Optical element and optical deflection device

Abstract

To provide an optical element and an optical deflector that average the in-plane diffraction efficiency and improve the average diffraction efficiency.SOLUTION: An optical element and an optical deflector comprise, in a thickness direction, a plurality of optical anisotropic layers having an in-plane alignment pattern in which an orientation of an optical axis derived from a liquid crystal compound changes while continuously rotating along at least one in-plane direction. The optical anisotropic layer has a region in which lengths until the orientation of the optical axis rotates by 180° are different from each other in the one direction. At least one layer of the plurality of optical anisotropic layers is an inclined optical anisotropic layer having a region in which there are a plurality of pairs of bright lines and dark lines derived from the orientation of the optical axis along the one direction in a cross-sectional image obtained by observing a cross section cut along the one direction in the thickness direction with a scanning electron microscope, and the pairs of the bright lines and the dark lines are inclined at inclination angles different from each other with respect to a normal line of a boundary surface of the optical anisotropic layer.SELECTED DRAWING: Figure 3

Description

[Technical field]

[0001] The present disclosure relates to an optical element and an optical deflection device including the optical element. [Background technology]

[0002] Polarized light is used in many optical devices and systems, and optical elements for controlling the reflection, focusing, and divergence of polarized light are being developed.

[0003] Japanese Patent Application Publication No. 2014-16632 (hereinafter referred to as Patent Document 1) and Japanese Patent Application Publication No. 2010-525394 (hereinafter referred to as Patent Document 2) disclose polarizing diffraction elements formed by pattern-aligning liquid crystal compounds having optical anisotropy.

[0004] In addition, JP 2016-519327 A (hereinafter referred to as Patent Document 3) discloses a polarization conversion system using a geometric phase element having optical anisotropy with a local optical axis direction that changes nonlinearly in at least one dimension along the surface. Here, too, pattern alignment of liquid crystal compounds is utilized. Summary of the Invention [Problem to be solved by the invention]

[0005] Patent Documents 1 and 2 are not technologies for outputting light in a direction with different diffraction angles depending on the incident position, and there is no description of such in the documents. The inventors' investigations revealed that when light is incident on a layer having optical anisotropy with a local optical axis direction that changes nonlinearly in one dimension as in Patent Document 3, the degree of diffraction differs depending on the incident position. In such an element, when light is incident at different incident angles depending on the region and emitted, the in-plane diffraction efficiency differs depending on the region, and there are cases where regions have reduced diffraction efficiency.

[0006] In view of the above circumstances, an object of the present disclosure is to provide an optical element and a light deflection device that average out the diffraction efficiency within a plane and improve the average diffraction efficiency. [Means for solving the problem]

[0007] The technology of the present disclosure includes the following aspects. <1> a plurality of optically anisotropic layers in a thickness direction, each having an in-plane orientation pattern in which the direction of an optical axis derived from a liquid crystal compound changes while continuously rotating along at least one direction in the plane; the optically anisotropic layer has regions having different lengths until the direction of the optical axis rotates 180° in the one direction, At least one of the plurality of optically anisotropic layers is an inclined optically anisotropic layer, in which, in a cross-sectional image obtained by observing a cross-section cut in the thickness direction along the one direction with a scanning electron microscope, there are a plurality of pairs of bright and dark lines originating from the orientation of the optical axis along the one direction, and the pairs of bright and dark lines have regions inclined at different angles relative to the normal to the interface of the optically anisotropic layer. <2> The optically inclined anisotropic layer is provided in two layers, and in the cross-sectional image, in at least a part of the opposing regions of the two optically inclined anisotropic layers, the pair of bright and dark lines in one optically inclined anisotropic layer and the pair of bright and dark lines in the other optically inclined anisotropic layer have different inclination angles. <1> The optical element according to claim 1. <3> The optically inclined anisotropic layer is provided in two layers, and in the cross-sectional image, the pair of bright and dark lines in one of the optically inclined anisotropic layers and the pair of bright and dark lines in the other optically inclined anisotropic layer are aligned along the normal line in at least a part of the opposing region of the two optically inclined anisotropic layers. The tilt direction is different. <1> or <2> 13. The optical element according to claim 12 . <4> The optically inclined anisotropic layer has two layers, and in the cross-sectional image, in at least a portion of the opposing regions of the two optically inclined anisotropic layers, the pair of bright and dark lines in one optically inclined anisotropic layer and the pair of bright and dark lines in the other optically inclined anisotropic layer have the same inclination direction with respect to the normal line. <1> from <3> 13. The optical element according to claim 12 . <5> The tilted optically anisotropic layer has a region in which the optical axis is twisted in the thickness direction. <1> from <4> 13. The optical element according to claim 12 . <6> It has the function of diffracting and transmitting incident light. <1> from <5> 13. The optical element according to claim 12 . <7> In the tilted optical anisotropy layer, the liquid crystal compound is cholesterically aligned. <1> from <5> 13. The optical element according to claim 12 . <8> It has the function of diffracting and reflecting incident light. <7> The optical element according to claim 1. <9> The in-plane alignment pattern of the optically anisotropic layer is a pattern in which the length until the orientation of the optical axis rotates 180° in the one direction gradually changes in the one direction. <1> from <8> 13. The optical element according to claim 12 . <10> The in-plane alignment pattern of the optically anisotropic layer is a pattern having the one direction radially from the inside to the outside. <1> from <9> 13. The optical element according to claim 12 . <11> The in-plane alignment pattern of the optically anisotropic layer has a region in which the length of the optical axis in the one direction is rotated by 180° is 10 μm or less. <1> from <10> 13. The optical element according to claim 12 . <12> An optical deflection element that deflects and emits incident light, a driving means that drives the optical deflection element, and a light output side of the optical deflection element. <1> from <11> and an optical element according to any one of claims 1 to 5. Effect of the Invention

[0008] According to the present disclosure, in an optical element and an optical deflection device, it is possible to average the diffraction efficiency within a plane and improve the average diffraction efficiency. [Brief description of the drawings]

[0009] [Figure 1] 2 is a plan view showing a schematic alignment pattern of optical axes on a part of the surface of the optical element according to the first embodiment. FIG. [Diagram 2] 2 is a schematic diagram of a cross-sectional image of the optical element shown in FIG. 1 obtained by a scanning microscope. [Diagram 3] 2 is a diagram showing a schematic diagram of a liquid crystal alignment pattern in the thickness direction (z direction) and the horizontal direction (x direction) of the optical element shown in FIG. [Figure 4] FIG. 2 is a conceptual diagram showing the function of an optically anisotropic layer having a horizontal rotation alignment pattern. [Diagram 5] 6 is a schematic diagram of a cross-sectional image obtained by a scanning microscope of the optical element according to the second embodiment. FIG. [Figure 6] 13 is a schematic diagram of a cross-sectional image obtained by a scanning microscope of the optical element of the third embodiment. FIG. [Figure 7] FIG. 13 is a diagram illustrating a cross section of an optical element according to a fourth embodiment. [Figure 8] FIG. 13 is a plan view showing a schematic orientation pattern of optical axes on the surface of an optical element according to a modified example of the design. [Figure 9] FIG. 1 is a diagram conceptually illustrating an example of an exposure apparatus for forming an alignment pattern by exposing an alignment film. [Figure 10] FIG. 1 is a diagram illustrating a schematic configuration of an example of a light deflection device. [Figure 11] FIG. 2 is a diagram showing a layer structure of an optical element of Comparative Example 1. [Figure 12] FIG. 2 is a diagram showing a layer structure of the optical element of Example 1. [Figure 13] FIG. 11 is a diagram showing a layer structure of an optical element according to a second embodiment. [Figure 14] FIG. 11 is a diagram showing a layer structure of an optical element according to a third embodiment. [Figure 15] FIG. 13 is a diagram showing a layer structure of an optical element according to Example 4. [Figure 16] FIG. 13 is a diagram showing a layer structure of an optical element according to a fifth embodiment. [Figure 17]FIG. 2 is a conceptual diagram showing a method for measuring transmitted light intensity. [Figure 18] FIG. 13 is a diagram showing a layer structure of an optical element of Comparative Example 11. [Figure 19] FIG. 13 is a diagram showing a layer structure of an optical element according to an eleventh embodiment. [Figure 20] FIG. 4 is a conceptual diagram showing a method for measuring reflected light intensity. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0010] Hereinafter, an embodiment of the optical element of the present invention will be described with reference to the drawings. In each drawing, the scale of the components is appropriately changed from the actual one to make it easier to see. In this specification, a numerical range expressed using "~" means a range including the numerical values ​​written before and after "~" as the lower and upper limit values. In addition, "perpendicular" and "parallel" with respect to angles mean a range of the strict angle of ±10°.

[0011] [Optical elements] Fig. 1 is a plan view showing a schematic view of a part of the surface of the optical element 1 of the first embodiment, and Fig. 2 is a schematic view of a cross-sectional image obtained by observing a cross section of the optical element 1 with a scanning electron microscope (SEM). In the following drawings, the sheet surface of the sheet-like optical element is defined as the xy plane, and the thickness direction is defined as the z direction.

[0012] The optical element 1 includes two optically anisotropic layers 10 and 20 laminated in the thickness direction. The optically anisotropic layers 10 and 20 are made of cured layers of a composition containing a liquid crystal compound. The optical element 1 may include a support and an alignment film, and the optically anisotropic layer may be provided on the alignment film. The optical element of the present disclosure may include a plurality of optically anisotropic layers in the thickness direction, and is not limited to a two-layer structure, and may include three or more layers.

[0013] The optically anisotropic layers 10 and 20 have an in-plane alignment pattern (in-plane liquid crystal alignment pattern) in which the orientation of the optical axis 30A derived from the liquid crystal compound changes while continuously rotating along at least one in-plane direction A. Fig. 1 shows a schematic in-plane alignment pattern of the optical axis 30A derived from the liquid crystal compound on the surface of the optically anisotropic layer 20.

[0014] In addition, the optical axis 30A derived from the liquid crystal compound is the long axis direction (slow axis) of the rod shape in the case of a rod-shaped liquid crystal compound, and is the direction perpendicular to the disc surface (fast axis) in the case of a discotic liquid crystal compound. In the following description, the optical axis 30A derived from the liquid crystal compound is also referred to as the optical axis 30A of the liquid crystal compound, or simply as the optical axis 30A.

[0015] The in-plane alignment pattern in which the orientation of the optical axis 30A changes while continuously rotating in one direction A is a pattern in which the angle between the optical axis 30A of the liquid crystal compound aligned along one direction A (hereinafter also referred to as axis A) and the axis A varies depending on the position in the axis A direction, and the angle between the optical axis 30A and the axis A gradually changes from φ to φ+180° or φ-180° along the axis A and is aligned and fixed. Hereinafter, an in-plane alignment pattern in which the optical axis of the liquid crystal compound is parallel to the surface of the optical anisotropic layer, and local regions (unit regions) in which the orientation of the optical axis is constant are arranged in such a way that the orientation of the optical axis changes continuously in one direction between a plurality of local regions aligned in one direction as shown in FIG. 1 is referred to as a horizontal rotation alignment pattern.

