Three-dimensional substrate for microbial cultures

Abstract

To provide a three-dimensional substrate with structural and compositional gradient for microbial cultures and cocultures, and to provide a method for producing the same.SOLUTION: The production method includes the following steps of: a) filling a first compartment 2 with a base solution or a pre-formed hydrogel comprising a polysaccharide, a protein, and a salt; b) filling a second compartment 3 with a cross-linking medium comprising a salt, a culture medium, and distilled water, wherein the first compartment is placed on top of the second compartment and the compartments 2, 3 are separated by a semipermeable membrane 4 which is permeable to the salt, but impermeable to the polysaccharide and protein; c) incubating at a temperature of 4°C to 25°C for 2 minutes to 20 hours to allow the salt to diffuse from the second compartment through the semipermeable membrane into the first compartment and to crosslink; and d) separating a three-dimensional substrate formed in the first compartment; wherein in the substrate solution or pre-formed hydrogel, the polysaccharide is selected from sodium alginate and pectin, and the protein is selected from mucin and serum albumin.SELECTED DRAWING: Figure 1

Description

[Technical field]

[0001] The present invention relates to three-dimensional gradient substrates for microbial culture and co-culture, as well as methods for simultaneously preparing substrates and gradients thereon.

[0002] In one embodiment, the present invention relates to a three-dimensional substrate for microbial culture and co-culture and a method for preparing the same, wherein the three-dimensional substrate comprises: - a diffusion system (1) comprising a first compartment (2) and a second compartment (3), in which the first compartment (2) is placed above the second compartment (3) and the first and second compartments (2, 3) are separated by a semipermeable membrane (4); - a substrate solution comprising a polysaccharide, a protein and a salt or a preformed hydrogel comprising a polysaccharide, a protein and a salt; - Crosslinking medium containing salts, culture medium and distilled water Includes. [Background technology]

[0003] Background technology Currently, bacterial cultures are commonly obtained in agar, which has its attendant limitations. It is noteworthy that, among other things, the soft agar gel allows for some degree of bacterial mobility, in addition to the diffusion of materials into it. However, the gel is necessarily placed on top of and confined by a hard agar substrate (1.5-2.0% w / v), so that three-dimensional movement is partially limited.

[0004] Furthermore, pouring of soft agar gel into high-strength supports such as cell culture plates or multi-well plates for high-throughput screening and result interpretation requires some manual procedures and complicated structures, thus limiting the screening capacity and increasing the risk of contamination. Summary of the Invention [Problem to be solved by the invention]

[0005] There is a strong need for alternative methods for microbial culture and co-culture that can mimic both the conditions found in mucus and physiopathological culture conditions. [Means for solving the problem]

[0006] Object of the invention Forming a first object of the present invention is a three-dimensional matrix adapted for the study of bacterial and / or microbial cultures and co-cultures.

[0007] In a second object, the present invention describes a method for simultaneously preparing a three-dimensional matrix and a gradient therein. [Brief description of the drawings]

[0008] [Figure 1] FIG. 1 is a diagrammatic representation of a diffusion system comprising a three-dimensional substrate of the present invention.

[0009] [Diagram 2] Rheological properties of the three-dimensional gradient substrate of the present invention loaded with human serum albumin.

[0010] [Diagram 3] 1 illustrates the possibility of altering the viscoelastic properties of three-dimensional matrices according to embodiments of the present invention (mucin-matrix).

[0011] [Figure 4] Barrier effect on the diffusion of active ingredients and nanoparticles.

[0012] [Diagram 5] A) Three-dimensional matrices of the present invention stained with Alizarin Red to reveal internal crosslinking gradients; B) Variation of viscoelastic properties controlled by different crosslinking times.

[0013] [Figure 6] Culturability (CFU / mL) of Pseudomonas aeruginosa assessed on the three-dimensional substrate of the present invention shows viability equivalent to planktonic cultures.

[0014] [Figure 7] Culturability (CFU / mL) of Escherichia coli assessed on the three-dimensional substrate of the present invention shows viability comparable to planktonic cultures.

[0015] [Figure 8] Similar to the case of chronic co-infection (results of Example 7) and unlike the case of suspension in liquid (planktonic) medium, it shows the ability to reproduce the simultaneous presence of several bacterial strains.

[0016] [Figure 9] 1 illustrates the possibility of controlling the oxygen tension profile of the substrate of the present invention.

[0017] [Figure 10] Modification of the profile shows how bacteria can respond to changes in oxygen gradients (Results from Example 9).

[0018] [Figure 11] It shows the presence of aggregates similar to those observed in chronic infection (results from Example 10, bar corresponds to 10 μm). DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0019] Detailed Description of the Invention In a first objective, the present invention describes a three-dimensional substrate.

[0020] In the following description, the term "substrate" refers to examples of substrates.

[0021] The three-dimensional matrices of the present invention comprise a mixture of multiple components that can form gels with different cross-linking agents through a diffusion process that controls the process of gradient formation.

[0022] The present inventors have surprisingly shown that the rheological properties of this matrix can be precisely modified by varying the cross-linking parameters.

[0023] The "substrate" includes a diffusion system, which is a two-compartment system (formed by the distance between two bridges) that forms a bridge gradient to mimic and replicate the typical diffusion of nutrients and molecules in a microbial microenvironment.

