Method for determining the quantity and / or composition of a powdered resin layer applied to a carrier material

Description

[0001] The present invention relates to methods for determining the amount and / or composition of at least one layer of at least one powdered resin applied to at least one carrier material. Description

[0002] The use of wood-based panels in the furniture industry, as floor coverings or for cladding walls and ceilings requires the surface of the wood-based panels to be processed or refined. In the applications mentioned, the wood-based panels are usually coated with an impregnated decorative paper. There is no limit to the variety of differently patterned decorative papers, so wood-based panels are available with a multitude of different decors, such as stone or wood decors. To increase wear resistance, overlays are applied to the decorative paper. Thin papers are used as overlays, which are typically already impregnated with a melamine resin. Overlays are also available in which abrasion-resistant particles, such as corundum particles, are mixed into the resin of the overlay in order to increase the abrasion resistance of the laminate or wood-based panel.

[0003] Direct printing on wood-based panels has emerged in the past as an alternative to using decorative paper on wood-based panels, eliminating the need for printing on paper and subsequently laminating or directly coating it onto the wood-based panel. Several liquid, thermosetting resin layers are then applied to the directly printed design. These layers may contain abrasion-resistant particles to increase wear resistance. This type of thermosetting resin layer is also known as a liquid overlay.

[0004] The resins or glues used in these applications are usually liquid, often water-based formulations for impregnating paper layers or coating substrates. These are applied to paper via an impregnation process in an impregnation channel or to sheet-like substrates via roller application. The solvent is then evaporated by heated air or radiation. This is a relatively energy-intensive process and also results in emissions that must be eliminated through thermal afterburning or an exhaust air purification system. Furthermore, this process is also considered critical from an ecological perspective.

[0005] The application quantities on paper or substrates are adjusted using roller gaps, doctor blades, etc., and then usually controlled by weighing. The described technology was also used when using resin mixtures.

[0006] An alternative to liquid resins or glues is the use of powder resins. These can be applied to paper or carrier boards using scattering devices or spray nozzles. Since these applications are contactless, the application rate per unit area can at best be determined by the amount consumed per unit time. However, with powder applications, inhomogeneities due to turbulence or static influences are possible. This can be particularly problematic at the edges / boundaries of the system. Determining the application rates on paper or carrier materials can often only be done at the end of the production line after the powder has been fixed by pressing or baking. Otherwise, the powder may fall out during sample taking. This is particularly critical when multiple applications are carried out one after the other, since at the end only the total application rate can be determined.For many products, however, product quality depends crucially on the precise application of the individual layers. Cost disadvantages can also arise if certain functional layers are not applied in the desired manner.

[0007] The disadvantages are the lack of in-line control and the necessary readjustment, which can only be carried out with a time delay. Furthermore, variations in the composition of the applied resin powder or resin powder mixtures are not detectable.

[0008] The invention is therefore based on the technical problem of developing a non-destructive method that can determine the application quantity and composition of a powdered resin or glue coating. The method is to be installed in-line in production lines and deliver as many measurements as possible per unit of time in the direction of production and across it. The measurements should not disrupt the production process.

[0009] This object is achieved by a method having the features of claim 1.

[0010] Accordingly, a method is provided for determining the amount and / or composition of at least one layer of at least one powdered resin or resin mixture applied to at least one carrier material, the method comprising the following steps: Applying at least one powdered resin or a powdered mixture of at least two resins in a defined mixing ratio in different quantitatively defined amounts to a carrier material as reference samples; recording at least one NIR spectrum of each of the reference samples using at least one NIR measuring head in a wavelength range between 700 nm and 2000 nm, preferably between 900 nm and 1700 nm, particularly preferably between 1400 nm and 1600 nm, and particularly advantageously between 1450 nm and 1550 nm; assigning the different quantitative amounts of powdered resin or resin mixture of the reference samples to the recorded NIR spectra of said reference samples;and creating a calibration model for the relationship between the spectral data of the NIR spectra and the associated quantitative amounts of powdered resin or resin mixture of the reference samples by means of multivariate data analysis; applying at least one layer of at least one powdered resin of the resin mixture to a carrier material, recording at least one NIR spectrum of the carrier material coated with the powdered resin or resin mixture using the at least one NIR measuring head in a wavelength range between 700 nm and 2000 nm, preferably between 900 nm and 1700 nm, particularly preferably between 1400 nm and 1600 nm, and particularly advantageously between 1450 nm and 1550 nm; and determining the quantitative amount of powdered resin or resin mixture applied to the carrier material by comparing the NIR spectrum recorded for the reference samples with the created calibration model.