[0016] In addition, "the angle between the optical axis 30A and the axis A gradually changes" may mean that the direction of the optical axis changes by a predetermined angle between unit areas, or may change at non-uniform angular intervals rather than at constant angular intervals, or may change continuously. However, the angular difference between the optical axes 30A of unit regions adjacent to each other in the x direction is preferably 45° or less, more preferably 15° or less, and even more preferably a smaller angle.

[0017] In the optical element 1, in such a horizontal rotation alignment pattern of the liquid crystal compound 30, the length (distance) over which the optical axis 30A of the liquid crystal compound 30 rotates 180° is defined as the length Λ of one period in the horizontal rotation alignment. In other words, the length of one period in the horizontal rotation alignment pattern is the distance from the angle φ between the optical axis 30A of the liquid crystal compound 30 and the axis A to φ+180°. In the following description, this length Λ of one period is also referred to as "one period Λ" or simply "period Λ".

[0018] The optically anisotropic layers 10 and 20 in the optical element 1 include regions having different lengths Λ of one period in the direction of the axis A. In the example shown in FIG. A1 ,Λ A2 ,Λ A3 …(where Λ A1 <Λ A2 <Λ A3 ) and includes regions A1, A2, A3.... In this example, the liquid crystal orientation pattern has a period that gradually shortens from right to left on the page, but the optical element of the present disclosure may have two or more regions with different lengths of one period. However, when applied to an optical deflection device described later, a liquid crystal orientation pattern in which the length of one period gradually changes, as shown in this example, is preferable. It is preferable to include a region with a period Λ of 10 μm or less.

[0019] In addition, the length of one period in opposing regions of a plurality of optically anisotropic layers may differ, but it is preferable that the lengths are consistent within a range of ±10%. In such a configuration, the periods can be matched by forming multiple optically anisotropic layers in the following order: first, a first optically anisotropic layer, and then, by coating or the like, a second optically anisotropic layer.

[0020] 1, when an optical element 1 having an optically anisotropic layer is sandwiched between two orthogonal polarizers and observed with an optical microscope, alternating bright and dark areas 42 and 44 are observed with respect to the orientation pattern of the optical axes. The period of light and dark (i.e., the period of the light areas or the period of the dark areas) is half the period Λ of the horizontal rotation orientation pattern of the optical axes.

[0021] At least one of the two optically anisotropic layers 10 and 20, the first optically anisotropic layer 10 in this example, is an inclined optically anisotropic layer. Hereinafter, the first optically anisotropic layer is also referred to as the inclined optically anisotropic layer 10. Hereinafter, the inclined optically anisotropic layer is a layer in which, in a cross-sectional image (hereinafter referred to as a cross-sectional SEM image) obtained by observing a cross section cut in the thickness direction along one direction with a scanning electron microscope (SEM), there are a plurality of pairs of bright and dark lines (bright and dark lines) originating from the direction of the optical axis along one direction, and the bright and dark lines have regions inclined at different inclination angles with respect to the normal line n of the interface of the layer. The "bright and dark lines originating from the direction of the optical axis" are bright and dark lines observed depending on the alignment state of the liquid crystal compound in the thickness direction of the optically anisotropic layer.

[0022] Fig. 2 is a schematic diagram of a cross-sectional image obtained by observing a cross section cut in the thickness direction along one direction in which the optical axis rotates with an SEM. As shown in Fig. 2, in the cross-sectional image, there are multiple pairs of alternating bright and dark lines that are inclined obliquely with respect to the normal line n of the interface of the tilted optically anisotropic layer 10. The inclination of the interface of the bright and dark lines with respect to the normal line n varies depending on the position in the x direction, and in this example, the inclination angle gradually increases in the x-axis direction (α1<α2<α3...). Note that the inclination angle of the bright and dark lines is defined here as an acute angle smaller than 90° among the angles that the bright and dark lines make with the normal line n.

[0023] In the tilted optical anisotropic layer 10, for example, in addition to the horizontal rotation orientation, the twist in the thickness direction is Due to the orientation, bright and dark lines are observed in the cross-sectional image described above.

[0024] Fig. 3 shows a schematic diagram of a liquid crystal orientation pattern in a cross section of the optical element 1 shown in Fig. 1 and Fig. 2. Here, the liquid crystal compound is a rod-like liquid crystal compound 30. In Fig. 3, bright and dark lines observed when the cross section is observed by SEM are superimposed.

[0025] As shown in FIG. 3, the inclined optically anisotropic layer 10 has a liquid crystal alignment pattern in which rod-shaped liquid crystal compounds 30 (hereinafter simply referred to as liquid crystal compounds 30) are horizontally rotated in the x direction and twisted in the thickness direction.

[0026] "The optical axis is twisted in the thickness direction" refers to a state in which the direction of the optical axis arranged in the thickness direction from one surface to the other surface of the optically anisotropic layer 10 changes relatively, is twisted in one direction, and is fixed. There are right-handed and left-handed twists, and it is only necessary to apply according to the direction of diffraction. The twist of the optical axis in the thickness direction is less than one rotation, that is, the twist angle is less than 360°. For example, in the example of FIG. 3, the optical axis of the liquid crystal compound 30 rotates about 140° from one surface side to the other surface side in the thickness direction (z direction). The twist angle of the liquid crystal compound 30 in the thickness direction is preferably about 10° to 200°, and more preferably about 45° to 180°. In the case of cholesteric orientation described later, the twist angle is 360° or more, and the liquid crystal compound 30 has selective reflectivity that reflects specific circularly polarized light in a specific wavelength range. In this specification, the term "twisted orientation" does not include cholesteric orientation, and selective reflectivity does not occur in an optically anisotropic layer having a twisted orientation.

[0027] When a cross section of a tilted optically anisotropic layer having such a liquid crystal alignment pattern is observed by SEM, the bright and dark lines shown in Figure 2 are observed. As shown by superimposing the bright and dark lines in Figure 3, the period of these bright and dark lines coincides with the period of the horizontal rotation alignment.

[0028] On the other hand, in the cross-sectional image, the second optically anisotropic layer 20 also has a plurality of alternating bright and dark lines, but the bright and dark lines in the second optically anisotropic layer 20 are aligned along the normal n to the interface of the optically anisotropic layer 20 and have no inclination. In the second optically anisotropic layer 20, the direction of the optical axis in the thickness direction is uniform.

[0029] In the optical element 1, as shown in FIG. 2, the period Λ of the horizontal rotation alignment in the first optically anisotropic layer 10 is A1 , Λ A2...and the period Λ of the horizontal rotation orientation in the second optically anisotropic layer 20 B1 , Λ B2 ... are consistent in the opposing regions. That is, Λ A1 =Λ B1 , Λ A2 =Λ B2 ...is.

[0030] The optical element 1 diffracts and transmits incident light. For example, the incident light L in When incident light L in is subjected to a refractive power by the optically anisotropic layer 20 and emits the light in a curved direction. The refractive power varies depending on the period of the horizontal rotation orientation, and the smaller the period, the larger the diffraction angle obtained. When a predetermined circularly polarized light L is incident on the regions of the optically anisotropic layers 10 and 20 with different periods of horizontal rotation orientation at the same incident angle, in When the incident light is a relatively large period, the output light L out1 The output light L in the region where the period is relatively smaller than out2 The diffraction angle is large.

[0031] Here, the principle by which an optically anisotropic layer having a horizontally rotated alignment pattern functions as a transmission type diffraction element will be briefly described with reference to FIG. When the optically anisotropic layer is used as a transmission type diffraction element, the in-plane retardation Re(λ) (=Δn λ ×d) is preferably 0.3λ to 0.7λ. The retardation Re is preferably 0.4λ to 0.6λ, more preferably 0.45λ to 0.55λ, and particularly preferably 0.5λ. Δn λ is the optical anisotropy of the layer at wavelength λ Birefringence, d, is the thickness of the optically anisotropic layer. For example, when 940 nm light is assumed as the incident light, the retardation Re for 940 nm light may be in the range of 282 nm to 658 nm, and is particularly preferably 470 nm. When the optically anisotropic layer has such a retardation Re, it exhibits a function as a general λ / 2 plate, that is, a function of giving a phase difference of 180° (=π=λ / 2) between the orthogonal linearly polarized components of the incident light. Note that the closer the retardation is to λ / 2, the higher the diffraction efficiency is, which is preferable, but the retardation is not limited to the above range. When the optically anisotropic layer has a retardation of approximately λ / 2, it imparts a phase difference of λ / 2 to incident light, converting incident light having a predetermined circular polarization into circularly polarized light in the opposite direction and outputting it.

[0032] In FIG. 4, right-handed circularly polarized light P with a wavelength λ is incident on an optically anisotropic layer 11 having a horizontal rotation alignment pattern. R The following conceptually illustrates the effect of the optically anisotropic layer 11 when the right-handed circularly polarized incident light L1 having a wavelength λ is incident on the optically anisotropic layer 11. By passing through the optically anisotropic layer 11, the right-handed circularly polarized incident light L1 is given a phase difference of λ / 2 and is converted into left-handed circularly polarized light P L The incident light L1 is converted into an absolute phase Q of the liquid crystal compound 30 in each unit region (local region) in the horizontal rotation alignment pattern. In the optically anisotropic layer, the direction of the optical axis 30A of the liquid crystal compound 30 rotates along the axis A and changes, so that the amount of change in the absolute phase differs depending on the direction of the optical axis 30A of the liquid crystal compound 30 at the position of the axis A of the optically anisotropic layer 11 where the incident light is incident. The region indicated by the dashed line in FIG. 4 shows a schematic diagram of how the amount of change in the absolute phase Q differs depending on the x coordinate.

[0033] 4, due to a shift in absolute phase Q when passing through the optically anisotropic layer 11, an equiphase surface E of absolute phase having an angle with respect to the surface of the optically anisotropic layer 11 is formed. As a result, a bending force is applied to the incident light L1 incident from the normal direction in a direction perpendicular to the equiphase surface E, and the traveling direction of the incident light L1 changes. That is, the incident light L1, which is right-handed circularly polarized light PR, becomes left-handed circularly polarized light PL after passing through the optically anisotropic layer 11, and is emitted from the optically anisotropic layer 11 as outgoing light L2 traveling in a direction forming a predetermined angle with the normal direction.

[0034] When left-handed circularly polarized light is incident on the optically anisotropic layer 11, the incident light is converted to right-handed circularly polarized light in the optically anisotropic layer 11 and is subjected to a bending force in the opposite direction to that shown in the figure, causing the traveling direction to be changed. When the horizontal rotational orientation of the optical axis 30A of the liquid crystal compound 30 rotates in the opposite direction, the refraction direction of the light by the optically anisotropic layer is opposite to that described above.

[0035] The shorter one period in the in-plane alignment pattern in the optically anisotropic layer is, the greater the bending force that can be applied to the incident light, and therefore the greater the diffraction angle can be.

[0036] The wavelength λ of light that causes the diffraction effect by the optically anisotropic layer 11 may be from ultraviolet to visible light, infrared, or even electromagnetic wave level. For the same period, the larger the wavelength of the incident light, the larger the diffraction angle, and the smaller the wavelength of the incident light, the smaller the diffraction angle. Therefore, the period may be set according to the target wavelength and the desired diffraction angle.