[0024] As shown in FIG. 1, the diffusion system 1 comprises a first compartment 2 (also called apical side) and a second compartment 3 (also called basal side). In a preferred embodiment of the present invention, the first compartment 2 is placed above the second compartment 3. The first and second compartments are separated by a semipermeable membrane 4. For the purposes of the present invention, the semipermeable membrane 4 is permeable to salts but impermeable to polysaccharides and proteins. For example, the membrane is impermeable to alginate and / or mucin solutions. In a preferred embodiment, the semipermeable membrane 4 is made of materials such as those referred to as polycarbonate, polystyrene, poly(diallyldimethylammonium chloride), polyethylene terephthalate or polyamide (nylon).

[0025] In a preferred embodiment, the diffusion system 1 is designed by design software and manufactured by three-dimensional printing, or alternatively by rapid prototyping, additive machining, or injection molding.

[0026] A solution referred to as a substrate solution is deposited in the first apical compartment 2. For the purposes of the present invention, the substrate solution comprises a polysaccharide, a protein and a salt. In an embodiment, the substrate solution has a viscosity of 0.05 to 100 Pa.s, preferably 0.2 to 10 Pa.s.

[0027] In an alternative embodiment, a pre-formed gel comprising polysaccharides, proteins and salts may be introduced into the first apical compartment 2 instead of a solution.

[0028] In a preferred embodiment, the polysaccharide of the substrate solution is selected from sodium alginates of various molecular weights, pectins of various molecular weights and degrees of esterification and amidation, hyaluronic acids of various molecular weights, gellans of various molecular weights, dextrans of various molecular weights.

[0029] In a particularly preferred embodiment, the base solution contains alginate as the polysaccharide.

[0030] The alginate is present in an amount of about 0.2-8%, preferably about 5% (w / v).

[0031] In preferred embodiments, the protein of the substrate solution is selected from mucin, serum albumin, fibrinogen, fibronectin, collagen, elastin, insulin, and transferrin.

[0032] In a particularly preferred embodiment, the substrate solution comprises mucin.

[0033] Even more preferably, the mucin is at a concentration of about 25 mg / mL.

[0034] In an even more preferred embodiment, the mucin and alginate are present in the substrate solution in the following ratios (weight / weight): [Table 1]

[0035] In a preferred embodiment, the salt of the substrate solution is selected from sodium chloride, ammonium phosphate, potassium chloride, sodium hydrogen phosphate, sodium bicarbonate, potassium chloride, dipotassium hydrogen phosphate trihydrate, magnesium chloride hexahydrate, sodium sulfate, tris(hydroxymethyl)aminomethane, sodium nitrate, sodium nitrite, potassium nitrate, silver nitrate, ammonium nitrate, calcium nitrite, potassium bisulfate, potassium sulfate, sodium bisulfate, sodium sulfate and / or copper(I) sulfate.

[0036] In a preferred embodiment, the salt of the substrate solution is typically NaCl, which in an even more preferred embodiment is present in an amount of about 0.007-9 mg / mL, preferably about 7 mg / mL.

[0037] Concerning the second basolateral compartment 3, a bridging medium is deposited therein. For the purposes of the present invention, such a bridging medium comprises salts, culture medium and distilled water.

[0038] In certain embodiments, the salt included in the crosslinking medium is selected from calcium acetate, calcium citrate, calcium chloride, calcium glubionate, calcium gluceptate, calcium gluconate, calcium nitrate, calcium phosphate, calcium hydrogen phosphate, hydroxyapatite, carbonated hydroxyapatite, tricalcium phosphate, octacalcium phosphate, potassium nitrate, zinc nitrate, magnesium nitrate, barium nitrate, titanium nitrate, iron(III) nitrate, copper nitrate, gallium nitrate, calcium nitrite, aluminum sulfate, aluminum sulfoacetate, zinc sulfate, tetraamminecopper(II) sulfate, copper sulfate, iron(III) sulfate hydrate, ferrous sulfate, calcium sulfate and / or magnesium sulfate.

[0039] In a preferred embodiment, the salt is typically calcium gluconate, which in an even more preferred embodiment is present in an amount of about 0.05-1.2% (w / v), preferably about 0.16% (w / v).

[0040] In preferred embodiments, the culture medium is represented by Mueller-Hinton and Luria-Bertani culture media.

[0041] In one embodiment, the components of the "substrate" are dissolved in a bacterial medium or aqueous solution suitable for the purpose.

[0042] The person skilled in the art knows how to adjust the thickness of the “matrix” by varying the volume of solution introduced and the diameter of said first compartment 2 .

[0043] As noted above, in another embodiment, a preformed hydrogel containing the same ingredients as described for the solution is introduced into the first apical compartment (2).

[0044] In a second object, in effect, methods for preparing the "substrates" of the invention are described.

[0045] In particular, such a method - providing a diffusion system (1) comprising a first compartment (2) and a second compartment (3), in which the first compartment (2) is placed on the second compartment (3) and the first and second compartments (2, 3) are separated by a semipermeable membrane (4) that is permeable to salts but not to polysaccharides and proteins; - filling the first compartment (2) with a matrix solution or a preformed hydrogel comprising polysaccharides, proteins and salts; - filling said second compartment (3) with a cross-linking medium comprising salts, culture medium and distilled water, - Incubate The process includes:

[0046] In particular, the substrate solution and the crosslinking medium are as described above.

[0047] In particular, the incubation continues for a time sufficient to allow diffusion of salt from the second basolateral compartment (3) through the semipermeable membrane (4) to the first apical compartment and to allow cross-linking, the time also controlling the simultaneous formation of a gradient.

[0048] For example, incubation may be continued at a temperature of 4 to 25° C. for a period of time ranging from 2 minutes to 20 hours.

[0049] In a preferred embodiment, the incubation continues for 20 hours at a temperature of 4°C.

