Method and system for designing rubber compound

Abstract

To provide a method and a system for designing rubber compounding with which rubber compounding of vulcanized rubber having target rubber physical properties can be accurately and easily grasped.SOLUTION: A method for designing rubber compounding inputs compounding specification data Dx in which the specified range of the compounding amount of compounding components of object vulcanized rubber Ga is set and a target value D2a of a plurality of types of rubber physical property data D2 to an arithmetic unit 2 storing a prediction model PM constituted by performing machine learning using, as learning data, the plurality of types of rubber physical property data D2 of a number of types of vulcanized rubber G manufactured while making compounding data D1 different from each other, pieces of compounding data D1, and vulcanization condition data D3 of the number of vulcanized rubber G. The arithmetic unit 2 generates candidates for compounding data D1 that satisfies the specified range. The method selects, from the candidates, compounding data D1 in which pieces of rubber physical property data D2 calculated by using compounding data D1 of the candidates, vulcanization condition data D3 of the object vulcanized rubber Ga, and the prediction model PM are approximate to the target value D2a, and outputs the selected data to an output unit 4.SELECTED DRAWING: Figure 1

Description

[Technical field]

[0001] The present invention relates to a method and system for designing a rubber compound, and more particularly to a method and system for designing a rubber compound that can easily and accurately grasp a rubber compound that meets target rubber properties. [Background technology]

[0002] Vulcanized rubber is produced by vulcanizing unvulcanized rubber. Unvulcanized rubber is formed by blending multiple types of compounding components in specific amounts. By varying the amount of each compounding component, the rubber physical properties of the vulcanized rubber produced can be changed. In other words, to produce vulcanized rubber with the desired rubber physical properties, it is necessary to appropriately set the rubber compounding (the amount of each compounding component) according to the desired rubber physical properties.

[0003] Conventionally, in order to manufacture vulcanized rubber having targeted rubber properties, for example, first, a plurality of types of unvulcanized rubber are molded with different rubber compositions, and each unvulcanized rubber is vulcanized to manufacture a vulcanized rubber. Next, the rubber properties of the manufactured plurality of types of vulcanized rubber are measured to identify a vulcanized rubber having rubber properties similar to the targeted rubber properties. By referring to the rubber composition of the identified vulcanized rubber, a rubber composition that matches the targeted rubber properties is identified. It takes a great deal of trial and error to identify an appropriate rubber composition using this method.

[0004] In recent years, a device and method have been proposed that utilize machine learning to assist in the design of manufacturing recipes for products with specified characteristics (see, for example, Patent Document 1). The device and method proposed in Patent Document 1 are not specialized for rubber products, so rubber-specific considerations must be taken into account when applying them to rubber products. In addition, with the proposed device and method, there is a risk that the load of computation processing may become excessive in order to accurately grasp a rubber compounding that matches the target rubber physical properties, so it is necessary to reduce this load. Therefore, there is room for improvement in accurately and simply grasping a rubber compounding that matches the target rubber physical properties. [Prior art documents] [Patent documents]

[0005] [Patent Document 1] JP 2019-86817 A Summary of the Invention [Problem to be solved by the invention]

[0006] An object of the present invention is to provide a method and system for designing a rubber compound that can easily and accurately grasp a rubber compound that meets target rubber properties. [Means for solving the problem]

[0007] In order to achieve the above object, the rubber compounding design method of the present invention inputs compounding designation data in which a specified range of the compounding amount of each compounding component of the vulcanized rubber is set and target values ​​of multiple types of rubber property data of the vulcanized rubber into a calculation device, and performs calculation processing by the calculation device based on the compounding designation data to specify the compounding amount of each of the compounding components, and generates multiple candidates of compounding data that satisfy the specified range set by the compounding designation data, and uses a predictive model constructed by machine learning to perform calculation processing by the calculation device based on the compounding data and vulcanization condition data of each of the generated candidates to calculate each of the rubber property data of the target vulcanized rubber formed with the compounding data of each of the candidates and vulcanized based on the vulcanization condition data, and selects the compounding data of the target vulcanized rubber in which each of the calculated rubber property data is close to the target value from each of the candidates.

