Oil-based matte ink compositions, laminates, and industrial tapes

Abstract

To provide an oil-based matte ink composition, a laminate using the same, and an industrial tape that can form a coating film with excellent curl resistance, which prevents curling of printed materials even when printed on plastic films less than 10 μm thick, and also has excellent solvent resistance and blocking resistance. [Solution] An oil-based matte ink composition containing a urethane-modified (meth)acrylic resin (A), silica (B), and an organic solvent (C), wherein (A) is a graft polymer having a (meth)acrylic portion as its main backbone and a urethane portion as its side chain, the mass ratio expressed as urethane portion / (meth)acrylic portion is 0.1 to 0.9, the glass transition temperature of the (meth)acrylic portion is 40 to 100°C, the content of (A) is 28 to 53% by mass, and the mass ratio expressed as (B) / (A) on a solid content basis is 0.04 to 0.50.

Description

[Technical Field]

[0001] This invention relates to an oil-based matte ink composition, a laminate, and an industrial tape. [Background technology]

[0002] Industrial tapes used in electronic components such as smartphones and televisions are printed on plastic films using inks and varnishes, often via gravure printing, to improve durability, functionality, design, and workability. In recent years, in particular, there has been a growing demand for matte inks to give industrial tapes a matte finish, for reasons such as further enhancing design to reflect corporate image, adding tactile properties, and providing slipperiness.

[0003] Industrial tapes used in electronic components and other applications require thinness from the perspectives of miniaturization, weight reduction, cost reduction, flexibility, and conformability. The plastic films used are considerably thinner than those used in general flexible packaging, often less than 10 μm thick. A problem that arises in this context is the curling of printed materials obtained by printing on plastic films. The thinner the plastic film used, the more likely the printed material is to curl, significantly reducing workability. Therefore, even when using thin plastic films, matte inks are required to have good curl resistance to prevent curling.

[0004] On the other hand, solvent resistance is another important physical property required for matte inks used in industrial tapes. Organic solvents are used when cleaning parts and products during the manufacturing process, as well as during maintenance. In such cases, the printed coating on the industrial tape must be resistant to dissolution and must have excellent solvent resistance, preventing deterioration, degradation of physical properties, and changes in appearance. Furthermore, matte inks used in industrial tapes are also required to have excellent blocking resistance. It is generally known that adding silica can improve blocking resistance while providing a matte finish, but this negatively affects curl resistance, making it very difficult to achieve both simultaneously.

[0005] Patent Document 1 discloses a printing ink composition for shrink packaging containing an acrylic resin having an acid value, a cellulose-based resin esterified with a carboxylic acid, a polyurethane / acrylic copolymer resin, and a solvent. Patent Document 2 discloses a printing ink for plastic labels containing a urethane acrylic resin, an acrylic resin, and titanium dioxide. [Prior art documents] [Patent Documents]

[0006] [Patent Document 1] Japanese Patent Publication No. 2012-207129 [Patent Document 2] Japanese Patent Publication No. 2012-062415 [Overview of the Initiative] [Problems that the invention aims to solve]

[0007] However, the ink compositions described in Patent Documents 1 and 2 are intended for use in shrink packaging and plastic labels, and the plastic films used are thicker than those used in industrial tapes, so curl resistance is not a problem in the first place. Furthermore, the curl resistance of the ink compositions is not considered sufficient. Moreover, neither document assumes that the ink compositions contain silica, and the ink layer formed from the ink compositions does not have a matte finish. Furthermore, it cannot be said that they have excellent curl resistance. Solvent resistance is also not considered sufficient, and further improvement is needed regarding blocking resistance. In other words, a matte ink composition that simultaneously satisfies all of the following conditions does not yet exist: curl resistance, solvent resistance, and blocking resistance.

[0008] The present invention aims to provide an oil-based matte ink composition, a laminate using the same, and an industrial tape that can form a coating film having excellent curl resistance, which prevents curling of printed materials even when printed on plastic films less than 10 μm thick, and also having excellent solvent resistance and blocking resistance. [Means for solving the problem]

[0009] The present invention has the following aspects. [1] An oil-based matte ink composition containing a urethane-modified (meth)acrylic resin (A), silica (B), and an organic solvent (C), The urethane-modified (meth)acrylic resin (A) is a graft polymer having a (meth)acrylic portion as its main skeleton and urethane portions as its side chains. In the urethane-modified (meth)acrylic resin (A), the mass ratio represented by the urethane portion / (meth)acrylic portion is 0.1 to 0.9. The glass transition temperature of the (meth)acrylic portion constituting the urethane-modified (meth)acrylic resin (A) is 40 to 100°C. The content of the urethane-modified (meth)acrylic resin (A) on a solids basis is 28 to 53% by mass relative to the total solids of the oil-based matte ink composition. An oil-based matte ink composition having a mass ratio of 0.04 to 0.50 on a solid content basis, represented by the silica (B) and the urethane-modified (meth)acrylic resin (A). [2] The oil-based matte ink composition according to [1], wherein the mass ratio of the urethane portion to the (meth)acrylic portion in the urethane-modified (meth)acrylic resin (A) is 0.1 to 0.5. [3] The oil-based matte ink composition according to [1] or [2], wherein the hydroxyl value of the urethane-modified (meth)acrylic resin (A) is 40 to 120 mgKOH / g or less. [4] The oil-based matte ink composition according to any one of [1] to [3], wherein the average particle size of the silica (B) is 2 to 10 μm or less. [5] Further containing extender pigment (D), The extender pigment (D) comprises at least one of calcium carbonate and precipitated barium sulfate. An oil-based matte ink composition according to any one of [1] to [4], wherein the average particle size of the extender pigment (D) is 0.05 to 0.70 μm. [6] Further containing hydrocarbon wax (E), An oil-based matte ink composition according to any one of [1] to [5], wherein the penetration of the hydrocarbon wax (E) is 20 or less. [7] The oil-based matte ink composition according to any one of [1] to [6], further comprising a curing agent (F). [8] An oil-based matte ink composition according to any one of [1] to [7] above, for use in gravure printing. [9] A laminate comprising a plastic film and a matte ink layer formed on one surface of the plastic film using the oil-based matte ink composition described in [8].

[10] The laminate according to [9], further comprising a pattern layer between the plastic film and the matte ink layer, or on the other surface of the plastic film.

[11] An industrial tape comprising the laminate according to [9] or

[10] .

Advantages of the Invention

[0010] According to the present invention, an oil-based matte ink composition capable of forming a coating film having excellent curl resistance such that curling of a printed matter hardly occurs even when printed on a plastic film of less than 10 μm, and having excellent solvent resistance and blocking resistance, a laminate using the same, and an industrial tape can be provided.

Brief Description of the Drawings

[0011] [Figure 1] It is a cross-sectional view schematically showing an example of the laminate of the present invention. [Figure 2] It is a cross-sectional view schematically showing another example of the laminate of the present invention. [Figure 3] It is a cross-sectional view schematically showing another example of the laminate of the present invention.

Modes for Carrying Out the Invention

[0012] Hereinafter, the present invention will be described in detail. The following embodiments are merely illustrative for explaining the present invention, and it is not intended to limit the present invention only to these embodiments. The present invention can be implemented in various modes without departing from its gist. In the present invention, "oil-based" in the oil-based matte ink composition means containing an organic solvent as a medium. The proportion of the organic solvent in the medium of the oil-based matte ink composition is preferably 50% by mass or more, more preferably 70% by mass or more, particularly preferably 90% by mass or more, and may be 100% by mass with respect to the total mass of the medium. A "coating film" refers to a coating film formed by an oil-based matte ink composition. In particular, the coating film before drying is also called the "coated film," and the coating film after drying is also called the "matte ink layer." The coated film is obtained by coating the oil-based matte ink composition of the present invention onto a surface to be coated (for example, a plastic film, etc.). The matte ink layer is obtained by drying the coated film and removing volatile components such as the medium in the coated film. If necessary, the obtained matte ink layer may be aged after drying the coated film. "Variable component" refers to volatile components such as water and organic solvents. Specifically, it refers to components other than the solid components listed below (volatile components). The "solid content" of an oil-based matte ink composition refers to the non-volatile components of the composition, excluding the medium, and is the component that ultimately forms the matte ink layer. Even if components other than the medium are liquid at room temperature, they are not included in the medium and are included in the solid content. The solid content is measured in accordance with JIS K 5601-1-2:2008. The "total solids" of an oil-based matte ink composition refers to the total mass (sum) of solids contained in the oil-based matte ink composition. The content of components other than the medium in the oil-based matte ink composition is all calculated on a solids basis. "(Meth)acrylic" is a general term for "acrylic" and "methacrylic". "(Meth)acrylate" is a general term for "acrylate" and "methacrylate". "(Meth)acrylonitrile" is a general term for "acrylonitrile" and "methacrylonitrile." The "~" symbol indicating a numerical range means that the numbers before and after it are included as the lower and upper limits, respectively. For example, A~B is equivalent to A or greater and B or less. The lower and upper limits of the numerical ranges disclosed herein can be combined in any way to create new numerical ranges.

[0013] [Oil-based matte ink composition] The oil-based matte ink composition of this embodiment contains a urethane-modified (meth)acrylic resin (A), silica (B), and an organic solvent (C). The oil-based matte ink composition may further contain an extender pigment (D). The oil-based matte ink composition may further contain hydrocarbon wax (E). The oil-based matte ink composition may further contain a curing agent (F). The oil-based matte ink composition may further contain other components (hereinafter also referred to as "other optional components") as necessary, insofar as they do not impair the effects of the present invention, other than urethane-modified (meth)acrylic resin (A), silica (B), organic solvent (C), extender pigment (D), hydrocarbon wax (E), and curing agent (F).