[0050] In a preferred embodiment, the "substrate" is prepared using a 5% (w / v) alginate solution prepared in a 7.07 mg / mL solution of sodium chloride and 0.16% (w / v) calcium gluconate prepared in Mueller-Hinton culture medium, which acts as a cross-linking agent. Once the solution is prepared, 500 μL of the alginate solution is introduced into the upper chamber of the diffusion device, while 6 mL of 0.16% (w / v) calcium gluconate is introduced into the lower chamber. Finally, the two-compartment diffusion chamber is left to stand at a temperature of approximately 4 °C for 20 hours.

[0051] Advantageously, the preparation process does not expose the "substrate" to high temperatures or reagents incompatible with eukaryotic or prokaryotic cells, proteins or loads of heat-labile substances.

[0052] Also advantageously, the resulting three-dimensional substrates for the growth of microorganisms in pure or co-culture are characterized by adjustable modular cross-linking, gas concentration and composition gradients.

[0053] The inventors have surprisingly shown that the addition of human serum albumin to the "Matrix" increases its viscoelasticity, an observation that demonstrates not only that proteins are denatured by the "Matrix", but also that the "Matrix" is able to mimic the physiological interactions of albumin in mucus.

[0054] This observation makes the "Matrix" particularly advantageous for mimicking or recreating mucus. Indeed, currently available mucins cannot be cross-linked, since they lose cross-linking sites during the extraction and purification process. Mucin gelation is only possible under highly acidic conditions that are incompatible with microbial culture. The "Matrix" allows the preparation of hydrogels from commercially available mucins, and is defined as "mucin-matrix".

[0055] Therefore, the "mucin-matrix" was used for the evaluation of the diffusion of active ingredients through the mucus barrier. The "matrix" was shown to act as a barrier to the diffusion of active ingredients both in the presence and absence of mucin. The "matrix" also acts as a barrier to the diffusion of nanoparticles.

[0056] The technology for manufacturing the "matrix" allows the application of the processes described above to preformed hydrogels, thus creating gradients that can provide viscoelastic properties of interest for specific applications.

[0057] The use of the "substrate" in the antibiogram makes it possible to obtain more reliable results than those achieved by current methods for the calculation of the minimum inhibitory concentration (MIC) of both single strain cultures and complex cultures (microbial cultures containing different genera, species or strains). In fact, the "substrate" produces a material that makes it possible to provide bacteria in a suitable context to form aggregates or biofilms or to mimic a three-dimensional matrix such as mucus in order to reproduce phenomena related to the spatial heterogeneity of the medium. This is made possible by the three-dimensional structure of the "substrate", in addition to gradients of nutrients, oxygen and water, factors that are generally not adjustable in the media found in the background art.

[0058] In one embodiment, the "substrate" is separated from the diffusion system in which it is manufactured and placed in a support, e.g., a high strength support such as a cell culture plate or multi-well plate for high throughput screening, allowing for short analysis times and simple handling, avoiding cross contamination, and obtaining meaningful data.

[0059] In one embodiment, the "substrate" can be divided into multi-well plates of desired size.

[0060] The following examples should be construed as illustrative of the present invention, but not limiting thereof, the scope of which is defined by the appended claims. EXAMPLES

[0061] Example 1: "Substrate" with human serum albumin Human serum albumin (HSA) was added to the alginate and mucin-alginate solutions prior to crosslinking using the dual syringe method. 10 μL of 56.2 mg / mL HSA solution was mixed with the alginate or mucin / alginate solution to give a final concentration of 1.182 mg / mL HSA. The viscoelastic properties of the resulting hydrogels are shown in Figure 2.

[0062] Example 2: Preparation and characterization of "mucin-substrate" Mucin was added to the "Matrix" in the amounts shown in Table 1, where the mucin concentrations are given relative to the final product. [Table 2] Commercially available porcine gastric mucin was dissolved in aqueous NaCl (16.33 mg / mL) at a concentration of 25 mg / mL. After stirring overnight at 4° C., alginate powder was added until the desired concentration shown in Table 1 was achieved and stirred until completely dissolved. Hydrogels were formed using a two-compartment diffusion system. Briefly, 200 μL of mucin / alginate solution was introduced into the apical chamber of the diffusion system (diameter = 1.5 cm, thickness ≈ 120 μm) and left at 4 °C for 20 h, allowing the release of Ca from the calcium gluconate solution loaded into the lower chamber. 2+ The thickness of the "matrix" can be adjusted as needed by varying the volume of solution introduced and the diameter of the first compartment 2. The viscoelastic properties were measured and the obtained data are shown in FIG. The obtained data show that the system of the present invention offers the possibility to optimize the viscoelastic properties of mucin-based hydrogels by controlling the crosslinking degree, such as crosslinking time and crosslinker concentration, as well as the concentration of polysaccharide and its molecular weight. An example of the property variation by changing the alginate concentration is shown in Figure 3.

[0063] Example 3: Mucus Barrier Models and "Substrate" and "Mucin-Substrate 2" (Mus 3 SUB) A "substrate" having the properties described in Example 2 and Mus 3 SUB was tested for its ability to mimic the mucus barrier. In addition to gold nanoparticles, the active ingredients cephalexin and epirubicin were tested. Gold nanoparticles have a steric hindrance of about 25 nm, cephalexin about 3 nm, and epirubicin about 4 nm. The chart in FIG. 4 shows that the molecule is a permeable support, a "substrate" or Mus 3 Demonstrates the ability to pass through a barrier made of SUB. The results show that when a drug has a strong interaction with mucin, as in the case of epirubicin (pKa=8.01, logD7.4=0.03), the translocation of the drug is slowed down. In contrast, when the drug has a low interaction with mucin, as in the case of cephalexin (pKa=3.26 and 7.23, logD7.4=-2.5), the translocation is extremely fast. This indicates the ability to act as an interaction barrier and indicates that the mucin in the "matrix" maintains its ability to interact with molecules. If the interactions are equal, the steric hindrance effect can be shown by a comparison between gold nanoparticles (25 nm) and cephalexin (3 nm), where it is seen that the larger gold nanoparticles are slowed down by the presence of the "substrate".