[0011] According to the present method, an NIR spectrum of the powdered resin applied to a carrier material, such as a carrier board or paper, is recorded. This not only allows the application quantity to be determined but also the composition of a powdered resin or glue mixture to be analyzed. For this purpose, NIR spectra of various application quantities of powdered resins or resin mixtures on different carrier materials were recorded. This is intended to test the influence of the substrate on the spectrum. Surprisingly, it was shown that even application quantities of up to 600 g of resin powder / m² can be determined. The same is then carried out with resin mixtures. Calibration models were then created with the help of which conclusions can be drawn about unknown quantities and compositions. A further advantage is that other parameters (e.g. humidity, see e.g.EP 2 915 658 B1, EP 2 808636 B1). This can also help prevent quality defects.

[0012] As explained further below, NIR spectroscopy can be used to determine a wide variety of different resins / glues. These include powdered melamine-formaldehyde resins, urea-formaldehyde resins, phenol-formaldehyde resins, or mixtures thereof. Other resins can be based on powdered polyester or epoxy resins, etc. The powdered resins may also contain additives such as hardeners, pigments, antistatic agents, etc. Agents to improve application properties may also be used.

[0013] This method can be used on a production line both in the direction of production and across it. Visualization allows changes in order quantities or distribution to be shown promptly.

[0014] This method enables the provision of measured values ​​in a short time (online, preferably without disruptive time delays) compared to conventional (known) measurement methods. The measured data can be used for quality assurance, research and development, process control, process regulation, process control, etc. The measurement process does not reduce production speed, etc. Fundamentally, it improves production monitoring. Furthermore, downtimes due to quality control and system adjustments are reduced.

[0015] The determination of the application quantity of powdered resin or resin mixture possible with the present method is preferably carried out exclusively by NIR measurement.

[0016] A combination with other spectroscopic methods, especially using other wavelengths outside the NIR range, is not planned.

[0017] Therefore, an NIR measuring head is used, preferably an NIR multi-measuring head, which allows the amount of powdered resin to be determined by recording spectral data (spectra) in the near-infrared range (700-2000 nm). The NIR radiation interacts with the organic functional groups, such as OH, CH, and NH, which are present in both urea and melamine resin. During the interaction, the NIR radiation is scattered and reflected by the sample being measured. An NIR spectrum is generated by the reception of the reflected NIR radiation by the NIR detector. During this measurement, a large number of individual NIR measurements are performed within one second, thus ensuring statistical validation of the values.NIR spectroscopy together with multivariate data analysis (mentioned below) offers a possibility to establish a direct relationship between the spectral information (NIR spectra) and the parameters to be determined of the applied resin layer.

[0018] The present method exploits the fact that NIR radiation does not penetrate the substrate, but is reflected or scattered by the substrate's surface. The reflected or scattered NIR radiation is detected by the NIR detector, and the resulting NIR spectrum is used to determine the desired parameters (in this case, the application quantity of powdered resin).

[0019] To determine the amount of powdered resin applied, spectral data from the entire recorded spectral range are preferably used, i.e. not a single, discrete wavelength, but rather a whole range of several wavelengths is used.

[0020] According to the method according to the invention, reference samples of the substrate coated with a resin or resin mixture are first prepared. To prepare the reference samples, various amounts of powdered resin or a powdered resin mixture, e.g., 10 g / m 2 , 20 g / m 2 , 40 g / m 2 , 60 g / m 2 , 80 g / m 2 , and / or 100 g / m 2 , are applied to the substrate to be coated.

[0021] In the case of a powdered resin mixture, a defined mixture of a first powdered resin and a second powdered resin, e.g., a defined mixture of urea resin and melamine resin, was applied to the respective substrate to be coated. Thus, mixtures with a ratio of first powdered resin to second powdered resin of 25 wt%:75 wt%, 50 wt%:50 wt%, and 75 wt%:25 wt% were applied as reference samples. In this series, 100% of each of the first powdered resin and the second powdered resin were determined as reference samples.

[0022] It is also important to ensure that the reference sample is similar to the sample being measured; in particular, the resin layer of the reference sample has the same composition as the resin layer being measured. The similarity of the sample being measured and the reference sample is particularly important when using powdered resin layers with additives such as flame retardants, fibers, and other additives.

[0023] At least one NIR spectrum of these reference samples is recorded in a wavelength range between 700 nm and 2000 nm, preferably between 900 nm and 1700 nm, particularly preferably between 1400 nm and 1600 nm, and particularly advantageously between 1450 nm and 1550 nm.

[0024] The different quantitative amounts of powdered resin in the reference samples are then assigned to the recorded NIR spectra of these reference samples, and a calibration model is created for the relationship between the spectral data of the NIR spectra of the reference samples and the corresponding resin quantities as parameter values ​​using multivariate data analysis. This means that each parameter value of the reference sample corresponds to an NIR spectrum of the reference sample. The calibration models created for the various parameters are stored in a suitable data storage system.

