Packaged solid-state batteries

Abstract

The present invention provides a packaged solid-state battery which is provided with: a substrate; a solid-state battery with an end face electrode, the solid-state battery being provided on the substrate; and an outer package that covers the solid-state battery. The outer package contains a resin. A void part is present between the end face electrode and the outer package.

Description

[Technical Field]

[0001] This disclosure relates to packaged solid-state batteries. More specifically, this disclosure relates to solid-state batteries packaged for substrate mounting. [Background technology]

[0002] Rechargeable batteries, which can be repeatedly charged and discharged, have long been used in a variety of applications. For example, rechargeable batteries are used as power sources for electronic devices such as smartphones and laptop computers.

[0003] In secondary batteries, a liquid electrolyte is generally used as a medium for ion transfer that contributes to charging and discharging. In other words, so-called electrolyte solutions are used in secondary batteries. However, in such secondary batteries, safety is generally required in terms of preventing electrolyte leakage. Furthermore, since organic solvents used in electrolyte solutions are flammable substances, safety is required in that respect as well.

[0004] Therefore, research is underway on solid-state batteries that use solid electrolytes instead of liquid electrolytes. [Prior art documents] [Patent Documents]

[0005] [Patent Document 1] Special Publication No. 2010-503957 [Overview of the project] [Problems that the invention aims to solve]

[0006] Solid-state batteries may be mounted on a substrate such as a printed circuit board along with other electronic components. Solid-state batteries placed on a substrate may be covered with a covering member to prevent water vapor permeation (Patent Document 1). The covering member is provided so as to cover the end electrodes provided on the solid-state battery. In this case, the end electrodes are in physical contact with the solid-state battery and may deform as the solid-state battery expands and contracts during charging and discharging. On the other hand, in the region where the covering member covers the end electrodes, it is placed on the solid-state battery via the end electrodes. Therefore, the covering member is less able to follow the expansion and contraction of the solid-state battery compared to the end electrodes and may act to hinder the deformation of the end electrodes. As a result, distortion may occur inside the end electrodes, potentially causing them to break.

[0007] This invention has been made in view of the above problems. Specifically, the primary object of this disclosure is to provide a packaged solid-state battery in which the risk of damage to the end electrodes due to expansion and contraction of the solid-state battery is reduced. [Means for solving the problem]

[0008] To achieve the above objective, in one embodiment of this disclosure, The device comprises a substrate, a solid-state battery with end-face electrodes provided on the substrate, and an outer casing covering the solid-state battery. The exterior part includes resin, A packaged solid battery is provided, which includes a gap between the end electrode and the outer casing. [Effects of the Invention]

[0009] A packaged solid-state battery according to one embodiment of this disclosure can reduce the risk of damage to the end electrodes caused by the expansion and contraction of the solid-state battery. [Brief explanation of the drawing]

[0010] [Figure 1] Figure 1 is a schematic cross-sectional view showing the internal structure of a solid-state battery. [Figure 2]FIG. 2 is a cross-sectional view schematically showing the configuration of a packaged solid-state battery according to an embodiment of the present disclosure. [Figure 3] FIG. 3 is an enlarged cross-sectional view schematically showing part A of the packaged solid-state battery shown in FIG. 2. [Figure 4] FIG. 4 is an enlarged cross-sectional view schematically showing part A of a packaged solid-state battery according to another embodiment of the present disclosure. [Figure 5] FIG. 5 is a cross-sectional view schematically showing the configuration of a packaged solid-state battery according to an embodiment of the present disclosure. [Figure 6] FIG. 6 is an enlarged cross-sectional view schematically showing part B of the packaged solid-state battery shown in FIG. 5. [Figure 7A] FIG. 7A is a process cross-sectional view schematically showing the manufacturing process of a packaged solid-state battery according to an embodiment of the present disclosure. [Figure 7B] FIG. 7B is a process cross-sectional view schematically showing the manufacturing process of a packaged solid-state battery according to an embodiment of the present disclosure. [Figure 7C] FIG. 7C is a process cross-sectional view schematically showing the manufacturing process of a packaged solid-state battery according to an embodiment of the present disclosure. [Figure 7D] FIG. 7D is a process cross-sectional view schematically showing the manufacturing process of a packaged solid-state battery according to an embodiment of the present disclosure. [Figure 7E] FIG. 7E is a process cross-sectional view schematically showing the manufacturing process of a packaged solid-state battery according to an embodiment of the present disclosure.

MODE FOR CARRYING OUT THE INVENTION

[0011] Hereinafter, the packaged solid-state battery of the present disclosure will be described in detail. Although the description will be made with reference to the drawings as necessary, the illustrated contents are only schematically and exemplarily shown for the understanding of the present disclosure, and the appearance and dimensional ratios may be different from the actual ones.

[0012] In this specification, "packaged solid battery" broadly refers to a solid battery device configured to protect the solid battery from the external environment, and narrowly refers to a solid battery device that includes a mountable substrate and is protected from the external environment.

[0013] In this specification, "cross-sectional view" refers to the form of a solid-state battery's stacked structure as viewed from a direction approximately perpendicular to the stacking direction (simply put, the form when cut by a plane parallel to the thickness direction of the layers). Furthermore, in this specification, "plan view" or "plan view shape" refers to a sketch of the object as viewed from above or below along the thickness direction of the layers (i.e., the stacking direction mentioned above).

[0014] In this specification, “up and down” and “left and right” as used directly or indirectly correspond to the up and down and left and right directions in the figures, respectively. Unless otherwise specified, the same reference numeral or symbol indicates the same member, part, or has the same meaning. In a preferred embodiment, the vertical downward direction (i.e., the direction in which gravity acts) can be considered as “downward” / “bottom side,” and the opposite direction as “upward” / “top side.”

[0015] Furthermore, in this specification, "on top of" a component such as a substrate, solid battery, or layer includes not only cases where it is in contact with the upper surface of the component, but also cases where it is not in contact with the upper surface of the component. In other words, "on top of" a component such as a substrate, solid battery, or layer includes cases where a new component is formed above the component, and / or where another component is interposed between that component and the new component. Moreover, "on top of" does not necessarily mean the upper side in the vertical direction. "On top of" merely indicates the relative positional relationship between multiple components.

[0016] [Basic configuration of a secondary battery] As used herein, "rechargeable battery" refers to a battery that can be repeatedly charged and discharged. Therefore, the term "rechargeable battery" in this disclosure is not overly restrictive, and may also include, for example, energy storage devices.

[0017] In this disclosure, "solid-state battery" broadly refers to a battery whose constituent elements are solid, and narrowly refers to an all-solid-state battery whose constituent elements (particularly preferably all constituent elements) are solid. In one preferred embodiment, the solid-state battery in this disclosure is a stacked solid-state battery configured such that each layer constituting the battery constituent unit is stacked on top of each other, preferably such layers are made of a fired body. "Solid-state battery" includes not only so-called "secondary batteries" that can be repeatedly charged and discharged, but also "primary batteries" that can only be discharged. According to one preferred embodiment of this disclosure, the "solid-state battery" is a secondary battery. The term "secondary battery" is not overly restrictive and may also include, for example, energy storage devices. In this disclosure, a solid-state battery included in a package may also be referred to as a "solid-state battery element."

[0018] The following describes the basic configuration of the solid-state battery of this disclosure. The configuration of the solid-state battery described herein is merely an example for understanding the invention and does not limit the invention.

[0019] [Basic Configuration of Solid-State Batteries] A solid-state battery comprises at least positive and negative electrode layers and a solid electrolyte. Specifically, as shown in Figure 1, the solid-state battery 100 includes a solid-state battery stack comprising a battery component unit consisting of a positive electrode layer 110, a negative electrode layer 120, and a solid electrolyte 130 interposed between them.

[0020] In a solid-state battery, each of its constituent layers may be formed by firing, and the positive electrode layer, negative electrode layer, and solid electrolyte may form fired layers. Preferably, the positive electrode layer, negative electrode layer, and solid electrolyte are each fired integrally with each other, and therefore the solid-state battery laminate is a single fired body.

[0021] The positive electrode layer is an electrode layer containing at least a positive electrode active material. The positive electrode layer may further contain a solid electrolyte. In one preferred embodiment, the positive electrode layer is composed of a sintered body containing at least positive electrode active material particles and solid electrolyte particles. On the other hand, the negative electrode layer is an electrode layer containing at least a negative electrode active material. The negative electrode layer may further contain a solid electrolyte. In one preferred embodiment, the negative electrode layer is composed of a sintered body containing at least negative electrode active material particles and solid electrolyte particles.

