Steel plates and containers for liquefied CO2

Abstract

This steel sheet is for liquefied CO2 transport tanks, has a prescribed chemical composition, and has an α value of 1.00-1.50 mass%, a β value of 10.00-15.00, a γ value of 0.70-1.50 mass%, a Ceq value of 0.550-0.620 mass%, a yield strength of 670-870 MPa, a tensile strength of 780-940 MPa, a thickness of 25-60 mm, an average hardness at the t / 4 position of 265 Hv-290 Hv with a standard deviation of 20 or less, and a maximum hardness HVmax in the central segregation area of 400 Hv or less. The segregation degree in the center of the plate thickness satisfies a prescribed range. Of inclusion particles found in a cross section in the sheet thickness direction, in rectangular regions with a side length of 4 mm, the rectangular regions each being centered at the t / 4 and t / 2 positions, the inclusion particles having a circular equivalent diameter of 0.5 μm or more and having Ti at 20 mass% or more, 99% or more of the inclusion particles by number have a circular equivalent diameter of 4.0 μm or less. The average crystal grain diameter at the center of the plate thickness is 15.0 μm or less.

Description

Technical Field

[0001] The present invention relates to steel plates, particularly steel plates for liquefied CO2 transport tanks and containers for liquefied CO2. This application claims priority based on Japanese Patent Application No. 2024-004182 filed in Japan on January 15, 2024, and incorporates its content herein.

Background Art

[0002] In recent years, as a measure to address climate change issues, strong demands have been made for reducing greenhouse gas emissions. In such a situation, CCS (Carbon dioxide Capture and Storage), a technology for recovering and storing carbon dioxide (hereinafter referred to as CO2), has attracted attention as a technology for achieving carbon neutrality. In CCS, CO2 emitted from CO2 emission sources such as oil refineries, power plants, and chemical plants is separated and recovered, and then injected and stored in a deep underground storage layer. When the recovery facility for separating and recovering CO2 and the storage facility for injecting and storing CO2 into the underground storage layer are spatially separated, it is necessary to transport the separated and recovered CO2 between these facilities by pipelines, ships, etc.

[0003] When transporting CO2 by ship, the liquefied CO2 is filled into a transport tank installed on the ship for transportation. This improves the transportation efficiency of CO2. However, in order to prevent solidification (solid carbon dioxide formation) of CO2 in the transport tank, it is necessary to transport it while maintaining a pressure of about 2 MPa. Also, in order to maintain CO2 in a liquid state at a pressure of about 2 MPa, it is necessary to keep CO2 at about -35°C. Furthermore, there is a desire to make the wall thickness of the transport tank as thin as possible in order to reduce the weight of the ship.

[0004] Therefore, the steel plate used as the material for the transport tank is required to have a tensile strength of 780 MPa or more and excellent low-temperature toughness at -65°C.

[0005] Furthermore, in order to ensure the safety of welded structures such as transport tanks, fracture mechanics evaluation methods are now being used to assess the fracture resistance characteristics of welded structures and incorporate them into the design. Specifically, as a characteristic of brittle fracture, the CTOD test (Crack Tip Opening Displacement test), specified by standards such as the Japan Welding Society standard WES1108, is used to determine the amount of crack opening displacement called the CTOD value (hereinafter abbreviated as δc) as a fracture mechanics parameter, and it is increasingly common to evaluate whether δc satisfies the design criteria.

[0006] To improve the δc of a material, it is necessary to improve the material's properties from a different perspective than before. Traditionally, the Charpy impact test has been used to evaluate the brittle fracture resistance of materials. The value obtained from the Charpy impact test represents the average toughness of the area being evaluated. However, in the CTOD test, even if the average toughness of the area being evaluated is good, if there is even a small brittle area within the area being evaluated, its presence will be reflected in the δc. Because δc has this property, in order to obtain a high δc value, especially in areas where the microstructure of the steel changes unevenly and complexly, such as the heat-affected zone of welding, it is necessary to minimize localized brittle regions as much as possible.

[0007] Furthermore, in large welded structures such as transport tanks, stress relief annealing is sometimes performed on the welded joint to further reduce the possibility of failure. Stress relief annealing is a heat treatment method that aims to reduce residual stress caused by welding by heating the welded joint of a structure to a temperature below the Ac1 transformation point and then slowly cooling it. However, when stress relief annealing is applied to high-tensile steel with a tensile strength of 780 MPa or higher, alloy carbides selectively precipitate at the grain boundaries, and these alloy carbides cause grain boundary embrittlement, resulting in a significant decrease in toughness at the stress relief annealed area. This phenomenon is generally called SR (Stress Relieving) embrittlement. In particular, SR embrittlement tends to occur strongly in high-tensile steel that contains B and is manufactured by quenching and tempering. In such high-tensile steel, not only is the base material embrittlement significant, but the heat-affected zone obtained when a welded joint is made using this high-tensile steel is also significantly embrittlement.

[0008] Therefore, in order to obtain a high δc value and ensure high safety in transport tanks manufactured using such high-tensile steel, it is necessary to develop high-tensile steel that maintains high toughness of the base material even when stress relief annealing is performed.

[0009] From the above perspective, several technical proposals have been made in the past. For example, Patent Document 1 describes a high-strength steel sheet characterized by adjusting the chemical composition and reducing the average grain size to 15 μm or less. However, the low-temperature toughness of the steel sheet described in Patent Document 1 has not been evaluated at -65°C, and there is room for further improvement in low-temperature toughness. [Prior art documents] [Patent Documents]

[0010] [Patent Document 1] Japanese Patent No. 5590271 [Overview of the Initiative] [Problems that the invention aims to solve]

[0011] The present invention has been made in view of the above circumstances, and aims to provide a steel plate for a liquefied CO2 transport tank and a container for liquefied CO2 including the steel plate, which is excellent in strength, low-temperature toughness and low-temperature toughness after stress relief annealing, and also in low-temperature toughness before and after stress relief annealing when used as a welded joint. [Means for solving the problem]

[0012] To solve the above problems, the present invention adopts the following configuration. [1] A steel sheet according to one embodiment of the present invention is a steel sheet for a liquefied CO2 transport tank, and its chemical composition is, in mass%, C: 0.070~0.110%, Si: 0.10~0.15%, Mn: 0.70~1.20%, Ni: 1.00~2.50%, Cr: 0.20~0.80%, Mo: 0.20~0.80%, V: 0.005~0.070%, Al: 0.030~0.100%, B: 0.0005~0.0030%, N: 0.0015~0.0050%, P: 0.006% or less, S The composition is as follows: 0.0030% or less, Cu: 0~1.00%, Nb: 0~0.030%, Ti: 0~0.010%, Ca: 0~0.0030%, Mg: 0~0.0030%, REM: 0~0.0030%, O: 0.0040% or less, remainder: Fe and impurities, the α value defined by the following formula (1) is 1.00~1.50 mass%, the β value defined by the following formula (2) is 10.00~15.00, the γ value defined by the following formula (3) is 0.70~1.50 mass%, the Ceq defined by the following formula (4) is 0.550~0.620 mass%, the yield strength is 670~870 MPa, the tensile strength is 780~940 MPa, and when the plate thickness is t, the t is 25~60 mm. At the t / 4 position of the cross-section in the thickness direction of the plate, the martensitic structure and the lower bainite structure together account for 85.0 area or more.In hardness distribution measurements at the t / 4 position, with dimensions of 0.5 mm × 0.5 mm and a pitch of 0.05 mm, the average hardness at 121 measurement points was 265 Hv to 290 Hv, with a standard deviation of 20 or less, the maximum hardness HVmax of the central segregation was 400 HV or less, the degree of segregation at the center of the plate thickness satisfied all of the following equations (5) to (8), and the equivalent diameter of the circle in the cross-section in the thickness direction, in a rectangular region with sides of 4 mm centered at the t / 4 position and t / 2 position respectively, was 0.5 μm or more, and the material contained 20 mass% or more of Ti. In this case, 99% or more of the inclusion particles have an equivalent circular diameter of 4.0 μm or less. A region surrounded by grain boundaries with a crystal orientation difference of 15° or more, as determined by crystal orientation analysis using electron beam backscatter diffraction pattern analysis, is defined as a crystal grain. The equivalent circular grain size of the said crystal grain is defined as the crystal grain size. When the value calculated by area-weighted average, weighted by the area of ​​each crystal grain, is defined as the average crystal grain size, the average crystal grain size at the center of the thickness of the steel plate is 15.0 μm or less. α=[C]+6×[Si]+100×[P] …(1) β = 0.65 × [C] 1 / 2 ×(1+0.64×[Si])×(1+4.10×[Mn])×(1+0.27×[Cu])×(1+0.52×[Ni])×(1+2.33×[Cr])×(1+3.14×[Mo]) …(2) γ=[Mn]+20×[Nb]+36×[Ti]…(3) Ceq=[C]+[Mn] / 6+([Cu]+[Ni]) / 15+([Cr]+[Mo]+[V]) / 5 …(4) [Si]max / [Si]≦1.9 …(5) [P]max / [P]≦20.0 …(6) [Cu]max / [Cu]≦2.5 …(7) [Ni]max / [Ni]≦2.0 …(8) Here, in equations (1) to (8), [C], [Si], [P], [Mn], [Cu], [Ni], [Cr], [Mo], [Nb], [Ti], and [V] represent the mass %) content of C, Si, P, Mn, Cu, Ni, Cr, Mo, Nb, Ti, and V, respectively, including the amount of elements mixed in as impurities. Substitute 0 for elements that are not present. Furthermore, in equations (5) to (8), [Si]max, [P]max, [Cu]max, and [Ni]max are the average concentration values ​​of each element within the tertiary region, which is selected from a primary region of the cross-section of the steel sheet in the thickness direction, centered at the t / 2 position and extending ±5 mm in the thickness direction and 10 mm in the rolling direction. This secondary region is then selected from the secondary region as the region where the concentration of each element is maximized, based on the EPMA line analysis results for each element. Finally, a tertiary region is selected from the secondary region as the region where the concentration of each element is maximized, based on the EPMA surface analysis results for each element. The tertiary region is defined as the central segregation region. [2] The steel plate in [1] above may have a fB of 0.0003% or more, which can be determined by the following equations (A) to (E). [fB] = [B] - 0.77 × [fN] …(A) [fN]=[N]-0.29×[fTi]-0.52×[fAl] …(B) [fTi] = [Ti] - 2 × [fO] …(C) [fAl] = [Al] - 1.125 × [fO] …(D) [fO]=[O]-0.4×[Ca]-0.66×[Mg]-0.11×[REM] …(E) Here, in equations (A) to (E), [B], [N], [Ti], [Al], [O], [Ca], [Mg], and [REM] represent the content (mass%) of B, N, Ti, Al, O, Ca, Mg, and REM, respectively. This includes the amount of elements mixed in as impurities. Elements that are not present are substituted with 0, and if the calculated value of [fN], [fTi], [fAl], or [fO] is less than 0%, 0 is substituted. [3] When the steel plate described in [1] or [2] above is subjected to stress relief annealing in which the holding temperature is in the range of 600 to 620°C, the holding time is in the range of 2.0 to 2.8 hours, and the cooling rate is in the range of 55 to 100°C / h in the temperature range of 425°C or higher, the yield strength of the area where the stress relief annealing was performed is 670 to 870 MPa, the tensile strength is 780 to 940 MPa, and the Charpy absorption energy at -45°C is 40 J or more. [4] The container for liquefied CO2 according to another aspect of the present invention includes the steel plate described in any one of [1] to [3].

