Abstract

To provide a coated sheet that prevents formation of voids between sheets in sheet-based additive manufacturing such as LOM.SOLUTION: A coated sheet for use in additive manufacturing includes a base polymer layer formed of a base polymer material, and a coating polymer layer 20 formed of a coating polymer material. At least the coating polymer material is susceptible to dielectric heating in response to electromagnetic radiation, thereby promoting fusion between adjacent coated sheets during the additive manufacturing process. Specifically, when electromagnetic radiation is applied to at least an interface area 68 between adjacent coated sheets, the polymer coating layer of each coated sheet melts to diffuse across an interface area, thereby preventing formation of voids. The base polymer material and the coating polymer material may have similar melting points and compatible solubility parameters to further promote fusion between sheets.SELECTED DRAWING: Figure 2

Description

[Technical field]

[0001] The present disclosure relates to additive manufacturing apparatus and methods, and more particularly to additive manufacturing of seat bases. The additive manufacturing process disclosed herein is useful in manufacturing parts, such as environmental control ducts, door panels, tools, jigs, fixtures, etc. Additionally, embodiments of the present disclosure may be used in a wide variety of applications, particularly in the transportation industry, such as aerospace, marine, and automotive, and casings, for example, for auxiliary power units (APUs). [Background technology]

[0002] Parts and other components are produced using a variety of manufacturing techniques depending on the part's performance requirements and the availability of manufacturing equipment. For example, Laminated Object Manufacturing (LOM) is a type of additive manufacturing technique that uses sheets or layers of metal or plastic. In this process, an initial layer is placed on a substrate and selectively melted or compressed. One or more subsequent layers are placed on top of the initial layer and selectively melted or compressed to form a three-dimensional article. The sheets or layers used in such processes may be made of, for example, a thermoplastic material such as polycarbonate, a metal, or other materials of similar construction. Sheet-based additive manufacturing such as LOM can result in voids between the sheets, which can result in a lower structural integrity of the article. Summary of the Invention

[0003] According to a first aspect of the present disclosure, there is provided a coated sheet for use in an additive manufacturing process, the coated sheet comprising a base polymer layer formed as a first sheet, the base polymer layer being formed of a base polymer material having a first dielectric loss factor, and a coated polymer layer covering at least a portion of a surface of the first sheet, the coated polymer layer being formed of a coated polymer material having a second dielectric loss factor, the second dielectric loss factor of the coated polymer layer being greater than the first dielectric loss factor of the base polymer layer.

[0004] According to an additional aspect of the present disclosure, there is provided a method of producing a coated sheet for use in an additive manufacturing process, comprising: placing a sheet on a substrate, the sheet being formed of a base polymer material; applying a liquid paint to at least a portion of an outer surface of the sheet, the liquid paint being formed of a coated polymer material; and drying the liquid paint on the sheet to form the coated sheet, the coated sheet including a base polymer layer formed by the sheet and a coated polymer layer formed by the liquid paint after drying.

[0005] According to a further aspect of the present disclosure, there is provided a method of manufacturing an article by additive manufacturing, the method comprising forming a first coating sheet, the first coating sheet comprising a base polymer layer formed by the first sheet and a coating polymer layer formed by the liquid coating after drying, by providing a first sheet formed by a base polymer material, applying a liquid coating to at least a portion of an outer surface of the first sheet, the liquid coating being formed by a coating polymer material, and drying the liquid coating on the first sheet to form the first coating sheet, the first coating sheet comprising a base polymer layer formed by the first sheet and a coating polymer layer formed by the liquid coating after drying, the method further comprising forming a second coating sheet, the second coating sheet comprising a base polymer layer formed by the second sheet and a coating polymer layer formed by the liquid coating after drying, by providing a second sheet formed by the base polymer material, applying a liquid coating to at least a portion of an outer surface of the second sheet and drying the liquid coating on the second sheet to form the second coating sheet, the second coating sheet comprising a base polymer layer formed by the second sheet and a coating polymer layer formed by the liquid coating after drying. The method further includes positioning the first covering sheet relative to the second covering sheet such that the covering polymer layer of the first covering sheet overlaps the covering polymer layer of the second covering sheet at an interface region, compressing the first and second covering sheets, and dielectrically heating at least the covering polymer layer of the first covering sheet and the covering polymer layer of the second covering sheet using electromagnetic radiation, thereby fusing the first covering sheet to the second covering sheet at the interface region.

