Toothed belt

Abstract

To provide a toothed belt that is less prone to wear and deformation of a belt tooth and is also suitable for use under high load transmission.SOLUTION: A toothed belt has: a belt body having a flat strip-like back rubber part, and a plurality of tooth rubber parts disposed on an inner peripheral side of the back rubber part, with both the back rubber part and the tooth rubber part composed of a thermoplastic elastomer composition; a core wire containing a carbon filament; and a tooth part covering material that covers the tooth rubber part. The thermoplastic elastomer composition comprises an elastomer component that is a polyamide thermoplastic elastomer (TPAE) or a polyester thermoplastic elastomer (TPC), and also has predetermined hardness. The tooth part covering material is (a) a fabric treated with a binder, where the binder is filled into the fabric and also covers the surface of the fabric constituting the belt surface, or (b) a polyamide film.SELECTED DRAWING: Figure 1

Description

[Technical field]

[0001] The present invention relates to a toothed belt. [Background technology]

[0002] Conventionally, rubber belts and cast urethane belts are known as toothed belts. Both of these belts have a back rubber part, a number of toothed rubber parts integrally provided on the back rubber part at a predetermined pitch in the belt longitudinal direction, and a core wire embedded between the back rubber part and the toothed rubber part so as to extend in the belt longitudinal direction and at a predetermined pitch in the belt width direction. The difference between the two is whether the back rubber part and the toothed rubber part are molded from vulcanized rubber or from cast urethane.

[0003] These belts have low productivity because they require a vulcanization process and a post-vulcanization process in the manufacturing process. In addition, due to the nature of vulcanized rubber and cast urethane, these belts have problems in that post-processing such as shaping after belt formation is difficult, and recycling is also difficult.

[0004] As a toothed belt capable of solving such problems, a toothed belt in which the back rubber portion and the toothed rubber portion are made of a thermoplastic elastomer has been proposed (see, for example, Patent Documents 1 and 2). [Prior art documents] [Patent documents]

[0005] [Patent Document 1] Japanese Patent Application Publication No. 7-27178 [Patent Document 2] Japanese Patent Application Publication No. 10-2379 Summary of the Invention [Problem to be solved by the invention]

[0006] Toothed belts in which thermoplastic elastomers are used to form the back rubber portion and the tooth rubber portion have the problem that the belt teeth are easily deformed when the load on the belt increases.Furthermore, when the rotation speed of the pulley on which the belt is fastened increases, the belt generates heat, and in this case, the belt teeth are also easily deformed. In addition, toothed belts in which thermoplastic elastomers are used to form the back rubber portion and the tooth rubber portion have the problem that they are prone to wear if there is no tooth covering material, and even if they are provided with a tooth covering material, they are still prone to wear depending on the type of material. The deformation and wear of the rubber teeth can cause chipping of the belt teeth, which can lead to tooth skipping. [Means for solving the problem]

[0007] The present invention has been made in consideration of these problems, and has an object to provide a toothed belt that is capable of transmitting high loads and is less susceptible to wear and deformation of the belt teeth even when the rotational speed of the pulley is increased.

[0008] (1) The toothed belt of the present invention has a flat belt-shaped back rubber part, and a plurality of toothed rubber parts disposed on the inner circumferential side of the back rubber part and each of which is integrally formed with the back rubber part to constitute a tooth part, and the back rubber part and the toothed rubber part are both made of a thermoplastic elastomer composition. A belt main body; A core wire including a carbon filament is embedded in the inner peripheral portion of the back rubber portion so as to form a spiral having a pitch in the belt width direction; a tooth portion covering material provided on an inner peripheral side of the belt body and covering the plurality of tooth rubber portions; Equipped with The thermoplastic elastomer composition is Elastomer Component is a polyamide thermoplastic elastomer (TPAE) or a polyester thermoplastic elastomer (TPC), The hardness of the thermoplastic elastomer composition constituting the back rubber portion is 25 to 70, The hardness of the thermoplastic elastomer composition constituting the tooth rubber portion is 40 to 70, and is equal to or greater than the hardness of the thermoplastic elastomer composition constituting the back rubber portion; The tooth coating material is (a) A woven fabric treated with a binder, the binder being filled inside the woven fabric and also coating the surface of the woven fabric constituting the belt surface, or (b) a polyamide film; It is.

[0009] The back rubber part and the tooth rubber part of the toothed belt are made of a composition containing a polyamide thermoplastic elastomer (TPAE) or a polyester thermoplastic elastomer (TPC) as an elastomer component. Therefore, in the manufacturing process, a vulcanization process or a post-vulcanization process is not required, and productivity is excellent. In addition, the elastomer component is heat resistant, and the decrease in elastic modulus is small even at the heat generation temperature when the belt is driven under high load or at a high rotation speed. Therefore, deformation is unlikely to occur when the belt is driven, and problems such as tooth skipping caused by deformation of the tooth rubber part are unlikely to occur.

[0010] In addition, the thermoplastic elastomer compositions constituting the back rubber portion and the tooth rubber portion of the toothed belt each have a specific hardness. This prevents the belt from being too soft and deforming when subjected to power, causing chipping of teeth, or from being too hard and breaking when wound around a pulley, or from cracking the back surface of the belt when driven. Therefore, the toothed belt has a long belt life.

[0011] The toothed belt has a core wire including carbon filaments. The core wire containing carbon filaments has a high elastic modulus, so it is not easily deformed even when a high load is applied to the toothed belt, and it is difficult for the meshing with the pulley to shift. Therefore, it is possible to prevent the belt from riding on the pulley due to the meshing with the pulley being shifted, or to prevent the belt teeth from being chipped due to localized force being applied to the belt. In addition, the core wire containing carbon filaments does not have creep characteristics like organic fibers, so it is very difficult to stretch, and the tension of the belt is unlikely to decrease.

[0012] Furthermore, the toothed belt is provided with a tooth covering material made of a binder-treated fabric or polyamide film. The tooth covering material can restrain the thermoplastic elastomer composition constituting the tooth rubber portion and increase the rigidity of the belt teeth. Therefore, the belt teeth are less likely to deform even under high load transmission, and power can be transmitted. Furthermore, since the tooth coating material has a lower friction coefficient and excellent wear resistance compared to the thermoplastic elastomer composition, even if high surface pressure or slippage occurs on the tooth surface during high-load transmission, rapid wear can be avoided.

[0013] (2) In the toothed belt, the elastomer component is preferably a polyamide thermoplastic elastomer (TPAE). TPAE is more suitable than other thermoplastic elastomers as a material for the tooth rubber and back rubber parts of toothed belts because it has little energy loss due to dynamic deformation, generates little heat when bent, and has excellent chemical resistance.

[0014] (3) In the toothed belt, the tooth covering material is the woven fabric of (a) above, and the woven fabric is preferably a plain weave, a twill weave, or a satin weave. These woven fabrics have a small coefficient of friction and lubricity in wear particles, so they are resistant to wear. In addition, they are quiet because they easily absorb shock. Therefore, these woven fabrics are suitable as a tooth covering material for the toothed belt of the present invention.

[0015] (4) In the toothed belt, it is preferable that the woven fabric uses elastic yarn or crimped yarn as at least the yarn in the longitudinal direction of the belt. In this case, it is suitable to provide a tooth coating material that conforms to the shape of the inner peripheral surface of the toothed belt.

