Lithium primary battery

Abstract

This lithium primary battery is provided with a positive electrode, a negative electrode, and a non-aqueous electrolyte solution. The positive electrode contains manganese dioxide, and the negative electrode contains a lithium alloy. The lithium alloy contains magnesium, and the content of magnesium in the lithium alloy is 10% by mass or less.

Description

Technical Field

[0001] The present disclosure relates to lithium primary batteries. Background Art

[0002] Lithium primary batteries are used as power sources for many electronic devices because of their high energy density and low self-discharge. The positive electrode of a lithium primary battery uses manganese dioxide or the like. The negative electrode of a lithium primary battery uses, for example, sheet-shaped (foil-shaped) metal lithium or a lithium alloy.

[0003] Patent Document 1 proposes a non-aqueous electrolyte battery, characterized in that a positive electrode, a negative electrode, and an electrolyte formed of a solute and an organic solvent are provided in a battery can, and in a non-aqueous electrolyte battery using lithium trifluoromethanesulfonate as the solute, the negative electrode is formed of a lithium alloy. In the embodiment of Patent Document 1, the lithium alloy uses Li-Al, Li-In, or Li-Sn.

[0004] Prior art literature

[0005] Patent Literature

[0006] Patent Document 1: Japanese Patent Application Laid-Open No. 2-15566 Summary of the invention

[0007] Problem that the invention aims to solve

[0008] In lithium primary batteries, the battery capacity may decrease due to deterioration of the negative electrode.

[0009] Solutions for solving problems

[0010] One aspect of the present disclosure relates to a lithium primary battery including a positive electrode, a negative electrode, and a non-aqueous electrolyte, wherein the positive electrode includes manganese dioxide, the negative electrode includes a lithium alloy, the lithium alloy includes magnesium, and the content of the magnesium in the lithium alloy is 10% by mass or less.

[0011] Effects of the Invention

[0012] According to the present disclosure, it is possible to suppress a decrease in the capacity of a lithium primary battery.

[0013] Although the novel features of the present invention are described in the attached claims, both the technical solution and the content of the present invention can be further fully understood through the following detailed description with reference to the accompanying drawings in combination with other objects and features of the present invention. BRIEF DESCRIPTION OF THE DRAWINGS

[0014] Figure 1 This is a front view showing a part of a lithium primary battery according to an embodiment of the present disclosure as a cross section. DETAILED DESCRIPTION

[0015] Hereinafter, the embodiments of the present disclosure will be described with examples, but the present disclosure is not limited to the examples described below. In the following description, specific numerical values ​​and materials are sometimes exemplified, but other numerical values ​​and materials may also be applied as long as the effects of the present disclosure can be obtained. In this specification, the so-called "numerical value A to numerical value B" includes numerical value A and numerical value B, and can be read alternatively as "above numerical value A and below numerical value B". In the following description, when lower limits and upper limits are exemplified for numerical values ​​of specific physical properties, conditions, etc., any one of the exemplified lower limits can be arbitrarily combined with any one of the exemplified upper limits as long as the lower limit does not exceed the upper limit. When multiple materials are exemplified, one can be selected from them and used alone, or two or more can be used in combination.

[0016] In addition, the present disclosure includes a combination of matters recorded in two or more claims arbitrarily selected from the plurality of claims recorded in the attached claims. That is, as long as no technical contradiction occurs, matters recorded in two or more claims arbitrarily selected from the plurality of claims recorded in the attached claims may be combined.

[0017] The lithium primary battery of the embodiment of the present disclosure includes a positive electrode, a negative electrode and a non-aqueous electrolyte. The positive electrode includes manganese dioxide, and the negative electrode includes a lithium alloy. The lithium alloy includes magnesium (Mg), and the content of Mg in the lithium alloy is 10% by mass or less.

[0018] The lithium alloy contains Mg, thereby increasing the strength of the negative electrode, suppressing the local defect or fracture of the negative electrode caused by the expansion of the positive electrode during discharge, and suppressing the capacity reduction caused by the reduction in strength. In addition, the lithium alloy contains Mg, thereby suppressing the side reaction between the negative electrode and the electrolyte, and suppressing the capacity reduction caused by the side reaction. This side reaction easily occurs under high temperature environment. When the Mg content in the lithium alloy is less than 10% by mass, the capacity reduction caused by the reduction of the amount of Li (absolute amount of Li) occupied in the negative electrode can be suppressed. As a result, high capacity can be obtained in any case after initial and long-term storage, and the capacity degradation rate after storage can be greatly reduced. If the Mg content in the lithium alloy is greater than 10% by mass, the effect of improving strength and suppressing side reactions brought by containing Mg becomes greater, but the amount of Li (absolute amount of Li) occupied in the negative electrode is reduced, and the capacity is reduced.