[0006] The described features, functions, and advantages may be realized individually in various embodiments, but may also be combined with each other in other embodiments, further details of which will become apparent by reference to the following description and drawings. [Brief description of the drawings]

[0007] The novel features believed characteristic of the illustrative embodiments are set forth in the appended claims. The illustrative embodiments, however, as well as the preferred mode of use, together with their objects and advantages, will be best understood by reference to the following detailed description of illustrative examples of the present disclosure taken in conjunction with the accompanying drawings.

[0008] [Figure 1] FIG. 1 is a schematic diagram of an apparatus for converting a first sheet into a coated sheet for use in a sheet-based additive manufacturing process according to the present disclosure. [Diagram 2] FIG. 2 is a schematic diagram of a process for converting a second sheet into a cover sheet. [Diagram 3] 3 is a schematic diagram showing a process of applying electromagnetic radiation to fuse the first and second sheets at their interface regions when the second sheet of FIG. 2 is placed on top of the first sheet of FIG. 1. FIG. [Figure 4] FIG. 2 is a schematic diagram of multiple coated sheets stacked and fused together. [Diagram 5] 5 is a schematic diagram showing a process of cutting the cover sheet laminate of FIG. 4 with a laser. FIG. [Figure 6] FIG. 6 illustrates an article formed after cutting the laminate shown in FIG. 5. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0009] The following detailed description relates to sheet-based additive manufacturing techniques such as layered object manufacturing (LOM). Examples disclosed herein include coating sheets for use in such processes, methods of forming the coating sheets, and methods of using the coating sheets to build articles in additive manufacturing processes. The coating sheets include a base polymer layer formed by a base polymer material and a coating polymer layer formed by a coating polymer material. The coating sheets are susceptible to selective heating, such as dielectric heating using electromagnetic radiation, thereby enhancing the strength of the built article. <Definition>

[0010] "Fused Filament Fabrication" (FFF) is an additive manufacturing technique used to build up layers to form products, such as three-dimensional products, prototypes, or models. The process is a rapid prototyping and manufacturing process in which successive layers of molten material are built up to rapidly create models, products, or articles.

[0011] As used herein, "filament" refers to a thin, thread-like feed material used in additive manufacturing processes.

[0012] As used herein, "powder coating," "coating powder," or similar terms refer to a type of coating that is applied, typically electrostatically, as a dry powder and then cured by heat, electromagnetic radiation such as microwaves, or other curing source, such as a thermoplastic material, a thermosetting polymer, or other similar polymer or material.

[0013] As used herein, "selective laser sintering" or "selective laser melting" and similar terms refer to an additive manufacturing process in which a laser is used to sinter powdered material, firing the laser into space and using a 3D model as a pattern to bond the material together to form a solid structure. Typically, the powdered material is nylon, polyamide, or similar material.

[0014] The term "Laminated Article Manufacturing (LOM)" refers to a process in which layers of material, such as plastic or paper, are bonded together using heat and pressure by fusing, crimping, laminating, etc. The product is then sliced ​​or cut into the desired shape using computer-controlled lasers, blades, knives, or other cutting tools. Description of the embodiment

[0015] Reference is made to the accompanying drawings which form a part hereof, and in which specific embodiments or examples are shown by way of illustration. Like numerals in the several drawings refer to like elements.

