METHOD FOR PRODUCING A COMPOSITE MATERIAL

Description

[0001] The present invention relates to a method for producing a composite material and to a composite material as such.

[0002] Wood-containing composite materials are known in various forms in the prior art and are used in different fields of technology. They typically involve processing fine wood particles (fibers, chips, or the like) with a binder to form a solid composite material.

[0003] A particular disadvantage of many of these materials is that they use binders based on fossil raw materials with a high water content of at least 30%. While composite materials with bio-based additives such as lignin are also known, these typically require processing in the liquid state. This necessitates the removal of the water, which requires a correspondingly high energy input, and also causes swelling of the wood, resulting in technological disadvantages that often require additional processing steps to compensate. The environmental footprint and sustainability of wood- or lignocellulose-based materials are therefore significantly worsened by the use of binders based on fossil raw materials.

[0004] Panel materials, such as those used for parquet flooring, must possess a wide range of mechanical and physical properties. High-density fiberboard (HDF), manufactured using binders derived from fossil raw materials, serves as the benchmark for panel-shaped parquet substrates. Due to its properties, it can also be fitted with delicate milling and click-system profiles at the edges.

[0005] Also worth mentioning in this context are so-called wood-plastic composites (WPC), which, however, have a high plastic content, making their production costly and energy-intensive. Typically, WPC made from bio-based plastics is not available. Even with higher wood content, WPCs exhibit very high material densities due to their extrusion manufacturing technology and are therefore not suitable for the desired applications in the field of parquet flooring due to these material and density-related properties.

[0006] It would therefore be desirable to overcome the aforementioned disadvantages of the state of the art and to create a composite material that can be produced without the use of fossil-based raw materials and without the addition of water, which necessarily results in subsequent drying in the process steps, and yet has sufficient mechanical stability, especially for subsequent processing steps, and at the same time has an excellent environmental footprint.

[0007] Document JP2022119673A discloses the preambles of claims 1 and 11.

[0008] One object of the present invention can be seen as achieving at least one of these objectives. In particular, one object can be seen as providing a completely bio-based composite material based on lignocellulose, which has a high lignocellulose or wood content and which can be produced with the lowest possible energy input.

[0009] The problem is solved in particular by a method according to claim 1, in which a lignocellulosic base material is mixed with a matrix material and subsequently compressed. The base material is in particular in the form of dust, while the matrix material can in particular be in the form of powder, wherein the average particle size of the base material and matrix material is at most 500 µm.

[0010] Surprisingly, it was discovered within the scope of the present invention that a small particle size of the base material and matrix material in combination with a fine mixture of the two components enables the production of a plate-shaped composite material whose property profile is comparable to that of known composite materials and is therefore suitable as an adequate replacement in many areas of application.

[0011] The lignocellulosic base material content is greater than or equal to 60 wt.% of the total mass of the mixture, and the composite material produced therefrom can have densities of less than 800 kg / m³, thus distinguishing it from wood-plastic composites, which, as already mentioned, typically have a significantly higher matrix material content and, in any case, a higher density. In the composite material according to the invention, the matrix material content is therefore less than or equal to 40 wt.%, but it can also be less than or equal to 20 wt.% or less than or equal to 10 wt.%.

[0012] In the process according to the invention, the resulting mixture is compressed and heated until the core temperature of the compact reaches or exceeds the softening point of the matrix material. The softening point refers in particular to the Vicat softening temperature determined according to DIN EN ISO 306.

[0013] Without being bound to this theory, the present inventors assume that heating the compact at least to the softening point, in combination with compression and the intimate mixing of the dust and powder components, enables a particularly good bond between the two components to form a dimensionally stable and mechanically robust composite material.

[0014] In certain embodiments, smaller particle sizes of the base material and matrix material offer improved properties; however, excessive comminution can negatively impact the energy balance of the process without significantly improving the properties of the composite material. Therefore, the matrix material powder preferably has an average particle size of less than 100 µm, more preferably less than 50 µm or less than 20 µm.

[0015] In this context, the average particle size refers in particular to the median value, i.e., the 0.5 quartile, of the particle size distribution.