[0008] The rubber compounding design system of the present invention has a calculation device, an input unit for inputting data to the calculation device, and an output unit connected to the calculation device so as to be capable of communicating with the calculation device. In the rubber compounding design system, compounding designation data in which a designated range of compounding amounts of each compounding component of a vulcanized rubber is set, and target values ​​of multiple types of rubber property data of the vulcanized rubber are input to the calculation device, and the calculation device performs calculation processing based on the compounding designation data, thereby specifying the compounding amounts of each of the compounding components, and satisfying the designated ranges set by the compounding designation data. Formulation Data A plurality of candidates are generated, and using a predictive model constructed by machine learning, the arithmetic device performs calculations based on the compounding data and vulcanization condition data of each of the generated candidates, thereby calculating the rubber property data of each of the target vulcanized rubbers formed from the compounding data of each of the candidates and vulcanized based on the vulcanization condition data, and the compounding data of the target vulcanized rubber for which each of the calculated rubber property data is approximate to the target value is selected from each of the candidates and output by the output unit.

[0009] According to the present invention, the compounding amounts of each compounding component of the vulcanized rubber are specified based on the compounding designation data in which the designated range of the compounding amount of each compounding component of the vulcanized rubber is set, and a plurality of candidates of compounding data satisfying the designated range are generated by the calculation processing by the arithmetic device. That is, the candidate compounding data is generated under a constraint condition that satisfies the designated range, so that the burden of the calculation processing for generating the candidate compounding data and the calculation processing using the prediction model is reduced. In addition, by using the prediction model, the calculation device performs calculation processing based on the compounding data and vulcanization condition data of each of the generated candidates, so that the rubber physical property data of each of the target vulcanized rubbers can be calculated with high accuracy. As a result, the compounding data of the target vulcanized rubber in which each of the rubber physical property data is highly accurately approximated to the target value can be easily grasped. [Brief description of the drawings]

[0010] [Figure 1] FIG. 1 is an explanatory diagram illustrating a rubber compound design system of the present invention. [Diagram 2] 1 is a flow diagram illustrating a procedure for determining compounding data of a target vulcanized rubber whose rubber physical property data approximates a target value. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0011] Hereinafter, the rubber compound design method and system of the present invention will be specifically described based on the embodiments shown in the drawings.

[0012] The rubber compound design method of the present invention is carried out using a rubber compound design system 1 of the present invention illustrated in FIG. 1. The vulcanized rubber G is produced by vulcanizing the unvulcanized rubber R. The vulcanized rubber G and the unvulcanized rubber R are each made of a plurality of compounding components C (C 1 , C 2 , C n The present invention has been created with a view to accurately and simply grasping the rubber compounding of a vulcanized rubber G (target vulcanized rubber Ga) having targeted rubber properties, that is, the compounding amounts of the respective compounding components C that form the vulcanized rubber G.

[0013] This design system 1 has a calculation device 2, an input unit 3, and an output unit 4. The calculation device 2, the input unit 3, and the output unit 4 are connected to each other so that they can communicate with each other via wire or wirelessly. In this embodiment, the design system 1 further has a measurement device 5. Data acquired by the measurement device 5 is input to the calculation device 2 through the input unit 3. The measurement device 5 may be independent and separate from the design system 1, and the data acquired by the measurement device 5 may be input to the calculation device 2.

[0014] Various data are input and stored in the arithmetic unit 2, and the arithmetic unit 2 performs arithmetic processing using these data. Various computers can be used as the arithmetic unit 2. Therefore, the arithmetic unit 2 has a memory in which various data are stored, and a CPU that performs arithmetic processing.