[0019] The lithium alloy used in the negative electrode is in the form of, for example, a foil (sheet). From the viewpoint of increasing the capacity, the content of Li in the lithium alloy may be, for example, 90% by mass or more, or 95% by mass or more.

[0020] The Mg content in the lithium alloy is 10 mass % or less, may be 0.01 mass % or more and 10 mass % or less, or may be 0.5 mass % or more and 5 mass % or less.

[0021] In lithium alloys, Mg may be dispersed or unevenly distributed. In lithium alloy foils, Mg may be unevenly distributed in the thickness direction and / or surface direction of the foil. In either case of dispersion or uneven distribution of Mg, the strength of the negative electrode containing Mg increases, and the reduction in capacity is suppressed compared to the negative electrode not containing Mg, which can suppress the degradation of the negative electrode during high temperature storage.

[0022] The lithium alloy may include other metal elements other than Li and Mg. As other metal elements, Al, Sn, Ni, Pb, In, K, Fe, Si, etc. may be listed. From the viewpoint of ensuring discharge capacity and stabilizing internal resistance, the overall content of metal elements other than lithium contained in the lithium alloy may also be 0.05 mass % or more and 15 mass % or less (or 10 mass % or less).

[0023] The content of each element in the lithium alloy is determined by inductively coupled plasma (ICP) emission spectrometry or atomic absorption spectrometry (AAS).

[0024] (Additives for non-aqueous electrolytes)

[0025] The non-aqueous electrolyte preferably includes at least one additive selected from the group consisting of a cyclic imide compound, a phthalate compound and an isocyanate compound. In the case where the non-aqueous electrolyte includes the above-mentioned additive, a composite coating comprising Mg from the lithium alloy and components from the additive can be formed on the surface of the lithium alloy (negative electrode) containing Mg. The chemical stability of the coating is excellent, and the coating includes Mg from the lithium alloy, so the wettability of the negative electrode to the non-aqueous electrolyte can be improved, and the resistance of the negative electrode can be reduced. Through the coating, it is easier to evenly consume Li on the negative electrode surface.

[0026] The content of the additive in the non-aqueous electrolyte is, for example, more than 0.01% by mass and less than 5% by mass. It should be noted that the content of the additive in the non-aqueous electrolyte is the mass ratio (percentage) of the additive relative to the entire non-aqueous electrolyte. For example, just after the battery is manufactured (or when the non-aqueous electrolyte is prepared), the content of the additive in the non-aqueous electrolyte is expected to be within the above range. In contrast, in a battery that has just been manufactured for a certain period of time, a portion of the additive is consumed during the formation of the coating, and the content of the additive in the non-aqueous electrolyte may also be a value less than the above range. In this case, even if the content of the additive in the non-aqueous electrolyte is a small amount (e.g., a value close to the detection limit), the above-mentioned effect brought about by the additive can be confirmed. The same is true for the content of various compounds such as cyclic imide compounds described later.

[0027] (Cyclic imide compound)

[0028] As the cyclic imide compound, for example, a cyclic diacylamine compound can be cited. The cyclic imide compound may have a diacylamine ring (hereinafter, also referred to as an imide ring). Other rings (hereinafter, also referred to as the second ring) may also be condensed in the imide ring. The cyclic imide compound may be contained in the non-aqueous electrolyte in the form of an imide or in the form of an anion or a salt. In the case where the cyclic imide compound is contained in the non-aqueous electrolyte in the form of an imide, it may be contained in the form of a free NH group or in the form of a tertiary amine.

[0029] Examples of the second ring include an aromatic ring, a saturated or unsaturated aliphatic ring, etc. The second ring may also contain at least one heteroatom. Examples of the heteroatom include an oxygen atom, a sulfur atom, and a nitrogen atom.