[0016] Referring to the figures, FIG. 1 shows an apparatus 2 for transforming a first sheet 4 into a coated sheet 6 that can be used in an additive manufacturing process to create articles with improved structural integrity. In particular, the first sheet 4 is placed on a substrate 8, which can be, for example, a worktable of an additive manufacturing apparatus. A nozzle 10 is disposed adjacent to the substrate 8 and is fluidly connected to a paint source 12 that holds a liquid paint 14. In operation, the paint source is activated to spray the paint 14 onto at least a portion of the outer surface of the first sheet 4. The liquid paint 14 can be, for example, supplied in a liquid phase and later dried and solidified on the first sheet 4. Ultimately, the apparatus 2 produces a coated sheet 6 having a base polymer layer 18 and a coated polymer layer 20.

[0017] The materials used to form the base polymer layer 18 and the cover polymer layer 20 in the cover sheet 6 can be selectively heated during a sheet-based additive manufacturing process to promote chain diffusion and bonding between the layers, resulting in a shaped article with improved structural integrity. As described in more detail below, the materials used for the base polymer layer 18 and the cover polymer layer 20 can be selected based on their relative reactivity to dielectric heating, as well as the closeness of their melting points and solubility parameters.

[0018] With regard to responsiveness to dielectric heating, for example, the material used in the cover sheet 6 is selected such that the cover polymer layer 20 is more susceptible to heating in response to electromagnetic radiation than the base polymer layer 18. The ability of a material to dissipate irradiated electromagnetic energy in the form of heat is quantified by a property known as the dielectric loss factor (also known as the loss factor and represented by the symbol tan δ). A material with a higher dielectric loss factor will heat up more in response to an applied electromagnetic field than a material with a lower dielectric loss factor. To concentrate the heating on the outer surface of the cover sheet 6, the cover polymer layer 20 is formed of a cover polymer material with a higher dielectric loss factor than the base polymer material used in the base polymer layer 18. In some examples, the cover polymer material has a tan δ value that is at least about 50 times the tan δ value of the base polymer material. Additionally or alternatively, the base polymer material may have a tan δ value less than 0.05 and the cover polymer material may have a tan δ value greater than 0.05.

[0019] The covering sheet 6 may also use materials with similar melting points for the base polymer layer 18 and the covering polymer layer 20, which may improve the strength of the shaped article formed by stacking multiple covering sheets during the additive manufacturing process. As described above, the covering polymer material has a higher dielectric loss factor and therefore generates heat in direct response to the application of electromagnetic energy. The base polymer material may be selected to have a melting point close to that of the covering polymer material, such that heating the covering polymer layer 20 with electromagnetic energy may also heat at least the outer portion of the base polymer layer 18. Indirect heating of the base polymer layer 18 in this manner may maintain the base polymer layer 18 in a softened and / or molten state for a longer period of time, which may further promote diffusion and bonding between adjacent covering sheets stacked on the substrate. The melting points of the base polymer material and the covering polymer material respectively preferably allow the formation of solid and liquid morphologies. In some instances, the base polymeric material has a first melting point and the coating polymeric material has a second melting point, the first melting point of the base polymeric material being within 20 degrees Celsius of the second melting point of the coating polymeric material. It has been found that such materials having melting points within about 20 degrees Celsius, or about 18 degrees Celsius, or about 15 degrees Celsius, can generate sufficient heat to prolong the molten state of the base polymer layer 18 to promote diffusion and bonding between adjacent beads of the coating sheet 6 that are deposited and heated during additive manufacturing.

[0020] The materials selected for the base polymer layer 18 and the coat polymer layer 20 may also have compatible solubility parameters to further promote bonding between adjacent coat sheets 6 when used in an additive manufacturing process. For example, the coat polymer material may be immiscible with the base polymer material to prevent phase separation and promote fusing of the base polymer layers of adjacent coat sheets 6 during additive manufacturing. In some examples, the base polymer material has a first solubility parameter and the coat polymer material has a second solubility parameter that differs from the first solubility parameter by about 10. (J / cc) 0.5 The difference in solubility parameters is about 10 (J / cc) 0.5 , or about 8 (J / cc) 0.5 , or about 5 (J / cc) 0.5 Materials within the above range have been found to be advantageous in promoting mixing when heated during additive manufacturing processes.

