Rubber composition and tire

Abstract

The purpose of the present invention is to provide a rubber composition which is excellent in terms of low heat buildup property, high modulus, and crack propagation resistance.　This rubber composition includes carbon black, a bismaleimide compound, and a hydrazide compound, and is characterized in that the bismaleimide compound is represented by general formula (I), the hydrazide compound is represented by general formula (II), and the carbon black has a nitrogen-adsorption specific surface area (N2SA) less than 40 m2 / g and, when examined as a compact specimen, has an oil absorption (COAN) of 60 ml / 100 g or greater, the content of the carbon black being 35 parts by mass or higher but less than 45 parts by mass per 100 parts by mass of the rubber component.

Description

[Technical field]

[0001] The present invention relates to a rubber composition and a tire. [Background technology]

[0002] From the viewpoint of fuel economy, tires used on vehicles are required to generate little heat and have low rolling resistance, and are also required to rotate at high speeds without breaking down. As means for satisfying these requirements, for example, there are techniques for increasing the particle size of carbon black in a rubber composition used as a tire material, and techniques for increasing the dispersibility of carbon black by using a carbon dispersion aid. However, when the particle size of carbon black is increased, although it contributes to low heat generation, there is a problem that the mechanical properties of the tire are reduced, and when a carbon dispersion aid is used, although low heat generation and high strength can be achieved at the initial stage, there is a risk that heat aging, which is a side effect of the carbon dispersion aid, occurs in tires after long-term use, and the breaking strength is reduced (heat aging resistance is reduced).

[0003] Here, as a technique for achieving both low heat generation and high strength, a technique of compounding a bismaleimide compound or a hydrazide compound in a rubber composition is known. For example, Patent Documents 1 and 2 disclose technologies that achieve both a high elastic modulus and low rolling resistance by using a rubber composition containing a rubber component and a specific bismaleimide compound or hydrazide compound in a pneumatic tire. Furthermore, Patent Document 3 discloses a technology in which a rubber composition containing a rubber component, a reinforcing filler, and a specific hydrazide compound is used in a tire to suppress a decrease in elastic modulus caused by reversion due to over-vulcanization while maintaining low heat generation properties. Furthermore, Patent Document 4 discloses a technology that uses a rubber composition containing a hydrazone compound having a specific structure and sodium 1,6-hexamethylenedithiosulfate dihydrate in tires to improve creep resistance and crack growth resistance while maintaining low heat buildup. [Prior art documents] [Patent documents]

[0004] [Patent Document 1] JP 2001-172431 A [Patent Document 2] JP 2002-121326 A [Patent Document 3] JP 2001-213112 A [Patent Document 4] JP 2002-146110 A Summary of the Invention [Problem to be solved by the invention]

[0005] However, in the techniques disclosed in Patent Documents 1 to 4, it is difficult to achieve both low heat buildup and high levels of performance such as high elastic modulus and crack growth resistance, and further improvement is desired, particularly with regard to low heat buildup.

[0006] Therefore, an object of the present invention is to provide a rubber composition that achieves low heat buildup while also having a high elastic modulus and excellent crack growth resistance, and also to provide a tire that has a high elastic modulus, excellent crack growth resistance, and reduced rolling resistance. [Means for solving the problem]

[0007] The gist of the present invention for solving the above problems is as follows. The rubber composition of the present invention is a rubber composition including a rubber component, carbon black, a bismaleimide compound, and a hydrazide compound, The bismaleimide compound is represented by the following general formula (I), and its content is more than 0 part by mass and less than 1 part by mass per 100 parts by mass of the rubber component, [ka] (In general formula (I), A represents a divalent aromatic group having 6 to 18 carbon atoms or a divalent alkyl aromatic group having 7 to 24 carbon atoms, and x and y each independently represent an integer of 0 to 3.) The hydrazide compound is represented by the following general formula (II), and its content is 0.5 parts by mass or more based on 100 parts by mass of the rubber component, [ka] (In the general formula (II), B represents a polyvalent acyclic aliphatic group having 2 to 18 carbon atoms (the functional group may contain an aromatic group therein), a polyvalent cyclic aliphatic group having 5 to 20 carbon atoms, a polyvalent aromatic group having 6 to 18 carbon atoms, or a polyvalent alkyl aromatic group having 7 to 24 carbon atoms, and the functional group may contain at least one hetero atom selected from oxygen, nitrogen, and sulfur atoms. X represents a hydrogen atom, a hydroxyl group, an amino group, or a mercapto group. R1 and R2 each independently represent a hydrogen atom, an alkyl group having 1 to 18 carbon atoms, a cycloalkyl group, or an aromatic ring, and the substituent may contain at least one hetero atom selected from oxygen, nitrogen, and sulfur atoms. z represents an integer of 1 to 3.) The carbon black has a nitrogen adsorption specific surface area (N2SA) of 40 m 2 / g, and the oil absorption (COAN) of a compressed sample is 60 ml / 100 g or more, and the oil content is 35 parts by mass or more and less than 45 parts by mass per 100 parts by mass of the rubber component. By having the above-mentioned configuration, it is possible to achieve low heat build-up, high elastic modulus, and high crack growth resistance all at the same time.