[0015] The input unit 3 is an input means for inputting various data to the arithmetic device 2. Examples of the input unit 3 include a keyboard, a mouse, various terminal devices, and an interface provided in the arithmetic device 2.

[0016] The output unit 4 is an output means for displaying various data input to the arithmetic device 2 and the results of arithmetic processing using these data (numerical values, tables, drawings, etc.). Examples of the output unit 4 include various monitors and printers.

[0017] The measuring device 5 is a means for measuring and acquiring rubber property data D2 of the vulcanized rubber G. Examples of the rubber property data D2 include various known rubber properties such as tan δ (loss factor), hardness, breaking strength, breaking elongation, 300% modulus, and specific gravity. In the present invention, a desired plurality of types of rubber property data D2 are used. As the measuring device 5, a known device corresponding to the measurement of each rubber property data D2 is used, and each rubber property data D2 is measured and acquired by a method conforming to a known method (such as the corresponding JIS standard).

[0018] In the present invention, a prediction model PM constructed by machine learning is used. This prediction model PM is a type of computer program for predicting desired multiple types of rubber property data D2 of a target vulcanized rubber Ga produced by vulcanizing a target unvulcanized rubber Ra under a predetermined vulcanization condition. An example of a procedure for constructing this prediction model PM will be described.

[0019] First, unvulcanized rubber R is molded based on the compounding data D1 in which the compounding amount of each compounding component C is set. At that time, a large number of types of unvulcanized rubber R with different compounding data D1 are molded. Making the compounding data D1 different means making the compounding amount of at least one type of each compounding component C different. There are cases where the compounding amount of a specific compounding component C is zero, and in this case, the type of compounding component C used is made different.

[0020] Next, each molded unvulcanized rubber R is vulcanized under a predetermined vulcanization condition to produce vulcanized rubber G. That is, many types of vulcanized rubber G with different blending data D1 are produced. The blending amount of each blending component C affects the rubber physical property data D2 of the vulcanized rubber G, but the degree of the influence differs depending on the type and blending amount of the blending component C.

[0021] Examples of vulcanization conditions include vulcanization temperature, vulcanization pressure, and vulcanization time. An index indicating these vulcanization conditions is the vulcanization condition data D3. The vulcanization conditions are set to appropriate conditions for the unvulcanized rubber R, without over- or under-vulcanization. The vulcanization condition data D3 also affects the rubber physical property data D2. When manufacturing vulcanized rubber G at a laboratory level, for example, vulcanization can be performed under unified vulcanization conditions, and the vulcanization conditions for all vulcanized rubbers G can be set to be constant. This makes it possible to substantially eliminate the influence of differences in the vulcanization condition data D3 on the rubber physical property data D2 of the vulcanized rubber G.

[0022] Next, rubber property data D2 of each produced vulcanized rubber G is measured and obtained using a measuring device 5. From the many types of rubber property data D2 exemplified above, desired types of rubber property data D2 are measured and obtained.

[0023] Prepare compounding data D1 for each vulcanized rubber G and vulcanization condition data D3 for each vulcanized rubber G together with desired rubber property data D2 obtained from each manufactured vulcanized rubber G. Next, the rubber property data D2, compounding data D1, and vulcanization condition data D3 for each vulcanized rubber G are used as basic data (i.e., learning data) for predicting the rubber property data D2 of the target vulcanized rubber Ga. Then, construct a prediction model PM by machine learning using this learning data.

[0024] Specifically, the above data D1, D2, and D3 are input to the arithmetic device 2, and machine learning is performed using these data D1, D2, and D3. That is, the relationship between each rubber property data D2 and the compounding data D1 and the vulcanization condition data D3 is linked, and the influence of the compounding data D1 and the vulcanization condition data D3 on each rubber property data D2 of the vulcanized rubber G to be manufactured is analyzed and evaluated to construct a prediction model PM. As for the compounding data D1, the influence of the type and compounding amount of compounding component C on the rubber property data D2 is analyzed and evaluated.