[0037] Although the above describes the case where a bending force is applied to light incident from the normal direction, a bending force can also be applied to obliquely incident light using the same principle, and output light can be obtained with an output angle different from the incident angle.

[0038] In the optical element 1 of this configuration, the first and second optically anisotropic layers 10 and 20 each have an area in the plane where the period of the horizontal rotation alignment pattern is different, so that light can be emitted at different exit angles for the same angle of incidence. In the case where there is no twist alignment in the thickness direction like the second optically anisotropic layer 20, the diffraction efficiency for light incident in the normal direction is high, but the diffraction efficiency for light incident obliquely is low. On the other hand, the inclined optically anisotropic layer 10 can improve the diffraction efficiency for obliquely incident light.

[0039] The optical element 1 has a layered structure of two or more optically anisotropic layers, at least one of which is an inclined optically anisotropic layer, and therefore can improve the average diffraction efficiency when light is incident at different angles depending on the region, and can suppress intensity differences in the exiting light to average out the exiting intensity.

[0040] In this embodiment, the optically anisotropic layer has a two-layer structure, but may have three or more layers. Also, the inclined optically anisotropic layer may have one layer, but more preferably has two or more layers.

[0041] As the optical elements 2 and 3 of the second and third embodiments, configuration examples each having two tilted optically anisotropic layers are shown in Figures 5 and 6. Figures 5 and 6 are schematic diagrams of cross-sectional images of the optical elements 2 and 3, respectively. The cross-sectional images are SEM images obtained by observing a cross section cut in the thickness direction along one direction of horizontal rotation alignment, as described above.

[0042] As shown in FIG. 5, in a cross-sectional image of two inclined optically anisotropic layers, the inclination direction of the bright and dark lines in one inclined optically anisotropic layer 10 with respect to the normal n in the opposing region of the two layers may be different from the inclination direction of the bright and dark lines in the other inclined optically anisotropic layer 22 with respect to the normal n. The inclination directions with respect to the normal n are different when the inclination direction of the bright and dark lines in one inclined optically anisotropic layer 10 with respect to the normal n is on the negative side of the x-axis (left side of the paper), whereas the inclination direction of the bright and dark lines in the other inclined optically anisotropic layer 22 with respect to the normal n is on the positive side of the x-axis (right side of the paper). The inclination angles of the two inclined optically anisotropic layers with respect to the normal n may be the same in the opposing region (α n =β n ) and even if they are different (α n ≠β n In the case where two inclined optically anisotropic layers are provided, the opposing regions in which the inclination directions of the light and dark lines are different may be over the entire region or may be only a part of the region. In this specification, the opposing regions of two inclined optically anisotropic layers are regions that overlap when viewed from the thickness direction in the same xy region.

[0043] By reversing the twist orientation in the thickness direction in one inclined optically anisotropic layer 10 and the other inclined optically anisotropic layer 22, the inclinations of the light and dark lines with respect to the normal line can be reversed.

[0044] 6, in a cross-sectional image of two inclined optically anisotropic layers, the inclination direction of the interface of the bright and dark lines in one inclined optically anisotropic layer 10 in the opposing region of the two layers with respect to the normal line n may be the same as the inclination direction of the interface of the bright and dark lines in the other inclined optically anisotropic layer 24 with respect to the normal line n. However, in this case, the inclination angle α of the bright and dark lines in one inclined optically anisotropic layer 10 in the opposing region n and the inclination angle γ of the light and dark lines in the other inclined optically anisotropic layer 24. n When two inclined optically anisotropic layers are provided, the opposing region in which the inclination directions of the light and dark lines are the same may be the entire region or may be only a part of the region.

[0045] The inclinations of the light and dark lines relative to the normal can be made different by making the twist pitch of the twist orientation in the thickness direction different between one inclined optically anisotropic layer 10 and the other inclined optically anisotropic layer 22. The difference in twist pitch means that the thicknesses until the optical axis is twisted to the same twist angle are different.

[0046] In addition, two tilted optically anisotropic layers provided in one optical element may simultaneously include opposing regions having the same tilt direction and opposing regions having different tilt directions.

[0047] In the above, the optical element functioning as a transmission type diffraction element has been described. The optical elements shown may also function as reflective diffractive elements.

[0048] Fig. 7 shows a cross-sectional view of an optical element 5 according to a fourth embodiment that functions as a reflective diffraction element. Fig. 7 shows a schematic overlap of bright and dark lines in a cross-sectional SEM image.

[0049] The optical element 5 includes two inclined optically anisotropic layers 12 and 14. Both of the two inclined optically anisotropic layers 12 and 14 are horizontally rotated and cholesterically oriented in the thickness direction. The two inclined optically anisotropic layers 12 and 14 have opposite directions of rotation of the optical axes in the horizontally rotated orientation, and the cholesteric orientation is also rotated in opposite directions.

[0050] Since the inclined optically anisotropic layers 12 and 14 have a cholesteric orientation, they selectively reflect only light of a specific selected wavelength range with a specific circular polarization. The central wavelength of the light that is selectively reflected is determined by the cholesteric helical pitch and film thickness, and which circularly polarized light is reflected is determined by the direction of rotation of the helix.

[0051] Since the liquid crystal alignment pattern has horizontal rotation alignment and cholesteric alignment, in the cross-sectional image, bright and dark lines with different angles of inclination in the normal direction are observed, as in the previously described embodiments (see Figure 7).

[0052] The orientation pattern of the optical axis 30A in the in-plane direction of the tilted optically anisotropic layers 12 and 14 is a horizontal rotation orientation as in the previous embodiment, so that the same effect as the optical element 1 is produced. That is, the optical element 5 has the effect of bending the incident light in a predetermined direction by changing the absolute phase of the incident light. Therefore, the optical element 5 has both the effect of bending the incident light in a direction different from the incident direction and the effect of the above-mentioned cholesteric orientation, and reflects the light at an angle in a predetermined direction with respect to the reflection direction of the specular reflection. In addition, since the optical element 5 has regions with different periods of the horizontal rotation orientation in the in-plane direction, it is possible to reflect the light at different reflection angles for the same incident angle. In addition, it is possible to improve the average diffraction efficiency when the incident angle is changed depending on the region, and to suppress the difference in intensity of the reflected light.

[0053] In each of the above embodiments, a pattern in which one period of the horizontal rotation alignment gradually becomes longer in the x direction is shown. As an optical element, it is also preferable that the optically anisotropic layer has an in-plane alignment pattern in which one period gradually becomes shorter from the center to one end and the other end in one axial direction in the plane.

[0054] Furthermore, as shown in Fig. 8, it is also preferable to have an in-plane alignment pattern in which one direction of horizontal rotation alignment is set radially from the inside to the outside. Fig. 8 is a plan view schematic diagram of an optically anisotropic layer of an optical element of a design modification example. In Fig. 8, the in-plane alignment pattern is indicated by the optical axis 30A of the liquid crystal compound. The optically anisotropic layer has an in-plane alignment pattern in which regions having the same optical axis direction are arranged concentrically, and one direction in which the direction of the optical axis 30A changes while continuously rotating is arranged radially from the center of the optically anisotropic layer 15.

[0055] In the optically anisotropic layer 15, the direction of the optical axis 30A changes while rotating continuously in a number of directions, for example, the directions indicated by arrows A1, A2, and A3, extending from the center of the optically anisotropic layer 15 toward the outside. The directions of rotation of the optical axis rotating along each axial direction are rotationally symmetrical with respect to the center.

[0056] When an optical element 1 having an optically anisotropic layer with an in-plane orientation pattern shown in FIG. 8 is sandwiched between two orthogonal polarizers and observed with an optical microscope, alternating bright and dark areas are observed in a concentric pattern. The period of light and dark on the concentric periodic orientation surface (i.e., the period of the dark areas or the period of the light areas) is half the period Λ of the horizontal rotation orientation pattern. The period is oriented outward. Since the diameter of each concentric circle is gradually shortened, the difference between the diameters of the adjacent concentric circles becomes smaller as the circle moves outward.

[0057] The circularly polarized light incident on the optically anisotropic layer 15 having this in-plane alignment pattern changes in absolute phase in each local region having a different optical axis direction of the liquid crystal compound 30. At this time, the amount of change in each absolute phase differs depending on the optical axis direction of the liquid crystal compound 30 into which the circularly polarized light is incident.

[0058] As described above, the angle of refraction of light with respect to the incident direction increases as the period Λ of the liquid crystal alignment pattern becomes shorter. Therefore, by gradually shortening the period Λ of the in-plane alignment pattern from the center of the optically anisotropic layer 15 toward the outside in one direction in which the optical axis continuously rotates, the focusing or diverging power of the optically anisotropic layer 15 can be further improved.

[0059] Conversely, one period Λ in the concentric liquid crystal alignment pattern may be gradually lengthened from the center of the optically anisotropic layer 15 toward the outside in one direction in which the optic axis continuously rotates. Furthermore, depending on the application of the optical element, for example when it is desired to provide a light intensity distribution in transmitted light, it is also possible to use a configuration in which, rather than gradually changing one period Λ in one direction in which the optical axis rotates continuously, there is an area in which one period Λ differs partially in one direction in which the optical axis rotates continuously.

[0060] Next, the constituent materials and methods of formation provided in the optical elements of the present disclosure will be described.

[0061] <Optical anisotropic layer> The liquid crystal composition containing a liquid crystal compound for forming an optically anisotropic layer may contain, in addition to the liquid crystal compound, other components such as a leveling agent, an alignment control agent, a polymerization initiator, and an alignment assistant. An alignment film is formed on a support, and a liquid crystal composition is applied on the alignment film and cured, thereby obtaining an optically anisotropic layer consisting of a cured layer of the liquid crystal composition and having a predetermined liquid crystal alignment pattern fixed thereon.

[0062] -Rod-shaped liquid crystal compound- As the rod-shaped liquid crystal compound, azomethines, azoxys, cyanobiphenyls, cyanophenyl esters, benzoates, cyclohexane carboxylic acid phenyl esters, cyanophenylcyclohexanes, cyano-substituted phenylpyrimidines, alkoxy-substituted phenylpyrimidines, phenyldioxanes, tolanes, and alkenylcyclohexylbenzonitriles are preferably used. Not only the above-mentioned low molecular weight liquid crystal molecules, but also polymeric liquid crystal molecules can be used.

[0063] It is more preferable to fix the orientation of the rod-shaped liquid crystal compound by polymerization. As the polymerizable rod-shaped liquid crystal compound, compounds described in Makromol. Chem., Vol. 190, p. 2255 (1989), Advanced Materials, Vol. 5, p. 107 (1993), U.S. Patent Nos. 4,683,327, 5,622,648, and 5,770,107, International Publication Nos. 95 / 22586, 95 / 24455, 97 / 00600, 98 / 23580, and 98 / 52905, JP-A-1-272551, 6-16616, 7-110469, 11-80081, and 2001-328973 can be used. Furthermore, as the rod-shaped liquid crystal compound, for example, those described in JP-T-11-513019 and JP-A-2007-279688 can also be preferably used.

[0064] -Discoid liquid crystal compound- Examples of the discotic liquid crystal compound include those described in JP-A-2007-108732 and JP-A-2007-108732. The one described in 010-244038 can be preferably used.

