Positive electrode sheet, secondary battery, and electric device

Abstract

A positive electrode sheet (10), a secondary battery (100), and an electric device (1000). The positive electrode sheet (10) comprises a positive electrode current collector (11), and a first positive electrode coating (12) and a second positive electrode coating (13) laminated in this order on the positive electrode current collector (11). The first positive electrode coating (12) comprises a first positive electrode active material and an inorganic filler. The number of particle accumulation layers in the first positive electrode coating (12) is calculated by the following formula: n=T×(M+1) / (M×D 1 v 50+D 2 v 50), n is in the range of 4 to 7, T is the thickness of the first positive electrode coating (12) in μm, M is the mass ratio of the first positive electrode active material to the inorganic filler contained in the first positive electrode coating (12), and D 1 v 50 is the median particle diameter of the first positive electrode active material, and D 2 v 50 is the median particle size of the inorganic filler, and D 1 v 50 is 0.6 μm to 1.2 μm, and D 2 v 50 is 0.6 μm to 1.5 μm.

Description

[Technical Field]

[0001] CROSS-REFERENCE TO RELATED APPLICATIONS This application claims priority to and the benefit of Chinese Patent Application No. 202211047596.1, filed on August 29, 2022. The entire contents of the above-referenced applications are incorporated herein by reference.

[0002] The present disclosure relates to the field of battery technology, and in particular to positive electrodes, secondary batteries, and electrical devices. [Background technology]

[0003] Secondary batteries are widely used in consumer electronic products (such as mobile phones and tablet computers) and electric vehicles. However, if a secondary battery is pierced with a nail, crushed, shocked, or otherwise mistreated, a short circuit can occur within the battery, releasing a large amount of Joule heat and potentially leading to thermal runaway. Among the common short-circuit modes in batteries, the short circuit that occurs when the positive electrode current collector (e.g., aluminum foil) comes into contact with the negative electrode active material layer releases the most heat and is the most dangerous short-circuit mode for batteries. Therefore, it is necessary to provide effective safety measures against this short-circuit mode. Summary of the Invention [Problem to be solved by the invention]

[0004] Therefore, embodiments of the present disclosure provide a positive electrode, a secondary battery, and an electrical device that effectively solves the problem of thermal runaway caused by the battery's positive electrode current collector contacting the negative electrode, and controls the increase in the battery's internal resistance value within a narrow range so as not to affect the battery's electrochemical performance during normal operation. [Means for solving the problem]

[0005] According to a first aspect, the present disclosure further provides a method for manufacturing a semiconductor device comprising: a positive electrode current collector; a first positive electrode coating laminated on at least one surface of the positive electrode current collector, the first positive electrode coating including a first positive electrode active material and an inorganic filler that is not electrochemically active; a second positive electrode coating laminated on a surface of the first positive electrode coating facing away from the positive electrode current collector, the second positive electrode coating including a second positive electrode active material; Including, The number n of particle packing layers in the first positive electrode coating is determined by the following relationship: n=T×(M+1) / (M×D 1 v 50+D 2 v 50), where n is in the range of 4 to 7, where T represents the thickness of the first positive electrode coating measured in μm, M represents the mass ratio of the first positive electrode active material to the inorganic filler, and D 1 v 50 represents the median particle size of the first positive electrode active material measured in μm, and D 2 v 50 represents the median particle size of the inorganic filler measured in μm, where D 1 v 50 ranges from 0.6 μm to 1.2 μm, and D 2 v 50 provides a positive electrode having a thickness in the range of 0.6 μm to 1.5 μm.

[0006] In a positive electrode according to a first aspect of the present disclosure, the relationship between the thickness of the first positive electrode coating, the mass ratio of the first positive electrode active material to the inorganic filler, and the number n of particle packing layers in the first positive electrode active material is established, with n being controlled to be within a range of 4 to 7, the median particle size of the particles of the first positive electrode active material being controlled to be within a range of 0.6 μm to 1.2 μm, and the median particle size of the inorganic filler being controlled to be within a range of 0.6 μm to 1.5 μm. This ensures that the number of packing layers and particle density in the first positive electrode coating are appropriate, effectively protecting the positive electrode current collector in an abnormal event such as when the battery is pierced with a nail or crushed, thereby preventing the positive electrode current collector from contacting the negative electrode and causing thermal runaway, and preventing the internal resistance of the battery from becoming too large during normal operation and affecting electrochemical performance.

[0007] In an embodiment of the present disclosure, D 1 v 50 ranges from 0.6 μm to 0.9 μm.

[0008] In an embodiment of the present disclosure, T ranges from 2 μm to 10 μm.

[0009] In an embodiment of the present disclosure, T ranges from 4 μm to 7 μm.

[0010] In an embodiment of the present disclosure, M ranges from 1 to 5.

[0011] In an embodiment of the present disclosure, the thermal decomposition temperature of the inorganic filler is 300° C. or higher.

[0012] In an embodiment of the present disclosure, the inorganic filler comprises one or more of boehmite, alumina, zirconia, silica, or magnesium hydroxide.