[0030] Examples of cyclic imide compounds include aliphatic dicarboxylic acid imide compounds and cyclic imide compounds having a second ring. Examples of aliphatic dicarboxylic acid imide compounds include succinimide. Examples of cyclic imide compounds having a second ring include imide compounds of aromatic or alicyclic dicarboxylic acids. Examples of aromatic dicarboxylic acids or alicyclic dicarboxylic acids include substances having carboxyl groups on two adjacent atoms constituting the ring. Examples of cyclic imide compounds having a second ring include phthalimide and hydrogenated products of phthalimide. Examples of hydrogenated products of phthalimide include cyclohex-3-ene-1,2-dicarboximide and cyclohexane-1,2-dicarboximide.

[0031] The imide ring may also be an N-substituted imide ring having a substituent on the nitrogen atom of the imide. Examples of such substituents include hydroxyl groups, alkyl groups, alkoxy groups, and halogen atoms. Examples of alkyl groups include C1 to C4 alkyl groups, which may be methyl groups, ethyl groups, and the like. Examples of alkoxy groups include C1 to C4 alkoxy groups, which may be methoxy groups, ethoxy groups, and the like. Examples of halogen atoms include chlorine atoms and fluorine atoms, and the like.

[0032] The cyclic imide compound is preferably selected from at least one of the group consisting of phthalimide and N-substituted phthalimide. As a substituent on the nitrogen atom of the N-substituted phthalimide, it can be selected from the substituents exemplified for the N-substituted imide ring. N-substituted phthalimide, for example, preferably includes at least one selected from the group consisting of N-hydroxyphthalimide, N-(2-hydroxyethyl)phthalimide, N-(cyclohexylthio)phthalimide and N-(phenylthio)phthalimide. Phthalimide and / or N-substituted phthalimide can account for more than 50% by mass of the cyclic imide compound, and further can account for more than 70% by mass or more than 90% by mass.

[0033] The non-aqueous electrolyte may contain one cyclic imide compound, or may contain two or more. The content of the cyclic imide compound in the non-aqueous electrolyte may be 1% by mass or less, may be 0.001% by mass or more and 1% by mass or less, or may be 0.001% by mass or more and 0.8% by mass or less.

[0034] (Phthalate Compounds)

[0035] Phthalic acid ester compounds include phthalic acid esters and derivatives thereof. The derivatives may have a substituent bonded to an aromatic ring derived from phthalic acid. Examples of such substituents include hydroxyl groups, alkyl groups, alkoxy groups, and halogen atoms. Examples of alkyl groups include C1 to C4 alkyl groups, which may be methyl groups, ethyl groups, and the like. Examples of alkoxy groups include C1 to C4 alkoxy groups, which may be methoxy groups, ethoxy groups, and the like. Examples of halogen atoms include chlorine atoms and fluorine atoms, and the like.

[0036] The phthalate compound may be a phthalate monoester compound, but from the viewpoint that the resulting coating is easy to protect the surface of the Li alloy, a phthalate diester compound is desirable. As the alcohol constituting the ester with phthalic acid (or its derivative), a saturated or unsaturated aliphatic alcohol of C1 to C20 (preferably C1 to C6) is desirable.

[0037] Specific examples of phthalic acid diester compounds include dimethyl phthalate, diethyl phthalate, diallyl phthalate, dibutyl phthalate, diisobutyl phthalate, bis(2-ethylhexyl)phthalate, etc. These may be used alone or in combination of two or more. The phthalic acid diester compound may account for 50% by mass or more of the phthalate ester compound, and may also account for 70% by mass or more or 90% by mass or more.

[0038] The non-aqueous electrolyte solution may contain one phthalate compound or two or more phthalate compounds. The content of the phthalate compound in the non-aqueous electrolyte solution may be 1% by mass or less, or may be 0.1% by mass or more and 1% by mass or less.

[0039] (Isocyanate compound)

[0040] The isocyanate compound has, for example, at least one isocyanate group and a C1-C20 aliphatic hydrocarbon group or a C6-C20 aromatic hydrocarbon group. The aliphatic hydrocarbon group and the aromatic hydrocarbon group constituting the isocyanate compound may have a substituent. The substituent may be a group that can exist stably, for example, a halogen atom or a nitrile group. The aliphatic group may be an alicyclic aliphatic group, or a linear or branched aliphatic group. The aromatic hydrocarbon group is a hydrocarbon group having one or more aromatic rings, or a group in which an aromatic ring is connected to an aliphatic group.