[0008] In the rubber composition of the present invention, the hydrazide compound is preferably 3-hydroxy-N'-(1,3-dimethylbutylidene)-2-naphthoic acid hydrazide, which can further enhance the low heat buildup property and improve the Mooney viscosity.

[0009] In the rubber composition of the present invention, the bismaleimide compound is preferably at least one selected from the group consisting of N,N'-1,2-phenylene bismaleimide, N,N'-1,3-phenylene bismaleimide, and N,N'-1,4-phenylene bismaleimide, which can further increase the elastic modulus and improve the heat aging resistance.

[0010] In the rubber composition of the present invention, the rubber component preferably contains 90% by mass or more of natural rubber, which can further improve low heat build-up, high elastic modulus, and crack growth resistance.

[0011] In the rubber composition of the present invention, it is preferable that the rubber composition does not contain silica as a filler, in which case the crack growth resistance and processability of the rubber composition can be further improved.

[0012] The rubber composition of the present invention preferably further contains less than 5 parts by mass of zinc oxide (ZnO) per 100 parts by mass of the rubber component, which can improve the high elastic modulus and heat aging resistance without reducing the crack growth resistance of the rubber composition.

[0013] In the tire of the present invention, it is preferable that the rubber composition is used in at least one of the ply coating rubber, the inter-ply rubber, the belt coating rubber, the inter-belt cushion rubber, the belt end cover rubber, and the stiffener rubber, which can more effectively exhibit high elastic modulus, crack growth resistance, and reduced rolling resistance. Effect of the Invention

[0014] According to the present invention, it is possible to provide a rubber composition that achieves low heat buildup while also exhibiting high elastic modulus and excellent crack growth resistance. Also, according to the present invention, it is possible to provide a tire that has high elastic modulus, excellent crack growth resistance, and reduced rolling resistance. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0015] An embodiment of the rubber composition and tire of the present invention will be described below by way of example.

[0016] <Rubber composition> The rubber composition of the present invention contains a rubber component, carbon black, a bismaleimide compound, and a hydrazide compound.

[0017] In the present invention, the bismaleimide compound is represented by the following general formula (I), and its content is more than 0 part by mass and less than 1 part by mass per 100 parts by mass of the rubber component, [ka] (In general formula (I), A represents a divalent aromatic group having 6 to 18 carbon atoms or a divalent alkyl aromatic group having 7 to 24 carbon atoms, and x and y each independently represent an integer of 0 to 3.) The hydrazide compound is represented by the following general formula (II), and its content is 0.5 parts by mass or more based on 100 parts by mass of the rubber component, [ka] (In the general formula (II), B represents a polyvalent acyclic aliphatic group having 2 to 18 carbon atoms (the functional group may contain an aromatic group therein), a polyvalent cyclic aliphatic group having 5 to 20 carbon atoms, a polyvalent aromatic group having 6 to 18 carbon atoms, or a polyvalent alkyl aromatic group having 7 to 24 carbon atoms, and the functional group may contain at least one hetero atom selected from oxygen, nitrogen, and sulfur atoms. X represents a hydrogen atom, a hydroxyl group, an amino group, or a mercapto group. R1 and R2 each independently represent a hydrogen atom, an alkyl group having 1 to 18 carbon atoms, a cycloalkyl group, or an aromatic ring, and the substituent may contain at least one hetero atom selected from oxygen, nitrogen, and sulfur atoms. z represents an integer of 1 to 3.) The carbon black has a nitrogen adsorption specific surface area (N2SA) of 40 m 2 / g, and the oil absorption (COAN) of a compressed sample is 60 ml / 100 g or more, and the oil content is 35 parts by mass or more and less than 45 parts by mass per 100 parts by mass of the rubber component.