[0025] Subsequently, at least one layer of at least one powdered resin or resin mixture is applied to a substrate, and at least one NIR spectrum of the powdered resin layer applied to the substrate is recorded. The quantitative amount of the powdered resin or resin mixture applied to the substrate can be determined by comparing the NIR spectrum recorded for the impregnated paper layer with the created calibration model.

[0026] A comparison and interpretation of the NIR spectra is best performed across the entire recorded spectral range. This is best done using a well-known multivariate data analysis (MDA). Multivariate analysis methods typically examine several statistical variables simultaneously in a well-known manner. To achieve this, these methods typically reduce the number of variables contained in a data set without simultaneously diminishing the information contained therein.

[0027] In this case, the multivariate data analysis is carried out using the method of P artial Least SPartial least squares regression (PLS) is used to create a suitable calibration model. The obtained data is preferably evaluated using suitable analysis software, such as SIMCA-P from Umetrics AB or The Unscrambler from CAMO.

[0028] In a further embodiment, spectral data from the NIR spectral range between 1450 and 1550 nm are used to create the calibration model, which data are pretreated using suitable mathematical methods and then fed to the multivariate data analysis.

[0029] The significance of a wavelength for predicting resin layer parameters, such as the amount of resin, from the NIR spectrum is illustrated using the regression coefficients. Regions with large coefficient values ​​have a strong influence on the regression model. The representation of the regression coefficients in a PLS regression model for determining the amount of resin or resin content shows that the wavelength range between 1460 nm and 1530 nm, with a maximum at 1490 nm (absorption band of the amino groups of the resin), is the most important for calculating the model, as the regression coefficient values ​​are largest here. Although the other regions in the spectrum have less information content with regard to the NIR measurement, they nevertheless help to take into account or eliminate other information or interfering factors (such as the transparency of the layer, surface quality of the resin layer or the carrier material, etc.).to minimize.

[0030] To eliminate interfering influences (such as the nature of the surface of the support material, the color of the samples, light scattering on solid particles or other additives, etc.), it is necessary to process the spectral data using mathematical pretreatment methods (e.g., derivative data pretreatment, standardization according to SNVT ( S standard N normal V ariats T transformation), multiplicative signal correction (EMSC, E xtended M ultiplicative S signal Correction, etc.). Baseline effects, which are mainly caused by the different colors of the samples, are removed from the spectra, overlapping bands are separated, and the dependence of light scattering on the substrate surface or on the solid particles in the coating is taken into account. If, for example, the resin application rate on untreated surfaces of substrate materials such as wood-based panels is to be determined, data pretreatment is preferably carried out to reduce light scattering on the rough surface of the substrate. When measuring on a decorative layer, the focus of calibration and data pretreatment is on removing the baseline shift.

[0031] In one embodiment of the present process, the powdered resin to be applied is a formaldehyde resin, preferably a urea resin, a melamine resin, or a phenolic resin, particularly preferably a melamine-formaldehyde resin or a urea-formaldehyde resin. Other resins based on powdered polyester, epoxy resin, etc., can also be used.

[0032] The particle size of the powdered resin is between 20 and 100 µm, preferably between 40 and 89 µm.

[0033] In one embodiment of the present process, at least one mixture of at least two powdered resins is applied to the at least one carrier material. A mixture of urea and melamine resin is preferred. Urea and melamine resin exhibit very similar NIR spectra, with the urea resin peak lying in the shoulder of the melamine resin peak.

[0034] The at least one mixture may contain a first powdered resin and a second powdered resin in a ratio between 10 wt%: 90 wt% and 90 wt%: 10 wt%, preferably between 25 wt%: 75 wt% and 75 wt%: 25 wt%, particularly preferably between 55 wt%: 45 wt% and 45 wt%: 55 wt%, e.g. 50: 50 wt%.

[0035] In one embodiment of the present process, the powdered resin or the mixture of at least two powdered resins is applied to the at least one carrier material in an amount of up to 600 g / m 2 , preferably up to 400 g / m 2 , particularly preferably up to 200 g / m 2 . Thus, according to the invention, the powdered resin or the mixture of at least two powdered resins can be applied to the at least one carrier material in an amount between 10 and 150 g / m 2 , preferably between 20 and 100 g / m 2 , particularly preferably between 40 and 80 g / m 2 .

[0036] Other substances can also be added to the resin powder. A particular advantage is that even substances that are poorly compatible with liquid melamine resin due to salting-out, thickening, settling, curing-influencing effects, etc., can be used. These can include salts to increase conductivity, organic or inorganic flame retardants, cellulose derivatives, radical scavengers, pigments, UV absorbers, etc.

[0037] Accordingly, the powdered resin used may contain additives such as pigments, conductive substances and cellulose.