[0013] In embodiments of the present disclosure, the first active cathode material includes one or more of lithium iron phosphate, lithium manganese iron phosphate, lithium vanadium phosphate, lithium vanadyl phosphate, or lithium vanadium fluorophosphate, and the second active cathode material includes one or more of lithium cobalt oxide, lithium manganese oxide, lithium nickel oxide, lithium vanadate, lithium titanate, lithium nickel manganese oxide, lithium nickel cobalt oxide, lithium nickel cobalt manganese oxide, lithium nickel cobalt aluminum oxide, or a lithium-rich manganese-based material.

[0014] In an embodiment of the present disclosure, the median particle size of the second positive electrode active material is in the range of 6 μm to 18 μm.

[0015] In an embodiment of the present disclosure, the first positive electrode coating further comprises a first binder and a first conductive agent, and the second positive electrode coating further comprises a second binder and a second conductive agent.

[0016] In embodiments of the present disclosure, the weight percentage of the first binder in the first positive electrode coating is greater than the weight percentage of the second binder in the second positive electrode coating.

[0017] In an embodiment of the present disclosure, the weight percentage of the first binder in the first positive electrode coating ranges from 5% to 10%, and the weight percentage of the first conductive agent in the first positive electrode coating ranges from 1% to 3%.

[0018] In embodiments of the present disclosure, the first binder and the second binder separately comprise one or more of polyvinylidene fluoride (PVDF), vinylidene fluoride-hexafluoropropylene copolymer, vinylidene fluoride-acrylic acid copolymer, polytetrafluoroethylene (PTFE), polyacrylic acid (PAA), polyacrylate, polyvinyl alcohol (PVA), polyimide (PI), polyurethane, epoxy resin, styrene-butadiene rubber (SBR), fluororubber, or sodium carboxymethyl cellulose (CMC-Na).

[0019] In an embodiment of the present disclosure, the first conductive agent and the second conductive agent each include one or more of conductive carbon black, graphite, carbon fiber, carbon nanotubes, or graphene.

[0020] In an embodiment of the present disclosure, the first positive electrode coating includes the following components in weight percentages: 50% to 85% first positive electrode active material, 10% to 40% inorganic filler, 5% to 10% first binder, and 1% to 3% first conductive agent.

[0021] In an embodiment of the present disclosure, the second positive electrode coating includes the following components in weight percentages: 90% to 99% second positive electrode active material, 0.5% to 1.5% second binder, and 0.5% to 1.5% second conductive agent.

[0022] According to a second aspect, the present disclosure provides a secondary battery including a positive electrode according to the first aspect of the present disclosure.

[0023] The secondary battery according to the second embodiment of the present disclosure has a low internal resistance and excellent safety performance.

[0024] According to a third aspect, the present disclosure provides an electric device including a secondary battery according to the second aspect of the present disclosure. [Brief explanation of the drawings]

[0025] [Figure 1A] FIG. 1 is a schematic structural diagram of a negative electrode according to an embodiment of the present disclosure. [Figure 1B] FIG. 2 is a schematic structural diagram of another negative electrode according to an embodiment of the present disclosure. [Figure 2] 1 is a schematic diagram of a secondary battery according to an embodiment of the present disclosure. [Figure 3] 1 is a schematic diagram of an electrical device according to an embodiment of the present disclosure. DETAILED DESCRIPTION OF THE INVENTION

[0026] Embodiments of the present disclosure are described below with reference to the accompanying drawings in which embodiments of the present disclosure are shown.

[0027] 1A and 1B, an embodiment of the present disclosure provides a positive electrode 10. The positive electrode 10 includes a positive electrode current collector 11, and a first positive electrode coating 12 and a second positive electrode coating 13 laminated in this order on at least one surface of the positive electrode current collector 11. The first positive electrode coating 12 includes a first positive electrode active material and an inorganic filler that is not electrochemically active. The second positive electrode coating 13 includes a second positive electrode active material. The number n of particle packing layers in the first positive electrode coating 12 is determined by the following relationship: n=T×(M+1) / (M×D 1 v 50+D 2 v 50), where n is in the range of 4 to 7, where T represents the thickness of the first positive electrode coating 12 measured in μm, M represents the mass ratio of the first positive electrode active material to the inorganic filler, and D 1 v 50 represents the particle diameter of the first positive electrode active material when the cumulative volume ratio of the first positive electrode active material reaches 50%, and D 2 v 50 represents the particle size value of the inorganic filler when the cumulative volume fraction of the inorganic filler reaches 50% (i.e., D 1 v 50 represents the median particle diameter of the first positive electrode active material, and D 2 v50 represents the median particle size of the inorganic filler), both measured in μm, where D 1 v 50 ranges from 0.6 μm to 1.2 μm, and D 2 v 50 ranges from 0.6 μm to 1.5 μm.