[0021] With the above in mind, suitable base polymer materials include polyethylene, polyethylene terephthalate, polypropylene, polyamide, polyetheretherketone, polyphenylene sulfide, polyetherimide, polystyrene, acrylonitrile-butadiene-styrene, polyacrylate, polyacrylonitrile, polycarbonate, or any mixture thereof.

[0022] Suitable coating polymeric materials include polyvinyl alcohol, polyvinylidene fluoride, polyurethane, polyamideimide, polyamide, polyvinyl chloride, acrylic, cellulose ester, or mixtures thereof. Other examples of suitable coating polymeric materials include high dielectric loss factor materials and solvents containing -OH, -NH, C=O, -N=O functional groups. Further examples of suitable coating polymeric materials include polyacrylonitrile (tan δ=0.1 at 60 Hz), polyethylene glycol, or mixtures thereof. In some examples, the coating polymeric material is particularly responsive to electromagnetic energy in a particular frequency range, such as microwave energy in the gigahertz range.

[0023] Table 1 compares the dielectric loss factor, melting point, and solubility parameters for examples in which the coating polymer material is polyvinyl alcohol and the base polymer material is Ultem® 1010 (a polyetherimide). [Table 1]

[0024] In this example, using Ultem® 1010 (a polyetherimide) as the base polymer material and polyvinyl alcohol as the coating polymer material is advantageous because polyvinyl alcohol has a high dielectric loss factor (tan δ=0.185 in the MHz-GHz frequency range) compared to Ultem® 1010 (tan δ=0.001 in the MHz-GHz frequency range), the melting points of these two materials differ by 14 degrees Celsius, and their solubility parameters are close to each other, i.e., compatible.

[0025] In addition to the chemical properties, the base polymer layer 18 and the coating polymer layer 20 may further have suitable physical properties to facilitate fusing, bonding, and intermixing. For example, the base polymer layer 18 may have a thickness in the range of about 0.1 to about 5 millimeters, or about 0.5 to about 4 millimeters, or about 1 to about 3 millimeters. The coating polymer layer 20 may have a thickness in the range of about 1 micron to about 1,000 microns, or about 50 microns to about 750 microns, or about 100 microns to about 300 microns. Furthermore, the liquid coating 14 may be characterized by a viscosity of about 0.1 to about 10 Pascal seconds (Pa·s), or about 0.5 to about 8 Pa·s, or about 1 to about 5 Pa·s.

[0026] In conventional sheet-based additive manufacturing techniques, a first and second uncoated sheet are stacked and fused together by compression and / or sintering. Subsequent uncoated sheets are stacked and compressed / sintered until the stack of uncoated sheets is of a desired height. This fused stack of uncoated sheets is cut, for example by a laser, to form a final article of a desired shape. Due to the nature of conventional uncoated sheets, compressing and / or sintering adjacent uncoated sheets creates voids between the uncoated sheets, which weakens the article.

[0027] 1-6 show an example of a method for forming an article 50 using a coating sheet according to the present disclosure. As described above, FIG. 1 shows a first sheet 4 formed of a base polymer material disposed on a substrate 8. In the illustrated example, the first sheet 4 has a substantially flat upper surface 52 and a lower surface 54. Also, the first sheet 4 is formed in a rectangular shape, but the sheet may have other shapes. A nozzle 10 is disposed above the upper surface 52 of the first sheet 4 and dispenses a coating material 14 onto at least a portion of the first sheet 4. When the coating material 14 dries, the first sheet 4 becomes a first coating sheet 56 having a base polymer layer 18 and a coating polymer layer 20.

