combination, one or more features from a claimed combination can, in some cases, be deleted from the combination, and the combination can be claimed as a subcombination or a variation of the subcombination.

[0097] Furthermore, although operations may be shown in the figures or described in the specification in a particular order, such operations need not be performed in the particular order or sequential order shown, or all of the operations to achieve desirable results. Other operations not shown or described may be incorporated into the exemplary methods and processes. For example, one or more additional operations may be performed before, after, simultaneously with, or between any of the described operations. Furthermore, in other implementations, operations may be rearranged or resequenced. Those skilled in the art will appreciate that in some embodiments, the actual steps performed in the illustrated and / or disclosed processes may differ from those shown in the figures. Depending on the embodiment, certain steps described above may be omitted and other steps may be added. Furthermore, the features and attributes of the specific embodiments disclosed above may be combined in different ways to form additional embodiments, all of which are within the scope of the present disclosure. Also, the separation of various system components in the above implementations may be combined in different ways to form additional embodiments, all of which are within the scope of the present disclosure. Also, the separation of various system components in the above implementations may be combined in different ways to form additional embodiments, all of which may be within the scope of the present disclosure. Separation should not be understood to be necessary, and it should be understood that the components and systems described can generally be integrated into a single product or packaged into multiple products. For example, any of the components of the energy storage systems described herein can be provided separately or integrated together (e.g., packaged together or attached together) to form an energy storage system.

[0098] For the purposes of this disclosure, certain aspects, advantages, and novel features are described herein. Not all such advantages are necessarily achieved according to a particular embodiment. Thus, for example, a person skilled in the art will recognize that the present disclosure may be embodied or performed in a manner that achieves one advantage or a group of advantages taught herein, without necessarily achieving other advantages that may be taught or suggested herein.

[0099] Conditional language such as "can," "could," "can," and "may" are generally intended to convey that certain embodiments include certain features, elements, and / or steps, while other embodiments do not, unless expressly stated otherwise or understood otherwise within the context in which they are used. Thus, such conditional language is not generally intended to imply that features, elements, and / or steps are required in one or more embodiments, or that one or more embodiments necessarily include logic for determining whether those features, elements, and / or steps are included in or performed in a particular embodiment, with or without user input or direction.

[0100] Conjunctions such as "at least one of X, Y, and Z," unless otherwise indicated, are understood apart from the context in which they are commonly used to convey items, terms, and the like, and either X, Y, or Z are the same. Thus, such conjunctions are not generally intended to suggest that a particular embodiment requires the presence of at least one X, at least one Y, and at least one Z.

[0101] As used herein, words indicating degree, such as "approximately," "about," "generally," and "substantially," indicate a value, amount, or characteristic that approaches a stated value, amount, or characteristic yet performs a desired function or achieves a desired result.

[0102] The scope of the present disclosure is not intended to be limited by the specific disclosure of preferred embodiments in this section or elsewhere in this specification, but may be defined by the claims presented in this section or elsewhere in this specification, or presented in the future. The language of the claims should be interpreted broadly based on the language used in the claims, and not limited to the examples set forth herein, or that examples should be construed as non-limiting during prosecution of the application.

Claims

1. A current collector having a first surface and a second surface; a multilayer electrode film laminated with the first surface of the current collector; a second multilayer electrode film laminated to the second surface of the current collector; The multilayer electrode film is a first active layer having a first active material and a first binder; a second active layer having a second active material and a second binder. the first and second active layers are laminated to form the multilayer electrode film; The multilayer electrode film is a free-standing film, the first active layer and the second active layer are substantially free of solvent residues; At least one of the first active layer and the second active layer has a thickness of at least 120 μm, and the multilayer electrode film has a thickness of at least 200 μm. The multilayer electrode film and the second multilayer electrode film are asymmetric with each other.

2. The double-sided multilayer electrode according to claim 1 , wherein the multilayer electrode film has a thickness of 250 μm to 750 μm.

