Polyurethane formation catalyst

Abstract

The present invention relates to novel urethane or carbamate compounds that can act as catalysts for the reaction of at least one isocyanate compound with at least one isocyanate-reactive compound, in particular for the production of polyisocyanate polyaddition products such as polyurethanes, and in particular for the production of polyurethane (PU) foams, wherein the compounds exhibit excellent foaming performance.

Description

[Technical field]

[0001] The present invention relates to novel urethane or carbamate and urea compounds obtainable by reaction of an isocyanate compound with at least one isocyanate-reactive compound, said compounds being useful as catalysts, a process for the preparation of said compounds, the use of said compounds as catalysts, in particular for the reaction of at least one isocyanate compound with at least one isocyanate-reactive compound, in particular for the preparation of polyisocyanate polyaddition products such as polyurethanes, in particular for the preparation of water-blown polyurethane (PU) foams, which show excellent blowing performance. [Background technology]

[0002] technical challenges Polyurethane foams are generally produced by reacting polyisocyanates (or prepolymers made from them) with compounds containing two or more active hydrogens (chain extenders, polyether polyols, polyester polyols, polyether amines, etc.) in the presence of blowing agents (chemical blowing agents such as water and physical blowing agents such as pentane, cyclopentane, halohydrocarbons), catalysts (organometallic derivatives such as tertiary amines, tin, bismuth, zinc), silicone-based surfactants and other coagents. During the production of water-blown polyurethane foam, two main reactions are promoted among the reactants by catalysts. - The reaction of isocyanate reactive compounds such as polyols with isocyanates, which increases the molecular weight of the polymer, which leads to an increase in viscosity and gel strength; this reaction is called the gelation reaction. The reaction of water with isocyanate produces CO2 gas which acts as a blowing agent; this reaction is called the blowing reaction.

[0003] Tertiary amines are well-known PU catalysts. They have varying degrees of activity in promoting the gelling reaction. This is especially true when the polyol has high inherent reactivity. In some formulations, the amine catalyst may be the only catalyst used. Organotin catalysts promote the gelling reaction, whereas amine catalysts primarily affect the blowing reaction.

[0004] Most polyurethane foams emit volatile organic compounds. These emissions can consist, for example, of contaminants present in the raw materials, catalysts, decomposition products or unreacted volatile starting materials or other additives. Amine emissions from polyurethane foams have become a major topic, especially in car interior applications, furniture or mattresses, and the market is increasingly demanding low-emitting foams. Especially in the automotive industry, a significant reduction of volatile organic compounds (VOCs) and condensable compounds (fogging or FOG) in the foam is required. The evaluation of the VOC and FOG profile of PU foams can be done by the VDA278 test. One of the main components emitted from flexible molded foams is the amine catalyst.

[0005] The reduction of amine emissions can be achieved, among others, by a) introducing reactive hydroxyl or amino groups into the molecules of tertiary amine moieties, allowing them to be bound to the polymer network, or b) using tertiary amines with very low vapor pressure. Reactive amines are known to reduce some fatigue properties, such as humid aging compression set. In addition, reactive amines promote undesirable chain termination, thereby reducing the amount of strong and active amine catalyst moieties. The development of efficient polyurethane catalysts with low emission profiles is therefore one of the key goals of the modern polyurethane industry.

[0006] US6423756B1 describes tertiary amine-derived IPDI-based biscarbamates as PU catalysts. The specific reactive tertiary amines described in the patent application are based on dimethylaminoethoxyethanol, dimethylaminoethanol, bis(dimethylaminopropyl)amino-2-propanol. WO2020011343A1 describes the use of IPDI-derived biscarbamates of bicyclic tertiary amines.

[0007] Despite the attempts made in the prior art, there is still a need for catalyst compositions that are non-reactive and do not bind to polymer networks, but have low emission performance. The present invention describes new compounds that can be used as catalysts, meeting the aforementioned requirements. Surprisingly, despite their higher molecular weight, the new molecules have been found to be highly efficient and more differentiated blowing catalysts, similar to many other known catalysts. Summary of the Invention

[0008] According to the invention, therefore, there is provided a compound obtained by reacting an isocyanate compound with at least one isocyanate-reactive compound of formula (I): (R) a -X (I) where R is R 1 and R 2 is selected from, where R 1 is R 3 , R 4 , R 5 , R 6 , R 14 and R 16 wherein R 3 represents a hydrocarbyl group containing at least two tertiary amino groups and at least one ether (—O—) group; R 4 represents a hydrocarbyl group containing at least one monocyclic heterocyclic group; R 5 represents a group of the formula [ka] (The dotted line indicates the binding site for X.) Here, R 17 represents an aliphatic hydrocarbon group having at least 3 carbon atoms, and R 7 and R 8 each represents a linear or branched aliphatic hydrocarbyl residue optionally substituted with one or more tertiary amino groups and optionally containing one or more ether (—O—) groups; R 6 represents a group of the formula [ka] (The dotted line indicates the binding site for X.) Here, R 18 represents an aliphatic hydrocarbyl group having at least 2 carbon atoms; R 19 represents an aliphatic hydrocarbyl group having at least 3 carbon atoms, and R 9 From R 11 each independently represents a linear or branched aliphatic hydrocarbyl residue; R 14 represents a group of the formula [ka] (The dotted line indicates the binding site for X.) Here, R 15 are each independently selected from hydrocarbyl groups containing at least one tertiary amino group, and optionally containing one or more ether (—O—) groups; and R 16 represents an aromatic group substituted with at least two hydrocarbyl groups, each of which contains at least one tertiary amino group; R 2 represents a hydrocarbyl group, preferably an aliphatic saturated hydrocarbyl group having up to 10 carbon atoms, more preferably an alkyl group having up to 10 carbon atoms, or hydrogen; a is 2 or 3, and X is selected from the group consisting of O, S, or N; However, the compound contains at least one group R as defined above. 1 and R for hydrogen 2 and R 1 There is only one group R 5 The condition is that it is possible to express or salts thereof, and mixtures thereof are provided.

[0009] Thus, when X represents O or S, a is 2, and when X represents N, a is 3. To be isocyanate-reactive, a compound of formula (I) must have at least one hydrogen atom bonded to X (R 2 is hydrogen). X is preferably O or N. When X is N, it is preferably a group consisting of two hydrogen atoms and one group R bonded to N. 1 i.e., the isocyanate-reactive compound has a primary amino group and is represented by the formula R 1 -NH2. R 2 R represents a hydrocarbyl group 1 R 2 Compounds of NH are less preferred. When X is O or S, the compounds have the formula R accordingly. 1 -XH, and in particular the formula R 1 -OH and hydroxy compounds of formula R 1 Thus, essentially, the compound of formula (I) is a mercapto compound of formula R 1 -NH2, R 1 R 2 NH, where R 2 represents a hydrocarbyl group, and R 1 XH, where R 1 is defined above, includes any of the compounds of the formula (I). The isocyanate-reactive compounds of formula (I) usually do not contain further isocyanate-reactive functional groups apart from the isocyanate-reactive functional groups -OH, -SH, =NH or -NH2, i.e. they are usually monofunctional with respect to reaction with the isocyanate group of an isocyanate compound.

[0010] Examples of such isocyanate-reactive compounds of formula (I) are, for example, selected from the following compounds: [ka] [ka] [ka] [ka] [ka] [ka] [ka] [ka] [ka] [ka]

[0011] Particularly preferred compounds according to the invention are the reaction products of these isocyanate-reactive compounds with isophorone diisocyanate (IPDI) and hexamethylene-1,6-diisocyanate (HDI), most preferably isophorone diisocyanate (IPDI). Such compounds include in particular those in which two isocyanate groups of the diisocyanate react, which are most preferred, but can also include those in which only one isocyanate group reacts, and all molar ratios between the two as exemplified below for isophorone diisocyanate. [ka] where R is as defined above and b is 1 or 2 depending on whether X is S or O, or N.

[0012] In certain preferred embodiments of the present invention, R 1 is R 3 i.e., a hydrocarbyl group containing at least two tertiary amino groups and at least one ether (-O-) group. The hydrocarbyl group is preferably a saturated aliphatic hydrocarbyl group, e.g., a hydrocarbyl group containing at least one tertiary amino group, [ka] where all of the attachment sites on the nitrogen atom (shown by dotted lines) are attached to an aliphatic hydrocarbyl residue.

