Curable resin composition

Abstract

To provide a curable resin composition capable of achieving both dielectric characteristics and melt viscosity.SOLUTION: The curable resin composition according to the embodiment contains a linear copolymer (A) having a repeating unit corresponding to a monovinyl aromatic compound and a repeating unit corresponding to a divinyl aromatic compound, and a copolymer (B) that is a copolymer containing a styrene-based monomer and an aliphatic diene monomer having 4 to 7 carbon atoms as constituent monomers and / or a hydrogenated product thereof and has a number average molecular weight of 50000 or less. In the copolymer (A), the content of the repeating unit corresponding to the divinyl aromatic compound in 100 mol% of all the repeating units is less than 40 mol%. The amount of the copolymer (B) is 80 parts by mass or less based on 100 parts by mass of the total of the copolymer (A) and the copolymer (B).SELECTED DRAWING: None

Description

[Technical Field]

[0001] SUMMARY OF THE INVENTION An embodiment of the present invention relates to a curable resin composition. [Background technology]

[0002] In recent years, electronic devices have become smaller and more powerful, and as a result, the performance requirements for the various materials used in them have increased. For example, there is a demand for printed circuit board materials with low dielectric loss tangents that can be used for high-frequency communications.

[0003] Patent Document 1 discloses a thermosetting resin composition having excellent dielectric properties, heat resistance, adhesion, and moisture resistance, which contains a copolymer containing an acenaphthylene-based structural unit and a hydroxystyrene-based structural unit, a compound having at least two epoxy groups in one molecule, and a curing agent. Patent Document 1 discloses a copolymer of styrene, pt-butoxystyrene, divinylbenzene, and acenaphthylene as a specific example of the copolymer.

[0004] Patent Document 2 discloses a curable composition having excellent heat resistance, compatibility, dielectric properties, moist heat reliability, and resistance to thermal oxidative degradation, which contains a copolymer including a structural unit derived from a divinyl aromatic compound, a structural unit derived from a monovinyl aromatic compound, and a structural unit derived from a cycloolefin compound.

[0005] Patent Document 3 discloses a thermosetting resin composition having a high glass transition temperature, low water absorption, and excellent dielectric properties and moisture and heat resistance, which contains a polyfunctional vinyl aromatic copolymer having structural units derived from a divinyl aromatic compound and an ethylvinyl aromatic compound, and an olefin resin having a styrene structure and a butadiene structure. [Prior art documents] [Patent documents]

[0006] [Patent Document 1] Japanese Patent Application Laid-Open No. 2001-192539 [Patent Document 2] Japanese Patent Application Publication No. 2018-039995 [Patent Document 3] Special Publication No. 2020-515701 Summary of the Invention [Problem to be solved by the invention]

[0007] Conventional curable resin compositions are not necessarily satisfactory in terms of dielectric properties, and even those with excellent dielectric properties have problems such as high melt viscosity and poor processability, so it is necessary to achieve both good dielectric properties and good melt viscosity.

[0008] The polyfunctional vinyl aromatic copolymer described in Patent Document 3 is obtained by polymerizing a divinyl aromatic compound and an ethylvinyl aromatic compound as raw material monomers, and therefore, the divinyl aromatic compound inevitably forms branches, making it not a linear copolymer. Furthermore, since the content of structural units derived from the divinyl aromatic compound is high, the effects of improving the melt viscosity and dielectric properties are not necessarily sufficient.

[0009] In view of the above, an object of an embodiment of the present invention is to provide a curable resin composition that can achieve both dielectric properties and melt viscosity. [Means for solving the problem]

[0010] The present invention includes the embodiments shown below. [1] A curable resin composition comprising: a linear copolymer (A) having a repeating unit corresponding to a monovinyl aromatic compound and a repeating unit corresponding to a divinylaromatic compound, wherein the content of the repeating units corresponding to the divinylaromatic compound in 100 mol% of all repeating units is less than 40 mol%; and a copolymer (B) containing a styrene-based monomer and an aliphatic diene monomer having 4 to 7 carbon atoms as constituent monomers and / or a hydrogenated product thereof, the copolymer having a number average molecular weight of 50,000 or less, wherein the amount of the copolymer (B) is 80 parts by mass or less per 100 parts by mass of the total of the copolymer (A) and the copolymer (B).

[0011] [2] The curable resin composition according to [1], wherein the copolymer (B) contains a copolymer of a styrene-based monomer and butadiene and / or a hydrogenated product thereof. [3] The curable resin composition according to [1] or [2], wherein the content of repeating units corresponding to the divinyl aromatic compound is less than 20 mol% in 100 mol% of all repeating units of the copolymer (A). [4] The curable resin composition according to any one of [1] to [3], wherein the copolymer (A) further has a repeating unit corresponding to an aromatic ring-fused cyclic olefin compound having three rings. [5] The curable resin composition according to any one of [1] to [4], wherein the content of repeating units corresponding to the monovinyl aromatic compound is 50 mol % or more in 100 mol % of all repeating units of the copolymer (A). [6] The curable resin composition according to any one of [1] to [5], which is a printed circuit board material. [7] Use of the curable resin composition according to any one of [1] to [5] as a printed circuit board material. [Effects of the Invention]

[0012] The curable resin composition according to an embodiment of the present invention can achieve both dielectric properties and melt viscosity. DETAILED DESCRIPTION OF THE INVENTION

[0013] The curable resin composition according to the present embodiment includes (a) a linear copolymer (A) having a repeating unit corresponding to a monovinyl aromatic compound and (b) a repeating unit corresponding to a divinyl aromatic compound, and (B) a copolymer (B) containing, as constituent monomers, a styrene-based monomer and an aliphatic diene monomer having 4 to 7 carbon atoms.

[0014] The copolymer (A) has (a) a repeating unit corresponding to a monovinyl aromatic compound and (b) a repeating unit corresponding to a divinyl aromatic compound, and in one embodiment, may further have (c) a repeating unit corresponding to an aromatic ring-fused cyclic olefin compound.

