Scintillator array, radiation detector using the same, and radiation inspection apparatus

Abstract

To provide an X-ray ceramic scintillator array, which prevents a resin used for a reflective layer of the scintillator array from being colored due to X-ray irradiation so as to realize a significant improvement against the output drop of the scintillator array, a radiation detector using the same, and a radiation inspection apparatus.SOLUTION: As a feature with which a resin used for a reflective layer of an X-ray ceramic scintillator array is to be provided, in an absorption spectrum by Fourier transform infrared spectroscopy (FT-IR), the resin, in which a ratio of absorption intensity in a wavenumber range of 1490 cm-1 to 1750 cm-1 to absorption intensity in a wavenumber range of 2500 cm-1 to 2990 cm-1 has a value in a specific range, is used.SELECTED DRAWING: Figure 3

Description

[Technical field]

[0001] An embodiment of the present invention relates to a scintillator array, a radiation detector using the same, and a radiation inspection apparatus. [Background technology]

[0002] In the fields of medical diagnosis and industrial non-destructive testing, inspections are performed using radiation inspection devices such as X-ray computed tomography devices (hereinafter referred to as X-ray CT devices). X-ray CT devices are configured by arranging an X-ray tube (X-ray source) that irradiates a fan-shaped X-ray beam and an X-ray detector incorporating a number of X-ray detection elements facing each other with the tomographic plane of the object being inspected at the center. In the X-ray CT device, the X-ray tube irradiates the object being inspected with a fan-beam X-ray while rotating it, and the X-ray detector collects X-ray absorption data that has passed through the object being inspected. After this, the X-ray absorption data is analyzed by a computer to reconstruct a tomographic image. A detection element using a solid scintillator is widely used as the radiation detector of the X-ray CT device. In a radiation detector equipped with a detection element using a solid scintillator, it is easy to miniaturize the detection element and increase the number of channels, so that the resolution of the X-ray CT device and the like can be further improved.

[0003] Radiation inspection devices such as X-ray CT devices are used in various fields such as medical and industrial use. For example, a multi-slice type X-ray CT device is known in which detector elements such as photodiodes are arranged two-dimensionally vertically and horizontally, and a scintillator array is mounted on top of the detector elements. By using a multi-slice type, sliced ​​images can be superimposed, and a CT image can be displayed three-dimensionally. A radiation detector mounted on a radiation inspection device has detector elements arranged vertically and horizontally in multiple rows, and each detector element is provided with a scintillator segment. X-rays incident on the scintillator segment are converted into visible light, and the visible light is converted into an electrical signal by the detector element to create an image. In recent years, the detector elements have been made smaller in size to obtain high resolution, and the pitch between adjacent detector elements has been narrowed. Accordingly, the size of the scintillator segments has also been reduced.

[0004] Among the various scintillator materials used for the scintillator segments as described above, rare earth oxysulfide phosphor ceramics have high luminous efficiency and suitable properties for use in scintillator segments. For this reason, radiation detectors that combine ceramic scintillator segments processed by cutting or grooving a sintered body (ingot) of rare earth oxysulfide phosphor ceramic, which is the scintillator material, with a photodiode as a detection element are becoming more widespread.

[0005] As a scintillator using phosphor ceramic, for example, a ceramic scintillator made of a sintered body of gadolinium oxysulfide phosphor is known. A ceramic scintillator array is produced, for example, as follows. First, rare earth oxysulfide phosphor powder, which is the scintillator material, is molded into an appropriate shape and sintered to form a sintered body (ingot). From this sintered body of scintillator material, a plate one size larger than the scintillator array to be formed is cut, and cutting processing such as groove cutting is performed to form scintillator segments corresponding to a plurality of detection elements. Furthermore, a reflective layer is formed between these scintillator segments, and they are integrated to produce a scintillator array. The reflective layer between the scintillator segments may be made of a metal such as molybdenum, but nowadays it is generally formed by filling the spaces between the segments with a slurry of a transparent resin dispersed with a white pigment such as titanium oxide, and then curing it. Since such reflective layers are exposed to X-ray irradiation for a long period of time, like the scintillator, it is preferable that they are not easily deteriorated by X-rays. [Prior art documents] [Patent documents]

[0006] [Patent Document 1] Japanese Patent No. 6419692 [Patent Document 2] International Publication No. 2017 / 082337 [Patent Document 3] Japanese Patent Application Publication No. 2020-173226 Summary of the Invention [Problem to be solved by the invention]