[0022] The positive electrode active material and the negative electrode active material are materials that are involved in electron transfer in a solid-state battery. Charging and discharging occur when ions move (conduce) between the positive electrode layer and the negative electrode layer via a solid electrolyte, resulting in electron transfer. Preferably, each electrode layer of the positive and negative electrode layers is a layer capable of intercalating and deintercalating lithium ions or sodium ions. In other words, the solid-state battery is preferably an all-solid-state secondary battery in which lithium ions or sodium ions move between the positive and negative electrode layers via a solid electrolyte to perform charging and discharging.

[0023] (Cathode active material) Examples of positive electrode active materials included in the positive electrode layer include at least one selected from the group consisting of lithium-containing phosphate compounds having a NASICON-type structure, lithium-containing phosphate compounds having an olivine-type structure, lithium-containing layered oxides, and lithium-containing oxides having a spinel-type structure. An example of a lithium-containing phosphate compound having a NASICON-type structure is Li3V2(PO4)3. An example of a lithium-containing phosphate compound having an olivine-type structure is Li3Fe2(PO4)3, LiFePO4, and / or LiMnPO4. An example of a lithium-containing layered oxide is LiCoO2, and / or LiCo 1 / 3 Ni 1 / 3 Mn 1 / 3 Examples include O2. Examples of lithium-containing oxides having a spinel-type structure include LiMn2O4 and / or LiNi 0.5 Mn 1.5Examples include O4. The type of lithium compound is not particularly limited, but may be, for example, lithium transition metal composite oxides and lithium transition metal phosphate compounds. Lithium transition metal composite oxides are a general term for oxides that contain lithium and one or more transition metal elements as constituent elements, and lithium transition metal phosphate compounds are a general term for phosphate compounds that contain lithium and one or more transition metal elements as constituent elements. The type of transition metal element is not particularly limited, but may be, for example, cobalt (Co), nickel (Ni), manganese (Mn), and iron (Fe).

[0024] Furthermore, as a positive electrode active material capable of intercalating and deintercalating sodium ions, at least one selected from the group consisting of sodium-containing phosphate compounds having a nasicone-type structure, sodium-containing phosphate compounds having an olivine-type structure, sodium-containing layered oxides, and sodium-containing oxides having a spinel-type structure, etc. For example, in the case of sodium-containing phosphate compounds, at least one selected from the group consisting of Na3V2(PO4)3, NaCoFe2(PO4)3, Na2Ni2Fe(PO4)3, Na3Fe2(PO4)3, Na2FeP2O7, Na4Fe3(PO4)2(P2O7), and NaFeO2 as a sodium-containing layered oxide, is mentioned.

[0025] In addition, the positive electrode active material may be, for example, an oxide, disulfide, chalcogenide, or conductive polymer. Oxides may be, for example, titanium oxide, vanadium oxide, or manganese dioxide. Disulfides may be, for example, titanium disulfide or molybdenum sulfide. Chalcogenides may be, for example, niobium selenide. Conductive polymers may be, for example, disulfide, polypyrrole, polyaniline, polythiophene, polyparastyrene, polyacetylene, or polyacene.

[0026] (Negative electrode active material) Examples of negative electrode active materials included in the negative electrode layer include at least one selected from the group consisting of oxides containing at least one element selected from the group consisting of titanium (Ti), silicon (Si), tin (Sn), chromium (Cr), iron (Fe), niobium (Nb), and molybdenum (Mo), carbon materials such as graphite, graphite-lithium compounds, lithium alloys, lithium-containing phosphate compounds having a NASCICON-type structure, lithium-containing phosphate compounds having an olivine-type structure, and lithium-containing oxides having a spinel-type structure. An example of a lithium alloy is Li-Al. An example of a lithium-containing phosphate compound having a NASCICON-type structure is Li3V2(PO4)3 and / or LiTi2(PO4)3. An example of a lithium-containing phosphate compound having an olivine-type structure is Li3Fe2(PO4)3 and / or LiCuPO4. An example of a lithium-containing oxide having a spinel-type structure is Li4Ti5O 12 These are some examples.

[0027] Furthermore, examples of negative electrode active materials capable of intercalating and deintercalating sodium ions include at least one selected from the group consisting of sodium-containing phosphate compounds having a nasicone-type structure, sodium-containing phosphate compounds having an olivine-type structure, and sodium-containing oxides having a spinel-type structure.

[0028] In addition, in a solid-state battery, the positive electrode layer and the negative electrode layer may be made of the same material.

[0029] The positive electrode layer and / or negative electrode layer may contain a conductive material. Examples of conductive materials included in the positive electrode layer and negative electrode layer include at least one of metallic materials such as silver, palladium, gold, platinum, aluminum, copper, and nickel, as well as carbon.

[0030] Furthermore, the positive electrode layer and / or negative electrode layer may contain a sintering aid. Examples of sintering aids include at least one selected from the group consisting of lithium oxide, sodium oxide, potassium oxide, boron oxide, silicon oxide, bismuth oxide, and phosphorus oxide.

[0031] The thicknesses of the positive electrode layer and the negative electrode layer are not particularly limited, but for example, they may be 2 μm or more and 50 μm or less, and especially 5 μm or more and 30 μm or less, respectively.

[0032] (Positive electrode current collecting layer / Negative electrode current collecting layer) Although not essential elements of the electrode layer, the positive electrode layer and the negative electrode layer may each comprise a positive electrode current collector layer and a negative electrode current collector layer. The positive electrode current collector layer and the negative electrode current collector layer may each be in the form of foil. However, if greater emphasis is placed on aspects such as improved electronic conductivity through integral firing, reduction of manufacturing costs for solid-state batteries, and / or reduction of internal resistance of solid-state batteries, the positive electrode current collector layer and the negative electrode current collector layer may each be in the form of a fired body. It is preferable to use materials with high conductivity as the positive electrode current collector that constitutes the positive electrode current collector layer and the negative electrode current collector that constitutes the negative electrode current collector, for example, silver, palladium, gold, platinum, aluminum, copper, and / or nickel may be used. The positive electrode current collector and the negative electrode current collector may each have an electrical connection part for electrical connection to the outside and may be configured to be electrically connectable to an end electrode. When the positive electrode current collector layer and the negative electrode current collector layer are in the form of a fired body, they may be composed of a fired body containing a conductive material and a sintering aid. The conductive material included in the positive electrode current collector layer and the negative electrode current collector layer may be selected from materials similar to those that may be included in the positive electrode layer and the negative electrode layer. The sintering aid included in the positive electrode current collector layer and the negative electrode current collector layer may be selected from materials similar to those that may be included in the positive electrode layer and the negative electrode layer. As described above, the positive electrode current collector layer and the negative electrode current collector layer are not essential in a solid-state battery, and solid-state batteries without such positive electrode current collector layers and negative electrode current collector layers are also conceivable. In other words, the solid-state battery included in the package of this disclosure may be a solid-state battery without current collector layers.

[0033] (Solid electrolyte) The solid electrolyte is a material through which lithium ions or sodium ions can conduct. In particular, the solid electrolyte forming a battery constituent unit in a solid battery may form a layer through which lithium ions can conduct between the positive electrode layer 110 and the negative electrode layer 120 (see Fig. 1). Note that the solid electrolyte only needs to be provided at least between the positive electrode layer and the negative electrode layer. That is, the solid electrolyte may exist around the positive electrode layer and / or the negative electrode layer so as to protrude from between the positive electrode layer and the negative electrode layer. Specific examples of the solid electrolyte include, for example, any one or two or more of crystalline solid electrolytes, glass-based solid electrolytes, glass-ceramics-based solid electrolytes, etc.

[0034] The crystalline solid electrolyte is, for example, an oxide-based crystalline material and a sulfide-based crystalline material. Examples of the oxide-based crystalline material include, for example, a lithium-containing phosphate compound having a NASICON structure, an oxide having a perovskite structure, an oxide having a garnet type or a garnet type similar structure, an oxide glass-ceramics-based lithium ion conductor, etc.

[0035] Examples of the lithium-containing phosphate compound having a NASICON structure include Li x M y (PO4)3 (1 ≤ x ≤ 2, 1 ≤ y ≤ 2, M is at least one selected from the group consisting of titanium (Ti), germanium (Ge), aluminum (Al), gallium (Ga), and zirconium (Zr)). An example of the lithium-containing phosphate compound having a NASICON structure is, for example, Li 1.2 Al 0.2 Ti 1.8 (PO4)3, etc. Examples of the oxide having a perovskite structure include La 0.55 Li 0.35 TiO3, etc. Examples of the oxide having a garnet type or a garnet type similar structure include Li7La3Zr2O 12 , etc. Examples of the sulfide-based crystalline material include thio-LISICON, for example, Li 3.25 Ge 0.25 P 0.75S4 and Li 10 GeP2S 12 These are some examples. The crystalline solid electrolyte may also contain polymer materials (for example, polyethylene oxide (PEO)).