[0015] The repeating unit corresponding to the monovinyl aromatic compound (a) above (hereinafter also referred to as "monovinyl aromatic compound unit") is a constituent unit of the copolymer (A) and has a structure formed by addition polymerization of a monovinyl aromatic compound as a monomer. That is, the (a) monovinyl aromatic compound unit is a repeating unit having a structure in which the vinyl group of the monovinyl aromatic compound becomes a single bond through addition polymerization. The (a) monovinyl aromatic compound unit is not necessarily limited to one obtained by polymerization using the monovinyl aromatic compound, as long as it has a structure corresponding to the monovinyl aromatic compound, and may also be one that has a structure corresponding to the monovinyl aromatic compound by further reaction after polymerization.

[0016] As the (a) monovinyl aromatic compound unit, a repeating unit represented by the following general formula (1) is preferred. [ka]

[0017] In formula (1), R 1 represents a monovalent aromatic hydrocarbon group having 6 to 30 carbon atoms and therefore does not contain a heteroatom. 1is preferably a monovalent aromatic hydrocarbon group having 6 to 30 carbon atoms (more preferably 6 to 20 carbon atoms) selected from the group consisting of a phenyl group which may have a hydrocarbon group as a substituent, a biphenylyl group which may have a hydrocarbon group as a substituent, a naphthyl group which may have a hydrocarbon group as a substituent, and a terphenylyl group which may have a hydrocarbon group as a substituent. 1 If the group has a substituent such as an alkyl group, the number of carbon atoms in the group is the number of carbon atoms in the group including the number of carbon atoms in the substituent. 1 The total number of carbon atoms.

[0018] The monovinyl aromatic compound forming such a repeating unit may be any aromatic compound having one vinyl group, and examples thereof include vinyl aromatic compounds such as styrene, vinylnaphthalene, and vinylbiphenyl, and nuclear alkyl-substituted vinyl aromatic compounds such as alkylstyrenes (e.g., o-methylstyrene, m-methylstyrene, p-methylstyrene, o-ethylstyrene, m-ethylstyrene, p-ethylstyrene, and 4-tert-butylstyrene), dialkylstyrenes (e.g., 3,5-dimethylstyrene, 2,5-dimethylstyrene, and 2,5-diethylstyrene), alkylvinylbiphenyls (e.g., ethylvinylbiphenyl), and alkylvinylnaphthalenes (e.g., ethylvinylnaphthalene), and any of these may be used alone or in combination of two or more.

[0019] In one embodiment, the monovinyl aromatic compound preferably contains at least one (a1) selected from the group consisting of styrene, vinylnaphthalene, vinylbiphenyl, alkylstyrene, dialkylstyrene, alkylvinylbiphenyl, and alkylvinylnaphthalene. More preferably, the monovinyl aromatic compound contains styrene. That is, the (a) monovinyl aromatic compound unit preferably contains a repeating unit corresponding to the (a1) (hereinafter also referred to as "(a1) unit"), more preferably a repeating unit corresponding to styrene (hereinafter also referred to as "styrene unit").

[0020] The amount of repeating units of the above formula (1) (preferably (a1) units, more preferably styrene units) in 100 mol% of (a) monovinyl aromatic compound units is preferably 70 mol% or more, more preferably 80 mol% or more, even more preferably 90 mol% or more, and may be 100 mol%.

[0021] The repeating unit corresponding to the above (b) divinylaromatic compound (hereinafter also referred to as "divinylaromatic compound unit") is a constituent unit of the copolymer (A) and is a constituent unit having a structure containing one vinyl group, formed by addition polymerization of a divinylaromatic compound as a monomer. That is, the (b) divinylaromatic compound unit is a repeating unit having a structure in which one vinyl group of the divinylaromatic compound has become a single bond through addition polymerization, and also having one vinyl group. The (b) divinylaromatic compound unit is not necessarily limited to one obtained by polymerization using the divinylaromatic compound, as long as it has a structure corresponding to the divinylaromatic compound, and may also be one that has been further reacted after polymerization to form a structure corresponding to the divinylaromatic compound.

[0022] The (b) divinyl aromatic compound unit is preferably a repeating unit represented by the following general formula (2). [ka]

[0023] In formula (2), R 2 represents a divalent aromatic hydrocarbon group having 6 to 30 carbon atoms and therefore does not contain heteroatoms. 2 is preferably a divalent aromatic hydrocarbon group having 6 to 30 carbon atoms (more preferably 6 to 20 carbon atoms) selected from the group consisting of a phenylene group which may have a hydrocarbon group as a substituent, a biphenyldiyl group which may have a hydrocarbon group as a substituent, a naphthylene group which may have a hydrocarbon group as a substituent, and a terphenyldiyl group which may have a hydrocarbon group as a substituent. 2If the group has a substituent such as an alkyl group, the number of carbon atoms in the group is the number of carbon atoms in the group including the number of carbon atoms in the substituent. 2 The total number of carbon atoms.

[0024] The divinyl aromatic compound may be any aromatic compound having two vinyl groups, such as divinylbenzene (including each positional isomer or a mixture thereof), divinylnaphthalene (including each positional isomer or a mixture thereof), and divinylbiphenyl (including each positional isomer or a mixture thereof), and these may be used alone or in combination of two or more.

[0025] In one embodiment, the divinylaromatic compound preferably contains at least one (b1) selected from the group consisting of divinylbenzene, divinylnaphthalene, and divinylbiphenyl. More preferably, the divinylaromatic compound contains divinylbenzene (m-isomer, p-isomer, or a positional isomer mixture thereof). That is, the (b) divinylaromatic compound unit preferably contains a repeating unit corresponding to the (b1) (hereinafter also referred to as a "(b1) unit"), more preferably a repeating unit corresponding to divinylbenzene (hereinafter also referred to as a "divinylbenzene unit").

[0026] The amount of repeating units of the above formula (2) (preferably (b1) units, more preferably divinylbenzene units) in 100 mol% of (b) divinyl aromatic compound units is preferably 70 mol% or more, more preferably 80 mol% or more, even more preferably 90 mol% or more, and may be 100 mol%.

[0027] The repeating unit corresponding to the aromatic ring-fused cyclic olefin compound (c) (hereinafter also referred to as "cyclic olefin unit") is a constituent unit of the copolymer (A) and has a structure formed by addition polymerization of an aromatic ring-fused cyclic olefin compound as a monomer. That is, the (c) cyclic olefin unit is a repeating unit having a structure in which the double bond of the cyclic olefin of the aromatic ring-fused cyclic olefin compound has become a single bond through addition polymerization. The (c) cyclic olefin unit is not necessarily limited to one obtained by polymerization using the aromatic ring-fused cyclic olefin compound, as long as it has a structure corresponding to the aromatic ring-fused cyclic olefin compound, and may also be one that has been further reacted after polymerization to form a structure corresponding to the aromatic ring-fused cyclic olefin compound.