[0028] In the positive electrode, two positive electrode coatings are simultaneously disposed on one side of the positive electrode current collector 11. The first positive electrode coating 12, located closest to the positive electrode current collector 11, is controlled to contain both a first positive electrode active material and an inorganic filler. The first positive electrode coating 12 provides a safety protection function. The high thermal stability and non-conductivity of the inorganic filler in the first positive electrode coating reduce the possibility of the positive electrode current collector 11 coming into contact with the negative electrode active material layer in an emergency, such as when the battery is crushed, impacted, or pierced by a nail, thereby reducing the possibility of a short circuit. During the early stages of a short circuit within the battery, the inorganic filler's good thermal conductivity quickly transfers the Joule heat generated by the short circuit, preventing heat concentration and a continuous increase in the battery core temperature, thereby improving battery safety. In addition, the presence of the inorganic filler also reduces the distribution sites of the active material in the first positive electrode coating, reducing the risk of oxidative decomposition of the electrolyte and thus reducing heat generation during the decomposition reaction. The first positive electrode active material participates in the charge / discharge process of the battery during normal operation, contributing to capacity and thus reducing the loss of energy density and the increase in internal resistance of the battery core caused by the use of a safety coating (e.g., a filler layer) that is not electrochemically active.

[0029] It has been found that the number of layers and bulk density of the particles of the first positive electrode active material and the particles of the inorganic filler in the first positive electrode coating 12 have a significant impact on the safety and internal resistance of the battery, but the industry has not paid much attention to this point. In this disclosure, the thickness T of the first positive electrode coating 12, the mass ratio M of the particles of the first positive electrode active material and the particles of the inorganic filler, and the median particle diameters (i.e., D v50), a quantitative relationship is established for the number n of particle packing layers in the first positive electrode coating 12, where n is controlled to be within the range of 4 to 7, the median particle diameter of the particles of the first positive electrode active material is controlled to be within the range of 0.6 μm to 1.2 μm, and the median particle diameter of the inorganic filler is controlled to be within the range of 0.6 μm to 1.5 μm. This ensures that the number of packing layers and particle density in the first positive electrode coating are appropriate, effectively protecting the positive electrode current collector 11 without excessively sacrificing the battery's energy density and preventing an excessive increase in the battery's internal resistance, which would affect the battery's cycle performance and other electrochemical performance.

[0030] Specifically, if n is less than 4, the number of particle-packed layers in the first positive electrode coating 12 is too small, resulting in too coarse particle packing. As a result, in the event of an emergency, such as when the battery is crushed, impacted, or punctured by a nail, the first positive electrode coating 12 will not adequately protect the positive electrode current collector 11, increasing the likelihood that the positive electrode current collector 11 will come into direct contact with the negative electrode active material layer, thereby deteriorating the safety of the battery. If n is greater than 7, the number of particle-packed layers in the first positive electrode coating 12 will be too large, resulting in too dense particle packing. This will result in too high an internal resistance of the battery core, which will make it difficult for the electrolyte to penetrate the first positive electrode coating 12 and affect the battery's cycle performance, etc. Additionally, to ensure that the packing density of the two types of particles after mixing is not too dense, the median particle sizes of the first positive electrode active material particles and the inorganic filler particles must not differ significantly.

[0031] D of the particles of the first positive electrode active material 1 v 50 may be 0.6 μm, 0.7 μm, 0.8 μm, 0.9 μm, 1 μm, 1.1 μm, 1.2 μm, etc. 1 v 50 is in the range of 0.6 μm to 0.9 μm in some embodiments. 2 v50 may be 0.6 μm, 0.7 μm, 0.8 μm, 0.9 μm, 1 μm, 1.1 μm, 1.2 μm, 1.3 μm, 1.4 μm, 1.5 μm, etc.

[0032] In this disclosure, D 1 v The specific value of D 50 may be obtained from a particle size distribution graph of the first positive electrode active material obtained by a laser diffraction method. For the test method, refer to GB / T19077-2016 / ISO13320:2009 "Particle size analysis - laser diffraction method." The test equipment is generally a laser particle size analyzer (e.g., a Malvern3000 laser particle size analyzer). Similarly, D 2 v The particle diameter D 50 of the material when the cumulative volume fraction of the particles of the material reaches 50% may be obtained from a particle size distribution graph of the inorganic filler obtained by a laser diffraction method. v 50 may also be referred to as the "median particle size" of the material. In addition, T may be obtained by directly or indirectly measuring the thickness of first positive electrode coating 12. M may be obtained by analyzing the composition of first positive electrode coating 12.

[0033] It should be noted that in the present disclosure, the laminate structure including the first positive electrode coating 12 and the second positive electrode coating 13 may be provided on one surface of the positive electrode current collector 11 (as shown in FIG. 1A ) or on both surfaces of the positive electrode current collector 11 (as shown in FIG. 1B ). When a laminate structure is provided on each of both surfaces of the positive electrode current collector 11, only the first positive electrode coating of the laminate structure on one surface needs to satisfy the condition that the parameter n is in the range of 4 to 7. Of course, the first positive electrode coating of the laminate structure on both surfaces of the positive electrode current collector may also satisfy the condition that the parameter n is in the range of 4 to 7. The positive electrode current collector 11 may include aluminum foil, aluminum alloy foil, aluminum-plated organic film, carbon-coated aluminum foil, carbon-coated aluminum alloy foil, carbon-coated aluminum-plated organic film, etc. In some embodiments, the positive electrode current collector 11 is aluminum foil or aluminum alloy foil.

[0034] In an embodiment of the present disclosure, the mass ratio M of the first positive electrode active material to the inorganic filler may be in the range of 1 to 5. When M is in this range, the safety protection effect of the first positive electrode coating 12 and the energy density of the battery can be ensured.