[0007] Scintillators used in X-ray CT have a structure that uses a reflective layer to confine the light generated by X-rays within the pixels and efficiently extract it to the photodiode side. The reflective layer is generally formed to fill the spaces between the scintillator segments, and in some cases, a reflective layer (also called a top plate reflective layer) is formed on the X-ray incident surface side to cover the scintillator array. The light emitted by the scintillator due to X-rays is efficiently guided to the photodiode directly or via such a reflective layer. A mixture of epoxy resin and titanium oxide is often used as the transparent resin for the reflective material. Epoxy resin has a tendency to become colored (yellowing) when exposed to X-rays for a long period of time, and when this occurs, it absorbs the light converted by the scintillator, causing a decrease in light output. As described in Patent Document 1, a resin in which a white pigment is kneaded into an epoxy resin using amine has been widely used as a reflective material, due to the dimensional accuracy of the pixel pitch and ease of handling. Epoxy resin generally has low weather resistance, and becomes colored when exposed to X-rays, causing a decrease in reflectance, which causes a problem of a decrease in the light output of the scintillator. Patent Document 2 discloses a technique for making the glass transition point and thermal expansion coefficient of the transparent resin used in the reflective layer fall within a certain range in order to improve the dimensional accuracy of the scintillator array during its manufacture and use. It also discloses that a transparent resin that does not have a C=C bond in its molecular structure is preferable as a transparent resin that satisfies these conditions and is less likely to yellow due to X-ray irradiation. Patent Document 3 also describes that in a scintillator array, the use of a specific epoxy resin, hardener, etc. is effective as a countermeasure against output reduction caused by coloring of the reflective layer due to X-ray irradiation. It is believed that the methods described in Patent Documents 1 to 3 have improved to some extent the deterioration caused by coloring of the scintillator array reflective layer due to X-ray irradiation, but there is always a demand for improved diagnostic accuracy in medical equipment, and there is a constant demand for devices with better performance. [Means for solving the problem]

[0008] In the present invention, a resin having no C=C bonds but C=O bonds in its molecular structure is used as the transparent resin constituting the reflective material of the reflective layer formed so as to fill up the spaces between the scintillator segments, and is made white by kneading with a pigment or air bubbles having a refractive index different from that of the resin. The characteristics that the resin should have are that it has an absorption spectrum analysis by Fourier transform infrared spectroscopy (FT-IR) with a wavelength range of 1490 cm -1 ~1750cm -1 Absorption intensity in the wavenumber range 2500cm -1 ~2990cm -1 The present invention relates to a resin having a ratio of absorption intensities in a specific range.

[0009] According to an embodiment of the present invention, there is provided a scintillator array comprising at least two scintillator segments and a first reflective layer disposed between the two scintillator segments. The first reflective layer includes a resin having a C=O bond and reflective particles dispersed in the resin. The at least two scintillator segments are made of a sintered body.

[0010] According to another embodiment of the present invention, there is provided a scintillator array comprising at least two scintillator segments and a first reflective layer disposed between the two scintillator segments. The first reflective layer is configured to reflect light having a wavelength of 1490 cm by infrared spectroscopy. -1 ~1750cm -1 Wavenumber range 1 and 2500 cm -1 ~2990cm -1It has an absorption peak in wavenumber region 2. The area ratio of the peak in wavenumber region 1 to that in wavenumber region 2 is 0.01 to 4. According to another embodiment of the present invention, there is provided a scintillator array comprising a plurality of scintillator segments and a first reflective layer. The first reflective layer includes a resin having a C=O bond and reflective particles. The first reflective layer also has a 1490 cm -1 ~1750cm -1 Wavenumber range 1 and 2500 cm -1 ~2990cm -1 The ratio of the area of ​​the absorption peak in wavenumber region 1 to the area of ​​the absorption peak in wavenumber region 2 is 0.01 or more and 4 or less. According to another embodiment of the present invention, there is provided a scintillator array including a plurality of scintillator segments and a first reflective layer. The first reflective layer includes a resin that does not include a C=C bond and reflective particles. The first reflective layer also includes a scintillator array having a scintillator wavelength of 1490 cm in infrared spectroscopy. -1 ~1750cm -1 Wavenumber range 1 and 2500 cm -1 ~2990cm -1 The ratio of the area of ​​the absorption peak in wavenumber region 1 to the area of ​​the absorption peak in wavenumber region 2 is 0.01 or more and 4 or less. Effect of the Invention

[0011] In this way, it has been discovered that by using a specific resin in the reflective layer of the scintillator array, coloring caused by X-ray irradiation can be significantly reduced. [Brief description of the drawings]

