Abstract

A method for separating nickel and / or cobalt salts from crude nickel and / or cobalt bearing stock is disclosed which comprises treating the crude nickel and / or cobalt bearing stock with an iron or aluminum salt under conditions to remove at least a portion of one or more alkali metal ions and / or monovalent cation species as a jarosite / alunite precipitate to provide a solution having a reduced content of one or more alkali metal ions and / or monovalent cation species, and gradually increasing the pH of the resulting solution under conditions to provide a feed solution for further purification to produce nickel and / or cobalt salts suitable for producing battery grade nickel or cobalt salts. A method for obtaining purified nickel and cobalt from the feed solution is also disclosed.

Description

[Technical field]

[0001] Priority document This application claims priority to Australian Provisional Patent Application No. 2021901424, entitled "Production of High Purity Nickel and Cobalt Compounds", filed on May 13, 2021, the contents of which are incorporated herein by reference in their entirety.

[0002] Technical Field The present disclosure relates to a method for obtaining high purity nickel and cobalt compounds from crude nickel and crude cobalt bearing stock materials. [Background technology]

[0003] Background technology High purity nickel and cobalt sulfates are important precursors in the formation of lithium battery cathodes, typically formed from nickel-cobalt-manganese (NCM) and nickel-cobalt-aluminum (NCA).

[0004] Currently, there are no standards for high purity battery grade nickel and cobalt sulfates. However, high purity or battery grade nickel sulfate hexahydrate (NiSO4 6H2O) with low levels of trace elements such as Al, Ca, Cd, Co, Cr, Cu, Fe, Mg, Mn, Na, Pb, Si, and Zn is shown in Table 1.

[0005] [Table 1]

[0006] A typical high purity or battery grade nickel sulfate hexahydrate (NiSO4·6H2O) with low levels of trace elements is shown in Table 2.

[0007] [Table 2]

[0008] Similarly, high purity or battery grade cobalt sulfate heptahydrate (CoSO4 7H2O) with low levels of trace elements such as Al, Ca, Cd, Cr, Cu, Fe, Mg, Mn, Na, Ni, Pb, Si, Zn is shown in Table 3.

[0009] [Table 3]

[0010] A typical high purity or battery grade cobalt sulfate heptahydrate (CoSO4 7H2O) with low levels of trace elements is shown in Table 4.

[0011] [Table 4] Summary of the Invention [Problem to be solved by the invention]

[0012] Traditionally, nickel sulfide has been the key starting material used to produce battery grade nickel sulfate, but with the continued depletion of nickel sulfide deposits, low-grade nickel laterite deposits (which account for 73% of the world's nickel resources) are becoming increasingly important as a source of nickel and cobalt for the battery industry. However, profitable methods to process these low-grade laterite ores to produce high-purity battery grade nickel sulfate and cobalt sulfate have remained elusive. Existing refining processes to produce high-purity battery grade nickel sulfate and cobalt sulfate require the costly step of physically extracting the primary metal (i.e., nickel) from the relatively small amounts of associated impurities (ratio of impurities to nickel <1 / 15) by solvent extraction (SX), or can only produce other forms of nickel products, typically nickel liquors suitable for producing nickel cathodes by electrowinning or nickel powder by hydrogen reduction. These forms of nickel products require further refining processes to produce high-purity battery grade nickel sulfate.

[0013] Nickel laterite ores are typically processed by direct acid leaching, followed by precipitation of the major iron and aluminum impurities in a rich leach solution (PLS) by neutralization or thermal hydrolysis. Nickel and cobalt are then typically recovered as intermediate products, mixed sulfide precipitate (MSP) or mixed hydroxide precipitate (MHP), using basic chemicals such as magnesia, lime, limestone, or sodium hydroxide. Compared to the MSP process, which can remove more of the common impurities, the MHP process is becoming increasingly popular because it eliminates the costly and undesirable H2S precipitation step associated with the MSP process, and results in a product that is readily soluble in ammonia and acid, which aids in the purification and recovery process. Specifications for battery grade nickel sulfate and cobalt sulfate require very low levels of impurities, so methods to separate and purify them from the PLS formed by dissolution of the feedstock, such as MHP, are important.

[0014] Although there are several existing commercial hydrometallurgical processes for processing nickel laterite ores and subsequently refining intermediate products, e.g. MSP and MHP, the products from these processes require further purification to meet the required specifications for battery grade nickel and cobalt products. Even the nickel metal powder resulting from hydrogen reduction, although LME grade, requires further purification to produce battery grade nickel sulphate.

[0015] Generally, known commercial nickel laterite processes can be divided into acid-based and alkaline-based processes.

[0016] A typical alkaline leaching process is the modified Caron process using an ammonia-ammonium carbonate leachant, which has been previously employed at the Queensland Nickel Industries (QNI) and Cowes Nickel Operations nickel and cobalt refineries (Fittock 1992; Fittock et al. 1994; Price and Reid 1987). The refinery section of these plants used ammonia to releach MHP under mildly reducing conditions, followed by solvent extraction with LIX® 84 ketoxime to isolate nickel (Virnig et al. 1997). This precipitated from solution as the carbonate, calcined to nickel oxide, and further processed to various products, such as metallic nickel, produced by hydrogen reduction. Cobalt was recovered from the nickel-depleted raffinate by precipitating cobalt sulfide using sodium hydrosulfide. The cobalt product could be further processed to produce a high purity cobalt product.

[0017] The High Pressure Acid Leaching (HPAL) process is employed at Minara Resources' Murrin-Murrin Operations (Rodriguez 2008; Rodriguez 2009). MSP is produced to remove most of the impurities present in the leach liquor, e.g. aluminum, magnesium, and manganese. This is redissolved in the presence of oxygen and the solution is purified by solvent extraction (SX) to remove the zinc, then two Cyanex® 272 circuits are used to remove the cobalt, producing a raffinate containing nickel that is recovered as metallic nickel by hydrogen reduction.

[0018] The problem with existing processes is that they either do not produce nickel and / or cobalt liquor eligible for direct crystallization of high purity battery grade nickel sulfate and / or cobalt sulfate, or the processes involve costly steps to extract and separate the primary metal nickel from the relatively small amounts of impurities in the PLS.

[0019] There are also challenges and limitations associated with the separation of some associated impurities, such as alkali metals (Na and K), that occur with the nickel in nickel ores and other nickel materials and enter the PLS after leaching and subsequent intermediate products, such as MHP. When sodium hydroxide or ammonium hydroxide is used to neutralize and precipitate the MHP, more sodium ions or monovalent species, such as ammonium ions, may be introduced into the MHP.

[0020] The MHP after precipitation may be washed to remove partially soluble species. In Canadian Patent Application No. 2949580-A1 and Australian Patent Application No. 2016256773-A1 (Clout and Perry), washing of the MHP is included in the process as a step to remove or partially remove magnesium, calcium, sulfate, chloride and sodium components from the MHP, all to generally reduce the level of soluble impurities in the leach liquor to meet the requirements for integration into existing ammonia pressure leaching processes that produce cobalt and nickel powders, respectively, by hydrogen decompression.

[0021] Solvent extraction with an organophosphinic acid, e.g., Cyanex® 272, is usually required to separate the cobalt from the nickel, and base reagents, typically sodium hydroxide and ammonia / ammonium hydroxide, are required to neutralize the equivalent amount of acid produced or to control the pH during the SX process. The alkali metal and ammonium ions, together with some alkaline earth metals, e.g., calcium and magnesium, become nickel in the raffinate, causing contamination by the formation of double sulfates (or bisulfates) containing these impurities if the raffinate is used directly for the crystallization of nickel sulfate.

[0022] A problem in SX where ammonia is added directly to a concentrated nickel sulfate solution is the formation of nickel ammonium sulfate double salts. Prior art attempts have been made to address this problem by pre-neutralizing the organophosphate extractant and / or by pre-loading the organic phase with nickel.

[0023] Additionally, most of the methods and schemes for pre-neutralization and pre-charging were developed to prevent the formation of nickel double salts during the treatment of cobalt SX with concentrated nickel sulfate solutions from which nickel raffinate is recovered as nickel cathode by electrowinning or metallic nickel by hydrogen reduction in an ammonia process. Although some prior art schemes utilize pre-neutralization and pre-charging methods to minimize contamination of the cobalt and nickel mainstreams with alkali metal and ammonium ions introduced by neutralization as basic reagents, the cobalt and nickel liquors from these schemes are significantly contaminated with these impurities and are not suitable for use in producing high purity battery grade nickel sulfate.

[0024] From the foregoing, it will be apparent that the nickel produced by these processes tends to be significantly contaminated and that these processes do not provide sufficient separation of the individual magnesium, cobalt and nickel streams complete enough to enable the production of high purity battery grade nickel and cobalt sulfates.

[0025] Furthermore, current practices for producing high purity battery grade nickel sulfate include solvent extraction of nickel with organic carboxylic acids, typically Versatic® 10, to separate nickel from alkali metals, ammonia species, and alkaline earth metals (e.g., calcium and magnesium). The involvement of the key metal nickel SX step is very expensive and accounts for a large portion of the total operational and capital costs in the purification process.

[0026] What is needed is an integrated process for converting a nickel / cobalt mixed hydroxide intermediate, e.g., MHP, or other nickel bearing material or solution, to high purity battery grade nickel and cobalt sulfates that does not require a costly separation step of the primary metal nickel. Alternatively or additionally, what is needed is a process for producing high purity battery grade nickel and cobalt sulfates that overcomes one or more problems associated with the prior art or known processes. Alternatively or additionally, what is needed is a useful alternative to existing processes for producing high purity nickel and cobalt sulfates. [Means for solving the problem]

[0027] overview This disclosure arose from the inventors' research into processes for converting nickel / cobalt mixed hydroxide intermediates, such as, for example, MHP or other nickel bearing stocks or solutions, to high purity battery grade nickel and cobalt sulfates. The process described herein can generally be carried out in two stages.

[0028] In the first stage of the process described herein, nickel laterite ore, other nickel-bearing raw materials, intermediate products such as MHP or nickel-bearing solution, are converted to a feed solution substantially free of alkali metals and monovalent cation species, suitable for further purification processes to produce high purity battery grade nickel sulfate. This first stage may involve improving existing upstream processing of the nickel laterite ore or other nickel-containing material to efficiently produce a feed solution or MHP suitable for subsequent purification processes. Optionally, some, or preferably most, of the manganese may be converted to stable Mn(III / IV) oxides in the MHP or leach slurry, which are then separated to produce a feed solution with reduced manganese content for ease of purification and to produce high purity battery grade nickel sulfate.

[0029] Thus, in a first aspect, there is provided a method for separating nickel and / or cobalt salts from crude nickel and / or crude cobalt bearing stock, the method comprising the steps of: a) treating crude nickel and / or crude cobalt bearing stock with an iron or aluminum salt under conditions to remove at least a portion of one or more alkali metal ions and / or monovalent cation species as a jarosite / alunite (or alunite) precipitate to provide a solution having a reduced content of one or more alkali metal ions and / or monovalent cation species; b) stepwise increasing the pH of the solution from step a) under conditions to provide a feed solution for further purification to produce nickel and / or cobalt salts suitable for producing battery grade nickel or cobalt salts. Consisting of Step b) comprises the step of: i. Iron, ii. Aluminum; iii. Chromium, and iv.Copper The method comprises removing at least some or any combination of one or more of:

[0030] In certain embodiments of the first aspect, the process of the first aspect further comprises, prior to step a), treating the crude nickel and / or crude cobalt bearing stock containing material with an aqueous solution comprising water and / or sulfuric acid under conditions to remove at least some of the one or more alkali metal ions and / or monovalent cationic species. The step of treating the crude nickel and / or crude cobalt bearing stock with an aqueous solution comprising water and / or sulfuric acid may be carried out at a pH of 7 or greater.

[0031] In certain embodiments of the first aspect, the feed solution is treated with an oxidizing agent under conditions to oxidize any iron (II) to iron (III) and any manganese (II) to the higher oxidation state manganese (III / IV) to provide a feed solution containing nickel and / or cobalt and having reduced concentrations of any one or more of alkali metal ions, monovalent cation species, iron, aluminum, chromium, copper and manganese compared to crude nickel and / or crude cobalt bearing stock materials.

[0032] In certain embodiments of the first aspect, the iron and / or aluminium salt in step a) is an iron and / or aluminium sulphate, carbonate, oxide or hydroxide.

[0033] The second stage of the process described herein involves a novel solvent extraction (SX) process with minimal SX systems and circuits to separate impurities from cobalt and nickel, and to separate cobalt from nickel to produce cobalt liqueur suitable for crystallization of high purity battery grade cobalt sulfate, cobalt chloride, cobalt nitrate or other cobalt products, as required, and to produce raffinate nickel suitable for direct crystallization of high purity battery grade nickel sulfate or other nickel products, as required, without a primary nickel metal separation step. Advantageously, the second stage process avoids contamination from neutralization with base reagents such as sodium hydroxide, sodium carbonate, ammonia or ammonium hydroxide in the SX process. The second stage process provides an alternative process that allows for direct neutralization during solvent extraction with ammonia / ammonium hydroxide and selective removal of the ammonium component from the final hydrated nickel sulfate as ammonia for recycling (or recycle or reuse) as a base reagent in the process.

[0034] Thus, in a second aspect, there is provided a method for obtaining purified nickel and cobalt from a feed solution obtained according to the first aspect, the method comprising the steps of: a) reducing the concentration of zinc, calcium, manganese, copper, cadmium, lead, or other metal impurities having a higher affinity than cobalt and nickel in the feed solution by contacting with an organophosphorus extractant in a hydrocarbon diluent under solvent extraction conditions and separating the organic and aqueous phases to produce an aqueous raffinate containing purified cobalt and purified nickel; b) contacting the aqueous raffinate comprising purified cobalt and purified nickel with a cobalt-selective extractant in a hydrocarbon diluent under solvent extraction conditions and separating organic and aqueous phases to produce an organic phase comprising purified cobalt and an aqueous phase comprising purified nickel, thereafter selectively scrubbing and stripping the organic phase to obtain an aqueous phase comprising purified cobalt; c) purifying the purified cobalt-containing aqueous phase to produce a further purified cobalt-containing aqueous phase; d) purifying the purified cobalt-containing aqueous phase to produce a further purified cobalt-containing aqueous phase; e) recovering nickel from the aqueous phase containing the purified nickel; The present invention comprises:

[0035] It will be appreciated that the first and second stages described herein can be carried out separately from one another or can be combined to provide an improved process for producing high purity battery grade cobalt sulfate or other cobalt products, as well as high purity battery grade nickel sulfate from crude nickel and cobalt-containing materials such as laterite ore.