[0016] Polyhydroxyalkanoates or lignin are used as matrix materials. Of the polyhydroxyalkanoates, polyhydroxybutyrate or a mixture of polyhydroxybutyrate and polyhydroxyvalerate with a maximum of 2 wt% polyhydroxyvalerate is preferred. Kraft lignin is preferred as the lignin.

[0017] The base material is preferably dust from coniferous wood species, especially spruce wood.

[0018] No additional liquid, particularly water, needs to be added to the mixture of base material and matrix material to form a solid composite. To minimize or eliminate the energy required for liquid evaporation, the water content of the starting materials is preferably very low. Thus, the water content of the base material is typically less than 20 wt% based on the total mass of the base material, and particularly less than 12 wt%. The water content of the matrix material is typically less than 10 wt% based on the total mass of the matrix material. Regarding the water content of the matrix material, it should be noted that this can depend on the specific matrix material used, with a polyhydroxyalkanoate typically having a water content of less than 3 wt%, and particularly less than 0.4 wt%, and lignin typically having a water content of less than 10 wt%.-%, in particular less than 6 wt.%.

[0019] The mixture of base material and matrix material may optionally contain one or more additives, which may be selected from one or more of the following classes of substances: pigment, flame retardant, water-repellent agent, odorizing agent. The additive can be added to the mixture when the base material and matrix material are combined.

[0020] In special embodiments, the weight ratio between base material and additive can be adjusted as follows: base material to pigment 5:1 to 100:1; base material to flame retardant 5:1 to 1000:1; base material to hydrophobic agent 10:1 to 1000:1; base material to odorizing agent 10:1 to 1000:1.

[0021] The additive may also be added to the mixture as a powder, i.e., in particular with an average particle size of no more than 100 µm.

[0022] The base material can be wood dust directly from a woodworking machine. To achieve the desired particle size distribution, a fractionation device can be provided, which performs fractionation in a known manner. This fractionation device can be a sieve or a cyclone separator. The direct use of wood dust is advantageous because no energy is required for further comminution of the wood material.

[0023] The mixing of the base material, matrix material, and optional additive may take place in a high-performance mixer to ensure thorough homogenization of the components before pressing. A suitable high-performance mixer is, for example, a vertical belt mixer.

[0024] Pressing is carried out in a hot press, which has heated press plates. As mentioned, the temperature to be reached in the core of the pressed material must be adjusted to the softening point of the respective matrix material; however, it is typically above 120°C, especially between 140°C and 200°C. Pressing can also be carried out using continuous presses, as are typically used in the production of other wood-based panels.

[0025] In this process, further processing steps may be provided after pressing, such as machining or further forming of the manufactured composite material.

[0026] Lamination or other surface bonding with another material can also occur, creating a layered material. This additional material could be, for example, a real wood veneer applied to one side of the composite. In this way, panel materials can be produced that are used as parquet flooring or furniture construction materials.

[0027] By applying the method according to the invention, a composite material with special properties can be produced. Therefore, the present invention also relates to a composite material as such. In particular, it should be noted that the process features give the composite material a special property profile. The invention therefore also relates to a composite material obtainable via a method according to the invention.

[0028] The composite material may have one or more of the following properties: density between 500 and 1,200 kg / m³; transverse tensile strength between 0.3 and 2.5 MPa; thickness swelling in 24 h in water between 3% and 30%; increased resistance to fungal attack.

[0029] Increased resistance to fungal growth can mean, in particular, that no fungal growth occurs after 4 weeks of storage at a relative humidity above 90%. Storage can be carried out, in particular, in accordance with or based on ÖNORM B 6010, section 4.22. "No fungal growth" or "fungus-free" can mean, in particular, that no fungal growth can be detected by visual inspection in accordance with or based on EN ISO 846, section 9.1.

[0030] The composite material can be bonded with conventional wood adhesives, for example with adhesives based on polyurethane, polyvinyl acetate, emulsion polymer isocyanate, thermoset or thermoplastic adhesive systems.