[0028] The aromatic ring-fused cyclic olefin compound is a cyclic olefin compound in which an aromatic ring is fused, and more specifically, a compound having a fused ring of an aliphatic ring having a carbon-carbon double bond and an aromatic ring. The condensation may be ortho-condensation or ortho-peri-condensation. Examples of the aromatic ring-fused cyclic olefin compound include indene-based compounds, acenaphthylene-based compounds, phenalene-based compounds, acephenanthrylene-based compounds, aceanthrylene-based compounds, benzofuran-based compounds, and benzothiophene-based compounds, and these can be used alone or in combination.

[0029] Among these, aromatic ring-fused cyclic olefin compounds are preferably those having three or less rings. Specifically, those having two rings are preferably indene-based compounds, benzofuran-based compounds, and benzothiophene-based compounds; and those having three rings are preferably acenaphthylene-based compounds and phenalene-based compounds, more preferably indene-based compounds and / or acenaphthylene-based compounds. Furthermore, from the viewpoint of increasing the glass transition temperature of the cured product, it is preferable to use an aromatic ring-fused cyclic compound having three rings.

[0030] In one embodiment, the aromatic ring-fused cyclic olefin compound preferably contains at least one (c1) selected from the group consisting of indene-based compounds, acenaphthylene-based compounds, phenalene-based compounds, acephenanthrylene-based compounds, aceanthrylene-based compounds, benzofuran-based compounds, and benzothiophene-based compounds. In this case, the amount of repeating units corresponding to the at least one (c1) in 100 mol% of (c) cyclic olefin units is preferably 70 mol% or more, more preferably 80 mol% or more, even more preferably 90 mol% or more, and may be 100 mol%.

[0031] The indene-based compound may be, for example, at least one selected from the group consisting of indene, alkylindene, halogenated indene, arylindene, and alkoxyindene.

[0032] The acenaphthylene-based compound may be, for example, at least one selected from the group consisting of acenaphthylene, alkylacenaphthylene, halogenated acenaphthylene, arylacenaphthylene, and alkoxyacenaphthylene.

[0033] The phenalene-based compounds, acephenanthrylene-based compounds, aceanthrylene-based compounds, benzofuran-based compounds, and benzothiophene-based compounds include phenalene, acephenanthrylene, aceanthrylene, benzofuran, and benzothiophene, as well as compounds having the same substituents as the above-mentioned indene-based compounds.

[0034] In one embodiment, the (c) cyclic olefin unit is preferably a repeating unit represented by the following general formula (3). [ka]

[0035] In formula (3), R 3 and R 4each independently represents a monovalent saturated hydrocarbon group having 1 to 20 carbon atoms, a halogen atom, a monovalent aromatic hydrocarbon group having 6 to 20 carbon atoms, or an alkoxy group having 1 to 20 carbon atoms. Here, the monovalent saturated hydrocarbon group may be a linear or branched alkyl group or a cycloalkyl group, and is preferably an alkyl group. The monovalent aromatic hydrocarbon group may be an aryl group or an aralkyl group, and is preferably an aryl group. The monovalent saturated hydrocarbon group preferably has 1 to 10 carbon atoms, and more preferably has 1 to 5 carbon atoms. The monovalent aromatic hydrocarbon group preferably has 6 to 10 carbon atoms. The alkoxy group preferably has 1 to 10 carbon atoms, and more preferably has 1 to 5 carbon atoms.

[0036] In formula (3), m and n each independently represent an integer of 0 to 3. When m and n are 2 or more, R 3 and R 4 may be the same or different.

[0037] The aromatic ring-fused cyclic olefin compound forming the repeating unit of formula (3) is an acenaphthylene-based compound represented by the following general formula (4). [ka] R in equation (4) 3 , R 4 , m and n are R in formula (3). 3 , R 4 , m and n.

[0038] In one embodiment, the aromatic ring-fused cyclic olefin compound preferably contains an acenaphthylene-based compound represented by the above formula (4), more preferably contains acenaphthylene. That is, the (c) cyclic olefin unit preferably contains a repeating unit of formula (3), more preferably contains a repeating unit corresponding to acenaphthylene (hereinafter also referred to as "acenaphthylene unit").

[0039] (c) The amount of repeating units (preferably repeating units of formula (3), more preferably acenaphthylene units) corresponding to an aromatic ring-fused cyclic compound having three rings in 100 mol% of cyclic olefin units is preferably 70 mol% or more, more preferably 80 mol% or more, even more preferably 90 mol% or more, and may be 100 mol%.

[0040] As described above, copolymer (A) is linear. The linear structure results in entanglement of molecular chains, improving moldability. Here, linear refers to a structure in which the repeating units constituting the copolymer are linked together in a one-dimensional chain, without any branches such as cross-linked structures.

[0041] In the copolymer (A), the (a) monovinyl aromatic compound units, (b) divinylaromatic compound units, and (c) cyclic olefin units as an optional component may be arranged in a regular or random order. The copolymer (A) is preferably a random copolymer in which the (a) monovinyl aromatic compound units, (b) divinylaromatic compound units, and (c) cyclic olefin units as an optional component are arranged randomly.

[0042] In addition to (a) monovinyl aromatic compound units, (b) divinyl aromatic compound units, and (c) cyclic olefin units, the copolymer (A) may contain repeating units corresponding to other monomers, such as trivinyl aromatic compounds, trivinyl aliphatic compounds, divinyl aliphatic compounds, and monovinyl aliphatic compounds, to the extent that the effects of the other monomers are not impaired.

[0043] In copolymer (A), the content of (b) divinylaromatic compound units is less than 40 mol% based on 100 mol% of all repeating units constituting copolymer (A). A content of less than 40 mol% reduces the melt viscosity of the curable resin composition and improves the dielectric properties of the cured product. The content of (b) divinylaromatic compound units is preferably less than 20 mol% based on 100 mol% of all repeating units. From the viewpoints of improving thermosetting properties and increasing the glass transition temperature, the lower limit of the content is preferably 3 mol%. The content is more preferably 5 to 19 mol%, and even more preferably 10 to 18 mol%.