[0025] The factors of the data D1 and D3 described above affect each other in a complex manner, and the rubber physical property data D2 of the vulcanized rubber G changes. Therefore, by using the data D1, D2, and D3 as learning data, and having an artificial intelligence (AI) learn the degree of difference in the data D2 (rubber physical property data) due to the combination of the data D1 and D3, the combination of each compounding component C in the data D1, the difference in the compounding amount of each compounding component C, and the like, and by having the AI ​​learn the characteristics of the data D2 in each case, it becomes possible to construct a prediction model PM. As a machine learning method, a well-known method such as deep learning using a neural network can be exemplified. To construct this prediction model PM, the huge amount of data D1, D2, and D3 that has been accumulated in the past can be effectively used. The constructed prediction model PM is stored in the calculation device 2.

[0026] Next, an example of a procedure for grasping the rubber compounding D1 of the target vulcanized rubber Ga having the target rubber physical properties will be described. That is, a procedure for grasping the compounding data D1 of the target vulcanized rubber Ga having the rubber physical properties that satisfy each target value D2a set for the desired multiple types of rubber physical property data D2 will be illustrated. In the following explanation, the compounding data D1 of the conventional vulcanized rubber G in which the desired multiple types of rubber physical property data D2 do not satisfy the target value D2a is reviewed, and the compounding data D1 of the target vulcanized rubber Ga in which each rubber physical property data D2 satisfies the target value D2a will be grasped as an example.

[0027] The main steps are as shown in Fig. 2. First, the necessary data is input to the calculation device 2 using the input unit 3. The data to be input are the compounding specification data Dx for the target vulcanized rubber Ga shown in Table 1 below, the target value D2a of the rubber property data D2 for the target vulcanized rubber Ga shown in Table 2 below, and the vulcanization condition data D3 for the target vulcanized rubber Ga.

[0028] [Table 1]

[0029] [Table 2]

[0030] As shown in Table 1, the compounding specification data Dx sets the specified range of compounding amounts for each compounding component C of the target vulcanized rubber Ga. In this example, a total of 11 types of compounding components C are set: two types of rubber components, SBR and BR, as well as carbon, zinc oxide, ... and vulcanization accelerator B. Compounding components C are not limited to the types shown here, and types can be used as needed. The initial values ​​in Table 1 are the compounding data for conventional vulcanized rubber G.

[0031] In the example of the compounding specification data Dx in Table 1, for the target vulcanized rubber Ga, a variation of ±20 phr is set for each of SBR, BR, carbon, and aromatic oil from the compounding data (initial value) of the conventional vulcanized rubber G. Therefore, the compounding amounts of SBR, BR, carbon, and aromatic oil in the target vulcanized rubber Ga are set to 30 phr or more and 70 phr or less. For other compounding components C such as zinc oxide, a variation of zero is set from the compounding data (initial value) of the conventional vulcanized rubber G. Therefore, the compounding amounts of other compounding components C such as zinc oxide in the target vulcanized rubber Ga are set to the same compounding data (initial value) as the conventional vulcanized rubber G.

[0032] In this way, in the present invention, the blending amount of each compounding component C of the target vulcanized rubber Ga is set by the blending designation data Dx. Therefore, depending on the purpose, it is possible to change only the blending amount of the desired compounding component C, or to set the blending amount of the desired compounding component C to zero and remove that compounding component C.

[0033] As shown in Table 2, the target value D2a of the rubber physical property data D2 is set for multiple desired types of rubber physical property data D2. The initial value in Table 2 is the physical property data D2 of conventional vulcanized rubber G. In this example, two types of rubber physical property data D2, tan δ at 60°C and hardness HS at 20°C, are set as the multiple desired types of rubber physical property data D2, but the present invention is not limited to this and any desired type of rubber physical property data D2 can be adopted, and the number of rubber physical property data D2 adopted can be three or more. In Table 2, the targets are set to change tan δ at 60°C from 0.2 to 0.18 and hardness HS at 20°C from 65 to 64.