3. 2. The double-sided multi-layer electrode of claim 1, wherein at least one of the type and amount of the first and second active materials differs between the first and second active layers.

4. 2. The double-sided multilayer electrode of claim 1, wherein at least one of the type and amount of the first binder and the second binder differs between the first active layer and the second active layer.

5. The double-sided multi-layer electrode of claim 1 , wherein the first active layer and the second active layer have substantially the same composition.

6. The double-sided multi-layer electrode of any one of claims 1 to 5, further comprising a third active layer having a third active material and a third binder.

7. The double-sided multi-layer electrode of any one of claims 1 to 5, wherein at least one of the first active material and the second active material comprises a metal oxide or a metal sulfide.

8. 8. The double-sided multi-layer electrode of claim 7, wherein the metal oxide is a lithium metal oxide.

9. 9. The double-sided multilayer electrode of claim 8, wherein the lithium metal oxide is selected from the group consisting of lithium nickel manganese cobalt oxide (NMC), lithium manganese oxide (LMO), lithium nickel manganese oxide (LNMO), lithium iron phosphate (LFP), lithium cobalt oxide (LCO), lithium titanate, and lithium nickel cobalt aluminum oxide (NCA), or a combination thereof.

10. The double-sided multilayer electrode of any one of claims 1 to 5, wherein the first active layer is directly adjacent to the second active layer.

11. 6. The double-sided multilayer electrode according to claim 1, wherein no layer is provided between the first and second active layers.

12. 6. The double-sided multilayer electrode according to claim 1, wherein no adhesive layer is provided between the first active layer and the second active layer.

13. A double-sided multilayer electrode as described in any one of claims 1 to 5, further comprising an adhesive layer that bonds the first active layer and the second active layer.

14. The double-sided multilayer electrode according to any one of claims 1 to 5, wherein one of the first active layer and the second active layer is a free-standing film.

15. 6. The double-sided multilayer electrode according to claim 1, wherein the multilayer electrode film is directly laminated onto the first surface of the current collector.

16. 6. The double-sided multilayer electrode according to claim 1, wherein no adhesive layer is provided between the multilayer electrode film and the current collector.

17. The double-sided multilayer electrode according to any one of claims 1 to 5, wherein the multilayer electrode film has an opposite polarity to the second multilayer electrode film.

18. The double-sided multilayer electrode according to any one of claims 1 to 15, wherein the multilayer electrode film has a different number of layers than the second multilayer electrode film.

19. 16. The double-sided multilayer electrode according to claim 1, wherein an active layer of the multilayer electrode film directly adjacent to the first surface of the current collector has a different composition than an active layer of the second multilayer electrode film directly adjacent to the second surface of the current collector.

20. providing a first active layer having a first active material and a first binder, the first active layer being a free-standing film; providing a second active layer having a second active material and a second binder, the second active layer being a free-standing film; laminating the first active layer on the second active layer to form a multilayer electrode film; Providing a current collector having a first side and a second side; laminating the multilayer electrode film on the first surface of the current collector; Providing a second multilayer electrode film; laminating the second multilayer electrode film on the second surface of the current collector; the multilayer electrode film and the second multilayer electrode film are asymmetric with each other, At least one of the first active layer and the second active layer has a thickness of at least 120 μm; The multilayer electrode film is a free-standing film having a thickness of at least 200 μm, A method for producing a double-sided multilayer electrode, which is a dry manufacturing method.

21. 21. The method of claim 20, wherein the lamination of the first active layer to the second active layer is performed by a calendaring process.

22. 21. The method of claim 20, wherein laminating the first active layer to the second active layer is performed by a pressing process.

23. The method according to any one of claims 20 to 22, wherein the multilayer electrode film is laminated directly to the first surface of the current collector.

24. The method according to any one of claims 20 to 22, wherein no adhesive layer is provided between the multilayer electrode film and the current collector.

25. The method according to any one of claims 20 to 22, wherein laminating the multilayer electrode film to the first surface of the current collector is performed by a calendaring process.