[0036] Examples of glass-based solid electrolytes include oxide-based glass materials and sulfide-based glass materials. Examples of oxide-based glass materials include 50Li4SiO4·50Li3BO3. Examples of sulfide-based glass materials include 30Li2S·26B2S3·44LiI, 63Li2S·36SiS2·1Li3PO4, 57Li2S·38SiS2·5Li4SiO4, 70Li2S·30P2S5, and 50Li2S·50GeS2.

[0037] Glass-ceramic solid electrolytes include, for example, oxide-based glass-ceramic materials and sulfide-based glass-ceramic materials. Examples of oxide-based glass-ceramic materials include phosphate compounds containing lithium, aluminum, and titanium (LATP) and phosphate compounds containing lithium, aluminum, and germanium (LAGP). For example, LATP is composed of Li 1.07 Al 0.69 Ti 1.46 Examples include (PO4)3. Also, LAGP is, for example, Li 1.5 Al 0.5 Ge 1.5 Examples include (PO4). Also, as sulfide-based glass ceramic materials, for example, Li7P3S 11 and Li 3.25 P 0.95 Examples include S4.

[0038] Furthermore, examples of solid electrolytes capable of conducting sodium ions include sodium-containing phosphate compounds having a nasicone structure, oxides having a perovskite structure, and oxides having a garnet-type or garnet-type similar structure. Examples of sodium-containing phosphate compounds having a nasicone structure include Na x M y(PO4)3 (where 1≦x≦2, 1≦y≦2, and M is at least one selected from the group consisting of Ti, Ge, Al, Ga, and Zr) is an example.

[0039] The solid electrolyte may contain a sintering aid. The sintering aid included in the solid electrolyte may be selected from materials similar to those that may be included in the positive electrode layer and the negative electrode layer.

[0040] The thickness of the solid electrolyte is not particularly limited. The thickness of the solid electrolyte layer located between the positive electrode layer and the negative electrode layer may be, for example, 1 μm to 15 μm, and more particularly 1 μm to 5 μm.

[0041] (end face electrode) A solid-state battery 100 is generally provided with end electrodes 140. In particular, the end electrodes 140 are provided on the side surface 100C of the solid-state battery 100. More specifically, a positive electrode end electrode 140A connected to the positive electrode layer 110 and a negative electrode end electrode 140B connected to the negative electrode layer 120 are provided (see Figure 1). Such end electrodes preferably contain a material with high conductivity. The specific material of the end electrodes is not particularly limited, but at least one selected from the group consisting of silver, gold, platinum, aluminum, copper, tin, and nickel can be mentioned.

[0042] [Basic configuration of a packaged solid-state battery] This disclosure relates to a packaged solid-state battery; that is, a packaged solid-state battery having a mountable substrate and a configuration that protects the solid-state battery from the external environment.

[0043] Figure 2 is a schematic cross-sectional view showing the configuration of a packaged solid-state battery according to one embodiment of the present disclosure. As shown, the packaged solid-state battery 1000 according to one embodiment of the present disclosure comprises a substrate 200 on which a solid-state battery 100 is supported. Specifically, the packaged solid-state battery 1000 includes a mountable substrate 200 and a solid-state battery 100 provided on the substrate 200 and protected from the external environment.

[0044] As shown in Figure 2, the substrate 200 has a larger main surface area than, for example, a solid-state battery. The substrate 200 may be a resin substrate or a ceramic substrate. In short, the substrate 200 may fall into the category of printed circuit boards, flexible substrates, LTCC substrates, or HTCC substrates. If the substrate 200 is a resin substrate, the substrate 200 may be a substrate configured to include resin as a base material, for example, a substrate with a resin layer included in its laminated structure. The resin material of such a resin layer may be any thermoplastic resin and / or any thermosetting resin. The resin layer may also be, for example, constructed by impregnating a glass fiber cloth with a resin material such as epoxy resin.

[0045] The substrate preferably serves as a component for the external terminals of the packaged solid-state battery. In other words, the substrate can be said to be a terminal substrate for the external terminals of the solid-state battery. A packaged solid-state battery with such a substrate can be mounted on another secondary substrate, such as a printed circuit board, with the substrate interposed between the solid-state battery and the substrate. For example, the solid-state battery can be surface-mounted via the substrate through solder reflow. For this reason, the packaged solid-state battery of this disclosure preferably has an SMD (Surface Mount Device) type battery package.

[0046] Such a substrate can be provided to support a solid battery and can therefore be understood as a support substrate. Furthermore, since the substrate is a terminal substrate, it is preferable that it has wiring or an electrode layer, and in particular, it is preferable that it has an electrode layer that electrically connects the upper and lower surfaces or upper and lower surface layers. In one preferred embodiment, the substrate has wiring or an electrode layer that electrically connects the upper and lower surfaces of the substrate and serves as a terminal substrate for the external terminals of a packaged solid battery. In this embodiment, the wiring of the substrate can be used to extract the solid battery to the external terminals, so there is no need to extract it to the outside of the outer casing while packing it in the outer casing described later, and the design flexibility of the external terminal is increased.

[0047] A substrate 200 according to a preferred embodiment includes electrode layers (upper main surface electrode layer 210, lower main surface electrode layer 220) that electrically connect the upper and lower main surfaces of the substrate, and serves as a component for the external terminals of a packaged solid-state battery (see Figure 2). In a packaged solid-state battery equipped with such a substrate, the electrode layers of the substrate and the terminal portion of the solid-state battery are connected to each other. Preferably, the electrode layers of the substrate and the end electrodes of the solid-state battery are electrically connected to each other. For example, the positive electrode end electrode 140A of the solid-state battery is electrically connected to the positive electrode layer (210A, 220A) of the substrate. On the other hand, the negative electrode end electrode 140B of the solid-state battery is electrically connected to the negative electrode layer (210B, 220B) of the substrate. As a result, the positive and negative electrode layers of the substrate (particularly the electrode layers located on the lower / bottom side of the package, or the lands connected thereto) are provided as the positive and negative electrode terminals of the packaged solid-state battery, respectively.

[0048] As shown in Figure 2, in order to enable electrical connection between the solid battery 100 and the substrate electrode layer 210 of the substrate 200, the end electrode 140 of the solid battery 100 and the substrate electrode layer 210 of the substrate 200 can be connected via a bonding member 600. This bonding member 600 is responsible for at least the electrical connection between the end electrode 140 of the solid battery 100 and the substrate 200, and may include, for example, a conductive adhesive. As an example, the bonding member 600 may be composed of an epoxy-based conductive adhesive containing a metal filler such as Ag.

[0049] Furthermore, in one embodiment of this disclosure, not only the substrate 200 but also the packaged solid battery 1000 itself may be configured to prevent the permeation of water vapor as a whole. For example, in one embodiment of this disclosure, the solid battery package 1000 may be covered by an outer casing 150 so as to completely surround the solid battery 100 provided on the substrate 200. In other words, the term "outer casing" in this specification refers to a covering member that surrounds the solid battery 100 on the substrate 200, and the "outer casing" may also be referred to as "covering" or "packaging". Specifically, the solid battery 100 on the substrate 200 may be packaged such that its main surface 100A and side surface 100C are surrounded by the outer casing 150. With such a configuration, since all surfaces of the solid battery 100 are not exposed to the outside, it is possible to suitably prevent the permeation of water vapor (i.e., the intrusion of water vapor into the solid battery).

[0050] In this specification, "water vapor" is not limited to water in a gaseous state, but also includes water in a liquid state. In other words, the term "water vapor" is used to broadly encompass water in a gaseous state, liquid state, etc., regardless of its physical state. Therefore, "water vapor" can also be called moisture, and liquid water in particular may include condensed water that forms when water in a gaseous state condenses. Since the intrusion of water vapor into solid batteries is a factor in the deterioration of battery characteristics, the packaged form of solid batteries described above contributes to extending the lifespan of the battery characteristics of solid batteries.

[0051] For example, as shown in Figure 2, the outer casing 150 may consist of a coating insulating layer 160 and a coating inorganic layer 170. The solid-state battery 100 may have an outer casing 150 covered with a coating insulating layer 160 and a coating inorganic layer 170. The coating inorganic layer 170 is provided so as to cover the coating insulating layer 160. Since the coating inorganic layer 170 is positioned on the coating insulating layer 160, together with the coating insulating layer 160, it has a form that largely encloses the solid-state battery 100 on the substrate 200 as a whole. Furthermore, the coating inorganic layer 170 can also take a form that covers the side surface 250 of the substrate 200. The coating insulating layer 160, in combination with the coating inorganic layer 170, forms a suitable water vapor barrier, and the coating inorganic layer 170 is also formed to form a suitable water vapor barrier in combination with the coating insulating layer 160. Note that the coating insulating layer 160 may extend onto the side surface 250 of the substrate. In other words, the insulating coating layer 160 covering the top surface region 100B and the side surface region 100C of the solid battery may also cover the side surface 250 of the substrate, and an inorganic coating layer 170 may be provided on such insulating coating layer 160.