[0034] The calculation device 2 performs calculation processing based on the inputted blending specification data Dx to generate multiple candidates for blending data D1 that satisfy the specified range set by the blending specification data Dx under predetermined conditions. That is, all combinations of blending components C that satisfy this specified range are generated as candidates for blending data D1 according to the predetermined conditions. This predetermined condition is the pitch at which the fluctuation amount set in the blending components C is changed (fluctuation amount change pitch). The blending amounts of BR, BR, carbon, and aroma oil, each of which has a fluctuation amount set, are changed at a pitch of, for example, 1 phr, to generate all combinations of blending components C that satisfy the specified range set by the blending specification data Dx as candidates for blending data D1.

[0035] The smaller the pitch, the more combination data D1 will be generated as candidates. This is advantageous for grasping the desired combination data D1 with higher accuracy. On the other hand, if the pitch is made too small, the number of combination data D1 generated as candidates will be excessive, which will increase the burden of calculation processing. Therefore, the size of the pitch is set taking into consideration the improvement of accuracy and reduction of the burden of calculation processing. For example, the pitch is set to about 0.5 to 4 phr.

[0036] This pitch can be the same for each compounding component C, or can be relatively large (small) for a specific compounding component C. For example, this pitch can be set smaller for compounding components C that affect the rubber physical property data D2 in smaller amounts, and set larger for compounding components C that have no effect unless they are in larger amounts. In other words, the magnitude of this pitch for each compounding component C can be set based on the magnitude of the effect of that compounding component C on the rubber physical property data D2.

[0037] Next, the generated candidate compounding data D1 and the vulcanization condition data D3 of the target vulcanized rubber Ga (the vulcanization condition data D3 when vulcanizing the target unvulcanized rubber Ra) are input to the prediction model PM, and a calculation process is performed to execute the prediction model PM. The prediction model PM calculates the rubber property data D2 of the target vulcanized rubber Ga formed by the compounding data D1 based on the input compounding data D1 and vulcanization condition data D3.

[0038] Each calculated rubber physical property data D2 is compared with a target value D2a set for each rubber physical property data D2, and the calculation device 2 judges whether the data falls within the tolerance range set as being close to the target value D2a. This tolerance range can be set arbitrarily, and is, for example, a range of about ±5% or ±2% of the target value D2a. From all the generated candidate compounding data D1, the compounding data D1 for which the rubber physical property data D2 is judged to be close to the target value D2a is selected by the calculation device 2. The compounding data D1 selected is not limited to one, and may be multiple.

[0039] As shown in Table 3 below, the compounding data D1 of the selected target vulcanized rubber Ga is output to the output 4. If the output unit 4 is a monitor, the compounding data D1 is displayed, and if the output unit 4 is a printer, the compounding data D1 is printed.

[0040] [Table 3]

[0041] In Table 3, the compounding amount of each compounding component C satisfies the designated range set by the compounding designation data Dx. Moreover, the target vulcanized rubber Ga formed by this compounding data D1 and vulcanized based on the vulcanization conditions of the input vulcanization condition data D3 is predicted to satisfy the target value D2a of each rubber physical property data D2 listed in Table 2.

[0042] That is, the data shown in Table 3 can be grasped as the compounding data D1 of the target vulcanized rubber Ga appropriate for changing the tan δ at 60°C from the initial value of 0.2 to the target value of 0.18 and changing the hardness HS at 20°C from the initial value of 65 to 64. In this way, the compounding data D1 of the target vulcanized rubber Ga having rubber properties that satisfy the target value D2a that could not be obtained with the compounding data D1 of the conventional vulcanized rubber G can be grasped. The data shown in Tables 1 to 3 are data based on actual examples, and by using the present invention, it was possible to concisely and accurately grasp how to change the compounding data D1 of the conventional vulcanized rubber G in order to make the desired multiple types of rubber property data D2 the target value D2a.