[0018] By using the bismaleimide compound represented by the general formula (I) in combination with the hydrazide compound represented by the general formula (II), the bismaleimide compound increases the strength, elastic modulus, and heat resistance of the rubber composition, and the hydrazide compound improves the low heat generation property and heat aging resistance, so that the low heat generation property and high elastic modulus of the rubber composition of the present invention can be significantly improved. However, since a large content of the bismaleimide compound may lead to hardening of the rubber and hinder productivity and low heat generation property, by making the content of the bismaleimide compound in the rubber composition less than 1 part by mass, it is possible to maintain a high level of high elastic modulus and crack growth resistance while achieving low heat generation property of the tire. In addition, the rubber composition of the present invention uses carbon black with optimized nitrogen adsorption specific surface area (N2SA) and compressed oil absorption (COAN), which makes it possible to further enhance the excellent improvement effect of low heat buildup properties.

[0019] Each component constituting the rubber composition of the present invention will be described below. (Rubber component) The rubber component contained in the rubber composition of the present invention is not particularly limited, but from the viewpoint of obtaining excellent low heat buildup properties, crack growth resistance, and high elastic modulus, it is preferable that the rubber composition contains at least a diene rubber.

[0020] Examples of the diene rubber include natural rubber, polyisoprene rubber (IR), styrene-butadiene copolymer rubber (SBR), polybutadiene rubber (BR), etc., and among these, it is preferable to use natural rubber because it can achieve better low heat build-up and crack growth resistance. From the same viewpoint, the content of natural rubber in the rubber component is preferably 80% by mass or more, more preferably 90% by mass or more, and particularly preferably 95% by mass or more. The diene rubber may be contained alone or in the form of a blend of two or more kinds.

[0021] (Bismaleimide compounds) The rubber composition for a tire of the present invention contains, in addition to the above-mentioned rubber component, a bismaleimide compound represented by the following general formula (I). [ka] By incorporating the bismaleimide compound represented by the above general formula (I) in the rubber composition of the present invention, it is possible to improve the heat resistance, heat aging resistance, dynamic storage modulus (E'), and the like.

[0022] In the above general formula (I), A represents a divalent aromatic group having 6 to 18 carbon atoms or a divalent alkyl aromatic group having 7 to 24 carbon atoms, and x and y each independently represent an integer of 0 to 3. In the bismaleimide compound represented by the above general formula (I), x and y are both integers of 0 to 3. If x or y is 4 or more, the molecular weight becomes too large, and the intended effect of improving the heat aging resistance, dynamic storage modulus, etc., cannot be obtained in proportion to the blending amount, which is inconvenient.

[0023] Specific examples of the bismaleimide compound represented by general formula (I) include N,N'-1,2-phenylene dimaleimide, N,N'-1,3-phenylene dimaleimide, N,N'-1,4-phenylene dimaleimide, N,N'-(4,4'-diphenylmethane)bismaleimide, 2,2-bis[4-(4-maleimidophenoxy)phenyl]propane, bis(3-ethyl-5-methyl-4-maleimidophenyl]methane, etc. One or more of these bismaleimide compounds can also be blended. Among these bismaleimide compounds, it is preferable to use N,N'-1,2-phenylene dimaleimide, N,N'-1,3-phenylene dimaleimide, and N,N'-1,4-phenylene dimaleimide, and N,N'-(4,4'-diphenylmethane)bismaleimide is particularly preferable because of its remarkable effect.

[0024] The content of the bismaleimide compound in the rubber composition of the present invention must be more than 0 part by mass and less than 1 part by mass per 100 parts by mass of the rubber component. By making the content of the bismaleimide compound less than 1 part by mass per 100 parts by mass of the rubber component, excessive hardening of the rubber composition can be suppressed and a balance between low heat generation and crack growth resistance can be maintained. From the same viewpoint, the content of the bismaleimide compound is preferably 1 part by mass or less per 100 parts by mass of the rubber component. From the viewpoint of further improving the heat resistance, heat aging resistance, and dynamic storage modulus (E'), the content of the bismaleimide compound is preferably 0.5 parts by mass or more based on 100 parts by mass of the rubber component.