[0064] Example 4: Fabrication of a "Matrix" with Viscoelasticity and Differential Gradient "Matrix" made from pre-crosslinked hydrogels are indicated with a "double." Several "substrates" were prepared in a two-compartment diffusion system using different cross-linking times to form a double cross-linked structure. Sodium alginate was dissolved at 2.8% (w / v) in NaCl solution (16.33 mg / mL) for 12 hours under slow magnetic stirring. The alginate solution and distilled water were mixed in a 1:4 ratio using a double syringe method (step 1). A suspension of calcium carbonate (7 mg / mL) in NaCl solution (16.33 mg / mL) was sonicated for 5 minutes (UP200S, ultrasonicator, Hielscher, Ultrasound Technology), centrifuged at 3500 rpm for 1 minute (Vortex IKA MS3 100-240 V orbital stirrer), and further mixed with the solution prepared in step 1 in a 1:5 ratio (step 2). Finally, a GDL solution (10 mg / mL) was prepared in NaCl (16.33 mg / mL) and mixed with the solution prepared in step 2 in a 1:6 ratio. Approximately 706 μL of the final mixture was inserted into the first apical compartment and the mixture was allowed to react overnight ("Substrate" - single). After overnight cross-linking, 0.2% calcium gluconate or calcium chloride was dissolved in 40 mM Alizarin Red and 6 mL of this solution was introduced into the second basolateral compartment and allowed to react for different times, e.g., 5 min, 30 min and 60 min, and 20 h, to allow the generation of a gradient ("Substrate" - double). Alizarin Red is an organic red stain used to identify calcium deposits in cell cultures with a well-defined staining protocol. As can be seen in Figure 5A, diffusion of calcium gluconate resulted in the formation of a calcium gradient in the "Matrix" with deep red or mixed regions (lower and upper parts of the sample, respectively), while the "Matrix"-single was transparent and the "Matrix"-double after 20 h of second crosslinking showed a uniform red color (black in the figure). The viscoelastic changes induced by the second crosslinking of the "matrix" were also analyzed (Figure 5B). Both conservative and dissipative moduli increased with time of second crosslinking, more pronounced between 60 min and 20 h. In fact, the maximum value of the conservative moduli was detected in samples exposed to 20 h of diffusion, with no significant difference observed between 30 and 60 min of diffusion.

[0065] Example 5: "Substrates" mimic physiological or pathological situations Bacterial starter cultures were inoculated into appropriate media and grown overnight. To inoculate the starter culture, in this case P. aeruginosa, a small amount of frozen bacterial culture was mechanically removed from the original cryovial stored at -80°C, suspended in 10 mL of Mueller-Hinton (MH) medium, and then maintained at 37°C overnight with agitation at 200 rpm. The next day, the estimation of the bacterial count was performed spectrophotometrically at λ=600 nm (optical density 600; OD600). To prepare the samples for the absorbance test, the suspension was flushed with fresh MH medium in a 1:10 ratio. The same medium was used as a blank. Once the absorbance of the diluted samples was measured, the bacterial count was estimated using a calibration curve showing the bacterial count at OD600 values. This concentration was then converted to the undiluted medium concentration. To test the bacterial viability in the "substrates", each "substrate" was infected with 500, 1000 and 5000 bacteria for 24 and 48 hours of incubation. For this purpose, 1 mL of suspension was taken from the initial starter culture and diluted to the required concentration. The "substrates" were then infected by introducing 100 μL of the bacterial suspension and incubated at 37° C. under stationary conditions. CFU counts were used to test for the presence of bacteria in the "substrate", i.e., bacteria that migrated and successfully grew in the "substrate", compared to bacteria cultured under planktonic conditions, where axenic cultures were performed both under planktonic conditions and in the "substrate". To estimate the number of bacteria that migrated and multiplied inside the "substrate", residual bacteria found on the top of the "substrate" and on the well walls were removed by means of two washes with fresh MH medium. The "substrate" was then lysed using a 50 mM sodium citrate solution at pH 7.4. After lysis, the suspension was poured off and plated after CFU counting. Briefly, the medium was introduced into a 1.5 mL centrifuge tube and then washed with 0.9% sodium chloride solution, pH 7.4 [10 -6 ~10 -10 ]-fold dilution. Then, 10 μl of the diluted suspension was evenly distributed onto MH agar plates. The MH agar plates were left in an incubator overnight. The actual colonies in the infected "substrate" were calculated by multiplying by the dilution factor. For the "substrate", 150 μL of lysis agent was taken into account to calculate the CFU / mL. The results are shown in Figure 6A. In further experiments, the "substrate" was added 10 8 10 needed to obtain bacteria 4 After this time, the "substrate" supernatant was removed and the "substrate" was washed twice with fresh culture medium. Then, 100 μL of antibiotics at three concentrations, 0.1 MIC, 1 MIC and 10 MIC, were added. The antibiotics were allowed to act for 24 hours under static incubation at 37°C. After the effective antibiotic action time, viable CFU counts were performed. Different controls were performed: (I) planktonic bacteria at each concentration of antibiotic; (II) planktonic bacteria without any treatment; (III) untreated infected "substrate"; and (IV) solutions for "substrate" formation. For infected "substrates" tested with antibiotics, even in the latter case, only the CFU of the dissolved "substrate" was taken into account. The data obtained are shown in Figure 6B.