[0035] To ensure that the first positive electrode coating 12 has excellent safety performance, in embodiments of the present disclosure, the thickness T of the first positive electrode coating 12 may be controlled to be within a range of 2 μm to 10 μm. Herein, the thickness T refers to the thickness of a single layer of the first positive electrode coating. In some embodiments, the thickness T of the first positive electrode coating 12 may be within a range of 4 μm to 7 μm. In this case, the thickness of the first positive electrode coating 12 is appropriate for providing effective safety protection and further improving the capacity performance of the positive electrode.

[0036] In embodiments of the present disclosure, the inorganic filler has a thermal decomposition temperature of 300°C or higher. The inorganic filler has excellent thermal stability and will not fail before thermal runaway of the battery occurs, ensuring that the first positive electrode coating 12 effectively provides its safety function. In some embodiments, the inorganic filler may include one or more of boehmite, alumina, zirconia, silica, magnesium hydroxide, and the like. The thermal decomposition onset temperature of boehmite is approximately 350°C. The thermal decomposition onset temperature of magnesium hydroxide is approximately 340°C.

[0037] In some embodiments, the inorganic filler is boehmite. Boehmite has excellent thermal conductivity and low hardness, and is able to transfer Joule heat generated by a short circuit in the battery core as quickly as possible, thereby reducing heat concentration. In addition, boehmite has a Mohs hardness of less than 5. This low hardness virtually eliminates damage to the coating equipment when applying the suspension to form the first positive electrode coating 12, ensures the flatness of the first positive electrode coating 12, and makes it easier to attach the second positive electrode coating 13 to the first positive electrode coating 12, ultimately ensuring a high product yield during mass production.

[0038] In the present disclosure, the first positive electrode coating 12 may further include a first binder and a first conductive agent, and the second positive electrode coating 13 further includes a second binder and a second conductive agent. The presence of the binder and conductive agent in the two positive electrode coatings can ensure excellent adhesion and conductivity of the coatings. The first binder, second binder, first conductive agent, and second conductive agent may be conventional choices in the battery field. The first binder and the second binder are independently selected from one or more of polyvinylidene fluoride (PVDF), vinylidene fluoride-hexafluoropropylene copolymer, vinylidene fluoride-acrylic acid copolymer, polytetrafluoroethylene (PTFE), polyacrylic acid (PAA), polyacrylate (e.g., polymethyl methacrylate, polymethyl acrylate, polyethyl acrylate, etc.), polyvinyl alcohol (PVA), polyimide (PI), polyurethane, epoxy resin, styrene-butadiene rubber (SBR), fluororubber, sodium carboxymethyl cellulose (CMC-Na), etc. The first conductive agent and the second conductive agent are independently selected from one or more of conductive carbon black (e.g., acetylene black, Ketjen black, Super P, 350G carbon black, etc.), graphite, carbon fiber, carbon nanotubes, graphene, etc., without limitation.

[0039] In some embodiments, the weight percentage of the first binder in the first positive electrode coating 12 is greater than the weight percentage of the second binder in the second positive electrode coating 13. The binder content in the first positive electrode coating 12 is greater than the binder content in the second positive electrode coating 13, ensuring stronger adhesion between the first positive electrode coating 12 and the positive electrode current collector 11. Therefore, even if the second positive electrode coating 13 peels off in an abnormal event such as when the battery is crushed, impacted, or pierced by a nail, the first positive electrode coating 12 will not peel off from the surface of the positive electrode current collector 11, thereby preventing the positive electrode current collector 11 from contacting the negative electrode active material layer, increasing resistance to short circuits, reducing the risk of thermal runaway in the battery core, and further improving the safety performance of the battery.

[0040] Additionally, if the weight percentage of the first positive electrode active material in first positive electrode coating 12 is the same as the weight percentage of the second positive electrode active material in second positive electrode coating 13, provided that the weight percentage of the binder in first positive electrode coating 12 is greater than the weight percentage of the binder in second positive electrode coating 13, the weight percentage of the first conductive agent in first positive electrode coating 12 is less than the weight percentage of the second conductive agent in second positive electrode coating 13. In this manner, first positive electrode coating 12, having a slightly lower electrical conductivity, can better cover and passivate positive electrode current collector 11 and reduce contact between positive electrode current collector 11 and the battery's negative electrode if the battery is handled roughly.

[0041] In an embodiment of the present disclosure, the weight percentage of the first binder in the first positive electrode coating 12 is 5% to 10%, such as 5%, 6%, 7%, 8%, 9%, 9.5%, etc. The weight percentage of the first binder not only ensures an excellent bonding effect, but also allows the content of the first positive electrode active material in the first positive electrode coating 12 to be appropriate, which can further improve the energy density of the battery.

[0042] In an embodiment of the present disclosure, the weight percentage of the first conductive agent in the first positive electrode coating 12 is 1% to 3%, which ensures appropriate electrical conductivity of the first positive electrode coating 12, improves the low-temperature performance, rate performance, and cycle performance of the battery, and also increases the short-circuit internal resistance value, further improving the safety of the battery.