[0044] In this specification, 100 mol % of all repeating units does not include structures derived from the polymerization initiator or the chain transfer agent present at the terminals of the copolymer.

[0045] In the copolymer (A), the content of (a) monovinyl aromatic compound units is not particularly limited, but from the viewpoint of melt viscosity, it is preferably 50 mol % or more of the total 100 mol % of repeating units constituting the copolymer (A). The content of (a) monovinyl aromatic compound units is more preferably 50 to 90 mol %, more preferably 60 to 85 mol %, and even more preferably 65 to 80 mol %.

[0046] In the copolymer (A), the content of the (c) cyclic olefin unit is not particularly limited, and may be 30 mol % or less, 3 to 25 mol %, or 5 to 20 mol % relative to 100 mol % of all repeating units constituting the copolymer (A).

[0047] In the copolymer (A), the total content of (a) monovinyl aromatic compound units and (b) divinyl aromatic compound units is preferably 70 mol % or more, more preferably 75 mol % or more, and even more preferably 80 mol % or more, based on 100 mol % of all repeating units constituting the copolymer (A).

[0048] The linear copolymer (A) may have a structure derived from a polymerization initiator at its end. Examples of the polymerization initiator include radical initiators such as azo compounds and organic peroxides. Preferably, the polymerization initiator does not contain a heteroatom in the structure derived from the polymerization initiator introduced at the end. Examples of such polymerization initiators include azo compounds in which the organic groups on both sides of the azo group (-N=N-) are hydrocarbon groups. For example, a polymerization initiator represented by the following general formula (5) is preferred. In this case, R 5 - and / or R 6 - is introduced into the end of the copolymer (A). R 5 -N=NR 6 (5)

[0049] In formula (5), R 5 and R 6 each independently represents a monovalent saturated hydrocarbon group or a monovalent aromatic hydrocarbon group, and therefore does not contain a heteroatom. Here, the monovalent saturated hydrocarbon group may be a branched or linear alkyl group or a cycloalkyl group. The monovalent aromatic hydrocarbon group may be an aryl group or an aralkyl group. The number of carbon atoms in the monovalent saturated hydrocarbon group is not particularly limited and may be, for example, 1 to 23 or 4 to 13. The number of carbon atoms in the monovalent aromatic hydrocarbon group is not particularly limited and may be, for example, 6 to 23 or 6 to 13.

[0050] The linear copolymer (A) may have a structure derived from a chain transfer agent at its terminal. The chain transfer agent is not particularly limited, but it is preferable to use α-methylstyrene dimer (i.e., 2,4-diphenyl-4-methyl-1-pentene).

[0051] Copolymer (A) is preferably substantially free of heteroatoms (i.e., atoms other than carbon and hydrogen atoms), i.e., substantially composed of hydrocarbons, because it has an excellent effect of improving dielectric properties. The heteroatom content in 100% by mass of copolymer (A) is preferably 3.0% by mass or less, more preferably 2.0% by mass or less, more preferably 1.0% by mass or less, and even more preferably contains no heteroatoms.

[0052] The weight-average molecular weight Mw of the copolymer (A) is not particularly limited and may be, for example, 1,000 to 100,000, 1,200 to 20,000, 1,300 to 10,000, 1,500 to 7,000, or 2,000 to 5,000. A weight-average molecular weight Mw of 1,000 or more can improve moldability and glass transition temperature. A weight-average molecular weight Mw of 100,000 or less can reduce melt viscosity. Here, the weight-average molecular weight Mw is the weight-average molecular weight in terms of polystyrene measured by gel permeation chromatography (GPC).

[0053] The method for producing the copolymer (A) is not particularly limited. In a preferred embodiment of the method for synthesizing a linear copolymer, a vinylbenzyl phosphonium salt, a monovinyl aromatic compound, and an optional aromatic ring-fused cyclic olefin compound are copolymerized, and the resulting copolymer is reacted with formaldehyde. However, the method is not limited to this method.

[0054] As the vinylbenzyl phosphonium salt, it is preferable to use a vinylbenzyl phosphonium halide.The phosphonium group in the vinylbenzyl phosphonium salt may be, for example, a quaternary phosphonium group such as a trialkyl phosphonium, a triaryl phosphonium, or a triaralkyl phosphonium.In addition, the halogen atom that forms a salt with the phosphonium group may be, for example, chlorine, bromine, or the like.

[0055] As the method for copolymerizing vinylbenzyl phosphonium salt with monovinyl aromatic compound, known vinyl polymerization method can be used.For example, vinylbenzyl phosphonium salt, monovinyl aromatic compound, aromatic ring fused cyclic olefin compound as optional component, polymerization initiator and chain transfer agent are charged into an organic solvent and reacted, thereby obtaining a copolymer having the repeating unit derived from vinylbenzyl phosphonium salt, the repeating unit derived from monovinyl aromatic compound, and the repeating unit derived from aromatic ring fused cyclic olefin compound as optional component, and having the structure derived from polymerization initiator and / or the structure derived from chain transfer agent at the end.

[0056] The copolymer thus obtained can be reacted with formaldehyde by the well-known Wittig reaction, in which the copolymer is treated with a base and then reacted with formaldehyde to remove the phosphonium group and introduce a vinyl group, thereby obtaining copolymer (A).

[0057] In this production method, since the vinylbenzyl phosphonium salt is monovinyl in the copolymerization step, a linear copolymer without branches can be obtained, and since a vinyl group is introduced into the repeating unit derived from the vinylbenzyl phosphonium salt after copolymerization, a linear copolymer without branches can be obtained, although it has a repeating unit corresponding to the divinyl aromatic compound.

[0058] Copolymer (B) is a copolymer containing a styrene-based monomer and an aliphatic diene monomer having 4 to 7 carbon atoms as constituent monomers and / or a hydrogenated product thereof. Therefore, the copolymer has repeating units derived from the styrene-based monomer and repeating units derived from the aliphatic diene monomer having 4 to 7 carbon atoms. The hydrogenated product of the copolymer refers to a copolymer in which, when the copolymer molecule contains carbon-carbon double bonds, at least a portion of the carbon-carbon double bonds have been hydrogenated.

