Method for preparing easily processable heat-stable phosphorus-containing flame retardant materials

Abstract

The present disclosure enables the direct production of non-halogenated phosphorus-containing, thermally stable, flame-retardant materials in powder or small particle form. The method generally involves heating one or more phosphonate salts to a dehydration reaction temperature of 200° C. or above in a high-boiling, water-miscible, acid-stable solvent.

Description

[Technical field]

[0001] This application claims the benefit of priority to U.S. Provisional Application No. 62 / 782,907, filed December 20, 2018, which is incorporated herein by reference in its entirety.

[0002] An improved process for preparing phosphorus-containing flame retardant materials having high thermal stability is disclosed which comprises heating one or more phosphonates in a high boiling, water-miscible acid inert solvent at elevated temperature to produce the flame retardant material directly, i.e., in the form of a powder or small particles, without or requiring grinding, granulation, or other such physical processing. [Background technology]

[0003] Polymers such as polyolefins, polyesters, polycarbonates, polyamides, polyurethanes, epoxy resins, and other thermoplastic or thermosetting polymer resins are often made flame retardant by incorporating phosphorus-containing compounds, halogen-containing compounds, or mixtures thereof. For example, U.S. Patent No. 3,689,602 discloses halogenated phosphate esters as flame retardant additives for plastics.

[0004] Some polymers are processed at high temperatures, for example, 200°C, 225°C, 250°C, 275°C or higher. Many known flame retardants are not suitable under these conditions because they are too volatile, have insufficient thermal stability, adversely affect processing, etc. Certain organophosphorus flame retardant compounds, such as some phosphate esters, exhibit a plasticizing effect that can adversely affect the mechanical properties of the polymers to which they are added. Compounds such as some phosphates are relatively unstable to hydrolysis, which can lead to the undesirable formation of various phosphoric acid compounds.

[0005] Many phosphorus-containing acid salts are known flame retardant additives, useful, for example, in thermoplastic polymers. US Patent 3,894,986 discloses flame retardant thermoplastic polyesters containing alkali salts of phosphonic acids, i.e., salts prepared from compounds of formula (X) where R is alkyl, such as the monosodium salt of ethanephosphonic acid or the sodium salt of the monomethyl ester of alkanephosphonic acid. US Patent 4,972,011 discloses aluminum salts of alkylphosphonic acids or monoalkyl esters of alkanephosphonic acids, i.e., salts of compounds of formula (Xa) where R is, for example, alkyl or alkyl substituted with one or more halo or hydroxy groups, and R' is hydrogen, methyl, ethyl, propyl, or isopropyl.

[0006] [ka]

[0007] US 2006 / 0138391 discloses salts formed from compounds of formula (X) as flame retardants, which may contain any of a wide variety of metals. The only salts actually exemplified in US 2006 / 0138391 are the aluminum salts of methyl phosphonic acid, i.e., R and R 1 The compound was the aluminum salt of the above formula (Xa) in which R is methyl.

[0008] DE 3833977 discloses metal salts prepared from compounds of formula (Xa) prepared from the reaction of dimethylmethylphosphonate and metal oxides or hydroxides in water at high pressure and elevated temperatures of 120° C. to 200° C., with examples being given of reactions carried out in aqueous solutions under high pressure in an autoclave at temperatures up to 190° C. Adducts of these salts with amines, for example ethylenediamine with melamine, and the use of the adducts as flame retardants in thermoplastics are also disclosed.

[0009] Salts of phosphinic acids, i.e. compounds of formula (II) where R1 and R2 are alkyl or carboaromatic, are also known flame retardant additives for thermoplastic polymers.

[0010] [ka]

[0011] Salts in which M is selected from Mg, Ca, Al, Sb, Sn, Ge, Ti, Zn, Fe, Zr, Ce, Bi, Li, Na, K, or protonated nitrogen bases are known. For example, U.S. Patent Nos. 5,780,534 and 6,013,707 disclose that calcium and aluminum phosphinates of formula (II), such as the calcium and aluminum salts of dimethylphosphinic acid, ethylmethylphosphinic acid, diethylphosphinic acid, n-propylmethylphosphinic acid, n-propylethylphosphinic acid, di-n-propylphosphinic acid, diisopropylphosphinic acid, or diphenylphosphinic acid, are particularly useful in polyesters.

[0012] As with many flame retardant systems, the performance of phosphorus-containing acid derivatives can be enhanced by the presence of other flame retardants, synergists, and adjuvants. US Patent No. 6,472,448 discloses flame retardant rigid polyurethane foams in which a combination of oxaalkylated alkylphosphonic acid and ammonium polyphosphate is present as the flame retardant.

[0013] U.S. Pat. No. 6,365,071 discloses a synergistic flame retardant combination for thermoplastic polymers, such as engineering plastics, especially polyesters, comprising A) a phosphinate salt of formula (II) above, such as aluminum dimethylphosphinate, aluminum methylethylphosphinate, and aluminum methylpropylphosphinate, and B) a nitrogen compound, such as allantoin, benzoguanamine, glycoluril, urea cyanurate, melamine cyanurate, melamine phosphate.

[0014] U.S. Pat. No. 6,255,371 discloses a flame retardant combination comprising A) a phosphinate salt of formula (II) above, such as diethylphosphinate, where M is calcium, magnesium, aluminum and / or zinc, and B) a condensation or reaction product of melamine, such as melamine polyphosphate, melam polyphosphate, and melem polyphosphate.

[0015] US Patent No. 6,547,992 discloses a flame retardant combination for thermoplastic polymers, comprising a phosphinate salt and a small amount of a non-nitrogen-containing inorganic and / or mineral compound. WO2012 / 045414 discloses a flame retardant composition comprising A) a phosphinate salt of the above formula (II) (wherein M is selected from Mg, Ca, Al, Sb, Sn, Ge, Ti, Zn, Fe, Zr, Ce, Bi, Li, Na, K or a protonated nitrogen base); and B) a metal salt of phosphorous acid; and other optional components.

[0016] The phosphinates cited above, for example in US Patent Nos. 6,365,071 and 6,255,371, are said to be thermally stable, do not degrade polymers during processing, and do not affect the preparation process of polymer compositions.Phosphinates are not volatile under the normal preparation and processing conditions of thermoplastic polymers.However, these materials are not necessarily suitable for use in all polymer systems, and may cause processing problems or lack the effectiveness of flame retardants required for certain polymers.

[0017] Phosphonates, particularly metal phosphonates, have been reported to be thermally stable, but as disclosed in U.S. Patent Application Publication No. 2007 / 0029532, decomposition of phosphonates at temperatures encountered during processing of polyesters and polyamides is well known, damaging the polymers being processed and providing only "brittle compositions that are unusable" as engineering thermoplastics.

[0018] US Patent No. 5,053,148 also includes teachings on the thermal conversion of phosphonic acid salts, also called phosphonates, i.e., when a metal phosphonate or a metal phosphonate precursor is heated to a temperature above, typically much higher than 200°C, the material forms an intractable, insoluble foam. The foam can be used as an electrical and / or thermal insulating material. US Patent No. 5,053,148 also discloses that when the foam is formed by heating the metal phosphonate or a metal phosphonate precursor in the presence of a thermoplastic material, such as an aromatic polyester, polyether, etc., a porous polymer composition is produced due to the decomposition of the polymer caused by the thermal conversion of the phosphonate or phosphonate precursor. Neither US Patent Application Publication No. 2007 / 0029532 nor US Patent No. 5,053,148 includes any discussion of the chemical makeup of the salt conversion product, nor any suggestion to first thermally convert the salt and then incorporate the conversion product into a polymer composition.

[0019] US Patent Nos. 9,534,108; 9,745,449; 9,752,009; 9,752,011; 9,758,640; and 9,765,204 disclose that when phosphonates are heated at a sufficiently high temperature, generally in the absence of other materials, the phosphonates are thermally converted into other materials that are more thermally stable and exhibit excellent flame retardant activity when incorporated into polymeric substrates.The thermally converted materials do not degrade at high temperatures and do not cause polymer degradation when processed in polymeric compositions at high temperatures, such as 240°C, 250°C, 260°C, 270°C or higher, which is a major advantage over previously known phosphonates that exhibit flame retardant activity but often degrade polymers during processing.The thermally converted materials are represented by the empirical formula (IV):

[0020] [ka]

[0021] (wherein R is an alkyl or aryl, M is a metal, q is a number from 1 to 7, for example 1, 2 or 3, r is a number from 0 to 5, for example 0, 1 or 2, often 0 or 1, y is a number from 1 to 7, for example 1 to 4, and n is 1 or 2, with the proviso that 2(q)+r=n(y). and its complex dehydration products. As with the inorganic coordination compounds, it is also disclosed that the compounds of empirical formula (IV) are idealized such that the products can include coordination polymers, complex salts, salts sharing certain valences, and the like.