[0066] Example 6: Add E. coli to the "Substrate" prepared in Example 5 ("Substrate" - Single) Bacterial starter cultures were inoculated into Luria-Bertani (LB) broth and grown overnight. To inoculate the starter culture, in this case E. coli, a small amount of frozen bacterial culture was mechanically removed from the original cryovial stored at -80°C, suspended in 10 mL of Luria-Bertani (LB) broth medium, and then maintained at 37°C overnight with agitation at 200 rpm. The next day, the estimation of the bacterial count was performed spectrophotometrically at λ=600 nm (optical density 600; OD600). To prepare the samples for absorbance testing, the suspension was flushed with fresh medium in a 1:10 ratio. The same medium was used as a blank. Once the absorbance of the diluted samples was measured, the bacterial count was estimated using a calibration curve showing the bacterial count at OD600 values. This concentration was then converted to the undiluted medium concentration. To test the bacterial viability in the "substrates", each "substrate" was infected with 500, 1000 and 5000 bacteria for 24 hours of incubation. For this purpose, 1 mL of suspension was taken from the initial starter culture and diluted to the required concentration. The "substrates" were then infected by introducing 100 μL of the bacterial suspension and incubated at 37° C. under stationary conditions. CFU counts were used to test for the presence of bacteria in the "substrate", i.e., bacteria that migrated and successfully grew in the "substrate", compared to bacteria cultured under planktonic conditions, where axenic cultures were performed both under planktonic conditions and in the "substrate". To estimate the number of bacteria that migrated and multiplied inside the "substrate", residual bacteria found on the top of the "substrate" and on the well walls were removed by means of two washes with fresh medium. The "substrate" was then lysed using a 50 mM sodium citrate solution at pH 7.4. After lysis, the suspension was poured off and plated after CFU counting. Briefly, the medium was introduced into a 1.5 mL centrifuge tube, then lysed with 0.9% sodium chloride aqueous solution, pH 7.4 [10 -6 ~10 -10 ]-fold dilution. Then, 10 μl of the diluted suspension was evenly distributed onto the LB agar plate. The LB agar plates were left in an incubator overnight. The actual colonies in the infected "substrate" were calculated by multiplying by the dilution factor. For the "substrate", 150 μL of lysis agent was taken into account to calculate the CFU / mL. The results are shown in Figure 7. Various controls were performed: (I) planktonic bacteria at each concentration of antibiotic; (II) "substrate" without infection; and (III) solution for "substrate" formation.

[0067] Example 7: The "matrix" of the present invention was produced using a 5% (w / v) alginate solution prepared in a solution of sodium chloride (7.07 mg / mL) and 0.16% (w / v) calcium gluconate prepared in Mueller-Hinton culture medium as a cross-linking agent. Once the solution was prepared, 500 μL of the alginate solution was placed in the upper chamber of the diffusion device, while 6 mL of 0.16% (w / v) calcium gluconate was introduced into the lower chamber. Finally, the two-compartment diffusion chamber was kept at 4 °C overnight for 20 h. In parallel, bacterial cultures were inoculated and grown overnight. To inoculate the cultures, a small amount of frozen bacterial culture was mechanically taken from the original cryovial (stored at -80°C) suspended in 10 mL of Mueller-Hinton culture medium and maintained at 37°C and 200 rpm. After overnight inoculation, bacterial numbers were quantified spectrophotometrically at λ = 600 nm (OD600). Staphylococcus aureus ATCC 25923 and Pseudomonas aeruginosa PAO1 ATCC 15692 were cultivated in a 1:1 ratio under substrate and planktonic conditions and incubated at 37°C for evaluation of bacterial growth in the substrate. The "substrate" was infected with 100 μL 103 S. aureus and P. aeruginosa in a 1:1 ratio. After 24 hours of incubation, 150 μL of 50 mM trisodium citrate dihydrate, pH 7.4, was used to dissolve the substrate. After 2 minutes of reaction, the new suspension was diluted with 0.9% NaCl solution, pH 7.4 [10 -6 ~10 -10 ]-fold dilutions were then poured out. 10 μL of the diluted suspension was then evenly distributed onto Mueller-Hinton medium agar plates and incubated overnight at 37°C. Colony forming units (CFU) were then calculated taking into account the dilution factor. The results are shown in Figure 8. In suspension in culture medium (planktonic conditions), S. aureus could not be cultivated in the co-presence of P. aeruginosa. Only P. aeruginosa was counted (black bars), whereas S. aureus was not detectable (ND in FIG. 8). If the co-culture was carried out on the substrate of the invention (grey bars), both bacteria were viable and could form colonies. This result represents a situation of simultaneous presence of two bacterial infections in chronic infections, but only with the substrate of the invention, and indicates the possibility of testing competitive effects, not under standard culture conditions.