[0059] In this embodiment, the copolymer (B) used has a number-average molecular weight Mn of 50,000 or less. By including such a copolymer (B) with a relatively small molecular weight, the melt viscosity of the curable resin composition can be reduced while maintaining the excellent dielectric properties provided by the copolymer (A). The number-average molecular weight Mn of the copolymer (B) is preferably 1,000 to 50,000, more preferably 2,000 to 30,000, more preferably 3,000 to 20,000, and even more preferably 5,000 to 10,000. Here, the number-average molecular weight Mn is the number-average molecular weight in terms of polystyrene measured by gel permeation chromatography (GPC).

[0060] Examples of the styrene-based monomer include styrene and derivatives thereof, such as styrene, α-methylstyrene, alkylstyrenes (e.g., o-methylstyrene, m-methylstyrene, p-methylstyrene, o-ethylstyrene, m-ethylstyrene, p-ethylstyrene, 4-tert-butylstyrene), and dialkylstyrenes (e.g., 3,5-dimethylstyrene, 2,5-dimethylstyrene, 2,5-diethylstyrene). These can be used alone or in combination of two or more. Among these, styrene is preferred as the styrene-based monomer.

[0061] As the aliphatic diene monomer having 4 to 7 carbon atoms, an aliphatic hydrocarbon having 4 to 7 carbon atoms and having two carbon-carbon double bonds in the molecule is used, and preferably an aliphatic conjugated diene monomer having 4 to 7 carbon atoms is used. Examples of the aliphatic conjugated diene monomer include isoprene, 1,3-butadiene, 2,4-dimethyl-1,3-butadiene, piperylene, 3-methyl-1,3-pentadiene, 2,4-hexadiene, 2,4-heptadiene, cyclopentadiene, and methylcyclopentadiene. These can be used alone or in combination of two or more. Among these, as the aliphatic diene monomer, a chain aliphatic conjugated diene monomer is preferred, and 1,3-butadiene is more preferred.

[0062] Copolymer (B) may contain only styrene-based monomers and aliphatic diene monomers having 4 to 7 carbon atoms as constituent monomers, or may contain other monomers. The total amount of styrene-based monomers and aliphatic diene monomers having 4 to 7 carbon atoms in 100% by mass of all constituent monomers of copolymer (B) is not particularly limited, but is preferably 80% by mass or more, and more preferably 90% by mass or more.

[0063] The copolymer (B) may be a random copolymer or a block copolymer, and is preferably a random copolymer.

[0064] In one embodiment, the copolymer (B) preferably contains (B1) a copolymer of a styrene-based monomer and butadiene and / or a hydrogenated product thereof. More preferably, the copolymer (B) contains (B2) a styrene-butadiene copolymer and / or a hydrogenated styrene-butadiene copolymer. The amount of (B1) (more preferably (B2)) in 100% by mass of the copolymer (B) is preferably 50% by mass or more, more preferably 70% by mass or more, more preferably 90% by mass or more, and even more preferably 100% by mass.

[0065] The content of styrene-based monomers in all constituent monomers of copolymer (B) is not particularly limited, but from the viewpoint of further enhancing the effect of achieving both dielectric properties and melt viscosity, it is preferably 10% by mass or more and 90% by mass or less, more preferably 15% by mass or more and 80% by mass or less, and even more preferably 20% by mass or more and 70% by mass or less.

[0066] It is preferable to use a copolymer (B) that is liquid at room temperature (23°C). This can further enhance the effect of reducing the melt viscosity. Here, being liquid at room temperature means having fluidity at 23°C.

[0067] The glass transition temperature Tg of the copolymer (B) is not particularly limited and may be, for example, from −70 to 0° C., from −65 to −5° C., or from −60 to −15° C. Here, the glass transition temperature is measured by a differential scanning calorimeter in accordance with JIS K6240:2011.

[0068] Examples of commercialized products of such copolymer (B) include, but are not limited to, "L-SBR-820," "L-SBR-841," "L-SBR-870," "L-SBR-822," and "L-SBR-841N," which are random polymers of polystyrene butadiene manufactured by Kuraray Co., Ltd.

[0069] The curable resin composition according to this embodiment contains the copolymer (A) and copolymer (B). The copolymer (A) has a vinyl group in its molecular chain, which allows crosslinking by polymerization, and a cured product can be obtained by thermal curing. Therefore, the curable resin composition according to this embodiment can be said to be a thermosetting resin composition.

[0070] The amount of copolymer (A) in the curable resin composition is not particularly limited as long as the composition has the property of being cured by heat or the like, and may be, for example, 1 to 99.9 mass % or 10 to 95 mass % relative to 100 mass % of the solid content of the curable resin composition. Here, the solid content refers to the amount excluding the organic solvent when the curable resin composition contains an organic solvent, or the amount of the entire composition when the organic solvent is not contained.

[0071] The amount of copolymer (B) in the curable resin composition is 80 parts by mass or less per 100 parts by mass of the total of copolymer (A) and copolymer (B). By keeping the amount of copolymer (B) 80 parts by mass or less, it is possible to suppress deterioration in the dielectric properties of the cured product. Since copolymer (B) has the effect of reducing the melt viscosity according to the amount even when added in small amounts, the lower limit is not particularly limited, but it may be, for example, 0.1 parts by mass or more. The amount of copolymer (B) is preferably 0.1 to 80 parts by mass, more preferably 1 to 50 parts by mass, more preferably 3 to 40 parts by mass, and more preferably 5 to 30 parts by mass per 100 parts by mass of the total of copolymer (A) and copolymer (B).

[0072] The curable resin composition may contain, in addition to the copolymer (A) and the copolymer (B), various components such as other thermosetting resins (thermosetting crosslinking agents), thermoplastic resins, fillers, flame retardants, curing accelerators, polymerization initiators, chain transfer agents, antifoaming agents, heat stabilizers, antistatic agents, ultraviolet absorbers, colorants such as dyes and pigments, lubricants, and dispersants.

[0073] The curable resin composition may contain an organic solvent to adjust its viscosity, and the curable resin composition may be a solution containing the copolymer (A) and the copolymer (B). The organic solvent used may be one that can dissolve the copolymer (A) and the copolymer (B), and examples thereof include ketones such as acetone, methyl ethyl ketone, and methyl isobutyl ketone; esters such as ethyl acetate, propyl acetate, and butyl acetate; amides such as dimethylacetamide and dimethylformamide; and aromatic hydrocarbons such as toluene and xylene. Any one of these may be used alone or in combination of two or more.