26. The method according to any one of claims 20 to 22, wherein laminating the multilayer electrode film onto the first surface of the current collector is performed by a pressing process.

27. providing a first active layer having a first active material and a first binder, the first active layer being a free-standing film; providing a second active layer having a second active material and a second binder, the second active layer being a free-standing film; Providing a current collector having a first side and a second side; forming a multi-layer electrode film by stacking the first active layer on the second active layer, the stacked first active layer and the second active layer having a thickness of at least 200 μm; laminating the first active layer to the first surface of the current collector; Providing a second multilayer electrode film; laminating the second multilayer electrode film onto the second surface of the current collector; At least one of the first active layer and the second active layer has a thickness of at least 120 μm; the multilayer electrode film and the second multilayer electrode film are asymmetric with each other, A method for producing a double-sided multilayer electrode, which is a dry manufacturing method.

28. 30. The method of claim 27, further comprising laminating the first active layer to the current collector prior to laminating the first active layer to the second active layer.

29. 30. The method of claim 27, wherein the first active layer is laminated to the second active layer prior to laminating the first active layer to the current collector.

30. The method according to any one of claims 27 to 29, wherein the multilayer electrode film is of opposite polarity to the second multilayer electrode film.

31. The method according to any one of claims 27 to 29, wherein the multilayer electrode film comprises a different number of layers than the second multilayer electrode film.

32. 30. The method according to any one of claims 27 to 29, wherein an active layer of the multilayer electrode film directly adjacent to a first surface of the current collector has a different composition than an active layer of the second multilayer electrode film directly adjacent to a second surface of the current collector.

33. A current collector having a first surface and a second surface; a multilayer electrode film laminated with the first surface of the current collector; a second multilayer electrode film laminated to the second surface of the current collector; The multilayer electrode film is a first active layer having a first active material and a first binder; a second active layer having a second active material and a second binder. the first and second active layers are laminated to form the multilayer electrode film; The multilayer electrode film is a free-standing film, the first active layer and the second active layer are substantially free of solvent residues; At least one of the first active layer and the second active layer has a thickness of at least 120 μm, and the multilayer electrode film has a thickness of at least 200 μm; The multilayer electrode film is of opposite polarity to the second multilayer electrode film.

34. A double-sided multilayer electrode as described in claim 33, wherein the multilayer electrode film and the second multilayer electrode film are symmetrical to each other.

35. A method of manufacturing a semiconductor device comprising: providing a first active layer having a first active material and a first binder, the first active layer being a free-standing film; providing a second active layer having a second active material and a second binder, the second active layer being a free-standing film; laminating the first active layer on the second active layer to form a multilayer electrode film; Providing a current collector having a first side and a second side; laminating the multilayer electrode film on the first surface of the current collector; Providing a second multilayer electrode film; laminating the second multilayer electrode film on the second surface of the current collector; the multilayer electrode film has an opposite polarity to the second multilayer electrode film, At least one of the first active layer and the second active layer has a thickness of at least 120 μm; The multilayer electrode film is a free-standing film having a thickness of at least 200 μm, A method for producing a double-sided multilayer electrode, which is a dry manufacturing method.

36. A method of manufacturing a semiconductor device comprising: providing a first active layer having a first active material and a first binder, the first active layer being a free-standing film; providing a second active layer having a second active material and a second binder, the second active layer being a free-standing film; Providing a current collector having a first side and a second side; forming a multi-layer electrode film by stacking the first active layer on the second active layer, the stacked first active layer and the second active layer having a thickness of at least 200 μm; laminating the first active layer to the first surface of the current collector; Providing a second multilayer electrode film; laminating the second multilayer electrode film onto the second surface of the current collector; At least one of the first active layer and the second active layer has a thickness of at least 120 μm; the multilayer electrode film has an opposite polarity to the second multilayer electrode film, A method for producing a double-sided multilayer electrode, which is a dry manufacturing method.

Images