[0013] Particularly preferred compounds according to the invention are R 1 R is selected from the group consisting of saturated aliphatic hydrocarbyl groups having up to 20, preferably up to 15, carbon atoms and containing at least two tertiary amino groups and at least one ether (—O—) group. 3 In such preferred compounds, R of formula (I) is selected from the group consisting of 1 is selected from the following formula: 3Suitably selected from the group consisting of: [ka] (where the wavy line represents the binding site for X) Here, R 13 The groups are independently selected from divalent linear, branched or cyclic hydrocarbyl groups, and two of A, B, and C represent tertiary amino groups (A and B are -N(R 12 )-, and for C, -N(R 12 )2, where R 12 is an organic group, preferably an aliphatic hydrocarbyl group having up to 15 carbon atoms, preferably an alkyl group having up to 6 carbon atoms), and one of A, B, C represents an ether group (selected from -O- in the cases of A and B and -OR in the case of C). 12 is selected from, where R 12 is defined above).

[0014] In particularly preferred compounds according to the invention, R 1 is selected from the following formula: 3 is selected from the group consisting of [ka] (where the wavy line represents the binding site for X) where x, y, and z are integers from 2 to 6, preferably 2 or 3, and where A, B, and C are as defined above. 1 R 3 The isocyanate-reactive compound according to the present invention, selected from the group consisting of, can be illustrated by the following formula: [ka]

[0015] In such exemplary compounds, X represents O or N, and R 2 R represents hydrogen. 1R 3 Particularly preferred isocyanate-reactive compounds selected from the group consisting of: [ka]

[0016] In a further preferred embodiment, R 1 is R 4 i.e., R 1 represents a hydrocarbyl group containing at least one monocyclic heterocyclic group, preferably R 1 =R 4 = an aliphatic hydrocarbyl group having up to 20 carbon atoms, which is substituted with at least one monocyclic heterocyclic group.

[0017] In particularly preferred isocyanate-reactive compounds, R 1 is R 4 R is selected from the group consisting of a saturated linear or branched hydrocarbyl group having up to 10 carbon atoms, which may contain up to three heteroatoms such as N or O, which may be optionally substituted with one or more hydroxy groups, and which hydrocarbyl group is preferably substituted by at least one monocyclic heterocyclic group selected from a saturated or unsaturated or aromatic optionally substituted 5- to 6-membered heterocycle having 1 or 2 heteroatoms selected from N, O and S, preferably N and O, more preferably N. 4 Particularly preferred monocyclic heterocyclic groups in are selected from the group consisting of pyrrolidinyl, piperidyl, 4-alkylpiperazin-1-yl, imidazolyl, and morpholin-4-yl, preferably imidazolyl, and more preferably R 4 is imidazol-1-yl.

[0018] R in formula (I) 1 R 4 Particularly preferred isocyanate-reactive compounds selected from the group consisting of, for example, are selected from: [ka] [ka] [ka] [ka] [ka] [ka] [ka] [ka]

[0019] In a preferred embodiment, R in formula (I) of the isocyanate-reactive compound 1 is R 5 and R 6 wherein R 5 represents a group of the formula [ka] (The dotted line indicates the binding site for X.) Here, R 17 represents an aliphatic, preferably saturated, hydrocarbyl group having at least 3 carbon atoms, preferably up to 10, more preferably up to 6 carbon atoms, and R 7 and R 8each represents a linear or branched aliphatic, preferably saturated hydrocarbyl residue having up to 10, preferably up to 6 carbon atoms, which may optionally be substituted with one or more tertiary amino groups, preferably di(C1-C6)alkylamino groups, and which may optionally contain one or more ether (-O-) groups; R 6 represents a group of the formula [ka] Here, R 18 represents an aliphatic, preferably saturated, hydrocarbyl group having at least 2 carbon atoms, preferably having up to 10, more preferably up to 6 carbon atoms; R 19 represents an aliphatic, preferably saturated, hydrocarbyl group having at least 3 carbon atoms, preferably up to 10, more preferably up to 6 carbon atoms, and R 9 From R 11 each independently represents a straight or branched aliphatic, preferably saturated hydrocarbyl residue having from 1 to 10 carbon atoms, more preferably from 1 to 6 carbon atoms, and even more preferably 1 carbon atom (methyl).

[0020] In a further preferred embodiment, R in formula (I) of the isocyanate-reactive compound 1 is R 5 and R 6 wherein R 5 represents a group of the formula [ka] where n represents an integer of 3 or more, preferably 3 to 10, more preferably 3 to 6, and even more preferably 3; and R 7 and R 8each represents a linear or branched aliphatic, preferably saturated hydrocarbyl residue, preferably having from 1 to 10 carbon atoms, more preferably from 1 to 6 carbon atoms, and even more preferably one carbon atom (methyl), which may optionally be substituted with one or more tertiary amino groups, preferably di(C1-C6)alkylamino groups, and which may optionally contain one or more ether (-O-) groups; and R 6 represents a group of the formula [ka] where o represents an integer of 2 or more, preferably 2 to 10, more preferably 2 to 6, even more preferably 2 or 3, p represents an integer of 3 or more, preferably 3 to 10, more preferably 3 to 6, even more preferably 3, and R 9 From R 11 each represents a straight-chain or branched aliphatic hydrocarbyl residue.

[0021] In a further preferred embodiment, R in formula (I) of the isocyanate-reactive compound 1 is R 5 and R 6 wherein R 5 represents a group of the formula [ka] Here, n is an integer from 3 to 6, and R 7 and R 8 each represents a linear or branched alkyl group having up to 6 carbon atoms, preferably having 1 carbon atom (methyl), and R 6 represents a group of the formula [ka] where o represents an integer from 2 to 6, preferably 2 or 3, p represents an integer from 3 to 6, preferably 3, and R 9 From R 11 each represents a straight or branched alkyl group of up to 6 carbon atoms, preferably methyl.

[0022] In a further preferred embodiment, R in formula (I) of the isocyanate-reactive compound 1 is R 5 and R 6 and the isocyanate-reactive compound is selected from the group consisting of: [ka]

[0023] In a further preferred embodiment, R in formula (I) of the isocyanate-reactive compound 1 is R 14 or R 16 is selected from the group consisting of R 14 represents a group of the formula [ka] Here, R 15 are each independently selected from hydrocarbyl groups, preferably aliphatic, preferably saturated hydrocarbyl groups, having preferably up to 10, even more preferably up to 6, carbon atoms, containing at least one tertiary amino group (especially a dialkylamino group such as a dimethylamino group), and optionally containing one or more ether (—O—) groups; and R 16 represents a phenyl group substituted with an aromatic group, e.g. a C6-C10 aromatic group, preferably with at least two hydrocarbyl, preferably saturated aliphatic groups having up to 6 carbon atoms, each of which contains at least one tertiary amino group (especially a dialkylamino group such as a dimethylamino group).

[0024] R in formula (I)1 R 14 or R 16 Preferred isocyanate-reactive compounds selected from the group consisting of: [ka]

[0025] The isocyanate-reactive compounds which react with the isocyanate compounds are in particular selected from the group of formulae (Ia) and (Ib), R 1 -OH (Ia), R 1 -NH-R 2 (Ib), and R 1 -NH-R 1 (I C), Here, R 1 and R 2 R in formula (Ib) is as defined above. 2 is hydrogen, the formula R 1 A primary amine of formula -NH2(Id) is obtained, where R 1 is as defined above. According to the invention, in particular, R 1 is preferably R 3 Preferred are compounds of formula (Ia) and (Id) selected from:

[0026] Preferably, the isocyanate compounds used to prepare the compounds of the present invention are selected from monoisocyanates and polyisocyanates (having two or more isocyanate groups), and mixtures thereof. The mixtures may include mixtures of monoisocyanates, mixtures of polyisocyanates, or mixtures of one or more monoisocyanates and one or more polyisocyanates. Polyisocyanates are preferred.

[0027] The monoisocyanate may be selected, for example, from aliphatic or aromatic isocyanates such as octadecyl isocyanate; octyl isocyanate; butyl and t-butyl isocyanate; cyclohexyl isocyanate; adamantyl isocyanate; ethyl isocyanatoacetate; ethoxycarbonyl isocyanate; phenyl isocyanate; alpha methylbenzyl isocyanate; 2-phenylcyclopropyl isocyanate; 2-ethylphenyl isocyanate; benzyl isocyanate; meta and para-tolyl isocyanate; 2-, 3-, or 4-nitrophenyl isocyanate; 2-ethoxyphenyl isocyanate; 3-methoxyphenyl isocyanate; 4-methoxyphenyl isocyanate; ethyl 4-isocyanatobenzoate; 2,6-dimethylphenyl isocyanate; 1-naphthyl isocyanate; and (naphthyl)ethyl isocyanate.