Advantages of the Invention

[0013] According to the above aspect of the present invention, there can be provided a steel plate for a liquefied CO2 transport tank that is excellent in the strength and low-temperature toughness of the steel plate and the low-temperature toughness after stress relief annealing, and is also excellent in the low-temperature toughness after stress relief annealing when used as a welded joint, and a container for liquefied CO2.

Brief Description of the Drawings

[0014] [Figure 1] It is an explanatory diagram of a state where a sample for metallographic observation is processed at a position including the center of the plate thickness (t / 2 position). [Figure 2] It is an explanatory diagram of a state where a portion with the highest average Mn concentration is specified centered on the t / 2 position, and a 1 mm × 1 mm visual field area (secondary area) is specified. [Figure 3] In a 1 mm × 1 mm square visual field area (secondary area), a 20 × 20 μm square portion is scanned in the vertical and horizontal directions (rolling direction and plate thickness direction), and the average value of each region is determined from the mass percentages of Si, P, Cu, and Ni at the measurement points included in the region of the square portion at each position. It is an explanatory diagram of the state. [Figure 4] It is an explanatory diagram exemplifying the regions (tertiary regions) of the square portions where the average values of Si, P, Cu, and Ni are the maximum values. [Figure 5] It is a diagram showing an example of a tissue photograph revealed by nital etching and observed with an optical microscope.

Embodiments for Carrying Out the Invention

[0015] Hereinafter, the steel plate according to an embodiment of the present invention (the steel plate according to this embodiment) and the container for liquefied CO2 according to this embodiment will be described in detail. In this embodiment, "stress relief annealing" means stress relief annealing in accordance with the provisions of JIS Z 3700:2009 "Post-weld heat treatment methods" unless otherwise specified. In this embodiment, "welding" refers to welding with a welding heat input of 1.1 to 4.5 kJ / mm unless otherwise specified. These conditions are general conditions in the technical field to which this invention belongs. However, even if stress relief annealing or welding is performed under conditions different from those described above, the same effect as stress relief annealing or welding performed under the above conditions can be obtained. Therefore, stress relief annealing or welding may be performed on the steel plate according to this embodiment under conditions different from those described above. In this embodiment, when the thickness of the steel plate is denoted as t, the position at half the thickness from the surface in the thickness direction (t / 2 position) is described as the t / 2 position, and the position at one-quarter the thickness from the surface in the thickness direction (t / 4 position) is described as the t / 4 position.

[0016] <Steel plate> First, the range of elemental content constituting the chemical composition of the steel sheet according to this embodiment and the reasons for its limitation will be described. Hereafter, unless otherwise specified, "%" refers to mass percent.

[0017] (C: 0.070~0.110%) Carbon (C) is an element that improves the strength of the base material. In order for the steel sheet according to this embodiment to achieve the desired strength, the carbon content is set to 0.070% or more. Preferably, the carbon content is 0.080% or more. On the other hand, if a large amount of carbon is included, the hardness of the heat-affected zone during welding increases while its toughness decreases, so the carbon content is set to 0.110% or less. Preferably, the carbon content is 0.100% or less, and more preferably less than 0.100%.

[0018] (Si: 0.10~0.15%) Si is generally often included in steel as a deoxidizing element. However, in this embodiment, Si is an element that reduces the toughness of steel after stress relief annealing. Therefore, the Si content is set to 0.15% or less. Preferably, the Si content is 0.14% or less, 0.13% or less, or 0.12% or less. Furthermore, a lower Si content is preferable in order to suppress the reduction in toughness of the heat-affected zone after stress relief annealing. On the other hand, in order to include Si for the purpose of deoxidation, the Si content should be 0.10% or more.

[0019] (Mn: 0.70~1.20%) Mn is an effective element for deoxidation and also improves the strength of steel. Therefore, the Mn content should be 0.70% or more. Preferably, the Mn content should be 0.90% or more. On the other hand, excessive Mn content may impair the toughness of the steel after stress relief annealing due to tempering embrittlement. Therefore, the Mn content should be 1.20% or less. Preferably, the Mn content should be 1.10% or less.

[0020] (Ni: 1.00~2.50%) Ni is an effective element for improving the hardenability and toughness of steel. Therefore, the Ni content should be 1.00% or more. Preferably, the Ni content should be 1.20% or more. On the other hand, excessive Ni content may reduce the toughness of the steel after stress relief annealing. Furthermore, it may worsen the toughness of the heat-affected zone after stress relief annealing. Therefore, the Ni content should be 2.50% or less. Preferably, the Ni content should be 2.00% or less.

[0021] (Cr: 0.20~0.80%) Cr is an effective element for improving the hardenability of steel and for improving the strength of steel through precipitation strengthening during tempering. Therefore, the Cr content should be 0.20% or more. Preferably, the Cr content should be 0.40% or more. On the other hand, excessive chromium content may reduce the toughness of the base material and the heat-affected zone of the weld after stress relief annealing. Therefore, the chromium content should be 0.80% or less. Preferably, the chromium content should be 0.70% or less.

[0022] (Mo: 0.20~0.80%) Mo, like Cr, is an effective element for improving hardenability and steel strength through precipitation strengthening during tempering. Therefore, the Mo content should be 0.20% or more. Preferably, the Mo content should be 0.30% or more, more preferably 0.35% or more, and even more preferably 0.40% or more. On the other hand, if the Mo content is excessive, there is a risk that Mo carbides will precipitate at the grain boundaries after stress relief annealing, reducing the toughness of the base material and the heat-affected zone of the weld. The effect on the heat-affected zone of the weld is particularly significant. Therefore, the Mo content should be 0.80% or less. Preferably, the Mo content should be 0.60% or less.

[0023] (V: 0.005~0.070%) V, like Cr and Mo, is an effective element for improving hardenability and steel strength through precipitation strengthening during tempering. Therefore, the V content should be 0.005% or more. Preferably, the V content should be 0.010% or more. On the other hand, if V is included in excess, there is a risk that the toughness of the base material and the toughness of the heat-affected zone of the weld will decrease after stress relief annealing. Therefore, the V content should be 0.070% or less. Preferably, the V content should be 0.050% or less.

[0024] (Al: 0.030~0.100%) Al is an element useful for deoxidation and also refines the grain size during quenching by forming nitrides. In the steel sheet according to this embodiment, the Al content is 0.030% or more. Preferably, the Al content is 0.040% or more. On the other hand, if Al is included in excess, the Al may form coarse nitrides, which may reduce the toughness of the base material and the heat-affected zone of the weld. Therefore, the Al content should be 0.100% or less. Preferably, the Al content should be 0.080% or less.

[0025] (B: 0.0005~0.0030%) In this embodiment, B is an element that improves the hardenability of steel when included in trace amounts. Therefore, the B content is set to 0.0005% or more. The B content may also be 0.0006% or more, 0.0008% or more, or 0.0010% or more. On the other hand, if B is included in excess, the B may form coarse nitrides and / or carbides, which can reduce the toughness of the base material. Therefore, the B content should be 0.0030% or less. The B content may also be 0.0020% or less or 0.0010% or less.

