Phosphorus-modified MFI structured molecular sieve, catalytic cracking aid and catalytic cracking catalyst containing phosphorus-modified MFI structured molecular sieve, and preparation method thereof

Abstract

having a K value that satisfies 70%≦K≦90%, for example 75%≦K≦90%, further for example 78%≦K≦85%; K = P1 / P2 × 100% The present invention provides a phosphorus-modified MFI molecular sieve, wherein P1 represents the mass content of phosphorus within a region having an area of ​​100 square nanometers and a vertical depth of 0 to 2 nm on any crystal face of the molecular sieve crystal grain, as measured by XPS, and P2 represents the mass content of phosphorus within a region having an area of ​​100 square nanometers and a vertical depth of 5 to 10 nm on any crystal face of the molecular sieve crystal grain, as measured by EPMA. The present invention also provides a catalytic cracking aid and a catalytic cracking catalyst containing the phosphorus-modified MFI molecular sieve, as well as methods for preparing and using the same.

Description

Detailed Description of the Invention

[0001] CROSS-REFERENCE TO RELATED APPLICATIONS This application claims priority to Chinese patent application No. 202010283498.2 filed on April 13, 2020, Chinese patent application No. 202011169092.8 filed on October 28, 2020, and Chinese patent application No. 202011175729.4 filed on October 29, 2020. The disclosures of the foregoing applications are incorporated herein by reference in their entireties.

[0002] [Technical Field] The present invention relates to a phosphorus-modified MFI structured molecular sieve, a catalytic cracking aid containing the phosphorus-modified MFI structured molecular sieve, and a catalytic cracking catalyst containing the phosphorus-modified MFI structured molecular sieve.The present invention further relates to a method for preparing the phosphorus-modified MFI structured molecular sieve, the catalytic cracking aid containing the phosphorus-modified MFI structured molecular sieve, and the catalytic cracking catalyst containing the phosphorus-modified MFI structured molecular sieve.The present invention further relates to the use of the catalytic cracking aid and the catalytic cracking catalyst in the catalytic cracking of hydrocarbon oils.

[0003] [Background technology] ZSM-5 molecular sieves, a typical example of molecular sieves with an MFI framework structure, were developed by Mobil Corporation in 1972 and are widely used zeolite molecular sieve catalyst materials. ZSM-5 molecular sieves have a three-dimensional intersecting channel structure. The a-axis channels are straight channels with nearly circular cross sections of 0.54 × 0.56 nm. The b-axis channels are zigzag channels with elliptical cross sections of 0.51 × 0.56 nm. ZSM-5 molecular sieves have openings consisting of 10-membered rings. Because the opening size is between that of small-pore and large-pore zeolites, they have a unique shape-selective catalytic effect. ZSM-5 molecular sieves have a unique channel structure, excellent shape-selective catalytic and isomerization performance, high thermal and hydrothermal stability, a high specific surface area, a wide range of silica-alumina ratios, unique surface acidity, and relatively low carbon production. Therefore, they are widely used as catalysts and catalyst supports, and are successfully used in processes such as alkylation, isomerization, disproportionation, catalytic cracking, and the preparation of methanol-based gasoline and methanol-based olefins. ZSM-5 molecular sieves have been introduced into catalytic cracking and C4 hydrocarbon catalytic cracking, where they exhibit excellent catalytic performance. Their molecular shape selectivity can significantly improve the yield of low-carbon olefins.

[0004] Since 1983, ZSM-5 molecular sieves have been used as catalytic cracking octane additives / catalysts in catalytic cracking processes to improve the octane number and low-carbon olefin selectivity of catalytic cracked gasoline. U.S. Pat. No. 3,758,403 first reported the use of ZSM-5 molecular sieves as an active ingredient for increasing propylene production. ZSM-5 molecular sieves are used together with REY as an active ingredient in FCC catalysts, or are used to prepare FCC catalysts with REY. U.S. Pat. No. 5,997,728 also disclosed the use of ZSM-5 molecular sieves without any modification as an additive for increasing propylene production. However, the propylene yields of these two technologies are not high.

[0005] Although HZSM-5 molecular sieves have good shape selectivity and isomerization, they have the drawback of poor hydrothermal stability and are easily deactivated under severe high-temperature hydrothermal conditions, which reduces their catalytic performance.

[0006] In the 1980s, Mobil discovered that phosphorus improves the hydrothermal stability of ZSM-5 molecular sieves and that modifying ZSM-5 molecular sieves with phosphorus increases the yield of low-carbon olefins. Conventional additives typically contain phosphorus-activated ZSM-5, which selectively converts primary cracking products (e.g., gasoline olefins) to C3 and C4 olefins. ZSM-5 molecular sieves can be modified after synthesis by introducing an appropriate amount of inorganic phosphorus compounds to stabilize the framework aluminum under harsh hydrothermal conditions.

[0007] CN106994364A discloses a method for modifying ZSM-5 molecular sieves with phosphorus. This method involves mixing one or more phosphorus-containing compounds selected from phosphoric acid, diammonium hydrogen phosphate, ammonium dihydrogen phosphate, and ammonium phosphate with ZSM-5 molecular sieves containing a high alkali metal ion content to obtain a mixture with a phosphorus loading of at least 0.1 wt% based on P2O5. The mixture is then dried and calcined, and further subjected to ammonium exchange and washing to reduce the alkali metal ion content to 0.10 wt% or less. The mixture is then dried and hydrothermally aged at 400-1000°C under 100% steam. The phosphorus-containing ZSM-5 molecular sieves obtained by this method have a high total acid content, excellent cracking conversion and propylene selectivity, and a relatively high liquefied gas yield.

[0008] US Patent No. 5,171,921 discloses a method for modifying ZSM-5 molecular sieves. This method involves obtaining ZSM-5 molecular sieves through conventional synthesis, filtration, ammonium exchange, drying, and calcination. The ZSM-5 molecular sieves are then modified with phosphoric acid, dried, and calcined to obtain phosphorus-modified HZSM-5 molecular sieves, where the P2O5 loading is typically in the range of 1-7 wt%. However, phosphoric acid or ammonium phosphate salts self-aggregate during calcination to form phosphorus species with different aggregate states. During hydrothermal treatment, only the phosphorus groups that enter the pores interact with the framework aluminum, retaining the B acid centers and reducing the distribution of phosphorus species.

[0009] Hierarchical ZSM-5 molecular sieves are ZSM-5 molecular sieves containing both micropores and mesopores. Various hierarchical ZSM-5 molecular sieves with mesopore channels are typically prepared by hard template, soft template, or acid-base post-treatment.

[0010] Modification of ZSM-5 molecular sieves (with a hierarchical structure) with an appropriate amount of inorganic phosphorus compounds can delay framework dealumination and improve hydrothermal stability. Furthermore, the phosphorus atoms bond with distorted, four-coordinate framework aluminum to form weak B acid centers, achieving high cracking conversion of long-chain alkanes and high selectivity for light olefins. However, using excessive amounts of inorganic phosphorus compounds for modification can clog the channels of the molecular sieve, reducing the pore volume and specific surface area and occupying a large number of strong B acid centers. Furthermore, in conventional techniques, phosphoric acid or ammonium phosphate salts self-aggregate during the calcination process, forming phosphorus species with different aggregate states, resulting in insufficient coordination between phosphorus and framework aluminum, low phosphorus utilization efficiency, and insufficient improvement in hydrothermal stability. Therefore, new technologies are urgently needed to promote coordination between phosphorus and framework aluminum, improve the hydrothermal stability of phosphorus-modified ZSM-5 molecular sieves, and further increase cracking activity.

[0011] Summary of the Invention One object of the present invention is to provide a phosphorus-modified MFI molecular sieve, which, unlike the prior art, has a high dispersity of phosphorus species and can achieve excellent cracking conversion, low-carbon olefin yield, and high liquefied gas yield when applied to the catalytic cracking of petroleum hydrocarbons. Another object of the present invention is to provide a catalytic cracking aid using a phosphorus-modified ZSM-5 molecular sieve with a high dispersity of phosphorus species as an active ingredient, which can achieve excellent cracking conversion, low-carbon olefin yield, and high liquefied gas yield in the catalytic cracking of petroleum hydrocarbons. Another object of the present invention is to provide a catalytic cracking catalyst using a phosphorus-modified MFI molecular sieve with a high dispersity of phosphorus species as one of its active ingredients, which can achieve excellent cracking conversion, low-carbon olefin yield, and high liquefied gas yield in the catalytic cracking of petroleum hydrocarbons. Another object of the present invention is to provide methods for preparing the phosphorus-modified MFI molecular sieve, the catalytic cracking aid, and the catalytic cracking catalyst. Another object of the present invention is to provide applications for the catalytic cracking aid and the catalytic cracking catalyst.

[0012] To achieve the above object, the present invention provides a molecular sieve having a K value satisfying 70%≦K≦90%, where K=mass content of phosphorus in an area having an area of ​​100 square nanometers and a vertical depth of 5 to 10 nm on any crystal face of the crystal grain of the molecular sieve, as measured by EPMA / mass content of phosphorus in an area having an area of ​​100 square nanometers and a vertical depth of 0 to 2 nm on any crystal face of the crystal grain of the molecular sieve, as measured by XPS×100%, and an ESCAREB 250 X-ray photoelectron spectrometer from Thermo Fisher-VG is used as an excitation source, with monochromatic AlKα X-rays at an output of 150 W, and charge shift is calibrated with the C1s peak (284.8 eV) of contaminating carbon, to perform XPS analysis of the molecular sieve surface, and a JXA-8230 energy spectrometer X-ray detector is used. Regarding counting rate and counting time, the total counts are generally 10 5 Larger, count rate 10 3 ~10 4The phosphorus-modified MFI structure molecular sieve is characterized in that the counting time is 10 to 100 seconds, and the molecular sieve surface is subjected to EPMA analysis.

[0013] In the phosphorus-modified MFI molecular sieve, the molar ratio of the phosphorus content to the alumina content based on P2O5 is ≥ 0.01, for example ≥ 0.2, ≥ 0.3, or further for example 0.4 to 0.7. The phosphorus-modified MFI molecular sieve may be a microporous ZSM-5 molecular sieve or a hierarchical ZSM-5 molecular sieve, having a phosphorus loading of at least 0.1 wt% based on P2O5. In the microporous ZSM-5 molecular sieve, the silica / alumina molar ratio is 15 to 1000, for example 20 to 200. In the hierarchical ZSM-5 molecular sieve, the ratio of mesopore volume to total pore volume is more than 10%, the average pore diameter is 2 to 20 nm, and the silica / alumina molar ratio is 15 to 1000, for example 20 to 200.

[0014] In order to achieve the above object, the present invention provides a catalytic cracking aid comprising 5 to 75 wt % of a phosphorus-modified MFI structured molecular sieve on a dry basis of the catalytic cracking aid, wherein the phosphorus-modified MFI structured molecular sieve has a K value satisfying 70%≦K≦90%, for example 75%≦K≦90%, further for example 78%≦K≦85%, wherein K=mass content of phosphorus in an area having an area of ​​100 square nanometers and a vertical depth of 5 to 10 nm on any crystal face of a crystal grain of the molecular sieve, as measured by an EPMA method / mass content of phosphorus in an area having an area of ​​100 square nanometers and a vertical depth of 0 to 2 nm on any crystal face of a crystal grain of the molecular sieve, as measured by an XPS method×100%, and wherein the XPS method is carried out using a Thermo Fisher Scientific ESCAREB 250 X-ray photoelectron spectrometer with a 150 W output power and a monochromatic AlKα excitation source. X-rays were used, and the charge shift was calibrated with the C1s peak (284.8 eV) of contaminating carbon. XPS analysis of the molecular sieve surface was performed using a JXA-8230 energy spectrometer X-ray detector. Regarding the counting rate and counting time, the total counts were generally 10 5 Larger, count rate 10 3 ~10 4The counting time is 10 to 100 seconds, and EPMA analysis of the molecular sieve surface is performed to provide a catalytic cracking aid.

[0015] In the phosphorus-modified MFI molecular sieve, the molar ratio of the phosphorus content to the alumina content based on P2O5 is ≥ 0.01, for example ≥ 0.2, ≥ 0.3, or further for example 0.4 to 0.7. The phosphorus-modified MFI molecular sieve may be a microporous ZSM-5 molecular sieve or a hierarchical ZSM-5 molecular sieve, having a phosphorus loading of at least 0.1 wt% based on P2O5. In the microporous ZSM-5 molecular sieve, the silica / alumina molar ratio is 15 to 1000, for example 20 to 200. In the hierarchical ZSM-5 molecular sieve, the ratio of mesopore volume to total pore volume is more than 10%, the average pore diameter is 2 to 20 nm, and the silica / alumina molar ratio is 15 to 1000, for example 20 to 200.

[0016] The catalytic cracking aid of the present invention may further comprise, based on the dry weight of the catalytic cracking aid, 1 to 40 wt. % of a binder and 0 to 65 wt. % of a second clay. The binder comprises a phosphorus-aluminum inorganic binder. The phosphorus-aluminum inorganic binder is a phosphorus-aluminum adhesive and / or a first clay-containing phosphorus-aluminum inorganic binder.

[0017] In order to achieve the above object, the present invention provides a catalytic cracking catalyst comprising a phosphorus-modified MFI structured molecular sieve, wherein, on a dry basis of the catalyst, the catalytic cracking catalyst comprises 1-25 wt% of a Y-type molecular sieve, 5-50 wt% of the phosphorus-modified MFI structured molecular sieve, 1-60 wt% of an inorganic binder, and optionally 0-60 wt% of a second clay, wherein the inorganic binder comprises a phosphorus-aluminum inorganic binder and / or other inorganic binder, and the phosphorus-modified MFI structured molecular sieve has a K of 70%≦K≦90%, for example 7 The molecular sieve surface has a K value that satisfies 5%≦K≦90%, further, for example, 78%≦K≦85%, where K=mass content of phosphorus in an area having an area of ​​100 square nanometers and a vertical depth of 5 to 10 nm on any crystal face of the molecular sieve crystal grain, as measured by EPMA method / mass content of phosphorus in an area having an area of ​​100 square nanometers and a vertical depth of 0 to 2 nm on any crystal face of the molecular sieve crystal grain, as measured by XPS method × 100%. XPS analysis of the molecular sieve surface was performed using a Thermo Fisher-VG ESCAREB 250 X-ray photoelectron spectrometer with a 150 W output monochromatic AlKα X-ray as the excitation source, and the charge shift was calibrated with the C1s peak (284.8 eV) of contaminating carbon. A JXA-8230 energy spectrometer X-ray detector was used, and the total counts were generally 10 5 Larger, count rate 10 3 ~10 4 The counting time is 10 to 100 seconds, and EPMA analysis of the molecular sieve surface is performed to provide a catalytic cracking catalyst.

[0018] In the phosphorus-modified MFI molecular sieve, the molar ratio of the phosphorus content to the alumina content based on P2O5 is ≥ 0.01, for example ≥ 0.2, ≥ 0.3, or further for example 0.4 to 0.7. The phosphorus-modified MFI molecular sieve may be a microporous ZSM-5 molecular sieve or a hierarchical ZSM-5 molecular sieve, having a phosphorus loading of at least 0.1 wt% based on P2O5. In the microporous ZSM-5 molecular sieve, the silica / alumina molar ratio is 15 to 1000, for example 20 to 200. In the hierarchical ZSM-5 molecular sieve, the ratio of mesopore volume to total pore volume is more than 10%, the average pore diameter is 2 to 20 nm, and the silica / alumina molar ratio is 15 to 1000, for example 20 to 200.

[0019] In the catalytic cracking catalyst, the Y-type molecular sieve can be at least one of a PSRY-type molecular sieve, a rare earth-containing PSRY-type molecular sieve, a USY-type molecular sieve, a rare earth-containing USY-type molecular sieve, a REY-type molecular sieve, a REHY-type molecular sieve, and a HY-type molecular sieve. For example, the inorganic binder can be a phosphorus-aluminum inorganic binder, and the phosphorus-aluminum inorganic binder can be a phosphorus-aluminum adhesive and / or a first clay-containing phosphorus-aluminum inorganic binder.

[0020] To achieve the above object, the present invention provides a method for preparing a phosphorus-modified MFI molecular sieve, which is obtained by a dipping method comprising: mixing and contacting an aqueous solution of a phosphorus-containing compound at 40 to 150°C, for example, 50 to 150°C, further for example, 70 to 130°C, with an MFI molecular sieve at 40 to 150°C, for example, 50 to 150°C, further for example, 70 to 130°C, at substantially the same temperature for 0.1 hours or more; drying the mixture; and calcining the mixture at 200 to 600°C in an air or steam atmosphere for 0.1 hours or more; or vigorously mixing and stirring the phosphorus-containing compound, the MFI molecular sieve, and water to form a slurry, adjusting (heating) the temperature to 40 to 150°C, for example, 50 to 150°C, further for example, 70 to 130°C, maintaining the slurry for 0.1 hours or more, drying the slurry, and calcining the mixture at 200 to 600°C in an air or steam atmosphere for 0.1 hours or more.

[0021] In the preparation method of the phosphorus-modified MFI molecular sieve, the MFI molecular sieve may be a hydrogen-type microporous ZSM-5 molecular sieve or a hydrogen-type hierarchical ZSM-5 molecular sieve. The MFI molecular sieve is obtained by ammonium exchange to reduce the sodium content to <0.1 wt% NaO and has a silica / alumina ratio (molar ratio of silicon oxide to aluminum oxide) of ≥10, typically 10-200.

[0022] In the method for preparing the phosphorus-modified MFI-structured molecular sieve, the molar ratio of the phosphorus-based (oxide-based) phosphorus-containing compound to the aluminum-based (oxide-based) MFI-structured molecular sieve (such as a hydrogen-type ZSM-5 molecular sieve or a ZSM-5 molecular sieve having a hydrogen-type hierarchical structure) is 0.01 to 2, for example, 0.1 to 1.5, further for example, 0.2 to 1.5. The phosphorus-containing compound may be selected from organic phosphorus compounds such as trimethyl phosphate, triphenylphosphine, trimethyl phosphite, tetrabutyl phosphonium bromide, tetrabutyl phosphonium chloride, tetrabutyl phosphonium hydroxide, triphenylethyl phosphonium bromide, triphenylbutyl phosphonium bromide, triphenylbutyl phosphonium bromide, triphenylbenzyl phosphonium bromide, hexamethylphosphoric triamide, dibenzyl diethyl phosphoramidite, and 1,3-bis((triethylphosphinyl)methyl)benzene; or inorganic phosphorus compounds such as phosphoric acid, ammonium hydrogen phosphate, diammonium hydrogen phosphate, ammonium phosphate, and boron phosphate, or a mixture thereof. The inventors have found that using boron phosphate as one of the phosphorus-containing compounds and performing hydrothermal calcination at 300-500°C results in better phosphorus dispersion in molecular sieves. Therefore, for example, the combination of phosphorus-containing compounds is a mixture of boron phosphate with one or more selected from trimethyl phosphate, triphenylphosphine, trimethyl phosphite, phosphoric acid, ammonium hydrogen phosphate, diammonium hydrogen phosphate, and ammonium phosphate. In the boron phosphate-containing mixture, the boron phosphate is present in an amount of 10 to 80% by weight, for example, 20 to 40% by weight, or further for example, 25 to 35% by weight.

[0023] In the preparation method of phosphorus-modified MFI molecular sieves, the contacting step involves contacting an aqueous solution of a phosphorus-containing compound at 30 to 150°C with a hydrogen-type MFI molecular sieve at 30 to 150°C for at least 0.1 hours at substantially the same temperature by immersion. Contacting at a relatively high temperature range of 40°C or higher, such as 50 to 150°C, or even 70 to 130°C, produces better results. This improves the dispersion of phosphorus species, facilitating migration of phosphorus into the interior of the hydrogen-type MFI molecular sieve crystals and bonding with the framework aluminum, further improving the coordination between phosphorus and framework aluminum, and ultimately contributing to improved hydrothermal stability of the molecular sieve. The term "substantially the same temperature" refers to a temperature difference of within ±5°C between the aqueous solution of the phosphorus-containing compound and the hydrogen-type MFI molecular sieve. For example, if the aqueous solution of the phosphorus-containing compound is at 80°C, the HZSM-5 molecular sieve must be heated to 75 to 85°C.

[0024] In the method for preparing a phosphorus-modified MFI molecular sieve, the contacting step may involve mixing a phosphorus-containing compound, a (hydrogen-type) MFI molecular sieve, and water and maintaining the mixture at 30 to 150°C for at least 0.1 hours. For example, to obtain better results, i.e., to improve the dispersion of phosphorus species, facilitate the migration of phosphorus into the crystal interior of the hydrogen-type MFI molecular sieve and its bonding with the framework aluminum, further improve the coordination between phosphorus and framework aluminum, and ultimately contribute to improving the hydrothermal stability of the molecular sieve, the phosphorus-containing compound, the hydrogen-type MFI molecular sieve, and water are mixed and then maintained at a relatively high temperature range of 40°C or higher, for example, 50 to 150°C, or even 70 to 130°C, for 0.1 hours. The contacting step is performed at a water / molecular sieve weight ratio of 0.5 to 1 and for 0.5 to 40 hours. The calcination step is performed at 450 to 550°C in a steam atmosphere.

[0025] The present invention improves the hydrothermal stability of phosphorus-modified molecular sieves by promoting the coordination of phosphorus species with the framework aluminum of the MFI molecular sieve.In the cracking of n-tetradecane, the phosphorus-containing MFI molecular sieve of the present invention can achieve excellent cracking conversion and low-carbon olefin yield, and also high liquefied gas yield.

[0026] To achieve the above object, the present invention provides a method for preparing a phosphorus-modified MFI molecular sieve, which comprises vigorously mixing and stirring the phosphorus-modified MFI molecular sieve prepared by the method for preparing a phosphorus-modified MFI molecular sieve of the present invention, a binder, and optionally a second clay with water, followed by spray drying to obtain a catalytic cracking aid.

[0027] In the method for preparing a catalytic cracking aid, the binder includes a phosphorus-aluminum inorganic binder. The phosphorus-aluminum inorganic binder is a phosphorus-aluminum adhesive and / or a first clay-containing phosphorus-aluminum inorganic binder. Based on the dry weight of the first clay-containing phosphorus-aluminum inorganic binder, the first clay-containing phosphorus-aluminum inorganic binder contains 10 to 40 wt %, for example, 15 to 40 wt %, of an aluminum component based on Al2O3, 45 to 90 wt %, or 45 to 80 wt %, of a phosphorus component based on P2O5, and a first clay content of greater than 0 and not more than 40 wt % on a dry basis. The first clay-containing phosphorus-aluminum inorganic binder has a P / Al weight ratio of 1.0 to 6.0, a pH of 1 to 3.5, and a solids content of 15 to 60 wt %. The first clay includes at least one of kaolin, sepiolite, attapulgite, rectorite, smectite, and diatomaceous earth. The binder includes at least one other inorganic binder selected from the group consisting of pseudoboehmite, alumina sol, silica-alumina sol, and water glass. The second clay is at least one selected from the group consisting of kaolin, sepiolite, attapulgite, rectorite, smectite, metahalloysite, halloysite, hydrotalcite, bentonite, and diatomaceous earth.