[0038] By adding color pigments, the resin powder layer can also serve as a white primer layer for a subsequent printed decorative layer. White pigments such as titanium dioxide (TiO2) can be used as color pigments. Additional color pigments can be calcium carbonate, barium sulfate, or barium carbonate. The color pigments can make up up to 50% by weight of the total powder.

[0039] The addition of color pigments to the first layer of resin powder increases the opacity, so that it can be used as the (sole) base or primer for the subsequent decorative layer.

[0040] The amount of cellulose fibers applied with the resin powder can be between 0.1 and 1 wt.%, preferably between 0.5 and 0.8 wt.% (based on the amount of resin to be applied), or between 0.1-0.5 g / m 2 , preferably 0.2-0.4 g / m 2 , particularly preferably 0.25 g / m 2 . The preferably used cellulose fibers are colorless and in the form of a fine or granular, slightly hygroscopic powder.

[0041] The conductive substances can be selected from the group consisting of carbon black, carbon fibers, metal powder, and nanoparticles, especially carbon nanotubes. Combinations of these substances can also be used.

[0042] The resins used preferably contain additives such as hardeners, wetting agents (surfactants or mixtures thereof), release agents and / or other components.

[0043] In one embodiment, a paper layer is used as the carrier material. Overlay papers, decorative papers, or kraft papers, for example, are used as paper layers. Overlay papers are thin papers that have typically already been impregnated with a conventional melamine resin. Overlay papers are also available in which abrasion-resistant particles, such as corundum particles, are mixed into the overlay resin to increase abrasion resistance. Decorative papers are specialty papers for surface finishing of wood materials that enable a wide variety of decors. In addition to the typical prints of various wood structures, more complex prints of geometric shapes or artistic products are available. There are virtually no restrictions on the choice of motifs.Kraft papers are highly durable and consist of cellulose fibers to which starch, alum, and glue are added to create surface effects and increase strength.

[0044] In another embodiment, a carrier board is used as the carrier material. In this case, this carrier board is preferably a board made of a wood-based material, plastic, a wood-based material-plastic mixture, or a composite material, in particular a chipboard, medium-density fiberboard (MDF), high-density fiberboard (HDF), oriented strand board (OSB), or plywood board, a cement fiberboard, gypsum fiberboard, or a WPC (wood-plastic composite) board or an SPC (stone-plastic composite) board.

[0045] As already indicated above, the method according to the invention for determining the amount of powdered resin or resin mixture applied to the carrier material can be carried out continuously and online in a production line, in particular in a production line for the manufacture of wood-based panels or in a production line for the impregnation of paper layers. In particular, the method can be carried out in an automatically controlled system with alarm notification.

[0046] The determination of the amount of powdered resin applied to at least one carrier material can be carried out several times in the production line, in particular after each leaving a device for applying a layer of powdered resin.

[0047] In one embodiment of the present measuring method, it is provided that the at least one NIR measuring head moves transversely to the running direction of the carrier material provided with the powdered resin in the production line and traverses across the entire width of the carrier material in order to analyze certain problem areas, in particular under-applications in the edge or central area of ​​the carrier material.

[0048] In a further embodiment of the present measuring method, it is provided that the at least one NIR measuring head moves in the direction of travel of the carrier material provided with the powdered resin in the production line; i.e., in this embodiment, the measuring head can remain stationary in a position that is considered, for example, to be particularly critical.

[0049] Thus, a method is provided in which, by using an NIR measuring head, the quantity and composition of an applied resin powder or resin mixture can be determined from a single NIR spectrum or the reflection or scattering of NIR radiation, namely through a non-contact measurement. In an advantageous embodiment of the invention, the data acquired with the measuring head(s) are used directly for system control or regulation.

[0050] Furthermore, in a further advantageous embodiment of the invention, storing the data enables improved quality control. The stored data can also advantageously contribute to the evaluation of system tests, e.g., commissioning of a system during a new installation or after maintenance or repair, or for in-situ testing of new production or measurement processes. The immediate availability of the measured values ​​and the high measurement frequency enable very close monitoring, control, or regulation of the systems.

[0051] The advantages of this method are manifold: non-contact multi-parameter determination ("real-time" measurement) with significantly reduced time delay in the evaluation of the measured parameter values; improved plant control and regulation, reduction of waste, improvement in the quality of the products manufactured on the plant, and improvement in plant availability.

[0052] The control system of each production facility includes at least one computer-based evaluation unit (or processor unit) and a database. The evaluation unit compares or compares the NIR spectrum measured for the product (i.e., coated substrate) with the calibration models created for the individual parameters. The parameter data thus determined is stored in the database.