[0031] The composite material can be coated with films or liquid systems, for example with resin films, paints, oils or waxes.

[0032] The invention relates to a method according to claim 1.

[0033] Optionally, the water content of the mixture obtained in step (b) before compaction in step (c) is provided for to be at most 20 wt.%, in particular at most 10 wt.%, of the total mass of the mixture. Optionally, the matrix material content is provided for to be at least 5 wt.% of the total mass of the mixture.

[0034] If necessary, the base material is wood dust from softwood, in particular from spruce wood.

[0035] According to the invention, the matrix material is a polyhydroxyalkanoate, lignin, in particular kraft lignin, or a mixture thereof.

[0036] If applicable, the matrix material is specified as polyhydroxybutyrate.

[0037] Optionally, the matrix material is provided to be a mixture of polyhydroxybutyrate and polyhydroxyvalerate, wherein the mixture contains at most 2 wt% polyhydroxyvalerate.

[0038] If necessary, the mixture is pressed until the core temperature of the composite material is at least 120°C, in particular until the core temperature is between 140°C and 200°C.

[0039] If applicable, the additive is selected from one or more of the following: pigment, flame retardant, water repellent, odorizing agent.

[0040] If necessary, the composite material is subjected to a processing step after pressing, for example laminating, coating, sawing, grinding, milling, drilling.

[0041] If necessary, the composite material is to be bonded over its entire surface to a layer of wood veneer after pressing to form a parquet material.

[0042] The invention also relates to a composite material, in particular produced by a method according to the invention, as defined in claim 11.

[0043] If necessary, the composite material is designed to have a density between 500 and 1200 kg / m 3<.

[0044] If necessary, the composite material is designed to have a transverse tensile strength of between 0.3 and 2.5 MPa.

[0045] If necessary, the composite material is designed to exhibit a thickness swelling in water of between 3.0% and 30% over 24 hours.

[0046] If necessary, it is stipulated that the composite material is free from fungal growth after 4 weeks of storage at over 90% relative humidity, whereby the test procedure during storage is carried out in accordance with ÖNORM B 6010, section 4.22, and where a visual determination of fungal growth is carried out in accordance with EN ISO 846, section 9.1.

[0047] If applicable, the composite material is intended to be a parquet material comprising a wood layer as well as a base layer containing the base material and the matrix material.

[0048] The figures show: Fig. 1 a schematic representation of a composite material according to an embodiment of the present invention; and Fig. 2 a schematic representation of a composite material according to a further embodiment of the present invention.

[0049] Unless otherwise indicated, the figures show the following components: composite material 1, milled recess 2, milled profile 3, cover lamella 4. Example 1:

[0050] Spruce wood dust from an industrial grinding machine was fractionated using a cyclone separator to provide wood dust with a median particle size of approximately 350 µm. The wood dust had a moisture content of approximately 9 wt.% and was subsequently used as a base material in a process according to the invention.

[0051] Polyhydroxybutyrate with a median particle size of about 7 µm and a moisture content of about 0.4% was used as a matrix material in a process according to the invention, as supplied by the manufacturer.

[0052] Approximately 80 wt% of the base material and approximately 20 wt% of the matrix material were homogenized in a high-performance double-blade mixer at approximately 30,000 rpm and a power output of approximately 2 hp / l.

[0053] The resulting mixture was then pressed in a hot press to form a sheet material with dimensions of 250 mm x 1000 mm x 10 mm. Pressing continued until a core temperature of approximately 180°C was reached. This temperature is significantly above the softening point of the matrix material used.

[0054] After pressing, a compact composite material with the following properties was obtained: density approximately 650 kg / m³; transverse tensile strength approximately 1 MPa; thickness swelling approximately 5% over 24 hours in water; no mold growth after 10 days of storage at 90% relative humidity. Compared to typical HDF materials, this composite material exhibits an improved property profile, particularly with regard to thickness swelling and mold growth.

[0055] The composite material was further bonded over its entire surface with a layer of real wood top lamellae, and a tongue-and-groove system was formed by milling on opposite edges, so that the material produced in this way could be used as a floor parquet material.