[0036] In certain embodiments of the second aspect, step b) comprises a) co-extracting both cobalt and magnesium in the aqueous raffinate from step a) into an organic phase; (ii) selectively scrubbing the co-extracted nickel from the organic phase with a scrubbing solution of sulfuric acid and / or cobalt sulfate at a relatively high equilibrium pH range to obtain a nickel-depleted organic phase and a nickel-rich scrub liquor (aqueous phase) which is recycled to step (i); (iii) further selectively scrubbing magnesium from the organic phase with a scrubbing solution of sulfuric acid and / or cobalt sulfate at a relatively low equilibrium pH range to obtain an organic phase containing purified cobalt and a magnesium-rich scrub liquor (aqueous phase); (iv) re-extracting the co-scrubbed cobalt in the magnesium-rich scrub liquor (aqueous phase) with a small amount of the organic phase to obtain a small amount of a cobalt-loaded organic phase which is mixed with the majority of the organic phase in step (iii); (v) stripping the organic phase from step (iii) to produce an aqueous phase containing purified cobalt; or b) (i) selectively extracting cobalt in the aqueous raffinate from step a) into an organic phase; (ii) scrubbing both the co-extracted nickel and magnesium in the organic phase with a sulfuric acid and / or cobalt sulfate scrubbing solution to obtain an organic phase containing purified cobalt and a nickel- and magnesium-rich scrubbed liquor (aqueous phase) which is recycled to step i); (iii) stripping cobalt from the purified organic phase of step (ii) with an acid to obtain an aqueous phase containing purified cobalt (strip liquor); (iv) selectively extracting magnesium from the raffinate of step (i) with a portion of the organic solution to obtain an aqueous phase containing purified nickel (final raffinate) and a magnesium-rich organic phase; (v) scrubbing the co-extracted nickel in the organic phase with a sulfuric acid scrubbing solution to obtain a purified nickel-rich scrubbed liquor which is recycled to step (iv); and (vi) stripping the magnesium-rich organics to recover a magnesium by-product to obtain an aqueous phase containing purified magnesium for recovering the magnesium by-product. The present invention comprises:

[0037] In certain embodiments of the second aspect, the organophosphate extractant has the formula (RO)2PO2H, where each R group, which may be the same or different, is an optionally substituted branched, straight chain, or cyclic alkyl, alkenyl, or alkynyl group.

[0038] In certain embodiments of the second aspect, the organophosphate extractant is di-2-ethylhexyl phosphoric acid (D2EHPA) or an organophosphate having similar or identical extraction properties to di-2-ethylhexyl phosphoric acid, such as, for example, mono-2-ethylhexyl phosphoric acid (M2EHPA) or di-p-octylphenyl phosphoric acid (OPPA).

[0039] In certain embodiments of the second aspect, the cobalt-selective extractant is an organophosphinic acid having the formula R2PO2H, where the R groups, which may be the same or different, are selected from optionally substituted branched, linear, or cyclic alkyl, alkenyl, or alkynyl groups.

[0040] In certain embodiments of the second aspect, the cobalt-selective extractant is di-2,4,4-trimethylpentylphosphinic acid or an organophosphinic acid having similar or identical extraction properties to di-2,4,4-trimethylpentylphosphinic acid, such as, for example, di-2-ethylhexylphosphinic acid. By way of example only, di-2,4,4-trimethylpentylphosphinic acid is the functional component of the commercial products Cyanex® 272 and Ionquest® 290.

[0041] In certain embodiments of the second aspect, a phase adjuster or modifier may be present in the organic solution. The modifier may be any suitable modifier that improves separation of the organic and aqueous phases, including but not limited to isodecanol, isotridecanol, 2-ethylhexanol, and tri-n-butyl phosphate.

[0042] In certain embodiments of the second aspect, the hydrocarbon diluent is an aliphatic or aromatic hydrocarbon solvent, or a mixture thereof. In certain embodiments of the second aspect, the hydrocarbon diluent is kerosene (or heating oil).

[0043] In certain embodiments of the second aspect, the step c) of purifying the aqueous phase comprising purified cobalt comprises: contacting the aqueous phase containing the purified cobalt with an ion exchange (IX) resin under conditions that selectively bind impurities to the resin to form a loaded resin; washing the loaded resin with water and / or an aqueous solution of an acid to recover the co-loaded cobalt; In certain embodiments, step c) further comprises leaching the loaded resin with an acid to remove impurities and regenerate the resin.

[0044] In certain embodiments of the second aspect, the step c) of purifying the purified cobalt-containing aqueous phase further comprises removing at least a portion of the copper from the purified cobalt-containing aqueous phase. The step of removing at least some of the copper from the purified cobalt-containing aqueous phase may comprise contacting the purified cobalt-containing aqueous phase with an iminodiacetic acid resin under conditions that bind copper, and separating the copper-loaded resin from the aqueous phase.

[0045] In certain embodiments of the second aspect, step c) of purifying the purified cobalt-containing aqueous phase further comprises removing at least some of any zinc from the purified cobalt-containing aqueous phase. Removing at least some of any zinc from the purified cobalt-containing aqueous phase may comprise contacting the purified cobalt-containing aqueous phase with a D2EHPA impregnated resin under conditions to bind zinc, and separating the zinc-loaded resin from the aqueous phase.

[0046] In certain embodiments of the second aspect, step c) of purifying the purified cobalt-containing aqueous phase optionally comprises simultaneously removing at least some of any zinc and at least some of any copper from the purified cobalt-containing aqueous phase. The step of simultaneously removing at least some of the zinc and at least some of the copper from the purified cobalt-containing aqueous phase may comprise contacting the purified cobalt-containing aqueous phase with an aminophosphonic acid resin under conditions to bind the zinc and copper, and separating the copper and zinc-loaded resin from the aqueous phase.

[0047] In a particular embodiment of the second aspect, the step c) of purifying the purified cobalt-containing aqueous phase further comprises removing at least some of any manganese from the purified cobalt-containing aqueous phase. The step of removing at least some of any manganese from the purified cobalt-containing aqueous phase may comprise contacting the purified cobalt-containing aqueous phase with an oxidizing agent under conditions to oxidize any manganese (II) to the higher oxidation state manganese (III / IV) and separating the solid manganese (III / IV) oxide from the aqueous phase. The oxidizing agent may be selected from the group consisting of ozone, a mixture of SO2 / O2 (air) in a ratio that functions as an oxidizing agent, peroxymonosulfuric acid (Caro's acid) and peroxydisulfuric acid, when the purified cobalt-containing aqueous phase is sulfate or is selected from the same other group of oxidizing agents (chlorides and nitrates) as the purified cobalt-containing aqueous phase.

[0048] In certain embodiments of the second aspect, step c) of purifying the aqueous phase comprising purified cobalt optionally comprises removing at least one of one or more of zinc, calcium, manganese, copper, cadmium, lead or other metal impurities in the aqueous phase comprising purified cobalt by contacting with an organophosphorous extractant in a hydrocarbon diluent, optionally under solvent extraction conditions in the presence of a phase modifier, and separating the aqueous phase and the organic phase to further produce an aqueous phase comprising purified cobalt.

[0049] In certain embodiments of the second aspect, the step of recovering nickel from the aqueous phase comprising the purified nickel comprises crystallizing nickel sulfate from the aqueous phase comprising the purified nickel.

[0050] In a particular embodiment of the second aspect, process step a) further comprises scrubbing at least some of the co-extracted cobalt and nickel from the organic phase using a scrubbing solution comprising water and / or sulfuric acid and / or metal sulfates to purify the aqueous phase that is recycled to the extraction.

[0051] In a particular embodiment of the second aspect, the process further comprises stripping at least some of the zinc, calcium, manganese and copper, as well as one or more of the other charge impurities having a higher affinity for the organic extractant than the cobalt and nickel present in the organic extractant in the organic phase obtained in step a) by (a) treating the organic phase with sulfuric acid by controlling the calcium concentration below saturation to avoid the formation of gypsum, or (b) treating the organic phase with hydrochloric acid, if the calcium concentration in the system is relatively high and there is a risk of gypsum formation.

[0052] In certain embodiments of the second aspect, the process further comprises contacting the organic phase with a hydrochloric acid solution (typically 6 M HCl) to remove some of the one or more iron, aluminum and other strongly bound metal ions from the organic phase by periodic bleeding of the organic phase in step a).

[0053] In certain embodiments of the second aspect, step b), selective scrubbing of the extracted nickel from the purified cobalt-containing organic phase is carried out at a relatively high equilibrium pH range, preferably an equilibrium pH range of 4.5 to 6.5, and selectively at a relatively low equilibrium pH range, preferably an equilibrium pH range of 3 to 5. The nickel and magnesium scrubbing may be carried out sequentially at a higher pH range to remove nickel and then at a lower pH range to remove magnesium, resulting in two separate scrubbed liquors, or may be carried out simultaneously at the lower pH range to remove both nickel and magnesium.

[0054] In a particular embodiment of the second aspect, step b) further comprises co-extracting magnesium present in the raffinate containing refined cobalt and refined nickel into an organic phase. Magnesium may be separated from cobalt by further scrubbing the co-extracted magnesium with sulfuric acid at a preferred equilibrium pH range of 3 to 5 and selectively re-extracting the co-scrubbed cobalt from the magnesium-rich scrubbed liquor into a portion of the organic phase that may be recycled and integrated into the majority of the organic phase upon magnesium scrubbing.

[0055] In certain embodiments of the second aspect, step b) further comprises purifying the organic phase containing purified cobalt by scrubbing both the nickel and magnesium co-extracted from the organic phase with a sulfuric acid and / or cobalt sulfate scrub solution to obtain a nickel-rich scrub liquor that can be recycled to the extraction of step b) to recover nickel.

[0056] In a particular embodiment of the second aspect, step b) further comprises scrubbing with sulfuric acid under conditions to extract any magnesium present in the purified nickel-containing raffinate with a portion of the organics to remove the co-extracted nickel which is then recycled to the extraction of step b), and stripping the scrubbed organics with sulfuric acid to regenerate the organics and produce a magnesium-rich aqueous phase for further recovery of magnesium by-products.

[0057] In certain embodiments of the second aspect, the process further comprises preloading one or more organic solutions used in the process with nickel, cobalt and / or magnesium sulfate, carbonate, oxide or hydroxide salts. The process may also comprise preloading one or more organic solutions used in the process with nickel sulfate. The process may further comprise treating with a basic reagent, such as, for example, nickel hydroxide, sodium hydroxide or carbonate, ammonia, ammonium hydroxide or carbonate, and magnesium oxide / hydroxide or carbonate, for neutralization or pH control in the preload. The process may further comprise preneutralizing the organic solution with a basic reagent to produce a preneutralized organic for preloading with nickel by exchange. The basic reagent may be selected from the group consisting of sodium hydroxide, sodium carbonate, ammonia, ammonium hydroxide or ammonium carbonate. The process may further comprise washing the organic solution preloaded with nickel sulfate with water and / or a scrub solution containing sulfuric acid and / or nickel sulfate to remove entrained and extracted sodium or ammonium ions.

[0058] In certain embodiments of the second aspect, the process further comprises directly neutralizing the acid generated during the solvent extraction with ammonia, ammonium hydroxide or ammonium carbonate under conditions that avoid the formation of nickel ammonium double salts or ammonium sulfate salts, followed by thermal decomposition of the ammonium component in the nickel sulfate hydrate.

[0059] In a particular embodiment of the second aspect, the process comprises one or more stages of an optional extraction step, an optional scrubbing step and an optional stripping step in solvent extraction, and an optional loading step, an optional washing step and an optional elution step in ion exchange, which may be operated in countercurrent mode or in simultaneous mode, or in a combination of the two modes.

[0060] In a third aspect, there is provided herein high purity nickel sulfate obtainable by the method of the first and / or second aspects.

[0061] In a fourth aspect, there is provided high purity cobalt sulfate, and optionally cobalt chloride, cobalt nitrate, obtainable by the method of the first and / or second aspects. [Brief description of the drawings]

[0062] BRIEF DESCRIPTION OF THE DRAWINGS Embodiments of the present disclosure will now be described with reference to the accompanying drawings.

[0063] [Figure 1] FIG. 1 shows a schematic flowsheet of an embodiment of the present disclosure with schemes and methods for the treatment of MHP and / or PLS to provide a feed solution that is substantially free of alkali metal ions (Na+ and K+) and monovalent cationic species (NH4+), iron, aluminum and chromium, and optionally with a portion of manganese removed.

[0064] [Diagram 2]2 shows a schematic flow sheet of an embodiment of the present disclosure including a scheme and method for processing nickel laterite ore or nickel blanks and a solution for producing an MHP having an optimal ratio of iron and aluminum to the total amount of alkali metal ions (Na+ and K+) and monovalent cationic species (NH4+), which is advantageous for the improved processing efficiency and subsequent purification process shown in FIG. 1, or for the production of a feed solution or MHP that is substantially free of alkali metal ions (Na+ and K+) and monovalent cationic species (NH4+), iron, aluminum and chromium, and optionally removing a portion of the manganese.