[0014] <Urethane-modified (meth)acrylic resin (A)> Urethane-modified (meth)acrylic resin (A) is a binder resin. The urethane-modified (meth)acrylic resin (A) is a graft polymer having a (meth)acrylic portion as its main skeleton and urethane portions as its side chains. In other words, the main chain, which is the (meth)acrylic portion, and the side chains, which are the urethane portions, are connected by urethane bonds. The urethane-modified (meth)acrylic resin (A) imparts solvent resistance to the coating film by having a (meth)acrylic portion and curl resistance to the coating film by having a urethane portion. Therefore, by including the urethane-modified (meth)acrylic resin (A) in the oil-based matte ink composition, a coating film with excellent curl resistance and solvent resistance can be obtained.

[0015] Typical examples of the synthesis of urethane-modified (meth)acrylic resin (A) include a method in which a urethane prepolymer having isocyanate groups at its termini is reacted with a (meth)acrylate monomer having hydroxyl groups to synthesize a (meth)acrylate monomer having a urethane portion, and then (meth)acrylic polymerization is carried out using the (meth)acrylate monomer having a urethane portion; and a method in which a (meth)acrylic polymer having hydroxyl groups in its side chains is synthesized by (meth)acrylic polymerization using a (meth)acrylate monomer having hydroxyl groups, and then (meth)acrylic polymer having hydroxyl groups in its side chains is reacted with a urethane prepolymer having isocyanate groups at its termini. Alternatively, urea prepolymer may be used instead of urethane prepolymer.

[0016] Examples of (meth)acrylic monomers constituting the (meth)acrylic portion include (meth)acrylates having hydroxyl groups. Examples of (meth)acrylates having hydroxyl groups include hydroxymethyl (meth)acrylate, 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, 3-hydroxypropyl (meth)acrylate, and 4-hydroxybutyl (meth)acrylate. Other monomers having a hydroxyl group besides (meth)acrylate may be used as the (meth)acrylic monomer. Examples include methyl (meth)acrylate, ethyl (meth)acrylate, butyl (meth)acrylate, cyclohexyl (meth)acrylate, glycidyl (meth)acrylate, and (meth)acrylic acid. These (meth)acrylic monomers may be used individually or in combination of two or more types.

[0017] Furthermore, polymerizable monomers other than (meth)acrylic monomers (hereinafter also referred to as "other polymerizable monomers") may be used in combination as needed. Other polymerizable monomers are not particularly limited as long as they can copolymerize with (meth)acrylic monomers, but examples include styrene monomers such as styrene, α-methylstyrene, vinyltoluene, and their derivatives; unsaturated carboxylic acid monomers such as itaconic acid, maleic acid, fumaric acid, and crotonic acid; and (meth)acrylamide and (meth)acrylonitrile. Other polymerizable monomers may be used individually or in combination of two or more.

[0018] Methods for synthesizing the urethane prepolymer that constitutes the urethane portion include, for example, a method involving the reaction of a polyisocyanate compound with a polyol compound. Additionally, chain extenders may be used as needed. Urethane prepolymers are reaction products obtained by reacting polyol compounds with polyisocyanate compounds, and are compounds having isocyanate groups at the molecular ends.

[0019] Examples of polyisocyanate compounds include 2,4-tolylene diisocyanate, 2,6-tolylene diisocyanate, m-xylylene diisocyanate, 4,4'-diphenylmethane diisocyanate, 2,2'-diphenylmethane diisocyanate, 2,4'-diphenylmethane diisocyanate, 4,4-diphenyl ether diisocyanate, 2-nitrodiphenyl-4,4-diisocyanate, 2,2-diphenylpropane-4,4-diisocyanate, 3,3-dimethyldiphenylmethane-4,4-diisocyanate, 4,4-diphenylpropane diisocyanate, m-phenylene diisocyanate, p-phenylene diisocyanate, and naphth. Examples include aromatic diisocyanates such as ethylene-1,4-diisocyanate, naphthylene-1,5-diisocyanate, and 3,3-dimethoxydiphenyl-4,4-diisocyanate; aliphatic diisocyanates such as tetramethylene diisocyanate, hexamethylene diisocyanate, 2,2,4-trimethylhexamethylene diisocyanate, 2,4,4-trimethylhexamethylene diisocyanate, and lysine diisocyanate; and alicyclic diisocyanates such as isophorone diisocyanate, norbornane diisocyanate, hydrogenated tolylene diisocyanate, hydrogenated xylylene diisocyanate, and hydrogenated diphenylmethane diisocyanate. These polyisocyanate compounds may be used individually or in combination of two or more.

[0020] Examples of polyol compounds include polyester polyols, polycarbonate polyols, and polyether polyols. Polyol compounds may be used individually or in combination of two or more.

[0021] Examples of polyester polyols include polyester polyols or polyester amide polyols obtained by a dehydration polycondensation reaction between polycarboxylic acids and polyhydric alcohols or secondary to tertiary amines. Specific examples of polycarboxylic acids include succinic acid, adipic acid, sebacic acid, azelaic acid, terephthalic acid, isophthalic acid, orthophthalic acid, hexahydroterephthalic acid, hexahydroisophthalic acid, hexahydroorthophthalic acid, and polycarboxylic acids such as naphthalenedicarboxylic acid and trimellitic acid, as well as their acid esters and acid anhydrides, and one or more of these can be used. Specific examples of polyhydric alcohols include ethylene glycol, 1,2-propanediol, 1,3-propanediol, 1,2-butanediol, 1,3-butanediol, 1,4-butanediol, 1,5-pentanediol, 1,6-hexanediol, 3-methyl-1,5-pentanediol, neopentyl glycol, 1,8-octanediol, 1,9-nonanediol, diethylene glycol, dipropylene glycol, 1,4-cyclohexanedimethanol, ethylene oxide or propylene oxide adducts of bisphenol A, trimethylolpropane, glycerin, and low molecular weight alcohol compounds such as pentaerythritol; and low molecular weight amino alcohol compounds such as monoethanolamine and diethanolamine. One or more of these can be used. Specific examples of secondary and tertiary amines include low-molecular-weight amine compounds such as hexamethylenediamine, xylylenediamine, and isophoronediamine, and one or more of these can be used.

[0022] Furthermore, examples of polyester polyols include lactone-based polyester polyols obtained by ring-opening polymerization of cyclic ester (lactone) monomers such as ε-caprolactone and γ-valerolactone using low molecular weight alcohol compounds and low molecular weight amino alcohol compounds as initiators.

[0023] Examples of polycarbonate polyols include those obtained by the dehydrochlorination reaction of a low molecular weight alcohol compound with phosgene, and those obtained by the transesterification reaction of a low molecular weight alcohol compound with a diester carbonate. Examples of low-molecular-weight alcohol compounds include those similar to those used in the synthesis of polyester polyols. Examples of diester carbonates include diethylene carbonate, dimethyl carbonate, diethyl carbonate, and diphenyl carbonate.

[0024] Examples of polyether polyols include those obtained by ring-opening polymerization of a cyclic ether using at least one initiator selected from the group consisting of low molecular weight alcohol compounds, low molecular weight amine compounds, low molecular weight amino alcohol compounds, and phenols. Specifically, examples include polyoxyethylene polyols, polyoxypropylene polyols, polytetramethylene ether polyols, and polyoxyethylene polyoxypropylene polyols. Furthermore, as polyether polyols, polyester ether polyols initiated from the aforementioned polyester polyols or polycarbonate polyols can also be mentioned. Examples of low-molecular-weight alcohol compounds, low-molecular-weight amine compounds, and low-molecular-weight amino alcohol compounds include those similar to those used in the synthesis of polyester polyols. Examples of cyclic ethers include alkylene oxides such as ethylene oxide, propylene oxide, butylene oxide, and tetrahydrofuran.

[0025] As a chain elongator, a compound having two or more functional groups (e.g., amino groups, hydroxyl groups, etc.) that can react with isocyanate groups within the molecule can be used. Examples of chain elongators include diamine compounds such as ethylenediamine, 1,3-propylenediamine, 1,4-butylenediamine, hexamethylenediamine, isophoronediamine, and 2-ethylaminoethylamine; polyamine compounds such as diethylenetriamine and triethylenetetramine; low molecular weight diol compounds such as ethylene glycol, propylene glycol, butylene glycol, diethylene glycol, and triethylene glycol; and aminoethylethanolamine and aminopropylethanolamine. These chain extenders may be used individually or in combination of two or more.

[0026] The glass transition temperature of the urethane-modified (meth)acrylic resin (A) is preferably 20 to 80°C, more preferably 30 to 70°C, and particularly preferably 40 to 65°C. If the glass transition temperature of the urethane-modified (meth)acrylic resin (A) is below the lower limit, the solvent resistance, blocking resistance, and heat resistance of the coating film will be slightly reduced. If the glass transition temperature of the urethane-modified (meth)acrylic resin (A) exceeds the upper limit, the curl resistance and adhesion to the substrate of the coating film will be slightly reduced.

[0027] The glass transition temperature of urethane-modified (meth)acrylic resin (A) is measured in accordance with JIS K 7121:2012 as follows: Using a differential scanning calorimeter, 10 mg of urethane-modified (meth)acrylic resin (A) is heated from -100°C to 160°C at a rate of 20°C / min. The glass transition temperature is determined from the intersection point of the baseline and the tangent to the endothermic curve in the resulting curve (DSC curve).