[0012] [Figure 1] FIG. 1 is an explanatory diagram showing a scintillator array. (The top plate reflective layer (second reflective layer) is omitted.) [Figure 2a] 1 shows a cross-sectional view of a scintillator array of the present invention. [Figure 2b] 1 shows a cross-sectional view of a scintillator array of the present invention. [Figure 2c]1 shows a cross-sectional view of a scintillator array of the present invention. [Diagram 3] FIG. 3 is a diagram showing an absorption spectrum of the reflective layer of the present invention by Fourier transform infrared spectroscopy (FT-IR). [Figure 4] FIG. 4 is a diagram showing a radiation detector according to the present invention. [Diagram 5] FIG. 5 is a diagram showing a radiological inspection apparatus according to the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0013] DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, embodiments for carrying out the scintillator array, radiation detector, and radiation inspection apparatus of the present invention will be described. (Ceramic scintillator array) FIG. 1 is a plan view showing a ceramic scintillator array of an embodiment. In these figures, 1 is a scintillator array, 2 is a scintillator segment, and 3 is a first reflective layer. The scintillator array 1 has a plurality of scintillator segments 2. A first reflective layer 3 is interposed between adjacent scintillator segments 2. The first reflective layer 3 is bonded to each of the adjacent scintillator segments 2. The plurality of scintillator segments 2 are integrated with the first reflective layer 3 bonded thereto. In other words, the scintillator array 1 has a structure in which the plurality of scintillator segments 2 are integrated with the first reflective layer 3. In addition, a second reflective layer is formed so as to cover the entirety of each individual scintillator segment (omitted in FIG. 1). 2a to 2c show three types of cross-sectional configurations of the scintillator array of the present invention. FIG. 2a shows a first reflecting layer 3 interposed between each scintillator segment and a second reflecting layer 4 arranged on the X-ray incidence side so as to cover the entire scintillator array. In this case, the second reflecting layer is coated with a reflective material and then hardened. FIG. 2b is similar to FIG. 2a, but further shows a configuration in which a part of the first reflecting layer 3 interposed between the scintillator segments is embedded inside the second reflecting layer 4. The details of the configuration will be explained. The first reflecting layer 3 has a shape that protrudes from the upper surface of the array toward the second reflecting layer 4, that is, a convex portion toward the second reflecting layer 4 side. The distance (thickness) of the convex portion from the upper surface of the array to the upper surface of the second reflecting layer 4 is smaller than the maximum thickness of the second reflecting layer 4. By adopting such a configuration, peeling of the second reflecting layer from the scintillator array can be reduced. FIG. 2c shows a second reflective layer 4 previously molded into a sheet-like shape from a resin containing reflective particles, which is laminated via an adhesive layer 5. As in FIG. 2b, a part of the first reflective layer 3 interposed between the scintillator segments is embedded in the second reflective layer 4 through the adhesive layer 5. The details of the structure will be described. The first reflective layer 3 has a shape protruding from the upper surface of the array toward the second reflective layer 4, that is, a convex portion toward the second reflective layer 4 side. The adhesive layer 5 is formed on the lower surface of the second reflective layer 4 and is in contact with the vicinity of the upper end of the convex portion of the first reflective layer 3. The distance (thickness) from the upper surface of the array of the convex portion to the upper surface of the second reflective layer 4 is smaller than the maximum thickness of the second reflective layer 4. The structures of FIG. 2b and FIG. 2c can further reduce peeling of the second reflective layer, making it more preferable. A photodiode array that detects light converted from X-rays to visible light by the scintillator is laminated on the opposite side to the X-ray incident side, forming the radiation detector of the present invention.

[0014] The scintillator array 1 may have a structure in which a plurality of scintillator segments 2 are arranged in a line, or a structure in which a predetermined number of a plurality of scintillator segments 2 are arranged two-dimensionally in the vertical and horizontal directions as shown in Fig. 1. When a plurality of scintillator segments 2 are arranged two-dimensionally, a first reflective layer 3 is provided between each of the scintillator segments 2 in the vertical and horizontal directions. The number of scintillator segments 2 is set appropriately depending on the structure, resolution, etc. of a radiation detector such as an X-ray detector.

[0015] The scintillator segment 2 is made of a sintered body of a rare earth oxysulfide phosphor or a sintered body of a garnet-structured oxide. The scintillator segment 2 is formed of one type of sintered body or two or more types of sintered bodies. The rare earth oxysulfide phosphor ceramic is exemplified by a rare earth oxysulfide phosphor containing praseodymium (Pr) as an activator. The rare earth oxysulfides constituting the phosphor ceramic include oxysulfides of rare earth elements such as yttrium (Y), gadolinium (Gd), lanthanum (La), and lutetium (Lu). Examples of garnet-structured oxides include gadolinium gallium aluminum garnet (GGAG), lutetium aluminum garnet (LuAG), lutetium gallium aluminum garnet (LuGAG), gadolinium aluminum garnet (GdAG), and gadolinium gallium aluminum garnet (GdGAG). Lutetium gallium aluminum garnet (LuGAG) is preferred.

[0016] In the ceramic scintillator array 1 of the embodiment, the scintillator segment 2 is General formula: RE2O2S:Pr…(1) (In the formula, RE represents at least one element selected from the group consisting of Y, Gd, La, and Lu). It is preferable that the scintillator material is a rare earth oxysulfide phosphor ceramic (scintillator material) having a composition represented by the following formula:

[0017] Among the rare earth elements mentioned above, Gd has a particularly large X-ray absorption coefficient and contributes to improving the light output of the ceramic scintillator array 1. Therefore, it is more preferable to use a Gd2O2S:Pr phosphor for the scintillator segments 2 of the embodiment. Note that a portion of Gd may be replaced with another rare earth element. In this case, it is preferable that the amount of Gd replaced by the other rare earth element is 10 mol % or less.

[0018] That is, in the ceramic scintillator array 1 of the embodiment, General formula: (Gd 1-X ,RE X )2O2S:Pr …(2) It is desirable to use a rare earth oxysulfide phosphor ceramic substantially represented by the formula: (wherein RE represents at least one element selected from the group consisting of Y, La, and Lu, and X is a number (atomic ratio) satisfying 0≦X≦0.1) for the scintillator segment 2.

[0019] In the ceramic scintillator array 1 of the embodiment, praseodymium (Pr) is used as an activator that increases the light output of the rare earth oxysulfide phosphor ceramic (scintillator material). Pr can also reduce afterglow compared to other activators. Therefore, a rare earth oxysulfide phosphor ceramic (scintillator material) containing Pr as an activator is effective as a fluorescence generating means for a radiation detector.

[0020] The Pr content in the rare earth oxysulfide phosphor ceramic is preferably in the range of 0.001 to 10 mol% relative to the phosphor host (e.g., RE2O2S such as Gd2O2S). If the Pr content exceeds 10 mol%, it will result in a decrease in light output. If the Pr content is less than 0.001 mol%, it will not be possible to fully exert the effect as a main activator. The Pr content is more preferably in the range of 0.01 to 1 mol%.