[0052] The insulating coating layer may be made of any material that exhibits insulating properties. For example, the insulating coating layer may contain a resin, which may be either a thermosetting resin or a thermoplastic resin. The insulating coating layer may also contain an inorganic filler. As merely one example, the insulating coating layer may be made of an epoxy resin containing an inorganic filler such as SiC.

[0053] The material of the coating inorganic layer is not particularly limited and may be metal, glass, oxide ceramics, or mixtures thereof. The coating inorganic layer may correspond to an inorganic layer having a thin film form, for example, a metal film. For example, the coating inorganic layer may be a plating film containing at least one selected from the group consisting of Cu (copper), Sn (tin), Zn (zinc), Bi (bismuth), Au (gold), Ag (silver), Ni (nickel), Cr (chromium), Pd (palladium), and Pt (platinum) as its main component. In one preferred embodiment, the coating inorganic layer is composed of a plated Cu-based and / or Ni-based material with a thickness of 2 μm to 50 μm.

[0054] [Features of the packaged solid-state battery of this disclosure] The inventors of the present invention have diligently studied solutions to reduce the risk of damage to the end electrodes 140 caused by the expansion and contraction of the solid battery 100 during charging and discharging in the above-mentioned packaged solid battery 1000, and as a result have come up with the present invention having the following technical concept.

[0055] This disclosure has the technical concept of "a structure that includes a gap between the end electrode and the outer casing." More specifically, this disclosure has the technical concept of "a structure that includes an air gap between the end electrode and the outer casing, and the end electrode and the outer casing are separated by this air gap."

[0056] To realize the above technical concept, this disclosure has the following technical features. As shown in Figure 2, the solid battery 100 arranged on the substrate 200 includes an end electrode 140 provided on the side surface 100C of the solid battery 100. The outer casing 150 is provided so as to surround the solid battery 100 on the substrate 200, including the end electrode 140. Figure 3 is a schematic enlarged cross-sectional view showing portion A, which is part of the boundary region between the end electrode 140 and the outer casing 150, in the packaged solid battery 1000 shown in Figure 2. As shown in Figures 2 and 3, a gap 180 is included between the end electrode 140 and the outer casing 150. In other words, the end electrode 140 and the outer casing 150 may face each other with a gap 180 between them. In other words, the outer casing 150 may be provided so as to cover the solid battery 100 with a gap formed between it and the end electrode 140 via the gap 180.

[0057] In such a configuration, the end electrode 140 and the outer casing 150 may be separated by a gap 180. In other words, the packaged solid battery of this disclosure includes a portion where the solid battery 100 and the outer casing 150 are separated and facing each other, and a portion where the solid battery 100 and the outer casing 150 are in contact. In such a configuration, the separated and facing portions may be located between the end electrode 140 and the outer casing 150. In short, the packaged solid battery of this disclosure includes a portion where the end electrode 140 and the outer casing 150 are separated and facing each other. This means that the outer casing 150 may be provided to cover the solid battery with the end electrode, at least partially separated from the end electrode 140.

[0058] The solid-state battery 100, which is covered by the outer casing 150, has a first main surface 100A facing the substrate 200 and a second main surface 100B located opposite the first main surface 100A. That is, assuming a typical solid-state battery with two opposing main surfaces, the second main surface 100B located opposite the substrate 200 is the main surface on the mounting side in the SMD type and can also be called the "bottom surface" or "underside." The second main surface 100B also refers to the main surface located on the opposite side of the first main surface 100A and can also be called the "top surface," "overhead surface," or "upper surface."

[0059] Furthermore, "side surface of the solid battery" refers to the surface connecting the first main surface 100A and the second main surface 100B. In one embodiment of this disclosure, the end electrode 140 may be provided on each of two opposing side surfaces 100C of the solid battery 100. Specifically, as shown in Figure 1, the positive electrode side end electrode 140A connected to the positive electrode layer 110 and the negative electrode side end electrode 140B connected to the negative electrode layer 120 may be arranged on two opposing side surfaces 100C. In this disclosure, the void 180 may be provided on at least one of the positive electrode side end electrode 140A and the negative electrode side end electrode 140B. In other words, the outer casing 150 may cover the solid battery in a manner that includes a portion that is spaced apart from and opposite to at least one of the positive electrode side end electrode 140A and the negative electrode side end electrode 140B.

[0060] Furthermore, as described above, the outer casing 150 may include a covering insulating layer 160. In one preferred embodiment, the covering insulating layer 160 is provided so as to cover the solid battery 100, and a covering inorganic layer 170 is provided on the covering insulating layer 160. In this embodiment, the end electrode 140 may have a gap 180 between it and the covering insulating layer 160. In other words, the end electrode 140 and the covering insulating layer 160 may be separated from each other and facing each other with the gap 180 in between.

[0061] A force can act on the end electrode 140 that pulls it in the direction of expansion and contraction of the solid-state battery 100. When the solid-state battery 100 expands and contracts in the direction of the electrode layer stacking, this expansion and contraction direction is the same as the direction of extension of the end electrode 140 (see Figure 1). That is, the expansion and contraction direction can also be understood as being the same as the direction of extension of the side surface 100C of the solid-state battery. On the side surface 100C of the solid-state battery, the end electrode 140 is in contact with the solid-state battery 100. On the other hand, the outer casing 150 is positioned on the solid-state battery 100 via the end electrode 140 in the region covering the end electrode 140. Compared to the end electrode 140 which is in physical contact with the solid-state battery 100, the force acting on the end electrode 140 in the direction of extension due to the expansion and contraction of the solid-state battery is less likely to propagate to the outer casing 150. Therefore, the outer casing 150 may be inferior in its ability to follow the expansion and contraction of the solid-state battery 100.

[0062] Thus, the outer casing 150 may be less able to follow the expansion and contraction of the solid-state battery 100 compared to the end electrode 140. Therefore, when the end electrode 140 and the outer casing 150 are joined to each other, the outer casing 150 can restrain the end electrode 140 at the joining surface with the end electrode 140 (i.e., the outer surface 145 of the end electrode), thereby suppressing the deformation of the end electrode 140 that follows the expansion and contraction of the solid-state battery 100. As a result, when the solid-state battery 100 expands and contracts, the outer surface 145 of the end electrode 140 is less likely to deform due to the restraint by the outer casing 150, while the inner surface of the end electrode 140 that is physically joined to the solid-state battery 100 is more likely to deform in accordance with the expansion and contraction. As a result, the ease of deformation differs between the inner surface of the end electrode 140 and the outer surface 145 of the end electrode that is joined to the outer casing 150. This can cause distortion inside the end electrode 140, potentially leading to damage to the end electrode 140.

[0063] According to the configuration of this disclosure, the outer surface 145 of the end electrode located on the exterior part 150 side has a portion separated from the exterior part 150 by a gap 180, so that in this separated portion, the outer surface of the end electrode is not constrained by the exterior part 150. In other words, by providing a gap 180 between the end electrode 140 and the exterior part 150, the restraint of the outside of the end electrode 140 by the exterior part 150 can be relaxed as a whole. Therefore, when the end electrode 140 deforms due to volume changes such as expansion and contraction of the solid battery 100, the influence of restraint by the exterior part 150 can be reduced. As a result, strain inside the end electrode 140 caused by the expansion and contraction of the solid battery 100 can be suppressed, and the risk of damage to the end electrode 140 can be reduced. Furthermore, by reducing such strain, fatigue of the end electrode 140 caused by repeated expansion and contraction of the solid battery 100 can also be reduced. As a result, deterioration and peeling of the end electrode 140 can be suppressed, and the long-term reliability of the packaged solid battery can be improved.

[0064] Furthermore, as shown in Figure 2, the outer casing 150 is in physical contact with the second main surface 100B of the solid-state battery. Therefore, when the solid-state battery 100 expands and contracts in the direction of electrode layer stacking, the outer casing 150 located on the second main surface 100B of the solid-state battery can suitably deform along the expansion and contraction direction of the solid-state battery 100. In addition, the outer casing 150 is also bonded to the substrate 200 on which the solid-state battery 100 is placed. Such bonding can play a role in helping to suitably hold the outer casing 150 on the solid-state battery 100. Therefore, even in the embodiment in which a gap 180 is formed between the end electrode 140 and the outer casing 150 as described above, the outer casing 150 can be suitably held on the solid-state battery 100 without being easily damaged and / or peeled off by deformation accompanying the expansion and contraction of the solid-state battery.