[0068] Example 8: The "substrates" of the present invention were prepared using a 5% (w / v) alginate solution prepared in a 7.07 mg / mL solution of sodium chloride and 0.16% (w / v) calcium gluconate prepared in Mueller-Hinton culture medium acting as a cross-linking agent. Once the solutions were prepared, 250 or 500 μL of the alginate solution was introduced into the upper chamber of the diffusion device, while 6 mL of 0.16% (w / v) calcium gluconate was introduced into the lower chamber. The "substrates" prepared using 250 μL of alginate solution are designated as "thin," while those prepared using 500 μL are referred to as "thick." Finally, the two-compartment diffusion chambers were stored overnight at 4 °C for 20 h. The O2 tension in the "substrate" was measured using a Clark-type oxygen sensor (OX-25; Unisense, Aarhus N, Denmark) connected to a highly sensitive picoamp 4-channel amplifier called Microsensor Multimeter S / N 8678 (Unisense). O2 diffuses into the environment through a silicone membrane with the sensor chip and is reduced at the gold cathode surface, thus generating an electric current. The picoamp meter converts the resulting reduction current into a signal. The signal from the oxygen sensor is prepared in picoamps. Therefore, the oxygen sensor needs to be connected to a picoamp amplifier during the measurement. The Unisense SensorTrace software then automatically converts the signal from the partial pressure (oxygen tension) to the equivalent oxygen concentration (μmol / L). Before starting the measurements, the electrodes, i.e. the control anode and the protective cathode, are polarized overnight and further calibrated with air-saturated water (positive control) and 2% w / v sodium dithionite (negative control). Before the measurements, low-melting-point agarose, consisting of 2% (w / v) agarose in 7.07 mg / mL NaCl, was placed in a Petri dish. The freshly prepared "substrate" was placed on the agarose layer. The microelectrode was placed using a motorized micromanipulator (MXU2; PyroScience, Aquisgrana, Germany). Measurements were performed in the center of the "substrate", from its surface (0 mm) through its thickness until the tip completely penetrated the structure. To avoid oxygen diffusing from the side of the "substrate", an O-ring with an inner diameter corresponding to the "substrate" diameter was used. The maximum depth reached by the tip, referred to as the final depth, was approximately 2200 μm and 3200 μm for the "thin" and "thick" "substrates", respectively. Successive points were taken 100 μm apart. Each point was performed in triplicate. The results are shown in Figure 9. A continuous decrease in oxygen tension was observed throughout the thickness of both types of matrices, with variations of 83.0 μmol / L and 70.3 μmol / L for the thin and thick matrices, respectively. A larger decrease in oxygen tension was seen in the thin matrices. This result indicates the possibility of obtaining an oxygen gradient within the same matrices.

[0069] Example 9: The "substrate" of the present invention was prepared using a 5% (w / v) alginate solution prepared in a 7.07 mg / mL solution of sodium chloride and 0.16% (w / v) calcium gluconate prepared in Mueller-Hinton culture medium acting as a cross-linking agent. Once the solutions were prepared, 500 μL of the alginate solution was introduced into the upper chamber of the diffusion device, while 6 mL of 0.16% (w / v) calcium gluconate was introduced into the lower chamber. Finally, the two-compartment diffusion chamber was stored at 4 °C overnight for 20 hours. In parallel, bacterial cultures were inoculated and grown overnight. To inoculate the cultures, a small amount of frozen bacterial culture was mechanically taken from the original frozen vial (stored at -80°C) suspended in 10 mL of Mueller-Hinton culture medium and maintained at 37°C and 200 rpm. After overnight inoculation, bacterial numbers were quantified spectrophotometrically at λ = 600 nm (OD600). 100 μL P. aeruginosa PAO1 ATCC 15692 was cultured on the “substrate” with a bacterial count equal to 10 3 and the oxygen tension was measured as described in Example 2 after 12 h, 24 h and 48 h of infection. The results are shown in Figure 10. The oxygen tension profile inside the "substrate" continued to decrease with incubation time, achieving anoxic conditions at a depth of about 300 μm after 48 h. As the incubation time increased, for example from 12 to 24 h, the oxygen tension difference between the most superficial and innermost layers became gradually more pronounced. This result indicates the synergy of bacteria and the "substrate" matrix in reconstructing culture conditions more suitable for certain types of bacteria.

[0070] Example 10: The "substrate" of the present invention was prepared using a 5% (w / v) alginate solution prepared in a 7.07 mg / mL solution of sodium chloride and 0.16% (w / v) calcium gluconate prepared in Mueller-Hinton culture medium acting as a cross-linking agent. Once the solutions were prepared, 500 μL of the alginate solution was introduced into the upper chamber of the diffusion device, while 6 mL of 0.16% (w / v) calcium gluconate was introduced into the lower chamber. Finally, the two-compartment diffusion chamber was stored at 4 °C overnight for 20 hours. To express the fluorescent proteins, P. aeruginosa PA01 was transformed with the plasmids by the process suggested by Cadoret et al. (2014). Briefly, electrocompetent P. aeruginosa and electroporation of the fluorescent plasmid pMF440. P. aeruginosa was electroporated by means of a series of dilution steps in electroporation buffer (sucrose solution 300 mM) from an overnight culture in Luria-Bertani (LB). The overnight culture was pelleted and resuspended in electroporation buffer. The suspension was then recentrifuged and resuspended in fresh electroporation buffer in half the volume of the initial culture. This process was repeated until the volume was reduced to 0.01 of the initial volume. These steps aim to provide the bacteria with a high nutrient environment for growth, even in the absence of ions that could create an electric arc during the electroporation process. Plasmid pMF440 was obtained as a bacterial transformation of E. coli DH5α from the database Addgene (ID code: 62550). For plasmid DNA extraction, E. coli was grown in LB containing 100 μg / mL ampicillin. Plasmid DNA was extracted using a QIAprep Spin Miniprep (Quiagen) kit according to the manufacturer's instructions. After extraction, DNA was eluted with MilliQ water and stored at -20 °C until required. DNA was extracted with deionized water to achieve a concentration of 0.1–1 μg / mL. 80 mL of competent P. aeruginosa cell suspension was mixed with 10 mL of DNA suspension, and this suspension was placed on ice for 30 min before electroporation. The electroporation process was carried out in a gene pulser electroporation system using a conductive cuvette. An electronic impulse was applied for 5 ms at 2.5 kV, 200 Ω, 25 μF. After this shock, the cuvette contents were transferred to a Falcon tube containing 2 mL of optimal glucose-enriched broth and incubated at 37°C for 2 h under stirring conditions. After 2 h of recovery, the suspension was plated on selective agar plates containing 300 μg / mL carbenicillin. Further cultivation and expansion of the transformed bacteria was carried out in carbenicillin-containing medium. Bacterial cultures were inoculated and grown overnight. To inoculate the cultures, a small amount of frozen bacterial material was mechanically taken from the original cryovial (stored at -80°C) suspended in 10 mL of Mueller-Hinton culture medium and maintained at 37°C and 200 rpm. After overnight inoculation, bacterial numbers were quantified spectrophotometrically at λ = 600 nm (OD600). 100 μL of 103 P. aeruginosa PACC 1 ATCC 15692 expressing green were cultured with the "substrate" and incubated at 37°C. The bacterial formation was evaluated by confocal microscopy. After 24 hours of incubation, the samples were observed under a confocal laser microscope. Scanning was performed using an excitation wavelength of 587 nm and a maximum depth of approximately 50 μm. The gains were analyzed using the LasX software provided by Leica. The results are shown in Figure 11. The "substrate" allows the formation of bacterial aggregates similar to those observed in human infections, whereas these aggregates are not obtained under suspension culture conditions. The bacteria respond to the gradient by organizing themselves into multicellular aggregates with a morphology and size similar to those previously observed in cystic fibrosis sputum and chronic wounds. These bacterial aggregates correlate with the oxygen gradient and then lead to the preparation of alginate by P. aeruginosa, the latter thought to be the root of chronic infections by this pathogen.