[0028] The polyisocyanate is, for example, preferably, isophorone diisocyanate (IPDI); toluene diisocyanate (TDI); diphenylmethane-2,4'-diisocyanate (2,4'-MDI); diphenylmethane-4,4'-diisocyanate (4,4'-MDI); hydrogenated diphenylmethane-4,4'-diisocyanate (H.12MDI); tetramethylxylene diisocyanate (TMXDI); hexamethylene-1,6-diisocyanate. cyanate (HDI);Naphthylene-1,5-diisocyanate;3,3'-dimethoxy-4,4'-biphenyl diisocyanate;3,3'-dimethyl-4,4'-bimethyl-4,4'-biphenyl diisocyanate;Phenylene diisocyanate;4,4'-Biphenyl diisocyanate;Trimethylhexamethylene diisocyanate;Tetramethylene xylene diisocyanate;4,4'-methylenebis(2,6-diethylphenylisocyanate) 1,12-diisocyanatododecane; 1,5-diisocyanato-2-methylpentane; 1,4-diisocyanatobutane; and cyclohexylene diisocyanate, and its isomers or derivatives thereof, such as biurets, isocyanurates, allophanates and oligomers thereof, such as uretdione dimers of HDI; trimethylolpropane trimers of TDI, isocyanurate trimers of TDI, HDI, IPDI; biuret trimers of TDI, HDI or IPDI; and the abovementioned polyisocyanates, in which the isocyanate groups are preferably selected from hydrocarbons which may contain one or more heteroatoms, optionally substituted with OH-, NH- and NH2-functional groups, such as alcohols, such as methanol, tert.-butanol, isopropanol, sec.-butanol, OH-functional monoglycol ethers, OH-functional diglycol ethers, etc. 1 In one embodiment, the polyisocyanate may be selected from aliphatic or aromatic polyisocyanates, preferably aliphatic polyisocyanates, selected from the group consisting of:

[0029] The trivalent or higher aliphatic polyisocyanates include, in particular, biurets, allophanates, urethanes, isocyanurates, and higher oligomers of diisocyanates, in particular hexamethylene diisocyanate (HDI), 1-isocyanato-3,3,5-trimethyl-5-isocyanatomethyl-cyclohexane (IPDI or isophorone diisocyanate) and / or bis(isocyanatocyclohexyl)-methane. Specific examples of such polyisocyanates include, for example: Biurets of hexamethylene diisocyanate and its oligomers, e.g. [ka] commercially available as Desmodur® 100; - isocyanurate trimer of hexamethylene diisocyanate, e.g. [ka] Commercially available as Desmodur® N3300, or higher oligomers thereof such as pentamers: [ka] Or an asymmetric trimer like this: [ka] where R is an isocyanate-containing aliphatic residue derived from HDI or 4,4'-methylenebis(cyclohexylisocyanate) (HMDI or hydrogenated MDI); - isocyanurate trimers of isophorone diisocyanate, e.g. [ka] commercially available as Desmodur® Z4470 or Tolonate IDT 70B; Includes:

[0030] Additional polyisocyanates can be prepared, for example, from polyhydroxy-functional compounds or polymers, preferably with at least an equimolar amount of a diisocyanate, such as HDI, IPDI or HMDI, to form the corresponding polyisocyanate.

[0031] Preferably, the isocyanate compound is isophorone diisocyanate (IPDI), hexamethylene diisocyanate (HDI), and derivatives derived from IPDI and / or HDI, such as biurets, isocyanurates, allophanates, and oligomers thereof, preferably isophorone diisocyanate (IPDI) or hexamethylene-1,6-diisocyanate (HDI) isophorone diisocyanate (IPDI) and hexamethylene-1,6-diisocyanate (HDI), and uretidione dimer; trimethylolpropane trimer , isocyanurate trimers and their biuret trimers, preferably isophorone diisocyanate (IPDI) and hexamethylene-1,6-diisocyanate (HDI). More preferred isocyanate compounds include aliphatic polyisocyanates, preferably aliphatic diisocyanate compounds, especially hexamethylene-1,6-diisocyanate (HDI) and isophorone diisocyanate (IPDI). The most preferred isocyanate compound is isophorone diisocyanate (IPDI).

[0032] In the compounds of the present invention, the isocyanate groups of the polyisocyanate are fully or partially reacted, preferably they are fully reacted with the isocyanate-reactive compound of formula (I). That is, for example, in a diisocyanate compound, by selecting a suitable molar ratio of 1:1 NCO / isocyanate-reactive functional groups (e.g., -OH, -SH, -NH2 or -NHR (R is a hydrocarbyl group)), only one of the two isocyanate groups may react with the isocyanate-reactive compound. Thus, if the number of isocyanate groups in the polyisocyanate is designated v, the number of moles of isocyanate-reactive groups in the isocyanate-reactive compound per isocyanate group in the polyisocyanate compound may be v or less than v. It is also possible to react a molar excess of the isocyanate-reactive compound (relative to the isocyanate groups in the isocyanate compound), thereby preparing a mixture of the compound according to the present invention and the isocyanate-reactive compound. Such compositions of the compounds of the present invention are also included in the scope of the present invention and are described in more detail below.

[0033] Depending on the isocyanate-reactive compound, the compounds according to the invention are compounds of carbamate compounds of formula (II), [ka] Here, R 1 is as defined above, x is 1 to 6, and R 20 is an optionally substituted hydrocarbyl group having a valence of 1 to 6 and optionally containing one or more heteroatoms and attached by a carbon atom to the nitrogen atom of the urethane group; and a urea compound of formula (III): [ka] where one R is R as defined above. 1 and the other R is defined as R above. 1 or R 2 and x and R 20is as defined above, where R 20 is attached to the nitrogen atom of the urea group by a carbon atom, You can choose from.

[0034] base R 20 is derived from an isocyanate compound, including the monoisocyanate and polyisocyanate compounds described above. It is therefore preferably a saturated, unsaturated or aromatic hydrocarbyl group having up to 40 carbon atoms, preferably up to 30 carbon atoms, more preferably up to 20 carbon atoms, which may contain one or more heteroatoms, and even more preferably it is an aliphatic saturated hydrocarbyl group having up to 20 carbon atoms, such as that derived from HDI or IPDI.

[0035] Specific examples of compounds according to the invention are selected, for example, from HDI or IPDI reaction products of the isocyanate-reactive compounds of formula (I) above, in particular from such compounds in which both isocyanate groups have been reacted with an isocyanate-reactive compound of formula (I).

[0036] Particularly preferred compounds according to the invention are [ka] is selected from.

[0037] The present invention further relates to a method for the preparation of the compounds according to the invention, which comprises reacting at least one isocyanate compound with at least one isocyanate-reactive compound of formula (I) as defined above. Preferably, such a method is carried out at a temperature of about 20-140°C, more preferably about 40-120°C, most preferably about 60-100°C, optionally in the presence of one or more diluents and one or more catalysts. Non-reactive diluents / solvents may include, for example, aprotic organic solvents (ethyl acetate, acetone, acetonitrile, ketones, haloalkanes, diglyme, dioxane, ether-diethyl ether, methyl butyl ether, tetrahydrofuran, alkanes, dimethyl sulfoxide (DMSO), dimethylformamide (DMF), toluene, benzene, xylene and analogs thereof or mixtures thereof) that can be used to dissolve or melt the components before mixing them. Preferably, the reaction is carried out with vigorous stirring, and the isocyanate compound is added to the isocyanate-reactive compound under an inert gas atmosphere, or vice versa. The addition of the isocyanate compound is carried out slowly and continuously or in portions and discontinuously. In view of the exothermic reaction, the temperature will rise. In general, it is preferred to carry out the reaction under an inert atmosphere (nitrogen, argon, etc.) to exclude moisture. After the reaction is complete, the diluent / solvent can be partially or completely removed to obtain the final compound, a mixture thereof or a concentrated solution thereof.

[0038] The present invention further relates to a composition comprising one or more compounds according to the present invention, further comprising at least one diluent.Such a diluent can be particularly useful for reducing the viscosity of the composition.Reactive diluents can include compounds that react with polyurethanes in the polyurea-forming reaction, in which the compound of the present invention acts as a catalyst.