[0028] The glass transition temperature of the (meth)acrylic portion constituting the urethane-modified (meth)acrylic resin (A) is 40 to 100°C, preferably 50 to 90°C, and particularly preferably 65 to 85°C. If the glass transition temperature of the (meth)acrylic portion constituting the urethane-modified (meth)acrylic resin (A) is below the above lower limit, the solvent resistance, blocking resistance, and heat resistance of the coating film will decrease. If the glass transition temperature of the (meth)acrylic portion constituting the urethane-modified (meth)acrylic resin (A) exceeds the above upper limit, the curl resistance and adhesion to the substrate of the coating film will decrease.

[0029] The glass transition temperature of the (meth)acrylic portion constituting the urethane-modified (meth)acrylic resin (A) is determined by using the value disclosed by the manufacturer for commercially available products, and otherwise by measuring as follows: Specifically, the (meth)acrylic portion of the urethane-modified (meth)acrylic resin (A) that has not undergone urethane modification treatment is synthesized, and in accordance with JIS K 7121:2012, the glass transition temperature is determined from the intersection of the baseline and the tangent to the endothermic curve in the curve (DSC curve) obtained by heating 10 mg of the (meth)acrylic portion from -100°C to 160°C at a rate of 20°C / min using a differential scanning calorimeter.

[0030] The glass transition temperature of the urethane portion constituting the urethane-modified (meth)acrylic resin (A) is preferably -50 to 50°C, more preferably -40 to 30°C, and particularly preferably -35 to 15°C. If the glass transition temperature of the urethane portion constituting the urethane-modified (meth)acrylic resin (A) is below the above lower limit, the solvent resistance, blocking resistance, and heat resistance of the coating film will be slightly reduced. If the glass transition temperature of the urethane portion constituting the urethane-modified (meth)acrylic resin (A) exceeds the above upper limit, the curl resistance and adhesion to the substrate of the coating film will be slightly reduced.

[0031] The glass transition temperature of the urethane portion constituting the urethane-modified (meth)acrylic resin (A) is determined by using the value disclosed by the manufacturer for commercially available products, and otherwise by measuring as follows: Specifically, the urethane portion is synthesized by reacting a urethane prepolymer having isocyanate groups at the ends, used in the synthesis of urethane-modified (meth)acrylic resin (A), with methanol. In accordance with JIS K 7121:2012, the glass transition temperature is determined from the intersection of the baseline and the tangent to the endothermic curve in the curve (DSC curve) obtained by heating 10 mg of the urethane portion from -100°C to 160°C at a rate of 20°C / min using a differential scanning calorimeter.

[0032] In urethane-modified (meth)acrylic resin (A), the mass ratio expressed as urethane portion / (meth)acrylic portion (hereinafter also referred to as the "urethane / (meth)acrylic ratio") is 0.1 to 0.9, preferably 0.1 to 0.5, and more preferably 0.2 to 0.4. If the urethane / (meth)acrylic ratio in urethane-modified (meth)acrylic resin (A) is below the above lower limit, the curl resistance and adhesion to the substrate of the coating film will decrease. If the urethane / (meth)acrylic ratio in urethane-modified (meth)acrylic resin (A) exceeds the above upper limit, the solvent resistance, blocking resistance, and heat resistance of the coating film will decrease.

[0033] For urethane-modified (meth)acrylic resin (A), the urethane / (meth)acrylic ratio shall be the value disclosed by the manufacturer for commercially available products. Otherwise, the urethane / (meth)acrylic ratio shall be the mass ratio calculated from the mass of the (meth)acrylic monomer and the mass of the urethane prepolymer used in the synthesis of urethane-modified (meth)acrylic resin (A).

[0034] The hydroxyl value of the urethane-modified (meth)acrylic resin (A) is preferably 40 to 120 mg KOH / g, more preferably 60 to 115 mg KOH / g, and particularly preferably 80 to 110 mg KOH / g. If the hydroxyl value of the urethane-modified (meth)acrylic resin (A) is below the lower limit, the adhesion of the coating film to the substrate, heat resistance, and solvent resistance will be slightly reduced. If the hydroxyl value of the urethane-modified (meth)acrylic resin (A) exceeds the upper limit, the blocking resistance of the coating film and the viscosity stability when the curing agent (F) is added will be slightly reduced.

[0035] The hydroxyl value of urethane-modified (meth)acrylic resin (A) is expressed in milligrams as the amount of potassium hydroxide required to neutralize the acetic acid bonded to the hydroxyl group when 1 g of the non-volatile content of the sample is acetylated, and is measured in accordance with JIS K 0070:1992.

[0036] The acid value of the urethane-modified (meth)acrylic resin (A) is preferably 15 mg KOH / g or less, more preferably 10 mg KOH / g or less, and particularly preferably 7 mg KOH / g or less. It may also be 0 mg KOH / g or more, 0.5 mg KOH / g or more, or 1 mg KOH / g or more. The above upper and lower limits can be combined as appropriate. If the acid value of the urethane-modified (meth)acrylic resin (A) exceeds the above upper limit, the solvent resistance and blocking resistance of the coating film will decrease slightly.

[0037] The acid value of urethane-modified (meth)acrylic resin (A) is expressed in milligrams as the amount of potassium hydroxide required to neutralize acidic groups such as carboxyl groups per gram of non-volatile matter in the sample, and is measured in accordance with JIS K 5601-2-1:1999.

[0038] The weight-average molecular weight of the urethane-modified (meth)acrylic resin (A) is preferably 10,000 to 100,000, more preferably 20,000 to 80,000, and particularly preferably 30,000 to 50,000. If the weight-average molecular weight of the urethane-modified (meth)acrylic resin (A) is below the lower limit, the solvent resistance, blocking resistance, and heat resistance of the coating film will be slightly reduced. If the weight-average molecular weight of the urethane-modified (meth)acrylic resin (A) exceeds the upper limit, the curl resistance and adhesion to the substrate of the coating film will be slightly reduced.

[0039] The weight-average molecular weight of urethane-modified (meth)acrylic resin (A) is the weight-average molecular weight converted to the standard polystyrene molecular weight and is measured by gel permeation chromatography (GPC).

[0040] The solubility parameter of urethane-modified (meth)acrylic resin (A) is 10.0~12.5 (cal / cm³). 3 ) 1 / 2 Preferably, 10.5-12.0 (cal / cm³) 3 ) 1 / 2 More preferably, 11.0~11.8 (cal / cm 3 ) 1 / 2This is particularly preferable. If the solubility parameter of the urethane-modified (meth)acrylic resin (A) is below the above lower limit, the solvent resistance of the coating film, especially its solvent resistance to ethyl acetate, will be slightly reduced. If the solubility parameter of the urethane-modified (meth)acrylic resin (A) exceeds the above upper limit, the storage stability of the oil-based matte ink composition will be slightly reduced.

[0041] The solubility parameter (SP value) of urethane-modified (meth)acrylic resin (A) is calculated using the Fedors method. The calculation of the SP value using the Fedors method is described in (Polymer Engineering and Science, February, 1974, Vol. 14, No. 2, pp. 147-154) as Δei (cal / mol) and Δvi (cm 3 The value (per mole) can be used to calculate the following formula. SP value = (ΣΔei / ΣΔvi) 1 / 2

[0042] The urethane-modified (meth)acrylic resin (A) may be one manufactured by a known manufacturing method or a commercially available product. The urethane-modified (meth)acrylic resin (A) may be used alone or in combination of two or more types.

[0043] <Silica (B)> Silica (B) is a matting agent used to impart a matte appearance to the coating film. In addition, the inclusion of silica (B) in the oil-based matte ink composition improves the coating film's resistance to blocking. Silica (B) may be either naturally occurring or synthetic, and may be crystalline or amorphous. The synthesis method may be either dry or wet. Known dry methods include combustion and arc synthesis. Known wet methods include sedimentation and gel synthesis. Silica (B) may be either hydrophobic silica or hydrophilic silica. Silica (B) may be used alone or in combination of two or more types.

[0044] The average particle size of silica (B) is preferably 2 to 10 μm, more preferably 2.5 to 8 μm, and even more preferably 3 to 6 μm. If the average particle size of silica (B) is below the lower limit, the blocking resistance of the coating film will be slightly reduced. If the average particle size of silica (B) exceeds the upper limit, the adhesion of the coating film to the substrate, abrasion resistance, and printability of the oil-based matte ink composition will be slightly reduced.

[0045] The average particle size of silica (B) is the particle size at 50% of the volume-based cumulative value (D50) in the particle size distribution measured by laser diffraction-scattering.

[0046] <Organic solvent (C)> Examples of organic solvents (C) include aromatic organic solvents such as toluene and xylene; ketone organic solvents such as acetone, methyl ethyl ketone, and methyl isobutyl ketone; ester organic solvents such as ethyl acetate, n-propyl acetate, isopropyl acetate, and isobutyl acetate; and alcohol organic solvents such as methanol, ethanol, n-propanol, i-propanol, n-butanol, and i-butanol. Organic solvent (C) may be used alone or in combination of two or more types.

[0047] As the organic solvent (C), it is preferable to use a mixed solvent consisting of two or more organic solvents. An example of a preferred combination is a combination of a ketone-based organic solvent and an ester-based organic solvent. Among these, a combination of methyl ethyl ketone and n-propyl acetate is particularly preferred.

[0048] <Extender pigment (D)> Extender pigments (D) (excluding silica (B)) are solid particles formed from inorganic materials and can exist stably in oil-based matte ink compositions. The inclusion of extender pigment (D) in the oil-based matte ink composition enhances the matte finish of the matte ink layer. The extender pigment (D) is a matting agent.