[0021] In the rare earth oxysulfide phosphor ceramic used in the embodiment, in addition to Pr as a main activator, a small amount of at least one element selected from the group consisting of Ce, Zr, and P may be contained as a co-activator. These elements are effective in suppressing deterioration due to exposure and suppressing afterglow. The total content of these co-activators is preferably in the range of 0.00001 to 0.1 mol% with respect to the phosphor matrix.

[0022] Furthermore, the scintillator sintered body forming the scintillator segment 2 of the embodiment is preferably made of a high-purity rare earth oxysulfide phosphor ceramic (scintillator material). Since impurities are a factor in reducing the sensitivity of the scintillator, it is preferable to reduce the amount of impurities as much as possible. In particular, since phosphate radicals (PO4) cause a decrease in sensitivity, it is preferable that the content be 100 ppm or less. When fluorides or the like are used as sintering aids for densification, the sintering aids remain as impurities, resulting in a decrease in sensitivity.

[0023] The scintillator segment 2 is made of a cubic or rectangular shaped sintered body. The volume of the scintillator segment 2 is 1 mm 3 By miniaturizing the scintillator segment 2, it is possible to increase the resolution of the detected image. The vertical (L), horizontal (S) and thickness (T) dimensions of the scintillator segment 2 are not necessarily limited, but each is preferably 1 mm or less. 3 When the first reflective layer 3 is made smaller in size to 100 μm or less, the width (W) of the first reflective layer 3 can be made thinner to 100 μm or less, or even 50 μm or less. However, when the width is made smaller than 40 μm, the manufacturing process becomes complicated, so that the width (W) of the first reflective layer 3 is preferably 40 μm or more. In the ceramic scintillator array 1 of the embodiment, the first reflective layer 3 that integrates the multiple scintillator segments 2 contains a transparent resin and reflective particles dispersed in the transparent resin. The transparent resin contains at least one of epoxy resin, silicone resin, unsaturated polyester, polyurethane, acrylic resin, polyethylene terephthalate, epoxy-modified silicone, and glycidyl ether, and contains air bubbles as reflective particles or one of titanium oxide, alumina oxide, barium sulfate, zinc oxide, zirconium oxide, and silicon oxide as pigments, and the air bubbles contained in the resin may also serve as reflective particles. The reflective layer 4 that covers the ceramic scintillator array 1 can use the same transparent resin and reflective particles as the first reflective layer 3. Note that the epoxy resin, epoxy-modified silicone, and glycidyl ether are each cured using an acid anhydride curing agent and contain a C=O bond in the cured product. Resins other than these, that is, silicone resin, unsaturated polyester, polyurethane, acrylic resin, and polyethylene terephthalate, each contain a C=O bond. Examples of acid anhydride hardeners include hydrogenated methylnadic anhydride, ethylene glycol bis(anhydrotrimellitate), methyltetrahydrophthalic anhydride, acid anhydride, trimellitic anhydride, dodecenyl succinic anhydride, benzophenone tetracarboxylic anhydride, methyltetrahydrophthalic anhydride, methylhexahydrophthalic anhydride, trialkyltetrahydrophthalic anhydride maleic anhydride, 4-methylhexahydrophthalic anhydride, 3-methylhexahydrophthalic anhydride, trialkyltetrahydrophthalic anhydride, methyl ... Examples of the acid anhydride include phthalic anhydride, chlorendic anhydride, hexahydrophthalic anhydride, tetrahydrophthalic anhydride, succinic anhydride, 3or4-methyl-1,2,3,6-tetrahydrophthalic anhydride, 3or4-methyl-hexahydrophthalic anhydride, methyl-3,6-endomethylene-1,2,3,6-tetrahydrophthalic anhydride, maleic anhydride, phthalic anhydride, pyrrolic anhydride, methylcyclohexenetetracarboxylic dianhydride, glycerin bis(anhydrotrimellitate) monoacetate, aliphatic dibasic acid polyanhydride, etc. The type of acid anhydride hardener used can be one or more types. Generally, resins tend to become colored (yellowing) when exposed to X-rays, and this coloring causes the light generated in the scintillator to be absorbed, resulting in a decrease in light output. However, the degree of yellowing varies depending on the structure of the resin. -1 ~1750cm -1 The band (wave number region 1) is characterized by absorption due to C=O, such as ester groups, carboxyl groups, and keto groups (ketone groups). -1 ~2990cm -1 Absorption due to C-H bonds can be seen in the band (wavenumber region 2). Through many experimental results, it has been found that for reflective materials that undergo minimal discoloration due to X-rays, the ratio of the absorption peak area in wavenumber region 1 to the absorption peak area in wavenumber region 2, i.e., the peak area ratio, is preferably within a certain range. FIG. 3 shows the infrared absorption spectrum of the reflective layer of the scintillator array of the present invention, measured by Fourier transform infrared spectroscopy (FT-IR). -1 ~1750cm -1 (wavenumber region 1), 2500 cm -1 ~2990cm -1 3. Absorption peaks are observed in the band (wavenumber region 1) and the band (wavenumber region 2), which are due to the resin and not the pigment contained therein. The absorption peak area means the area above the baseline shown by the dotted line in FIG. 3. In the present invention, the ratio of the absorption peak area of ​​wavenumber region 1 to wavenumber region 2 has a value in the range of 0.01 to 4. The ratio is preferably 3.6 or less, and more preferably in the range of 0.1 to 2.5. The infrared absorption spectrum as shown in FIG. 3 can be easily measured by peeling off the reflective layer from the scintillator array or by scraping off a part of it.