[0022] Although the materials of U.S. Patent No. 9,745,449 and the like are effective flame retardants that do not cause degradation of polymer properties during processing, the materials are generally formed according to the methods of this invention as solid masses that require grinding or other such physical processing prior to incorporation into the polymer composition. Furthermore, the results of scale-up of the methods exemplified in the art tend to be inconsistent, and run-to-run reproducibility, e.g., conversion yields and physical properties, can be difficult to achieve.

[0023] The phosphate salts of formula (VI) and their derivatives can be thermally converted under suitable conditions to pyrophosphoric acid salts of formula (V). U.S. Patent No. 4,859,466 discloses that pyrophosphonates of formula (V) have fungicidal activity, and U.S. Patent Application Publication No. 2016 / 0032076 discloses their use as flame retardants.

[0024] [ka]

[0025] The pyrophosphonates can be prepared by heating the phosphates alone or in the presence of diphenylmethane. [Prior art documents] [Patent documents]

[0026] [Patent Document 1] U.S. Patent No. 3,689,602 [Patent Document 2] U.S. Patent No. 4,972,011 [Patent Document 3] US Patent Application Publication No. 2006 / 0138391 [Patent Document 4] DE3833977 [Patent Document 5] U.S. Patent No. 5,780,534 [Patent Document 6] U.S. Patent No. 6,013,707 [Patent Document 7] U.S. Patent No. 6,472,448 [Patent Document 8] U.S. Patent No. 6,365,071 [Patent Document 9] U.S. Patent No. 6,255,371 [Patent Document 10] U.S. Patent No. 6,547,992 [Patent Document 11] WO2012 / 045414 [Patent Document 12] US Patent Application Publication No. 2007 / 0029532 [Patent Document 13] U.S. Patent No. 5,053,148 [Patent Document 14] U.S. Patent No. 9,534,108 [Patent Document 15] U.S. Patent No. 9,745,449 [Patent Document 16] U.S. Patent No. 9,752,009 [Patent Document 17] U.S. Patent No. 9,752,011 [Patent Document 18] U.S. Patent No. 9,758,640 [Patent Document 19] U.S. Patent No. 9,765,204 [Patent Document 20] U.S. Patent No. 4,859,466 [Patent Document 21] US Patent Application Publication No. 2016 / 0032076 [Patent Document 22] US Patent Application Publication No. 2006 / 0138391 [Patent Document 23] US Patent Application Publication No. 2015 / 0031805 Summary of the Invention [Problem to be solved by the invention]

[0027] There remains a need for improvements in the preparation, handling, and batch reproducibility of thermally converted flame retardants such as at least those of US Pat. Nos. 9,534,108 and 9,745,449. [Means for solving the problem]

[0028] The present disclosure provides improved methods for making thermally stable, flame retardant materials that exhibit <5%, e.g., <3% or <1%, mass loss in thermogravimetric analysis (TGA) above 350° C. and up to, e.g., 400° C., 450° C., or higher.

[0029] The method of the present disclosure improves upon some of the shortcomings of existing methods for the thermal conversion of metal phosphonates to more thermally stable flame retardant materials. For example, the method provides flame retardant materials with improved physical morphology and handling properties, while also improving reproducibility, especially on scale-up. Other advantages will be apparent to those skilled in the art from this disclosure.

[0030] One embodiment of the present disclosure is a method for providing a flame retardant material in the form of a powder or small particles, comprising: i) reacting a high boiling, water miscible, acid stable solvent, such as a sulfone solvent, having a boiling point (bp) greater than 200° C., 220° C., 240° C., or 260° C. with a hydroxy group-containing olefin polymer having formula (I):

[0031] [ka]

[0032] where R is H, alkyl, aryl, alkylaryl or arylalkyl group, p is a number from 2 to 7, for example 2 to 4, e.g. 2, 3 or 4, M is a metal, y is a number from 2 to 7, for example 2 to 4, e.g. 2, 3 or 4, often 2 or 3, and thus M (+)y (wherein (+)y represents a charge formally assigned to the cation) is a metal cation. and heating a mixture of one or more phosphonates of at least 200° C., typically at least 220° C., e.g., at least 250° C., e.g., in the range of about 220° C. to about 400° C., or about 240° C. to about 360° C., to produce the flame retardant material directly, i.e., as a powder or small particles, without or without the need for grinding, granulation, etc. It should be understood that producing the flame retardant material “directly” as a powder or small particles in accordance with the methods disclosed herein allows for post-processing of the reaction product, such as isolation of the flame retardant product (e.g., separating the flame retardant product from residual solvent), which may include processing of the reaction product by, for example, filtering, washing, drying, etc.

[0033] Good results are obtained when the high boiling, water miscible, acid stable solvent is, for example, a sulfone with a bp above 200° C., for example, about 220° C. or higher, about 240° C. or higher, about 260° C. or higher, or about 280° C. or higher. Non-limiting examples of such solvents include sulfolane, with a bp of 285° C., and dimethyl sulfone.

[0034] Typically, the high boiling, water-miscible, acid-stable solvent component i) is the major component in the solvent / phosphonate mixture that is heated, i.e., the high boiling, water-miscible, acid-stable solvent is 51% or more by weight of the solvent / phosphonate mixture, e.g., the solvent concentration may be 60% or more, 70% or more, 80% or more, 85% or more, 90% or more, or 95% or more by weight. For example, in a mixture of i) a high boiling, water-miscible, acid-stable solvent and ii) a phosphonate, the high boiling, water-miscible, acid-stable solvent may be present at about 60-99%, 65-98%, or 70-98% by weight based on the total weight of i) and ii).

[0035] The reaction to produce the flame retardants of the present disclosure releases water as a by-product, which is often referred to as a dehydration reaction. It is believed that the solvents of the present disclosure, in addition to also transferring heat to the reaction and suspending the starting materials and products as they are formed, are also water-miscible, and that the solvents of the present disclosure may absorb water as it is produced during the reaction and / or aid in efficient mixing with the phosphonate salt in the aqueous solution.

[0036] The present method of obtaining the thermally stable flame retardant directly (without grinding, etc.) as a powder or small particles, in contrast to the method of the present invention, offers a significant improvement over existing manufacturing methods, such as those described in 9,745,449, etc., which generally involve heating a phosphonate salt in the absence of other materials to produce the thermally stable flame retardant material as a hard solid mass.

[0037] Another embodiment of the present disclosure provides a flame retardant material obtained from the above method, wherein the flame retardant material is a powder or small particle aggregate. The powder or small particle aggregate may have a median particle size (d50) of, for example, about 100 μm or less, for example, about 80 μm or less, or about 60 μm or less, as measured by laser diffraction according to ISO 13320. For example, the powder or small particle aggregate may have a median particle size (d50) of about 1 μm to about 100 μm, about 10 μm to about 90 μm, about 20 μm to about 80 μm, or about 20 μm to about 60 μm. The powder or small particle aggregate is obtained from the reaction product described herein without the need for grinding or similar physical processing.

[0038] In another embodiment, the flame retardant polymer composition comprises: a) a thermosetting or thermoplastic polymer, e.g. a thermoplastic polymer; b) 1% by mass to 50% by mass of the flame-retardant material relative to the total mass of the flame-retardant polymer composition; c) Optionally with other flame retardants or flame retardant synergists. Includes.

[0039] Another embodiment provides a method of preparing a flame retardant polymer composition comprising heating one or more metal phosphonates of formula (I) in a high boiling, water miscible, acid stable solvent under conditions to chemically convert the phosphonates to the more thermally stable flame retardant materials of the present disclosure as described above, and then incorporating the thermally stable flame retardant thus prepared into a polymer resin, for example by melt processing. For example, the flame retardant can be introduced into the molten polymer by blending, extrusion, fiber or film formation, etc.

[0040] In a further embodiment, the flame retardant material is in the form of a powder or small particles and has the empirical formula (IV):

[0041] [ka]

[0042] where R is H, alkyl, aryl, alkylaryl or arylalkyl group, q is a number from 1 to 7, for example 1, 2 or 3, r is a number from 0 to 5, for example 0, 1 or 2, often 0 or 1, M is a metal, y is a number from 2 to 7, for example 2 to 4, for example 2, 3 or 4, often 2 or 3, and thus M (+)y (wherein (+)y represents a charge formally attached to the cation) is a metal cation and n is 1 or 2, with the proviso that 2(q)+r=n(y). The flame retardant material may have a median particle size (d50) of, for example, about 100 μm or less, such as about 80 μm or less, or about 60 μm or less, as measured by laser diffraction according to ISO 13320. For example, the powder or aggregate of small particles may have a median particle size (d50) of about 1 μm to about 100 μm, about 10 μm to about 90 μm, about 20 μm to about 80 μm, or about 20 μm to about 60 μm. In some embodiments, the flame retardant material consists essentially of a compound or mixture of compounds of empirical formula (IV).