[0016] (5) In the toothed belt, the tooth covering material is the woven fabric (a) above, and the binder preferably contains a particulate wear modifier. In this case, the granular wear modifier reduces the friction coefficient of the belt tooth surface, and the frictional energy received by the belt tooth surface during belt drive can be reduced. Therefore, the toothed belt has a reduced wear rate and can reduce heat generation due to friction, and can suppress heat generation in the belt, thereby suppressing a decrease in the rigidity of the belt teeth. Therefore, the toothed belt is more suitable for preventing chipping of the belt teeth.

[0017] (6) In the toothed belt, the granular wear modifier is preferably at least one of ultra-high molecular weight polyethylene (UHMWPE) particles and PTFE (polytetrafluoroethylene) particles. These particulate wear modifiers are particularly suitable for use in the toothed belt of the present invention as particles for lowering the coefficient of friction on the surface of the belt teeth.

[0018] (7) It is preferable that the particulate wear modifier is exposed on the surface of the fabric constituting the belt surface by a total of 1 to 15%. In this case, it is more preferable that the adhesion between the tooth covering material and the thermoplastic elastomer composition constituting the tooth rubber portion is not inhibited while ensuring the effect of reducing wear of the belt teeth.

[0019] (8) In the above toothed belt, the tooth coating material is the polyamide film of (b) above, and it is preferable that the surface of the polyamide film constituting the belt surface or the inside including the surface contains a granular wear modifier. In this case, the granular wear modifier reduces the friction coefficient of the belt tooth surface, and the frictional energy received by the belt tooth surface during belt drive can be reduced. Therefore, the toothed belt can reduce the wear rate and heat generation due to friction, and the heat generation of the belt can be suppressed, so that the decrease in rigidity of the belt teeth can be suppressed. Therefore, the toothed belt is more suitable for preventing chipping of the belt teeth.

[0020] (9) In the toothed belt, the granular wear modifier is preferably at least one of ultra-high molecular weight polyethylene (UHMWPE) particles and PTFE (polytetrafluoroethylene) particles. These particulate wear modifiers are particularly suitable for use in the toothed belt of the present invention as particles for lowering the coefficient of friction on the surface of the belt teeth.

[0021] (10) In the toothed belt, the particulate wear modifier is preferably exposed to a total of 1 to 15% of the surface of the polyamide film constituting the belt surface. In this case, it is more preferable that the adhesion between the tooth covering material and the thermoplastic elastomer composition constituting the tooth rubber portion is not inhibited while ensuring the effect of reducing wear of the belt teeth. Effect of the Invention

[0022] According to the present invention, it is possible to provide a toothed belt in which the belt teeth are resistant to wear and deformation and which is capable of transmitting high loads. [Brief description of the drawings]

[0023] [Figure 1] FIG. 1 is a perspective view that shows a schematic view of a part of a toothed belt according to an embodiment of the present invention. [Diagram 2] FIG. 2 is a front view taken along an arrow X in FIG. [Diagram 3] FIG. 2 is an end view taken along line AA in FIG. [Figure 4] FIG. 2 is a partial cross-sectional view of a belt forming die used for manufacturing a toothed belt. [Diagram 5] 3A to 3C are diagrams illustrating a manufacturing process of a toothed belt. [Figure 6] 3A to 3C are diagrams illustrating a manufacturing process of a toothed belt. [Figure 7] 3A to 3C are diagrams illustrating a manufacturing process of a toothed belt. [Figure 8] FIG. 1 is a diagram showing a pulley layout in durability test 1. [Figure 9] FIG. 13 is a diagram showing a pulley layout in durability test 2. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0024] Hereinafter, embodiments of the present invention will be described with reference to the drawings, but the present invention is not limited to these embodiments. (First embodiment) Fig. 1 is a perspective view showing a part of a toothed belt 10 according to an embodiment of the present invention, Fig. 2 is a front view taken along an arrow X in Fig. 1, Fig. 3 is an end view taken along line AA in Fig. 1.

[0025] <Toothed belt> The toothed belt 10 is an endless intermeshing power transmission belt. FIG. 1 shows only a portion of the toothed belt 10. As shown in FIG. 1, the toothed belt 10 includes a belt body 11, a core wire 13, and a reinforcing cloth 14 as a tooth covering material.

[0026] The dimensions of the toothed belt 10 are not particularly limited and can be selected according to the design. The dimensions of the toothed belt 10 may be, for example, a belt circumference (belt length at the belt pitch line BL) of 54 mm to 6600 mm, a belt width of 3 mm to 340 mm, and a maximum belt thickness of 1.3 mm to 13.2 mm.

[0027] The toothed belt 10 has a plurality of belt teeth 12 arranged at a predetermined pitch on the inner periphery side. The belt teeth 12 have an S-tooth profile. In the embodiment of the present invention, the tooth profile of the belt teeth 12 is not limited to an S-shape, but may be a circular arc tooth profile other than an S-shape, a trapezoidal tooth profile, or another tooth profile.

[0028] In the toothed belt 10, the belt teeth 12 are straight teeth extending parallel to the belt width direction. In the embodiment of the present invention, the belt teeth 12 may be helical teeth extending in a direction inclined with respect to the belt width direction.

[0029] In the toothed belt 10, the tooth pitch P of the belt teeth 12 (see P in FIG. 3) is, for example, not less than 2 mm and not more than 20 mm. The tooth height of the belt teeth 12 is defined as the dimension from the tooth bottom 15 between a pair of adjacent belt teeth 12 in the belt length direction to the tip of the belt tooth 12 (see H in FIG. 3), and is, for example, 0.76 mm to 8.4 mm. The toothed belt 10 has a number of teeth of, for example, 27 to 560, a tooth width (dimension in the belt length direction) of, for example, 1.3 mm to 15.0 mm, and a PLD of, for example, 0.254 mm to 2.159 mm. These belt tooth dimensions are exemplary and are not limited to these ranges.

[0030] <Belt body> The belt body 11 has an endless flat band-shaped back rubber part 11a and multiple toothed rubber parts 11b. The multiple toothed rubber parts 11b are integrally provided at intervals in the belt length direction on the inner peripheral side, which is one side, of the back rubber part 11a. The back rubber part 11a and the toothed rubber parts 11b of the belt body 11 are each made of a thermoplastic elastomer composition. The thermoplastic elastomer composition constituting the back rubber portion 11a and the thermoplastic elastomer composition constituting the tooth rubber portion 11b may be the same as or different from each other.

[0031] In the present invention, the thermoplastic elastomer composition refers to a composition that contains a thermoplastic elastomer component as an essential component and various additives other than the elastomer component as optional components that can be contained as necessary. The thermoplastic elastomer composition may contain only the elastomer component.

[0032] The thermoplastic elastomer composition constituting the belt body 11 has an elastomer component of a polyamide thermoplastic elastomer (TPAE) or a polyester thermoplastic elastomer (TPC). TPAE and TPC are more heat resistant than other thermoplastic elastomers such as olefin, styrene, and urethane, and the decrease in elastic modulus is small even at high belt temperatures during high load driving or high speed rotation driving. Therefore, deformation of the tooth rubber due to heat generation of the belt during high load driving or high speed rotation driving is unlikely to occur.

[0033] The elastomer component is preferably a polyamide thermoplastic elastomer (TPAE). Compared to TPC, TPAE has less energy loss due to dynamic deformation and generates less heat due to bending. Therefore, the belt temperature during driving is relatively low, making it suitable for power transmission under high load and high speed. TPAE also has excellent chemical resistance, making it suitable for applications where contact with chemicals is anticipated, such as toothed belts used in industrial machines equipped with hydraulic devices, the drive parts of motorcycles, and electric seats in passenger cars.