[0028] Turning to FIG. 2, a second sheet 60 of base polymer material is placed on top of the first sheet 4. A coating material 14 is applied to at least a portion of an upper surface 62 of the second sheet 60 and allowed to dry, forming the second sheet 60 into a second coating sheet 66 having a base polymer layer 18 and a coating polymer layer 20. The shape of the second sheet 60 may be the same as that of the first sheet 4, or may be a different shape. Also, in this example, the first coating sheet 56 is positioned relative to the second coating sheet 66 such that the coating polymer layer 20 of the first coating sheet 56 overlaps the coating polymer layer 20 of the second coating sheet 66 at an interface region 68. Although the coating polymer layers 20 are shown perfectly aligned in FIG. 2, in other embodiments, the coating polymer layers 20 may be partially misaligned with respect to one another.

[0029] Compression / sintering is used in combination with dielectric heating to fuse the first and second cover sheets 56, 66 together in intimate contact. With the first and second cover sheets 56, 66 positioned as shown in FIG. 2, they are first fused together as shown in FIG. 3 by compressing them in a conventional manner with a press 70 (shown in phantom). To strengthen the bond between the first and second cover sheets 56, 66, electromagnetic radiation 72 is applied to at least the interface region 68. In the illustrated example, the electromagnetic radiation 72 is applied by a heat source 74 that not only applies the electromagnetic radiation 72 to the interface region 68, but also controls the duration that the electromagnetic radiation 72 is applied to strengthen localized regions of the cover sheets 56, 66. At least the cover polymer layer 20 of the first and second cover sheets 56, 66 is dielectrically heated in response to the electromagnetic radiation 72. In one example, the electromagnetic radiation 72 can be microwave having a frequency in the range between 300 MHz and 300 GHz. In this case, the coating polymer material has a high dielectric loss factor and is susceptible to microwave radiation, i.e., dielectric heating.

[0030] Since the coating polymeric material has a higher dielectric loss factor and the base polymeric material has a lower dielectric loss factor, the frequency of the electromagnetic radiation can be selected such that only the coating polymeric layer 20 directly melts in response to the electromagnetic radiation. Alternatively, the base polymeric material may have a melting point close to that of the coating polymeric material, in which case the base polymeric layer 18 at least partially melts in response to heating of the coating polymeric layer 20. Thus, in response to the electromagnetic radiation 72, the coating polymeric layer 20 melts directly and the base polymeric layer 18 melts indirectly. In other examples, the electromagnetic radiation 72 may directly heat both the coating polymeric layer 20 and the base polymeric layer 18. In either case, the melted portions of the base polymeric layer 18 of the first and second coating sheets 56, 66 fuse together, thereby preventing the formation of voids between the sheets and improving the structural integrity of the shaped article.

[0031] If the coat polymer material and the base polymer material have compatible solubility parameters (see Table 1 for a non-limiting example), then melting both the coat polymer layer 20 and the base polymer layer 18 will form a homogenous mixture, and therefore no phase separation will occur when the molten layers subsequently cool and solidify.

[0032] Additional cover sheets are added over the first and second cover sheets 56, 66 to form a sheet stack 80 having dimensions sufficient to form the final shaped article. As best seen in Figure 4, a third cover sheet 82, a fourth cover sheet 84, a fifth cover sheet 86, and a sixth cover sheet 88 are stacked over the first and second cover sheets 56, 66, so that the sheet stack 80 has a desired height dimension "H". After each additional cover sheet, the method may include compressing the stack of cover sheets using a press 70 and dielectrically heating at least the cover polymer layer 20 with electromagnetic radiation 72 from a heating source 74.

[0033] After the cover sheets are fused together, the stack of sheets 80 can be cut to form the desired shape of the article 50. As best seen in FIG. 5, a laser cutter 90 generates an energy beam 92 that cuts at least the fused portions of the stack of sheets 80. In the illustrated embodiment, the laser cutter 90 follows a circular cut pattern 94 that surrounds the fused portions of the stack of sheets 80, thereby forming a cylindrical article as shown in FIG. 6. It should be noted that the cut pattern 94 may be a shape other than circular to obtain the desired final shape of the shaped article 50 as shown in FIG. 6. The resulting article 50 does not have any voids between the cover sheets 56, 66, 82, 84. <Additional Notes>

[0034] The present disclosure also includes embodiments or examples according to the following appendices.