[0065] [Diagram 3] FIG. 3 shows a flowsheet of an embodiment of the present disclosure with a scheme and method for purifying the feed solution produced by SX and IX from the process shown in FIG. 1 and FIG. 2, characterized by (i) organic preloading, (ii) SX for removing one or more impurities from the group of zinc, calcium, manganese, cadmium, copper, lead, and other impurities having a higher affinity for the organic extractant than cobalt and nickel, (iii) one SX circuit for extracting both cobalt and magnesium from nickel and separating magnesium from cobalt in the SX circuit, (iv) direct crystallization of nickel sulfate from the final SX raffinate, (v) purification of the aqueous phase containing purified cobalt from step (iii), and (vi) crystallization of cobalt sulfate or other cobalt salts from the aqueous phase containing purified cobalt from step (v).

[0066] [Figure 4]FIG. 4 shows a flowsheet of an embodiment of the present disclosure for purifying the feed solution produced from the process shown in FIG. 1 and FIG. 2 by SX and IX, characterized by (i) direct neutralization with ammonia / ammonium hydroxide in SX, (ii) SX for removing one or more impurities from the group of zinc, calcium, manganese, copper, cadmium, lead, and other impurities having a higher affinity for organic extractants than cobalt and nickel, (iii) one SX circuit for extracting both cobalt and magnesium from nickel and separating magnesium from cobalt in the SX circuit, (iv) direct crystallization of nickel sulfate from the final SX raffinate, (v) thermal decomposition of the ammonium sulfate component in the hydrated nickel sulfate to remove the ammonium component as ammonia for reuse as a base reagent, (vi) purification of the aqueous phase containing purified cobalt from step (iii), and (vii) crystallization of cobalt sulfate or other cobalt salts from the aqueous phase containing purified cobalt from step (vi).

[0067] [Diagram 5] FIG. 5 shows a flowsheet of an embodiment of the present disclosure for purifying the feed solution produced from the process shown in FIG. 1 and FIG. 2 by SX and IX, featuring (i) organic pre-charge, (ii) SX for removal of one or more impurities from the group of zinc, calcium, manganese, copper, cadmium, lead, and other impurities that have a higher affinity for the organic extractant than cobalt and nickel, (iii) two separate SX circuits for separation of cobalt from magnesium and then magnesium from nickel, (iv) direct crystallization of nickel sulfate from the final SX raffinate, (v) purification of the aqueous phase containing the purified cobalt from step (iii), and (vi) crystallization of cobalt sulfate or other cobalt salts from the aqueous phase containing the purified cobalt from step (v).

[0068] [Figure 6]FIG. 6 shows a flowsheet of an embodiment of the present disclosure for purifying the feed solution produced from the process shown in FIG. 1 and FIG. 2 by SX and IX, characterized by (i) direct neutralization with ammonia / ammonium hydroxide in SX, (ii) SX for removing one or more impurities from the group of zinc, calcium, manganese, copper, cadmium, lead, and other impurities having a higher affinity for organic extractants than cobalt and nickel, (iii) two separate SX circuits for separating cobalt from magnesium and magnesium from nickel, (iv) direct crystallization of nickel sulfate in the final SX raffinate, (v) thermal decomposition of the ammonium sulfate component in the hydrated nickel sulfate to remove the ammonium component as ammonia for reuse as a base reagent, (vi) purification of the aqueous phase containing purified cobalt from step (iii), and (vii) crystallization of cobalt sulfate or other cobalt salts from the aqueous phase containing purified cobalt from step (vi).

[0069] [Figure 7] FIG. 7 compares the efficiency of conversion of Mn(II) to stable Mn(III / IV) oxides using air alone and a mixture of SO2 / air.

[0070] [Figure 8] FIG. 8 shows the nickel preloading isotherm using 10% D2EHPA and 62 g / L nickel (sulfate) solution at pH about 5 and 50° C.

[0071] [Figure 9] FIG. 9 shows the sodium scrubbing isotherm from pre-loaded 10% D2EHPA containing 64.7 g / L nickel (sulfate) solution at pH 3.6 and 50° C.

[0072] [Figure 10] FIG. 10 shows the extraction distribution isotherms with Ni preloaded 10% D2EHPA at pH 3.1 and 40° C.

[0073] [Figure 11] FIG. 11 shows the McCabe-Thiele diagram for the extraction of Zn(II) and Cu(II) using 10% D2EHPA preloaded with Ni at pH 3.1 and 40° C.

[0074] [Figure 12] FIG. 12 shows the McCabe-Thiele diagram for the extraction of Mn(II) and Ca(II) using 10% D2EHPA preloaded with Ni at pH 3.1 and 40° C.

[0075] [Figure 13] FIG. 13 shows the nickel preloading isotherm using 25% Cyanex® 272 and 60 g / L nickel (sulfate) solution at 50° C. and pH 6.8-7.0.

[0076] [Figure 14] FIG. 14 shows the scrubbing isotherm of sodium from pre-loaded 25% Cyanex® 272 at pH 5.5 and 50° C.

[0077] [Figure 15] FIG. 15 shows the extraction distribution isotherms of Ni(II), Co(II) and Mg(II) at 40° C. for 25% Cyanex® 272 preloaded with Ni(II).

[0078] [Figure 16] FIG. 16 shows the McCabe-Thiele diagram for the extraction of Co(II) and Mg(II) at 40° C. using 25% Cyanex® 272 preloaded with Ni(II).

[0079] [Figure 17] FIG. 17 shows the McCabe-Thiele diagram for nickel scrubbing from a loaded 25% Cyanex® 272 at pH about 4.2 and pH about 5 and 40° C.

[0080] [Figure 18] FIG. 18 shows the McCabe-Thiele diagram for magnesium scrubbing from a loaded 25% Cyanex® 272 at pH about 3.5 and pH about 4.2 and 40° C. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0081] Description of the embodiments For the purpose of guiding those skilled in the art in the practice of the present disclosure, the following details of terms and processes are provided to clarify the compositions, processes, and their use. The terms in this disclosure are understood to be useful for the purpose of better describing certain embodiments, and should not be considered limiting.

[0082] In the context of the present disclosure, the term "about" when referring to a measurable value, such as an amount, temporal duration, and the like, is intended to encompass variations of ±20%, ±10%, ±5%, ±1%, or ±0.1% from the specified value, where such variations are appropriate for carrying out the disclosed processes.

[0083] In the context of this disclosure, the terms "purified," "purity," and related terms are intended to mean a composition, compound, or material from which impurities or portions of a substance that contaminate or contaminate the substance have been removed. The term purified is a relative term and does not require absolute purity. Thus, for example, a purified compound is one that is more concentrated than the compound is in its natural environment or prior to a purification process.

[0084] In the context of this disclosure, the terms "high purity" and "battery grade," when used with respect to nickel or cobalt salts, mean that the material has minimum levels of nickel or cobalt, and / or low levels of trace elements, such as, for example, Al, Ca, Cd, Cr, Cu, Fe, Mg, Mn, Na, Pb, Si, and Zn, that make it suitable for battery applications. For example, a "high purity" and / or "battery grade" nickel salt may have a nickel content of at least 21% by weight, e.g., from about 22% to about 23% by weight. For example, nickel salts having a nickel content of 22.0%, 22.1%, 22.2%, 22.3%, 22.4%, 22.5%, 22.6%, 22.7%, 22.8%, 22.9%, or 23.0% by weight (e.g., nickel sulfate hexahydrate: NiSO4·6H2O) are considered high purity or battery grade. Similarly, "high purity" and / or "battery grade" cobalt salts may have a cobalt content of at least 20% by weight, such as at least 21% by weight, or, for example, from about 20% to about 22% by weight. For example, a cobalt content of 20.0 wt%, 20.1 wt%, 20.2 wt%, 20.3 wt%, 20.4 wt%, 20.5 wt%, 20.6 wt%, 20.7 wt%, 20.8 wt%, 20.9 wt%, 21.0 wt%, 21.1 wt%, 21.2 wt%, 21.3 wt%, 21.4 wt%, 21.5 wt%, 21.6 wt%, 21.7 wt%, 21.8 wt%, 21.9 wt%, or 22.0 wt% (e.g., cobalt sulfate heptahydrate) would be considered high purity or battery grade.

[0085] In the context of this disclosure, the term "soluble" is intended to mean capable of being molecularly or ionically dispersed in a solvent to form a homogeneous solution. Solubility can be determined by visual inspection, turbidity measurements, or dynamic light scattering.

[0086] Those skilled in the art will recognize that the definitions provided above are not intended to include impermissible combinations. Unless otherwise specified, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this disclosure belongs. The singular terms "a," "an," and "the" include plural referents unless the context clearly dictates otherwise. The term "comprises" means "includes." Thus, comprising "A" or "B" refers to including A, including B, or including both A and B. Although processes and materials similar or equivalent to those described herein can be used in the practice or testing of the present disclosure, suitable processes and materials are described herein. In case of conflict, the present specification, including explanations of terms, shall control. Additionally, the materials, methods, and examples are merely illustrative and are not intended to be limiting.

[0087] Described herein is a process by which high purity cobalt sulfate and high purity (battery grade) nickel sulfate can be produced from nickel and cobalt containing crude feedstocks such as mixed hydroxide precipitate (MHP) without the need for an expensive nickel extraction step with SX, providing economic advantages. The process described herein comprises one or more of the following steps: a) washing nickel / cobalt MHP or other nickel-containing material to remove most or substantially all of the alkali metal ions (e.g., Na+ and K+) and monovalent cationic species (e.g., NH4+), while partially removing other soluble impurities such as magnesium and calcium, and optionally converting divalent manganese ions to stable manganese(IV) oxide using an oxidizing agent while retaining the nickel and cobalt as solid hydroxides; b) Redissolution of nickel and cobalt, optionally followed by jarosite / alunite precipitation as required to remove residual alkali metal and monovalent cation species. This removal step can be carried out simultaneously or sequentially. c) neutralization of the leach solution to precipitate the remaining iron and aluminum as goethite, alumina or hydroxides, together with oxidative precipitation of Mn(IV) oxide with an oxidizing agent to provide chromium hydroxide and partial copper hydroxide, and a feed solution; d) solid-liquid separation to obtain a nickel- and cobalt-rich leach solution (PLS) containing nickel, cobalt, zinc, calcium, manganese (trace amounts), copper, magnesium, and substantially free of alkali metal and monovalent cationic species, and iron, aluminum and chromium; e) Separation of zinc, manganese, copper, and calcium and other impurities (e.g., cadmium, lead) that have a higher affinity for organic extractants than cobalt and nickel from PLS using SX-based extraction and organophosphate extractants (e.g., D2EHPA), while leaving the PLS containing cobalt, nickel, and magnesium in the raffinate; f) leaving the nickel-rich PLS solution substantially free of impurities. Sequential or simultaneous SX-based extraction of both cobalt and magnesium from PLS using an organophosphinic acid extractant (e.g., Cyanex® 272); g) Separation of loaded magnesium from cobalt resulting from co-separation in step f) using a new scrubbing scheme in the SX circuit; h) stripping cobalt from the refined cobalt-loaded organics with the addition of acid to produce a refined cobalt-containing strip liquor (stripping liquid) and regenerating the organics; i) purification of the strip solution containing purified cobalt, for example by ion exchange (IX) to remove trace impurities such as copper and zinc, optionally by oxidative precipitation to remove traces of manganese, or by SX similar to step e) to remove, for example, zinc, manganese, copper and various trace impurities such as calcium, cadmium and lead; j) crystallization of high purity battery grade cobalt sulfate or other cobalt salts from the purified cobalt-loaded strip liquor (step i) above; and k) Direct crystallization of high purity battery grade nickel sulfate from the above final SX raffinate (step f) - refined nickel liquor.

[0088] The processes described herein provide novel refining approaches and schemes that enable significant economic value chains for producing high purity battery grade nickel and cobalt sulfate products as lithium battery cathode precursor materials for the lithium battery industry, for example, to liberate crude nickel and / or crude cobalt bearing raw materials such as nickel laterite ores.

[0089] Advantageously, the processes described herein can be retrofitted to conventional existing commercial processes to produce improved intermediate products or solutions suitable for the subsequent refining processes described herein. Furthermore, the processes described herein offer great potential to expand existing operations or justify investment in greenfield operations and revitalize the nickel laterite industry.

[0090] In a first aspect of the present disclosure, disclosed herein is a process for separating nickel and / or cobalt salts from crude nickel and / or crude cobalt bearing stock, comprising: a) treating crude nickel and / or crude cobalt bearing stock with an iron or aluminum salt under conditions to remove at least some of the one or more alkali metal ions and / or monovalent cation species as jarosite / alunite precipitate to provide a solution having a reduced content of the one or more alkali metal ions and / or monovalent cation species; b) stepwise increasing the pH of the solution from step a) under conditions to provide a feed solution for further purification to produce nickel and / or cobalt salts suitable for producing battery grade nickel or cobalt salts. Consisting of Step b) comprises the step of: i. Iron, ii. Aluminum; iii. Chromium, and iv.Copper The method comprises removing at least some or any combination of one or more of:

[0091] The process of this first embodiment therefore involves precipitation of jarosite / alunite to remove alkali metal ions and monovalent cationic species (Figures 1 and 2).

[0092] Jarosite / alunite precipitation is used to thoroughly remove alkali metal ions (Na+, K+) and monovalent cation (NH4+) species, which can be used alone or in a successive step after washing. The treatment process schemes described herein include washing only, jarosite / alunite treatment only, and optimal combination of washing with jarosite / alunite, depending on the specific conditions related to cost-effective factors such as, for example, the content of alkali metal ions and monovalent cation species, water balance from the washing solution, available highly efficient solid-liquid separation equipment, iron and aluminum content in the MHP, and / or available forms / sources of iron and aluminum suitable for jarosite / alunite precipitation.

[0093] Precipitation of jarosite / alunite can be carried out simultaneously with or consecutively after leaching. If necessary, various iron and aluminum forms, preferably their sulfates or carbonates and oxides or hydroxides, can be added to obtain the optimum ratio to alkali metal ions and monovalent cation species for efficient jarosite / alunite precipitation, which may be accompanied by the presence of an oxidizing agent to oxidize iron(II) to iron(III) and manganese(II) to stable manganese(IV) oxide.

[0094] Typical nickel laterite ores are rich in iron and aluminum, which partially enter the PLS and are removed as hydroxides by neutralization prior to precipitation of the MHP. If required, a portion of the iron and aluminum hydroxides can be utilized as the iron source for the jarosite process.