[0039] The diluent may in particular comprise an excess of the isocyanate-reactive compound of formula (I) or any other isocyanate-reactive compound or a non-isocyanate-reactive compound, i.e. a diluent that does not react with isocyanates. When using an isocyanate-reactive compound of formula (I), in particular a molar excess of such isocyanate-reactive compound is used, which then serves as a diluent for the composition according to the invention. With regard to such isocyanate-reactive compound of formula (I), reference may be made to the above-mentioned preferred embodiment. After the reaction of at least one isocyanate compound for formula (I) with at least one isocyanate-reactive compound, it is also possible to add any diluent, including any other isocyanate-reactive compound different from formula (I). Such isocyanate-reactive compound different from formula (I) may comprise various types of amines or alcohols, and may also comprise known amine catalysts for polyurethane formation, which are described below.

[0040] Non-reactive diluents / solvents may include, inter alia, dialkyl sulfoxides such as dimethyl sulfoxide, diethyl sulfoxide, diisobutyl sulfoxide, and the like; N,N-dialkyl alkanolamides such as N,N-dimethylformamide, N,N-dimethylacetamide, N,N-diethylacetamide, and the like; phosphonates such as O,O-dimethyl, O,O-diethyl, O,O-diisopropylmethylphosphonate, O,O-di(2-chloroethyl)vinylphosphonate, and the like; aromatic solvents such as toluene, xylene, benzene, and the like; ether solvents such as diethyl ether, dioxane, diglyme, and the like; tetramethylene sulfone, 1-methyl-2-pyrrolidone, trialkyl phosphates such as trimethyl and triethyl phosphate, acetonitrile, and the like, and organic carbonates such as dimethyl carbonate, ethylene carbonate, propylene carbonate, or combinations thereof. The diluents / solvents may be used with co-solvents such as fatty acids, vegetable oils, or combinations thereof. Preferred solvents include glycols, such as ethane-1,2-diol, propane-1,2-diol, propane-1,3-diol, butane-1,4-diol, propane-1,2,3-triol, diethylene glycol, dipropylene glycol, triethylene glycol, tetraethylene glycol, tripropylene glycol, 2-methyl-1,3-propanediol, 2-methyl-2,4-pentanediol. These diluents / solvents may be used as mixtures or co-solvents with the amines.

[0041] A particularly preferred diluent may be water, which may act as a blowing agent in the subsequent polyurethane or polyurea foam-forming reaction in which the compounds of the present invention act as catalysts.

[0042] In a further preferred embodiment of the composition according to the invention, it can optionally contain one or more additional amines or amine catalysts for forming polyisocyanate polyaddition products, such as amines different from the isocyanate-reactive compounds. For example, such catalysts include alkylamines, such as bis(2-dimethylaminoethyl)ether, N,N-dimethylcyclohexylamine, N,N,N',N',N''-pentamethyldiethylenetriamine, N,N,N',N',N''-pentamethyldipropylenetriaminetriethylenediamine, ethanolamines, such as 2-aminoethanol, diethanolamine, triethanolamine, N-methyldiethanolamine, N,N-dimethylethanolamine, N,N-diethylethanolamine, N-methyl ... N-ethylethanolamine, diisopropylamine, bis(2-hydroxypropyl)amine, 2-[2-(dimethylamino)ethoxy]ethanol, 1-[bis[3-(dimethylamino)propyl]amino]-2-propanol, 3-dimethylamino-N,N-dimethylpropionamide, N,N'-dimorpholinodiethyl ether, N,N'-dimethylpiperazine, N-methylmorpholine, N-ethylmorpholine, 2-{[2-(dimethylamino)ethyl]methylamino}ethanol, 3,3'-iminobis(N,N-dimethylpropylamine), 3-(dimethylamino)-1-propylamine, 3-(diethylamino)-1-propanol, 1-(3-hydroxypropyl)pyrrolidine, 1-(2-hydroxypropyl)pyrrolidine, 1-(2-hydroxyethyl)pyrrolidine, 1-(2-hydroxyethyl)piperidine, 1-(3-hydroxypropyl)piperidine, 1-(2-hydroxypropyl)piperidine, 1-(3-aminopropyl)pyrrolidine, 1-(2-aminoethyl)pyrrolidine, 1-(3-aminopropyl)piperidine, 1-(2-aminoethyl)piperidine, 1-(1-pyrrolidinyl)-2-propanamine, 1-(piperidin-1-yl)propan-2-amine, N-methoxyethylmorpholine, N-methylimidazole, 1-(3-aminopropyl)imidazole, 2-[2-[2-(dimethylamino)ethoxy]ethyl-methylamino]ethanol, N-methyldicyclohexyl amine, 3-{[3-(dimethylamino)propyl]methylamino}propanol, tris(dimethylaminopropyl)amine, 2-{[3-(dimethylamino)propyl]methylamino}ethanol, N,N,N',N'-tetramethylhexamethylenediamine, N,N,N',N'-tetramethylethylenediamine, 2,4,6-tris(dimethylaminomethyl)phenol, 1,3,5-tris(dimethylaminopropyl)-hexahydrotriazine, N,N-dimethylbenzylamine, 1,8 diazabicyclo-5,4,0 undecene-7, N-methyl-N'-(2-dimethylamino)ethyl-piperazine, N,N'-bis[3-(dimethylamino)propyl]urea, N-[3-(dimethylamino)propyl]urea, N,N,N',N'-tetrakis(2-hydroxypropyl)ethylenediamine, and N,N,N',N'-tetrakis(2-hydroxyethyl)ethylenediamine. Preferred amines include alkyl amines, such as bis(2-dimethylaminoethyl)ether, N,N-dimethylaminopropylamine, N,N-dimethylcyclohexylamine, N,N,N',N',N''-pentamethyldiethylenetriamine, triethylenediamine, ethanolamines such as diethanolamine, 2(2-dimethylaminoethoxy)ethanol, N-[2-(dimethylamino)ethyl]-N-methylethanolamine, dimethylethanolamine, or other amines such as 3-dimethylamino-N,N-dimethylpropionamide and N-ethylmorpholine, triethanolamine, 2-dimethylaminoethanol, N,N-dimethylaminopropylamine, diethanolamine, trimethylamine, triethylenediamine, bis(2-dimethylaminoethyl)ether.

[0043] Preferred compositions according to the present invention comprise one or more compounds according to the present invention, further comprising at least one conventional polyurethane-forming catalyst, preferably at least one conventional polyurethane foam-forming gel catalyst as described above.

[0044] Another preferred composition comprises one or more compounds according to the invention, further comprising at least one carboxylic acid. In a preferred embodiment, the composition according to the invention comprises at least one carboxylic acid, such as those described in US 6,387,972 B1. Preferably, the carboxylic acid is selected from the group consisting of monocarboxylic acid compounds, such as benzoic acid, polycarboxylic acid compounds, such as dicarboxylic acid compounds, such as oxalic acid, malonic acid, succinic acid, glutaric acid, adipic acid, azelaic acid, sebacic acid, and hydroxyl functional carboxylic acid compounds, in particular salicylic acid, citric acid. In a particularly preferred embodiment, the composition comprises at least one carboxylic acid selected from the group consisting of salicylic acid, benzoic acid, oxalic acid, malonic acid, succinic acid, glutaric acid, adipic acid, azelaic acid, sebacic acid, and citric acid.

[0045] The compound or composition according to the present invention is preferably used as a catalyst for catalyzing the reaction of at least one isocyanate compound with at least one isocyanate-reactive compound, i.e., as a catalyst for the production of polyisocyanate polyaddition products. Such polyisocyanate polyaddition products have one or more functional groups, in particular consisting of groups selected from urethane groups and urea groups. The compound or composition according to the present invention is preferably used as a catalyst for the production of polyurethanes, in particular polyurethane foams, most preferably as a blowing catalyst for the production of polyurethane foams, which acts as a blowing agent, in particular catalyzing the blowing reaction of water with isocyanate and producing CO2 gas.

[0046] The present invention therefore also relates to a catalyst comprising a compound or composition according to the invention, in particular a catalyst composition comprising a compound according to the invention and one or more further catalysts for the production of polyisocyanate polyaddition products.

[0047] The present invention therefore also relates to a process for the preparation of an isocyanate addition product, comprising reacting an isocyanate compound, in particular a polyisocyanate compound, with an isocyanate-reactive compound in the presence of a compound or composition according to any of the present invention. Such a process for the preparation of an isocyanate addition product comprises in particular reacting an isocyanate compound, preferably a polyisocyanate compound, with an isocyanate-reactive compound in the presence of a compound or composition according to the present invention in the presence of water. In the process for the preparation of an isocyanate addition product using a compound or composition according to the present invention as catalyst, the isocyanate is preferably a polyisocyanate and the isocyanate-reactive compound is preferably a polyol, and the process is for the preparation of a polyurethane, in particular a polyurethane foam.