[0025] (Hydrazide compounds) The rubber composition for tires of the present invention contains, in addition to the above-mentioned rubber component and bismaleimide compound, a hydrazide compound represented by the following general formula (II). [ka] By incorporating the hydrazide compound represented by the above general formula (II) in the rubber composition of the present invention, the dispersibility of the carbon black described below can be increased to improve low heat build-up properties, and heat aging resistance caused by reversion, etc. can also be improved.

[0026] In the above general formula (II), B represents a polyvalent acyclic aliphatic group having 2 to 18 carbon atoms (the functional group may contain an aromatic group therein), a polyvalent cyclic aliphatic group having 5 to 20 carbon atoms, a polyvalent aromatic group having 6 to 18 carbon atoms, or a polyvalent alkyl aromatic group having 7 to 24 carbon atoms, and the functional group may contain at least one heteroatom selected from oxygen, nitrogen, and sulfur atoms. X represents a hydrogen atom, a hydroxyl group, an amino group, or a mercapto group. R1 and R2 each independently represent a hydrogen atom, an alkyl group having 1 to 18 carbon atoms, a cycloalkyl group, or an aromatic ring, and the substituent may contain at least one heteroatom selected from oxygen, nitrogen, and sulfur atoms. z represents an integer of 1 to 3.

[0027] Specific examples of the hydrazide compound represented by the above general formula (II) preferably include derivatives of 3-hydroxy-2-naphthoic acid hydrazide (HNH), as well as derivatives of N'-(1,3-dimethylbutylidene)salicylic acid hydrazide (BMS), 4-hydroxybenzoic acid hydrazide, anthranilic acid hydrazide, and 1-hydroxy-2-naphthoic acid hydrazide. In addition, examples of the derivatives of 3-hydroxy-2-naphthoic acid hydrazide (HNH) include 3-hydroxy-2-naphthoic acid hydrazides such as 3-hydroxy-2-naphthoic acid (1-methylethylidene) hydrazide, 3-hydroxy-2-naphthoic acid (1-methylpropylidene) hydrazide, 3-hydroxy-2-naphthoic acid (1,3-dimethylpropylidene) hydrazide, and 3-hydroxy-2-naphthoic acid (1-phenylethylidene) hydrazide.

[0028] Among these hydrazide compounds, derivatives of 3-hydroxy-2-naphthoic acid hydrazide (for example, a product of Otsuka Chemical Co., Ltd. under the trade name "HNH" corresponds to this compound) and derivatives of N'-(1,3-dimethylbutylidene)salicylic acid hydrazide (for example, a product of Otsuka Chemical Co., Ltd. under the trade name "BMS" corresponds to this compound) are preferred in that they can maintain low heat generation while keeping the Mooney viscosity low. Furthermore, 3-hydroxy-N'-(1,3-dimethylbutylidene)-2-naphthoic acid hydrazide, which is a derivative of 3-hydroxy-2-naphthoic acid hydrazide ("HNH"), can be preferably used because of its remarkable effect.

[0029] In addition, the hydrazide compound represented by the above general formula (II) has excellent reversion resistance, is particularly suitable for rubber compositions containing natural rubber as a rubber component, and exhibits little deterioration in performance even under high temperature vulcanization conditions. The hydrazide compound may be used alone or in combination of two or more kinds. The hydrazide compound represented by the above general formula (II) can be produced based on the method described in the literature of Pant, UC; Ramchandran, Reena; Joshi, BC Rev. Roum. Chim. (1979) 24(3), 471-82.

[0030] The content of the hydrazide compound in the rubber composition of the present invention must be 0.5 parts by mass or more per 100 parts by mass of the rubber component. By making the content of the hydrazide compound 0.5 parts by mass or more per 100 parts by mass of the rubber component, the low heat build-up property and heat aging resistance of the rubber composition can be sufficiently improved. In addition, if the content of the hydrazide compound is too large, the low heat build-up property of the rubber composition may be deteriorated, so the content of the hydrazide compound is set to 0.5 parts by mass or more per 100 parts by mass of the rubber component. 2 It is preferably less than or equal to parts by mass.