[0095] A known problem with the precipitation of iron and aluminum hydroxides in conventional processes is the co-precipitation of nickel and cobalt, which becomes important at higher pH for more complete removal of iron and aluminum to meet the standard specifications of MHP. To minimize the loss of nickel and cobalt in iron and aluminum hydroxides, it is conventionally adopted to precipitate iron and aluminum in stages and recycle the final stage precipitate to leaching, but high recycle loadings significantly reduce the process efficiency and increase the operating costs.

[0096] The disclosed process is beneficial not only for providing a scheme for processing intermediate products, e.g., MHP, but also for helping improve the entire nickel laterite ore process. Current processes do not require exhaustive removal of iron and aluminum, since precipitation of jarosite / alunite requires the presence of stoichiometric amounts of iron and aluminum species relative to the alkali metal ions (Na+, K+) and monovalent cation (NH4+) species to remove these important impurities. Thus, MHP can contain the desired ratio of iron / aluminum to the sum of the alkali metal and monovalent cation components for the subsequent precipitation of jarosite / alunite.

[0097] Alternatively, the jarosite / alunite process is applicable for the removal of alkali metal ions (Na+, K+) and monovalent cation (NH4+) species during leaching of nickel laterite ores or after leaching prior to MHP precipitation. Coprecipitation of nickel and cobalt in jarosite precipitates is known to be very low.

[0098] In either the primary leaching process or the MHP purification process, the stoichiometric portion of MHP relative to the stoichiometric portion of the total alkali metal ion (Na+, K+) and monovalent cation (NH4+) species can be utilized for neutralizing the acid generated during jarosite / alunite precipitation, or in other words, the acid generated is simultaneously utilized to dissolve an equivalent amount of MHP without the need to add other basic reagents to avoid the introduction of impurities. In application, a portion of the jarosite can be recycled to seed the solution at an appropriate dose to improve the precipitation rate of jarosite.

[0099] Once jarosite precipitation is complete, the pH of the slurry is increased, preferably stepwise from a low pH to a higher pH, to minimize nickel and cobalt losses, to precipitate most of the remaining iron(III) and crystalline forms such as goethite, as well as to precipitate the remaining aluminum as alunite / alumina to iron hydroxide and aluminum hydroxide. A basic reagent, preferably nickel hydroxide, magnesium oxide / hydroxide, limestone / lime, can be added for the neutralization process, which also removes chromium and a portion of the copper as hydroxides.

[0100] Optionally, the process of this first aspect may also include a washing step to remove alkali metal ions and monovalent cation species (Figures 1 and 2). Thus, the method may further comprise, prior to step a), treating the crude nickel and / or crude cobalt bearing stock with water or an aqueous solution comprising dilute sulphuric acid under conditions to remove at least a portion of the alkali metal ion or univalent cation species.

[0101] Washing of MHPs may be included in conventional existing purification processes, but is not specifically designed to remove most, or preferably substantially all, of the alkali metal ion (Na+, K+) and monovalent cation (NH4+) species.

[0102] Washing is the first step of the present method for treating MHP, in which the MHP is repulped with a wash solution containing water and / or sulfuric acid to remove a substantial portion, preferably substantially all, of the alkali metal ions (Na+, K+) and monovalent cationic species (NH4+) with minimal dissolution of nickel and cobalt. The wash step can be carried out at a pH of 7 or higher. Multiple washes may be performed to achieve a desired degree of washing efficiency. Washing simultaneously removes a significant portion of other soluble species, such as calcium and magnesium, for example, as an added advantage in favor of subsequent purification by SX. Optionally, a portion, preferably most, of the Mn(II) is simultaneously converted to stable solid Mn(IV) oxide using an oxidizing agent.

[0103] Optionally, the process of this first aspect may also comprise oxidative conversion of divalent Mn(II) to the stable Mn(III / IV) form. Thus, the method may comprise treating the first nickel and / or cobalt bearing stock extract, the second nickel and / or cobalt bearing stock, and / or the third nickel and / or cobalt bearing stock extract with an oxidizing agent under conditions to oxidize any iron(II) to iron(III) and any manganese(II) to manganese(III / IV) to provide a rich liquor solution comprising nickel and / or cobalt and having reduced concentrations of one or more alkali metal ions, monovalent cation species, iron, aluminum, chromium, copper, and manganese relative to the crude nickel and / or crude cobalt bearing stock, the rich liquor solution being suitable for further purification to produce high purity battery grade nickel and / or cobalt salts.

[0104] If necessary, a suitable oxidizing agent may be optionally added to the above neutralization process under controlled conditions, referred to as oxidative neutralization, to convert any iron(II) to iron(III) and Mn(II) to stable Mn(III / IV) oxides. It is preferable to remove most of the manganese early to facilitate subsequent purification by solvent extraction.

[0105] For example, nickel and cobalt losses in solid forms such as jarosite / alunite, goethite and Mn(IV) oxide are known to be minimal compared to amorphous iron and aluminum hydroxides. Furthermore, the morphology of these solid phases facilitates separation of the liquid and solids by filtration or other separation means.

[0106] After the above treatment, the resulting feed solution is substantially free of alkali metal ions (Na+, K+) and monovalent cation (NH4+) species, iron, aluminum and chromium, and the major metals - nickel, cobalt, zinc, remaining copper and manganese in the feed solution, copper and manganese with calcium and magnesium are partially removed for further purification.

[0107] In a second aspect of the disclosure, disclosed herein is a process for obtaining purified nickel and cobalt from a feed solution produced according to the first aspect, the process comprising: a) reducing the concentration of zinc, calcium, manganese, copper, cadmium, lead or other metal impurities in the feed solution that have a higher affinity for the organic extractant than cobalt and nickel by contacting the feed solution with an organophosphoric acid extractant in a hydrocarbon diluent and separating the organic and aqueous phases under solvent extraction conditions to produce an aqueous raffinate containing purified cobalt and nickel; b) contacting the aqueous raffinate with a cobalt-selective extractant in a hydrocarbon diluent under solvent extraction conditions and separating the organic and aqueous phases to produce an organic phase comprising purified cobalt and an aqueous phase comprising purified nickel; c) selectively scrubbing and stripping the organic phase to obtain an aqueous phase containing purified cobalt; d) purifying the aqueous phase comprising purified cobalt to produce a further aqueous phase comprising purified cobalt; e) recovering cobalt from the further aqueous phase; and f) Recovering nickel from the purified nickel-containing aqueous phase.

[0108] In a particular embodiment, the feed solution produced in the process of the first aspect is further purified by SX and IX to separate impurities from cobalt and cobalt from nickel, where the cobalt-rich liquor is purified by ion exchange (IX) or SX to remove various trace impurities such as zinc and copper to produce purified cobalt liquor for cobalt sulfate crystallization, while the major metallic nickel in the final SX raffinate is fed directly to crystallization to produce high purity nickel sulfate. The purification process comprises the following scheme:

[0109] Impurity SX (Figures 3, 4, 5, and 6)

[0110] The zinc, calcium, manganese and copper, cadmium, lead impurities, as well as other impurities that have a higher affinity for the organic extractant than the cobalt and nickel in the feed solution, are extracted and separated from the cobalt and nickel with an organophosphoric acid (D2EHPA) extractant in a hydrocarbon diluent such as Exxsol D80 and Escaid 110 and optionally in the presence of a phase modifier, while the cobalt and nickel remain in the raffinate together with some magnesium. There are the following options for removing the organic loaded impurities: (a) using sulfuric acid by controlling the calcium concentration below saturation when the calcium concentration in the system is low, to avoid the formation of gypsum, and (b) using hydrochloric acid when the calcium concentration in the system is relatively high and there is a risk of gypsum formation.

[0111] Separation of cobalt and magnesium (Figures 3, 4, 5, and 6)

[0112] For example, organophosphinic acids (e.g., Cyanex® 272 or Ionquest® 290) in hydrocarbon diluents such as Exxsol D80 and Escaid 110, optionally in the presence of a phase modifier, can be used to separate cobalt, magnesium and nickel into their respective liquors. Two SX schemes may be used.

[0113] SX scheme option 1 for Co and Mg (Figures 3, 4): In a particular embodiment, cobalt and magnesium are co-extracted and separated from nickel, loaded magnesium is separated from cobalt by an internal scrubbing scheme in the SX circuit, the co-extracted nickel is first scrubbed from the loaded organics to obtain a nickel-rich scrubbed liquor that is recycled to the extract, and the extracted magnesium is scrubbed from the loaded organics to produce a magnesium-rich liquor that contains some co-scrubbed cobalt, which is then extracted by a small stream of organic solution and recycled to the main scrubbing section. This scheme allows the separation of the respective magnesium and cobalt streams from nickel in just one SX circuit.

[0114] Co and Mg SX scheme option 2 (Figures 5, 6): In certain other embodiments, cobalt is selectively extracted and the co-extracted nickel and magnesium are scrubbed and recycled to the extraction, thus separating the cobalt from the magnesium and nickel. The magnesium in the raffinate is then extracted and separated from the nickel in a separate solvent extraction circuit using a portion of the same organic solution.

[0115] Purification and crystallization of cobalt liqueur (Figure 3, Figure 4, Figure 5, Figure 6)

[0116] The cobalt-loaded strip liquor is purified by ion exchange (IX) to remove trace impurities such as copper, for example, using an iminodiacetic acid type resin, and zinc, for example, using a D2EHPA-impregnated resin, or both copper and zinc are simultaneously removed using an aminophosphonic acid resin. Trace manganese can be selectively removed by oxidative precipitation, for example, using ozone, a mixture of SO2 / O2 (air) in a ratio acting as an oxidizing agent, or a suitable oxidizing agent such as peroxymonosulfuric acid (Caro's acid) and peroxydisulfuric acid. If desired, various trace impurities including zinc, copper, manganese, calcium, cadmium, and lead can be removed from the cobalt-loaded strip liquor by SX using an organophosphoric acid (D2EHPA) extractant as described above. The purified cobalt liquor is fed to crystallization to produce high purity cobalt sulfate or other cobalt salts.

[0117] Direct crystallization of nickel sulfate (Figures 3, 4, 5, and 6)

[0118] The final raffinate - refined nickel liquor - is fed directly to crystallization to produce high purity nickel sulfate without the expensive step of nickel separation by SX.

[0119] Neutralizing SX

[0120] Stoichiometric amounts of acid equivalent to the extracted divalent metal will be generated during the SX process using acidic extractants such as organophosphoric acids (e.g., D2EHPA) and organophosphinic acids (e.g., Cyanex® 272). It is therefore important in the SX scheme to be able to produce the final high purity nickel sulfate product without contamination. Two approaches and schemes may be used.

[0121] Scheme 1 - Organic pre-loading (Figures 3 and 5)

[0122] Certain embodiments utilize pre-charging nickel sulfate directly into the organic solution that is available in the process. Other metal sulfates, carbonates, or oxides / hydroxides may be used to pre-charge, for example, cobalt sulfate and magnesium sulfate, or their oxides / hydroxides, but nickel sulfate or nickel carbonate, or oxides / hydroxides are preferred because any nickel introduced into the feed solution does not require further separation, compared to cobalt or magnesium salts that must be separated again in the subsequent SX scheme. For example, suitable base reagents such as nickel hydroxide, sodium hydroxide or sodium carbonate, ammonia / ammonium hydroxide or ammonium carbonate, and magnesium oxide / hydroxide or magnesium carbonate can be used for neutralization or pH control in the pre-charge.

[0123] Alternatively, the stripped organics can be pre-neutralized with a basic reagent such as sodium hydroxide or sodium carbonate, or ammonia / ammonium hydroxide or carbonate to produce pre-neutralized organics for pre-loading with nickel by exchange.

[0124] The nickel preloaded organic solution is then washed with a scrubbing solution containing water and / or sulfuric acid and / or nickel sulfate to remove entrained and extracted sodium or ammonium ions and avoid contamination of the system. The scrubbed organic solution is then fed to the respective main SX circuit where the metal ions are extracted through exchange of the preloaded nickel with minimal or no pH control.

[0125] Scheme 2 - Direct Neutralization and Heat Treatment (Figures 4 and 6)

[0126] Another approach employs direct neutralization of the acids generated during SX using ammonia / ammonium hydroxide under controlled conditions, preferably as ammonia which can be recycled in the process as the base reagent, avoiding the formation of nickel ammonium double salts or ammonium sulfate salts and the subsequent selective thermal decomposition of the ammonium component in the hydrated nickel sulfate.

[0127] The present disclosure also provides schemes for improving the overall upstream processing of nickel laterite ores or other nickel-containing materials or solutions, including the following schemes:

[0128] Upstream Scheme 1: Controlled neutralization of iron and aluminum precipitation to produce MHP containing the desired ratio of iron and aluminum to alkali metal ion (Na+ and K+) and monovalent cation (NH4+) species for precipitation of jarosite / alunite in the subsequent refining process described herein.

[0129] Upstream scheme 2: Simultaneous or sequential leaching and jarosite precipitation followed by neutralization and solid-liquid separation to produce a feed solution substantially free of alkali metal ions (Na+ and K+) and monovalent cation (NH4+) species. This feed solution can be fed directly to the subsequent purification schemes SX and IX described herein, or as a subsequent leaching option, directly to the production of MHP substantially free of alkali metal ions (Na+ and K+) and monovalent cation (NH4+) species, as shown in Figure 1.

[0130] Further details of embodiments of the processes disclosed herein are described with reference to the accompanying drawings.

[0131] MHP processing scheme (Figure 1)

[0132] The methods and schemes described herein for the treatment of various MHPs to produce a feed solution (126) suitable for subsequent purification processes to produce high purity battery grade cobalt sulfate and nickel sulfate, respectively, without a costly primary metal-nickel separation step, are shown in FIG.

[0133] Methods for removing alkali metal ions (Na+, K+) and monovalent cation (NH4+) species include washing (105) and / or co-leaching-jarosite / alunite (119) or sequential leaching (112) and jarosite / alunite (115). Washing (105) or jarosite / alunite (119, 112, and 115) can be used alone or in combination.