[0071] From the above, the advantages of the present invention will be readily apparent to those skilled in the art.

[0072] The "substrate" of the present invention has properties that make it beneficial for applications in the food, environmental and health fields. The "substrate" is also used in the field of bacteria-related products, such as, for example, cellulose, polyester, insulin, antibacterial, antifungal, antiviral, antithrombotic agents, immunomodulators, anticancer agents, enzyme inhibitors, insecticides, herbicides, bactericides (e.g., alkaloids and flavonoids) and substances that promote the growth of animals and plants. By way of example, the "substrate" is beneficially used in analyses aimed at monitoring bacterial growth, interactions between microbial communities and / or antibacterial potential of drugs and micro / nano particles, pollutants, probiotics, probiotic release. Furthermore, the three-dimensional substrate is suitable for aerospheric studies to understand microbial adaptation to space environments, such as microgravity and high radiation levels, as well as screening methods for the selection of effective antibacterial treatments and early steps in the search for new drugs. Further applications are in the food industry, for example to understand how certain diets and / or probiotics and probiotic carriers as dietary supplements affect bacterial behavior and microbial communities, and in environmental science, for example to evaluate contaminants or biocides in cleaning agents in relation to microbial communities, products for increasing agricultural production or environmental pollution repurification. Other examples include the cosmetics field, such as cosmetics that release microorganisms that affect the skin. The "matrix" can also be used as a way to recreate the microbial microenvironment in a microbial pad to treat water and reduce contamination. The co-culture of different microorganisms in a three-dimensional matrix can also be used in biofuel production and bioenergy conversion, since these applications require the physical and spatial organization of the microorganisms. Finally, the three-dimensional matrix can also be used as a microbial fuel cell.

[0073] The use of the three-dimensional substrate described herein is immediately understandable and does not require any technical experience or special equipment. Moreover, the three-dimensional substrate of the present invention is compatible with commonly used platforms such as 6-well, 12-well, 24-well, 48-well, 96-well or 384-well multi-well plates, Transwell® systems and microfluidic devices. The three-dimensional substrate is absolutely cost-competitive, its manufacture is scalable and modular, its viscoelasticity and gradient can be easily modified according to research purposes.

[0074] Experiments using the three-dimensional substrates of the present invention have given highly reproducible and realistic results.

[0075] The "Substrate" has further advantages compared to synthetic or agar-based materials, which are summarized below. - The component is a carbon source for the bacteria and in some cases is produced by the bacteria themselves, for example Pseudomonas aeruginosa secretes alginate. - "Substrate" grows bacteria in three-dimensional gradient structures that are not possible with current methods. - The microorganisms cultured on the "substrate" are supported on a high-strength support (e.g. high-throughput screening plates), allowing for rapid analysis and minimal manual handling, while avoiding cross-contamination and providing meaningful data. - The preparation process avoids the use of high temperatures or reagents that are incompatible with the encapsulation of microorganisms (e.g. bacterial cells) or cell monolayers. - The preparation process avoids the use of high temperatures or reagents that are incompatible with the addition of eukaryotic or prokaryotic cells, proteins or heat-labile substances. - The kinetic control of the "Substrate" allows the "Substrate" to be subsequently efficiently divided into multi-well plates of different sizes, from 6 to 96 or 384 wells.