[0026] (N: 0.0015~0.0050%) N is an element that forms nitrides, which refines the grain size of the base material and improves its toughness. Therefore, the N content should be 0.0015% or more. The N content may also be 0.0030% or more, or 0.0035% or more. On the other hand, excessive nitrogen content leads to coarsening of the nitride, reducing the toughness of the heat-affected zone in the as-welded state. Therefore, the nitrogen content should be kept below 0.0050%.

[0027] (P:0.006% or less) (S:0.0030% or less) P and S are impurity elements contained in steel, and it is preferable that their content be as low as possible. For this reason, the lower limit for P and S content is 0%. If the P content exceeds 0.006% or the S content exceeds 0.0030%, the adverse effect on toughness becomes significant. Therefore, in this embodiment, in order to improve the toughness of the welded joint after stress relief annealing, the P content is set to 0.006% or less and the S content is set to 0.0030% or less. The P content is preferably 0.005% or less. If necessary, the S content may also be set to 0.0020% or less.

[0028] (Cu: 0~1.00%) Since Cu is not an essential element in this embodiment, the lower limit of the Cu content is 0%. However, since Cu has the effect of improving the strength of steel, it can be included as needed. When Cu is included, it is preferable to have a Cu content of 0.10% or more, and may be 0.20% or more, in order to utilize its effect. If necessary, the Cu content may be 0.15% or more or 0.30% or more. On the other hand, excessive copper content may lead to cracking on the steel sheet surface and copper precipitation, potentially reducing the toughness of the base material. Therefore, the copper content should be 1.00% or less. Preferably, the copper content should be 0.80% or less. If necessary, the upper limit of the copper content may be set to 0.70%, 0.60%, 0.50%, or 0.40% or less.

[0029] (Nb: 0~0.030%) Since Nb is not an essential element in this embodiment, the lower limit of the Nb content is 0%. However, since Nb is an element that refines the crystal grains during quenching, it can be included as needed. When including Nb, it is preferable to include 0.001% or more Nb in order to utilize its effect. On the other hand, if Nb is included in excess, the Nb may form coarse carbonitrides, which may reduce the toughness of the base material. Therefore, the Nb content should be 0.030% or less. Since a lower Nb content improves the toughness of the heat-affected zone of the weld, the Nb content may also be 0.020% or less, 0.010% or less, or 0.005% or less.

[0030] (Ti: 0~0.010%) Since Ti is not an essential element in this embodiment, the lower limit of the Ti content is 0%. However, Ti can be included as needed because it can refine the crystal grains when the steel is heated to high temperatures, such as during slab heating. When Ti is included, it is preferable to have a Ti content of 0.001% or more in order to utilize its effect. On the other hand, if the Ti content is excessive, similar to Nb, the Ti may form coarse carbonitrides, potentially reducing the toughness of the base material. Therefore, the Ti content should be 0.010% or less. If necessary, the Ti content may be 0.005% or less or 0.002% or less.

[0031] (Ca: 0~0.0030%) (Mg: 0~0.0030%) (REM: 0~0.0030%) The steel sheet according to this embodiment may contain one or more of Ca, Mg, and REM. Since Ca, Mg, and REM are not essential elements, the lower limit of the Ca, Mg, and REM content is 0% for all of them.

[0032] Ca is an element that reduces the effect of MnS, which lowers the toughness of steel sheets, by spheroidizing sulfides in the steel sheets. To obtain this effect, the Ca content may be set to 0.0001% or more. On the other hand, if a large amount of Ca is included, the weldability of the steel may be impaired, so the Ca content should be 0.0030% or less. If necessary, the Ca content may be 0.0015% or less, 0.0010% or less, 0.0005% or less, or 0.0002% or less.

[0033] Mg and REM are elements that form oxides and improve the toughness of the heat-affected zone during welding. To obtain this effect, the Mg content and REM content may be set to 0.0001% or more, respectively. On the other hand, if large amounts of Mg and REM are included, coarse oxides may form, potentially reducing the toughness of the steel. Therefore, the Mg content and REM content should be 0.0030% or less, respectively. If necessary, the Mg content and REM content may be 0.015% or less, 0.010% or less, 0.005% or less, or 0.002% or less, or less than 0.0015%, respectively. REM is a general term for rare earth metals including Sc, Y, La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Tb, and Lu. Compared to other additive elements, it is characterized by its strong deoxidizing properties and forms stable oxides in steel.

[0034] (O:0.0040% or less) Oxygen (O) is an impurity element contained in steel, and in steel, it often forms oxides with a size of several μm to tens of μm together with elements that have strong deoxidizing power, such as Ca, Mg, REM, Al, and Ti. When coarse oxides are present or when the number density of oxides is high, the oxides can become the starting point for brittle fracture. Therefore, a lower O content is preferable. Accordingly, the lower limit of the O content is 0%. In this embodiment, in order to improve the toughness of the welded joint, the O content is set to 0.0040% or less. Preferably, the O content is set to 0.0030% or less.

[0035] (Remainder: Fe and impurities) The steel sheet according to this embodiment consists of the above-mentioned components, with the remainder being Fe and impurities. Here, impurities refer to components that are mixed in during the industrial manufacture of steel sheets due to raw materials such as ore or scrap, or various factors in the manufacturing process, and are acceptable within a range that does not adversely affect the present invention.

[0036] The content of each element can be measured by the following method. For elements such as C, Si, Mn, P, S, Nb, V, Ni, Cu, Cr, Mo, Ti, Al, Ca, B, Mg, and REM, inductively coupled plasma atomic emission spectrometry (ICP-OES) using an ICP emission spectrometer is applicable. For trace amounts of S, O, and N (on the ppm order), infrared absorption spectrometry or thermal conductivity methods using CS analyzers, ON analyzers, etc., can be applied. If necessary, other analytical methods such as inductively coupled plasma mass spectrometry (ICP-MS) and atomic absorption spectrometry (AAS) may also be applied. Since the chemical composition of the steel sheet according to this embodiment hardly changes during the manufacturing process, if the chemical composition measured by a sample taken from the molten steel in the tundish during the steelmaking stage is known, that chemical composition may be considered as the chemical composition of the steel sheet according to this embodiment.

[0037] Furthermore, in addition to satisfying the above chemical composition, it is preferable that the steel sheet according to this embodiment has a [fB] of 0.0003% or more, which can be determined by the following equations (A) to (E). [fB] represents the amount of B dissolved in the steel. By setting [fB] to 0.0003% or more, the hardenability of the steel can be improved in high-tensile steel with a yield strength of 670 to 870 MPa and a tensile strength of 780 to 940 MPa. B readily forms nitrides in steel. Also, Ti and Al readily form nitrides and oxides. Therefore, the amount of B dissolved in the steel [fB] is determined by the following equations (A) to (E). [fB] may be 0.0005% or more, or 0.0015% or more. Also, [fB] may be 0.0025% or less, or 0.0018% or less.

[0038] [fB] = [B] - 0.77 × [fN] …(A) [fN]=[N]-0.29×[fTi]-0.52×[fAl] …(B) [fTi] = [Ti] - 2 × [fO] …(C) [fAl] = [Al] - 1.125 × [fO] …(D) [fO]=[O]-0.4×[Ca]-0.66×[Mg]-0.11×[REM] …(E)

[0039] Here, in equations (A) to (E), [B], [N], [Ti], [Al], [O], [Ca], [Mg], and [REM] represent the content (mass %) of B, N, Ti, Al, O, Ca, Mg, and REM, respectively, including the amount of elements mixed in as impurities. Elements that are not present are substituted with 0. Also, if the calculated value of [fN], [fTi], [fAl], or [fO] is less than 0%, 0 is substituted.

[0040] Furthermore, in the steel sheet according to this embodiment, in addition to the limitations on the chemical composition (content of individual elements) described above, the ranges of the α, β, and γ values ​​are limited as follows (the content of individual elements is limited so that the α, β, and γ values ​​fall within predetermined ranges).

[0041] (α value: 1.00~1.50 mass%) The alpha value is given by the following equation (1).

[0042] α=[C]+6×[Si]+100×[P] …(1) Here, in equation (1), [C], [Si], and [P] represent the mass percentage of C, Si, and P contained in the steel, including the amount of elements mixed in as impurities, and 0 is substituted for elements that are not present.

[0043] In this embodiment, the α value is set to 1.50 mass% or less. This is a necessary condition to improve the toughness of the coarse-grained portion of the heat-affected zone after stress relief annealing, and C, Si, and P must be adjusted within this range. After stress relief annealing, the concentration of P at grain boundaries increases, making brittle fracture at grain boundaries more likely, but brittle fracture can be controlled by P, C, and Si. P is inevitably included in the steel due to the process, and because it significantly reduces grain boundary strength due to grain boundary segregation, it is a representative element that causes SR embrittlement, and has the highest coefficient. C and Si are also elements that are inevitably included in the steel, and if these elements are present in large amounts, it leads to embrittlement due to cementite formation at grain boundaries. It is desirable to reduce all of these elements, but a certain amount may be included for property reasons or specifications. If necessary, the α value may be set to 1.40 mass% or less in order to improve the toughness after stress relief annealing. On the other hand, the α value is 1.00 mass% or higher. This lower limit (1.00 mass%) is determined by the component constraints in the standards of the application field and the limits of elemental control in manufacturing, and is calculated by substituting the lower limits of the C, Si, and P content and the practical minimum values ​​in manufacturing into equation (1). The preferred lower limit of the α value can be calculated from the preferred lower limits of the C, Si, and P content. The α value may be greater than 1.10 mass% or greater than 1.30 mass%.