[0134] The steps of the processing scheme shown in FIG. 1 are described below.

[0135] Washing (or washing step) (105): A typical MHP (101) from a conventional existing nickel laterite process, or MHP (164, 191) produced from an upstream nickel laterite process described herein (FIG. 2), is washed with a washing solution (104) of deionized water or dilute sulfuric acid at an appropriate liquid to solid ratio to remove a portion, preferably a majority, and desirably a complete portion, of the alkali metal ions (Na+, K+) and monovalent cation (NH4+) species (108). Other soluble components such as, for example, alkaline earth metals, Ca(II) and Mg(II), nitrate ions and chloride ions may also be partially removed. Washing can be done in a variety of ways, including one or more repulpings, filter cake rinsings, and combinations of these means, or continuous countercurrent decantation in multiple stages.

[0136] In the wash, an oxidizing agent (103) can be added to convert some, preferably most, of the Mn(II) ions to stable solid Mn(IV) oxides. The oxidizing agent may be selected from, but is not limited to, air, oxygen, ozone, oxides, persulfuric acid, peroxides, peroxymonosulfuric acid (Caro's acid), oxidizing mixtures of sulfur dioxide (SO2) with air or oxygen in appropriate ratios. The addition of the oxidizing agent is controlled by monitoring the slurry potential and pH to minimize the oxidation of Co(II) and Ni(II) to Co(III) and Ni(III) oxides. For continuous addition and easy control to minimize the oxidation of Co(II) and Ni(II), oxidizing agents of weak to medium oxidizing power, such as air, oxygen, and their mixtures with sulfur dioxide in appropriate ratios, and Caro's acid, are preferred. The oxidation process is preferably carried out under conditions where most (>95%) of the MHP is insoluble in the solid state and minimizes the oxidation of Co(II) and Ni(II) to solid forms of Co(III) and Ni(III) oxides.

[0137] The liquids and solids in the wash solution are separated (107) to produce a washed MHP (109) with desirable washing efficiency of alkali metal ions and monovalent cation species and reduced content of other soluble species such as, for example, Ca(II), Mg(II), Mn(II), nitrate and chloride ions.

[0138] Leaching (or leaching step) (112) and jarosite / alunite (115 and 119). In leaching, a quantitative amount of sulfuric acid is added in a net stoichiometric ratio to the amount of MHP, either all at once or continuously, to dissolve the MHP. Depending on the content of alkali metal ions (Na+, K+) and monovalent cation (NH4+) species, the precipitation of jarosite / alunite (119) can be carried out either simultaneously with the leaching (119) or continuously after leaching (115). The precipitation of jarosite / alunite proceeds according to the following reactions: [ka]

[0139] Either simultaneously or consecutively with the leaching and jarosite / alunite treatment, an equal amount of MHP is added to neutralize the acid generated during the jarosite / alunite precipitation (119) according to reaction (1) and to control the desired pH range for the jarosite / alunite treatment (119) without the need to use other basic reagents that may introduce more impurities. In this way, the acid generated is simultaneously available to dissolve an equivalent portion of the MHP.

[0140] When the Fe(III) and Al(III) contents are insufficient for the formation of jarosite / alunite and to completely remove the monovalent cationic species (Na+, K+ and NH4+) according to reaction (1), various iron aluminum forms, preferably Fe(III) and Al(III) hydroxides, oxides and sulfates, can be added in a stoichiometric ratio of Fe(III) / Al(III) to Na+ / K+ / NH4+ of 3:1 or more, preferably in the range of 4:1 to 5:1 ratio.

[0141] Iron and aluminum hydroxides from conventional upstream precipitation processes are potential sources of iron and hydroxides. Improvements in the upstream processing of nickel laterite ores for controlled Fe / Al precipitation so that the desired ratio of (Fe+Al) to (Na++K++NH4+) is present in the feed solution and in the MHP is shown in Figure 2 and is described below.

[0142] Jarosite precipitation can be operated at temperatures ranging from 60-100°C and pH 1.6-2.0, preferably 85-95°C and pH 1.8-2.0, and redox potentials (Eh) in the stable region of jarosite formation. Recycling some of the jarosite as seeds is preferred to accelerate the kinetics of jarosite / alunite precipitation. If necessary, an oxidizing agent may be added to oxidize the lower oxidation valence of the iron species, e.g., from Fe(II) to Fe(III).

[0143] After jarosite precipitation is complete, alunite precipitation may be carried out continuously, preferably under conditions ranging from 85-95°C and pH 3.5-5.0, where the pH of the slurry is raised by neutralization (122), which can be preferably carried out in stages, for example at pH 2.5, pH 3.5, and pH 4-4.5, to precipitate the remaining iron(III) as goethite, oxide / hydroxide, aluminum as alunite and alumina / hydroxide, while simultaneously precipitating chromium and some of the copper as hydroxides. Some candidates for base reagent (121) for neutralization (122) include nickel oxide / hydroxide, magnesium oxide / hydroxide, limestone / lime, and thoroughly washed MHP substantially free of alkali metal ions and monovalent cation species depending on the particular requirements. An oxidizing agent (103) can optionally be present to oxidize Fe(II) to Fe(III) and / or most of the Mn(II) to solid Mn(III / IV), a process called “oxidative neutralisation” (122).

[0144] The slurry (123) from neutralization (122) is then transferred to solid-liquid separation (124) to dispose of the residue (125) containing jarosite, alunite, goethite, hydroxides of Fe(III), Al(III), Cr(III) and Cu(II), and any manganese (III / IV) oxides, while the resulting feed solution (126) is substantially free of alkali metal ions (Na+, K+) and monovalent cation (NH4+) species, as well as iron, aluminum, chromium, including nickel (major), cobalt, zinc, calcium, manganese (trace) and partially reduced copper, and is suitable for the subsequent purification processes described herein as shown in Figures 3, 4, 5 and 6.

[0145] Overall processing scheme (Fig. 2)

[0146] The present disclosure not only provides a scheme as shown in FIG. 1 for purifying the MHP intermediate product from a conventional or existing nickel laterite process, but also provides a scheme as shown in FIG. 2 for the upstream processing of nickel laterite ore or other nickel-bearing raw materials and solutions, The support material and solution are used to directly produce a suitable feed solution suitable for subsequent refining processes (Figures 3, 4, 5, and 6) or to produce the desired MHP for refining (Figure 2) using schemes presented herein such as those shown in Figure 1. Scheme options for the overall processing of nickel laterite ore or nickel bearing raw materials and solutions are described as follows:

[0147] Scheme Option 1 - Improved conventional process for producing alkali metal free feed solution / MHP

[0148] Jarosite / alunite precipitation has been employed in the prior art to remove or control iron and aluminum concentrations and / or generate acid, with the addition of alkali metal salts (Na2CO3 or Na2SO4) or ammonium salts such as, for example, (NH4)2SO4. The present process is directed to utilizing jarosite / alunite precipitation for the removal of alkali metal ions (Na+, K+) or monovalent cation (NH4+) species, preferably requiring Fe3+ and Al3+ in excess of the stoichiometric amounts via reaction (1).

[0149] It is advantageous to take advantage of the abundant iron and aluminum components in the feed material, e.g. nickel laterite ore, in the leaching, in order to remove these monovalent components early by precipitation of jarosite / alunite. The jarosite and alunite forms are easily separated by filtration and other liquid-solid separation techniques. It is known that the losses of nickel and cobalt due to precipitation in jarosite and alunite are very small. Scheme option 1 consists of the following steps:

[0150] For example, leaching by conventional leaching methods such as high pressure acid leaching (HPAL) and atmospheric leaching (AL) can be carried out simultaneously with jarosite / alunite precipitation in one step (156) under the conditions described above for step (115) or in successive leaching steps (152) and jarosite / alunite (154) (FIG. 1).

[0151] The slurry (155 or 157) is neutralized (158) with a base reagent (121) to remove the remaining iron as goethite / hydroxide and aluminum as alumina / hydroxide, along with other metal hydroxides such as chromium and copper hydroxide. An oxidizing agent (103) can optionally be added to oxidize any Fe(II) to Fe(III) and Mn(II) to stable solid Mn(IV) oxide under conditions described above for the neutralization step (122) (FIG. 1).

[0152] The slurry (159) from neutralization (158) undergoes solid-liquid separation (160) to obtain a feed solution (162) that is substantially free of monovalent cations (Na+, K+, NH4+), iron, aluminum and chromium, and a residue (161) that contains jarosite / alunite, goethite, alumina and hydroxides of iron, aluminum, chromium and copper, and Mn(III / IV) oxides.

[0153] The feed solution (162) can be fed to a subsequent purification scheme, as desired, as shown in Figures 3, 4, 5, and 6. Depending on the nickel and / or cobalt concentration, the feed solution (162) may be concentrated by water separation means, e.g., membrane distillation, before being fed to the subsequent purification schemes shown in Figures 3, 4, 5, and 6.

[0154] Alternatively, feed solution (162) can undergo mixed hydroxide precipitation (163) to produce MHP (164), which is then leached in step (112) (FIG. 1) to produce feed solution (126) for further purification using the schemes shown in FIGS. 3, 4, 5, and 6 to produce high purity battery grade nickel and cobalt sulfates.

[0155] Scheme Option 2 - Conventional process modified to produce MHP with desired Fe / Al to Na / K ratios

[0156] In conventional nickel laterite processes, a challenging problem is the loss of nickel and cobalt due to adsorption / precipitation by iron and aluminum hydroxide precipitates. To minimize losses, iron and aluminum precipitation is usually operated in multiple stages with the final stage of iron and aluminum hydroxide precipitates being recycled to leaching, but this significantly reduces the process efficiency and increases the process costs.

[0157] As mentioned above, the MHP feeding the flowsheet shown in Figure 1 allows for the presence of iron and aluminum in the desired ratios relative to the alkali metal ions and monovalent cation species required for the subsequent jarosite / alunite precipitation. Thus, exhaustive removal of iron and aluminum by primary neutralization is not required, and the final stage recycle of iron and aluminum hydroxide precipitates as practiced in conventional processes can be reduced or eliminated. The main steps of scheme option 2, as well as the principles for controlling the iron and aluminum content within the MHP, are described below.

[0158] After leaching (152) and solid-liquid separation (181), the PLS (183) is neutralized with a basic reagent such as limestone or lime (185) to precipitate iron and aluminum (184) under controlled conditions, leaving behind partial Fe(III) and Al(III) relative to monovalent cations (Na++K++NH4+) in the PLS, which is measured based on the ratio of MHP (191), preferably in the range of (3-6):1, more preferably (4-5):1.

[0159] After solid-liquid separation (187) of the slurry (186), the residue (188) is discarded and the PLS (189) is fed to a mixed hydroxide precipitation (190) by addition of a base reagent, e.g., magnesium oxide / hydroxide (14), to produce MHP (191) with the desired ratio of [Fe(III)+Al(III)] to (Na++K++NH4+) for jarosite / alunite precipitation (115 or 119) and to remove the monovalent cations (Na++K++NH4+) in a subsequent purification process.

[0160] Impurities (typically Zn(II), Mn(II), Cu(II) and Ca(II)) Solvent Extraction (Figures 3, 4, 5 and 6)

[0161] The impurities Zn(II), Mn(II), Cu(II) and Ca(II), Cd(II), Pb(II), as well as other impurities that have a higher affinity for the organic extractant than cobalt and nickel in the feed solution (126, 162), are extracted with an organic phosphoric acid, e.g., di(2-ethylhexyl)phosphoric acid (DEHPA). This SX scheme consists of the following steps:

[0162] The stripped organics (211) can be treated with nickel sulfate (126 or 162, or 221 or 331) as shown in Figure 3 and nickel sulfate (419 or 503) as shown in Figure 5 using a base reagent (213) such as, for example, sodium hydroxide or sodium carbonate or ammonia / ammonium hydroxide to produce nickel pre-loaded organics (216) and sodium sulfate or ammonium sulfate by-product (215). Alternatively, the stripped organics can be pre-neutralized (222) with a base reagent (213) such as, for example, sodium hydroxide or sodium carbonate or ammonia / ammonium hydroxide to produce pre-neutralized organics (223) for nickel pre-loading by exchange (212).

[0163] The pre-charged organics (216) are scrubbed (217) with a scrubbing solution (218) containing water and / or dilute sulfuric acid and / or nickel sulfate to remove extracted and entrained sodium or ammonium ions resulting in a scrubbed liquor (219) which is recycled to the pre-charge (212).

[0164] The scrubbed / pre-loaded organics (220) are fed to an impurity extraction (201) where the impurities Zn(II), Mn(II), Cu(II) and Ca(II), Cd(II), Pb(II) as well as other impurities having a higher affinity for the organic extractant than the cobalt and nickel in the feed solution (126 or 162) are extracted into the organic phase by exchanging the pre-loaded nickel for the aqueous phase. Minimal pH control with sulfuric acid may optionally be employed to maintain a desired pH profile during the multiple stages of extraction, if desired.

[0165] The loaded organics (202) are scrubbed (203) with a scrubbing solution of water and / or sulfuric acid and / or metal sulfates (205) to remove the extracted nickel and cobalt, resulting in a scrubbing liquor (204) that is recycled to the extraction (201).

[0166] The scrubbed organics (206) are stripped (207) using a sulfuric acid or hydrochloric acid (HCl) strip solution (208) to regenerate the organics (211) to provide a precharge (212) or, optionally, a preneutralization (222).

[0167] The choice of acid, H2SO4 or HCl (208), for stripping (207) depends on the concentration of calcium. When the calcium concentration is significantly below the saturation concentration that forms gypsum, sulfuric acid is preferred for stripping under controlled conditions to avoid the formation of gypsum, since the sulfate matrix is ​​the same. When the calcium concentration is high, hydrochloric acid can be employed to avoid the formation of gypsum. If hydrochloric acid is used, a washing step may be required to remove chloride ions entrained in the organic phase before transferring the stripped organics (211) for precharging (212) or preneutralization (222).