[0043] It has been found that the metal phosphonate of formula I can be uniformly converted to a more thermally stable flame retardant material with processing flexibility by heating the metal phosphonate in a high boiling, water-miscible, acid-stable solvent. This method provides greater uniformity in flame retardant yield and quality than previous methods. Furthermore, the product of this method is obtained directly as a powder or finely divided solid, and does not require grinding, granulation, or other such physical processing prior to use, in contrast to the solid mass obtained using the prior art methods.

[0044] The foregoing summary is not intended to be in any way limiting as to the scope of the invention as claimed. Moreover, it is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory only and are not restrictive of the invention as claimed. [Brief description of the drawings]

[0045] [Figure 1] 1 is a graph showing the results of thermogravimetric analysis (TGA) of an exemplary flame retardant material produced according to Example 1 of the present disclosure. [Diagram 2] 1 is a graph showing particle size distribution of an exemplary flame retardant of Example 1. [Diagram 3] FIG. 2 shows a scanning electron microscope (SEM) image of an exemplary flame retardant of Example 1. [Figure 4] 1 is a graph showing TGA results of an exemplary flame retardant material produced according to Example 2 of the present disclosure. [Diagram 5] 1 is a graph showing the TGA results of a flame retardant material produced according to Comparative Example 3 of the present disclosure. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0046] In this application, "a" or "an" means "one or more" unless otherwise specified.

[0047] In this method, (i) Formula I

[0048] [ka]

[0049] where R is H, alkyl, aryl, alkylaryl or arylalkyl group, p is a number from 2 to 7, for example 2 to 4, e.g. 2, 3 or 4, M is a metal, y is a number from 2 to 7, for example 2 to 4, e.g. 2, 3 or 4, often 2 or 3, and thus M (+)y (wherein (+)y represents a charge formally assigned to the cation) is a metal cation. and a phosphonate of (ii) a high-boiling, water-miscible, acid-stable solvent, the solvent being from 51 to 99% by weight of the mixture, for example from about 60 to 99%, 65 to 98%, or 70 to 98% by weight of the mixture, based on the combined weight of the phosphonate of Formula I and the high-boiling, water-miscible, acid-stable solvent; The mixture is typically heated to a dehydration temperature of greater than 200° C., e.g., 220° C. or higher (e.g., 250° C. or higher), e.g., a temperature in the range of about 220° C. to about 400° C., or about 240° C. to about 360° C., to provide the flame retardant of the present disclosure as a powder or small particles, typically as a free-flowing powder or free-flowing small particles.

[0050] In formula (I), y is 2 (+)y is Mg ++ , Ca ++ , or Zn ++ and the like, and y is 3. (+)y Al +++ As with inorganic coordination compounds, the formula is idealized and the starting materials and products may include coordination polymers or complex salts (e.g., salts sharing certain valences, such as salts sharing a single oxygen anion between two metal cations). Typically the starting salts are charge balanced, i.e., as represented by formula (I) where p=y, e.g., M (+)y Al +++ then p is 3, etc.

[0051] Phosphonates of formula (I) and their preparation methods are known in the art, some of which are known as flame retardants, such as tris-[methylphosphonic acid]aluminum salts. The phosphonates used as starting materials herein can be found as starting materials used to make flame retardants, such as in U.S. Patent Nos. 9,745,449 and 9,752,009.

[0052] In contrast to methods in the art where the salt is generally heated in the absence of other materials, in the present disclosure the phosphonate is subjected to dehydration temperatures while being mixed with a high boiling, water-miscible, acid-stable solvent as the dehydration medium described herein. The dehydration reaction produces water, which is compatible with the solvents of the present disclosure and may help promote a smooth reaction. The water miscibility and acid stability of the solvent may also help promote mixing when the phosphonate is added as a solution in an aqueous solvent.

[0053] The solvent used in the dehydration step of the process must be stable under the dehydration reaction conditions. The dehydration reaction is carried out at an elevated temperature, e.g., the reaction temperature is often greater than 220°C, 230°C, 240°C or 250°C, e.g., from about 220°C to about 400°C, or from about 240°C to about 360°C, e.g., from 240 to 290 or 300°C.

[0054] Water-miscible, acid-stable solvents of the present disclosure have a high boiling point, e.g., a bp greater than 200° C., e.g., about 220° C. or higher, about 240° C. or higher, about 260° C. or higher, about 270° C. or higher, or about 280° C. or higher, e.g., about 220° C. to about 360° C., or about 230° C. to about 350° C. Exemplary solvents that meet all three criteria of high boiling point, acid stability, and water miscibility include sulfones. In some embodiments, the high boiling, acid-stable, water-miscible solvent has the formula R1R2SO2, where R1 and R2 are C 1~6 Hydrocarbon groups, e.g. C 1~3 or R1 and R2 together with S form a ring having 2, 3, 4, or 5 carbon atoms, which ring is unsubstituted or C 1~3In some embodiments, R1 and R2 together with S form a di-, tri-, tetra-, or pentamethylene ring. In some embodiments, R1 and R2 are C 1~6 In some embodiments, R or R is independently selected from C 1~6 alkyl and the other is C 1~3 In some embodiments, R and R are C 1~3 In some embodiments, R1 and R2 are both methyl, both ethyl, or both propyl. In other embodiments, R1 or R2 is methyl and the other is ethyl or propyl. In other embodiments, R1 or R2 is ethyl and the other is propyl. In some embodiments, the sulfone is sulfolane.

[0055] According to the present disclosure, the phosphonate salt of formula (I) is combined with a high-boiling, acid-stable, water-miscible solvent and heated to a dehydration temperature as described herein to produce the flame retardant material of the present disclosure in the form of a powder or small particles. In general, the phosphonate salt is mixed with the high-boiling, acid-stable, water-miscible solvent under conditions sufficient to form a suspension or slurry, e.g., a homogeneous suspension or slurry. For example, in some embodiments, the phosphonate salt (i.e., the phosphonate salt of formula (I)) is mixed or combined with a high-boiling, acid-stable, water-miscible solvent at an elevated temperature to form a suspension or slurry, and then the mixture is subjected to a dehydration temperature as described herein. The heating can be gradually increased to one or more elevated temperatures over time and / or can be, but need not be, performed under vacuum conditions, such as under a gentle vacuum. The elevated temperature may depend on the melting point of the high-boiling, acid-stable, water-miscible solvent. For example, some useful high-boiling, acid-stable, water-miscible solvents may be solid at room temperature but may be converted to liquid solvents at elevated temperatures. Generally, the elevated temperature is higher than room temperature, for example, higher than 25, 30, 35, 40, 45, or 50°C, for example, about 30°C to about 160°C, about 60°C to about 160°C, about 40°C to about 130°C, about 80°C to about 120°C, about 40°C to about 100°C, or about 50°C to about 90°C. In some embodiments, the elevated temperature is less than 100°C, for example, any of the temperature ranges disclosed above, but less than 100°C. The mixture can be heated and maintained at two or more elevated temperatures. For example, the mixture can be heated to an elevated temperature for a period of time and then heated or cooled to one or more other elevated temperatures. For example, the mixture can be heated to an elevated temperature in the range of about 60°C to about 140°C, for example, about 80°C to about 120°C for a period of time, and then an elevated temperature in the range of about 140°C to about 160°C for an additional period of time.

[0056] Mixing of the phosphonate with the high boiling, acid stable, water miscible solvent is carried out at one or more elevated temperatures, optionally under vacuum conditions, over a period of time, for example, about 5 minutes or more, about 10 minutes or more, about 30 minutes or more, about 1 hour or more, about 3 hours or more, about 4 hours or more, about 6 hours or more, about 8 hours or more, about 12 hours or more, about 24 hours or more, about 36 hours or more, or about 48 hours or more, or any range therebetween. For example, the period of time may be about 30 minutes to about 72 hours, about 1 hour to about 48 hours, or about 2 hours to about 36 hours. During this time, undesirable volatile materials may be removed and a certain amount of water may be removed or distilled from the mixture. Generally, the resulting mixture forms a suspension or slurry, for example a homogeneous suspension or slurry. It will be apparent to one skilled in the art that the conditions such as temperature, pressure (e.g., vacuum conditions), stirring speed, time, etc. for mixing the phosphonate with the high boiling, acid stable, water miscible solvent are interrelated and these conditions can be adjusted to result in the formation of a suspension or slurry, e.g., to achieve a homogenous suspension or slurry.

[0057] In some embodiments, after the suspension or slurry is formed (e.g., the slurry or suspension may appear after about 10 minutes, about 30 minutes, about 1 hour, about 2 hours, about 4 hours, or about 6 hours after mixing the phosphonate salt with the high boiling, acid-stable, water-miscible solvent at an elevated temperature), the suspension or slurry is stirred for a period of time, such as at an elevated temperature as described herein. In some embodiments, the elevated temperature at which the suspension or slurry is stirred is reduced from the elevated temperature at which the mixture is heated to form the suspension or slurry. In some embodiments, the suspension or slurry is stirred at an elevated temperature ranging from about 30° C. to about 95° C. or from about 40° C. to about 80° C. In some embodiments, the suspension or slurry is stirred for about 1 minute or more, about 10 minutes or more, about 30 minutes or more, about 1 hour or more, about 4 hours or more, about 12 hours or more, about 24 hours or more, about 36 hours or more, about 48 hours or more, or any range therebetween.