[0043] According to the present invention, the candidate compounding data D1 is generated under the constraint condition that satisfies the designated range set by the compounding designation data Dx, so the burden of the calculation process for generating the candidate compounding data D1 is small. And, the number of candidates of the compounding data D1 that predict the rubber physical property data D2 thereafter is also limited, so the burden of the calculation process for this prediction is reduced.

[0044] In addition, by performing calculation processing using the above-mentioned prediction model PM based on the generated candidate compounding data D1 and the vulcanization condition data D3 of the target vulcanized rubber Ga, it is possible to accurately calculate the rubber physical property data D2 of the target vulcanized rubber Ga. As a result, it is possible to easily grasp the compounding data D1 of the target vulcanized rubber Ga in which the rubber physical property data D2 closely approximates the target value D2a with high accuracy.

[0045] When generating candidates for each of the blending data D1, it is desirable to correct the total blending amount of the rubber components in the blending data D1 to 100 phr. In Table 3, the total blending amount of the rubber components (SBR, BR) is corrected to 100 phr, and the blending amounts of each of the other blending components C are listed. By correcting the blending data D1 in this way when generating candidates for the blending data D1, it becomes easier to grasp the blending amount of each of the blending components C.

[0046] When there are multiple compounding data D1 of the target vulcanized rubber Ga, each of which is selected because its respective rubber property data D2 is judged to be approximate to the target value D2a, each compounding data D1 can be output by the output unit 4 in the following order.

[0047] For example, the selected compounding data D1 is output by the output unit 4 in the order of approximation of the rubber physical property data D2 of the target vulcanized rubber Ga formed by each compounding data D1 to the target value D2a for each type of rubber physical property data D2. In detail, each rubber physical property data D2 of the target vulcanized rubber Ga formed by each compounding data D1 is compared with the target value D2a for each type of rubber physical property data D2. The compounding data D1 of the target vulcanized rubber Ga having the rubber physical property data D2 with the smallest difference between the two compared is ranked first. The compounding data D1 of the target vulcanized rubber Ga having the rubber physical property data D2 with the second and third smallest difference between the two are ranked second and third, respectively. This ranking may change depending on the type of rubber physical property data D2. Each compounding data D1 is output by the output unit 4 in the order ranked in this way. By ranking in this way, it becomes easier to grasp the superiority of each blending data D1 using the degree of approximation of each rubber physical property data D2 to the target value D2a for each type as an index.

[0048] Alternatively, each selected compounding data D1 is output by the output unit 4 in order of the degree of approximation of each rubber physical property data D2 of the target vulcanized rubber Ga formed with each compounding data D1 determined based on the priority weighting set for the type of rubber physical property data D2 to the target value D2a. For example, a case will be described in which a coefficient k1 with a large priority weighting is set for the rubber physical property data D2 of tan δ@60°C, and a coefficient k2 with a small priority weighting is set for the rubber physical property data D2 of hardness HC@20°C. The coefficients k1 and k2 mean that the higher the numerical value, the higher the priority. Then, when the rubber physical property data D2 of tan δ@60°C is an approximation coefficient n1 indicating the degree of approximation to the target value D2a, and the rubber physical property data D2 of hardness HC@20°C is an approximation coefficient n2 to the target value D2a, the evaluation of the degree of approximation of the target vulcanized rubber Ga having these rubber physical property data D2 is calculated by the coefficient k1×approximation coefficient n1+coefficient k2×approximation coefficient n2. The approximation coefficients n1 and n2 are closer to the target value D2a as the values ​​are larger. Then, the selected compounding data D1 are ranked in order of the degree of approximation of the target vulcanized rubber Ga formed by each compounding data D1, and output by the output unit 4. By ranking in this way, it becomes easier to grasp the superiority of each compounding data D1 taking into account the weighting of the priority of each rubber physical property data D2.