[0053] The data determined with this spectroscopic method can be used to control the respective production line. The contactless measured

[0054] As previously described, parameter values ​​from the NIR multi-sensor head ("actual values") can be used directly and in real time for the control or regulation of the relevant system. For example, by storing the measured actual values ​​in a database, e.g., a relational database, and comparing them with the target values ​​of these parameters. The resulting differences are then used to control or regulate the production line.

[0055] For the calibration and control of the respective production line, a computer-implemented method and a computer program comprising instructions that, when executed by a computer, cause the computer to execute the computer-implemented method are provided. The computer program is stored in a memory unit of the control system of the respective production line.

[0056] In the following, two processes and production lines in which the measuring method according to the invention can be used are described in detail.

[0057] A first method for producing a wood-based panel provided with a decoration comprises the following steps: a) applying at least one first layer of at least one powdered resin or resin mixture to at least one side of a wood-based panel and melting the at least one applied layer of a powdered resin; b) applying at least one decorative layer by means of a direct printing process; and c) applying at least one further (second) layer of at least one powdered resin or resin mixture to the at least one printed decorative layer and melting the at least one layer of powdered resin sprinkled onto the decorative layer.

[0058] The measuring method according to the invention for determining the application quantity of the powdered resin (or powdered resin mixture) is preferably carried out following the respective step of applying the first and / or second and / or each further layer of powdered resin.

[0059] "Fusing" or "gelling" in the context of this application means that the resin layer is not yet fully polymerized; rather, the polymerization is stopped at an intermediate stage, allowing further crosslinking or polymerization to occur at a later processing stage. The purpose of "gelling" is therefore usually to apply additional functional layers to the already applied protective layer at a later time, or to complete the product in subsequent processing steps.

[0060] In a preferred embodiment, the resin powder is applied by electrostatic charging. Application can also be carried out by powder coating using the tribo-process, in which the powder is charged by friction.

[0061] The melting of the applied layer of powdered resin or resin mixture can be achieved using an IR emitter, microwave systems, or similar. The use of IR emitters is particularly preferred.

[0062] The surface of the core board can be surface-treated. For example, in the case of a wood-based core board, the surface can be sanded or unsanded and provided with a pressed skin. In the case of a plastic core board, the surface can be corona-treated.

[0063] In a preferred embodiment, in a next step, at least one primer is applied to the (first) melted resin powder layer to increase the opacity.

[0064] The primer preferably comprises casein, corn starch or soy protein and can contain inorganic color pigments and thus serve as a primer layer for the decorative layer to be printed subsequently.

[0065] White pigments such as titanium dioxide (TiO2) can be used as color pigments. Other color pigments can include calcium carbonate, barium sulfate, or barium carbonate, as well as iron oxide pigments (for a brownish primer). In addition to the color pigments and casein, corn starch, or soy protein, the primer can also contain water as a solvent.

[0066] The amount of liquid primer applied may be between 10 and 50 g / m 2< , preferably between 15 and 30 g / m 2< , particularly preferably between 20 and 25 g / m 2<.

[0067] It is also conceivable that the primer consists of at least one, preferably at least two or more successively applied layers or applications (e.g. up to five applications), wherein the application quantity between the layers or applications is the same or different, ie the application quantity of each individual layer can vary.

[0068] The primer can be applied to the wood-based substrate using a roller, followed by drying. It is also possible to apply the primer to the plastic substrate using digital printing. The digital printing inks used for digitally printing the primer are preferably UV inks or water-based inks enriched with white pigments. However, water-based digital printing inks or so-called hybrid inks are also possible. Application using digital printing is advantageous because the printing system is significantly shorter than a roller system, thus saving space, energy, and costs.

[0069] In a further variant of the present process, a primer layer is applied to the primer, preferably as a single application followed by drying. The primer layer is particularly useful in the case of a subsequent gravure printing process (with rollers), whereas it is not absolutely necessary when using a digital printing process.

[0070] The amount of liquid primer applied is between 10 and 30 g / m², preferably between 15 and 20 g / m². Polyurethane-based compounds are preferred as primers.

[0071] Intaglio and digital printing processes are advantageously used as direct printing methods for printing on wood-based panels. Intaglio printing is a printing technique in which the elements to be reproduced are indentations in a printing form, which is inked prior to printing. The printing ink is primarily located in the indentations and is transferred to the object to be printed, such as a substrate, due to the contact pressure of the printing form and adhesive forces. Indirect gravure printing uses multiple printing rollers.

[0072] In a particularly preferred embodiment, the at least one decoration is applied to the (surface-treated and pre-coated) carrier board using a digital printing process. With digital printing, the print image is transferred directly from a computer to a printing machine, such as a laser printer or inkjet printer. This eliminates the use of a static printing form. Decoration printing is carried out according to the inkjet principle in a single-pass process, spanning the entire width of the top side to be printed, with the boards being moved underneath the printer. However, it is also possible for the carrier board to be printed to be held under the printer, which then passes over the surface at least once during printing.