[0058] The phosphonate may be in a liquid medium or in a solid form (e.g., a powder) when combined with the high-boiling, acid-stable, water-miscible solvent. For example, in some embodiments, the phosphonate is in an aqueous liquid (e.g., dissolved or partially dissolved in an aqueous liquid). For example, an aqueous solution of the salt of formula I may be mixed with a high-boiling, acid-stable, water-miscible solvent.

[0059] In some embodiments, it may be desirable to add an aqueous solvent to the mixture of the phosphonate salt and the high-boiling, acid-stable, water-miscible solvent to avoid gelation, for example during the formation of a suspension or slurry, or to prevent gelation if it occurs. It is believed that the use of certain metal-containing starting materials (i.e., certain metal compound precursors of the phosphonate salt) that provide the metal cation to the salt of formula (I) may also increase the likelihood of gelation. The addition of the aqueous solvent can be repeated as necessary / desired during the mixing process.

[0060] Further, in some embodiments, it may be desirable to add a seeding material (optionally in addition to the aqueous solvent or without the aqueous solvent) to the mixture of the phosphonate salt and the high boiling, acid-stable, water-miscible solvent to accelerate the formation of a suspension or slurry, for example, a homogeneous slurry. Reducing the time of slurry formation may also help reduce the formation of gels, as described above. During the mixing process, the addition of seeding material (optionally in addition to the aqueous solvent or without the aqueous solvent) can be repeated as necessary / desired. In some embodiments, the seeding material comprises an inert filler, which can be any material that is inert to the dehydration reaction and of the desired particle size. Silica, alumina, talc, and titanium dioxide are non-limiting examples of suitable inert fillers. In some embodiments, the seeding material comprises a flame retardant material (and optionally an inert filler) produced according to the method of the present disclosure, for example, a flame retardant material of formula (IV) described herein, and / or a flame retardant material according to U.S. Pat. No. 9,745,449, etc. The seeding material may have a median particle size (d50) of, for example, about 100 μm or less, such as about 80 μm or less, or about 60 μm or less, as measured by laser diffraction according to ISO 13320. For example, the seeding material may have a median particle size (d50) of about 1 μm to about 100 μm, about 10 μm to about 90 μm, about 20 μm to about 80 μm, or about 20 μm to about 60 μm.

[0061] In one embodiment, an aqueous solution of aluminum tris-[methylphosphonate] salt prepared from aluminum chloride hexahydrate starting material and sulfolane as a high boiling, water-miscible, acid-stable solvent are mixed at an elevated temperature ranging from about 80° C. to about 140° C., for example from about 100° C. to about 125° C., optionally under gentle vacuum, and a seeding material is added to the mixture. In some embodiments, for example, when the mixture or a portion thereof forms a gel-like consistency, an aqueous solvent is also added to the mixture. In some embodiments, after heating for, for example, about 2 to 6 hours, the mixture is heated to an even higher temperature ranging from about 100° C. to about 160° C., for example from about 120° C. to about 160° C., or from about 140° C. to about 160° C. In some embodiments, after formation of a suspension or slurry, for example, after about 1 to 2 hours, the temperature is reduced to a lower elevated temperature for subsequent stirring of the suspension or slurry as described herein. The resulting mixture is then heated to a dehydration temperature (eg, about 240° C. to about 360° C.) as described herein for a period of time (eg, about 2 hours to about 6 hours).

[0062] In another embodiment, an aqueous solution of aluminum tris-[methylphosphonate] salt prepared from an aluminum isopropoxide starting material is mixed with sulfolane as a high boiling, water-miscible, acid-stable solvent at an elevated temperature ranging from about 60° C. to about 100° C., such as from about 80° C. to about 95° C., optionally under moderate vacuum. In some embodiments, the aqueous solution of the salt and sulfolane are mixed at an elevated temperature for a period ranging from about 2 hours to about 6 hours. After formation of a suspension or slurry, the resulting mixture is heated to a dehydration temperature (e.g., from about 240° C. to about 360° C.) for a period of time (e.g., from about 2 hours to about 6 hours) as described herein.

[0063] Phosphonates of formula (I) are known, and various methods for their preparation are described in the art. For example, the phosphonates of formula (I) can be selected from salts disclosed in U.S. Patent Application Publication No. 2006 / 0138391, U.S. Patent Application Publication No. 2015 / 0031805, and elsewhere in the art. In some embodiments, the salts of formula (I) are those in which R is H, C 1~12 Alkyl, C 6~10Aryl, C 7~18 Alkylaryl or C 7~18 Arylalkyl groups, which may be further substituted as described in U.S. Patent Application Publication No. 2006 / 0138391, but often R is an unsubstituted C 1~12 Alkyl, C 6~10 Aryl, C 7~18 Alkylaryl or C 7~18 For example, R is a substituted or unsubstituted, often unsubstituted, C 1~6 Alkyl, C6 aryl, C 7~10 Alkylaryl or C 7~12 Arylalkyl, e.g., C 1~4 It may be alkyl.

[0064] The present disclosure relates to any particular metal cation M (+)y Examples of suitable metals include, but are not limited to, Mg, Ca, Ba, Zn, Zr, Ge, B, Al, Si, Ti, Cu, Fe, Sn, and Sb. In some embodiments, M is selected from Mg, Ca, Ba, Zn, Zr, B, Al, Si, Ti, Fe, Sn, and Sb. In some embodiments, M is selected from Mg, Ca, Ba, Zn, Zr, B, Al, Fe, Sn, and Sb. In some embodiments, M is selected from Al, Fe, Zn, and Ca.

[0065] R as alkyl is a straight or branched chain alkyl group having the specified number of carbon atoms, including, for example, unbranched alkyls such as methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, undecyl, dodecyl, and branched alkyls such as isopropyl, isobutyl, sec-butyl, t-butyl, ethylhexyl, t-octyl, etc. For example, R as alkyl can be methyl, ethyl, propyl, isopropyl, butyl, isobutyl, sec-butyl, t-butyl, and often R is methyl, ethyl, propyl, or isopropyl, e.g., methyl.

[0066] Often, when R is aryl, it is phenyl or naphthyl, e.g., phenyl. Examples of R as alkylaryl include phenyl substituted with one or more alkyl groups, e.g., groups selected from methyl, ethyl, propyl, isopropyl, butyl, isobutyl, sec-butyl, t-butyl, etc. Examples of R as arylalkyl include, e.g., benzyl, phenethyl, styryl, cumyl, phenpropyl, etc.

[0067] In some embodiments, R is H, methyl, ethyl, propyl, isopropyl, phenyl or benzyl, e.g., methyl, ethyl, propyl, isopropyl or phenyl, e.g., methyl, ethyl, propyl or isopropyl, e.g., methyl.

[0068] In some embodiments, the phosphonate is a compound of formula (I) where R is H, methyl, ethyl, propyl, isopropyl, benzyl, or phenyl, M is Al, Fe, Zn, or Ca, and p is 2 or 3. In some embodiments, R is H, methyl, ethyl, propyl, or isopropyl, p=3, and M is Al or Fe; in other embodiments, R is H, methyl, ethyl, propyl, or isopropyl, p=2, and M is Zn or Ca, e.g., Ca.

[0069] As noted above, two or more phosphonates of formula (I) can be used with different R and / or M. In some embodiments, at least one R is selected from H, methyl, ethyl, propyl, isopropyl, butyl, isobutyl, sec-butyl, t-butyl, and phenyl, and at least one M is selected from Al, Fe, Zn, and Ca. In some embodiments, each R is selected from H, methyl, ethyl, propyl, isopropyl, butyl, isobutyl, sec-butyl, t-butyl, and phenyl, and each M is selected from Al, Fe, Zn, and Ca.

[0070] The time it takes to convert the phosphonate of formula (I) to the flame retardant of the present invention will vary depending on a variety of factors, including, for example, the chemical structure of the starting phosphonate, the temperature of the reaction, and the like.