[0041] The isocyanate compound may be a monoisocyanate compound having one isocyanate group, but is preferably a diisocyanate compound having two isocyanate groups. It is believed that the diisocyanate compound generates a composite film having higher chemical stability than the monoisocyanate compound, and generates a composite film having lower resistance than the triisocyanate. In addition, even if the diisocyanate compound is in a small amount, the ability to form a composite film is high, and the stability in the battery is excellent.

[0042] Specific examples of diisocyanate compounds include OCN-C n H 2n -NCO (n is an integer of 1 to 10.) represented by a compound (for example, hexamethylene diisocyanate), a compound having an alicyclic diyl group (for example, 1,3-bis(isocyanatomethyl)cyclohexane, dicyclohexylmethane-4,4'-diisocyanate, bicyclo[2.2.1]heptane-2,5-diylbis(methylisocyanate), bicyclo[2.2.1]heptane-2,6-diylbis(methylisocyanate), isophorone diisocyanate), 2,2,4-trimethylhexamethylene diisocyanate, 2,4,4-trimethylhexamethylene diisocyanate, hexyl isocyanate, etc. Among these, at least one selected from the group consisting of hexamethylene diisocyanate, 1,3-bis(isocyanatomethyl)cyclohexane and isophorone diisocyanate is preferred. These may account for 50% by mass or more of the isocyanate compound, and may further account for 70% by mass or more or 90% by mass or more.

[0043] When a diisocyanate compound is added to a non-aqueous electrolyte, the diisocyanate compounds react with each other in the battery (in the non-aqueous electrolyte) to form an isocyanurate body, a urea body, or a biuret body. Therefore, when the battery is decomposed and the non-aqueous electrolyte is analyzed, an isocyanurate body, a urea body, or a biuret body derived from the diisocyanate compound is sometimes detected.

[0044] The non-aqueous electrolyte may contain one isocyanate compound, or may contain two or more. The content of the isocyanate compound in the non-aqueous electrolyte may be 3% by mass or less, 0.01% by mass or more and 2% by mass or less, or 0.01% by mass or more and 1.5% by mass or less.

[0045] The non-aqueous electrolyte solution (additive) can be analyzed by, for example, liquid chromatography mass spectrometry (LC / MS) and gas chromatography mass spectrometry (GC / MS), nuclear magnetic resonance analysis (NMR), infrared absorption spectroscopy (IR), mass spectrometry (MS), and ultraviolet spectroscopy (UV).

[0046] Hereinafter, the lithium primary battery of the present disclosure will be described in more detail.

[0047] [Lithium primary battery]

[0048] (positive electrode)

[0049] The positive electrode contains manganese dioxide as a positive electrode active material. As manganese dioxide, electrolytic manganese dioxide is suitable. The positive electrode containing manganese dioxide exhibits a higher voltage and excellent pulse discharge characteristics. Manganese dioxide can be a mixed crystal state containing multiple crystal states. The positive electrode can contain manganese oxides other than manganese dioxide. As manganese oxides other than manganese dioxide, MnO, Mn3O4, Mn2O3, Mn2O7, etc. can be listed. The main component of the manganese oxide contained in the positive electrode is preferably manganese dioxide. The so-called main component here means that the proportion of manganese dioxide in manganese oxide is 50% by mass or more. The proportion of manganese dioxide in manganese oxide can be 70% by mass or more, or it can be 90% by mass or more.

[0050] Other active materials other than manganese dioxide may be included as positive electrode active materials. Other active materials include graphite fluoride, iron disulfide, antimony trisulfide, etc. The proportion of other active materials other than manganese dioxide in the overall positive electrode active material may be 0.5 mass % or more and 10 mass % or less.

[0051] The positive electrode may include a positive electrode mixture containing a positive electrode active material, a binder, a conductive agent, etc. As the binder, for example, fluororesins such as polytetrafluoroethylene, rubber particles, acrylic resins, and polyimide resins can be listed. As the conductive agent, for example, conductive carbon materials can be listed. As the conductive carbon material, for example, natural graphite, artificial graphite, carbon black, carbon fiber, and carbon nanotubes can be listed.

[0052] The positive electrode may further include a positive electrode current collector that holds the positive electrode mixture. Examples of the material of the positive electrode current collector include stainless steel, aluminum, and titanium.