[0048] In the process for producing an isocyanate addition product according to the present invention, the isocyanate addition product is preferably a polyurethane, more preferably a polyurethane foam selected from cellular or non-cellular polyurethanes, and preferably the process optionally comprises a blowing agent, more preferably water.

[0049] The process for the production of an isocyanate addition product according to the present invention is preferably for producing a polyurethane, and the process optionally includes the addition of a surfactant, a flame retardant, a chain extender, a crosslinker, an adhesion promoter, an antistatic additive, a hydrolysis stabilizer, a UV stabilizer, a lubricant, an antimicrobial agent, or a combination of two or more thereof.

[0050] In the process for the preparation of an isocyanate addition product according to the present invention, the compound or composition according to the present invention is present in an amount of about 0.005% to about 5% by weight, based on the total weight of the entire composition including all components.

[0051] The present invention also relates to foam-forming isocyanate addition products obtained from the process for the production of the isocyanate addition products of the present invention. Particularly preferred foam-forming isocyanate addition products can be selected, for example, from the group consisting of slabstock, molded foam, flexible foam, rigid foam, semi-rigid foam, spray foam, thermoformable foam, microcellular foam, footwear foam, open-cell foam, closed-cell foam, adhesives.

[0052] The process for the preparation of polyurethanes using the compounds or compositions according to the invention as catalysts is described in more detail below.

[0053] The term "polyurethane" as used herein refers to the reaction product of an isocyanate containing two or more isocyanate groups with a compound containing two or more active hydrogens, such as polyols (copolymer polyols also known as polyether polyols, polyester polyols, graft polyols) and / or primary and secondary amine-terminated polymers known as polyamines. These reaction products are commonly known to those skilled in the art as polyurethanes and / or polyureas. The reaction in forming cellular and non-cellular foams optionally includes a blowing agent. In the production of polyurethane foams, the reaction includes a blowing agent and other optional ingredients, such as surfactants, flame retardants, chain extenders, crosslinkers, adhesion promoters, antistatic additives, hydrolysis and UV stabilizers, lubricants, antimicrobial agents, catalysts and / or other application-specific additives that can be used in the production of compact or cellular polyurethane materials (The polyurethanes book, Editors David Randall and Steve Lee, John Willey& Sons, LTD, 2002). The catalyst material of the present invention is particularly suitable for producing flexible, semi-flexible, and rigid foams using one-shot blowing, quasi-prepolymer, and prepolymer processes. The polyurethane production process of the present invention typically includes the reaction of a polyol, generally having a hydroxyl value of about 10 to about 700, an organic polyisocyanate, a blowing agent and optional additives known to those skilled in the art, and one or more catalysts, at least one of which is selected from the subject tertiary amine compounds. As the blowing agent and optional additives, flexible and semi-flexible foam formulations (hereinafter simply referred to as flexible foams) generally also include, for example, water, an organic low-boiling auxiliary blowing agent or optional non-reactive gas, a silicone surfactant, an optional catalyst other than the catalyst according to the present invention, and an optional crosslinking agent or agents. Rigid foam formulations often include both a low-boiling organic material and water for blowing.The "one-shot foam process" for producing polyurethane foam is a one-step process in which all of the necessary (or desired) ingredients for producing a foamed polyurethane product, including polyisocyanates, organic polyols, water, catalysts (catalysts of the present invention and others), surfactant(s), optional blowing agents, etc., are efficiently mixed and poured onto a moving conveyor or into a mold of suitable shape for curing (Chemistry and Technology of Polyols for Polyurethanes, by MihailIonescu, Rapra Technology LTD. (2005)). The one-shot process is to be contrasted with the prepolymer and quasi-prepolymer processes (Flexible polyurethane foams, by Ron Herrington and Kathy Hock, DowPlastics, 1997). In the prepolymer process, most prepolymers currently used are isocyanate-tipped. The addition of just enough polyisocyanate to react with all available hydroxyl sites results in the formation of a true prepolymer. If excess or residual isocyanate monomer is present, the product is called a quasi-prepolymer. A prepolymer or quasi-prepolymer is first prepared in the absence of foam-forming ingredients. In a second step, a high molecular weight polyurethane material is formed in the presence of a catalyst by reaction of the prepolymer with water and / or a chain extender, such as ethylene glycol, diethylene glycol, 1,4-butanediol or a diamine.

[0054] The catalyst compounds and compositions of the present invention can be used as the sole catalyst or in combination with one or more additional catalysts for forming polyisocyanate addition products, such as the tertiary amine catalysts described above.

[0055] Further, the catalyst composition of the present invention may comprise two or more different compounds according to the present invention described above. The catalyst compound or composition of the present invention may be present in the reactive mixture for forming polyurethane containing all necessary components in an amount of about 0.005% to about 5%; preferably about 0.01% to about 3.0%; or more preferably about 0.03% to about 1.00% by weight of the total reactive composition. Other catalysts useful for making polyurethane foam include, for example, tertiary amines such as the alkylamines described above, organometallic catalysts such as organotin catalysts, metal salt catalysts such as alkali metal or alkaline earth metal carboxylate catalysts, other delayed action catalysts, or other known polyurethane catalysts. Organometallic or metal salt catalysts can also be, and are often, used in polyurethane foam formulations. For example, for flexible slabstock foams, the generally preferred metal salt and organometallic catalysts are stannous octoate and dibutyltin dilaurate, respectively. For flexible molded foams, exemplary organometallic catalysts are dibutyltin dilaurate and dibutyltin dialkyl mercaptides. For rigid foams, exemplary metal salt and organometallic catalysts are potassium acetate, potassium octanoate, and dibutyltin dilaurate, respectively. Metal salt or organometallic catalysts are usually used in small amounts in polyurethane formulations, typically from about 0.001 parts per hundred (pphp) to about 0.5 pphp based on the total weight of the composition.

[0056] Polyols useful in the process of the present invention for producing polyurethanes, particularly in the one-shot foaming procedure, are any of the types currently used in the art for the production of flexible slabstock foams, flexible molded foams, semi-flexible foams, and rigid foams. Such polyols are typically liquid at ambient temperature and pressure and include polyether polyols and polyester polyols having hydroxyl numbers ranging from about 15 to about 700. The hydroxyl number is preferably about 20 to about 60 for flexible foams, about 100 to about 300 for semi-flexible foams, and about 250 to about 700 for rigid foams.

[0057] For flexible foams, the preferred functionality of the polyol, i.e., the average number of hydroxyl groups per polyol molecule, is from about 2 to about 4, most preferably from about 2.3 to about 3.5. For rigid foams, the preferred functionality is from about 2 to about 8, most preferably from about 3 to about 5.

[0058] Of the polyamines different from the compounds according to the invention which are useful in the process of the invention for producing polyurethanes, diamines such as piperazine, 2,5-dimethylpiperazine, bis(4-aminophenyl)ether, 1,3-phenylenediamine and hexamethylenediamine are preferred.

[0059] Polyfunctional isocyanate-reactive compounds that can be used alone or in mixtures as copolymers in the process for producing polyurethanes and / or polyureas in the presence of the catalyst composition of the present invention include, for example, any of the following non-limiting classes of polyols: (a) polyether polyols derived from the reaction of polyhydroxyalkanes with one or more alkylene oxides, such as ethylene oxide, propylene oxide, and the like; (b) polyether polyols derived from the reaction of mixtures of higher functional alcohols, sugar alcohols, saccharides and / or higher functional amines, optionally lower functional alcohols and / or amines, with alkylene oxides, e.g., ethylene oxide, propylene oxide, and the like; (c) polyether polyols derived from the reaction of phosphoric and polyphosphorous acids with alkylene oxides, e.g., ethylene oxide, propylene oxide, and the like; (d) polyether polyols derived from the reaction of polyaromatic alcohols with alkylene oxides, such as ethylene oxide, propylene oxide, and the like; (e) polyether polyols derived from the ring-opening polymerization reaction of tetrahydrofuran; (f) polyether polyols derived from the reaction of ammonia and / or amines with alkylene oxides, such as ethylene oxide, propylene oxide, and the like; (g) polyester polyols derived from the reaction of a polyfunctional initiator, such as a diol, with a hydroxycarboxylic acid or its lactone, such as hydroxylcaproic acid or ε-caprolactone; (h) polyoxamate polyols derived from the reaction of oxalic acid esters and diamines, such as hydrazine, ethylenediamine, etc., with direct polyether polyols; (i) Polyurea polyols derived from the reaction of diisocyanates and diamines, such as hydrazine, ethylene diamine, etc., directly with polyether polyols.