[0073] The printing inks are grouped in separate rows of print heads, with one or two rows of print heads per color. Digital printing inks are available in colors such as black, blue, red, reddish yellow, and greenish yellow. CMYK is also optionally available. Digital printing inks are optionally based on the same pigments used for analog and / or digital printing with water-based inks. Digital printing inks are preferably based on UV inks. However, water-based digital printing inks or so-called hybrid inks can also be used. After printing, the decorative print is dried and / or irradiated.

[0074] The printing inks are applied in an amount of between 1 and 30 g / m 2< , preferably between 3 and 20 g / m 2< , particularly preferably between 3 and 15 g / m 2<.

[0075] Along with the decoration, the markings required for alignment in the press are also printed.

[0076] It is possible to send the printed board to intermediate storage after this process step. In this case, the applied and melted resin powder layer acts as a protective layer, which on the one hand protects the printed surface during intermediate storage and on the other hand (because the resin layer has not yet fully cured) enables further processing. Particularly in complex manufacturing processes, a decoupling of certain work steps is necessary for reasons of cost, technology, etc. For example, linked production lines can differ greatly in terms of productivity. In this case, buffer stores must be set up in which materials are stacked on top of one another. Furthermore, multiple runs may be necessary in a production line because order quantities, etc., cannot be processed in a single run. In all of these cases, dried orHardened surfaces are advantageous because they protect the printed surface in the event of intermediate storage and also enable further processing.

[0077] In a further embodiment, abrasion-resistant particles are evenly scattered onto the decorative layer or the resin powder layer applied in step c) (step d).

[0078] Abrasion-resistant particles such as corundum (aluminum oxide), boron carbides, silicon dioxide, and silicon carbides can be used. Corundum particles are particularly preferred. These are preferably high-transparency white corundum particles, so that the optical effect of the underlying decoration is minimally affected. Corundum has an irregular spatial shape.

[0079] The quantity of scattered abrasion-resistant particles is 7 to 50 g / m², preferably 10 to 30 g / m², and particularly preferably 15 to 25 g / m². The quantity of scattered abrasion-resistant particles depends on the desired abrasion class and the grain size. Thus, the quantity of abrasion-resistant particles in the case of abrasion class AC3 is in the range between 10 to 15 g / m², in abrasion class AC4 between 15 to 20 g / m², and in abrasion class AC5 between 20 to 35 g / m² when using grain size F200. In this case, the finished panels preferably have abrasion class AC4.

[0080] Abrasion-resistant particles with grain sizes in the F180 to F240 classes, preferably F200, are used. The grain size of class F180 covers a range of 53-90 µm, F220 45-75 µm, F230 34-82 µm, and F240 28-70 µm (FEPA standard). In one variant, white fused alumina particles F180 to F240 are used as abrasion-resistant particles, preferably with a main grain size range of 53-90 µm. In a particularly preferred embodiment, fused alumina particles of classes F180-220 are used. The abrasion-resistant particles must not be too fine-grained (risk of dust formation), but also not too coarse-grained. The size of the abrasion-resistant particles therefore represents a compromise. In a more extensive embodiment, silanized fused alumina particles can be used. Typical silanizing agents are aminosilanes.

[0081] In a further embodiment of the present method, at least a third layer of at least one powdered resin (step e) is applied and melted, in particular, onto the layer of abrasion-resistant particles. This layer serves as a separating layer to seal off the abrasion-resistant particles.

[0082] In a further embodiment of the present method, glass beads are sprinkled (step f), particularly onto the at least one third molten resin powder layer. The glass beads serve as spacers between the abrasion-resistant particles and the subsequent press sheet. This can at least partially reduce sheet wear.

[0083] The preferred glass beads have a diameter of 60-120 µm, preferably 80-90 µm. The diameter of the glass beads is matched to the average particle size of the abrasion-resistant particles used to ensure optimal sealing against the downstream press plate. For example, in the case of Corundum F220, glass beads with a diameter between 70-90 µm are used, and in the case of Corundum F180, glass beads with a diameter between 80-120 µm are used. The amount of glass beads is 5 to 30 g / m², preferably 8 to 20 g / m², particularly preferably 8 to 15 g / m². The glass beads can also be in silanized form. Silanizing the glass beads improves the embedding of the glass beads in the resin matrix.

[0084] In a further embodiment of the present method, at least a fourth layer of at least one powdered resin (step f) is applied and melted, in particular, onto the layer of glass beads. This layer serves to seal off the glass beads and as a finishing layer.