[0034] The polyester-based thermoplastic elastomer (TPC) is a block copolymer that employs a polyester structure such as polybutylene terephthalate (PBT) as a hard segment and a polyether, polyester, or polycarbonate as a soft segment.

[0035] The polyamide-based thermoplastic elastomer (TPAE) is a block copolymer having polyamide (nylon) as a hard segment and polyol as a soft segment. Examples of the polyamide (nylon) include nylon 6, nylon 66, nylon 11, nylon 12, nylon 610, nylon 612, nylon 1212, and the like. Among these, nylon 11 and nylon 12 are preferred because they have a low amide bond content and are less susceptible to dimensional changes.

[0036] As the polyol, one or both of a polyester polyol and a polyether polyol can be used. Comparing polyester polyols with polyether polyols, polyether polyols are preferred because they tend to exhibit rubber elasticity at room temperature even without the inclusion of a plasticizer and are less likely to crack when the belt is bent. In addition, when polyether polyol is used as the polyol component of TPAE, it is not necessary to add a plasticizer, and in a toothed belt in which the tooth rubber portion and the back rubber portion are made of a thermoplastic elastomer composition that does not contain a plasticizer, the plasticizer does not volatilize and adhere to equipment or products, and therefore such a toothed belt can be suitably used in a clean room.

[0037] Examples of the polyester polyol include polyethylene adipate and polybutylene adipate. Examples of the polyether polyol include polytetramethylene ether glycol and polyoxypropylene glycol.

[0038] The polyester-based thermoplastic elastomer and the polyamide-based thermoplastic elastomer may each be a commercially available product. Examples of commercially available polyester thermoplastic elastomers include the Hytrel (registered trademark) series manufactured by DuPont-Toray Co., Ltd. Examples of commercially available polyamide-based thermoplastic elastomers include the PEBAX (registered trademark) series manufactured by Arkema, the VESTAMID (registered trademark) series and DIAMID (registered trademark) series manufactured by Daicel-Evonik, and the Grillflex (registered trademark) series manufactured by EMS.

[0039] The thermoplastic elastomer composition constituting the back rubber portion 11a and the tooth rubber portion 11b may contain, in addition to the TPAE or TPC elastomer components, additives such as short fibers, whiskers, fillers, colorants, antistatic agents, flame retardants, antioxidants, UV absorbers, light stabilizers, hydrolysis inhibitors, plasticizers, lubricants, preservatives, anti-fungal agents, solid lubricants, lubricating oils, and greases, as necessary.

[0040] On the other hand, when these additives are contained, they may come off from the back rubber portion 11a and the toothed rubber portion 11b and contaminate the environment in which they are used. Therefore, when the toothed belt 10 is a toothed belt used in, for example, a clean room, it is preferable that the thermoplastic elastomer composition does not contain the additives and is composed of only the elastomer component.

[0041] In the belt body 11, the hardness of the thermoplastic elastomer composition constituting the back rubber part 11a is 25 to 70. The hardness of the thermoplastic elastomer composition constituting the tooth rubber part 11b is 40 to 70. In addition, the hardness of the thermoplastic elastomer composition constituting the back rubber part 11a is equal to or lower than the hardness of the thermoplastic elastomer composition constituting the tooth rubber part 11b.

[0042] Hereinafter, in this specification, the hardness of the thermoplastic elastomer composition constituting the back rubber portion will be simply referred to as the "back rubber portion hardness", and the hardness of the thermoplastic elastomer composition constituting the tooth rubber portion will be simply referred to as the "tooth rubber portion hardness".

[0043] In a toothed belt having such a configuration, the hardness of the back rubber part is within the above range and is less than the hardness of the tooth rubber part, so that the belt is prevented from being broken when wound around a pulley, and from cracking the back surface of the belt when driven. Also, since the hardness of the tooth rubber part is greater than or equal to the hardness of the back rubber part and within the above range, the belt teeth are less likely to wear during use, and deformation of the belt teeth is less likely to occur. The hardness of the thermoplastic elastomer composition constituting the back rubber portion 11a may be less than the hardness of the thermoplastic elastomer composition constituting the tooth rubber portion 11b.

[0044] The hardness of the thermoplastic elastomer composition is measured at 23° C. using a type D durometer in accordance with the provisions of JIS K6253-3. This hardness is also called Shore D hardness.

[0045] The difference between the hardness of the back rubber portion and the hardness of the tooth rubber portion is preferably at least 5, and more preferably at least 10. This is more suitable for suppressing the occurrence of back cracks.

[0046] The hardness of the back rubber portion is determined by the hardness of the thermoplastic elastomer contained in the thermoplastic elastomer composition constituting the back rubber portion. Elastomer Component The molecular weight of the hard segment and the soft segment, the ratio of the hard segment and the soft segment contained in the thermoplastic elastomer composition Elastomer Component It can be controlled by adjusting the type and amount of additives other than the above. The hardness of the tooth rubber portion is also determined by the hardness of the thermoplastic elastomer contained in the thermoplastic elastomer composition constituting the tooth rubber portion. Elastomer Component or Elastomer Component The amount of the oxidized carbon can be controlled by additives other than the above.

[0047] <Core wire> The core wire 13 is embedded in the inner peripheral portion of the back rubber portion 11a of the belt body 11 so as to form a spiral having a pitch in the belt width direction. The outer diameter of the core wire 13 is, for example, not less than 0.45 mm and not more than 3.0 mm. The pitch of the core wires 13 (the arrangement pitch in the belt width direction) is, for example, not less than 0.5 mm and not more than 4.0 mm.

[0048] The core wire 13 includes a large number of filaments which are twisted together. The way in which the core wire 13 is twisted is not particularly limited, and may be a single twist consisting of one twist layer, a ply twist or Lang twist having two twist layers, or a twist having three twist layers.

[0049] All or some of the filaments contained in the core wire 13 are carbon filaments made of carbon fibers. The carbon filaments have a filament diameter of, for example, 5 μm or more and 7 μm or less. The number of carbon filaments included in the core wire 13 is, for example, 3000 or more. There is no particular upper limit to the number of the filaments, and it is, for example, 96000.

[0050] Examples of carbon filaments include PAN-based carbon filaments and pitch-based carbon filaments. PAN-based carbon filaments are preferred as carbon filaments because of their flexibility.

[0051] In the toothed belt 10, the core wire 13 may contain filaments made of other fibers in addition to the carbon filaments. Examples of the other fibers include inorganic fibers such as glass fibers and metal fibers, and organic fibers such as aramid fibers, polyester fibers, PBO fibers, nylon fibers, and polyketone fibers. When the core wire 13 contains carbon filaments and filaments made of other fibers as its constituent materials, the proportion of the carbon filaments to the total filaments is 50% by mass or more. The higher the proportion of the carbon filaments, the more preferable it is (for example, 90% by mass or more).

[0052] As described above, the core wire 13 includes carbon filaments. Since the elastic modulus of carbon filaments is high, the toothed belt 10 having the core wire 13 is less likely to deform even when a high load is applied, and is less likely to slip out of mesh with the pulley. This makes it possible to prevent the toothed belt 10 from riding up onto the pulley due to a slip in mesh between the toothed belt 10 and the pulley, or to prevent the belt teeth 12 from being chipped due to a local force being applied to the toothed belt 10. In addition, since carbon filaments do not have creep characteristics like filaments made of organic fibers, the toothed belt 10 is very unlikely to stretch, and tension loss in the toothed belt 10 is unlikely to occur.