[0065] -Other ingredients- It should be noted that known materials can be used for the other components such as the alignment control agent, polymerization initiator, alignment assistant, etc. In order to obtain an optically anisotropic layer having a twisted alignment in the thickness direction or an optically anisotropic layer having a cholesteric alignment in the thickness direction, a chiral agent is added.

[0066] --Chiral agents (optically active compounds)-- The chiral agent has a function of inducing a helical structure of the cholesteric liquid crystal phase. Since the twist direction or helical pitch of the helical structure induced by the chiral agent varies depending on the compound, the chiral agent may be selected according to the purpose. The chiral agent is not particularly limited, and may be any of known compounds (for example, Liquid Crystal Device Handbook, Chapter 3, Section 4-3, TN (twisted nematic), STN (Super Examples of chiral agents that can be used include chiral agents for twisted nematics, described on page 199, 142nd Committee of the Japan Society for the Promotion of Science, 1989, isosorbide, and isomannide derivatives. Although the chiral agent generally contains an asymmetric carbon atom, an axially asymmetric compound or a planar asymmetric compound that does not contain an asymmetric carbon atom can also be used as the chiral agent. Examples of the axially asymmetric compound or the planar asymmetric compound include binaphthyl, helicene, paracyclophane, and derivatives thereof. The chiral agent may have a polymerizable group. When both the chiral agent and the liquid crystal compound have a polymerizable group, a polymer having a repeating unit derived from the polymerizable liquid crystal compound and a repeating unit derived from the chiral agent can be formed by a polymerization reaction between the polymerizable chiral agent and the polymerizable liquid crystal compound. In this embodiment, the polymerizable group of the polymerizable chiral agent is preferably the same type of group as the polymerizable group of the polymerizable liquid crystal compound. Therefore, the polymerizable group of the chiral agent is also preferably an unsaturated polymerizable group, an epoxy group, or an aziridinyl group, more preferably an unsaturated polymerizable group, and even more preferably an ethylenically unsaturated polymerizable group. The chiral agent may also be a liquid crystal compound.

[0067] When the chiral agent has a photoisomerizable group, it is preferable because a pattern of a desired reflection wavelength corresponding to the emission wavelength can be formed by irradiating a photomask with actinic rays or the like after coating and alignment. As the photoisomerizable group, an isomerization site of a compound exhibiting photochromic properties, an azo group, an azoxy group, or a cinnamoyl group is preferable. Specific compounds that can be used include those described in JP-A-2002-80478, JP-A-2002-80851, JP-A-2002-179668, JP-A-2002-179669, JP-A-2002-179670, JP-A-2002-179681, JP-A-2002-179682, JP-A-2002-338575, JP-A-2002-338668, JP-A-2003-313189, and JP-A-2003-313292.

[0068] -solvent- As the solvent for the liquid crystal composition, an organic solvent is preferably used. Examples of the organic solvent include amides (e.g., N,N-dimethylformamide), sulfoxides (e.g., dimethyl sulfoxide), heterocyclic compounds (e.g., pyridine), hydrocarbons (e.g., benzene, hexane), alkyl halides (e.g., chloroform, dichloromethane), esters (e.g., methyl acetate, butyl acetate), ketones (e.g., acetone, methyl ethyl ketone, cyclohexanone), and ethers (e.g., tetrahydrofuran, 1,2-dimethoxyethane). Alkyl halides and ketones are preferred. Two or more organic solvents may be used in combination.

[0069] <Formation of Optically Anisotropic Layer> The optically anisotropic layer can be formed, for example, by coating a liquid crystal composition on an alignment film in multiple layers. Multilayer coating refers to a process in which a liquid crystal composition is coated on an alignment film, heated, cooled, and then cured with ultraviolet light to form a first liquid crystal fixing layer, and then layers from the second layer onward are coated on the liquid crystal fixing layer by overlaying, heated in the same manner, cooled, and then cured with ultraviolet light, and the process is repeated.

[0070] <Support> The support supports the optically anisotropic layer or the optically anisotropic layer and the alignment film. The support is not an essential component of the optical element. It may be used when forming the optically anisotropic layer and then peeled off.

[0071] As the support, various types of sheet-like materials (films, plates) can be used as long as they can support the optically anisotropic layer. The support is preferably a transparent support, and examples of the support include polyacrylic resin films such as polymethyl methacrylate, cellulose resin films such as cellulose triacetate, cycloolefin polymer films (for example, trade name "Arton" manufactured by JSR Corporation, trade name "ZEONOR" manufactured by Zeon Corporation), polyethylene terephthalate (PET), polycarbonate, polyvinyl chloride, etc. The support is not limited to a flexible film, and may be a non-flexible substrate such as a glass substrate.

[0072] There is no limitation on the thickness of the support, and the thickness capable of supporting the alignment film and the optically anisotropic layer may be appropriately set depending on the application of the optical element and the material forming the support. The thickness of the support is preferably from 1 to 1000 μm, more preferably from 3 to 250 μm, and further preferably from 5 to 150 μm.

[0073] <Alignment film> The alignment film is provided in order to align the liquid crystal compound in a predetermined liquid crystal alignment pattern when the optically anisotropic layer is formed.

[0074] As the alignment film, various known films can be used. Examples include rubbed films made of organic compounds such as polymers, obliquely evaporated films of inorganic compounds, films with microgrooves, and films formed by stacking LB (Langmuir-Blodgett) films made of organic compounds such as ω-tricosanoic acid, dioctadecylmethylammonium chloride, and methyl stearate using the Langmuir-Blodgett method.

[0075] The alignment layer formed by rubbing treatment can be formed by rubbing the surface of the polymer layer several times in a certain direction with paper or cloth. Preferred examples of materials used for the alignment film include polyimide, polyvinyl alcohol, polymers having polymerizable groups as described in JP-A-9-152509, and materials used for forming alignment films as described in JP-A-2005-97377, JP-A-2005-99228, and JP-A-2005-128503.

[0076] In the optical element of the present disclosure, the alignment film is preferably a so-called photo-alignment film obtained by irradiating a photo-alignable material with polarized or non-polarized light to form an alignment film. That is, in the optical element of the present disclosure, the alignment film is preferably a photo-alignment film formed by applying a photo-alignment material onto a support. The photo-alignment film can be irradiated with polarized light from a vertical direction or an oblique direction, while the photo-alignment film can be irradiated with unpolarized light from an oblique direction.

[0077] Examples of photo-alignment materials used in the photo-alignment film include those described in JP-A-2006-285197, JP-A-2007-76839, JP-A-2007-138138, JP-A-2007-94071, JP-A-2007-121721, JP-A-2007-140465, JP-A-2007-156439, and JP-A-2007-1331. azo compounds described in JP-A-2009-109831, Japanese Patent No. 3883848 and Japanese Patent No. 4151746, aromatic ester compounds described in JP-A-2002-229039, maleimides and / or amides having photo-alignable units described in JP-A-2002-265541 and JP-A-2002-317013, Preferred examples of the photo-dimerizable compounds include alkenyl-substituted nadimide compounds, photo-crosslinkable silane derivatives described in Japanese Patent Nos. 4205195 and 4205198, photo-crosslinkable polyimides, photo-crosslinkable polyamides, and photo-crosslinkable esters described in JP-T-2003-520878, JP-T-2004-529220, and JP-T-4162850, and photo-dimerizable compounds described in JP-A-9-118717, JP-T-10-506420, JP-T-2003-505561, WO 2010 / 150748, JP-A-2013-177561, and JP-A-2014-12823, in particular cinnamate compounds, chalcone compounds, and coumarin compounds. Among these, azo compounds, photocrosslinkable polyimides, photocrosslinkable polyamides, photocrosslinkable esters, cinnamate compounds, and chalcone compounds are preferably used.

[0078] There is no limitation on the thickness of the alignment film, and the thickness may be appropriately set so as to obtain the necessary alignment function depending on the material from which the alignment film is formed. The thickness of the alignment film is preferably from 0.01 to 5 μm, and more preferably from 0.05 to 2 μm.

[0079] There is no limitation on the method for forming the alignment film, and various known methods can be used depending on the material for forming the alignment film. One example is a method in which an alignment film is applied to the surface of a support and dried, and then the alignment film is exposed to laser light to form an alignment pattern.

[0080] 9 conceptually shows an example of an exposure device that exposes an alignment film to form an alignment pattern. The exposure device includes a laser light source 81 that emits laser light, a beam expander 82 that expands the beam diameter of the laser light L emitted from the laser light source 81, a λ / 2 plate 83 arranged on the optical path of the laser light L, and a drive stage 86 on which a lens 84 and an alignment film 90 are placed. The λ / 2 plate 83 is attached to a rotating mount (not shown) and functions as a variable polarization rotator.

[0081] The beam diameter of the laser light L emitted from the laser light source 81 is expanded by the beam expander 82, adjusted to an arbitrary polarization direction by the rotation of the λ / 2 plate 83, and focused on the optical alignment film by the lens 84. The optical alignment film is patterned by scanning and exposing it by driving the driving stage 86. This makes it possible to form a patterned alignment film of a desired pattern.

[0082] In the optical element of the present disclosure, the alignment film is provided as a preferred embodiment, but is not an essential component. For example, it is possible to form an optically anisotropic layer having a horizontal rotation alignment pattern by forming an alignment pattern on the support by a method such as rubbing the support or processing the support with laser light.

[0083] Although the above optical elements have been described with respect to a configuration that basically assumes a single wavelength of incident light, they can also be configured to have a similar effect on multiple wavelengths of incident light. If an optical element has a structure in which optically anisotropic layers having liquid crystal orientation patterns corresponding to each wavelength are laminated, multiple wavelengths of incident light can be used.

[0084] [Light deflection device] FIG. 10 is a schematic diagram showing an example of a light deflection device according to an embodiment. The optical deflection device 130 includes, from the upstream side in the traveling direction of light (light beam), a condenser lens 131, a λ / 4 plate 111, an optical deflection element 132, and an optical element 120 according to an embodiment of the present invention. In the following description, upstream and downstream refer to the upstream and downstream in the traveling direction of light.

[0085] The condenser lens 131 is a known condenser lens, and is provided to make the light (light beam) from a light source (not shown) enter the light deflection element 132 in a slightly condensed state. The condenser lens 131 is provided as a preferred embodiment, but is not an essential component. However, by providing the condenser lens 131, the light (light beam) emitted from the light deflection device 130 can be made into an appropriate parallel light, improving the linearity. Note that the present invention is not limited to the condenser lens 131, and any known condenser element capable of condensing light (light beam) can be used.

[0086] The λ / 4 plate 111 is a known λ / 4 plate (1 / 4 retardation plate) that converts linearly polarized light emitted from a light source to circularly polarized light. Any known plate can be used as the λ / 4 plate 111 without any restrictions. Therefore, the λ / 4 plate 111 may be made of a polymer or a liquid crystal. The λ / 4 plate 111 may be disposed between a MEMS (Micro Electro Mechanical System) deflection element 132 and the optical element 120. However, it is preferable to provide the λ / 4 plate 111 upstream of the MEMS optical deflection element 132 in terms of miniaturization of the λ / 4 plate 111, etc. When circularly polarized light is incident on the optical deflection device 130 using the MEMS optical deflection element 132, the λ / 4 plate 111 is not required to be provided.