[0065] The end electrode 140 and the outer casing 150 do not necessarily have to be completely separated. In other words, the end electrode 140 may be in partial contact with the outer casing 150. In one embodiment, the end electrode 140 includes a non-contact portion 145A and a contact portion 145B with respect to the outer casing 150 (see Figure 4). With this configuration, the contact portion 145B can contribute to supporting the outer casing 150 on the end electrode 140. For example, even when stress is applied near the gap 180, the stress is suitably distributed to the end electrode 140 and / or the outer casing 150 by the contact portion 145B, and damage to the end electrode 140 and the outer casing 150 can be prevented. The support of the outer casing 150 by the contact portion 145B on the end electrode 140 can improve the overall strength of the outer casing 150. Furthermore, at the contact portion 145B, the end electrode 140 can be held on the solid battery 100 by the outer casing 150. The contact portion 145B between the end electrode 140 and the outer casing 150 can suitably hold the end electrode 140 on the solid battery and help prevent the end electrode 140 from peeling off the solid battery.

[0066] For example, the contact portion between the end electrode 140 and the casing 150 may be at least the end 141 of the end electrode 140. Specifically, the end electrode 140 may be in contact with the casing 150 at at least one of the substrate-side end 141a located on the first main surface 100A side of the solid battery, and the top-side end 141b located on the second main surface 100B side. The "top-side end" and the "bottom-side end" correspond to the end 141 located distal to the substrate 200 and the end 141 located proximal to the substrate 200, respectively, on the end electrode 140. In other words, the contact portion between the end electrode 140 and the casing 150 may be located at the end 141 of the end electrode located on the second main surface 100B side and / or the substrate 200 side of the solid battery.

[0067] As described above, the outer casing 150 has a contact portion with the end portion 141 of the end electrode, so that the joint between the end portion 141 of the end electrode and the solid battery 100 is covered by the outer casing 150. With this structure, the end portion 141 of the end electrode can be suitably held by the solid battery by the outer casing 150. Therefore, it is possible to suitably prevent the end electrode from separating from the solid battery due to the expansion and contraction of the solid battery 100. Furthermore, by covering the joint between the end portion 141 of the end electrode and the solid battery 100 with the outer casing 150, the intrusion of water vapor into the solid battery 100 from the connection point between the end electrode 140 and the solid battery 100 can be suitably suppressed. In other words, according to this disclosure, a packaged solid battery can be provided that achieves both a reduction in the risk of damage to the end electrode due to expansion and contraction and prevention of water vapor intrusion into the solid battery.

[0068] Figure 5 is a schematic cross-sectional view showing a packaged solid-state battery according to another embodiment. In one embodiment, the end electrode 140 may extend to at least one of the first main surface 100A and the second main surface 100B of the solid-state battery. That is, the end portion 141 of the end electrode may extend to at least one of the first main surface 100A and the second main surface 100B of the solid-state battery. With this structure, by extending the end electrode to the first main surface 100A, the contact area between the end electrode 140 and the bonding member 600 can be increased. Therefore, the above-described structure can contribute to improving the connection reliability between the end electrode 140 and the bonding member 600.

[0069] The outer casing 150 may be in contact with the end electrode 140 at the end 141 of the end electrode positioned on the first main surface 100A and / or the second main surface 100B. In other words, the contact portion between the outer casing 150 and the end electrode 140 may be located at the end 141 of the end electrode extending on the first main surface 100A and / or the second main surface 100B.

[0070] With this structure, the end electrode 140 can extend along the side surface 100C of the solid-state battery, and along the first main surface 100A and / or the second main surface 100B. That is, the contact area between the end electrode 140 and the solid-state battery 100 becomes larger, which can effectively prevent the end electrode from peeling off due to volume changes of the solid-state battery. Furthermore, by joining the outer casing 150 and the end electrode 140 at the end 141 of the end electrode extending on the first main surface 100A and / or the second main surface 100B, the end electrode 140 can be effectively clamped on the solid-state battery 100 by the outer casing 150. This can more effectively prevent the end electrode from peeling off the solid-state battery due to expansion and contraction of the solid-state battery.

[0071] Figure 4 is a schematic enlarged cross-sectional view showing the boundary region between the end electrode 140 and the outer casing 150 in another embodiment of the present disclosure. As shown, the packaged solid battery may include a plurality of voids 180. The plurality of voids 180 may be formed intermittently along the end electrode 140. That is, the plurality of voids 180 may be formed intermittently by providing a plurality of contact portions 145B and non-contact portions 145A in the end electrode 140.

[0072] In this specification, "intermittently formed voids" do not necessarily mean that multiple voids 180 are formed independently of each other. For example, in a cross-sectional view, multiple voids 180 may be in a state where adjacent voids 180 are partially connected to each other. This means that the inner surface 155 of the outer casing facing the end electrode 140 may be a surface that includes irregularities in a cross-sectional view. For example, the contact portion 145B and non-contact portion 145A between the end electrode 140 and the outer casing 150 may be provided alternately and repeatedly. In such a structure, the multiple voids 180 may be provided irregularly along the end electrode, or they may be provided substantially regularly.

[0073] Thus, when a packaged solid-state battery intermittently includes multiple voids 180, providing multiple non-contact portions 145A on the end electrode 140 where the end electrode 140 is not constrained by the outer casing 150 prevents the unconstrained and constrained portions of the end electrode from becoming localized. As a result, the strain generated in the end electrode due to the expansion and contraction of the solid-state battery is more effectively mitigated overall, and the risk of damage to the end electrode can be suitably reduced. Furthermore, by providing contact portions 145B at multiple locations while ensuring non-contact portions 145A, the non-contact portions 145A can suppress the generation of strain in the end electrode 145, and the contact portions 145B can suitably hold the end electrode 145 in the solid-state battery 100.

[0074] In one preferred embodiment, in cross-sectional view, the void portion 180 has an elongated shape that extends along the end face electrode 140. In other words, the cross-sectional shape of the void portion 180 may be an elongated or flattened shape along the extending direction of the end face electrode 140. Furthermore, in embodiments having multiple void portions 180, the cross-sectional shapes of the void portions 180 do not necessarily have to be the same and may have different cross-sectional shapes. For example, the cross-sectional shapes of the multiple void portions 180 may be elongated shapes of different dimensions.

[0075] The void portion 180, which has an elongated cross-sectional shape, may extend along the main surface region 143 of the end electrode. In one preferred embodiment, the void portion 180 has an elongated cross-sectional shape that extends along the outer surface 145 of the main surface region 143 of the end electrode. In this specification, "main surface region of the end electrode" means the region of the end electrode 140 located on the side surface 100C of the solid battery. In other words, the void portion 180 may be located on the end electrode 140 located on the side surface 100C of the solid battery. With such a structure, the end electrode 140 is separated from the outer casing portion 150 over a wider area, and the constraint on the end electrode 140 by the outer casing portion 150 can be more effectively relieved. As a result, the end electrode can more preferably follow the volume change of the solid battery, and the strain that may occur within the end electrode can be suppressed, thereby reducing the risk of damage to the end electrode.

[0076] Furthermore, the cross-sectional shape of the void 180 may correspond to the cross-sectional shape of the outer surface 145 of the end electrode. Specifically, in cross-sectional view, the void 180 may have a shape corresponding to the cross-sectional shape of the outer contour forming surface of the end electrode 140. For example, as shown in Figure 6, if the outer surface 145 of the end electrode has a curved cross-sectional shape, the void 180 may have a long, curved cross-sectional shape that follows the curved portion. With such a structure, in cross-sectional view, the void 180 can extend along the outer surface 145 of the end electrode with a certain width. In other words, the end electrode 140 and the outer casing 150 may include portions that face each other with a certain distance between them. As a result, the restraining force on the end electrode 140 by the outer casing 150 is more effectively reduced. Therefore, even if deformation occurs in the end electrode 140 due to the expansion and contraction of the solid battery 100, excessive strain will not occur inside the end electrode 140, and the risk of damage to the end electrode 140 can be reduced.

[0077] In one embodiment, the void 180 may be continuous over the entire main surface region 143 of the end electrode. In other words, the end electrode 140 may be spaced apart from and facing the outer casing 150 over the entire main surface region 143. In such an embodiment, the void 180 may have an elongated cross-sectional shape extending over the main surface region 143 of the end electrode, as shown in Figures 2 and 5. Although not shown, such a void 180 may communicate not only in the planar direction but also in the cross-sectional direction. That is, the void 180 may be continuous two-dimensionally over the main surface region 143 of the end electrode. With such a structure, the constraint on the end electrode by the outer casing is more effectively relieved, and the end electrode can more suitably follow the volume change of the solid battery. Therefore, this disclosure can provide a more suitable packaged solid battery in which the strain that may occur in the end electrode is reduced and the risk of damage to the end electrode due to volume change of the solid battery is reduced.