[0071] Good conversion of the phosphonate of formula (I) to the flame retardant material of the present disclosure is obtained by heating a mixture of the salt and a high-boiling, water-miscible, acid-stable solvent at a dehydration temperature described herein, typically at a temperature of 200° C. or higher, generally at a temperature of 220° C. or higher, for example at a temperature of 250° C. or higher, for example at a temperature in the range of about 220° C. to about 400° C., or about 240° C. to about 360° C., for a time of 20 hours or less, for example 12 hours or less. In general, the mixture of the phosphonate of formula (I) and the high-boiling, water-miscible, acid-stable solvent is heated at a temperature of about 200° C. (for example, about 220° C.) to about 400° C. for about 1 minute to about 20 hours, for example, about 30 minutes to about 12 hours, about 1 hour to about 8 hours, or about 2 hours to about 6 hours. In one example, the mixture is heated at about 220° C. to about 400° C. for about 1 hour to about 12 hours, or about 1 hour to about 8 hours. In another example, the mixture is heated for about 1 hour to about 6 hours, or about 2 hours to about 6 hours, at about 240° C. to about 360° C. In some circumstances, e.g., at higher temperatures (e.g., about 250° C. to about 400° C. or higher than 400° C.) and / or when the reaction vessel or environment allows for very efficient heat transfer to the starting materials, heating can be performed on the order of minutes or seconds, e.g., less than 1 hour, less than 30 minutes, less than 15 minutes, less than 6 minutes, less than 1 minute, or less than 30 seconds.

[0072] Without wishing to be bound by theory, the flame retardant material obtained by the method of the present disclosure has the empirical formula (IV):

[0073] [ka]

[0074] (In the formula, R is H, alkyl, aryl, alkylaryl or arylalkyl as described above; M is a metal as described above; q is a number from 1 to 7, for example, 1, 2 or 3; r is a number from 0 to 5, for example, 0, 1 or 2, often 0 or 1; y is a number from 2 to 7, for example, 2 to 4; and n is 1 or 2, with the proviso that 2(q)+r=n(y). It is believed to include a compound or mixture of compounds represented by the formula (IV). Of course, the identities of the R group and M closely reflect the groups used as R and M in the salt of formula (I) used as the starting material. As with inorganic coordination compounds as described above, formula (IV) is empirical and includes coordination polymers and complex salts (e.g., salts sharing certain valences).

[0075] The flame retardant material comprising a compound or mixture of compounds represented by empirical formula (IV) is produced in the form of a powder or small particles without the need for grinding, granulation, or other such physical processing. Such flame retardant materials generally have a median particle size (d50) of about 100 μm or less, for example about 80 μm or less, or about 60 μm or less, as measured by laser diffraction according to ISO 13320. For example, the powder or small particles may have a median particle size (d50) of about 1 μm to about 100 μm, about 10 μm to about 90 μm, about 20 μm to about 80 μm, or about 20 μm to about 60 μm.

[0076] As mentioned above, even when starting from a single compound of formula (I) with one R group and one metal, a mixture of compounds is often formed according to empirical formula (IV) described herein. In some embodiments, a flame retardant material is prepared from a mixture of phosphonates with multiple values ​​of R and / or M to produce a mixture of compounds according to empirical formula (IV) with multiple R groups and / or metals. In some embodiments, a flame retardant material of the present disclosure is prepared by separately obtaining two or more flame retardant materials according to the methods described herein and mixing these two or more flame retardant materials together such that the resulting flame retardant comprises a mixture of compounds according to empirical formula (IV) with multiple values ​​of R and / or M. U.S. Patent No. 9,752,011 is incorporated herein by reference for disclosure of techniques for preparing a mixture of phosphonates with different R groups and / or metals.

[0077] The flame retardants of the present disclosure can be used with a variety of other flame retardants, synergists, or flame retardant coagents known in the art. For example, the flame retardants include: Carbon black, graphite, carbon nanotubes, siloxanes, polysiloxanes. Polyphenylene ethers (PPE), phosphine oxides and polyphosphine oxides, such as benzylphosphine oxide, polybenzylphosphine oxide, etc.; Melamine, melamine derivatives and melamine condensation products, melamine salts such as melamine cyanurate, melamine borate, melamine phosphate, melamine metal phosphate, melam, melem, melon, etc.; Inorganic compounds including clays, metal salts, e.g. hydroxides, oxides, oxide hydrates, borates, carbonates, sulfates, phosphates, phosphites, hypophosphites, silicates, mixed metal salts, etc., e.g. talc and other magnesium silicates, calcium silicates, aluminosilicates, aluminosilicates as hollow tubes (DRAGONITE), calcium carbonate, magnesium carbonate, barium sulfate, calcium sulfate, HALLOYSITE or boron phosphate, calcium molybdate, exfoliated vermiculite, zinc stannate, zinc hydroxystannate, zinc sulfide, and zinc borate, zinc molybdate (KEMGARD 911A / B), zinc phosphate (KEMGARD 981), magnesium oxide or magnesium hydroxide, aluminum oxide, aluminum oxide hydroxide (boehmite), aluminum trihydrate, silica, tin oxide, antimony (III and V) oxide and antimony oxide hydrate, titanium oxide and zinc oxide or zinc oxide hydrate, zirconium oxide and / or zirconium hydroxide, etc.

[0078] Unless otherwise specified, in the context of this application, the term "phosphate" when used as a component in "phosphate", e.g., metal phosphate, melamine phosphate, melamine metal phosphate, refers to phosphate, hydrogen phosphate, dihydrogen phosphate, pyrophosphate, polyphosphate, or phosphoric acid condensation product anion or polyanion.

[0079] Similarly, unless otherwise stated, in the context of this application, the term "phosphite" when used as a component in "phosphites", e.g., in metal phosphites, refers to phosphites or hydrogen phosphites.

[0080] The flame retardants of the present application can also be combined with other flame retardants, such as halogenated flame retardants, alkyl or aryl phosphine oxide flame retardants, alkyl or aryl phosphate flame retardants, alkyl or aryl phosphonates, alkyl or aryl phosphinates, and salts of alkyl or aryl phosphinic acids. In some embodiments, the flame retardant is a combination of a flame retardant material according to the present disclosure and a phosphinate salt of formula (II) (e.g., aluminum tris(dialkylphosphinate)).

[0081] [ka]

[0082] (wherein R1 and R2 may each independently be a group according to R as described herein, M is a metal as described herein (e.g., Al or Ca), and n is a number from 2 to 7, for example 2 to 4, often 2 or 3.) Includes mixtures of.

[0083] Thus, in many embodiments, a flame retardant polymer composition according to the present disclosure includes (a) a polymer, (b) a flame retardant of the present disclosure, and (c) one or more additional flame retardants and / or one or more synergists or flame retardant coagents.

[0084] For example, in some embodiments, the flame retardant polymer composition comprises one or more additional flame retardants, such as a halogenated flame retardant, a phosphine oxide flame retardant, an alkyl or aryl phosphonate, or a salt of an alkyl or aryl phosphinate, such as an aluminum tris(dialkylphosphinate), for example, aluminum tris(diethylphosphinate).

[0085] In some embodiments, the flame retardant polymer composition comprises one or more synergists or flame retardant adjuvants, such as melamine, melamine derivatives and melamine condensation products, melamine salts, phosphine oxides and polyphosphine oxides, metal salts, such as hydroxides, oxides, oxide hydrates, borates, phosphates, phosphites, silicates, and the like, such as aluminum hydrogen phosphite, melem, or melamine metal phosphates, such as melamine metal phosphates, where the metal comprises aluminum, magnesium, or zinc. In certain embodiments, the one or more additional flame retardants, synergists or flame retardant coagents include aluminum tris(dialkylphosphinate), aluminum hydrogen phosphite, methylene diphenylphosphine oxide substituted polyaryl ethers, xylylene bis(diphenylphosphine oxide), 4,4'-bis(diphenylphosphinylmethyl)-1,1'-biphenyl, ethylene bis-1,2-bis-(9,10-dihydro-9-oxy-10-phosphaphenanthrene-10-oxide)ethane, melem, melam, melon, or dimelamine zinc pyrophosphate.

[0086] Certain embodiments provide halogen-free polymer compositions, in which halogen-containing flame retardants or synergists are excluded to the greatest extent possible.

[0087] The flame retardant material of the present disclosure can be combined with additional flame retardants, synergists, or adjuvants, for example, in a range of 100:1 to 1:100 by weight of the flame retardant of the present invention to the total weight of the additional flame retardants, synergists, and / or adjuvants. In some embodiments, the flame retardant material of the present disclosure is present in a range of 10:1 to 1:10 by weight of the flame retardant of the present invention to the total weight of the additional flame retardants, synergists, and / or adjuvants, for example, in a range of 7:1 to 1:7, 6:1 to 1:6, 4:1 to 1:4, 3:1 to 1:3, 2:1 to 1:2 by weight. The flame retardant of the present invention will often be the major component in such combinations, e.g., the weight ratio of the flame retardant material of the present invention to the total weight of additional flame retardants, synergists and / or adjuvants is from 10:1 to 1.2:1 or from 7:1 to 2:1, although the material of the present invention may be a minor component of the mixture, e.g., in a ratio of from 1:10 to 1:1.2 or in a ratio of from 1:7 to 1:2.

[0088] The heat stable flame retardant of the present invention can be incorporated into thermoplastic polymers, such as high temperature polyamides and polyterephthalate esters, at high temperatures without degrading the polymer or adversely affecting the physical properties of the polymer, and has excellent flame retardant activity.The flame retardant of the present invention can be used in other polymers with other synergists and conventional polymer additives.