[0028] In the method for preparing the catalytic cracking aid, based on the catalytic cracking aid, the binder comprises 3-39 wt % of a phosphorus-aluminum inorganic binder on a dry basis and 1-30 wt % of other inorganic binders on a dry basis.

[0029] The method for preparing the catalytic cracking aid includes first calcining the product obtained by spray drying, washing, and optionally drying to obtain the catalytic cracking aid. In the first calcination, the calcination temperature is 300 to 650°C, the calcination time is 0.5 to 8 hours, the drying temperature is 100 to 200°C, and the drying time is 0.5 to 24 hours.

[0030] The method for preparing a catalytic cracking aid may further include vigorously mixing and stirring an alumina source, the first clay, and water to disperse them into a slurry with a solids content of 5 to 48% by weight, adding concentrated phosphoric acid to the slurry under stirring at a weight ratio of P / Al=1 to 6, and reacting the resulting mixed slurry at 50 to 99°C for 15 to 90 minutes to prepare the first clay-containing phosphorus-aluminum inorganic binder. The alumina source is aluminum hydroxide and / or alumina that can be peptized with acid, and the amount of the first clay used on a dry weight basis is more than 0 parts by weight and not more than 40 parts by weight relative to 10 to 40 parts by weight, for example 15 to 40 parts by weight, of the alumina source based on Al2O3, and in the P / Al, P is the weight of phosphorus as a simple substance in the phosphoric acid, and Al is the weight of aluminum as a simple substance in the alumina source.

[0031] To achieve the above objective, the present invention provides a catalytic cracking aid, i.e., a method for catalytically cracking hydrocarbon oils, comprising catalytically reacting a hydrocarbon oil with the catalytic cracking aid under catalytic cracking conditions. For example, the hydrocarbon oil is catalytically reacted with a catalytic cracking aid and a catalytic cracking catalyst, with the catalytic cracking aid content in the catalytic mixture being 0.1 to 30 wt%. The catalytic cracking conditions include a reaction temperature of 500 to 800°C and the hydrocarbon oil being one or more selected from crude oil, naphtha, gasoline, atmospheric residue, vacuum residue, atmospheric wax oil, vacuum wax oil, straight-run wax oil, propane light / heavy deoiling, coking wax oil, and coal liquids. In the catalytic cracking reaction of petroleum hydrocarbons, the catalytic cracking aid of the present invention can achieve excellent cracking conversion and low-carbon olefin yield, as well as a high liquefied gas yield.

[0032] In order to achieve the above object, the present invention further provides a method for preparing a catalytic cracking catalyst, which comprises vigorously mixing and stirring a Y-type molecular sieve, a phosphorus-modified MFI structure molecular sieve prepared by the method for preparing a phosphorus-modified MFI structure molecular sieve of the present invention, an inorganic binder, and optionally a second clay with water, and then spray-drying the mixture to prepare a catalytic cracking catalyst.

[0033] In the method for preparing a catalytic cracking catalyst of the present invention, the binder is a phosphorus-aluminum inorganic binder. The phosphorus-aluminum inorganic binder is a phosphorus-aluminum adhesive and / or a first clay-containing phosphorus-aluminum inorganic binder. The first clay-containing phosphorus-aluminum inorganic binder contains, on a dry weight basis, 10 to 40 wt %, for example, 15 to 40 wt %, of an aluminum component based on Al2O3, 45 to 90 wt %, or 45 to 80 wt %, of a phosphorus component based on P2O5, and a first clay that is greater than 0 and not greater than 40 wt %. The first clay-containing phosphorus-aluminum inorganic binder has a P / Al weight ratio of 1.0 to 6.0, a pH of 1 to 3.5, and a solids content of 15 to 60 wt %. The first clay includes at least one of kaolin, sepiolite, attapulgite, rectorite, smectite, and diatomaceous earth.

[0034] In the method for preparing a catalytic cracking catalyst of the present invention, the second clay is at least one selected from kaolin, sepiolite, attapulgite, rectorite, smectite, metahalloysite, halloysite, hydrotalcite, bentonite, and diatomaceous earth.

[0035] In the method for preparing a catalytic cracking catalyst of the present invention, the binder contains, based on the catalytic cracking catalyst, 3 to 39 wt % of a phosphorus-aluminum inorganic binder on a dry basis and 1 to 30 wt % of another inorganic binder on a dry basis, the other inorganic binder including at least one of pseudoboehmite, alumina sol, silica-alumina sol, and water glass.

[0036] The method for preparing a catalytic cracking catalyst of the present invention includes first calcining, washing, and optionally drying the product obtained by spray drying to obtain a catalytic cracking catalyst. In the first calcination, the calcination temperature is 300 to 650°C, the calcination time is 0.5 to 8 hours, the drying temperature is 100 to 200°C, and the drying time is 0.5 to 24 hours.

[0037] The method for preparing a catalytic cracking catalyst of the present invention may further include vigorously mixing and stirring an alumina source, the first clay, and water to disperse them into a slurry with a solids content of 5 to 48% by weight, adding concentrated phosphoric acid to the slurry with stirring at a weight ratio of P / Al of 1 to 6, and reacting the resulting mixed slurry at 50 to 99°C for 15 to 90 minutes to prepare the first clay-containing phosphorus-aluminum inorganic binder. The alumina source is aluminum hydroxide and / or alumina that can be peptized with acid, and the amount of the first clay used on a dry weight basis is more than 0 parts by weight and not more than 40 parts by weight relative to 10 to 40 parts by weight, for example, 15 to 40 parts by weight, of the alumina source based on Al2O3. In the P / Al ratio, P is the weight of phosphorus as a simple substance in the phosphoric acid, and Al is the weight of aluminum as a simple substance in the alumina source.

[0038] To achieve the above object, the present invention provides an application of a catalytic cracking catalyst, i.e., a method for catalytically cracking hydrocarbon oils, comprising catalytically reacting hydrocarbon oils with the catalytic cracking catalyst under catalytic cracking conditions. The catalytic cracking conditions include a reaction temperature of 500 to 800°C, and the hydrocarbon oil being one or more selected from crude oil, naphtha, gasoline, atmospheric residue, vacuum residue, atmospheric wax oil, vacuum wax oil, straight-run wax oil, propane light / heavy deoiling, coked wax oil, and coal liquids. In the catalytic cracking reaction of petroleum hydrocarbons, the catalytic cracking catalyst of the present invention can achieve excellent cracking conversion and low-carbon olefin yield, as well as a high liquefied gas yield.

[0039] [Specific Embodiments] Specific embodiments of the present invention will be described in detail below. It should be understood that the specific embodiments described herein are used only to illustrate and explain the present invention, and are not intended to limit the present invention.

[0040] In the present invention, pores having a pore diameter of less than 2 nm are called micropores, pores having a pore diameter of more than 50 nm are called macropores, and pores having a pore diameter of 2 to 50 nm are called mesopores.

[0041] In the present invention, the term "first clay" refers to a clay contained in the phosphorus-aluminum inorganic binder, and the term "second clay" refers to a clay other than the first clay, and the terms "first" and "second" are used only to distinguish whether the clay is contained in the phosphorus-aluminum inorganic binder or not. The first clay includes, but is not limited to, kaolin, sepiolite, attapulgite, rectorite, smectite, and diatomaceous earth. The second clay includes, but is not limited to, kaolin, sepiolite, attapulgite, rectorite, smectite, diatomaceous earth, metahalloysite, halloysite, hydrotalcite, and bentonite.

[0042] In the present invention, the inorganic binder and the binder have the same meaning.

[0043] The binders of the present invention include phosphorus-aluminum inorganic binders and other inorganic binders.

[0044] According to the present invention, other inorganic binders refer to binders other than binders containing both phosphorus and aluminum elements, and phosphorus-aluminum inorganic binders include phosphorus-aluminum adhesives and first clay-containing phosphorus-aluminum inorganic binders.

[0045] In accordance with the present invention, examples of other inorganic binders include, but are not limited to, pseudoboehmite, alumina sol, silica-alumina sol, and water glass.

[0046] According to the present invention, the active ingredient in the phosphorus-aluminum adhesive is aluminum dihydrogen phosphate, with a theoretical molar ratio of P2O5 / Al2O3 = 3:1. The phosphorus-aluminum adhesive can be used as a binder to prepare catalysts with excellent strength. In the present invention, the actual ratio of P2O5 / Al2O3 in the phosphorus-aluminum adhesive is 3:1 or more, for example, 3:1 to 10:1, or even more, for example, greater than 3:1 and less than 5:1. For example, the alumina source and water are vigorously mixed and stirred to disperse them into a slurry, and concentrated phosphoric acid is added to the slurry while stirring. The resulting mixed slurry is reacted for a certain period of time (for example, at 50 to 99°C for 15 to 90 minutes), thereby obtaining a phosphorus-aluminum adhesive. The alumina source is at least one selected from ρ-alumina, x-alumina, η-alumina, γ-alumina, κ-alumina, σ-alumina, θ-alumina, gibbsite, bayerite, nordstrandite, diaspore, boehmite, and pseudoboehmite. The concentration of concentrated phosphoric acid may be 60 to 98 wt %, further, for example, 75 to 90 wt %, and the supply rate of phosphoric acid may be, for example, 0.01 to 0.10 kg phosphoric acid / min / kg alumina source, further, for example, 0.03 to 0.07 kg phosphoric acid / min / kg alumina source.

[0047] According to the present invention, the first clay-containing phosphorus-aluminum inorganic binder contains, on a dry weight basis, 10 to 40 wt %, for example, 15 to 40 wt %, based on Al2O3, an aluminum component, 45 to 90 wt %, for example, 45 to 80 wt %, based on P2O5, a phosphorus component, and more than 0 and not more than 40 wt % of a first clay, and the first clay-containing phosphorus-aluminum inorganic binder has a P / Al weight ratio of 1.0 to 6.0, a pH of 1 to 3.5, and a solid content of 15 to 60 wt %.

[0048] According to the present invention, a first clay-containing phosphorus-aluminum inorganic binder can be prepared by the following method: An alumina source, a first clay, and water are vigorously mixed and stirred to disperse them into a slurry with a solids content of 5 to 48% by weight, the alumina source being acid-peptizable aluminum hydroxide and / or alumina, and the amount of the first clay used on a dry weight basis is greater than 0 parts by weight and not more than 40 parts by weight per 10 to 40 parts by weight, e.g., 15 to 40 parts by weight, of the alumina source based on Al2O3. Concentrated phosphoric acid is added to the slurry under stirring at a weight ratio of P / Al=1 to 6, and the resulting mixed slurry is reacted at 50 to 99°C for 15 to 90 minutes, where P is the weight of phosphorus as a simple substance in the phosphoric acid and Al is the weight of aluminum as a simple substance in the alumina source. The alumina source is at least one selected from ρ-alumina, x-alumina, η-alumina, γ-alumina, κ-alumina, σ-alumina, θ-alumina, gibbsite, bayerite, nordstrandite, diaspore, boehmite, and pseudoboehmite, the concentration of the concentrated phosphoric acid may be 60 to 98% by weight, further, for example, 75 to 90% by weight, and the supply rate of phosphoric acid may be, for example, 0.01 to 0.10 kg phosphoric acid / minute / kg alumina source, further, for example, 0.03 to 0.07 kg phosphoric acid / minute / kg alumina source.

[0049] The present invention relates to a molecular sieve having a K value that satisfies 70%≦K≦90%, for example, 75%≦K≦90%, further for example, 78%≦K≦85%, where K=mass content of phosphorus in a region having an area of ​​100 square nanometers and a vertical depth of 5 to 10 nm on any crystal face of the molecular sieve crystal grain, as measured by EPMA method / mass content of phosphorus in a region having an area of ​​100 square nanometers and a vertical depth of 0 to 2 nm on any crystal face of the molecular sieve crystal grain, as measured by XPS method×100%. XPS analysis of the molecular sieve surface is performed using a Thermo Fisher-VG ESCAREB 250 X-ray photoelectron spectrometer with a 150 W output monochromatic AlKα X-ray as an excitation source, and the charge shift is calibrated with the C1s peak (284.8 eV) of contaminating carbon. A JXA-8230 energy spectrometer X-ray detector is used, and the total counts are generally 105 Larger, count rate 10 3 ~10 4 The phosphorus-modified MFI structure molecular sieve is characterized in that the counting time is 10 to 100 seconds, and the molecular sieve surface is subjected to EPMA analysis.

[0050] In the phosphorus-modified MFI molecular sieve, the molar ratio of the phosphorus content to the alumina content on a P2O5 basis is ≥ 0.01, e.g., ≥ 0.2, ≥ 0.3, or even 0.4 to 0.7. For example, the phosphorus-modified MFI molecular sieve is a microporous ZSM-5 molecular sieve or a ZSM-5 molecular sieve with a hierarchical structure. For example, the microporous ZSM-5 molecular sieve has a silica / alumina molar ratio of 15 to 1000, e.g., 20 to 200. The hierarchical ZSM-5 molecular sieve has a mesopore volume ratio of more than 10% to the total pore volume, an average pore diameter of 2 to 20 nm, and a silica / alumina molar ratio of 15 to 1000, e.g., 20 to 200.

[0051] The present invention further provides a method for preparing the phosphorus-modified MFI molecular sieve. The phosphorus-modified MFI molecular sieve can be obtained by a dipping method comprising: mixing and contacting an aqueous solution of a phosphorus-containing compound at 40 to 150°C, for example, 50 to 150°C, further for example, 70 to 130°C, with an MFI molecular sieve at 40 to 150°C, for example, 50 to 150°C, further for example, 70 to 130°C, at substantially the same temperature for 0.1 hours or more; drying; and then calcining at 200 to 600°C in an air or steam atmosphere for 0.1 hours or more; or vigorously mixing and stirring the phosphorus-containing compound, the MFI molecular sieve, and water to form a slurry; adjusting (heating) the temperature to 40 to 150°C, for example, 50 to 150°C, further for example, 70 to 130°C; maintaining the slurry for 0.1 hours or more; drying; and calcining at 200 to 600°C in an air or steam atmosphere for 0.1 hours or more.

[0052] According to the preparation method of the phosphorus-modified MFI molecular sieve, the MFI molecular sieve may be a hydrogen-type microporous ZSM-5 molecular sieve or a hydrogen-type hierarchical ZSM-5 molecular sieve. It is obtained by ammonium exchange to reduce the sodium content to <0.1 wt% NaO and has a silica / alumina ratio (molar ratio of silicon oxide to aluminum oxide) of ≥10, typically 10-200.

[0053] According to the method for preparing the phosphorus-modified MFI molecular sieve, the molar ratio of the phosphorus-based (oxide-based) phosphorus-containing compound to the aluminum-based (oxide-based) hydrogen-type ZSM-5 molecular sieve or hydrogen-type hierarchical ZSM-5 molecular sieve is 0.01 to 2, for example, 0.1 to 1.5, further for example, 0.2 to 1.5. The phosphorus-containing compound is selected from one or a mixture of organic phosphorus compounds such as trimethyl phosphate, triphenylphosphine, trimethyl phosphite, tetrabutyl phosphonium bromide, tetrabutyl phosphonium chloride, tetrabutyl phosphonium hydroxide, triphenylethyl phosphonium bromide, triphenylbutyl phosphonium bromide, triphenylbenzyl phosphonium bromide, hexamethylphosphoric triamide, dibenzyldiethylphosphoramidite, and 1,3-bis((triethylphosphanyl)methyl)benzene; and inorganic phosphorus compounds such as phosphoric acid, ammonium hydrogen phosphate, diammonium hydrogen phosphate, ammonium phosphate, and boron phosphate. The present inventors have found that using boron phosphate as one of the phosphorus-containing compounds and performing hydrothermal calcination at 300 to 500°C results in better dispersion of phosphorus in the molecular sieve. Therefore, for example, a combination of phosphorus-containing compounds is a mixture of boron phosphate and one or more compounds selected from trimethyl phosphate, triphenylphosphine, trimethyl phosphite, phosphoric acid, ammonium hydrogen phosphate, diammonium hydrogen phosphate, and ammonium phosphate. In the boron phosphate-containing mixture, the weight percentage of boron phosphate is 10% to 80%, for example, 20% to 40%, or further, for example, 25% to 35%.

[0054] According to the method for preparing a phosphorus-modified MFI molecular sieve, contacting involves contacting an aqueous solution of a phosphorus-containing compound at 30 to 150°C with a hydrogen-type MFI molecular sieve at 30 to 150°C for at least 0.1 hours at substantially the same temperature by immersion. Contacting at a relatively high temperature range of 40°C or higher, such as 50 to 150°C, or even 70 to 130°C, produces better results, i.e., improved dispersion of phosphorus species, facilitating phosphorus migration into the interior of the hydrogen-type MFI molecular sieve crystals and bonding with framework aluminum, further improving the coordination between phosphorus and framework aluminum, and ultimately contributing to improved hydrothermal stability of the molecular sieve. The term "substantially the same temperature" refers to a temperature difference of within ±5°C between the aqueous solution of the phosphorus-containing compound and the hydrogen-type MFI molecular sieve. For example, if the aqueous solution of the phosphorus-containing compound is at 80°C, the HZSM-5 molecular sieve must be heated to 75 to 85°C.

[0055] According to the method for preparing the phosphorus-modified MFI molecular sieve, the contacting step may involve mixing a phosphorus-containing compound, a (hydrogen-type) MFI molecular sieve, and water, and then maintaining the mixture at 30 to 150°C for 0.1 hours or more. For example, to obtain a better effect, i.e., to improve the dispersion of phosphorus species, facilitate the migration of phosphorus into the crystal interior of the hydrogen-type MFI molecular sieve and its bonding with framework aluminum, further improve the degree of coordination between phosphorus and framework aluminum, and ultimately contribute to improving the hydrothermal stability of the molecular sieve, the phosphorus-containing compound, the hydrogen-type MFI molecular sieve, and water may be mixed and then maintained at a relatively high temperature of 40°C or higher, for example, 50 to 150°C, or even 70 to 130°C, for 0.1 hours.

[0056] According to the method for preparing phosphorus-modified MFI molecular sieve, the weight ratio of water / molecular sieve is 0.5-1, and the time is 0.5-40 hours. The calcination is carried out at 450-550°C in a water vapor atmosphere.

[0057] The present invention relates to a catalytic cracking aid comprising 5 to 75 wt % of a phosphorus-modified MFI structured molecular sieve based on the dry weight of the catalytic cracking aid, wherein K=mass content of phosphorus in an area having an area of ​​100 square nanometers and a vertical depth of 5 to 10 nm on any crystal face of the crystal grain of the molecular sieve, as measured by EPMA method / mass content of phosphorus in an area having an area of ​​100 square nanometers and a vertical depth of 0 to 2 nm on any crystal face of the crystal grain of the molecular sieve, as measured by XPS method × 100%. XPS analysis of the molecular sieve surface was performed using a Thermo Fisher-VG ESCAREB 250 X-ray photoelectron spectrometer with a 150 W output monochromatic AlKα X-ray as the excitation source, correcting the charge shift with the C1s peak (284.8 eV) of contaminating carbon, and a JXA-8230 energy spectrometer X-ray detector. The total counts were generally 10 5 Larger, count rate 10 3 ~10 4 The counting time is 10 to 100 seconds, and the catalytic cracking aid is further provided for performing EPMA analysis of the molecular sieve surface.

[0058] In the catalytic cracking aid of the present invention, the K value of the phosphorus-modified MFI molecular sieve satisfies 75%≦K≦90%, for example, 78%≦K≦85%.

[0059] In the catalytic cracking aid of the present invention, for the phosphorus-modified MFI structure molecular sieve, the molar ratio of the phosphorus content to the alumina content on a P2O5 basis is ≧0.01, for example ≧0.2, ≧0.3, further for example 0.4-0.7.

[0060] In the catalytic cracking aid of the present invention, for example, the phosphorus-modified MFI molecular sieve is a microporous ZSM-5 molecular sieve or a ZSM-5 molecular sieve having a hierarchical structure. The microporous ZSM-5 molecular sieve has a silica / alumina molar ratio of 15 to 1000, for example, 20 to 200. The hierarchical ZSM-5 molecular sieve has a mesopore volume ratio to total pore volume of more than 10%, an average pore diameter of 2 to 20 nm, and a silica / alumina molar ratio of 15 to 1000, for example, 20 to 200.

[0061] The catalytic cracking aid of the present invention contains, on a dry basis of the catalytic cracking aid, 5 to 75 wt %, for example, 8 to 60 wt %, of the phosphorus-modified MFI molecular sieve. It may further contain 1 to 40 wt % of a binder and 0 to 65 wt % of a second clay. The binder may be an inorganic oxide binder commonly used as a binder component for catalysts or additives, as known to those skilled in the art. For example, it may be one or more of pseudoboehmite, alumina sol, silica-alumina sol, and water glass. For example, the binder may be a phosphorus-aluminum inorganic binder, i.e., a phosphorus-aluminum inorganic binder or a mixture of a phosphorus-aluminum inorganic binder with another inorganic binder.

[0062] In the catalytic cracking aid of the present invention, the phosphorus-aluminum inorganic binder is, for example, a phosphorus-aluminum adhesive and / or a first clay-containing phosphorus-aluminum inorganic binder. The first clay-containing phosphorus-aluminum inorganic binder, on a dry basis, contains 10 to 40 wt%, 15 to 40 wt%, 10 to 35 wt%, or 15 to 35 wt% of an aluminum component based on Al2O3, 45 to 90 wt%, 45 to 80 wt%, or 50 to 75 wt% of a phosphorus component based on P2O5, and a first clay of more than 0 to 40 wt%, for example, 8 to 35 wt%, on a dry basis. The first clay-containing phosphorus-aluminum inorganic binder has a P / Al weight ratio of 1.0 to 6.0, for example, 1.2 to 6.0, or even 2.0 to 5.0, a pH of 1 to 3.5, or 2.0 to 3.0, and a solids content of 15 to 60 wt%. For example, in one specific embodiment of the phosphorus-aluminum inorganic binder, based on the dry weight of the phosphorus-aluminum inorganic binder, the phosphorus-aluminum inorganic binder comprises 20-40 wt. % aluminum component based on Al2O3 and 60-80 wt. % phosphorus component based on P2O5.

[0063] In the catalytic cracking aid of the present invention, the first clay may be at least one selected from kaolin, sepiolite, attapulgite, rectorite, smectite, and diatomaceous earth. The other inorganic binder may be one or more inorganic oxide binders conventionally used in the binder component of catalytic cracking aids or catalysts, excluding phosphorus-aluminum adhesives and phosphorus-aluminum inorganic binders, such as at least one selected from pseudoboehmite, alumina sol, silica-alumina sol, and water glass, and further at least one selected from pseudoboehmite and alumina sol.

[0064] The catalytic cracking aid of the present invention further comprises 0 to 65 wt %, for example 5 to 55 wt %, of a second clay, based on the dry weight of the catalytic cracking aid. The second clay is also at least one selected from kaolin, sepiolite, attapulgite, rectorite, smectite, metahalloysite, halloysite, hydrotalcite, bentonite, and diatomaceous earth, which are well known to those skilled in the art.

[0065] In one specific embodiment of the catalytic cracking aid of the present invention, the catalytic cracking aid comprises, on a dry basis, 20-60 wt % of the phosphorus-modified MFI structured molecular sieve, 5-35 wt % of the binder, and 5-55 wt % of the second clay.