[0085] In a further embodiment of the present process, the layer structure is pressed in a short-cycle press (short-cycle press) (step h). The pressing step takes place under the influence of pressure and temperature at temperatures between 180 and 250°C, preferably between 200 and 230°C, particularly preferably at 200°C and a pressure between 30 and 60 kg / cm², particularly preferably between 40 and 50 kg / cm². The pressing time is between 8 and 30 seconds, preferably between 10 and 25 seconds.

[0086] Preferably, the coated wood-based panel is aligned in the short-cycle press with a structured press plate located in the short-cycle press using markings on the wood-based panel, ensuring congruence between the decor on the wood-based panel and the structure to be imprinted on the press plate. This enables the production of a decor-synchronous structure. During pressing, the melamine resin layers melt, forming a laminate through a condensation reaction that includes the corundum / glass / fiber components.

[0087] A counterlayer, e.g., consisting of several resin layers without additives or a counterlayer paper, can be applied to the underside of the wood-based panel. This ensures that the tensile forces generated by the applied layers during pressing cancel each other out. The counterlayer applied to the underside corresponds approximately in layer structure and thickness to the layer sequence applied to the top side, but without the addition of the additives, abrasion-resistant particles, or glass beads. An impregnated compound can also be used as a counterlayer.

[0088] The production line for manufacturing a carrier board with a decor, in particular a wood-based panel, can therefore comprise the following elements: at least one application device for applying a first resin powder layer, which may contain fibers, to the top side of the wood-based panel and at least one device for melting the first resin powder layer, in particular an IR radiator; opt. at least one application device for applying at least one primer layer; opt. at least one application device for applying at least one primer layer; at least one printing device, opt. at least one application device for applying a further resin powder layer and at least one device for melting the resin powder layer, in particular an IR radiator;, opt. at least one device for scattering a predetermined amount of abrasion-resistant particles; at least one application device for applying a further resin powder layer and at least one device for melting the resin powder layer, in particular an IR radiator; opt.at least one device for scattering a predetermined quantity of glass beads; opt. at least one application device for applying a further resin powder layer and at least one device for melting the first resin powder layer, in particular an IR radiator; and opt. at least one short-cycle press arranged downstream of the last drying device in the processing direction; wherein at least one NIR measuring head, preferably at least one NIR multi-measuring head, is provided downstream of the application device for applying a first resin powder layer and / or downstream of the application devices for applying a further resin powder layer, for recording at least one NIR spectrum of the wood-based panel coated with the powdered resin.

[0089] As mentioned, the NIR measurement method according to the invention can also be used for coating paper layers with resin powder.

[0090] A process for coating a paper layer as a carrier material comprises the following steps: Applying at least one layer of at least one powdered resin (or powdered resin mixture) to at least one side of a paper layer and melting the at least one applied layer of a powdered resin or resin mixture; and drying and curing the layer structure.

[0091] The measuring method according to the invention for determining the application quantity of the powdered resin (or powdered resin mixture) is preferably carried out following the step of applying the layer of powdered resin or resin mixture.

[0092] A production line used for coating paper layers with a powdered resin comprises at least one application device for applying at least one resin powder layer, in particular by means of tribo guns, at least one device for melting the resin powder layer, preferably using an IR radiator, and at least one device for drying and curing the coated paper layer.

[0093] At least one NIR measuring head is provided downstream of the application device for applying a resin powder layer to record at least one NIR spectrum of the paper layer coated with the powdered resin.

[0094] In both production line configurations (wood-based panel, impregnated), the NIR measuring heads are each connected to a control system with an evaluation unit and database for processing and storing the measured NIR data. If the measured actual values ​​deviate from the target values, the system control and regulation system automatically adjusts the data. In principle, all NIR measuring heads used in a production line transmit their measured actual values ​​to the central control and evaluation unit, which, if the measured actual values, for example, of a single NIR measuring head, deviate from the corresponding target values, regulates or predictively controls the production process accordingly.

[0095] The invention is explained in more detail below using exemplary embodiments with reference to the figures. They show: Figure 1: NIR spectra of different amounts of melamine powder resin Figure 2: NIR spectra of different amounts of urea resin Figure 3: NIR spectra of urea and melamine powder resins as well as mixtures of both powder resins Example 1:

[0096] Different amounts of powdered melamine resin were applied to a medium-colored decorative paper (20, 40, 80, and 100 g powder resin / m²). Spectra of the different applied amounts were recorded using an NIR measuring head. A calibration model was created from these spectra using software. The peak at approximately 1500 nm proved to be particularly suitable (see Fig. 1 ). Unknown application quantities of melamine resin were then determined on various substrate materials with different substrate colors. Example 2:

[0097] The same procedure was used for powdered urea resin. The same application quantities were analyzed. Here, too, the peak around approximately 1500 nm could be used to create a calibration model (see Fig. 2 ). Example 3:

[0098] Next, mixtures of urea and melamine resin were prepared. The total amount in each case was 40 g / m². The concentrations varied between 100%, 25% / 75%, 50% / 50%, 25% / 75%, and 100%. Here, too, it was shown that analysis was possible. The spectra of the mixtures lay between the spectra of urea powder resin and melamine powder resin. They approached the melamine spectrum with increasing melamine content. Here, too, the peak around 1500 nm is suitable for establishing a calibration (see Fig. 3 ). After creating a calibration, the homogeneity of powder mixtures can be checked or application quantities can be determined.

Claims

1. A non-destructive method for determining the quantity and / or composition of at least one layer of at least one powdered resin or resin mixture spread on the upper surface of at least one carrier board or at least one paper layer, wherein the quantity of the powdered resin or resin mixture spread is between 10 and 150 g / m2 , comprising the steps of - Applying at least one powdered resin or a powdered mixture of at least two resins in a defined mixing ratio in different quantitatively defined quantities to a carrier material as reference samples; - Recording of at least one NIR spectrum of each of the reference samples using at least one NIR measuring head in a wavelength range between 1400 nm and 1600 nm, and particularly advantageously between 1450 nm and 1550 nm; - Correlating the different quantitative amounts of powdered resin or resin mixture of the reference samples to the recorded NIR spectra of said reference samples; and - Creating a calibration model for the relationship between the spectral data of the NIR spectra and the corresponding quantitative quantities of powdered resin or resin mixture of the reference samples by means of multivariate data analysis; - Applying at least one layer of at least one powdered resin or resin mixture to a carrier material, - Recording at least one NIR spectrum of the carrier material coated with the powdered resin or resin mixture using the at least one NIR measuring head in a wavelength range between 1400 nm and 1600 nm and particularly advantageously between 1450 nm and 1550 nm; and - Determining the quantitative amount of powdered resin or resin mixture applied to the carrier material by comparing the NIR spectrum recorded from the coated carrier material with the calibration model created.

2. Method according to claim 1, characterized in that the powdered resin is a formaldehyde resin, preferably a urea resin, a melamine resin or a phenolic resin, in particular preferably a melamine-formaldehyde resin or a urea resin.

3. Method according to one of the preceding claims, characterized in that at least one mixture of a first powdered resin and a second powdered resin is applied to the at least one carrier material.

4. Method according to claim 3, characterized in that the at least one mixture comprises a first powdered resin and a second powdered resin in a ratio of between 10 wt%: 90 wt% and 90 wt% : 10 wt%, preferably between 25 wt% : 75 wt% and 75 wt% : 25 wt%, more preferably between 55 wt% : 45 wt% and 45 wt% : 55 wt%, e.g. 50 : 50 wt%.

5. Method according to one of the preceding claims, characterized in that the powdered resin contains pigments, conductive substances and / or cellulose.

6. Method according to one of the preceding claims, characterized in that the powdered resin or the mixture of at least two powdered resins is applied in an amount of up to 600 g / m2 , preferably up to 400 g / m2 , in particular preferably up to 200 g / m2 .

7. Method according to one of the preceding claims, characterized in that the powdered resin or the mixture of at least two powdered resins is applied in an amount of between 20 and 100 g / m2 , preferably between 40 and 80 g / m .

28. Method according to one of the preceding claims, characterized in that the one paper layer comprises at least one base paper or at least one pre-treated, impregnated paper.

9. Method according to one of claims 1-7, characterized in that the at least one carrier board is made of a wood-based material, in particular a chipboard, medium-density fibreboard (MDF), high-density fibreboard (HDF), oriented strand board (OSB) or plywood board, of plastic, a wood-based material / plastic mixture or a composite material, a cement fibreboard, gypsum fibreboard or a WPC board (Wood Plastic Composites) or an SPC board (Stone Plastic Composites).

10. Method according to one of the preceding claims, characterized in that spectral data from the entire recorded spectral range are used to determine the amount of powdered resin or resin mixture applied.

11. Method according to one of the preceding claims, characterized in that the determination of the amount of powdered resin or resin mixture applied to the carrier material is carried out continuously and online in a production line, in particular in a production line for the manufacture of wood-based boards or in a production line for the impregnation of paper layers.

12. Method according to claim 11, characterized in that the at least one NIR measuring head moves transversely to the running direction of the carrier material provided with the powdered resin in the production line and traverses over the entire width of the carrier material in order to analyze certain problem areas, in particular shortfall orders in the edge or middle area of the carrier material.

13. Method according to claim 11, in that the at least one NIR measuring head moves in the production line in the direction of travel of the carrier material provided with the powdered resin.

14. Method according to one of claims 11-13, characterized in that the determination of the amount of powdered resin or resin mixture applied to at least one carrier material is carried out several times in the production line, in particular in each case after leaving a device for applying a layer of powdered resin or resin mixture.