[0053] In the toothed belt 10, the core wire 13 may have each filament contained in the core wire 13 covered with a converging coating layer made of a converging agent, or a plurality of twisted filaments may be covered with an adhesive coating layer made of an adhesive. Examples of the binder and adhesive include an emulsion in which an epoxy group-containing compound and a curing agent are dispersed in water, an aqueous solution containing an initial condensation product of resorcinol and formaldehyde (also referred to as an RF liquid), and an aqueous solution containing an initial condensation product of resorcinol and formaldehyde and latex (also referred to as an RFL liquid).

[0054] In the toothed belt 10, the core wire 13 may be formed of two types of yarn, an S twisted yarn and a Z twisted yarn, arranged in a double spiral shape so that they are alternately arranged in the belt width direction. This is suitable for preventing the toothed belt 10 from shifting to one side while running. The core wire 13 may be made up of only S twisted yarns or only Z twisted yarns.

[0055] <Reinforcing fabric> The reinforcing cloth 14 is applied so as to cover the inner peripheral surface on which the multiple toothed rubber portions 11b of the belt body 11 are provided. Therefore, the toothed rubber portions 11b of each belt tooth 12 are covered with the reinforcing cloth 14. This makes it possible to prevent the thermoplastic elastomer composition constituting the tooth rubber portion from coming into direct contact with the pulley.

[0056] The reinforcing fabric 14 is a woven fabric treated with a binder. The weaving method (textile) of the woven fabric is, for example, a plain weave, a twill weave, a satin weave, or the like. The woven fabric has threads aligned along the longitudinal direction of the belt, and it is preferable that at least the threads in the longitudinal direction of the belt are elastic threads or threads that have been subjected to a crimping process. In this case, it is suitable to make the tooth covering material conform to the shape of the tooth rubber portion on the inner peripheral surface of the toothed belt. The thickness of the reinforcing fabric 14 is, for example, not less than 0.1 mm and not more than 2.5 mm.

[0057] Examples of the elastic yarn include polyurethane elastic yarn and yarn in which a polyurethane elastic yarn is used as a core yarn and is covered with a covering yarn. Examples of the crimped yarn include yarns obtained by false twisting (woolly processing) polyamide fibers (nylon fibers), polyester fibers, and the like.

[0058] The binder is a treatment agent for enhancing adhesion between the reinforcing fabric 14 and the thermoplastic elastomer composition constituting the tooth rubber portion. Examples of the binder include RF aqueous solution, RFL aqueous solution, emulsion in which an epoxy group-containing compound and a curing agent are dispersed in water, rubber adhesive, etc. Examples of the rubber adhesive include Chemlock (registered trademark) manufactured by Lord Corporation.

[0059] The RF aqueous solution is an aqueous solution of an initial condensation product of resorcinol and formaldehyde. The molar ratio (R / F) of the initial condensation product (RF) of resorcinol (R) and formaldehyde (F) in the RF aqueous solution is, for example, 1 / 3 to 1 / 0.5.

[0060] The RFL aqueous solution is an aqueous solution obtained by mixing a precondensation product of resorcinol and formaldehyde with latex. Examples of the latex include vinylpyridine-styrene-butadiene rubber latex (VP-SBR), styrene-butadiene rubber latex (SBR), natural rubber latex (NR), chloroprene rubber latex (CR), chlorosulfonated polyethylene rubber latex (CSM), 2,3-dichlorobutadiene rubber latex (2,3-DCB), hydrogenated nitrile rubber latex (H-NBR), carboxylated hydrogenated nitrile rubber latex, butadiene rubber latex (BR), nitrile rubber latex (NBR), etc. The latex preferably contains one or more of these.

[0061] The solid content concentration, which is the sum of the content of the initial condensate of resorcin and formaldehyde and the content of the solid content derived from the latex in the RFL aqueous solution, is, for example, from 10% by mass to 30% by mass. Regarding the initial condensation product (RF) of resorcin (R) and formaldehyde (F) in the RFL aqueous solution, the molar ratio (R / F) of resorcin (R) to formalin (F) is, for example, 1 / 3 to 1 / 0.5. The mass ratio (RF / L) of the initial condensation product (RF) of resorcin (R) and formaldehyde (F) in the RFL aqueous solution to the solid content (L) derived from the latex is, for example, 1 / 20 to 1 / 0, and preferably about 1 / 15.

[0062] When the binder is an RF aqueous solution or an RFL aqueous solution, the treatment with the binder can be carried out by immersing the fabric in the RF aqueous solution or the RFL aqueous solution and then heating it. The above-mentioned woven fabric may be subjected to a surface preparation treatment by immersing it in an epoxy solution or an isocyanate solution and then heating it, prior to the treatment with the RF aqueous solution or the RFL aqueous solution. In the fabric treated with the binder, the binder is filled inside the fabric and also covers the surface of the fabric.

[0063] The reinforcing fabric 14, in which the binder is filled inside the fabric and also covers the surface of the fabric that constitutes the belt surface, can be formed, for example, by immersing the fabric in the RF aqueous solution or the RFL aqueous solution.

[0064] The binder preferably contains a particulate wear modifier, which provides the reinforcing fabric 14 with a lower coefficient of friction. Examples of materials for the granular wear modifier include fluororesins such as polytetrafluoroethylene (PTFE), perfluoroalkoxyalkane (PFA), perfluoroethylenepropene copolymer (FEP), ethylene-tetrafluoroethylene copolymer (ETFE), and polyvinylidene fluoride (PVDF), and ultra-high molecular weight polyethylene (UHMWPE) having a weight average molecular weight of 1,000,000 or more. The particulate wear modifiers made of these materials may be used alone or in combination of two or more kinds.

[0065] More preferably, the binder contains at least one of ultra-high molecular weight polyethylene (UHMWPE) particles and polytetrafluoroethylene (PTFE) particles as the particulate wear modifier, which acts as a wear modifier and provides the reinforcing fabric 14 with a lower coefficient of friction. By incorporating these particles and reducing the coefficient of friction of the reinforcing fabric 14, the above-mentioned effects can be obtained.

[0066] The weight-average molecular weight of the UHMWPE constituting the ultra-high molecular weight polyethylene particles is preferably 1.1 million to 3.3 million. If the weight-average molecular weight of the UHMWPE is less than 1.1 million, the UHMWPE particles may melt and disappear due to frictional heat between the tooth rubber part and the pulley during use. On the other hand, if the weight-average molecular weight of the UHMWPE is more than 3.3 million, some UHMWPE particles may break due to impact during use, and sufficient friction coefficient reduction effect may not be obtained.

[0067] The average particle size of the UHMWPE particles is preferably 10 to 65 μm. If the average particle size is less than 10 μm, the amount of the UHMWPE particles exposed on the belt tooth surface is small, and the effect of adhering the binder to the surface of the fabric may be poor, whereas if the average particle size is more than 65 μm, the particles may fall off from the belt surface during use. The average particle size of the UHMWPE particles is a value measured by a laser diffraction type particle size distribution measuring device. As the UHMWPE particles, commercially available products may be used.