[0043] In some embodiments of the present disclosure, the first positive electrode coating 12 may include the following components in weight percentages: 50% to 85% first positive electrode active material, 10% to 40% inorganic filler, 5% to 10% first binder, and 1% to 3% first conductive agent.

[0044] The second positive electrode coating 13 of the present disclosure corresponds to the positive electrode active material layer of a conventional battery. In a conventional battery, no safety coating is provided between the positive electrode active material layer and the positive electrode current collector 11. Therefore, the second positive electrode coating 13 is a conventional component in the battery field and primarily performs the function of contributing to energy.

[0045] In some embodiments of the present disclosure, second positive electrode coating 13 may include the following components in weight percentages: 90% to 99% second positive electrode active material, 0.5% to 1.5% second binder, and 0.5% to 1.5% second conductive agent.

[0046] In the present disclosure, the first and second positive electrode active materials may be the same or different materials and may be independently selected from one or more of lithium iron phosphate, lithium manganese iron phosphate, lithium vanadium phosphate, lithium vanadyl phosphate, lithium vanadium fluorophosphate, lithium cobalt oxide, lithium manganate, lithium nickel oxide, lithium vanadate, lithium titanate, lithium nickel manganese oxide, lithium nickel cobalt oxide, lithium nickel cobalt manganate, lithium nickel cobalt aluminum oxide, lithium manganese-based materials, etc. These positive electrode active materials may be undoped or modified by doping, and may or may not have a cladding layer on their surface. Generally, phosphate-based active materials generally have a coating layer.

[0047] To ensure excellent battery safety, in embodiments of the present disclosure, the structural stability of the first positive electrode active material is higher than that of the second positive electrode active material. In this case, the first positive electrode active material and the second positive electrode active material are different materials. In some embodiments, the first positive electrode active material is a phosphate-based active material, and the second positive electrode active material is a layered transition metal oxide. The first positive electrode active material may specifically include one or more of lithium iron phosphate, lithium manganese iron phosphate, lithium vanadium phosphate, lithium vanadyl phosphate, lithium vanadium fluorophosphate, etc. The second positive electrode active material may include one or more of lithium cobalt oxide, lithium manganese oxide, lithium nickel oxide, lithium vanadate, lithium titanate, lithium nickel manganese oxide, lithium nickel cobalt oxide, lithium nickel cobalt manganese oxide, lithium nickel cobalt aluminum oxide, lithium-rich manganese-based materials, etc. The second positive electrode active material, in some embodiments, is lithium cobalt oxide, which has a high operating voltage and a large specific capacity.

[0048] In an embodiment of the present disclosure, the median particle diameter (D 3 vThe particle size (or particle diameter) of the second positive electrode active material (may be defined as "50") is in the range of 6 μm to 18 μm. In this case, the median particle size of the second positive electrode active material is large, which allows the specific surface area of the second positive electrode active material to be controlled within an appropriate range, thereby achieving high structural stability and facilitating lithium ion conduction. In some embodiments, the median particle size of the second positive electrode active material is in the range of 14 μm to 16 μm.

[0049] The positive electrode 10 may be fabricated by the following method: a first positive electrode suspension containing a first positive electrode active material, an inorganic filler, a first binder, and a first conductive agent is applied to at least one surface of a positive electrode current collector 11 and dried to form a first positive electrode coating 12, and then a second positive electrode suspension containing a second positive electrode active material, a second binder, and a second conductive agent is applied to the same and dried to form a second positive electrode coating 13, which is then pressed to obtain a positive electrode.

[0050] One or both surfaces of the positive electrode current collector may be coated. In other words, the laminate structure including the first and second positive electrode coatings may be formed on one surface of the positive electrode current collector, or may be formed on both surfaces of the positive electrode current collector. When both surfaces of the positive electrode current collector are coated, only the first positive electrode coating on one surface needs to satisfy the requirement that the parameter n is within the above range.

[0051] 2, an embodiment of the present disclosure further provides a secondary battery 100. The secondary battery 100 includes the above-described positive electrode 10. Because the secondary battery 100 includes the above-described positive electrode 10, the secondary battery 100 has excellent safety performance and high energy density.

[0052] The secondary battery may be a liquid battery using a liquid electrolyte, or a semi-solid or all-solid battery using a semi-solid or solid electrolyte. Specific examples of the secondary battery include a lithium secondary battery, a sodium secondary battery, a potassium secondary battery, a magnesium secondary battery, an aluminum secondary battery, and a zinc secondary battery.

[0053] In some embodiments, the secondary battery may include the above-described positive electrode, negative electrode, and semi-solid or solid electrolyte between the positive electrode and the negative electrode. In addition, when a semi-solid or solid electrolyte is used, the positive electrode and negative electrode may further include a semi-solid or solid electrolyte material.

[0054] In some other embodiments, the secondary battery may include the positive electrode, negative electrode, and separator described above, and an electrolyte between the positive electrode and the negative electrode. The secondary battery may be assembled by the following method: stacking the positive electrode, separator, and negative electrode in order to form a battery core, placing the battery core in a battery housing, injecting the electrolyte, and then sealing the battery housing to obtain a secondary battery.