[0066] The present invention also provides a method for preparing a catalytic cracking aid, comprising vigorously mixing and stirring the phosphorus-modified MFI structured molecular sieve of the present invention, a binder, and optionally a second clay with water, and spray-drying to obtain the catalytic cracking aid.

[0067] In the method for preparing a catalytic cracking aid, the binder comprises a phosphorus-aluminum inorganic binder and other inorganic binders, and the weight ratio of the phosphorus-modified MFI structured molecular sieve to the phosphorus-aluminum inorganic binder to the other inorganic binders is (10-75):(3-39):(1-30) on a dry basis, and may be, for example, (10-75):(8-35):(5-25). The phosphorus-aluminum inorganic binder may be a phosphorus-aluminum adhesive and / or a first clay-containing phosphorus-aluminum inorganic binder. The other inorganic binder may include at least one of pseudoboehmite, alumina sol, silica-alumina sol, and water glass. The preparation method may include "mixing" or "vigorously mixing and stirring (with water)" the phosphorus-modified MFI structured molecular sieve, the phosphorus-aluminum inorganic binder, and the other inorganic binders. The order of feeding is not particularly limited. For example, the phosphorus-aluminum inorganic binder, other inorganic binders, phosphorus-modified MFI molecular sieve, and second clay (if no second clay is present, the corresponding supply step can be omitted) can be mixed and then vigorously mixed and stirred with water. Alternatively, the second clay, phosphorus-modified MFI molecular sieve, and other inorganic binders can be vigorously mixed and stirred with water, and then the phosphorus-aluminum inorganic binder can be added. This can contribute to improving the activity and selectivity of the auxiliary.

[0068] The method for preparing a catalytic cracking aid further includes a step of spray-drying the slurry obtained by "vigorously mixing and stirring with water." The spray-drying method is not particularly limited in the present invention and may be any method known to those skilled in the art. Optionally, the preparation method may further include subjecting the product obtained by spray-drying to a first calcination, washing, and optionally drying treatment to obtain a catalytic cracking aid. Here, for the first calcination, the calcination temperature may be 300 to 650°C, for example, 400 to 600°C, or further, for example, 450 to 550°C, and the calcination time may be 0.5 to 8 hours. For washing, any one of ammonium sulfate, ammonium chloride, and ammonium nitrate may be used, the washing temperature may be 40 to 70°C, the drying temperature may be 100 to 200°C, for example, 100 to 150°C, and the drying time may be 0.5 to 24 hours, for example, 1 to 12 hours.

[0069] In one specific embodiment of the method for preparing a catalytic cracking aid, a binder, a second clay, and water (e.g., decationized water and / or deionized water) are mixed to form a slurry with a solids content of 10 to 50% by weight. The slurry is thoroughly stirred, and the pH of the slurry is adjusted to 1 to 4 with an inorganic acid such as hydrochloric acid, nitric acid, phosphoric acid, or sulfuric acid. The pH is maintained at this level and aged at 20 to 80°C for 0 to 2 hours (e.g., 0.3 to 2 hours). An inorganic binder such as alumina sol and / or silica sol is then added, and the mixture is stirred for 0.5 to 1.5 hours to form a gel. Next, a phosphorus-modified MFI structured molecular sieve is added to form an aid slurry with a solids content of 20 to 45% by weight. The slurry is continuously stirred and spray-dried to form a microsphere aid. Thereafter, the microsphere auxiliary agent is subjected to a first calcination, for example, at 350 to 650°C, 400 to 600°C, or 450 to 550°C for 0.5 to 6 hours or 0.5 to 2 hours, and then washed with ammonium sulfate (the washing temperature may be 40 to 70°C, and the weight ratio of ammonium sulfate:microsphere auxiliary agent:water is 0.2 to 0.8:1:5 to 15) until the sodium oxide content is less than 0.25% by weight, and then washed with water, filtered, and dried.

[0070] In one specific embodiment of the method for preparing a catalytic cracking aid, phosphorus-modified MFI structure molecular sieve, second clay (e.g., kaolin), and binder (e.g., pseudoboehmite) are mixed with water (e.g., deionized water and / or deionized water) and an inorganic binder such as alumina sol and / or silica sol, and the mixture is vigorously mixed and stirred for 0.1 to 10 hours (e.g., 120 minutes) to form a slurry with a solids content of 10 to 50% by weight (e.g., 30% by weight). An inorganic acid such as hydrochloric acid, nitric acid, phosphoric acid, or sulfuric acid is added to adjust the pH of the slurry to 1 to 4 (e.g., 3.0), and the mixture is then vigorously mixed and stirred for 0.1 to 10 hours (e.g., 45 minutes). Next, a phosphorus-aluminum inorganic binder is added and stirred for 0.1 to 10 hours (e.g., 30 minutes). The resulting slurry is spray-dried to obtain microspheres. The microspheres are calcined at 350 to 650°C or 400 to 600°C (for example, 500°C) for 0.5 to 6 hours or 0.5 to 2 hours (for example, 1 hour) to prepare a catalytic cracking aid.

[0071] In a specific embodiment of the method for preparing a catalytic cracking aid, a binder (e.g., alumina sol) and a second clay (e.g., kaolin) are mixed, and water (e.g., decationized water and / or deionized water) is added to form a slurry with a solid content of 10 to 50% by weight (e.g., 30% by weight). The slurry is stirred thoroughly, and the pH of the slurry is adjusted to 1 to 4 (e.g., 2.8) using an inorganic acid such as hydrochloric acid, nitric acid, phosphoric acid, or sulfuric acid. The slurry is then aged at 20 to 80°C (e.g., 55°C) for 0.1 to 2 hours (e.g., 1 hour). Then, a phosphorus-modified MFI molecular sieve is added to form a slurry with a solid content of 10 to 50% by weight (e.g., 35% by weight). The slurry is stirred and spray-dried to form a microsphere aid. Next, the microsphere auxiliary agent is subjected to a first calcination, for example, at 350 to 650°C, 400 to 600°C, or 450 to 550°C for 0.5 to 6 hours or 0.5 to 2 hours (for example, 1 hour at 500°C), and then washed with ammonium sulfate (the washing temperature may be 40 to 70°C, for example, 60°C, and the ammonium sulfate:microsphere auxiliary agent:water ratio is 0.2 to 0.8:1:5 to 15 (weight ratio, for example, 0.5:1:10)) until the sodium oxide content is less than 0.25% by weight, washed with water, filtered, and dried (for example, at 100 to 200°C (for example, 110°C)).

[0072] The method for preparing a catalytic cracking aid may further include preparing a first clay-containing phosphorus-aluminum inorganic binder by the following steps: An alumina source, a first clay, and water are vigorously mixed and stirred to disperse them into a slurry with a solids content of 5 to 48% by weight. The alumina source is aluminum hydroxide and / or alumina that can be peptized with acid. The amount of the first clay used on a dry weight basis is greater than 0 parts by weight and not more than 40 parts by weight, relative to 10 to 40 parts by weight, e.g., 15 to 40 parts by weight, of the alumina source based on Al2O3. Concentrated phosphoric acid is added to the slurry with stirring at a weight ratio of P / Al = 1 to 6, and the resulting mixed slurry is reacted at 50 to 99°C for 15 to 90 minutes. In P / Al, P is the weight of phosphorus as a simple substance in the phosphoric acid, and Al is the weight of aluminum as a simple substance in the alumina source. The alumina source is at least one selected from ρ-alumina, x-alumina, η-alumina, γ-alumina, κ-alumina, σ-alumina, θ-alumina, gibbsite, bayerite, nordstrandite, diaspore, boehmite, and pseudoboehmite, and the aluminum component in the first clay-containing phosphorus-aluminum inorganic binder is derived from the alumina source. The first clay may be one or more of kaolin, sepiolite, attapulgite, rectorite, smectite, and diatomaceous earth, for example, rectorite. The concentration of the concentrated phosphoric acid is 60 to 98 wt %, further for example, 75 to 90 wt %. The supply rate of phosphoric acid may be, for example, 0.01 to 0.10 kg phosphoric acid / min / kg alumina source, further for example, 0.03 to 0.07 kg phosphoric acid / min / kg alumina source.

[0073] In the method for preparing a catalytic cracking aid, the introduction of clay into the first clay-containing phosphorus-aluminum inorganic binder not only improves mass transfer and heat transfer between materials during the preparation process, but also prevents binder solidification due to excessive temperatures caused by localized violent reactions of heterogeneous materials and heat release, and the resulting binder has binding performance equivalent to that of a phosphorus-aluminum binder prepared by a method without introducing clay.In addition, the introduction of clay, especially rectorite with a layered structure, can improve the heavy oil conversion ability of the catalytic composition and the selectivity of the resulting aid.

[0074] Furthermore, the present invention provides an application of the catalytic cracking aid, i.e., a method for catalytically cracking a hydrocarbon oil, which comprises catalytically reacting a hydrocarbon oil with the catalytic cracking aid of the present invention under catalytic cracking conditions.

[0075] The method for catalytic cracking of hydrocarbon oil of the present invention comprises catalytically reacting hydrocarbon oil with a catalytic mixture containing a catalytic cracking aid and a catalytic cracking catalyst under catalytic cracking conditions, wherein the content of the catalytic cracking aid in the catalytic mixture is 0.1 to 30% by weight.

[0076] Optionally, the catalytic cracking conditions include a reaction temperature of 500 to 800°C, and the hydrocarbon oil is one or more selected from crude oil, naphtha, gasoline, atmospheric residue, vacuum residue, atmospheric wax oil, vacuum wax oil, straight run wax oil, propane light / heavy deoiling, coking wax oil, and coal liquid.

[0077] The present invention also provides a catalytic cracking catalyst, on a dry basis of the catalyst, comprising 1-25 wt % of a Y-type molecular sieve, 5-50 wt % of a phosphorus-modified MFI structured molecular sieve, 1-60 wt % of an inorganic binder, and optionally 0-60 wt % of a second clay, wherein the inorganic binder comprises a phosphorus-aluminum inorganic binder and / or other inorganic binder, and the phosphorus-modified MFI structured molecular sieve has a K value satisfying 70%≦K≦90%, where K=mass content of phosphorus in an area having an area of ​​100 square nanometers and a vertical depth of 5-10 nm on any crystal face of the molecular sieve crystal grain, as measured by an EPMA method / mass content of phosphorus in an area having an area of ​​100 square nanometers and a vertical depth of 0-2 nm on any crystal face of the molecular sieve crystal grain, as measured by an XPS method×100%, and ESCAREB from Thermo Fisher Scientific, VG. Using a 250-type X-ray photoelectron spectrometer, the excitation source was set to monochromatic AlKα X-rays with an output of 150 W, and the charge shift was calibrated with the C1s peak (284.8 eV) of contaminating carbon. XPS analysis of the molecular sieve surface was performed. A JXA-8230 energy spectrometer X-ray detector was used, and the total counts were generally 10 5 Larger, count rate 10 3 ~10 4 The counting time is 10 to 100 seconds, and EPMA analysis of the molecular sieve surface is performed to provide a catalytic cracking catalyst.

[0078] In the catalytic cracking catalyst of the present invention, the Y-type molecular sieve includes at least one of a PSRY-type molecular sieve, a rare earth-containing PSRY-type molecular sieve, a USY-type molecular sieve, a rare earth-containing USY-type molecular sieve, a REY-type molecular sieve, a REHY-type molecular sieve, and a HY-type molecular sieve.

[0079] In the catalytic cracking catalyst of the present invention, the phosphorus-modified MFI molecular sieve has a K value that satisfies 75%≦K≦90%, for example, 78%≦K≦85%.

[0080] In the catalytic cracking catalyst of the present invention, the phosphorus-modified MFI structure molecular sieve has a molar ratio of phosphorus content to alumina content based on P2O5 of ≧0.01, for example ≧0.2, ≧0.3, further for example 0.4-0.7.

[0081] In the catalytic cracking of the present invention, for example, the phosphorus-modified MFI molecular sieve is a microporous ZSM-5 molecular sieve or a ZSM-5 molecular sieve with a hierarchical structure. The microporous ZSM-5 molecular sieve has a silica / alumina molar ratio of 15 to 1000, for example, 20 to 200. The hierarchical ZSM-5 molecular sieve has a mesopore volume ratio to total pore volume of more than 10%, an average pore diameter of 2 to 20 nm, and a silica / alumina molar ratio of 15 to 1000, for example, 20 to 200.

[0082] For example, the catalytic cracking catalyst of the present invention may contain, on a dry basis of the catalyst, 2-20 wt% of Y-type molecular sieve, 10-40 wt% or 20-40 wt% of phosphorus-modified MFI molecular sieve, and may further contain 1-40 wt% of inorganic binder and 0-50 wt% of second clay. Furthermore, for example, on a dry basis of the catalyst, the catalytic cracking catalyst may contain, for example, 3-40 wt% of phosphorus-aluminum inorganic binder, or 3-40 wt% of phosphorus-aluminum inorganic binder and 1-30 wt% of other inorganic binder.

[0083] In the catalytic cracking catalyst of the present invention, the phosphorus-aluminum inorganic binder is a phosphorus-aluminum adhesive and / or a first clay-containing phosphorus-aluminum inorganic binder, which, on a dry basis, contains 10 to 40 wt %, for example, 15 to 40 wt %, of an aluminum component based on Al2O3, 45 to 90 wt %, for example, 45 to 80 wt %, of a phosphorus component based on P2O5, and a first clay content of more than 0 to 40 wt % on a dry weight basis, and the first clay-containing phosphorus-aluminum inorganic binder has a P / Al weight ratio of 1.0 to 6.0, a pH of 1 to 3.5, and a solid content of 15 to 60 wt %.

[0084] In the catalytic cracking process of the present invention, the first clay comprises at least one of kaolin, sepiolite, attapulgite, rectorite, smectite, and diatomaceous earth.

[0085] In one specific embodiment of the phosphorus-aluminum inorganic binder in the catalytic cracking catalyst of the present invention, the phosphorus-aluminum inorganic binder contains, on a dry weight basis, 10 to 40 wt %, for example, 15 to 40 wt %, of an aluminum component based on Al2O3, 45 to 90 wt %, for example, 45 to 80 wt %, of a phosphorus component based on P2O5, and 0 to 40 wt %, of a first clay. Furthermore, the phosphorus-aluminum inorganic binder has a P / Al weight ratio of 1.0 to 6.0, a pH of 1 to 3.5, and a solids content of 15 to 60 wt %. For example, the binder contains 15 to 35 wt %, of an aluminum component based on Al2O3, 50 to 75 wt %, of a phosphorus component based on P2O5, and 8 to 35 wt %, of a first clay, a P / Al weight ratio of 1.2 to 6.0, for example, 2.0 to 5.0, and a pH of 2.0 to 3.0.

[0086] In another specific embodiment of the phosphorus-aluminum inorganic binder in the catalytic cracking catalyst of the present invention, the phosphorus-aluminum inorganic binder contains, on a dry weight basis of the phosphorus-aluminum inorganic binder, 20 to 40 wt % of an aluminum component based on Al2O3 and 60 to 80 wt % of a phosphorus component based on P2O5.

[0087] In the catalytic cracking catalyst of the present invention, the other inorganic binder may be one or more selected from inorganic oxide binders conventionally used in catalytic cracking catalysts or binder components of catalysts, excluding the phosphorus-aluminum adhesive and the phosphorus-aluminum inorganic binder, such as at least one selected from pseudoboehmite, alumina sol, silica-alumina sol, and water glass, and further at least one selected from pseudoboehmite and alumina sol.

[0088] The catalytic cracking catalyst of the present invention further comprises 0 to 65 wt %, for example, 5 to 55 wt %, of a second clay on a dry basis, which is at least one selected from kaolin, sepiolite, attapulgite, rectorite, smectite, metahalloysite, halloysite, hydrotalcite, bentonite, and diatomaceous earth, which are well known to those skilled in the art.

[0089] In addition, the present invention further provides a method for preparing a catalytic cracking catalyst, which comprises vigorously mixing and stirring a Y-type molecular sieve, a phosphorus-modified MFI structure molecular sieve, an inorganic binder, and optionally a second clay, followed by spray drying to obtain a catalytic cracking catalyst.

[0090] The method for preparing a catalytic cracking catalyst of the present invention may further include washing and optionally drying the product obtained by the calcination treatment to obtain a catalytic cracking catalyst. Here, the calcination temperature may be 300 to 650°C, for example, 400 to 600°C, or further, for example, 450 to 550°C, and the calcination time may be 0.5 to 12 hours. For washing, any one of ammonium sulfate, ammonium nitrate, and ammonium chloride may be used, the washing temperature may be 40 to 80°C, the drying temperature may be 110 to 200°C, for example, 120 to 150°C, and the drying time may be 0.5 to 18 hours, or 2 to 12 hours.

[0091] In a specific embodiment of the catalytic cracking catalyst preparation method of the present invention, an inorganic binder (e.g., pseudoboehmite, alumina sol, silica sol, silica-alumina gel, or a mixture of two or more thereof) is mixed with a second clay (e.g., kaolin) and water (e.g., decationized water and / or deionized water) to prepare a slurry with a solids content of 10 to 50 wt. %. The slurry is thoroughly stirred, and the pH of the slurry is adjusted to 1 to 4 with an inorganic acid such as hydrochloric acid, nitric acid, phosphoric acid, or sulfuric acid. The pH is maintained at this level and aged at 20 to 80°C for 0 to 2 hours (e.g., 0.3 to 2 hours). Alumina sol and / or silica sol are then added and stirred for 0.5 to 1.5 hours to form a gel. Next, molecular sieves (including phosphorus-modified ZSM-5 molecular sieves and Y-type molecular sieves) are added to form a catalyst slurry with a solids content of 20 to 45 wt. %. The catalyst slurry is then stirred and spray-dried to form a microsphere catalyst. Thereafter, the microsphere catalyst is calcined, for example, at 350 to 650°C, 400 to 600°C, or 450 to 550°C for 0.5 to 6 hours or 0.5 to 2 hours, and then washed with ammonium sulfate (the washing temperature may be 40 to 70°C, and the weight ratio of ammonium sulfate:microsphere catalyst:water=0.2 to 0.8:1:5 to 15) until the sodium oxide content is less than 0.25% by weight, washed with water, filtered, and dried.

[0092] In one specific embodiment of the catalytic cracking catalyst preparation method of the present invention, phosphorus-modified ZSM-5 molecular sieve, Y-type molecular sieve, secondary clay (e.g., kaolin), and inorganic binder (e.g., pseudoboehmite, alumina sol, silica sol, silica-alumina gel, or a mixture of two or more thereof) are mixed, water (e.g., decationized water and / or deionized water) and alumina sol and / or silica sol are added, and the resulting mixture is vigorously mixed and stirred for 0.1 to 10 hours (e.g., 120 minutes) to form a slurry with a solids content of 20 to 45% by weight (e.g., 30% by weight). An inorganic acid such as hydrochloric acid, nitric acid, phosphoric acid, or sulfuric acid is added to adjust the pH of the slurry to 1 to 4 (e.g., 3.0). The mixture is then vigorously mixed and stirred for 0.1 to 10 hours (e.g., 45 minutes). Next, a phosphorus-aluminum inorganic binder is added and stirred for 0.1 to 10 hours (e.g., 30 minutes). The resulting slurry is spray-dried to obtain a microsphere catalyst. Thereafter, the microspherical catalyst is calcined at 350 to 650°C, 400 to 600°C, or 450 to 550°C for 0.5 to 6 hours or 0.5 to 2 hours (for example, at 500°C for 1 hour) to prepare a catalytic cracking catalyst.

[0093] In a specific embodiment of the catalytic cracking catalyst preparation method of the present invention, an inorganic binder (e.g., pseudoboehmite, alumina sol, silica sol, silica-alumina gel, or a mixture of two or more thereof) is mixed with a second clay (e.g., kaolin), and water (e.g., deionized water and / or deionized water) is added to form a slurry with a solids content of 10-50 wt% (e.g., 30 wt%). The slurry is stirred thoroughly, and the pH of the slurry is adjusted to 1-4 (e.g., 2.8) using an inorganic acid such as hydrochloric acid, nitric acid, phosphoric acid, or sulfuric acid. The slurry is then aged at 20-80°C (e.g., 55°C) for 0.1-2 hours (e.g., 1 hour). Then, phosphorus-modified ZSM-5 molecular sieves and Y-type molecular sieves are added to form a catalyst slurry with a solids content of 20-45 wt% (e.g., 35 wt%). The catalyst slurry is stirred and spray-dried to form a microsphere catalyst. Next, the microsphere catalyst is calcined, for example, at 350 to 650°C, 400 to 600°C, or 450 to 550°C for 0.5 to 6 hours or 0.5 to 2 hours (for example, 1 hour at 500°C), and then washed with ammonium sulfate (the washing temperature may be 40 to 70°C, for example, 60°C, and the ammonium sulfate:microsphere catalyst:water ratio is 0.2 to 0.8:1:5 to 15 (weight ratio, for example, 0.5:1:10)) until the sodium oxide content is less than 0.25% by weight, washed with water, filtered, and dried (for example, at 100 to 200°C, 110°C).

[0094] In another specific embodiment of the method for preparing a catalytic cracking catalyst of the present invention, the Y-type molecular sieve, the phosphorus-modified ZSM-5 molecular sieve, the phosphorus-aluminum inorganic binder, and other inorganic binders, optionally a second clay, can be vigorously mixed and stirred with water, and then spray-dried.

[0095] In the method for preparing a catalytic cracking catalyst of the present invention, the inorganic binder comprises a phosphorus-aluminum inorganic binder and other inorganic binders, and the weight ratio of the phosphorus-aluminum inorganic binder to the other inorganic binders may be (3-40):(1-30), for example (5-35):(5-28), further for example (10-30):(5-25). The phosphorus-aluminum inorganic binder may be a phosphorus-aluminum adhesive and / or a first clay-containing phosphorus-aluminum inorganic binder. The other inorganic binders may include at least one of pseudoboehmite, alumina sol, silica-alumina sol, and water glass.

[0096] The method for preparing a catalytic cracking catalyst of the present invention may include "mixing" or "vigorously mixing and stirring (with water)" the phosphorus-modified molecular sieve ZSM-5 molecular sieve, the phosphorus-aluminum inorganic binder, and other inorganic binders. The order of feeding is not particularly limited. For example, the phosphorus-aluminum inorganic binder, other inorganic binders, molecular sieve, and second clay (if there is no second clay, the corresponding feeding step can be omitted) can be mixed and then vigorously mixed and stirred with water. Alternatively, the second clay, molecular sieve, and other inorganic binders can be vigorously mixed and stirred, and then the phosphorus-aluminum inorganic binder can be added. This can contribute to improving the activity and selectivity of the additive.

[0097] The method for preparing a catalytic cracking catalyst of the present invention further includes a step of spray-drying the slurry obtained by "vigorously mixing and stirring with water." The method for spray-drying is not particularly limited in the present invention, and any method well known to those skilled in the art may be used.