[0087] The optical deflection element 132 is a MEMS optical deflection element that performs two-dimensional scanning of light. The MEMS optical deflection element is not particularly limited, and any known MEMS optical deflection element (MEMS (optical) scanner, MEMS optical deflector, MEMS mirror, or DMD (Digital Micromirror Device)) that deflects (deflectively scans) light by swinging a mirror using a piezoelectric actuator or the like, such as the MEMS optical deflection element described in JP 2012-208352 A, the MEMS optical deflection element described in JP 2014-134642 A, and the MEMS optical deflection element described in JP 2015-22064 A, can be appropriately used.

[0088] A driving device 134 for driving and rotating the mirror is connected to the optical deflection element 132. As the driving device 134, a known device corresponding to the configuration of the MEMS optical deflection element 132 and the like may be used.

[0089] The optical element 120 includes two optically anisotropic layers having an in-plane liquid crystal orientation pattern in which the optical axis is horizontally rotated along the axis radially arranged from the center as shown in FIG. 8, and the period becomes smaller toward the outside. As shown in FIG. 10, the period becomes smaller toward the outside compared to the period Λ1 in the central region of the optical element 120 (Λ1>Λ2>Λ3>Λ4...). Here, one optically anisotropic layer 121 is an inclined optically anisotropic layer, and the other optically anisotropic layer 122 is an optically anisotropic layer that does not have a torsion in the thickness direction and has a uniform pattern in the thickness direction. The optical element 120 is arranged so that the center coincides with the center of deflection of the optical deflection element 132. The inclination of the bright and dark lines with respect to the normal in the cross-sectional SEM image of the optical element 120 is larger toward the center and smaller toward the outside.

[0090] In the optical deflection device 130, P-polarized light emitted from a light source (not shown) toward the exit surface 120b of the optical element 120 is slightly condensed by the condenser lens 131, and then deflected by a wavelength of λ / 4 The plate 111 converts it into, for example, right-handed circularly polarized light.

[0091] The light converted into circularly polarized light by the λ / 4 plate 111 is deflected by the MEMS optical deflection element 132 and is incident on the incident surface 120a of the optical element 120. The light incident on the optical element 120 is diffracted and is emitted from the exit surface 120b of the optical element 120, i.e., from the optical deflection device 130.

[0092] Since the optical element 120 is arranged so that the center of the optical element 120 coincides with the center of the deflection of the optical deflection element 132, the light scanned by the optical deflection element 132 is incident on one surface of the optical element 120 at a larger incident angle as it moves away from the center of the surface. The period of the horizontal rotational orientation is configured to become shorter as it moves away from the center, and the bending force is stronger toward the outside. Therefore, the optical element 120 hardly generates a bending force for vertically incident light, transmits the light as it is, and bends the light more toward the outside of the optical element 120 before outputting it. By making polarized light that is given a bending force from the center to the outside by the horizontal rotational orientation of the optically anisotropic layers 121 and 122 incident on the optical element 120 as incident light, a scan angle θmaxout larger than the scan angle θmax of the optical deflection element 132 can be obtained.

[0093] Here, if the incident angle of light incident on incident surface 120a of optical element 120 is θ1, the refractive index of the medium on the incident side is n1, the exit angle of light exiting surface 120b of optical element 120 is θ2, the refractive index of the medium on the exit side is n2, the wavelength of light is λ, the periodic structure pitch of the liquid crystal diffraction element is Λ, and the diffraction order is m, these values ​​are related by the following equation (1). n1·sinθ1-n2·sinθ2=m·λ / Λ (1)

[0094] As described above, by changing the period Λ of the horizontal rotation alignment pattern in the optically anisotropic layer of the optical element 120, the angle of the emitted light from the optical element 120 can be changed. Considering Snell's law, the angle at which the light is finally emitted into the air can be up to an absolute value of about 80°, so it is possible to expand the emission angle to a very large angle. In addition, by continuously changing the period of the horizontal rotation orientation pattern in the optically anisotropic layer of the optical element 120 within the plane, it is possible to continuously emit light in any direction.

[0095] As is clear from the above description, the optical deflection device of the present disclosure makes it possible to perform optical scanning at a scan angle wider than the scan angle (angle of view) of the optical deflection element. Note that, although FIG. 10 shows the scan angle being expanded in the x direction, the horizontal rotation orientation pattern is provided radially, so that the scan angle can also be expanded in the y direction by the same principle. Therefore, by diffracting and scanning the deflected light (scanning light) from the optical deflection element 132 by the optical element 120, it becomes possible to greatly expand the scanning range beyond the scanning range that can be two-dimensionally scanned by the optical deflection element 132.

[0096] Even if the optical element 120 applied to such an optical deflection device 130 does not include the inclined optical anisotropic layer 121, the effect of expanding the scan angle can be obtained. However, when an optical element that does not include the inclined optical anisotropic layer 121 and includes only the optical anisotropic layer 122 is applied, there is a problem that a large difference in diffraction efficiency occurs between the vicinity of the center where the incident angle is small and the peripheral area where the incident angle is large and the diffraction angle is large, and the overall diffraction efficiency (average diffraction efficiency) is low. By providing the inclined optical anisotropic layer 121, the diffraction efficiency of the peripheral area of ​​the element where the incident angle is large can be improved, the difference in diffraction efficiency due to the incident position and incident angle can be suppressed, and the light amount variation of the output light can be suppressed. In addition, by providing two or more optical anisotropic layers, the average diffraction efficiency can also be improved.

[0097] In addition, in the optical deflection device, the optical element is not limited to the optical element 120, and for example, a horizontal rotation alignment pattern in which the period in the x-axis direction gradually decreases from one side to the other as shown in FIG. Alternatively, an optical element may be used that has an optically anisotropic layer having a horizontal rotation alignment pattern whose period gradually decreases from the center of the element to the outside in the x-axis direction, and in which the rotation directions of the optical axes of the horizontal rotation alignment patterns on both sides of the center are opposite to each other. EXAMPLES

[0098] The features of the present invention will be described in more detail below with reference to examples. The materials, reagents, amounts used, amounts of substances, ratios, processing contents, and processing procedures shown in the following examples can be changed as appropriate without departing from the spirit of the present invention. Therefore, the scope of the present invention should not be interpreted as being limited by the specific examples shown below. In the following examples and comparative examples, the liquid crystal orientation pattern was designed assuming infrared light with a target wavelength of 940 nm as the incident light.

[0099] [Comparative Example 1] An optical element having a non-tilted optically anisotropic layer 211 in which the light-dark lines are not inclined in a cross-sectional SEM image as the first optically anisotropic layer was produced as Comparative Example 1 (see FIG. 11).

[0100] <Fabrication of optical elements> (Formation of alignment film) The following coating solution for forming an alignment film was applied to a glass substrate by spin coating. The support on which the coating film of the coating solution for forming an alignment film was formed was dried on a hot plate at 60° C. for 60 seconds to form an alignment film.

[0101] Coating solution for forming alignment film ---------------------------------------------------------------------------------- Photoalignment material A 1.00 parts by mass Water 16.00 parts by mass Butoxyethanol 42.00 parts by weight Propylene glycol monomethyl ether 42.00 parts by mass ----------------------------------------------------------------------------------

[0102] -Photo alignment material A- [ka]

[0103] (Exposure of alignment film) The alignment film was exposed to light using an exposure device that scans and patterns the alignment film while arbitrarily changing the polarization direction of the focused laser light shown in Figure 9, to form an alignment film P-1 having an alignment pattern. In the exposure device, a laser that emits laser light with a wavelength of 325 nm was used. The alignment pattern was a concentric circle, and one period of the alignment pattern was gradually shortened from the center to the outside.

[0104] (Formation of the first optically anisotropic layer) As a liquid crystal composition for forming an optically anisotropic layer, the following composition A-1 was prepared.

[0105] Composition A-1 ------------------------------------------------------------------ Liquid crystal compound L-1 100.00 parts by mass Polymerization initiator (BASF, Irgacure (registered trademark) 907) 3.00 parts by mass Photosensitizer (KAYACURE DETX-S, Nippon Kayaku) 1.00 parts by mass Leveling agent T-1 0.08 parts by weight Methyl ethyl ketone 2840.00 parts by mass ------------------------------------------------------------------

[0106] Liquid crystal compound L-1 [ka]

[0107] Leveling agent T-1 [ka]

[0108] The first optically anisotropic layer was formed by applying composition A-1 in multiple layers onto the alignment film P-1. First, composition A-1 was applied as a first layer onto the alignment film, heated, cooled, and then cured with UV light to prepare a liquid crystal fixing layer, and then the second and subsequent layers were repeatedly applied to the liquid crystal fixing layer, and similarly heated, cooled, and cured with UV light were repeatedly performed.

[0109] First, the first layer was formed by applying the following composition A-1 onto the alignment film P-1, heating the coating to 70°C on a hot plate, then cooling to 25°C, and irradiating the coating with ultraviolet light of 365 nm in wavelength at 300 mJ / cm using a high-pressure mercury lamp in a nitrogen atmosphere. 2 The alignment of the liquid crystal compound was fixed by irradiating the coating with a dose of 1000 nm. The thickness of the first liquid crystal layer was 0.2 μm.

[0110] The second and subsequent layers were coated on top of the liquid crystal layer, heated and cooled under the same conditions as above, and then cured with ultraviolet light to form a liquid crystal fixing layer. In this manner, coating was repeated until the desired total thickness was reached, forming the first optically anisotropic layer.

[0111] The optical element of Comparative Example 1 was produced by the above steps.

[0112] The complex refractive index Δn of the cured layer of the liquid crystal composition A1 was determined by measuring the retardation Re(λ) and film thickness of the liquid crystal fixed layer (cured layer) obtained by applying the liquid crystal composition A1 onto a support with an alignment film for retardation measurement prepared separately, aligning the director of the liquid crystal compound so that it was horizontal to the substrate, and then irradiating it with ultraviolet light to fix it. The retardation Re(λ) was divided by the film thickness to obtain Δn λ The retardation Re(λ) was measured at the desired wavelength using a Woollam spectroscopic ellipsometer, and the film thickness was measured using a SEM. In the notation of Re(λ), λ is the wavelength of the incident light. In the following, the wavelength λ of the incident light is set to 940 nm.

[0113] The first optically anisotropic layer is finally formed by controlling the Δn 940 It was confirmed by a polarizing microscope that the surface had a concentric periodic alignment as shown in FIG. 8, with the result that the surface had a concentric periodic alignment (Re(940)) of 470 nm. The concentric periodic alignment surface means that the axis of horizontal rotation alignment is an in-plane alignment pattern arranged radially from the center. In the horizontal rotation alignment pattern of this first optically anisotropic layer, one period was very large at the center (the reciprocal of the period can be considered to be 0), and was 9.0 μm at a distance of 1.0 mm from the center, 4.5 μm at a distance of 2.5 mm from the center, and 3.0 μm at a distance of 4.0 mm from the center, with the period becoming shorter toward the outside. In addition, the twist angle in the thickness direction of the first optically anisotropic layer was 0°. Hereinafter, unless otherwise specified, "Δn 940 Measurements such as "length x thickness" were also performed in the same manner. In addition, in the cross-sectional image taken by SEM, bright and dark lines were observed extending in the vertical direction, i.e., along the normal line, to the lower interface (interface with the glass substrate) of the optically anisotropic layer. In the repeated pattern of bright and dark lines, it was observed that the period became shorter from the center to the outside.