[0035] Appendix 1. A covering sheet (6) for use in an additive manufacturing process, comprising: a base polymer layer (18) formed as a first sheet (4), the base polymer layer (18) being formed of a base polymer material having a first dielectric loss factor; A coated sheet (6) including a coated polymer layer (20) covering at least a portion of a surface of the first sheet (4), the coated polymer layer (20) being formed from a coated polymer material having a second dielectric loss factor, the second dielectric loss factor of the coated polymer layer (20) being greater than the first dielectric loss factor of the base polymer layer (18).

[0036] Appendix 2. The coated sheet (6) of Appendix 1, wherein the base polymer material has a first melting point and the coating polymer material has a second melting point, the first melting point being within about 20 degrees Celsius of the second melting point.

[0037] Addendum 3. The base polymer material has a first solubility parameter, and the coating polymer material has a second solubility parameter, and the second solubility parameter has a difference of about 10 from the first solubility parameter. (J / cc) 0.5The covering sheet (6) according to appendix 2, wherein the thickness is within the range of 0.1 to 1.0 mm.

[0038] Addendum 4. The base polymer material has a first solubility parameter, and the coating polymer material has a second solubility parameter, and the second solubility parameter has a difference of about 10 from the first solubility parameter. (J / cc) 0.5 The covering sheet (6) according to any one of appendices 1 to 3, wherein the thickness is within the range of 0.1 to 0.5 mm.

[0039] Appendix 5. The covering sheet (6) according to any one of Appendixes 1 to 4, wherein the base polymer material contains polyetherimide, and the covering polymer material contains polyvinyl alcohol.

[0040] Appendix 6. The covering sheet (6) according to any one of Appendixes 1 to 5, wherein the base polymer layer (18) has a thickness of about 0.1 to about 5 millimeters, and the covering polymer layer (20) has a thickness of about 1 to about 1,000 microns.

[0041] Appendix 7. A method for producing a covering sheet (6) for use in an additive manufacturing process, comprising: A sheet (4) is placed on the substrate (8), the sheet (4) being made of a base polymer material; A liquid paint (14) is applied to at least a portion of the outer surface of the sheet (4), the liquid paint (14) being formed by a coating polymer material; The liquid paint on the sheet (4) is dried to form the covering sheet (6); The coated sheet (6) comprises a base polymer layer (18) formed by the sheet (4) and a coated polymer layer (20) formed by the liquid coating (14) after drying.

[0042] Appendix 8. The method of appendix 7, wherein the liquid paint (14) is sprayed from a nozzle (10) positioned adjacent to the substrate (8) when applying the liquid paint (14) to at least a portion of the outer surface of the sheet (4).

[0043] Addendum 9. The base polymer material has a first dielectric loss factor; the coating polymeric material has a second dielectric loss factor; 9. The method of claim 7 or 8, wherein the second dielectric loss factor of the coating polymeric material is greater than the first dielectric loss factor of the base polymeric material.

[0044] Clause 10. The base polymer material has a first melting point; the coating polymeric material has a second melting point; 10. The method of any one of claims 7 to 9, wherein the first melting point is within about 20 degrees Celsius of the second melting point.

[0045] Addendum 11. The base polymer material has a first solubility parameter; the coating polymeric material has a second solubility parameter; The second solubility parameter has a difference of about 10 J / cc from the first solubility parameter. 0.5 The method according to any one of claims 7 to 10, wherein the range is within 1 to 50%.

[0046] Addendum 12. The method of any one of Addendums 7 to 11, wherein the base polymer material comprises polyetherimide and the coating polymer material comprises polyvinyl alcohol.

[0047] Appendix 13. The method according to any one of Appendixes 7 to 12, wherein the base polymer layer (18) has a thickness of about 0.1 to about 5 millimeters, and the coating polymer layer (20) has a thickness of about 1 to about 1,000 microns.