[0053] In the case of a coin-shaped battery, a positive electrode current collector having an L-shaped cross section may be mounted on positive electrode mixture particles to form a positive electrode, or the positive electrode may be formed only by positive electrode mixture particles. The positive electrode mixture particles may be obtained by, for example, compressing and drying a wet positive electrode mixture prepared by adding an appropriate amount of water to a positive electrode active material.

[0054] In the case of a cylindrical battery, a positive electrode having a sheet-shaped positive electrode collector and a positive electrode held in a positive electrode mixture layer of the positive electrode collector can be used. As a sheet-shaped positive electrode collector, a porous collector is preferred. As a porous collector, porous metal mesh, mesh, punching metal, etc. can be listed. The positive electrode mixture layer can be obtained, for example, by applying the above-mentioned positive electrode mixture in a wet state to the surface of the sheet-shaped positive electrode collector or filling it in the positive electrode collector, pressing and drying in the thickness direction.

[0055] (negative electrode)

[0056] The negative electrode contains the above-mentioned lithium alloy. The lithium alloy is formed into any shape and thickness according to the shape, size, specification performance, etc. of the lithium primary battery. The negative electrode can have a negative electrode collector such as copper foil together with a lithium alloy sheet. Since the lithium alloy contains Mg, Mg with relatively high strength remains at the end of discharge, so it is also possible to use only a lithium alloy sheet (foil) to form the negative electrode without using a negative electrode collector. In a lithium alloy containing Mg, local defects or fractures of the negative electrode at the end of discharge are suppressed, and the Li in the negative electrode can be effectively used without reservation.

[0057] In the case of a coin-shaped battery, a strip-shaped lithium alloy may be punched into a disc-shaped lithium alloy for use as a negative electrode. In the case of a cylindrical battery, a sheet-shaped lithium alloy may also be used as a negative electrode. The sheet is obtained, for example, by extrusion molding. More specifically, in a cylindrical battery, a lithium alloy foil having a shape in a length direction and a width direction is used.

[0058] The negative electrode may include an active material layer including a carbon material and / or a silicon-containing material capable of absorbing and releasing lithium ions.

[0059] (Non-aqueous electrolyte)

[0060] The nonaqueous electrolyte solution includes, for example, a nonaqueous solvent and a lithium salt. The concentration of lithium ions (total concentration of lithium salts) contained in the nonaqueous electrolyte solution is, for example, 0.2 mol / L to 2.0 mol / L, or 0.3 mol / L to 1.5 mol / L.

[0061] As the non-aqueous solvent, organic solvents that are generally used in non-aqueous electrolytes for lithium primary batteries can be cited. As the non-aqueous solvent, ethers, esters, carbonates, etc. can be cited. As the non-aqueous solvent, dimethyl ether, γ-butyrolactone, propylene carbonate (PC), ethylene carbonate (EC), dimethyl carbonate, diethyl carbonate, ethyl methyl carbonate, 1,2-dimethoxyethane (DME), 1,2-diethoxyethane, methyl acetate, ethyl acetate, propyl acetate, etc. can be used. The non-aqueous electrolyte can contain one non-aqueous solvent or two or more non-aqueous solvents.

[0062] From the viewpoint of improving the discharge characteristics of lithium primary batteries, the nonaqueous solvent preferably includes a cyclic carbonate with a high boiling point and a chain ether with a low viscosity even at low temperatures. The cyclic carbonate preferably includes at least one selected from the group consisting of PC and EC, and PC is particularly preferred. The chain ether preferably includes DME.

[0063] As lithium salts, for example, lithium salts used as solutes in lithium primary batteries can be cited. As such lithium salts, for example, LiCF3SO3, LiClO4, LiBF4, LiPF6, LiRaSO3 (Ra is a fluoroalkyl group having 1 to 4 carbon atoms), LiFSO3, LiN(SO2Rb)(SO2Rc)(Rb and Rc are each independently a fluoroalkyl group having 1 to 4 carbon atoms), LiN(FSO2)2, LiN(SO2CF3)2, LiN(SO2F)(POF2), LiPO2F2, LiB(C2O4)2, LiBF2(C2O4). Among them, from the viewpoint of the stability of lithium alloys containing Mg, it is preferred to select at least one of the group consisting of LiCF3SO3, LiBF4 and LiN(FSO2)2. The non-aqueous electrolyte may contain one of these lithium salts, or may contain two or more.