[0049] Examples of extender pigments (D) include calcium carbonate, barium sulfate, calcium silicate, magnesium silicate, aluminum oxide, zirconium oxide, tin oxide, clay, and kaolin. Among these, calcium carbonate and barium sulfate are preferred from the viewpoint of superior storage stability, design, and cost of the oil-based matte ink composition, and calcium carbonate and precipitated barium sulfate are more preferred. Extender pigments (D) may be used individually or in combination of two or more types.

[0050] The average particle size of the extender pigment (D) is preferably 0.05 to 0.70 μm, more preferably 0.07 to 0.65 μm, and particularly preferably 0.10 to 0.60 μm. If the average particle size of the extender pigment (D) is below the lower limit, the blocking resistance and matte properties of the coating film will be slightly reduced. If the average particle size of the extender pigment (D) exceeds the upper limit, the storage stability and printability of the oil-based matte ink composition will be slightly reduced.

[0051] The average particle size of the extender pigment (D) is the particle size at 50% of the volume-based cumulative value (D50) in the particle size distribution measured by laser diffraction-scattering if the average particle size is 100 nm or more, and the particle size at 50% of the number-based cumulative value (D50) in the particle size distribution measured using a transmission electron microscope (TEM) if the average particle size is less than 100 nm.

[0052] <Hydrogen wax (E)> To further improve the abrasion resistance of the coating film, the oil-based matte ink composition may contain a hydrocarbon wax (E). The hydrocarbon wax (E) may be any conventionally known wax, such as polyolefin wax, Fischer-Tropsch wax, paraffin wax, modified paraffin wax, or microcrystalline wax. Among these, polyolefin wax and Fischer-Tropsch wax are preferred, and polyolefin wax is more preferred. Hydrocarbon wax (E) may be used alone or in combination of two or more types.

[0053] Examples of polyolefin waxes include polyethylene wax and polypropylene wax. Among these, polyethylene wax is preferred. Examples of polyethylene waxes include high-density polymerized polyethylene, low-density polymerized polyethylene, oxidized polyethylene, acid-modified polyethylene, and special monomer-modified polyethylene. Fischer-Tropsch wax is a wax produced using carbon monoxide and hydrogen as raw materials by the Fischer-Tropsch process, and has a nearly saturated, unbranched, linear molecular structure.

[0054] The penetration (hardness) of hydrocarbon wax (E) is preferably 20 or less, more preferably 17 or less, particularly preferably 15 or less, and may also be 1 or more, 3 or more, or 5 or more. The above upper and lower limits can be combined as appropriate. If the penetration of hydrocarbon wax (E) exceeds the above upper limit, the solvent resistance and heat resistance of the coating film will decrease slightly. If the penetration of hydrocarbon wax (B) is below the above lower limit, the curl resistance and abrasion resistance of the coating film will decrease slightly.

[0055] The penetration of hydrocarbon wax (E) is determined in accordance with JIS K 2235:2022. The measurement temperature is 25°C.

[0056] <Hardening agent (F)> Examples of curing agents (F) include isocyanate-based curing agents and blocked isocyanate-based curing agents. Among these, isocyanate-based curing agents are preferred from the viewpoint of mild aging conditions and crosslinking rate. The hardening agent (F) may be used alone or in combination of two or more types.

[0057] Isocyanate-based curing agents are compounds that have two or more isocyanate groups in one molecule. Examples of isocyanate-based curing agents include aromatic diisocyanates such as 4,4'-diphenylmethane diisocyanate (MDI), 2,2'-MDI, 2,4'-MDI, 2,4-tolylene diisocyanate (TDI), 2,6-TDI, m-xylylene diisocyanate (XDI), and 1,4-phenylene diisocyanate; isophorone diisocyanate (IPDI), 1,3-bis(isocyanatomethyl)cyclohexane (hydrogenated XDI), and dicyclohexylmethane-4,4'-diisocyanate. Examples include alicyclic diisocyanates such as (hydrogenated MDI) and 1-methylcyclohexane-2,4-diisocyanate (hydrogenated TDI); aliphatic diisocyanates such as tetramethylene diisocyanate, hexamethylene diisocyanate (HDI), and 2,4,4-trimethylhexamethylene diisocyanate; and isocyanate prepolymers such as adducts of various diisocyanates, isocyanurates of various diisocyanates, biuretes of HDI, and allophanates of HDI. Among these, HDI, IPDI, XDI, or their adducts, isocyanurates, biuretes, and allophanates are preferred from the viewpoint of further improving the curl resistance of the coating film, HDI, IPDI, XDI, or their adducts are more preferred, HDI or adducts of HDI are even more preferred, and adducts of HDI are particularly preferred. Isocyanate-based curing agents may be used individually or in combination of two or more types.

[0058] Adduct compounds are a general term for isocyanate compounds with two or more functions, obtained by reacting a polyisocyanate having two or more isocyanate groups in one molecule (e.g., diisocyanate) with a low molecular weight active hydrogen-containing compound with two or more functions (e.g., low molecular weight triols such as trimethylolpropane and glycerin). Examples of adduct compounds include reaction products of HDI and trimethylolpropane (TMP), reaction products of XDI and TMP, and reaction products of IPDI and TMP.

[0059] <Other optional components> Other optional components include known additives. Examples of additives include binder resins other than urethane-modified (meth)acrylic resin (A) (hereinafter also referred to as "other binder resins"), defoamers, surfactants, anti-settling agents, UV absorbers, antioxidants, leveling agents, surface tension modifiers, rheology modifiers, light stabilizers, lubricants, dispersants, stabilizers, pH adjusters, fillers, antifungal agents, antistatic agents, metal nanoparticles, magnetic powders, etc. Other optional components may be used individually or in combination of two or more.

[0060] Other binder resins are not particularly limited, but examples include (meth)acrylic resins such as acrylic polyol resins, polyurethane resins, polyolefin resins, and polyester resins. Other binder resins may be used individually or in combination of two or more types.

[0061] The oil-based matte ink composition may contain colorants other than extender pigment (D), but it is preferable that it substantially omits them from the perspective of visibility. Furthermore, it is preferable that the oil-based matte ink composition contains substantially no water. In this specification, "substantially absent" means intentionally omitted.

[0062] <Content of each ingredient> The solid content of urethane-modified (meth)acrylic resin (A) is preferably 11 to 32% by mass, more preferably 13 to 28% by mass, and particularly preferably 15 to 25% by mass, relative to the total mass of the oil-based matte ink composition. The solid content of urethane-modified (meth)acrylic resin (A) is 28 to 53% by mass, preferably 32 to 50% by mass, and more preferably 35 to 45% by mass, relative to the total solid content of the oil-based matte ink composition. If the content of urethane-modified (meth)acrylic resin (A) is below the lower limit, the curl resistance, solvent resistance, abrasion resistance, adhesion to the substrate, and printability of the oil-based matte ink composition of the coating film will decrease. If the content of urethane-modified (meth)acrylic resin (A) exceeds the upper limit, the blocking resistance of the coating film will decrease.

[0063] The solid content of urethane-modified (meth)acrylic resin (A) is preferably 60% by mass or more, more preferably 70% by mass or more, and particularly preferably 80% by mass or more, relative to the total solid content of the binder resin. It may also be 100% by mass or less, 95% by mass or less, or 90% by mass or less. If the content of urethane-modified (meth)acrylic resin (A) is below the above lower limit, the ability to achieve both curl resistance, solvent resistance, and blocking resistance of the coating film will be impaired.

[0064] The silica (B) content, calculated on a solids basis, is preferably 0.1 to 15.0% by mass, more preferably 0.5 to 12.5% ​​by mass, and particularly preferably 1.0 to 10.0% by mass, relative to the total mass of the oil-based matte ink composition. The silica (B) content, calculated on a solids basis, is preferably 1.1 to 26.5% by mass, more preferably 1.5 to 23.0% by mass, and particularly preferably 2.0 to 20.0% by mass, relative to the total solids of the oil-based matte ink composition. If the silica (B) content is below the lower limit, the blocking resistance of the coating film will be slightly reduced. If the silica (B) content exceeds the upper limit, the curl resistance, solvent resistance, abrasion resistance, adhesion to the substrate, and printability of the oil-based matte ink composition will be slightly reduced.

[0065] The mass ratio of silica (B) / urethane-modified (meth)acrylic resin (A) in terms of solid content (hereinafter also referred to as the "B / A ratio") is 0.04 to 0.50, preferably 0.06 to 0.48, and more preferably 0.08 to 0.45. If the B / A ratio is below the lower limit, the blocking resistance of the coating film decreases. If the B / A ratio exceeds the upper limit, the curl resistance, solvent resistance, abrasion resistance, adhesion to the substrate, and printability of the oil-based matte ink composition of the coating film decrease.

[0066] The total content of urethane-modified (meth)acrylic resin (A) and silica (B) on a solid content basis (hereinafter also referred to as "A+B amount") is preferably 11.1 to 32.5% by mass, more preferably 12.5 to 27.5% by mass, and particularly preferably 15.0 to 25.0% by mass, relative to the total mass of the oil-based matte ink composition. The amount of A+B is preferably 29.1 to 70.0% by mass, more preferably 30.0 to 68.0% by mass, and particularly preferably 35.0 to 65.0% by mass, relative to the total solid content of the oil-based matte ink composition. If the A+B ratio is below the lower limit, the adhesion of the coating film to the substrate and the storage stability of the oil-based matte ink composition will be slightly reduced. If the A+B ratio exceeds the upper limit, the printability of the oil-based matte ink composition will be slightly reduced.