[0044] (β value: 10.00~15.00) The β value is calculated using the following equation (2).

[0045] β = 0.65 × [C] 1 / 2×(1+0.64×[Si])×(1+4.10×[Mn])×(1+0.27×[Cu])×(1+0.52×[Ni])×(1+2.33×[Cr])×(1+3.14×[Mo]) …(2) Here, in equation (2), [C], [Si], [Mn], [Cu], [Ni], [Cr], and [Mo] represent the mass %) content of C, Si, Mn, Cu, Ni, Cr, and Mo in the steel, including the amount of elements mixed in as impurities. Substitute 0 for elements that are not present.

[0046] In the steel sheet according to this embodiment, the β value is set to a range of 10.00 to 15.00. The β value is an indicator of the hardenability of the steel sheet, and the higher the β value, the more reliably the formation of the upper bainite structure, which has an inferior balance of strength and toughness, can be avoided. On the other hand, if the β value is too high, the strength of the steel sheet increases, leading to a deterioration of toughness. In other words, it also serves as an indicator of the target range of alloying element content necessary to improve the toughness of the as-welded heat-affected zone. If necessary, the beta value may be set to 11.00 or higher. Alternatively, the beta value may be set to 14.00 or lower.

[0047] (γ value: 0.70~1.50 mass%) The gamma value is calculated using the following equation (3).

[0048] γ=[Mn]+20×[Nb]+36×[Ti]…(3) Here, in equation (3), [Mn], [Nb], and [Ti] represent the mass percentage of Mn, Nb, and Ti contained in the steel, including the amount of elements mixed in as impurities. Substitute 0 for elements that are not present.

[0049] In the steel sheet according to this embodiment, the γ value is set to a range of 0.70 to 1.50 mass%. Mn, Nb, and Ti are all elements that promote grain boundary embrittlement after stress relief annealing, and by setting the γ value to 1.50 mass% or less, the decrease in toughness after stress relief annealing can be suppressed. Several mechanisms can be considered for how these elements promote grain boundary embrittlement, but possible mechanisms include a decrease in grain boundary strength due to grain boundary segregation and embrittlement due to carbonitrides formed at the grain boundaries. On the other hand, in order to ensure a certain degree of hardenability and obtain a microstructure with a superior balance of strength and toughness, it is preferable to include a certain amount of Mn, Nb, and Ti, with a γ value of 0.70 mass% or more. The γ value may also be 0.75 mass% or more, or 1.40 mass% or less.

[0050] By satisfying the numerical ranges for α, β, and γ values, it is possible to provide steel with excellent low-temperature toughness of the welded joint both in the as-welded state and after stress-relieving annealing.

[0051] Furthermore, in the steel sheet according to this embodiment, the carbon equivalent Ceq, which is an index indicating the hardening properties of steel and is calculated by the following formula (4), is set to 0.550 to 0.620 mass%.

[0052] Ceq=[C]+[Mn] / 6+([Cu]+[Ni]) / 15+([Cr]+[Mo]+[V]) / 5 …(4) Here, in equation (4), [C], [Mn], [Cu], [Ni], [Cr], [Mo], and [V] represent the mass percentage content of C, Mn, Cu, Ni, Cr, Mo, and V in the steel, including the amount of elements mixed in as impurities. Substitute 0 for elements that are not present.

[0053] If the Ceq is less than 0.550 mass%, the strength of the steel plate may be insufficient. Therefore, the Ceq should be 0.550 mass% or higher. If necessary, the Ceq may be 0.570 mass% or higher, or 0.600 mass% or higher. Also, if the Ceq exceeds 0.620 mass%, the toughness of the steel plate may decrease. Therefore, the Ceq should be 0.620 mass% or lower. If necessary, the upper limit of the Ceq may be 0.600 mass% or lower.

[0054] In the steel sheet according to this embodiment, the chemical composition, Ceq, α value, β value, and γ value are within predetermined ranges, and preferably, [fB] is further controlled within a predetermined range. Chemical composition, Ceq, fB, α-value, β-value, and γ-value are controlled by the elemental content, but since removing or adding specific elements during the refining process can also change the amounts of other elements, it is not easy to change only a single element. Furthermore, since multiple elements may form compounds in molten steel and steel materials, the desired effect may not be achieved unless the balance of additions with other components is included in the target range.

[0055] (Degree of segregation) Next, we will explain the segregation of Si, P, Cu, and Ni in steel sheets. The steel sheet according to this embodiment must satisfy all of the following equations (5) to (8) in terms of segregation degree at the center of the sheet thickness (within a range of ±5 mm in the sheet thickness direction including the t / 2 position).

[0056] [Si]max / [Si]≦1.9 …(5) [P]max / [P]≦20.0 …(6) [Cu]max / [Cu]≦2.5 …(7) [Ni]max / [Ni]≦2.0 …(8)

[0057] Here, in equations (5) to (8), [Si], [P], [Cu], and [Ni] are the mass %) of Si, P, Cu, and Ni contained in the steel as described above, and include the amount of elements mixed in as impurities. Elements that are not present are substituted with 0. Furthermore, in equations (5) to (8), [Si]max, [P]max, [Cu]max, and [Ni]max are the average concentration (content) values ​​of each element within the tertiary region, which is selected from a primary region of ±5 mm in the thickness direction and 10 mm in the rolling direction, centered on the t / 2 position in the cross-section of the steel sheet, based on the EPMA line analysis results for each element, where the concentration of each element is maximum. Subsequently, a tertiary region of 20 μm on each side is selected from the secondary region based on the EPMA surface analysis results for each element, where the concentration of each element is maximum. The tertiary region is measured at the 1 / 2 width position, which is the center position in the width direction of the sheet, and at the 1 / 4 width position, which is 1 / 4 of the width from the end in the width direction of the sheet, and the higher of the two values ​​is taken as the representative value of that steel sheet.

[0058] The center of a steel plate has a higher concentration of alloying elements, resulting in a locally higher hardenability and a harder structure, thus reducing toughness. Furthermore, if impurity elements such as P are concentrated, the decrease in toughness after stress relief annealing becomes more pronounced. To ensure the toughness of the base material, all of the above equations (5) to (8) must be satisfied.

[0059] The degree of segregation of each element is expressed as [Si]max / [Si], for example, in the case of Si. The degree of segregation of each element can be determined by EPMA (Electron Probe Micro Analysis) measurement according to the following steps (a), (b), (c), and (d).

[0060] (a) First, as shown in Figure 1, a metallographic sample 11 is processed in a cross section (TD surface) of the steel plate 10 parallel to the rolling direction and the thickness direction, with the plate width positions set to the 1 / 2 width position and the 1 / 4 width position, including the t / 2 position. Then, as shown in Figure 2, on the TD surface appearing in the metallographic sample 11, a line analysis with an analysis length of 10 mm is performed by EPMA measurement at a 50 μm pitch in the thickness direction, centered on the t / 2 position, in a range 12 (primary region) of ±5 mm from the center of the plate thickness to measure the mass % of Mn. Then, the plate thickness position range (region) 13 with the highest average Mn concentration, obtained by averaging the average Mn concentration of each line analysis over ±0.5 mm in the thickness direction, is identified. Within that plate thickness position range (region) 13, the range with a high average Mn concentration within a range of ±0.5 mm in the rolling direction is determined, and a 1 mm × 1 mm field of view region 14 (secondary region) is identified as follows.

[0061] (b) Specifically, in the TD surface appearing on the metallographic sample 11, the center in the thickness direction of the region 13 with a high average Mn concentration is defined as the longitudinal center position, and a 1 mm × 1 mm square field of view 14 is identified as the secondary region, with the center in the rolling direction of the region within region 13 with a high average Mn concentration within a range of ±0.5 mm in the rolling direction being the transverse center position. Then, in this field of view 14, surface analysis is performed by EPMA measurement at a 2 μm pitch in both the longitudinal and transverse directions (rolling direction and thickness direction), and the mass percent of Si, P, Cu, and Ni are measured.

[0062] (c) Next, as shown in Figure 3, within a 1 mm × 1 mm square field of view area 14 (secondary region), a 20 × 20 μm square portion 15 is scanned in the vertical and horizontal directions (rolling direction and plate thickness direction). At each position, the average value of the Si, P, Cu, and Ni content (mass%) of the measurement points contained within the square portion 15 is determined. The square portion 15 with the highest average value is identified as the tertiary region, and the average values ​​of the Si, P, Cu, and Ni content in this tertiary region are taken as the respective maximum values ​​([Si]max, [P]max, [Cu]max, [Ni]max). The third region is defined as the central segregation region.