[0031] (Carbon Black) The rubber composition of the present invention contains carbon black in addition to the above-mentioned rubber component, bismaleimide compound, and hydrazide compound. By containing carbon black in the rubber composition, the reinforcement property and elastic modulus of the rubber composition can be increased.

[0032] The carbon black has a nitrogen adsorption specific surface area (N2SA) of 40 m 2 The carbon black has a nitrogen adsorption specific surface area (N2SA) of 40 m 2 By reducing the carbon black content to less than 1 / g, the primary particles of the carbon black become larger, thereby realizing excellent low heat generation properties. On the other hand, by increasing the oil absorption (COAN) of the compressed sample of the carbon black to 60 ml / 100 g or more, highly structured carbon black in which aggregates, which are secondary particles, are developed can be obtained, which can contribute to the reinforcing properties of the rubber composition. Therefore, by using the above-mentioned carbon black in the rubber composition of the present invention, low heat generation, high elastic modulus, and crack growth resistance can be achieved at the same time.

[0033] In addition, the N2SA of the carbon black is 35m 2 / g or less is more preferable, and 30m 2 It is more preferable that the molecular weight is not more than 1 / g. On the other hand, from the viewpoint of suppressing deterioration of the crack growth resistance of the rubber composition, the N2SA of the carbon black is 22m 2 It is preferable that the molecular weight is 1 / g or more. The nitrogen adsorption specific surface area (N2SA) can be measured by the method specified in JIS K 6217-2:2017 "Carbon black for rubber - Basic characteristics - Part 2, Determination of specific surface area - Nitrogen adsorption method, single point method".

[0034] Furthermore, from the above-mentioned viewpoint, the COAN of the carbon black is preferably 65 ml / 100 g or more, and more preferably 70 ml / 100 g or more. On the other hand, from the viewpoint of obtaining a high level of reinforcing properties of the rubber composition, the COAN of the carbon black is preferably 100 ml / 100 g or less, more preferably 85 ml / 100 g or less, and even more preferably 75 ml / 100 g or less. The oil absorption (COAN) of the compressed sample can be measured by the method specified in JIS K 6217-4:2017 "Carbon black for rubber - Basic properties - Part 4, Determination of oil absorption (including compressed samples)".

[0035] Furthermore, the type of carbon black is not particularly limited, except that it has the above-mentioned N2SA and COAN. For example, any hard carbon produced by the oil furnace method can be used. Among these, it is preferable to use SRF, GPF, and FEF grade carbon black from the viewpoint of achieving better low heat generation and wear resistance. These carbon blacks may be used alone or in combination of two or more kinds.

[0036] Here, the content of the carbon black in the rubber composition of the present invention is 35 parts by mass or more and less than 45 parts by mass per 100 parts by mass of the rubber component. By including 35 parts by mass or more of the carbon black per 100 parts by mass of the rubber component, it is possible to sufficiently obtain the effect of improving the reinforcement property and the elastic modulus, and by including less than 45 parts by mass of the carbon black per 100 parts by mass of the rubber component, it is possible to suppress deterioration of low heat build-up property caused by an excessive amount of carbon black.

[0037] (Other Ingredients) In addition to the above-mentioned components, the rubber composition of the present invention may contain other components selected appropriately according to purpose or need, within a range that does not impair the effects of the present invention. Examples of other components include additives such as inorganic fillers, zinc oxide, softeners, tackifiers, dispersants, crosslinking agents, crosslinking accelerators, crosslinking aids, stearic acid, antioxidants, antioxidants, antiozonants, colorants, antistatic agents, and lubricants, as well as various known compounding chemicals that are commonly used in the rubber industry. Commercially available products may be used.

[0038] Examples of the inorganic filler include aluminum hydroxide, clay, etc. Among the inorganic fillers, aluminum hydroxide, etc. is preferred because it has a relatively high reinforcing property, and clay, etc. is effective because it can take advantage of its shape characteristics. In addition, from the viewpoint of further improving crack growth resistance and processability, it is preferable that the rubber composition of the present invention does not contain silica as a filler.

[0039] In addition, the rubber composition of the present invention preferably contains zinc oxide (ZnO) as a crosslinking promoter. This is because the inclusion of ZnO can further improve heat aging resistance and high elastic modulus. However, if the ZnO content is too high, crack growth properties may deteriorate, so the ZnO content is preferably less than 5 parts by mass per 100 parts by mass of the rubber component.