[0168] The stripped liquor (210), which contains impurities (typically Zn(II), Mn(II), Cu(II) and Ca(II)), can be further processed to separate and recover specific metals of interest. For example, zinc can be separated from other impurities by selective stripping, if desired, to produce separate by-products.

[0169] It is known that trace amounts of iron, aluminum and other high-value ions are strongly extracted by D2EHPA and periodic bleed treatment of the organics with 6M HCl may be necessary depending on loading and capacity requirements.

[0170] Extraction of cobalt and magnesium in one SX cycle loaded with organic matter (Figure 3)

[0171] The present disclosure provides a SX scheme using an organic phosphinic acid, such as bis(2,4,4-trimethylpentyl)phosphinic acid (Cyanex® 272 or Ionquest® 290), in a hydrocarbon diluent, optionally in the presence of an organic phase modifier, to extract both cobalt and magnesium (301) from the raffinate (221), separating the magnesium from the cobalt in the circuit. The scheme consists of the following steps:

[0172] The stripped organics (324) can be preloaded (325) with nickel sulfate (221 or 331) which can be used in the process with a basic reagent (213) such as ammonium hydroxide or ammonium carbonate, or sodium hydroxide for neutralization to produce preloaded nickel organics (326) and ammonium sulfate or sodium sulfate by-product (215). Alternatively, the stripped organics (324) can be preneutralized (332) with a basic reagent (213) such as sodium hydroxide or sodium carbonate, or ammonium hydroxide to produce preneutralized organics (333) for nickel preloading (325) in exchange.

[0173] The pre-charged organics (326) are scrubbed (327) with a scrubbing solution of water and / or sulfuric acid and / or nickel sulfate (328) and extracted and entrained sodium and ammonium ions are removed from the organic phase into a scrubbed liquor (329) that is recycled to the pre-charge (325).

[0174] Both the cobalt and magnesium in the raffinate (221) are extracted (301) with the scrubbed / pre-loaded organics (330) and separated from the nickel remaining in the raffinate (331).

[0175] The loaded organics (302) are first scrubbed (303) with a scrubbing solution of water and / or sulfuric acid and / or cobalt sulfate (304) to selectively remove extracted nickel from the organic phase into a scrubbed liquor (305) that is recycled to the Co / Mg extraction (301).

[0176] The nickel-scrubbed organics (306) are further scrubbed (307) with a scrub solution of water and / or sulfuric acid and / or cobalt sulfate solution (308) to remove the extracted magnesium from the organic phase to obtain a magnesium-rich scrubbed liquor (309) that contains some co-scrubbed cobalt.

[0177] The co-scrubbed cobalt in the magnesium-rich scrubbed liquor (309) is then extracted (310) with a small amount of the stripped organics (321) and a basic reagent (311), such as ammonia / ammonium hydroxide or sodium, can be used directly for neutralization if necessary. Alternatively, the stripped organics (321) can be pre-charged (334) with a solution of magnesium sulfate (MgSO4) (312) and a basic reagent (311) for pH adjustment, preferably magnesium oxide / hydroxide and / or ammonia / ammonium hydroxide, or sodium hydroxide or sodium carbonate, and then fed for extraction of the cobalt (310) through exchange of the pre-charged base metal.

[0178] Ammonium or sodium entrained or extracted into the organic phase in the above steps (334 and 310) is removed from the organic phase by a scrubbing step (314) into a scrubbed liquor (316) that is recycled to the extraction (310).

[0179] The magnesium-rich raffinate (312) can be further processed to produce magnesium sulfate, or magnesium oxide or magnesium hydroxide for recycling as base (311) for precharge and neutralization in the process.

[0180] A minor stream (317) of cobalt-loaded organics is combined with the main stream (306) of nickel-scrubbed organics as feed (318) for magnesium (307) scrubbing.

[0181] The magnesium scrubbed organics (319) are stripped (320) with a sulfuric acid strip solution (323) to obtain a cobalt loaded stripped liquor (322) and regenerate the organics (321 and 324) which are recycled to the pre-charge (325 or 334). If desired, the cobalt can be stripped with other acids, e.g., hydrochloric acid and nitric acid, respectively, to produce other salt products, and wash steps may be required before and after stripping to avoid cross contamination with carryover of the organic phase.

[0182] Cobalt loaded strip liquor (322) containing traces of zinc and copper can be purified by IX (601) using a type of iminodiacetic acid resin such as Lewatit® TP207 to remove copper, followed by zinc IX using a resin impregnated with D2EHPA such as Lewatit® VP OC 1026. Alternatively, an aminophosphonic acid chelating resin such as Purolite® S950 can be used for both copper and zinc removal.

[0183] It is known that nickel can be separated from cobalt, if desired, by means of a bispicolylamine chelating resin such as Dowex® M4195.

[0184] Small amounts of manganese may also be present in the cobalt loaded strip liquor (322) which can be selectively precipitated as Mn(III / IV) oxide using oxidizing agents such as ozone, a mixture of SO2 / O2 (air) in a ratio that acts as an oxidizing agent, peroxymonosulfuric acid (Caro's acid) and peroxydisulfuric acid.

[0185] The purified cobalt liqueur (603) is fed to cobalt crystallization (604) to produce high purity battery grade hydrous cobalt sulfate (605).

[0186] The raffinate (331) from the Co / Mg SX (301) is fed directly to crystallization (701) to produce high purity battery grade hydrated nickel sulfate (702).

[0187] Optionally, if desired, the cobalt-loaded strip liquor (322) can be purified to remove various trace impurities such as, for example, zinc, copper, calcium, manganese, cadmium, lead, and other impurities by SX with an organophosphoric acid (D2EHPA) extractant as described above.

[0188] Extraction of cobalt and magnesium in one SX cycle using direct neutralization (Figure 4)

[0189] An alternative SX scheme (Figure 4) that uses direct neutralization of the acid generated during the SX processes (201) and (301) with ammonia / ammonium hydroxide (222) instead of pre-charging as shown in Figure 3.

[0190] The main SX scheme (201) using D2EHPA for separation of impurities (typically Zn(II), Mn(II), Cu(II) and Ca(II)) and subsequent extraction of cobalt and magnesium (301) is the same as shown in Figure 3. The ratio of aqueous to organic matter (A / O) is selected and controlled to avoid the formation of nickel ammonium sulfate double salt during the SX process.

[0191] The ammonium sulfate produced in the neutralization (201 and 301) eventually becomes nickel in the SX raffinate (331). The partial ammonium sulfate crystallizes as a nickel ammonium sulfate double salt with hydrated nickel sulfate (703).

[0192] The thermal decomposition step (704 or 706) is designed to convert the double sulfate to nickel sulfate (708), where ammonium sulfate can decompose to ammonia, sulfur trioxide and nitrogen gas (705) at temperatures above 280° C. It is preferable to selectively decompose only the ammonium component to ammonia (222) for recycling as a base reagent, to which an oxide / hydroxide, e.g. nickel oxide / hydroxide (707), may be added to form nickel sulfate (708). If present, nitrate, nitrite and nitrite components will be at least partially removed in this step.

[0193] Extraction of cobalt and magnesium by separate SX circuits with pre-loaded organics (Figure 5)

[0194] The present disclosure provides an alternative SX scheme for first extracting cobalt from magnesium and nickel, and then extracting magnesium from nickel using the same Cyanex® 272, as shown in Figure 5. The SX scheme for removing impurities (typically Zn(II), Mn(II), Cu(II), and Ca(II)) using D2EHPA is the same as that described above and shown in Figure 3.

[0195] An alternative SX scheme for the extraction and separation of cobalt and magnesium by separate SX circuits includes the following steps:

[0196] The stripped Cyanex® 272 (410 and 511) is pre-loaded (411) with nickel sulfate (419 or 503) available in the process to generate nickel-loaded organics (413) and ammonium sulfate or sodium sulfate by-product (215) with a basic reagent (213) such as, for example, sodium hydroxide or sodium carbonate, or ammonia / ammonium hydroxide. Alternatively, the stripped organics (410 and 511) can be pre-neutralized (420) with a basic reagent (213) to generate pre-neutralized organics (421) for pre-loading (411) with nickel by exchange.

[0197] The pre-charged organics (413) are scrubbed (414) with a scrubbing solution of water and / or sulfuric acid, and / or nickel sulfate (415) and extracted and entrained sodium or ammonium ions are removed from the organic phase into a scrubbed liquor (416) that is recycled back to the pre-charge (411).

[0198] The cobalt in the raffinate (221) from impurity SX (201) is extracted (401) with a portion of the scrubbed / pre-loaded organics (418) by exchange and separated from the magnesium and nickel in the raffinate (419).

[0199] The cobalt-loaded organics (402) are scrubbed (403) with a scrubbing solution (404) containing water and / or sulfuric acid and / or cobalt sulfate, and the extracted nickel and magnesium are removed in a scrub liquor (405) that is recycled to the cobalt extraction (401).

[0200] The nickel and magnesium scrubbed organics (406) are stripped (407) with a sulfuric acid strip solution (408) to regenerate the organics (410) which are recycled to the pre-charge (411).

[0201] Cobalt loaded strip liquor (409), containing small amounts of zinc and copper, is purified by IX (601) as described above. If desired, small amounts of nickel can be removed by IX (601) using a bispicolylamine chelating resin, and small amounts of manganese can be removed by oxidation using an oxidizing agent such as Caro's acid.

[0202] Optionally, if desired, the cobalt-loaded strip liquor (409) can be purified (601) to remove various trace impurities such as, for example, zinc, copper, calcium, manganese, cadmium, lead, and other impurities by SX using an organophosphoric acid (D2EHPA) extractant as described above.

[0203] The purified cobalt liqueur (603) is fed to cobalt crystallization (604) to produce high purity battery grade hydrous cobalt sulfate (605).

[0204] Magnesium in the cobalt extraction raffinate (419) is extracted (501) using a portion of the precharged organics (502).

[0205] The magnesium-loaded organics (504) are scrubbed (505) with a scrubbing solution (506) containing water and / or sulfuric acid, and the extracted nickel is removed with the scrubbing solution (507) which is recycled to the magnesium extraction (501).

[0206] The scrubbed organics (508) are stripped (509) using a sulfuric acid strip solution (510) to obtain a magnesium loaded stripped liquor (512) and regenerate the organics (511) which are recycled to the pre-charge (411).

[0207] The magnesium-added strip liquid (512) containing magnesium sulfate (513) can be crystallized to produce a magnesium sulfate by-product or can be further processed to produce a MgO / Mg(OH)2 by-product which can be used as a base reagent.

[0208] The raffinate (503) from the nickel-laden magnesium solvent extraction (501) is fed directly to nickel crystallization (701) to produce high purity battery grade hydrated nickel sulfate (702).

[0209] Extraction of cobalt and magnesium by separate SX cycles with direct neutralization (Figure 6)

[0210] The present disclosure provides an alternative approach and scheme (FIG. 6) that uses direct neutralization of the acids generated during the SX processes (201), (401), and (501) with ammonia / ammonium hydroxide (222) instead of the preloading approach and scheme shown in (FIG. 5). The aqueous to organic ratio (A / O) is selected and controlled to avoid the formation of nickel ammonium sulfate double salt during the SX process.

[0211] The main SX scheme with D2EHPA (201) for the separation of impurities (Zn(II), Mn(II), Cu(II) and Ca(II)) and for the separation of cobalt (401) and magnesium (501) using two separate SX circuits is the same as shown in Figure 5.

[0212] Ammonium sulfate produced from acid neutralization in the SX processes (201, 401, and 501) ultimately becomes nickel in the final SX raffinate (503). Partial ammonium sulfate is crystallized as nickel ammonium sulfate double salt with nickel sulfate (703).

[0213] The thermal decomposition step (704 or 706) is designed to convert the double sulfate to nickel sulfate (708), where ammonium sulfate can decompose to ammonia, sulfur trioxide and nitrogen gas (705) at temperatures above 280° C. It is preferable to selectively decompose only the ammonium component to ammonia (222) for recycling as a base reagent, to which an oxide / hydroxide, e.g. nickel oxide / hydroxide (707), may be added to form nickel sulfate (708). If present, nitrate, nitrite and nitrite components will be at least partially removed in this step. EXAMPLES

[0214] Working Example Example 1 - Washing of MHP

[0215] The wet MHP (4.2 kg, 48.9% moisture) was repulped with deionized water at 40° C. for 30 min with constant agitation and subsequently filtered through a pressure filter. This repulping / filtration procedure was repeated for multiple washes. The conditions and results are shown in Table 5.

[0216] The sodium and potassium contents in the feed MHP decreased with washing, corresponding to an increase in the Ni / Na and Ni / K ratios.

[0217] After three washes, the Ni / Na and Ni / K ratios increased from 142 to 3929 and 378 to 3522, respectively. These correspond to 25 ppm Na and less than 28 ppm K in the feed solution normalized to 100 g / L Ni if the washed MHP is fully dissolved.

[0218] After six washes, the Ni / Na and Ni / K ratios increased from 142 to 26281 and 378 to 12533, respectively, which corresponds to less than 10 ppm Na and less than 20 ppm K in the final nickel sulfate product containing 22.3% Ni, assuming all the Na and K goes into the nickel sulfate product.

[0219] Therefore, in principle, the sodium and potassium content in the MHP can be removed by washing and efficient filtration such as pressure filtration to very low levels to meet the requirements and specifications of the final nickel sulfate product. However, this does not limit the cost-effective combination of jarosite / alunite precipitation and washing described in the examples below.

[0220] The magnesium and calcium contents in MHP were also significantly reduced through washing, which may be beneficial for the subsequent purification process.

[0221] [Table 5]

[0222] Example 2 - Precipitation and Neutralization of Jarosite

[0223] This example illustrates the precipitation of jarosite using a feed having the composition shown in Table 6. The feed was heated to 95°C with stirring and aeration while 20 grams of jarosite seeds generated from a previous jarosite precipitation were added. The pH of the slurry was adjusted and maintained in the pH range of 1.8 to 2.0 by adding washed MHP obtained as described in Example 1. After 7.3 hours, the slurry was vacuum filtered using a Macherey-Nagel MN615 filter paper. The compositions of the final solution and washed solids are shown in Table 6.