[0024] The ratio of the transparent resin and the reflective particles forming the first reflective layer 3 and the second reflective layer 4 is preferably such that the mass ratio of the transparent resin is 15 to 60% and the mass ratio of the reflective particles is 40 to 85% (mass ratio of the transparent resin + mass ratio of the reflective particles = 100%). If the mass ratio of the reflective particles is less than 40%, the reflection efficiency of the reflective layer decreases, and the reflection efficiency of the reflective layer for light with a wavelength of 512 nm is likely to be lower than 90%. If the mass ratio of the reflective particles exceeds 85%, the reflection efficiency of the reflective layer remains unchanged, but the mass ratio of the transparent resin decreases relatively, making it difficult to stably solidify the reflective layer. In the case of a configuration in which a prefabricated second reflective layer is bonded to the ceramic scintillator array 1 of the embodiment, the adhesive layer is made of a resin that contains at least an epoxy resin, a silicone resin, an acrylic resin, a urethane resin, or a polyester resin and is hardened by light, heat, or moisture. The adhesive layer may be a transparent resin, but may also contain air bubbles or a pigment selected from the group consisting of titanium oxide, alumina oxide, barium sulfate, zinc oxide, zirconium oxide, and silicon oxide. The scintillator array of the present invention is manufactured as follows. The preferred structure shown in FIG. 2c will be taken as an example. In the first step, a white sheet is formed of a resin such as epoxy containing a white reflective material, and a sheet of a predetermined size is prepared. A mixture of reflective particles and transparent resin, a lacquer-based paint, or the like is used for the white sheet. The mixture of reflective particles and transparent resin preferably has a structure similar to that of the reflective layer between the scintillator segments. The white sheet may be a commercially available product such as a white PET film. The white sheet is the second reflective layer of the scintillator array, and its thickness is in the range of 50 to 500 μm. If the thickness of the second reflective layer is less than 50 μm, the effect of improving the reflection efficiency cannot be sufficiently obtained. If the thickness of the second reflective layer exceeds 250 μm, the amount of X-rays that penetrate the second reflective layer decreases, and the detection sensitivity decreases. Separately, a scintillator material such as a rare earth oxysulfide phosphor ceramic is cut into a thin plate of a predetermined size (thickness 0.5 to 2 mm) and pasted onto the white sheet. The thin plate is made by butting the ends of one ceramic plate or multiple ceramic plates together and bonding them to the white sheet with epoxy resin, thermoplastic adhesive, etc. It is preferable that the width of the gap at the boundary when butted together is smaller than the width of the groove processed in step 2. In the second step, grooves are made by dicing. The width of the grooves is in the range of 40 to 200 μm. The grooves are formed from the ceramic scintillator material, and reach the ceramic scintillator material, the adhesive layer, and even into the white sheet. The position of the grooves is adjusted so that the boundary surface where the multiple ceramic plates are butted together becomes the groove portion. Part of the reflective layer (first reflective layer) between the segments is provided so as to fill the grooves in the white sheet, and the anchor effect of this prevents the top plate reflective layer (second reflective layer) from peeling off. The third step is to provide a reflective layer in the grooves formed in the second step. First, the reflective particles and an uncured resin composition (uncured transparent resin) constituting the transparent resin are prepared, and the mixture is filled into the grooves between the scintillator segments. The uncured resin composition preferably has a viscosity of 0.2 to 1 Pa·s (200 to 1000 cps). If the viscosity of the resin composition is less than 0.2 Pa·s, the fluidity is high and the workability of filling between the scintillator segments decreases. If the viscosity of the resin composition exceeds 1 Pa·s, the fluidity decreases, and therefore the coating property or filling property decreases. In addition, the total light transmittance of the transparent resin is preferably 85% or more. If the total light transmittance of the transparent resin is less than 85%, the reflection efficiency of the reflective layer is likely to decrease.

[0025] A mixture of reflective particles and an uncured resin composition is filled between the scintillator segments, and then the resin composition in the mixture is cured to form a reflective layer. The curing treatment of the mixture is appropriately set according to the type of uncured resin composition and curing agent. For example, in the case of a thermosetting resin composition, the curing reaction is advanced by heat treatment. In some cases, the curing reaction of a resin composition such as a two-liquid epoxy resin is advanced by leaving it at room temperature. Next, in step 4, the scintillator array of the present invention is completed by peripheral processing to remove unnecessary parts from the periphery and further polishing. (Radiation detector) The radiation detector of the embodiment includes the ceramic scintillator array 1 of the above-mentioned embodiment as a fluorescence generating means that emits light in response to incident radiation, and further includes a photoelectric conversion means that receives light from the fluorescence generating means and converts the light output into an electrical output. Fig. 4 shows an X-ray detector, which is an example of the radiation detector of the embodiment. The X-ray detector 6 shown in Fig. 4 includes the ceramic scintillator array 1 as a fluorescence generating means, and a photoelectric conversion element 7 such as a photodiode as a photoelectric conversion means. The configuration of the ceramic scintillator array 1 is the same as that described with reference to Fig. 2c. Therefore, the same reference numerals as in Fig. 2c are used and the description will be omitted.