[0067] The content of organic solvent (C) is preferably 5.0 to 88.9% by mass, more preferably 10.0 to 80.0% by mass, and particularly preferably 20.0 to 70.0% by mass, based on the total mass of the oil-based matte ink composition. If the content of organic solvent (C) is below the lower limit, the fluidity and printability of the oil-based matte ink composition will be slightly reduced. If the content of organic solvent (C) exceeds the upper limit, the printability and storage stability of the oil-based matte ink composition will be slightly reduced.

[0068] The total amount of urethane-modified (meth)acrylic resin (A) and silica (B) on a solid content basis, plus the amount of organic solvent (C) (hereinafter also referred to as "A+B+C amount"), is preferably 50-100% by mass, more preferably 50-95% by mass, even more preferably 60-90% by mass, and particularly preferably 70-85% by mass, based on the total mass of the oil-based matte ink composition. If the amount of A+B+C is below the lower limit, the adhesion of the coating film to the substrate and the storage stability of the oil-based matte ink composition will be slightly reduced. If the amount of A+B+C exceeds the upper limit, the solvent resistance and abrasion resistance of the coating film will be slightly reduced.

[0069] When the oil-based matte ink composition contains an extender pigment (D), the content of the extender pigment (D) on a solid content basis is preferably 1.0 to 25.0% by mass, more preferably 2.5 to 22.5% by mass, and particularly preferably 5.0 to 20.0% by mass, based on the total mass of the oil-based matte ink composition. When the oil-based matte ink composition contains an extender pigment (D), the content of the extender pigment (D) on a solids basis is preferably 5 to 45% by mass, more preferably 10 to 40% by mass, and particularly preferably 20 to 36% by mass, relative to the total solids of the oil-based matte ink composition. If the content of extender pigment (D) is below the lower limit, the blocking resistance and heat resistance of the coating film will be slightly reduced. If the content of extender pigment (D) exceeds the upper limit, the adhesion of the coating film to the substrate, abrasion resistance, and printability of the oil-based matte ink composition will be slightly reduced.

[0070] When the oil-based matte ink composition contains hydrocarbon wax (E), the content of hydrocarbon wax (E) on a solid content basis is preferably 0.1 to 5.0% by mass, more preferably 0.2 to 3.0% by mass, and particularly preferably 0.4 to 2.0% by mass, based on the total mass of the oil-based matte ink composition. When an oil-based matte ink composition contains hydrocarbon wax (E), the content of hydrocarbon wax (E) on a solids basis is preferably 0.1 to 8.0% by mass, more preferably 0.5 to 5.0% by mass, and particularly preferably 1.0 to 3.0% by mass, relative to the total solids of the oil-based matte ink composition. If the hydrocarbon wax (E) content is below the lower limit, the abrasion resistance of the coating film will be slightly reduced. If the hydrocarbon wax (E) content exceeds the upper limit, the solvent resistance and blocking resistance of the coating film will be slightly reduced.

[0071] When the oil-based matte ink composition contains a curing agent (F), the content of the curing agent (F) on a solid content basis is preferably 0.5 to 20.0% by mass, more preferably 3.0 to 18.0% by mass, and particularly preferably 6.0 to 16.0% by mass, based on the total mass of the oil-based matte ink composition. When the oil-based matte ink composition contains a curing agent (F), the content of the curing agent (G) on a solids basis is preferably 10 to 40% by mass, more preferably 12 to 35% by mass, and particularly preferably 15 to 30% by mass, relative to the total solids of the oil-based matte ink composition. If the content of hardener (F) is below the lower limit, the solvent resistance and abrasion resistance of the coating film will be slightly reduced. If the content of hardener (F) exceeds the upper limit, the blocking resistance of the coating film will be slightly reduced.

[0072] The content of other optional components on a solids basis is not particularly limited as long as it does not impair the effects of the present invention, but for example, 0 to 20% by mass is preferred, 0 to 15% by mass is more preferred, and 0 to 10% by mass is particularly preferred, based on the total mass of the oil-based matte ink composition. If the oil-based matte ink composition contains other optional components, the content of these other optional components on a solids basis is preferably 0.01% by mass or more, more preferably 0.10% by mass or more, and particularly preferably 0.50% by mass or more, relative to the total mass of the oil-based matte ink composition. If the content of other optional components exceeds the above upper limit, the effects of the present invention may not be fully obtained.

[0073] <Manufacturing method> The oil-based matte ink composition of this embodiment can be obtained, for example, by mixing a urethane-modified (meth)acrylic resin (A), silica (B), an organic solvent (C), an extender pigment (D) if necessary, a hydrocarbon wax (E) if necessary, a curing agent (F) if necessary, and other optional components if necessary. The method of mixing each component is not particularly limited, and the components can be mixed by various methods. For example, one method is to dissolve or disperse urethane-modified (meth)acrylic resin (A), silica (B), optionally extender pigment (D), optionally hydrocarbon wax (E), optionally curing agent (F), and optionally other optional components in an organic solvent (C). In particular, it is preferable to add the curing agent (F) immediately before using the oil-based matte ink composition.

[0074] The method for dissolving or dispersing each component in the organic solvent (C) is not particularly limited and can be carried out using known dispersers. Examples of dispersers include paint shakers, dissolvers, ball mills, attritors, sand mills, bead mills, dyno mills, roll mills, ultrasonic mills, and high-pressure impact dispersers. In this case, the dispersion treatment may be performed once or multiple times using one type of disperser, or multiple dispersion treatments may be performed using two or more types of dispersers in combination.

[0075] <Effects and Effects> According to the oil-based matte ink composition of this embodiment described above, by containing the above-mentioned specific urethane-modified (meth)acrylic resin (A), silica (B), and organic solvent (C), and having a solid content of urethane-modified (meth)acrylic resin (A) of 28 to 53% by mass, and a B / A ratio of 0.04 to 0.50, it is possible to form a coating film that has excellent curl resistance, which prevents curling of printed materials even when printed on plastic films less than 10 μm thick, and also has excellent solvent resistance and blocking resistance.

[0076] <Application> The oil-based matte ink composition of this embodiment is suitable as a matte ink for printing on the surface of any substrate, such as a plastic film (or, if any layer, such as a pattern layer, is formed on the surface of the substrate, on the surface of this layer). In particular, it is suitable as a matte ink for printing on the surface of the substrate or the surface of the aforementioned layer by gravure printing. That is, the oil-based matte ink composition of this embodiment is especially suitable for gravure printing. The oil-based matte ink composition of this embodiment may be used as is as a matte ink, or a diluted solution obtained by diluting it with a medium such as an organic solvent may be used as a matte ink. The oil-based matte ink composition of this embodiment is printed on any substrate to form a matte ink layer. Hereinafter, the matte ink layer formed using the oil-based matte ink composition will also be referred to as the printed layer.

[0077] [Laminated structure] Figure 1 shows an example of a laminate according to one embodiment of the present invention. Note that the dimensional ratios in Figure 1 differ from those of the actual dimensions for the sake of explanation. The laminate 10 in Figure 1 is a printed material comprising a plastic film 11 which is a base material and a matte ink layer 12 printed on one surface of the plastic film 11.

[0078] <Plastic film> Examples of resins constituting the plastic film 11 include plastic films (base films) made of polyolefins (e.g., polyethylene (PE), milky polyethylene, polypropylene (PP), etc.), polyesters (e.g., polyethylene terephthalate (PET), etc.), polystyrene (PS), stretched polypropylene (OPP), polyamide (NY), etc.). These plastic films 11 may be used individually or two or more types may be laminated together.

[0079] The plastic film 11 may have a single-layer structure or a laminated structure. That is, the plastic film 11 may be a single-layer film or a laminated film. If the plastic film 11 is a laminated film, it may be a configuration in which two or more films of the same type are laminated together, or a configuration in which two or more films of different types are laminated together.

[0080] The plastic film 11 may or may not be subjected to corona treatment. The thickness of the plastic film 11 (or the thickness after lamination if two or more types are used together) is not particularly limited, but for example, when the laminate 10 is used as an industrial tape, it is preferably 25 μm or less, more preferably 15 μm or less, even more preferably 10 μm or less, and particularly preferably less than 10 μm. It may also be 1 μm or more, 3 μm or more, or 5 μm or more. The above upper and lower limits can be combined as appropriate. Furthermore, the thickness of the plastic film 11 may be 10 μm or more, for example, 10 to 50 μm.

[0081] <Matte ink layer> In the illustrated example laminate 10, the matte ink layer 12 is provided on one surface of the plastic film 11. The matte ink layer 12 is a layer formed using the oil-based matte ink composition of the present invention described above. The matte ink layer 12 may be a single layer or a laminated layer. The matte ink layer 12 provides the laminate with a matte appearance. The matte ink layer 12 also protects the plastic film 11 from external contact, such as human hands. The thickness of the matte ink layer 12 is not particularly limited and may be, for example, 0.1 to 1 μm. However, if the matte ink layer contains particles (for example, silica (B) particles, extender pigment (D) particles, hydrocarbon wax (E) particles, etc.) and some of the particles protrude above the surface of the matte ink layer, the thickness of the matte ink layer shall be the thickness of the portion where the particles do not protrude.

[0082] <Method for manufacturing laminates> The manufacturing method of the laminate 10 of this embodiment includes the step of forming a matte ink layer 12 on one surface of the plastic film 11 using the oil-based matte ink composition of the present invention. In the method for manufacturing the laminate 10 of the present invention, for example, the oil-based matte ink composition of the present invention is applied to one surface of a plastic film 11 to form a coating film to serve as a laminate precursor, and then the coating film is dried to form a matte ink layer 12. After drying the coating film to form the matte ink layer 12, the obtained matte ink layer 12 may be further aged. In particular, if the oil-based matte ink composition contains a curing agent (F), it is preferable to age the matte ink layer 12. Aging promotes the crosslinking reaction by the curing agent (F). The step of aging the matte ink layer 12 is also called the "aging step". Alternatively, the oil-based matte ink composition of the present invention may be applied to one surface of a plastic film 11, the resulting coating film may be dried to form a matte ink layer 12, and then the oil-based matte ink composition of the present invention may be applied again (overcoated), and the resulting coating film may be dried. This process may be repeated one or more times to form a laminated matte ink layer. When applying multiple coats of the oil-based matte ink composition of the present invention, the composition of each oil-based matte ink composition may be the same or different.

[0083] The method for forming the matte ink layer 12 may be a known printing method. For example, the matte ink layer 12 is formed by coating one surface of the plastic film 11 with the oil-based matte ink composition of the present invention and drying the coating film. The coating method may be any known coating method, such as gravure printing, flexographic printing, brush coating, gravure coater, die coater, bar coater, spray coating, flow coating, dip coating, spin coating, and curtain coating. Among these, gravure printing is preferred due to its superior quality and productivity.

[0084] The drying method for the coating film is not particularly limited as long as it removes the organic solvent (C) contained in the oil-based matte ink composition coated on one surface of the plastic film 11, and known drying methods can be used. For example, it may be air-dried, or it may be a forced drying method such as vacuum drying, pressure drying, heat drying, or air drying. When drying by heating, the drying temperature is preferably 30 to 70°C. The conditions for the aging process are not particularly limited, but for example, the aging temperature is preferably 30 to 70°C and the aging time is preferably 24 to 72 hours.

[0085] <Effects and Effects> The laminate of this embodiment described above has a matte ink layer formed using the oil-based matte ink composition of the present invention on one surface of a plastic film, and exhibits excellent curl resistance, solvent resistance, and blocking resistance. In addition, the laminate of this embodiment has a matte appearance and is aesthetically pleasing.

[0086] <Application> The laminate of this embodiment is suitable as an industrial tape. An example of an industrial tape is one that comprises the laminate of the present invention. Furthermore, the laminate of this embodiment can also be used as packaging material, such as a packaging label.

[0087] <Other Embodiments> The laminate is not limited to the embodiments described above. For example, as shown in Figure 2, the laminate 10 may further include a pattern layer 13 between the plastic film 11 and the matte ink layer 12. That is, the pattern layer 13 and the matte ink layer 12 may be formed in this order on one surface of the plastic film 11. Furthermore, as shown in Figure 3, for example, the laminate 10 may further include a pattern layer 13 on the other surface of the plastic film 11. That is, the pattern layer 13, the plastic film 11, and the matte ink layer 12 may be laminated in this order.

[0088] The pattern layer 13 is a printed layer typically formed using ink. The ink may be a known ink. The ink typically contains a pigment. The method for forming the pattern layer 13 may be a known printing method, similar to the method for forming the matte ink layer 12. The pattern layer 13 shown in FIG. 2 is provided on the entire one surface of the plastic film 11, but the pattern layer 13 may be provided on a part of the one surface of the plastic film 11. That is, a part of the one surface of the plastic film 11 may be exposed from the pattern layer 13. Also, the pattern layer 13 shown in FIG. 3 is provided on the entire other surface of the plastic film 11, but the pattern layer 13 may be provided on a part of the other surface of the plastic film 11. That is, a part of the other surface of the plastic film 11 may be exposed from the pattern layer 13.

Example

[0089] Hereinafter, the present invention will be described more specifically with reference to examples, but the present invention is not limited to the following examples as long as it does not exceed the gist thereof.

[0090] [Raw materials used] <Urethane-modified (meth)acrylic resin (A)> The following compounds were used as urethane-modified (meth)acrylic resin (A) or its comparative product. ·A-1: Urethane / (meth)acrylic ratio: 0.25, glass transition temperature of (meth)acrylic part: 75 °C, glass transition temperature of urethane part: -20 °C, overall glass transition temperature: 56 °C, hydroxyl value: 103 mgKOH / g, acid value: 1 mgKOH / g, SP value: 11.40 (cal / cm 3 ) 1 / 2 , (meth)acrylic part: methyl methacrylate-based, non-volatile content: 30% by mass. ·A-2: Urethane / (meth)acrylic ratio: 0.43, glass transition temperature of (meth)acrylic part: 82 °C, glass transition temperature of urethane part: 10 °C, overall glass transition temperature: 60 °C, hydroxyl value: 43 mgKOH / g, acid value: 6.3 mgKOH / g, SP value: 10.96 (cal / cm 3 ) 1 / 2 , (meth)acrylic part: methyl methacrylate-based, non-volatile content: 40% by mass. A-3: Urethane / (meth)acrylic ratio: 0.25, Glass transition temperature of (meth)acrylic portion: 75°C, Glass transition temperature of urethane portion: -30°C, Overall glass transition temperature: 54°C, Hydroxyl value: 103 mg KOH / g, Acid value: 0.77 mg KOH / g, SP value: 11.41 (cal / cm²) 3 ) 1 / 2 (Meth)acrylic part: methyl methacrylate type, non-volatile content: 29.5% by mass. · A-4: Urethane / (meth)acrylic ratio: 0.67, Glass transition temperature of (meth)acrylic portion: 60℃, Glass transition temperature of urethane portion: -10℃, Overall glass transition temperature: 32℃, Hydroxyl value: 35 mg KOH / g, Acid value: 6.9 mg KOH / g, SP value: 10.84 (cal / cm²) 3 ) 1 / 2 (Meth)acrylic part: methyl methacrylate type, non-volatile content: 30% by mass. · A-5: Urethane / (meth)acrylic ratio: 1.0, Glass transition temperature of (meth)acrylic part: 60°C, Glass transition temperature of urethane part: 40°C, Overall glass transition temperature: 50°C, Hydroxyl value: 0 mg KOH / g, Acid value: 7.5 mg KOH / g, (meth)acrylic part: Methyl methacrylate type, Non-volatile content: 41.5% by mass. A comparative product of urethane-modified (meth)acrylic resin (A). · A-6: Urethane / (meth)acrylic ratio: 0.43, Glass transition temperature of (meth)acrylic part: 30℃, Glass transition temperature of urethane part: -10℃, Overall glass transition temperature: 18℃, Hydroxyl value: 90 mg KOH / g, Acid value: 5.7 mg KOH / g, SP value: 11.26 (cal / cm²) 3 ) 1 / 2 (Meth)acrylic part: methyl methacrylate type, non-volatile content: 35.5% by mass. Comparative product of urethane-modified (meth)acrylic resin (A). A-7: Urethane / (meth)acrylic ratio: 0.82, (meth)acrylic part glass transition temperature: 105℃, hydroxyl value: 11mgKOH / g, acid value: 0.57mgKOH / g, (meth)acrylic part: methyl methacrylate type, non-volatile content: 35% by mass. A comparative product of urethane-modified (meth)acrylic resin (A).

[0091] <Other binder resins> The following compounds were used as other binder resins. • Acrylic polyol resin: Manufactured by Taisei Fine Chemical Co., Ltd., product name "Acrit 6AN-830D", hydroxyl value: 27.4 mg KOH / g, acid value: 1.0 mg KOH / g, glass transition temperature: 86.1℃, non-volatile content: 40% by mass. • Polyurethane resin: Manufactured by Sanyo Chemical Industries, Ltd., product name "Sunprene IB-1700D", hydroxyl value: 3.3 mg KOH / g, glass transition temperature: -45℃, non-volatile content: 30% by mass.

[0092] <Silica (B)> The following compounds were used as silica (B). • B-1: Manufactured by Tosoh Silica Co., Ltd., product name "Nipgel AZ200", average particle size: 4.2 μm, non-volatile content: 95% by mass, hydrophilic silica. • B-2: Manufactured by Fuji Silysia Chemical Co., Ltd., product name "Silysia 300", average particle size: 1.7 μm, non-volatile content: 100% by mass, hydrophilic silica. • B-3: Manufactured by Tosoh Silica Co., Ltd., product name "Nip Gel AY-603", average particle size: 10.8 μm, non-volatile content: 100% by mass, hydrophilic silica.

[0093] <Organic solvent (C)> The following compounds were used as the organic solvent (C). • C-1: A mixed solvent of methyl ethyl ketone and n-propyl acetate (methyl ethyl ketone: n-propyl acetate = 3:1 (mass ratio)).

[0094] <Extender pigment (D)> The following compounds were used as extender pigments (D). D-1: Calcium carbonate (manufactured by Shiraishi Calcium Co., Ltd., product name "Shiratsuka DD", average particle size: 0.1 μm, non-volatile content: 100% by mass). D-2: Precipitating barium sulfate (manufactured by Sakai Chemical Industry Co., Ltd., product name "Senbari 100", average particle size: 0.6 μm, non-volatile content: 100% by mass). D-3: Precipitating barium sulfate (manufactured by Sakai Chemical Industry Co., Ltd., product name "VariFine BF20", average particle size: 0.03 μm, non-volatile content: 100% by mass). D-4: Precipitating barium sulfate (manufactured by Sakai Chemical Industry Co., Ltd., product name "Senbari 200", average particle size: 0.8 μm, non-volatile content: 100% by mass).

[0095] <Hydrogen wax (E)> The following compounds were used as hydrocarbon wax (E). E-1: Polyolefin wax (manufactured by Mitsui Chemicals, Inc., product name "High Wax 220P", penetration: 13, non-volatile content: 100% by mass). E-2: Polyolefin wax (manufactured by Mitsui Chemicals, Inc., product name "High Wax 110P", penetration: 25, non-volatile content: 100% by mass).

[0096] <Hardening agent (F)> The following compounds were used as the curing agent (F). F-1: Isocyanate-based curing agent (manufactured by Mitsui Chemicals, Inc., product name "Takenate D-160N", non-volatile content: 75% by mass, TMP adduct of hexamethylene diisocyanate).

[0097] [Evaluation Method] <Evaluation of curl resistance> The laminate (after aging) was cut into pieces measuring 2.5 cm in width and 15 cm in length to prepare test specimens. The obtained test specimens were left standing for 1 hour in an environment of 25°C and 60% relative humidity. Then, the test specimens were placed on a flat surface with the curled side facing upwards, and the distance from the surface to the end of the curled test specimen (curl height) was measured. Curl tests were performed on three test specimens, the curl height was measured, and the average value was taken as the curl height. The curl resistance of the matte ink layer was evaluated according to the evaluation criteria shown below. A score of 3 to 5 is considered acceptable. 5: The curl height is 0 mm. 4: Curl height is greater than 0mm but less than or equal to 1mm. 3: The curl height is greater than 1 mm and less than or equal to 3 mm. 2: The curl height is greater than 3mm but less than or equal to 5mm. 1: The curl height exceeds 5mm.

[0098] <Evaluation of solvent resistance (isopropanol)> The laminate (after aging) was left to stand for 1 hour in an environment of 25°C and 60% relative humidity. After standing, the surface of the matte ink layer of the laminate was subjected to a friction test using a JSPS-type friction fastness tester (manufactured by Tester Sangyo Co., Ltd., product name "AB-301"), with a black cloth (No. 3) soaked in isopropanol (IPA) applied under a load of 500 gf and rubbed back and forth 30 times. After that, the appearance of the matte ink layer was visually inspected, and the solvent resistance (isopropanol) of the matte ink layer was evaluated according to the evaluation criteria shown below. A score of 3 to 5 is considered acceptable. 5: The area of ​​the matte ink layer that has been transferred to the black cloth (gold cloth No. 3) is 0% of the total area of ​​the matte ink layer. 4. The percentage of the matte ink layer area that has been transferred to the black cloth (gold cloth No. 3) is greater than 0% and less than or equal to 5% of the total area of ​​the matte ink layer. 3: The area of ​​the matte ink layer that has been transferred to the black cloth (gold cloth No. 3) is more than 5% and 10% or less of the total area of ​​the matte ink layer. 2: The proportion of the matte ink layer area that has been transferred to the black cloth (gold cloth No. 3) is more than 10% and 30% or less of the total area of ​​the matte ink layer. 1: The area of ​​the matte ink layer that has been transferred to the black cloth (gold cloth No. 3) exceeds 30% of the total area of ​​the matte ink layer.

[0099] <Evaluation of solvent resistance (ethyl acetate)> The laminate (after aging) was left to stand for 1 hour in an environment of 25°C and 60% relative humidity. After standing, the surface of the matte ink layer of the laminate was subjected to a friction test using a JSPS-type friction fastness tester (manufactured by Tester Sangyo Co., Ltd., product name "AB-301"), by rubbing it back and forth 30 times with a black cloth (No. 3) soaked in ethyl acetate (EtAc) under a load of 500 gf. After that, the appearance of the matte ink layer was visually inspected, and the solvent resistance (ethyl acetate) of the matte ink layer was evaluated according to the evaluation criteria shown below. A score of 3 to 5 is considered acceptable. 5: The area of ​​the matte ink layer that has been transferred to the black cloth (gold cloth No. 3) is 0% of the total area of ​​the matte ink layer. 4. The percentage of the matte ink layer area that has been transferred to the black cloth (gold cloth No. 3) is greater than 0% and less than or equal to 5% of the total area of ​​the matte ink layer. 3: The area of ​​the matte ink layer that has been transferred to the black cloth (gold cloth No. 3) is more than 5% and 10% or less of the total area of ​​the matte ink layer. 2: The proportion of the matte ink layer area that has been transferred to the black cloth (gold cloth No. 3) is more than 10% and 30% or less of the total area of ​​the matte ink layer. 1: The area of ​​the matte ink layer that has been transferred to the black cloth (gold cloth No. 3) exceeds 30% of the total area of ​​the matte ink layer.

[0100] <Evaluation of blocking resistance> Two laminate precursors were prepared. Two laminate precursors are stacked so that the coated surface (printed surface) of one laminate precursor is in contact with the coated surface (printed surface) of the other laminate precursor, and the load is 2 kg / cm². 2 The samples were subjected to a load and stored in a 40°C constant temperature chamber for 24 hours. Afterward, the two laminate precursors were separated, and the blocking resistance of the coating films was evaluated according to the evaluation criteria shown below. A score of 3 to 5 is considered acceptable. Note that "matt ink removal" below refers to the situation where, during separation, the coating film of one laminate precursor remains attached to the opposing surface (in this evaluation, the printed surface of the other laminate precursor) while the coating film of the other laminate precursor peels off the plastic film. 5: No matte ink is absorbed onto the printed surface. 4. Matte ink removal from the printed surface is greater than 0% and less than or equal to 10% of the total surface area of ​​the coating film. 3: The amount of matte ink removed from the printed surface is between 10% and 30% of the total surface area of ​​the coating film. 2: The amount of matte ink removed from the printed surface is between 30% and 50% of the total surface area of ​​the coating film. 1: The amount of matte ink removed from the printed surface exceeds 50% of the total surface area of ​​the coating film.

[0101] <Evaluation of printability> An oil-based matte ink composition was diluted with an organic solvent (C-1) to a viscosity of 17 seconds at 25°C, as measured using a Zahn cup #3, to prepare a matte ink for printing. The obtained matte ink was supplied to the ink pan of a 5-color gravure printing press (manufactured by Fuji Machinery Industry Co., Ltd.) equipped with a commercially available steel doctor blade and a plate with only non-image areas, and the plate was run idle for 30 minutes at a rate of 150 m / min. After that, streaky stains (doctor blade streaks) that appeared on the plate surface were visually inspected, and the printability of the oil-based matte ink composition was evaluated according to the evaluation criteria shown below. A score of 3 to 5 was considered acceptable. 5: No or very faint doctor's muscle was observed, or 1-2 very faint doctor's muscles were found. 4: Three to five thin muscle fibers were identified. 3: Six or more thin doctor's muscles, or one or two thick doctor's muscles were identified. 2: Three to five thick muscle fibers were observed. 1: More than six thick, defined muscle fibers were observed.

[0102] <Evaluation of abrasion resistance> The laminate (after aging) was left to stand for 1 hour in an environment of 25°C and 60% relative humidity. After standing, the surface of the matte ink layer of the laminate was subjected to a friction test using a JSPS-type friction fastness tester (manufactured by Tester Sangyo Co., Ltd., product name "AB-301"), with a black cloth (metal cloth No. 3) applied under a load of 500 gf and rubbed back and forth 200 times. After that, the appearance of the matte ink layer was visually inspected, and the friction resistance of the matte ink layer was evaluated according to the evaluation criteria shown below. A score of 3 to 5 is considered acceptable. 5: The area of ​​the matte ink layer that has been transferred to the black cloth (gold cloth No. 3) is 0% of the total area of ​​the matte ink layer. 4. The percentage of the matte ink layer area that has been transferred to the black cloth (gold cloth No. 3) is greater than 0% and less than or equal to 5% of the total area of ​​the matte ink layer. 3: The area of ​​the matte ink layer that has been transferred to the black cloth (gold cloth No. 3) is more than 5% and 10% or less of the total area of ​​the matte ink layer. 2: The proportion of the matte ink layer area that has been transferred to the black cloth (gold cloth No. 3) is more than 10% and 30% or less of the total area of ​​the matte ink layer. 1: The area of ​​the matte ink layer that has been transferred to the black cloth (gold cloth No. 3) exceeds 30% of the total area of ​​the matte ink layer.

[0103] [Examples 1-18, Comparative Examples 1-10] <Preparation of oil-based matte ink composition> According to the compositions shown in Tables 1-5, urethane-modified (meth)acrylic resin (A), other binder resins, silica (B), organic solvent (C), extender pigment (D), and hydrocarbon wax (E) were mixed to obtain a mixture. After mixing the obtained mixture in a paint shaker, if a curing agent (F) was to be added, the curing agent (F) was added and the mixture was further mixed in the paint shaker to obtain an oil-based matte ink composition. The hardening agent (F) was added immediately before preparing the matte ink for printing in the following step, <Laminate Preparation>.

[0104] <Fabrication of laminates> The prepared oil-based matte ink composition was diluted with an organic solvent (C-1) to a viscosity of 18 seconds at 25°C, as measured using a Zahn cup #3, to prepare a matte ink for printing. Using a gravure printing press (manufactured by Matsuo Sangyo Co., Ltd., product name "K Printing Proofer") equipped with a 150-line / inch (40 μm) gravure engraving plate, a prepared matte ink for printing was applied to one side of a PET film (manufactured by Toray Industries, Inc., product name "Lumirror #6C-F53", thickness: 6 μm) to obtain a laminate precursor with a coated film formed on the plastic film. Next, the laminate precursor was hot-air dried at 60°C for 1 minute, and then aged at 40°C for 48 hours to obtain a laminate (printed material) with a 3 μm thick matte ink layer formed on the plastic film. The printability was evaluated using an oil-based matte ink composition, blocking resistance was evaluated using a laminate precursor, and curl resistance, solvent resistance, and abrasion resistance were evaluated using the laminate (after aging). These results are shown in Tables 1 to 5.

[0105] [Examples 19, 20] <Preparation of oil-based matte ink composition> According to the composition shown in Table 3, a urethane-modified (meth)acrylic resin (A), another binder resin, silica (B), an organic solvent (C), an extender pigment (D), and a hydrocarbon wax (E) were mixed to obtain a mixture. The obtained mixture was kneaded in a paint shaker, and then a curing agent (F) was added and kneaded further in the paint shaker to obtain an oil-based matte ink composition. The hardening agent (F) was added immediately before preparing the matte ink for printing in the <Laminate Preparation> section described later.

[0106] <Preparation of Ink Composition> A mixture was obtained by mixing 22 parts by mass of urethane-modified (meth)acrylic resin (A-1) on a solid content basis, 18.5 parts by mass of carbon black (manufactured by Mitsubishi Chemical Corporation, product name "Mitsubishi Carbon Black MA100") on a solid content basis, 1 part by mass of hydrocarbon wax (E-1) on a solid content basis, 1 part by mass of dispersant (manufactured by Nippon Lubrizol Co., Ltd., product name "Solspers 20000") on a solid content basis, and an organic solvent (C-1). The obtained mixture was kneaded in a paint shaker, and then 11 parts by mass of hardener (F-1) on a solid content basis was added and kneaded further in a paint shaker to obtain an oil-based ink composition. The hardening agent (F-1) was added immediately before preparing the printing ink in the <Laminate Preparation> section described later. Furthermore, the amount of organic solvent (C-1) was adjusted so that the total amount (mass%) of all components contained in the oil-based ink composition equaled 100% by mass.

[0107] <Fabrication of laminates> The prepared oil-based matte ink composition was diluted with an organic solvent (C-1) to a viscosity of 18 seconds at 25°C, as measured using a Zahn cup #3, to prepare a matte ink for printing. Separately, an oil-based ink composition was prepared and diluted with an organic solvent (C-1) to a viscosity of 18 seconds at 25°C, as measured using a Zahn cup #3, to prepare a printing ink.

[0108] Using a gravure printing press (manufactured by Matsuo Sangyo Co., Ltd., product name "K Printing Proofer") equipped with a 150-line / inch (40μm) gravure engraving plate, the prepared printing ink was applied to one side of a PET film (manufactured by Toray Industries, Inc., product name "Lumirror #6C-F53", thickness: 6μm) as the plastic film. Then, after hot-air drying at 60°C for 1 minute, aging was performed at 40°C for 48 hours to form a 3μm thick pattern layer (ink layer) on the plastic film. Next, using a gravure printing press (manufactured by Matsuo Sangyo Co., Ltd., product name "K Printing Proofer") equipped with a 150-line / inch (40 μm) gravure engraving plate, the prepared matte ink for printing was applied to the image layer, obtaining a laminate precursor with a coated film formed on the image layer. Then, the laminate precursor was hot-air dried at 60°C for 1 minute, and then aged at 40°C for 48 hours to obtain a laminate (printed material) on which the image layer and a 3 μm thick matte ink layer were formed in that order on a plastic film. The printability was evaluated using an oil-based matte ink composition, blocking resistance was evaluated using a laminate precursor, and curl resistance, solvent resistance, and abrasion resistance were evaluated using the laminate (after aging). These results are shown in Table 3.

[0109] [Table 1]

[0110] [Table 2]

[0111] [Table 3]

[0112] [Table 4]

[0113] [Table 5]

[0114] The amounts of each component other than organic solvent (C) in Tables 1-5 are calculated on a solids basis. A blank space in Tables 1-5 indicates that the ingredient is not included (0% by mass). In Tables 1-5, "residue" refers to the amount of organic solvent (C) added, adjusted so that the total amount (mass%) of all components in the oil-based matte ink composition equals 100% by mass. In Tables 1-5, "F / M" refers to a layer configuration in which a matte ink layer is formed on one side of the plastic film, and "F / I / M" refers to a layer configuration in which a pattern layer (ink layer) and a matte ink layer are formed in that order on one side of the plastic film. In Tables 1-5, "Content of (A)" refers to the content of urethane-modified (meth)acrylic resin (A) on a solids basis relative to the total solids of the oil-based matte ink composition, rounded to two decimal places. The "B / A ratio" in Tables 1-5 represents the mass ratio on a solid content basis, expressed as silica (B) / urethane-modified (meth)acrylic resin (A), and is rounded to the fourth decimal place.

[0115] As is clear from the results in Tables 1-3, the oil-based matte ink compositions obtained in each example exhibited excellent printability. Furthermore, the coatings formed from these oil-based matte ink compositions exhibited excellent curl resistance, solvent resistance, blocking resistance, and abrasion resistance.

[0116] On the other hand, as is clear from the results in Tables 4 and 5, the coating film formed from the oil-based matte ink composition obtained in Comparative Example 1, which used a urethane-modified (meth)acrylic resin with a urethane / (meth)acrylic ratio of 1.0, had poor solvent resistance and blocking resistance. In Comparative Example 2, which used a urethane-modified (meth)acrylic resin with a glass transition temperature of 30°C in the (meth)acrylic portion, the coating film formed from the oil-based matte ink composition was poor in solvent resistance and blocking resistance. In Comparative Example 3, which used a urethane-modified (meth)acrylic resin with a glass transition temperature of 105°C in the (meth)acrylic portion, the coating film formed from the oil-based matte ink composition had poor curl resistance. In Comparative Example 4, where an acrylic polyol resin was used instead of a urethane-modified (meth)acrylic resin (A), the coating film formed from the oil-based matte ink composition exhibited poor curl resistance. In Comparative Example 5, where a polyurethane resin was used instead of a urethane-modified (meth)acrylic resin (A), the coating film formed from the oil-based matte ink composition exhibited poor solvent resistance and blocking resistance. The coating film formed from the oil-based matte ink composition obtained in Comparative Example 6, which contained 26.3% by mass of urethane-modified (meth)acrylic resin (A), exhibited poor solvent resistance. The coating film formed from the oil-based matte ink composition obtained in Comparative Example 7, which contained 54.8% by mass of urethane-modified (meth)acrylic resin (A), exhibited poor blocking resistance. The coating film formed from the oil-based matte ink composition obtained in Comparative Example 8, which had a B / A ratio of 0.027, exhibited poor blocking resistance. The coating film formed from the oil-based matte ink composition obtained in Comparative Example 9, which had a B / A ratio of 0.541, exhibited poor curl resistance and solvent resistance. The coating film formed from the oil-based matte ink composition obtained in Comparative Example 10, which did not contain silica (B), exhibited poor blocking resistance. [Industrial applicability]

[0117] The oil-based matte ink composition of the present invention has excellent curl resistance, which prevents curling of printed materials even when printed on plastic films less than 10 μm thick, and can form a coating film with excellent solvent resistance and blocking resistance, making it useful as a matte ink for industrial tapes. [Explanation of Symbols]

[0118] 10 Laminate 11 Plastic film 12 Matte ink layers 13 Image Layers

Claims

1. An oil-based matte ink composition containing a urethane-modified (meth)acrylic resin (A), silica (B), and an organic solvent (C), The urethane-modified (meth)acrylic resin (A) is a graft polymer having a (meth)acrylic portion as its main skeleton and a urethane portion as its side chains. In the urethane-modified (meth)acrylic resin (A), the mass ratio represented by the urethane portion / (meth)acrylic portion is 0.1 to 0.

9. The glass transition temperature of the (meth)acrylic portion constituting the urethane-modified (meth)acrylic resin (A) is 40 to 100°C. The content of the urethane-modified (meth)acrylic resin (A) on a solids basis is 28 to 53% by mass relative to the total solids of the oil-based matte ink composition. An oil-based matte ink composition having a mass ratio of 0.04 to 0.50 on a solid content basis, represented by the silica (B) and the urethane-modified (meth)acrylic resin (A).

2. The oil-based matte ink composition according to claim 1, wherein the mass ratio of the urethane portion to the (meth)acrylic portion in the urethane-modified (meth)acrylic resin (A) is 0.1 to 0.

5.

3. The oil-based matte ink composition according to claim 1, wherein the hydroxyl value of the urethane-modified (meth)acrylic resin (A) is 40 to 120 mgKOH / g or less.

4. The oil-based matte ink composition according to claim 1, wherein the average particle size of the silica (B) is 2 to 10 μm or less.

5. It further contains extender pigment (D), The extender pigment (D) comprises at least one of calcium carbonate and precipitated barium sulfate. The oil-based matte ink composition according to claim 1, wherein the average particle size of the extender pigment (D) is 0.05 to 0.70 μm.

6. It further contains hydrocarbon wax (E), The oil-based matte ink composition according to claim 1, wherein the penetration of the hydrocarbon wax (E) is 20 or less.

7. The oil-based matte ink composition according to claim 1, further comprising a curing agent (F).

8. An oil-based matte ink composition according to any one of claims 1 to 7, for use in gravure printing.

9. A laminate comprising a plastic film and a matte ink layer formed on one surface of the plastic film using the oil-based matte ink composition described in claim 8.

10. The laminate according to claim 9, further comprising a pattern layer between the plastic film and the matte ink layer, or on the other surface of the plastic film.

11. An industrial tape comprising the laminate described in claim 10.