[0068] The average particle size of the PTFE particles is preferably 10 to 30 μm. If the average particle size is less than 10 μm, the amount of the PTFE particles exposed on the belt tooth surface is small, and the effect of adhering the binder to the surface of the fabric may be poor, whereas if the average particle size is more than 30 μm, the PTFE particles may fall off from the belt surface during use. The average particle size of the PTFE particles is a value measured by a laser diffraction type particle size distribution measuring device. The PTFE particles may be commercially available products, such as Fluon (registered trademark) PTFE L150J and Fluon PTFE L169J manufactured by AGC, and Algoflon (registered trademark) L100 manufactured by Solvey.

[0069] The particulate wear modifier is preferably exposed on the surface of the fabric constituting the belt surface by a total of 1 to 15%. If the amount of exposure on the belt surface is less than 1%, the effect of lowering the friction coefficient of the belt tooth surface is poor, whereas if the amount of exposure exceeds 15%, the adhesion between the tooth coating material and the thermoplastic elastomer composition constituting the tooth rubber portion may be inhibited by the granular wear modifier present between them.

[0070] The amount (%) of exposed particulate wear modifier on the belt surface was determined by observing the surface of the fabric under an optical microscope and calculating the ratio of the area occupied by the particulate wear modifier to the area of ​​the fabric surface.

[0071] The amount of exposed particulate wear modifier on the belt surface can be adjusted by changing the concentration of the particulate wear modifier contained in the binder, the viscosity of the binder when treating the woven fabric, etc. It can also be adjusted by polishing the surface of the woven fabric that constitutes the belt surface after treatment with the binder.

[0072] Second embodiment The toothed belt according to this embodiment differs from the toothed belt according to the first embodiment in the configuration of the reinforcing fabric. The reinforcing fabric of the toothed belt of this embodiment is a polyamide film (nylon film). The reinforcing fabric made of polyamide film also has a low coefficient of friction, so frictional energy is small and the belt teeth are less likely to be worn. In addition, since the polyamide film has a high melting point, even if the temperature of the contact portion with the pulley rises, the polyamide film is unlikely to melt and undergo rapid wear.

[0073] Examples of polyamide (nylon) constituting the polyamide film include nylon 6, nylon 66, nylon 11, nylon 12, nylon 610, nylon 612, nylon 1212, and nylon 6T.

[0074] The polyamide film may be composed of only polyamide, but may also contain other components. In particular, it is preferable that the reinforcing fabric contains a particulate wear modifier as another component, since the particulate wear modifier can be contained to further reduce the coefficient of friction of the reinforcing fabric. Specific examples of the material of the particulate wear modifier are as exemplified in the description of embodiment 1. The particulate wear modifier may be used alone or in combination of two or more types.

[0075] The polyamide film preferably contains at least one of ultra-high molecular weight polyethylene (UHMWPE) particles and polytetrafluoroethylene (PTFE) particles, which are particularly suitable for lowering the coefficient of friction of the polyamide film. By incorporating these particles and reducing the coefficient of friction of the reinforcing fabric (coefficient of friction on the belt tooth surface), the above-mentioned effects can be obtained.

[0076] When the polyamide film as the reinforcing fabric contains UHMWPE particles, suitable examples of the particles (weight average molecular weight and average particle size) include those similar to the UHMWPE particles that can be contained in the binder in the toothed belt of the first embodiment.

[0077] When the polyamide film serving as the reinforcing fabric contains PTFE particles, suitable examples of the particles (average particle size) include the same PTFE particles that can be contained in the binder in the toothed belt of the first embodiment.

[0078] When the polyamide film contains a granular wear modifier, it is preferable that the granular wear modifier is dispersed throughout the polyamide film, or a layer of the granular wear modifier is formed on the surface of the polyamide film. In the latter case, the layer of the granular wear modifier may be formed, for example, by spraying a dispersion containing the granular wear modifier and then removing the dispersion medium. In addition, the layer of the granular wear modifier may be formed by applying the granular wear modifier to the surface of the mold in advance and transferring it during belt molding.

[0079] Furthermore, the amount of the particulate wear modifier contained in the polyamide film is preferably an amount such that 1 to 15% in total of the particulate wear modifier is exposed on the surface of the polyamide film constituting the belt surface. If the amount of exposure on the belt surface is less than 1%, the effect of lowering the friction coefficient of the belt tooth surface is poor, whereas if the amount of exposure exceeds 15%, and if the particulate wear modifier is dispersed throughout the polyamide film, the adhesion between the tooth coating material and the thermoplastic elastomer composition constituting the tooth rubber portion may be inhibited by the particulate wear modifier present between them.

[0080] The method for calculating the amount of exposed particulate wear modifier on the belt surface is the same as when the reinforcing fabric is made of woven fabric.

[0081] The amount of exposed particulate abrasion modifier on the surface of the polyamide film can be adjusted by changing the concentration or dispersion state of the particulate abrasion modifier, etc. It can also be adjusted by polishing the surface of the resin film.

[0082] The polyamide film may contain additives other than the particulate wear modifier, such as fillers, colorants, antistatic agents, flame retardants, antioxidants, UV absorbers, light stabilizers, hydrolysis inhibitors, plasticizers, lubricants, preservatives, and fungicides.

[0083] Next, an example of a method for manufacturing the toothed belt according to the present embodiment will be described. The toothed belt of the first embodiment and the toothed belt of the second embodiment can be manufactured by the same method except that the reinforcing fabric used is different.

[0084] Here, an example of the manufacturing method will be described with reference to FIGS. Fig. 4 is a partial cross-sectional view of a belt forming mold used in the method for producing a toothed belt. Figs. 5 to 7 are diagrams illustrating the production steps of the production method. The manufacturing method includes a material preparation step, a lamination step, a molding step, and a finishing step.

[0085] <Material preparation process> <Elastomer sheet> A thermoplastic elastomer sheet for the back rubber and a thermoplastic elastomer sheet for the teeth rubber are prepared. Each elastomer sheet is obtained by preparing a thermoplastic elastomer composition containing, for example, TPAE or TPC as an elastomer component and necessary additives, and molding it into a sheet by extrusion molding or the like. The thermoplastic elastomer sheet for the back rubber portion and the thermoplastic elastomer sheet for the tooth rubber portion may be molded by co-extrusion, in which case a laminate of the thermoplastic elastomer sheet for the back rubber portion and the thermoplastic elastomer sheet for the tooth rubber portion is obtained. The elastomer sheet formed in this step may be temporarily wound up, or may be directly supplied to the next step.

[0086] <Reinforcing Fabric> A reinforcing fabric (tooth covering material) having a tooth shape corresponding to the shape of the belt teeth is prepared. (1) When the reinforcing fabric 14 is a woven fabric treated with a binder First, the fabric is subjected to a binder treatment so that the interior of the fabric is filled with the binder, and the surface of the fabric constituting the belt surface is also coated with the binder. Next, the binder-treated fabric is aligned over a heated mold that has recesses shaped like the teeth of the belt, and a soft elastic body is pressed against the fabric from the side opposite the mold, forming the fabric into the shape of the teeth. The toothed fabric may then be formed into a tubular shape.