[0063] For example, as shown in Figure 4, if the average value of Si determined from the mass % of Si at each measurement point within the square region 15-1 reaches its maximum value, then the average value of Si determined from the Si content (mass %) at each measurement point within the square region 15-1 (tertiary region) will be the maximum value [Si]max. Similarly, if the average value of P determined from the P content (mass %) at each measurement point within the square region 15-3 reaches its maximum value, then the average value of P determined from the P content (mass %) at each measurement point within the square region 15-3 (tertiary region) will be the maximum value [P]max. Similarly, if the average value of Cu determined from the Cu content (mass %) at each measurement point within the square region 15-4 reaches its maximum value, then the average value of Cu determined from the Cu content (mass %) at each measurement point within the square region 15-4 (tertiary region) will be the maximum value [Cu]max. Similarly, if the average value of Ni determined from the Ni content (mass%) at each fixed point within the square region 15-5 is the maximum value, then the average value of Ni determined from the Ni content (mass%) at each measurement point within the square region 15-5 (tertiary region) will be the maximum value [Ni]max. In this way, the tertiary region may be specified for each element.

[0064] (d) The degree of segregation of each element at the center of the plate thickness is determined by dividing the maximum value of each element ([Si]max, [P]max, [Cu]max, [Ni]max) by the content of each element in the steel plate ([Si], [P], [Cu], [Ni]) ([Si]max / [Si], [P]max / [P], [Cu]max / [Cu], [Ni]max / [Ni]). For EPMA analysis, the measurement conditions are as follows: using the EPMA system with the electron gun of LaB6, the acceleration voltage is 15kV, the irradiation current is 100nA, the beam diameter is the same as the measurement pitch, and the measurement time is 50ms. For line and surface analysis with a 50μm pitch, a shorter measurement time of 20ms is also acceptable.

[0065] (The equivalent circular diameter of inclusion particles is 4.0 μm or less for 99% or more of the particles by number) In this embodiment, when inclusion particles with an equivalent circle diameter of 0.5 μm or more and containing 20 mass% or more of Ti are identified in a rectangular region with sides of 4 mm centered at the t / 4 and t / 2 positions of the cross-section in the thickness direction, it is necessary that the equivalent circle diameter of 99% or more of these inclusion particles is 4.0 μm or less. In other words, in the particle size distribution for the equivalent circle diameter of the identified inclusion particles, the equivalent circle diameter corresponding to 99% of the cumulative distribution function must be 4.0 μm or less. If the equivalent circle diameter of 99% or more of the inclusion particles exceeds 4.0 μm, the decrease in toughness after stress relief annealing becomes significant. The equivalent circle diameter of 99% or more of the inclusion particles may be 3.0 μm or less, or 2.5 μm or less.

[0066] The equivalent circular diameter of inclusion particles that make up 99% or more of the total number of particles is measured by the following method. For inclusion particles that make up 99% or more of the particle size, the equivalent circle diameter is determined by randomly selecting a rectangular area with sides of 4 mm on the observation surface of a mirror-finished steel plate, with the center positions at the t / 4 and t / 2 positions of the cross-section in the thickness direction, respectively. This area is observed using a SEM equipped with an EDS analyzer, with an acceleration voltage of 3 to 30 kV. The field of view is scanned within the area, and inclusion particles with a different contrast from the observed matrix are extracted. The area is determined by image analysis, and EDS point analysis is performed near the center of the particle. The equivalent circle diameter is calculated as √(4A / π), where A is the area of ​​the inclusion particle. Among the inclusion particles, those with an equivalent circle diameter of 0.5 μm or more and containing 20 mass% or more of Ti are identified, and the equivalent circle diameter circle corresponding to the 99% cumulative distribution function is determined in the particle size distribution for the equivalent circle diameter of these inclusion particles.

[0067] (Yield strength: 670-870 MPa) (Tensile strength: 780~940MPa) In this embodiment, the yield strength of the steel plate is set to 670-870 MPa, and the tensile strength of the steel plate is set to 780-940 MPa. In order to reduce the weight of large welded structures such as transport tanks for liquefied CO2, a steel plate is required that can ensure the strength of the structure even with a thin plate thickness. Typically, the steel plate selected for use in such applications is one that has the yield strength and tensile strength described above, so this embodiment is also manufactured to have the yield strength and tensile strength described above. If necessary, the yield strength may be 690 MPa or higher, or 830 MPa or lower. The tensile strength may be 800 MPa or higher, or 900 MPa or lower.

[0068] (Average hardness, standard deviation) In this embodiment, the steel plate, when measuring the hardness distribution at t / 4 positions with a width of 0.5 mm × 0.5 mm and a pitch of 0.05 mm, must have an average hardness of 265 Hv to 290 Hv at 121 measurement points, and a standard deviation of 20 or less. If the hardness distribution is uneven, the toughness of the base material may deteriorate. If the average hardness is less than 265 Hv and the standard deviation exceeds 20, the toughness of the base material cannot be ensured. On the other hand, if the average value exceeds 290 Hv, the strength may become too high, potentially leading to a decrease in toughness. The microstructure of the steel sheet according to this embodiment is preferably a mixed structure of martensitic and lower bainite structures, which is superior in terms of strength-toughness balance. When the standard deviation of hardness and the average hardness are within the above range, it is considered that the microstructure mainly consists of martensitic and lower bainite structures. If upper bainite is present, there is concern that the average hardness will be less than 265 Hv or the standard deviation will exceed 20. Upper bainite may be formed due to localized variations in γ grain size and microsegregation, which can lead to a partial decrease in hardenability.

[0069] The hardness standard deviation (distribution) is measured by taking micro-samples of steel plates with the TD (tip-to-top) as the observation surface and using a micro-Vickers hardness tester. The measurement area is a 0.5 mm × 0.5 mm range centered at any t / 4 position within the micro-observation surface, with a measurement pitch of 0.05 mm and a measurement load of 25 gf, measuring at 11 points vertically × 11 points horizontally for a total of 121 points. The mean and standard deviation are calculated from the obtained measurements.

[0070] (Maximum hardness HVmax of the central segregation: 400HV or less) The toughness of the base material decreases as its hardness increases after stress relief annealing. To maintain toughness after stress relief annealing, the maximum hardness at the measurement location of the segregation degree [M]max / [M] must be 400HV or less. Specifically, within the tertiary region (central segregation area) described above, optical microscope observations are taken at random intervals, for example, five fields, and the hardness at the center of each field is measured using a Vickers test with a load of 100g, with the maximum hardness being defined as the maximum hardness HVmax of the central segregation area. If the tertiary regions differ for Si, P, Cu, and Ni, the maximum hardness in the tertiary region of Ni (measurement location of segregation degree [Ni]max / [Ni]) must be 400HV or less.

[0071] (Plate thickness: 25~60mm) When welding steel plates with a thickness of less than 25 mm, stress relief annealing is generally not required. However, since the steel plates used in this embodiment are those that require stress relief annealing, the plate thickness is set to 25 mm or more. On the other hand, steel plates with a thickness exceeding 60 mm are undesirable because they increase the weight of the transport tank. Therefore, the thickness of the steel plate according to this embodiment is set to 60 mm or less.

[0072] Furthermore, the steel plate according to this embodiment may have the following characteristics.

[0073] (organization) In this embodiment, the steel sheet preferably has a mixed structure of martensitic and lower bainite structures at the t / 4 position of the cross-section in the thickness direction. The martensitic and lower bainite structures should together account for 85.0% or more of the area. In this case, the above-mentioned standard deviation and mean hardness are more likely to be satisfied.

[0074] The area ratio of martensitic tissue and lower bainite tissue is measured by the following method. The area percentage of each metallographic structure is measured on the L-section of the steel sheet, i.e., on a plane parallel to the rolling direction RD of the steel sheet and perpendicular to the sheet surface. The observation field has an area of ​​40,000 μm². 2 The above is sufficient. For example, a steel plate with a dimension of 250 μm along the surface and a dimension of 200 μm along the thickness direction of the steel plate, with an area of ​​50,000 μm. 2 It has a rectangular shape. The metallic microstructure is revealed by nital etching. The area ratio of the metallic microstructure in each observation region is obtained by observing the microstructure with an optical microscope and determining the microstructure according to the following procedure. Upper bainite is a nodular, needle-like, or amorphous (mainly nodular, with curved grain boundaries) structure in which one or more cementite and austenite-martensite hybrids are observed as distinct black contrasts, appearing as points or granules within a ferrite base grain that is observed as a white contrast. The cementite and austenite-martensite hybrids observed in upper bainite may form in rows along the ferrite lath, but they may also appear to be randomly arranged. The lath structure of upper bainite has a lath width of 1.0 μm or more, and consists of multiple lath-like structures arranged in parallel, although the spacing and direction of the laths may not be very uniform. The prior austenite grain boundaries may have poor contrast or be difficult to distinguish due to their uneven, saw-tooth-like morphology. For example, the micrograph on the left side of Figure 5 is a micrograph of upper bainite structure. The martensite and lower bainite mixed structure is characterized by fine laths of distinct black contrast within the matrix grains, which are observed as white contrast. In this embodiment, the lath width is 1.0 to 3.0 μm, and numerous cementite particles are observed as black contrast within and at the lath boundaries. However, because the cementite observed in tempered martensite is fine and has a high precipitation density, it may appear as countless white granular contrasts or cloud-like contrasts of varying intensity under an optical microscope. Prior austenite grain boundaries can be clearly observed as linear black contrasts, but they can be difficult to distinguish from the laths within the grains. For example, the tissue image on the right side of Figure 5 is a tissue image of a mixed tissue consisting of martensite tissue and lower bainite tissue.