[0040] Furthermore, the softener is not particularly limited and can be appropriately selected depending on the purpose. For example, naphthenic base oil, paraffinic base oil, aromatic base oil, etc. can be mentioned. Here, the content of the softener is preferably 2 to 30 parts by mass per 100 parts by mass of the rubber component. If the content of the softener exceeds 30 parts by mass per 100 parts by mass of the rubber component, the softener may bleed onto the surface of the rubber product or the abrasion resistance may decrease. Furthermore, among the above-mentioned softeners, it is preferable to use naphthenic base oil or paraffinic base oil, and it is most preferable to use naphthenic base oil. Aromatic oil is undesirable because it contains a lot of aromatic components, has a high affinity with the chemical, which is an aromatic compound, and inhibits the reaction with the polymer more. On the other hand, naphthenic base oil and paraffinic base oil have the effect of diffusing into the polymer and helping it to react, and oils with low pour points diffuse into the polymer better. The classification of naphthenic base oil, paraffinic base oil, and aromatic base oil is determined by CA value, CP value, and CN value. For example, naphthenic base oil includes TDAE, SRAE, RAE, and black oil. Also, paraffinic base oil includes spindle oil and paraffin oil. Furthermore, a more preferable effect can be obtained by using a mixed oil such as A / O Mix (Sankyo Yuka Kogyo Co., Ltd.) in which the naphthenic base oil and the naphthenic asphalt are mixed. The timing of adding these lubricating oils is not particularly limited. For example, the lubricating oils may be added during the production of the rubber component, or may be added when the rubber composition is kneaded.

[0041] The crosslinking agent is not particularly limited, and may be, for example, sulfur. The crosslinking accelerator may be any known one and is not particularly limited. For example, thiazole-based vulcanization accelerators such as 2-mercaptobenzothiazole and dibenzothiazyl disulfide; sulfenamide-based vulcanization accelerators such as N-cyclohexyl-2-benzothiazyl sulfenamide and Nt-butyl-2-benzothiazyl sulfenamide; guanidine-based vulcanization accelerators such as diphenyl guanidine; thiuram-based vulcanization accelerators such as tetramethylthiuram disulfide, tetraethylthiuram disulfide, tetrabutylthiuram disulfide, tetradodecylthiuram disulfide, tetraoctylthiuram disulfide, tetrabenzylthiuram disulfide, and dipentamethylenethiuram tetrasulfide; dithiocarbamate-based vulcanization accelerators such as zinc dimethyldithiocarbamate; and zinc dialkyldithiophosphate.

[0042] The antiaging agent may be any known agent and is not particularly limited. For example, phenol-based antiaging agents, imidazole-based antiaging agents, amine-based antiaging agents, etc. may be used. These antiaging agents may be used alone or in combination of two or more.

[0043] (Production of Rubber Composition) The rubber composition of the present invention can be produced by blending the carbon black, the bismaleimide compound, and the hydrazide compound with the rubber component, kneading with zinc oxide, stearic acid, an antioxidant, sulfur, a vulcanization accelerator, a carbon black dispersant, and other additives appropriately selected depending on the purpose or need, extruding or rolling, and then vulcanizing.

[0044] The conditions for the kneading are not particularly limited, and various conditions such as the input volume of the kneading device, the rotation speed of the rotor, the ram pressure, the kneading temperature, the kneading time, the type of the kneading device, etc. can be appropriately selected depending on the purpose. Examples of the kneading device include a Banbury mixer, an intermix, a kneader, a roll, etc. that are usually used for kneading rubber compositions.

[0045] The conditions for the heating are not particularly limited, and the heating temperature, heating time, heating device, and other conditions can be appropriately selected depending on the purpose. The heat-treating device may be a heat-treating roll machine which is generally used for heat-treating a rubber composition.

[0046] Furthermore, the extrusion conditions are not particularly limited, and various conditions such as extrusion time, extrusion speed, extrusion device, and extrusion temperature can be appropriately selected depending on the purpose. Examples of the extrusion device include an extruder that is usually used for extruding rubber compositions for tires. The extrusion temperature can be appropriately determined.

[0047] Furthermore, the vulcanization apparatus, method, conditions, etc. are not particularly limited and can be appropriately selected according to the purpose. As the vulcanization apparatus, a molding vulcanizer using a mold used for vulcanizing rubber compositions for tires can be mentioned. As the vulcanization condition, the temperature is, for example, about 100 to 190°C.