[0074] A cured product obtained by curing the curable resin composition has a low dielectric tangent and excellent dielectric properties, and therefore can be used for electronic materials such as printed circuit board materials and semiconductor encapsulation materials. That is, the curable resin composition according to one embodiment is a curable resin composition for electronic materials.

[0075] Examples of the printed circuit board material include rigid printed circuit board materials such as single-sided boards, double-sided boards, multilayer boards, and build-up boards, as well as film- or sheet-like flexible printed circuit board materials. In addition, because of their excellent dielectric properties, they are suitably used as high-frequency board materials for use in high-frequency communication devices. [Example]

[0076] The present invention will be explained in more detail below with reference to examples, but the present invention is not limited to the following examples.

[0077] <Measurement and evaluation methods> [Molar ratio of styrene / divinylbenzene / acenaphthylene] The products obtained in Examples 1 to 3, 8 to 12, and Comparative Example 1 (products before mixing with copolymer (B). The same applies to the measurements of other molar ratios below) were dissolved in deuterated chloroform and analyzed by a nuclear magnetic resonance spectrometer (manufactured by JEOL). 1 H-NMR measurement was carried out to determine the molar ratios of repeating units corresponding to styrene, repeating units corresponding to divinylbenzene, and repeating units relative to acenaphthylene, and the content of repeating units corresponding to styrene (styrene ratio), the content of repeating units corresponding to divinylbenzene (divinylbenzene ratio), and the content of repeating units corresponding to acenaphthylene (acenaphthylene ratio) relative to 100 mol% of all repeating units were calculated.

[0078] [4-vinylbiphenyl / divinylbenzene / acenaphthylene molar ratio] The product obtained in Example 4 was dissolved in deuterated chloroform and analyzed by a nuclear magnetic resonance spectrometer (manufactured by JEOL). 1H-NMR measurement was carried out to determine the molar ratios of repeating units corresponding to 4-vinylbiphenyl, repeating units corresponding to divinylbenzene, and repeating units relative to acenaphthylene, and the content of repeating units corresponding to 4-vinylbiphenyl (4-vinylbiphenyl ratio), the content of repeating units corresponding to divinylbenzene (divinylbenzene ratio), and the content of repeating units corresponding to acenaphthylene (acenaphthylene ratio) relative to 100 mol% of all repeating units were calculated.

[0079] [4-tert-butylstyrene / divinylbenzene / acenaphthylene molar ratio] The product obtained in Example 5 was dissolved in deuterated chloroform and analyzed by a nuclear magnetic resonance spectrometer (manufactured by JEOL). 1 H-NMR measurement was carried out to determine the molar ratios of repeating units corresponding to 4-tert-butylstyrene, repeating units corresponding to divinylbenzene, and repeating units relative to acenaphthylene, and the content of repeating units corresponding to 4-tert-butylstyrene relative to 100 mol% of all repeating units (4-tert-butylstyrene ratio), the content of repeating units corresponding to divinylbenzene (divinylbenzene ratio), and the content of repeating units corresponding to acenaphthylene (acenaphthylene ratio) were calculated.

[0080] [Molar ratio of styrene / divinylbenzene / indene] The product obtained in Example 6 was dissolved in deuterated chloroform and analyzed by a nuclear magnetic resonance spectrometer (manufactured by JEOL). 1 H-NMR measurement was carried out to determine the molar ratios of repeating units corresponding to styrene, repeating units corresponding to divinylbenzene, and repeating units relative to indene, and the content of repeating units corresponding to styrene (styrene ratio), the content of repeating units corresponding to divinylbenzene (divinylbenzene ratio), and the content of repeating units corresponding to indene (indene ratio) relative to 100 mol% of all repeating units were calculated.

[0081] [Molar ratio of styrene / divinylbenzene] The product obtained in Example 7 was dissolved in deuterated chloroform and analyzed by a nuclear magnetic resonance spectrometer (manufactured by JEOL). 1 H-NMR measurement was carried out to determine the molar ratio of repeating units corresponding to styrene and repeating units corresponding to divinylbenzene, and the content of repeating units corresponding to styrene (styrene ratio) and the content of repeating units corresponding to divinylbenzene (divinylbenzene ratio) relative to 100 mol% of all repeating units were calculated.

[0082] [Mw of copolymer (A), Mn of copolymer (B)] The sample was dissolved in tetrahydrofuran, and the weight-average molecular weight (Mw) or number-average molecular weight (Mn) in terms of polystyrene was measured using gel permeation chromatography (GPC) (Prominence, Shimadzu Corporation) connected with four columns packed with polystyrene gel (Shodex GPC columns KF-601, KF-602, KF-603, and KF-604, Showa Denko K.K.). The column oven temperature was 40°C, the THF flow rate was 0.6 mL / min, the sample concentration was 0.1% by mass, and the sample injection volume was 10 μL. A differential refractive index detector (Shodex RI-504, Showa Denko K.K.) was used.

[0083] [Melt viscosity] The compositions obtained in Examples 1 to 12 and Comparative Example 1, as well as the products of Reference Example 1 and Comparative Examples 2 and 3, were used as samples. Using a manual hydraulic pump: P-1B (manufactured by Riken), 0.4 g of sample was pressed at a pressure of 10 MPa for 1 minute to produce pellets with a diameter of 20 mm and a thickness of 1 mm. The obtained pellets were used as samples and heated from 50°C to 200°C at a heating rate of 5°C / min using a dynamic viscoelasticity measuring device: Rheosol-G5000NT (manufactured by UBM Corporation). The minimum value of the complex viscosity was defined as the minimum melt viscosity, with a minimum melt viscosity of less than 1000 poise being rated "A" (good), 1000 poise or more but less than 10,000 poise being rated "B" (fair), and 10,000 poise or more being rated "C" (poor).

[0084] [Moldability] Using the compositions obtained in Examples 1 to 12 and Comparative Example 1, and the products of Reference Example 1 and Comparative Examples 2 and 3 as samples, 1.5 g of the sample was pressed for 15 minutes at a pressure of 10 Pa and a temperature of 220°C using a test single-action compression molding machine (manufactured by Yasuda Seiki Seisakusho). Those that obtained flat plates measuring 30 mm x 30 mm x 1 mm thick were rated as "A" (good moldability), and those that obtained flat plates but had cracks were rated as "B" (average moldability).