[0055] The negative electrode includes a negative electrode current collector and a negative electrode active material layer disposed on the surface of the negative electrode current collector. The negative electrode current collector may include, but is not limited to, copper foil, copper alloy foil, carbon-coated copper foil, copper-plated thin film, etc. The negative electrode active material in the negative electrode active material layer may include, but is not limited to, one or more of a carbon material, a silicon-based material, a tin-based material, or lithium titanate. The carbon material may include, but is not limited to, one or more of soft carbon, hard carbon, carbon fiber, graphitized carbon microbeads, artificial graphite, or natural graphite. The silicon-based material may include, but is not limited to, one or more of elemental silicon, a silicon alloy, a silicon oxide, a silicon-carbon composite, etc. The tin-based material may include, but is not limited to, one or more of elemental tin, tin oxide, a tin-based alloy, a tin-carbon compound, etc.

[0056] The separator is generally a porous substrate through which the active ions pass. The separator may have a single-layer structure or a multi-layer structure. The separator may include, but is not limited to, a polymer separator such as a single-layer PP membrane, a single-layer polyethylene (PE) membrane, a two-layer PP / PE membrane, a two-layer PP / PP membrane, or a three-layer PP / PE / PP membrane, a nonwoven fabric, etc. The electrolyte generally contains an electrolyte salt (e.g., a lithium salt) containing the active ions, a solvent (e.g., an organic solvent), optional additives, etc. The organic solvent may include, but is not limited to, one or more of ethylene carbonate, propylene carbonate, dimethyl carbonate, ethyl methyl carbonate, propyl propionate, ethyl propionate, ethyl acetate, etc.

[0057] 3 , an embodiment of the present disclosure further provides an electric device 1000. The electric device 1000 includes a secondary battery 100 according to an embodiment of the present disclosure. The electric device 1000 may be a vehicle such as an automobile (e.g., an electric vehicle) or a boat, or may be a 3C product (e.g., a mobile phone, a tablet computer, or a smart band).

[0058] The technical solutions of the present disclosure are further illustrated below through several examples. [Example]

[0059] The positive electrode was fabricated by the following steps.

[0060] (1) A first positive electrode active material (specifically, a D 1 v 50), inorganic filler (specifically, D 2 vA first positive electrode suspension was obtained by mixing a binder (specifically, boehmite having thermal decomposition starting temperatures of 50°C and 350°C), a binder (specifically, PVDF), and a conductive agent (specifically, conductive carbon black) in a mass ratio of 57:30:10:3 in a solvent, N-methylpyrrolidone (NMP) (here, the parameter M was 1.9). The mixture was stirred uniformly to obtain a first positive electrode suspension.

[0061] The second positive electrode active material (specifically, D 3 v 50), a binder (specifically, PVDF), and a conductive agent (specifically, conductive carbon black) were mixed in a mass ratio of 98:1:1 in a solvent NMP and stirred uniformly to obtain a second positive electrode suspension.

[0062] (2) The first positive electrode suspension was applied to one surface of an aluminum foil and dried to form a first positive electrode coating with a thickness T of 5 μm. Then, the second positive electrode suspension was applied to the first positive electrode coating and dried to form a second positive electrode coating with a thickness of 47 μm. Next, the first positive electrode coating and the second positive electrode coating were similarly applied to the other surface of the aluminum foil, sequentially, to obtain a double-sided electrode. Finally, the double-sided electrode was rolled to obtain the positive electrode for later use.

[0063] The lithium secondary battery was created through the following steps:

[0064] 1) Preparation of the negative electrode: The negative electrode active material (specifically, artificial graphite), conductive carbon black, SBR, and carboxymethyl cellulose (CMC) were dispersed in deionized water in a mass ratio of 97:1:1:1 and stirred uniformly to obtain a negative electrode suspension. The negative electrode suspension was then applied to both surfaces of copper foil, dried, and rolled to obtain a negative electrode.

[0065] 2) Battery assembly: The positive electrode, separator, and negative electrode of the example were stacked in order and wound to form a battery core. The battery core was packaged in an aluminum plastic film case. Then, an electrolyte was injected into the battery case. After formation, venting, secondary packaging, and capacity grading, a lithium-ion battery was obtained. The lithium-ion battery had a capacity of 4500 mAh, a 2C charging system with a charge cutoff voltage of 4.45 V.

[0066] Other Examples Based on the parameters in Table 1 below, positive electrodes and secondary batteries of other examples were fabricated using the method for fabricating positive electrodes and secondary batteries described in Example 1. The calculation results for the parameter n defined above are also summarized in Table 1.

[0067] Comparative Example 1 Comparative Example 1 differs from Example 1 in that the first positive electrode coating does not include an inorganic filler that is not electrochemically active.

[0068] Comparative Example 2 Comparative Example 2 differs from Example 1 in that the positive electrode does not include a first positive electrode coating.

[0069] [Table 1]

[0070] To highlight the beneficial effects of the technical solutions of the present disclosure, the following performance tests were also carried out on the lithium-ion battery, and the results are also summarized in Table 1 above.