[0089] The polymer of the flame retardant composition of the present disclosure may be any polymer known in the art, such as polyolefin homopolymers and copolymers, rubbers, polyesters with polyalkylene terephthalates, epoxy resins, polyurethanes, polysulfones, polyimides, polyphenylene ethers, styrene polymers and copolymers, polycarbonates, acrylic polymers, polyamides, polyacetals, and biodegradable polymers. Mixtures of different polymers may also be used, such as polyphenylene ether / styrene resin blends, polyvinyl chloride / acrylonitrile butadiene styrene (ABS), or other impact-modified polymers, such as methacrylonitrile and alpha-methylstyrene-containing ABS, and polyester / ABS or polycarbonate / ABS, and polyester or polystyrene + some other impact modifiers. Such polymers are commercially available or made by means well known in the art.

[0090] The flame retardants of the present disclosure are particularly useful in thermoplastic polymers that are processed and / or used at high temperatures, such as styrenic polymers including high impact polystyrene (HIPS), polyolefins, polyesters, polycarbonates, polyamides, polyurethanes, polyphenylene ethers, and the like.

[0091] For example, the polymer may be a polyester, styrene, polyamide, polycarbonate, polyphenylene oxide, vinyl, olefin, acrylic, epoxy, or polyurethane. The polymer may be a thermoplastic or thermoset and may be reinforced, e.g., glass reinforced. There may be multiple polymer resins. In certain embodiments, the polymer is an engineering polymer, e.g., a thermoplastic or reinforced thermoplastic polymer, e.g., a glass reinforced thermoplastic polymer, e.g., an optionally glass-filled polyester, an epoxy, or a polyamide, e.g., a glass-filled polyester, e.g., a glass-filled polyalkylene terephthalate, or a glass-filled polyamide.

[0092] Examples of polyester resins include homopolyesters and copolyesters obtained by polycondensation of a dicarboxylic acid component and a diol component, and by polycondensation of a hydroxycarboxylic acid or lactone component, and aromatic saturated polyester resins such as polybutylene terephthalate or polyethylene terephthalate.

[0093] Polyamide (PA) based resins include polyamides derived from diamines and dicarboxylic acids; polyamides derived from aminocarboxylic acids, optionally in combination with diamines and / or dicarboxylic acids; and polyamides derived from lactams, optionally in combination with diamines and / or dicarboxylic acids. Polyamides also include copolyamides derived from at least two different polyamide components. Examples of polyamide based resins include aliphatic polyamides, such as PA46, PA6, PA66, PA610, PA612, PA11, and PA12, polyamides derived from aromatic dicarboxylic acids, such as terephthalic acid and / or isophthalic acid, and aliphatic diamines, such as hexamethylenediamine or nonamethylenediamine; and polyamides derived from both aromatic and aliphatic dicarboxylic acids, such as terephthalic acid and adipic acid, and aliphatic diamines, such as hexamethylenediamine, and others. These polyamides may be used alone or in combination. In some embodiments, the polymer comprises polyphthalamide.

[0094] Polyamides with a melting point of at least 280°C are widely used, for example, for the production of molding compositions for the electrical and electronics industry, which allow the production of molded articles, with good dimensional stability at high temperatures and very good flame retardant properties. Moulding compositions of this type are required, for example, in the electronics industry, for the production of components that are mounted on printed circuit boards by the so-called surface mount technology, SMT. In this application, these components must withstand temperatures of up to 270°C for short periods without dimensional changes.

[0095] Such high temperature polyamides include certain polyamides made from alkyl diamines and diacids, such as polyamides 4, 6, but many high temperature polyamides are aromatic and semi-aromatic polyamides, i.e., homopolymers, copolymers, terpolymers, or higher polymers derived from monomers containing aromatic groups. A single aromatic or semi-aromatic polyamide may be used, or blends of aromatic and / or semi-aromatic polyamides are used. The above polyamides and blends of polyamides can also be blended with other polymers, including aliphatic polyamides.

[0096] Examples of these high temperature aromatic or semi-aromatic polyamides include polyamide 4T, poly(m-xylylene adipamide) (polyamide MXD,6), poly(dodecamethylene terephthalamide) (polyamide 12,T), poly(decamethylene terephthalamide) (polyamide 10,T), poly(nonamethylene terephthalamide) (polyamide 9,T), hexamethylene adipamide / hexamethylene terephthalamide copolyamide (polyamide 6,T / 6,6), hexamethylene terephthalamide copolyamide (polyamide 7,T), hexamethylene terephthalamide copolyamide (polyamide 8,T), hexamethylene terephthalamide copolyamide (polyamide 9,T), hexamethylene terephthalamide copolyamide (polyamide 10 ... Examples of such copolymers include hexamethylene adipamide / 2-methylpentamethylene terephthalamide copolyamide (polyamide 6,T / D,T); hexamethylene adipamide / hexamethylene terephthalamide / hexamethylene isophthalamide copolyamide (polyamide 6,6 / 6,T / 6,1); poly(caprolactam-hexamethylene terephthalamide) (polyamide 6 / 6,T); hexamethylene terephthalamide / hexamethylene isophthalamide (6,T / 6,I) copolymer, and the like.

[0097] Accordingly, certain embodiments of the present disclosure relate to compositions comprising polyamides that melt at high temperatures, e.g., 280°C or higher, 300°C or higher, and in some embodiments 320°C or higher, e.g., 280-340°C, such as polyamides 4, 6, and the aromatic and semi-aromatic polyamides listed above, articles comprising high temperature polyamides and the flame retardant materials of the present disclosure, methods of preparing the compositions, and methods of molding the articles.

[0098] As described herein, in many embodiments, the flame retardant polymer composition comprises (a) a polymer, (b) a flame retardant of the present disclosure, and (c) one or more additional flame retardants and / or one or more synergists or flame retardant adjuvants. Thus, the flame retardant (b) alone exhibits excellent activity in the polymer system, but may also be used in combination with (c) one or more compounds selected from other flame retardants, synergists, and adjuvants. Examples of compound (c) include halogenated flame retardants, alkyl or aryl phosphine oxides, alkyl or aryl polyphosphine oxides, alkyl or aryl phosphates, alkyl or aryl phosphonates, alkyl or aryl phosphinates, salts of alkyl or aryl phosphinic acids, carbon black, graphite, carbon nanotubes, siloxanes, polysiloxanes, polyphenylene ethers, melamine, melamine derivatives, melamine condensation products, melamine salts, metal hydroxides, metal oxides, metal oxide hydrates, metal borates, metal carbonates, metal sulfates, metal phosphates, metal phosphites, metal hypophosphites, metal silicates, and mixed metal salts. For example, the one or more compounds (c) may be selected from aluminium tris(dialkylphosphinite), aluminium hydrogen phosphite, benzylphosphine oxide, polybenzylphosphine oxide, melam, melem, melon, melamine phosphate, melamine metal phosphate, melamine cyanurate, melamine borate, talc, clay, calcium silicate, aluminosilicate, aluminosilicate as hollow tubes, calcium carbonate, magnesium carbonate, barium sulfate, calcium sulfate, boron phosphate, calcium molybdate, exfoliated vermiculite, zinc stannate, zinc hydroxystannate, zinc sulfide, zinc borate, zinc molybdate, zinc phosphate, magnesium oxide, magnesium hydroxide, aluminium oxide, aluminium oxide hydroxide, aluminium trihydrate, silica, tin oxide, antimony (III and V) oxide, antimony (III and V) oxide hydrate, titanium oxide, zinc oxide, zinc oxide hydrate, zirconium oxide, zirconium hydroxide.For example, the one or more compounds (c) may be selected from aluminum tris(dimethylphosphinate), aluminum tris(diethylphosphinate), aluminum tris(dipropylphosphinate), aluminum tris(dibutylphosphinate), methylene diphenylphosphine oxide substituted polyaryl ethers, xylylene bis(diphenylphosphine oxide), 1,2-bis-(9,10-dihydro-9-oxy-10-phosphaphenanthrene-10-oxide)ethane, 4,4'-bis(diphenylphosphinylmethyl)-1,1'-biphenyl, melam, melem, melon, and dimelamine zinc pyrophosphate.

[0099] In some embodiments, the flame retardant polymer composition comprises one or more compounds selected from hydrotalcite clays, metal borates, metal oxides, and metal hydroxides, e.g., metal borates, metal oxides, or metal hydroxides, where the metal is zinc or calcium.