[0085] [Dissipation Factor] The flat plates obtained in [Moldability] were cut to prepare test pieces 2 mm wide, 1 mm thick, and 30 mm long, and the dielectric loss tangent at 10 GHz was measured using a cavity resonator dielectric constant measuring device (manufactured by KEYSIGHT). Dielectric loss tangents of less than 0.0008 were rated "A" (good), those between 0.0008 and 0.0015 were rated "B" (fair), and those 0.0015 or greater were rated "C" (poor).

[0086] [Glass transition temperature Tg] The flat plates obtained in [Moldability] were cut to prepare test pieces measuring 5 mm in width, 1 mm in thickness, and 25 mm in length. The glass transition temperature of these test pieces was measured using a dynamic viscoelasticity measuring device: Rheogel-E4000 (manufactured by UBM Corporation). The maximum value of the loss tangent (tanδ) measured for the test pieces under conditions of a tensile sine wave, a frequency of 1 Hz, and a heating rate of 3°C / min was determined as the glass transition temperature. Glass transition temperatures of 160°C or higher were rated "A" (good), those between 140°C and 160°C were rated "B" (fair), and those below 140°C were rated "C" (poor).

[0087] (Synthesis Example 1) Compound 1: Synthesis of triphenylvinylbenzylphosphonium chloride (quaternized CMS) 1.5 mol (228.9 g) of vinylbenzyl chloride (trade name: CMS-14, manufactured by AGC Seimi Chemical Co., Ltd.), 1.8 mol (472.1 g) of triphenylphosphine, and 622.4 g of dimethylformamide were placed in a 2.0 L reactor and reacted at 70°C under nitrogen for 3 hours, resulting in the precipitation of a white solid. The solid was thoroughly washed with acetone and then dried under reduced pressure at 92°C, yielding 490 g of compound 1.

[0088] Example 1 51.4 g of styrene, 40.2 g of Compound 1, 8.4 g of acenaphthylene, 27.6 g of α-methylstyrene dimer, 3.80 g of 2,2'-azobis(2,4,4-trimethylpentane) (product name: VR-110, Fujifilm Wako Pure Chemical Industries, Ltd.), and 233.3 g of dimethylformamide were placed in a reactor and reacted at 120 °C for 3 hours under nitrogen conditions to obtain a copolymer as a dimethylformamide solution. This dimethylformamide solution was diluted with an equal amount of toluene, and 37% by weight formalin and 28% by weight potassium hydroxide aqueous solution were added so that the formaldehyde and potassium hydroxide amounts were 12 and 6 equivalents relative to Compound 1, respectively, and the reaction was carried out at room temperature for 4 hours. The reaction solution was diluted with toluene, and the organic layer was washed with distilled water and isopropyl alcohol. After dehydration and concentration of the organic layer, 6 equivalents of anhydrous magnesium chloride relative to Compound 1 were added and the mixture was stirred at 65 °C for 2 hours. The solid matter was removed by filtration, and the filtrate was diluted with toluene and reprecipitated in methanol. The solid matter was then removed by filtration, and the product (copolymer (A)) was recovered by drying under reduced pressure at 60°C. 92.5 parts by mass of this product and 7.5 parts by mass of SBR1 as copolymer (B) (3.52 parts by mass per 100 parts by mass of the monomer of copolymer (A)) were dissolved and mixed in toluene, and the toluene was distilled off by drying under reduced pressure at 60°C, obtaining the composition of Example 1.

[0089] (Examples 2 to 12 and Comparative Example 1) The types and amounts of the monomers of copolymer (A), the amount of α-methylstyrene dimer, and the type and amount of copolymer (B) were changed as shown in the formulations (parts by mass) in Tables 1 to 3 below, and the rest of the compositions were the same as in Example 1 to obtain the compositions of Examples 2 to 12 and Comparative Example 1.

[0090] (Reference Example 1 and Comparative Examples 2 and 3) The copolymers (A) obtained in Examples 1, 4 and 5 were directly used for evaluation as the products of Reference Example 1 and Comparative Examples 2 and 3, respectively.

[0091] Details of the copolymer (B) used in Examples 1 to 12 and Comparative Example 1 are as follows. SBR1: Styrene-butadiene copolymer, Kuraray Co., Ltd. "L-SBR-870", number average molecular weight Mn: 6000, glass transition temperature: -18°C SBR2: Styrene-butadiene copolymer, Kuraray Co., Ltd. "L-SBR-822", number average molecular weight Mn: 8800, glass transition temperature: -60°C

[0092] The weight-average molecular weight of copolymer (A) and the content of each repeating unit were measured for the compositions of Examples 1 to 12 and Comparative Example 1, and the products of Reference Example 1 and Comparative Examples 2 and 3. Furthermore, the melt viscosity, dielectric loss tangent, glass transition temperature, and moldability were evaluated. The results are shown in Tables 1 to 3 below. In Tables 1 to 3, the "content (mass%) of copolymer (B)" corresponds to the parts by mass of copolymer (B) relative to 100 parts by mass of the total of copolymer (A) and copolymer (B).

[0093] [Table 1]

[0094] [Table 2]

[0095] [Table 3]

[0096] The copolymer (A) obtained in Example 1 had a weight-average molecular weight of 3,200, a styrene ratio of 72.4 mol%, a divinylbenzene ratio of 17.4 mol%, and an acenaphthylene ratio of 10.2 mol%. The composition of Example 1 contained copolymer (B) in addition to copolymer (A), and had a low melt viscosity, a low dielectric loss tangent, a high glass transition temperature, and excellent moldability. In Reference Example 1, which is used for comparison, the copolymer (A) itself is the same as in Example 1, but does not contain copolymer (B). Therefore, the melt viscosity was higher than that of Example 1. This shows that by combining copolymer (A) with copolymer (B), the melt viscosity can be reduced without impairing the excellent dielectric properties, glass transition temperature, and moldability.

[0097] The copolymer (A) obtained in Example 2 differed from the copolymer (A) obtained in Example 1 in that it had a smaller weight-average molecular weight. Therefore, the composition of Example 2 was inferior to the composition of Example 1 in moldability and glass transition temperature, but was excellent in dielectric properties and melt viscosity, similar to Example 1.