[0064] The non-aqueous electrolyte may further include other components other than the above-mentioned additives. As other components other than the above-mentioned additives, propane sultone, propylene sultone, ethylene sulfite, 3,2-dioxazole thiophene-2,2-dioxide, vinylene carbonate, vinyl ethylene carbonate, fluoroethylene carbonate, adiponitrile, succinonitrile, succinic anhydride, etc. can be listed. Other components can be lithium salts, and can also generate lithium ions.

[0065] (Separator)

[0066] A lithium primary battery generally has a separator sandwiched between the positive electrode and the negative electrode. As the separator, a porous sheet formed of an insulating material resistant to the internal environment of the lithium primary battery can be used. Specifically, a nonwoven fabric made of a synthetic resin, a microporous membrane made of a synthetic resin, or a laminate thereof can be cited.

[0067] As the synthetic resin used in the nonwoven fabric, for example, polypropylene, polyphenylene sulfide, polybutylene terephthalate, etc. can be cited. As the synthetic resin used in the microporous membrane, for example, polyolefin resins such as polyethylene, polypropylene, and ethylene-propylene copolymer can be cited. The microporous membrane can also contain inorganic particles as needed.

[0068] The thickness of the separator is, for example, 5 μm or more and 100 μm or less.

[0069] The structure of the lithium primary battery is not particularly limited. The lithium primary battery may be a coin-shaped battery having a stacked electrode group composed of a disk-shaped positive electrode and a disk-shaped negative electrode stacked with a separator. It may also be a cylindrical battery having a wound electrode group composed of a strip-shaped positive electrode and a strip-shaped negative electrode wound in a spiral with a separator.

[0070] Figure 1 A front view showing a portion of a cylindrical lithium primary battery of one embodiment of the present disclosure as a cross section is shown. In the lithium primary battery 10, an electrode group formed by winding a positive electrode 1 and a negative electrode 2 with a separator 3 interposed therebetween is housed in a battery case 9 together with a non-aqueous electrolyte (not shown). A sealing plate 8 is installed at the opening of the battery case 9. A positive electrode lead 4 connected to the collector 1a of the positive electrode 1 is connected to the sealing plate 8. The negative electrode lead 5 connected to the negative electrode 2 is connected to the battery case 9. In addition, an upper insulating plate 6 and a lower insulating plate 7 are respectively arranged at the upper and lower parts of the electrode group to prevent internal short circuits.

[0071] "appendix"

[0072] Based on the description of the above embodiments, the following techniques are disclosed.

[0073] (Technology 1)

[0074] A lithium primary battery comprising a positive electrode, a negative electrode and a non-aqueous electrolyte.

[0075] The positive electrode comprises manganese dioxide,

[0076] The negative electrode comprises a lithium alloy.

[0077] The lithium alloy contains magnesium.

[0078] The content of the magnesium in the lithium alloy is 10 mass % or less.

[0079] (Technique 2)

[0080] The lithium primary battery according to technology 1, wherein the nonaqueous electrolyte solution contains at least one additive selected from the group consisting of cyclic imide compounds, phthalate compounds, and isocyanate compounds.

[0081] (Technique 3)

[0082] The lithium primary battery according to technology 2, wherein the cyclic imide compound includes at least one selected from the group consisting of phthalimide and N-substituted phthalimide.

[0083] (Technique 4)

[0084] The lithium primary battery according to technology 3, wherein the N-substituted phthalimide includes at least one selected from the group consisting of N-hydroxyphthalimide, N-(2-hydroxyethyl)phthalimide, N-(cyclohexylthio)phthalimide and N-(phenylthio)phthalimide.

[0085] (Technique 5)

[0086] The lithium primary battery according to any one of aspects 2 to 4, wherein the content of the cyclic imide compound in the nonaqueous electrolyte is 1% by mass or less.

[0087] (Technique 6)

[0088] The lithium primary battery according to any one of techniques 2 to 5, wherein the phthalate ester compound includes a phthalate diester compound.

[0089] (Technique 7)

[0090] The lithium primary battery according to technology 6, wherein the phthalic acid diester compound includes dimethyl phthalate.

[0091] (Technology 8)

[0092] The lithium primary battery according to any one of techniques 2 to 7, wherein the content of the phthalate compound in the nonaqueous electrolyte is 1% by mass or less.

[0093] (Technique 9)

[0094] The lithium primary battery according to any one of techniques 2 to 8, wherein the isocyanate compound includes a diisocyanate compound.

[0095] (Technology 10)

[0096] The lithium primary battery according to technology 9, wherein the diisocyanate compound includes at least one selected from the group consisting of hexamethylene diisocyanate, 1,3-bis(isocyanatomethyl)cyclohexane, and isophorone diisocyanate.

[0097] (Technology 11)

[0098] The lithium primary battery according to any one of techniques 2 to 10, wherein the content of the isocyanate compound in the nonaqueous electrolyte is 3% by mass or less.

[0099] [Example]

[0100] Hereinafter, the present disclosure will be specifically described based on Examples and Comparative Examples, but the present disclosure is not limited to the following Examples.

[0101] 《Examples 1 to 5, Comparative Examples 1 to 2》

[0102] (Production of positive electrode)

[0103] 5 parts by mass of Ketjen Black as a conductive agent, 5 parts by mass of polytetrafluoroethylene as a binder and an appropriate amount of pure water were added to 100 parts by mass of the positive electrode active material and kneaded to prepare a wet positive electrode mixture. Electrolytic manganese dioxide (MnO2) was used as the positive electrode active material.

[0104] Next, the positive electrode mixture is filled in a positive electrode current collector formed by a porous metal mesh with a thickness of 0.1 mm made of stainless steel (SUS444) to make a positive electrode precursor. Then, the positive electrode precursor is dried, rolled by roller pressing, and cut into a size of 3.5 cm in length and 20 cm in width, thereby obtaining a positive electrode. Next, a portion of the filled positive electrode mixture is peeled off, and one end of the positive electrode lead made of SUS444 is resistance welded to the portion where the positive electrode current collector is exposed.

[0105] (Production of negative electrode)

[0106] The lithium alloy foil (thickness 250 μm) was cut into a size of 3.7 cm in length and 22 cm in width to obtain a negative electrode. One end of a nickel negative electrode lead was connected to a specified position of the negative electrode by crimping. Li-Mg alloy foil or Li-Al alloy foil (Al content: 2 mass %) having a Mg content as shown in Table 1 was used in the lithium alloy foil. The content of Mg, etc. was determined by ICP emission spectrometry or atomic absorption spectrometry, and the "-" in the column of the content of Mg, etc. of the lithium alloy indicates that Mg, etc. was not detected by ICP emission spectrometry or atomic absorption spectrometry.

[0107] (Production of Electrode Group)

[0108] The positive electrode and the negative electrode were wound with a separator interposed therebetween to produce an electrode group. A 25 μm-thick polypropylene microporous film was used as the separator.

[0109] (Preparation of non-aqueous electrolyte)

[0110] LiCF3SO3 was dissolved at a concentration of 0.5 mol / L in a mixed solvent of PC, EC and DME (volume ratio 3:2:5) to prepare a non-aqueous electrolyte.

[0111] (Assembly of lithium primary batteries)

[0112] The electrode group is housed in a cylindrical battery case that also serves as a negative terminal. The battery case uses an iron case (outer diameter 17 mm, height 45.5 mm). Next, after injecting a non-aqueous electrolyte into the battery case, the opening of the battery case is sealed with a metal sealing plate that also serves as a positive terminal. The other end of the positive lead is connected to the sealing plate, and the other end of the negative lead is connected to the inner bottom surface of the battery case. A lithium primary battery is made in this way. It should be noted that in Table 1, A1 to A5 are batteries of Examples 1 to 5, and B1 to B2 are batteries of Comparative Examples 1 to 2.

[0113] The batteries of the examples and comparative examples thus obtained were aged for 3 days in an atmosphere at 45° C. after assembly, and the following evaluations were performed.

[0114] [evaluate]

[0115] (initial capacity)

[0116] The aged battery was discharged at a constant current of 2.5 mA in an environment of 20° C. until the battery voltage reached 0.9 V. The discharge time at this time was measured to determine the initial capacity.

[0117] (Capacity after saving)

[0118] The aged battery was stored at 85° C. for 3 months. The stored battery was discharged at a constant current of 2.5 mA at 20° C. until the battery voltage reached 0.9 V. The discharge time was measured to determine the post-storage capacity.

[0119] (Capacity degradation rate after storage)

[0120] Using the initial capacity and the capacity after storage obtained above, the capacity degradation rate after storage was obtained according to the following formula.