[0224] Sodium in solution was reduced from 118 mg / L in the feed to 3.1 mg / L, corresponding to a Na precipitation efficiency of 99.8% and an increase in the Ni / Na ratio from 770 to 31119. Nickel and sodium in the jarosite precipitate were measured at 0.03% and 0.07%, respectively.

[0225] This example demonstrates that sodium ions can be thoroughly removed to very low levels by jarosite precipitation, which meets the requirements and specifications of a feed solution suitable for subsequent purification by SX and IX to produce high purity battery grade nickel sulfate.

[0226] [Table 6]

[0227] After the above jarosite precipitation, the pH of the slurry was increased stepwise by adding a certain amount of lime: pH 2.1 (95°C), pH 2.4 (62°C), pH 3.6 (62°C) and pH 4.4 (62°C). Meanwhile, the slurry temperature was decreased from 95°C to 62°C after 80 min. The test conditions and results are shown in Table 7.

[0228] The remaining iron and aluminum in solution were reduced to less than 1 mg / L at pH 4.4 (62 °C), while the total nickel and cobalt coprecipitated in the jarosite and final washed solids upon neutralization were approximately 0.04%–0.08%, respectively.

[0229] [Table 7]

[0230] Example 3 - Oxidative Conversion of Mn(II) Oxide to Mn(IV) Oxide

[0231] This example demonstrates the conversion of soluble Mn(II) to stable solid Mn(IV) oxide in MHP (44.46% Ni, 4.6% Co, 0.88% Mn) with air and SO2 / air mixtures. The MHP was repulped in deionized water at a pulp density of 29% (dry solids) and 60 °C. The slurry was constantly stirred while continuously blowing in air, or a mixture of sulfur dioxide (SO2) and air with 0.5-1% (v / v) SO2.

[0232] Slurry samples were taken periodically and vacuum filtered through Macherey-Nagel MN615 filter paper. The solid cake from the filtration was leached with 1M sulfuric acid solution, and then the insoluble leach residue samples were completely dissolved in 6M HCl solution. The concentrations of nickel, cobalt and manganese in the leachate (or leach liquor) samples were analyzed by ICP-AES / MS, based on which the conversion efficiencies of manganese, as well as precipitated nickel and cobalt, were calculated. The results of conversion by sparging with air only and by sparging with a mixture of SO2 / air are compared in Figure 7.

[0233] With air alone, the conversion was fast initially but decreased over time to about 60% conversion at 60 min. With alternative air and SO2 / air mixtures, the conversion increased almost linearly to over 97% conversion efficiency at 170 min. This corresponds to <0.1 g / L Mn for 100 g / L Ni in the leach solution when MHP was dissolved.

[0234] Further analysis of the data showed that the kinetic behavior of the conversion with air alone can be approximated by a second-order rate reaction with respect to the content of soluble Mn(II), while the conversion with SO2 / air mixture is characterized by zero-order rate kinetics, i.e., independent of the Mn(II) content. In application, the conversion can be carried out initially by sparging air alone to rapidly convert most of the Mn(II), followed by sparging SO2 / air gas mixture to obtain a more complete conversion.

[0235] In principle, complete conversion of Mn(II) can be achieved if desired, although this is optional in this process, since any remaining lower levels of Mn(II) can be removed by a subsequent SX scheme using D2EHPA.

[0236] The precipitated cobalt and nickel in the final solid residue were 0.88% and 0.08%, respectively, when air alone was used for 90 min, and 3.37% and 0.09%, respectively, when alternating SO2 / air mixture and air was used for 300 min. Thus, conversion parameters such as pH, flow rate, SO2 / air (O2) ratio, and residence time can be optimized to achieve the desired conversion efficiency of Mn(II) while minimizing the conversion of nickel and cobalt.

[0237] Example 4 - Nickel Preloaded (or Pre-Charged) of D2EHPA

[0238] The preloading distribution isotherm shown in this example was established using a feed solution of 10% D2EHPA and 62.6 g / L Ni(sulfate) in Exxsol D80 at 50 °C and approximately pH 5 using sodium hydroxide for neutralization and pH control. The results are shown in Figure 8. The McCabe-Thiele diagram suggests two to three theoretical stages for nickel extraction at an operating A / O ratio of 1:10 (Figure 8).

[0239] Example 5 - Scrubbing of pre-loaded D2EHPA

[0240] This example shows that entrained loaded sodium from sodium hydroxide as the base reagent for neutralization in the preload can be scrubbed from the loaded organics.

[0241] The scrubbing distribution isotherms shown in this example were performed at 50° C. and about pH 3.6 using a scrubbing solution of 10% D2EHPA and 64.8 g / L Ni(sulfate) in Exxsol D80 preloaded with nickel. The scrubbing results are shown in FIG.

[0242] A McCabe-Thiele diagram constructed based on the data suggests 2-3 theoretical stages for scrubbing the charged sodium with an operating A / O ratio of about 1:10. Nickel scrubbing is in the range of 10-15%, which is recycled to the precharged section in continuous operation. Scrubbing conditions in terms of scrub solution composition, scrub pH, A / O ratio and stages can be further optimized. In a multi-stage continuous SX process, an optimal pH profile can be applied.

[0243] Example 6 - Extraction of impurities with pre-loaded D2EHPA

[0244] This example shows the extraction distribution isotherms for the extraction of impurities (Zn(II), Cu(II), Mn(II) and Ca(II)) by nickel (6.3 g / L) preloaded with 10% (v / v) D2EHPA in Exxsol D80. Portions of the nickel preloaded organics were contacted separately with respective portions of synthetic PLS (g / L: 93.1 Ni, 9.23 Co, 2.80 Mg, 3.2 Zn, 0.08 Mn, 0.034 Ca and 0.087 Cu) at various A / O ratios, a pH of about 3.1, and 40° C. for 10 minutes with constant mechanical stirring.

[0245] Metal distribution isotherms are shown in Figure 10. The negative extraction efficiency of nickel indicated that the metal impurities were extracted by displacement of the preloaded nickel. The McCabe-Thiele diagrams shown in Figures 11 and 12 suggest three theoretical extraction stages for the extraction and separation of impurities (Zn(II), Mn(II), Cu(II), and Ca(II)) from nickel and cobalt using 10% D2EHPA with an operating A / O ratio of 1.5.

[0246] Example 7 - Nickel Preloaded Cyanex® 272

[0247] This example shows a preloading of 25% Cyanex® 272 in Exxsol D80 with 56 g / L Ni(sulfate) at 50° C. and pH 6.8-7.0 using sodium hydroxide for neutralization and pH control. The distribution isotherm and McCabe-Thiele diagram of the nickel preloading are shown in FIG. 13, which predicts two to three theoretical stages for nickel extraction at an operating A / O ratio of 1:4.

[0248] Example 8 - Scrubbing of sodium from pre-filled Cyanex® 272

[0249] This example demonstrates the scrubbing distribution isotherm for removing entrained and extracted sodium from pre-loaded 25% Cyanex® 272 in Exxsol D80 at pH 5.5 using a scrubbing solution of 65 g / L Ni(sulfate). The metal distribution isotherm and McCabe-Thiele diagram constructed based on the data are shown in Figure 14. This suggests two to three theoretical stages of scrubbing of sodium at an operating A / O ratio of 1:15 with reasonable scrubbing of nickel being further minimized with multi-stage operation using an optimal pH profile. The scrubbing liquor can be recycled to the pre-loading section to recover nickel in a continuous operation.

[0250] Example 9 - Extraction of cobalt and magnesium using Cyanex® 272

[0251] As shown in Figure 3, the present disclosure provides a SX scheme for extracting both cobalt and magnesium and then separating the loaded magnesium from the cobalt through a scrubbing scheme in the SX circuit. This example shows the metal distribution isotherms for the extraction of cobalt and nickel and their separation from nickel using a pre-nickeled (14.44 g / L Ni) organic solution of 25% (v / v) Cyanex® 272 in Exxsol D80 and a synthetic solution containing (g / L) 103 Ni, 11.4 Co, 3.2 Mg.

[0252] The test results are shown in Figure 15. The negative extraction efficiency of nickel indicates that the preloaded nickel was replaced by the extraction of cobalt and magnesium. The McCabe-Thiele diagram predicts that both cobalt and magnesium can be extracted in two to three (theoretical) extraction stages at an operating A / O of 0.6:1 using 25% Cyanex® 272 (Figure 16).

[0253] Example 10 - Scrubbing of nickel and magnesium from loaded organics

[0254] These examples show the scrubbing distribution isotherms of nickel loaded at the higher pH range and then magnesium loaded at the lower pH range from 25% (v / v) Cyanex® 272 in Exxsol D80 preloaded with 6.477 g / l Co, 1.632 g / L Ni, and 1.722 g / L Mg. The scrubbing distribution isotherms at pH 5, pH 4.2, and pH 3.5 are shown in Figures 17 and 18, respectively.

[0255] The distribution isotherms and McCabe-Thiele diagram suggest one to two theoretical extraction stages using 25% Cyanex® 272 with an operating A / O of 1:7 to scrub nickel loaded in the pH range of 4.2 to 5 (Figure 17). The nickel-rich scrub liquor is recycled to the extraction section in a continuous operation.

[0256] The distribution isotherms and McCabe-Thiele diagrams suggest three to four scrubbing stages for scrubbing magnesium loaded at pH range of 3.5-4.2 and operating A / O ratio in the range of 1:4-1:9 (Figure 18), which indicates that the scrubbing efficiency of magnesium and selectivity towards cobalt can be further optimized in continuous operation with multi-stage operation using optimal pH profile.

[0257] Some important features and advantages of the processes described herein are summarized as follows: 1) To produce high purity battery grade nickel and cobalt sulfates, conventional and existing refining processes require costly SX-based extraction followed by stripping of the primary metal nickel from relatively small amounts of impurities (typically less than 1 / 15 impurity / nickel ratio in the original MHP) using organic carboxylic acids such as Versatic 10. Furthermore, two additional SX stages are required. This disclosure avoids the most costly nickel SX stage, requiring only two SX stages, reducing capital and operational costs. 2) The present disclosure provides a process that allows for the straightforward separation of alkali metal and monovalent cationic species. 3) The present disclosure provides novel SX schemes for the extraction and separation of cobalt and magnesium from nickel, respectively, in one SX circuit or in two separate SX circuits. Both schemes for the separation of magnesium from nickel are novel, with the former in one SX circuit providing minimal SX requirements, thus minimizing capital and operational costs. 4) This disclosure provides two approaches and schemes for neutralization of the acid produced in the SX process: (a) pre-loading the nickel sulfate available in the process with organics to avoid contamination of the system with basic reagents, or (b) direct neutralization with ammonia / ammonium hydroxide which is then removed from the final hydrated nickel sulfate by pyrolysis, preferably to ammonia for recycling as a basic reagent in the process. 5) The present disclosure provides an oxidative precipitation method for converting soluble divalent manganese ions, i.e., Mn(II), to stable solid Mn(III / IV) oxides while minimizing nickel and cobalt losses during the washing stage and / or subsequent oxidative neutralization steps, allowing early removal of manganese and facilitating its separation in subsequent purification by SX. 6) To minimize nickel and cobalt losses, the abundant iron and aluminum contents in nickel laterite ores are traditionally leached and removed as hydroxides by neutralization with large amounts of final stage precipitate recycled, which significantly reduces process efficiency and increases processing costs. 7) The present disclosure provides approaches and schemes for improving the overall process efficiency of nickel laterite processing, including: (a) the controlled neutralization of iron and aluminum hydroxide precipitation allows for desirable ratios of iron and aluminum to alkali metal ion (Na+ and K+) and monovalent cation (e.g., NH4+) species in the MHP, enabling the subsequent purification processes described herein to remove these monovalent cations without the need for extensive deep removal or extensive recycling of iron and aluminum in conventional upstream processing of the product MHP due to the use of species such as jarosite / alunite; and (b) Jarosite / alunite precipitation to remove alkali metal ions (Na+ and K+) and monovalent cation (e.g., NH4+) species that can be operated simultaneously with leaching or continuously after leaching to produce a feed solution or MHP that is substantially free of these monovalent cations and species and can be fed to the subsequent simplified purification and purification processes described herein.

[0258] The present disclosure relates to a purification process for producing high purity battery grade nickel and cobalt sulfate products from a wide range of feed materials, including but not limited to: Nickel- and cobalt-containing intermediate products, e.g. MHP, Nickel laterite ores or other nickel- and cobalt-containing materials, Nickel and cobalt containing solutions, Used battery materials, Manganese ocean nodules, as well as ·Wastes and tails containing nickel and cobalt.

[0259] As used in this specification and the claims that follow, the terms "comprise" and "include" and any of their derivatives (e.g., comprises, comprising, includes, including) are to be interpreted as including the feature referred to by the term, but are understood not to exclude the presence of additional features, unless specifically stated or implied.

[0260] The reference to prior art in this specification is not, and should not be construed as, any sort of suggestion that such prior art forms part of the common general knowledge.

[0261] In some cases, a single embodiment may combine multiple features for brevity and / or to aid in understanding the scope of the disclosure. In such cases, it should be understood that these multiple features may be provided separately (in separate embodiments) or in any other suitable combination. Alternatively, if separate features are described in separate embodiments, these separate features may be combined in a single embodiment, unless otherwise stated or implied. This also applies to claims that may be recombined in any combination. That is, a claim may be amended to include features defined in other claims. Furthermore, a phrase referring to "at least one" of a list of items refers to any combination of those items, including single members. As an example, "at least one of a, b, or c" is intended to cover a, b, c, ab, ac, bc, and abc.

[0262] Those skilled in the art will understand that the use of the present disclosure is not limited to the particular application described. Also, the present disclosure is not limited to its preferred embodiments with respect to the particular elements and / or features described or illustrated herein. It will be understood that the present disclosure is not limited to the disclosed embodiments, and that many rearrangements, modifications, and substitutions are possible without departing from the scope described and defined in the claims.