[0098] The copolymer (A) obtained in Example 3 differs from the copolymer (A) of Example 1 in that it has a larger weight-average molecular weight. Therefore, the composition of Example 3 had a higher melt viscosity than the composition of Example 1. However, in Example 3, due to the inclusion of copolymer (B), the weight-average molecular weight of copolymer (A) was larger than that of Reference Example 1, and the melt viscosity was evaluated to be the same as that of Reference Example 1, and the dielectric properties were also excellent.

[0099] The copolymer (A) obtained in Example 4 had a weight-average molecular weight of 3,200, a 4-vinylbiphenyl ratio of 76.1 mol %, a divinylbenzene ratio of 14.9 mol %, and an acenaphthylene ratio of 9.0 mol %. In Comparative Example 2, which was used for comparison, the copolymer (A) itself was the same as in Example 4, but did not contain copolymer (B), and the melt viscosity was high. In contrast, in Example 4, by blending copolymer (B) together with copolymer (A), it was possible to reduce the melt viscosity compared to Comparative Example 2 without impairing the dielectric properties, glass transition temperature, and moldability.

[0100] The copolymer (A) obtained in Example 5 had a weight-average molecular weight of 3,200, a 4-tert-butylstyrene ratio of 72.4 mol%, a divinylbenzene ratio of 17.4 mol%, and an acenaphthylene ratio of 10.2 mol%. In Comparative Example 3, which was used for comparison, the copolymer (A) itself was the same as in Example 5, but did not contain copolymer (B), and the melt viscosity was high. In contrast, in Example 5, by blending copolymer (B) together with copolymer (A), it was possible to reduce the melt viscosity compared to Comparative Example 3 without impairing the dielectric properties, glass transition temperature, and moldability.

[0101] The copolymer (A) obtained in Example 6 had a weight-average molecular weight of 3600, a styrene ratio of 71.8 mol%, a divinylbenzene ratio of 17.5 mol%, and an indene ratio of 10.7 mol%. Example 6 was obtained by replacing acenaphthylene in the copolymer (A) of Example 1 with indene, and was inferior to Example 1 in moldability and glass transition temperature, but was excellent in dielectric properties and melt viscosity, similar to Example 1.

[0102] The copolymer (A) obtained in Example 7 had a weight average molecular weight of 3200, a styrene ratio of 83.1 mol %, and a divinylbenzene ratio of 16.9 mol %. Example 7 was obtained by removing acenaphthylene from the copolymer (A) of Example 1, and had a glass transition temperature inferior to that of Example 1. However, like Example 1, it had excellent dielectric properties, melt viscosity, and moldability.

[0103] The copolymer (A) obtained in Example 8 had a weight-average molecular weight of 3,200, a styrene ratio of 56.5 mol%, a divinylbenzene ratio of 33.7 mol%, and an acenaphthylene ratio of 9.7 mol%. Example 8 had a higher divinylbenzene ratio in copolymer (A) than Example 1, and was inferior in dielectric properties and melt viscosity to Example 1, but by using copolymer (B) in combination, these were able to remain within the acceptable range. In contrast, in Comparative Example 1, the divinylbenzene ratio was 53.9 mol%, which was too high, and therefore the dielectric properties and melt viscosity were significantly deteriorated.

[0104] The copolymer (A) obtained in Example 9 had a weight average molecular weight of 3200, a styrene ratio of 77.3 mol%, a divinylbenzene ratio of 17.4 mol%, and an acenaphthylene ratio of 5.2 mol%. Example 9 had a higher styrene ratio and a lower acenaphthylene ratio in the copolymer (A) than Example 1, and was inferior in glass transition temperature to Example 1. However, like Example 1, it was excellent in dielectric properties, melt viscosity, and moldability.

[0105] The copolymer (A) obtained in Example 10 had a weight average molecular weight of 3200, a styrene ratio of 62.9 mol%, a divinylbenzene ratio of 16.9 mol%, and an acenaphthylene ratio of 20.2 mol%. Example 10 had a lower styrene ratio and a higher acenaphthylene ratio in the copolymer (A) than Example 1, and although the melt viscosity was inferior to that of Example 1, it was within an acceptable range, and the dielectric properties, glass transition temperature, and moldability were as excellent as those of Example 1.

[0106] In Example 11, the amount of copolymer (B) was increased compared to Example 1, and the dielectric properties were inferior to those of Example 1, but were within the acceptable range. The melt viscosity, glass transition temperature, and moldability were excellent, just like those of Example 1.

[0107] The various numerical ranges described in this specification can be arbitrarily combined with their upper and lower limits, and all such combinations are considered to be preferred numerical ranges described in this specification. Furthermore, a numerical range described as "X to Y" means from X to Y.

[0108] Although several embodiments of the present invention have been described above, these embodiments are presented as examples and are not intended to limit the scope of the invention. These embodiments can be implemented in various other forms, and various omissions, substitutions, and modifications can be made without departing from the spirit of the invention. These embodiments and their omissions, substitutions, modifications, etc. are included within the scope and spirit of the invention, as well as within the scope of the invention described in the claims and their equivalents.

Claims

1. a linear copolymer (A) having a repeating unit corresponding to a monovinyl aromatic compound and a repeating unit corresponding to a divinyl aromatic compound, wherein the content of the repeating unit corresponding to the divinyl aromatic compound in 100 mol % of all repeating units is less than 40 mol %; a copolymer (B) containing a styrene-based monomer and an aliphatic diene monomer having 4 to 7 carbon atoms as constituent monomers and / or a hydrogenated product thereof, the copolymer having a number average molecular weight of 50,000 or less; Including, the amount of the copolymer (B) is 80 parts by mass or less relative to 100 parts by mass of the total of the copolymer (A) and the copolymer (B); Curable resin composition.

2. The curable resin composition according to claim 1 , wherein the copolymer (B) comprises a copolymer of a styrene-based monomer and butadiene and / or a hydrogenated product thereof.

3. 3. The curable resin composition according to claim 1, wherein the content of the repeating units corresponding to the divinyl aromatic compound is less than 20 mol% in 100 mol% of all repeating units of the copolymer (A).

4. The curable resin composition according to claim 1 or 2, wherein the copolymer (A) further has a repeating unit corresponding to an aromatic ring-fused cyclic olefin compound having three rings.

5. 3. The curable resin composition according to claim 1, wherein the content of repeating units corresponding to the monovinyl aromatic compound is 50 mol% or more in 100 mol% of all repeating units of the copolymer (A).

6. The curable resin composition according to claim 1 or 2, which is a material for a printed circuit board.

Images