[0048] Additive manufacturing method for producing an article, comprising: A first covering sheet (6) is formed, Providing a first sheet (4) formed of a base polymer material; A liquid paint (14) is applied to at least a portion of the outer surface of the first sheet (4), the liquid paint (14) being formed by a coating polymer material; The liquid coating (14) on the first sheet (6) is dried to form the first coating sheet (6), the first coating sheet (6) including a base polymer layer (18) formed by the first sheet (4) and a coating polymer layer (20) formed by the liquid coating (14) after drying, the method further comprising: forming a second covering sheet (66), providing a second sheet (60) formed from the base polymer material; applying the liquid paint (14) to at least a portion of an outer surface of the second sheet (66); The liquid paint (14) on the second sheet (60) is dried to form the second coating sheet (66), the second coating sheet (66) including a base polymer layer formed by the second sheet (60) and a coating polymer layer formed by the liquid paint (14) after drying, the method further comprising: The first covering sheet (6) is disposed relative to the second covering sheet (66) such that the covering polymer layer of the first covering sheet overlaps the covering polymer layer of the second covering sheet at an interface region (68); Compressing the first and second covering sheets (6, 66), the coating polymer layer of at least the first coating sheet (6) and the coating polymer layer of the second coating sheet (66) are dielectrically heated using electromagnetic radiation (72), thereby fusing the first coating sheet (6) to the second coating sheet (66) at the interface region (68).

[0049] Addendum 15. The base polymer material has a first dielectric loss factor; the coating polymeric material has a second dielectric loss factor; 15. The method of claim 14, wherein the second dielectric loss factor of the coating polymeric material is greater than the first dielectric loss factor of the base polymeric material.

[0050] Clause 16. The base polymer material has a first melting point; the coating polymeric material has a second melting point; 16. The method of claim 14 or 15, wherein the first melting point is within about 20 degrees Celsius of the second melting point.

[0051] Addendum 17. The base polymer material has a first solubility parameter; the coating polymeric material has a second solubility parameter; The second solubility parameter has a difference of about 10 from the first solubility parameter. (J / cc) 0.5 17. The method according to any one of claims 14 to 16, wherein the range is within 1 to 20 minutes.

[0052] Addendum 18. The method of any one of Addendums 14 to 17, wherein the base polymer material comprises polyetherimide and the coating polymer material comprises polyvinyl alcohol.

[0053] Appendix 19. The method according to any one of Appendixes 14 to 18, wherein at least the coating polymer layer of the first coating sheet (6) and the coating polymer layer of the second coating sheet (66) are dielectrically heated, and then the first coating sheet (6) and the second coating sheet (66) are cut to form the article.

[0054] Addendum 20. The method according to any one of Addendums 14 to 19, wherein at least the coating polymer layer of the first coating sheet (6) and the coating polymer layer of the second coating sheet (66) are dielectrically heated by irradiating with electromagnetic radiation (72) in a microwave frequency range.

[0055] It should be noted that the drawings are not necessarily drawn to scale, and that the examples of the present disclosure may be presented in a schematic manner. Furthermore, the detailed description is merely exemplary in nature and is not intended to limit the present disclosure or its application or uses. Thus, for convenience of explanation, the present disclosure is shown and described in terms of several exemplary embodiments, but the present disclosure may be implemented in a variety of other types of embodiments and in various other systems and environments.

Claims

1. 1. A coated sheet for use in an additive manufacturing process, comprising: a base polymer layer formed as a first sheet, the base polymer layer being formed from a base polymer material having a first dielectric loss factor; a coating polymer layer covering at least a portion of a surface of the first sheet, the coating polymer layer being formed of a coating polymer material having a second dielectric loss factor, the second dielectric loss factor of the coating polymer layer being greater than the first dielectric loss factor of the base polymer layer; the base polymer material is selected from the group consisting of polyethylene, polyethylene terephthalate, polypropylene, polyamide, polyetheretherketone, polyphenylene sulfide, polyetherimide, polystyrene, acrylonitrile-butadiene-styrene, polyacrylate, polyacrylonitrile, polycarbonate, and mixtures thereof; The coated sheet, wherein the coated polymeric material is selected from the group consisting of polyvinyl alcohol, polyvinylidene fluoride, polyurethane, polyamideimide, polyamide, polyvinyl chloride, acrylic, cellulose ester, polyacrylonitrile, polyethylene glycol, and mixtures thereof.