[0076] Agar gels available in the prior art, especially 0.2-0.8% w / v agar gels, offer the potential for microbial culture in three dimensions but have several limitations. - Does not show a gradient and remains aligned on a 2D hard agar plate; - Soft agar gels show the mobility of bacteria and the possibility of diffusion of substances into the gel. However, they are placed on a hard agar substrate (1.5-2.0% w / v), which allows the cells to move partially in three dimensions, since they are prevented by the base level. - The pouring of soft agar gel onto high strength supports (high throughput screening plates) and interpretation of results requires manual handling and complex setup, increasing the possibility of contamination and limiting the screening capabilities associated with cost-effectiveness compared to the "substrate" of the present invention. - Agar needs to be boiled to completely dissolve and maintained at 50-55°C to maintain liquid form until inoculation and plating. These temperatures are unfavorable to many microorganisms and may affect the heat-labile components of the medium, necessitating enrichment of culture constituents (e.g. proteins and vitamins). "Substrate" allows for synthesis and polymerization under conditions that do not affect the heat-labile components or encapsulation of microorganisms (e.g. bacterial cells) or stratification on the cell monolayer.

[0077] Finally, the three-dimensional matrices of the present invention, which are made from water-soluble polymers of natural origin and prepared without the use of toxic solvents, are environmentally friendly devices.

Claims

1. A diffusion system (1) for preparing a microbial growth substrate having a modular bridging gradient, comprising a first apical compartment (2) and a second basolateral compartment (3), the first compartment (2) being placed on top of the second compartment (3), a substrate solution comprising polysaccharides, proteins and salts being contained in the first apical compartment (2), a bridging medium comprising salts, culture medium and distilled water being contained in the second basolateral compartment (3), and the first and second compartments (2, 3) being separated by a semi-permeable membrane (4) that is permeable to salts but not to polysaccharides and proteins.

2. 2. The diffusion system (1) of claim 1, wherein the semipermeable membrane is made of polycarbonate, polystyrene, poly(diallyldimethylammonium chloride), polyethylene terephthalate or polyamide (nylon).

3. 3. The diffusion system (1) of claim 1 or 2, wherein the polysaccharide in the base solution is selected from sodium alginate of various molecular weights, pectin of various molecular weights and various degrees of esterification and amidation, hyaluronic acid of various molecular weights, gellan of various molecular weights, and dextran of various molecular weights.

4. 4. The diffusion system (1) of any one of claims 1 to 3, wherein the solution has a viscosity of 0.05 to 100 Pa.s, or 0.2 to 10 Pa.s.

5. 5. The diffusion system (1) according to any one of claims 1 to 4, wherein the protein in the substrate solution is selected from the group consisting of mucin, serum albumin, fibrinogen, fibronectin, collagen, elastin, insulin and transferrin.

6. 6. The diffusion system (1) according to any one of claims 1 to 5, wherein in the base solution, the salt is selected from sodium chloride, ammonium phosphate, potassium chloride, sodium hydrogen phosphate, sodium bicarbonate, potassium chloride, dipotassium hydrogen phosphate trihydrate, magnesium chloride hexahydrate, sodium sulfate, tris(hydroxymethyl)aminomethane, sodium nitrate, sodium nitrite, potassium nitrate, silver nitrate, ammonium nitrate, calcium nitrite, potassium bisulfate, potassium sulfate, sodium bisulfate, sodium sulfate and / or copper(I) sulfate.

7. 7. The diffusion system (1) according to any one of claims 1 to 6, wherein in the base solution, the salt is selected from calcium acetate, calcium citrate, calcium chloride, calcium glubionate, calcium gluceptate, calcium gluconate, calcium nitrate, calcium phosphate, calcium hydrogen phosphate, hydroxyapatite, carbonated hydroxyapatite, tricalcium phosphate, octacalcium phosphate, potassium nitrate, zinc nitrate, magnesium nitrate, barium nitrate, titanium nitrate, iron (III) nitrate, copper nitrate, gallium nitrate, calcium nitrite, aluminum sulfate, aluminum sulfoacetate, zinc sulfate, tetraammine copper (II) sulfate, copper sulfate, iron (III) sulfate hydrate, iron sulfate, calcium sulfate and / or magnesium sulfate.

8. The diffusion system (1) of any of claims 1 to 7, wherein a preformed hydrogel comprising polysaccharides, proteins and salts is inserted into the first apical compartment (2) instead of a matrix solution.

9. 1. A method for producing a three-dimensional substrate for microbial culture, comprising: - providing a diffusion system (1) comprising a first compartment (2) and a second compartment (3), in which the first compartment (2) is placed on the second compartment (3) and the first and second compartments (2, 3) are separated by a semipermeable membrane (4) which is permeable to salts but not to polysaccharides and proteins; - filling said first compartment (2) with a matrix solution or a preformed hydrogel comprising polysaccharides, proteins and salts; - filling said second compartment (3) with a bridging medium containing salts, culture medium and distilled water; - Incubate for a time sufficient to allow the salt to diffuse from the second basolateral compartment (3) through the semipermeable membrane (4) to the first apical compartment and to cross-link. The method includes:

10. 10. The method of claim 9, wherein the substrate solution comprises polysaccharides represented by alginate and proteins represented by mucin.

11. 11. The method of claim 9 or 10, wherein the cross-linking medium comprises a salt represented by calcium gluconate.

12. 12. The method of any of claims 9 to 11, wherein the crosslinking medium comprises a culture medium selected from Mueller-Hinton and Luria-Bertani.

13. The method according to any of claims 9 to 12, wherein the incubation lasts for a period of time ranging from 2 minutes to 20 hours, at a temperature ranging from 4 to 25°C, preferably for 20 hours at 4°C.

14. A three-dimensional substrate for growing microorganisms in pure or co-culture, characterized by modular bridges, gas concentration and composition gradients, obtainable by the method of claim 13.

15. A method for cultivating microbial cultures comprising the use of a three-dimensional substrate obtained by the method of any of claims 9 to 14.

16. 16. The method of claim 15, wherein said microbial culture is a bacterial culture, which may include a variety of strains.