[0263] References Clout, R. and Perry, S. Selective leaching of nickel and cobalt from a mixed hydroxide intermediate involves forming a mixed hydroxide intermediate slurry, treating the hydroxide intermediate slurry with an oxidizing agent, and leaching the oxidizing slurry in an acidic sulfate medium. Patent Nos. CA2949580-A1; AU2016256773-A1.

[0264] Fittock, J.E. 1992, Nickel and cobalt refining at QNI Pty Ltd Yabulu Queensland, AUSIMM Monograph 19, pp. 1-47.

[0265] Fittock, JE, Price, MJ, Reid, JG, White, DT and Davis, MR, 1994. Preparation of high purity cobalt intermediates cpds from cobalt sulfate solutions using solvent extraction with formation of the tetramine complex. Patent Nos. EP651062-A1; AU9477522-A; CA2134490-A; ZA9408497-A; AU670398-B; AU9667964-A; US5605668-A; AU677559-B; EP651062-B1; DE69415633-E; ES2126071-T3; US6048506-A; CA2134490-C.

[0266] Proce, MJ and Reid, JG, 1987. Separation of nickel and cobalt in an ammoniacal system - by organic extraction of nickel and stripping from the organic phase with ammoniacal ammonium carbonate solution. Patent numbers WO8809389-A; AU8816454-A; EP364463-A; BR8807511-A; JP2503575-W; US5174812-A; EP364463-A4; CA1335332-C; EP364463-B1; DE3854499-G; JP96009741-B2.

[0267] Rodriguez, M., 2008. Hydrometallurgical leaching of nickel comprises combining nickel sulfide ore with nickel laterite and grinding to form a slurry, leaching the combined slurry in a pressure acid leach circuit, and supplying an oxidant to the pressure acid leach circuit. Patent Nos. AU2008100563-A4; AU2008100563-B4.

[0268] Rodriguez, M., 2009. A hydrometallurgical process for leaching nickel from a nickel ore composition comprises adding a sulfide ore to an autoclave of a high pressure acid leach circuit containing a nickel laterite feed material and adding an oxidizing agent to the autoclave. Patent Nos. AU2008101213-A4; AU2008101213-B4; AU2008101213-A8; AU2008101213-B8.

[0269] Virnig, MJ, Mackenzie, J. and Mackenzie, JM, 1997. Nickel recovery from laterite ores using oxime extractants - acid leaching, precipitation of nickel hydroxide, releaching with aqueous ammonia, extraction with non-soluble oximes in immiscible hydrocarbons. By acid stripping and electrowinning. Patent numbers WO9743023-A1; AU9730543-A; EP915727-A1; US5976218-A; AU727561-B; CA2252592-C.

Claims

1. 1. A process for separating nickel and / or cobalt salts from a crude nickel and / or cobalt salt bearing stock comprising the steps of: a) treating crude nickel and / or crude cobalt bearing stock with an iron or aluminum salt under conditions to remove at least a portion of one or more alkali metal ions and / or monovalent cation species as a jarosite / alunite precipitate to provide a solution having a reduced content of one or more alkali metal ions and / or monovalent cation species; b) stepwise increasing the pH of said solution from step a) under conditions to provide a feed solution for further purification to produce nickel and / or cobalt salts suitable for producing battery grade nickel or cobalt salts; Consisting of Step b) comprises the steps of: i. iron, ii. aluminum; iii. Chromium, and iv. copper A process for removing at least some of one or more of, or a combination of,

2. and further comprising, prior to step a), treating the crude nickel and / or crude cobalt bearing stock with water and / or an aqueous solution comprising sulfuric acid under conditions to remove at least some of the one or more alkali metal ions and / or monovalent cationic species.

2. The process of claim 1, comprising:

3. and treating said feed solution from step b) with an oxidizing agent under conditions to oxidize iron(II) to iron(III) and manganese(II) to the higher oxidation state manganese(III / IV).

2. The process of claim 1, comprising:

4. 2. The process of claim 1, wherein the iron salt or the aluminum salt in step a) is selected from the group consisting of sulfates, carbonates, oxides, and hydroxides.

5. A process for obtaining refined nickel and refined cobalt from a feed solution obtained according to claim 1, comprising the steps of: a) reducing the concentration of zinc, calcium, manganese, copper, cadmium, lead or other metal impurities which have a higher affinity for the organic extractant than the cobalt and nickel in the feed solution by contacting the impurities with an organophosphorus extractant in a hydrocarbon diluent under solvent extraction conditions and separating the impurities into organic and aqueous phases to produce an aqueous raffinate containing purified cobalt and purified nickel; b) contacting the aqueous raffinate with a cobalt-selective extractant in a hydrocarbon diluent under solvent extraction conditions and separating the aqueous raffinate into organic and aqueous phases to produce an organic phase containing purified cobalt and an aqueous phase containing purified nickel; c) selectively scrubbing and stripping the organic phase to obtain an aqueous phase containing purified cobalt; d) purifying said aqueous phase containing purified cobalt to obtain a further aqueous phase containing purified cobalt; e) further recovering cobalt from said aqueous phase; and f) recovering nickel from said aqueous phase containing purified nickel; The process comprising:

6. Step b) is a) (i) co-extracting both cobalt and magnesium in the aqueous raffinate from step a) into an organic phase; (ii) selectively scrubbing the co-extracted nickel from the organic phase with a scrubbing solution of sulfuric acid and / or cobalt sulfate at a relatively high equilibrium pH range to obtain a nickel-depleted organic phase and a nickel-rich scrubbed liquor (aqueous phase) which is recycled to step (i); and (iii) selectively scrubbing the co-extracted nickel from the organic phase with a scrubbing solution of sulfuric acid and / or cobalt sulfate at a relatively low equilibrium pH range to obtain a nickel-depleted organic phase and a nickel-rich scrubbed liquor (aqueous phase) which is recycled to step (i). (iv) re-extracting the cobalt co-scrubbed in the magnesium-rich scrub liquor (aqueous phase) with a small amount of the organic phase to obtain a cobalt-loaded small amount of the organic phase that is integrated into the majority of the organic phase in step (iii); and (v) stripping the organic phase from step (iii) to produce a purified cobalt-containing aqueous phase; or b) (i) selectively extracting cobalt in the aqueous raffinate from step a) into the organic phase; (ii) scrubbing both the co-extracted nickel and magnesium in the organic phase with a sulfuric acid and / or cobalt sulfate scrubbing liquor to obtain the organic phase containing purified cobalt and purified nickel and a magnesium-rich scrub liquor (aqueous phase) which is recycled to step i); and (iii) stripping cobalt from the purified organic phase of step (ii) with an acid to obtain an aqueous phase containing purified cobalt (scrub liquor). (iv) selectively extracting the magnesium from step (i) using a portion of the organic solution to obtain a purified nickel-containing aqueous phase (final raffinate) and a magnesium-rich organic phase; (v) scrubbing the co-extracted nickel in the organic phase with a sulfuric acid scrub solution to obtain a purified nickel-containing scrub liquor (aqueous phase) which is recycled to step (iv); and (vi) stripping the magnesium-rich organics to obtain a purified magnesium-containing aqueous phase for recovering magnesium by-products. The process of claim 5, comprising:

7. The organophosphoric acid extractant has the formula (RO) ２ P.O. ２ H, wherein each R group may be the same or different and is selected from optionally substituted branched, straight chain, or cyclic alkyl, alkenyl, or alkynyl groups.

8. 8. The process of claim 7, wherein the organophosphoric acid is di-2-ethylhexyl phosphoric acid or an organophosphoric acid having similar or the same extraction properties as di-2-ethylhexyl phosphoric acid.

9. The cobalt-selective extractant has the formula R ２ P.O. ２ 6. The process of claim 5, wherein the organophosphinic acid has the formula: H, where each R group may be the same or different and is selected from optionally substituted branched, straight chain, or cyclic alkyl, alkenyl, or alkynyl groups.

10. 10. The process of claim 9, wherein the organophosphoric acid is di-2,4,4-trimethylpentylphosphinic acid (bis(2,4,4-trimethylpentyl)phosphinic acid) or an organophosphinic acid having similar or the same extraction properties as di-2,4,4-trimethylpentylphosphinic acid.

11. 6. The process of claim 5, wherein the hydrocarbon diluent is an aliphatic or aromatic hydrocarbon solvent, or a mixture thereof.

12. 12. The process of claim 11, wherein the hydrocarbon diluent is kerosene.

13. 7. The process of claim 6, wherein step a and / or step b are carried out in the presence of a phase modifier or combination of phase modifiers present in any of the hydrocarbon diluents.

14. 14. The process of claim 13, wherein the phase modifier is selected from one or more of the group consisting of isodecanol, tridecanol, 2-ethylhexanol and tri-n-butyl phosphate.

15. 6. The process of claim 5, wherein step c) of purifying the aqueous phase containing purified cobalt further comprises removing at least some of the copper from the aqueous phase containing purified cobalt.

16. 16. The process of claim 15, wherein the step of removing at least some of the copper from the aqueous phase containing purified cobalt further comprises contacting the aqueous phase containing purified cobalt with an iminodiacid resin under conditions to bind copper, and separating the copper-loaded resin from the aqueous phase.

17. 6. The process of claim 5, wherein said step c) of purifying said aqueous phase containing purified cobalt comprises removing at least some of the zinc from said aqueous phase containing purified cobalt.

18. 18. The process of claim 17, wherein the step of removing at least some of the zinc from the aqueous phase containing purified cobalt comprises contacting the organic phase containing purified cobalt with a D2EHPA impregnated resin under conditions which bind zinc, and separating the zinc-loaded resin from the aqueous phase.

19. 6. The process of claim 5, wherein step c) of purifying the aqueous phase containing purified cobalt comprises removing at least some of the magnesium from the aqueous phase containing purified cobalt.

20. 20. The process of claim 19, wherein the step of removing at least some of the magnesium from the aqueous phase containing purified cobalt comprises contacting the aqueous phase containing purified cobalt with an oxidizing agent under conditions to oxidize manganese(II) to the higher oxidation state manganese(III / IV) and separating manganese(III / IV) from the aqueous phase.

21. The oxidizing agents are oxygen (air), ozone, and SO in a ratio that functions as an oxidizing agent. ２ / O ２ 21. The process of claim 20, wherein the mixture is selected from the group consisting of (air), peroxymonosulfuric acid (Caro's acid), and peroxydisulfuric acid.

22. 6. The process of claim 5, wherein said step c) of purifying said aqueous phase containing purified cobalt comprises removing one or more of zinc, calcium, manganese, copper, cadmium, lead or other metal impurities in said aqueous phase containing purified cobalt by contacting with an organophosphorous extractant in a hydrocarbon diluent under solvent extraction conditions and separating the organic and aqueous phases to further produce an aqueous phase containing purified cobalt.

23. The organophosphoric acid extractant has the formula (RO) ２ P.O. ２ 23. The process of claim 22, having formula: H, where each R group may be the same or different and is selected from optionally substituted branched, straight chain, or cyclic alkyl, alkenyl, or alkynyl groups.

24. 24. The process of claim 23, wherein the organophosphoric acid is di-2-ethylhexyl phosphoric acid or an organophosphoric acid having similar or the same extraction properties as di-2-ethylhexyl phosphoric acid.

25. 6. The process of claim 5, wherein the step of re-recovering cobalt from the aqueous phase containing purified cobalt comprises crystallizing cobalt sulfate from the aqueous phase containing purified cobalt.

26. 6. The process of claim 5, wherein the step of re-recovering nickel from the aqueous phase containing purified cobalt comprises crystallizing nickel sulfate from the aqueous phase containing purified nickel.

27. 6. The process of claim 5, further comprising stripping at least some of any one or more of zinc, calcium, manganese and copper present in the organic phase obtained in step a) by either (a) treating the organic phase with sulfuric acid by controlling the calcium concentration below its saturation to avoid the formation of gypsum, or (b) treating the organic phase with hydrochloric acid when the calcium concentration in the system is relatively high and there is a risk of forming gypsum.

28. 28. The process of claim 27, comprising periodic bleeding of the organic phase in step a) by contacting the organic phase with a hydrochloric acid solution to remove some of any one or more of the iron, aluminum and other tightly bound metal ions from the organic phase.

29. 6. The process of claim 5, further comprising pre-charging one or more of the organic solutions used in the process with nickel, cobalt and / or magnesium sulfate, carbonate, oxide or hydroxide salts.

30. 30. The process of claim 29, comprising pre-charging one or more of the organic solutions used in the process with nickel sulfate.

31. 30. The process of claim 29, further comprising treating with a base reagent selected from the group consisting of nickel hydroxide, sodium hydroxide or carbonate, ammonia, ammonium hydroxide or carbonate, and magnesium oxide / hydroxide or carbonate for neutralization or pH control in said pre-loading.

32. 30. The process of claim 29, comprising pre-neutralizing the organic solution with a base reagent to produce a pre-neutralized organic for pre-loading with nickel by exchange.

33. 33. The process of claim 32, wherein the basic reagent is selected from the group consisting of sodium hydroxide or carbonate, ammonia, and ammonium hydroxide or carbonate.

34. 31. The process of claim 30, further comprising washing the nickel sulfate pre-loaded organic solution with water and / or sulfuric acid and / or a scrubbing solution containing nickel sulfate to remove entrained and extracted sodium or ammonium ions.

35. 6. The process of claim 5, further comprising directly neutralizing the acid generated during the solvent exchange with ammonia, ammonium hydroxide or ammonium carbonate under conditions that avoid the formation of nickel ammonium double salts, followed by thermally decomposing the ammonium sulfate component in the hydrated nickel sulfate to remove the ammonium component.

36. 6. The process according to claim 5, comprising one or more stages of extraction, scrubbing and stripping steps in solvent extraction, and loading, washing and elution steps in ion exchange, operating in countercurrent or simultaneous mode or a combination of the two modes.

37. 6. High purity nickel sulfate obtained using the process of claim 5.

38. High purity cobalt sulfate obtained using the process of claim 5.