[0060] For flexible foams, the preferred types of alkylene oxide adducts of polyhydroxyalkanes are the ethylene oxide and propylene oxide adducts of aliphatic triols such as glycerol, trimethylolpropane, etc. For rigid foams, the preferred classes of alkylene oxide adducts are the ethylene oxide and propylene oxide adducts of ammonia, toluene diamine, sucrose, and phenol-formaldehyde-amine resins (Mannich bases).

[0061] Graft polyols or polymer polyols are widely used in the production of flexible foams and, together with standard polyols, are one of the preferred classes of polyols useful in the process of the present invention. Polymer polyols are polyols that contain stable dispersions of polymers, such as polyols a) to e) above, more preferably polyols of type a). Other polymer polyols useful in the process of the present invention are polyurea polyols and polyoxamate polyols.

[0062] Polyisocyanates useful in the polyurethane foam forming process of the present invention are organic compounds containing at least two isocyanate groups and will generally be any of the known aromatic or aliphatic polyisocyanates. Suitable organic polyisocyanates include, for example, the hydrocarbon diisocyanates (e.g., alkylene diisocyanates and arylene diisocyanates), such as methylene diphenyl diisocyanate (MDI) and 2,4- and 2,6-toluene diisocyanate (TDI), as well as the known triisocyanates and polymethylene poly(phenylene isocyanates) (also known as polymeric or crude MDI). For flexible and semi-flexible foams, preferred isocyanates are generally, for example, mixtures of 2,4-toluene diisocyanate and 2,6-toluene diisocyanate (TDI), in weight percentages of about 80% and about 20%, respectively, and about 65% and about 35%, respectively, based on the total weight of the composition; mixtures of TDI and polymeric MDI, preferably in weight percentages of about 80% TDI and about 20% crude polymeric MDI to about 50% TDI and about 50% crude polymeric MDI, based on the total weight of the mixed composition; all polyisocyanates of MDI type. For rigid foams, preferred isocyanates are, for example, isocyanates of MDI type and preferably crude polymeric MDI.

[0063] The amount of polyisocyanate included in a foam formulation used relative to the amount of other materials in the formulation is described in terms of "isocyanate index". "Isocyanate index" means the actual amount of polyisocyanate used divided by the theoretically required stoichiometric amount of polyisocyanate required to react with all the active hydrogens in the reaction mixture, multiplied by 100 (see Oertel, Polyurethane Handbook, Hanser Publishers, New York, NY (1985)). The isocyanate index in the reaction mixture used in the process of the present invention is generally between 60 and 140. More generally, the isocyanate index is typically 85 to 120 for flexible TDI foams; typically 90 to 105 for molded TDI foams; usually 70 to 90 for molded MDI foams; and generally 90 to 130 for rigid MDI foams. Some examples of polyisocyanurate rigid foams have been produced with isocyanate indexes as high as 250-400.

[0064] In the polyurethane-forming reaction according to the invention using the compounds of the invention as catalysts, it is preferred to use water as a reactive blowing agent in both flexible and rigid foams. In the production of flexible slabstock foams, water can generally be used at a concentration of, for example, 2 to 6.5 parts per hundred parts of polyol formulation (pphp), more often 3.5 to 5.5 pphp of the polyol formulation. The water level of TDI molded foams is usually in the range of, for example, 3 to 4.5 pphp of the polyol formulation. For MDI molded foams, for example, the water level is usually 2.5 to 5 pphp. The water level of rigid foams is in the range of, for example, 0.5 to 5 pphp, more often 0.5 to 2 pphp of the polyol formulation. Physical blowing agents such as blowing agents based on volatile or halogenated hydrocarbons and other non-reactive gases can also be used in the production of polyurethane foams according to the invention. The majority of rigid insulating foams produced are blown with volatile or halogenated hydrocarbons, with the preferred blowing agents being hydrochlorofluorocarbons (HCFCs) and the volatile hydrocarbons pentane and cyclopentane. In the production of flexible slabstock foams, water is the primary blowing agent; however, other blowing agents can be used as auxiliary blowing agents. For flexible slabstock foams, the preferred auxiliary blowing agents are carbon dioxide and dichloromethane (methylene chloride). Other blowing agents, such as chlorofluorocarbons (CFCs) and trichloromonofluoromethane (CFC-11), can also be used.

[0065] Flexible molded foams do not typically use inert auxiliary blowing agents, and in any case incorporate less auxiliary blowing agents than slabstock foams. However, there is considerable interest in using carbon dioxide in some molding techniques. MDI molded foams in Asia and some developing countries use methylene chloride, CFC-11 and other blowing agents. The amount of blowing agent varies according to the desired foam density and foam hardness, as will be recognized by those skilled in the art. If used, the amount of hydrocarbon-type blowing agents varies, for example, from trace amounts to about 50 parts per 100 parts of polyol formulation (pphp), and CO2 varies from about 1 to about 10 pphp of polyol formulation.

[0066] Crosslinking agents can also be used in the production of polyurethane foams. Crosslinking agents are usually small molecules; usually with a molecular weight less than 350 and containing active hydrogens for reacting with isocyanates. The functionality of the crosslinking agent is greater than 3, preferably between 3 and 5. The amount of crosslinking agent used can vary between about 0.1 pphp to about 20 pph based on the polyol formulation, and the amount used is adjusted to achieve the required foam stabilization or foam hardness. Examples of crosslinking agents include glycerin, diethanolamine, triethanolamine, and tetrahydroxyethylethylenediamine.

[0067] Silicone surfactants that can be used in the process of the present invention include, for example, "hydrolyzable" polysiloxane-polyoxyalkylene block copolymers, "non-hydrolyzable" polysiloxane-polyoxyalkylene block copolymers, cyanoalkylpolysiloxanes, alkylpolysiloxanes, and polydimethylsiloxane oils. The type of silicone surfactant used and the amount required will depend on the type of foam being produced, as will be appreciated by those skilled in the art. The silicone surfactant can be used as is or dissolved in a solvent such as glycol. For flexible slabstock foams, the reaction mixture typically contains about 0.1 to about 6 pphp of silicone surfactant, more often about 0.7 to about 2.5 pphp. For flexible molded foams, the reaction mixture typically contains about 0.1 to about 5 pphp of silicone surfactant, more often about 0.5 to about 2.5 pphp. For rigid foams, the reaction mixture typically contains about 0.1 to about 5 pphp of silicone surfactant, more often about 0.5 to about 3.5 pphp. The amount of surfactant used is adjusted to achieve the desired foam cell structure and foam stability.

[0068] Useful temperatures for the production of polyurethanes vary depending on the type of foam and the particular process used to produce it, as is well understood by those skilled in the art. Flexible slabstock foams are usually produced by mixing the reactants at ambient temperatures between about 20°C and about 40°C. The conveyor on which the foam rises and cures is essentially at ambient temperature, which can vary widely depending on the region and season in which the foam is made. Flexible molded foams are usually produced by mixing the reactants at temperatures between about 20°C and about 30°C, more often between about 20°C and about 25°C. The mixed starting materials are typically delivered to a mold by pouring. The mold is preferably heated to a temperature between about 20°C and about 70°C, more often between about 40°C and about 65°C. Sprayed rigid foam starting materials are mixed and sprayed at ambient temperatures. Molded rigid foam starting materials are mixed at temperatures ranging from about 20°C to about 35°C. The preferred process used to make flexible slabstock, molded, and rigid foams in accordance with the present invention is the "one-shot" process, in which the starting materials are mixed and reacted in one step.

[0069] Thus, one embodiment of the present invention relates to a method for the preparation of an isocyanate addition product according to any of the preceding claims, wherein the isocyanate addition product is a polyurethane foam, preferably selected from cellular or non-cellular polyurethanes, and the method optionally includes a blowing agent. Such a method optionally includes the addition of surfactants, flame retardants, chain extenders, crosslinkers, adhesion promoters, antistatic additives, hydrolysis stabilizers, UV stabilizers, lubricants, antimicrobial agents, or other common auxiliary additives used in the preparation of polyurethanes, or a combination of two or more thereof. Thus, one embodiment of the present invention also relates to a foam-forming isocyanate addition product formed from the aforementioned method for the preparation of an isocyanate addition product using the catalyst composition of the present invention. Such foam-forming isocyanate addition products are, for example, selected from the group consisting of slabstock, molded foam, flexible foam, rigid foam, semi-rigid foam, spray foam, thermoformable foam, footwear foam, open-cell foam, closed-cell foam, and adhesives.