[0026] The ceramic scintillator array 1 has an X-ray incident surface, and photoelectric conversion elements 7 are integrally provided on the surface opposite to the X-ray incident surface. For example, a photodiode is used as the photoelectric conversion element 7. The photoelectric conversion elements 7 are arranged to correspond to each of the multiple scintillator segments 2 that make up the ceramic scintillator array 1. These constitute a radiation detector. (Radiation Inspection Equipment) The radiation inspection apparatus of the embodiment includes a radiation source that irradiates radiation toward an object to be inspected, and a radiation detector that detects radiation that has passed through the object to be inspected. The radiation detector of the above-mentioned embodiment is used as the radiation detector. FIG. 5 shows an X-ray CT apparatus 10 as an example of the radiation inspection apparatus of the embodiment. In FIG. 5, 10 is an X-ray CT apparatus, 11 is an object to be inspected, 12 is an X-ray tube, 13 is a computer, 14 is a display, and 15 is an image of the object to be inspected. The X-ray CT apparatus 10 includes an X-ray detector 6 of the embodiment. The X-ray detector 6 is attached to, for example, an inner wall surface of a cylinder on which an imaging part of the object to be inspected 11 is disposed. An X-ray tube 12 that emits X-rays is disposed at approximately the center of the arc of the cylinder to which the X-ray detector 6 is attached. The object to be inspected 11 is disposed between the X-ray detector 6 and the X-ray tube 12. A collimator (not shown) is provided on the X-ray incident surface side of the X-ray detector 6.

[0027] The X-ray detector 6 and the X-ray tube 12 are configured to rotate around the subject 11 while performing X-ray imaging. Image information of the subject 11 is collected three-dimensionally from different angles. Signals obtained by X-ray imaging (electrical signals converted by photoelectric conversion elements) are processed by a computer 13 and displayed as a subject image 15 on a display 14. The subject image 15 is, for example, a tomographic image of the subject 11. As shown in FIG. 1, it is also possible to configure a multi-tomographic image type X-ray CT device 10 by using a scintillator array 1 in which scintillator segments 2 are arranged two-dimensionally. In this case, multiple tomographic images of the subject 11 are simultaneously captured, and the imaging results can be depicted three-dimensionally, for example.

[0028] The X-ray CT device 10 shown in FIG. 5 includes an X-ray detector 6 having the ceramic scintillator array 1 of the embodiment. As described above, the ceramic scintillator array 1 of the embodiment has a high reflection efficiency of visible light emitted from the scintillator segment 2 based on the configuration of the first reflecting layer 3 and the second reflecting layer 4, and therefore has excellent light output. By using the X-ray detector 6 having such a scintillator array 1, the imaging time by the X-ray CT device 10 can be shortened. As a result, the exposure time of the subject 11 can be shortened, and low exposure can be achieved. The radiation inspection device (X-ray CT device 10) of the embodiment is not limited to X-ray inspection for medical diagnosis of the human body, but can also be applied to X-ray inspection of animals and X-ray inspection for industrial use. Furthermore, it also contributes to improving the inspection accuracy by the X-ray nondestructive inspection device. EXAMPLES

[0029] Next, specific examples of the present invention and the results of evaluation thereof will be described. (Examples 1 to 6, Comparative Examples 1 to 2) Each resin material was mixed with 60 wt% titanium oxide (CR-90 manufactured by Ishihara Sangyo Kaisha, Ltd.) to prepare a cured product. The infrared absorption spectrum of the cured product was obtained using FT-IR (FT / IR-6600 manufactured by Nippon Bunko Co., Ltd.) from 1490 to 1750 cm -1 Peak and 2500-2990cm -1 The area of ​​the peak was calculated. -1 Peaks from 1490 to 1750 cm -1The area ratio of the peak was calculated. In addition, the prepared cured product was irradiated with 4.2 kGy of X-rays, and the reflectance (average of wavelengths of 510 nm and 670 nm) of the irradiated and unirradiated areas was measured, and the difference was calculated as the decrease in reflectance. The results are shown in Table 1. The details of the decrease in reflectance (%) are described below. The reflectance of the X-ray irradiated and unirradiated areas was measured at wavelengths of 510 nm and 670 nm, respectively, using a spectroreflectometer. The average value of the reflectance at the two wavelengths measured at each location was calculated, and the difference (decrease rate %) was calculated by subtracting the reflectance of the unirradiated area from the reflectance of the X-ray irradiated area. The smaller the area ratio of Fourier transform infrared spectroscopy (FT-IR), the smaller the decrease in reflectance due to X-ray irradiation tends to be.

[0030] The cured products of Examples 1 to 6 each contain a C=O bond, whereas the cured products of Comparative Examples 1 and 2 do not have a C=O bond.