[0114] [Example 1] An optical element having two optically anisotropic layers, the first optically anisotropic layer being an inclined optically anisotropic layer 212 in which the light-dark lines in a cross-sectional SEM image are inclined to the normal to the interface, and the second optically anisotropic layer being a non-inclined optically anisotropic layer 211, was fabricated as Example 1 (see Figure 12).

[0115] (Formation of the first optically anisotropic layer) As a liquid crystal composition for forming an optically anisotropic layer, the following composition A-2 was prepared.

[0116] Composition A-2 ---------------------------------------------------------------------------------- Liquid crystal compound L-1 100.00 parts by mass Chiral agent A 0.21 parts by mass Polymerization initiator (BASF, Irgacure (registered trademark) 907) 3.00 parts by mass Photosensitizer (KAYACURE DETX-S, Nippon Kayaku) 1.00 parts by mass Leveling agent T-1 0.08 parts by weight Methyl ethyl ketone 2840.00 parts by mass ----------------------------------------------------------------------------------

[0117] Chiral agent A [ka]

[0118] A first optically anisotropic layer was formed on the alignment film P-1 in the same manner as in Comparative Example 1, except that the composition A-2 was used.

[0119] (Formation of the second optically anisotropic layer) The second optically anisotropic layer of Example 1 was similar to the first optically anisotropic layer of Comparative Example 1, and the second optically anisotropic layer was formed on the first optically anisotropic layer using composition A-1 in the same manner as the first optically anisotropic layer of Comparative Example 1, to produce the optical element of Example 1.

[0120] The first optically anisotropic layer and the second optically anisotropic layer are finally formed by the Δn 940It was confirmed by a polarizing microscope that the value of Re(940) × thickness was 470 nm, and the surface had a periodic concentric alignment as shown in FIG. 8. In the horizontal rotation alignment pattern of the first optically anisotropic layer, one period was very large at the center (the reciprocal of the period can be considered as 0), 9.0 μm at a distance of 1.0 mm from the center, 4.5 μm at a distance of 2.5 mm from the center, and 3.0 μm at a distance of 4.0 mm from the center, and the period became shorter toward the outside. Since the second optically anisotropic layer was formed by coating on the first optically anisotropic layer, its period was the same as that of the first optically anisotropic layer. The other layers formed by coating on the first optically anisotropic layer have the same period as described below. The twist angle in the thickness direction of the first optically anisotropic layer was 140° right twist. The twist angle in the thickness direction of the second optically anisotropic layer was 0°. In addition, in the cross-sectional images taken by SEM, bright and dark lines inclined obliquely with respect to the normal to the interface below the optically anisotropic layer (interface with the glass substrate) were observed in the first optically anisotropic layer, while bright and dark lines extending in the normal direction were observed in the second optically anisotropic layer. In the first optically anisotropic layer, the inclination angle of the bright and dark lines with respect to the normal became smaller from the center to the outside. It was observed that the period of the bright and dark line patterns became shorter from the center to the outside in both the first optically anisotropic layer and the second optically anisotropic layer.

[0121] [Example 2] An optical element having two optically anisotropic layers, the first optically anisotropic layer being a non-inclined optically anisotropic layer 211 and the second optically anisotropic layer being an inclined optically anisotropic layer 212, was fabricated as Example 2 (see FIG. 13). That is, Example 2 has a configuration in which the first optically anisotropic layer and the second optically anisotropic layer of Example 1 are reversed.

[0122] An optical element of Example 2 was produced in the same manner as in Example 1, except that the first optically anisotropic layer was formed using composition A-1 and the second optically anisotropic layer was formed using composition A-2.

[0123] The first optically anisotropic layer and the second optically anisotropic layer are finally formed by the Δn 940It was confirmed by a polarizing microscope that the thickness (Re(940)) was 470 nm and the surface had a concentric periodic alignment as shown in FIG. 8. In the horizontal rotation alignment pattern of the first optically anisotropic layer, one period was very large at the center (the reciprocal of the period can be considered as 0), 9.0 μm at a distance of 1.0 mm from the center, 4.5 μm at a distance of 2.5 mm from the center, and 3.0 μm at a distance of 4.0 mm from the center, and the period became shorter toward the outside. In addition, the twist angle in the thickness direction of the first optically anisotropic layer was 0°. The twist angle in the thickness direction of the second optically anisotropic layer was 140° to the right. In addition, in the cross-sectional image by SEM, bright and dark lines extending in the normal direction of the interface under the optically anisotropic layer (interface with the glass substrate) were observed in the first optically anisotropic layer, and bright and dark lines inclined obliquely to the normal were observed in the second optically anisotropic layer. In the second optically anisotropic layer, the angle of inclination of the bright and dark lines with respect to the normal line became smaller from the center to the outside. It was observed that the period of the bright and dark line patterns became shorter from the center to the outside in both the first and second optically anisotropic layers.

[0124] [Comparative Example 2] An optical element was produced as Comparative Example 2, which had a tilted optically anisotropic layer 212 as a first optically anisotropic layer, in which bright and dark lines in a cross-sectional SEM image were tilted with respect to the normal line to the interface.

[0125] (Formation of the first optically anisotropic layer) The first optically anisotropic layer of Comparative Example 2 was the same as the first optically anisotropic layer of Example 1, and the first optically anisotropic layer was formed on the alignment film P-1 using composition A-2 in the same manner as the first optically anisotropic layer of Example 1 to produce the optical element of Comparative Example 2. That is, the optical element of Comparative Example 2 was configured to include only one tilted optically anisotropic layer as the optically anisotropic layer.

[0126] The first optically anisotropic layer is finally formed by controlling the Δn 940It was confirmed by a polarizing microscope that the surface had a periodic alignment with concentric circles as shown in FIG. 8, and the horizontal rotation alignment pattern of the first optically anisotropic layer had a very large period at the center (the reciprocal of the period was considered to be 0), 9.0 μm at a distance of 1.0 mm from the center, 4.5 μm at a distance of 2.5 mm from the center, and 3.0 μm at a distance of 4.0 mm from the center, and the period became shorter toward the outside. The twist angle in the thickness direction of the first optically anisotropic layer was 140° right twist. In addition, in the cross-sectional image by SEM, a light and dark line inclined obliquely with respect to the normal line of the interface under the optically anisotropic layer (interface with the glass substrate) was observed in the first optically anisotropic layer. In the first optically anisotropic layer, the inclination angle of the light and dark line with respect to the normal line became smaller from the center to the outside. It was observed that the period of the light and dark line pattern became shorter from the center to the outside.

[0127] [Example 3] An optical element having two optically anisotropic layers, the first optically anisotropic layer and the second optically anisotropic layer being tilted optically anisotropic layers 213, 214 in which the bright and dark lines in the cross-sectional SEM images are tilted toward the normal line of the interface, was produced as Example 3 (see FIG. 14). The first optically anisotropic layer and the second optically anisotropic layer had the same tilt direction of the bright and dark lines in the cross-sectional SEM images, but the tilt angle was made different.

[0128] (Formation of the first optically anisotropic layer) As a liquid crystal composition for forming the first optically anisotropic layer, the following composition A-3 was prepared.

[0129] Composition A-3 ---------------------------------------------------------------------------------- Liquid crystal compound L-1 100.00 parts by mass Chiral agent A 0.24 parts by mass Polymerization initiator (BASF, Irgacure (registered trademark) 907) 3.00 parts by mass Photosensitizer (KAYACURE DETX-S, Nippon Kayaku) 1.00 parts by mass Leveling agent T-1 0.08 parts by weight Methyl ethyl ketone 2840.00 parts by mass ----------------------------------------------------------------------------------

[0130] A first optically anisotropic layer was formed on the alignment film P-1 in the same manner as in Example 1, except that the composition A-3 was used.

[0131] (Formation of the second optically anisotropic layer) As a liquid crystal composition for forming an optically anisotropic layer, the following composition A-4 was prepared.

[0132] Composition A-4 ---------------------------------------------------------------------------------- Liquid crystal compound L-1 100.00 parts by mass Chiral agent A 0.03 parts by mass Polymerization initiator (BASF, Irgacure (registered trademark) 907) 3.00 parts by mass Photosensitizer (KAYACURE DETX-S, Nippon Kayaku) 1.00 parts by mass Leveling agent T-1 0.08 parts by weight Methyl ethyl ketone 2840.00 parts by mass ----------------------------------------------------------------------------------

[0133] An optical element of Example 3 was prepared in the same manner as in Example 1, except that composition A-4 was used, by forming a second optically anisotropic layer on the first optically anisotropic layer.

[0134] The first optically anisotropic layer and the second optically anisotropic layer are finally formed by the Δn 940It was confirmed by a polarizing microscope that the thickness x thickness = Re(940) was 470 nm, and the surface had a concentric periodic alignment as shown in FIG. 8. In the horizontal rotation alignment pattern of the first optically anisotropic layer, one period was very large at the center (the reciprocal of the period can be considered as 0), 9.0 μm at a distance of 1.0 mm from the center, 4.5 μm at a distance of 2.5 mm from the center, and 3.0 μm at a distance of 4.0 mm from the center, and the period became shorter toward the outside. In addition, the twist angle in the thickness direction of the first optically anisotropic layer was 160° right twist. The twist angle in the thickness direction of the second optically anisotropic layer was 20° right twist. The twist directions of the first optically anisotropic layer and the second optically anisotropic layer were the same. In addition, in the cross-sectional image by SEM, inclined light and dark lines were observed in both the first optically anisotropic layer and the second optically anisotropic layer, which were inclined obliquely with respect to the normal line of the interface below the optically anisotropic layer. Furthermore, the inclination angle of the light and dark lines with respect to the normal line became smaller from the center to the outside, and the inclination direction from the normal line of the light and dark lines of the first optically anisotropic layer and the second optically anisotropic layer was the same. It was observed that the period of the light and dark line pattern became shorter from the center to the outside in both the first optically anisotropic layer and the second optically anisotropic layer.

[0135] [Example 4] An optical element having two optically anisotropic layers, the first optically anisotropic layer and the second optically anisotropic layer being tilted optically anisotropic layers 215, 216 in which the bright and dark lines in the cross-sectional SEM image are tilted toward the normal line of the interface, was produced as Example 4 (see FIG. 15). The first optically anisotropic layer and the second optically anisotropic layer were made to differ in the direction of the tilt of the bright and dark lines in the cross-sectional SEM image.

[0136] (Formation of the first optically anisotropic layer) As a liquid crystal composition for forming an optically anisotropic layer, the following composition A-5 was prepared.

[0137] Composition A-5 ---------------------------------------------------------------------------------- Liquid crystal compound L-1 100.00 parts by mass Chiral agent A 0.13 parts by mass Polymerization initiator (BASF, Irgacure (registered trademark) 907) 3.00 parts by mass Photosensitizer (KAYACURE DETX-S, Nippon Kayaku) 1.00 parts by mass Leveling agent T-1 0.08 parts by weight Methyl ethyl ketone 2840.00 parts by mass ----------------------------------------------------------------------------------

[0138] A first optically anisotropic layer was formed on the alignment film P-1 in the same manner as in Example 1, except that the composition A-5 was used.