[0078] In cross-sectional view, the width W of the void portion 180 may be 1 μm to 50 μm, 1 μm to 30 μm, or 1 μm to 25 μm, for example, 2 μm to 10 μm (see Figure 3). Here, the width W of the void portion can also be understood as the distance at which the end electrode 140 and the outer casing portion 150 are separated and facing each other by the void portion 180. Note that the above-mentioned width W of the void portion can be appropriately changed depending on the size of the solid-state battery, the thickness of the end electrode, and the thickness of the outer casing portion. For example, as shown in Figure 4, multiple void portions 180 may each have different widths.

[0079] Furthermore, in a cross-sectional view, the non-contact portion 145A between the outer casing 150 and the end electrode 140 may be larger than the contact portion 145B (see Figure 4). In other words, the contact ratio between the outer casing 150 and the end electrode 140 may be less than 50%. To put it another way, the non-contact portion 145A may occupy 50% or more of the outer surface 145 of the end electrode. For example, in a cross-sectional view, the ratio of the non-contact portion 145A to the length of the outer surface of the end electrode may be 50% to 100%, 60% to 99%, or 65% to 99%, and can be, for example, 70% to 95%. In a cross-sectional view, if the non-contact portion 145A occupies the total length of the outer surface 145 of the end electrode within the above range, the end electrode can suitably follow the expansion and contraction of the solid-state battery, and the risk of fracture of the end electrode due to volume changes of the solid-state battery can be reduced.

[0080] As shown in Figure 5, the end electrode 140 may be provided to cover the corner of the solid-state battery. In this specification, “corner of the solid-state battery” means the corner between the main surface 100A or 100B and the side surface 100C of the solid-state battery, and includes both the apex corner where the main surface 100A or 100B and the two side surfaces 100C intersect, and the ridge corner between the main surface 100A or 100B and the side surface 100C. Specifically, the solid-state battery 100 includes a first corner 102a located proximal to the substrate 200, and a second corner 102b located distal to the substrate 200, and the end electrode 140 may be provided to cover at least one of the first corner 102a and the second corner 102b. In this embodiment, the end electrode 140 covering the first corner portion 102a can be referred to as the first corner portion covering region 142a, and the end electrode 140 covering the second corner portion 102b can be referred to as the second corner portion covering region 142b.

[0081] Figure 6 is a schematic enlarged cross-sectional view showing portion B, which is the connection portion between the end electrode 140 and the joining member, in the packaged solid-state battery 1000 shown in Figure 5. In cross-sectional view, the thickness Ta of the first corner covering region 142a may be greater than the thickness of other regions other than the first corner covering region 142a. Here, the thickness of the corner covering region means the thickness of the end electrode 140 in the extending direction of the main surface of the solid-state battery. Specifically, it means the distance from the contact point between the corner of the solid-state battery covered by the corner covering region and the inner surface of the end electrode 140 to the intersection point between the extension line in the extending direction of the main surface of the solid-state battery and the outer surface 145 of the end electrode. As shown in Figure 6, in cross-sectional view, the end electrode 140 covering the first corner 102a may have a greater thickness than other regions. In other words, in cross-sectional view, the end electrode 140 may be provided such that it is relatively thicker in the first corner covering region 142a.

[0082] Of the stresses caused by the expansion and contraction of the solid-state battery 100, the stress acting from the solid-state battery 100 side toward the substrate 200 side may increase as it moves from the solid-state battery 100 toward the end electrode 140 side. That is, of the stresses acting from the solid-state battery 100 side toward the substrate 200 side, the stress along the end electrode 140 may be relatively the largest. In particular, in the first corner covering region 142a that covers the first corner portion 102a located on the substrate 200 side, a larger stress may act, and such stress may cause damage. In this disclosure, as described above, a packaged solid-state battery can be provided in which the connection reliability of the end electrode is improved by providing an end electrode having a relatively large thickness in the first corner covering region 142a.

[0083] More specifically, in a cross-sectional view, the thickness Ta of the first corner covering region 142a of the end face electrode may be greater than the thickness Tb of the second corner covering region 142b located distal to the substrate 200 (see Figure 5). As mentioned above, the stress caused by the expansion and contraction of the solid-state battery may be greater on the first corner 102a side, which is located proximal to the connection point with the substrate 200, than on the second corner 102b side, which is located on the second main surface 100B side of the solid-state battery. Therefore, in a cross-sectional view, the first corner covering region 142a may have a greater thickness than the second corner covering region 142b. With such a structure, a packaged solid-state battery can be provided in which the risk of damage to the end face electrode in the corner covering region is reduced.

[0084] In a cross-sectional view, the ratio of the thickness Ta of the first corner covering region 142a to the thickness Tb of the second corner covering region 142b of the end face electrode may be 101% to 500%, 200% to 400%, or 280% to 370%, and for example, it can be 300% to 350%. In a cross-sectional view, if the thickness Ta of the first corner covering region 142a of the end face electrode is within the above range, a packaged solid-state battery with improved connection reliability of the end face electrode can be provided.

[0085] Furthermore, in cross-sectional view, the thickness Ta of the end electrode 140 in the first corner covering region 142a may be greater than the thickness Tc of the end electrode 140 in the main surface region 143 located on the side surface 100C of the solid battery. In one preferred embodiment, as shown in Figures 5 and 6, in cross-sectional view, the thickness of the end electrode 140 may gradually increase from the substrate 200 side region of the main surface region to the first corner covering region 142a. With such a structure, a packaged solid battery can be provided in which the risk of damage to the end electrode in the corner covering region is reduced.

[0086] The structure of the packaged solid-state battery described herein may be observed from images obtained by cutting a cross-sectional view using an ion milling device (Hitachi High-Tech Corporation, model SU-8040) and acquiring the image using a scanning electron microscope (SEM) (Hitachi High-Tech Corporation, model SU-8040). Furthermore, the dimensions of the void and end face electrodes as referred to herein may refer to values ​​calculated from dimensions measured from images acquired by the above method.

[0087] [Manufacturing method for packaged solid-state batteries] The object of this disclosure can be obtained by preparing a solid battery comprising a battery component having a positive electrode layer, a negative electrode layer, and a solid electrolyte between these electrodes, and then packaging the solid battery (see Figures 7A to 7E).

[0088] The manufacturing of the solid-state battery described herein can be broadly divided into the manufacturing of the solid-state battery itself (hereinafter also referred to as the "pre-packaged battery"), which is the stage prior to packaging, the preparation of the substrate, and packaging.

[0089] <<Method of manufacturing batteries before packaging>> Pre-packaged batteries can be manufactured by printing methods such as screen printing, the green sheet method using green sheets, or a combination of these methods. In other words, the pre-packaged battery itself may be manufactured in accordance with the conventional manufacturing methods for solid-state batteries (therefore, the raw materials such as the solid electrolyte, organic binder, solvent, any additives, positive electrode active material, and negative electrode active material described below may be those used in the manufacture of known solid-state batteries).

[0090] In the following, one manufacturing method is described as an example for better understanding of this disclosure, but this disclosure is not limited to that method. Furthermore, the order of description and other chronological matters below are for illustrative purposes only and are not necessarily binding.

[0091] (Laminate block formation) A slurry is prepared by mixing a solid electrolyte, an organic binder, a solvent, and any additives. Then, a sheet containing the solid electrolyte is formed from the prepared slurry by calcination. • A paste for the positive electrode is prepared by mixing the positive electrode active material, solid electrolyte, conductive material, organic binder, solvent, and any additives. Similarly, a paste for the negative electrode is prepared by mixing the negative electrode active material, solid electrolyte, conductive material, organic binder, solvent, and any additives. Print the positive electrode paste onto the sheet, and print the current collector layer and / or negative layer as needed. Similarly, print the negative electrode paste onto the sheet, and print the current collector layer and / or negative layer as needed. A laminate is obtained by alternately stacking sheets printed with positive electrode paste and sheets printed with negative electrode paste. The outermost layer (top and / or bottom layer) of the laminate may be an electrolyte layer, an insulating layer, or an electrode layer.

[0092] (Formation of battery-fired body) After the laminate is compressed and integrated, it is cut to a predetermined size. The resulting cut laminate is then degreased and fired. This yields a fired laminate. Alternatively, the laminate may be degreased and fired before cutting, and then cut.

[0093] (Edge electrode formation) The positive end electrode 140A can be formed by applying a conductive paste to the exposed positive electrode side of the fired laminate. Similarly, the negative end electrode 140B can be formed by applying a conductive paste to the exposed negative electrode side of the fired laminate. As shown in Figure 7A, the positive and negative end electrodes 140 may extend to the main surface of the fired laminate. The components of the end electrodes can be selected from at least one selected from silver, gold, platinum, aluminum, copper, tin, and nickel.