[0031] [Table 1]

[0032] (Examples 8 and 9, Comparative Examples 3 and 4) A scintillator array was formed using the resins of Examples 1 and 4 and Comparative Examples 1 and 2. A phosphor powder having a composition of Gd2O2S:Pr (Pr concentration = 0.05 mol%) was provisionally molded by a rubber press, and this provisionally molded body was degassed and sealed in a capsule made of Ta, and then set in a HIP processing device. Argon gas was sealed in the HIP processing device as a pressurizing medium, and the HIP processing device was treated for 3 hours under conditions of a pressure of 147 MPa and a temperature of 1425°C. In this way, a cylindrical sintered body with a diameter of about 80 mm and a height of about 120 mm was produced. A GOS ceramic plate was cut out from this sintered body. Two GOS ceramic plates, 70 mm long, 22 mm wide, and 2 mm thick, were butted together with their long sides facing each other, and a white PET film (100 μm thick, manufactured by Mitsubishi Chemical) with a larger surface area was attached to the surface with epoxy adhesive. When attaching, the GOS ceramic plate, epoxy adhesive, and white PET sheet were stacked, and a load of 16 kg was applied and they were heated to 100°C to bond them. After cooling to room temperature, the load was removed, completing a laminate with a length of 70 mm and a width of 44 mm. The surface of the GOS ceramic plate of this laminate was grooved by dicing. The groove depth was 2.1 mm. The groove was formed up to the white PET sheet. The groove position was adjusted so that the boundary between the two ceramic plates was the groove. The resin material of Examples 1 and 4 and Comparative Examples 1 and 2, which had titanium oxide mixed in it, was poured into the groove, heat-cured, and polished. The outer periphery was then cut to produce a scintillator array corresponding to Figure 2c, measuring 66 mm in length, 40 mm in width, and 1.99 mm in thickness. In the scintillator array of the present invention, as shown in the examples, in comparison with the comparative example, in Fourier transform infrared spectroscopy (FT-IR), -1 ~1750cm -1 ) absorption peak area in wavenumber range 2 (2500 cm -1 ~2990cm -1 It was found that the reduction in light output due to X-ray irradiation can be reduced by using a resin with a small ratio (peak area ratio) of the absorption peak area of ​​the reflecting layer to the absorption peak area of ​​the reflecting layer.There is no doubt that the measures of the present invention are effective in that direction.

[0033] [Table 2]

[0034] The invention as originally filed is described below. [1] A ceramic scintillator array made of a sintered body of a rare earth oxysulfide phosphor, the array comprising a plurality of scintillator segments and a reflective layer portion provided between the scintillator segments so as to integrate the plurality of scintillator segments, the reflective layer containing a resin not containing a C=C bond, and a reflective material constituting the reflective layer having a wavelength of 1490 cm by infrared spectroscopy. -1 ~1750cm -1 Wavenumber range 1 and 2500 cm -1 ~2990cm -1 a ceramic scintillator array having an absorption peak in wavenumber region 2, and an area ratio of the peak in wavenumber region 1 to the peak in wavenumber region 2 being 0.01 to 4. [2] In the ceramic scintillator array described in [1] above, the inter-segment reflective layer and the top plate reflective layer contain at least one of epoxy resin, silicone resin, unsaturated polyester, polyurethane, acrylic resin, and polyethylene terephthalate, and contain as bubbles or pigments one of titanium oxide, alumina oxide, barium sulfate, zinc oxide, zirconium oxide, and silicon oxide. [3] The ceramic scintillator array according to [1] or [2], wherein the top plate reflective layer is attached via an adhesive layer. [4] In the ceramic scintillator array according to any one of [1] to [3], the rare earth oxysulfide phosphor is General formula:RE2O2S:Pr (wherein RE is at least one selected from the group consisting of Y, Gd, La, and Lu), and the Pr content relative to RE2O2S is 0.001 mol % or more and 10 mol % or less. [5] A radiation detector comprising the ceramic scintillator array according to any one of [1] to [4]. [6] [5] A radiation inspection device comprising the radiation detector according to the present invention. <1> A scintillator array comprising at least two scintillator segments and a first reflective layer provided between the two scintillator segments, the first reflective layer including a resin having a C=O bond. <2> The first reflective layer contains at least one of an epoxy resin, a silicone resin, an unsaturated polyester, a polyurethane, an acrylic resin, a polyethylene terephthalate, an epoxy-modified silicone, and a glycidyl ether. <1> 2. A scintillator array according to claim 1 . <3> The resin contains at least one of an ester group, a carboxyl group, and a keto group. <1> 2. A scintillator array according to claim 1 . <4> The first reflective layer contains at least one of titanium oxide, alumina oxide, barium sulfate, zinc oxide, zirconium oxide, silicon oxide, and air bubbles. <1> ~ <3> 2. A scintillator array according to any one of claims 1 to 11. <5> A second reflective layer is provided on the two scintillator segments and the first reflective layer, and contains the same resin as the first reflective layer. <1> ~ <4> 2. A scintillator array according to any one of claims 1 to 11. <6> The scintillator segment includes a rare earth oxysulfide phosphor or a garnet structure oxide phosphor. <1> ~ <5> 2. A scintillator array according to any one of claims 1 to 11. <7> At least two scintillator segments and a first reflective layer provided between the two scintillator segments, the first reflective layer being capable of detecting a wavelength of 1490 cm by infrared spectroscopy. -1 ~1750cm -1 Wavenumber range 1 and 2500 cm -1 ~2990cm -1 a scintillator array having an absorption peak in wavenumber region 2, and an area ratio of the peak in wavenumber region 1 to the peak in wavenumber region 2 is 0.01 to 4. <8> The peak area ratio of the wavenumber region 1 to the wavenumber region 2 is 3.6 or less. <7> 2. A scintillator array according to claim 1 . <9> A second reflective layer is provided on the two scintillator segments and the first reflective layer, and contains the same resin as the first reflective layer. <7> or <8> 2. A scintillator array according to claim 1 . <10> The scintillator segment includes a rare earth oxysulfide phosphor or a garnet structure oxide phosphor. <7> ~ <9> 2. A scintillator array according to any one of claims 1 to 11. <11> <1> ~ <10> A radiation detector comprising the scintillator array according to any one of claims 1 to 5. <12> <11> A radiation inspection device comprising the radiation detector according to claim 1. (1) A scintillator array comprising at least two scintillator segments made of a sintered body and a first reflective layer provided between the two scintillator segments, the first reflective layer including a resin having a C=O bond and reflective particles dispersed in the resin. (2) The scintillator array according to (1), wherein the first reflective layer contains at least one of an epoxy resin, a silicone resin, an unsaturated polyester, a polyurethane, an acrylic resin, polyethylene terephthalate, an epoxy-modified silicone, and a glycidyl ether. (3) The scintillator array according to (1), wherein the resin contains at least one of an ester group, a carboxyl group, and a keto group. (4) The scintillator array according to any one of (1) to (3), wherein the first reflective layer is provided so as to completely fill a space between the two scintillator segments. (5) The scintillator array according to any one of (1) to (3), wherein the first reflective layer is provided by filling a space between the two scintillator segments. (6) The scintillator array according to any one of (1) to (5), wherein the reflective particles of the first reflective layer include at least one of titanium oxide, alumina oxide, barium sulfate, zinc oxide, zirconium oxide, silicon oxide, and air bubbles. (7) The scintillator array described in any one of (1) to (6), further comprising a second reflective layer provided on the two scintillator segments and the first reflective layer, the second reflective layer containing the same resin as the first reflective layer. (8) The scintillator array according to any one of (1) to (7), wherein the sintered body of the scintillator segment includes a sintered body of a rare earth oxysulfide phosphor or a sintered body of a garnet-structure oxide phosphor. (9) At least two scintillator segments and a first reflective layer provided between the two scintillator segments, the first reflective layer being reflective to a wavelength of 1490 cm by infrared spectroscopy. -1 ~1750cm -1 Wavenumber range 1 and 2500 cm -1 ~2990cm -1 a scintillator array having an absorption peak in wavenumber region 2, and an area ratio of the peak in wavenumber region 1 to the peak in wavenumber region 2 is 0.01 to 4. (10) A scintillator array according to (9), wherein the peak area ratio of the wavenumber region 1 to the wavenumber region 2 is 3.6 or less. (11) The scintillator array of claim 9 or 10, further comprising a second reflective layer provided on the two scintillator segments and the first reflective layer, the second reflective layer containing the same resin as the first reflective layer. (12) The scintillator array according to any one of (9) to (11), wherein the scintillator segments contain a rare earth oxysulfide phosphor or a garnet-structure oxide phosphor. (13) A radiation detector comprising the scintillator array according to any one of (1) to (12). (14) (13) A radiation inspection device comprising the radiation detector according to (13). [Industrial Applicability]