[0098] The method for preparing a catalytic cracking catalyst of the present invention may further include preparing a first clay-containing phosphorus-aluminum inorganic binder by the following steps: An alumina source, a first clay, and water are vigorously mixed and stirred to disperse them into a slurry with a solids content of 5 to 48% by weight. The alumina source is aluminum hydroxide and / or alumina that can be peptized with acid. The amount of the first clay used on a dry weight basis is greater than 0 parts by weight and not more than 40 parts by weight, relative to 10 to 40 parts by weight, e.g., 15 to 40 parts by weight, of the alumina source based on Al2O3. Concentrated phosphoric acid is added to the slurry with stirring at a weight ratio of P / Al = 1 to 6, and the resulting mixed slurry is reacted at 50 to 99°C for 15 to 90 minutes. In P / Al, P is the weight of phosphorus as a simple substance in the phosphoric acid, and Al is the weight of aluminum as a simple substance in the alumina source. The alumina source is at least one selected from ρ-alumina, x-alumina, η-alumina, γ-alumina, κ-alumina, σ-alumina, θ-alumina, gibbsite, bayerite, nordstrandite, diaspore, boehmite, and pseudoboehmite, and the aluminum component in the first clay-containing phosphorus-aluminum inorganic binder is derived from the alumina source. The first clay may be one or more of kaolin, sepiolite, attapulgite, rectorite, smectite, and diatomaceous earth, for example, rectorite. The concentration of concentrated phosphoric acid may be 60 to 98 wt%, further for example, 75 to 90 wt%, and the phosphoric acid supply rate may be, for example, 0.01 to 0.10 kg phosphoric acid / min / kg alumina source, further for example, 0.03 to 0.07 kg phosphoric acid / min / kg alumina source.

[0099] In the method for preparing a catalytic cracking catalyst of the present invention, the introduction of clay into the first clay-containing phosphorus-aluminum inorganic binder not only improves mass transfer and heat transfer between materials during the preparation process, but also prevents binder solidification due to excessive temperatures caused by heat release due to localized violent reactions of heterogeneous materials, and the resulting binder has binding performance equivalent to that of phosphorus-aluminum binders prepared by methods without introducing clay. Furthermore, the introduction of clay, especially rectorite with a layered structure, can improve the heavy oil conversion ability of the catalyst and improve the selectivity of the resulting catalyst.

[0100] The present invention also provides a catalytic cracking catalyst obtained by the above-mentioned preparation method.

[0101] The present invention also provides an application of the catalytic cracking catalyst, i.e., a method for catalytically cracking hydrocarbon oils, comprising catalytically reacting the hydrocarbon oils with the catalytic cracking catalyst of the present invention under catalytic cracking conditions. The catalytic cracking conditions include a reaction temperature of 500 to 800°C, and the hydrocarbon oil being one or more selected from crude oil, naphtha, gasoline, atmospheric residue, vacuum residue, atmospheric wax oil, vacuum wax oil, straight-run wax oil, propane light / heavy deoiling, coking wax oil, and coal liquids. The hydrocarbon oil may contain heavy metal impurities such as nickel and vanadium, as well as sulfur and nitrogen impurities. For example, the sulfur content of the hydrocarbon oil may be 3.0 wt. %, the nitrogen content may be 2.0 wt. , and the content of metal impurities such as vanadium and nickel may be as high as 3,000 ppm.

[0102] When used in a catalytic cracking process, in a specific embodiment, the catalytic cracking catalyst can be added alone to a catalytic cracking reactor. For example, a hydrocarbon oil is catalytically reacted with the catalytic cracking catalyst of the present invention under catalytic cracking conditions. In another specific embodiment, when used in a catalytic cracking process, the catalyst can be mixed with other catalytic cracking catalysts. For example, a hydrocarbon oil can be catalytically reacted with a catalyst mixture containing the catalytic cracking catalyst of the present invention and other catalytic cracking catalysts. The catalyst of the present invention can account for 30% by weight or less, for example, 1 to 25% by weight, and further for example, 3 to 15% by weight, of the total amount of the mixture.

[0103] The EPMA / XPS hybrid method scans the surface, analyzes the chemical composition of a microscopic region, and quantitatively analyzes the phosphorus content corresponding to the depth structure. The K value indicates the percentage of the phosphorus mass content at the depth interface of the molecular sieve crystal grains to the phosphorus mass content at the surface of the molecular sieve crystal grains. Here, K = P2(EPMA) / P1(XPS)%, where P1(XPS) represents the phosphorus mass content in a microscopic region with a depth of less than 2 nm on any crystal face of the molecular sieve crystal grain, as quantitatively measured by the XPS method, and P2(EPMA) represents the phosphorus mass content in a microscopic region with a depth of 5-10 nm, as quantitatively measured by the EPMA method, obtained by focused ion beam (FIB) cutting.

[0104] The surface of the molecular sieve is analyzed by X-ray photoelectron spectroscopy (XPS). A Thermo Fisher Scientific ESCAREB 250 X-ray photoelectron spectrometer is used. The excitation source is monochromatic AlKα X-rays with a power of 150 W. The charge shift is calibrated with the C1s peak (284.8 eV) of contaminating carbon.

[0105] EPMA uses a JXA-8230 energy spectrometer X-ray detector, and the counting rate and counting time are generally 10 5 Larger, count rate 10 3 ~10 4 It is a CPS, and the counting time is 10 to 100 seconds.

[0106] The present invention also provides the following technical solutions:

[0107] (Embodiment 1) A phosphorus-modified MFI-structure molecular sieve having a K value that satisfies 70%≦K≦90%, for example, 75%≦K≦90%, further for example, 78%≦K≦85%, where K=P1 / P2×100%, where P1 represents the mass content of phosphorus in a region having an area of ​​100 square nanometers and a vertical depth of 0 to 2 nm on any crystal face of a crystal grain of the molecular sieve, as measured by an XPS method, and P2 represents the mass content of phosphorus in a region having an area of ​​100 square nanometers and a vertical depth of 5 to 10 nm on any crystal face of a crystal grain of the molecular sieve, as measured by an EPMA method.

[0108] (Embodiment 2) The molecular sieve according to any one of the above embodiments, wherein the molar ratio of the phosphorus content on a P2O5 basis to the alumina content is ≥ 0.01, for example ≥ 0.2, further for example ≥ 0.3, and further for example 0.4 to 0.7.

[0109] (Embodiment 3) The molecular sieve of any one of the preceding embodiments, wherein the phosphorus-modified MFI structure molecular sieve is a microporous ZSM-5 molecular sieve or a ZSM-5 molecular sieve having a hierarchical structure.

[0110] (Embodiment 4) The molecular sieve according to any one of the above embodiments, wherein the microporous ZSM-5 molecular sieve has a silica / alumina molar ratio of 15 to 1000, for example, 20 to 200.

[0111] (Embodiment 5) The molecular sieve according to any one of the above embodiments, wherein the ZSM-5 molecular sieve having a hierarchical structure has a mesopore volume ratio to total pore volume of more than 10%, an average pore diameter of 2 to 20 nm, and a silica / alumina molar ratio of 15 to 1000, e.g., 20 to 200.

[0112] (Embodiment 6) A catalytic cracking aid comprising, based on the dry basis of the catalytic cracking aid, 5 to 75 wt. %, e.g., 8 to 60 wt. %, of the phosphorus-modified MFI-structured molecular sieve according to any one of the preceding embodiments, 1 to 40 wt. % of a binder, and 0 to 65 wt. %, e.g., 5 to 55 wt. % of a second clay.

[0113] (Embodiment 7) A catalytic cracking catalyst comprising a phosphorus-modified MFI-structured molecular sieve, the catalytic cracking catalyst comprising, on a dry basis of the catalyst, 1 to 25 wt. % of a Y-type molecular sieve, 5 to 50 wt. % of the phosphorus-modified MFI-structured molecular sieve of any one of the preceding embodiments, 1 to 60 wt. % of an inorganic binder, and optionally, 0 to 60 wt. % of a second clay.

[0114] (Embodiment 8) The binder or inorganic binder includes a phosphorus-aluminum inorganic binder and / or other inorganic binders, for example, the phosphorus-aluminum inorganic binder is a phosphorus-aluminum adhesive and / or a first clay-containing phosphorus-aluminum inorganic binder, and further, the first clay is selected from kaolin, sepiolite, attapulgite, rectorite, smectite, and diatomaceous earth, and for example, the first clay-containing phosphorus-aluminum inorganic binder has an aluminum component of 10 to 40 wt %, for example, 15 to 40 wt %, based on Al2O3, and a phosphorus component of 45 to 90 wt %, for example, 45 to 80 wt %, based on P2O5. and a first clay in an amount of more than 0 and not more than 40 wt % on a dry basis, wherein the first clay-containing phosphorus-aluminum inorganic binder has a P / Al weight ratio of 1.0 to 6.0, a pH of 1 to 3.5, and a solids content of 15 to 60 wt %, and the second clay is selected from kaolin, sepiolite, attapulgite, rectorite, smectite, diatomaceous earth, metahalloysite, halloysite, hydrotalcite, and bentonite, for example, and the other inorganic binder is selected from pseudoboehmite, alumina sol, silica-alumina sol, and water glass, for example.

[0115] (Aspect 9) The catalytic cracking catalyst according to any one of the preceding aspects, wherein the Y-type molecular sieve comprises at least one of a PSRY-type molecular sieve, a PSRY-S-type molecular sieve, a rare earth-containing PSRY-type molecular sieve, a rare earth-containing PSRY-S-type molecular sieve, a USY-type molecular sieve, a rare earth-containing USY-type molecular sieve, a REY-type molecular sieve, a REHY-type molecular sieve, and a HY-type molecular sieve.

[0116] (Embodiment 10) A method for preparing the phosphorus-modified MFI molecular sieve according to any one of the above embodiments, characterized in that the phosphorus-modified MFI molecular sieve is obtained by a dipping method comprising: mixing and contacting an aqueous solution of a phosphorus-containing compound at 40 to 150°C, for example, 50 to 150°C, further for example, 70 to 130°C, with an MFI molecular sieve at 40 to 150°C, for example, 50 to 150°C, further for example, 70 to 130°C, at substantially the same temperature for 0.1 hours or more; drying the mixture; and calcining the mixture at 200 to 600°C in an air or steam atmosphere for 0.1 hours or more; or vigorously mixing and stirring the phosphorus-containing compound, the MFI molecular sieve, and water to form a slurry, adjusting the temperature to 40 to 150°C, for example, 50 to 150°C, further for example, 70 to 130°C, maintaining the slurry for 0.1 hours or more, drying the slurry, and calcining the mixture at 200 to 600°C in an air or steam atmosphere for 0.1 hours or more.

[0117] (Aspect 11) The method for preparing a phosphorus-modified MFI-structured molecular sieve according to any one of the above aspects, wherein the phosphorus-containing compound is selected from organic phosphorus compounds and / or inorganic phosphorus compounds, the organic phosphorus compound being selected from trimethyl phosphate, triphenylphosphine, trimethyl phosphite, tetrabutyl phosphonium bromide, tetrabutyl phosphonium chloride, tetrabutyl phosphonium hydroxide, triphenylethyl phosphonium bromide, triphenylbutyl phosphonium bromide, triphenylbenzyl phosphonium bromide, hexamethylphosphoric triamide, dibenzyl diethyl phosphoramidite, and 1,3-bis((triethylphosphine)methyl)benzene, and the inorganic phosphorus compound being selected from phosphoric acid, ammonium hydrogen phosphate, diammonium hydrogen phosphate, ammonium phosphate, and boron phosphate.

[0118] (Embodiment 12) The method for preparing a phosphorus-modified MFI molecular sieve according to any one of the above embodiments, wherein the molar ratio of the phosphorus-containing compound on a phosphorus basis (oxide basis) to the MFI molecular sieve (e.g., hydrogen-type ZSM-5 molecular sieve) on an aluminum basis (oxide basis) is 0.01 to 2, for example, 0.1 to 1.5, further for example, 0.2 to 1.5.

[0119] (Aspect 13) The phosphorus-containing compound is a mixture of boron phosphate and one or more compounds selected from the group consisting of trimethyl phosphate, triphenyl phosphine, trimethyl phosphite, phosphoric acid, ammonium hydrogen phosphate, diammonium hydrogen phosphate, and ammonium phosphate; The method for preparing a phosphorus-modified MFI-structured molecular sieve according to any one of the above aspects, wherein the boron phosphate content in the mixture is 10 to 80% by weight, for example, 20 to 40% by weight.

[0120] (Embodiment 14) The method for preparing a phosphorus-modified MFI-structured molecular sieve according to any one of the above embodiments, wherein the weight ratio of water to molecular sieve in the contact is 0.5 to 1, and the contact time is 0.5 to 40 hours.

[0121] (Embodiment 15) The method for preparing a phosphorus-modified MFI-structure molecular sieve according to any one of the above embodiments, wherein the calcination is carried out at 450 to 550°C in a steam atmosphere.

[0122] (Embodiment 16) A method for preparing the catalytic cracking aid of any one of the preceding embodiments, comprising vigorously mixing and stirring a phosphorus-modified MFI structured molecular sieve, a binder, and optionally a second clay with water, and then spray drying to obtain the catalytic cracking aid.

[0123] (Embodiment 17) The method for preparing a catalytic cracking aid according to any one of the preceding embodiments, wherein the binder is or comprises a phosphorus-aluminum inorganic binder.

[0124] (Embodiment 18) The phosphorus-aluminum inorganic binder is a phosphorus-aluminum adhesive and / or a first clay-containing phosphorus-aluminum inorganic binder, and the first clay-containing phosphorus-aluminum inorganic binder has, based on Al2O3, 10 to 40 wt. %, e.g., 15 to 40 wt. %, or 10 to 30 wt. %, or 15 to 35 wt. %, or 20 to 40 wt. % aluminum component and, based on P2O5, 45 to 90 wt. %, e.g., 45 to 80 wt. %, or 50 to 75 wt. %, or 60 to 80 wt. % aluminum component, based on P2O5, based on the dry basis weight of the first clay-containing phosphorus-aluminum inorganic binder. % by weight of a phosphorus component and more than 0 and 40% by weight or less, for example, 8 to 35% by weight of a first clay, on a dry basis; wherein the first clay-containing phosphorus-aluminum inorganic binder has a P / Al weight ratio of 1.0 to 6.0, for example, 1.2 to 6.0, further for example, 2.0 to 5.0, a pH of 1 to 3.5, for example, 2.0 to 3.0, and a solids content of 15 to 60% by weight; and the first clay comprises at least one of kaolin, sepiolite, attapulgite, rectorite, smectite, and diatomaceous earth.

[0125] (Aspect 19) The method for preparing a catalytic cracking aid according to any one of the above aspects, wherein the second clay is at least one selected from kaolin, sepiolite, attapulgite, rectorite, smectite, metahalloysite, halloysite, hydrotalcite, bentonite, and diatomaceous earth.

[0126] (Aspect 20) The method for preparing a catalytic cracking aid according to any one of the preceding aspects, wherein the binder comprises, on a dry weight basis, 3 to 39 wt % of the phosphorus-aluminum inorganic binder and 1 to 30 wt % of the other inorganic binder, based on the total weight of the catalytic cracking aid.

[0127] (Aspect 21) The method for preparing a catalytic cracking aid according to any one of the preceding aspects, wherein the other inorganic binder may further include at least one of pseudoboehmite, alumina sol, silica-alumina sol, and water glass.

[0128] (Aspect 22) The method for preparing a catalytic cracking aid according to any one of the above aspects, comprising first calcining, washing, and optionally drying the product obtained by the spray drying to obtain the catalytic cracking aid, wherein the first calcination is performed at a calcination temperature of 300 to 650°C for a calcination time of 0.5 to 8 hours, and the drying is performed at a drying temperature of 100 to 200°C for a drying time of 0.5 to 24 hours.

[0129] (Embodiment 23) The method for preparing a catalytic cracking aid according to any one of the above embodiments, further comprising: vigorously mixing and stirring an alumina source, the first clay, and water to disperse them into a slurry having a solids content of 5 to 48% by weight; adding concentrated phosphoric acid to the slurry under stirring at a weight ratio of P / Al of 1 to 6; and reacting the resulting mixed slurry at 50 to 99°C for 15 to 90 minutes to prepare the first clay-containing phosphorus-aluminum inorganic binder; the alumina source is acid-peptizable aluminum hydroxide and / or alumina; the amount of the first clay used on a dry weight basis is more than 0 parts by weight and not more than 40 parts by weight relative to 10 to 40 parts by weight, for example 15 to 40 parts by weight, of the alumina source based on Al2O3; and in the P / Al ratio, P is the weight of phosphorus as a simple substance in the phosphoric acid, and Al is the weight of aluminum as a simple substance in the alumina source.

[0130] (Embodiment 24) A method for preparing the catalytic cracking catalyst described in any one of the preceding embodiments, comprising vigorously mixing and stirring a Y-type molecular sieve, the phosphorus-modified MFI structure molecular sieve described in any one of the preceding embodiments, an inorganic binder, and optionally a second clay with water, and spray-drying to prepare the catalytic cracking catalyst.

[0131] (Aspect 25) The method for preparing a catalytic cracking catalyst according to any one of the preceding aspects, wherein the inorganic binder is or includes a phosphorus-aluminum inorganic binder.

[0132] (Aspect 26) The method for preparing a catalytic cracking catalyst according to any one of the preceding aspects, wherein the phosphorus-aluminum inorganic binder is a phosphorus-aluminum adhesive and / or a first clay-containing phosphorus-aluminum inorganic binder, and the first clay-containing phosphorus-aluminum inorganic binder contains, based on the dry weight of the first clay-containing phosphorus-aluminum inorganic binder, 10 to 40 wt %, for example, 15 to 40 wt %, of an aluminum component based on Al2O3, 45 to 90 wt %, for example, 45 to 80 wt %, of a phosphorus component based on P2O5, and a first clay content greater than 0 and not greater than 40 wt % on a dry basis, and the first clay-containing phosphorus-aluminum inorganic binder has a P / Al weight ratio of 1.0 to 6.0, a pH of 1 to 3.5, and a solids content of 15 to 60 wt %, and the first clay comprises at least one of kaolin, sepiolite, attapulgite, rectorite, smectite, and diatomaceous earth.

[0133] (Aspect 27) The method for preparing a catalytic cracking catalyst according to any one of the above aspects, wherein the second clay is at least one selected from kaolin, sepiolite, attapulgite, rectorite, smectite, metahalloysite, halloysite, hydrotalcite, bentonite, and diatomaceous earth.

[0134] (Embodiment 28) A method for preparing a catalytic cracking catalyst according to any one of the above embodiments, wherein the inorganic binder contains, on a dry basis, 3 to 39 wt % of the phosphorus-aluminum inorganic binder and 1 to 30 wt % of the other inorganic binder, and the other inorganic binder is at least one selected from pseudoboehmite, alumina sol, silica-alumina sol, and water glass, based on the catalytic cracking catalyst.

[0135] (Aspect 29) The method for preparing a catalytic cracking catalyst according to any one of the above aspects, comprising first calcining, washing, and optionally drying the product obtained by the spray drying to obtain the catalytic cracking catalyst, wherein the first calcination is performed at a calcination temperature of 300 to 650°C for a calcination time of 0.5 to 8 hours, and the drying is performed at a drying temperature of 100 to 200°C for a drying time of 0.5 to 24 hours.

[0136] (Aspect 30) The method for preparing a catalytic cracking catalyst according to any one of the above aspects, further comprising: vigorously mixing and stirring an alumina source, the first clay, and water to disperse them into a slurry having a solids content of 5 to 48% by weight; adding concentrated phosphoric acid to the slurry under stirring at a weight ratio of P / Al of 1 to 6; and reacting the resulting mixed slurry at 50 to 99°C for 15 to 90 minutes to prepare the first clay-containing phosphorus-aluminum inorganic binder; the alumina source is acid-peptizable aluminum hydroxide and / or alumina; the amount of the first clay used on a dry weight basis is more than 0 parts by weight and not more than 40 parts by weight relative to 10 to 40 parts by weight, for example 15 to 40 parts by weight, of the alumina source based on Al2O3; and in the P / Al ratio, P is the weight of phosphorus as a simple substance in the phosphoric acid, and Al is the weight of aluminum as a simple substance in the alumina source.

[0137] (Aspect 31) A catalytic cracking aid obtained by the method for preparing a catalytic cracking aid according to any one of the above aspects.

[0138] (Aspect 32) A catalytic cracking catalyst obtained by the method for preparing a catalytic cracking catalyst according to any one of the above aspects.

[0139] (Aspect 33) A method for catalytic cracking of hydrocarbon oil, comprising catalytically reacting a hydrocarbon oil with the catalytic cracking aid described in any one of the above aspects or the catalytic cracking catalyst described in any one of the above aspects under catalytic cracking conditions.

[0140] (Aspect 34) A method for catalytically cracking a hydrocarbon oil according to any one of the preceding aspects, comprising catalytically reacting the hydrocarbon oil with a catalytic cracking aid according to any one of the preceding aspects and a catalytic cracking catalyst under the catalytic cracking conditions, wherein the content of the catalytic cracking aid in the catalytic mixture is 0.1 to 30 wt %.

[0141] (Aspect 35) The catalytic cracking method for hydrocarbon oil according to any one of the above aspects, wherein the catalytic cracking conditions include a reaction temperature of 500 to 800°C, and the hydrocarbon oil is one or more selected from crude oil, naphtha, gasoline, atmospheric residue, vacuum residue, atmospheric wax oil, vacuum wax oil, straight-run wax oil, propane light / heavy deoiled wax oil, coked wax oil, and coal liquid.

[0142] The present invention will be further described below with reference to examples, but the contents of the present invention are not limited thereto.

[0143] Unless otherwise specified, all of the equipment and reagents used in the examples of the present invention are commonly used by those skilled in the art.

[0144] The microreactor was used to evaluate the effect of the catalytic cracking aid / catalyst of the present invention on the yield of low carbon olefins in the catalytic cracking of petroleum hydrocarbons.

[0145] The prepared catalytic cracking aid sample / catalyst sample was aged in a fixed-bed ageing apparatus at 800°C with 100% steam for 17 hours and then evaluated in a microreactor. The feedstock was VGO or naphtha. The evaluation conditions were a reaction temperature of 620°C, a regeneration temperature of 620°C, and a catalyst oil ratio of 3.2. The microreactivity was measured according to the ASTM D5154-2010 standard method.

[0146] The RIPP standard method of the present invention can be found in the 1990 edition of "Analysis Methods for Petrochemical Industry" edited by Yang Cuiding et al.

[0147] The properties of some of the raw materials used in the examples are as follows:

[0148] The pseudo-boehmite was an industrial product manufactured by Shandong Aluminum Co., Ltd., and had a solid content of 60 wt %.

[0149] The alumina sol was an industrial product manufactured by China Petrochemical Catalyst Co., Ltd. Qilu Branch, and had an Al2O3 content of 21.5 wt%.

[0150] The silica sol was an industrial product manufactured by China Petrochemical Catalyst Co., Ltd. Qilu Branch, with an SiO2 content of 28.9 wt% and a Na2O content of 8.9%.

[0151] The kaolin was catalytic cracking catalyst kaolin manufactured by Suzhou Kaolin Co., Ltd., and had a solids content of 78 wt %.

[0152] The rectorite was manufactured by Hubei Zhongxiang Mingliu Rectorite Development Co., Ltd., and had a quartz sand content of less than 3.5 wt%, an Al2O3 content of 39.0 wt%, a Na2O content of 0.03 wt%, and a solid content of 77 wt%.

[0153] The SB aluminum hydroxide powder was manufactured by Condex, Germany, and had an Al2O3 content of 75 wt%.

[0154] The γ-alumina was manufactured by Condex, Germany, and had an Al2O3 content of 95 wt%.