[0070] While the scope of the present invention is defined by the appended claims, the following examples describe certain aspects of the invention, and more particularly, the evaluation methods thereof. The examples are presented for illustrative purposes and should not be construed as limitations on the invention. EXAMPLES

[0071] example Example of catalyst formation First, an 80 wt% aqueous solution of C1 from US6423756B1 (C1 is the reaction product of dimethylaminoethoxyethanol and isophorone diisocyanate) was prepared and further used as an amine catalyst with mainly gel properties. The 80% aqueous solution of C1 is called C1.1.

[0072] Catalyst 1 of the present invention (or IC1) [reaction product of 2 mol of N,N,N'-trimethyl-N'-(2-hydroxyethyl)bis(2-aminoethyl)ether with 1 mol of isophorone diisocyanate]

[0073] Four bare 250 mL round bottom flasks were then fitted with thermometers, mechanical stirrers, and reflux condensers. The flasks were flushed with dry nitrogen. Under a nitrogen atmosphere, N,N,N'-trimethyl-N'-(2-hydroxyethyl)bis(2-aminoethyl)ether (96.09 g, 0.505 mol) was charged to the flasks. Isophorone diisocyanate (55.58 g, 0.25 mmol) was added over 30 min while vigorously stirring the reaction mixture and maintaining the temperature of the reaction mixture below 80 °C. After the complete addition of isophorone diisocyanate, the reaction mixture was heated at 75 °C for 2.5 h to give a clear, viscous product. 43.32 g of product. 13 C and 1 H NMR data confirmed the formation of catalyst 1 of the present invention (IC1, shown below as the reaction product). 43.32 g of IC1 was dissolved in 10.83 g of water to give an 80 wt% aqueous solution, IC1.1, which was used in the polyurethane foam production. Additionally, 71.70 g of IC1 was dissolved in 10.43 g of dipropylene glycol to give IC1.2, which was used in the polyurethane foaming reaction. [ka]

[0074] Catalyst 2 of the invention (or IC2) [reaction product of 2 moles of 2-{2-[(3-aminopropyl)(methyl)amino]ethoxy}ethyl)dimethylamine (or N'-[2-[2-(dimethylamino)ethoxy]ethyl]-N'-methyl-propane-1,3-diamine) with 1 mole of isophorone diisocyanate] [ka]

[0075] To a 10 mL glass vial equipped with a magnetic stirrer, 2.03 g (10 mmol) of 2-{2-[(3-aminopropyl)(methyl)amino]ethoxy}ethyl)dimethylamine was added under nitrogen atmosphere and the vial was sealed with a septum cap. 1.11 g of isophorone diisocyanate (5.0 mmol) was added dropwise while the reaction mixture was vigorously stirred. The mixture was vigorously stirred for approximately 5 min and the vial was placed in a 75 °C heating block. After 2 h, the vial was removed from the heating block and allowed to cool to room temperature. A clear glassy highly viscous mass was obtained. 13 C and 1 1 H NMR data confirmed the formation of catalyst 2 of the present invention (IC2, shown as the reaction product in the scheme above).

[0076] Foaming experiment: Polyurethane foams were prepared according to the following procedure: A premix P1 of 4950.00 g of reactive polyether polyol (Hyperlite® (or HP) 1629; hydroxyl number 29.5-33.5 mg KOH / g), 49.50 g of EO rich cell opener (Voranol® CP1421; hydroxyl number 33 mg KOH / g), 32.67 g of a 90 wt% aqueous solution of diethanolamine (DEOA 90% in water), 29.70 g of silicone stabilizer (Niax® Silicone L-3639S), 148.50 g of water and 39.60 g of the predominantly gel catalyst C1.1 (for polyurethane foams as shown in Table 1) was prepared by thoroughly mixing the mixture in a plastic bucket for 20 minutes using a propeller stirrer with a ring at 800 rpm. From the premixes, single batches of 291.67 g each were weighed into a suitable mixing plastic container, and additional amounts of water and corresponding catalysts (e.g., C1.1, IC1.1) were added to obtain the final polyol formulations adjusted according to the ratios in Table 1.

[0077] For the foam systems shown in Table 2, premixes P2 were prepared without adding water and catalyst by thoroughly mixing the mixture in a plastic bucket for 20 minutes using a propeller stirrer with ring at 800 rpm. For the foam compositions after preparing the premixes, single batches of 281.22 g each were weighed into a suitable mixing plastic container. The required amount of water and the corresponding catalyst (e.g., C1.1, IC1.1) were added to obtain the final polyol formulation according to the ratios shown in Table 2.

[0078] To produce the foam pads, the polyol formulation was thoroughly mixed in a plastic container for 30 seconds using a propeller stirrer with a ring at 3000 rpm. A specified amount of Suprasec 2447 isocyanate (MDI, NCO content 32.6%) was added according to the ratios shown in Table 1 or 2, and the reaction mixture was mixed for 4-6 seconds. The reaction mixture was immediately poured into an aluminum mold of 30 x 30 x 10 cm, and the mold was immediately closed and clamped. The mold lid had four vent holes with a diameter of 0.4 mm at the four corners. The mold temperature was controlled at 55°C via a hot water circulating thermostat. A mold release agent Chem-Trend® PU-1705M was used to coat the mold. The foam was demolded after 4 minutes. The processing and physical properties of the foam were evaluated as follows: [Table 1A]

[0079] A summary of the PU foam composition and PU foam properties is given in Table 1 below for reactive mixtures 1 to 4 (the chemical composition is given in parts per weight or pbw). [Table 1B]

[0080] It was found that the addition of the catalyst solution IC1.1 of the present invention to the catalyst solution C1.1 significantly improved the foaming efficiency of the catalyst formulation. Thus, the exit time of reaction mixture 1 was 78 seconds, while the exit time of reaction mixture 3 was 60 seconds, although the total weight of active catalyst in their comparative runs 1 and 3 is the same (0.80+0.25=1.05 pbw). Similarly, a comparison of the exit time from run 2 (52 seconds) with run 4 clearly shows the higher foaming efficiency of the catalyst solution IC1.1 of the present invention. Furthermore, it was found that the ILD values ​​of the PU foams produced using the catalyst solution IC1.1 of the present invention tend to be advantageously higher compared to the PU foams produced using only the state-of-the-art catalyst solution C1.1. This trend is shown by a comparison of the ILD values ​​of foams 2 and 4, made with higher catalyst usage levels (0.80+0.75=1.55 pbw). In particular, the catalyst composition of 0.80 pbw C1.1 and 0.75 pbw IC1.1 (Reaction Mixture 4) provided PU foams with higher ILD values ​​compared to the PU foam obtained from Reaction Mixture 2 where C1.1 was used as the only one at a usage level of 1.55 pbw.

[0081] The experimental summary shown in Table 2 below shows a comparison where only a single catalyst was used and the catalyst of the invention in solution IC1.1 is compared to the state-of-the-art catalyst in solution C1.1. [Table 2] *After demolding, the foam was very soft, sticky and brittle, indicating incomplete curing, which is also evident from the low FTC and hot ILD values. After demolding, the foam skin was wrinkled. Therefore, it is not recommended to use the ILD value of this foam for further discussion.

[0082] The foaming efficiency of the inventive catalyst IC1.1 was found to be significantly higher compared to the state of the art catalyst C1.1. Thus, the exit time of reaction mixture A1 catalyzed by IC1.1 is 83 seconds, while the exit time of reaction mixture A3 catalyzed by state of the art catalyst C1.1 is significantly higher, 143 seconds. Furthermore, compared to PU foam A1, foam A3 is very soft, sticky and fragile after demolding, as evidenced by the lower FTC and hot ILD values. The skin of PU foam A3 was wrinkled after demolding, confirming incomplete polymerization. Similarly, the comparison of the exit time from run A2 (44 seconds) with run A4 clearly indicates the better foaming efficiency of the inventive catalyst IC1. Furthermore, the faster exit time plus the favorable higher hot ILD and ILD values ​​of A2 PU foam compared to A4 PU foam demonstrate the better curing efficiency of the inventive catalyst IC1.1.