[0087] (2) When the reinforcing fabric 14 is a polyamide film The polyamide film is shaped into the toothed shape by aligning it with a heated mold having recesses with the same shape as the teeth of the belt and pressing a soft elastic body against it from the side opposite the mold. Alternatively, after extruding a polyamide film by extrusion molding, it is passed between two rolls having teeth that are the same shape as the teeth of the belt, forming teeth in the polyamide film while cooling, thereby producing a polyamide film with teeth. Alternatively, a polyamide film with a toothed profile is produced by passing the polyamide film between two rolls having heated toothed profiles. The toothed polyamide film may then be formed into a cylindrical shape.

[0088] <Core wire> The carbon filaments are twisted in a predetermined manner, adhesively treated, etc. to prepare the core wire 13. Here, it is preferable to prepare a pair of core wires, an S-twisted core wire and a Z-twisted core wire.

[0089] <Lamination process> FIG. 4 is a partial cross-sectional view showing a part of the belt forming die 30. As shown in FIG. The belt forming die 30 is cylindrical and has an outer circumferential surface on which a plurality of teeth forming grooves 31 are formed and spaced apart in the circumferential direction so as to extend in the axial direction.

[0090] As shown in FIG. 5, a cylindrical reinforcing cloth 14 having teeth is placed on the outer circumferential surface of a belt forming mold 30, and a pair of core wires 13 is wound around the reinforcing cloth 14 in a spiral shape. Then, a thermoplastic elastomer sheet 11b' for the tooth rubber portion and a thermoplastic elastomer sheet 11a' for the back rubber portion are wound on top of it in this order. The number of layers of each sheet that is wound may be one layer or two or more layers depending on the size of the belt to be produced. Furthermore, release paper or release film (not shown) is wrapped around it as necessary. As a result, a laminate S′ is formed on the belt forming die 30 .

[0091] <Forming process> The laminate S' is covered with a jacket having a rubber sleeve 32 on its inner surface and a sealed space between the rubber sleeve 32 and the main body. As a result, the rubber sleeve 32 is placed over the laminate S' on the belt mold 30, as shown in FIG. High pressure steam is introduced into the interior of the mold 30 around which the laminate S' is wound and into the space in the jacket to heat and compress it. This causes the thermoplastic elastomer constituting the thermoplastic elastomer sheets 11a', 11b' to pass through the gaps between the core wires and flow into the tooth forming grooves 31, forming the belt teeth 12 as shown in FIG. In this case, the temperature of the high-pressure steam is set to a temperature at which the thermoplastic elastomer flows or higher. If the elastomer component of the thermoplastic elastomer sheet is TPAE, the temperature of the high-pressure steam is set to 170°C or higher.

[0092] After the belt teeth 12 are formed, the jacket and mold 30 are cooled with water or the like to reduce the temperature of the elastomer to 100°C or less, and then the mold 30 and the molded body S are removed from the jacket. If the temperature of the molded body S is still 40°C or higher, it is further cooled, and when the temperature of the molded body S drops below 40°C, the molded body S is removed from the mold 30.

[0093] <Finishing process> The molded body is taken out and cut to a specified width to separate it, thereby producing a toothed belt. Through these steps, the toothed belt 10 can be manufactured.

[0094] <Other> In addition, if the hardness of the thermoplastic elastomer sheet 11b' for the toothed rubber portion and the thermoplastic elastomer sheet 11a' for the back rubber portion are different, the reinforcing fabric 14, the core wires 13, and the thermoplastic elastomer sheet 11b' for the toothed rubber portion can be laminated on the outer peripheral surface of the belt molding die 30, and then the belt teeth can be formed by heating and compressing with high-pressure steam as described above. After cooling once, the thermoplastic elastomer sheet 11a' for the back rubber portion can be wrapped around it, and then heated and compressed with high-pressure steam again, and then cooled again, and finally a finishing process can be performed to produce a toothed belt. EXAMPLES

[0095] The present invention will be described in more detail below with reference to examples, but the present invention is not limited to the following examples.

[0096] <Examples and Comparative Examples> Here, a toothed belt with a tooth type of S8M was produced and its performance was evaluated. Each toothed belt was produced using the manufacturing method already described above. The thermoplastic elastomer composition, core wires, and reinforcing fabric for forming the belt body (back rubber portion and tooth rubber portion) were prepared as follows.

[0097] (Thermoplastic elastomer composition) The following thermoplastic elastomer compositions were prepared. All of the thermoplastic elastomer compositions were commercially available products.

[0098] TPAE1: Polyamide-based thermoplastic elastomer composition PEBAX® 4033SP-01 manufactured by Arkema was used. This thermoplastic elastomer composition has a hardness of 42.

[0099] TPAE2: Polyamide-based thermoplastic elastomer composition PEBAX® 5533SP-01 manufactured by Arkema was used. This thermoplastic elastomer composition has a hardness of 54. PEBAX uses polyol as the soft segment.

[0100] TPC: Thermoplastic polyester elastomer The thermoplastic elastomer composition used was Hytrel (registered trademark) 5557 manufactured by DuPont-Toray Co., Ltd. The hardness of this thermoplastic elastomer composition is 53. Hytrel uses polyol as the soft segment.

[0101] TPO: Thermoplastic polyolefin elastomer Thermorun (registered trademark) QT85KB manufactured by Mitsubishi Chemical Corporation was used. The hardness of this thermoplastic elastomer composition is 31.

[0102] TPS: Thermoplastic polystyrene elastomer The thermoplastic elastomer composition used was Rabalon (registered trademark) QE548AE manufactured by Mitsubishi Chemical Corporation. The hardness of this thermoplastic elastomer composition is 42.

[0103] TPU: Thermoplastic polyurethane elastomer The thermoplastic elastomer composition used was Miractoran (registered trademark) E490 manufactured by Nippon Miractoran Co., Ltd. The hardness of this thermoplastic elastomer composition is 43.

[0104] (Core) An S-twisted yarn and a Z-twisted yarn were prepared using a carbon core wire (manufactured by Teijin Tenax Co., Ltd., filament diameter 7 μm, number of filaments 12,000). This core wire is a single-twisted yarn with a core wire diameter of 0.95 mm and is treated with an adhesive.

[0105] (Reinforcing fabric) As the tooth covering materials, reinforcing fabrics A0 to A11 made of woven fabric and reinforcing fabrics B0 to B9 made of resin film were prepared. The details are as follows.

[0106] Reinforcement fabric A0: Woven fabric without binder treatment The warp threads are 6,6-nylon fiber, the weft threads are 6,6-nylon fiber woolly processed yarn, and the fabric has a 2 / 2 twill weave.

[0107] Reinforcement fabric A1: Binder-treated woven fabric A fabric was prepared in which the warp yarn was 6,6-nylon fiber and the weft yarn was a woolly processed yarn of 6,6-nylon fiber, with a 2 / 2 twill weave. Separately, an RFL aqueous solution (latex is vinylpyridine-styrene-butadiene rubber latex) was prepared. The solids concentration of this RFL aqueous solution, which is the sum of the contents of the initial condensation product of resorcin and formaldehyde and the solids derived from the latex, was set to 10 mass%. In addition, the molar ratio (R / F) of resorcin (R) to formalin (F) of the above RFL aqueous solution was set to 1 / 1.2, and the mass ratio (RF / L) of the initial condensation product (RF) of resorcin (R) and formaldehyde (F) to the solids derived from the latex (L) was set to 1 / 15. The fabric was immersed in the RFL aqueous solution, and then heat-treated after being removed from the solution, with the immersion time set to 20 seconds, the heating temperature set to 150° C., and the heating time set to 5 minutes.