[0139] (Formation of the second optically anisotropic layer) As a liquid crystal composition for forming an optically anisotropic layer, the following composition A-6 was prepared.

[0140] Composition A-6 ---------------------------------------------------------------------------------- Liquid crystal compound L-1 100.00 parts by mass Chiral agent B 0.22 parts by mass Polymerization initiator (BASF, Irgacure (registered trademark) 907) 3.00 parts by mass Photosensitizer (KAYACURE DETX-S, Nippon Kayaku) 1.00 parts by mass Leveling agent T-1 0.08 parts by weight Methyl ethyl ketone 2840.00 parts by mass ----------------------------------------------------------------------------------

[0141] Chiral agent B [ka]

[0142] A second optically anisotropic layer was formed on the first optically anisotropic layer in the same manner as in Example 1, except that composition A-6 was used, to prepare an optical element of Example 4.

[0143] The first optically anisotropic layer and the second optically anisotropic layer are finally formed by the Δn 940 It was confirmed by a polarizing microscope that the surface had a concentric periodic alignment as shown in FIG. 8, with the thickness=Re(940) being 470 nm. In addition, in the horizontal rotation alignment pattern of the first optically anisotropic layer, one period was very large at the center (the reciprocal of the period can be considered as 0), 9.0 μm at a distance of 1.0 mm from the center, 4.5 μm at a distance of 2.5 mm from the center, and 3.0 μm at a distance of 4.0 mm from the center, and the period became shorter toward the outside. In addition, the twist angle in the thickness direction of the first optically anisotropic layer was 80° right twist. The twist angle in the thickness direction of the second optically anisotropic layer was 80° left twist. The twist directions of the first optically anisotropic layer and the second optically anisotropic layer were opposite to each other. In addition, in the cross-sectional images taken by SEM, it was observed that the bright and dark lines in both the first and second optically anisotropic layers were inclined obliquely with respect to the normal line of the interface below the optically anisotropic layers. Furthermore, the inclination angle of the bright and dark lines with respect to the normal line became smaller from the center to the outside, and the inclination direction of the bright and dark lines from the normal line of the first and second optically anisotropic layers was opposite. It was observed that the period of the bright and dark line patterns became shorter from the center to the outside in both the first and second optically anisotropic layers.

[0144] [Example 5] An optical element having three optically anisotropic layers, in which the first optically anisotropic layer and the third optically anisotropic layer are inclined optically anisotropic layers 217, 218 in which the light and dark lines in the cross-sectional SEM image are inclined to the normal line of the interface, and the second optically anisotropic layer 219 disposed between the first and third optically anisotropic layers is a non-inclined optically anisotropic layer, was produced as Example 5 (see FIG. 16). The first optically anisotropic layer and the third optically anisotropic layer were made to have different inclination directions of the light and dark lines in the cross-sectional SEM image.

[0145] (Formation of the first optically anisotropic layer) As a liquid crystal composition for forming an optically anisotropic layer, the following composition A-7 was prepared.

[0146] Composition A-7 ---------------------------------------------------------------------------------- Liquid crystal compound L-1 100.00 parts by mass Chiral agent A 0.19 parts by mass Polymerization initiator (BASF, Irgacure (registered trademark) 907) 3.00 parts by mass Photosensitizer (KAYACURE DETX-S, Nippon Kayaku) 1.00 parts by mass Leveling agent T-1 0.08 parts by weight Methyl ethyl ketone 2840.00 parts by mass ----------------------------------------------------------------------------------

[0147] A first optically anisotropic layer was formed on the alignment film P-1 in the same manner as in Example 1, except that the composition A-7 was used.

[0148] (Formation of the second optically anisotropic layer) A second optically anisotropic layer was formed on the first optically anisotropic layer in the same manner as for the first optically anisotropic layer in Comparative Example 1, except that Composition A-1 was used and the film thickness was changed.

[0149] (Formation of the third optically anisotropic layer) As a liquid crystal composition for forming an optically anisotropic layer, the following composition A-8 was prepared.

[0150] Composition A-8 ---------------------------------------------------------------------------------- Liquid crystal compound L-1 100.00 parts by mass Chiral agent B 0.32 parts by mass Polymerization initiator (BASF, Irgacure (registered trademark) 907) 3.00 parts by mass Photosensitizer (KAYACURE DETX-S, Nippon Kayaku) 1.00 parts by mass Leveling agent T-1 0.08 parts by weight Methyl ethyl ketone 2840.00 parts by mass ----------------------------------------------------------------------------------

[0151] A third optically anisotropic layer was formed on the second optically anisotropic layer in the same manner as in Example 1, except that composition A-8 was used, to prepare an optical element of Example 5.

[0152] The first optically anisotropic layer and the third optically anisotropic layer are finally 940 × thickness = Re(940) is 470 nm, and the second optically anisotropic layer has a thickness of Δn 940 × thickness (Re(940)) was 564 nm. In addition, it was confirmed by a polarizing microscope that the surface had a concentric periodic alignment as shown in FIG. 8. In the horizontal rotation alignment pattern of this first optically anisotropic layer, one period was very large at the center (the reciprocal of the period can be considered as 0), 9.0 μm at a distance of 1.0 mm from the center, 4.5 μm at a distance of 2.5 mm from the center, and 3.0 μm at a distance of 4.0 mm from the center, and the period became shorter toward the outside. In addition, the twist angle in the thickness direction of the first optically anisotropic layer was 130° right twist. The twist angle in the thickness direction of the second optically anisotropic layer was 0°, and the twist angle in the thickness direction of the third optically anisotropic layer was 130° left twist. The twist directions of the first optically anisotropic layer and the third optically anisotropic layer were opposite to each other. In the cross-sectional images taken by SEM, the first and third optically anisotropic layers had bright and dark lines that were inclined obliquely with respect to the normal line of the interface below the optically anisotropic layers, while the second optically anisotropic layer had bright and dark lines that ran along the normal line. In the first and third optically anisotropic layers, the inclination angle of the bright and dark lines with respect to the normal line became smaller from the center to the outside, and the inclination direction of the bright and dark lines with respect to the normal line of the first and third optically anisotropic layers was opposite. It was observed that the period of the bright and dark line patterns became shorter from the center to the outside in the first, second and third optically anisotropic layers.

[0153] [evaluation] The optical elements of Comparative Example 1 and Examples 1 to 5 function as transmission type diffraction elements. For each optical element, the angle of the transmitted diffracted light with respect to the normal direction of the optical element when light was incident was measured, and the light intensity increase rate was evaluated with respect to the element of Comparative Example 1. The specific measurement method is as follows.

[0154] First, a laser beam was irradiated onto the surface of the optical element at a specific angle of incidence, and the transmitted light was projected onto a screen placed 30 cm away in the normal direction of the optical element. The angle of the transmitted diffracted light was calculated from the image captured by an infrared camera. A laser diode with a wavelength of 940 nm was used as the light source.

[0155] Next, as shown in FIG. 17, a laser light having a wavelength of 940 nm emitted from a laser light source 251 is transmitted through a linear polarizer 252 and a λ / 4 plate 254 to become right-circularly polarized light Li. This light Li is incident on a predetermined position on the surface of an optical element S at a predetermined incident angle. The light intensity of the transmitted diffracted light Ld diffracted by the optical element S is measured by a photodetector 256. Then, the ratio of the light intensity of the diffracted light Ld to the light intensity of the light Li is calculated to obtain a relative light intensity value of the diffracted light Ld with respect to the incident light. In addition, the relative light intensity value is similarly calculated by changing the incident angle. The light intensity increase rate of the example with respect to the comparative example 1 is evaluated based on the average value of the relative light intensity values ​​for different incident angles according to the following criteria.

[0156] A: Light intensity increase rate is 20% or more B: Light intensity increase rate is 10% or more but less than 20% C: Light intensity increase rate is 5% or more but less than 10% D: Light intensity increase rate is less than 5%

[0157] In comparing Comparative Example 1 and Comparative Example 2 with Examples 1 to 3, the evaluation was performed with the incidence angle at a distance of 1.0 mm from the center (one period: 9.0 μm) set to 10°, the incidence angle at a distance of 2.5 mm from the center (one period: 4.5 μm) set to 20°, and the incidence angle at a distance of 4.0 mm from the center (one period: 3.0 μm) set to 30°. In addition, when comparing Comparative Example 1 and Comparative Example 2 with Example 4 and Example 5, the incidence angle was evaluated at a distance of 1.0 mm from the center (one period: 9.0 μm) of ±10°, the incidence angle at a distance of 2.5 mm from the center (one period: 4.5 μm) of ±20°, and the incidence angle at a distance of 4.0 mm from the center (one period: 3.0 μm) of ±30°.

[0158] The results are shown in Table 1. [Table 1]

[0159] In Examples 1 to 3, the average diffraction efficiency was higher than that of Comparative Example 1 in the incidence angle range of 10 to 30°, and in Examples 4 and 5, the average diffraction efficiency was higher than that of Comparative Example 1 in the incidence angle range of -30 to +30°. By combining tilted optically anisotropic layers with opposite light-dark line gradients in cross-sectional SEM images, the diffraction efficiency could be increased over a wider incidence angle range. In the optical element of Comparative Example 2, the effect of increasing the average diffraction efficiency was not obtained.

[0160] [Comparative Example 11] An optical element having a first optically anisotropic layer 221 with a horizontal rotation alignment pattern whose period gradually changes and cholesterically aligned in the thickness direction was produced as Comparative Example 11 (see FIG. 18). In FIG. 18, part of the cholesteric alignment in the thickness direction is shown diagrammatically.

[0161] (Formation of the first optically anisotropic layer) The following composition C-1 was prepared as a liquid crystal composition for forming an optically anisotropic layer. This composition C-1 is a liquid crystal composition that forms a cholesteric liquid crystal layer that has a selective reflection center wavelength of 940 nm and reflects right-handed circularly polarized light.

[0162] Composition C-1 ---------------------------------------------------------------------------------- Liquid crystal compound L-1 100.00 parts by mass Chiral agent A 3.11 parts by mass Polymerization initiator (BASF, Irgacure (registered trademark) 907) 3.00 parts by mass Photosensitizer (KAYACURE DETX-S, Nippon Kayaku) 1.00 parts by mass Leveling agent T-1 0.08 parts by weight Methyl ethyl ketone 2840.00 parts by mass ----------------------------------------------------------------------------------

[0163] An optical element of Comparative Example 11 was prepared by forming a first optically anisotropic layer on an alignment film P-1 in the same manner as in Example 1, except that the composition C-1 was used and the film thickness was changed.