[0071] (1) Internal resistance test Each lithium-ion battery was placed in a room temperature environment (23°C to 25°C) and charged at a constant current of 0.2 C to 3.95 V, and then charged at a constant voltage of 3.95 V to a cutoff current of 0.01 C. The internal resistance of the battery core was then tested using a 1 kHz alternating-current (AC) internal resistance meter. Ten batteries were tested for each example and comparative example, and the test results were averaged. The internal resistance increase rate of the batteries in the example and other comparative examples was calculated using the internal resistance value of the battery in Comparative Example 2 (approximately 25 mΩ) as the standard. A battery with an internal resistance increase rate of 30% or less was considered to have passed the internal resistance test.

[0072] (2) Nail penetration test Each lithium-ion battery was placed in a room temperature environment (23°C to 25°C) and charged at a constant current of 0.2 C to 4.45 V, and then charged at a constant voltage of 4.45 V to a cutoff current of 0.025 C. The lithium-ion battery was then mounted in a needle penetration test device at an ambient temperature of 23°C to 25°C and humidity of 40% to 60%. The center of the lithium-ion battery was pierced at a constant speed of 50 mm / s using a 3 mm diameter steel needle. The steel needle was left in the battery for 10 minutes and then withdrawn, and the battery was observed for ignition or explosion. Ten batteries were tested for each example and comparative example. The number of batteries that did not ignite or explode was recorded to obtain the nail penetration test pass rate. A 100% pass rate was considered to have passed the nail penetration test.

[0073] According to Table 1, when a positive electrode according to an embodiment of the present disclosure is constructed such that the particle packing parameter n of the first positive electrode coating is in the range of 4 to 7, and the average particle sizes of the first and second positive electrode active materials are in the ranges of 0.6 μm to 1.2 μm and 0.6 μm to 1.5 μm, respectively, a lithium-ion battery fabricated using the positive electrode passed a nail penetration test, demonstrating excellent safety performance of the lithium-ion battery. In addition, the internal resistance increase rate of the lithium-ion battery according to the embodiment of the present disclosure was 30% or less lower than that of the battery of Comparative Example 2, which did not include a safety coating, which was advantageous in ensuring excellent cycle performance of the battery.

[0074] Comparing Example 1 and Comparative Example 2, it can be seen that the positive electrode current collector is protected by the first positive electrode coating, and when the battery is pierced with a steel needle, the positive electrode current collector does not come into direct contact with the negative electrode active material, thereby significantly reducing the risk of thermal runaway in the lithium-ion battery. Comparing Example 1 and Comparative Example 1, it can be seen that the safety of the battery can be further improved when an inorganic filler with high thermal stability is added to the first positive electrode coating.

[0075] Comparing Examples 1 and 2 with Comparative Examples 3 to 6, when the median particle diameters of the first positive electrode active material particles and inorganic filler particles remained unchanged, if the thickness T of the first positive electrode coating was set to a value less than 4 (as in Comparative Examples 5 and 6), the nail penetration test pass rate of the battery decreased, indicating that the first positive electrode coating did not effectively provide safety protection. If n exceeded 7 (as in Comparative Examples 3 and 4), the increase in the battery's internal resistance was too large, exceeding 30% compared to Comparative Example 2, which did not include a first positive electrode coating. If the number n of particle packed layers was greater than 4 but less than 7 (as in Examples 1 and 2), safety was ensured while ensuring that the battery's internal resistance did not increase excessively.

[0076] Comparing Examples 1 and 3 to 4 with Comparative Examples 7 to 9, the median particle diameter D of the first positive electrode active material (i.e., lithium iron phosphate)1 v 50 and the thickness T of the first positive electrode coating are kept constant, the median particle diameter D of the inorganic filler that is not electrochemically active 2 v It can be seen that 50 did not have a significant impact on battery safety but had a significant impact on the battery's internal resistance. In Comparative Examples 7 and 8, the median particle size of the inorganic filler was too small, resulting in a particle packing layer number n greater than 7, and the increase in the battery's internal resistance exceeded 30%. In Comparative Example 9, the median particle size of the inorganic filler was too large, resulting in a correspondingly large increase in the battery's internal resistance. This is primarily because inorganic fillers are electronic and ionic insulators, and excessively large particle sizes of the inorganic filler may have caused localized blockages of electronic and ionic pathways within the first positive electrode coating, resulting in a significant increase in the battery's internal resistance. When the median particle size of the inorganic filler was in the range of 0.8 μm to 1.5 μm, an appropriate number of packing layers could be achieved, and the increase in the battery's internal resistance could be controlled within a small range.

[0077] Comparing Example 1, Examples 5 and 6, and Comparative Examples 10 to 13, the thickness T of the first positive electrode coating and the median particle diameter D of the inorganic filler 2 v It can be seen that when 50 was kept unchanged, the median particle size of the first positive electrode active material (i.e., lithium iron phosphate) had a significant impact on the safety performance and internal resistance of the battery. When the median particle size of the lithium iron phosphate was too small (e.g., as in Comparative Examples 10 and 11), the number of particle packing layers n in the first positive electrode coating was too large, resulting in denser packing of the small particles and an excessively high increase in the internal resistance of the battery. When the median particle size of the lithium iron phosphate was too large (e.g., as in Comparative Examples 12 and 13), the increase in the internal resistance of the battery was very small, but the nail penetration test pass rate was significantly reduced. This may be due to the fact that an excessively large particle size led to an excessively small value of n, which prevented the first positive electrode coating from providing effective protection.