[0108] Reinforcement fabrics A2 to A5: Binder-treated woven fabrics Reinforcing fabrics A2 to A5 were produced in the same manner as reinforcing fabric A1, except that an RFL aqueous solution containing a predetermined amount of UHMWPE particles (Mipelon XM-220, manufactured by Mitsui Chemicals, Inc.) was used as the RFL aqueous solution. The concentrations of UHMWPE particles in the RFL aqueous solutions used to produce reinforcing fabrics A2 to A5 are as follows: Reinforcement fabric A2: 5% by mass Reinforcement fabric A3: 15% by mass Reinforcement fabric A4: 60% by mass Reinforcement fabric A5: 80% by mass

[0109] Reinforcement fabrics A6 to A9: Binder-treated woven fabrics Reinforcing fabrics A6 to A9 were produced in the same manner as reinforcing fabric A1, except that an RFL aqueous solution containing a predetermined amount of PTFE particles (FluonPTFE L150J, manufactured by AGC) was used as the RFL aqueous solution. The concentrations of PTFE particles in the RFL aqueous solutions used to produce reinforcing fabrics A6 to A9 are as follows: Reinforcement fabric A6: 5% by mass Reinforcement fabric A7: 15% by mass Reinforcement fabric A8: 60% by mass Reinforcement fabric A9: 80% by mass

[0110] Reinforcement fabric A10: Binder-treated woven fabric Reinforcing fabric A10 was produced in the same manner as reinforcing fabric A1, except that the fabric used had a 2 / 2 plain weave with a warp thread of 6,6-nylon fiber and a weft thread of woolly processed 6,6-nylon fiber.

[0111] Reinforcement fabric A11: Binder-treated woven fabric Reinforcing fabric A11 was produced in the same manner as reinforcing fabric A1, except that the warp yarn was 6,6-nylon fiber, the weft yarn was 6,6-nylon fiber woolly processed yarn, and the weft had a five-ply satin weave.

[0112] Reinforcement fabric B0: Low density polyethylene film A film (thickness: 0.75 mm) made of LLDPE (Linear Low Density Polyethylene) was prepared.

[0113] Reinforcement fabric B1: Polyamide film As the polyamide film, a 0.65 mm thick film made of Leona 1500 manufactured by Asahi Kasei Corporation was prepared.

[0114] Reinforcing fabric B2 to B5: Polyamide film A polyamide resin composition prepared by blending a predetermined amount of UHMWPE particles (Mipelon XM-220) with Leona 1500 was extruded into a sheet to produce a polyamide film having a thickness of 0.65 mm. The concentrations (mass%) of UHMWPE particles in the polyamide resin composition used to produce each of reinforcing fabrics B2 to B5 are as follows. In the production of reinforcing fabrics B4 and B5, the surface of the obtained sheet was polished after extrusion to adjust the amount of exposed UHMWPE particles. Reinforcement fabric B2: 5% by mass Reinforcement fabric B3: 15% by mass Reinforcement fabric B4: 20% by mass Reinforcement fabric B5: 30% by mass

[0115] Reinforcing fabric B6 to B9: Polyamide film A polyamide resin composition prepared by blending a predetermined amount of PTFE particles (FluonPTFE L150J) with Leona 1500 was extruded into a sheet to produce a polyamide film having a thickness of 0.65 mm. The concentrations (mass%) of PTFE particles in the polyamide resin composition used to produce each of reinforcing fabrics B6 to B9 are as follows. In the production of reinforcing fabrics B8 and B9, the surface of the obtained sheet was polished after extrusion to adjust the amount of exposed PTFE particles. Reinforcement fabric B6: 5% by mass Reinforcement fabric B7: 15% by mass Reinforcement fabric B8: 20% by mass Reinforcement fabric B9: 30% by mass

[0116] (Example 1-1) A toothed belt with a tooth type of S8M was manufactured by the above-mentioned manufacturing method (see Figs. 4 to 7) using the above-mentioned TPAE1 as the thermoplastic elastomer composition for the back rubber part, the above-mentioned TPAE2 as the thermoplastic elastomer composition for the tooth rubber part, the above-mentioned carbon core wire as the core wire, and the above-mentioned reinforcing cloth A1 as the reinforcing cloth. The belt width was 8 mm, and the belt length was 1200 mm. Here, the reinforcing fabric A1 was used so that the weft yarn direction was aligned along the longitudinal direction of the belt.

[0117] (Example 1-2) A toothed belt was produced in the same manner as in Example 1-1, except that the above TPC was used as the thermoplastic elastomer composition for the back rubber portion and the thermoplastic elastomer composition for the tooth rubber portion.

[0118] (Examples 1-3) A toothed belt was produced in the same manner as in Example 1-1, except that the reinforcing fabric A10 was used as the reinforcing fabric.

[0119] (Examples 1 to 4) A toothed belt was produced in the same manner as in Example 1-1, except that the reinforcing fabric A11 was used as the reinforcing fabric.

[0120] Example 2 A toothed belt was produced in the same manner as in Example 1-1, except that the reinforcing fabric B1 was used as the reinforcing fabric.

[0121] Comparative Example 1 A toothed belt was produced in the same manner as in Example 1-1, except that the reinforcing fabric A0 was used as the reinforcing fabric.

[0122] Comparative Example 2 A toothed belt was produced in the same manner as in Example 1-1, except that the reinforcing fabric B0 was used as the reinforcing fabric.

[0123] Comparative Example 3 A toothed belt was produced in the same manner as in Example 1-1, except that no reinforcing fabric was used.

[0124] Comparative Example 4 A toothed belt was produced in the same manner as in Example 1-1, except that the above TPO was used as the thermoplastic elastomer composition for the back rubber portion and the thermoplastic elastomer composition for the tooth rubber portion.

[0125] Comparative Example 5 A toothed belt was produced in the same manner as in Example 1-1, except that the above TPS was used as the thermoplastic elastomer composition for the back rubber portion and the thermoplastic elastomer composition for the tooth rubber portion.

[0126] Comparative Example 6 A toothed belt was produced in the same manner as in Example 1-1, except that the above TPU was used as the thermoplastic elastomer composition for the back rubber portion and the thermoplastic elastomer composition for the tooth rubber portion.

[0127] (Examples 3-1 to 3-4) Toothed belts were produced in the same manner as in Example 1-1, except that each of the reinforcing fabrics A2 to A5 was used as the reinforcing fabric. In the toothed belt produced in this example, the amount of exposed UHMWPE particles on the belt surface (surface of the reinforcing fabric) was measured by the method described above. The results are shown in Table 2.

[0128] (Examples 4-1 to 4-4) Toothed belts were produced in the same manner as in Example 1-1, except that each of the reinforcing fabrics A6 to A9 was used as the reinforcing fabric. In the toothed belt produced in this example, the amount of exposed PTFE particles on the belt surface (surface of the reinforcing fabric) was measured by the method described above. The results are shown in Table 2.

[0129] (Examples 5-1 to 5-4) Toothed belts were produced in the same manner as in Example 2, except that each of the reinforcing fabrics B2 to B5 was used as the reinforcing fabric. In the toothed belt produced in this example, the amount of exposed UHMWPE particles on the belt surface (surface of the reinforcing fabric) was measured by the method described above. The results are shown in Table 3.