[0155] The hydrochloric acid was manufactured by Beijing Chemical Works and was chemically pure with a concentration of 36–38 wt %.

[0156] The PSRY molecular sieve was an industrial product manufactured by Changling Branch of China Petrochemical Catalyst Co., Ltd. Its Na2O content was less than 1.5 wt%, its P2O5 content was 0.8-1.2 wt%, its unit cell constant was less than 2.456 nm, and its crystallinity was more than 64%.

[0157] The HRY-1 product molecular sieve was an industrial product manufactured by Changling Branch of China Petrochemical Catalyst Co., Ltd., with a La2O3 content of 11-13 wt%, a unit cell constant of less than 2.464 nm, and a crystallinity of more than 40%.

[0158] The equilibrium catalyst was an industrial FCC equilibrium catalyst available from Sinopec Yanshan Branch, with industrial number DVR-3, having a microactivity of 63 for diesel.

[0159] The following examples illustrate the phosphorus-modified hierarchical ZSM-5 molecular sieves of the present invention and their preparation methods. These molecular sieves can be used to prepare the catalytic cracking aid of the present invention and the catalytic cracking catalyst of the present invention.

[0160] (Example 1-1) Example 1-1 illustrates the phosphorus-containing hierarchical ZSM-5 molecular sieve and its preparation method of the present invention.

[0161] 18.5 g of diammonium hydrogen phosphate, 108 g of hydrogen-type hierarchical ZSM-5 molecular sieve (obtained from China Petrochemical Catalyst Co., Ltd. Qilu Branch, relative crystallinity 88.6%, silica / alumina molar ratio 20.8, NaO content 0.017 wt%, specific surface area 373 m / g, total pore volume 0.256 mL / g, mesopore volume 0.119 mL / g, average pore diameter 5.8 nm), and 60 g of deionized water were vigorously mixed and stirred to form a slurry. The slurry was heated to 100 °C, held for 2 hours, dried in an oven at 110 °C, and calcined in air at 550 °C for 2 hours. The resulting phosphorus-containing hierarchical ZSM-5 molecular sieve sample was designated GPZ1-1.

[0162] (Comparative Example 1-1) The procedure was the same as in Example 1-1, except that the ZSM-5 molecular sieve having a hydrogen-type hierarchical structure was immersed at 20° C. using the immersion method. The obtained comparative sample of the ZSM-5 molecular sieve having a phosphorus-containing hierarchical structure was designated D1-1.

[0163] (Example 1-2) The procedure was the same as in Example 1-1, except that after drying, the sample was treated in a 60% steam atmosphere at 450°C for 0.5 hours. The resulting phosphorus-containing hierarchical ZSM-5 molecular sieve sample was designated GPZ1-2.

[0164] (Comparative Example 1-2) The procedure was the same as in Example 1-2, except that the ZSM-5 molecular sieve having a hydrogen-type hierarchical structure was immersed at 20° C. using the immersion method. The obtained comparative sample of the ZSM-5 molecular sieve having a phosphorus-containing hierarchical structure was designated D1-2.

[0165] The phosphorus dispersity K of GPZ1-1, D1-1, GPZ1-2 and D1-2 is shown in Table 1.

[0166] Example 2-1 Example 2-1 illustrates the phosphorus-containing hierarchical ZSM-5 molecular sieve and its preparation method of the present invention.

[0167] 18.5 g of diammonium hydrogen phosphate, 108 g of hydrogen-type hierarchical ZSM-5 molecular sieves, and 120 g of deionized water were vigorously mixed and stirred to form a slurry. The slurry was kept at 70 °C for 2 hours, dried in an oven at 110 °C, and calcined in air at 550 °C for 2 hours. The resulting phosphorus-containing hierarchical ZSM-5 molecular sieve sample was designated GPZ2-1.

[0168] (Comparative Example 2-1) The procedure was the same as in Example 2-1, except that the ZSM-5 molecular sieve having a hydrogen-type hierarchical structure was immersed at 20° C. using the immersion method. The obtained comparative sample of the ZSM-5 molecular sieve having a phosphorus-containing hierarchical structure was designated D2-1.

[0169] (Example 2-2) The procedure was the same as in Example 2-1, except that after drying, the sample was treated in a 50% steam atmosphere at 600°C for 2 hours. The resulting phosphorus-containing hierarchical ZSM-5 molecular sieve sample was designated GPZ2-2.

[0170] (Comparative Example 2-2) The procedure was the same as in Example 2-2, except that the ZSM-5 molecular sieve having a hydrogen-type hierarchical structure was soaked at 20°C using the soaking method. D2-2.

[0171] The phosphorus dispersity K of GPZ2-1, D2-1, GPZ2-2 and D2-2 is shown in Table 1.

[0172] Example 3-1 Example 3-1 illustrates the phosphorus-containing hierarchical ZSM-5 molecular sieve and its preparation method of the present invention.

[0173] 11.8 g of phosphoric acid was dissolved in 60 g of deionized water and stirred for 2 hours to obtain a phosphorus-containing aqueous solution. 108 g of ZSM-5 molecules with hydrogen-type hierarchical structure were taken, and the phosphorus-containing aqueous solution and the ZSM-5 molecules with hydrogen-type hierarchical structure were heated to 80°C, mixed, and contacted for 4 hours, dried in an oven at 110°C, and calcined in air at 550°C for 2 hours. The resulting phosphorus-modified ZSM-5 molecular sieve was designated GPZ3-1.

[0174] (Comparative Example 3-1) The procedure was the same as in Example 3-1, except that the ZSM-5 molecular sieve having a hydrogen-type hierarchical structure was immersed at 20° C. using the immersion method. The obtained comparative sample of the ZSM-5 molecular sieve having a phosphorus-containing hierarchical structure was designated D3-1.

[0175] (Example 3-2) The procedure was the same as in Example 3-1, except that after drying, the sample was treated in a 100% steam atmosphere at 430° C. for 2 hours. The resulting phosphorus-containing hierarchical ZSM-5 molecular sieve sample was designated GPZ3-2.

[0176] (Comparative Example 3-2) The procedure was the same as in Example 3-2, except that the ZSM-5 molecular sieve having a hydrogen-type hierarchical structure was immersed at 20° C. using the immersion method. The obtained comparative sample of the ZSM-5 molecular sieve having a phosphorus-containing hierarchical structure was designated D3-2.

[0177] The phosphorus dispersity K of GPZ3-1, D3-1, GPZ3-2 and D3-2 is shown in Table 1.

[0178] (Example 4-1) Example 4-1 illustrates the phosphorus-containing hierarchical ZSM-5 molecular sieve and its preparation method of the present invention.

[0179] 9.3 g of diammonium hydrogen phosphate, 108 g of hydrogen-type hierarchical ZSM-5 molecular sieves, and 120 g of deionized water were vigorously mixed and stirred to form a slurry. The slurry was kept at 90 °C for 2 hours, dried in an oven at 110 °C, and calcined in air at 550 °C for 2 hours. The resulting phosphorus-containing hierarchical ZSM-5 molecular sieve sample was designated GPZ4-1.

[0180] (Comparative Example 4-1) The procedure was the same as in Example 4-1, except that the ZSM-5 molecular sieve having a hydrogen-type hierarchical structure was immersed at 20° C. using the immersion method. The obtained comparative sample of the ZSM-5 molecular sieve having a phosphorus-containing hierarchical structure was designated D4-1.

[0181] (Example 4-2) The procedure was the same as in Example 4-1, except that after drying, the sample was treated in a 100% steam atmosphere at 350°C for 2 hours. The resulting phosphorus-containing hierarchical ZSM-5 molecular sieve sample was designated GPZ4-2.

[0182] (Comparative Example 4-2) The procedure was the same as in Example 4-2, except that the ZSM-5 molecular sieve having a hydrogen-type hierarchical structure was immersed at 20° C. using the immersion method. The obtained comparative sample of the ZSM-5 molecular sieve having a phosphorus-containing hierarchical structure was designated D4-2.

[0183] The phosphorus dispersity K of GPZ4-1, D4-1, GPZ4-2 and D4-2 is shown in Table 1.

[0184] (Example 5-1) Example 5-1 illustrates the phosphorus-containing hierarchical ZSM-5 molecular sieve and its preparation method of the present invention.

[0185] 9.7 g of trimethyl phosphate, 108 g of hydrogen-type hierarchical ZSM-5 molecular sieve, and 80 g of deionized water were vigorously mixed and stirred to form a slurry. The slurry was heated to 120 °C and held for 8 hours, dried in an oven at 110 °C, and calcined in air at 550 °C for 2 hours. The resulting phosphorus-containing hierarchical ZSM-5 molecular sieve sample was designated GPZ5-1.

[0186] (Comparative Example 5-1) The procedure was the same as in Example 5-1, except that the ZSM-5 molecular sieve having a hydrogen-type hierarchical structure was immersed at 20° C. using the immersion method. The obtained comparative sample of the ZSM-5 molecular sieve having a phosphorus-containing hierarchical structure was designated D5-1.

[0187] (Example 5-2) The procedure was the same as in Example 5-1, except that after drying, the sample was calcined at 500°C in a 40% water vapor atmosphere for 4 hours. The resulting phosphorus-containing hierarchical ZSM-5 molecular sieve sample was designated GPZ5-2.

[0188] (Comparative Example 5-2) The procedure was the same as in Example 5-2, except that the ZSM-5 molecular sieve having a hydrogen-type hierarchical structure was immersed at 20° C. using the immersion method. The obtained comparative sample of the ZSM-5 molecular sieve having a phosphorus-containing hierarchical structure was designated D5-2.

[0189] The phosphorus dispersity K of GPZ5-1, D5-1, GPZ5-2 and D5-2 is shown in Table 1.

[0190] Example 6-1 Example 6-1 illustrates the phosphorus-containing hierarchical ZSM-5 molecular sieve and its preparation method of the present invention.

[0191] 13.2 g of boron phosphate, 108 g of hydrogen-type hierarchical ZSM-5 molecular sieve, and 100 g of deionized water were vigorously mixed and stirred to form a slurry. The slurry was heated at 150 °C for 2 hours, dried in an oven at 110 °C, and calcined in air at 550 °C for 2 hours. The resulting phosphorus-containing hierarchical ZSM-5 molecular sieve sample was designated GPZ6-1.

[0192] (Comparative Example 6-1) The procedure was the same as in Example 6-1, except that the ZSM-5 molecular sieve having a hydrogen-type hierarchical structure was immersed at 20° C. using the immersion method. The obtained ZSM-5 molecular sieve sample having a phosphorus-containing hierarchical structure was designated as D6-1.

[0193] (Example 6-2) The procedure was the same as in Example 6-1, except that after drying, the sample was subjected to hydrothermal calcination treatment at 350°C in a 60% water vapor atmosphere for 4 hours. The obtained ZSM-5 molecular sieve sample having a phosphorus-containing hierarchical structure was designated GPZ6-2.

[0194] (Comparative Example 6-2) The procedure was the same as in Example 6-2, except that the ZSM-5 molecular sieve having a hydrogen-type hierarchical structure was immersed at 20° C. using the immersion method. The obtained comparative sample of the ZSM-5 molecular sieve having a phosphorus-containing hierarchical structure was designated D6-2.

[0195] The phosphorus dispersity K of GPZ6-1, D6-1, GPZ6-2 and D6-2 is shown in Table 1.

[0196] Example 7-1 Example 7-1 illustrates the phosphorus-containing hierarchical ZSM-5 molecular sieve of the present invention and its preparation method.

[0197] 16.3 g of triphenylphosphine was dissolved in 80 g of deionized water and stirred for 2 hours to obtain a phosphorus-containing aqueous solution. 108 g of ZSM-5 molecules with hydrogen-type hierarchical structure were taken, and the phosphorus-containing aqueous solution and the ZSM-5 molecules with hydrogen-type hierarchical structure were heated to 80 °C, mixed, and contacted for 4 hours, dried in an oven at 110 °C, and calcined in air at 550 °C for 2 hours. The resulting phosphorus-modified ZSM-5 molecular sieve was designated GPZ7-1.

[0198] (Comparative Example 7-1) The procedure was the same as in Example 7-1, except that the ZSM-5 molecular sieve having a hydrogen-type hierarchical structure was immersed at 20° C. using the immersion method. The obtained comparative sample of the ZSM-5 molecular sieve having a phosphorus-containing hierarchical structure was designated D7-1.

[0199] (Example 7-2) The procedure was the same as in Example 7-1, except that after drying, the sample was calcined at 600°C in a 50% steam atmosphere for 2 hours. The resulting phosphorus-containing hierarchical ZSM-5 molecular sieve sample was designated GPZ7-2.

[0200] (Comparative Example 7-2) The procedure was the same as in Example 7-2, except that the ZSM-5 molecular sieve having a hydrogen-type hierarchical structure was immersed at 20° C. using the immersion method. The obtained comparative sample of the ZSM-5 molecular sieve having a phosphorus-containing hierarchical structure was designated D7-2.

[0201] The phosphorus dispersity K of GPZ7-1, D7-1, GPZ7-2 and D7-2 is shown in Table 1.

[0202] Example 8-1 The procedure was the same as in Example 4-1, except that the phosphorus source was diammonium hydrogen phosphate and crystallized boron phosphate in a weight ratio of 3:1. The obtained phosphorus-containing hierarchical ZSM-5 molecular sieve sample was designated as GPZ8-1.

[0203] (Example 8-2) The procedure was the same as in Example 4-2, except that the phosphorus source was diammonium hydrogen phosphate and crystallized boron phosphate in a weight ratio of 3:1. The obtained phosphorus-containing hierarchical ZSM-5 molecular sieve sample was designated GPZ8-2.

[0204] (Example 9-1) The same procedure as in Example 4-1 was used, except that the phosphorus source was diammonium hydrogen phosphate and crystallized boron phosphate in a weight ratio of 2:2. The obtained phosphorus-containing hierarchical ZSM-5 molecular sieve sample was designated as GPZ9-1.

[0205] (Example 9-2) The procedure was the same as in Example 4-2, except that the phosphorus source was diammonium hydrogen phosphate and crystallized boron phosphate in a weight ratio of 2:2. The obtained phosphorus-containing hierarchical ZSM-5 molecular sieve sample was designated GPZ9-2.

[0206] (Example 10-1) The procedure was the same as in Example 4-1, except that the phosphorus source was diammonium hydrogen phosphate and crystallized boron phosphate in a weight ratio of 1:3. The obtained phosphorus-containing hierarchical ZSM-5 molecular sieve sample was designated as GPZ10-1.

[0207] (Example 10-2) The procedure was the same as in Example 4-2, except that the phosphorus source was diammonium hydrogen phosphate and crystallized boron phosphate in a weight ratio of 1:3. The obtained phosphorus-containing hierarchical ZSM-5 molecular sieve sample was designated GPZ10-2.

[0208] The phosphorus dispersity K of GPZ8-1, GPZ8-2, GPZ9-1, GPZ9-2, GPZ10-1 and GPZ10-2 is shown in Table 1.

[0209] (Example 11-1) The procedure was the same as in Example 8-1, except that the phosphorus source was phosphoric acid and crystallized boron phosphate in a weight ratio of 3:1. The obtained phosphorus-containing hierarchical ZSM-5 molecular sieve sample was designated as GPZ11-2.

[0210] (Example 11-2) The procedure was the same as in Example 8-2, except that the phosphorus source was phosphoric acid and crystallized boron phosphate in a weight ratio of 3:1. The obtained phosphorus-containing hierarchical ZSM-5 molecular sieve sample was designated as GPZ11-2.

[0211] (Example 12-1) The procedure was the same as in Example 9-1, except that the phosphorus source was phosphoric acid and crystallized boron phosphate in a weight ratio of 2:2. The obtained phosphorus-containing hierarchical ZSM-5 molecular sieve sample was designated as GPZ12-1.

[0212] (Example 12-2) The same procedure was followed as in Example 9-2, except that the phosphorus sources were phosphoric acid and crystallized boron phosphate in a weight ratio of 2:2 (the same as or close to the ratio in Example 9-1). The resulting phosphorus-containing hierarchical ZSM-5 molecular sieve sample was designated GPZ12-2.

[0213] (Example 13-1) The procedure was the same as in Example 10-1, except that the phosphorus source was phosphoric acid and crystallized boron phosphate in a weight ratio of 1:3. The obtained phosphorus-containing hierarchical ZSM-5 molecular sieve sample was designated as GPZ13-2.

[0214] (Example 13-2) The procedure was the same as in Example 10-2, except that the phosphorus source was phosphoric acid and crystallized boron phosphate in a weight ratio of 1:3. The obtained phosphorus-containing hierarchical ZSM-5 molecular sieve sample was designated as GPZ13-2.

[0215] The phosphorus dispersity K of GPZ11-1, GPZ11-2, GPZ12-1, GPZ12-2, GPZ13-1 and GPZ13-2 is shown in Table 1.

[0216] As can be seen from the data in Table 1, all of the phosphorus-modified hierarchical ZSM-5 molecular sieves of the present invention have high phosphorus dispersion. For example, in Example 8-2, sample GPZ8-2, which was modified with two phosphorus sources, i.e., phosphoric acid and crystallized boron phosphate, achieved a dispersion K of 85%.

[0217] The following examples illustrate the phosphorus-modified microporous ZSM-5 molecular sieves of the present invention and their preparation methods. These molecular sieves can be used to prepare the catalytic cracking aid of the present invention and the catalytic cracking catalyst of the present invention.

[0218] (Example 14-1) Example 14-1 illustrates the phosphorus-containing microporous ZSM-5 molecular sieve of the present invention and its preparation method.

[0219] 16.2 g of diammonium hydrogen phosphate, 113 g of HZSM-5 molecular sieve (manufactured by China Petrochemical Catalyst Co., Ltd. Qilu Branch, relative crystallinity 91.1%, silica / alumina molar ratio 24.1, NaO content 0.039 wt%, specific surface area 353 m / g, total pore volume 0.177 mL / g; same below), and 60 g of deionized water were vigorously mixed and stirred to form a slurry. The slurry was heated to 100°C, held for 2 hours, dried at 110°C, and then treated in an air atmosphere at 550°C for 0.5 hours. The resulting phosphorus-modified ZSM-5 molecular sieve sample was designated GPZ14-1.

[0220] (Comparative Example 14-1) Comparative Example 14-1 illustrates current industry practice and the resulting phosphorus-modified ZSM-5 comparison sample.

[0221] The procedure was the same as in Example 14-1, except that the HZSM-5 molecular sieve was soaked using the soaking method for 2 hours at 20° C. The resulting phosphorus-modified ZSM-5 molecular sieve comparison sample was designated D14-1.

[0222] (Example 14-2) Example 14-2 illustrates the phosphorus-containing microporous ZSM-5 molecular sieve of the present invention and its preparation method.

[0223] The procedure was the same as in Example 14-1, except that the air atmosphere at 550° C. was replaced by a 50% steam atmosphere at 500° C. for 0.5 hours. The resulting phosphorus-modified ZSM-5 molecular sieve sample was designated GPZ14-2.

[0224] (Comparative Example 14-2) The procedure was the same as in Example 14-2, except that the ZSM-5 molecular sieve with hydrogen-type hierarchical structure was soaked for 2 hours at 20° C. The resulting phosphorus-modified ZSM-5 molecular sieve comparison sample was designated D14-2.

[0225] The phosphorus dispersity K of GPZ14-1, D14-1, GPZ14-2 and D14-2 is shown in Table 1.

[0226] (Example 15-1) Example 15-1 illustrates the phosphorus-containing microporous ZSM-5 molecular sieve of the present invention and its preparation method.

[0227] 16.2 g of diammonium hydrogen phosphate, 113 g of HZSM-5 molecular sieve, and 120 g of deionized water were vigorously mixed and stirred to form a slurry. The slurry was kept at 70°C for 2 hours, dried at 110°C, and then treated in an air atmosphere at 550°C for 2 hours. The resulting phosphorus-modified ZSM-5 molecular sieve sample was designated GPZ15-1.

[0228] (Comparative Example 15-1) Comparative Example 15-1 illustrates current industry practice and the resulting phosphorus-modified ZSM-5 comparison sample.

[0229] The procedure was the same as in Example 15-1, except that the HZSM-5 molecular sieve was soaked for 2 hours at 20° C. The resulting phosphorus-modified ZSM-5 molecular sieve comparison sample was designated D15-1.

[0230] (Example 15-2) Example 15-2 illustrates the phosphorus-containing microporous ZSM-5 molecular sieve of the present invention and its preparation method.

[0231] The procedure was the same as in Example 15-1, except that the air atmosphere at 550° C. was replaced by a 30% steam atmosphere at 600° C. for 2 hours. The resulting phosphorus-modified ZSM-5 molecular sieve sample was designated GPZ15-2.

[0232] (Comparative Example 15-2) The procedure was the same as in Example 15-2, except that the soaking method was used and the HZSM-5 molecular sieve was soaked for 2 hours at 20° C. The resulting phosphorus-modified ZSM-5 molecular sieve comparison sample was designated D15-2.

[0233] The phosphorus dispersity K of GPZ15-1, D15-1, GPZ15-2 and D15-2 is shown in Table 1.

[0234] (Example 16-1) Example 16-1 illustrates the phosphorus-containing microporous ZSM-5 molecular sieve of the present invention and its preparation method.

[0235] 10.4 g of phosphoric acid was dissolved in 60 g of deionized water and stirred for 2 hours to obtain a phosphorus-containing aqueous solution. 113 g of HZSM-5 molecular sieve was taken, and the phosphorus-containing aqueous solution and the HZSM-5 molecular sieve were heated to 80°C, respectively, and then mixed and contacted for 4 hours, dried at 110°C, and treated in an air atmosphere at 550°C for 2 hours. The resulting phosphorus-modified ZSM-5 molecular sieve sample was designated GPZ16-1.

[0236] (Comparative Example 16-1) Comparative Example 16-1 illustrates current industry practice and the resulting phosphorus-modified ZSM-5 comparison sample.

[0237] The procedure was the same as in Example 16-1, except that the HZSM-5 molecular sieve was immersed in a phosphorus-containing aqueous solution at 20° C. using the immersion method. The resulting phosphorus-modified ZSM-5 molecular sieve comparison sample was designated D16-1.

[0238] (Example 16-2) Example 16-2 illustrates the phosphorus-containing microporous ZSM-5 molecular sieve of the present invention and its preparation method.

[0239] The procedure was the same as in Example 16-1, except that the air atmosphere at 550° C. was replaced by a 100% steam atmosphere at 400° C. for 2 hours. The resulting phosphorus-modified ZSM-5 molecular sieve sample was designated GPZ16-2.

[0240] (Comparative Example 16-2) The procedure was the same as in Example 16-2, except that the HZSM-5 molecular sieve was immersed in a phosphorus-containing aqueous solution at 20° C. using the immersion method. The resulting phosphorus-modified ZSM-5 molecular sieve comparison sample was designated D16-2.

[0241] The phosphorus dispersity K of GPZ16-1, D16-1, GPZ16-2 and D15-2 is shown in Table 1.

[0242] (Example 17-1) Example 17-1 illustrates the phosphorus-containing microporous ZSM-5 molecular sieve of the present invention and its preparation method.

[0243] 8.1 g of diammonium hydrogen phosphate, 113 g of HZSM-5 molecular sieves, and 120 g of deionized water were vigorously mixed and stirred to form a slurry. The slurry was maintained at 90°C for 4 hours, dried at 110°C, and then treated in an air atmosphere at 550°C for 2 hours. The resulting phosphorus-modified ZSM-5 molecular sieve sample was designated GPZ17-1.