[0100] The concentration of the flame retardant of the present invention in the polymer composition will of course depend on the exact chemical composition of the flame retardant, polymer, and other components found in the final polymer composition. For example, the flame retardant of the present invention, when used as the sole flame retardant component of the polymer formulation, may be present in a concentration of 1-50% by weight, such as 1-30% by weight, of the total weight of the final composition. Typically, when used as the sole flame retardant, the material of the present invention is present at least 2%, such as 3% or more, 5% or more, 10% or more, 15% or more, 20% or more, or 25% or more. In many embodiments, the flame retardant of the present invention is present in an amount of up to 45%, while in other embodiments, the amount of the flame retardant of the present invention is 40% or less, such as 35% or less, of the polymer composition. When used in combination with other flame retardants or flame retardant synergists, less of the material of the present invention may be required.

[0101] Any known compounding technique can be used to prepare the flame retardant polymer compositions of the present disclosure, for example, the flame retardant can be introduced into the molten polymer by blending, extrusion, fiber or film formation, etc. In some cases, the flame retardant is introduced into the polymer during its formation or curing, for example, the flame retardant may be added to a polyurethane prepolymer prior to crosslinking, or to a polyamine or alkyl-polycarboxyl compound prior to polyamide formation, or to an epoxy mixture prior to curing.

[0102] Flame retardant polymer compositions often contain common stabilizers or other additives frequently encountered in the art, such as phenolic antioxidants, hindered amine light stabilizers (HALS), UV absorbers, phosphites, phosphonites, alkali metal salts of fatty acids, hydrotalcites, metal oxides, borates, epoxidized soybean oil, hydroxylamines, tertiary amine oxides, lactones, thermal reaction products of tertiary amine oxides, thiosynergists, basic co-stabilizers, such as melamine, melem, and the like, polyvinylpyridine ... lolidone, dicyandiamide, triallyl cyanurate, urea derivatives, hydrazine derivatives, amines, polyamides, polyurethanes, hydrotalcites, alkali metal salts and alkaline earth metal salts of higher fatty acids, such as Ca stearate, calcium stearoyl lactylate, calcium lactate, Zn stearate, Zn octanoate, Mg stearate, Na ricinoleate, and K palmitate, antimony pyrocatecholate, or zinc pyrocatecholate, nucleating agents, clarifying agents, and the like.

[0103] Other additives may also be present, such as plasticizers, lubricants, emulsifiers, pigments, dyes, optical brighteners, other flame retardants, antistatic agents, foaming agents, anti-drip agents such as PTFE, and the like.

[0104] Optionally, the polymer may include fillers and reinforcing agents, such as calcium carbonate, silicates, glass fibers, talc, kaolin, mica, barium sulfate, metal oxides and hydroxides, carbon black, and graphite. Such fillers and reinforcing agents include formulations in which the filler or reinforcing agent is present in a concentration of more than 50% by weight based on the weight of the final composition, and are often present in relatively high concentrations. More typically, the fillers and reinforcing agents are present in an amount of about 5 to about 50% by weight, such as about 10 to about 40% by weight or about 15 to about 30% by weight based on the weight of the total polymer composition.

[0105] In some embodiments, the polymer compositions of the present disclosure can be combined with any of the following additives: carbon black, graphite, carbon nanotubes, siloxanes, polysiloxanes, talc, calcium carbonate, magnesium carbonate, barium sulfate, calcium sulfate, calcium silicate, magnesium silicate, aluminosilicate hollow tubes (Dragonite), halloysite, boron phosphate, calcium molybdate, exfoliated vermiculite, zinc stannate, zinc hydroxystannate, zinc sulfide, zinc borate, zinc molybdate (Kemgard 911A / B), zinc phosphate (Kemgard 981), etc.; hydroxides, oxides, and oxide hydrates of group 2, 4, 12, 13, 14, 15 (semi) metals, such as magnesium oxide or hydroxide, aluminum oxide, aluminum oxide hydroxide (boehmite), aluminum trihydrate, silica, silicates, tin oxide, antimony (III and V) oxide and antimony oxide hydrate, titanium oxide and zinc oxide or zinc oxide hydrate, zirconium oxide and / or hydroxide, etc.; melamine and urea based resins, such as melamine cyanurate, melamine borate, melamine polyphosphate, melamine pyrophosphate, polyphenylene ether (PPE), etc.; and clays, including, for example, hydrotalcite, boehmite, kaolin, mica, montmorillonite, wollastonite, nanoclays, or organically modified nanoclays.

[0106] Further non-limiting disclosure is provided in the Examples below. EXAMPLES

[0107] Example 1 An aqueous solution containing 400 g of aluminum tris-[methylphosphonate] salt, prepared from aluminum trichloride hexahydrate and methylphosphonic acid (MPA), was added to the reaction flask along with 2.5 kg of sulfolane. The reaction mixture was stirred under gentle vacuum and heated to gradually increase the temperature. As the temperature increased, water was removed.

[0108] When approximately 400 mL of water was distilled from the reaction mixture, the pot temperature was 95° C. and a gel-like material was deposited on the walls of the reaction vessel. Approximately 0.1 grams of seeding material with a median particle size (d50) of less than 100 μm was added along with 200 mL of water, causing the gel-like material to disappear from the walls. Further episodes of gel formation were ameliorated by the addition of more seeding material and water. Heating was continued for approximately 4 hours, during which time the temperature increased to approximately 120° C. and the desired slurry began to form, at which point the vacuum was removed. Heating was continued, raising the pot temperature to 160° C. and then held at 160° C. for 2 hours to complete the homogenous slurry formation. The pot temperature was then reduced to 60° C. and the homogenous slurry was stirred at 60° C. for 36 hours.

[0109] The reaction mixture was then gradually heated to 250° C. and held at that temperature for 3 h to produce a suspension of white fine particles. The reaction mixture was cooled to 60° C., filtered, and the solid was washed with IPA (500 mL×3) to give a white powder and a pale yellow filtrate. 31 No phosphorus compounds were detected in the filtrate by P NMR. The solid was then dried at 160 °C for 1 hour to give the product as 370 grams of white powder (99% yield). The powder was quickly sieved through a 325 mesh screen (87% sieved in 1 day) and had a free-flowing, non-fluffy physical appearance. Thermogravimetric analysis (TGA) performed in N2 showed that the product was thermally stable up to >400 °C (Figure 1). Elemental analysis (ICP-OES) was as follows: 31.0% P, 9.0% Al. The BET surface area of ​​the product was approximately 2.5-2.6 m2 / g and the bulk density was 0.53 g / mL. The particle size distribution and SEM images of the product are shown in Figures 2 and 3, respectively.

[0110] Example 2 An aqueous solution of tris-[methylphosphonic acid]aluminum salt prepared from MPA and aluminum isopropoxide was added along with sulfolane in a mass ratio of 100 grams of sulfolane per 15 grams of aluminum salt to a 4-neck 5 L round bottom flask equipped with an overhead stirrer, an addition funnel, and a Vigreux column with a Dean-Stark trap.

[0111] The reaction mixture was stirred under nitrogen at 90°C for 4 h to give a homogenous white suspension. The reaction mixture was then gradually heated to 250°C and held at 250°C for 3 h. The off-white suspension was then cooled to 60°C, the sulfolane was filtered off, and the solid was washed with isopropanol (500 mL x 3). The solid was then dried in an oven at 160°C for 1 h to give the product as a white powder (142 g) in 92% yield. TGA performed with N2 showed that the product was thermally stable up to >400°C (Figure 4). Elemental analysis (ICP-OES) was as follows: 26.7% P, 8.5% Al.

[0112] Comparative Example 3 A pre-weighed 1 L resin kettle was charged with 282.3 g of ethylphosphonic acid (EPA) and 157 mL of deionized HO. The reactor was placed in an ice bath and increasing amounts of solid Al(O- i Pr)3, a total of 174.7 g of Al(O- i3)3. After addition, the pot temperature was maintained below 20°C using an ice bath for approximately 15 minutes, at which point the ice bath was removed and the pot was allowed to warm to room temperature. The mixture was stirred until no aluminum isopropoxide was visible (at least 5 hours). A milky mixture was formed and concentrated using a distillation head and pump. The concentrated mixture was poured into a 1 L beaker and placed in an oven settable at 100°C and heated to 160°C over 8 hours and held for 8 hours. The temperature was increased to 230°C over 2 hours and held for 6 hours. The resulting product formed as a solid mass which was cooled to room temperature. The solid mass was coarsely crushed using a mortar and pestle and heat treated again to 230°C over 1 hour and held for 4 hours. The product was re-crushed and transferred to a drying container in a yield of 276.4g (96.2%). TGA performed in N2 showed that the product was thermally stable up to >350 °C (Figure 5).

[0113] Example 4 The flame retardant activity of the material produced according to the present disclosure is excellent and no problems were observed in incorporating the material into polymer compositions. A) a polyamide 66 composition containing 30% by weight of glass fiber, 13.7% by weight of FR 1 / 2, and 10% melem; and B) Polyphthalamide composition containing 25% by weight of glass fiber and 16.7% by weight of FR 1 / 2 where FR 1 / 2 represents a flame retardant material prepared according to Example 1 in one test series and a flame retardant material prepared according to Example 2 in a separate test series.