[0094] Furthermore, the end face electrodes 140 on the positive and negative sides are not limited to being formed after firing the laminate; they may also be formed before firing and subjected to simultaneous firing.

[0095] By going through the process described above, the desired pre-packaged battery (corresponding to the solid-state battery 100 shown in Figure 7A) can finally be obtained.

[0096] (Void formation treatment) Next, the outer surface 145 of the end electrode may be treated to form a gap between the end electrode 140 and the outer casing. The gap between the end electrode 140 and the outer casing may be formed by applying a gap-forming agent 190 before the formation of the outer casing (see Figure 7B). For example, after the end electrode 140 is formed, the gap-forming agent 190 for forming the gap may be applied to the end electrode 140. The gap-forming agent 190 only needs to be applied to the areas on the end electrode 140 where the gap is to be formed. For example, the gap-forming agent 190 may be applied over the entire end electrode 140, or it may be applied only to a part of the end electrode, for example, only to the main surface area 143 of the end electrode located on the side surface of the solid battery (see Figure 5).

[0097] Examples of void-forming agents used include, for example, known materials that vaporize near the heating temperature during the molding process for forming the insulating coating layer 160 (see Figure 7C), which will be described later. Such void-forming agents can be selected from any material depending on the conditions for forming the insulating coating layer (e.g., heating temperature). Although this is merely an example, examples of such void-forming agents include wax-based materials such as paraffin wax and microcrystalline wax. When such a void-forming agent is used, it vaporizes when heated during the molding process for forming the insulating coating layer, penetrates the insulating coating layer and disappears, resulting in the formation of a void between the end electrode 140 and the insulating coating layer.

[0098] Furthermore, the void-forming agent may be a material that reduces the adhesion between the end electrode 140 and the outer casing. For example, the void-forming agent may be a known material that improves the release properties of the outer casing provided on the end electrode 140 from the end electrode. Although this is merely an example, examples of such void-forming agents include fluorine-based materials, silicone-based materials, and wax-based materials. When such a void-forming agent is used, the outer casing separates from the end electrode 140 at the location where the void-forming agent is applied, and a void is formed between the end electrode 140 and the outer casing.

[0099] Alternatively, the void-forming agent may be a foaming material such as a foamed resin. The foamed resin may be a resin that foams up to form a foam during the molding of the outer casing. The foamed resin is not particularly limited, and known foamed resins used for foam molding of resins can be used. For example, the foaming material may be a thermoplastic resin blended with at least one of a chemical foaming agent and foam beads. Although it is preferable that no void-forming agent remains in the final packaged solid battery, the packaged solid battery may contain a void-forming agent.

[0100] <Preparation of circuit boards> In this process, the substrate is prepared.

[0101] While not particularly limited, when a resin substrate is used as the substrate, its preparation may be carried out by laminating multiple layers and then heating and pressurizing them. For example, a substrate precursor can be formed using a resin sheet constructed by impregnating a fibrous cloth, which serves as the base material, with a resin raw material. After the formation of the substrate precursor, this substrate precursor is subjected to heating and pressurizing in a press machine. On the other hand, when a ceramic substrate is used as the substrate, its preparation may be carried out, for example, by forming a green sheet laminate by thermocompression bonding multiple green sheets, and then firing the green sheet laminate to obtain a ceramic substrate. The preparation of the ceramic substrate can be carried out, for example, in accordance with the preparation of an LTCC substrate. The semi-lacquered substrate may have vias and / or lands. In such cases, for example, holes may be formed in the green sheet by a punch press or a carbon dioxide laser, and conductive paste material may be filled into the holes, or precursors of conductive parts such as vias and lands may be formed by performing a printing method. Note that lands, etc., can also be formed after firing the green sheet laminate.

[0102] By going through the above steps, the desired substrate 200 can finally be obtained.

[0103] <<Packaging>> Next, the battery and circuit board obtained above are packaged (see Figures 7C to 7E).

[0104] First, the unpackaged battery 100 is placed on the circuit board 200. In other words, an "unpackaged solid battery" is placed on the circuit board (hereinafter, the battery used for packaging will also be simply referred to as a "solid battery").

[0105] Preferably, the solid-state battery 100 is placed on the substrate such that the conductive portion of the substrate and the end face electrodes 140 of the solid-state battery 100 are electrically connected to each other. For example, a conductive paste may be applied to the substrate to electrically connect the conductive portion of the substrate and the end face electrodes 140 of the solid-state battery 100. More specifically, the conductive portions on the positive and negative sides of the main surface of the substrate (especially the lower lands / bottom lands) are aligned with the positive and negative end face electrodes 140 of the solid-state battery 100, respectively, and then bonded using a conductive paste (e.g., Ag conductive paste). In other words, a precursor for the bonding member responsible for the electrical connection between the solid-state battery 100 and the substrate may be provided on the substrate in advance.

[0106] Such a precursor for the bonding member can be formed by printing a conductive paste that does not require cleaning with flux or other means after formation, such as Ag conductive paste, nanopaste, alloy-based paste, or brazing material. Next, the solid battery 100 is placed on the substrate so that the end electrode 140 and the precursor for the bonding member are in contact with each other, and then subjected to a heat treatment, thereby forming a bonding member that contributes to the electrical connection between the solid battery 100 and the substrate from the precursor.

[0107] Next, the outer casing 150 is formed. The outer casing 150 may consist of a covering insulating layer 160 and a covering inorganic layer 170.

[0108] First, a coating insulating layer 160 is formed so as to cover the solid battery 100 on the substrate 200 (see Figure 7C). Therefore, the raw material for the coating insulating layer is provided so as to completely cover the solid battery 100 on the substrate. If the coating insulating layer is made of a resin material, a resin precursor is placed on the substrate and subjected to curing or other processes to form the coating insulating layer. In one preferred embodiment, the coating insulating layer may be formed by applying pressure in a mold. For illustrative purposes only, the coating insulating layer that seals the solid battery 100 on the substrate may be formed by compression molding. The form of the raw material for the coating insulating layer may be granular, and the type may be thermoplastic, as long as it is a resin material commonly used in molds. Note that such molding is not limited to mold molding, but may also be performed through polishing, laser processing and / or chemical processing.

[0109] During the molding process of the insulating coating layer 160, a void 180 is formed between the end electrode 140 and the insulating coating layer 160 by the void-forming agent 190 applied to the end electrode 140 as described above (see Figure 7D). For example, the void 180 may be formed by the vaporization and disappearance of the void-forming agent due to heating during the molding process of the insulating coating layer 160.

[0110] After forming the insulating coating layer 160, the inorganic coating layer 170 is formed (see Figure 7E). The inorganic coating layer 170 may be formed by plating the coating precursor. In one embodiment, the inorganic coating layer is formed on the coating precursor by forming a plating film on the exposed surfaces other than the bottom surface of the coating precursor (i.e., other than the bottom surface of the support substrate).

[0111] By going through the above process, a packaged product having a gap between the end electrode and the outer casing can be obtained. In other words, the "packaged solid battery" according to this disclosure can be obtained in the end.

[0112] Although not shown in the figures, the inorganic coating layer may extend to the bottom main surface of the substrate, which is located on the opposite side of the main surface of the substrate facing the solid battery. In other words, the insulating coating layer and / or the inorganic coating layer as the outer casing may extend to the side surface of the substrate, and may extend beyond that side surface to the bottom main surface of the substrate (especially its peripheral portion). In such a configuration, a packaged solid battery can be obtained in which the intrusion of moisture from the outside into the solid battery is more effectively prevented.

[0113] Furthermore, the inorganic coating layer can also be provided as a multi-layer structure consisting of at least two layers. Such a multi-layer structure is not limited to dissimilar materials, but may also consist of materials of the same type. For example, the inorganic coating layer may be a multi-layer structure in which two or more dry-plated films formed by dry plating and wet-plated films formed by wet plating are stacked in any order. Providing such a multi-layer inorganic coating layer makes it easier to construct a suitable water vapor barrier for solid-state batteries.

[0114] Furthermore, a water vapor barrier layer may be formed on the substrate. In other words, a water vapor barrier may be formed on the substrate prior to packaging the substrate and solid-state battery together.

[0115] The water vapor barrier layer is not particularly limited as long as it can form the desired barrier layer. For example, in the case of a "water vapor barrier layer having Si-O bonds and Si-N bonds," it is preferably formed by coating a liquid raw material and irradiating it with ultraviolet light. In other words, the water vapor barrier layer is formed under relatively low temperature conditions (for example, a temperature of about 100°C) without using vapor deposition methods such as CVD or PVD.

[0116] Specifically, a liquid raw material containing, for example, silazane is prepared, and this liquid raw material is applied to a substrate by spin coating or spray coating, and dried to form a barrier precursor. Then, by irradiating the barrier precursor with UV light in a nitrogen-containing environment, a "water vapor barrier layer having Si-O bonds and Si-N bonds" can be obtained.

[0117] Furthermore, it is preferable to locally remove the water vapor barrier layer at the junction between the conductive portion of the substrate and the end-face electrodes of the solid-state battery, so that no water vapor barrier layer is present at that location. Alternatively, a mask may be used to prevent the formation of a water vapor barrier layer at the junction. In other words, a mask may be applied to the region that will be the junction to form a water vapor barrier layer throughout, and then the mask may be removed.

[0118] The embodiments of this disclosure have been described above, but these are merely typical examples. Those skilled in the art will readily understand that this disclosure is not limited thereto, and various embodiments are conceivable without altering the essence of this disclosure.

[0119] Furthermore, the above-described embodiment of the present disclosure includes the following preferred embodiments. First aspect: The device comprises a substrate, a solid-state battery with end-face electrodes provided on the substrate, and an outer casing covering the solid-state battery. The exterior part includes resin, A packaged solid battery having a gap between the end electrode and the outer casing. Second aspect: In the first embodiment described above, the solid battery and the casing portion are separated from each other and the solid battery and the casing portion are in contact with each other, A packaged solid battery in which the separated opposing portions are located between the end electrode and the outer casing. Third aspect: A packaged solid battery in which, according to the first or second embodiment described above, the void is located between at least one of the end face electrode on the positive electrode side and the end face electrode on the negative electrode side and the outer casing. Fourth aspect: A packaged solid battery in which, in any of the first to third embodiments described above, a plurality of the voids are formed intermittently along the end face electrodes. Fifth aspect: A packaged solid battery in any of the first to fourth embodiments described above, wherein the end face electrode includes a contact portion with the outer casing and a non-contact portion. Sixth aspect: A packaged solid battery in the fifth embodiment described above, wherein the contact portion is located at at least one of the top surface end of an end electrode located distal to the substrate and the substrate side end located proximal to the substrate. Seventh aspect: In the fifth or sixth embodiment described above, the solid battery comprises a first main surface facing the substrate and a second main surface located opposite the first main surface. The end of the end face electrode extends to at least one of the first main surface and the second main surface, A packaged solid battery in which the contact portion is located at the end. Eighth aspect: A packaged solid battery in any of the first to seventh embodiments described above, wherein, in cross-sectional view, the void portion has an elongated shape that extends along the main surface region of the end face electrode. Appearance 9: A packaged solid battery in any of the first to eighth embodiments described above, wherein the void is continuous over the entire main surface region of the end face electrode. Tenth aspect: In any of the above first to ninth embodiments, the exterior portion includes a covering insulating layer that covers the solid battery, A packaged solid battery in which the end electrode and the insulating coating layer are separated and facing each other via the aforementioned void. Appearance No. 11: A packaged solid battery in any of the first to tenth embodiments described above, wherein the cross-sectional shape of the void corresponds to the cross-sectional shape of the outer surface of the end electrode. Appearance 12: A packaged solid battery in any of the above-described embodiments 1 to 11, wherein, in a cross-sectional view, the occupancy rate of the non-contact portion on the outer surface of the end electrode is 50% or more and 100% or less. Appearance 13: In any of the above first to twelfth embodiments, the solid battery comprises a first corner portion located proximal to the substrate, The end face electrode includes a first corner covering region that covers the first corner, A packaged solid battery in which, in a cross-sectional view, the thickness of the first corner covering region is greater than the thickness of other regions other than the first corner covering region. Appearance 14: In the 13th embodiment described above, the solid battery comprises a second corner located distal to the substrate, The end face electrode includes a second corner covering region that covers the second corner, A packaged solid battery, wherein the other region is the second corner covering region. Appearance 15: A packaged solid battery in the twelfth or thirteenth embodiment described above, wherein the other region is the main surface region of the end face electrode. [Industrial applicability]

[0120] The packaged solid-state battery described herein can be used in a variety of fields where battery use or energy storage is anticipated. While these are merely examples, the packaged solid-state batteries described herein can be used in the electrical, information, and communication fields where mobile devices are used (e.g., the electrical and electronic equipment field or mobile device field, including mobile phones, smartphones, laptops and digital cameras, activity trackers, ARM computers, electronic paper, and small electronic devices such as RFID tags, card-type electronic money, and smartwatches), household and small industrial applications (e.g., power tools, golf carts, household, caregiving, and industrial robots), large industrial applications (e.g., forklifts, elevators, and port cranes), transportation systems (e.g., hybrid vehicles, electric vehicles, buses, trains, electric-assist bicycles, electric motorcycles, etc.), power grid applications (e.g., various power generation systems, road conditioners, smart grids, and general household energy storage systems), medical applications (medical equipment such as earphones and hearing aids), pharmaceutical applications (medication management systems, etc.), as well as IoT applications and space and deep-sea applications (e.g., space probes, submersible research vessels, etc.). [Explanation of symbols]

[0121] 100 solid state battery First main surface of a 100A solid-state battery Second main surface of a 100B solid-state battery Side view of a 100C solid-state battery 102a First corner of a solid-state battery 102b Second corner of a solid-state battery 110 Positive electrode layer 120 Negative electrode layer 130 Solid electrolyte or solid electrolyte layer 140 End electrode 140A Positive end face electrode 140B Negative side end electrode 141a Top side end 141b Bottom side corner 142a First corner coverage area 142b Second corner coverage area 143 Main surface region of end face electrode 145 Outer surface of end-face electrode 145A Non-contact part 145B Contact part 150 Exterior part 155 Inner surface of exterior part 160 Insulating coating layer 170 Inorganic coating layer 180 Cavity 190 Void-forming agent 200 circuit boards 210 Substrate electrode layer (upper side of the substrate) 210A Positive side substrate electrode layer 210B Negative electrode substrate electrode layer 220 Electrode layer on the mounting side substrate (lower side of the substrate) 220A Positive side mounting side substrate electrode layer 220B Negative electrode side mounting substrate electrode layer 250 Side view of the circuit board 600 Joining member 1000 packaged solid batteries

Claims

1. The device comprises a substrate, a solid-state battery with end-face electrodes provided on the substrate, and an outer casing that covers the solid-state battery and is joined to the substrate. The exterior part includes resin, The end electrode includes a gap between it and the outer casing, The solid battery comprises a first main surface facing the substrate and a second main surface located on the opposite side from the first main surface. The solid battery and the casing portion are separated and facing each other, and the solid battery and the casing portion are in contact with each other. The separated opposing portions are the portions where the end face electrode and the outer casing portion are separated and facing each other. A packaged solid battery in which the contact portion is the portion that contacts the second main surface and the outer casing.

2. The packaged solid battery according to claim 1, wherein the void is located between at least one of the positive electrode end face electrode and the negative electrode end face electrode and the outer casing.

3. The packaged solid battery according to claim 1, wherein the end electrode includes a contact portion with the outer casing and a non-contact portion.

4. The packaged solid battery according to claim 3, wherein the contact portion between the end electrode and the outer casing is located at least one of the top end of the end electrode located distal to the substrate and the substrate end located proximal to the substrate.

5. The end of the end face electrode extends to at least one of the first main surface and the second main surface, The packaged solid battery according to claim 3, wherein the contact portion between the end electrode and the outer casing is located at the end.

6. The packaged solid battery according to claim 3, wherein, in a cross-sectional view, the occupancy rate of the non-contact portion on the outer surface of the end electrode is 50% or more and 100% or less.

7. The packaged solid battery according to claim 1, wherein, in cross-sectional view, the void portion has an elongated shape that extends along the main surface region of the end face electrode.

8. The packaged solid battery according to claim 1, wherein a plurality of the aforementioned voids are formed intermittently along the end face electrode.

9. The packaged solid battery according to claim 1, wherein the void is continuous over the entire main surface region of the end face electrode.

10. The exterior portion includes a covering insulating layer that covers the solid battery, The packaged solid battery according to claim 1, wherein the end electrode and the insulating coating layer are separated and facing each other via the aforementioned void.

11. The packaged solid battery according to claim 1, wherein the cross-sectional shape of the void corresponds to the cross-sectional shape of the outer surface of the end electrode.

12. The solid battery comprises a first corner portion located proximal to the substrate, The end face electrode includes a first corner covering region that covers the first corner, The packaged solid battery according to claim 1, wherein, in a cross-sectional view, the thickness of the first corner covering region is greater than the thickness of other regions other than the first corner covering region.

13. The solid battery comprises a second corner located distal to the substrate, The end face electrode includes a second corner covering region that covers the second corner, The packaged solid battery according to claim 12, wherein the other region is the second corner covering region.

14. The packaged solid battery according to claim 12, wherein the other region is the main surface region of the end face electrode.