[0035] The scintillator array of the present invention can reduce the decrease in light output due to X-ray irradiation, and therefore can be said to be industrially useful. [Explanation of symbols]

[0036] 1 Scintillator Array 2 Scintillator Segments 3 Reflective layer between scintillator segments 4. Reflective layer (second reflective layer) attached to the scintillator array on the X-ray entrance side 5 Adhesive layer 6 X-ray detector 7 Photoelectric conversion element

Claims

1. A plurality of scintillator segments; The resin contains a C=O bond and reflective particles, and is irradiated at 1490 cm by infrared spectroscopy. -1 ~1750cm -1 Wavenumber range 1 and 2500 cm -1 ~2990cm -1 a first reflective layer having an absorption peak in wavenumber region 2, and a ratio of an area of ​​the absorption peak in wavenumber region 1 to an area of ​​the absorption peak in wavenumber region 2 being 0.01 or more and 4 or less; A scintillator array comprising:

2. A plurality of scintillator segments; The resin does not contain C═C bonds and contains reflective particles. Infrared spectroscopy shows an emission spectrum of 1490 cm -1 ~1750cm -1 Wavenumber range 1 and 2500 cm -1 ~2990cm -1 a first reflective layer having an absorption peak in wavenumber region 2, and a ratio of an area of ​​the absorption peak in wavenumber region 1 to an area of ​​the absorption peak in wavenumber region 2 being 0.01 or more and 4 or less; A scintillator array comprising:

3. 3. The scintillator array according to claim 1, wherein the ratio of the absorption peak areas is 0.01 or more and 3.6 or less.

4. 3. The scintillator array according to claim 1, wherein the first reflective layer contains at least one of an epoxy resin, a silicone resin, an unsaturated polyester, a polyurethane, an acrylic resin, polyethylene terephthalate, an epoxy-modified silicone, and a glycidyl ether.

5. 3. The scintillator array according to claim 1, wherein the resin contains at least one of an ester group, a carboxyl group, and a keto group.

6. 3. The scintillator array according to claim 1, wherein the reflective particles of the first reflective layer include at least one of titanium oxide, alumina oxide, barium sulfate, zinc oxide, zirconium oxide, silicon oxide, and air bubbles.

7. The scintillator array of claim 1 or 2, further comprising: a second reflective layer provided on the plurality of scintillator segments and on the first reflective layer.

8. 3. The scintillator array according to claim 1, wherein the scintillator segments include a sintered body of a rare earth oxysulfide phosphor or a sintered body of a garnet-structure oxide phosphor.

9. A radiation detector comprising the scintillator array according to any one of claims 1 to 8.

10. A radiation inspection device comprising the radiation detector according to claim 9.