[0121] Capacity degradation rate after storage (%) = {1-(capacity after storage / initial capacity)}×100

[0122] The evaluation results are shown in Table 1. In addition, the initial capacity and the capacity after storage in Table 1 are expressed as relative values ​​(indexes) when the initial capacity of the battery B1 of Comparative Example 1 is set to 100.

[0123] [Table 1]

[0124]

[0125] Batteries A1 to A5 have larger initial and post-storage capacities and smaller capacity degradation rates than batteries B1 to B2.

[0126] 《Examples 6 to 14》

[0127] In the preparation of the negative electrode, the lithium alloy foil used had a Mg content of 1% by mass. In the preparation of the non-aqueous electrolyte, the non-aqueous electrolyte further contained additives as needed. The additives used were compounds shown in Table 2. The content of the additives in the non-aqueous electrolyte was the value shown in Table 2.

[0128] Batteries A6 to A14 of Examples 6 to 14 were prepared in the same manner as the battery A1 of Example 1 except for the above, and were evaluated.

[0129] The evaluation results are shown in Table 2. In Table 2, the initial capacity and the capacity after storage are expressed as relative values ​​(indexes) with the initial capacity of the battery B1 of Comparative Example 1 being 100.

[0130] [Table 2]

[0131]

[0132] Batteries A6 to A14 had large initial and post-storage capacities and small capacity degradation rates. Batteries A7 to A14 containing additives in the nonaqueous electrolyte had further reduced capacity degradation rates.

[0133] Industrial Applicability

[0134] The lithium primary battery of the present disclosure can be suitably used as a main power source or a memory power source of various meters (for example, smart meters for electricity, water, gas, etc.), for example.

[0135] The present invention has been described with respect to the presently preferred embodiments, but such disclosure is not to be construed in a limiting sense. Various modifications and changes should be apparent to those skilled in the art in the art of the present invention upon reading the above disclosure. Therefore, the appended claims should be construed as including all modifications and changes without departing from the spirit and scope of the present invention.

[0136] Description of Reference Numerals

[0137] 1: Positive electrode, 1a: Positive electrode current collector, 2: Negative electrode, 3: Separator, 4: Positive electrode lead, 5: Negative electrode lead, 6: Upper insulating plate, 7: Lower insulating plate, 8: Sealing plate, 9: Battery case, 10: Lithium primary battery

Claims

1. A lithium primary battery comprising a positive electrode, a negative electrode and a non-aqueous electrolyte, The positive electrode comprises manganese dioxide, The negative electrode comprises a lithium alloy, The lithium alloy contains magnesium, The content of the magnesium in the lithium alloy is 10 mass % or less.

2. The lithium primary battery according to claim 1, wherein: The non-aqueous electrolyte solution includes at least one additive selected from the group consisting of cyclic imide compounds, phthalate compounds, and isocyanate compounds.

3. The lithium primary battery according to claim 2, wherein: The cyclic imide compound includes at least one selected from the group consisting of phthalimide and N-substituted phthalimide.

4. The lithium primary battery according to claim 3, wherein: The N-substituted phthalimide includes at least one selected from the group consisting of N-hydroxyphthalimide, N-(2-hydroxyethyl)phthalimide, N-(cyclohexylthio)phthalimide, and N-(phenylthio)phthalimide.

5. The lithium primary battery according to claim 2, wherein: The content of the cyclic imide compound in the non-aqueous electrolyte is 1 mass % or less.

6. The lithium primary battery according to claim 2, wherein: The phthalate compound includes a phthalic acid diester compound.

7. The lithium primary battery according to claim 6, wherein: The phthalic acid diester compound includes dimethyl phthalate.

8. The lithium primary battery according to claim 2, wherein: The content of the phthalate compound in the non-aqueous electrolyte is 1 mass % or less.

9. The lithium primary battery according to claim 2, wherein: The isocyanate compound includes a diisocyanate compound.

10. The lithium primary battery according to claim 9, wherein: The diisocyanate compound includes at least one selected from the group consisting of hexamethylene diisocyanate, 1,3-bis(isocyanatomethyl)cyclohexane, and isophorone diisocyanate.

11. The lithium primary battery according to claim 2, wherein: The content of the isocyanate compound in the non-aqueous electrolyte is 3% by mass or less.