[0048] <Tires> The tire of the present invention is characterized by using the above-mentioned rubber composition of the present invention. By including the rubber composition of the present invention as a tire material, it is possible to achieve a high elastic modulus and improved crack growth resistance, and to reduce rolling resistance.

[0049] The tire of the present invention is not particularly limited except that the above-mentioned rubber composition of the present invention is used in any of the tire components, and can be produced according to a conventional method. The gas to be filled in the tire may be normal air or air with an adjusted oxygen partial pressure, or an inert gas such as nitrogen, argon, or helium.

[0050] In the tire of the present invention, the above-mentioned rubber composition of the present invention is used in any of the tire components, and among the tire components, it is preferable to use it in at least one of the ply coating rubber, the inter-ply rubber, the belt coating rubber, the inter-belt cushion rubber, the belt end cover rubber, and the stiffener rubber, because by applying it to these components, the benefits of the improved effect of the rubber composition of the present invention on the high elastic modulus, crack growth resistance, and low rolling resistance can be fully enjoyed. EXAMPLES

[0051] The present invention will be described in more detail below with reference to examples, but the present invention is not limited to the following examples in any way.

[0052] <Samples 1-15> According to the formulation shown in Table 1, each component was blended and kneaded using a Banbury mixer to prepare a rubber composition sample.

[0053] <Evaluation> Each sample of the obtained rubber composition was extruded into a sheet and then vulcanized at a temperature of 145°C for a vulcanization time 1.5 times the time (T90) until the increase in torque due to the vulcanization reaction reached 90% of the total, to prepare a vulcanized rubber sample for measuring physical properties. The obtained vulcanized rubber samples were then subjected to the following evaluations.

[0054] (1) tan δ (low heat generation) For vulcanized rubber samples obtained from the rubber compositions of each sample, the loss tangent (tan δ) was measured using a spectrometer (manufactured by Ueshima Seisakusho Co., Ltd.) under conditions of a temperature of 25° C., an initial load of 1600 mN, a dynamic strain of 2%, and a frequency of 52 Hz. The evaluation was expressed as an index when the tan δ of Sample 1, which is a comparative example, was taken as 100, and the smaller the index value, the more excellent the low heat build-up property. The evaluation results are shown in Table 1.

[0055] (2) Crack propagation resistance A vulcanized rubber sample obtained from each sample rubber composition was repeatedly pulled at a stress of 1.1 N using a tensile testing device (manufactured by Shimadzu Corporation), and the number of times until the sample broke was measured. For the evaluation, the common logarithm (log) of the number of times measured until break was calculated and expressed as an index value with the logarithm value of the reference example set to 100. A higher index value indicates greater tear strength and better crack propagation resistance. The evaluation results are shown in Table 1. Note that the index of the reference example is listed merely as a standard value for easy comparison, so even if the crack propagation resistance index of each sample is below 100, it is considered to be at the same level as long as it is 98 or higher.

[0056] (3) 300% modulus For the vulcanized rubber samples obtained from the rubber compositions of each sample, specimens were prepared according to methods conforming to JIS-K-6299 and JIS-K-6250. Then, a tensile test was carried out on the specimens at a speed of 500 mm / min using a tensile tester (Strograph manufactured by Toyo Seiki Co., Ltd.) according to JIS-K-6252, to measure the 300% modulus. is shown in Table 1. The evaluation was carried out by showing an index value with the 300% modulus of the reference example taken as 100, and the closer the index value is to 100, the more suitable the modulus is as a rubber composition for tires.

[0057] (4) Storage modulus (E1) For the vulcanized rubber samples obtained from the rubber compositions of each sample, the storage modulus E1' (MPa) was measured using a spectrometer (manufactured by Ueshima Seisakusho Co., Ltd.) under conditions of a temperature of 25°C, an initial load of 1600 mN, a dynamic strain of 2%, and a frequency of 52 Hz. The index for the reference example was set to 100 and is shown in Table 1. Regarding the evaluation, the closer the index value is to 100, the more appropriate the elastic modulus is for a rubber composition for tires. The evaluation results are shown in Table 1.