[0164] The cross section of the coating layer of the first optically anisotropic layer was observed with a scanning electron microscope, and it was confirmed with a polarizing microscope that the cholesteric liquid crystal phase had an 8-pitch and was a concentrically periodic alignment surface as shown in FIG. 8. In the horizontal rotation alignment pattern of this first optically anisotropic layer, one period was very large at the center (the reciprocal of the period can be considered to be 0), 9.0 μm at a distance of 1.0 mm from the center, 4.5 μm at a distance of 2.5 mm from the center, and 3.0 μm at a distance of 4.0 mm from the center, and the period became shorter toward the outside. In addition, in the cross-sectional image by SEM, the bright and dark lines in the first optically anisotropic layer were inclined obliquely with respect to the normal line of the interface below the optically anisotropic layer. In the first optically anisotropic layer, the inclination angle of the bright and dark lines increased from the center to the outside. It was observed that the period of the bright and dark line pattern of the first optically anisotropic layer became shorter from the center to the outside.

[0165] [Example 11] An optical element having a horizontal rotation alignment pattern with a gradually changing period and including a first optically anisotropic layer 222 and a second optically anisotropic layer 223 cholesterically aligned in the thickness direction was produced as Example 11 (see FIG. 19). In FIG. 19, a part of the cholesteric alignment in the thickness direction is shown diagrammatically.

[0166] (Formation of the first optically anisotropic layer) A first optically anisotropic layer was formed on an alignment film P-1 in the same manner as in Comparative Example 11 using the composition C-1.

[0167] When the cross section of the coating layer of the first optically anisotropic layer was observed with a scanning electron microscope, it was found that the layer It was confirmed by a polarizing microscope that the liquid crystal phase had an 8-pitch and formed a concentric (radial) periodic alignment surface as shown in Figure 8. In the horizontal rotation alignment pattern of this first optically anisotropic layer, one period was very large at the center (the reciprocal of the period can be considered to be 0), was 9.0 μm at a distance of 1.0 mm from the center, 4.5 μm at a distance of 2.5 mm from the center, and 3.0 μm at a distance of 4.0 mm from the center, and the period became shorter toward the outside.

[0168] (Formation of the second optically anisotropic layer) The following composition C-2 was prepared as a liquid crystal composition for forming a second optically anisotropic layer. This composition C-2 is a liquid crystal composition that forms a cholesteric liquid crystal layer that has a selective reflection center wavelength of 940 nm and reflects left-handed circularly polarized light.

[0169] <Composition C-2> ---------------------------------------------------------------------------------- Liquid crystal compound L-1 100.00 parts by mass Chiral agent B 4.42 parts by mass Polymerization initiator (BASF, Irgacure (registered trademark) 907) 3.00 parts by mass Photosensitizer (KAYACURE DETX-S, Nippon Kayaku) 1.00 parts by mass Leveling agent T-1 0.08 parts by weight Methyl ethyl ketone 2840.00 parts by mass ----------------------------------------------------------------------------------

[0170] In the same manner as in Comparative Example 11, a second optically anisotropic layer was formed on the alignment film P-1.

[0171] When the cross section of the coating layer of the first optically anisotropic layer was examined with a scanning electron microscope, it was confirmed with a polarizing microscope that the cholesteric liquid crystal phase had an 8-pitch and formed a concentric periodic alignment surface as shown in Fig. 8. In addition, in the horizontal rotation alignment pattern of this first optically anisotropic layer, one period was very large at the center (the reciprocal of the period can be considered to be 0), and was 9.0 μm at a distance of 1.0 mm from the center, 4.5 μm at a distance of 2.5 mm from the center, and 3.0 μm at a distance of 4.0 mm from the center, with the period becoming shorter toward the outside.

[0172] The first optically anisotropic layer and the second optically anisotropic layer were laminated to prepare the optical element of Example 11. Note that, when laminating the first optically anisotropic layer and the second optically anisotropic layer, they were laminated so that the continuous rotation directions of the optical axes in the liquid crystal alignment patterns were different from each other.

[0173] In the cross-sectional images taken by SEM, it was observed that the bright and dark lines in both the first and second optically anisotropic layers were inclined obliquely with respect to the normal line of the interface below the optically anisotropic layers. Furthermore, the angle of inclination of the bright and dark lines became smaller from the center to the outside, and the direction of inclination of the bright and dark lines with respect to the normal line of the first and second optically anisotropic layers was the same. It was observed that the period of the bright and dark line patterns became shorter from the center to the outside in both the first and second optically anisotropic layers.

[0174] [evaluation] The optical elements of Comparative Example 11 and Example 11 function as reflective diffraction elements. For each element, the angle of the reflected diffracted light with respect to the normal direction of the optical element when light is incident on the optical element was measured, and the light intensity increase rate was evaluated. The specific measurement method is as follows.

[0175] Laser light is incident on a specified position on the surface of an optical element at a specified angle of incidence, and the reflected light is projected onto a screen placed 30 cm away in the normal direction of the optical element. The image captured by an infrared camera is used to determine the The angle of the reflected and diffracted light was calculated. A laser diode with a wavelength of 940 nm was used as the light source.

[0176] Next, as shown in FIG. 20, a laser light having a wavelength of 940 nm emitted from a laser light source 251 is transmitted through a linear polarizer 252 to become linearly polarized light Lir. This light Lir is incident on a predetermined position on the surface of the optical element S at a predetermined incident angle. The light intensity of the reflected diffracted light Ldr diffracted by the optical element S is measured by a photodetector 256. Then, the ratio of the light intensity of the diffracted light Ldr to the light intensity of the light Lir is calculated to obtain the relative light intensity value of the diffracted light Ldr with respect to the incident light. In addition, the relative light intensity value is similarly calculated by changing the incident angle. The light intensity increase rate of the example with respect to the comparative example is evaluated based on the following criteria for the average value of the relative light intensity values ​​for different incident angles.

[0177] A: Light intensity increase rate is 20% or more B: Light intensity increase rate is 10% or more but less than 20% C: Light intensity increase rate is 5% or more but less than 10% D: Light intensity increase rate is less than 5%

[0178] In comparing Comparative Example 11 with Example 11, the evaluation was performed with the incidence angle set to 10° at a distance of 1.0 mm from the center (one period: 9.0 μm), the incidence angle set to 20° at a distance of 2.5 mm from the center (one period: 4.5 μm), and the incidence angle set to 30° at a distance of 4.0 mm from the center (one period: 3.0 μm).

[0179] The results are shown in Table 2. [Table 2]

[0180] In Example 11, a higher average diffraction efficiency than in Comparative Example 11 was obtained within the incident angle range of 10 to 30°.

[0181] The disclosure of Japanese Patent Application No. 2018-185584, filed on September 28, 2018, is incorporated herein by reference in its entirety. All publications, patent applications, and standards mentioned in this specification are herein incorporated by reference to the same extent as if each individual publication, patent application, or standard was specifically and individually indicated to be incorporated by reference.

Claims

1. a plurality of optically anisotropic layers in a thickness direction, each having an in-plane orientation pattern in which the direction of an optical axis derived from a liquid crystal compound changes while continuously rotating along at least one direction in the plane; the plurality of optically anisotropic layers each have a region having a length different from one another until the orientation of the optical axis rotates 180° in the one direction, each of the optically anisotropic layers has a plurality of pairs of bright and dark lines along the one direction, the pairs being derived from the orientation of the optical axis, in a cross-sectional image obtained by observing a cross-section cut in the thickness direction along the one direction with a scanning electron microscope; a first optically anisotropic layer which is one of the plurality of optically anisotropic layers has regions in which the lengths until the orientation of the optical axis rotates 180° in the one direction are different from each other, and thus the first optically anisotropic layer has regions in which the pair of bright and dark lines in the cross-sectional image are inclined at different inclination angles with respect to a normal to an interface of the optically anisotropic layer, the plurality of optically anisotropic layers includes a second optically anisotropic layer disposed adjacent to the first optically anisotropic layer, no alignment film is provided between the first optically anisotropic layer and the second optically anisotropic layer; the second optically anisotropic layer is a non-tilted optically anisotropic layer in which, in the cross-sectional image, each of the pairs of bright and dark lines extends along the normal line; Optical elements.

2. The optical element described in claim 1, wherein the first optically anisotropic layer and the second optically anisotropic layer are laminated such that regions in which the lengths up to when the orientation of the optical axis is rotated 180° coincide with each other, and in the cross-sectional image, the bright lines and the dark lines of the first optically anisotropic layer and the second optically anisotropic layer are connected at the interface between the two layers.

3. A liquid crystal display device comprising a plurality of optically anisotropic layers in a thickness direction, each having an in-plane orientation pattern in which the direction of an optical axis derived from a liquid crystal compound changes while continuously rotating along at least one direction in the plane, the plurality of optically anisotropic layers each have a region having a length different from one another until the orientation of the optical axis rotates 180° in the one direction, each of the optically anisotropic layers has a plurality of pairs of bright and dark lines along the one direction, the pairs being derived from the orientation of the optical axis, in a cross-sectional image obtained by observing a cross-section cut in the thickness direction along the one direction with a scanning electron microscope; a first optically anisotropic layer which is one of the plurality of optically anisotropic layers has regions in which the lengths until the orientation of the optical axis rotates 180° in the one direction are different from each other, and thus the first optically anisotropic layer has regions in which the pair of bright and dark lines in the cross-sectional image are inclined at different inclination angles with respect to a normal to an interface of the optically anisotropic layer, the plurality of optically anisotropic layers includes a second optically anisotropic layer disposed adjacent to the first optically anisotropic layer, no alignment film is provided between the first optically anisotropic layer and the second optically anisotropic layer; the second optically anisotropic layer is a tilted optically anisotropic layer having regions in which the pairs of bright and dark lines are tilted at different angles with respect to the normal line in the cross-sectional image, In the cross-sectional image, in at least a part of an opposing region between the first optically anisotropic layer and the second optically anisotropic layer, the pair of bright and dark lines in the first optically anisotropic layer and the pair of bright and dark lines in the second optically anisotropic layer have different inclination directions with respect to the normal line. Optical elements.

4. The optical element described in claim 3, wherein in the cross-sectional image, the inclination angles of the pair of bright and dark lines in the first optically anisotropic layer and the pair of bright and dark lines in the second optically anisotropic layer are different from each other in at least a portion of the opposing region between the first optically anisotropic layer and the second optically anisotropic layer.

5. 5. The optical element according to claim 1, wherein the tilted optically anisotropic layer has a region in which the optical axis is twisted in a thickness direction.

6. 6. The optical element according to claim 1, having a function of diffracting and transmitting incident light.

7. 5. The optical element according to claim 1, wherein the liquid crystal compound is cholesterically aligned in the tilted optically anisotropic layer.

8. 8. The optical element according to claim 7, having a function of diffracting and reflecting incident light.

9. 9. An optical element according to claim 1, wherein the in-plane orientation pattern of each of the plurality of optically anisotropic layers is a pattern in which the length until the orientation of the optical axis rotates 180° in the one direction gradually changes in the one direction.

10. 9. The optical element according to claim 1, wherein the in-plane orientation pattern of each of the plurality of optically anisotropic layers is a pattern having the one direction radially from the inside to the outside.

11. The optical element according to claim 1 , wherein the in-plane orientation pattern of each of the plurality of optically anisotropic layers has a region in which the length over which the orientation of the optical axis rotates 180° in the one direction is 10 μm or less.

12. an optical deflection element that deflects and emits incident light; A driving means for driving the optical deflection element; An optical deflection device comprising: the optical element according to claim 1 , which is disposed on a light exit side of the optical deflection element.