[0244] (Comparative Example 17-1) Comparative Example 17-1 illustrates current industry practice and the resulting phosphorus-modified ZSM-5 comparison sample.

[0245] The procedure was the same as in Example 17-1, except that the HZSM-5 molecular sieve was soaked using the soaking method at 20° C. The resulting phosphorus-modified ZSM-5 molecular sieve comparison sample was designated D17-1.

[0246] (Example 17-2) The procedure was the same as in Example 17-1, except that the air atmosphere at 550° C. was replaced by a 100% steam atmosphere at 300° C. for 2 hours. The resulting phosphorus-modified ZSM-5 molecular sieve sample was designated GPZ17-2.

[0247] (Comparative Example 17-2) The procedure was the same as in Example 17-2, except that the HZSM-5 molecular sieve was soaked using the soaking method at 20° C. The resulting phosphorus-modified ZSM-5 molecular sieve comparison sample was designated D17-2.

[0248] The phosphorus dispersity K of GPZ17-1, D17-1, GPZ17-2 and D17-2 is shown in Table 1.

[0249] (Example 18-1) 8.5 g of trimethyl phosphate, 113 g of HZSM-5 molecular sieves, and 80 g of deionized water were vigorously mixed and stirred to form a slurry. The slurry was heated to 120°C, held for 8 hours, dried at 110°C, and then treated in an air atmosphere at 550°C for 2 hours. The resulting phosphorus-modified ZSM-5 molecular sieve sample was designated GPZ18-1.

[0250] (Comparative Example 18-1) Comparative Example 18-1 illustrates current industry practice and the resulting phosphorus-modified ZSM-5 comparison sample.

[0251] The procedure was the same as in Example 18-1, except that the HZSM-5 molecular sieve was soaked using the soaking method at 20° C. The resulting phosphorus-modified ZSM-5 molecular sieve comparison sample was designated D18-1.

[0252] (Example 18-2) Example 18-2 illustrates the phosphorus-containing microporous ZSM-5 molecular sieve of the present invention and its preparation process.

[0253] The procedure was the same as in Example 18-1, except that the air atmosphere at 550° C. was replaced by an 80% steam atmosphere at 500° C. for 4 hours. The resulting phosphorus-modified ZSM-5 molecular sieve sample was designated GPZ18-2.

[0254] (Comparative Example 18-2) The procedure was the same as in Example 18-2, except that the soaking method was used and the HZSM-5 molecular sieve was soaked at 20° C. The resulting phosphorus-modified ZSM-5 molecular sieve comparison sample was designated D18-2.

[0255] The phosphorus dispersity K of GPZ18-1, D18-1, GPZ18-2 and D18-2 is shown in Table 1.

[0256] (Example 19-1) Example 19-1 illustrates the phosphorus-containing microporous ZSM-5 molecular sieve of the present invention and its preparation method.

[0257] 11.6 g of boron phosphate, 113 g of HZSM-5 molecular sieve, and 100 g of deionized water were vigorously mixed and stirred to form a slurry. The slurry was maintained at 150 °C for 2 hours, dried at 110 °C, and then treated in an air atmosphere at 550 °C for 2 hours. The resulting phosphorus-modified ZSM-5 molecular sieve sample was designated GPZ19-1.

[0258] (Comparative Example 19-1) Comparative Example 19-1 illustrates current industry practice and the resulting phosphorus-modified ZSM-5 comparison sample.

[0259] The procedure was the same as in Example 19-1, except that the HZSM-5 molecular sieve was soaked using the soaking method at 20° C. The resulting phosphorus-modified ZSM-5 molecular sieve comparison sample was designated D19-1.

[0260] (Example 19-2) Example 19-2 illustrates the phosphorus-containing microporous ZSM-5 molecular sieve of the present invention and its preparation method.

[0261] The procedure was the same as in Example 19-1, except that the air atmosphere at 550° C. was replaced by a 100% steam atmosphere at 400° C. for 4 hours. The resulting phosphorus-modified ZSM-5 molecular sieve sample was designated GPZ19-2.

[0262] (Comparative Example 19-2) The same as Example 19-2, except that a phosphorus-modified ZSM-5 molecular sieve comparison sample was prepared by soaking the HZSM-5 molecular sieve at 20°C, and designated as D19-2.

[0263] The phosphorus dispersity K of GPZ19-1, D19-1, GPZ19-2 and D19-2 is shown in Table 1.

[0264] (Example 20-1) Example 20-1 illustrates the phosphorus-containing microporous ZSM-5 molecular sieve of the present invention and its preparation method.

[0265] 14.2 g of triphenylphosphine was dissolved in 80 g of deionized water and stirred for 2 hours to obtain a phosphorus-containing aqueous solution. 113 g of HZSM-5 molecular sieve was taken, and the phosphorus-containing aqueous solution and the HZSM-5 molecular sieve were heated to 80°C, respectively, and then mixed and contacted for 4 hours, dried at 110°C, and treated in an air atmosphere at 550°C for 2 hours. The resulting phosphorus-modified ZSM-5 molecular sieve sample was designated GPZ20-1.

[0266] Comparative Example 20-1 Comparative Example 20-1 illustrates current industry practice and the resulting phosphorus-modified ZSM-5 comparison sample.

[0267] The procedure was the same as in Example 20-1, except that the HZSM-5 molecular sieve was immersed in a phosphorus-containing aqueous solution at 20° C. using the immersion method. The resulting phosphorus-modified ZSM-5 molecular sieve comparison sample was designated as D20-1.

[0268] Example 20-2 Example 20-2 illustrates the phosphorus-containing microporous ZSM-5 molecular sieve of the present invention and its preparation method.

[0269] The procedure was the same as in Example 20-1, except that the air atmosphere at 550° C. was replaced by a 30% steam atmosphere at 600° C. for 4 hours. The resulting phosphorus-modified ZSM-5 molecular sieve sample was designated GPZ20-2.

[0270] Comparative Example 20-2 The procedure was the same as in Example 20-2, except that the HZSM-5 molecular sieve was immersed in a phosphorus-containing aqueous solution at 20° C. using the immersion method. The resulting phosphorus-modified ZSM-5 molecular sieve comparison sample was designated D20-2.

[0271] The phosphorus dispersities K of GPZ20-1, D20-1, GPZ20-2 and D20-2 are shown in Table 1.

[0272] Example 21-1 The procedure was the same as in Example 17-1, except that the phosphorus source was diammonium hydrogen phosphate and crystallized boron phosphate in a weight ratio of 3:1. The resulting phosphorus-modified ZSM-5 molecular sieve sample was designated as GPZ21-1.

[0273] Example 21-2 The procedure was the same as in Example 17-2, except that the phosphorus source was diammonium hydrogen phosphate and crystallized boron phosphate in a weight ratio of 3:1. The resulting phosphorus-modified ZSM-5 molecular sieve sample was designated as GPZ21-2.

[0274] Example 22-1 For example, the procedure was the same as in Example 17-1, except that the two phosphorus sources were diammonium hydrogen phosphate and crystallized boron phosphate, and the weight ratio of the two was 2:2. The resulting phosphorus-modified ZSM-5 molecular sieve sample was designated as GPZ22-1.

[0275] Example 22-2 The procedure was the same as in Example 17-2, except that the phosphorus source was diammonium hydrogen phosphate and crystallized boron phosphate in a weight ratio of 2:2. The resulting phosphorus-modified ZSM-5 molecular sieve sample was designated as GPZ23-2.

[0276] Example 23-1 The procedure was the same as in Example 17-1, except that the phosphorus source was diammonium hydrogen phosphate and crystallized boron phosphate in a weight ratio of 1:3. The resulting phosphorus-modified ZSM-5 molecular sieve sample was designated as GPZ23-1.

[0277] Example 23-2 The procedure was the same as in Example 17-2, except that the phosphorus source was diammonium hydrogen phosphate and crystallized boron phosphate in a weight ratio of 1:3. The resulting phosphorus-modified ZSM-5 molecular sieve sample was designated as GPZ23-2.

[0278] The phosphorus dispersity K of GPZ21-1, GPZ21-2, GPZ22-1, GPZ22-2, GPZ23-1 and GPZ23-2 is shown in Table 1.

[0279] Examples 24-1 to 26-2 The phosphorus sources of Examples 21-1 to 23-2 were replaced with phosphoric acid and crystallized boron phosphate, respectively, at ratios of 3:1, 3:1, 2:2, 2:2, 1:3, and 1:3, respectively. The phosphorus dispersities K of the resulting samples GPZ24-1, GPZ24-2, GPZ25-1, GPZ25-2, GPZ26-1, and GPZ26-2 are shown in Table 1.

[0280] As can be seen from the data in Table 1, all of the phosphorus-modified ZSM-5 molecular sieves of the present invention have high phosphorus dispersion. In particular, in Example 24-2, the sample modified with two phosphorus sources, i.e., diammonium hydrogen phosphate and crystallized boron phosphate, achieved a dispersion of 80%, with the maximum being 18%.

[0281] [Table 1-1]

[0282] [Table 1-2]

[0283] <Micro-reaction evaluation> Micro-reaction evaluation conditions: molecular sieve loading amount is 2 g, raw oil is n-tetradecane, oil supply amount is 1.56 g, reaction temperature is 550 °C, regeneration temperature is 600 °C (same below).

[0284] GPZ-1, D1-1, GPZ1-2 and D1-2; GPZ2-1, D2-1, GPZ2-2 and D2-2; GPZ3-1, D3-1, GPZ3-2 and D3-2; GPZ4-1, D4-1, GPZ4-2 and D4-2; GPZ5-1, D5-1, GPZ5-2 and D5-2; GPZ6-1, D6-1, GPZ6-2 and D6-2; GPZ7-1 , D7-1, GPZ7-2 and D7-2; GPZ8-1, GPZ8-2, GPZ9-1, GPZ9-2, GPZ10-1, GPZ10-2, GPZ11-1, GPZ11-2, GPZ12-1, GPZ12-2, GPZ13-1 and GPZ13-2; GPZ14-1, D14-1, GPZ14-2 and D14-2; GPZ15-1, D15-1, G PZ15-2, and D15-2; GPZ16-1, D16-1, GPZ16-2, and D16-2; GPZ17-1, D17-1, GPZ17-2, and D17-2; GPZ18-1, D18-1, GPZ18-2, and D18-2; GPZ19-1, D19-1, GPZ19-2, and D19-2; GPZ20-1, D20-1, and GPZ20-2 , and D20-2; GPZ21-1, GPZ21-2, GPZ22-1, GPZ22-2, GPZ23-1, GPZ23-2, GPZ24-1, GPZ24-2, GPZ25-1, GPZ25-2, GPZ26-1, and GPZ26-2 were subjected to hydrothermal aging treatment at 800°C in 100% steam for 17 hours, and the decomposition of n-tetradecane was evaluated. The evaluation data are shown in Table 2.

[0285] [Table 2-1]

[0286] [Table 2-2]

[0287] [Table 2-3]

[0288] [Table 2-4]

[0289] [Table 2-5]

[0290] [Table 2-6]

[0291] After hydrothermal aging at 800°C with 100% steam for 17 hours, the example sample showed excellent catalytic cracking activity for n-tetradecane, with improved conversion, liquefied gas yield, and yields of three olefins. The phosphorus-modified MFI molecular sieve of the present invention was found to increase the yield of low-carbon olefins and have a higher liquefied gas yield.

[0292] Examples 27-30 illustrate the phosphorus-aluminum inorganic binders used in the catalytic cracking aid / catalyst of the present invention.

[0293] Example 27 1.91 kg of pseudoboehmite (containing 1.19 kg of Al2O3), 0.56 kg of kaolin (0.5 kg dry basis), and 3.27 kg of deionized water were vigorously mixed and stirred for 30 minutes to form a slurry. While stirring, 5.37 kg of concentrated phosphoric acid (85% mass concentration) was added to the slurry at a phosphoric acid addition rate of 0.04 kg / min / kg alumina source. The mixture was heated to 70°C and then reacted at this temperature for 45 minutes to obtain a phosphorus-aluminum inorganic binder. The raw material composition is shown in Table 3, and the sample number was Binder 1.

[0294] Examples 28 to 30 Phosphorus-aluminum inorganic binders were prepared according to the method of Example 27. The raw material compositions are shown in Table 3, and the sample numbers were Binder2, Binder3, and Binder4.

[0295] [Table 3]

[0296] [Table 4]

[0297] [Table 5]

[0298] Examples 31 to 56 provide catalytic cracking aids of the present invention, and Comparative Examples 31 to 56 illustrate comparative catalytic cracking aids. Examples 31 to 43 are ZSM-5 molecular sieves having a hierarchical structure, and Examples 44 to 56 are microporous ZSM-5 molecular sieves.

[0299] (Example 31-1) The phosphorus-modified molecular sieve GPZ1-1 prepared in Example 1-1, kaolin, and pseudoboehmite were added to decationized water and alumina sol, and the mixture was vigorously mixed and stirred for 120 minutes to obtain a slurry with a solids content of 30% by weight. After adjusting the pH of the slurry to 3.0 by adding hydrochloric acid, the mixture was vigorously mixed and stirred for 45 minutes. Then, the phosphorus-aluminum inorganic binder Binder 1 prepared in Example 27 was added and stirred for 30 minutes. The resulting slurry was spray-dried to obtain microspheres. The microspheres were calcined at 500°C for 1 hour to obtain a catalytic cracking aid sample designated CAZ1-1. The composition of the mixture was 50% molecular sieve, 23% kaolin, 18% Binder 1, 5% pseudoboehmite (based on Al2O3), and 4% alumina sol (based on Al2O3).

[0300] Using a fixed-bed microreactor, the reaction performance of a 100% equilibrium catalyst and an equilibrium catalyst incorporating CAZ1-1 was evaluated to demonstrate the catalytic cracking reaction effect of the catalytic cracking aid provided herein.

[0301] CAZ1-1 was aged at 800°C in a 100% steam atmosphere for 17 hours. The aged CAZ1-1 was mixed with an industrial FCC equilibrium catalyst (industrial number DVR-3, diesel micro-reaction activity 63). The mixture of the equilibrium catalyst and additive was loaded into a fixed-bed micro-reaction reactor, and the feedstock oil shown in Table 4 was catalytically cracked. The evaluation conditions were a reaction temperature of 620°C, a regeneration temperature of 620°C, and a catalyst-to-oil ratio of 3.2. Table 6 shows the reaction results, including a blank test example.

[0302] (Example 31-2) The procedure was the same as in Example 31-1, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with the phosphorus-modified molecular sieve GPZ1-2 prepared in Example 1-2. The resulting catalytic cracking aid sample was designated CAZ1-2. It was evaluated in the same manner as in Example 31-1, and the results are shown in Table 6.

[0303] (Comparative Example 31-1) The same procedure as in Example 12-1 was followed, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with comparative sample D1-1 from Comparative Example 1-1. The obtained comparative catalytic cracking aid sample was designated DCAZ1-1. Evaluation was carried out in the same manner as in Example 31-1, and the results are shown in Table 6.

[0304] (Comparative Example 31-2) The same procedure as in Example 31-1 was followed, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with comparative sample D1-2 from Comparative Example 1-2. The obtained comparative catalytic cracking aid sample was designated DCAZ1-2. Evaluation was carried out in the same manner as in Example 31-1, and the results are shown in Table 6.

[0305] (Example 32-1) The procedure was the same as in Example 31-1, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with the phosphorus-modified molecular sieve GPZ2-1 prepared in Example 2-1. The resulting catalytic cracking aid sample was designated CAZ2-1. It was evaluated in the same manner as in Example 31-1, and the results are shown in Table 6.

[0306] (Example 32-2) The procedure was the same as in Example 32-1, except that the phosphorus-modified molecular sieve GPZ2-1 was replaced with the phosphorus-modified molecular sieve GPZ2-2 prepared in Example 2-2. The resulting catalytic cracking aid sample was designated CAZ2-2. Evaluation was performed in the same manner as in Example 31-1, and the results are shown in Table 6.

[0307] (Comparative Example 32-1) The same procedure as in Example 32-1 was followed, except that the phosphorus-modified molecular sieve GPZ2-1 was replaced with comparative sample D2-1 from Comparative Example 2-1. The obtained comparative catalytic cracking aid sample was designated DCAZ2-1. Evaluation was carried out in the same manner as in Example 31-1, and the results are shown in Table 6.

[0308] (Comparative Example 32-2) The same procedure as in Example 32-1 was followed, except that the phosphorus-modified molecular sieve GPZ2-1 was replaced with comparative sample D2-2 from Comparative Example 2-2. The obtained catalytic cracking aid comparative sample was designated DCAZ2-2. Evaluation was carried out in the same manner as in Example 31-1, and the results are shown in Table 6.

[0309] (Example 33-1) The procedure was the same as in Example 31-1, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with the phosphorus-modified molecular sieve GPZ3-1 prepared in Example 3-1. The resulting catalytic cracking aid sample was designated CAZ3-1. It was evaluated in the same manner as in Example 31-1, and the results are shown in Table 6.

[0310] (Example 33-2) The same procedure as in Example 31-1 was followed, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with the phosphorus-modified molecular sieve GPZ3-2 prepared in Example 3-2. The resulting catalytic cracking aid sample was designated CAZ3-2. Evaluation was carried out in the same manner as in Example 31-1, and the results are shown in Table 6.

[0311] (Comparative Example 33-1) The same procedure as in Example 31-1 was followed, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with comparative sample D3-1 from Comparative Example 3-1. The obtained comparative catalytic cracking aid sample was designated DCAZ3-1. Evaluation was carried out in the same manner as in Example 31-1, and the results are shown in Table 6.

[0312] (Comparative Example 33-2) The same procedure as in Example 31-1 was followed, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with comparative sample D3-2 from Comparative Example 3-2. The obtained comparative catalytic cracking aid sample was designated DCAZ3-2. Evaluation was carried out in the same manner as in Example 31-1, and the results are shown in Table 6.

[0313] (Example 34-1) The procedure was the same as in Example 31-1, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with the phosphorus-modified molecular sieve GPZ4-1 prepared in Example 4-1. The resulting catalytic cracking aid sample was designated CAZ4-1. It was evaluated in the same manner as in Example 31-1, and the results are shown in Table 6.

[0314] (Example 34-2) The procedure was the same as in Example 34-1, except that the phosphorus-modified molecular sieve GPZ4-1 was replaced with the phosphorus-modified molecular sieve GPZ4-2 prepared in Example 4-2. The resulting catalytic cracking aid sample was designated CAZ4-2. It was evaluated in the same manner as in Example 31-1, and the results are shown in Table 6.

[0315] (Comparative Example 34-1) The same procedure as in Example 34-1 was followed, except that the phosphorus-modified molecular sieve GPZ4-1 was replaced with comparative sample D4-1 from Comparative Example 4-1. The obtained comparative catalytic cracking aid sample was designated DCAZ4-1. Evaluation was carried out in the same manner as in Example 31-1, and the results are shown in Table 6.

[0316] (Comparative Example 34-2) The same procedure as in Example 34-1 was followed, except that the phosphorus-modified molecular sieve GPZ4-1 was replaced with comparative sample D4-2 from Comparative Example 2-2. The obtained comparative catalytic cracking aid sample was designated DCAZ4-2. Evaluation was carried out in the same manner as in Example 31-1, and the results are shown in Table 6.

[0317] (Example 35-1) The procedure was the same as in Example 31-1, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with the phosphorus-modified molecular sieve GPZ5-1 prepared in Example 5-1. The resulting catalytic cracking aid sample was designated CAZ5-1. It was evaluated in the same manner as in Example 31-1, and the results are shown in Table 6.

[0318] (Example 35-2) The procedure was the same as in Example 35-1, except that the phosphorus-modified molecular sieve GPZ5-1 was replaced with the phosphorus-modified molecular sieve GPZ5-2 prepared in Example 5-2. The resulting catalytic cracking aid sample was designated CAZ5-2. Evaluation was performed in the same manner as in Example 35-1, and the results are shown in Table 6.

[0319] (Comparative Example 35-1) The same procedure as in Example 35-1 was followed, except that the phosphorus-modified molecular sieve GPZ5-1 was replaced with comparative sample D5-1 from Comparative Example 5-1. The obtained comparative catalytic cracking aid sample was designated DCAZ5-1. Evaluation was carried out in the same manner as in Example 35-1, and the results are shown in Table 6.

[0320] (Comparative Example 35-2) The same procedure as in Example 35-1 was followed, except that the phosphorus-modified molecular sieve GPZ5-1 was replaced with comparative sample D5-2 from Comparative Example 2-2. The obtained comparative catalytic cracking aid sample was designated DCAZ5-2. Evaluation was carried out in the same manner as in Example 35-1, and the results are shown in Table 6.

[0321] (Example 36-1) The procedure was the same as in Example 31-1, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with the phosphorus-modified molecular sieve GPZ6-1 prepared in Example 6-1. The resulting catalytic cracking aid sample was designated CAZ6-1. It was evaluated in the same manner as in Example 31-1, and the results are shown in Table 6.

[0322] (Example 36-2) The procedure was the same as in Example 36-1, except that the phosphorus-modified molecular sieve GPZ6-1 was replaced with the phosphorus-modified molecular sieve GPZ6-2 prepared in Example 6-2. The resulting catalytic cracking aid sample was designated CAZ6-2. Evaluation was performed in the same manner as in Example 36-1, and the results are shown in Table 6.

[0323] (Comparative Example 36-1) The same procedure as in Example 36-1 was followed, except that the phosphorus-modified molecular sieve GPZ6-1 was replaced with comparative sample D6-1 from Comparative Example 6-1. The obtained comparative catalytic cracking aid sample was designated DCAZ6-1. Evaluation was carried out in the same manner as in Example 36-1, and the results are shown in Table 6.

[0324] (Comparative Example 36-2) The same procedure as in Example 36-1 was followed, except that the phosphorus-modified molecular sieve GPZ6-1 was replaced with comparative sample D6-2 from Comparative Example 6-2. The obtained catalytic cracking aid comparative sample was designated DCAZ6-2. Evaluation was carried out in the same manner as in Example 36-1, and the results are shown in Table 6.

[0325] (Example 37-1) The procedure was the same as in Example 31-1, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with the phosphorus-modified molecular sieve GPZ7-1 prepared in Example 7-1. The resulting catalytic cracking aid sample was designated CAZ7-1. It was evaluated in the same manner as in Example 31-1, and the results are shown in Table 6.

[0326] (Example 37-2) The procedure was the same as in Example 37-1, except that the phosphorus-modified molecular sieve GPZ7-1 was replaced with the phosphorus-modified molecular sieve GPZ7-2 prepared in Example 7-2. The resulting catalytic cracking aid sample was designated CAZ7-2. It was evaluated in the same manner as in Example 31-1, and the results are shown in Table 6.

[0327] (Comparative Example 37-1) The same procedure as in Example 37-1 was followed, except that the phosphorus-modified molecular sieve GPZ7-1 was replaced with comparative sample D7-1 from Comparative Example 7-1. The obtained comparative catalytic cracking aid sample was designated DCAZ7-1. Evaluation was carried out in the same manner as in Example 31-1, and the results are shown in Table 6.