[0083] The following polyurethane foams based on TDI were prepared according to the following procedure: A premix P3 of 1425.00 g of reactive polyether polyol (Hyperlite® Polyol 1629; hydroxyl number 29.5-33.5 mg KOH / g), 1425.00 g of styrene-acrylonitrile (SAN) polymer modified reactive polyether polyol with 43% SAN content (Hyperlite® Polyol 1639; hydroxyl number 20 mg KOH / g), 34.20 g of a 90% by weight aqueous diethanolamine solution (DEOA 90% in water), 28.50 g of silicone stabilizer (Niax® Silicone L-3555), and 85.50 g of water was prepared by thoroughly mixing the mixture in a plastic bucket for 20 minutes using a propeller stirrer with a ring at 800 rpm. From premix P3, a single batch of 315.60 g each was weighed into a suitable mixing plastic container, and additional amounts of water and the corresponding catalysts in solution (e.g., C1.1, IC1.1) were added to obtain the final polyol formulation according to the ratios shown in Table 3. To produce the PU foam pads, the polyol formulation was thoroughly mixed in a plastic container using a propeller stirrer with a ring at 3000 rpm for 30 seconds. A specified amount of Scuranate T80 isocyanate (TDI, NCO content 48.1%) was added according to the ratios shown in Table 3, and the reaction mixture was mixed for 4-6 seconds. The reaction mixture was immediately poured into an aluminum mold of 30 x 30 x 10 cm, and the mold was immediately closed and clamped. The mold lid had four vent holes with a diameter of 0.4 mm at the four corners. The mold temperature was controlled at 65°C by a hot water circulation thermostat. The mold release agent Chem-Trend® PU-1705M was used to coat the mold. The foam was demolded after 5 minutes. The processing and physical properties of the foams were evaluated as described above.

[0084] Table 3 lists the reactive mixtures B1 to B4 of the PU foam compositions in pbw and the physical properties of the corresponding PU foams. [Table 3] *After demolding, the foam was very soft, sticky and brittle, indicating incomplete curing, which is also evident from the low FTC and hot ILD values. After demolding, the foam skin was wrinkled. Therefore, it is not recommended to use the ILD value of this foam for further discussion.

[0085] The foaming efficiency of the inventive catalyst IC1.1 was found to be significantly higher compared to the state of the art catalyst C1.1. Thus, the exit time of reaction mixture B1 catalyzed by IC1.1 is 49 seconds, while the exit time of reaction mixture B3 catalyzed by state of the art catalyst C1.1 is significantly higher, at 68 seconds. Furthermore, compared to foam B1, foam B3 is very soft, sticky and more fragile after demolding, as evidenced by the lower FTC and hot ILD values. The skin of foam B3 was very wrinkled after demolding, confirming incomplete polymerization. Similarly, a comparison of the exit time from run B2 (33 seconds) with run B4 clearly indicates the better foaming efficiency of the invented catalyst. Moreover, the trend for the advantageously higher hot ILD and ILD values ​​of B2 foam compared to B4 foam, in addition to the faster exit time, demonstrates the better curing efficiency of the inventive catalyst IC1.1.

Claims

1. Compounds obtained by reaction of isophorone diisocyanate (IPDI) with at least one isocyanate-reactive compound of formula (I), (R) ａ -X (I) where R is R １ and R ２ is selected from, where R １ is R ３ wherein R ３ represents a hydrocarbyl group containing at least two tertiary amino groups and at least one ether (—O—) group; R ２ represents a hydrocarbyl group or hydrogen; a is 2 or 3, and X is selected from the group consisting of O, S, or N; However, the compound contains at least one group R １ and hydrogen R ２ with the proviso that it contains at least one group R which is or a salt thereof, and a mixture thereof.

2. R in formula (I) of the isocyanate-reactive compound １ R is selected from the group consisting of saturated aliphatic hydrocarbyl groups having up to 20 carbon atoms and containing at least two tertiary amino groups and at least one ether (—O—) group. ３ 2. The compound of claim 1 selected from the group consisting of:

3. R １ R is selected from the group consisting of saturated aliphatic hydrocarbyl groups having up to 15 carbon atoms and containing at least two tertiary amino groups and at least one ether (—O—) group. ３ 3. The compound of claim 2 selected from the group consisting of:

4. R in formula (I) of the isocyanate-reactive compound １ is selected from the following formulas: ３ is selected from the group consisting of 【Chemistry 14】 Here, R １３ The groups are independently selected from divalent linear, branched or cyclic hydrocarbyl groups, and two of A, B, and C represent tertiary amino groups (A and B are each independently -N(R １２ )-, and for C, -N(R １２ ) ２ where R １２ is an alkyl group), and one of A, B, C represents an ether group (A and B are selected from -O-, and C is selected from -OR １２ where R １２ is as defined above), the compound of claim 1.

5. R in formula (I) of the isocyanate-reactive compound １ is selected from the following formulas: ３ is selected from the group consisting of 【Chemistry 15】 where x, y, and z are integers from 2 to 6, and two of A, B, and C represent tertiary amino groups (A and B are each -N(R １２ )-, and for C, -N(R １２ ) ２ where R １２ is an alkyl group), and one of A, B, C represents an ether group (A and B are selected from -O-, and C is selected from -OR １２ where R １２ is as defined above), the compound of claim 1.

6. The compound of claim 5, wherein x, y, and z are 2 or 3.

7. R in formula (I) of the isocyanate-reactive compound １ is R ３ and wherein the isocyanate-reactive compound is selected from the group consisting of: 【Chemistry 16】 7. The compound according to any one of claims 1 to 6, selected from the group consisting of:

8. The at least one isocyanate-reactive compound is selected from the group of formulas (Ia) and (Ib): R １ -OH (Ia)、 R １ -NH-R ２ (Ib), and R １ -NH-R １ (Ic)、 Here, R １ and R ２ 8. The compound according to claim 1 , wherein each of the formulas is as defined above.

9. 【Chemical 34】 9. The compound according to claim 1 , selected from:

10. 10. A composition comprising one or more compounds according to any of claims 1 to 9, further comprising at least one diluent, at least one conventional polyurethane-forming catalyst, or at least one carboxylic acid selected from the group consisting of monocarboxylic acid compounds, polycarboxylic acid compounds, and hydroxyl-functional carboxylic acid compounds.

11. 11. A composition comprising one or more compounds of claim 10, wherein the polyurethane-forming catalyst is a polyurethane foam-forming gel catalyst.

12. 12. The composition of claim 10 or 11, wherein the at least one carboxylic acid is selected from the group consisting of salicylic acid, benzoic acid, oxalic acid, malonic acid, succinic acid, glutaric acid, adipic acid, azelaic acid, sebacic acid, and citric acid.

13. 13. Use of a compound or composition according to any one of claims 1 to 12 as a catalyst for the production of polyurethanes.

14. 14. Use of a compound or composition according to claim 13, wherein the polyurethane is a polyurethane foam.

15. 13. A process for the preparation of an isocyanate addition product comprising reacting an isocyanate compound with an isocyanate-reactive compound in the presence of a compound or composition according to any one of claims 1 to 12.

16. 16. The process for making an isocyanate addition product of claim 15, wherein the isocyanate is a polyisocyanate, the isocyanate-reactive compound is a polyol, and the process is for making a polyurethane, the process optionally including a blowing agent.

17. 17. The process for making the isocyanate addition product of claim 16, wherein the polyurethane is a polyurethane foam.

18. 18. The process for the preparation of an isocyanate addition product according to claim 17, wherein the polyurethane foam is selected from cellular or non-cellular polyurethanes.

19. 19. A process for the preparation of an isocyanate addition product according to any one of claims 16 to 18, wherein the blowing agent is water.

20. 20. The method for producing an isocyanate addition product according to any of claims 16 to 19, wherein the method is for producing a polyurethane, and the method optionally comprises the addition of a surfactant, a flame retardant, a chain extender, a crosslinking agent, an adhesion promoter, an antistatic additive, a hydrolysis stabilizer, a UV stabilizer, a lubricant, an antimicrobial agent, or a combination of two or more thereof.

21. 21. A process for the preparation of an isocyanate addition product according to any one of claims 15 to 20, wherein the compound or composition according to any one of claims 1 to 12 is present in an amount of from 0.005% to 5% by weight, based on the total weight of the entire composition including all components.

22. 22. A process for the preparation of the isocyanate addition product of any of claims 15 to 21, wherein the isocyanate addition product forms a foam and is selected from the group consisting of slabstock, molded foam, flexible foam, rigid foam, semi-rigid foam, spray foam, thermoformable foam, microcellular foam, footwear foam, open cell foam, closed cell foam, adhesive.