[0075] (Average grain size at the center of the steel plate thickness: 15.0 μm or less) In this embodiment, in order to ensure a predetermined toughness, the average grain size at the center of the steel plate thickness is set to 15.0 μm or less. To improve the toughness of the base material before and after stress relief annealing, the upper limit of the average grain size may be set to 14.5 μm or less, or 14.0 μm or less, as needed. Since a smaller average grain size at the center of the steel plate thickness is preferable, it is not necessary to specify a lower limit. Typically, the smallest average grain size is about 10.0 μm.

[0076] The average grain size is measured by the following method. To allow observation of the L-shaped cross-section, a sample measuring 10-20 mm in the longitudinal direction and 10-30 mm in the thickness direction is cut from the steel plate. This sample is polished with colloidal silica. Crystal orientation measurements are performed using the Electron Backscatter Diffraction (EBSD) method in 1.0 μm steps on a 500 × 500 μm area of ​​the target cross-section using an EBSD instrument (TSL or Ametek-EDAX). The acceleration voltage is set to 10-30 kV. The obtained crystal orientations are analyzed using crystal orientation analysis software (TSL OIM Analysis7 x64). A region enclosed by grain boundaries with a crystal orientation difference of 15° or more is defined as a crystal grain. The equivalent circular grain size of a crystal grain is defined as the crystal grain size, and the average crystal grain size is calculated using an area-weighted average weighted by the area of ​​each crystal grain. In crystal orientation analysis software, crystal orientation data is recorded for each hexagonal pixel created on the observation surface. Therefore, each of these pixels has adjacent pixels, and a crystal orientation difference (degree) is defined for each boundary (one side of the hexagon) between adjacent pixels. If the crystal orientation difference between adjacent pixels is 15° or greater (hereinafter referred to as the 15° boundary), that pixel boundary is retained on the map as a candidate grain boundary, as it may correspond to a crystal grain boundary. This orientation difference calculation is performed for all pixel boundaries, and if adjacent candidate grain boundaries are continuous, they are connected to form a closed curve (polyline) within the observation (data acquisition) area. In this case, the region enclosed by that closed curve is defined as a single grain. If a 15° boundary does not form a closed curve and has an end within the observation region, it is not considered a grain boundary and is ignored (as a subgrain boundary). Also, if a 15° boundary intersects with an edge of the observation region, it means that the grain extends outside the observation region, and since that region does not reflect the region of a single grain, it is ignored as a half-region. In this way, only regions that are completely closed by a 15° boundary within the observation region are considered to correspond to grains, and the area of ​​a grain is considered to be the product of the number of such regions and the area of ​​one pixel (a hexagon with sides equal to the step size). Finally, the diameter of a circle with the same area as the area of ​​each closed region is found and defined as the diameter of a single grain. Even if a 15° boundary forms a closed curve within the observation area, if the number of pixels within that curve is one or less, it is considered noise and will not be used in calculating the particle size.

[0077] (Charpy absorption energy at -45°C after stress relief annealing is 40 J or higher) In this embodiment, the steel plate undergoes stress relief annealing of the welded joints after assembly into a transport tank, with the aim of preventing fracture. During this process, not only the welded joints but also the base metal is heated. When the base metal is heated, its toughness tends to decrease. Although the exact cause is unclear, it is presumed that phosphorus (P) diffuses into the grain boundaries, and inclusions grow or aggregate in the microstructure, reducing brittleness and thus toughness. Therefore, in this embodiment, the Charpy absorption energy at -45°C after stress relief annealing is preferably 40 J or higher. This further enhances safety.

[0078] The Charpy absorption energy at -45°C after stress relief annealing is measured at the location where stress relief annealing was performed on a steel plate, with a holding temperature of 600-620°C, a holding time of 2.0-2.8 hours, and a cooling rate of 55-100°C / h (°C / hour) in the temperature range of 425°C or higher.

[0079] (δ value of 0.05 mm or higher in the CTOD test at -35°C) The steel plate according to this embodiment exhibits excellent toughness due to the above-described characteristics. However, from the viewpoint of ensuring the safety of transport tanks made from the steel plate according to this embodiment, it is preferable that the δ value of the CTOD test at -35°C is 0.05 mm or higher.

[0080] (Charpy absorption energy at -70°C is 50 J or higher) Furthermore, it is preferable that the steel plate according to this embodiment has a Charpy absorption energy of 50 J or more at -70°C. This makes it possible to ensure the safety of transport tanks that include or are made of the steel plate according to this embodiment. The Charpy absorption energy at -70°C is the value measured at position t / 4. In this embodiment, a Charpy absorption energy of 50 J or more means that the minimum value is 50 J or more when measured at three different measurement positions at position t / 4.

[0081] (Yield strength after stress relief annealing is 670-870 MPa, tensile strength is 780-940 MPa) In this embodiment, the steel plate preferably has a yield strength of 670 to 870 MPa and a tensile strength of 780 to 940 MPa after stress relief annealing. In this case, sufficient strength can be ensured in a transport tank for liquefied CO2 that has undergone stress relief annealing.

[0082] <Container for liquefied CO2> The container for liquefied CO2 according to this embodiment is formed by processing and welding the steel plate according to this embodiment as described above. Therefore, the container for liquefied CO2 according to this embodiment includes the steel plate according to this embodiment. It may substantially consist of the steel plate (base material) according to this embodiment and a welded portion formed by the melting and re-solidification of the steel plate and welding material according to this embodiment.

[0083] <Manufacturing method> Next, the manufacturing method for the steel plate and the container for liquefied CO2 according to this embodiment will be described below. The steel plate according to this embodiment will exhibit the above-mentioned effects regardless of the manufacturing method, as long as it has the above-mentioned characteristics, but it can be manufactured stably according to the manufacturing method shown below. To manufacture steel sheets from steel having the above-mentioned components, it is preferable to produce steel by the converter method or electric furnace method, refine it in a secondary refining facility, and then form slabs by continuous casting or ingot formation. Subsequently, the slabs are heated to approximately 950-1250°C in a slab heating furnace, and then rolled to a predetermined thickness by hot rolling to form steel sheets. Furthermore, these steel sheets are quenched and tempered to obtain steel sheets (final steel sheets) with predetermined properties. The preferred conditions for each process will be described. (Secondary refining process) The secondary refining process can be carried out by known methods. The steel sheet according to this embodiment needs to have a phosphorus content of 0.006% or less. Conventional dephosphorization methods may not be able to reduce the phosphorus content to 0.006% or less, but in such cases, measures such as extending the dephosphorization treatment time can be taken.

[0084] (Casting process) In the casting process, a slab is obtained. To control the equivalent diameter of inclusion particles, which account for 99% or more by number, to 4.0 μm or less, the following measures are taken: separation of inclusions by flotation in the tundish, separation of inclusions by electromagnetic braking of the molten steel flow during the initial stage of solidification in the mold, and reduction of central segregation by light reduction during casting. The light reduction may be, for example, a reduction rate of 3% or less, 2% or less, or 1% or less. Light reduction is preferably performed at the end of solidification.

[0085] (Hot rolling process) Next, we will explain the hot rolling process. If the heating temperature before rolling exceeds 1250°C, it leads to coarsening of the average grain size. Therefore, it is preferable to keep the heating temperature before rolling below 1250°C. Also, if the heating temperature before rolling falls below 950°C, low-temperature rolling occurs during rolling, resulting in a smaller reduction amount per pass, and insufficient reduction effect is not obtained near the center of the sheet thickness. Therefore, it is preferable to keep the heating temperature before rolling above 950°C.

[0086] During rolling, it is desirable to achieve a cumulative reduction ratio of 50% or more within the rolling temperature range of 1150 to 900°C. When direct quenching treatment, in which water cooling is performed immediately after hot rolling, is carried out on the steel sheet, it is desirable to achieve a cumulative reduction ratio of 50% or more within the rolling temperature range of 1150 to 900°C. There is no particular need to specify an upper limit for the cumulative reduction ratio, but it may be, for example, 80% or less, or 70% or less.

[0087] (Heat treatment process) After hot rolling, either direct quenching or reheat quenching, in which the steel sheet is cooled after hot rolling and then reheated, or both, are performed. If both are performed, reheat quenching is performed after direct quenching. Direct quenching is a quenching process in which the steel sheet is immediately water-cooled after hot rolling. Reheat quenching is a quenching process in which the steel sheet is cooled after hot rolling and then reheated.

[0088] The conditions for direct quenching are to start the cooling at an Ar3 point or higher, and to perform water cooling to 300°C or lower. Preferably, the average cooling rate during water cooling should be 5°C / second or higher. There is no particular upper limit to the average cooling rate, but for example, it may be 50°C / second or lower, 20°C / second or lower, or 15°C / second or lower.

[0089] The conditions for the reheating and quenching treatment are as follows: The heating temperature during the quenching process (i.e., the quenching temperature) is preferably 925°C or lower, but may also be 920°C or lower, 915°C or lower, or 910°C or lower. This is because, in the case of thick steel plates, the microstructure may not be sufficiently refined after rolling. If the quenching temperature for a steel plate with an insufficiently refined microstructure exceeds 925°C, the reverse transformation γ structure formed during heating will become coarse, and the average grain size of the final structure after the γ / α transformation due to subsequent cooling will also become coarse. On the other hand, a lower limit of the quenching temperature that is slightly above the Ac3 point (for example, within the temperature range of Ac3 point or higher and Ac3 point + 20°C or lower) is undesirable because it may result in insufficient hardenability due to variations in the reverse transformation γ grain size and insufficient solid solution of carbides containing B. Therefore, a lower limit of the quenching temperature is preferably 880°C or higher, and more preferably 890°C or higher.

[0090] The Ar3 point can be determined using the following method. Ar3(℃)=910-310×C-80×Mn-20×Cu-15×Cr-55×Ni-80×Mo+0.35×(t-8) …(A) In equation (A) above, C, Mn, Cu, Cr, Ni, and Mo are the mass %) content of each element in the steel, and t is the thickness (mm) of the steel sheet after hot rolling. The steel billet temperature refers to the surface temperature of the steel billet.

[0091] (Tempering process) In the steel sheet manufacturing method according to this embodiment, the steel sheet is further tempered after the quenching process. The heating temperature for tempering (i.e., the tempering temperature) is 660°C or lower. If the tempering temperature exceeds 660°C, the tempering effect becomes excessive, making it difficult to secure yield strength and tensile strength. On the other hand, if the tempering temperature is too low, the tempering will be insufficient, making it difficult to secure the yield strength and tensile strength. Therefore, the tempering temperature should be 500°C or higher. Preferably, the tempering temperature should be 600°C or higher.

[0092] When cooling is performed after reheating quenching or tempering, it is desirable to cool the steel plate by water cooling (accelerated cooling) rather than by air cooling in order to prevent a decrease in the toughness of the base material due to tempering embrittlement. In this case, it is preferable to set the average cooling rate up to 300°C to 0.1°C / second or 0.5°C / second or higher. The average cooling rate may also be 5°C / second or higher.

[0093] The steel plate according to this embodiment is suitable for use as a steel plate for liquefied CO2 transport tanks (containers for liquefied CO2). For example, it can be used as a transport tank mounted on a ship. When transporting CO2 by ship, liquefied CO2 is filled into a transport tank installed on the ship and transported, but in order to prevent the CO2 from solidifying inside the transport tank, it is preferable to transport it while maintaining a pressure of about 2 MPa. Furthermore, in order to maintain the CO2 in a liquid state at a pressure of about 2 MPa, it is preferable to keep the CO2 at about -35°C. The steel plate according to this embodiment can be suitably used for such applications.

[0094] The container for liquefied CO2 according to this embodiment is formed by cutting and processing a steel plate according to this embodiment into a predetermined shape, and joining multiple steel plates by welding. Stress relief annealing may also be performed after welding. For welding, the welding heat input should be 1.1 to 4.5 kJ / mm, and the process should be carried out under general conditions. Stress relief annealing should be performed in accordance with the provisions of JIS Z 3700:2009 "Post-weld heat treatment methods". [Examples]

[0095] Next, embodiments of the present invention will be described. The conditions in the embodiments are merely examples of conditions adopted to confirm the feasibility and effectiveness of the present invention, and the present invention is not limited to these examples of conditions. The present invention can adopt various conditions as long as they do not depart from the spirit of the invention and achieve the objectives of the present invention.

[0096] After the blast furnace treatment was completed, the molten iron was tapped into the molten iron ladle, and after pre-treatment such as desulfurization was performed on the molten iron, it was inserted into the converter, and the molten steel in the converter was adjusted for composition.

[0097] This molten steel was cast by continuous casting to obtain slabs having the chemical compositions shown in Tables 1A to 3B. In the casting process, inclusions were separated by flotation in the tundish and by electromagnetic braking of the molten steel flow during the initial solidification stage in the mold. In addition, except for a few cases, central segregation was reduced by light reduction (reduction ratio: 1% or less) during casting. Subsequently, the slabs were heated in a heating furnace to the heating temperatures shown in Tables 4A and 4B, and then rolled to the specified thickness by hot rolling to produce steel plates. Furthermore, this steel plate was subjected to quenching and tempering to obtain a steel plate (final steel plate) with predetermined properties. Tables 4A and 4B show the presence or absence of light reduction during casting, the heating temperature before rolling, the cumulative reduction ratio from 1150 to 900°C during hot rolling, the plate thickness after rolling, the conditions for direct quenching (cooling start temperature, cooling end temperature, average cooling rate), the conditions for reheat quenching (quenching temperature), and the conditions for tempering (tempering temperature). Cooling after reheating, quenching, and tempering was performed by water cooling, with an average cooling rate of 0.1°C / second or higher up to 300°C.

[0098] Tables 1A to 3B show the chemical composition, α, β, γ, fB values, and carbon equivalent (Ceq) of the steel sheets. Tables 5A to 6B show the average value (average Hv) of the base material hardness at 121 measurement points, its standard deviation, maximum hardness (HVmax), microstructure fraction (%) of martensitic and lower bainite structures, average grain size (EBSD grain size), yield strength (MPa), tensile strength (MPa), yield ratio, Charpy absorption energy (J) at -70°C at t / 4 and t / 2 positions, and δ value (mm) of the CTOD test at -35°C. Furthermore, Tables 5A and 5B indicate whether the degree of segregation at the center of the plate thickness ([Si]max / [Si], [P]max / [P], [Cu]max / [Cu], [Ni]max / [Ni]) meets the specified range, and whether the equivalent circular diameter of inclusion particles accounting for 99% or more of the total number of particles was 4.0 μm or less (indicated by "○" if 4.0 μm or less, and "×" if greater than 4.0 μm).

[0099] The methods for measuring the degree of segregation at the center of the plate thickness ([Si]max / [Si], [P]max / [P], [Cu]max / [Cu], [Ni]max / [Ni]) and the average grain size were as described above.

[0100] Tensile tests were conducted using two test specimens in accordance with JIS Z 2241:2023. The yield strength (0.2% proof stress) and tensile strength are the average values ​​of the two test specimens. The yield ratio is the ratio of the yield strength YS to the tensile strength TS, and is expressed as a percentage, i.e., 100 × (YS / TS). The unit of the yield ratio is %.

[0101] Hardness was measured by taking micro-samples from a surface parallel to the rolling direction of the steel and measuring them using a micro-Vickers hardness tester. The measurement area was a 0.5 mm × 0.5 mm range centered at an arbitrary t / 4 position within the micro-observation surface, with a measurement pitch of 0.05 mm and a measurement load of 25 gf. A total of 121 measurements were taken at 11 points vertically and 11 points horizontally. The mean and standard deviation were calculated from the obtained measurements.

[0102] Furthermore, within the tertiary region identified when measuring the degree of segregation at the center of the plate thickness, optical microscope observations were randomly taken, for example, in 5 fields. The hardness at the center of each field was measured using a Vickers test with a load of 100g, and the maximum hardness was defined as the maximum hardness HVmax of the central segregation area.

[0103] The tissue fractions of martensitic and lower bainite tissues were determined by SEM observation in the same cross-section as the hardness distribution measurement. The martensitic and lower bainite tissues were identified, and their total area fractions were calculated. The method for measuring tissue fractions was as described above.

[0104] Furthermore, welded joints were fabricated and evaluated. A K-groove was prepared, argon gas containing 20% ​​CO2 was used as the shielding gas, YM-69F welding wire manufactured by Nippon Steel Welding Industries Co., Ltd. was used as the welding wire, the heat input was 2.0 kJ / mm, and the preheating was 100°C. Multi-layer gas shielded arc welding was performed to produce welded joints. Subsequently, stress relief annealing (SR) was performed on the base metal and the weld. For stress relief annealing, the holding temperature was set to 600-620°C, the holding time to 2.0-2.8 hours (2 hours 48 minutes), and the cooling rate was set to the range of 55-100°C / h in the temperature range above 425°C.

[0105] Tables 6A and 6B show the yield strength and tensile strength of the base material after SR (Surface Restoration).

[0106] Tables 6A and 6B also show the Charpy absorption energy at -45°C after SR at the t / 4 position of the base material, and the δ value of the CTOD test at -35°C after SR.

[0107] Furthermore, Tables 7A and 7B show the Charpy absorption energy at -70°C and the δ value of the CTOD test at -35°C, which is the surface layer (I-side FL) and t / 2 position of the base metal adjacent to the weld on the front side of the weld before SR.

[0108] Furthermore, Tables 7A and 7B show the Charpy absorption energy at -45°C and the δ value of the CTOD test at -35°C at the surface layer (I-side FL) and t / 2 position of the base metal adjacent to the weld after SR.

[0109] The Charpy impact energy absorbed by the base metal and weld is determined by taking three V-notch test specimens from the base metal and the weld, and performing a Charpy impact test at a predetermined temperature, thereby determining the absorbed energy (vE -65 The following measurements were taken. The V-notch test specimens were prepared in accordance with the V-notch test specimens described in JIS Z 2242:2023. The Charpy impact test was also performed in accordance with JIS Z 2242:2023. The Charpy absorption energy at -70°C is recorded as the minimum value obtained when measured at three different measurement positions with different t / 4 positions.

[0110] The σ value of the CTOD test is (δc at-10℃ Measurements were performed in accordance with BS7448 (British Standard) Part 1 (1991) and BS7448 (British Standard) Part 2 (1997). Specifically, gas shielded arc welding was performed on the butt joint of steel plates processed with a K-groove at a heat input of 35 kJ / mm. The CTOD test specimen of the weld was processed so that the tip of the fatigue notch was at the center of the plate thickness of the I-side fusion line of the weld, and the CTOD test was performed at the specified temperature. For the base material, evaluation was performed in the C direction (plate width direction) where the longitudinal direction of the test specimen is perpendicular to the rolling direction. For welded joints, evaluation was performed only in the L direction (rolling direction). In the evaluation of CTOD of welded joints, test specimens were taken so that the tip of the fatigue crack corresponds to the weld bond. Three tests were performed at each test temperature, and the lowest value of the obtained measurement data was taken as the δ value of the CTOD test. The units of CTOD shown in Tables 6A to 7B are mm.

[0111] A product was deemed acceptable if the minimum Charpy absorption energy of the base material at -70°C was 50J or more, the CTOD of the base material at -35°C was 0.05mm or more, and the CTOD of the joint at -35°C before and after SR was 0.05mm or more.

[0112] As shown in Tables 1A to 7B, all of the present invention examples No. 1 to 14 exhibited excellent toughness at low temperatures in the base material before and after SR treatment. In particular, the δ value of the CTOD test at -35°C after SR at the t / 4 position was 0.05 mm or higher, indicating excellent resistance to brittle fracture at low temperatures even after SR treatment. Furthermore, the yield strength after SR treatment was 670 to 870 MPa and the tensile strength was 780 to 940 MPa, showing good values. Moreover, for No. 1 to 14, the δ value of the CTOD test at -35°C of the welded joints was 0.05 mm or higher before and after SR treatment, indicating excellent resistance to brittle fracture at low temperatures.

[0113] On the other hand, as shown in Tables 1A to 7B, comparative examples No. 15 to 44 and 58 exhibited inferior low-temperature toughness because the chemical composition of the steel fell outside the range specified in the present invention. Specifically, the minimum Charpy absorption energy of the base material at -70°C was less than 50 J, or the CTOD of the base material at -35°C was less than 0.05 mm, or the CTOD of the welded joint at -35°C before or after SR was less than 0.05 mm.

[0114] Furthermore, although the steel composition of samples No. 45 to 57 met the component range of the present invention, the manufacturing conditions did not satisfy the preferred manufacturing conditions, resulting in inferior low-temperature toughness. Specifically, the minimum Charpy absorption energy of the base material at -70°C was less than 50 J, or the CTOD of the base material at -35°C was less than 0.05 mm, or the CTOD of the welded joint at -35°C before or after SR was less than 0.05 mm.

[0115] [Table 1A]

[0116] [Table 1B]

[0117] [Table 2A]

[0118] Table 2B

[0119] Table 3A

[0120] Table 3B

[0121] Table 4A

[0122] Table 4B

[0123] Table 5A

[0124] Table 5B

[0125] Table 6A

[0126] Table 6B

[0127] Table 7A

[0128] [Table 7B] [Industrial applicability]

[0129] According to the present invention, it is possible to provide steel plates for liquefied CO2 transport tanks and containers for liquefied CO2 that are excellent in strength, low-temperature toughness, and low-temperature toughness after stress relief annealing of steel plates, as well as in low-temperature toughness after stress relief annealing when used in welded joints. Therefore, they have high potential for industrial application. [Explanation of Symbols]

[0130] 10 steel plate 11. Samples for metallographic observation

Claims

1. liquefied CO ２ Steel plates for transport tanks, The chemical composition is expressed in mass percent. C: 0.070 to 0.110%, Si: 0.10-0.15%, Mn: 0.70 to 1.20%, Ni: 1.00-2.50%, Cr: 0.20-0.80%, Mo: 0.20-0.80%, V: 0.005 to 0.070%, Al: 0.030-0.100%, B: 0.0005-0.0030%, N: 0.0015-0.0050%, P: 0.006% or less, S: 0.0030% or less, Cu: 0 to 1.00%, Nb: 0 to 0.030%, Ti: 0 to 0.010%, Ca: 0-0.0030%, Mg: 0 to 0.0030%, REM: 0 to 0.0030%, O: 0.0040% or less, The remainder consists of Fe and impurities. The α value defined by the following equation (1) is 1.00 to 1.50 mass%, The β value defined by equation (2) below is between 10.00 and 15.

00. The γ value defined by the following equation (3) is 0.70 to 1.50 mass%, The Ceq defined by the following equation (4) is 0.550 to 0.620 mass%, The yield strength is 670 to 870 MPa. The tensile strength is 780 to 940 MPa. When the plate thickness is denoted as t, the aforementioned t is between 25 and 60 mm. At the t / 4 position of the cross-section in the thickness direction of the plate, the martensitic structure and the lower bainite structure together account for 85.0 area or more. In hardness distribution measurements at t / 4 positions with a 0.5 mm × 0.5 mm, 0.05 mm pitch, the average hardness at 121 measurement points was 265 Hv to 290 Hv, with a standard deviation of 20 or less. The maximum hardness HVmax of the central segregation is 400HV or less. The degree of segregation at the center of the plate thickness satisfies all of the following equations (5) to (8), In the cross-section in the thickness direction of the plate, in a rectangular region with sides of 4 mm centered at the t / 4 position and the t / 2 position, the equivalent circle diameter of the inclusion particles is 0.5 μm or more and contains 20% by mass or more Ti, and the equivalent circle diameter of 99% or more of the inclusion particles is 4.0 μm or less. When crystal orientation analysis is performed using electron beam backscatter diffraction pattern analysis, a region surrounded by grain boundaries with a crystal orientation difference of 15° or more is defined as a crystal grain, the circular equivalent grain size of the said crystal grain is defined as the crystal grain size, and the value calculated by area-weighted average weighted by the area of ​​each crystal grain is defined as the average crystal grain size, then the average crystal grain size at the center of the thickness of the steel plate is 15.0 μm or less. steel plate. α=[C]+6×[Si]+100×[P]…(1) β00.65×13) １／２ ×(1000064×23))×(10044.10×271))×(100020272) ×(10000502×2000)×(10+2.33×232))×(100×144)). …(2) γ=[Mn]+20×[Nb]+36×[Ti]…(3) Ceq=[C]+[Mn] / 6+([Cu]+[Ni]) / 15+([Cr]+[Mo]+[V]) / 5...(4) [Si]max / [Si]≦1.9 (5) [P]max / [P]≦20.0…(6) [Cu]max / [Cu]≦2.5…(7) [Ni]max / [Ni]≦2.0…(8) Here, in equations (1) to (8), [C], [Si], [P], [Mn], [Cu], [Ni], [Cr], [Mo], [Nb], [Ti], and [V] represent the content (mass%) of C, Si, P, Mn, Cu, Ni, Cr, Mo, Nb, Ti, and V, respectively, including the amount of elements mixed in as impurities. If an element is not present, substitute 0. Furthermore, in equations (5) to (8), [Si]max, [P]max, [Cu]max, and [Ni]max are the average concentration values ​​of each element within the tertiary region, which is selected from a primary region of the cross-section of the steel plate in the thickness direction, centered at the t / 2 position and extending ±5 mm in the thickness direction and 10 mm in the rolling direction. This secondary region is then selected from the secondary region as a rectangular region with sides of 20 μm where the concentration of each element is maximized, based on the EPMA surface analysis results for each element. The tertiary region is defined as the central segregation region.

2. The [fB] calculated by equations (A) to (E) below is 0.0003% or more. The steel plate according to claim 1. [fB]=[B]-0.77×[fN]...(A) [fN]=[N]-0.29×[fTi]-0.52×[fAl]…(B) [fTi]=[Ti]-2×[fO]...(C) [fAl]=[Al]-1.125×[fO]...(D) [fO]=[O]-0.4×[Ca]-0.66×[Mg]-0.11×[REM]…(E) Here, in equations (A) to (E), [B], [N], [Ti], [Al], [O], [Ca], [Mg], and [REM] represent the content (mass%) of B, N, Ti, Al, O, Ca, Mg, and REM, respectively. This includes the amount of elements mixed in as impurities. Elements that are not present are substituted with 0, and if the calculated value of [fN], [fTi], [fAl], or [fO] is less than 0%, 0 is substituted.

3. When stress relief annealing is performed on the steel plate, with a holding temperature in the range of 600 to 620°C, a holding time in the range of 2.0 to 2.8 hours, and a cooling rate in the range of 55 to 100°C / h in the temperature range of 425°C or higher, the yield strength of the area where the stress relief annealing was performed is 670 to 870 MPa, the tensile strength is 780 to 940 MPa, and the Charpy absorption energy at -45°C is 40 J or more. The steel plate according to claim 1 or claim 2.

4. Liquefied CO2 containing the steel plate described in claim 1 or claim 2 ２ container.

5. Liquefied CO2 containing the steel plate described in claim 3 ２ container.