2. 2. The coated sheet of claim 1, wherein the base polymeric material has a first melting point and the coated polymeric material has a second melting point, the first melting point being within 20 degrees Celsius of the second melting point.

3. 3. The coating sheet according to claim 1, wherein the base polymer material has a first solubility parameter, and the coating polymer material has a second solubility parameter, the second solubility parameter having a difference from the first solubility parameter of within 10 (J / cc) 0.

5.

4. The coated sheet according to any one of claims 1 to 3, wherein the base polymer material comprises polyetherimide and the coating polymer material comprises polyvinyl alcohol.

5. 1. A method for producing a coated sheet for use in an additive manufacturing process, comprising: disposing a sheet over the substrate, the sheet being formed of a base polymer material having a first dielectric loss factor; applying a liquid coating to at least a portion of an outer surface of the sheet, the liquid coating being formed from a coated polymeric material having a second dielectric loss factor greater than the first dielectric loss factor; drying the liquid coating on the sheet to form the coated sheet; The coating sheet includes a base polymer layer formed by the sheet and a coating polymer layer formed by the liquid paint after drying, the base polymer material is selected from the group consisting of polyethylene, polyethylene terephthalate, polypropylene, polyamide, polyetheretherketone, polyphenylene sulfide, polyetherimide, polystyrene, acrylonitrile-butadiene-styrene, polyacrylate, polyacrylonitrile, polycarbonate, and mixtures thereof; The method of claim 1, wherein the coating polymeric material is selected from the group consisting of polyvinyl alcohol, polyvinylidene fluoride, polyurethane, polyamideimide, polyamide, polyvinyl chloride, acrylic, cellulose ester, polyacrylonitrile, polyethylene glycol, and mixtures thereof.

6. 6. The method of claim 5, wherein applying the liquid coating to the at least a portion of the outer surface of the sheet comprises spraying the liquid coating from a nozzle positioned adjacent to the substrate.

7. The method of claim 5 or 6, wherein the base polymeric material comprises polyetherimide and the coating polymeric material comprises polyvinyl alcohol.

8. 1. A method of producing an article by additive manufacturing, comprising: forming a first covering sheet, Providing a first sheet formed from a base polymer material; applying a liquid coating to at least a portion of an outer surface of the first sheet, the liquid coating being formed by a coated polymeric material; The liquid coating on the first sheet is dried to form the first coating sheet, the first coating sheet including a base polymer layer formed by the first sheet and a coating polymer layer formed by the liquid coating after drying, the method further comprising: forming a second covering sheet, providing a second sheet formed from the base polymer material; applying the liquid paint to at least a portion of an outer surface of the second sheet; The liquid coating on the second sheet is dried to form the second coating sheet, the second coating sheet comprising a base polymer layer formed by the second sheet; and a coating polymer layer formed by the liquid coating after drying, the method further comprising: placing the first cover sheet relative to the second cover sheet such that the cover polymer layer of the first cover sheet overlaps the cover polymer layer of the second cover sheet at an interface region; compressing the first and second covering sheets; The method of claim 1, further comprising: dielectrically heating at least the coated polymer layer of the first coated sheet and the coated polymer layer of the second coated sheet using electromagnetic radiation, thereby fusing the first coated sheet to the second coated sheet at the interface region.

9. The method of claim 8, further comprising: dielectrically heating at least the coated polymer layer of the first coated sheet and the coated polymer layer of the second coated sheet, followed by shaping the article by cutting the first coated sheet and the second coated sheet.

10. The method according to claim 8 or 9, wherein at least the coated polymer layer of the first coated sheet and the coated polymer layer of the second coated sheet are dielectrically heated by irradiating with electromagnetic radiation in the microwave frequency range.