[0328] (Comparative Example 37-2) The same procedure as in Example 37-1 was followed, except that the phosphorus-modified molecular sieve GPZ7-1 was replaced with comparative sample D7-2 from Comparative Example 7-2. The obtained comparative catalytic cracking aid sample was designated DCAZ7-2. Evaluation was carried out in the same manner as in Example 31-1, and the results are shown in Table 6.

[0329] (Examples 38 to 43) The procedure was the same as in Example 31-1, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with the phosphorus-modified molecular sieves GPZ8-1 to GPZ13-2 prepared in Examples 8-1 to 13-2, respectively. The numbers of the resulting catalytic cracking aid samples were designated CAZ8-1 to CAZ13-2, respectively. Evaluations were performed in the same manner as in Example 31-1, and the results are shown in Table 6.

[0330] (Examples 44 to 56) Examples 44 to 56 are respectively the auxiliary materials CAZ14 to CAZ26 ​​containing microporous ZSM-5 (GPZ14 to GPZ26), and their raw material compositions correspond to those of Examples 31 to 43. For example, in Example 44-1, GPZ1-1 was replaced with GPZ14-1, in Example 44-2, GPZ1-2 was replaced with GPZ14-2, in Example 56-1, GPZ14-1 was replaced with GPZ26-1, and in Example 56-2, GPZ14-2 was replaced with GPZ26-2. Evaluations were carried out in the same manner as in Example 31-1, and the results are shown in Table 6.

[0331] (Comparative Examples 44 to 50) Comparative Examples 44 to 50 are DCAZ-14 to DCAZ-20 containing microporous ZSM-5 (D14 to D20), respectively, and their raw material compositions correspond to those of Examples 44 to 50, respectively. For example, in Comparative Example 44-1, GPZ1-1 was replaced with D14-1, in Comparative Example 44-2, GPZ1-2 was replaced with D14-2, in Comparative Example 50-1, GPZ14-1 was replaced with D20-1, and in Comparative Example 50-2, GPZ14-2 was replaced with D20-2. Evaluations were performed in the same manner as in Example 31-1, and the results are shown in Table 6.

[0332] (Examples 57 to 62) The procedure was the same as in Example 31-1, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with the phosphorus-modified molecular sieves GPZ21-1 to GPZ26-2 prepared in Examples 21-1 to 26-2, respectively. The resulting catalytic cracking aid samples were numbered CAZ27-1 to CAZ32-2, respectively. Evaluations were performed in the same manner as in Example 31-1, and the results are shown in Table 6.

[0333] (Example 63-1) The procedure was the same as in Example 31-1, except that the phosphorus-aluminum inorganic binder was replaced with Binder 2 prepared in Example 28. The catalytic cracking aid obtained was designated CAZ33-1. It was evaluated in the same manner as in Example 31-1, and the results are shown in Table 6.

[0334] (Example 63-2) The procedure was the same as in Example 31-2, except that the phosphorus-aluminum inorganic binder was replaced with Binder 2 prepared in Example 28. The resulting catalytic cracking aid was designated CAZ33-2. It was evaluated in the same manner as in Example 31-1, and the results are shown in Table 6.

[0335] (Example 64-1) The procedure was the same as in Example 31-1, except that the phosphorus-aluminum inorganic binder was replaced with Binder 3 prepared in Example 29. The resulting catalytic cracking aid was designated CAZ34-1. It was evaluated in the same manner as in Example 31-1, and the results are shown in Table 6.

[0336] (Example 64-2) The procedure was the same as in Example 31-2, except that the phosphorus-aluminum inorganic binder was replaced with Binder 3 prepared in Example 29. The resulting catalytic cracking aid was designated CAZ34-2. It was evaluated in the same manner as in Example 31-1, and the results are shown in Table 6.

[0337] (Example 65-1) The procedure was the same as in Example 31-1, except that the phosphorus-aluminum inorganic binder was replaced with Binder 4 prepared in Example 30. The resulting catalytic cracking aid was designated CAZ35-1. It was evaluated in the same manner as in Example 31-1, and the results are shown in Table 6.

[0338] (Example 65-2) The procedure was the same as in Example 31-2, except that the phosphorus-aluminum inorganic binder was replaced with Binder 4 prepared in Example 30. The catalytic cracking aid obtained was designated CAZ35-2. It was evaluated in the same manner as in Example 31-1, and the results are shown in Table 6.

[0339] (Example 66-1) The procedure was the same as in Example 31-1, except that a catalytic cracking aid was prepared using phosphorus-modified ZSM-5 molecular sieve sample GPZ1-1 (45 wt%), kaolin (18 wt%), phosphorus-aluminum inorganic binder Binder 3 (22 wt%), pseudoboehmite (10 wt%), and alumina sol (5 wt%). The catalytic cracking aid was designated CAZ36-1. Evaluation was performed in the same manner as in Example 31-1, and the results are shown in Table 6.

[0340] (Example 66-2) The procedure was the same as in Example 66-1, except that GPZ1-1 was replaced with GPZ1-2. The resulting catalytic cracking aid was designated CAZ36-2. Evaluation was performed in the same manner as in Example 31-1, and the results are shown in Table 6.

[0341] (Comparative Example 66-1) The same procedure as in Example 66-1 was followed, except that GPZ1-1 was replaced with D1-1. The obtained comparative catalytic cracking aid sample was designated DCAZ36-1. It was evaluated in the same manner as in Example 31-1, and the results are shown in Table 6.

[0342] (Comparative Example 66-2) The same procedure was followed as in Example 66-1, except that GPZ1-1 was replaced with D1-2. The obtained comparative catalytic cracking aid sample was designated DCAZ36-2. It was evaluated in the same manner as in Example 31-1, and the results are shown in Table 6.

[0343] (Example 67-1) The procedure was the same as in Example 44-1, except that a catalytic cracking aid was prepared using phosphorus-modified ZSM-5 molecular sieve sample GPZ14-1 (40 wt%), kaolin (24 wt%), phosphorus-aluminum inorganic binder Binder 4 (20 wt%), pseudoboehmite (6 wt%), and silica sol (10 wt%). The catalytic cracking aid was designated CAZ37-1. It was evaluated in the same manner as in Example 31-1, and the results are shown in Table 6.

[0344] (Example 67-2) The procedure was the same as in Example 67-1, except that GPZ14-1 was replaced with GPZ14-2. The resulting catalytic cracking aid was designated CAZ37-2. Evaluation was performed in the same manner as in Example 31-1, and the results are shown in Table 6.

[0345] (Comparative Example 67-1) The same procedure as in Example 67-1 was followed, except that GPZ14-1 was replaced with D14-1. The obtained comparative catalytic cracking aid sample was designated DCAZ37-1. It was evaluated in the same manner as in Example 31-1, and the results are shown in Table 6.

[0346] (Comparative Example 67-2) The same procedure as in Example 67-1 was followed, except that GPZ14-1 was replaced with D14-2. The obtained comparative catalytic cracking aid sample was designated DCAZ37-2. Evaluation was carried out in the same manner as in Example 31-1, and the results are shown in Table 6.

[0347] (Example 68-1) Alumina sol, a binder, was mixed with kaolin and decationized water was added to prepare a slurry with a solids content of 30 wt%. The slurry was thoroughly stirred and the pH was adjusted to 2.8 with hydrochloric acid. The slurry was aged at 55°C for 1 hour. Next, the phosphorus-modified molecular sieve GPZ1-1 prepared in Example 1-1 was added to form a slurry with a solids content of 35 wt%. The slurry was stirred continuously and spray-dried to form microspheres. The microspheres were then calcined at 500°C for 1 hour and further washed with ammonium sulfate (ammonium sulfate:microspheres:water = 0.5:1:10) at 60°C until the sodium oxide content was less than 0.25 wt%, followed by rinsing with deionized water, filtering, and drying at 110°C to obtain additive CAZ38-1. The composition of the additive was 50% molecular sieve, 23% kaolin, and 27% alumina sol (based on Al2O3). The evaluation was carried out in the same manner as in Example 31-1, and the results are shown in Table 6.

[0348] (Example 68-2) The procedure was the same as in Example 68-1, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with the phosphorus-modified molecular sieve GPZ1-2 prepared in Example 1-2. The resulting catalytic cracking aid sample was designated CAZ38-2. It was evaluated in the same manner as in Example 31-1, and the results are shown in Table 6.

[0349] (Comparative Example 68-1) The same procedure as in Example 68-1 was followed, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with comparative sample D1-1 from Comparative Example 1-1. The obtained comparative catalytic cracking aid sample was designated DCAZ38-1. It was evaluated in the same manner as in Example 31-1, and the results are shown in Table 6.

[0350] (Comparative Example 68-2) The same procedure as in Example 68-1 was followed, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with comparative sample D1-2 from Comparative Example 1-2. The obtained catalytic cracking aid comparative sample was designated DCAZ38-2. Evaluation was carried out in the same manner as in Example 31-1, and the results are shown in Table 6.

[0351] [Table 6-1]

[0352] [Table 6-2]

[0353] [Table 6-3]

[0354] [Table 6-4]

[0355] (Example 69-1, Example 69-2) In Examples 69-1 and 69-2, the catalytic cracking aids CAZ1-1 and CAZ1-2 in Examples 31-1 and 31-2 were used, respectively. The feedstock for catalytic cracking was naphtha shown in Table 5.

[0356] The evaluation conditions were a reaction temperature of 620°C, a regeneration temperature of 620°C, and a catalyst oil ratio of 3.2.

[0357] Table 7 shows the weight composition of each catalyst mixture containing a catalytic cracking aid and the reaction results.

[0358] (Comparative Example 69-1, Comparative Example 69-2) The same procedures as in Example 69-1 were carried out except that comparative catalytic cracking aids DCAZ1-1 and DCAZ1-2 of Comparative Examples 31-1 and 31-2, respectively, were used.

[0359] Table 7 shows the weight composition and reaction results of each catalyst mixture containing the comparative catalytic cracking aid sample.

[0360] (Example 70-1, Example 70-2) Examples 70-1 and 70-2 used the catalytic cracking aids CAZ14-1 and CAZ14-2 of Examples 44-1 and 44-2, respectively. The feedstock for catalytic cracking was naphtha shown in Table 5.

[0361] The evaluation conditions were a reaction temperature of 620°C, a regeneration temperature of 620°C, and a catalyst oil ratio of 3.2.

[0362] Table 7 shows the weight composition of each catalyst mixture containing a catalytic cracking aid and the reaction results.

[0363] (Comparative Example 70-1, Comparative Example 70-2) The same procedures were carried out as in Example 70-1, except that comparative catalytic cracking aids DCAZ14-1 and DCAZ14-2 of Comparative Examples 44-1 and 44-2, respectively, were used.

[0364] Table 7 shows the weight composition and reaction results of each catalyst mixture containing the comparative catalytic cracking aid sample.

[0365] [Table 7]

[0366] Examples Y31 to Y56 provide catalytic cracking catalysts of the present invention, and Comparative Examples Y31 to Y56 illustrate comparative catalytic cracking catalysts. Examples Y31 to Y43 contain phosphorus-modified hierarchical ZSM-5 molecular sieves, and Examples Y44 to Y56 contain phosphorus-modified microporous ZSM-5 molecular sieves.

[0367] (Example Y31-1) The phosphorus-modified molecular sieve GPZ1-1 prepared in Example 1-1, Y-type molecular sieve (PSRY-type molecular sieve), kaolin, and pseudoboehmite were added to decationized water and alumina sol, and the mixture was vigorously mixed and stirred for 120 minutes to obtain a slurry with a solids content of 30% by weight. Hydrochloric acid was added to adjust the pH of the slurry to 3.0, and the mixture was vigorously mixed and stirred for 45 minutes. Next, Binder 1, the phosphorus-aluminum inorganic binder prepared in Example 27, was added and stirred for 30 minutes. The resulting slurry was spray-dried to prepare microspheres. The microspheres were calcined at 500°C for 1 hour. The obtained catalytic cracking catalyst sample was designated CAZY1-1, and its composition was 40% phosphorus-modified ZSM-5 molecular sieve, 10% PSRY-type molecular sieve, 18% kaolin, 18% Binder 1, 5% pseudoboehmite (based on Al2O3), and 9% alumina sol (based on Al2O3).

[0368] To illustrate the catalytic cracking reaction effect, a fixed-bed microreactor is used to evaluate the reaction performance of a 100% equilibrium catalyst and an equilibrium catalyst incorporating CAZY1-1.

[0369] Catalyst CAZY1-1 was aged for 17 hours at 800°C in a 100% steam atmosphere. The aged CAZY1-1 was mixed with an industrial FCC equilibrium catalyst (industrial number DVR-3, diesel micro-reaction activity 63). The mixture of the equilibrium catalyst and catalyst was loaded into a fixed-bed micro-reaction reactor, and the feedstock oil shown in Table 4 was catalytically cracked. The evaluation conditions were a reaction temperature of 620°C, a regeneration temperature of 620°C, and a catalyst-to-oil ratio of 3.2. The reaction results, including a blank test example, are shown in Table 8.

[0370] (Example Y31-2) The procedure was the same as in Example Y31-1, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with the phosphorus-modified molecular sieve GPZ1-2 prepared in Example 1-2. The resulting catalytic cracking catalyst sample was designated CAZY1-2. The same evaluation as in Example Y31-1 was carried out, and the results are shown in Table 8.

[0371] (Comparative Example Y31-1) The same procedure as in Example Y31-1 was followed, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with comparative sample D1-1 from Comparative Example 1-1. The obtained comparative catalytic cracking catalyst sample was designated DCAZY1-1. Evaluation was carried out in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0372] (Comparative Example Y31-2) The same procedure as in Example Y31-1 was followed, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with comparative sample D1-2 from Comparative Example 1-2. The obtained comparative catalytic cracking catalyst sample was designated DCAZY1-2. Evaluation was carried out in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0373] (Example Y32-1) The procedure was the same as in Example Y31-1, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with the phosphorus-modified molecular sieve GPZ2-1 prepared in Example 2-1. The resulting catalytic cracking catalyst sample was designated CAZY2-1. It was evaluated in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0374] (Example Y32-2) The procedure was the same as in Example Y32-1, except that the phosphorus-modified molecular sieve GPZ2-1 was replaced with the phosphorus-modified molecular sieve GPZ2-2 prepared in Example 2-2. The resulting catalytic cracking catalyst sample was designated CAZY2-2. The evaluation was carried out in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0375] (Comparative Example Y32-1) The same procedure as in Example Y32-1 was followed, except that the phosphorus-modified molecular sieve GPZ2-1 was replaced with comparative sample D2-1 from Comparative Example 2-1. The obtained comparative catalytic cracking catalyst sample was designated DCAZY2-1. Evaluation was carried out in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0376] (Comparative Example Y32-2) The same procedure as in Example Y32-1 was followed, except that the phosphorus-modified molecular sieve GPZ2-1 was replaced with comparative sample D2-2 from Comparative Example 2-2. The obtained catalytic cracking catalyst comparative sample was designated DCAZY2-2. Evaluation was carried out in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0377] (Example Y33-1) The procedure was the same as in Example Y31-1, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with the phosphorus-modified molecular sieve GPZ3-1 prepared in Example 3-1. The resulting catalytic cracking catalyst sample was designated CAZY3-1. It was evaluated in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0378] (Example Y33-2) The procedure was the same as in Example Y31-1, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with the phosphorus-modified molecular sieve GPZ3-2 prepared in Example 3-2. The catalytic cracking catalyst sample obtained was numbered CAZY3-2. It was evaluated in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0379] (Comparative Example Y33-1) The same procedure as in Example Y31-1 was followed, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with comparative sample D3-1 from Comparative Example 3-1. The obtained comparative catalytic cracking catalyst sample was designated DCAZY3-1. Evaluation was carried out in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0380] (Comparative Example Y33-2) The same procedure as in Example Y31-1 was followed, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with comparative sample D3-2 from Comparative Example 3-2. The obtained comparative catalytic cracking catalyst sample was designated DCAZY3-2. Evaluation was carried out in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0381] (Example Y34-1) The procedure was the same as in Example Y31-1, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with the phosphorus-modified molecular sieve GPZ4-1 prepared in Example 4-1. The resulting catalytic cracking catalyst sample was designated CAZY4-1. It was evaluated in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0382] (Example Y34-2) The procedure was the same as in Example Y34-1, except that the phosphorus-modified molecular sieve GPZ4-1 was replaced with the phosphorus-modified molecular sieve GPZ4-2 prepared in Example 4-2. The resulting catalytic cracking catalyst sample was designated CAZY4-2. It was evaluated in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0383] (Comparative Example Y34-1) The same procedure as in Example Y34-1 was followed, except that the phosphorus-modified molecular sieve GPZ4-1 was replaced with comparative sample D4-1 from Comparative Example 4-1. The obtained comparative catalytic cracking catalyst sample was designated DCAZY4-1. Evaluation was carried out in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0384] (Comparative Example Y34-2) The procedure was the same as in Example Y34-1, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with comparative sample D4-2 from Comparative Example 4-2. The obtained catalytic cracking catalyst comparative sample was designated DCAZY4-2. It was evaluated in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0385] (Example Y35-1) The procedure was the same as in Example Y31-1, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with the phosphorus-modified molecular sieve GPZ5-1 prepared in Example 5-1. The resulting catalytic cracking catalyst sample was designated CAZY5-1. The same evaluation as in Example Y31-1 was carried out, and the results are shown in Table 8.

[0386] (Example Y35-2) The procedure was the same as in Example Y35-1, except that the phosphorus-modified molecular sieve GPZ5-1 was replaced with the phosphorus-modified molecular sieve GPZ5-2 prepared in Example 5-2. The obtained catalytic cracking catalyst comparative sample was designated CAZY5-2. Evaluation was carried out in the same manner as in Example Y35-1, and the results are shown in Table 8.

[0387] (Comparative Example Y35-1) The same procedure as in Example Y35-1 was followed, except that the phosphorus-modified molecular sieve GPZ5-1 was replaced with comparative sample D5-1 from Comparative Example 5-1. The obtained comparative catalytic cracking catalyst sample was designated DCAZY5-1. Evaluation was carried out in the same manner as in Example Y35-1, and the results are shown in Table 8.

[0388] (Comparative Example Y35-2) The same procedure as in Example Y35-1 was followed, except that the phosphorus-modified molecular sieve GPZ5-1 was replaced with comparative sample D5-2 from Comparative Example 5-2. The obtained catalytic cracking catalyst comparative sample was designated DCAZY5-2. Evaluation was carried out in the same manner as in Example Y35-1, and the results are shown in Table 8.

[0389] (Example Y36-1) The procedure was the same as in Example Y31-1, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with the phosphorus-modified molecular sieve GPZ6-1 prepared in Example 6-1. The resulting catalytic cracking catalyst sample was designated CAZY6-1. It was evaluated in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0390] (Example Y36-2) The procedure was the same as in Example Y36-1, except that the phosphorus-modified molecular sieve GPZ6-1 was replaced with the phosphorus-modified molecular sieve GPZ6-2 prepared in Example 6-2. The resulting catalytic cracking catalyst sample was designated CAZY6-2. The same evaluation as in Example Y36-1 was carried out, and the results are shown in Table 8.

[0391] (Comparative example Y36-1) The same procedure as in Example Y36-1 was followed, except that the phosphorus-modified molecular sieve GPZ6-1 was replaced with comparative sample D6-1 from Comparative Example 6-1. The obtained comparative catalytic cracking catalyst sample was designated DCAZY6-1. Evaluation was carried out in the same manner as in Example Y36-1, and the results are shown in Table 8.

[0392] (Comparative example Y36-2) The same procedure as in Example Y36-1 was followed, except that the phosphorus-modified molecular sieve GPZ6-1 was replaced with comparative sample D6-2 from Comparative Example 6-2. The obtained catalytic cracking catalyst comparative sample was designated DCAZY6-2. Evaluation was carried out in the same manner as in Example Y36-1, and the results are shown in Table 8.