[0130] (Examples 6-1 to 6-4) Toothed belts were produced in the same manner as in Example 2, except that each of the reinforcing fabrics B6 to B9 was used as the reinforcing fabric. In the toothed belt produced in this example, the amount of exposed PTFE particles on the belt surface (surface of the reinforcing fabric) was measured by the method described above. The results are shown in Table 3.

[0131] (Evaluation method) The toothed belts manufactured in the examples and comparative examples were subjected to durability tests 1 and 2 to evaluate their durability. The results are shown in the table.

[0132] <Durability test 1> Durability test 1 is a test for evaluating durability under standard running conditions, and was carried out on the toothed belts produced in Examples 1-1 to 1-4, Example 2, and Comparative Examples 1 to 6. FIG. 8 shows a belt running test machine 80 used in the durability test 1. The belt running tester 80 includes a drive pulley 81 with 22 teeth and a tooth profile of 8M, and a driven pulley 82 with 33 teeth and a tooth profile of 8M provided on the right side of the drive pulley 81. The driven pulley 82 is provided so as to be movable left and right so that an axial load (dead weight) can be applied.

[0133] The toothed belt 110 manufactured in the specific examples and comparative examples was wound around the driving pulley 81 and driven pulley 82 of the belt running tester 80, and an axial load of 608 N was applied to the right side of the driven pulley 82 to apply belt tension. A rotation load of 34.2 N m was also applied to the driven pulley 82. The driving pulley 81 was rotated for 4200 min at room temperature. -1 The belt was rotated at a rotation speed of 1000 rpm and the belt was run. The belt was periodically stopped to visually check whether cracks had occurred on the back surface of the back rubber, and the belt running time until cracks were confirmed was measured. The maximum belt running time was set to 1000 hours. Furthermore, if tooth chipping or skipping occurred even without causing cracks, the test was terminated at that point.

[0134] <Durability test 2> Durability test 2 is a test for evaluating durability under high load conditions, and was carried out on the toothed belts manufactured in Examples 1-1, 2, 3-1 to 3-4, 4-1 to 4-4, 5-1 to 5-4, and 6-1 to 6-4. FIG. 9 shows a belt running test machine 90 used in the durability test 2. The belt running tester 90 includes a drive pulley 91 with 24 teeth and a tooth profile of 8M, and a driven pulley 92 with 36 teeth and a tooth profile of 8M provided on the right side of the drive pulley 91. The driven pulley 92 is provided so as to be movable left and right so that an axial load (dead weight) can be applied.

[0135] The toothed belt 120 manufactured in the specific embodiment was wound around the driving pulley 91 and driven pulley 92 of the belt running tester 90, and an axial load of 980 N was applied to the right side of the driven pulley 92 to apply belt tension. A rotation load of 39.2 N m was also applied to the driven pulley 92. The driving pulley 81 was rotated for 3000 min at room temperature. -1 The belt was rotated at a rotation speed of 100 rpm and run at 100 rpm. The belt was periodically stopped to visually check for chipped teeth, and the belt running time until the occurrence of chipped teeth was measured. In addition, tooth chipping due to wear and tooth chipping due to adhesion were observed in this durability test 2. The former is a tooth chip caused by a part of the belt tooth being worn away, and the latter is a tooth chip caused by UHMWPE particles or PTFE particles melting due to heat adhering to the surface of the belt tooth and riding on a mass of these adhered particles.

[0136] [Table 1]

[0137] [Table 2]

[0138] [Table 3]

[0139] As is clear from the results in Tables 1 to 3, the toothed belt according to the embodiment of the present invention is less susceptible to wear and deformation of the belt teeth, and is also suitable for use in high load transmission. [Industrial Applicability]

[0140] INDUSTRIAL APPLICABILITY The present invention is useful in the technical field of toothed belts in which a thermoplastic elastomer composition is used as the material for the tooth rubber portion and the back rubber portion. [Explanation of symbols]

[0141] 10, 110, 120 Toothed belt 11 Belt body 11a Back rubber 11b Rubber teeth part 12 belt teeth 13 Core Wire 14 Reinforcement fabric 15 Tooth root 30 Belt forming mold 31 Tooth formation groove 32 Rubber sleeve 80, 90 Belt Testing Machine 81, 82 Drive pulley 91, 92 Driven pulley

Claims

1. a belt body having a flat band-shaped back rubber portion and a plurality of tooth rubber portions disposed on the inner circumferential side of the back rubber portion and each of which is integrally formed with the back rubber portion to form a tooth portion, the back rubber portion and the tooth rubber portion both being made of a thermoplastic elastomer composition; A core wire including a carbon filament is embedded in the inner peripheral portion of the back rubber portion so as to form a spiral having a pitch in the belt width direction; a tooth portion covering material provided on an inner peripheral side of the belt body and covering the plurality of tooth rubber portions; Equipped with The thermoplastic elastomer composition has an elastomer component selected from the group consisting of a polyamide thermoplastic elastomer (TPAE) and a polyester thermoplastic elastomer (TPC), the hardness of the thermoplastic elastomer composition constituting the back rubber portion is 25 to 70; the hardness of the thermoplastic elastomer composition constituting the tooth rubber portion is 40 to 70 and is equal to or greater than the hardness of the thermoplastic elastomer composition constituting the back rubber portion; The tooth coating material is (a) a woven fabric treated with a binder, the binder being filled inside the woven fabric and also coating a surface of the woven fabric constituting the belt surface; The binder contains a particulate wear modifier; The particulate wear modifier is exposed over a total of 1 to 15% of the surface of the fabric constituting the belt surface.

2. 2. The toothed belt according to claim 1, wherein the fabric is a plain weave, a twill weave, or a satin weave.

3. 3. The toothed belt according to claim 1 or 2, wherein the woven fabric has threads extending along the longitudinal direction of the belt, and elastic threads or threads that have been subjected to a crimping process are used as at least the threads in the longitudinal direction of the belt.

4. 4. The toothed belt according to claim 1, wherein the particulate wear modifier is at least one of ultra-high molecular weight polyethylene (UHMWPE) particles and PTFE (polytetrafluoroethylene) particles.

5. A belt body having a flat band-shaped back rubber portion, and a plurality of tooth rubber portions disposed on the inner periphery of the back rubber portion and each being integrally formed with the back rubber portion to form a tooth portion, the back rubber portion and the tooth rubber portion both being made of a thermoplastic elastomer composition; A core wire including a carbon filament is embedded in the inner peripheral portion of the back rubber portion so as to form a spiral having a pitch in the belt width direction; a tooth portion covering material provided on an inner peripheral side of the belt body and covering the plurality of tooth rubber portions; Equipped with The thermoplastic elastomer composition has an elastomer component selected from the group consisting of a polyamide thermoplastic elastomer (TPAE) and a polyester thermoplastic elastomer (TPC), the hardness of the thermoplastic elastomer composition constituting the back rubber portion is 25 to 70; the hardness of the thermoplastic elastomer composition constituting the tooth rubber portion is 40 to 70 and is equal to or greater than the hardness of the thermoplastic elastomer composition constituting the back rubber portion; The tooth coating material is (b) A polyamide film containing a particulate wear modifier on the surface of the film constituting the belt surface or inside the film including the surface, The toothed belt, wherein the particulate wear modifier is exposed in a total amount of 1 to 15% on the surface of the polyamide film constituting the belt surface.

6. 6. The toothed belt according to claim 5, wherein the particulate wear modifier is at least one of ultra-high molecular weight polyethylene (UHMWPE) particles and PTFE (polytetrafluoroethylene) particles.