[0049] The selected combination data D1 can also be output by the output unit 4 in ascending order of material cost per unit weight calculated based on each combination data D1. In detail, the cost per unit weight of each combination component C is grasped, and the material cost per unit weight of each combination data D1 is calculated based on the grasped cost of each combination component C and the blending amount of each combination component C in each combination data D1. Based on this calculation result, each combination data D1 is ranked and output to the output unit 4. By ranking in this way, it becomes easier to grasp the superiority of the material cost of each combination data D1. [Explanation of symbols]

[0050] 1. Rubber compound design system 2 Arithmetic unit 3. Input section 4 Output section 5. Measuring Equipment PM Prediction Model D1 Mixture Data Dx Mixture specification data D2 Rubber property data D2a Target Value D3 Vulcanization condition data R Unvulcanized rubber Ra target unvulcanized rubber G Vulcanized rubber Ga Target vulcanized rubber C(C1, C2...Cn) Compounding ingredients

Claims

1. Inputting into a calculation device blending designation data in which a designated range of blending amounts of each blending component of the vulcanized rubber is set, and target values ​​of multiple types of rubber property data of the vulcanized rubber, By performing a calculation process by the arithmetic device based on the blending designation data, the blending amounts of the respective blending components are specified, and a plurality of candidates for blending data that satisfy the designated range set by the blending designation data are generated; A rubber compounding design method, characterized in that: using a predictive model constructed by machine learning, calculations are performed by the arithmetic device based on the generated compounding data and vulcanization condition data of each of the candidates, thereby calculating the rubber property data of each of the target vulcanized rubbers formed from the compounding data of each of the candidates and vulcanized based on the vulcanization condition data, and the compounding data of the target vulcanized rubber for which the calculated rubber property data of each of the candidates approximates the target value is selected from each of the candidates.

2. A rubber compounding design method as described in claim 1, wherein when a plurality of compounding data are selected, each of the selected compounding data is output by an output unit for each type of rubber property data in order of approximation of the rubber property data of the target vulcanized rubber formed with each of the compounding data to the target value.

3. 2. The rubber compounding design method according to claim 1, wherein when a plurality of compounding data are selected, the selected compounding data are output by the output unit in order of the degree of approximation of each of the rubber physical property data of the target vulcanized rubber formed with each of the compounding data to the target value, the degree of approximation being determined based on the priority weighting set for the type of rubber physical property data.

4. The rubber compounding design method according to claim 1, wherein when a plurality of compounding data are selected, each of the selected compounding data is output by an output unit in order of lowest material cost per unit weight calculated based on each of the compounding data.

5. 5. The rubber compounding design method according to claim 1, wherein when generating the candidates for the compounding data, a total compounding amount of the rubber components in the compounding data is corrected to 100 phr.

6. A rubber compounding design system having a calculation device, an input unit for inputting data to the calculation device, and an output unit connected to the calculation device so as to be capable of communicating with the calculation device, A compounding specification data in which a specified range of compounding amounts of each compounding component of the vulcanized rubber is set, and target values ​​of a plurality of types of rubber property data of the vulcanized rubber are input to the arithmetic device, The calculation device performs calculation processing based on the blending designation data to specify the blending amounts of the respective blending components, and generates a plurality of candidates for blending data that satisfy the designated range set by the blending designation data; A rubber blend design system characterized in that, using a predictive model constructed by machine learning, the arithmetic device performs calculations based on the compounding data and vulcanization condition data of each of the generated candidates, thereby calculating the rubber property data of each of the target vulcanized rubbers formed from the compounding data of each of the candidates and vulcanized based on the vulcanization condition data, and the compounding data of the target vulcanized rubber for which the calculated rubber property data of each of the target vulcanized rubbers approximates the target value is selected from each of the candidates and output by the output unit.