[0056] The resulting composite material 1 with its groove-shaped milled recess 2 and milled profile 3, but without cover lamellae, is shown in the axonometric representation of Fig. 1 shown schematically. Fig. 2 shows a view with cover lamella 4. Example 2:

[0057] The second embodiment was carried out analogously to the first embodiment, with the difference that a kraft lignin powder with a median particle size of approximately 25 µm and a moisture content of approximately 6 wt% was used as the matrix material, comprising approximately 40% by weight. All other parameters and process steps were identical to those of the first embodiment.

[0058] The resulting composite material had a property profile that was only slightly different compared to the first embodiment.

Claims

1. A method for producing a composite, in particular in the form of a panel, comprising the steps of: a. providing a lignocellulosic base material, in particular present as dust, having an average particle size of at most 500 µm, and a thermoplastic matrix material, in particular present as powder, having an average particle size of at most 500 µm, preferably at most 100 µm, b. mixing the base material, matrix material and optionally at least one further additive, wherein the base material content relative to the total mass of the mixture is at least 60 wt% and wherein the matrix material content relative to the total mass of the mixture is at most 40 wt%, c. pressing the mixture obtained in step (b) in a hot press at least until the core temperature of the composite reaches the softening point of the matrix material, characterised in that the matrix material is a polyhydroxyalkanoate, lignin, or a mixture thereof.

2. The method according to claim 1, characterised in that the water content of the mixture obtained in step (b) is, prior to pressing, at most 20 wt% weight, in particular at most 10 wt%, based on the total mass of the mixture.

3. The method according to any one of claims 1 or 2, characterised in that the matrix material content relative to the total mass of the mixture is at least 5 wt%.

4. The method according to any one of claims 1 to 3, characterised in that the base material is wood dust from softwood, in particular from spruce wood.

5. The method according to any one of claims 1 to 4, characterised in that the lignin in the matrix material, if present, is kraft lignin.

6. The method according to claim 1, characterised in that - the matrix material is polyhydroxybutyrate, - or that the matrix material is a mixture of polyhydroxybutyrate and polyhydroxyvalerate, the mixture containing at most 2 wt% polyhydroxyvalerate.

7. The method according to any one of claims 1 to 6, characterised in that the mixture is pressed until the core temperature of the composite reaches at least 120°C, in particular until the core temperature is between 140°C and 200°C.

8. The method according to any one of claims 1 to 7, characterised in that the additive is selected from one or more of: pigment, flame retardant, hydrophobing agent, odorant.

9. The method according to any one of claims 1 to 8, characterised in that after pressing, the composite is subjected to a processing step, for example, laminating, coating, sawing, grinding, milling, drilling.

10. The method according to any one of claims 1 to 9, characterised in that after pressing, the composite is joined to a wooden veneer layer in a flush manner for forming a parquet material.

11. A composite, in particular produced by a method according to any one of claims 1 to 10, comprising a lignocellulosic base material having an average particle size of at most 500 µm, a thermoplastic matrix material and optionally at least one further additive, wherein the base material content relative to the total mass of the mixture is at least 60 wt%, and wherein the matrix material content relative to the total mass of the mixture is at most 40 wt%, characterised in that the matrix material is a polyhydroxyalkanoate, lignin, or a mixture thereof.

12. The composite according to claim 11, characterised in that the composite has a density between 500 and 1200 kg / m3.

13. The composite according to any one of claims 11 or 12, characterised in that the composite has a transverse tensile strength between 0.3 and 2.5 MPa.

14. The composite according to any one of claims 11 to 13, characterised in that the composite has a swelling in thickness between 3.0% and 30% after 24 hours in water.

15. The composite according to any one of claims 11 to 14, characterised in that the composite is free of fungal decay after 4 weeks of storage at 90% relative humidity, the test during storage being performed according to ÖNORM B 6010, section 4.22, and the fungal decay being visually determined according to EN ISO 846, section 9.1.

16. The composite according to any one of claims 11 to 15, characterised in that the composite is a parquet material, which comprises a wooden layer and a base layer containing the base material and matrix material.