[0078] The above embodiments merely illustrate some exemplary implementations of the present disclosure, and the descriptions are specific and particular, but should not be construed as limiting the scope of the present disclosure. It should be noted that those skilled in the art can make some modifications and improvements without departing from the concept of the present disclosure, and all of them are deemed to be included in the protection scope of the present disclosure. Therefore, the protection scope of the present disclosure is defined by the appended claims.

Claims

1. A positive electrode current collector (11), a first positive electrode coating (12) laminated on at least one surface of the positive electrode current collector (11) and comprising a first positive electrode active material and an inorganic filler that is not electrochemically active; a second positive electrode coating (13) laminated on a surface of the first positive electrode coating (12) facing away from the positive electrode current collector (11), the second positive electrode coating (13) comprising a second positive electrode active material; Equipped with The number n of particle-filled layers in the first positive electrode coating (12) satisfies the following relationship: n=T×(M+1) / (M×D １ ｖ 50+D ２ ｖ 50), n is in the range of 4 to 7, T represents the thickness of the first cathode coating (12) measured in μm, M represents the mass ratio of the first cathode active material to the inorganic filler, and D １ ｖ 50 represents the median particle diameter of the first positive electrode active material measured in μm, and D ２ ｖ D 50 represents the median particle size of the inorganic filler measured in μm, １ ｖ 50 is in the range of 0.6 μm to 1.2 μm, and D ２ ｖ 50 is in the range of 0.6 μm to 1.5 μm.

2. D １ ｖ 50 is in the range of 0.6 μm to 0.9 μm.

3. 3. The positive electrode (10) of claim 1 or 2, wherein T is in the range of 2 μm to 10 μm.

4. 4. The positive electrode (10) of claim 3, wherein T is in the range of 4 μm to 7 μm.

5. The positive electrode (10) of any one of claims 1 to 4, wherein M is in the range of 1 to 5.

6. The positive electrode (10) according to any one of claims 1 to 5, wherein the inorganic filler has a thermal decomposition temperature of 300°C or higher.

7. 7. The positive electrode (10) of any one of claims 1 to 6, wherein the inorganic filler comprises one or more of boehmite, alumina, zirconia, silica, or magnesium hydroxide.

8. 8. The cathode (10) of any one of claims 1 to 7, wherein the first active cathode material comprises one or more of lithium iron phosphate, lithium manganese iron phosphate, lithium vanadium phosphate, lithium vanadyl phosphate, or lithium vanadium fluorophosphate, and the second active cathode material comprises one or more of lithium cobalt oxide, lithium manganese oxide, lithium nickel oxide, lithium vanadate, lithium titanate, lithium nickel manganese oxide, lithium nickel cobalt oxide, lithium nickel cobalt manganese oxide, lithium nickel cobalt aluminum oxide, or a lithium-rich manganese-based material.

9. The cathode (10) of any one of claims 1 to 8, wherein the second cathode active material has a median particle size in the range of 6 μm to 18 μm.

10. 10. The cathode (10) of any one of claims 1 to 9, wherein the first cathode coating (12) further comprises a first binder and a first conductive agent, and the second cathode coating (13) further comprises a second binder and a second conductive agent.

11. 11. The cathode (10) of claim 10, wherein a weight percentage of the first binder in the first cathode coating (12) is greater than a weight percentage of the second binder in the second cathode coating (13).

12. 12. The cathode (10) of claim 10 or 11, wherein a weight percentage of the first binder in the first cathode coating (12) ranges from 5% to 10% and a weight percentage of the first conductive agent in the first cathode coating (12) ranges from 1% to 3%.

13. 13. The cathode (10) of any one of claims 10 to 12, wherein the first binder and the second binder independently comprise one or more of polyvinylidene fluoride (PVDF), vinylidene fluoride-hexafluoropropylene copolymer, vinylidene fluoride-acrylic acid copolymer, polytetrafluoroethylene (PTFE), polyacrylic acid (PAA), polyacrylate, polyvinyl alcohol (PVA), polyimide (PI), polyurethane, epoxy resin, styrene-butadiene rubber (SBR), fluororubber, or sodium carboxymethyl cellulose (CMC-Na).

14. 14. The positive electrode (10) of any one of claims 10 to 13, wherein the first conductive agent and the second conductive agent independently comprise one or more of conductive carbon black, graphite, carbon fiber, carbon nanotubes, or graphene.

15. 15. The cathode (10) of any one of claims 10 to 14, wherein the first cathode coating (12) comprises the following components in weight percentages: 50% to 85% of the first cathode active material, 10% to 40% of the inorganic filler, 5% to 10% of the first binder, and 1% to 3% of the first conductive agent.

16. 16. The cathode (10) of any one of claims 10 to 15, wherein the second cathode coating (13) comprises the following components in weight percentages: 90% to 99% of the second cathode active material, 0.5% to 1.5% of the second binder, and 0.5% to 1.5% of the second conductive agent.

17. A secondary battery (100) comprising the positive electrode (10) according to any one of claims 1 to 16.

18. An electric device (1000) comprising the secondary battery (100) of claim 17.