[0058] [Table 1]

[0059] *1 N2SA:26m 2 / g, COAN: 70ml / 100g carbon black *2 N2SA:69m 2 / g, COAN: 87ml / 100g of carbon black *3 N2SA: 35m 2 / g, COAN: 74ml / 100g of carbon black *4 N2SA: 40m 2 / g, COAN: 83ml / 100g of carbon black *5 3-Hydroxy-N'-(1,3-dimethylbutylidene)-2-naphthoic acid hydrazide, manufactured by Otsuka Chemical Co., Ltd. *6 N,N'-(4,4'-diphenylmethane)bismaleimide, manufactured by Mitsui Chemicals, Inc. *7 "Mu-Clon OT-20" manufactured by Shikoku Chemical Industry Co., Ltd. *8 Nt-butyl-2-benzothiazolylsulfenamide, "Noccera-NS-P" manufactured by Ouchi Shinko Chemical Industry Co., Ltd.

[0060] It can be seen from Table 1 that each sample of the rubber composition corresponding to the examples exhibits a well-balanced and excellent effect in terms of low heat build-up property, crack growth resistance, and elastic modulus. [Industrial Applicability]

[0061] According to the present invention, it is possible to provide a rubber composition that achieves low heat buildup while also exhibiting high elastic modulus and excellent crack growth resistance. Also, according to the present invention, it is possible to provide a tire that has high elastic modulus, excellent crack growth resistance, and reduced rolling resistance.

Claims

1. A rubber composition comprising a rubber component, carbon black, a bismaleimide compound, and a hydrazide compound, The bismaleimide compound is represented by the following general formula (I), and its content is more than 0 part by mass and less than 1 part by mass per 100 parts by mass of the rubber component, [Formula 1] (In general formula (I), A represents a divalent aromatic group having 6 to 18 carbon atoms or a divalent alkyl aromatic group having 7 to 24 carbon atoms, and x and y each independently represent an integer of 0 to 3.) The hydrazide compound is represented by the following general formula (II), and its content is 0.5 parts by mass or more based on 100 parts by mass of the rubber component, [chemical 2] (In general formula (II), B represents a polyvalent acyclic aliphatic group having 2 to 18 carbon atoms (the functional group may contain an aromatic group therein), a polyvalent cyclic aliphatic group having 5 to 20 carbon atoms, a polyvalent aromatic group having 6 to 18 carbon atoms, or a polyvalent alkyl aromatic group having 7 to 24 carbon atoms, and the functional group may contain at least one heteroatom selected from oxygen atoms, nitrogen atoms, and sulfur atoms. X represents a hydrogen atom, a hydroxyl group, an amino group, or a mercapto group. R １ and R ２ each independently represents a hydrogen atom, an alkyl group having 1 to 18 carbon atoms, a cycloalkyl group, or an aromatic ring, and the substituent may contain at least one heteroatom selected from an oxygen atom, a nitrogen atom, and a sulfur atom. z represents an integer of 1 to 3. The carbon black has a nitrogen adsorption specific surface area (N ２ SA) is 40m ２ / g or less, and an oil absorption (COAN) of a compressed sample is 60 ml / 100 g or more, and the oil content is 35 parts by mass or more and less than 45 parts by mass per 100 parts by mass of the rubber component.

2. 2. The rubber composition according to claim 1, wherein the hydrazide compound is 3-hydroxy-N'-(1,3-dimethylbutylidene)-2-naphthoic acid hydrazide.

3. 3. The rubber composition according to claim 1, wherein the bismaleimide compound is at least one selected from the group consisting of N,N'-1,2-phenylene bismaleimide, N,N'-1,3-phenylene bismaleimide, and N,N'-1,4-phenylene bismaleimide.

4. The rubber composition according to any one of claims 1 to 3, wherein the rubber component contains 90 mass % or more of natural rubber.

5. The rubber composition according to any one of claims 1 to 4, wherein the rubber composition does not contain silica as a filler.

6. The rubber composition according to any one of claims 1 to 5, further comprising less than 5 parts by mass of zinc oxide (ZnO) per 100 parts by mass of the rubber component.

7. A tire comprising the rubber composition according to any one of claims 1 to 6.

8. 8. The tire according to claim 7, wherein the rubber composition is used for at least one of a ply coating rubber, an inter-ply rubber, a belt coating rubber, an inter-belt cushion rubber, a belt end cover rubber, and a stiffener rubber.