[0393] (Example Y37-1) The procedure was the same as in Example Y31-1, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with the phosphorus-modified molecular sieve GPZ7-1 prepared in Example 7-1. The resulting catalytic cracking catalyst sample was designated CAZY7-1. It was evaluated in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0394] (Example Y37-2) The procedure was the same as in Example Y37-1, except that the phosphorus-modified molecular sieve GPZ7-1 was replaced with the phosphorus-modified molecular sieve GPZ7-2 prepared in Example 7-2. The resulting catalytic cracking catalyst sample was designated CAZY7-2. It was evaluated in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0395] (Comparative example Y37-1) The same procedure as in Example Y37-1 was followed, except that the phosphorus-modified molecular sieve GPZ7-1 was replaced with comparative sample D7-1 from Comparative Example 7-1. The obtained comparative catalytic cracking catalyst sample was designated DCAZY7-1. It was evaluated in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0396] (Comparative example Y37-2) The same procedure as in Example Y37-1 was followed, except that the phosphorus-modified molecular sieve GPZ7-1 was replaced with comparative sample D7-2 from Comparative Example 7-2. The obtained catalytic cracking catalyst comparative sample was designated DCAZY7-2. Evaluation was carried out in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0397] (Examples Y38 to Y43) The procedure was the same as in Example Y31-1, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with the phosphorus-modified molecular sieves GPZ8-1 to GPZ13-2 prepared in Examples 8-1 to 13-2, respectively. The numbers of the resulting catalytic cracking catalyst samples were designated CAZY8-1 to CAZY13-2, respectively. Evaluations were performed in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0398] (Examples Y44 to Y56) Examples Y44 to Y56 are catalysts CAZY14 to CAZY26 containing microporous ZSM-5 (GPZ14 to GPZ26), respectively, and their raw material compositions correspond to those of Examples Y31 to Y43, respectively. For example, in Example Y44-1, GPZ1-1 was replaced with GPZ14-1, in Example 44-2, GPZ1-2 was replaced with GPZ14-2, in Example Y56-1, GPZ13-1 was replaced with GPZ26-1, and in Example 56-2, GPZ13-2 was replaced with GPZ26-2. Evaluations were performed in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0399] (Comparative examples Y44~Y50) Comparative Examples Y44 to Y50 use microporous ZSM-5 (D14 to D20) and comparative catalysts DCAZY-14 to DCAZY-20, respectively, and their raw material compositions correspond to those of Examples Y44 to Y50, respectively. For example, in Comparative Example Y44-1, GPZ1-1 was replaced with D14-1, in Comparative Example Y44-2, GPZ1-2 was replaced with D14-2, in Comparative Example Y50-1, GPZ14-1 was replaced with D20-1, and in Comparative Example Y50-2, GPZ14-2 was replaced with D20-2. Evaluations were performed in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0400] (Examples Y57 to Y62) The procedure was the same as in Example Y31-1, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with the phosphorus-modified molecular sieves GPZ21-1 to GPZ26-2 prepared in Examples 21-1 to 26-2, respectively. The numbers of the resulting catalytic cracking aid samples were designated CAZY27-1 to CAZY32-2, respectively. Evaluations were performed in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0401] (Example Y63-1) The same procedure as in Example Y31-1 was followed, except that the phosphorus-aluminum inorganic binder was replaced with Binder2 prepared in Example Y28. The resulting catalytic cracking aid was designated CAZY33-1. It was evaluated in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0402] (Example Y63-2) The same procedure as in Example Y31-2 was followed, except that the phosphorus-aluminum inorganic binder was replaced with Binder2 prepared in Example Y28. The resulting catalytic cracking aid was designated CAZY33-2. It was evaluated in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0403] (Example Y64-1) The same procedure as in Example Y31-1 was followed, except that the phosphorus-aluminum inorganic binder was replaced with Binder 3 prepared in Example Y29. The resulting catalytic cracking aid was designated CAZY34-1. It was evaluated in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0404] (Example Y64-2) The same procedure as in Example Y31-2 was followed, except that the phosphorus-aluminum inorganic binder was replaced with Binder 3 prepared in Example Y29. The resulting catalytic cracking aid was designated CAZY34-2. It was evaluated in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0405] (Example Y65-1) The same procedure as in Example Y31-1 was followed, except that the phosphorus-aluminum inorganic binder was replaced with Binder 4 prepared in Example Y30. The resulting catalytic cracking aid was designated CAZY35-1. It was evaluated in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0406] (Example Y65-2) The same procedure was followed as in Example Y31-2, except that the phosphorus-aluminum inorganic binder was replaced with Binder 4 prepared in Example Y30. The resulting catalytic cracking aid was designated CAZY35-2. It was evaluated in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0407] (Example Y66-1) The catalytic cracking catalyst was prepared in the same manner as in Example Y31-1, except that the phosphorus-modified hierarchical ZSM-5 molecular sieve sample GPZ1-1 (35 wt%), PSRY-type molecular sieve (10 wt%), kaolin (18 wt%), phosphorus-aluminum inorganic binder Binder 3 (22 wt%), pseudoboehmite (10 wt%), and alumina sol (5 wt%) were used. The catalytic cracking catalyst was designated CAZY36-1. It was evaluated in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0408] (Example Y66-2) The procedure was the same as in Example Y66-1, except that GPZ1-1 was replaced with GPZ1-2. The resulting catalytic cracking catalyst was designated CAZY36-2. It was evaluated in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0409] (Comparative Example Y66-1) The procedure was the same as in Example Y66-1, except that GPZ1-1 was replaced with D1-1. The resulting catalytic cracking catalyst sample was designated DCAZY36-1. It was evaluated in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0410] (Comparative Example Y66-2) The procedure was the same as in Example Y66-1, except that GPZ1-1 was replaced with D1-2. The resulting catalytic cracking catalyst sample was designated DCAZY36-2. It was evaluated in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0411] (Example Y67-1) The catalytic cracking catalyst was prepared in the same manner as in Example Y44-1, except that it was prepared using phosphorus-modified microporous ZSM-5 molecular sieve sample GPZ14-1 (30 wt%), PSRY-type molecular sieve (6 wt%), kaolin (24 wt%), phosphorus-aluminum inorganic binder Binder 4 (22 wt%), pseudoboehmite (8 wt%), and silica sol (10 wt%). The catalytic cracking catalyst was designated CAZY37-1. It was evaluated in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0412] (Example Y67-2) The procedure was the same as in Example Y67-1, except that GPZ14-1 was replaced with GPZ14-2. The resulting catalytic cracking catalyst was designated CAZY37-2. It was evaluated in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0413] (Comparative Example Y67-1) The procedure was the same as in Example Y67-1, except that GPZ14-1 was replaced with D14-1. The resulting catalytic cracking catalyst sample was designated DCAZY37-1. It was evaluated in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0414] (Comparative Example Y67-2) The procedure was the same as in Example Y67-1, except that GPZ14-1 was replaced with D14-2. The resulting catalytic cracking catalyst sample was designated DCAZY37-2. It was evaluated in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0415] (Example Y68-1) Alumina sol, a binder, was mixed with kaolin and decationized water was added to prepare a slurry with a solids content of 30 wt%. The slurry was thoroughly stirred and the pH was adjusted to 2.8 with hydrochloric acid. The slurry was aged at 55°C for 1 hour. Next, the phosphorus-modified molecular sieve GPZ1-1 prepared in Example 1-1 and Y-type molecular sieve (PSRY-type molecular sieve) were added to form a catalyst slurry with a solids content of 35 wt%. The slurry was stirred continuously and spray-dried to form a microsphere catalyst. The microsphere catalyst was then calcined at 500°C for 1 hour, washed with ammonium sulfate (ammonium sulfate:microsphere catalyst:water = 0.5:1:10) at 60°C until the sodium oxide content was less than 0.25 wt%, rinsed with deionized water, filtered, and then dried at 110°C to obtain catalyst CAZY38-1. The composition is 40% phosphorus-modified ZSM-5 molecular sieve GPZ1-1, 10% PSRY type molecular sieve, 25% kaolin, and 25% alumina sol (based on Al2O3). Evaluation was carried out in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0416] (Example Y68-2) The procedure was the same as in Example Y68-1, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with the phosphorus-modified molecular sieve GPZ1-2 prepared in Example 1-2. The resulting catalytic cracking catalyst sample was designated CAZY38-2. Evaluations were performed in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0417] (Comparative Example Y68-1) The same as Example Y68-1, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with comparative sample D1-1 of Comparative Example Y1-1. The obtained comparative catalytic cracking aid sample was designated DCAZY38-1. It was evaluated in the same manner as Example Y31-1, and the results are shown in Table 8.

[0418] (Comparative Example Y68-2) The same procedure as in Example Y68-1 was followed, except that the phosphorus-modified molecular sieve GPZ1-1 was replaced with comparative sample D1-2 from Comparative Example Y1-2. The obtained comparative catalytic cracking aid sample was designated DCAZY38-2. Evaluation was carried out in the same manner as in Example Y31-1, and the results are shown in Table 8.

[0419] (Example Y69-1, Example Y69-2) Examples Y69-1 and Y69-2 used the catalytic cracking catalysts CAZY1-1 and CAZY1-2 of Examples Y31-1 and Y31-2, respectively. The feedstock for catalytic cracking was naphtha shown in Table 5.

[0420] The evaluation conditions were a reaction temperature of 620°C, a regeneration temperature of 620°C, and a catalyst oil ratio of 3.2.

[0421] The weight composition of the catalyst mixture containing the catalytic cracking catalyst and the reaction results are shown in Table 9.

[0422] (Comparative Example Y69-1, Comparative Example Y69-2)

[0423] [Table 8-1]

[0424] [Table 8-2]

[0425] [Table 8-3]

[0426] [Table 8-4]

[0427] [Table 8-5]

[0428] [Table 8-6]

[0429] [Table 8-7]

[0430] Comparative Examples Y31-1 and Y31-2 were the same as Example Y69-1 except that comparative catalytic cracking catalysts DCAZY1-1 and DCAZY1-2, respectively, were used.

[0431] Table 9 shows the weight composition and reaction results of each catalyst mixture including the comparative catalytic cracking catalyst sample.

[0432] (Example Y70-1, Example Y70-2) Examples Y70-1 and Y70-2 used the catalytic cracking catalysts CAZY14-1 and CAZY14-2 of Examples Y44-1 and Y44-2, respectively. The feedstock for catalytic cracking was naphtha shown in Table 5.

[0433] The evaluation conditions were a reaction temperature of 620°C, a regeneration temperature of 620°C, and a catalyst oil ratio of 3.2.

[0434] The weight composition of each catalyst mixture containing a catalytic cracking catalyst and the reaction results are shown in Table 9.

[0435] (Comparative Example Y70-1, Comparative Example Y70-2) Comparative Examples Y44-1 and Y44-2 were the same as Example Y70-1 except that comparative catalytic cracking catalysts DCAZY14-1 and DCAZY14-2, respectively, were used.

[0436] Table 9 shows the weight composition and reaction results of each catalyst mixture including the comparative catalytic cracking catalyst sample.

[0437] [Table 9]

[0438] (Example Y71-1) The procedure was the same as in Example Y31-1, except that the Y-type molecular sieve (PSRY) was replaced with HRY-1. The resulting catalyst sample was designated CAZY39-1. Evaluations were carried out in the same manner as in Example Y31-1, and the results are shown in Table 10.

[0439] (Example Y71-2) The procedure was the same as in Example Y31-1, except that the Y-type molecular sieve (PSRY) was replaced with HRY-1. The resulting catalyst sample was designated CAZY39-2. Evaluations were carried out in the same manner as in Example Y31-1, and the results are shown in Table 10.

[0440] (Comparative Example Y71-1) The procedure was the same as in Example Y31-1, except that the Y-type molecular sieve (PSRY) was replaced with HRY-1. The obtained catalyst comparison sample was designated DCAZY39-1. Evaluation was performed in the same manner as in Example Y31-1, and the results are shown in Table 10.

[0441] (Comparative Example Y71-2) The procedure was the same as in Example Y31-1, except that the Y-type molecular sieve (PSRY) was replaced with HRY-1. The obtained catalyst comparison sample was designated DCAZY39-2. Evaluation was performed in the same manner as in Example Y31-1, and the results are shown in Table 10.

[0442]

Table 10

Claims

1. A phosphorus-modified MFI structured molecular sieve, Having a K value that satisfies 70%≦K≦90%, K = P1 / P2 x 100%; P1 represents the mass content of phosphorus in a region having an area of ​​100 square nanometers and a vertical depth of 0 to 2 nm on any crystal face of a crystal grain of the molecular sieve, as measured by an XPS method; P2 represents the mass content of phosphorus in a region having an area of ​​100 square nanometers and a vertical depth of 5 to 10 nm on any crystal face of a crystal grain of the molecular sieve, as measured by EPMA.

2. 2. The molecular sieve of claim 1, wherein the molar ratio of the phosphorus content on a P2O5 basis to the alumina content is ≥ 0.

01.

3. 3. The molecular sieve according to claim 1, wherein the phosphorus-modified MFI-structured molecular sieve is a microporous ZSM-5 molecular sieve or a ZSM-5 molecular sieve having a hierarchical structure.

4. 4. The molecular sieve of claim 3, wherein the microporous ZSM-5 molecular sieve has a silica / alumina molar ratio of 15-1000.

5. 4. The molecular sieve according to claim 3, wherein the ZSM-5 molecular sieve having a hierarchical structure has a ratio of mesopore volume to total pore volume of more than 10%, an average pore diameter of 2 to 20 nm, and a silica / alumina molar ratio of 15 to 1000.

6. On a dry basis, catalytic cracking aid 5 to 75 wt. % of the phosphorus-modified MFI-structured molecular sieve according to any one of claims 1 to 5; 1 to 40 wt. % of a binder; and 0 to 65 wt. % of a second clay.

7. the binder comprises a phosphorus-aluminum inorganic binder and / or other inorganic binders; the phosphorus-aluminum inorganic binder is a phosphorus-aluminum adhesive and / or a first clay-containing phosphorus-aluminum inorganic binder, the first clay-containing phosphorus-aluminum inorganic binder comprising, on an Al2O3 basis, 10 to 40 wt. % of an aluminum component, on a P2O5 basis, 45 to 90 wt. % of a phosphorus component, and on a dry basis, greater than 0 and not more than 40 wt. % of a first clay, the first clay-containing phosphorus-aluminum inorganic binder having a P / Al weight ratio of 1.0 to 6.0, a pH of 1 to 3.5, and a solids content of 15 to 60 wt. %; the second clay is selected from kaolin, sepiolite, attapulgite, rectorite, smectite, diatomaceous earth, metahalloysite, halloysite, hydrotalcite, and bentonite; The catalytic cracking aid according to claim 6, wherein the other inorganic binder is selected from the group consisting of pseudoboehmite, alumina sol, silica-alumina sol, and water glass.

8. A catalytic cracking catalyst comprising a phosphorus-modified MFI structured molecular sieve, On a dry basis of the catalyst, 1 to 25 wt. % of Y-type molecular sieve; 5 to 50 wt. % of the phosphorus-modified MFI-structured molecular sieve according to any one of claims 1 to 5; 1 to 60 wt. % of an inorganic binder; and optionally, 0 to 60 wt. % of a second clay.

9. The inorganic binder comprises a phosphorus-aluminum inorganic binder and / or other inorganic binders; The phosphorus-aluminum inorganic binder is a phosphorus-aluminum adhesive and / or a first clay-containing phosphorus-aluminum inorganic binder; the first clay-containing phosphorus-aluminum inorganic binder comprises, on an Al2O3 basis, 10 to 40 wt% of an aluminum component, on a P2O5 basis, 45 to 90 wt% of a phosphorus component, and, on a dry basis, more than 0 and not more than 40 wt% of a first clay, wherein the first clay-containing phosphorus-aluminum inorganic binder has a P / Al weight ratio of 1.0 to 6.0, a pH of 1 to 3.5, and a solids content of 15 to 60 wt%; the second clay is selected from kaolin, sepiolite, attapulgite, rectorite, smectite, diatomaceous earth, metahalloysite, halloysite, hydrotalcite, and bentonite; 9. The catalytic cracking catalyst according to claim 8, wherein the other inorganic binder is selected from the group consisting of pseudoboehmite, alumina sol, silica-alumina sol, and water glass.

10. 9. The catalytic cracking catalyst according to claim 8, wherein the Y-type molecular sieve comprises at least one of a PSRY-type molecular sieve, a rare earth-containing PSRY-type molecular sieve, a USY-type molecular sieve, a rare earth-containing USY-type molecular sieve, a REY-type molecular sieve, a REHY-type molecular sieve, and a HY-type molecular sieve.

11. Mixing and contacting an aqueous solution of a phosphorus-containing compound at 40 to 150°C with an MFI-structured molecular sieve at 40 to 150°C at substantially the same temperature for 0.1 hours or more, then drying and calcining the mixture at 200 to 600°C in an air or water vapor atmosphere for 0.1 hours or more; or 6. A method for preparing the phosphorus-modified MFI molecular sieve according to claim 1, wherein the phosphorus-modified MFI molecular sieve is obtained by a dipping method comprising vigorously mixing and stirring a phosphorus-containing compound, an MFI molecular sieve, and water to form a slurry, adjusting the temperature to 40 to 150°C, maintaining the temperature for 0.1 hour or more, drying the slurry, and calcining the slurry at 200 to 600°C in an air or water vapor atmosphere for 0.1 hour or more.

12. the phosphorus-containing compound is selected from organic phosphorus compounds and / or inorganic phosphorus compounds, the organic phosphorus compound is selected from trimethyl phosphate, triphenylphosphine, trimethyl phosphite, tetrabutyl phosphonium bromide, tetrabutyl phosphonium chloride, tetrabutyl phosphonium hydroxide, triphenylethyl phosphonium bromide, triphenylbutyl phosphonium bromide, triphenylbenzyl phosphonium bromide, hexamethylphosphoric triamide, dibenzyl diethyl phosphoramidite, and 1,3-bis((triethylphosphine)methyl)benzene; 12. The method for preparing a phosphorus-modified MFI-structured molecular sieve according to claim 11, wherein said inorganic phosphorus compound is selected from the group consisting of phosphoric acid, ammonium hydrogen phosphate, diammonium hydrogen phosphate, ammonium phosphate, and boron phosphate.

13. 13. The method for preparing a phosphorus-modified MFI-structured molecular sieve according to claim 11 or 12, wherein the molar ratio of the phosphorus-containing compound on a phosphorus basis (oxide basis) to the MFI-structured molecular sieve on an aluminum basis (oxide basis) is 0.01 to 2.

14. the phosphorus-containing compound is a mixture of one or more compounds selected from trimethyl phosphate, triphenylphosphine, trimethyl phosphite, phosphoric acid, ammonium hydrogen phosphate, diammonium hydrogen phosphate, and ammonium phosphate with boron phosphate; The method for preparing a phosphorus-modified MFI-structured molecular sieve according to any one of claims 11 to 13, wherein the boron phosphate in the mixture is 10 to 80 wt%.

15. The method for preparing phosphorus-modified MFI-structured molecular sieve according to any one of claims 11 to 14, wherein the weight ratio of water / molecular sieve in said contact is 0.5 to 1, and the contact time is 0.5 to 40 hours.

16. The method for preparing a phosphorus-modified MFI-structured molecular sieve according to any one of claims 11 to 15, wherein the calcination is carried out at 450 to 550°C in a steam atmosphere.

17. 8. A method for preparing the catalytic cracking aid of claim 6 or 7, comprising vigorously mixing and stirring the phosphorus-modified MFI structured molecular sieve, binder, and optionally, second clay with water, and then spray drying to obtain the catalytic cracking aid.

18. The method for preparing a catalytic cracking aid according to claim 17, wherein the binder is or comprises a phosphorus-aluminum inorganic binder.

19. The phosphorus-aluminum inorganic binder is a phosphorus-aluminum adhesive and / or a first clay-containing phosphorus-aluminum inorganic binder; the first clay-containing phosphorus-aluminum inorganic binder, based on a dry basis, comprises 10 to 40 wt. % of an aluminum component, based on Al2O3, 45 to 90 wt. % of a phosphorus component, based on P2O5, and a first clay, based on a dry basis, of greater than 0 and not more than 40 wt. %, wherein the first clay-containing phosphorus-aluminum inorganic binder has a P / Al weight ratio of 1.0 to 6.0, a pH of 1 to 3.5, and a solids content of 15 to 60 wt. %; 20. The method for preparing a catalytic cracking aid according to claim 18, wherein the first clay comprises at least one of kaolin, sepiolite, attapulgite, rectorite, smectite, and diatomaceous earth.

20. The method for preparing a catalytic cracking aid according to any one of claims 17 to 19, wherein the second clay is at least one selected from kaolin, sepiolite, attapulgite, rectorite, smectite, metahalloysite, halloysite, hydrotalcite, bentonite, and diatomaceous earth.

21. 19. The method for preparing a catalytic cracking aid according to claim 18, wherein, based on the total weight of the catalytic cracking aid, the binder comprises 3 to 39 wt % of the phosphorus-aluminum inorganic binder on a dry weight basis and 1 to 30 wt % of other inorganic binders on a dry weight basis.

22. The method for preparing a catalytic cracking aid according to claim 21, wherein the other inorganic binder may further include at least one of pseudoboehmite, alumina sol, silica-alumina sol, and water glass.

23. the product obtained by the spray drying is first calcined, washed and optionally dried to obtain the catalytic cracking aid; The first firing has a firing temperature of 300 to 650°C and a firing time of 0.5 to 8 hours, The method for preparing a catalytic cracking aid according to any one of claims 17 to 22, wherein the drying is carried out at a drying temperature of 100 to 200°C for a drying time of 0.5 to 24 hours.

24. vigorously mixing and stirring an alumina source, the first clay and water to decompose them into a slurry with a solid content of 5 to 48% by weight; adding concentrated phosphoric acid to the slurry under stirring in a weight ratio of P / Al=1 to 6; and reacting the resulting mixed slurry at 50 to 99°C for 15 to 90 minutes to prepare the first clay-containing phosphorus-aluminum inorganic binder; the alumina source is aluminum hydroxide and / or alumina that can be peptized with an acid; the amount of the first clay used on a dry weight basis is greater than 0 parts by weight and less than or equal to 40 parts by weight for 10 to 40 parts by weight of the alumina source on an Al2O3 basis; 20. The method for preparing a catalytic cracking aid according to claim 19, wherein in the P / Al, P is the weight of phosphorus as a simple substance in the phosphoric acid, and Al is the weight of aluminum as a simple substance in the alumina source.

25. A method for preparing the catalytic cracking catalyst according to any one of claims 8 to 10, comprising vigorously mixing and stirring a Y-type molecular sieve, the phosphorus-modified MFI-structured molecular sieve according to any one of claims 1 to 5, an inorganic binder, and optionally a second clay with water, and then spray-drying to prepare the catalytic cracking catalyst.

26. 26. The method for preparing a catalytic cracking catalyst according to claim 25, wherein the inorganic binder is or comprises a phosphorus-aluminum inorganic binder.

27. The phosphorus-aluminum inorganic binder is a phosphorus-aluminum adhesive and / or a first clay-containing phosphorus-aluminum inorganic binder; the first clay-containing phosphorus-aluminum inorganic binder comprises, on a dry weight basis, 10 to 40 wt. % of an aluminum component based on Al2O3, 45 to 90 wt. % of a phosphorus component based on P2O5, and a first clay of greater than 0 and not more than 40 wt. % on a dry weight basis; and the first clay-containing phosphorus-aluminum inorganic binder has a P / Al weight ratio of 1.0 to 6.0, a pH of 1 to 3.5, and a solids content of 15 to 60 wt. %; 27. The method for preparing a catalytic cracking catalyst according to claim 26, wherein the first clay comprises at least one of kaolin, sepiolite, attapulgite, rectorite, smectite, and diatomaceous earth.

28. The method for preparing a catalytic cracking catalyst according to any one of claims 25 to 27, wherein the second clay is at least one selected from the group consisting of kaolin, sepiolite, attapulgite, rectorite, smectite, metahalloysite, halloysite, hydrotalcite, bentonite, and diatomaceous earth.

29. Based on the catalytic cracking catalyst, the inorganic binder comprises, on a dry basis, 3 to 39 wt. % of the phosphorus-aluminum inorganic binder and, on a dry basis, 1 to 30 wt. % of other inorganic binders; 27. The method for preparing a catalytic cracking catalyst according to claim 26, wherein the other inorganic binder is at least one selected from the group consisting of pseudoboehmite, alumina sol, silica-alumina sol, and water glass.

30. the product obtained by the spray drying is first calcined, washed and optionally dried to obtain the catalytic cracking catalyst; The first firing has a firing temperature of 300 to 650°C and a firing time of 0.5 to 8 hours, The method for preparing a catalytic cracking catalyst according to any one of claims 25 to 29, wherein the drying is carried out at a drying temperature of 100 to 200°C for a drying time of 0.5 to 24 hours.

31. The method further comprises vigorously mixing and stirring an alumina source, the first clay, and water to disperse them into a slurry having a solid content of 5 to 48% by weight, adding concentrated phosphoric acid to the slurry under stirring in a weight ratio of P / Al=1 to 6, and reacting the resulting mixed slurry at 50 to 99°C for 15 to 90 minutes to prepare the first clay-containing phosphorus-aluminum inorganic binder; the alumina source is aluminum hydroxide and / or alumina that can be peptized with an acid; the amount of the first clay used on a dry weight basis is greater than 0 parts by weight and less than or equal to 40 parts by weight for 10 to 40 parts by weight of the alumina source on an Al2O3 basis; 28. The method for preparing a catalytic cracking catalyst according to claim 27, wherein in the P / Al, P is the weight of phosphorus as a simple substance in the phosphoric acid, and Al is the weight of aluminum as a simple substance in the alumina source.

32. A method for catalytically cracking a hydrocarbon oil, comprising catalytically reacting a hydrocarbon oil with the catalytic cracking aid according to claim 6 or 7 or the catalytic cracking catalyst according to any one of claims 8 to 10 under catalytic cracking conditions.

33. The method for catalytically cracking hydrocarbon oil according to claim 32, comprising catalytically reacting the hydrocarbon oil with a catalytic cracking aid according to claim 6 or 7 and a catalytic cracking catalyst according to any one of claims 8 to 10 under the catalytic cracking conditions, wherein the content of the catalytic cracking aid in the catalytic mixture is 0.1 to 30% by weight.

34. The catalytic cracking method for hydrocarbon oil according to claim 32 or 33, wherein the catalytic cracking conditions include a reaction temperature of 500 to 800°C, and the hydrocarbon oil is one or more selected from crude oil, naphtha, gasoline, atmospheric residue, vacuum residue, atmospheric wax oil, vacuum wax oil, straight-run wax oil, propane light / heavy deoiled wax oil, coked wax oil, and coal liquefaction.