[0114] In particular, polymer compositions were prepared and evaluated for flame retardant activity under the UL94 test, as shown in Table 1 below. As shown in Table 1, certain compositions also contained melem (a melamine condensation product) as a synergist. Formulations 1 and 2, containing 56.3 parts nylon 66, 30 parts glass, 13.7 parts flame retardant FR 1 / 2, and 10 parts melem, were made by compounding at 265°C and molding into 1 / 16" and 1 / 32" bars, respectively, at 280°C. Formulation 3, containing 58.3 parts polyphthalamide, 25 parts glass, and 16.7 parts flame retardant FR 1 / 2, was made by compounding at 320-330°C and molding into 1 / 32" bars at 320-330°C. The formulations were evaluated according to UL94, and the results are shown in Table 1.

[0115] The results showed that the flame retardants prepared according to Example 1 and Example 2 achieved the highest UL-94 vertical flame test rating, V-0, respectively, at different sample thicknesses (while the polymer composition without the flame retardant (Formulation 4) failed the UL94 test). The results from Formulation 3 also showed that the flame retardants produced according to Example 1 and Example 2 each achieved the highest UL-94 vertical burn test rating, V-0, at 1 / 32" in glass-filled semi-aromatic nylon.

[0116] [Table 1]

[0117] While particular embodiments of the invention have been illustrated and described, it will be apparent to those skilled in the art from consideration of the specification and practice of the disclosure that various modifications and changes can be made without departing from the scope of the invention as claimed. Therefore, it is intended that the specification and examples be considered as exemplary only, with the true scope of the invention being indicated by the following claims and their equivalents.

Claims

1. 1. A method for preparing a thermally stable phosphorus-containing flame retardant material, comprising: i) a majority by weight, based on the weight of the mixture, of one or more high-boiling, water-miscible, acid-stable solvents having a boiling point greater than 200° C., said acid-stable solvents being selected from the group consisting of sulfolane and dimethylsulfone; ii) Formula (I): 【Chemistry 1】 (wherein R is a methyl group, p is 3, M is aluminum, and y is 3, so M (+)y (wherein (+)y represents the charge formally assigned to the cation) is an aluminum cation. and (iii) water; to a reaction temperature of 200° C. or higher to produce a slurry containing particles of the flame retardant material dispersed in the solvent; and isolating particles of the flame retardant material from said slurry to produce a powder of the flame retardant material.

2. Prior to the step of heating the mixture at a temperature of 200° C. or greater, a) providing a salt of formula (I) in solid or liquid form; b) preparing a mixture by combining the salt of formula (I) provided in a) with said one or more acid-stable solvents and water under conditions and for a time sufficient to form a slurry; The method of claim 1 further comprising:

3. 3. The method of claim 2, wherein the salt of formula (I) is provided as a solution in an aqueous solvent.

4. 4. The method of claim 2 or 3, wherein the step of preparing the mixture is carried out at one or more temperatures in the range of from 30°C to 160°C.

5. 5. The process according to any one of claims 1 to 4, wherein the mixture is heated to a reaction temperature in the range of from 220°C to 400°C.

6. 6. The method according to claim 1, wherein the powder or particles have a median particle size of less than or equal to 100 μm, measured by laser diffraction according to ISO 13320.

7. The method of claim 6, wherein the median particle size is between 20 μm and 80 μm.

8. 10. A process for the preparation of a flame retardant polymer composition comprising the steps of: (i') preparing a flame retardant material using the process according to any one of claims 1 to 7; and (ii') incorporating the flame retardant material obtained in (i') into a polymer substrate, wherein the amount of the flame retardant material is between 1 and 50% by weight relative to the total weight of the flame retardant polymer composition.

9. 9. The method of claim 8, wherein the polymer substrate comprises one or more of a polyolefin homopolymer or copolymer, rubber, polyester, epoxy resin, polyurethane, polysulfone, polyimide, polyphenylene ether, styrene polymer or copolymer, polycarbonate, acrylic polymer, polyamide, or polyacetal.

10. 10. The method of claim 9, wherein the polymeric substrate comprises one or more of a styrene polymer or copolymer, a polyolefin homopolymer or copolymer, a polyester, a polycarbonate, an acrylic polymer, an epoxy resin, a polyamide, or a polyurethane.

11. The method of claim 10, wherein the polymer substrate comprises polyalkylene terephthalate, high impact polystyrene (HIPS), epoxy resin, or polyamide.

12. The method of claim 11 , wherein the polymeric substrate comprises a glass-filled polyalkylene terephthalate, a glass-reinforced epoxy resin, or a glass-filled polyamide.

13. The method of claim 11 , wherein the polymeric substrate comprises polyphthalamide.

14. The method of claim 11 , wherein the polymer substrate comprises polyamide 46, polyamide 6, polyamide 66, polyamide 4T, or polyamide 9T.

15. 12. The method of claim 11 , wherein the polymer substrate comprises polyamide MXD,6, polyamide 12,T, polyamide 10,T, polyamide 6,T / 6,6, polyamide 6,T / D,T, polyamide 6,6 / 6,T / 6,I, polyamide 6 / 6,T, or polyamide 6,T / 6,I.

16. 9. The method of claim 8, wherein the polymer substrate comprises a polyphenylene ether / styrene resin blend, acrylonitrile butadiene styrene (ABS), a polyvinyl chloride / ABS blend, a methacrylonitrile / ABS blend, an alpha-methylstyrene-containing ABS, polyester / ABS, polycarbonate / ABS, impact modified polyester, or impact modified polystyrene.

17. 17. The process of any one of claims 8 to 16, further comprising adding to the mixture comprising the polymeric substrate and the flame retardant material one or more additional compounds selected from halogenated flame retardants, alkyl or aryl phosphine oxides, alkyl or aryl polyphosphine oxides, alkyl or aryl phosphates, alkyl or aryl phosphonates, alkyl or aryl phosphinates, salts of alkyl or aryl phosphinic acids, carbon black, graphite, carbon nanotubes, siloxanes, polysiloxanes, polyphenylene ethers, melamine, melamine derivatives, melamine condensation products, melamine salts, metal hydroxides, metal oxides, metal oxide hydrates, metal borates, metal carbonates, metal sulfates, metal phosphates, metal phosphites, metal hypophosphites, metal silicates, and mixed metal salts.

18. 18. The process of claim 17, wherein the one or more additional compounds are selected from the group consisting of aluminum tris(dialkylphosphinite), aluminum hydrogen phosphite, benzylphosphine oxide, polybenzylphosphine oxide, melam, melem, melon, melamine phosphate, melamine metal phosphate, melamine cyanurate, melamine borate, talc, clay, calcium silicate, aluminosilicate, aluminosilicate as hollow tubes, calcium carbonate, magnesium carbonate, barium sulfate, calcium sulfate, boron phosphate, calcium molybdate, exfoliated vermiculite, zinc stannate, zinc hydroxystannate, zinc sulfide, zinc borate, zinc molybdate, zinc phosphate, magnesium oxide, magnesium hydroxide, aluminum oxide, aluminum oxide hydroxide, aluminum trihydrate, silica, tin oxide, antimony (III and V) oxide, antimony (III and V) oxide hydrate, titanium oxide, zinc oxide, zinc oxide hydrate, zirconium oxide, and zirconium hydroxide.

19. 20. The process of claim 18, wherein the one or more additional compounds are selected from the group consisting of aluminum tris(dimethylphosphinate), aluminum tris(diethylphosphinate), aluminum tris(dipropylphosphinate), aluminum tris(dibutylphosphinate), methylene diphenylphosphine oxide substituted polyaryl ethers, xylylene bis(diphenylphosphine oxide), 1,2-bis-(9,10-dihydro-9-oxy-10-phosphaphenanthrene-10-oxide)ethane, 4,4'-bis(diphenylphosphinylmethyl)-1,1'-biphenyl, melam, melem, melon, and dimelamine zinc pyrophosphate.

20. 9. The method of claim 8, further comprising adding to the mixture comprising the polymeric substrate and the flame retardant material one or more compounds selected from the group consisting of hydrotalcite clay, metal borates, metal oxides, and metal hydroxides.

21. 21. The process of claim 20, wherein the metal of the metal borate, metal oxide and metal hydroxide is zinc or calcium.

22. 1. A method for improving the flame retardancy of a polymer, comprising: i) a majority by weight, based on the weight of the mixture, of sulfones selected from the group consisting of sulfolane and dimethyl sulfone; ii) Formula (I): 【Chemistry 2】 (wherein R is a methyl group, p is 3, M is aluminum, and y is 3, therefore, M (+)y (wherein (+)y represents the charge formally assigned to the cation) is an aluminum cation. and (iii) water; heating the mixture to a reaction temperature of 200° C. or greater to form a flame retardant material; Separating the flame retardant material from the solvent to obtain the flame retardant material as a powder or in the form of small particles; combining a flame retardant material with a polymer; A method comprising: